JP2008211169A - Sheet-like magnetic substance and its manufacturing method - Google Patents
Sheet-like magnetic substance and its manufacturing method Download PDFInfo
- Publication number
- JP2008211169A JP2008211169A JP2007296339A JP2007296339A JP2008211169A JP 2008211169 A JP2008211169 A JP 2008211169A JP 2007296339 A JP2007296339 A JP 2007296339A JP 2007296339 A JP2007296339 A JP 2007296339A JP 2008211169 A JP2008211169 A JP 2008211169A
- Authority
- JP
- Japan
- Prior art keywords
- magnetic
- sheet
- layer
- resin body
- hard coat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、電磁波を遮蔽するシート状磁性体およびその製造方法に関するものである。 The present invention relates to a sheet-like magnetic body that shields electromagnetic waves and a method for producing the same.
この種のシート状磁性体として、特開平9−116293号公報に開示されたシート状磁性体(電磁波遮蔽材料)が知られている。このシート状磁性体は、シート状の樹脂体(プラスチック製フィルム)の裏面を導電性材料の蒸着層で被覆し、さらに蒸着層の裏面に接着剤を塗布し、この接着剤の面に剥離紙を貼着して形成されている。このシート状磁性体では、シート状樹脂体の裏面の剥離紙を剥ぎ取り、施工すべき部材にアースして貼り付け、必要に応じて、その表面に壁紙を接着剤で貼着するだけで施工が完了する。また、シート状の樹脂体の表面に模様印刷を施したものにあっては、さらに壁紙を貼着する必要はなく、そのままで施工が完了する。したがって、このシート状磁性体によれば、施工コストを低廉になし得ることができる。
ところが、上記のシート状磁性体には、以下の問題点がある。すなわち、このシート状磁性体では、シート状の樹脂体の表面が露出している。このため、このシート状磁性体には、擦れなどにより、シート状の樹脂体の表面自体が傷付いたり、またこの表面に施された模様印刷などが薄くなったり消えたりするといった問題点がある。 However, the above sheet-like magnetic body has the following problems. That is, in this sheet-like magnetic body, the surface of the sheet-like resin body is exposed. For this reason, the sheet-like magnetic body has problems that the surface of the sheet-like resin body itself is damaged by rubbing or the like, and the pattern printing applied to the surface becomes thin or disappears. .
本発明は、かかる問題点に鑑みてなされたものであり、シート状の樹脂体の表面およびその表面に形成された印刷部の少なくとも一方を擦れなどから保護し得るシート状磁性体、およびその製造方法を提供することを主目的とする。 The present invention has been made in view of such problems, and a sheet-like magnetic body capable of protecting at least one of the surface of a sheet-like resin body and a printed portion formed on the surface from rubbing, and the production thereof The main purpose is to provide a method.
上記目的を達成すべく本発明に係るシート状磁性体は、シート状の樹脂体と、少なくとも軟磁性金属磁性粉と結合材とを含んで前記樹脂体の一方の表面に形成された磁性層と、前記樹脂体の他方の表面に形成されたハードコート層とを備えている。 In order to achieve the above object, a sheet-like magnetic body according to the present invention includes a sheet-like resin body, a magnetic layer formed on one surface of the resin body, including at least a soft magnetic metal magnetic powder and a binder. And a hard coat layer formed on the other surface of the resin body.
また、本発明に係るシート状磁性体は、前記ハードコート層は透光性を備え、前記樹脂体の前記他方の表面にインクが印刷されて文字、記号および図形のうちの少なくとも一種を含む印刷部が形成され、前記ハードコート層は、前記印刷部を被覆するように前記樹脂体の前記他方の表面に形成されている。 In the sheet-like magnetic body according to the present invention, the hard coat layer has translucency, and ink is printed on the other surface of the resin body to include at least one of characters, symbols, and figures. A portion is formed, and the hard coat layer is formed on the other surface of the resin body so as to cover the printing portion.
また、本発明に係るシート状磁性体は、前記樹脂体および前記ハードコート層は透光性を備え、前記樹脂体の前記一方の表面にインクが印刷されて文字、記号および図形のうちの少なくとも一種を含む印刷部が形成され、前記磁性層は、前記印刷部を被覆するように前記樹脂体の前記一方の表面に形成されている。 Further, in the sheet-like magnetic body according to the present invention, the resin body and the hard coat layer have translucency, and ink is printed on the one surface of the resin body so that at least one of characters, symbols, and figures A printing part including one kind is formed, and the magnetic layer is formed on the one surface of the resin body so as to cover the printing part.
また、本発明に係るシート状磁性体は、シート状の樹脂体と、少なくとも軟磁性金属磁性粉と結合材とを含んで前記樹脂体の一方の表面に形成された磁性層と、前記磁性層における前記樹脂体との接触面の裏面に形成されたハードコート層とを備えている。 The sheet-like magnetic body according to the present invention includes a sheet-like resin body, a magnetic layer formed on one surface of the resin body including at least a soft magnetic metal magnetic powder and a binder, and the magnetic layer And a hard coat layer formed on the back surface of the contact surface with the resin body.
さらに、本発明に係るシート状磁性体は、前記ハードコート層は透光性を備え、前記磁性層の前記裏面にインクが印刷されて文字、記号および図形のうちの少なくとも一種を含む印刷部が形成され、前記ハードコート層は、前記印刷部を被覆するように前記磁性層の前記裏面に形成されている。 Further, in the sheet-like magnetic body according to the present invention, the hard coat layer has translucency, and an ink is printed on the back surface of the magnetic layer to include a printing unit including at least one of characters, symbols, and figures. The hard coat layer is formed on the back surface of the magnetic layer so as to cover the printing portion.
また、本発明に係るシート状磁性体は、シート状の樹脂体と、少なくとも軟磁性金属磁性粉と結合材とを含んで前記樹脂体における一方の表面および他方の表面にそれぞれ形成された磁性層と、前記両磁性層のうちの一方における前記樹脂体との接触面の裏面に形成されたハードコート層とを備えている。 In addition, the sheet-like magnetic body according to the present invention includes a sheet-like resin body, at least a soft magnetic metal magnetic powder, and a binder, and a magnetic layer formed on one surface and the other surface of the resin body, respectively. And a hard coat layer formed on the back surface of the contact surface with the resin body in one of the magnetic layers.
また、本発明に係るシート状磁性体は、前記ハードコート層は透光性を備え、前記一方の磁性層の前記裏面にインクが印刷されて文字、記号および図形のうちの少なくとも一種を含む印刷部が形成され、前記ハードコート層は、前記印刷部を被覆するように前記磁性層の前記裏面に形成されている。 In the sheet-like magnetic material according to the present invention, the hard coat layer has translucency, and ink is printed on the back surface of the one magnetic layer to include at least one of characters, symbols, and figures. The hard coat layer is formed on the back surface of the magnetic layer so as to cover the printing portion.
また、本発明に係るシート状磁性体は、前記磁性層における前記樹脂体との接触面の裏面側に接着剤層が形成されている。 In the sheet-like magnetic body according to the present invention, an adhesive layer is formed on the back side of the contact surface with the resin body in the magnetic layer.
さらに、本発明に係るシート状磁性体は、前記樹脂体の他方の表面側に接着剤層が形成されている。 Furthermore, in the sheet-like magnetic body according to the present invention, an adhesive layer is formed on the other surface side of the resin body.
また、本発明に係るシート状磁性体は、前記両磁性層のうちの他方における前記樹脂体との接触面の裏面側に接着剤層が形成されている。 In the sheet-like magnetic body according to the present invention, an adhesive layer is formed on the back side of the contact surface with the resin body in the other of the two magnetic layers.
また、本発明に係るシート状磁性体は、前記接着剤層の表面に剥離紙が貼着されている。 In the sheet-like magnetic body according to the present invention, a release paper is attached to the surface of the adhesive layer.
本発明に係るシート状磁性体の製造方法は、シート状の樹脂体の一方の表面に磁性層を形成し、次いで、前記樹脂体の他方の表面にハードコート層を形成し、続いて、前記磁性層の表面に接着剤層および剥離紙をこの順序で積層することによってシート状磁性体を製造する。 In the method for producing a sheet-like magnetic body according to the present invention, a magnetic layer is formed on one surface of a sheet-like resin body, and then a hard coat layer is formed on the other surface of the resin body, An adhesive layer and release paper are laminated in this order on the surface of the magnetic layer to produce a sheet-like magnetic body.
また、本発明に係るシート状磁性体の製造方法は、シート状の樹脂体の一方の表面に磁性層を形成し、次いで、前記樹脂体の他方の表面にインクを印刷して、文字、記号および図形のうちの少なくとも一種を含む印刷部を形成し、続いて、前記樹脂体の他方の表面にハードコート層を形成し、次いで、前記磁性層の表面に接着剤層および剥離紙をこの順序で積層することによってシート状磁性体を製造する。 In the method for producing a sheet-like magnetic body according to the present invention, a magnetic layer is formed on one surface of a sheet-like resin body, and then ink is printed on the other surface of the resin body, so that characters and symbols are printed. And a printed part including at least one of the figures, and subsequently forming a hard coat layer on the other surface of the resin body, and then placing an adhesive layer and release paper on the surface of the magnetic layer in this order. A sheet-like magnetic body is manufactured by laminating the layers.
また、本発明に係るシート状磁性体の製造方法は、シート状の樹脂体の一方の表面にインクを印刷して、文字、記号および図形のうちの少なくとも一種を含む印刷部を形成し、次いで、前記樹脂体の一方の表面に磁性層を形成し、続いて、前記樹脂体の他方の表面にハードコート層を形成し、次いで、前記磁性層の表面に接着剤層および剥離紙をこの順序で積層することによってシート状磁性体を製造する。 Further, in the method for producing a sheet-like magnetic body according to the present invention, ink is printed on one surface of the sheet-like resin body to form a printing unit including at least one of characters, symbols, and figures, A magnetic layer is formed on one surface of the resin body, a hard coat layer is subsequently formed on the other surface of the resin body, and then an adhesive layer and a release paper are formed on the surface of the magnetic layer in this order. A sheet-like magnetic body is manufactured by laminating the layers.
また、本発明に係るシート状磁性体の製造方法は、シート状の樹脂体の一方の表面に磁性層を形成し、次いで、前記磁性層の表面にハードコート層を形成し、続いて、前記樹脂体の他方の表面に接着剤層および剥離紙をこの順序で積層することによってシート状磁性体を製造する。 Further, in the method for producing a sheet-like magnetic body according to the present invention, a magnetic layer is formed on one surface of the sheet-like resin body, and then a hard coat layer is formed on the surface of the magnetic layer. A sheet-like magnetic body is manufactured by laminating an adhesive layer and release paper in this order on the other surface of the resin body.
さらに、本発明に係るシート状磁性体の製造方法は、シート状の樹脂体の一方の表面に磁性層を形成し、次いで、前記磁性層の表面にインクを印刷して、文字、記号および図形のうちの少なくとも一種を含む印刷部を形成し、続いて、前記磁性層の表面にハードコート層を形成し、次いで、樹脂体の他方の表面に前記磁性層の表面に接着剤層および剥離紙をこの順序で積層することによってシート状磁性体を製造する。 Furthermore, in the method for producing a sheet-like magnetic body according to the present invention, a magnetic layer is formed on one surface of a sheet-like resin body, and then ink is printed on the surface of the magnetic layer, so that characters, symbols, and figures are printed. Forming a printing portion including at least one of the above, subsequently forming a hard coat layer on the surface of the magnetic layer, and then forming an adhesive layer and release paper on the surface of the magnetic layer on the other surface of the resin body. Are laminated in this order to produce a sheet-like magnetic body.
また、本発明に係るシート状磁性体の製造方法は、シート状の樹脂体の一方の表面に磁性層を形成し、次いで、前記樹脂体の他方の表面に磁性層を形成し、続いて、前記両磁性層のうちの一方の表面にハードコート層を形成し、次いで、前記両磁性層のうちの他方の表面に接着剤層および剥離紙をこの順序で積層することによってシート状磁性体を製造する。 Moreover, the method for producing a sheet-like magnetic body according to the present invention includes forming a magnetic layer on one surface of the sheet-like resin body, then forming a magnetic layer on the other surface of the resin body, A hard coat layer is formed on one surface of both magnetic layers, and then an adhesive layer and release paper are laminated in this order on the other surface of both magnetic layers to form a sheet-like magnetic body. To manufacture.
また、本発明に係るシート状磁性体の製造方法は、シート状の樹脂体の一方の表面に磁性層を形成し、次いで、前記樹脂体の他方の表面に磁性層を形成し、続いて、前記両磁性層のうちの一方の表面にインクを印刷して、文字、記号および図形のうちの少なくとも一種を含む印刷部を形成し、次いで、前記一方の磁性層の表面にハードコート層を形成し、続いて、前記両磁性層のうちの他方の表面に接着剤層および剥離紙をこの順序で積層することによってシート状磁性体を製造する。 Moreover, the method for producing a sheet-like magnetic body according to the present invention includes forming a magnetic layer on one surface of the sheet-like resin body, then forming a magnetic layer on the other surface of the resin body, Ink is printed on one surface of both magnetic layers to form a printed portion including at least one of characters, symbols, and figures, and then a hard coat layer is formed on the surface of the one magnetic layer Subsequently, a sheet-like magnetic body is manufactured by laminating an adhesive layer and release paper in this order on the other surface of the magnetic layers.
本発明に係るシート状磁性体では、シート状磁性体の表面にハードコート層が形成されている。したがって、このシート状磁性体によれば、ハードコート層によって樹脂体の表面を擦れなどから保護することができると共に、ハードコート層自体が擦れに強く、傷が付きにくいため、シート状磁性体自体の表面への傷付きを大幅に低減することができる。また、本発明に係るシート状磁性体の製造方法によれば、このようなシート状磁性体を簡単、かつ確実に製造することができる。 In the sheet-like magnetic body according to the present invention, a hard coat layer is formed on the surface of the sheet-like magnetic body. Therefore, according to the sheet-like magnetic body, the hard coat layer can protect the surface of the resin body from rubbing and the like, and the hard coat layer itself is resistant to rubbing and is not easily scratched. It is possible to greatly reduce the damage to the surface of the surface. Moreover, according to the method for producing a sheet-like magnetic body according to the present invention, such a sheet-like magnetic body can be produced easily and reliably.
また、本発明に係るシート状磁性体では、樹脂体の表面に印刷部が形成され、透光性を備えたハードコート層がこの印刷部を被覆するように樹脂体の表面に形成されている。したがって、このシート状磁性体によれば、シート状磁性体の表面に印刷部が直接露出しない構成のため、上記した樹脂体の表面の保護などと共に、印刷部に対する擦れも防止することができる結果、印刷部の傷付きや剥がれについても確実に防止することができる。また、本発明に係るシート状磁性体の製造方法によれば、このようなシート状磁性体を簡単、かつ確実に製造することができる。 Further, in the sheet-like magnetic body according to the present invention, a printed portion is formed on the surface of the resin body, and a hard coat layer having translucency is formed on the surface of the resin body so as to cover the printed portion. . Therefore, according to this sheet-like magnetic body, the printed part is not directly exposed on the surface of the sheet-like magnetic body, and therefore, the surface of the resin body can be protected and the rubbing against the printed part can be prevented. Further, it is possible to reliably prevent the printed part from being scratched or peeled off. Moreover, according to the method for producing a sheet-like magnetic body according to the present invention, such a sheet-like magnetic body can be produced easily and reliably.
また、本発明に係るシート状磁性体では、透光性を備えた樹脂体の表面に印刷部が形成され、透光性を備えたハードコート層がこの印刷部を被覆するように樹脂体のこの表面に形成されている。したがって、このシート状磁性体によれば、シート状磁性体の表面に印刷部が直接露出しない構成のため、上記した樹脂体の表面の保護などと共に、印刷部に対する擦れも防止することができる結果、印刷部の傷付きや剥がれについても確実に防止することができる。また、本発明に係るシート状磁性体の製造方法によれば、このようなシート状磁性体を簡単、かつ確実に製造することができる。 Further, in the sheet-like magnetic body according to the present invention, a printed part is formed on the surface of the resin body having translucency, and the hard coat layer having translucency covers the printed part. It is formed on this surface. Therefore, according to this sheet-like magnetic body, the printed part is not directly exposed on the surface of the sheet-like magnetic body, and therefore, the surface of the resin body can be protected and the rubbing against the printed part can be prevented. Further, it is possible to reliably prevent the printed part from being scratched or peeled off. Moreover, according to the method for producing a sheet-like magnetic body according to the present invention, such a sheet-like magnetic body can be produced easily and reliably.
また、本発明に係るシート状磁性体では、磁性層における樹脂体との接触面の裏面にハードコート層が形成されている。したがって、このシート状磁性体によれば、ハードコート層によって磁性層の表面を擦れなどから保護することができると共に、ハードコート層自体が擦れに強く、傷が付きにくいため、シート状磁性体自体の表面への傷付きを大幅に低減することができる。また、本発明に係るシート状磁性体の製造方法によれば、このようなシート状磁性体を簡単、かつ確実に製造することができる。 In the sheet-like magnetic body according to the present invention, a hard coat layer is formed on the back surface of the magnetic layer in contact with the resin body. Therefore, according to this sheet-like magnetic body, the hard coat layer can protect the surface of the magnetic layer from rubbing and the like, and the hard coat layer itself is resistant to rubbing and is not easily scratched. It is possible to greatly reduce the damage to the surface of the surface. Moreover, according to the method for producing a sheet-like magnetic body according to the present invention, such a sheet-like magnetic body can be produced easily and reliably.
さらに、本発明に係るシート状磁性体では、磁性層における樹脂体との接触面の裏面に印刷部が形成され、透光性を備えたハードコート層がこの印刷部を被覆するように磁性層の裏面に形成されている。したがって、このシート状磁性体によれば、シート状磁性体の表面に印刷部が直接露出しない構成のため、上記した磁性層の表面の保護などと共に、印刷部に対する擦れも防止することができる結果、印刷部の傷付きや剥がれについても確実に防止することができる。また、本発明に係るシート状磁性体の製造方法によれば、このようなシート状磁性体を簡単、かつ確実に製造することができる。 Furthermore, in the sheet-like magnetic body according to the present invention, the printed portion is formed on the back surface of the magnetic layer in contact with the resin body, and the hard coat layer having translucency covers the printed portion. It is formed on the back surface. Therefore, according to this sheet-like magnetic body, the printed portion is not directly exposed on the surface of the sheet-like magnetic body, and therefore, the surface of the magnetic layer can be protected and the rubbing against the printed portion can be prevented. Further, it is possible to reliably prevent the printed part from being scratched or peeled off. Moreover, according to the method for producing a sheet-like magnetic body according to the present invention, such a sheet-like magnetic body can be produced easily and reliably.
また、本発明に係るシート状磁性体では、樹脂体における一方の表面および他方の表面にそれぞれ形成された磁性層のうちの一方における樹脂体との接触面の裏面にハードコート層が形成されている。したがって、上記した磁性層の表面の保護などを実現することができると共に、樹脂体の両面に磁性層が形成されているため、電磁波の遮蔽特性を十分に高めることができる。また、本発明に係るシート状磁性体の製造方法によれば、このようなシート状磁性体を簡単、かつ確実に製造することができる。 In the sheet-like magnetic body according to the present invention, the hard coat layer is formed on the back surface of the contact surface with the resin body in one of the magnetic layers formed on one surface and the other surface of the resin body, respectively. Yes. Therefore, the above-described surface protection of the magnetic layer can be realized, and the magnetic layer is formed on both surfaces of the resin body, so that the electromagnetic wave shielding characteristics can be sufficiently enhanced. Moreover, according to the method for producing a sheet-like magnetic body according to the present invention, such a sheet-like magnetic body can be produced easily and reliably.
また、本発明に係るシート状磁性体では、樹脂体の両面にそれぞれ形成された両磁性層のうちの一方における樹脂体との接触面の裏面に印刷部が形成され、透光性を備えたハードコート層がこの印刷部を被覆するように磁性層の裏面に形成されている。したがって、このシート状磁性体によれば、上記した磁性層の表面の保護および印刷部の傷付きや剥がれなどを実現することができると共に、樹脂体の両面に磁性層が形成されているため、電磁波の遮蔽特性を十分に高めることができる。また、本発明に係るシート状磁性体の製造方法によれば、このようなシート状磁性体を簡単、かつ確実に製造することができる。 Moreover, in the sheet-like magnetic body according to the present invention, a printing portion is formed on the back surface of the contact surface with the resin body in one of the two magnetic layers formed on both surfaces of the resin body, and thus has translucency. A hard coat layer is formed on the back surface of the magnetic layer so as to cover the printed portion. Therefore, according to the sheet-like magnetic body, the surface of the magnetic layer can be protected and the printed portion can be scratched or peeled, and the magnetic layer is formed on both surfaces of the resin body. Electromagnetic shielding properties can be sufficiently enhanced. Moreover, according to the method for producing a sheet-like magnetic body according to the present invention, such a sheet-like magnetic body can be produced easily and reliably.
また、本発明に係るシート状磁性体によれば、磁性層における透光性樹脂体との接触面の裏面側に接着剤層を形成したことにより、電磁干渉を抑制しようとする対象製品に容易に貼り付けることができる。 Moreover, according to the sheet-like magnetic body according to the present invention, the adhesive layer is formed on the back side of the contact surface of the magnetic layer with the translucent resin body, so that it is easy for the target product to suppress electromagnetic interference. Can be pasted on.
さらに、本発明に係るシート状磁性体によれば、樹脂体の他方の表面側に接着剤層を形成したことにより、電磁干渉を抑制しようとする対象製品に容易に貼り付けることができる。 Furthermore, according to the sheet-like magnetic body according to the present invention, since the adhesive layer is formed on the other surface side of the resin body, it can be easily attached to a target product for suppressing electromagnetic interference.
また、本発明に係るシート状磁性体によれば、樹脂体の両面にそれぞれ形成された両磁性層のうちの他方における樹脂体との接触面の裏面側に接着剤層を形成したことにより、電磁干渉を抑制しようとする対象製品に容易に貼り付けることができる。 Further, according to the sheet-like magnetic body according to the present invention, by forming the adhesive layer on the back surface side of the contact surface with the resin body in the other of the two magnetic layers respectively formed on both surfaces of the resin body, It can be easily affixed to a target product for suppressing electromagnetic interference.
また、本発明に係るシート状磁性体によれば、接着剤層の表面に剥離紙を貼着したことにより、シート状磁性体を重ね合わせて保管することができるなど、シート状磁性体の保存性を良好なものにすることができる。 In addition, according to the sheet-like magnetic body according to the present invention, the sheet-like magnetic body can be stored, for example, by stacking the sheet-like magnetic body by attaching release paper to the surface of the adhesive layer. The property can be improved.
以下、本発明に係るシート状磁性体およびシート状磁性体の製造方法についての最良の形態について、添付図面を参照して説明する。なお、一例として、クレジットカードなどに記録されている情報のスキミングを防止するためのカードケースに貼着されるシート状磁性体を例に挙げて説明する。 Hereinafter, the best mode of a sheet-like magnetic body and a method for producing a sheet-like magnetic body according to the present invention will be described with reference to the accompanying drawings. As an example, a sheet-like magnetic body attached to a card case for preventing skimming of information recorded on a credit card or the like will be described as an example.
最初に、シート状磁性体1の構成について、図面を参照して説明する。
Initially, the structure of the sheet-like
図1に示すシート状磁性体1は、電磁干渉を抑制すると共に電磁波を遮蔽するシート状磁性体であって、同図に示すように、シート状の樹脂体2、磁性層3、ハードコート層4、接着剤層5および剥離紙6を備えて構成されている。この場合、樹脂体2は、一例として厚みが一例として10μm以上100μm以下の範囲内に規定されたPETフィルムで構成されている。
A sheet-like
磁性層3は、一例として、樹脂等を主材とする結合材に軟磁性金属磁性粉を混合・撹拌して形成された複合磁性材ペーストを、樹脂体2の一方の表面に塗布して乾燥することにより、複合磁性体層として形成されている。この場合、軟磁性金属磁性粉としては、フェライト、センダスト、軟磁性アモルファス合金、軟磁性合金などを使用することができ、また結合材としては、熱可塑性樹脂、熱硬化性樹脂、紫外線硬化性樹脂、電子線硬化性樹脂やこれらの混合物が使用される。具体的には、ポリアミド樹脂、ポリエーテルケトン樹脂、塩化ビニル樹脂、ポリエステル樹脂、エポキシ樹脂、アクリル樹脂、ウレタン樹脂、セルロース樹脂、酢酸ビニル樹脂、ポリカーボネート樹脂などである。これらのポリマー以外に、モノマー、オリゴマーも使用できる。また、軟磁性金属磁性粉の充填量については特に限定されないが、電磁干渉抑制効果の面からは70重量%以上にするのが好ましく、シート状磁性体1において必要な柔軟性を確保するためには95重量%以下とするのが好ましい。また、磁性層3は、一例として、約40μm以上100μm以下の範囲内の厚みで形成されている。この結果、磁性層3は、高い電磁干渉抑制効果を発揮する。
For example, the
ハードコート層4は、ハードコート剤を必要に応じて溶剤に溶解した液を、樹脂体2の他方の表面に塗布、乾燥して、硬化させることによって形成されている。ハードコート剤としては、特に制限されることなく、公知の各種ハードコート剤を用いることができる。例えば、シロキサン系樹脂などの熱硬化型ハードコート剤や、エステル系、アクリル系、ウレタン系、アミド系、シリコーン系、エポキシ系などのモノマーやオリゴマーを光重合開始剤により硬化処理するタイプの紫外線硬化型ハードコート剤や、アクリル・ウレタン系やアクリル・エポキシ系などのモノマーやオリゴマーの複合型紫外線硬化型ハードコート剤を用いることができる。また、ハードコート剤は、グラビアシリンダー、リバース、メイヤーバー等のロールコーター、スリットダイコーター等公知の方法で塗布される。熱硬化型ハードコート剤の場合には、例えば常温〜100℃以下の範囲内の温度で硬化させる。紫外線硬化型ハードコート剤の場合には、紫外線照射を行い、硬化させる。ハードコート層4の厚みは、例えば、0.1μm以上20μm以下の範囲内とする。
The
接着剤層5は、一例として両面テープ(寺岡製作所製:No.707)を磁性層3の表面に貼り付けることによって形成されている。この場合、接着剤層5は、シート状磁性体1の厚みを抑制するため、薄いほど好ましい。なお、両面テープに代えて、接着剤を塗布して接着剤層5を形成してもよい。剥離紙6は、紙やPETフィルムで構成されて、接着剤層5の表面に貼り付けられている。
As an example, the
次に、シート状磁性体1の製造方法について説明する。
Next, the manufacturing method of the sheet-like
まず、不図示のフィルム送り出しロールに巻回された長尺で帯状の樹脂体2を引き出しつつ、不図示の磁性材料塗布装置から、上記のようにして調製された複合磁性材ペーストを樹脂体2の一方の表面に塗布することにより、この一方の表面上に磁性層3を形成する(磁性層形成工程)。次いで、磁性材料塗布装置の下流に配設された不図示の乾燥装置が、形成された磁性層3を乾燥させる(乾燥工程)。続いて、乾燥装置の下流側に配設された不図示のハードコート剤塗布装置からハードコート剤を樹脂体2の他方の表面に塗布することにより、この他方の表面にハードコート層4を形成する(ハードコート層形成工程)。次いで、ハードコート剤塗布装置の下流に配設された不図示の硬化装置が、形成されたハードコート層4を硬化させる(硬化工程)。
First, while pulling out a long and belt-
次いで、一方の表面に剥離紙6が予め貼り付けられた両面テープ(寺岡製作所製:No.707)を不図示の両面テープ供給ロールから引き出しつつ、他方の表面を樹脂体2における磁性層3が形成された一方の表面側(つまり磁性層3の表面)に貼り付けて、両面テープおよび剥離紙6を樹脂体2などと一体化させる(接着剤層形成工程)。これにより、樹脂体2上に形成された磁性層3の表面に両面テープによる接着剤層5が形成されると共に接着剤層5の表面に剥離紙6が形成されて(つまり、磁性層3の表面に接着剤層5および剥離紙6がこの順序で積層されて)、長尺な帯状のシート状磁性体が作製される。この場合、剥離紙6が貼り付けられた両面テープと、磁性層3などが形成された樹脂体2とを一体化させる方法としては、例えば、乾燥装置の下流側に一対のピンチロール(図示せず)を配設し、剥離紙6が貼り付けられた両面テープと、磁性層3などが形成された樹脂体2とを一対のピンチロール間に供給して通過させる方法を採用することができる。最後に、長尺な帯状のシート状磁性体が、カードケースの形状および大きさに合わせて裁断される(裁断工程)。これにより、図1に示すシート状磁性体1が製造される。
Next, while pulling out a double-sided tape (manufactured by Teraoka Seisakusho: No. 707) having
このように、このシート状磁性体1では、剥離紙6を剥いでシート状磁性体1を貼り付けた際に、その表側となる樹脂体2の他方の表面にハードコート層4が形成されている。したがって、このシート状磁性体1によれば、ハードコート層4によって樹脂体2の表面を擦れなどから保護することができると共に、ハードコート層4自体が擦れに強く、傷が付きにくいため、シート状磁性体1自体の表面への傷付きを大幅に低減することができる。
Thus, in this sheet-like
また、このシート状磁性体1によれば、磁性層3における樹脂体2との接触面の裏面側に接着剤層5を形成したことにより、電磁波の遮蔽が必要とされる対象製品自体(本例ではクレジットカード)や、この対象製品を収納する収納体(本例ではカードケース)に容易に貼り付けることができ、これによって電磁波の遮蔽機能をカードケースに容易に付与することができる。
Further, according to the sheet-like
さらに、このシート状磁性体1によれば、接着剤層5の表面に剥離紙6を貼着したことにより、シート状磁性体1を重ね合わせて保管することができるなど、シート状磁性体1の保存性を良好なものにすることができる。
Further, according to the sheet-like
なお、本発明は上記の構成に限定されない。例えば、図2,3に示すシート状磁性体1A,1Bのように、樹脂体2の表面に印刷部7を形成することもできる。
In addition, this invention is not limited to said structure. For example, the
最初に、図2を参照して、シート状磁性体1Aの構造について説明する。なお、シート状磁性体1と同一の構成については同一の符号を付して重複する説明を省略する。
First, the structure of the sheet-like
シート状磁性体1Aは、図2に示すように、シート状の樹脂体2、磁性層3、ハードコート層4、接着剤層5、剥離紙6および印刷部7を備えて構成されている。シート状磁性体1Aは、樹脂体2の他方の表面に印刷部7が形成され、ハードコート層4が樹脂体2の他方の表面に印刷部7を被覆するようにして形成されている点においてシート状磁性体1と相違している。また、ハードコート層4を介して(通して)印刷部7を視認可能とするため、ハードコート層4は、透光性を有するハードコート剤で形成されている。なお、シート状磁性体1Aは、その他の構成についてはシート状磁性体1と同一に構成されている。
As shown in FIG. 2, the sheet-like
印刷部7は、樹脂体2の他方の表面に印刷されたインクによって形成された文字(数字を含む)、記号および図形のうちの少なくとも一種で構成されている。この場合、インクとしては、溶剤型や水性のインクを用いるのが一般的である。また、印刷部7の形成方法としては、グラビア印刷、凸版印刷、オフセット印刷、シルク印刷など、様々な印刷方法を採用することができる。また、シート状磁性体1Aにおいて、印刷部7は上記したようにハードコート層4を介して視認されるため、印刷部7の視認性を向上させるべく、樹脂体2やハードコート層4などと良好に区別し得る色のインクを使用するのが好ましい。また、印刷部7は、インクを一層塗りして形成してもよいし、多層塗りして形成することもできる。
The
このシート状磁性体1Aの製造に際しては、上記したシート状磁性体1の製造工程における磁性層3の乾燥工程の後、ハードコート層形成工程の前に、不図示のグラビア印刷機の版胴からインクを樹脂体2の他方の表面に転写することにより、印刷部7を形成する(印刷部形成工程)。なお、他の工程については、シート状磁性体1と同じである。
When manufacturing this sheet-like
このシート状磁性体1Aにおいても、樹脂体2の他方の表面にハードコート層4が形成されているため、このハードコート層4によって樹脂体2の表面を擦れなどから保護することができ、またハードコート層4自体の傷付きにくさとも相俟って、シート状磁性体1A自体の表面への傷付きを大幅に低減することができる。さらに、このシート状磁性体1Aによれば、シート状磁性体1Aの表面に印刷部7が直接露出しない構成のため、印刷部7に対する擦れも防止することができる結果、印刷部7の傷付きや剥がれについても確実に防止することができる。
Also in this sheet-like
次に、図3を参照して、シート状磁性体1Bの構造について説明する。なお、シート状磁性体1Aと同一の構成については同一の符号を付して重複する説明を省略する。
Next, the structure of the sheet-like
シート状磁性体1Bは、図3に示すように、シート状磁性体1Aと同様にして、シート状の樹脂体2、磁性層3、ハードコート層4、接着剤層5、剥離紙6および印刷部7を備えて構成されている。一方、シート状磁性体1Bは、樹脂体2の一方の表面に印刷部7が形成され、磁性層3が樹脂体2の一方の表面に印刷部7を被覆するようにして形成されている点においてシート状磁性体1Aと相違している。また、ハードコート層4を介して(通して)印刷部7を視認可能とするため、ハードコート層4だけでなく、樹脂体2も透光性を備える材料(樹脂材料)で形成されている。なお、シート状磁性体1Bは、その他の構成についてはシート状磁性体1Aと同一に構成されている。
As shown in FIG. 3, the sheet-like
このシート状磁性体1Bの製造に際しては、上記したシート状磁性体1の製造工程における磁性層形成工程に先立ち、不図示のグラビア印刷機の版胴からインクを樹脂体2の一方の表面に転写することにより、印刷部7を形成する(印刷部形成工程)。なお、他の工程については、シート状磁性体1と同じである。
In the production of the sheet-like
このシート状磁性体1Bにおいても、樹脂体2の他方の表面にハードコート層4が形成されているため、シート状磁性体1,1Aと同様にして、シート状磁性体1B自体の表面への傷付きを大幅に低減することができる。さらに、シート状磁性体1Bにおいても、シート状磁性体1Bの表面に印刷部7が直接露出しない構成のため、印刷部7の傷付きや剥がれを確実に防止することができる。
Also in this sheet-like
また、上記した各シート状磁性体1,1A,1Bの製造においては、磁性層3を形成した後にハードコート層4を形成しているが、磁性層3の形成前にハードコート層4を樹脂体2に形成することもできる。
Further, in the manufacture of each of the sheet-like
また、図4〜図7に示すシート状磁性体1C〜1Fのように、磁性層3の表面にハードコート層4を形成することもできる。この場合、図5,7に示すシート状磁性体1D,1Fのように、磁性層3の表面に印刷部7を形成することもできる。
Moreover, the hard-
最初に、図4を参照して、シート状磁性体1Cの構造について説明する。なお、シート状磁性体1と同一の構成については同一の符号を付して重複する説明を省略する。
First, the structure of the sheet-like magnetic body 1C will be described with reference to FIG. In addition, about the structure same as the sheet-like
シート状磁性体1Cは、図4に示すように、シート状の樹脂体2、磁性層3、ハードコート層4、接着剤層5および剥離紙6を備えて構成されている。このシート状磁性体1Cは、樹脂体2の一方の表面(この場合、同図における上側の表面)に磁性層3が形成され、磁性層3の表面(同図における上側の表面であって、本発明における、樹脂体との接触面の裏面)にハードコート層4が形成されている点において、シート状磁性体1,1A,1Bと相違している。また、シート状磁性体1Cは、接着剤層5および剥離紙6が樹脂体2の他方の表面側(この場合、同図における下側の表面側)にこの順序で積層されている点においても、シート状磁性体1,1A,1Bと相違している。
As shown in FIG. 4, the sheet-like
このシート状磁性体1Cの製造に際しては、上記したシート状磁性体1の製造工程におけるハードコート層形成工程において、磁性層3の表面にハードコート層4を形成する。また、接着剤層形成工程において樹脂体2の他方の表面側(同図における下側の表面側)に接着剤層5および剥離紙6をこの順序で積層する。なお、他の工程については、シート状磁性体1と同じである。
When manufacturing the sheet-like magnetic body 1C, the
このシート状磁性体1Cでは、磁性層3の表面にハードコート層4が形成されているため、このハードコート層4によって磁性層3の表面を擦れなどから保護することができ、またハードコート層4自体の傷付きにくさとも相俟って、シート状磁性体1C自体の表面への傷付きを大幅に低減することができる。
In the sheet-like magnetic body 1C, since the
次に、図5を参照して、シート状磁性体1Dの構造について説明する。なお、シート状磁性体1A,1Bと同一の構成については同一の符号を付して重複する説明を省略する。
Next, the structure of the sheet-like
シート状磁性体1Dは、図5に示すように、シート状磁性体1A,1Bと同様にして、シート状の樹脂体2、磁性層3、透光性を備えたハードコート層4、接着剤層5、剥離紙6および印刷部7を備えて構成されている。一方、シート状磁性体1Dは、樹脂体2の一方の表面(同図における上側の表面)に磁性層3が形成され、磁性層3の表面(同図における上面)に印刷部7が形成されると共に、印刷部7を被覆するようにして、ハードコート層4が磁性層3の表面に形成されている点において、シート状磁性体1A,1Bと相違している。また、シート状磁性体1Cは、接着剤層5および剥離紙6が樹脂体2の他方の表面側(同図における下側の表面側)にこの順序で積層されている点においても、シート状磁性体1A,1Bと相違している。
As shown in FIG. 5, the sheet-like
このシート状磁性体1Dの製造に際しては、上記したシート状磁性体1の製造工程における磁性層3の乾燥工程の後、ハードコート層形成工程の前に、不図示のグラビア印刷機の版胴からインクを磁性層3の表面に転写することによって印刷部7を形成する(印刷部形成工程)。また、ハードコート層形成工程において、印刷部7を被覆するようにして、ハードコート層4を磁性層3の表面に形成し、接着剤層形成工程において樹脂体2の他方の表面側に接着剤層5および剥離紙6をこの順序で積層する。なお、他の工程については、シート状磁性体1と同じである。
When manufacturing the sheet-like
このシート状磁性体1Dにおいても、樹脂体2の他方の表面にハードコート層4が形成されているため、シート状磁性体1,1A〜1Cと同様にして、シート状磁性体1D自体の表面への傷付きを大幅に低減することができる。さらに、シート状磁性体1Dにおいても、シート状磁性体1Dの表面に印刷部7が直接露出しない構成のため、印刷部7の傷付きや剥がれを確実に防止することができる。
Also in this sheet-like
次に、図6を参照して、シート状磁性体1Eの構造について説明する。なお、シート状磁性体1Cと同一の構成については同一の符号を付して重複する説明を省略する。
Next, the structure of the sheet-like
シート状磁性体1Eは、図6に示すように、シート状の樹脂体2、2つの磁性層3,3、ハードコート層4、接着剤層5および剥離紙6を備えて構成されている。このシート状磁性体1Eは、樹脂体2の一方の表面(この場合、同図における上側の表面)、および他方の表面(この場合、同図における下側の表面)の双方(樹脂体2の両面)に磁性層3が形成されている点において、シート状磁性体1Cと相違している。
As shown in FIG. 6, the sheet-like
このシート状磁性体1Eの製造に際しては、上記したシート状磁性体1の製造工程において、樹脂体2の一方の表面に磁性層3を形成した後に、樹脂体2の他方の表面にも磁性層3を形成する。この場合、両磁性層3を樹脂体2の両面に一度に形成する方法を採用することもできる。また、ハードコート層形成工程において、両磁性層3,3のうちの一方の表面にハードコート層4を形成し、両磁性層3,3のうちの他方の表面に接着剤層5および剥離紙6をこの順序で積層する。なお、他の工程については、シート状磁性体1と同じである。
In manufacturing the sheet-like
このシート状磁性体1Eにおいても、磁性層3の表面にハードコート層4が形成されているため、このハードコート層4によって磁性層3の表面を擦れなどから保護することができ、またハードコート層4自体の傷付きにくさとも相俟って、シート状磁性体1E自体の表面への傷付きを大幅に低減することができる。また、このシート状磁性体1Eでは、樹脂体2の両面に磁性層3が形成されているため、電磁波の遮蔽特性を十分に高めることができる。
Also in this sheet-like
次に、図7を参照して、シート状磁性体1Fの構造について説明する。なお、シート状磁性体1Dと同一の構成については同一の符号を付して重複する説明を省略する。
Next, the structure of the sheet-like
シート状磁性体1Fは、図7に示すように、シート状の樹脂体2、2つの磁性層3,3、透光性を備えたハードコート層4、接着剤層5、剥離紙6および印刷部7を備えて構成されている。このシート状磁性体1Fは、樹脂体2の両面に磁性層3が形成されている点において、シート状磁性体1Dと相違している。
As shown in FIG. 7, the sheet-like
このシート状磁性体1Fの製造に際しては、上記したシート状磁性体1の製造工程において、樹脂体2の一方の表面に磁性層3を形成した後に、樹脂体2の他方の表面にも磁性層3を形成し(または、樹脂体2の両面に両磁性層3を一度に形成し)、ハードコート層形成工程の前に、両磁性層3,3のうちの一方の表面に不図示のグラビア印刷機の版胴からインクを転写することによって印刷部7を形成する(印刷部形成工程)。また、ハードコート層形成工程において、印刷部7を被覆するようにして、ハードコート層4を磁性層3の表面に形成し、接着剤層形成工程において、両磁性層3,3のうちの他方の表面側に接着剤層5および剥離紙6をこの順序で積層する。なお、他の工程については、シート状磁性体1と同じである。
In manufacturing the sheet-like
このシート状磁性体1Fにおいても、磁性層3の表面にハードコート層4が形成されているため、このハードコート層4によって磁性層3の表面を擦れなどから保護することができ、またハードコート層4自体の傷付きにくさとも相俟って、シート状磁性体1F自体の表面への傷付きを大幅に低減することができる。また、このシート状磁性体1Fにおいても、シート状磁性体1Fの表面に印刷部7が直接露出しない構成のため、印刷部7の傷付きや剥がれを確実に防止することができる。さらに、このシート状磁性体1Fでは、樹脂体2の両面に磁性層3が形成されているため、電磁波の遮蔽特性を十分に高めることができる。
Also in this sheet-like
1,1A〜1F シート状磁性体
2 樹脂体
3 磁性層
4 ハードコート層
5 接着剤層
6 剥離紙
7 印刷部
1, 1A to 1F Sheet-like
Claims (18)
少なくとも軟磁性金属磁性粉と結合材とを含んで前記樹脂体の一方の表面に形成された磁性層と、
前記樹脂体の他方の表面に形成されたハードコート層とを備えたシート状磁性体。 A sheet-like resin body;
A magnetic layer formed on one surface of the resin body including at least a soft magnetic metal magnetic powder and a binder;
A sheet-like magnetic body provided with a hard coat layer formed on the other surface of the resin body.
前記樹脂体の前記他方の表面にインクが印刷されて文字、記号および図形のうちの少なくとも一種を含む印刷部が形成され、
前記ハードコート層は、前記印刷部を被覆するように前記樹脂体の前記他方の表面に形成されている請求項1記載のシート状磁性体。 The hard coat layer has translucency,
Ink is printed on the other surface of the resin body to form a printing unit including at least one of characters, symbols, and figures,
The sheet-like magnetic body according to claim 1, wherein the hard coat layer is formed on the other surface of the resin body so as to cover the printing portion.
前記樹脂体の前記一方の表面にインクが印刷されて文字、記号および図形のうちの少なくとも一種を含む印刷部が形成され、
前記磁性層は、前記印刷部を被覆するように前記樹脂体の前記一方の表面に形成されている請求項1記載のシート状磁性体。 The resin body and the hard coat layer have translucency,
Ink is printed on the one surface of the resin body to form a printing unit including at least one of characters, symbols, and figures,
The sheet-like magnetic body according to claim 1, wherein the magnetic layer is formed on the one surface of the resin body so as to cover the printing portion.
少なくとも軟磁性金属磁性粉と結合材とを含んで前記樹脂体の一方の表面に形成された磁性層と、
前記磁性層における前記樹脂体との接触面の裏面に形成されたハードコート層とを備えたシート状磁性体。 A sheet-like resin body;
A magnetic layer formed on one surface of the resin body including at least a soft magnetic metal magnetic powder and a binder;
The sheet-like magnetic body provided with the hard-coat layer formed in the back surface of the contact surface with the said resin body in the said magnetic layer.
前記磁性層の前記裏面にインクが印刷されて文字、記号および図形のうちの少なくとも一種を含む印刷部が形成され、
前記ハードコート層は、前記印刷部を被覆するように前記磁性層の前記裏面に形成されている請求項4記載のシート状磁性体。 The hard coat layer has translucency,
Ink is printed on the back surface of the magnetic layer to form a printing unit including at least one of characters, symbols, and figures,
The sheet-like magnetic body according to claim 4, wherein the hard coat layer is formed on the back surface of the magnetic layer so as to cover the printing portion.
少なくとも軟磁性金属磁性粉と結合材とを含んで前記樹脂体における一方の表面および他方の表面にそれぞれ形成された磁性層と、
前記両磁性層のうちの一方における前記樹脂体との接触面の裏面に形成されたハードコート層とを備えたシート状磁性体。 A sheet-like resin body;
A magnetic layer including at least a soft magnetic metal magnetic powder and a binder and formed on one surface and the other surface of the resin body,
A sheet-like magnetic body comprising a hard coat layer formed on the back surface of the contact surface with the resin body in one of the magnetic layers.
前記一方の磁性層の前記裏面にインクが印刷されて文字、記号および図形のうちの少なくとも一種を含む印刷部が形成され、
前記ハードコート層は、前記印刷部を被覆するように前記磁性層の前記裏面に形成されている請求項6記載のシート状磁性体。 The hard coat layer has translucency,
Ink is printed on the back surface of the one magnetic layer to form a printing unit including at least one of characters, symbols, and figures,
The sheet-like magnetic body according to claim 6, wherein the hard coat layer is formed on the back surface of the magnetic layer so as to cover the printing portion.