JP2008207346A

JP2008207346A - Composite sheet

Info

Publication number: JP2008207346A
Application number: JP2007043548A
Authority: JP
Inventors: Minoru Mitani; 稔三谷
Original assignee: Individual
Current assignee: Individual
Priority date: 2007-02-23
Filing date: 2007-02-23
Publication date: 2008-09-11

Abstract

<P>PROBLEM TO BE SOLVED: To provide a composite sheet having an anodized coating film rich in corrosion resistance and weathering properties and being easily molded. <P>SOLUTION: The composite sheet comprises an aluminum foil one surface of which has the anodized coating film and its protective member. The anodized coating film is impregnated with gold, silver, iron, copper, tungsten, tin, cobalt, titanium and/or germanium and other metals to provide antifungal properties. The composite sheet is flexible or rigid, and is utilized for manufacturing products such as various home products, stationaries, construction materials and medical products by sticking it on the surfaces or the inner faces of various products and molding it alone. <P>COPYRIGHT: (C)2008,JPO&INPIT

Description

本発明は、複合シート、特に陽極酸化皮膜を有するアルミ箔を含む複合シートに関する。 The present invention relates to a composite sheet, particularly a composite sheet including an aluminum foil having an anodized film.

金属箔に粘着シート又は両面接着シートを貼着してなる複合シートは、導電性シート、電磁は遮蔽シートなどに用いられているが、陽極酸化皮膜を有するアルミ箔に粘着シート又は両面接着シートを貼着して成る複合シート、及び、陽極酸化皮膜を有するアルミ箔を貼り合せてなる複合シートは知られていない。 Composite sheet made by sticking adhesive sheet or double-sided adhesive sheet to metal foil is used for conductive sheet, electromagnetic shielding sheet, etc., but adhesive sheet or double-sided adhesive sheet is used for aluminum foil with anodized film A composite sheet formed by bonding and a composite sheet formed by bonding an aluminum foil having an anodized film are not known.

このような陽極酸化皮膜を有する複合シートは、耐食性、耐候性に富み、成形加工が容易であり、特に、陽極酸化被覆中に、銀、銅などの抗菌作用を奏する金属を含侵したものは、様々な家庭用品、家電製品、日用雑貨その他の抗菌性製品の製造に広く利用できるものである。
又、ゲルマニウムは状態によっては、半導体となるが、人体に対して様々な活性を示すので、その性質を利用して、様々な製品に利用することができる。
上記以外の金属，例えば、金、錫、鉄、コバルト、チタン等を含浸したものもその色彩、風合い、成形の容易性、耐候性、耐食性等の性質を利用し、例えば建築物の内装材、外装材その他様々な用途に用いることができる。 The composite sheet having such an anodized film is rich in corrosion resistance and weather resistance, and is easy to be molded. Particularly, the anodized coating impregnated with a metal having an antibacterial action such as silver or copper. It can be widely used in the manufacture of various household goods, household appliances, household goods and other antibacterial products.
Further, although germanium becomes a semiconductor depending on the state, it exhibits various activities on the human body, and can be used for various products by utilizing its properties.
Metals other than the above, for example, those impregnated with gold, tin, iron, cobalt, titanium, etc. also take advantage of their color, texture, ease of molding, weather resistance, corrosion resistance, etc., for example, interior materials for buildings, It can be used for exterior materials and other various uses.

本発明が解決しようとする課題は、上記の如く各種製品の材料として使用できる、陽極酸化皮膜を有する複合シートを提供するである。
尚本明細書で，「シート」と言うときは、柔軟で幅広い、所謂シート形状のもののみでなく、テープ状、帯状、フィルム状のもの、シール形状のもの、剛性を有する板状などのもの、パンチングシートなどを総て包含するものとする。
「複合シート」とは、少なくとも一方の表面に陽極酸化被膜を形成したアルミ箔と、接着剤層及び／又はその接着剤のシート状担体から成る「シート」を言うものとする。 The problem to be solved by the present invention is to provide a composite sheet having an anodized film that can be used as a material for various products as described above.
In this specification, the term “sheet” is not limited to a so-called sheet shape that is flexible and broad, but also includes a tape shape, a belt shape, a film shape, a seal shape, a rigid plate shape, and the like. All punching sheets are included.
“Composite sheet” refers to a “sheet” comprising an aluminum foil having an anodized film formed on at least one surface thereof, an adhesive layer and / or a sheet-like carrier of the adhesive.

本発明の第一実施例において、複合シートは、少なくとも一方の表面に陽極酸化被膜を形成したアルミ箔と、そのアルミ箔の他の一方の表面に貼着された粘着シートとから成る。 In the first embodiment of the present invention, the composite sheet is composed of an aluminum foil having an anodized film formed on at least one surface and an adhesive sheet adhered to the other surface of the aluminum foil.

本発明の第二実施例において、複合シートは、少なくとも一方の表面に陽極酸化被膜を形成したアルミ箔と、そのアルミ箔の他の一方の表面に貼着された両面接着シートと、その離型紙とから成る。 In the second embodiment of the present invention, the composite sheet includes an aluminum foil having an anodized film formed on at least one surface, a double-sided adhesive sheet adhered to the other surface of the aluminum foil, and a release paper thereof. It consists of.

本発明の第三実施例において、複合シートは、少なくとも一方の表面に陽極酸化被膜を形成したアルミ箔と、そのアルミ箔の他の一方の表面に積層された合成樹脂シートとから成る。 In the third embodiment of the present invention, the composite sheet comprises an aluminum foil having an anodized film formed on at least one surface and a synthetic resin sheet laminated on the other surface of the aluminum foil.

本発明の第四実施例において、複合シートは、それぞれ少なくとも一方の表面に陽極酸化被膜を形成したアルミ箔を両面接着シートで接着して成る。 In the fourth embodiment of the present invention, the composite sheet is formed by adhering an aluminum foil having an anodized film formed on at least one surface with a double-sided adhesive sheet.

本発明の第五実施例において、複合シートは、それぞれ少なくとも一方の表面に陽極酸化被膜を形成したアルミ箔を接着剤で接着して成る。 In the fifth embodiment of the present invention, the composite sheet is formed by bonding an aluminum foil having an anodized film formed on at least one surface thereof with an adhesive.

本発明の第六実施例において、複合シートは、一方の表面に陽極酸化被膜を形成したアルミ箔と、その裏面に設けられた接着剤層と、離型紙とから成る。 In the sixth embodiment of the present invention, the composite sheet is composed of an aluminum foil having an anodized film formed on one surface thereof, an adhesive layer provided on the back surface thereof, and release paper.

本発明の第七実施例において、複合シートは、一方の表面に陽極酸化被膜を形成したアルミ箔と、その裏面に設けられた接着剤層とから成る。 In the seventh embodiment of the present invention, the composite sheet is composed of an aluminum foil having an anodized film formed on one surface and an adhesive layer provided on the back surface thereof.

本発明の第八実施例において、複合シートは、一方の表面に陽極酸化被膜を形成したアルミ箔と、その陽極酸化被膜の上に積層される多数のスリットを有する粘着剤層と、粘着剤層に上に積層される離型紙と、アルミ箔の他の一方の表面に貼着された保護シートとから成る。 In the eighth embodiment of the present invention, the composite sheet comprises an aluminum foil having an anodized film formed on one surface, an adhesive layer having a number of slits laminated on the anodized film, and an adhesive layer. The release paper is laminated on top of the other, and the protective sheet is attached to the other surface of the aluminum foil.

上記何れの実施例においても、アルミ箔の陽極酸化皮膜中に金、銀、鉄、銅、タングステン、錫、コバルト、チタン、ゲルマニウム及び／又は他の金属を含浸させておくことが望ましい。 In any of the above embodiments, it is desirable to impregnate the anodized film of the aluminum foil with gold, silver, iron, copper, tungsten, tin, cobalt, titanium, germanium and / or other metals.

本発明に係る複合シートは、特に抗菌性を必要とする各種製品の表面に貼着して使用することができる。
又、本発明に係る複合シートは、それ単独で成形し、硬化させ、各種製品を製造するため使用することができる。
このため、本発明を実施すれば多大の利益がある。 The composite sheet according to the present invention can be used by sticking to the surface of various products that require antibacterial properties.
Further, the composite sheet according to the present invention can be molded and cured by itself to be used for producing various products.
For this reason, if this invention is implemented, there will be a great profit.

図1、図2、図3、図4、図5、図6、図7及び図8は、それぞれ本発明の第一、第二、第三、第四、第五、第六、第七及び第八実施例の構成を示す一部拡大部分断面図である。
以下、第一実施例から順次説明する。 1, 2, 3, 4, 5, 6, 7, and 8 are the first, second, third, fourth, fifth, sixth, seventh, and seventh of the present invention, respectively. It is a partial expanded partial sectional view which shows the structure of an 8th Example.
Hereinafter, the first embodiment will be described sequentially.

図1において、10は複合シートであり、本実施例においては一方の表面に陽極酸化皮膜12aを形成したアルミ箔12と、そのアルミ箔12の他の一方の陽極酸化皮膜が形成されていない面に貼着された粘着シート14とから成る。 In FIG. 1, reference numeral 10 denotes a composite sheet. In this embodiment, an aluminum foil 12 having an anodized film 12a formed on one surface thereof, and a surface on which the other anodized film of the aluminum foil 12 is not formed. And an adhesive sheet 14 affixed to.

アルミ箔としては、特に限定はされないが、純アルミ若しくはアルミ合金製の箔で、厚みが5〜20μ程度、望ましくは、8〜12μ程度のものを使用することが推奨される。市販のアルミホイルは、通常厚み10μであるので好適に用いることができる。
この場合、陽極酸化皮膜の厚みは、2〜5μ程度、望ましくは、3〜4μとすることが望ましい。 The aluminum foil is not particularly limited, but it is recommended to use a pure aluminum or aluminum alloy foil having a thickness of about 5 to 20 μm, preferably about 8 to 12 μm. Commercially available aluminum foil has a thickness of usually 10 μm and can be suitably used.
In this case, the thickness of the anodized film is about 2 to 5 μm, preferably 3 to 4 μm.

尚、剛性が求められる複合シートにおいては、アルミ箔のアルミは制限されないが、アルミは高価であるから、20ミクロン以下とし、必要な剛性は、粘着シート14として、不織布に熱硬化性樹脂を含浸させて成るボードを用いるようにすることが推奨される。 In the composite sheet where rigidity is required, aluminum of aluminum foil is not limited, but aluminum is expensive, so it should be 20 microns or less, and the required rigidity is as adhesive sheet 14, impregnating the nonwoven fabric with thermosetting resin It is recommended to use a board made of

粘着シート14は、繊維からなる織布又は不織布、又は、それらに合成樹脂を含浸して成るシートを担体12aとし、これの一表面に例えばポリオレフィン系樹脂や天然ゴム系粘着剤などから成る感圧接着剤12ｂを塗布したものを用いることができる。 The pressure-sensitive adhesive sheet 14 is a woven or non-woven fabric made of fibers, or a sheet formed by impregnating them with a synthetic resin as a carrier 12a, and a pressure sensitive material made of, for example, a polyolefin resin or a natural rubber pressure sensitive adhesive on one surface thereof. What apply | coated the adhesive agent 12b can be used.

粘着シート12の担体12aとしては、各種動植物繊維、合成樹脂繊維、カーボン繊維、ガラス繊維などの無機質繊維などから成る織布又は不織布が用いられる。
又、複合シートの用途によっては、感圧接着剤に代えて、熱可塑性若しくは熱硬化性接着剤を用いることがある。 As the carrier 12a of the pressure-sensitive adhesive sheet 12, a woven fabric or a non-woven fabric made of various animal and plant fibers, synthetic resin fibers, carbon fibers, glass fibers, and other inorganic fibers is used.
Depending on the use of the composite sheet, a thermoplastic or thermosetting adhesive may be used instead of the pressure sensitive adhesive.

又、別異の実施例においては、粘着シート14として、熱可塑性樹脂フィルム、熱硬化性樹脂フィルム又は光硬化性樹脂フィルムなどをアルミ箔12の一面に積層して使用する。 In another embodiment, as the pressure-sensitive adhesive sheet 14, a thermoplastic resin film, a thermosetting resin film, a photocurable resin film or the like is laminated on one surface of the aluminum foil 12.

この複合シート10を製造する際には、陽極酸化処理をしていないアルミ箔と粘着シートを貼り合せた後、陽極酸化処理を行なってもよく、又、片面又は両面に陽極酸化処理を施したアルミ箔12を、粘着シート14に貼着するようにしても良い。 When manufacturing this composite sheet 10, anodized aluminum foil and an adhesive sheet may be bonded to each other and then anodized, or one or both sides may be anodized. The aluminum foil 12 may be adhered to the adhesive sheet 14.

而して、このときの処理条件は以下のようにすることが推奨される。
浴液組成
硫酸 15〜40 gr／リットル
アクリル酸 15〜 2 gr／リットル
酒石酸 1.0〜 2 gr／リットル
マロン酸 1.0〜 2 gr／リットル
浴液温度 15〜32 ℃
電流密度 0.5〜1.5 A／dm² Therefore, it is recommended that the processing conditions at this time be as follows.
Bath solution composition Sulfuric acid 15-40 gr / liter Acrylic acid 15-2 gr / liter Tartaric acid 1.0-2 gr / liter Malonic acid 1.0-2 gr / liter Bath solution temperature 15-32 ℃
Current density 0.5 to 1.5 A / dm ²

更に、上記による陽極酸化処理を行なった後、以下の条件で、銀、鉄、銅、錫、チタン、タングステン、コバルト及び／又は有機ゲルマニウムを含浸させる。
1．浴液
1‐1 銀含浸の場合
硫酸銀又は硝酸銀 6〜12 gr／リットル
ほう酸 10〜15 gr／リットル
硫酸ニッケル 10〜12 gr／リットル
1−2 鉄含浸の場合
硫酸鉄又は硝酸鉄 6〜12 gr／リットル
ほう酸 10〜15 gr／リットル
硫酸ニッケル 10〜12 gr／リットル
1‐3 銅含浸の場合
硫酸銅又は硝酸銅 10〜15 gr／リットル
ほう酸 10〜15 gr／リットル
硫酸ニッケル 10〜12 gr／リットル
1‐4 タングステン含浸の場合
硫酸タングステン又は硝酸タングステン 10〜15 gr／リットル
ほう酸 10〜15 gr／リットル
硫酸ニッケル 10〜12 gr／リットル
1‐5 錫含浸の場合
硫酸錫又は硝酸錫 10〜15 gr／リットル
ほう酸 10〜15 gr／リットル
硫酸ニッケル 10〜12 gr／リットル
1‐6 コバルト含浸の場合
硫酸コバルト又は硝酸コバルト 10〜15 gr／リットル
ほう酸 10〜15 gr／リットル
硫酸ニッケル 10〜12 gr／リットル
1‐7 チタン含浸の場合
硫酸チタン又は硝酸チタン 10〜15 gr／リットル
ほう酸 10〜15 gr／リットル
硫酸ニッケル 10〜15 gr／リットル
1‐8 有機ゲルマニウム含浸の場合
水溶性有機ゲルマニウム 13〜18 gr／リットル
硫酸又は硝酸 10〜15 gr／リットル
ほう酸 10〜15 gr／リットル
硫酸ニッケル 5〜10 gr／リットル
2. 処理条件
浴液温度 15〜40 ℃
電流密度 0.5〜3 A／dm²
通電時間 2〜5 分
直量電圧 10〜15V Further, after the anodizing treatment as described above, silver, iron, copper, tin, titanium, tungsten, cobalt and / or organic germanium are impregnated under the following conditions.
1． Bath solution
1-1 In case of silver impregnation
Silver sulfate or silver nitrate 6-12 gr / liter Boric acid 10-15 gr / liter Nickel sulfate 10-12 gr / liter
1-2 Iron impregnation Iron sulfate or iron nitrate 6-12 gr / liter Boric acid 10-15 gr / liter Nickel sulfate 10-12 gr / liter
1-3 In the case of copper impregnation Copper sulfate or copper nitrate 10-15 gr / liter Boric acid 10-15 gr / liter Nickel sulfate 10-12 gr / liter
1-4 In the case of tungsten impregnation Tungsten sulfate or tungsten nitrate 10-15 gr / liter Boric acid 10-15 gr / liter Nickel sulfate 10-12 gr / liter
1-5 Tin impregnation Tin sulfate or tin nitrate 10-15 gr / liter Boric acid 10-15 gr / liter Nickel sulfate 10-12 gr / liter
1-6 Cobalt impregnation Cobalt sulfate or cobalt nitrate 10-15 gr / liter Boric acid 10-15 gr / liter Nickel sulfate 10-12 gr / liter
1-7 Titanium impregnation Titanium sulfate or titanium nitrate 10-15 gr / liter Boric acid 10-15 gr / liter Nickel sulfate 10-15 gr / liter
1-8 In the case of impregnation with organic germanium Water-soluble organic germanium 13-18 gr / liter Sulfuric acid or nitric acid 10-15 gr / liter Boric acid 10-15 gr / liter Nickel sulfate 5-10 gr / liter
2. Treatment conditions Bath temperature 15 ~ 40 ℃
Current density 0.5-3 A / dm ²
Energizing time 2-5 minutes Direct voltage 10-15V

このようにして製造された複合フィルムは、強い抗菌性と耐摩耗性を有し、且つ、用途に応じて所望の柔軟性又は剛性、成形性を有するので、様々な場所で使用することができる。
例えば、医院や病院の、待合室、病室、トイレ等の壁紙や床材、ベッドやイス、ディスクその他の各種什器備品の外装材などとして用いれば、院内感染などの危険を大幅に軽減できる。 The composite film produced in this way has strong antibacterial properties and abrasion resistance, and has desired flexibility, rigidity, and moldability depending on the application, so it can be used in various places. .
For example, if it is used as wallpaper or flooring for waiting rooms, hospital rooms, toilets, etc. in hospitals or hospitals, as exterior materials for beds, chairs, disks, and other various fixtures, the risk of nosocomial infections can be greatly reduced.

又更に、この複合シートは、それ自体で様々な形状に成型加工し得るから，各種のトレイや食器、事務用品、建築資材その他の製造に利用できるものである。
この複合シートで製造した建築資材を鶏舎の構築に使用すれば、鳥インフルエンaザの予防に役立つと考えられる。 Furthermore, since the composite sheet can be molded into various shapes by itself, it can be used for manufacturing various trays, tableware, office supplies, building materials and the like.
If building materials made with this composite sheet are used to build a poultry house, it is thought to be useful in preventing bird flu.

図2において、20は複合シートであり、本実施例においては一方の表面に陽極酸化皮膜22aを形成したアルミ箔22と、そのアルミ箔22の他の一方の陽極酸化皮膜が形成されていない面に貼着された用面接着シート24と、剥離紙26とから成る。 In FIG. 2, 20 is a composite sheet, and in this embodiment, an aluminum foil 22 having an anodized film 22a formed on one surface and a surface on which the other anodized film of the aluminum foil 22 is not formed. And a release sheet 26. The surface adhesive sheet 24 and the release paper 26 are attached to each other.

この複合シート20は、図1に示した複合シート10の粘着シート14の代わりに、両面接着シート24とその剥離紙26を用いたものである。従って、この製造方法、使用方法は既に明らかであると思量するので、それらの説明は省略する。 This composite sheet 20 uses a double-sided adhesive sheet 24 and its release paper 26 instead of the adhesive sheet 14 of the composite sheet 10 shown in FIG. Therefore, since it is assumed that the manufacturing method and the usage method are already clear, the description thereof will be omitted.

図3に示す複合シート30は、アルミ箔32と合成樹脂シート34を貼りあわせ、これに陽極酸化処理を施し、アルミ箔32の表面に陽極酸化被膜32aを形成して成るものである。
即ち、この複合シート30は、少なくとも一方の表面に陽極酸化被膜32aを形成したアルミ箔32と、そのアルミ箔32の他の一方の表面に積層された合成樹脂シート34とから成る。 The composite sheet 30 shown in FIG. 3 is formed by bonding an aluminum foil 32 and a synthetic resin sheet 34, anodizing them, and forming an anodized film 32a on the surface of the aluminum foil 32.
That is, the composite sheet 30 includes an aluminum foil 32 having an anodized film 32a formed on at least one surface, and a synthetic resin sheet 34 laminated on the other surface of the aluminum foil 32.

この合成樹脂シート34の材料は、例えば熱可塑性樹脂でも、熱硬化性樹脂でも良く、又、適宜のフィラーを混合しておくことも推奨される。
張り合わせる方法は、加熱圧着、超音波接着、接着剤による方法など何であっても良い。
又、アルミ箔32には、予めエンボス加工などを施すこともある。
この複合シート30の使用法、用途については、前に説明した複合シート10、20と同様であるから最早説明する必要はないと思量する。 The material of the synthetic resin sheet 34 may be, for example, a thermoplastic resin or a thermosetting resin, and it is also recommended to mix an appropriate filler.
The bonding method may be any method such as thermocompression bonding, ultrasonic bonding, or an adhesive method.
The aluminum foil 32 may be embossed in advance.
Since the usage and use of the composite sheet 30 are the same as those of the composite sheets 10 and 20 described above, it is considered unnecessary to explain them anymore.

図4に示す複合シート40は、二枚のアルミ箔42及び43を両面接着シート44により貼り合わせ、陽極酸化処理を施し、陽極酸化被膜42a、43aを形成して成るものである。
即ち、この複合シート40は、それぞれ一方の表面に陽極酸化被膜42a、43aを形成した2枚のアルミ箔42、43と、それらのアルミ箔42、43の他の一方の表面同士を接着する両面接着シート44とから成る。 The composite sheet 40 shown in FIG. 4 is formed by bonding two aluminum foils 42 and 43 together with a double-sided adhesive sheet 44 and performing anodizing treatment to form anodized films 42a and 43a.
That is, the composite sheet 40 has two aluminum foils 42 and 43 each having an anodic oxide coating 42a and 43a formed on one surface thereof, and both surfaces for bonding the other surfaces of the aluminum foils 42 and 43 to each other. And an adhesive sheet 44.

両面接着シート44は、不織布から成る担体44aの両面に接着剤層44b、44cを設けたタイプのものを示してあるが、他の構成のもの、例えば、不織布から成る担体に接着剤を含浸させたものなどであっても良い。
接着剤としては、天然ゴム系、ウレタン系、ポリエチレン系などの樹脂を、複合シート40の用途に応じて適宜に選択することが推奨される。
このアルミ箔42、43の双方又は一方に、予めエンボス加工などを施すこともある。
この複合シート40の使用法、用途については、説明を省略する。 The double-sided adhesive sheet 44 is of a type in which adhesive layers 44b and 44c are provided on both sides of a carrier 44a made of nonwoven fabric. However, other configurations, for example, a carrier made of nonwoven fabric is impregnated with an adhesive. It may be a thing.
As the adhesive, it is recommended that a natural rubber-based resin, urethane-based resin, polyethylene-based resin, or the like is appropriately selected according to the application of the composite sheet 40.
Both or one of the aluminum foils 42 and 43 may be embossed in advance.
Description of the usage and application of the composite sheet 40 is omitted.

図5に示す複合シート50は、二枚のアルミ箔52及び53を接着剤層54により貼り合わせ、陽極酸化処理を施し、陽極酸化被膜42a、43aを形成して成るものである。
この複合シート50は、それぞれ一方の表面に陽極酸化被膜52a、53aを形成した2枚のアルミ箔52、53と、それらのアルミ箔52、53の他の一方の表面同士を接着する接着剤層54とから成る。 A composite sheet 50 shown in FIG. 5 is formed by bonding two aluminum foils 52 and 53 together with an adhesive layer 54 and performing anodizing treatment to form anodized films 42a and 43a.
This composite sheet 50 is composed of two aluminum foils 52 and 53 each having an anodized film 52a and 53a formed on one surface thereof, and an adhesive layer that bonds the other surfaces of the aluminum foils 52 and 53 to each other. It consists of 54.

接着剤としては、天然ゴム系、ウレタン系、ポリエチレン系などの樹脂を、複合シート40の用途に応じて適宜に選択することが推奨される。
このアルミ箔52、53の双方又は一方に、予めエンボス加工などを施すこともある。
この複合シート50の使用法、用途についても説明を省略する。 As the adhesive, it is recommended that a natural rubber-based resin, urethane-based resin, polyethylene-based resin, or the like is appropriately selected according to the application of the composite sheet 40.
Both or one of the aluminum foils 52 and 53 may be embossed in advance.
Description of the usage and application of the composite sheet 50 is also omitted.

図6に示した複合シート60は、アルミ箔62の一面に、接着剤を塗布して接着剤層64を形成し、離型紙66を貼り合せ、アルミ箔62の表面に陽極酸化処理を施して成るものである。
即ち、この複合シート60は、一方の表面に陽極酸化被膜62aを形成したアルミ箔62と、その裏面に設けられた接着剤層64と、離型紙66とから成る。
この複合シート60の使用法、用途についても説明を省略する。 In the composite sheet 60 shown in FIG. 6, an adhesive is applied to one surface of an aluminum foil 62 to form an adhesive layer 64, a release paper 66 is bonded, and the surface of the aluminum foil 62 is anodized. It consists of.
That is, the composite sheet 60 includes an aluminum foil 62 having an anodized film 62a formed on one surface, an adhesive layer 64 provided on the back surface thereof, and a release paper 66.
Description of the usage and application of the composite sheet 60 is also omitted.

図7に示した複合シート70は、アルミ箔72の一面に、接着剤を塗布して乾燥させた後、アルミ箔72の表面に陽極酸化処理を施して成るものである。
即ち、この複合シート70は、一方の表面に陽極酸化被膜72aを形成したアルミ箔72と、その裏面に設けられた接着剤層74とから成る。
この複合シート70の使用法、用途についても説明を省略する。 The composite sheet 70 shown in FIG. 7 is obtained by applying an adhesive to one surface of an aluminum foil 72 and drying it, and then subjecting the surface of the aluminum foil 72 to an anodic oxidation treatment.
That is, the composite sheet 70 includes an aluminum foil 72 having an anodized film 72a formed on one surface and an adhesive layer 74 provided on the back surface thereof.
Description of the usage and application of the composite sheet 70 is also omitted.

図8に示した複合シート80は、絆創膏などとして使用できる複合シートであり、図中、82はアルミ箔、84は多数のスリット84aを有する粘着剤シート、86は離型紙、88は保護シートである。
この複合シート80を製造するときは、アルミ箔82の一面に、粘着剤を塗布し乾燥させて保護シート88を形成し、陽極酸化処理を施してアルミ箔82の表面に陽極酸化被膜82aを形成し、その陽極酸化被膜82aの上に、多数のスリットを有する粘着剤層84を設け、その上に離型紙86を貼着し、所望の形状に切断する。 The composite sheet 80 shown in FIG. 8 is a composite sheet that can be used as an adhesive bandage or the like. In the figure, 82 is an aluminum foil, 84 is an adhesive sheet having a large number of slits 84a, 86 is a release paper, and 88 is a protective sheet. is there.
When manufacturing this composite sheet 80, an adhesive is applied to one surface of the aluminum foil 82 and dried to form a protective sheet 88, and anodized to form an anodized film 82a on the surface of the aluminum foil 82. Then, an adhesive layer 84 having a large number of slits is provided on the anodic oxide coating 82a, and a release paper 86 is adhered thereon and cut into a desired shape.

この複合シート80は、一方の表面に陽極酸化被膜82aを形成したアルミ箔82と、その陽極酸化被膜82aの上に積層される多数のスリット84aを有する粘着剤層84と、粘着剤層84に上に積層される離型紙86と、アルミ箔82の他の一方の表面に貼着された保護シート88とから成る。 This composite sheet 80 includes an aluminum foil 82 having an anodized film 82a formed on one surface thereof, an adhesive layer 84 having a large number of slits 84a laminated on the anodized film 82a, and an adhesive layer 84. It comprises a release paper 86 laminated thereon and a protective sheet 88 attached to the other surface of the aluminum foil 82.

而して、上記の各実施例において、様々な付加加工、例えばアルミ箔の酸化被膜には保護フィルムを被覆したり、適宜に着色加工又はプリント加工を施したり、切断加工、成型加工を施したりすることもある。 Thus, in each of the above embodiments, various additional processes, for example, an oxide film of aluminum foil is covered with a protective film, appropriately colored or printed, cut, or molded. Sometimes.

又、本発明の構成は叙上の実施例に限定されるものでなく、上記の説明から容易に想到し得る陽極酸化被膜を形成したアルミ箔を含む総てのシート、フィルム、テープ、ボード、プレート、シールなどの総てを包摂するものである。 Further, the structure of the present invention is not limited to the above-described embodiments, and all sheets, films, tapes, boards, including aluminum foils on which an anodized film that can be easily conceived from the above description, are provided. Includes all plates, seals, etc.

図1は、本発明に係る複合シートの第一実施例の構成を示す一部切断拡大断面図である。FIG. 1 is a partially cut-away enlarged sectional view showing the configuration of the first embodiment of the composite sheet according to the present invention. 図2は、本発明に係る複合シートの第二実施例の構成を示す一部切断拡大断面図である。FIG. 2 is a partially cut-away enlarged sectional view showing the configuration of the second embodiment of the composite sheet according to the present invention. 図3は、本発明に係る複合シートの第三実施例の構成を示す一部切断拡大断面図である。FIG. 3 is a partially cut-away enlarged sectional view showing the configuration of the third embodiment of the composite sheet according to the present invention. 図4は、本発明に係る複合シートの第四実施例の構成を示す一部切断拡大断面図である。FIG. 4 is a partially cut-away enlarged sectional view showing the configuration of the fourth embodiment of the composite sheet according to the present invention. 図5は、本発明に係る複合シートの第五実施例の構成を示す一部切断拡大断面図である。FIG. 5 is a partially cut-away enlarged sectional view showing the configuration of the fifth embodiment of the composite sheet according to the present invention. 図6は、本発明に係る複合シートの第六実施例の構成を示す一部切断拡大断面図である。FIG. 6 is a partially cut enlarged sectional view showing the configuration of the sixth embodiment of the composite sheet according to the present invention. 図7は、本発明に係る複合シートの第七実施例の構成を示す一部切断拡大断面図である。FIG. 7 is a partially cut-away enlarged sectional view showing the configuration of the seventh embodiment of the composite sheet according to the present invention. 図8は、本発明に係る複合シートの第八実施例の構成を示す一部切断拡大断面図である。FIG. 8 is a partially cut-away enlarged sectional view showing the configuration of the eighth embodiment of the composite sheet according to the present invention.

Explanation of symbols

10、20、30、40、50、60、70、80：複合シート
12、22、32、42、52、62、72、82：アルミ箔
12a、22a、32a、42a、52a、53a、62a、72a、82a：陽極酸化被膜
14：粘着シート
24、44：両面接着シート
26、66：離型紙
34：合成樹脂シート
54、64、74、84：接着剤層
88：保護シート 10, 20, 30, 40, 50, 60, 70, 80: Composite sheet
12, 22, 32, 42, 52, 62, 72, 82: Aluminum foil
12a, 22a, 32a, 42a, 52a, 53a, 62a, 72a, 82a: Anodized film
14: Adhesive sheet
24, 44: Double-sided adhesive sheet
26, 66: Release paper
34: Synthetic resin sheet
54, 64, 74, 84: Adhesive layer
88: Protection sheet

Claims

A composite sheet comprising an aluminum foil (12) having an anodized film (12a) formed on at least one surface, and an adhesive sheet (14) adhered to the other surface of the aluminum foil (12) ( Ten).

An aluminum foil (22) having an anodized film (22a) formed on at least one surface, a double-sided adhesive sheet (24) adhered to the other surface of the aluminum foil (22), and a release paper ( 26) a composite sheet (20).

Composite sheet (30) comprising an aluminum foil (32) having an anodized film (32a) formed on at least one surface and a synthetic resin sheet (34) laminated on the other surface of the aluminum foil (32) ).

Two aluminum foils (42, 43) each having an anodized film (42a) formed on one surface, and a double-sided adhesive sheet (44) that bonds the other surfaces of the aluminum foils (42, 43) to each other ) Composite sheet (40).

Two aluminum foils (52, 53) each having an anodized film (52a, 53a) formed on one surface, and an adhesive layer for bonding the other surfaces of the aluminum foils (52, 53) to each other A composite sheet (50) consisting of (54).

A composite sheet (60) comprising an aluminum foil (62) having an anodized film (62a) formed on one surface thereof, an adhesive layer (64) provided on the back surface thereof, and a release paper (66).

A composite sheet (70) comprising an aluminum foil (72) having an anodized film (72a) formed on one surface thereof and an adhesive layer (74) provided on the back surface thereof.

An aluminum foil (82) having an anodized film (82a) formed on one surface, an adhesive layer (84) having a number of slits (84a) laminated on the anodized film (82a), and an adhesive A composite sheet (80) comprising a release paper (86) laminated on the agent layer (84) and a protective sheet (88) adhered to the other surface of the aluminum foil (82).

Anodized film (12a, 22a, 32a, 33a, 42a, 43a, 52a, 53a, 62a, 72a, aluminum foil (12, 22, 32, 33, 42, 43, 52, 53, 62, 72, 82), The composite sheet according to any one of claims 1 to 8, wherein 82a) includes at least one metal selected from the group consisting of gold, silver, iron, copper, tungsten, tin, cobalt, titanium, and germanium. (10, 20, 30, 40, 50, 60, 70, 80).

The composite sheet (10, 20, 30, 40, 50, 60, 70, 80) according to any one of claims 1 to 8, which has flexibility.

The composite sheet (10, 20, 30, 40, 50, 60, 70) according to any one of claims 1 to 8, which has rigidity.