JP2008145692A - Adhesive for polarizing plate, polarizing plate, method for manufacturing the same, optical film and image display device - Google Patents

Adhesive for polarizing plate, polarizing plate, method for manufacturing the same, optical film and image display device Download PDF

Info

Publication number
JP2008145692A
JP2008145692A JP2006332171A JP2006332171A JP2008145692A JP 2008145692 A JP2008145692 A JP 2008145692A JP 2006332171 A JP2006332171 A JP 2006332171A JP 2006332171 A JP2006332171 A JP 2006332171A JP 2008145692 A JP2008145692 A JP 2008145692A
Authority
JP
Japan
Prior art keywords
polarizing plate
adhesive
film
polyvinyl alcohol
layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2006332171A
Other languages
Japanese (ja)
Other versions
JP4594290B2 (en
Inventor
Shigeki Kawabe
茂樹 河邊
Tetsuro Ikeda
哲朗 池田
Goukiyo Yoshida
剛教 吉田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nitto Denko Corp
Original Assignee
Nitto Denko Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nitto Denko Corp filed Critical Nitto Denko Corp
Priority to JP2006332171A priority Critical patent/JP4594290B2/en
Publication of JP2008145692A publication Critical patent/JP2008145692A/en
Application granted granted Critical
Publication of JP4594290B2 publication Critical patent/JP4594290B2/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

<P>PROBLEM TO BE SOLVED: To provide an adhesive for polarizing plates capable of suppressing the occurrence of knick (irregularity). <P>SOLUTION: The adhesive for polarizing plates used for providing a transparent protective film to at least one surface of a polarizer is a resin solution containing a polyvinyl alcohol resin, a crosslinking agent and a silica colloid having an average particle diameter of 1-100 nm, wherein the silica colloid is blended in a ratio of ≤200 pts.wt. based on 100 pts.wt. of the polyvinyl alcohol resin. <P>COPYRIGHT: (C)2008,JPO&INPIT

Description

本発明は、偏光板用接着剤に関する。また本発明は当該偏光板用接着剤を用いた偏光板およびその製造方法に関する。当該偏光板はこれ単独で、またはこれを積層した光学フィルムとして液晶表示装置、有機EL表示装置、PDP等の画像表示装置を形成しうる。   The present invention relates to an adhesive for polarizing plates. Moreover, this invention relates to the polarizing plate using the said adhesive agent for polarizing plates, and its manufacturing method. The polarizing plate can form an image display device such as a liquid crystal display device, an organic EL display device, or a PDP alone or as an optical film obtained by laminating the polarizing plate.

液晶表示装置には、その画像形成方式から液晶パネル表面を形成するガラス基板の両側に偏光子を配置することが必要不可欠である。偏光子は、一般的には、ポリビニルアルコール系フィルムとヨウ素などの二色性材料で染色を行った後、架橋剤を用いて架橋を行い、一軸延伸することにより製膜することにより得られる。前記偏光子は延伸により作成されるため、収縮し易い。またポリビニルアルコール系フィルムは親水性ポリマーを使用していることから、特に加湿条件下においては非常に変形し易い。またフィルム自体の機械的強度が弱いため、フィルムが裂けたりする問題がある。そのため、偏光子の両側または片側にトリアセチルセルロースなどの透明保護フィルムを貼り合わせて、強度を補った偏光板が用いられている。前記偏光板は、偏光子と透明保護フィルムを接着剤により貼り合わせることにより製造されている。   In a liquid crystal display device, it is indispensable to dispose polarizers on both sides of a glass substrate on which a liquid crystal panel surface is formed because of its image forming method. In general, a polarizer is obtained by dyeing with a polyvinyl alcohol film and a dichroic material such as iodine, followed by crosslinking using a crosslinking agent, and forming a film by uniaxial stretching. Since the polarizer is made by stretching, it easily contracts. In addition, since the polyvinyl alcohol film uses a hydrophilic polymer, it is very easily deformed particularly under humidified conditions. Moreover, since the mechanical strength of the film itself is weak, there is a problem that the film is torn. Therefore, a polarizing plate is used in which a transparent protective film such as triacetyl cellulose is bonded to both sides or one side of the polarizer to supplement the strength. The polarizing plate is manufactured by bonding a polarizer and a transparent protective film with an adhesive.

近年の液晶表示装置は用途が拡大し、携帯端末から家庭用の大型TVまで幅広く展開が進んできており、各用途に応じて、それぞれの規格が設けられるようになってきている。特に携帯端末用途では、使用者が持ち歩くことが前提であるため、耐久性に対する要求は非常に厳しい。例えば、偏光板には、結露が生じるような加湿条件下においても特性、形状が変化しない耐水性が求められている。   In recent years, the use of liquid crystal display devices has been expanded, and a wide range of development has been progressing from portable terminals to large-sized TVs for home use, and respective standards have been provided according to each application. Particularly in portable terminal applications, since it is assumed that the user carries around, the demand for durability is very strict. For example, a polarizing plate is required to have water resistance that does not change its characteristics and shape even under humidified conditions that cause condensation.

前記の通り偏光子は、透明保護フィルムにより強度を補強した偏光板として使用される。前記偏光子と透明保護フィルムの接着に用いる偏光板用接着剤としては、水系接着剤が好ましく、例えば、ポリビニルアルコール水溶液に架橋剤を混合したポリビニルアルコール系接着剤が使用されている。しかし、ポリビニルアルコール系接着剤は、加湿条件下では、偏光子と透明保護フィルムとの界面で剥がれが生じる場合がある。これは、前記接着剤の主成分であるポリビニルアルコール系樹脂が水溶性高分子であり、結露した状況下では接着剤の溶解が起こっている可能性が考えられる。上記問題に対して、アセトアセチル基を含有するポリビニルアルコール系樹脂と架橋剤を含有する偏光板用接着剤が提案されている(特許文献1)。   As described above, the polarizer is used as a polarizing plate whose strength is reinforced by a transparent protective film. As an adhesive for polarizing plates used for adhesion | attachment of the said polarizer and a transparent protective film, a water-system adhesive agent is preferable, for example, the polyvinyl alcohol-type adhesive agent which mixed the crosslinking agent in the polyvinyl alcohol aqueous solution is used. However, the polyvinyl alcohol-based adhesive may peel off at the interface between the polarizer and the transparent protective film under humidified conditions. This may be because the polyvinyl alcohol resin, which is the main component of the adhesive, is a water-soluble polymer, and the adhesive may be dissolved under the dew condensation condition. In order to solve the above problem, a polarizing plate adhesive containing a polyvinyl alcohol-based resin containing an acetoacetyl group and a crosslinking agent has been proposed (Patent Document 1).

一方、偏光板を作成するにあたって、偏光子と透明保護フィルムを、上記のポリビニルアルコール系接着剤を介して貼り合わせる際には、数μmピッチのスジ上の外観欠陥(レコードスジ欠陥)が偏光板全面又は一部に発生する問題がある。
特開平7−198945号公報
On the other hand, when a polarizer and a transparent protective film are bonded to each other via the polyvinyl alcohol-based adhesive in producing a polarizing plate, an appearance defect (record streak defect) on a stripe having a pitch of several μm is a polarizing plate. There is a problem that occurs on the entire surface or part of it.
JP-A-7-198945

本発明は、レコードスジ欠陥を抑えることができる偏光板用接着剤を提供することを目的とする。   An object of this invention is to provide the adhesive agent for polarizing plates which can suppress a record stripe defect.

また本発明は当該偏光板用接着剤を用いた偏光板およびその製造方法を提供することを目的とする。さらに本発明は、当該偏光板を積層した光学フィルムを提供すること、さらには、当該偏光板、光学フィルムを用いた液晶表示装置等の画像表示装置を提供することを目的とする。   Moreover, an object of this invention is to provide the polarizing plate using the said adhesive agent for polarizing plates, and its manufacturing method. Furthermore, an object of the present invention is to provide an optical film in which the polarizing plate is laminated, and to provide an image display device such as a liquid crystal display device using the polarizing plate and the optical film.

本発明者らは前記課題を解決すべく鋭意検討を重ねた結果、以下に示す偏光板用接着剤により前記目的に達成できることを見出し、本発明を完成するに至った。   As a result of intensive studies to solve the above problems, the present inventors have found that the object can be achieved by the following polarizing plate adhesive, and have completed the present invention.

すなわち本発明は、偏光子の少なくとも片面に透明保護フィルムを設けるために用いる偏光板用接着剤であって、
前記偏光板用接着剤は、ポリビニルアルコール系樹脂、架橋剤および平均粒子径が1〜100nmのシリカコロイドを含有してなる樹脂溶液であり、かつ、
シリカコロイドは、ポリビニルアルコール系樹脂100重量部に対して、200重量部以下の割合で配合されていることを特徴とする偏光板用接着剤、に関する。
That is, the present invention is an adhesive for polarizing plates used for providing a transparent protective film on at least one side of a polarizer,
The polarizing plate adhesive is a resin solution comprising a polyvinyl alcohol-based resin, a crosslinking agent, and a silica colloid having an average particle diameter of 1 to 100 nm, and
The silica colloid relates to an adhesive for polarizing plates, characterized in that it is blended at a ratio of 200 parts by weight or less with respect to 100 parts by weight of the polyvinyl alcohol resin.

本発明の偏光板用接着剤は、ポリビニルアルコール系樹脂、架橋剤に加えて、平均粒子径が1〜100nmのシリカコロイドを含有しており、かかるシリカコロイドの作用によって、レコードスジの発生が抑えられる。これにより、偏光板を作成する際の歩留まりを向上することができ、偏光板の生産性が向上する。   The polarizing plate adhesive of the present invention contains a silica colloid having an average particle diameter of 1 to 100 nm in addition to the polyvinyl alcohol resin and the crosslinking agent, and the action of the silica colloid suppresses the occurrence of record stripes. It is done. Thereby, the yield at the time of producing a polarizing plate can be improved, and the productivity of a polarizing plate improves.

また、偏光板を作成するにあたっては、レコードスジ欠陥の他に、局所的には凹凸欠陥(クニック欠陥)が発生する問題があるが、前記シリカコロイドを配合した接着剤を用いることにより、クニックの発生も抑えることができる。   Moreover, in producing a polarizing plate, in addition to the record streak defect, there is a problem that unevenness defects (knic defects) are locally generated. By using an adhesive containing the silica colloid, knick Occurrence can also be suppressed.

前記偏光板用接着剤に用いる架橋剤としては、メチロール基を有する化合物を含有することが好適である。   The crosslinking agent used for the polarizing plate adhesive preferably contains a compound having a methylol group.

前記偏光板用接着剤に用いる架橋剤の配合量は、ポリビニルアルコール系樹脂100重量部に対して、10〜60重量部であることが好適である。   The amount of the crosslinking agent used in the polarizing plate adhesive is preferably 10 to 60 parts by weight with respect to 100 parts by weight of the polyvinyl alcohol resin.

また本発明は、偏光子の少なくとも一方の面に、接着剤層を介して透明保護フィルムが設けられている偏光板において、前記接着剤層が前記偏光板用接着剤により形成されていることを特徴とする偏光板、に関する。かかる本発明の偏光板において、接着剤層中には、シリカコロイドが含まれており、偏光子と透明保護フィルムの貼り合せの際に生じるレコードスジ欠陥が抑えられている。さらには、接着剤層の厚みを上げることでクニック欠陥は減少する傾向にあるが、接着剤層の厚みがあがることで、レコードスジの発生を誘導して、工程の歩留まりを悪化させるおそれがある。本発明では、接着剤層中に、シリカコロイドが含有させることで、接着剤層の厚みは100nm以下に薄くした場合にも、クニックの発生を抑えることができる。   In the polarizing plate in which a transparent protective film is provided on at least one surface of the polarizer via an adhesive layer, the adhesive layer is formed of the polarizing plate adhesive. The present invention relates to a polarizing plate. In the polarizing plate of the present invention, the adhesive layer contains a silica colloid, and record streak defects generated when the polarizer and the transparent protective film are bonded to each other are suppressed. Furthermore, increasing the thickness of the adhesive layer tends to reduce nick defects, but increasing the thickness of the adhesive layer may lead to the occurrence of record streaks and worsen the process yield. . In the present invention, when silica colloid is contained in the adhesive layer, the occurrence of nicks can be suppressed even when the thickness of the adhesive layer is reduced to 100 nm or less.

前記偏光板において、接着剤層の厚みが、10〜300nmであり、かつ、接着剤層の厚みは、偏光板用接着剤に含有されているシリカコロイドの平均粒子径よりも大きいことが好ましい。接着剤層の厚みを、前記範囲とすることで、接着剤層中に、略均一にシリカコロイドを分散させることができる。また、接着剤層の厚みを、シリカコロイドの平均粒子径よりも大きくすることで、接着剤層の厚み凹凸を抑えて、良好な接着性の接着剤層を形成できる。   In the polarizing plate, the thickness of the adhesive layer is preferably 10 to 300 nm, and the thickness of the adhesive layer is preferably larger than the average particle diameter of the silica colloid contained in the polarizing plate adhesive. By setting the thickness of the adhesive layer within the above range, the silica colloid can be dispersed substantially uniformly in the adhesive layer. Moreover, by making the thickness of the adhesive layer larger than the average particle diameter of the silica colloid, it is possible to suppress the thickness unevenness of the adhesive layer and form an adhesive layer with good adhesiveness.

また本発明は、偏光子の少なくとも一方の面に、接着剤層を介して透明保護フィルムが設けられている前記偏光板を製造する方法であって、
前記偏光板用接着剤を調製する工程、偏光子の前記接着剤層を形成する面および/または透明保護フィルムの前記接着剤層を形成する面に前記偏光板用接着剤を塗布する工程、偏光子と透明保護フィルムとを貼り合わせる工程を有することを特徴とする偏光板の製造方法、に関する。
Further, the present invention is a method for producing the polarizing plate, wherein a transparent protective film is provided on at least one surface of a polarizer via an adhesive layer,
The step of preparing the polarizing plate adhesive, the step of applying the polarizing plate adhesive to the surface of the polarizer forming the adhesive layer and / or the surface of the transparent protective film forming the adhesive layer, polarizing The present invention relates to a method for producing a polarizing plate, comprising a step of bonding a child and a transparent protective film.

また本発明は、前記偏光板が、少なくとも1枚積層されていることを特徴とする光学フィルム、に関する。   The present invention also relates to an optical film in which at least one polarizing plate is laminated.

さらに本発明は、前記偏光板または前記光学フィルムが用いられていることを特徴とする画像表示装置、に関する。   Furthermore, this invention relates to the image display apparatus characterized by using the said polarizing plate or the said optical film.

本発明の偏光板用接着剤は、ポリビニルアルコール系樹脂、架橋剤および平均粒子径が1〜100nmのシリカコロイドを含有してなる樹脂溶液である。   The polarizing plate adhesive of the present invention is a resin solution comprising a polyvinyl alcohol resin, a crosslinking agent, and a silica colloid having an average particle size of 1 to 100 nm.

ポリビニルアルコール系樹脂としては、ポリビニルアルコール樹脂や、アセトアセチル基を有するポリビニルアルコール樹脂があげられる。アセトアセチル基を有するポリビニルアルコール樹脂は、反応性の高い官能基を有するポリビニルアルコール系接着剤であり、偏光板の耐久性を向上させる点において好ましい。   Examples of the polyvinyl alcohol resin include polyvinyl alcohol resins and polyvinyl alcohol resins having an acetoacetyl group. A polyvinyl alcohol resin having an acetoacetyl group is a polyvinyl alcohol-based adhesive having a highly reactive functional group, and is preferable in terms of improving the durability of the polarizing plate.

アセトアセチル基を含有するポリビニルアルコール系樹脂を用いた接着剤は、耐水性に優れる接着剤層を形成することができる。一方、アセトアセチル基を含有するポリビニルアルコール系樹脂を用いた偏光板用接着剤では、クニックの発生が多く観察されたが、本発明の偏光板用接着剤では、前記シリカコロイドを配合することにより、アセトアセチル基を含有するポリビニルアルコール系樹脂を用いた偏光板用接着剤における、クニックの発生を抑えることができる。これにより、耐水性を有し、かつレコードスジ、クニックの発生を抑えることができる偏光板用接着剤が得られる。   An adhesive using a polyvinyl alcohol-based resin containing an acetoacetyl group can form an adhesive layer having excellent water resistance. On the other hand, in the adhesive for polarizing plates using a polyvinyl alcohol-based resin containing an acetoacetyl group, many occurrences of nicks were observed. In the adhesive for polarizing plates of the present invention, the silica colloid was blended. In the adhesive for polarizing plates using a polyvinyl alcohol resin containing an acetoacetyl group, the occurrence of nicks can be suppressed. Thereby, the adhesive agent for polarizing plates which has water resistance and can suppress generation | occurrence | production of a record stripe and a nick is obtained.

ポリビニルアルコール系樹脂は、ポリ酢酸ビニルをケン化して得られたポリビニルアルコール;その誘導体;更に酢酸ビニルと共重合性を有する単量体との共重合体のケン化物;ポリビニルアルコールをアセタール化、ウレタン化、エーテル化、グラフト化、リン酸エステル化等した変性ポリビニルアルコールがあげられる。前記単量体としては、(無水)マレイン酸、フマール酸、クロトン酸、イタコン酸、(メタ)アクリル酸等の不飽和カルボン酸及びそのエステル類;エチレン、プロピレン等のα−オレフィン、(メタ)アリルスルホン酸(ソーダ)、スルホン酸ソーダ(モノアルキルマレート)、ジスルホン酸ソーダアルキルマレート、N−メチロールアクリルアミド、アクリルアミドアルキルスルホン酸アルカリ塩、N−ビニルピロリドン、N−ビニルピロリドン誘導体等があげられる。これらポリビニルアルコール系樹脂は一種を単独でまたは二種以上を併用することができる。   Polyvinyl alcohol resin is polyvinyl alcohol obtained by saponifying polyvinyl acetate; a derivative thereof; a saponified product of a copolymer of vinyl acetate and a monomer having copolymerizability; Examples thereof include modified polyvinyl alcohols that have been converted into ethers, ethers, grafts, or phosphoric esters. Examples of the monomer include unsaturated carboxylic acids such as (anhydrous) maleic acid, fumaric acid, crotonic acid, itaconic acid, (meth) acrylic acid, and esters thereof; α-olefins such as ethylene and propylene, (meth) Examples include allyl sulfonic acid (soda), sulfonic acid soda (monoalkyl malate), disulfonic acid soda alkyl maleate, N-methylol acrylamide, acrylamide alkyl sulfonic acid alkali salt, N-vinyl pyrrolidone, N-vinyl pyrrolidone derivatives and the like. . These polyvinyl alcohol resins can be used singly or in combination of two or more.

前記ポリビニルアルコール系樹脂は特に限定されないが、接着性の点からは、平均重合度100〜5000程度、好ましくは1000〜4000、平均ケン化度85〜100モル%程度、好ましくは90〜100モル%である。   The polyvinyl alcohol-based resin is not particularly limited, but from the viewpoint of adhesiveness, the average degree of polymerization is about 100 to 5000, preferably 1000 to 4000, the average saponification degree is about 85 to 100 mol%, preferably 90 to 100 mol%. It is.

アセトアセチル基を含有するポリビニルアルコール系樹脂は、ポリビニルアルコール系樹脂とジケテンとを公知の方法で反応して得られる。例えば、ポリビニルアルコール系樹脂を酢酸等の溶媒中に分散させておき、これにジケテンを添加する方法、ポリビニルアルコール系樹脂をジメチルホルムアミドまたはジオキサン等の溶媒にあらかじめ溶解しておき、これにジケテンを添加する方法等があげられる。またポリビニルアルコールにジケテンガスまたは液状ジケテンを直接接触させる方法があげられる。   A polyvinyl alcohol-based resin containing an acetoacetyl group is obtained by reacting a polyvinyl alcohol-based resin with diketene by a known method. For example, a method in which a polyvinyl alcohol resin is dispersed in a solvent such as acetic acid and diketene is added thereto, and a polyvinyl alcohol resin is previously dissolved in a solvent such as dimethylformamide or dioxane, and diketene is added thereto. And the like. Another example is a method in which diketene gas or liquid diketene is brought into direct contact with polyvinyl alcohol.

アセトアセチル基を含有するポリビニルアルコール系樹脂のアセトアセチル基変性度は、0.1モル%以上であれば特に制限はなない。0.1モル%未満では接着剤層の耐水性が不充分であり不適当である。アセトアセチル基変性度は、好ましくは0.1〜40モル%程度、さらに好ましくは1〜20モル%、特に好ましくは2〜7モル%である。アセトアセチル基変性度が40モル%を超えると、耐水性の向上効果が小さい。アセトアセチル基変性度はNMRにより測定した値である。   The degree of acetoacetyl group modification of the polyvinyl alcohol-based resin containing an acetoacetyl group is not particularly limited as long as it is 0.1 mol% or more. If it is less than 0.1 mol%, the water resistance of the adhesive layer is insufficient and unsuitable. The degree of acetoacetyl group modification is preferably about 0.1 to 40 mol%, more preferably 1 to 20 mol%, and particularly preferably 2 to 7 mol%. When the acetoacetyl group modification degree exceeds 40 mol%, the effect of improving water resistance is small. The degree of acetoacetyl modification is a value measured by NMR.

架橋剤としては、ポリビニルアルコール系接着剤に用いられているものを特に制限なく使用できる。前記ポリビニルアルコール系樹脂と反応性を有する官能基を少なくとも2つ有する化合物を使用できる。例えば、エチレンジアミン、トリエチレンジアミン、ヘキサメチレンジアミン等のアルキレン基とアミノ基を2個有するアルキレンジアミン類;トリレンジイソシアネート、水素化トリレンジイソシアネート、トリメチロールプロパントリレンジイソシアネートアダクト、トリフェニルメタントリイソシアネート、メチレンビス(4−フェニルメタントリイソシアネート、イソホロンジイソシアネートおよびこれらのケトオキシムブロック物またはフェノールブロック物等のイソシアネート類;エチレングリコールジグリシジルエーテル、ポリエチレングリコールジグリシジルエーテル、グリセリンジまたはトリグリシジルエーテル、1,6−ヘキサンジオールジグリシジルエーテル、トリメチロールプロパントリグリシジルエーテル、ジグリシジルアニリン、ジグリシジルアミン等のエポキシ類;ホルムアルデヒド、アセトアルデヒド、プロピオンアルデヒド、ブチルアルデヒド等のモノアルデヒド類;グリオキザール、マロンジアルデヒド、スクシンジアルデヒド、グルタルジアルデヒド、マレインジアルデヒド、フタルジアルデヒド等のジアルデヒド類;メチロール尿素、メチロールメラミン、アルキル化メチロール尿素、アルキル化メチロール化メラミン、アセトグアナミン、ベンゾグアナミンとホルムアルデヒドとの縮合物等のアミノ−ホルムアルデヒド樹脂、;更にナトリウム、カリウム、マグネシウム、カルシウム、アルミニウム、鉄、ニッケル等の二価金属、又は三価金属の塩及びその酸化物があげられる。これらのなかでもアミノ−ホルムアルデヒド樹脂やジアルデヒド類が好ましい。アミノ−ホルムアルデヒド樹脂としてはメチロール基を有する化合物が好ましく、ジアルデヒド類としてはグリオキザールが好適である。なかでもメチロール基を有する化合物である、メチロールメラミンが特に好適である。   As a crosslinking agent, what is used for the polyvinyl alcohol-type adhesive agent can be especially used without a restriction | limiting. A compound having at least two functional groups having reactivity with the polyvinyl alcohol resin can be used. For example, alkylene diamines having two alkylene groups and two amino groups such as ethylene diamine, triethylene diamine and hexamethylene diamine; tolylene diisocyanate, hydrogenated tolylene diisocyanate, trimethylolpropane tolylene diisocyanate adduct, triphenylmethane triisocyanate, methylene bis (Isocyanates such as 4-phenylmethane triisocyanate, isophorone diisocyanate and ketoxime block product or phenol block product thereof; ethylene glycol diglycidyl ether, polyethylene glycol diglycidyl ether, glycerin di or triglycidyl ether, 1,6-hexane Diol diglycidyl ether, trimethylolpropane triglycidyl ether, jig Epoxys such as sidylaniline and diglycidylamine; monoaldehydes such as formaldehyde, acetaldehyde, propionaldehyde, and butyraldehyde; Aldehydes: amino-formaldehyde resins such as methylol urea, methylol melamine, alkylated methylol urea, alkylated methylolated melamine, acetoguanamine, condensate of benzoguanamine and formaldehyde; further sodium, potassium, magnesium, calcium, aluminum, iron And salts of divalent metals such as nickel or trivalent metals and oxides thereof, among which amino-formaldehyde resins and dia Dehydro are preferred amino -.. Is preferably a compound having a methylol group as a formaldehyde resin, the dialdehydes are preferred glyoxal is inter alia a compound having a methylol group, methylol melamine is particularly preferred.

前記架橋剤の配合量は、ポリビニルアルコール系樹脂の種類等に応じて適宜設計できるが、ポリビニルアルコール系樹脂100重量部に対して、通常、10〜60重量部程度、好ましくは20〜50重量部である。かかる範囲において、良好な接着性が得られる。   The blending amount of the crosslinking agent can be appropriately designed according to the type of the polyvinyl alcohol resin, etc., but is usually about 10 to 60 parts by weight, preferably 20 to 50 parts by weight with respect to 100 parts by weight of the polyvinyl alcohol resin. It is. In such a range, good adhesiveness can be obtained.

耐久性を向上させるには、アセトアセチル基を含有するポリビニルアルコール系樹脂を用いる。この場合にも、ポリビニルアルコール系樹脂100重量部に対して、架橋剤を10〜60重量部、さらには20〜50重量部の範囲で用いるのが好ましい。架橋剤の配合量が多くなりすぎると、架橋剤の反応が短時間で進行し、接着剤がゲル化する傾向がある。その結果、接着剤としての可使時間(ポットライフ)が極端に短くなり、工業的な使用が困難になる。かかる観点からは、架橋剤の配合量は、上記配合量で用いられるが、本発明の樹脂溶液は、シリカコロイドを含有しているため、前記のように架橋剤の配合量が多い場合であっても、安定性よく用いることができる。   In order to improve the durability, a polyvinyl alcohol resin containing an acetoacetyl group is used. Also in this case, it is preferable to use the crosslinking agent in the range of 10 to 60 parts by weight, and further 20 to 50 parts by weight with respect to 100 parts by weight of the polyvinyl alcohol resin. When the amount of the crosslinking agent is too large, the reaction of the crosslinking agent proceeds in a short time and the adhesive tends to gel. As a result, the pot life as an adhesive is extremely shortened, making industrial use difficult. From such a viewpoint, the blending amount of the crosslinking agent is used in the above blending amount. However, since the resin solution of the present invention contains silica colloid, the blending amount of the crosslinking agent is large as described above. However, it can be used with good stability.

シリカコロイドは、微粒子が分散媒中に分散しているものであり、微粒子の同種電荷の相互反発に起因して静電的安定化し、永続的に安定性を有するものである。シリカコロイド(微粒子)の平均粒子径は1〜100nmである。前記シリカコロイドの平均粒子径が前記範囲であれば、接着剤層中において、シリカコロイドを略均一に分散させることができ、接着性を確保し、かつレコードスジの発生を抑えることができる。さらには、クニックの発生を抑える上でも好ましい。前記平均粒子径の範囲は、可視光線の波長領域よりもかなり小さく、形成される接着剤層中において、金属化合物によって透過光が散乱したとしても、偏光特性には悪影響を及ぼさない。シリカコロイドの平均粒子径は、1〜100nm、さらには1〜50nmであるのが好ましい。   The silica colloid is one in which fine particles are dispersed in a dispersion medium, and is electrostatically stabilized due to mutual repulsion of the same kind of fine particles and has permanent stability. The average particle diameter of the silica colloid (fine particles) is 1 to 100 nm. When the average particle diameter of the silica colloid is within the above range, the silica colloid can be dispersed substantially uniformly in the adhesive layer, the adhesiveness can be ensured, and the occurrence of record lines can be suppressed. Furthermore, it is also preferable for suppressing the occurrence of nicks. The range of the average particle diameter is considerably smaller than the wavelength range of visible light, and even if the transmitted light is scattered by the metal compound in the formed adhesive layer, the polarization characteristics are not adversely affected. The average particle size of the silica colloid is preferably 1 to 100 nm, more preferably 1 to 50 nm.

シリカコロイドとしては、各種のものを用いることができる。シリカコロイドは、分散媒に分散してコロイド溶液の状態で存在している。分散媒は、主として水である。水の他に、アルコール類等の他の分散媒を用いることもできる。シリカコロイド溶液中の固形分濃度は、特に制限されないが、通常、1〜50重量%程度、さらには、1〜30重量%のものが一般的である。また、シリカコロイドは、安定剤として硝酸、塩酸、酢酸などの酸を含有するものを用いることができる。   Various types of silica colloids can be used. The silica colloid is present in the state of a colloid solution dispersed in a dispersion medium. The dispersion medium is mainly water. In addition to water, other dispersion media such as alcohols can also be used. The solid content concentration in the silica colloid solution is not particularly limited, but is generally about 1 to 50% by weight, more preferably 1 to 30% by weight. Moreover, the silica colloid can use what contains acids, such as nitric acid, hydrochloric acid, and an acetic acid, as a stabilizer.

シリカコロイドは、ポリビニルアルコール系樹脂100重量部に対して、200重量部以下の割合(固形分の換算値)で配合される。またシリカコロイドの配合割合を前記範囲とすることで、偏光子と透明保護フィルムとの接着性を確保しながら、レコードスジの発生を抑えることができる。また、クニックの発生を抑えるうえで好ましい。シリカコロイドの配合割合は、5〜200重量部であるのが好ましく、さらには10〜175重量部、さらには20〜150重量部、さらには30〜125重量部であるのが好ましい。シリカコロイドの配合割合が、ポリビニルアルコール系樹脂100重量部に対して、200重量部を超えると、接着剤中における、ポリビニルアルコール系樹脂の割合が小さくなり、接着性の点から好ましくない。なお、シリカコロイドの配合割合は、特に制限されないが、有効にレコードスジ、クニックを抑えるには、前記範囲の下限値とするのが好ましい。   The silica colloid is blended at a ratio of 200 parts by weight or less (converted value of solid content) with respect to 100 parts by weight of the polyvinyl alcohol resin. Moreover, generation | occurrence | production of a record stripe can be suppressed, ensuring the adhesiveness of a polarizer and a transparent protective film by making the mixture ratio of a silica colloid into the said range. Moreover, it is preferable for suppressing the occurrence of nicks. The blending ratio of the silica colloid is preferably 5 to 200 parts by weight, more preferably 10 to 175 parts by weight, further 20 to 150 parts by weight, and further preferably 30 to 125 parts by weight. When the blending ratio of the silica colloid exceeds 200 parts by weight with respect to 100 parts by weight of the polyvinyl alcohol resin, the ratio of the polyvinyl alcohol resin in the adhesive is reduced, which is not preferable from the viewpoint of adhesiveness. The mixing ratio of the silica colloid is not particularly limited, but is preferably set to the lower limit of the above range in order to effectively suppress the record lines and nicks.

本発明の偏光板用接着剤は、ポリビニルアルコール系樹脂、架橋剤および平均粒子径が1〜100nmのシリカコロイドを含有してなる樹脂溶液であり、通常、水溶液として用いられる。樹脂溶液濃度は特に制限はないが、塗工性や放置安定性等を考慮すれば、0.1〜15重量%、好ましくは0.5〜10重量%である。   The polarizing plate adhesive of the present invention is a resin solution containing a polyvinyl alcohol resin, a crosslinking agent, and a silica colloid having an average particle size of 1 to 100 nm, and is usually used as an aqueous solution. The concentration of the resin solution is not particularly limited, but is 0.1 to 15% by weight, preferably 0.5 to 10% by weight in consideration of coating properties and storage stability.

偏光板用接着剤である樹脂溶液の粘度が、粘度は特に制限されないが、1〜50mPa・sの範囲のものが用いられる。偏光板の作成にあたって生じるクニックは、樹脂溶液の粘度が下がるに従って、クニックの発生も多くなる傾向があるが、本発明の偏光板用接着剤によれば、1〜20mPa・sの範囲のような低粘度の範囲においても、クニックの発生を抑えることができ、樹脂溶液の粘度に拘らず、クニックの発生を抑えることができる。アセトアセチル基を含有するポリビニルアルコール系樹脂は、一般的なポリビニルアルコール樹脂に比べて、重合度を高くすることができず、前記のような低粘度で用いられていたが、本発明では、アセトアセチル基を含有するポリビニルアルコール系樹脂を用いる場合にも、樹脂溶液の低粘度によって生じるクニックの発生を抑えられる。   The viscosity of the resin solution that is an adhesive for polarizing plates is not particularly limited, but those in the range of 1 to 50 mPa · s are used. The nick generated in the production of the polarizing plate tends to increase as the viscosity of the resin solution decreases. However, according to the polarizing plate adhesive of the present invention, a range of 1 to 20 mPa · s can be obtained. Even in the low viscosity range, the occurrence of nicks can be suppressed, and the occurrence of nicks can be suppressed regardless of the viscosity of the resin solution. A polyvinyl alcohol resin containing an acetoacetyl group cannot be increased in polymerization degree compared to a general polyvinyl alcohol resin and has been used at a low viscosity as described above. Even when a polyvinyl alcohol-based resin containing an acetyl group is used, the occurrence of nicks caused by the low viscosity of the resin solution can be suppressed.

偏光板用接着剤である樹脂溶液の調製法は特に制限されない。通常は、ポリビニルアルコール系樹脂および架橋剤を混合し、適宜に濃度を調製したものに、シリカコロイドを配合することで、樹脂溶液が調製される。また、ポリビニルアルコール系樹脂として、アセトアセチル基を含有するポリビニルアルコール系樹脂を用いたり、架橋剤の配合量が多いような場合には、溶液の安定性を考慮して、ポリビニルアルコール系樹脂とシリカコロイドを混合した後に、架橋剤を、得られる樹脂溶液の使用時期等を考慮しながら、混合することができる。なお、偏光板用接着剤である樹脂溶液の濃度は、樹脂溶液を調製した後に適宜に調整することもできる。   The method for preparing the resin solution that is the polarizing plate adhesive is not particularly limited. Usually, a resin solution is prepared by mixing a silica colloid with a mixture prepared by mixing a polyvinyl alcohol-based resin and a crosslinking agent and appropriately adjusting the concentration. In addition, when a polyvinyl alcohol resin containing an acetoacetyl group is used as the polyvinyl alcohol resin or the amount of the crosslinking agent is large, the polyvinyl alcohol resin and silica are taken into consideration in view of the stability of the solution. After mixing the colloids, the cross-linking agent can be mixed in consideration of the timing of use of the resulting resin solution. In addition, the density | concentration of the resin solution which is an adhesive agent for polarizing plates can also be adjusted suitably after preparing a resin solution.

なお、偏光板用接着剤には、さらにシランカップリング剤、チタンカップリング剤などのカップリング剤、各種粘着付与剤、紫外線吸収剤、酸化防止剤、耐熱安定剤、耐加水分解安定剤などの安定剤等を配合することもできる。また、本願における、シリカコロイドは非導電性の材料であるが、導電性物質の微粒子を含有することもできる。   The polarizing plate adhesive further includes coupling agents such as silane coupling agents and titanium coupling agents, various tackifiers, ultraviolet absorbers, antioxidants, heat stabilizers, and hydrolysis stabilizers. A stabilizer or the like can also be blended. Moreover, although the silica colloid in this application is a nonelectroconductive material, it can also contain the microparticles | fine-particles of an electroconductive substance.

本発明の偏光板は、透明保護フィルムと偏光子を、前記接着剤を用いて貼り合わせることにより製造する。得られた偏光板では、偏光子の片側または両側に、前記偏光板接着剤により形成された接着剤層を介して、透明保護フィルムが設けられている。   The polarizing plate of the present invention is produced by laminating a transparent protective film and a polarizer using the adhesive. In the obtained polarizing plate, a transparent protective film is provided on one or both sides of the polarizer via an adhesive layer formed of the polarizing plate adhesive.

前記接着剤の塗布は、透明保護フィルム、偏光子のいずれに行ってもよく、両者に行ってもよい。前記接着剤の塗布は、乾燥後の接着剤層の厚みが10〜300nm程度になるように行なうのが好ましい。接着剤層の厚みは、均一な面内厚みを得ることと、十分な接着力を得る点から、さらに好ましくは、10〜200nm、さらに好ましくは20〜150nmである。接着剤層の厚みを上げるとクニック欠陥は減少する傾向にあるが、レコードスジの発生を誘導して、工程の歩留まりを悪化させるおそれがある。かかる観点から、接着剤層の厚みは100nm以下とするのが好ましい。また、前述の通り、接着剤層の厚みは、偏光板用接着剤に含有されているシリカコロイドの平均粒子径よりも大きくなるように設計することが好ましい。   Application | coating of the said adhesive agent may be performed to any of a transparent protective film and a polarizer, and may be performed to both. The application of the adhesive is preferably performed so that the thickness of the adhesive layer after drying is about 10 to 300 nm. The thickness of the adhesive layer is more preferably 10 to 200 nm, and still more preferably 20 to 150 nm, from the viewpoint of obtaining a uniform in-plane thickness and obtaining a sufficient adhesive force. Increasing the thickness of the adhesive layer tends to reduce knick defects, but may lead to the occurrence of record streaks and deteriorate the process yield. From this viewpoint, the thickness of the adhesive layer is preferably 100 nm or less. Further, as described above, the thickness of the adhesive layer is preferably designed to be larger than the average particle diameter of the silica colloid contained in the polarizing plate adhesive.

接着剤層の厚みを調整する方法としては、特に制限されるものではないないが、例えば、接着剤溶液の固形分濃度や接着剤の塗布装置を調整する方法があげられる。このような接着剤層厚みの測定方法としては、特に制限されるものではないが、SEM(Scanning Electron Microscopy)や、TEM(Transmission Electron Microscopy)による断面観察測定が好ましく用いられる。接着剤の塗布操作は特に制限されず、ロール法、噴霧法、浸漬法等の各種手段を採用できる。   The method of adjusting the thickness of the adhesive layer is not particularly limited, and examples thereof include a method of adjusting the solid content concentration of the adhesive solution and an adhesive application device. The method for measuring the thickness of the adhesive layer is not particularly limited, but cross-sectional observation measurement using SEM (Scanning Electron Microscopy) or TEM (Transmission Electron Microscopy) is preferably used. The application operation of the adhesive is not particularly limited, and various means such as a roll method, a spray method, and an immersion method can be employed.

接着剤を塗布した後は、偏光子と透明保護フィルムをロールラミネーター等により貼り合わせる。貼り合わせ後には、乾燥工程を施し、塗布乾燥層からなる接着剤層を形成する。乾燥温度は、5〜150℃程度、好ましくは30〜120℃で、120秒間以上、さらには300秒間以上である。   After applying the adhesive, the polarizer and the transparent protective film are bonded together with a roll laminator or the like. After the bonding, a drying process is performed to form an adhesive layer composed of a coating dry layer. A drying temperature is about 5-150 degreeC, Preferably it is 30-120 degreeC, is 120 second or more, Furthermore, it is 300 second or more.

偏光子は、特に制限されず、各種のものを使用できる。偏光子としては、例えば、ポリビニルアルコール系フィルム、部分ホルマール化ポリビニルアルコール系フィルム、エチレン・酢酸ビニル共重合体系部分ケン化フィルム等の親水性高分子フィルムに、ヨウ素や二色性染料等の二色性材料を吸着させて一軸延伸したもの、ポリビニルアルコールの脱水処理物やポリ塩化ビニルの脱塩酸処理物等ポリエン系配向フィルム等があげられる。これらのなかでもポリビニルアルコール系フィルムとヨウ素などの二色性物質からなる偏光子が好適である。これら偏光子の厚さは特に制限されないが、一般的に、5〜80μm程度である。   The polarizer is not particularly limited, and various types can be used. Examples of the polarizer include hydrophilic polymers such as polyvinyl alcohol film, partially formalized polyvinyl alcohol film, and ethylene / vinyl acetate copolymer partially saponified film, and two colors such as iodine and dichroic dye. And polyene-based oriented films such as those obtained by adsorbing a functional material and uniaxially stretched, polyvinyl alcohol dehydrated products, and polyvinyl chloride dehydrochlorinated products. Among these, a polarizer composed of a polyvinyl alcohol film and a dichroic material such as iodine is preferable. The thickness of these polarizers is not particularly limited, but is generally about 5 to 80 μm.

ポリビニルアルコール系フィルムをヨウ素で染色し一軸延伸した偏光子は、例えば、ポリビニルアルコールをヨウ素の水溶液に浸漬することによって染色し、元長の3〜7倍に延伸することで作成することができる。必要に応じてホウ酸やヨウ化カリウムなどの水溶液に浸漬することもできる。さらに必要に応じて染色の前にポリビニルアルコール系フィルムを水に浸漬して水洗してもよい。ポリビニルアルコール系フィルムを水洗することでポリビニルアルコール系フィルム表面の汚れやブロッキング防止剤を洗浄することができるほかに、ポリビニルアルコール系フィルムを膨潤させることで染色のムラなどの不均一を防止する効果もある。延伸はヨウ素で染色した後に行っても良いし、染色しながら延伸してもよし、また延伸してからヨウ素で染色してもよい。ホウ酸やヨウ化カリウムなどの水溶液中や水浴中でも延伸することができる。   A polarizer obtained by dyeing a polyvinyl alcohol film with iodine and uniaxially stretching it can be prepared, for example, by immersing polyvinyl alcohol in an aqueous solution of iodine and stretching it 3 to 7 times the original length. If necessary, it can be immersed in an aqueous solution of boric acid or potassium iodide. Further, if necessary, the polyvinyl alcohol film may be immersed in water and washed before dyeing. In addition to washing the polyvinyl alcohol film surface with dirt and anti-blocking agents by washing the polyvinyl alcohol film with water, it also has the effect of preventing unevenness such as uneven coloring by swelling the polyvinyl alcohol film. is there. Stretching may be performed after dyeing with iodine, may be performed while dyeing, or may be dyed with iodine after stretching. The film can be stretched in an aqueous solution of boric acid or potassium iodide or in a water bath.

透明保護フィルムを形成する、透明ポリマーまたはフィルム材料としては、適宜な透明材料を用いうるが、透明性や機械的強度、熱安定性や水分遮断性などに優れるものが好ましく用いられる。前記透明保護フィルムを形成する材料としては、例えばポリエチレンテレフタレートやポリエチレンナフタレート等のポリエステル系ポリマー、ジアセチルセルロースやトリアセチルセルロース等のセルロース系ポリマー、ポリメチルメタクリレート等のアクリル系ポリマー、ポリスチレンやアクリロニトリル・スチレン共重合体(AS樹脂)等のスチレン系ポリマー、ポリカーボネート系ポリマーなどがあげられる。また、ポリエチレン、ポリプロピレン、シクロ系ないしはノルボルネン構造を有するポリオレフィン、エチレン・プロピレン共重合体の如きポリオレフィン系ポリマー、塩化ビニル系ポリマー、ナイロンや芳香族ポリアミド等のアミド系ポリマー、イミド系ポリマー、スルホン系ポリマー、ポリエーテルスルホン系ポリマー、ポリエーテルエーテルケトン系ポリマー、ポリフェニレンスルフィド系ポリマー、ビニルアルコール系ポリマー、塩化ビニリデン系ポリマー、ビニルブチラール系ポリマー、アリレート系ポリマー、ポリオキシメチレン系ポリマー、エポキシ系ポリマー、あるいは前記ポリマーのブレンド物なども前記透明保護フィルムを形成するポリマーの例としてあげられる。透明保護フィルムは、アクリル系、ウレタン系、アクリルウレタン系、エポキシ系、シリコーン系等の熱硬化型、紫外線硬化型の樹脂の硬化層として形成することもできる。   As the transparent polymer or film material for forming the transparent protective film, an appropriate transparent material can be used, but a material excellent in transparency, mechanical strength, thermal stability, moisture barrier property and the like is preferably used. Examples of the material for forming the transparent protective film include polyester polymers such as polyethylene terephthalate and polyethylene naphthalate, cellulose polymers such as diacetyl cellulose and triacetyl cellulose, acrylic polymers such as polymethyl methacrylate, polystyrene, acrylonitrile and styrene. Examples thereof include styrene polymers such as copolymers (AS resins), polycarbonate polymers, and the like. In addition, polyethylene, polypropylene, polyolefins having a cyclo or norbornene structure, polyolefin polymers such as ethylene / propylene copolymers, vinyl chloride polymers, amide polymers such as nylon and aromatic polyamide, imide polymers, sulfone polymers , Polyether sulfone polymer, polyether ether ketone polymer, polyphenylene sulfide polymer, vinyl alcohol polymer, vinylidene chloride polymer, vinyl butyral polymer, arylate polymer, polyoxymethylene polymer, epoxy polymer, or the above Polymer blends and the like are also examples of polymers that form the transparent protective film. The transparent protective film can also be formed as a cured layer of thermosetting or ultraviolet curable resin such as acrylic, urethane, acrylurethane, epoxy, and silicone.

また、特開2001−343529号公報(WO01/37007)に記載のポリマーフィルム、例えば、(A)側鎖に置換および/または非置換イミド基を有する熱可塑性樹脂と、(B)側鎖に置換および/または非置換フェニルならびにニトリル基を有する熱可塑性樹脂を含有する樹脂組成物があげられる。具体例としてはイソブチレンとN−メチルマレイミドからなる交互共重合体とアクリロニトリル・スチレン共重合体とを含有する樹脂組成物のフィルムがあげられる。フィルムは樹脂組成物の混合押出品などからなるフィルムを用いることができる。これらのフィルムは位相差が小さく、光弾性係数が小さいため偏光板の歪みによるムラなどの不具合を解消することができ、また透湿度が小さいため、加湿耐久性に優れる。   Moreover, the polymer film described in JP-A-2001-343529 (WO01 / 37007), for example, (A) a thermoplastic resin having a substituted and / or unsubstituted imide group in the side chain, and (B) a substitution in the side chain And / or a resin composition containing a thermoplastic resin having unsubstituted phenyl and a nitrile group. A specific example is a film of a resin composition containing an alternating copolymer composed of isobutylene and N-methylmaleimide and an acrylonitrile / styrene copolymer. As the film, a film made of a mixed extruded product of the resin composition or the like can be used. Since these films have a small phase difference and a small photoelastic coefficient, problems such as unevenness due to the distortion of the polarizing plate can be eliminated, and since the moisture permeability is small, the humidification durability is excellent.

透明保護フィルムの厚さは、適宜に決定しうるが、一般には強度や取扱性等の作業性、薄層性などの点より1〜500μm程度である。特に1〜300μmが好ましく、5〜200μmがより好ましい。レコードスジ、クニックは、透明保護フィルムが、薄型化するほど生じやすくなる。したがって、透明保護フィルムが、5〜100μmの場合に特に好適である。   Although the thickness of a transparent protective film can be determined suitably, generally it is about 1-500 micrometers from points, such as workability | operativity, such as intensity | strength and handleability, and thin layer property. 1-300 micrometers is especially preferable, and 5-200 micrometers is more preferable. Records lines and nicks are more likely to occur as the transparent protective film becomes thinner. Therefore, the transparent protective film is particularly suitable when the thickness is 5 to 100 μm.

前記透明保護フィルムは、正面位相差が40nm未満、かつ、厚み方向位相差が80nm未満であるものが、通常、用いられる。正面位相差Reは、Re=(nx−ny)×d、で表わされる。厚み方向位相差Rthは、Rth=(nx−nz)×d、で表される。また、Nz係数は、Nz=(nx−nz)/(nx−ny)、で表される。[ただし、フィルムの遅相軸方向、進相軸方向及び厚さ方向の屈折率をそれぞれnx、ny、nzとし、d(nm)はフィルムの厚みとする。遅相軸方向は、フィルム面内の屈折率の最大となる方向とする。]。なお、透明保護フィルムは、できるだけ色付きがないことが好ましい。厚み方向の位相差値が−90nm〜+75nmである保護フィルムが好ましく用いられる。かかる厚み方向の位相差値(Rth)が−90nm〜+75nmのものを使用することにより、透明保護フィルムに起因する偏光板の着色(光学的な着色)をほぼ解消することができる。厚み方向位相差値(Rth)は、さらに好ましくは−80nm〜+60nm、特に−70nm〜+45nmが好ましい。   As the transparent protective film, one having a front phase difference of less than 40 nm and a thickness direction retardation of less than 80 nm is usually used. The front phase difference Re is represented by Re = (nx−ny) × d. The thickness direction retardation Rth is represented by Rth = (nx−nz) × d. The Nz coefficient is represented by Nz = (nx−nz) / (nx−ny). [However, the refractive indexes in the slow axis direction, the fast axis direction, and the thickness direction of the film are nx, ny, and nz, respectively, and d (nm) is the thickness of the film. The slow axis direction is the direction that maximizes the refractive index in the film plane. ]. In addition, it is preferable that a transparent protective film has as little color as possible. A protective film having a thickness direction retardation value of −90 nm to +75 nm is preferably used. By using a film having a thickness direction retardation value (Rth) of −90 nm to +75 nm, the coloring (optical coloring) of the polarizing plate caused by the transparent protective film can be almost eliminated. The thickness direction retardation value (Rth) is more preferably −80 nm to +60 nm, and particularly preferably −70 nm to +45 nm.

前記観点からは、透明保護フィルムとしては、偏光特性や耐久性などの点より、トリアセチルセルロース等のセルロース系ポリマーが好ましい。特にトリアセチルセルロースフィルムが好適である。一方、透明保護フィルムは、位相差フィルム、光学補償フィルムを兼ねることもできる。この場合には、ノルボルネン系ポリマーが好適に用いられる。なお、偏光子の両側に保護フィルムを設ける場合、その表裏で同じポリマー材料からなる保護フィルムを用いてもよく、異なるポリマー材料等からなる保護フィルムを用いてもよい。   From the above viewpoint, the transparent protective film is preferably a cellulosic polymer such as triacetyl cellulose from the viewpoints of polarization characteristics and durability. A triacetyl cellulose film is particularly preferable. On the other hand, the transparent protective film can also serve as a retardation film and an optical compensation film. In this case, a norbornene polymer is preferably used. In addition, when providing a protective film in the both sides of a polarizer, the protective film which consists of the same polymer material may be used by the front and back, and the protective film which consists of a different polymer material etc. may be used.

一方、前記透明保護フィルムとして、正面位相差が40nm以上および/または、厚み方向位相差が80nm以上の位相差を有する位相差板を用いることができる。正面位相差は、通常、40〜200nmの範囲に、厚み方向位相差は、通常、80〜300nmの範囲に制御される。透明保護フィルムとして位相差板を用いる場合には、当該位相差板が透明保護フィルムとしても機能するため、薄型化を図ることができる。   On the other hand, as the transparent protective film, a phase difference plate having a phase difference with a front phase difference of 40 nm or more and / or a thickness direction retardation of 80 nm or more can be used. The front phase difference is usually controlled in the range of 40 to 200 nm, and the thickness direction phase difference is usually controlled in the range of 80 to 300 nm. When a retardation plate is used as the transparent protective film, the retardation plate functions also as a transparent protective film, so that the thickness can be reduced.

位相差板としては、高分子素材を一軸または二軸延伸処理してなる複屈折性フィルム、液晶ポリマーの配向フィルム、液晶ポリマーの配向層をフィルムにて支持したものなどがあげられる。位相差板の厚さも特に制限されないが、20〜150μm程度が一般的である。   Examples of the retardation plate include a birefringent film obtained by uniaxially or biaxially stretching a polymer material, a liquid crystal polymer alignment film, and a liquid crystal polymer alignment layer supported by a film. The thickness of the retardation plate is not particularly limited, but is generally about 20 to 150 μm.

高分子素材としては、例えば、ポリビニルアルコール、ポリビニルブチラール、ポリメチルビニルエーテル、ポリヒドロキシエチルアクリレート、ヒドロキシエチルセルロース、ヒドロキシプロピルセルロース、メチルセルロース、ポリカーボネート、ポリアリレート、ポリスルホン、ポリエチレンテレフタレート、ポリエチレンナフタレート、ポリエーテルスルホン、ポリフェニレンスルファイド、ポリフェニレンオキサイド、ポリアリルスルホン、ポリアミド、ポリイミド、ポリオレフィン、ポリ塩化ビニル、セルロース系重合体、ノルボルネン系樹脂、またはこれらの二元系、三元系各種共重合体、グラフト共重合体、ブレンド物などがあげられる。これらの高分子素材は延伸等により配向物(延伸フィルム)となる。   Examples of the polymer material include polyvinyl alcohol, polyvinyl butyral, polymethyl vinyl ether, polyhydroxyethyl acrylate, hydroxyethyl cellulose, hydroxypropyl cellulose, methyl cellulose, polycarbonate, polyarylate, polysulfone, polyethylene terephthalate, polyethylene naphthalate, polyether sulfone, Polyphenylene sulfide, polyphenylene oxide, polyallylsulfone, polyamide, polyimide, polyolefin, polyvinyl chloride, cellulose polymer, norbornene resin, or binary, ternary copolymers, graft copolymers, Examples include blends. These polymer materials become an oriented product (stretched film) by stretching or the like.

液晶ポリマーとしては、例えば、液晶配向性を付与する共役性の直線状原子団(メソゲン)がポリマーの主鎖や側鎖に導入された主鎖型や側鎖型の各種のものなどをあげられる。主鎖型の液晶ポリマーの具体例としては、屈曲性を付与するスペーサー部でメソゲン基を結合した構造の、例えばネマチック配向性のポリエステル系液晶性ポリマー、ディスコティックポリマーやコレステリックポリマーなどがあげられる。側鎖型の液晶ポリマーの具体例としては、ポリシロキサン、ポリアクリレート、ポリメタクリレート又はポリマロネートを主鎖骨格とし、側鎖として共役性の原子団からなるスペーサー部を介してネマチック配向付与性のパラ置換環状化合物単位からなるメソゲン部を有するものなどがあげられる。これらの液晶ポリマーは、例えば、ガラス板上に形成したポリイミドやポリビニルアルコール等の薄膜の表面をラビング処理したもの、酸化ケイ素を斜方蒸着したものなどの配向処理面上に液晶性ポリマーの溶液を展開して熱処理することにより行われる。   Examples of the liquid crystal polymer include various main chain types and side chain types in which a conjugated linear atomic group (mesogen) imparting liquid crystal alignment is introduced into the main chain or side chain of the polymer. . Specific examples of the main chain type liquid crystal polymer include a nematic alignment polyester liquid crystal polymer, a discotic polymer, and a cholesteric polymer having a structure in which a mesogen group is bonded at a spacer portion that imparts flexibility. Specific examples of the side chain type liquid crystal polymer include polysiloxane, polyacrylate, polymethacrylate, or polymalonate as a main chain skeleton, and a nematic alignment-providing para-substitution through a spacer portion composed of a conjugated atomic group as a side chain. Examples thereof include those having a mesogenic part composed of a cyclic compound unit. These liquid crystal polymers can be prepared by, for example, applying a solution of a liquid crystalline polymer on an alignment surface such as a surface of a thin film such as polyimide or polyvinyl alcohol formed on a glass plate, or an oblique deposition of silicon oxide. This is done by developing and heat treatment.

位相差板は、例えば各種波長板や液晶層の複屈折による着色や視角等の補償を目的としたものなどの使用目的に応じた適宜な位相差を有するものであって良く、2種以上の位相差板を積層して位相差等の光学特性を制御したものなどであっても良い。   The retardation plate may have an appropriate retardation according to the purpose of use, such as those for the purpose of compensating for various wavelength plates or birefringence of liquid crystal layers and compensation of viewing angle, etc. It may be one in which retardation plates are stacked and optical characteristics such as retardation are controlled.

位相差板は、nx=ny>nz、nx>ny>nz、nx>ny=nz、nx>nz>ny、nz=nx>ny、nz>nx>ny、nz>nx=ny、の関係を満足するものが、各種用途に応じて選択して用いられる。   The retardation plate has a relationship of nx = ny> nz, nx> ny> nz, nx> ny = nz, nx> nz> ny, nz = nx> ny, nz> nx> ny, nz> nx = ny. What is satisfactory is selected and used according to various applications.

例えば、nx>ny>nz、を満足する位相差板では、正面位相差は40〜100nm、厚み方向位相差は100〜320nm、Nz係数は1.8〜4.5を満足するものを用いるのが好ましい。例えば、nx>ny=nz、を満足する位相差板(ポジティブAプレート)では、正面位相差は100〜200nmを満足するものを用いるのが好ましい。例えば、nz=nx>ny、を満足する位相差板(ネガティブAプレート)では、正面位相差は100〜200nmを満足するものを用いるのが好ましい。例えば、nx>nz>ny、を満足する位相差板では、正面位相差は150〜300nm、Nz係数は0超え〜0.7を満足するものを用いるのが好ましい。また、上記の通り、例えば、nx=ny>nz、nz>nx>ny、またはnz>nx=ny、を満足する用いることができる。   For example, in a phase difference plate that satisfies nx> ny> nz, a surface plate having a front phase difference of 40 to 100 nm, a thickness direction phase difference of 100 to 320 nm, and an Nz coefficient of 1.8 to 4.5 is used. Is preferred. For example, in a retardation plate (positive A plate) that satisfies nx> ny = nz, it is preferable to use a retardation plate that satisfies a front phase difference of 100 to 200 nm. For example, for a retardation plate (negative A plate) that satisfies nz = nx> ny, it is preferable to use a retardation plate that satisfies a front phase difference of 100 to 200 nm. For example, in a phase difference plate that satisfies nx> nz> ny, it is preferable to use one that satisfies a front phase difference of 150 to 300 nm and an Nz coefficient of more than 0 to 0.7. Further, as described above, for example, nx = ny> nz, nz> nx> ny, or nz> nx = ny can be used.

透明保護フィルムの偏光子と接着する面には、易接着処理を施すことができる。易接着処理としては、プラズマ処理、コロナ処理等のドライ処理、アルカリ処理(ケン化処理)等の化学処理、易接着剤層を形成するコーティング処理等があげられる。これらのなかでも、易接着剤層を形成するコーティング処理やアルカリ処理が好適である。易接着剤層の形成には、ポリオール樹脂、ポリカルボン酸樹脂、ポリエステル樹脂等の各種の易接着材料を使用することができる。なお、易接着剤層の厚みは、通常、0.001〜10μm程度、さらには0.001〜5μm程度、特に0.001〜1μm程度とするのが好ましい。   The surface of the transparent protective film that adheres to the polarizer can be subjected to an easy adhesion treatment. Examples of the easy adhesion treatment include dry treatment such as plasma treatment and corona treatment, chemical treatment such as alkali treatment (saponification treatment), and coating treatment for forming an easy adhesive layer. Among these, a coating treatment or an alkali treatment for forming an easy-adhesive layer is preferable. For the formation of the easy-adhesive layer, various easy-adhesive materials such as polyol resin, polycarboxylic acid resin, and polyester resin can be used. The thickness of the easy-adhesive layer is usually about 0.001 to 10 μm, more preferably about 0.001 to 5 μm, and particularly preferably about 0.001 to 1 μm.

前記透明保護フィルムの偏光子を接着させない面には、ハードコート層や反射防止処理、スティッキング防止や、拡散ないしアンチグレアを目的とした処理を施したものであってもよい。   The surface of the transparent protective film to which the polarizer is not adhered may be subjected to a hard coat layer, an antireflection treatment, an antisticking treatment, or a treatment for diffusion or antiglare.

ハードコート処理は偏光板表面の傷付き防止などを目的に施されるものであり、例えばアクリル系、シリコーン系などの適宜な紫外線硬化型樹脂による硬度や滑り特性等に優れる硬化皮膜を透明保護フィルムの表面に付加する方式などにて形成することができる。反射防止処理は偏光板表面での外光の反射防止を目的に施されるものであり、従来に準じた反射防止膜などの形成により達成することができる。また、スティッキング防止処理は隣接層との密着防止を目的に施される。   The hard coat treatment is applied for the purpose of preventing scratches on the surface of the polarizing plate. For example, a transparent protective film with a cured film excellent in hardness, sliding properties, etc. by an appropriate ultraviolet curable resin such as acrylic or silicone is used. It can be formed by a method of adding to the surface of the film. The antireflection treatment is performed for the purpose of preventing reflection of external light on the surface of the polarizing plate, and can be achieved by forming an antireflection film or the like according to the conventional art. Further, the anti-sticking treatment is performed for the purpose of preventing adhesion with an adjacent layer.

またアンチグレア処理は偏光板の表面で外光が反射して偏光板透過光の視認を阻害することの防止等を目的に施されるものであり、例えばサンドブラスト方式やエンボス加工方式による粗面化方式や透明微粒子の配合方式などの適宜な方式にて透明保護フィルムの表面に微細凹凸構造を付与することにより形成することができる。前記表面微細凹凸構造の形成に含有させる微粒子としては、例えば平均粒径が0.5〜20μmのシリカ、アルミナ、チタニア、ジルコニア、酸化錫、酸化インジウム、酸化カドミウム、酸化アンチモン等からなる導電性のこともある無機系微粒子、架橋又は未架橋のポリマー等からなる有機系微粒子などの透明微粒子が用いられる。表面微細凹凸構造を形成する場合、微粒子の使用量は、表面微細凹凸構造を形成する透明樹脂100重量部に対して一般的に2〜70重量部程度であり、5〜50重量部が好ましい。アンチグレア層は、偏光板透過光を拡散して視角などを拡大するための拡散層(視角拡大機能など)を兼ねるものであってもよい。   The anti-glare treatment is applied for the purpose of preventing the outside light from being reflected on the surface of the polarizing plate and obstructing the visibility of the light transmitted through the polarizing plate. For example, the surface is roughened by a sandblasting method or an embossing method. It can be formed by imparting a fine concavo-convex structure to the surface of the transparent protective film by an appropriate method such as a blending method of transparent fine particles. Examples of the fine particles to be included in the formation of the surface fine concavo-convex structure include conductive materials made of silica, alumina, titania, zirconia, tin oxide, indium oxide, cadmium oxide, antimony oxide, and the like having an average particle diameter of 0.5 to 20 μm. In some cases, transparent fine particles such as inorganic fine particles, organic fine particles composed of a crosslinked or uncrosslinked polymer, and the like are used. When forming the surface fine uneven structure, the amount of fine particles used is generally about 2 to 70 parts by weight, preferably 5 to 50 parts by weight, based on 100 parts by weight of the transparent resin forming the surface fine uneven structure. The antiglare layer may also serve as a diffusion layer (viewing angle expanding function or the like) for diffusing the light transmitted through the polarizing plate to expand the viewing angle.

なお、前記反射防止層、スティッキング防止層、拡散層やアンチグレア層等は、透明保護フィルムそのものに設けることができるほか、別途光学層として透明保護フィルムとは別体のものとして設けることもできる。   The antireflection layer, antisticking layer, diffusion layer, antiglare layer, and the like can be provided on the transparent protective film itself, or can be provided separately from the transparent protective film as an optical layer.

本発明の偏光板は、実用に際して他の光学層と積層した光学フィルムとして用いることができる。その光学層については特に限定はないが、例えば反射板や半透過板、位相差板(1/2や1/4等の波長板を含む)、視角補償フィルムなどの液晶表示装置等の形成に用いられることのある光学層を1層または2層以上用いることができる。特に、本発明の偏光板に更に反射板または半透過反射板が積層されてなる反射型偏光板または半透過型偏光板、偏光板に更に位相差板が積層されてなる楕円偏光板または円偏光板、偏光板に更に視角補償フィルムが積層されてなる広視野角偏光板、あるいは偏光板に更に輝度向上フィルムが積層されてなる偏光板が好ましい。   The polarizing plate of the present invention can be used as an optical film laminated with another optical layer in practical use. The optical layer is not particularly limited. For example, for forming a liquid crystal display device such as a reflection plate, a semi-transmission plate, a retardation plate (including wavelength plates such as 1/2 and 1/4), and a viewing angle compensation film. One or more optical layers that may be used can be used. In particular, a reflective polarizing plate or a semi-transmissive polarizing plate in which a polarizing plate or a semi-transmissive reflecting plate is further laminated on the polarizing plate of the present invention, an elliptical polarizing plate or a circularly polarizing plate in which a retardation plate is further laminated on the polarizing plate. A wide viewing angle polarizing plate obtained by further laminating a viewing angle compensation film on a plate or a polarizing plate, or a polarizing plate obtained by further laminating a brightness enhancement film on the polarizing plate is preferable.

反射型偏光板は、偏光板に反射層を設けたもので、視認側(表示側)からの入射光を反射させて表示するタイプの液晶表示装置などを形成するためのものであり、バックライト等の光源の内蔵を省略できて液晶表示装置の薄型化を図りやすいなどの利点を有する。反射型偏光板の形成は、必要に応じ透明保護層等を介して偏光板の片面に金属等からなる反射層を付設する方式などの適宜な方式にて行うことができる。   A reflective polarizing plate is a polarizing plate provided with a reflective layer, and is used to form a liquid crystal display device or the like that reflects incident light from the viewing side (display side). Such a light source can be omitted, and the liquid crystal display device can be easily thinned. The reflective polarizing plate can be formed by an appropriate method such as a method in which a reflective layer made of metal or the like is attached to one surface of the polarizing plate via a transparent protective layer or the like as necessary.

反射型偏光板の具体例としては、必要に応じマット処理した透明保護フィルムの片面に、アルミニウム等の反射性金属からなる箔や蒸着膜を付設して反射層を形成したものなどがあげられる。また前記透明保護フィルムに微粒子を含有させて表面微細凹凸構造とし、その上に微細凹凸構造の反射層を有するものなどもあげられる。前記した微細凹凸構造の反射層は、入射光を乱反射により拡散させて指向性やギラギラした見栄えを防止し、明暗のムラを抑制しうる利点などを有する。また微粒子含有の透明保護フィルムは、入射光及びその反射光がそれを透過する際に拡散されて明暗ムラをより抑制しうる利点なども有している。透明保護フィルムの表面微細凹凸構造を反映させた微細凹凸構造の反射層の形成は、例えば真空蒸着方式、イオンプレーティング方式、スパッタリング方式等の蒸着方式やメッキ方式などの適宜な方式で金属を透明保護層の表面に直接付設する方法などにより行うことができる。   Specific examples of the reflective polarizing plate include those in which a reflective layer is formed by attaching a foil or a vapor deposition film made of a reflective metal such as aluminum on one side of a transparent protective film matted as necessary. Moreover, the transparent protective film contains fine particles so as to have a surface fine concavo-convex structure and a reflective layer having a fine concavo-convex structure thereon. The reflective layer having the fine concavo-convex structure has an advantage that incident light is diffused by irregular reflection to prevent directivity and glaring appearance and to suppress unevenness in brightness and darkness. The transparent protective film containing fine particles also has an advantage that incident light and its reflected light are diffused when passing through it, and light and dark unevenness can be further suppressed. The reflective layer of the fine concavo-convex structure reflecting the surface fine concavo-convex structure of the transparent protective film is formed by transparent the metal by an appropriate method such as a vapor deposition method such as a vacuum vapor deposition method, an ion plating method, a sputtering method, or a plating method. It can be performed by a method of directly attaching to the surface of the protective layer.

反射板は前記の偏光板の透明保護フィルムに直接付与する方式に代えて、その透明フィルムに準じた適宜なフィルムに反射層を設けてなる反射シートなどとして用いることもできる。なお反射層は、通常、金属からなるので、その反射面が透明保護フィルムや偏光板等で被覆された状態の使用形態が、酸化による反射率の低下防止、ひいては初期反射率の長期持続の点や、保護層の別途付設の回避の点などより好ましい。   Instead of the method of directly applying the reflecting plate to the transparent protective film of the polarizing plate, the reflecting plate can be used as a reflecting sheet provided with a reflecting layer on an appropriate film according to the transparent film. Since the reflective layer is usually made of metal, the usage form in which the reflective surface is covered with a transparent protective film, a polarizing plate or the like is used to prevent the reflectance from being lowered due to oxidation, and thus to maintain the initial reflectance for a long time. In addition, it is more preferable to avoid a separate attachment of the protective layer.

なお、半透過型偏光板は、上記において反射層で光を反射し、かつ透過するハーフミラー等の半透過型の反射層とすることにより得ることができる。半透過型偏光板は、通常液晶セルの裏側に設けられ、液晶表示装置などを比較的明るい雰囲気で使用する場合には、視認側(表示側)からの入射光を反射させて画像を表示し、比較的暗い雰囲気においては、半透過型偏光板のバックサイドに内蔵されているバックライト等の内蔵光源を使用して画像を表示するタイプの液晶表示装置などを形成できる。すなわち、半透過型偏光板は、明るい雰囲気下では、バックライト等の光源使用のエネルギーを節約でき、比較的暗い雰囲気下においても内蔵光源を用いて使用できるタイプの液晶表示装置などの形成に有用である。   The semi-transmissive polarizing plate can be obtained by using a semi-transmissive reflective layer such as a half mirror that reflects and transmits light with the reflective layer. A transflective polarizing plate is usually provided on the back side of a liquid crystal cell, and displays an image by reflecting incident light from the viewing side (display side) when a liquid crystal display device is used in a relatively bright atmosphere. In a relatively dark atmosphere, a liquid crystal display device or the like that displays an image using a built-in light source such as a backlight built in the back side of the transflective polarizing plate can be formed. In other words, the transflective polarizing plate is useful for forming a liquid crystal display device of a type that can save energy of using a light source such as a backlight in a bright atmosphere and can be used with a built-in light source even in a relatively dark atmosphere. It is.

偏光板に更に位相差板が積層されてなる楕円偏光板または円偏光板について説明する。直線偏光を楕円偏光または円偏光に変えたり、楕円偏光または円偏光を直線偏光に変えたり、あるいは直線偏光の偏光方向を変える場合に、位相差板などが用いられる。特に、直線偏光を円偏光に変えたり、円偏光を直線偏光に変える位相差板としては、いわゆる1/4波長板(λ/4板とも言う)が用いられる。1/2波長板(λ/2板とも言う)は、通常、直線偏光の偏光方向を変える場合に用いられる。   An elliptically polarizing plate or a circularly polarizing plate in which a retardation plate is further laminated on a polarizing plate will be described. A phase difference plate or the like is used when changing linearly polarized light to elliptically polarized light or circularly polarized light, changing elliptically polarized light or circularly polarized light to linearly polarized light, or changing the polarization direction of linearly polarized light. In particular, a so-called quarter-wave plate (also referred to as a λ / 4 plate) is used as a retardation plate that changes linearly polarized light into circularly polarized light or changes circularly polarized light into linearly polarized light. A half-wave plate (also referred to as a λ / 2 plate) is usually used when changing the polarization direction of linearly polarized light.

楕円偏光板はスーパーツイストネマチック(STN)型液晶表示装置の液晶層の複屈折により生じた着色(青又は黄)を補償(防止)して、前記着色のない白黒表示する場合などに有効に用いられる。更に、三次元の屈折率を制御したものは、液晶表示装置の画面を斜め方向から見た際に生じる着色も補償(防止)することができて好ましい。円偏光板は、例えば画像がカラー表示になる反射型液晶表示装置の画像の色調を整える場合などに有効に用いられ、また、反射防止の機能も有する。上記した位相差板の具体例としては、ポリカーボネート、ポリビニルアルコール、ポリスチレン、ポリメチルメタクリレート、ポリプロピレンやその他のポリオレフィン、ポリアリレート、ポリアミドの如き適宜なポリマーからなるフィルムを延伸処理してなる複屈折性フィルムや液晶ポリマーの配向フィルム、液晶ポリマーの配向層をフィルムにて支持したものなどがあげられる。位相差板は、例えば各種波長板や液晶層の複屈折による着色や視角等の補償を目的としたものなどの使用目的に応じた適宜な位相差を有するものであってよく、2種以上の位相差板を積層して位相差等の光学特性を制御したものなどであってもよい。   The elliptically polarizing plate is effectively used for black and white display without the above color by compensating (preventing) the coloration (blue or yellow) generated by the birefringence of the liquid crystal layer of the super twist nematic (STN) type liquid crystal display device. It is done. Further, the one in which the three-dimensional refractive index is controlled is preferable because it can compensate (prevent) coloring that occurs when the screen of the liquid crystal display device is viewed from an oblique direction. The circularly polarizing plate is effectively used, for example, when adjusting the color tone of an image of a reflective liquid crystal display device in which an image is displayed in color, and also has an antireflection function. Specific examples of the retardation plate include a birefringent film obtained by stretching a film made of an appropriate polymer such as polycarbonate, polyvinyl alcohol, polystyrene, polymethyl methacrylate, polypropylene, other polyolefins, polyarylate, and polyamide. And an alignment film of a liquid crystal polymer, and a liquid crystal polymer alignment layer supported by a film. The retardation plate may have an appropriate retardation according to the purpose of use, such as those for the purpose of compensating for various wavelength plates or birefringence of the liquid crystal layer, viewing angle, and the like. What laminated | stacked the phase difference plate and controlled optical characteristics, such as phase difference, etc. may be used.

また上記の楕円偏光板や反射型楕円偏光板は、偏光板又は反射型偏光板と位相差板を適宜な組み合わせで積層したものである。かかる楕円偏光板等は、(反射型)偏光板と位相差板の組み合わせとなるようにそれらを液晶表示装置の製造過程で順次別個に積層することによっても形成しうるが、前記の如く予め楕円偏光板等の光学フィルムとしたものは、品質の安定性や積層作業性等に優れて液晶表示装置などの製造効率を向上させうる利点がある。   The elliptical polarizing plate and the reflective elliptical polarizing plate are obtained by laminating a polarizing plate or a reflective polarizing plate and a retardation plate in an appropriate combination. Such an elliptically polarizing plate or the like can also be formed by sequentially laminating them sequentially in the manufacturing process of the liquid crystal display device so as to be a combination of a (reflection type) polarizing plate and a retardation plate. An optical film such as a polarizing plate has an advantage that it can improve the production efficiency of a liquid crystal display device and the like because of excellent quality stability and lamination workability.

視角補償フィルムは、液晶表示装置の画面を、画面に垂直でなくやや斜めの方向から見た場合でも、画像が比較的鮮明にみえるように視野角を広げるためのフィルムである。このような視角補償位相差板としては、例えば位相差フィルム、液晶ポリマー等の配向フィルムや透明基材上に液晶ポリマー等の配向層を支持したものなどからなる。通常の位相差板は、その面方向に一軸に延伸された複屈折を有するポリマーフィルムが用いられるのに対し、視角補償フィルムとして用いられる位相差板には、面方向に二軸に延伸された複屈折を有するポリマーフィルムとか、面方向に一軸に延伸され厚さ方向にも延伸された厚さ方向の屈折率を制御した複屈折を有するポリマーや傾斜配向フィルムのような二方向延伸フィルムなどが用いられる。傾斜配向フィルムとしては、例えばポリマーフィルムに熱収縮フィルムを接着して加熱によるその収縮力の作用下にポリマーフィルムを延伸処理又は/及び収縮処理したものや、液晶ポリマーを斜め配向させたものなどが挙げられる。位相差板の素材原料ポリマーは、先の位相差板で説明したポリマーと同様のものが用いられ、液晶セルによる位相差に基づく視認角の変化による着色等の防止や良視認の視野角の拡大などを目的とした適宜なものを用いうる。   The viewing angle compensation film is a film for widening the viewing angle so that an image can be seen relatively clearly even when the screen of the liquid crystal display device is viewed from a slightly oblique direction rather than perpendicular to the screen. As such a viewing angle compensation phase difference plate, for example, a retardation film, an alignment film such as a liquid crystal polymer, or an alignment layer such as a liquid crystal polymer supported on a transparent substrate is used. A normal retardation plate uses a birefringent polymer film uniaxially stretched in the plane direction, whereas a retardation plate used as a viewing angle compensation film stretches biaxially in the plane direction. Birefringent polymer film, biaxially stretched film such as polymer with birefringence with a controlled refractive index in the thickness direction that is uniaxially stretched in the plane direction and stretched in the thickness direction, etc. Used. Examples of the inclined alignment film include a film obtained by bonding a heat shrink film to a polymer film and stretching or / and shrinking the polymer film under the action of the contraction force by heating, and a film obtained by obliquely aligning a liquid crystal polymer. Can be mentioned. The raw material polymer for the phase difference plate is the same as the polymer described in the previous phase difference plate, preventing coloration due to a change in the viewing angle based on the phase difference by the liquid crystal cell and expanding the viewing angle for good visual recognition. An appropriate one for the purpose can be used.

また良視認の広い視野角を達成する点などより、液晶ポリマーの配向層、特にディスコティック液晶ポリマーの傾斜配向層からなる光学的異方性層をトリアセチルセルロースフィルムにて支持した光学補償位相差板が好ましく用いうる。   Also, from the viewpoint of achieving a wide viewing angle with good visibility, an optically compensated phase difference in which a liquid crystal polymer alignment layer, in particular an optically anisotropic layer composed of a discotic liquid crystal polymer gradient alignment layer, is supported by a triacetylcellulose film. A plate can be preferably used.

偏光板と輝度向上フィルムを貼り合わせた偏光板は、通常液晶セルの裏側サイドに設けられて使用される。輝度向上フィルムは、液晶表示装置などのバックライトや裏側からの反射などにより自然光が入射すると所定偏光軸の直線偏光または所定方向の円偏光を反射し、他の光は透過する特性を示すもので、輝度向上フィルムを偏光板と積層した偏光板は、バックライト等の光源からの光を入射させて所定偏光状態の透過光を得ると共に、前記所定偏光状態以外の光は透過せずに反射される。この輝度向上フィルム面で反射した光を更にその後ろ側に設けられた反射層等を介し反転させて輝度向上フィルムに再入射させ、その一部又は全部を所定偏光状態の光として透過させて輝度向上フィルムを透過する光の増量を図ると共に、偏光子に吸収させにくい偏光を供給して液晶表示画像表示等に利用しうる光量の増大を図ることにより輝度を向上させうるものである。すなわち、輝度向上フィルムを使用せずに、バックライトなどで液晶セルの裏側から偏光子を通して光を入射した場合には、偏光子の偏光軸に一致していない偏光方向を有する光は、ほとんど偏光子に吸収されてしまい、偏光子を透過してこない。すなわち、用いた偏光子の特性によっても異なるが、およそ50%の光が偏光子に吸収されてしまい、その分、液晶画像表示等に利用しうる光量が減少し、画像が暗くなる。輝度向上フィルムは、偏光子に吸収されるような偏光方向を有する光を偏光子に入射させずに輝度向上フィルムで一旦反射させ、更にその後ろ側に設けられた反射層等を介して反転させて輝度向上フィルムに再入射させることを繰り返し、この両者間で反射、反転している光の偏光方向が偏光子を通過し得るような偏光方向になった偏光のみを、輝度向上フィルムは透過させて偏光子に供給するので、バックライトなどの光を効率的に液晶表示装置の画像の表示に使用でき、画面を明るくすることができる。   A polarizing plate obtained by bonding a polarizing plate and a brightness enhancement film is usually provided on the back side of a liquid crystal cell. The brightness enhancement film reflects a linearly polarized light with a predetermined polarization axis or a circularly polarized light in a predetermined direction when natural light is incident due to a backlight such as a liquid crystal display device or reflection from the back side, and transmits other light. In addition, a polarizing plate in which a brightness enhancement film is laminated with a polarizing plate allows light from a light source such as a backlight to enter to obtain transmitted light in a predetermined polarization state, and reflects light without transmitting the light other than the predetermined polarization state. The The light reflected on the surface of the brightness enhancement film is further inverted through a reflective layer or the like provided behind the brightness enhancement film and re-incident on the brightness enhancement film, and part or all of the light is transmitted as light having a predetermined polarization state. Luminance can be improved by increasing the amount of light transmitted through the enhancement film and increasing the amount of light that can be used for liquid crystal display image display or the like by supplying polarized light that is difficult to be absorbed by the polarizer. That is, when light is incident through the polarizer from the back side of the liquid crystal cell without using a brightness enhancement film, light having a polarization direction that does not coincide with the polarization axis of the polarizer is almost polarized. It is absorbed by the polarizer and does not pass through the polarizer. That is, although depending on the characteristics of the polarizer used, approximately 50% of the light is absorbed by the polarizer, and the amount of light that can be used for liquid crystal image display or the like is reduced accordingly, resulting in a dark image. The brightness enhancement film allows light having a polarization direction that is absorbed by the polarizer to be reflected once by the brightness enhancement film without being incident on the polarizer, and further inverted through a reflective layer provided on the rear side thereof. Repeatedly re-enter the brightness enhancement film, and the brightness enhancement film transmits only polarized light whose polarization direction is such that the polarization direction of light reflected and inverted between the two can pass through the polarizer. Therefore, light such as a backlight can be efficiently used for displaying an image on the liquid crystal display device, and the screen can be brightened.

輝度向上フィルムと上記反射層等の間に拡散板を設けることもできる。輝度向上フィルムによって反射した偏光状態の光は上記反射層等に向かうが、設置された拡散板は通過する光を均一に拡散すると同時に偏光状態を解消し、非偏光状態となる。すなわち、拡散板は偏光を元の自然光状態にもどす。この非偏光状態、すなわち自然光状態の光が反射層等に向かい、反射層等を介して反射し、再び拡散板を通過して輝度向上フィルムに再入射することを繰り返す。このように輝度向上フィルムと上記反射層等の間に、偏光を元の自然光状態にもどす拡散板を設けることにより表示画面の明るさを維持しつつ、同時に表示画面の明るさのむらを少なくし、均一で明るい画面を提供することができる。かかる拡散板を設けることにより、初回の入射光は反射の繰り返し回数が程よく増加し、拡散板の拡散機能と相俟って均一の明るい表示画面を提供することができたものと考えられる。   A diffusion plate may be provided between the brightness enhancement film and the reflective layer. The polarized light reflected by the brightness enhancement film is directed to the reflective layer or the like, but the installed diffuser plate uniformly diffuses the light passing therethrough and simultaneously cancels the polarized state and becomes a non-polarized state. That is, the diffuser plate returns the polarized light to the original natural light state. The light in the non-polarized state, that is, the natural light state is directed toward the reflection layer and the like, reflected through the reflection layer and the like, and again passes through the diffusion plate and reenters the brightness enhancement film. Thus, while maintaining the brightness of the display screen by providing a diffuser plate that returns polarized light to the original natural light state between the brightness enhancement film and the reflective layer, etc., the brightness unevenness of the display screen is reduced at the same time, A uniform and bright screen can be provided. By providing such a diffuser plate, it is considered that the first incident light has a moderate increase in the number of repetitions of reflection, and in combination with the diffusion function of the diffuser plate, a uniform bright display screen can be provided.

前記の輝度向上フィルムとしては、例えば誘電体の多層薄膜や屈折率異方性が相違する薄膜フィルムの多層積層体の如き、所定偏光軸の直線偏光を透過して他の光は反射する特性を示すもの、コレステリック液晶ポリマーの配向フィルムやその配向液晶層をフィルム基材上に支持したものの如き、左回り又は右回りのいずれか一方の円偏光を反射して他の光は透過する特性を示すものなどの適宜なものを用いうる。   The brightness enhancement film has a characteristic of transmitting linearly polarized light having a predetermined polarization axis and reflecting other light, such as a multilayer thin film of dielectric material or a multilayer laminate of thin film films having different refractive index anisotropies. Such as an alignment film of a cholesteric liquid crystal polymer or an alignment liquid crystal layer supported on a film substrate, which reflects either left-handed or right-handed circularly polarized light and transmits other light. Appropriate things, such as a thing, can be used.

従って、前記した所定偏光軸の直線偏光を透過させるタイプの輝度向上フィルムでは、その透過光をそのまま偏光板に偏光軸を揃えて入射させることにより、偏光板による吸収ロスを抑制しつつ効率よく透過させることができる。一方、コレステリック液晶層の如く円偏光を透過するタイプの輝度向上フィルムでは、そのまま偏光子に入射させることもできるが、吸収ロスを抑制する点よりその円偏光を位相差板を介し直線偏光化して偏光板に入射させることが好ましい。なお、その位相差板として1/4波長板を用いることにより、円偏光を直線偏光に変換することができる。   Therefore, in the brightness enhancement film of the type that transmits linearly polarized light having the predetermined polarization axis as described above, the transmitted light is incident on the polarizing plate with the polarization axis aligned as it is, thereby efficiently transmitting while suppressing absorption loss due to the polarizing plate. Can be made. On the other hand, in a brightness enhancement film of a type that transmits circularly polarized light such as a cholesteric liquid crystal layer, it can be directly incident on a polarizer, but from the point of suppressing absorption loss, the circularly polarized light is linearly polarized through a retardation plate. It is preferable to make it enter into a polarizing plate. Note that circularly polarized light can be converted to linearly polarized light by using a quarter wave plate as the retardation plate.

可視光域等の広い波長範囲で1/4波長板として機能する位相差板は、例えば波長550nmの淡色光に対して1/4波長板として機能する位相差層と他の位相差特性を示す位相差層、例えば1/2波長板として機能する位相差層とを重畳する方式などにより得ることができる。従って、偏光板と輝度向上フィルムの間に配置する位相差板は、1層又は2層以上の位相差層からなるものであってよい。   A retardation plate that functions as a quarter-wave plate in a wide wavelength range such as a visible light region exhibits, for example, a retardation layer that functions as a quarter-wave plate for light-color light having a wavelength of 550 nm and other retardation characteristics. It can be obtained by a method of superposing a retardation layer, for example, a retardation layer functioning as a half-wave plate. Therefore, the retardation plate disposed between the polarizing plate and the brightness enhancement film may be composed of one or more retardation layers.

なお、コレステリック液晶層についても、反射波長が相違するものの組み合わせにして2層又は3層以上重畳した配置構造とすることにより、可視光領域等の広い波長範囲で円偏光を反射するものを得ることができ、それに基づいて広い波長範囲の透過円偏光を得ることができる。   In addition, the cholesteric liquid crystal layer can also be obtained by reflecting circularly polarized light in a wide wavelength range such as a visible light region by combining two or more layers having different reflection wavelengths and having an overlapping structure. Based on this, transmitted circularly polarized light in a wide wavelength range can be obtained.

また、偏光板は、上記の偏光分離型偏光板の如く、偏光板と2層又は3層以上の光学層とを積層したものからなっていてもよい。従って、上記の反射型偏光板や半透過型偏光板と位相差板を組み合わせた反射型楕円偏光板や半透過型楕円偏光板などであってもよい。   Further, the polarizing plate may be formed by laminating a polarizing plate and two or three or more optical layers like the above-described polarization separation type polarizing plate. Therefore, a reflective elliptical polarizing plate or a semi-transmissive elliptical polarizing plate in which the above-mentioned reflective polarizing plate or transflective polarizing plate and a retardation plate are combined may be used.

偏光板に前記光学層を積層した光学フィルムは、液晶表示装置等の製造過程で順次別個に積層する方式にても形成することができるが、予め積層して光学フィルムとしたものは、品質の安定性や組立作業等に優れていて液晶表示装置などの製造工程を向上させうる利点がある。積層には粘着層等の適宜な接着手段を用いうる。前記の偏光板やその他の光学フィルムの接着に際し、それらの光学軸は目的とする位相差特性などに応じて適宜な配置角度とすることができる。   An optical film in which the optical layer is laminated on a polarizing plate can be formed by a method of sequentially laminating separately in the manufacturing process of a liquid crystal display device or the like. There is an advantage that the manufacturing process of a liquid crystal display device or the like can be improved because of excellent stability and assembly work. For the lamination, an appropriate adhesive means such as an adhesive layer can be used. When adhering the polarizing plate and other optical films, their optical axes can be set at an appropriate arrangement angle in accordance with the target retardation characteristics.

前述した偏光板や、偏光板を少なくとも1層積層されている光学フィルムには、液晶セル等の他部材と接着するための粘着層を設けることもできる。粘着層を形成する粘着剤は特に制限されないが、例えばアクリル系重合体、シリコーン系ポリマー、ポリエステル、ポリウレタン、ポリアミド、ポリエーテル、フッ素系やゴム系などのポリマーをベースポリマーとするものを適宜に選択して用いることができる。特に、アクリル系粘着剤の如く光学的透明性に優れ、適度な濡れ性と凝集性と接着性の粘着特性を示して、耐候性や耐熱性などに優れるものが好ましく用いうる。   An adhesive layer for adhering to other members such as a liquid crystal cell may be provided on the polarizing plate described above or an optical film in which at least one polarizing plate is laminated. The pressure-sensitive adhesive forming the pressure-sensitive adhesive layer is not particularly limited. For example, an acrylic polymer, silicone-based polymer, polyester, polyurethane, polyamide, polyether, fluorine-based or rubber-based polymer is appropriately selected. Can be used. In particular, those having excellent optical transparency such as an acrylic pressure-sensitive adhesive, exhibiting appropriate wettability, cohesiveness, and adhesive pressure-sensitive adhesive properties, and being excellent in weather resistance, heat resistance and the like can be preferably used.

また上記に加えて、吸湿による発泡現象や剥がれ現象の防止、熱膨張差等による光学特性の低下や液晶セルの反り防止、ひいては高品質で耐久性に優れる液晶表示装置の形成性などの点より、吸湿率が低くて耐熱性に優れる粘着層が好ましい。   In addition to the above, in terms of prevention of foaming and peeling phenomena due to moisture absorption, deterioration of optical properties and liquid crystal cell warpage due to differences in thermal expansion, etc., as well as formability of liquid crystal display devices with high quality and excellent durability An adhesive layer having a low moisture absorption rate and excellent heat resistance is preferred.

粘着層は、例えば天然物や合成物の樹脂類、特に、粘着性付与樹脂や、ガラス繊維、ガラスビーズ、金属粉、その他の無機粉末等からなる充填剤や顔料、着色剤、酸化防止剤などの粘着層に添加されることの添加剤を含有していてもよい。また微粒子を含有して光拡散性を示す粘着層などであってもよい。   The adhesive layer is, for example, natural or synthetic resins, in particular, tackifier resins, fillers or pigments made of glass fibers, glass beads, metal powders, other inorganic powders, colorants, antioxidants, etc. It may contain an additive to be added to the adhesive layer. Moreover, the adhesion layer etc. which contain microparticles | fine-particles and show light diffusibility may be sufficient.

偏光板や光学フィルムの片面又は両面への粘着層の付設は、適宜な方式で行いうる。その例としては、例えばトルエンや酢酸エチル等の適宜な溶剤の単独物又は混合物からなる溶媒にベースポリマーまたはその組成物を溶解又は分散させた10〜40重量%程度の粘着剤溶液を調製し、それを流延方式や塗工方式等の適宜な展開方式で偏光板上または光学フィルム上に直接付設する方式、あるいは前記に準じセパレータ上に粘着層を形成してそれを偏光板上または光学フィルム上に移着する方式などがあげられる。   Attachment of the adhesive layer to one or both sides of the polarizing plate or the optical film can be performed by an appropriate method. For example, a pressure sensitive adhesive solution of about 10 to 40% by weight in which a base polymer or a composition thereof is dissolved or dispersed in a solvent composed of a suitable solvent alone or a mixture such as toluene and ethyl acetate is prepared. A method in which it is directly attached on a polarizing plate or an optical film by an appropriate development method such as a casting method or a coating method, or an adhesive layer is formed on a separator according to the above, and this is applied to a polarizing plate or an optical film. The method of moving up is mentioned.

粘着層は、異なる組成又は種類等のものの重畳層として偏光板や光学フィルムの片面又は両面に設けることもできる。また両面に設ける場合に、偏光板や光学フィルムの表裏において異なる組成や種類や厚さ等の粘着層とすることもできる。粘着層の厚さは、使用目的や接着力などに応じて適宜に決定でき、一般には1〜500μmであり、1〜200μmが好ましく、特に1〜100μmが好ましい。   The pressure-sensitive adhesive layer can be provided on one side or both sides of a polarizing plate or an optical film as a superimposed layer of different compositions or types. Moreover, when providing in both surfaces, it can also be set as the adhesion layers of a different composition, a kind, thickness, etc. in the front and back of a polarizing plate or an optical film. The thickness of the pressure-sensitive adhesive layer can be appropriately determined according to the purpose of use and adhesive force, and is generally 1 to 500 μm, preferably 1 to 200 μm, and particularly preferably 1 to 100 μm.

粘着層の露出面に対しては、実用に供するまでの間、その汚染防止等を目的にセパレータが仮着されてカバーされる。これにより、通例の取扱状態で粘着層に接触することを防止できる。セパレータとしては、上記厚さ条件を除き、例えばプラスチックフィルム、ゴムシート、紙、布、不織布、ネット、発泡シートや金属箔、それらのラミネート体等の適宜な薄葉体を、必要に応じシリコーン系や長鎖アルキル系、フッ素系や硫化モリブデン等の適宜な剥離剤でコート処理したものなどの、従来に準じた適宜なものを用いうる。   On the exposed surface of the adhesive layer, a separator is temporarily attached and covered for the purpose of preventing contamination until it is put to practical use. Thereby, it can prevent contacting an adhesion layer in the usual handling state. As the separator, except for the above thickness conditions, for example, a suitable thin leaf body such as a plastic film, rubber sheet, paper, cloth, non-woven fabric, net, foam sheet, metal foil, laminate thereof, and the like, silicone type or Appropriate conventional ones such as those coated with an appropriate release agent such as long-chain alkyl, fluorine-based, or molybdenum sulfide can be used.

なお本発明において、上記した偏光板を形成する偏光子や透明保護フィルムや光学フィルム等、また粘着層などの各層には、例えばサリチル酸エステル系化合物やベンゾフェノール系化合物、ベンゾトリアゾール系化合物やシアノアクリレート系化合物、ニッケル錯塩系化合物等の紫外線吸収剤で処理する方式などの方式により紫外線吸収能をもたせたものなどであってもよい。   In the present invention, the polarizer, the transparent protective film, the optical film, and the like that form the polarizing plate described above, and each layer such as an adhesive layer include, for example, a salicylic acid ester compound, a benzophenol compound, a benzotriazole compound, and a cyanoacrylate. It may be a compound having an ultraviolet absorbing ability by a method such as a method of treating with an ultraviolet absorber such as a compound based on nickel or a nickel complex salt compound.

本発明の偏光板または光学フィルムは液晶表示装置等の各種装置の形成などに好ましく用いることができる。液晶表示装置の形成は、従来に準じて行いうる。すなわち液晶表示装置は一般に、液晶セルと偏光板または光学フィルム、及び必要に応じての照明システム等の構成部品を適宜に組立てて駆動回路を組込むことなどにより形成されるが、本発明においては本発明による偏光板または光学フィルムを用いる点を除いて特に限定はなく、従来に準じうる。液晶セルについても、例えばTN型やSTN型、π型などの任意なタイプのものを用いうる。   The polarizing plate or the optical film of the present invention can be preferably used for forming various devices such as a liquid crystal display device. The liquid crystal display device can be formed according to the conventional method. That is, a liquid crystal display device is generally formed by appropriately assembling components such as a liquid crystal cell, a polarizing plate or an optical film, and an illumination system as necessary, and incorporating a drive circuit. There is no limitation in particular except the point which uses the polarizing plate or optical film by invention, and it can apply according to the former. As the liquid crystal cell, any type such as a TN type, an STN type, or a π type can be used.

液晶セルの片側又は両側に偏光板または光学フィルムを配置した液晶表示装置や、照明システムにバックライトあるいは反射板を用いたものなどの適宜な液晶表示装置を形成することができる。その場合、本発明による偏光板または光学フィルムは液晶セルの片側又は両側に設置することができる。両側に偏光板または光学フィルムを設ける場合、それらは同じものであってもよいし、異なるものであってもよい。さらに、液晶表示装置の形成に際しては、例えば拡散板、アンチグレア層、反射防止膜、保護板、プリズムアレイ、レンズアレイシート、光拡散板、バックライトなどの適宜な部品を適宜な位置に1層又は2層以上配置することができる。   An appropriate liquid crystal display device such as a liquid crystal display device in which a polarizing plate or an optical film is disposed on one side or both sides of a liquid crystal cell, or a backlight or a reflector used in an illumination system can be formed. In that case, the polarizing plate or optical film by this invention can be installed in the one side or both sides of a liquid crystal cell. When providing a polarizing plate or an optical film on both sides, they may be the same or different. Further, when forming a liquid crystal display device, for example, a single layer or a suitable part such as a diffusing plate, an antiglare layer, an antireflection film, a protective plate, a prism array, a lens array sheet, a light diffusing plate, a backlight, etc. Two or more layers can be arranged.

次いで有機エレクトロルミネセンス装置(有機EL表示装置)について説明する。一般に、有機EL表示装置は、透明基板上に透明電極と有機発光層と金属電極とを順に積層して発光体(有機エレクトロルミネセンス発光体)を形成している。ここで、有機発光層は、種々の有機薄膜の積層体であり、例えばトリフェニルアミン誘導体等からなる正孔注入層と、アントラセン等の蛍光性の有機固体からなる発光層との積層体や、あるいはこのような発光層とペリレン誘導体等からなる電子注入層の積層体や、またあるいはこれらの正孔注入層、発光層、および電子注入層の積層体等、種々の組み合わせをもった構成が知られている。   Next, an organic electroluminescence device (organic EL display device) will be described. Generally, in an organic EL display device, a transparent electrode, an organic light emitting layer, and a metal electrode are sequentially laminated on a transparent substrate to form a light emitter (organic electroluminescent light emitter). Here, the organic light emitting layer is a laminate of various organic thin films, for example, a laminate of a hole injection layer made of a triphenylamine derivative and the like and a light emitting layer made of a fluorescent organic solid such as anthracene, Alternatively, a structure having various combinations such as a laminate of such a light emitting layer and an electron injection layer composed of a perylene derivative or the like, or a laminate of these hole injection layer, light emitting layer, and electron injection layer is known. It has been.

有機EL表示装置は、透明電極と金属電極とに電圧を印加することによって、有機発光層に正孔と電子とが注入され、これら正孔と電子との再結合によって生じるエネルギーが蛍光物資を励起し、励起された蛍光物質が基底状態に戻るときに光を放射する、という原理で発光する。途中の再結合というメカニズムは、一般のダイオードと同様であり、このことからも予想できるように、電流と発光強度は印加電圧に対して整流性を伴う強い非線形性を示す。   In organic EL display devices, holes and electrons are injected into the organic light-emitting layer by applying a voltage to the transparent electrode and the metal electrode, and the energy generated by recombination of these holes and electrons excites the phosphor material. Then, light is emitted on the principle that the excited fluorescent material emits light when returning to the ground state. The mechanism of recombination in the middle is the same as that of a general diode, and as can be predicted from this, the current and the emission intensity show strong nonlinearity with rectification with respect to the applied voltage.

有機EL表示装置においては、有機発光層での発光を取り出すために、少なくとも一方の電極が透明でなくてはならず、通常酸化インジウムスズ(ITO)などの透明導電体で形成した透明電極を陽極として用いている。一方、電子注入を容易にして発光効率を上げるには、陰極に仕事関数の小さな物質を用いることが重要で、通常Mg−Ag、Al−Liなどの金属電極を用いている。   In an organic EL display device, in order to extract light emitted from the organic light emitting layer, at least one of the electrodes must be transparent, and a transparent electrode usually formed of a transparent conductor such as indium tin oxide (ITO) is used as an anode. It is used as. On the other hand, in order to facilitate electron injection and increase luminous efficiency, it is important to use a material having a small work function for the cathode, and usually metal electrodes such as Mg—Ag and Al—Li are used.

このような構成の有機EL表示装置において、有機発光層は、厚さ10nm程度ときわめて薄い膜で形成されている。このため、有機発光層も透明電極と同様、光をほぼ完全に透過する。その結果、非発光時に透明基板の表面から入射し、透明電極と有機発光層とを透過して金属電極で反射した光が、再び透明基板の表面側へと出るため、外部から視認したとき、有機EL表示装置の表示面が鏡面のように見える。   In the organic EL display device having such a configuration, the organic light emitting layer is formed of a very thin film having a thickness of about 10 nm. For this reason, the organic light emitting layer transmits light almost completely like the transparent electrode. As a result, light that is incident from the surface of the transparent substrate at the time of non-light emission, passes through the transparent electrode and the organic light emitting layer, and is reflected by the metal electrode is again emitted to the surface side of the transparent substrate. The display surface of the organic EL display device looks like a mirror surface.

電圧の印加によって発光する有機発光層の表面側に透明電極を備えるとともに、有機発光層の裏面側に金属電極を備えてなる有機エレクトロルミネセンス発光体を含む有機EL表示装置において、透明電極の表面側に偏光板を設けるとともに、これら透明電極と偏光板との間に位相差板を設けることができる。   In an organic EL display device comprising an organic electroluminescent light emitting device comprising a transparent electrode on the surface side of an organic light emitting layer that emits light upon application of a voltage and a metal electrode on the back side of the organic light emitting layer, the surface of the transparent electrode While providing a polarizing plate on the side, a retardation plate can be provided between the transparent electrode and the polarizing plate.

位相差板および偏光板は、外部から入射して金属電極で反射してきた光を偏光する作用を有するため、その偏光作用によって金属電極の鏡面を外部から視認させないという効果がある。特に、位相差板を1/4波長板で構成し、かつ偏光板と位相差板との偏光方向のなす角をπ/4に調整すれば、金属電極の鏡面を完全に遮蔽することができる。   Since the retardation plate and the polarizing plate have a function of polarizing light incident from the outside and reflected by the metal electrode, there is an effect that the mirror surface of the metal electrode is not visually recognized by the polarization action. In particular, the mirror surface of the metal electrode can be completely shielded by configuring the retardation plate with a quarter-wave plate and adjusting the angle formed by the polarization direction of the polarizing plate and the retardation plate to π / 4. .

すなわち、この有機EL表示装置に入射する外部光は、偏光板により直線偏光成分のみが透過する。この直線偏光は位相差板により一般に楕円偏光となるが、とくに位相差板が1/4波長板でしかも偏光板と位相差板との偏光方向のなす角がπ/4のときには円偏光となる。   That is, only the linearly polarized light component of the external light incident on the organic EL display device is transmitted by the polarizing plate. This linearly polarized light becomes generally elliptically polarized light by the phase difference plate, but becomes circularly polarized light particularly when the phase difference plate is a quarter wavelength plate and the angle formed by the polarization direction of the polarizing plate and the phase difference plate is π / 4. .

この円偏光は、透明基板、透明電極、有機薄膜を透過し、金属電極で反射して、再び有機薄膜、透明電極、透明基板を透過して、位相差板に再び直線偏光となる。そして、この直線偏光は、偏光板の偏光方向と直交しているので、偏光板を透過できない。その結果、金属電極の鏡面を完全に遮蔽することができる。   This circularly polarized light is transmitted through the transparent substrate, the transparent electrode, and the organic thin film, is reflected by the metal electrode, is again transmitted through the organic thin film, the transparent electrode, and the transparent substrate, and becomes linearly polarized light again on the retardation plate. And since this linearly polarized light is orthogonal to the polarization direction of a polarizing plate, it cannot permeate | transmit a polarizing plate. As a result, the mirror surface of the metal electrode can be completely shielded.

以下、本発明の構成と効果を具体的に示す実施例等について説明する。なお、各例中、部および%は特記ない限り重量基準である。   Examples and the like specifically showing the configuration and effects of the present invention will be described below. In each example, parts and% are based on weight unless otherwise specified.

(接着剤水溶液の粘度)
調製した接着剤水溶液を、レオメーター(RSI‐HS,HAAKE社製)により測定した。
(Viscosity of adhesive aqueous solution)
The prepared adhesive aqueous solution was measured with a rheometer (RSI-HS, manufactured by HAAKE).

(コロイドの平均粒子径)
シリカコロイド水溶液を粒度分布計(大塚電子(株)製,ELS‐8000)により、動的光散乱法(光相関法)で測定した。
(Average colloid particle size)
The aqueous silica colloid solution was measured by a dynamic light scattering method (light correlation method) with a particle size distribution meter (ELS-8000, manufactured by Otsuka Electronics Co., Ltd.).

実施例1
(偏光子)
平均重合度2400、ケン化度99.9モル%の厚み75μmのポリビニルアルコールフィルムを、30℃の温水中に60秒間浸漬し膨潤させた。次いで、ヨウ素/ヨウ化カリウム(重量比=0.5/8)の濃度0.3%の水溶液に浸漬し、3.5倍まで延伸させながらフィルムを染色した。その後、65℃のホウ酸エステル水溶液中で、トータルの延伸倍率が6倍となるように延伸を行った。延伸後に、40℃のオーブンにて3分間乾燥を行い、偏光子を得た。
Example 1
(Polarizer)
A polyvinyl alcohol film having an average polymerization degree of 2400 and a saponification degree of 99.9 mol% and a thickness of 75 μm was immersed in warm water at 30 ° C. for 60 seconds to swell. Next, the film was dyed while being immersed in an aqueous solution of 0.3% concentration of iodine / potassium iodide (weight ratio = 0.5 / 8) and stretched to 3.5 times. Then, it extended | stretched so that the total draw ratio might be 6 times in 65 degreeC borate ester aqueous solution. After extending | stretching, it dried for 3 minutes in 40 degreeC oven, and obtained the polarizer.

(透明保護フィルム)
厚さ80μmのトリアセチルセルロースフィルムを用いた。
(Transparent protective film)
A triacetyl cellulose film having a thickness of 80 μm was used.

(接着剤の調製)
ポリビニルアルコール系樹脂(平均重合度:1750,ケン化度:99.9モル%)100部に対し、メチロールメラミン50部を、30℃の温度条件下に、純水に溶解し、固形分濃度3.5%に調整した水溶液を調製した(この水溶液を接着剤Aという)。前記接着剤A100部に対し、シリカコロイド水溶液(平均粒子径45nm,固形分濃度20%)5.83部を加えて接着剤水溶液を調製した。接着剤水溶液の粘度は12.0mPa・sであった。接着剤水溶液のpHは、7.0〜7.8の範囲であった。
(Preparation of adhesive)
For 100 parts of polyvinyl alcohol resin (average polymerization degree: 1750, saponification degree: 99.9 mol%), 50 parts of methylol melamine are dissolved in pure water under a temperature condition of 30 ° C., and the solid content concentration is 3 An aqueous solution adjusted to 5% was prepared (this aqueous solution is referred to as adhesive A). To 100 parts of the adhesive A, 5.83 parts of an aqueous silica colloid solution (average particle diameter 45 nm, solid content concentration 20%) was added to prepare an aqueous adhesive solution. The viscosity of the aqueous adhesive solution was 12.0 mPa · s. The pH of the aqueous adhesive solution was in the range of 7.0 to 7.8.

(偏光板の作成)
上記透明保護フィルムの片面に、上記接着剤を乾燥後の接着剤層の厚みが80nmとなるように塗布した。接着剤の塗布は、その調製から30分間後に23℃の温度条件下で行なった。次いで、23℃の温度条件下で偏光子の両面に接着剤付きのトリアセチルセルロースフィルムをロール機で貼り合せた後、55℃で6分間乾燥して偏光板を作成した。
(Creation of polarizing plate)
The adhesive was applied to one side of the transparent protective film so that the thickness of the adhesive layer after drying was 80 nm. Application of the adhesive was performed under a temperature condition of 23 ° C. 30 minutes after the preparation. Next, a triacetyl cellulose film with an adhesive was bonded to both sides of the polarizer under a temperature condition of 23 ° C. with a roll machine, and then dried at 55 ° C. for 6 minutes to prepare a polarizing plate.

実施例2
(接着剤の調製)
アセトアセチル基を含有するポリビニルアルコール系樹脂(平均重合度:1200,ケン化度:98.5モル%,アセトアセチル化度:5モル%)100部に対し、メチロールメラミン50部を、30℃の温度条件下に、純水に溶解し、固形分濃度3.5%に調整した水溶液を調製した(この水溶液を接着剤Bという)。前記接着剤B100部に対し、シリカコロイド水溶液(平均粒子径45nm,固形分濃度20%)5.83部を加えて接着剤水溶液を調製した。接着剤水溶液の粘度は7.8mPa・sであった。接着剤水溶液のpHは、6.0〜6.8の範囲であった。
Example 2
(Preparation of adhesive)
Polyvinyl alcohol-based resin containing acetoacetyl group (average polymerization degree: 1200, saponification degree: 98.5 mol%, acetoacetylation degree: 5 mol%) to 100 parts, Under a temperature condition, an aqueous solution dissolved in pure water and adjusted to a solid content concentration of 3.5% was prepared (this aqueous solution is referred to as an adhesive B). An aqueous adhesive solution was prepared by adding 5.83 parts of an aqueous silica colloid solution (average particle diameter 45 nm, solid content concentration 20%) to 100 parts of the adhesive B. The viscosity of the adhesive aqueous solution was 7.8 mPa · s. The pH of the aqueous adhesive solution was in the range of 6.0 to 6.8.

(偏光板の作成)
実施例1において、接着剤Aの代わりに、上記接着剤Bを用いたこと以外は、実施例1と同様にして、偏光板を作成した。
(Creation of polarizing plate)
In Example 1, a polarizing plate was produced in the same manner as in Example 1 except that the adhesive B was used instead of the adhesive A.

実施例3〜38、比較例1〜6
実施例1において、接着剤の調製あたり、表1に示すように接着剤の種類、その固形分濃度、シリカコロイドの平均粒子径、その使用割合を変えたこと以外は、実施例1と同様にして接着剤を調製した。また、得られた接着剤を用いて、接着剤層の厚みを表1に示すように変えたこと以外は実施例1と同様にして偏光板を作成した。
Examples 3-38, Comparative Examples 1-6
In Example 1, the same procedure as in Example 1 was carried out except that the type of adhesive, its solid content concentration, the average particle diameter of silica colloid, and its use ratio were changed as shown in Table 1 per preparation of the adhesive. An adhesive was prepared. Moreover, the polarizing plate was created like Example 1 except having changed the thickness of the adhesive bond layer as shown in Table 1 using the obtained adhesive.

(評価)
実施例および比較例で得られた偏光板について下記評価を行なった。
(Evaluation)
The following evaluation was performed about the polarizing plate obtained by the Example and the comparative example.

(接着剤層の厚み)
接着剤層の厚みは、偏光子と透明保護フィルムを貼り合せ、乾燥させたときの厚みを示している。接着剤層の厚みはTEMを用いて測定した。
(Adhesive layer thickness)
The thickness of the adhesive layer indicates the thickness when the polarizer and the transparent protective film are bonded and dried. The thickness of the adhesive layer was measured using TEM.

(外観評価:レコードスジ・クニック欠陥)
偏光板を1000mm×1000mmになるように切り出してサンプルを調製した。サンプルの偏光板を、蛍光灯下に置いた。このときにレコード状のスジがサンプル偏光板全面に視認できるものを「×」、一部視認できるものを「△」、全く視認できないものを「○」と判断した。次いで、サンプルの偏光板の光源側に別の偏光板を、それぞれの吸収軸が直行するように設置し、この状態で、光抜けする箇所(クニック欠陥)の個数をカウントした。
(Appearance evaluation: Records line / Knick defect)
A sample was prepared by cutting out the polarizing plate to be 1000 mm × 1000 mm. A sample polarizing plate was placed under a fluorescent lamp. At this time, a record-like streak that was visible on the entire surface of the sample polarizing plate was judged as “X”, a part that was partially visible as “Δ”, and a case that could not be seen at all as “◯”. Next, another polarizing plate was installed on the light source side of the polarizing plate of the sample so that the respective absorption axes were perpendicular to each other, and in this state, the number of locations where light escaped (knic defects) was counted.

(光学特性)
得られた偏光板の幅方向中央部から50mm×25mmの大きさで、偏光板の吸収軸が長辺に対して45°となるようにサンプルを切り出し、積分球式透過率測定機((株)村上色彩研究所製:DOT−3C)を用いて、単体透過率(%)、偏光度を測定した。
(optical properties)
A sample was cut out with a size of 50 mm × 25 mm from the center in the width direction of the obtained polarizing plate so that the absorption axis of the polarizing plate was 45 ° with respect to the long side, and an integrating sphere type transmittance measuring machine ((stock ) Using Murakami Color Research Laboratory: DOT-3C), single transmittance (%) and degree of polarization were measured.

(密着性)
偏光板の端部において、偏光子と透明保護フィルムとの間にカッターの刃先を挿入した。当該挿入部において、偏光子と透明保護フィルムとを掴み、それぞれ反対方向に引っ張った。このとき、偏光子および/または透明保護フィルムが破断して剥離できなかった場合は、密着性が良好:「○」と判断した。一方、偏光子と透明保護フィルムとの間で一部または全部は剥離した場合は、密着性に乏しい:「×」と判断した。
(Adhesion)
At the end of the polarizing plate, a cutter edge was inserted between the polarizer and the transparent protective film. In the insertion portion, the polarizer and the transparent protective film were gripped and pulled in opposite directions. At this time, when the polarizer and / or the transparent protective film was broken and could not be peeled off, the adhesion was judged to be good: “◯”. On the other hand, when a part or all peeled between the polarizer and the transparent protective film, the adhesion was poor: “x” was judged.

Figure 2008145692
Figure 2008145692

なお、表1中、シリカコロイドの配合量は、ポリビニルアルコール系樹脂100重量部に対する固形分の配合量(換算値)を示す。接着剤水溶液のpHは、いずれも、6.0〜8.0の範囲であった。接着剤溶液の固形分濃度は、接着剤溶液中のポリビニルアルコール系樹脂、架橋剤およびシリカコロイドの割合を示す。   In Table 1, the compounding amount of the silica colloid indicates the compounding amount (converted value) of the solid content with respect to 100 parts by weight of the polyvinyl alcohol resin. The pH of the aqueous adhesive solution was in the range of 6.0 to 8.0. The solid content concentration of the adhesive solution indicates the ratio of the polyvinyl alcohol-based resin, the crosslinking agent, and the silica colloid in the adhesive solution.

表1より、実施例の偏光板は、密着性がよく、レコードスジの発生が抑えられていることが分かる。また、クニック欠陥を抑えられることが分かる。   From Table 1, it can be seen that the polarizing plates of the examples have good adhesion and suppress the occurrence of record streaks. It can also be seen that knick defects can be suppressed.

Claims (8)

偏光子の少なくとも片面に透明保護フィルムを設けるために用いる偏光板用接着剤であって、
前記偏光板用接着剤は、ポリビニルアルコール系樹脂、架橋剤および平均粒子径が1〜100nmのシリカコロイドを含有してなる樹脂溶液であり、かつ、
シリカコロイドは、ポリビニルアルコール系樹脂100重量部に対して、200重量部以下の割合で配合されていることを特徴とする偏光板用接着剤。
An adhesive for polarizing plates used to provide a transparent protective film on at least one side of a polarizer,
The polarizing plate adhesive is a resin solution comprising a polyvinyl alcohol-based resin, a crosslinking agent, and a silica colloid having an average particle diameter of 1 to 100 nm, and
Silica colloid is blended at a ratio of 200 parts by weight or less with respect to 100 parts by weight of a polyvinyl alcohol-based resin.
架橋剤が、メチロール基を有する化合物を含有することを特徴とする請求項1記載の偏光板用接着剤。   The adhesive for polarizing plates according to claim 1, wherein the crosslinking agent contains a compound having a methylol group. 架橋剤の配合量が、ポリビニルアルコール系樹脂100重量部に対して、10〜60重量部であることを特徴とする請求項1または2記載の偏光板用接着剤。   The adhesive for polarizing plates according to claim 1 or 2, wherein the amount of the crosslinking agent is 10 to 60 parts by weight with respect to 100 parts by weight of the polyvinyl alcohol resin. 偏光子の少なくとも一方の面に、接着剤層を介して透明保護フィルムが設けられている偏光板において、前記接着剤層が請求項1〜3のいずれかに記載の偏光板用接着剤により形成されていることを特徴とする偏光板。   In the polarizing plate by which the transparent protective film is provided in the at least one surface of the polarizer through the adhesive bond layer, the said adhesive bond layer is formed with the adhesive agent for polarizing plates in any one of Claims 1-3. A polarizing plate characterized by being made. 接着剤層の厚みが、10〜300nmであり、かつ、接着剤層の厚みは、偏光板用接着剤に含有されているシリカコロイドの平均粒子径よりも大きいことを特徴とする請求項4記載の偏光板。   The thickness of an adhesive bond layer is 10-300 nm, and the thickness of an adhesive bond layer is larger than the average particle diameter of the silica colloid contained in the adhesive agent for polarizing plates. Polarizing plate. 偏光子の少なくとも一方の面に、接着剤層を介して透明保護フィルムが設けられている請求項4または5記載の偏光板を製造する方法であって、
請求項1〜3のいずれかに記載の偏光板用接着剤を調製する工程、偏光子の前記接着剤層を形成する面および/または透明保護フィルムの前記接着剤層を形成する面に前記偏光板用接着剤を塗布する工程、偏光子と透明保護フィルムとを貼り合わせる工程を有することを特徴とする偏光板の製造方法。
A method for producing a polarizing plate according to claim 4 or 5, wherein a transparent protective film is provided on at least one surface of the polarizer via an adhesive layer,
The process of preparing the adhesive agent for polarizing plates in any one of Claims 1-3, the surface which forms the said adhesive bond layer of a polarizer, and / or the surface which forms the said adhesive bond layer of a transparent protective film The manufacturing method of the polarizing plate characterized by having the process of apply | coating the adhesive agent for plates, and the process of bonding a polarizer and a transparent protective film.
請求項4または5記載の偏光板が、少なくとも1枚積層されていることを特徴とする光学フィルム。   6. An optical film, wherein at least one polarizing plate according to claim 4 or 5 is laminated. 請求項4もしくは5記載の偏光板または請求項7記載の光学フィルムが用いられていることを特徴とする画像表示装置。   An image display device comprising the polarizing plate according to claim 4 or 5 or the optical film according to claim 7.
JP2006332171A 2006-12-08 2006-12-08 Adhesive for polarizing plate, polarizing plate, method for producing the same, optical film, and image display device Expired - Fee Related JP4594290B2 (en)