JP2008139717A - Hologram label - Google Patents

Hologram label Download PDF

Info

Publication number
JP2008139717A
JP2008139717A JP2006327699A JP2006327699A JP2008139717A JP 2008139717 A JP2008139717 A JP 2008139717A JP 2006327699 A JP2006327699 A JP 2006327699A JP 2006327699 A JP2006327699 A JP 2006327699A JP 2008139717 A JP2008139717 A JP 2008139717A
Authority
JP
Japan
Prior art keywords
layer
hologram
label
liquid crystal
metal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
JP2006327699A
Other languages
Japanese (ja)
Inventor
Takuo Ohata
拓郎 大畑
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dai Nippon Printing Co Ltd
Original Assignee
Dai Nippon Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dai Nippon Printing Co Ltd filed Critical Dai Nippon Printing Co Ltd
Priority to JP2006327699A priority Critical patent/JP2008139717A/en
Publication of JP2008139717A publication Critical patent/JP2008139717A/en
Withdrawn legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide a hologram with variable colors by means of a liquid crystal layer and with metallic gloss, and to provide a hologram label that maintains hologram effect, without inducing electrical corrosion in the label and that does not have significant degradation in the appearance, even if the label is transferred to a transfer material including a metal layer, and that is bright and superior in decorative properties and/or security properties. <P>SOLUTION: The hologram level is such that the label comprises a liquid crystal layer 45, a base material 11, a hologram layer 15, a transparent reflecting layer 17, a patterned high luminance ink layer 18 containing metal vapor-deposited film chips surface-treated with at least an organic fatty acid, methylsilylisocyanate or a cellulose derivative, and a black tacky layer 19; the label maintains hologram effect without inducing electrical corrosion, even if the label is stuck to a transfer body including a metal layer; the transparent reflecting layer 17 is made of titanium oxide; and all the layers, constituting the hologram label, have the surface resistivity prescribed by JIS-K6911 as being 10<SP>12</SP>Ω or higher. <P>COPYRIGHT: (C)2008,JPO&INPIT

Description

本発明は、ホログラムラベルに関し、さらに詳しくは、液晶層による色彩可変、金属光沢の明るいホログラム、かつ、金属層を含む被転写体へ転写した場合にも外観の著しい劣化がなく、明るく、意匠性及び/又はセキュリティ性の優れるホログラムラベルに関するものである。   The present invention relates to a hologram label, and more specifically, a color changeable by a liquid crystal layer, a bright hologram with a metallic luster, and a bright, designable property without significant deterioration in appearance even when transferred to a transferred material including a metal layer. And / or a hologram label with excellent security.

本明細書において、配合を示す「比」、「部」、「%」などは特に断わらない限り質量基準であり、「/」印は一体的に積層されていることを示す。また、「PET」は「ポリエチレンテレフタレート」、「スタンパ」は「金型」、「UV」は「紫外線」の略語、機能的表現、通称、又は業界用語である。   In the present specification, “ratio”, “part”, “%” and the like indicating the composition are based on mass unless otherwise specified, and the “/” mark indicates that they are integrally laminated. “PET” is an abbreviation, functional expression, common name, or industry term for “polyethylene terephthalate”, “stamper” for “mold”, and “UV” for “ultraviolet light”.

(主なる用途)本発明のホログラムラベルの主なる用途としては、被転写体へ貼着して用いる、クレジツトカード、証書等の金券類、証明書等、社員証、会員証、学生証などのIDカード、ギフト券、入場証、通行証、サービスポイントなどの、一定の金額を払い込んだ(プリペイドという)権利や資格などを証明する媒体や、本の表紙、パンフレツト、レコードジヤケツト、パツケージ、衣類、日用品等などの、意匠性及び/又はセキュリティ性を必要とするものである。しかしながら、意匠性及び/又はセキュリティ性を必要とする被転写体へ貼着する用途であれば、特に限定されるものではない。   (Main use) The main use of the hologram label of the present invention is such as credit cards, certificates such as certificates, certificates, etc., employee cards, membership cards, student cards, etc. ID card, gift certificate, admission card, pass card, service point, etc., media that proves the right and qualification (paid prepaid), a book cover, pamphlet, record jacket, package, clothing, It requires design and / or security such as daily necessities. However, it is not particularly limited as long as it is an application to be applied to a transfer target requiring design and / or security.

(背景技術)従来、ホログラムラベルは、真空成膜法で金属の薄膜を全面に形成して反射層とした金属光沢のホログラムが知られている。しかしながら、金属反射層では銀色金属光沢に極めて明るいホログラムが提供されているが、金属層を含む被転写体へ貼着した場合に、金属薄膜の反射層が電気的腐食を受けて、反射が部分的になったり、反射率が低下し、表面にムラが発生して光が乱反射してホログラムが白化したり、ホログラム効果が減じて、外観が著しく劣化し、時には全くホログラムが観察できなくなってしまうという問題があった。反射層としては、通常、銀色で金属光沢に優れるアルミニウムの薄膜が用いられるが、該アルミニウムの薄膜の厚さは100〜500nm程度と極めて薄く、またイオン化傾向も高く、電気的腐食を受けやすく、汗、食品や薬品などで酸性のものが影響する環境では特に著しい。消失、ムラの発生や、白化して、ホログラム効果が減じて、外観が著しく劣化し、時には全くホログラムが観察できなくなってしまう。
従って、ホログラムラベルは、金属層を含む被転写体へ転写した場合に、欠落、ムラ、や白化がなく、外観に著しい劣化がなく、明るく、意匠性及び/又はセキュリティ性の優れるホログラムを貼着できるホログラムラベルが求められている。
(Background Art) Conventionally, as a hologram label, a metal gloss hologram is known in which a metal thin film is formed on the entire surface by a vacuum film forming method to form a reflective layer. However, the metal reflection layer provides a very bright hologram with silver metallic luster. However, when the metal reflection layer is attached to a transfer object including the metal layer, the reflection layer of the metal thin film is subjected to electrical corrosion, and the reflection is partially reflected. , The reflectance decreases, unevenness occurs on the surface, light is irregularly reflected and the hologram is whitened, the hologram effect is reduced, the appearance is significantly deteriorated, and sometimes the hologram cannot be observed at all There was a problem. As the reflective layer, an aluminum thin film having a silver color and excellent metallic luster is usually used, but the thickness of the aluminum thin film is very thin, about 100 to 500 nm, and also has a high ionization tendency and is susceptible to electrical corrosion. This is especially true in environments where acidic substances such as sweat, food and medicine are affected. Disappearance, occurrence of unevenness, whitening, the hologram effect is reduced, the appearance is remarkably deteriorated, and sometimes the hologram cannot be observed at all.
Therefore, when the hologram label is transferred to a transfer object including a metal layer, a hologram having no omission, unevenness, whitening, no significant deterioration in appearance, bright, and excellent design and / or security is pasted. There is a need for hologram labels that can be made.

(先行技術)従来、ホログラムラベルは、真空成膜法で金属薄膜の全面反射層を設けるものが知られている(例えば、特許文献1参照。)。しかしながら、金属反射層では銀色金属光沢による明るいホログラムが得られるが、ホログラムラベルを用いて金属層を含む被転写体へホログラムを貼着すると、被転写体の金属層の影響で、ラベルの金属層が電気的な腐食を受けて、反射が部分的になったり、反射率が低下したり、表面にムラが発生して光が乱反射してホログラムが白化したりして、ホログラム効果が減じて、外観が著しく劣化し、時には全くホログラムが観察できなくなってしまう。
また、本出願人は、反射層として高輝度インキ層を用いたもの、及び透明反射層と高輝度インキ層を併用したものを開示している(例えば、特許文献2参照。)。しかしながら、反射層として高輝度インキ層のみを用いたものでは、実用上支障は少ないものの金属反射層並みの光回折効果が得られず、また、透明反射層と高輝度インキ層を併用したものについては、電気的な腐食に対する劣化の記載はなく、透明反射層と高輝度インキ層との併用で、上記の欠点の解消を図ったものである。
さらに、本出願人は、ホログラムとコレステリック液晶印刷を施したスレッドを抄き込んだ偽造防止用紙を開示している(例えば、特許文献3参照。)。しかしながら、透明反射層と黒印刷とを用いているので、金属層を含む被転写体へ転写した場合にも、電気的な腐食は受けないが、液晶層による色彩可変状態はよいものの、明るく金属層光沢のあるホログラムは観察できないという欠点がある。
(Prior Art) Conventionally, a hologram label is known in which a full-surface reflective layer of a metal thin film is provided by a vacuum film forming method (see, for example, Patent Document 1). However, a bright hologram with silver metallic luster can be obtained with a metallic reflective layer. However, when a hologram is attached to a transfer target including a metal layer using a hologram label, the metal layer of the label is affected by the metal layer of the transfer target. Is subject to electrical corrosion, the reflection becomes partial, the reflectance decreases, the surface is uneven, the light is irregularly reflected and the hologram is whitened, the hologram effect is reduced, The appearance is significantly degraded and sometimes the hologram cannot be observed at all.
Further, the present applicant discloses one using a high-brightness ink layer as a reflection layer and one using a transparent reflection layer and a high-brightness ink layer in combination (for example, see Patent Document 2). However, in the case of using only a high-brightness ink layer as a reflection layer, although there is little practical problem, the light diffraction effect equivalent to that of a metal reflection layer cannot be obtained, and a combination of a transparent reflection layer and a high-brightness ink layer There is no description of deterioration with respect to electrical corrosion, and the above-mentioned drawbacks are solved by using a transparent reflective layer and a high-brightness ink layer in combination.
Further, the present applicant has disclosed a forgery prevention paper in which a hologram and a thread subjected to cholesteric liquid crystal printing are incorporated (see, for example, Patent Document 3). However, since a transparent reflective layer and black printing are used, even when transferred to a transfer medium including a metal layer, it is not electrically corroded, but although the color change state by the liquid crystal layer is good, it is bright and metal There is a drawback that holograms with layer gloss cannot be observed.

特許第2877968号公報Japanese Patent No. 2877968 特開2003−285599号公報JP 2003-285599 A 特開2005−325482号公報JP 2005-325482 A

そこで、本発明は上記のような問題点を解消するために、本発明者らは鋭意研究を進め、本発明の完成に至ったものである。その目的は、液晶層による色彩可変、金属光沢の明るいホログラム、かつ、金属層を含む被転写体へ転写した場合にも、ラベルに電気的腐食が発生せずホログラム効果が維持され、外観の著しい劣化がなく、明るく、意匠性及び/又はセキュリティ性の優れるホログラムラベルを提供することである。   In order to solve the above-described problems, the present inventors have made extensive studies and have completed the present invention. Its purpose is to change the color with the liquid crystal layer, bright hologram with metallic luster, and even when transferred to the transfer object including the metal layer, the label does not cause electrical corrosion and the hologram effect is maintained, and the appearance is remarkable. It is an object of the present invention to provide a holographic label that is bright and has good design and / or security without deterioration.

上記の課題を解決するために、請求項1の発明に係わるホログラムラベルは、基材と、該基材の一方の面に、少なくともホログラム層、透明反射層、高輝度インキ層及び粘着層が順に積層され、前記基材の他方の面に液晶層を有するホログラムラベルであって、前記高輝度インキ層が少なくとも有機脂肪酸、メチルシリルイソシアネート又はセルロース誘導体で表面処理した金属蒸着膜細片を含み、かつパターン状であり、前記粘着層が黒色であり、かつ、前記ホログラムラベルを金属層を含む被転写体へ貼着しても、前記ホログラムラベルに電気的腐食が発生せずホログラム効果が維持されるように、したものである。
請求項2の発明に係わるホログラムラベルは、上記透明反射層が酸化チタンであるように、したものである。
請求項3の発明に係わるホログラムラベルは、上記ラベルを構成するすべての層のJIS−K6911で定める表面抵抗率が1012Ω以上であるように、したものである。
In order to solve the above-mentioned problems, a hologram label according to the invention of claim 1 includes a base material, and at least a hologram layer, a transparent reflection layer, a high-brightness ink layer, and an adhesive layer in order on one surface of the base material. A hologram label laminated and having a liquid crystal layer on the other surface of the substrate, wherein the high-brightness ink layer comprises at least a metal vapor-deposited film piece surface-treated with an organic fatty acid, methylsilyl isocyanate or a cellulose derivative; and Even if the adhesive layer has a pattern shape, the adhesive layer is black, and the hologram label is attached to a transfer target including a metal layer, the hologram label is not corroded and the hologram effect is maintained. As you can see.
The hologram label according to the invention of claim 2 is such that the transparent reflection layer is made of titanium oxide.
The hologram label according to the invention of claim 3 is such that the surface resistivity defined by JIS-K6911 of all the layers constituting the label is 10 12 Ω or more.

請求項1の本発明によれば、液晶層による色彩可変状態と、金属光沢の明るいホログラムとが同時に観察され、かつ、金属層を含む被転写体へ転写した場合にも、ラベルに電気的腐食が発生せずホログラム効果が維持され、外観の著しい劣化がなく、明るく、意匠性及び/又はセキュリティ性の優れるホログラムラベルが提供される。
請求項2〜3の本発明によれば、より明るく、意匠性及び/又はセキュリティ性の優れるホログラムを貼着できるホログラムラベルが提供される。
According to the first aspect of the present invention, even when the color-variable state by the liquid crystal layer and the bright hologram with metallic luster are observed at the same time and transferred to the transfer object including the metallic layer, the electric corrosion is applied to the label. The hologram effect is maintained, the hologram effect is maintained, the appearance is not significantly deteriorated, the hologram label is bright, and has excellent design and / or security.
According to the second to third aspects of the present invention, there is provided a hologram label on which a brighter hologram having excellent design and / or security can be attached.

以下、本発明の実施形態について、図面を参照しながら、詳細に説明する。
図1は、本発明の1実施例を示すホログラムラベルの断面図である。
図2は、金属層を含む被転写体へホログラムラベルを貼着した断面図である。
Hereinafter, embodiments of the present invention will be described in detail with reference to the drawings.
FIG. 1 is a sectional view of a hologram label showing one embodiment of the present invention.
FIG. 2 is a cross-sectional view in which a hologram label is attached to a transfer target including a metal layer.

(ホログラムラベル)本発明のホログラムラベル1は、図1に示すように、基材11と、該基材11の一方の面に、ホログラム層15、透明反射層17、高輝度インキ層18、プライマ層21、及び粘着層19が順に積層され、基材11の他方の面に液晶層41を有したもので、ハードコート層45/液晶層41/基材11/ホログラム層15/透明反射層17/高輝度インキ層18/プライマ層21/粘着層19の層構成とし、高輝度インキ層18がパターン状であり、粘着層19が黒色である。必要に応じて、液晶層41面へハードコート層45を設けたり、ハードコート層45と液晶層41との間にプライマ層を設けたり、粘着層19面へ剥離紙を剥離可能に設け設けたり、してもよい。   (Hologram Label) As shown in FIG. 1, the hologram label 1 of the present invention has a base material 11 and a hologram layer 15, a transparent reflection layer 17, a high brightness ink layer 18, a primer on one surface of the base material 11. The layer 21 and the adhesive layer 19 are sequentially laminated, and the liquid crystal layer 41 is provided on the other surface of the base material 11. The hard coat layer 45 / the liquid crystal layer 41 / the base material 11 / the hologram layer 15 / the transparent reflective layer 17. The high luminance ink layer 18 / primer layer 21 / adhesive layer 19 is layered, and the high luminance ink layer 18 has a pattern and the adhesive layer 19 is black. If necessary, a hard coat layer 45 is provided on the surface of the liquid crystal layer 41, a primer layer is provided between the hard coat layer 45 and the liquid crystal layer 41, or a release paper is provided on the adhesive layer 19 so as to be peelable. , You may.

本発明のホログラムラベル1は、ホログラム層15、透明反射層17、パターン状の高輝度インキ層18、黒色の粘着層19、及び液晶層41を必須としている。高輝度インキ層18は少なくとも有機脂肪酸、メチルシリルイソシアネート、又はセルロース誘導体で表面処理した金属蒸着膜細片を含有させる。また、好ましくは透明反射層17は酸化チタンの薄膜を用い、さらに、構成するすべての層のJIS−K6911で定める表面抵抗率を106Ω以上、好ましくは108Ω以上、さらに好ましくは1012Ω以上とする。 The hologram label 1 of the present invention includes the hologram layer 15, the transparent reflection layer 17, the patterned high-brightness ink layer 18, the black adhesive layer 19, and the liquid crystal layer 41. The high-brightness ink layer 18 contains at least metal vapor-deposited film strips surface-treated with an organic fatty acid, methylsilyl isocyanate, or a cellulose derivative. Preferably, the transparent reflective layer 17 uses a titanium oxide thin film, and the surface resistivity defined by JIS-K6911 of all the constituent layers is 10 6 Ω or more, preferably 10 8 Ω or more, more preferably 10 12. Ω or more.

ホログラム層15と透明反射層17とパターン状の高輝度インキ層18との相乗効果で明るい部分(図柄)ホログラムとなり、液晶層41はパターン状の高輝度インキ層18のない部分では黒色の粘着層19が背景となって、該粘着層19の色彩可変状態がハッキリ観察することができるのである。そして、金属層103を含む被転写体100へホログラムを貼着しても、被転写体100に金属層103を含むが、ラベルには導電性の層を含まず、しかもホログラムラベルのすべての層が表面抵抗率の高い層で構成されているので、金属層103との間で電気的な腐食を受けず、ホログラム効果が維持されるので、反射が部分的になったり、反射率が低下したり、表面にムラが発生して光が乱反射してホログラムが白化したりして、ホログラム効果が減ずることがなく、明るいホログラムを観察することができる。透明反射層17に耐熱性が高い酸化チタンを用いることで、例え若干のひび割れ(クラック)が入っても透明で目立たず、クラック部分の反射性はその下部の高輝度インキ層18の反射で代替され反射性が維持されているために、明るいホログラムを観察することができる。   The hologram layer 15, the transparent reflective layer 17, and the patterned high-brightness ink layer 18 produce a bright portion (design) hologram due to the synergistic effect, and the liquid crystal layer 41 is a black adhesive layer in the portion without the patterned high-brightness ink layer 18. With 19 as a background, the color variable state of the adhesive layer 19 can be clearly observed. Even if the hologram is attached to the transfer target 100 including the metal layer 103, the transfer target 100 includes the metal layer 103, but the label does not include a conductive layer, and all the layers of the hologram label are included. Is composed of a layer having a high surface resistivity, so that it is not subject to electrical corrosion with the metal layer 103 and the hologram effect is maintained, so that the reflection becomes partial or the reflectance decreases. Or the surface is uneven, the light is irregularly reflected and the hologram is whitened, and the hologram effect is not reduced, and a bright hologram can be observed. By using titanium oxide with high heat resistance for the transparent reflective layer 17, even if some cracks (cracks) enter, it is transparent and not conspicuous, and the reflectivity of the crack part is replaced by the reflection of the high brightness ink layer 18 below it In addition, since the reflectivity is maintained, a bright hologram can be observed.

また、ホログラム層15/透明反射層17/パターン状の高輝度インキ層18とすることで、ホログラムもパターン状に観察できるようになる。従来、パターン状ホログラムを作成するには、水溶性のレジストインキでパターン状に印刷し、該印刷面に全面の金属反射層を設けた後に、水などの溶媒でレジストインキを溶解すると、レジストインキのない部分の金属反射層のみが残ることで行われ、工程が多く、廃液処理もあり、高コストであった。しかし本発明によれば、その製造についても、従来の真空成膜法による酸化チタン薄膜による透明反射層以外は、既存設備での印刷法により形成可能で、小ロット生産にも対応でき、低コストで生産することができる。   Moreover, the hologram can be observed in a pattern by using the hologram layer 15 / transparent reflection layer 17 / patterned high-brightness ink layer 18. Conventionally, in order to create a patterned hologram, after printing in a pattern with a water-soluble resist ink, providing a metal reflective layer on the entire print surface, and then dissolving the resist ink in a solvent such as water, the resist ink This was performed by leaving only the metal reflection layer in a portion without any gap, and there were many steps, waste liquid treatment was also required, and the cost was high. However, according to the present invention, other than the transparent reflective layer made of a titanium oxide thin film formed by the conventional vacuum film forming method, it can be formed by a printing method using existing equipment, and can be produced in a small lot, with a low cost. Can be produced in

(基材)基材11としては、用途に応じて種々の材料が適用できる。例えば、ポリエチレンテレフタレート、ポリエチレンナフタレートなどのポリエステル系樹脂、ナイロン6などのポリアミド系樹脂、ポリプロピレンなどのポリオレフィン系樹脂、環状ポリオレフィン系樹脂、ポリ塩化ビニルなどのビニル系樹脂、ポリメチルメタアクリレートなどのアクリル系樹脂、イミド系樹脂、ポリカーボネート、ABS樹脂などのスチレン系樹脂、セルローストリアセテートなどのセルロース系フィルム、などがある。該基材11は、これら樹脂を主成分とする共重合樹脂、または、混合体(アロイでを含む)、若しくは複数層からなる積層体であっても良い。また、該基材11は、延伸フィルムでも、未延伸フィルムでも良いが、強度を向上させる目的で、一軸方向または二軸方向に延伸したフィルムが好ましい。該転写基材21の厚さは、通常、2.5〜100μm程度が適用できるが、4〜50μmが好適で、6〜25μmが最適である。   (Substrate) As the substrate 11, various materials can be applied depending on the application. For example, polyester resins such as polyethylene terephthalate and polyethylene naphthalate, polyamide resins such as nylon 6, polyolefin resins such as polypropylene, cyclic polyolefin resins, vinyl resins such as polyvinyl chloride, acrylics such as polymethyl methacrylate, etc. Examples thereof include styrene-based resins such as cellulose resins, imide resins, polycarbonates, and ABS resins, and cellulose films such as cellulose triacetate. The substrate 11 may be a copolymer resin containing these resins as a main component, a mixture (including an alloy), or a laminate composed of a plurality of layers. The substrate 11 may be a stretched film or an unstretched film, but a film stretched in a uniaxial direction or a biaxial direction is preferable for the purpose of improving the strength. The thickness of the transfer substrate 21 is usually about 2.5 to 100 μm, preferably 4 to 50 μm, and most preferably 6 to 25 μm.

該基材11は、これら樹脂の少なくとも1層からなるフィルム、シート、ボード状として使用する。通常は、ポリエチレンテレフタレート、ポリエチレンナフタレート等のポリエステル系のフィルムが、強度、耐熱性、価格面でバランスがよく、好適に使用され、特にポリエチレンテレフタレートが最適である。   The substrate 11 is used as a film, sheet or board formed of at least one layer of these resins. Usually, polyester-based films such as polyethylene terephthalate and polyethylene naphthalate have good balance in terms of strength, heat resistance and price, and are preferably used. Polyethylene terephthalate is particularly optimal.

該基材11は、塗布に先立って塗布面へ、コロナ放電処理、プラズマ処理、オゾン処理、フレーム処理、プライマー(アンカーコート、接着促進剤、易接着剤とも呼ばれる)塗布処理、予熱処理、除塵埃処理、蒸着処理、アルカリ処理、などの易接着処理を行ってもよい。また、該樹脂フィルムは、必要に応じて、充填剤、可塑剤、着色剤、帯電防止剤などの添加剤を加えても良い。   Prior to coating, the substrate 11 is applied to the coated surface by corona discharge treatment, plasma treatment, ozone treatment, flame treatment, primer (also called anchor coat, adhesion promoter, or easy adhesive) coating treatment, pre-heat treatment, dust removal. Easy adhesion treatment such as treatment, vapor deposition treatment, and alkali treatment may be performed. Moreover, you may add additives, such as a filler, a plasticizer, a coloring agent, and an antistatic agent, to this resin film as needed.

(ホログラム層)ホログラム層15としては、無色または着色された透明または半透明なもので、単層であっても多層状であってもよく、凹凸を注型や型押しで再現できる熱可塑性樹脂、硬化性樹脂、あるいは、光回折パターン情報に応じて硬化部と未硬化部とを成形することができる感光性樹脂組成物が利用できる。具体的には、例えば、ポリ塩化ビニル、アクリル(ポリメチルメタクリレート)、ポリスチレン、またはポリカーボネート等の熱可塑性樹脂、不飽和ポリエステル、メラミン、エポキシ、ポリエステル(メタ)アクリレート、ウレタン(メタ)アクリレート、エポキシ(メタ)アクリレート、ポリエーテル(メタ)アクリレート、ポリオール(メタ)アクリレート、メラミン(メタ)アクリレート、またはトリアジン系アクリレート等の熱硬化性樹脂であり、それぞれの単独、熱可塑性樹脂どうし、または熱硬化性樹脂同志の混合、もしくは熱可塑性樹脂と熱硬化性樹脂の混合等であってもよい。ラジカル重合性不飽和基を有し、熱成形性を有するものや、ラジカル重合性不飽和モノマーを添加した電離放射線硬化性樹脂組成物も利用できる。
電離放射線硬化樹脂としては、例えば、エポキシ変性アクリレート樹脂、ウレタン変性アクリレート樹脂、アクリル変性ポリエステル等が適用でき、好ましくはウレタン変性アクリレート樹脂である。
(Hologram layer) The hologram layer 15 is colorless or colored, transparent or translucent, and may be a single layer or a multilayer, and a thermoplastic resin capable of reproducing irregularities by casting or embossing. A curable resin or a photosensitive resin composition capable of forming a cured portion and an uncured portion according to light diffraction pattern information can be used. Specifically, for example, thermoplastic resins such as polyvinyl chloride, acrylic (polymethyl methacrylate), polystyrene, or polycarbonate, unsaturated polyester, melamine, epoxy, polyester (meth) acrylate, urethane (meth) acrylate, epoxy ( It is a thermosetting resin such as (meth) acrylate, polyether (meth) acrylate, polyol (meth) acrylate, melamine (meth) acrylate, or triazine acrylate, each of which is a single, a thermoplastic resin, or a thermosetting resin. It may be a mixture of comrades or a mixture of a thermoplastic resin and a thermosetting resin. An ionizing radiation curable resin composition having a radically polymerizable unsaturated group and having thermoformability or a radically polymerizable unsaturated monomer added can also be used.
As the ionizing radiation curable resin, for example, an epoxy-modified acrylate resin, a urethane-modified acrylate resin, an acrylic-modified polyester, and the like can be applied, and a urethane-modified acrylate resin is preferable.

また、好ましくは、ホログラム層15の材料としては、(1)分子中にイソシアネート基を3個以上有するイソシアネート類、(2)分子中に水酸基を少なくとも1個と(メタ)アクリロイルオキシ基を少なくとも2個有する多官能(メタ)アクリレート類、又は(3)分子中に水酸基を少なくとも2個有する多価アルコール類の反応生成物であるウレタン(メタ)アクリレートオリゴマーを含有する電離放射線硬化性樹脂(本明細書では「電離放射線硬化性樹脂組成物M」と呼称する)、反応性シリコーン及びポリエチレンワックスを含むようにする。さらに好ましくは、(メタ)アクリレートオリゴマーも含ませて硬化させる。該組成物を塗布し乾燥して、ホログラム機能を発現する微細な凹凸レリーフを賦型した後に、電離放射線で硬化させればよい。電離放射線硬化性樹脂は架橋性樹脂ともいわれ、他の層でも同様である。   Preferably, the material of the hologram layer 15 includes (1) an isocyanate having three or more isocyanate groups in the molecule, and (2) at least one hydroxyl group and at least two (meth) acryloyloxy groups in the molecule. Ionizing radiation curable resin containing urethane (meth) acrylate oligomer which is a reaction product of polyfunctional (meth) acrylates having one or polyhydric alcohols having at least two hydroxyl groups in the molecule (this specification) (Referred to as “ionizing radiation curable resin composition M”), reactive silicone and polyethylene wax. More preferably, a (meth) acrylate oligomer is also included and cured. What is necessary is just to harden with ionizing radiation, after apply | coating this composition and drying and shaping | molding the fine unevenness | corrugation relief which expresses a hologram function. The ionizing radiation curable resin is also called a crosslinkable resin, and the same applies to other layers.

(電離放射線硬化性樹脂組成物M)「電離放射線硬化性樹脂組成物M」としては、ウレタン(メタ)アクリレートオリゴマーを含有する電離放射線硬化性樹脂の硬化物、具体的には、特開2001−329031号公報で開示されている光硬化性樹脂などが例示でき、実施例でも述べる。即ち、「電離放射線硬化性樹脂組成物M」(1)分子中にイソシアネート基を3個以上有するイソシアネート類、(2)分子中に水酸基を少なくとも1個と(メタ)アクリロイルオキシ基を少なくとも2個有する多官能(メタ)アクリレート類、又は(3)分子中に水酸基を少なくとも2個有する多価アルコール類の反応生成物である。   (Ionizing radiation curable resin composition M) The “ionizing radiation curable resin composition M” is a cured product of an ionizing radiation curable resin containing a urethane (meth) acrylate oligomer. The photocurable resin etc. which are indicated by 329031 gazette can be illustrated, and it mentions also in an example. That is, “ionizing radiation curable resin composition M” (1) isocyanates having 3 or more isocyanate groups in the molecule, (2) at least one hydroxyl group and at least two (meth) acryloyloxy groups in the molecule Reaction product of polyfunctional (meth) acrylates having, or (3) polyhydric alcohols having at least two hydroxyl groups in the molecule.

((メタ)アクリレートオリゴマー)(メタ)アクリレートオリゴマーとしては、耐熱性のあるオリゴマーであればよく、例えば、日本合成化学社の商品名;紫光6630B、7510B、7630Bなどが例示できる。   ((Meth) acrylate oligomer) The (meth) acrylate oligomer may be a heat-resistant oligomer, and examples thereof include trade names of Nippon Synthetic Chemical Co., Ltd .; Purple light 6630B, 7510B, 7630B and the like.

(ポリエチレンワックス)ポリエチレンワックスとしては、ポリエチレン系樹脂の粒子やビーズが挙げられるが、好ましくは球状ビーズである。但し、ポリエチレンワックスを添加すると、箔切れ性は低下するので、その添加量は、電離放射線硬化樹脂100質量部に対して、0.01〜10質量部程度、好ましくは0.1〜5質量部とする。   (Polyethylene wax) Polyethylene wax includes polyethylene resin particles and beads, and is preferably spherical beads. However, when polyethylene wax is added, the foil breakage is reduced, so the amount added is about 0.01 to 10 parts by weight, preferably 0.1 to 5 parts by weight, with respect to 100 parts by weight of ionizing radiation curable resin. And

(反応性シリコーン)反応性シリコーンとしては、電離放射線で硬化時に樹脂と反応し結合して一体化するもので、アクリル変性、メタクリル変性、又はエポキシ変性などで変性した反応性シリコーンで、該反応性シリコーンを含有させる質量基準での割合としては「電離放射線硬化性樹脂組成物M」100に対して、0.1〜10部程度、好ましくは0.3〜5部である。この範囲未満ではレリーフの賦型時にプレススタンパとの剥離が不十分であり、プレススタンパの汚染を防止することが困難で賦型性が悪い。また、この範囲を超えてはホログラム層面への反射層の密着性が低く、ホログラム層と反射層との間で剥離し商品価値を失ってしまう。従来のシリコーンオイルの添加では、反射層との密着性が悪い。   (Reactive silicone) Reactive silicone is a reactive silicone that reacts with and binds with resin when cured with ionizing radiation, and is modified by acrylic, methacrylic, or epoxy modification. The ratio on the basis of mass containing silicone is about 0.1 to 10 parts, preferably 0.3 to 5 parts relative to “ionizing radiation curable resin composition M” 100. If it is less than this range, peeling from the press stamper is insufficient at the time of relief molding, and it is difficult to prevent contamination of the press stamper and the moldability is poor. Further, beyond this range, the adhesiveness of the reflective layer to the hologram layer surface is low, and the commercial value is lost by peeling between the hologram layer and the reflective layer. Addition of conventional silicone oil has poor adhesion to the reflective layer.

このように、ホログラム層15には、「電離放射線硬化性樹脂組成物M」、必要に応じて(メタ)アクリレートオリゴマー、反応性シリコーン、及びポリエチレンワックスを含ませることで、レリーフの賦型性がよく光回折効果が高く、かつ、ハードコート機能を兼ねさせることができる。特にポリエチレンワックスを含有させることで、耐擦傷性(耐スクラッチ性)が著しく向上する。   As described above, the hologram layer 15 includes the “ionizing radiation curable resin composition M”, and if necessary, (meth) acrylate oligomer, reactive silicone, and polyethylene wax, thereby providing relief moldability. It has a high light diffraction effect and can also serve as a hard coat function. In particular, by including polyethylene wax, the scratch resistance (scratch resistance) is remarkably improved.

(1)電離放射線硬化前の塗布状態のホログラム層15の塗膜は指乾状態でべとつかず、ブロッキングせずに巻き取ることができるので、ロールツーロール加工ができる。
(2)ホログラム層15へは反応性シリコーンを含ませると、塗布表面に集まりスタンパの凹凸からの剥離がよく賦型性が向上して、レリーフ構造を容易に賦型でき、賦型後には電離放射線で硬化すれば反応性シリコーンも硬化する。
(3)ポリエチレンワックスを含ませることで、転写後にはホログラム層15が最表面層となるが、極めて過酷な環境での使用、長期間にわたる使用、及び/又は多数回の繰り返し使用などでも、溶剤、機械的な摩擦、及び摩耗から被転写体に設けられた画像を保護し、傷付きにくく耐久性に優れる。
(1) Since the coated film of the hologram layer 15 in a coated state before ionizing radiation curing is not sticky in a finger dry state and can be wound up without blocking, roll-to-roll processing can be performed.
(2) When reactive silicone is included in the hologram layer 15, the relief from the unevenness of the stamper gathers on the coating surface and the moldability is improved, and the relief structure can be easily molded, and ionization is performed after molding. When cured with radiation, the reactive silicone also cures.
(3) By including polyethylene wax, the hologram layer 15 becomes the outermost surface layer after transfer, but the solvent can be used even in extremely harsh environments, for a long period of time, and / or for many repeated uses. It protects the image provided on the transfer member from mechanical friction and abrasion, is hardly scratched and has excellent durability.

(ホログラム層の形成)ホログラム層15は、上記の電離放射線硬化性樹脂、必要に応じて(メタ)アクリレートオリゴマー、反応性シリコーン、及びポリエチレンワックスを含ませ、さらに必要に応じて光重合開始剤、可塑剤、安定剤、界面活性剤等を加え、溶媒へ分散または溶解して、ロールコート、グラビアコート、コンマコート、ダイコートなどの公知のコーティング方法で塗布し乾燥して塗膜を形成したりすれば良い。ホログラム層15の厚さとしては、通常は0.5μm〜20μm程度、好ましくは1μm〜10m程度であり、複数回の塗布でもよい。   (Formation of hologram layer) The hologram layer 15 contains the above-mentioned ionizing radiation curable resin, (meth) acrylate oligomer, reactive silicone, and polyethylene wax, if necessary, and a photopolymerization initiator as necessary. Add a plasticizer, stabilizer, surfactant, etc., disperse or dissolve in a solvent, apply by a known coating method such as roll coating, gravure coating, comma coating, die coating and dry to form a coating film. It ’s fine. The thickness of the hologram layer 15 is usually about 0.5 μm to 20 μm, preferably about 1 μm to 10 m, and may be applied multiple times.

(ホログラム)次に、ホログラム層15の表面には、ホログラムなどの光回折効果の発現する所定のレリーフ構造を賦型し、硬化させる。ホログラムは物体光と参照光との光の干渉による干渉縞を凹凸のレリーフ形状で記録されたもので、例えば、フレネルホログラム等のレーザ再生ホログラム、及びレインボーホログラム等の白色光再生ホログラム、さらに、それらの原理を利用したカラーホログラム、コンピュータジェネレーティッドホログラム(CGH)、ホログラフィック回折格子などがある。レリーフ形状は凹凸形状であり、特に限定されるものではなく、微細な凹凸形状を有する光拡散、光散乱、光反射、光回折などの機能を発現するものでもよく、例えば、フーリエ変換やレンチキュラーレンズ、光回折パターン、モスアイ、が形成されたものである。また、光回折機能はないが、特異な光輝性を発現するヘアライン柄、マット柄、万線柄、干渉パターンなどでもよい。   (Hologram) Next, on the surface of the hologram layer 15, a predetermined relief structure such as a hologram that exhibits a light diffraction effect is formed and cured. A hologram is a recording of interference fringes due to the interference of light between object light and reference light in an uneven relief shape, such as a laser reproduction hologram such as a Fresnel hologram, a white light reproduction hologram such as a rainbow hologram, There are color holograms utilizing the above principle, computer generated holograms (CGH), holographic diffraction gratings and the like. The relief shape is a concavo-convex shape, and is not particularly limited, and may have a fine concavo-convex shape such as light diffusion, light scattering, light reflection, light diffraction, etc., such as Fourier transform or lenticular lens. , A light diffraction pattern, and a moth eye. Further, although it does not have a light diffraction function, it may be a hairline pattern, a mat pattern, a line pattern, an interference pattern, or the like that expresses a unique glitter.

これらのレリーフ形状の作製方法としてはホログラム撮影記録手段を利用して作製されたホログラムや回折格子の他に、干渉や回折という光学計算に基づいて電子線描画装置等を用いて作製されたホログラムや回折格子をあげることもできる。また、ヘアライン柄や万線柄のような比較的大きなパターンなどは機械切削法でもよい。これらのホログラム及び/又は回折格子の単一若しくは多重に記録しても、組み合わせて記録しても良い。これらの原版は公知の材料、方法で作成することができ、通常、感光性材料を塗布したガラス板を用いたレーザ光干渉法、電子線レジスト材料を塗布したガラス板に電子線描画装置を用いてパターン作製する電子線描画法をなどが適用できる。   As a method for producing these relief shapes, in addition to holograms and diffraction gratings produced using hologram photographing and recording means, holograms produced using an electron beam drawing device based on optical calculations such as interference and diffraction, A diffraction grating can also be mentioned. Also, a relatively large pattern such as a hairline pattern or a line pattern may be a machine cutting method. These holograms and / or diffraction gratings may be recorded single or multiple, or may be recorded in combination. These original plates can be prepared by known materials and methods, and usually, laser beam interference using a glass plate coated with a photosensitive material, using an electron beam drawing apparatus on a glass plate coated with an electron beam resist material. An electron beam drawing method for patterning can be applied.

(レリーフの賦型)ホログラム層15面へ、上記のレリーフ形状を賦形(複製ともいう)する。ホログラムの賦型は、公知の方法によって形成でき、例えば、回折格子やホログラムの干渉縞を表面凹凸のレリーフとして記録する場合には、回折格子や干渉縞が凹凸の形で記録された原版をプレス型として用い、上記樹脂層上に前記原版を重ねて加熱ロールなどの適宜手段により、両者を加熱圧着することにより、原版の凹凸模様を複製することができる。   (Relief shaping) The relief shape is shaped (also referred to as replication) on the surface of the hologram layer 15. Hologram shaping can be formed by a known method. For example, when recording diffraction gratings or interference fringes of holograms as reliefs of surface irregularities, a master on which the diffraction gratings or interference fringes are recorded in irregularities is pressed. The concave / convex pattern of the original plate can be duplicated by using it as a mold and superimposing the original plate on the resin layer and then heat-pressing both of them with an appropriate means such as a heating roll.

(レリーフの硬化)ホログラム層15は、スタンパでエンボス中、又はエンボス後に、電離放射線を照射して、電離放射線硬化性樹脂を硬化させる。上記の電離放射線硬化性樹脂は、レリーフを形成後に、電離放射線を照射して硬化(反応)させると電離放射線硬化樹脂(ホログラム層15)となる。電離放射線としては、電磁波が有する量子エネルギーで区分する場合もあるが、本明細書では、すべての紫外線(UV‐A、UV‐B、UV‐C)、可視光線、ガンマー線、X線、電子線を包含するものと定義する。従って、電離放射線としては、紫外線(UV)、可視光線、ガンマー線、X線、または電子線などが適用できるが、紫外線(UV)が好適である。電離放射線で硬化する電離放射線硬化性樹脂は、紫外線硬化の場合は光重合開始剤、及び/又は光重合促進剤を添加し、エネルギーの高い電子線硬化の場合は添加しないで良く、また、適正な触媒が存在すれば、熱エネルギーでも硬化できる。   (Relief Curing) The hologram layer 15 is irradiated with ionizing radiation during or after embossing with a stamper to cure the ionizing radiation curable resin. The ionizing radiation curable resin becomes an ionizing radiation curable resin (hologram layer 15) when cured (reacted) by irradiation with ionizing radiation after the relief is formed. The ionizing radiation may be classified according to the quantum energy of the electromagnetic wave, but in this specification, all ultraviolet rays (UV-A, UV-B, UV-C), visible rays, gamma rays, X-rays, electrons It is defined as including a line. Accordingly, ultraviolet (UV), visible light, gamma ray, X-ray, electron beam, or the like can be applied as ionizing radiation, but ultraviolet (UV) is preferable. An ionizing radiation curable resin that cures with ionizing radiation may contain a photopolymerization initiator and / or photopolymerization accelerator in the case of ultraviolet curing, and may not be added in the case of high energy electron beam curing. Can be cured even with thermal energy.

(レリーフの絵柄)ホログラム層15の絵柄は、特に限定されないが、個別の絵柄でも、擬似連続絵柄でもよい。擬似連続絵柄はプレス型を作成する際に、小さなレリーフ版の複数を、精度よく突合せてつなぎ目を目立たなくしたり、つなぎ目を樹脂で埋めたりすればよい。このように、擬似連続絵柄とすることで、できるだけ大きな面積、又は好ましくは全面とすることもできる。個別の絵柄の場合には絵柄と絵柄に同調した見当合わせマークを形成しておき、被転写体の所望の位置へ転写すればよい。   (Relief pattern) The pattern of the hologram layer 15 is not particularly limited, but may be an individual pattern or a pseudo-continuous pattern. When creating a press mold for the pseudo continuous pattern, a plurality of small relief plates may be matched with high accuracy so that the joints are not noticeable, or the joints are filled with resin. In this way, by using a quasi-continuous pattern, the area can be as large as possible, or preferably the entire surface. In the case of individual patterns, a registration mark synchronized with the pattern may be formed and transferred to a desired position on the transfer object.

(透明反射層)透明反射層17は、ほぼ無色透明な色相で、その光学的な屈折率がホログラム層のそれとは異なることにより、金属光沢が無いにもかかわらず、ホログラムなどの光輝性を視認できるから、透明なホログラムを作製することができる。例えば、ホログラム層15よりも光屈折率の高い薄膜、および光屈折率の低い薄膜とがあり、前者の例としては、ZnS、TiO2、Al23、Sb23、SiO、SnO2、ITO等があり、後者の例としては、LiF、MgF2、AlF3がある。好ましくは、金属酸化物又は窒化物であり、具体的には、Be、Mg、Ca、Cr、Mn、Cu、Ag、Al、Sn、In、Te、Fe、Co、Zn、Ge、Pb、Cd、Bi、Se、Ga、Rb、Sb、Pb、Ni、Sr、Ba、La、Ce、Au等の酸化物又は窒化物他はそれらを2種以上を混合したもの等が挙げられる。好ましくは、耐熱性及び屈折率差の大きい点で酸化チタン(TiO2)である。 (Transparent Reflective Layer) The transparent reflective layer 17 has a substantially colorless and transparent hue, and its optical refractive index is different from that of the hologram layer. Therefore, a transparent hologram can be produced. For example, there are a thin film having a higher refractive index than the hologram layer 15 and a thin film having a lower refractive index. Examples of the former include ZnS, TiO 2 , Al 2 O 3 , Sb 2 S 3 , SiO, SnO 2. ITO, etc., and examples of the latter include LiF, MgF 2 , and AlF 3 . Preferably, it is a metal oxide or nitride, specifically, Be, Mg, Ca, Cr, Mn, Cu, Ag, Al, Sn, In, Te, Fe, Co, Zn, Ge, Pb, Cd , Bi, Se, Ga, Rb, Sb, Pb, Ni, Sr, Ba, La, Ce, Au, and other oxides or nitrides, and the like may be a mixture of two or more thereof. Titanium oxide (TiO 2 ) is preferred because of its large heat resistance and refractive index difference.

透明金属化合物の形成は、金属の薄膜と同様、ホログラム層15のレリーフ面に、10〜2000nm程度、好ましくは20〜1000nmの厚さになるよう、蒸着、スパッタリング、イオンプレーティング、CVDなどの真空薄膜法などにより設ければよい。   The transparent metal compound is formed on the relief surface of the hologram layer 15 by vacuum such as vapor deposition, sputtering, ion plating, and CVD so that the thickness of the relief layer of the hologram layer 15 is about 10 to 2000 nm, preferably 20 to 1000 nm. It may be provided by a thin film method or the like.

(高輝度インキ層)高輝度インキ層18を透明反射層17面へ設けることにより、ホログラムの再生像および/または回折格子が明瞭に視認できるようになる。従来、金属光沢の反射層としては、通常、特殊機能を発揮させるものを除いては、真空蒸着法で形成したアルミニウムの金属薄膜が用いられてきた。他の、例えば、圧延法のアルミニウム箔では、真空薄膜法の金属薄膜ほどの金属光沢が、得られなかった。また、他の金属では、色調を帯びていたり、高コストためである。このように、真空蒸着法のアルミニウム薄膜が、実際に実用されている汎用用途では、全てと言って良いほどに、また、長期間にわたって用いられてきた。   (High-Brightness Ink Layer) By providing the high-brightness ink layer 18 on the surface of the transparent reflection layer 17, the reproduced image of the hologram and / or the diffraction grating can be clearly seen. Conventionally, an aluminum metal thin film formed by a vacuum deposition method has been used as a metallic glossy reflection layer, except for a layer that exhibits a special function. In other aluminum foils, for example, rolled, metal gloss as high as that obtained by vacuum thin film method was not obtained. In addition, other metals have a color tone or are expensive. Thus, vacuum-deposited aluminum thin films have been used over a long period of time for a wide range of practical applications.

また、従来からも、金属光沢を付与する印刷インキがあったが、該インキはアルミニウムペーストやアルミニウム粉等の金属顔料を用いた、シルバーまたはゴールド等のメタリック調印刷インキである。アルミニウムペーストには、リーフィングタイプとノンリーフィングタイプがあるが、いずれを用いても、真空薄膜法の金属薄膜の金属光沢には、はるかに及ばなかった。さらにまた、蒸着アルミニウム薄膜を粉砕した粉末を用いたインキがあったが、表面処理が異なり分散性が悪く、十分な高輝度が得られなかった。   Conventionally, there has been a printing ink that imparts a metallic luster. The ink is a metallic printing ink such as silver or gold using a metal pigment such as aluminum paste or aluminum powder. The aluminum paste has a leafing type and a non-leafing type, but using either of them did not reach the metallic luster of the metal thin film by the vacuum thin film method. Furthermore, although there was an ink using a powder obtained by pulverizing a vapor-deposited aluminum thin film, the surface treatment was different and the dispersibility was poor, and sufficient high luminance could not be obtained.

ところが、本発明では、透明反射層15、及び、少なくとも有機脂肪酸、メチルシリルイソシアネート、又はセルロース誘導体で表面処理した金属蒸着膜細片を含有させた高輝度インキを用いて印刷したメタリックインキ層(高輝度インキ層18)と併用することで、高温や曲げても白化しにくく、明るいホログラムラベルとなることを見出した。   However, in the present invention, the transparent reflective layer 15 and a metallic ink layer (high-intensity) printed using a high-brightness ink containing a metal-deposited film strip surface-treated with at least an organic fatty acid, methylsilyl isocyanate, or a cellulose derivative. It has been found that when used in combination with the brightness ink layer 18), it becomes difficult to whiten even when bent at high temperatures and becomes a bright hologram label.

該メタリックインキ層は、金属光沢様(メタリック調)を付与する印刷インキを用いた印刷層であり、少なくとも有機脂肪酸、メチルシリルイソシアネート又はセルロース誘導体で表面処理されている蒸着金属膜を粉砕した蒸着金属膜細片を含有させた高輝度インキを用いた印刷層である。印刷法なので、部分的に設けてもよく、高輝度インキ反射層を既存の印刷設備で安価に製造することができる。金属薄膜片とバインダとからなる高輝度インキを用いたメタリック印刷層17を透明反射層15面へ印刷することで、よりメタリック調の高輝度を発揮でき、光回折画像の反射層とする。また、意匠性が高く、かつ、目視で容易に真偽が判定できてセキュリティ性も高まり、小ロット生産にも対応でき、また、コストも低くできるという著しい効果を発揮する。また、高輝度インキ層18とは印刷法なので、他の印刷層があればこの印刷絵柄に同調させて、高輝度インキ層を設けることが容易である。印刷絵柄と同調するように設けることで、より一層意匠効果が高まる。部分的とは、文字、数字、記号、イラスト、模様、写真などのすべての絵柄が使用できる。   The metallic ink layer is a printing layer using a printing ink that gives a metallic luster-like appearance (metallic tone), and is a vapor-deposited metal obtained by pulverizing a vapor-deposited metal film that has been surface-treated with at least an organic fatty acid, methylsilyl isocyanate, or a cellulose derivative. It is a printing layer using the high-intensity ink containing the film strip. Since it is a printing method, it may be provided partially, and a high-brightness ink reflecting layer can be manufactured at low cost with existing printing equipment. By printing the metallic print layer 17 using a high-brightness ink composed of a metal thin film piece and a binder on the surface of the transparent reflection layer 15, it is possible to exhibit a higher metallic tone and to provide a reflection layer for a light diffraction image. In addition, it is highly designable, and it is possible to easily determine whether it is true or false by visual inspection, so that security is enhanced, small lot production can be handled, and cost can be reduced. In addition, since the high-brightness ink layer 18 is a printing method, if there is another print layer, it is easy to provide a high-brightness ink layer in synchronization with this print pattern. The design effect is further enhanced by providing the printed pattern so as to be synchronized. The term “partial” refers to all patterns such as letters, numbers, symbols, illustrations, patterns, and photographs.

また、従来の真空蒸着法で形成したアルミニウムの金属薄膜は、十分な金属光沢が得られる。しかしながら、意匠的に高めるために、部分的なアルミニウムの金属薄膜を設けるには、一旦、真空成膜法でアルミニウム金属薄膜を全面に設けた後に、別工程で、レジストを印刷しエッチングするので、コストが非常に高く、また、製造工程が多くなって小ロット生産に向かない。しかも、高温や曲げられると、白化するという欠点がある。   In addition, an aluminum metal thin film formed by a conventional vacuum deposition method can provide a sufficient metallic luster. However, in order to enhance the design, in order to provide a partial aluminum metal thin film, once the aluminum metal thin film is provided on the entire surface by a vacuum film forming method, a resist is printed and etched in a separate process. The cost is very high, and the number of manufacturing processes increases, making it unsuitable for small lot production. In addition, there is a drawback of whitening when bent at high temperatures.

(高輝度インキ)透明反射層15、及び高輝度インキ層18の2層とすることで、明るいホログラム層15の光回折画像が視認できるようになる。該高輝度インキとしては、金属蒸着膜に匹敵する金属光沢を有する高輝度インキで、金属蒸着膜細片の表面を有機脂肪酸、メチルシリルイソシアネート又はセルロース誘導体で処理して、インキ中への分散性を向上させて、インキ塗膜の金属光沢を高輝度としたものである。該インキは、有機脂肪酸、メチルシリルイソシアネート、またはセルロース誘導体で表面処理した金属蒸着膜細片、バインダ、添加剤、及び溶剤からなり、必要に応じてグラビアインキ、スクリーンインキ、又はフレキソインキ化すればよい。   (High-brightness ink) By making the transparent reflection layer 15 and the high-brightness ink layer 18 into two layers, the light diffraction image of the bright hologram layer 15 can be visually recognized. The high-brightness ink is a high-brightness ink having a metallic luster comparable to a metal vapor-deposited film. The surface of the metal vapor-deposited film strip is treated with an organic fatty acid, methylsilyl isocyanate, or a cellulose derivative, and dispersed in the ink. The metallic luster of the ink coating film is increased in brightness. The ink is composed of a metal vapor-deposited film strip treated with an organic fatty acid, methylsilyl isocyanate, or a cellulose derivative, a binder, an additive, and a solvent. If necessary, it can be converted into a gravure ink, a screen ink, or a flexo ink. Good.

金属蒸着膜細片の金属としては、アルミニウムが適用できるが、必要に応じて、金、銀、銅、真鍮、チタン、クロム、ニッケル、ニッケルクロム、ステンレス等も使用できる。金属蒸着膜の厚さは、0.01〜0.1μmが好ましく、さらに好ましくは0.03〜0.08μmであり、インキ中に分散させた金属蒸着膜細片の大きさは、5〜25μmが好ましく、さらに好ましくは10〜15μmである。大きさが、この範囲未満の場合はインキ塗膜の輝度が不十分となり、この範囲を超えると、グラビア版のセルに入りにくく、またスクリーン版が目詰まりし易く、印刷塗膜の光沢が低下する。   As the metal of the metal vapor deposited film strip, aluminum can be applied, but gold, silver, copper, brass, titanium, chromium, nickel, nickel chromium, stainless steel, etc. can also be used as necessary. The thickness of the metal vapor deposition film is preferably 0.01 to 0.1 μm, more preferably 0.03 to 0.08 μm, and the size of the metal vapor deposition film dispersed in the ink is 5 to 25 μm. Is more preferable, and it is 10-15 micrometers more preferably. If the size is less than this range, the brightness of the ink coating will be insufficient, and if it exceeds this range, it will be difficult to enter the gravure plate cell, the screen plate will be clogged easily, and the gloss of the printed coating will decrease. To do.

金属蒸着膜細片は、まず、ポリエステルフィルム/剥離層/蒸着膜/表面の酸化防止トップコート層からなる蒸着フィルムを作成する。剥離層、トップコート層は、特に限定されないが、例えば、セルロース誘導体、アクリル樹脂、塩素化ポリプロピレンなどが適用できる。上記蒸着フィルムを、溶剤中に浸積して、金属蒸着膜を剥離、撹拌、濾別、乾燥して、金属蒸着膜細片を得る。該金属蒸着膜細片を温度10〜35℃、30分程度、撹拌しながら、有機脂肪酸、メチルシリルイソシアネート又はセルロース誘導体溶液を加え、金属蒸着膜細片の表面に有機脂肪酸、メチルシリルイソシアネート又はセルロース誘導体を吸着させて、金属蒸着膜細片の表面処理を行う。セルロース誘導体としては、ニトロセルロース、セルロースアセテートプロピオネート、セルロースアセテートブチレート、エチルセルロース等が適用できる。セルロース誘導体の添加量は、金属がアルミニウムの場合は、蒸着膜細片に対して1〜20質量%が好ましい。   The metal vapor deposited film strip is first prepared as a vapor deposited film consisting of polyester film / release layer / deposited film / antioxidation top coat layer on the surface. The release layer and the topcoat layer are not particularly limited, and for example, cellulose derivatives, acrylic resins, chlorinated polypropylene, and the like can be applied. The vapor deposition film is immersed in a solvent, and the metal vapor deposition film is peeled, stirred, filtered and dried to obtain metal vapor deposition film strips. While stirring the metal vapor-deposited film strip at a temperature of 10 to 35 ° C. for about 30 minutes, an organic fatty acid, methylsilyl isocyanate or cellulose derivative solution is added, and the organic fatty acid, methylsilyl isocyanate or cellulose is added to the surface of the metal vapor-deposited film strip. The derivative is adsorbed and the surface treatment of the metal vapor deposited film strip is performed. As the cellulose derivative, nitrocellulose, cellulose acetate propionate, cellulose acetate butyrate, ethyl cellulose and the like can be applied. When the metal is aluminum, the addition amount of the cellulose derivative is preferably 1 to 20% by mass with respect to the deposited film strip.

該表面処理の後、金属蒸着膜細片を分離、又は金属蒸着膜細片スラリーをそのまま、バインダ及び溶剤へ配合、分散させてインキ化する。該バインダとしては、公知のインキ使われているものでよく、例えば、(メタ)アクリル樹脂、ポリエステル、ポリアミド、ポリウレタン、セラック、アルキッド樹脂等がある。該インキには、必要に応じて、着色用顔料、染料、ワックス、可塑剤、レベリング剤、界面活性剤、分散剤、消泡剤、キレート化剤などの添加剤を添加してもよい。インキの溶剤は、公知のインキ用溶剤を使用することができ、例えば、トルエン、キシレン等の芳香族系炭化水素、n−ヘキサン、シクロヘキサン等の脂肪族または脂環式炭化水素、酢酸エチル、酢酸プロピル等のエステル類、メタノール、エタノール、IPA等のアルコール類、アセトン、MEK等のケトン類、エチレングリコールモノエチルエーテル、プロピレングリコールモノメチルエーテル等のアルキレングリコールモノアルキルエーテル等がある。   After the surface treatment, the metal vapor-deposited film strips are separated, or the metal vapor-deposited film strip slurry is blended and dispersed in a binder and a solvent as they are to make an ink. As the binder, known inks may be used, and examples thereof include (meth) acrylic resin, polyester, polyamide, polyurethane, shellac, and alkyd resin. If necessary, additives such as coloring pigments, dyes, waxes, plasticizers, leveling agents, surfactants, dispersants, antifoaming agents, and chelating agents may be added to the ink. As the ink solvent, known ink solvents can be used, for example, aromatic hydrocarbons such as toluene and xylene, aliphatic or alicyclic hydrocarbons such as n-hexane and cyclohexane, ethyl acetate, acetic acid, and the like. Examples thereof include esters such as propyl, alcohols such as methanol, ethanol and IPA, ketones such as acetone and MEK, alkylene glycol monoalkyl ethers such as ethylene glycol monoethyl ether and propylene glycol monomethyl ether.

また、通常のインキは、ロールミル、ボールミルなどで混練して、顔料た添加剤をサブミクロンまで微粒子化し高度に分散させて、印刷適性を持たせる。しかしながら、本発明で使用する高輝度インキは、混練工程を必要とせず、攪拌機で混合するだけでよく分散し、金属光沢が損なわれない。即ち、高輝度の金属光沢を発現させるためには、金属蒸着膜細片の大きさが5〜25μm程度が必要で、上記混練工程を行うと金属光沢が極端に低下してしまう。   Ordinary inks are kneaded by a roll mill, a ball mill, or the like, and the pigment additive is finely dispersed to sub-micron and highly dispersed to give printability. However, the high-intensity ink used in the present invention does not require a kneading step, and can be dispersed only by mixing with a stirrer, and the metallic luster is not impaired. That is, in order to develop a high-brightness metallic luster, the metal vapor-deposited film strip needs to have a size of about 5 to 25 μm, and when the kneading step is performed, the metallic luster is extremely lowered.

(高輝度インキ印刷)以上のようにして得られた高輝度インキを、パターン状となるように、公知のグラビア印刷、スクリーン印刷、又はフレキソ印刷で印刷し、乾燥、必要に応じて硬化すればよい。パターン状の形状は特に限定されないが、例えば、文字、数字、イラスト、円形、矩形、多角形及び/又は星形などの任意の形状(結果として絵柄となる)であり、所望の絵柄を製版して、印刷すればよい。該高輝度インキ層18は、電気導電性の金属蒸着膜細片を含むが、表面処理をし、さらにバインダ中へ分散されているので、JIS−K6911で定める表面抵抗率は1012Ω以上である。 (High-brightness ink printing) If the high-brightness ink obtained as described above is printed by known gravure printing, screen printing, or flexographic printing so as to form a pattern, it can be dried and cured as necessary. Good. The shape of the pattern is not particularly limited, but may be any shape (resulting in a pattern) such as letters, numbers, illustrations, circles, rectangles, polygons, and / or stars. And print it. The high-brightness ink layer 18 includes electrically conductive metal vapor-deposited film strips, but is surface-treated and further dispersed in a binder. Therefore, the surface resistivity defined by JIS-K6911 is 10 12 Ω or more. is there.

(粘着層用のプライマ層)高輝度インキ層18はパターン状であり、パターンのない部分は透明反射層17が露出しているので、粘着層19を形成する際に、接着力を向上させるためにプライマ層21を設けることが好ましい。該プライマ層21としては、特に限定されないが、例えば、ポリウレタン系樹脂、ポリエステル系樹脂、ポリアミド系樹脂、エポキシ系樹脂、フェノ−ル系樹脂、ポリ塩化ビニル系樹脂、ポリ酢酸ビニル系樹脂、塩化ビニル−酢酸ビニル共重合体、酸変性ポリオレフィン系樹脂、エチレンと酢酸ビニル或いはアクリル酸などとの共重合体、(メタ)アクリル系樹脂、ポリビニルアルコール系樹脂、ポリビニルアセタール樹脂、ポリブタジエン系樹脂、ゴム系化合物、石油系樹脂、アルキルチタネ−ト系化合物、ポリエチレンイミン系化合物、イソシアネ−ト系化合物、澱粉、カゼイン、アラビアゴム、セルロ−ス誘導体、ワックス類などを使用することができる。該プライマ層21は、該材料樹脂を溶剤に溶解又は分散させて、適宜顔料などの添加剤を添加して、公知のロールコーティング、グラビアコーティングなどの方法で塗布し乾燥させて、厚さ0.1〜10μm程度の層を形成すればよい。   (Primer layer for pressure-sensitive adhesive layer) Since the high-brightness ink layer 18 has a pattern shape and the transparent reflective layer 17 is exposed in the portion without the pattern, the adhesive strength is improved when the pressure-sensitive adhesive layer 19 is formed. It is preferable to provide a primer layer 21 on the surface. The primer layer 21 is not particularly limited, and examples thereof include polyurethane resins, polyester resins, polyamide resins, epoxy resins, phenol resins, polyvinyl chloride resins, polyvinyl acetate resins, vinyl chloride. -Vinyl acetate copolymer, acid-modified polyolefin resin, copolymer of ethylene and vinyl acetate or acrylic acid, (meth) acrylic resin, polyvinyl alcohol resin, polyvinyl acetal resin, polybutadiene resin, rubber compound Petroleum resins, alkyl titanate compounds, polyethyleneimine compounds, isocyanate compounds, starch, casein, gum arabic, cellulose derivatives, waxes and the like can be used. The primer layer 21 is prepared by dissolving or dispersing the material resin in a solvent, adding an appropriate additive such as a pigment, and applying and drying by a known method such as roll coating or gravure coating. What is necessary is just to form a layer about 1-10 micrometers.

(基材の他方の面)次に、基材11の他方の面に液晶層41を形成する。ホログラムラベルとなった場合には、液晶層41が最表面となるので、保護のために液晶層41面へハードコート層45を設けたり、ハードコート層45との接着力を向上させるために、液晶層41面へプライマ層を設けてから、ハードコート層45を設けるのが好ましい。   Next, the liquid crystal layer 41 is formed on the other surface of the substrate 11. In the case of a hologram label, since the liquid crystal layer 41 is the outermost surface, in order to provide a hard coat layer 45 on the surface of the liquid crystal layer 41 for protection or to improve the adhesion with the hard coat layer 45, It is preferable to provide the hard coat layer 45 after providing the primer layer on the surface of the liquid crystal layer 41.

(液晶層)液晶層41としては、見る角度によって光の選択反射性および円偏光選択性を有し色彩変化を生じる液晶であるコレステリック液晶が好ましく用いられる。コレステリック液晶は、らせん構造を有する液晶ポリマーで、見る方向によって連続的に色調が変化する特性を有する。コレステリック液晶層は選択反射性を有することから、入射する光が入射角θを有している場合には、液晶の螺旋周期をP、液晶の平均屈折率をn、波長をλとすると、P・cosθ=λ/n、のBraggの反射条件を満足する波長の光を選択的に反射する。しかもこの時、その不斉炭素の絶対配置によって定まる構造に伴い、波長λの光の右円偏光成分あるいは左円偏光成分のどちらかのみを選択的に反射する。また、λ=n・P・cosθの式から明らかなように、コレステリック面(フィルム面)に入射する光の角度によってもλが異なる。   (Liquid Crystal Layer) As the liquid crystal layer 41, a cholesteric liquid crystal which is a liquid crystal having a selective reflectivity of light and a circular polarization selectivity depending on the viewing angle and causing a color change is preferably used. A cholesteric liquid crystal is a liquid crystal polymer having a helical structure, and has a characteristic that the color tone changes continuously depending on the viewing direction. Since the cholesteric liquid crystal layer has selective reflectivity, when the incident light has an incident angle θ, if the helical period of the liquid crystal is P, the average refractive index of the liquid crystal is n, and the wavelength is λ, P Selectively reflects light having a wavelength satisfying the Bragg reflection condition of cos θ = λ / n. In addition, at this time, according to the structure determined by the absolute configuration of the asymmetric carbon, only the right circularly polarized component or the left circularly polarized component of the light of wavelength λ is selectively reflected. Further, as is apparent from the equation of λ = n · P · cos θ, λ also varies depending on the angle of light incident on the cholesteric surface (film surface).

従って、コレステリック液晶層を有する媒体を傾けると当初の表面から観察した場合に視認される色彩とは異なる色彩を示すようになり、色彩可変効果を発揮する。そしてこのコレステリックカラーと呼ばれる色は他の手段では出すことのできない独特の美しい色となって人間の目に見える。これらの波長選択反射性、円偏光選択反射性、色の視角依存性およびコレステリックカラーの美しい色はいずれも他の物質あるいは方法で発現させることは困難であるため、これらの性質を利用した真偽判定体は偽造が困難であり、かつ偽造物の真偽判定が容易にでき、真偽判定体の偽造防止に極めて効果的である。   Therefore, when the medium having the cholesteric liquid crystal layer is tilted, a color different from the color visually recognized when observed from the original surface is exhibited, and a color changing effect is exhibited. The color called cholesteric color is visible to the human eye as a unique beautiful color that cannot be produced by other means. These wavelength selective reflectivity, circularly polarized light selective reflectivity, color viewing angle dependency, and beautiful colors of cholesteric color are difficult to express with other substances or methods. The determination object is difficult to counterfeit, and it is possible to easily determine the authenticity of the counterfeit product, which is extremely effective in preventing forgery of the authenticity determination object.

コレステリック液晶層は、サーモトロピックコレステリック液晶性高分子を、その液晶転移点以上に加熱して液晶構造を成長させたのち、急冷して液晶構造を固定化する方法、等により形成する方法が採用できる。コレステリック液晶は、各種のものが塗工用樹脂として市販されていて、これらを使用することができる。コレステリック液晶は、626.00nmにピーク(7.15%)を有するRed形、569.00nmにピーク(8.82%)を有するGreen形、502.50nmにピーク(4.43%)を有するBlue形などがある。   The cholesteric liquid crystal layer can be formed by a method in which a thermotropic cholesteric liquid crystalline polymer is heated to a temperature higher than its liquid crystal transition point to grow a liquid crystal structure and then rapidly cooled to fix the liquid crystal structure. . Various types of cholesteric liquid crystals are commercially available as coating resins, and these can be used. The cholesteric liquid crystal has a red type having a peak at 626.00 nm (7.15%), a green type having a peak at 6.69.00 nm (8.82%), and a blue type having a peak at 502.50 nm (4.43%). There are shapes.

コレステリック液晶層は、上記のコレステリック液晶樹脂そのものを媒体に塗布し配向・硬化して液晶塗膜を形成した塗工層であってもよく、また、コレステリック液晶片を微粉砕して顔料としたインキを使用し、オフセット、シルクスクリーン、グラビア、凹版、活版などの方法で印刷してもよい。これらの塗工用樹脂をグラビア印刷等により、基材に直接塗工し硬化乾燥させても、転写で形成することができる。塗工する際には、基材11面をラビング処理することで液晶を配向でき、また、基材11面をコロナ放電処理することで接着性を向上できる。   The cholesteric liquid crystal layer may be a coating layer in which the above cholesteric liquid crystal resin itself is applied to a medium and oriented and cured to form a liquid crystal coating film. And may be printed by a method such as offset, silk screen, gravure, intaglio, or letterpress. Even if these coating resins are directly applied to a substrate by gravure printing or the like and cured and dried, they can be formed by transfer. At the time of coating, the liquid crystal can be aligned by rubbing the surface of the substrate 11, and the adhesiveness can be improved by performing a corona discharge treatment on the surface of the substrate 11.

また、例えば、(1)色彩可変効果や偏光性を有するコレステリック液晶をバーコード状に塗布する、(2)コレステリック液晶を均一に塗布又はコレステリック液晶のフィルムを貼付し、レーザーによって一部を変質させ、配向状態を変化させてバーコード状にパターン化する、(3)コレステリック液晶を均一に塗布又はコレステリック液晶のフィルムを貼付し、その上に、光の偏光状態を変化させるバーコード状の位相差層を積層する、などの方法も挙げられる。   In addition, for example, (1) cholesteric liquid crystal having color change effect and polarization is applied in the form of a bar code, (2) cholesteric liquid crystal is uniformly applied or a cholesteric liquid crystal film is applied, and a part is altered by laser. (3) Apply a cholesteric liquid crystal uniformly or affix a cholesteric liquid crystal film and change the polarization state of the light on it to change the alignment state. The method of laminating | stacking a layer etc. is also mentioned.

液晶層41の厚さは、その特性を生かすため、1μm〜20μm程度の厚みを有することが望ましい。コレステリック液晶層15と黒色などの濃暗色の粘着層19とを組合わせることで、色彩可変機能が設けられるので、透過光を吸収し色鮮やかな色シフトが確認できるので、より反射光を観察しやすく、より色彩可変機能が向上する。本発明では液晶層41と粘着層19との層間にある不透明な高輝度インキ層18をパターン状として、該パターンのない部分を液晶層41の背景とすることで、色彩可変機能を向上できる。ホログラム部分には透明反射層17と高輝度インキ層18とが背景となっているので、明るいホログラムが観察でき、液晶層41の色彩可変機能と明るいホログラムを両立させることができる。   The thickness of the liquid crystal layer 41 is desirably about 1 μm to 20 μm in order to take advantage of the characteristics. By combining the cholesteric liquid crystal layer 15 and the dark and dark adhesive layer 19 such as black, a color variable function is provided, so that the transmitted light can be absorbed and a colorful color shift can be confirmed. Easy and more variable color function. In the present invention, the opaque high-brightness ink layer 18 between the liquid crystal layer 41 and the adhesive layer 19 is formed into a pattern, and the portion without the pattern is used as the background of the liquid crystal layer 41, so that the color changing function can be improved. Since the transparent reflection layer 17 and the high-brightness ink layer 18 are the background in the hologram portion, a bright hologram can be observed, and the color variable function of the liquid crystal layer 41 and the bright hologram can be compatible.

さらに、右円偏光又は左円偏光の円偏光選択性を有するフィルム(判別フィルム)を用いて、液晶層41の真贋を判別することもできる。判別フィルムを接するか、僅かな距離を隔てて保持し、平行して徐々に回転するようにして観察すると、判別フィルムは外観的には半透明状であるが、コレステリック液晶層の円偏光の向きにより、液晶層からの反射光が円偏光フィルムで遮断または透過される特性がある。例えば、コレステリック液晶層である印刷パターンが右円偏光で判別(円偏光)フィルムのそれが同じく右円偏光であると反射光が判別(円偏光)フィルムを透過するため印刷パターンが呈している色を観察することができる。逆に判別(円偏光)フィルムのそれが左円偏光であると右円偏光である反射光は判別(円偏光)フィルムで遮断され、一定の角度位置で印刷パターンの色が消失するので、判別できる。   Furthermore, the authenticity of the liquid crystal layer 41 can be determined using a film (discrimination film) having a circularly polarized light selectivity of right circularly polarized light or left circularly polarized light. When the discriminating film is touched or held at a small distance and observed to rotate gradually in parallel, the discriminating film is translucent in appearance, but the direction of circularly polarized light in the cholesteric liquid crystal layer Thus, the reflected light from the liquid crystal layer is blocked or transmitted by the circularly polarizing film. For example, if the print pattern that is a cholesteric liquid crystal layer is discriminated by right-handed circularly polarized light (circularly polarized light), and if it is also right-handed circularly polarized light, the reflected light will be discriminated (circularly polarized) and the color that the printed pattern exhibits Can be observed. Conversely, if the discriminating (circularly polarized) film is left circularly polarized light, the reflected light that is right circularly polarized light is blocked by the discriminating (circularly polarized) film, and the color of the printed pattern disappears at a certain angular position. it can.

(液晶プライマ層)液晶層41面へハードコート層45を設けるが、接着力向上のために、液晶層用のプライマ層43を設けるのが好ましい。該プライマ層43としては、特に限定されないが、例えば、ポリウレタン系樹脂、ポリエステル系樹脂、ポリアミド系樹脂、エポキシ系樹脂、フェノ−ル系樹脂、ポリ塩化ビニル系樹脂、ポリ酢酸ビニル系樹脂、塩化ビニル−酢酸ビニル共重合体、酸変性ポリオレフィン系樹脂、エチレンと酢酸ビニル或いはアクリル酸などとの共重合体、(メタ)アクリル系樹脂、ポリビニルアルコール系樹脂、ポリビニルアセタール樹脂、ポリブタジエン系樹脂、ゴム系化合物、石油系樹脂、アルキルチタネ−ト系化合物、ポリエチレンイミン系化合物、イソシアネ−ト系化合物、澱粉、カゼイン、アラビアゴム、セルロ−ス誘導体、ワックス類などを使用することができる。該プライマ層43は、該材料樹脂を溶剤に溶解又は分散させて、適宜顔料などの添加剤を添加して、公知のロールコーティング、グラビアコーティングなどの方法で塗布し乾燥させて、厚さ0.1〜10μm程度の層を形成すればよい。   (Liquid Crystal Primer Layer) Although the hard coat layer 45 is provided on the surface of the liquid crystal layer 41, it is preferable to provide a primer layer 43 for the liquid crystal layer in order to improve the adhesive strength. The primer layer 43 is not particularly limited, and examples thereof include polyurethane resins, polyester resins, polyamide resins, epoxy resins, phenol resins, polyvinyl chloride resins, polyvinyl acetate resins, and vinyl chloride. -Vinyl acetate copolymer, acid-modified polyolefin resin, copolymer of ethylene and vinyl acetate or acrylic acid, (meth) acrylic resin, polyvinyl alcohol resin, polyvinyl acetal resin, polybutadiene resin, rubber compound Petroleum resins, alkyl titanate compounds, polyethyleneimine compounds, isocyanate compounds, starch, casein, gum arabic, cellulose derivatives, waxes and the like can be used. The primer layer 43 is obtained by dissolving or dispersing the material resin in a solvent, adding an additive such as a pigment as appropriate, applying it by a known roll coating method, gravure coating method, etc., and drying it. What is necessary is just to form a layer about 1-10 micrometers.

(ハードコート層)ハードコート層45としては、電離放射線硬化樹脂を主成分とし、ポリエチレンワックスを含むようにする。該電離放射線硬化性樹脂としては、好ましくは、(1)分子中にイソシアネート基を3個以上有するイソシアネート類、(2)分子中に水酸基を少なくとも1個と(メタ)アクリロイルオキシ基を少なくとも2個有する多官能(メタ)アクリレート類、又は(3)分子中に水酸基を少なくとも2個有する多価アルコール類の反応生成物であるウレタン(メタ)アクリレートオリゴマーを含有する電離放射線硬化性樹脂を用い、ポリエチレンワックスを含ませて、塗布し乾燥して電離放射線で硬化させて、電離放射線硬化樹脂とすればよい。   (Hard Coat Layer) The hard coat layer 45 is mainly composed of an ionizing radiation curable resin and contains polyethylene wax. The ionizing radiation curable resin is preferably (1) an isocyanate having three or more isocyanate groups in the molecule, and (2) at least one hydroxyl group and at least two (meth) acryloyloxy groups in the molecule. Using an ionizing radiation curable resin containing a urethane (meth) acrylate oligomer which is a reaction product of a polyfunctional (meth) acrylate having a polyhydric alcohol having at least two hydroxyl groups in the molecule, or (3) A wax may be included, applied, dried, and cured with ionizing radiation to form an ionizing radiation curable resin.

前記ウレタン(メタ)アクリレートオリゴマーを含有する電離放射線硬化性樹脂(本明細書では電離放射線硬化性樹脂組成物Mと呼称する)は、ウレタン(メタ)アクリレートオリゴマーを含有する電離放射線硬化性樹脂の硬化物、具体的には、特開2001−329031号公報で開示されている光硬化性樹脂などが例示できる。   The ionizing radiation curable resin containing the urethane (meth) acrylate oligomer (referred to herein as the ionizing radiation curable resin composition M) is a cured ionizing radiation curable resin containing the urethane (meth) acrylate oligomer. Examples thereof include photocurable resins disclosed in Japanese Patent Application Laid-Open No. 2001-329031.

(ポリエチレンワックス)ポリエチレンワックスとしては、ポリエチレン系樹脂の粒子やビーズが挙げられるが、好ましくは球状ビーズである。但し、ポリエチレンワックスを添加すると、箔切れ性は低下するので、その添加量は、電離放射線硬化樹脂100質量部に対して、0.01〜10質量部程度、好ましくは0.1〜5質量部とする。転写後にはハードコート層45が最表面層となり、含まれるポリエチレンワックスは、機械的な摩擦、及び摩耗から媒体を保護し、後述する画像などの固有情報も保護する。   (Polyethylene wax) Polyethylene wax includes polyethylene resin particles and beads, and is preferably spherical beads. However, when polyethylene wax is added, the foil breakage is reduced, so the amount added is about 0.01 to 10 parts by weight, preferably 0.1 to 5 parts by weight, with respect to 100 parts by weight of ionizing radiation curable resin. And After the transfer, the hard coat layer 45 becomes the outermost layer, and the contained polyethylene wax protects the medium from mechanical friction and abrasion, and also protects unique information such as an image to be described later.

(ハードコート層の形成)ハードコート層45の形成は、上記の電離放射線硬化性樹脂にポリエチレンワックス、必要に応じて光重合開始剤、可塑剤、安定剤、界面活性剤等を加え、溶媒へ分散または溶解して、ロールコート、グラビアコート、コンマコート、ダイコートなどの公知のコーティング方法で塗布し乾燥して、電離放射線で反応(硬化)させればよい。   (Formation of hard coat layer) The hard coat layer 45 is formed by adding polyethylene wax to the above-mentioned ionizing radiation curable resin, and if necessary, adding a photopolymerization initiator, a plasticizer, a stabilizer, a surfactant and the like to the solvent. It may be dispersed or dissolved, applied by a known coating method such as roll coating, gravure coating, comma coating or die coating, dried, and reacted (cured) with ionizing radiation.

(ハードコート層の厚味)ハードコート層45の厚さは、通常、1〜30μm程度であり、特に限定されないが、10μm以上で、好ましくは15μm以上であるようにすることで耐久性が高まり、極めて過酷な環境での使用、使用期限がなかったり、長期にわたる使用、及び/又は多数回の繰り返し使用などでも、化学的機械的な外力から保護できる。   (Thickness of hard coat layer) The thickness of the hard coat layer 45 is usually about 1 to 30 μm, and is not particularly limited. However, the thickness is increased to 10 μm or more, preferably 15 μm or more. It can be protected from external chemical and mechanical forces even when used in extremely harsh environments, with no expiry date, for long periods of use, and / or for many repeated uses.

(粘着層)プライマ層21面へ、黒色などの濃暗色である粘着層19を形成し、該粘着層19としては公知の感圧で接着する粘着剤が適用できる。粘着剤としては、特に限定されるものではなく、例えば、天然ゴム系、ブチルゴム、ポリイソプレン、ポリイソブチレン、ポリクロロプレン、スチレン−ブタジエン共重合樹脂などの合成ゴム系樹脂、シリコーン系樹脂、アクリル系樹脂、ポリ酢酸ビニール、エチレン−酢酸ビニール共重合体などの酢酸ビニール系樹脂、ウレタン系樹脂、アクリロニトリル、炭化水素樹脂、アルキルフェノール樹脂、ロジン、ロジントリグリセリド、水素化ロジンなどのロジン系樹脂が適用できる。該材料樹脂と黒色などの濃暗色の顔料及び/又は染料を溶剤に溶解又は分散させて、適宜添加剤を添加して、公知のロールコーティング、グラビアコーティングなどの方法で塗布し乾燥させて、厚さ5μmから50μmの層を得る。   (Adhesive layer) A pressure-sensitive adhesive layer 19 having a dark and dark color such as black is formed on the surface of the primer layer 21. The adhesive is not particularly limited. For example, natural rubber, butyl rubber, polyisoprene, polyisobutylene, polychloroprene, styrene-butadiene copolymer resin and other synthetic rubber resins, silicone resins, and acrylic resins. A rosin resin such as polyvinyl acetate, ethylene-vinyl acetate copolymer, etc., urethane resin, acrylonitrile, hydrocarbon resin, alkylphenol resin, rosin, rosin triglyceride, hydrogenated rosin can be applied. Dissolve or disperse the material resin and dark pigment and / or dye such as black in a solvent, add an appropriate additive, and apply and dry by a known roll coating, gravure coating, etc. A layer of 5 μm to 50 μm is obtained.

(剥離紙)剥離紙は公知のものでよく、例えば上質紙、コート紙、含浸紙、又はプラスチックフィルムなどの基材の片面に離型層を有している。該離型層としては、離型性を有する材料であれば、特に限定されないが、例えば、シリコーン樹脂、有機樹脂変性シリコーン樹脂、フッ素樹脂、アミノアルキド樹脂、ポリエステル樹脂などがある。これらの樹脂は、エマルジョン型、溶剤型又は無溶剤型のいずれもが使用できる。必要に応じて剥離紙を除いた部分を半抜きして、粘着ラベルを得る。   (Release paper) The release paper may be a known one, and has a release layer on one surface of a base material such as high-quality paper, coated paper, impregnated paper, or plastic film. The release layer is not particularly limited as long as it has a release property, and examples thereof include silicone resins, organic resin-modified silicone resins, fluororesins, aminoalkyd resins, and polyester resins. These resins can be used in any of emulsion type, solvent type and solventless type. If necessary, the part excluding the release paper is half-cut to obtain an adhesive label.

(貼着)ホログラムラベル1の被転写体への貼着方法としては、公知の貼着法でよく、例えば、手作業、ラベラー、ジェットラベラーなどの公知の方法が適用できる。ラベルの形状は、円形、楕円形、矩形、多角形、星形など、任意の形状でよい。   (Adhesion) As a method for adhering the hologram label 1 to the transfer target, a known adhesion method may be used. For example, a known method such as manual work, a labeler, a jet labeler, etc. can be applied. The shape of the label may be any shape such as a circle, an ellipse, a rectangle, a polygon, and a star.

(被転写体)被転写体100としては、金属層103を含めば特に限定されず、単独でも複数層でもよい。例えば天燃繊維紙、コート紙、トレーシングペーパー、転写時の熱で変形しないプラスチックフイルム、ガラス、金属、セラミックス、木材や布などの媒体などの基体へ、メッキや蒸着したり、金属箔や金属層含む材料を積層して金属層103を設ければよく、金属のみの金属板でもよい。また、被転写体100の媒体はその少なくとも1部が、画像、着色、印刷、その他の加飾が施されていてもよい。   (Transfer To be Transferred) The transfer target 100 is not particularly limited as long as the metal layer 103 is included, and may be a single layer or a plurality of layers. For example, natural fiber paper, coated paper, tracing paper, plastic film that does not deform by heat during transfer, glass, metal, ceramics, substrates such as wood and cloth, plating, vapor deposition, metal foil and metal A metal layer 103 may be provided by stacking materials including layers, or a metal plate made of only metal may be used. Further, at least a part of the medium of the transfer target 100 may be subjected to image, coloring, printing, or other decoration.

従来の反射層であるアルミニウム薄膜では、厚さが100〜500nm程度と極めて薄く、またイオン化傾向も高く、また、汗、食品や薬品などで酸性アルカリ性のものが影響する環境では著しく、電気的腐食を受けて、ムラや白化し、酷い場合には欠落して、ホログラム画像がムラになったり、1部又は全部が観察されなくなったり、ホログラム効果が失われ易い。特に酸性物が接触していると影響が著しく、この場合のJIS−K6911で定める表面抵抗率は108Ω以上が好ましく、さらに好ましくは1012Ω以上であり、高温環境下でも電気的腐食を受けにくくなる。本発明のホログラムラベルでは、構成するすべての層のJIS−K6911で定める表面抵抗率を106Ω以上、好ましくは108Ω以上、さらに好ましくは1012Ω以上とする。ホログラム層15、粘着層19、プライマ層21・43、液晶層41、ハードコート層45なども合成樹脂を主体とするものであり、JIS−K6911で定める表面抵抗率は1012Ω以上である。透明反射層17も金属酸化物又は窒化物であり、また、好ましい酸化チタンもJIS−K6911で定める表面抵抗率は1012Ω以上である。 The aluminum thin film, which is a conventional reflective layer, is extremely thin with a thickness of about 100 to 500 nm, has a high ionization tendency, and is remarkably electrically corrosive in an environment affected by acidic alkaline substances such as sweat, food and chemicals. As a result, unevenness or whitening occurs, and when it is severe, the hologram image becomes uneven, and the hologram image becomes uneven, one or all of the images are not observed, and the hologram effect is easily lost. In particular, the influence is remarkable when an acidic substance is in contact. In this case, the surface resistivity defined by JIS-K6911 is preferably 10 8 Ω or more, more preferably 10 12 Ω or more, and it can be electrically corroded even in a high temperature environment. It becomes difficult to receive. In the hologram label of the present invention, the surface resistivity defined by JIS-K6911 of all layers constituting the layer is 10 6 Ω or more, preferably 10 8 Ω or more, more preferably 10 12 Ω or more. The hologram layer 15, the adhesive layer 19, the primer layers 21 and 43, the liquid crystal layer 41, the hard coat layer 45, etc. are also mainly composed of synthetic resin, and the surface resistivity defined by JIS-K6911 is 10 12 Ω or more. The transparent reflective layer 17 is also a metal oxide or nitride, and a preferable titanium oxide has a surface resistivity defined by JIS-K6911 of 10 12 Ω or more.

以下、実施例及び比較例により、本発明を更に詳細に説明するが、これに限定されるものではない。   EXAMPLES Hereinafter, although an Example and a comparative example demonstrate this invention further in detail, it is not limited to this.

(実施例1)基材11として厚さ50μmのPETフィルムを用い、下記の電離放射線硬化性樹脂組成物をグラビアリバースコーターで乾燥後の厚さが2μmになるように、塗工し100℃で乾燥させた。
・<電離放射線硬化性樹脂組成物の作製手順>
まず、「電離放射線硬化性樹脂組成物M」は以下の手順で、生成した。撹拌機、還流冷却器、滴下漏斗及び温度計を取り付けた反応器に、酢酸エチル206.1g及びイソホロンジイソシアネートの三量体(HULS社製品、VESTANAT T1890、融点110℃)133.5gを仕込み、80℃に昇温して溶解させた。溶液中に空気を吹き込んだのち、ハイドロキノンモノメチルエーテル0.38g、ペンタエリスリトールトリアクリレート(大阪有機化学工業社製品、ビスコート300)249.3g及びジブチル錫ジラウレート0.38gを仕込んだ。80℃で5時間反応させたのち酢酸エチル688.9gを添加して冷却した。
該「電離放射線硬化性樹脂組成物M」と、造膜性樹脂(アクリル系オリゴマー)、反応性シリコーン、ポリエチレンワックス、光重合開始剤、及び溶媒を下記の組成で配合して電離放射線硬化性樹脂組成物を調製した。
・<ホログラム層の電離放射線硬化性樹脂組成物>
「電離放射線硬化性樹脂組成物M」 25質量部
メタアクリレートオリゴマー(日本合成化学社製、商品名紫光6630B)5質量部
反応性シリコーン(信越化学社製、商品名X−22−2445) 0.2質量部
ポリエチレンワックス(平均粒径2.0m) 0.3質量部
光重合開始剤(チバ社製、商品名イルガキュア907) 0.9質量部
酢酸エチル 70質量部
次に、該層面へ、2光束干渉法による回折格子から2P法で複製した擬似連続絵柄としたプレス型を複製装置のエンボスローラーに貼着して、相対するローラーと間で加熱プレス(エンボス)して、微細な凹凸パターンからなるレリーフを賦形させた。賦形後直ちに、高圧水銀灯を用いて紫外線を照射して硬化させた。
該ホログラム層15のレリーフ面へ、厚さ50nmの酸化チタンを真空蒸着法で形成して、透明反射層17とした。
該反射層17面へ、ファインラップスーパーメタリックシルバーインキ(大日本インキ化学工業社製、高輝度インキ商品名)を用いて、グラビア印刷法で、乾燥後の厚さが2μmになるように、ハート模様をちりばめた絵柄を印刷して、パターン状の高輝度インキ層18を形成した。
該高輝度インキ層18面へ、プライマ層組成物(ポリエステル樹脂15質量部、塩化ビニル−酢酸ビニル共重合樹脂15質量部、トルエン35質量部、メチルエチルケトン35質量部)を、乾燥膜厚が1μmになるようにグラビアコーターで塗布し100℃で乾燥して溶剤を揮散させて、プライマ層21を形成して、基材11/ホログラム層15/透明反射層17/高輝度インキ層18/プライマ層21の積層体が得られた。
該積層体の基材11/面へ、該基材をコロナ処理し、ラビング処理しながら、コレステリック液晶樹脂をグラビアコーティング法で、乾燥後の厚さが2μmになるように塗布し乾燥して、赤−緑系の液晶層41を形成した。
該液晶層41面へ、プライマ層組成物(ポリエステル樹脂15質量部、塩化ビニル−酢酸ビニル共重合樹脂15質量部、トルエン35質量部、メチルエチルケトン35質量部)を、乾燥膜厚が1μmになるようにグラビアコーターで塗布し100℃で乾燥して溶剤を揮散させて、プライマ層43を形成した。
該プライマ層43面へ、下記の電離放射線硬化性樹脂組成物をグラビアリバースコーターで乾燥後の塗布厚さが2.5μmになるように塗工し100℃で乾燥させて、高圧水銀灯を用いて紫外線を照射して硬化させて、ハードコート層45を形成した。
・<電離放射線硬化性樹脂組成物の作製手順>
まず、反応性生物(A)は以下の手順で、生成した。撹拌機、還流冷却器、滴下漏斗及び温度計を取り付けた反応器に、酢酸エチル206.1g及びイソホロンジイソシアネートの三量体(HULS社製品、VESTANAT T1890、融点110℃)133.5gを仕込み、80℃に昇温して溶解させた。溶液中に空気を吹き込んだのち、ハイドロキノンモノメチルエーテル0.38g、ペンタエリスリトールトリアクリレート(大阪有機化学工業社製品、ビスコート300)249.3g及びジブチル錫ジラウレート0.38gを仕込んだ。80℃で5時間反応させたのち酢酸エチル688.9gを添加して冷却した。
該反応生成物(A)と、ポリエチレンワックス、光重合開始剤、及び溶媒を下記の組成で配合して電離放射線硬化性樹脂組成物を調製した。
・<電離放射線硬化性樹脂組成物>
反応性生物(A) 30質量部
ポリエチレンワックス(平均粒径5μm) 0.3質量部
光重合開始剤(チバ社製、商品名イルガキュア907) 0.9質量部
溶媒(酢酸エチル:メチルイソブチルケトン=1:1) 70質量部
このようにして、ハードコート層45/液晶層41/基材11/ホログラム層15/透明反射層17/高輝度インキ層18/プライマ層21の積層体を得た。
該積層体のプライマ層21面へ、粘着剤(ニッセツPE−118+CK101、日本カーバイド製)を、乾燥膜厚が30μmになるようにコンマコーターで塗布し100℃で乾燥して溶剤を揮散させて、粘着層19を形成した後、剥離紙としてシリコーン処理PETフイルム(SPO5、東京セロファン紙社製)を貼合して、ハードコート層45/プライマ層43/液晶層41/基材11/ホログラム層15/透明反射層17/高輝度インキ層18/プライマ層21/粘着層19/剥離紙の層構成からなる実施例1のホログラムラベル1を得た。
(Example 1) Using a PET film having a thickness of 50 µm as the substrate 11, the following ionizing radiation curable resin composition was applied with a gravure reverse coater so that the thickness after drying was 2 µm, at 100 ° C. Dried.
・ <Procedure for producing ionizing radiation curable resin composition>
First, “ionizing radiation curable resin composition M” was produced by the following procedure. A reactor equipped with a stirrer, reflux condenser, dropping funnel and thermometer was charged with 206.1 g of ethyl acetate and 133.5 g of isophorone diisocyanate trimer (HULS product, VESTANAT T1890, melting point 110 ° C.), 80 The solution was heated to 0 ° C. and dissolved. After air was blown into the solution, 0.38 g of hydroquinone monomethyl ether, 249.3 g of pentaerythritol triacrylate (product of Osaka Organic Chemical Industry Co., Ltd., Biscoat 300) and 0.38 g of dibutyltin dilaurate were charged. After reacting at 80 ° C. for 5 hours, 688.9 g of ethyl acetate was added and cooled.
The “ionizing radiation curable resin composition M”, a film-forming resin (acrylic oligomer), a reactive silicone, a polyethylene wax, a photopolymerization initiator, and a solvent are blended in the following composition to form an ionizing radiation curable resin. A composition was prepared.
・ <Ionizing radiation curable resin composition of hologram layer>
“Ionizing radiation curable resin composition M” 25 parts by mass Methacrylate oligomer (manufactured by Nippon Synthetic Chemical Co., Ltd., trade name Murasaki 6630B) 5 parts by weight of reactive silicone (manufactured by Shin-Etsu Chemical Co., Ltd., trade name X-22-2445) 0. 2 parts by mass Polyethylene wax (average particle size 2.0 m) 0.3 parts by mass Photopolymerization initiator (trade name Irgacure 907, manufactured by Ciba) 0.9 parts by mass Ethyl acetate 70 parts by mass From a fine concavo-convex pattern, a press die with a pseudo-continuous pattern duplicated by the 2P method from a diffraction grating by the beam interference method is attached to an embossing roller of a duplicating apparatus, and heated and pressed (embossed) with an opposing roller. A relief was formed. Immediately after shaping, it was cured by irradiating with ultraviolet rays using a high-pressure mercury lamp.
Titanium oxide with a thickness of 50 nm was formed on the relief surface of the hologram layer 15 by a vacuum deposition method to form a transparent reflective layer 17.
Using a fine wrap super metallic silver ink (manufactured by Dainippon Ink & Chemicals, Inc., trade name of high-brightness ink) on the reflective layer 17 surface, a heart pattern so that the thickness after drying becomes 2 μm by gravure printing. A pattern with a high brightness ink layer 18 was formed by printing a pattern inlaid with.
Primer layer composition (15 parts by mass of polyester resin, 15 parts by mass of vinyl chloride-vinyl acetate copolymer resin, 35 parts by mass of toluene, 35 parts by mass of methyl ethyl ketone) is applied to the surface of the high-brightness ink layer 18 to a dry film thickness of 1 μm. Then, it is applied with a gravure coater and dried at 100 ° C. to volatilize the solvent to form the primer layer 21, and the substrate 11 / hologram layer 15 / transparent reflective layer 17 / high-brightness ink layer 18 / primer layer 21. A laminate was obtained.
The substrate 11 / surface of the laminate is subjected to corona treatment and rubbing treatment, and a cholesteric liquid crystal resin is applied by a gravure coating method so that the thickness after drying is 2 μm and dried. A red-green liquid crystal layer 41 was formed.
A primer layer composition (15 parts by mass of a polyester resin, 15 parts by mass of vinyl chloride-vinyl acetate copolymer resin, 35 parts by mass of toluene, and 35 parts by mass of methyl ethyl ketone) is applied to the surface of the liquid crystal layer 41 so that the dry film thickness becomes 1 μm. The primer layer 43 was formed by coating with a gravure coater and drying at 100 ° C. to evaporate the solvent.
The surface of the primer layer 43 is coated with the following ionizing radiation curable resin composition with a gravure reverse coater so that the coating thickness after drying is 2.5 μm, dried at 100 ° C., and using a high pressure mercury lamp. The hard coat layer 45 was formed by curing by irradiating ultraviolet rays.
・ <Procedure for producing ionizing radiation curable resin composition>
First, the reactive organism (A) was produced by the following procedure. A reactor equipped with a stirrer, reflux condenser, dropping funnel and thermometer was charged with 206.1 g of ethyl acetate and 133.5 g of isophorone diisocyanate trimer (HULS product, VESTANAT T1890, melting point 110 ° C.), 80 The solution was heated to 0 ° C. and dissolved. After air was blown into the solution, 0.38 g of hydroquinone monomethyl ether, 249.3 g of pentaerythritol triacrylate (product of Osaka Organic Chemical Industry Co., Ltd., Biscoat 300) and 0.38 g of dibutyltin dilaurate were charged. After reacting at 80 ° C. for 5 hours, 688.9 g of ethyl acetate was added and cooled.
The reaction product (A), polyethylene wax, photopolymerization initiator, and solvent were blended in the following composition to prepare an ionizing radiation curable resin composition.
・ <Ionizing radiation curable resin composition>
Reactive organism (A) 30 parts by weight Polyethylene wax (average particle size 5 μm) 0.3 parts by weight Photopolymerization initiator (Ciba, trade name Irgacure 907) 0.9 parts by weight Solvent (ethyl acetate: methyl isobutyl ketone = 1: 1) 70 parts by mass In this way, a laminate of hard coat layer 45 / liquid crystal layer 41 / base material 11 / hologram layer 15 / transparent reflection layer 17 / high brightness ink layer 18 / primer layer 21 was obtained.
To the primer layer 21 surface of the laminate, an adhesive (Nissetsu PE-118 + CK101, manufactured by Nippon Carbide) was applied with a comma coater so that the dry film thickness was 30 μm, and dried at 100 ° C. to volatilize the solvent. After the adhesive layer 19 is formed, a silicone-treated PET film (SPO5, manufactured by Tokyo Cellophane Paper Co., Ltd.) is bonded as a release paper, and the hard coat layer 45 / primer layer 43 / liquid crystal layer 41 / substrate 11 / hologram layer 15 are bonded. The hologram label 1 of Example 1 having a layer configuration of: / transparent reflective layer 17 / high brightness ink layer 18 / primer layer 21 / adhesive layer 19 / release paper was obtained.

(比較例1)透明反射層17に代えて厚さ200nmのアルミニウムを真空蒸着法で形成して金属反射層とし、かつ、高輝度インキ層18を設けない以外は実施例1と同様にして、ハードコート層45/プライマ層43/液晶層41/基材11/ホログラム層15/金属反射層17/プライマ層21/粘着層19/剥離紙のの層構成からなる比較例1のホログラムラベル1を得た。   (Comparative example 1) Instead of the transparent reflective layer 17, aluminum having a thickness of 200 nm was formed by a vacuum deposition method to form a metal reflective layer, and the same as in Example 1 except that the high-brightness ink layer 18 was not provided. The hologram label 1 of Comparative Example 1 having a layer structure of hard coat layer 45 / primer layer 43 / liquid crystal layer 41 / base material 11 / hologram layer 15 / metal reflective layer 17 / primer layer 21 / adhesive layer 19 / release paper Obtained.

(評価方法)高温高湿下での経時による外観試験により、該外観試験は被転写体として、厚さ100μmの合成紙と厚さ50μmの銅箔を積層した積層体を用い、この胴箔面へ、実施例及び比較例のホログラムラベル1から剥離紙を除いて、粘着層19面を手で加圧して貼着した。貼着されたホログラム付きの被転写体を、温度40℃湿度90%RHの雰囲気に1週間放置した後に、ホログラムの外観を目視で観察した。
実施例1のホログラムラベル1を用いたものでは、著しい外観の変化はなく、明るいホログラムが観察できた。また、ハート型の銀色で明るいホログラムと鮮やかな色彩可変の液晶層が観察できた。なお、実施例1の高輝度インキ層18を形成した際に測定した、高輝度インキ層18のJIS−K6911で定める表面抵抗率は6×1013Ωであった。
比較例1のホログラムラベル1を用いたものでは、アルミニウムが電気的な腐食を受けて、周辺部が欠落しホログラムが観察されず、アルミニウムが残った部分も表面にムラが発生し白化しムラ状のホログラムであり、中央部分のみはホログラムが観察されたが、全体としては著しく劣化して、意匠性もセキュリティ性も失われていた。
(Evaluation method) According to an appearance test over time under high temperature and high humidity, the appearance test uses a laminated body in which a synthetic paper having a thickness of 100 μm and a copper foil having a thickness of 50 μm is laminated as a transfer target body. The release paper was removed from the hologram labels 1 of the examples and comparative examples, and the pressure-sensitive adhesive layer 19 surface was pressed by hand and pasted. The adhered transfer object with the hologram was left in an atmosphere of a temperature of 40 ° C. and a humidity of 90% RH for one week, and then the appearance of the hologram was visually observed.
In the case of using the hologram label 1 of Example 1, there was no significant change in appearance, and a bright hologram could be observed. In addition, a heart-shaped silver and bright hologram and a vividly variable liquid crystal layer could be observed. In addition, the surface resistivity defined by JIS-K6911 of the high-brightness ink layer 18 measured when the high-brightness ink layer 18 of Example 1 was formed was 6 × 10 13 Ω.
In the case of using the hologram label 1 of Comparative Example 1, the aluminum was subjected to electrical corrosion, the peripheral portion was missing and the hologram was not observed, and the remaining portion of the aluminum was uneven and whitened and uneven. The hologram was observed only in the central portion, but as a whole, the hologram was significantly deteriorated and the design and security were lost.

本発明の1実施例を示すホログラムラベルの断面図である。It is sectional drawing of the hologram label which shows one Example of this invention. 金属層を含む被転写体へホログラムラベルを貼着した断面図である。It is sectional drawing which affixed the hologram label to the to-be-transferred body containing a metal layer.

符号の説明Explanation of symbols

1:ホログラムラベル
11:基材
15:ホログラム層
17:透明反射層
18:高輝度インキ層
19:粘着層
21、43:プライマ層
41:液晶層
45:ハードコート層
100:被転写体
101:被転写体基材
103:金属層
1: Hologram label 11: Substrate 15: Hologram layer 17: Transparent reflection layer 18: High-brightness ink layer 19: Adhesive layer 21, 43: Primer layer 41: Liquid crystal layer 45: Hard coat layer 100: Transfer object 101: Subject Transfer material base 103: Metal layer

Claims (3)

基材と、該基材の一方の面に、少なくともホログラム層、透明反射層、高輝度インキ層及び粘着層が順に積層され、前記基材の他方の面に液晶層を有するホログラムラベルであって、前記高輝度インキ層が少なくとも有機脂肪酸、メチルシリルイソシアネート又はセルロース誘導体で表面処理した金属蒸着膜細片を含み、かつパターン状であり、前記粘着層が黒色であり、かつ、前記ホログラムラベルを金属層を含む被転写体へ貼着しても、前記ホログラムラベルに電気的腐食が発生せずホログラム効果が維持されることを特徴とするホログラムラベル。 A hologram label having a substrate and at least a hologram layer, a transparent reflective layer, a high-brightness ink layer, and an adhesive layer sequentially laminated on one surface of the substrate, and having a liquid crystal layer on the other surface of the substrate, The high-brightness ink layer includes at least a metal vapor-deposited thin film surface-treated with an organic fatty acid, methylsilyl isocyanate, or a cellulose derivative, is patterned, the adhesive layer is black, and the hologram label is made of metal. A hologram label characterized in that the hologram effect is maintained without causing electrical corrosion in the hologram label even if it is attached to a transfer medium including a layer. 上記透明反射層が酸化チタンであることを特徴とする請求項1に記載のホログラムラベル。 The hologram label according to claim 1, wherein the transparent reflective layer is titanium oxide. 上記転写層を構成するすべての層のJIS−K6911で定める表面抵抗率が1012Ω以上であることを特徴とする請求項1〜2のいずれかに記載のホログラムラベル。 3. The hologram label according to claim 1, wherein the surface resistivity defined by JIS-K6911 of all the layers constituting the transfer layer is 10 12 Ω or more.
JP2006327699A 2006-12-05 2006-12-05 Hologram label Withdrawn JP2008139717A (en)