JP2008063687A - Brass plated steel wire for reinforcing rubber article and method for producing the same - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To obtain a brass plated steel wire for reinforcing rubber articles, which has excellent initial adhesion performance and adhesion durability performance, and to provide a method for producing the same. <P>SOLUTION: The brass plated steel wire for reinforcing rubber articles includes a brass plated layer 11 having an amorphous part 11a composed of a crystal grain with a particle diameter of ≤20 nm. The brass plated layer 11 is composed of 55-66 wt.% of copper and 34-45 wt.% of zinc. The brass plated layer 11 includes a laminated structural part 13 in which the amorphous part 11a on the surface side and a crystalline part 11b on the inside are laminated to each other. The area ratio of the surface of the amorphous part 11a of the laminated structural part 13 to the whole surface of the brass plated layer 11 is ≥20% and the volume ratio of the amorphous part 11a of the laminated structural part 13 to the whole laminated structural part is ≥20% and ≤80%. <P>COPYRIGHT: (C)2008,JPO&INPIT

Description

  TECHNICAL FIELD The present invention relates to a brass-plated steel wire for reinforcing rubber articles having a surface provided with a brass (brass) plating layer, which is used for an element wire of a steel cord for reinforcing tires. It is related with the improvement of adhesiveness.

Conventionally, as a steel wire for reinforcing a rubber article used for a wire of a steel cord for reinforcing a tire, a brass-plated steel wire having a surface provided with a brass plating layer is used. This brass-plated steel wire is manufactured by cold-drawing a steel wire subjected to a heat treatment such as patenting and a brass plating process to a predetermined wire diameter.
Regarding the adhesion between the brass-plated steel wire and the rubber, for example, in the vulcanization process at the time of tire production, the sulfur in the rubber reacts with the copper in the brass plating by being heated in contact with the rubber. Thus, it is known that an adhesive layer is formed. The adhesive layer is required to be formed quickly and reliably in the vulcanization process (initial adhesion performance) and not deteriorated by moisture or heat when the rubber article is used (adhesion durability performance).

Conventionally, as a method of improving the adhesion of rubber-plated steel wire for reinforcing steel articles to rubber, a method of alloying the surface layer by adding an alloy element such as Fe or Ni to the plating component (for example, a patent) References 1 and 2), a method of performing surface treatment by irradiating plasma on a steel wire subjected to brass plating (for example, Patent Document 3), and a method for limiting the oxygen ratio on the outermost surface of the plating layer (for example, Patent Documents) 4), or a method of performing blasting after wire drawing (for example, see Patent Document 5).
JP-A-8-209386 JP 2002-13081 A JP 2003-160895 A JP 2004-68102 A JP-A-5-278147

  However, none of the above conventional methods can satisfy both the initial adhesive performance and the adhesive durability performance, although some improvement in adhesiveness is observed.

  The present invention has been made in view of the above-described conventional problems, and provides a brass-plated steel wire for reinforcing rubber articles and a method for producing the same, which can reliably improve the adhesion between the brass-plated steel wire and rubber. For the purpose.

The brass-plated steel wire for reinforcing rubber articles according to the present invention is a brass-plated steel wire for reinforcing rubber articles having a brass plating layer on the surface, and the brass plating layer is formed of crystal grains having a grain size of 20 nm or less. It has a qualitative part, and the composition of the brass plating layer is 55 to 66% by weight of copper and 34 to 45% by weight of zinc.
A brass-plated steel wire for reinforcing rubber articles having a brass plating layer on the surface, the brass plating layer comprising a laminated structure part in which a noncrystalline part on the surface side and an inner crystalline part are laminated, The amorphous part is formed of crystal grains having a particle diameter of 20 nm or less, the crystalline part is formed of crystal grains having a particle diameter exceeding 20 nm, and the composition of the brass plating layer is 55 to 66% by weight of copper, zinc It is also characterized by 34 to 45% by weight.
The volume ratio of the laminated structure portion to the whole brass plating layer is also 50% or more.
The ratio of the area occupied by the surface of the amorphous portion to the entire surface of the brass plating layer is 80% or more.
The area ratio of the surface of the amorphous portion of the laminated structure portion to the entire surface of the brass plating layer is 20% or more, and the volume ratio of the amorphous portion of the laminated structure portion to the entire laminated structure portion is It is also characterized by being 20% or more and 80% or less.
According to the method of manufacturing a brass-plated steel wire for reinforcing rubber articles according to the present invention, after forming a crystalline brass plating layer on the surface of the steel wire, an amorphous brass plating layer is formed on the surface of the crystalline brass plating layer. By forming, a brass plating layer having a laminated structure composed of a lower crystalline portion and a non-crystalline portion of the surface layer is formed on the surface of the steel wire.
After forming a crystalline brass plating layer on the surface of the steel wire, by strongly processing only the extreme surface layer of this crystalline brass plating layer, the lower crystalline portion and the surface layer are formed on the surface of the steel wire. The present invention is also characterized in that a brass plating layer having a laminated structure composed of non-crystalline parts is formed.

In the brass-plated steel wire of the present invention, the surface of the brass-plated layer has an amorphous part formed by crystal grains having a particle size of 20 nm or less, and the composition of the brass-plated layer is 55 to 66% by weight of copper. Since the zinc content is 34 to 45% by weight, it is possible to obtain a brass-plated steel wire having good initial adhesion performance with rubber and good adhesion durability performance.
In the brass-plated steel wire of the present invention, the surface brass-plated layer is formed of a non-crystalline portion on the surface side formed by crystal grains having a particle diameter of 20 nm or less and crystal grains having a particle diameter exceeding 20 nm. Since it has a laminated structure part in which the crystalline part on the inside is laminated and the composition of the brass plating layer is 55 to 66% by weight of copper and 34 to 45% by weight of zinc, the initial adhesion performance to rubber and the adhesion durability performance Can be obtained.
According to the brass-plated steel wire in which the volume ratio of the laminated structure portion to the entire brass-plated layer is 50% or more, it is possible to obtain a brass-plated steel wire with better initial adhesion performance and adhesion durability performance with rubber. Can do.
According to the brass-plated steel wire in which the area ratio of the surface of the amorphous portion to the entire surface of the brass-plated layer is 80% or more, a brass-plated steel wire with better initial adhesion performance with rubber is obtained. be able to.
The area ratio of the surface of the non-crystalline portion of the laminated structure portion to the entire surface of the brass plating layer is 20% or more, and the volume ratio of the non-crystalline portion of the laminated structure portion to the entire laminated structure portion is 20%. According to the brass-plated steel wire set to be not less than 80% and not more than 80%, a brass-plated steel wire having better initial adhesion performance with rubber and adhesion durability performance can be obtained.
According to the method for producing a brass-plated steel wire for reinforcing rubber articles according to the present invention, as described above, a brass-plated steel wire excellent in initial adhesion performance and adhesion durability performance with rubber can be produced.

Best form 1
Hereinafter, the structure of the brass-plated steel wire 10 will be described with reference to FIG.
The brass-plated steel wire 10 has a steel wire 12 and a brass-plated layer 11 formed on the surface of the steel wire 12. The brass plating layer 11 includes a laminated structure portion 13 in which a noncrystalline portion 11a on the front side and a crystalline portion 11b on the inner side are laminated. The amorphous part 11a is formed of crystal grains having a particle diameter of 20 nm or less. In other words, the amorphous portion 11a is a substantially amorphous portion that is formed of fine crystal grains of 20 nm or less, or has a feature that the crystal grains cannot be distinguished. The crystalline part 11b is a part formed by crystal grains having a grain size exceeding 20 nm. For example, when the backscattered electron beam pattern is taken, a clear Kikuchi pattern corresponding to the crystal orientation of Cu is obtained in the crystalline part 11b, but the amorphous part 11a does not have a clear crystal structure. The Kikuchi pattern cannot be obtained.

The brass plating layer 11 is formed of copper (Cu) and zinc (Zn), and the ratio of copper to zinc is 55 to 66% by weight of copper and 34 to 45% by weight of zinc. That is, the composition of the brass plating layer 11 is 55 to 66% by weight of copper and 34 to 45% by weight of zinc.
The reason why the composition of the brass plating layer is 55 to 66% by weight of copper and 34 to 45% by weight of zinc is that if the copper is less than 55% by weight, the number of hard and brittle β layers increases greatly during brass plating. This is because the wire drawing property is impaired, and when the copper content exceeds 66% by weight, the adhesion durability performance is remarkably impaired.
In addition, with regard to adhesion durability, the larger the amount of zinc in the bulk of the plating, the better in terms of the moisture resistance (corrosion resistance) of the plating against the ingress of deterioration factors (water, etc.) from the rubber side. This is because, in a poor wet heat degradation environment, higher adhesion durability can be obtained when the amount of zinc is large and the amount of copper is small.

  Further, the area ratio (hereinafter referred to as area ratio A) of the surface of the amorphous portion 11a of the laminated structure portion 13 with respect to the entire surface of the brass plating layer 11 was set to 80% or more.

  Furthermore, the volume ratio (hereinafter referred to as volume ratio A) of the laminated structure portion 13 with respect to the entire brass plating layer 11 was set to 50% or more.

According to the best mode 1, the brass plating layer 11 having the laminated structure portion 13 in which the amorphous portion 11a on the surface side and the crystalline portion 11b on the inner side are laminated is provided. A brass-plated steel wire 10 having an effect could be obtained.
Since the amorphous part 11a of the brass plating layer 11 has a very high lattice defect concentration, the activity is high and the diffusion rate of Cu atoms is fast. For this reason, the amorphous portion 11a of the brass-plated steel wire 10 and the rubber were brought into contact with each other in the vulcanization process when the tire was manufactured using the brass-plated steel wire 10 as an element wire of the tire reinforcing steel cord. When the brass-plated steel wire 10 is heated in the state, the adhesion reaction between the brass-plated steel wire 10 and rubber proceeds rapidly. Therefore, since the adhesive layer between the brass-plated steel wire 10 and the rubber is quickly formed in the vulcanization process, the initial adhesion performance is improved (hereinafter referred to as effect (1)). That is, in the best mode 1, it was possible to obtain a brass-plated steel wire 10 with good initial adhesion performance.
Further, even if the tire is placed in an environment (for example, a high temperature and high humidity environment) where Cu atoms are rapidly consumed at the adhesion interface after the adhesive layer is formed, Cu atoms from the amorphous portion 11a. Is promptly supplied, so that Cu atoms in the adhesive layer are prevented from being diluted and a strong adhesive layer is maintained.
Moreover, the crystalline part 11b of the brass plating layer 11 has a lower activity and a slower diffusion rate of Cu atoms than the non-crystalline part 11a. Therefore, in the case where the brass plating layer 11 includes only the non-crystalline part 11a having high activity, the brass plating / steel interface is likely to become brittle in a poor wet heat deterioration environment, and is likely to be a starting point of destruction. Therefore, in the best mode 1, by providing the crystalline portion 11b in the brass plating layer 11, the adhesion durability performance can be improved. In other words, since the brass plating layer 11 has the crystalline part 11b that gradually promotes the adhesion reaction with the rubber, the copper plating layer 11 can be used even if the reaction due to moisture or heat proceeds when the rubber article such as a tire is used. However, it was not depleted at an early stage, and the adhesion durability performance could be secured (hereinafter referred to as effect (2)).

  According to the best mode 1, since the composition of the brass plating layer 11 is 55 to 66% by weight of copper and 34 to 45% by weight of zinc, it is possible to prevent the wire drawability and adhesion durability performance from being impaired as described above. As a result, it was possible to obtain a brass-plated steel wire 10 having good drawability and adhesion durability performance.

The brass-plated steel wire 10 of the best mode 1 in which the area ratio A is 80% or more and the volume ratio A is 50% or more is, for example, only the extreme surface of the brass-plated layer of the steel wire 12 subjected to crystalline brass plating Can be manufactured by subjecting the surface of the brass plating layer to the amorphous portion 11a.
The strong processing of the extreme surface of the brass plating layer is performed, for example, by wire drawing using a die.
When lubrication is insufficient in the wire drawing process, it is known that when the work wire and the tool come into contact directly or through an incomplete film, a strong work layer is formed on the surface of the work wire. This strongly processed layer is a portion into which extremely high density lattice defects are introduced. The generation of such a hard-worked layer is generally said to cause problems such as brass plating dropout, steel wire material deterioration, or wire breakage or die wear. By processing, an extremely thin strong processing layer can be formed on the extreme surface of the brass plating layer.
For example, in order to perform wire drawing in a state where the lubricity is lowered to some extent by wet drawing using a liquid lubricating liquid, the concentration of the lubricating component in the lubricating liquid is higher than the concentration used for normal drawing. Lower the wire for drawing or lower the temperature of the lubricant below the recommended temperature for the lubricant.
Depending on the strength and wire diameter of the steel wire to be manufactured, how much the lubricity is reduced depends on the strength and wire diameter of the steel wire to be manufactured. The concentration may be 80% to 20% of the concentration of the lubricating liquid. If the lubricity is lowered too much, the brass plating may fall off, the steel wire material may deteriorate, or the wire may break or die wear. On the other hand, if the method of lowering the lubricity is insufficient, the ratio of the non-crystalline part 11a on the surface of the brass plating layer is reduced, so that the adhesiveness is deteriorated.

Also, if the heat generation during wire drawing is too large, there is a possibility that the lattice defect density of brass plating will decrease due to temperature rise and the ductility of steel wire may be deteriorated. It is preferable to set it to 150 ° C. or lower when the wire drawing conditions are set and the temperature of the outgoing wire from the die is measured with a contact-type thermometer.
・ Drawing conditions
-1 Set the area reduction per die low.
-Set the wire drawing speed lower.
-Cooling the die to suppress the temperature rise.
-Cool the wire that enters and / or exits the die.
At this time, in order to form the laminated structure portion 13 of the amorphous portion 11a and the crystalline portion 11b, it is better to increase the thickness of the brass plating layer 11.
In addition, when manufacturing by wet continuous wire drawing, wire drawing in a finishing die or several dies downstream of the wire drawing including the finishing die is performed in a state where the lubricity as described above is reduced to some extent, If the dies are used under good lubrication conditions, it is possible to reliably manufacture the brass plating layer 11 whose inside is the crystalline part 11b and whose surface is the amorphous part 11a.

  Then, the area ratio A is calculated from the degree of taking a backscattered electron pattern on the surface of the produced brass-plated steel wire 10 and obtaining a clear Kikuchi pattern corresponding to the crystal orientation of Cu, and the volume ratio A is prepared. The cross-sectional observation image of the brass-plated steel wire 10 is calculated by image analysis.

  As described above, according to the best mode 1, the brass plated steel wire 11 having an area ratio A of 80% or more and a volume ratio A of 50% or more is drawn by drawing a brass-plated steel wire with the lubricity lowered to some extent. As a result, the brass-plated steel wire 10 having both good initial adhesion performance and adhesion durability performance could be obtained.

  In the best mode 1, a steel wire having a crystalline brass plating layer formed on the surface is drawn in a state where the lubricity is lowered to some extent, and the inside is a crystalline portion 11b and the surface is amorphous. The brass plating layer 11 that is the portion 11a is formed. After forming the crystalline brass plating layer on the surface of the steel wire, the amorphous brass plating layer is formed on the surface of the crystalline brass plating layer by, for example, plasma CVD. The brass plating layer may be formed into a brass plating layer having a laminated structure including a lower layer portion made of a crystalline material and a surface layer portion made of an amorphous material. In this case, it is possible to make the outermost surface almost amorphous while maintaining the crystallinity inside the brass plating layer well.

Best form 2
When the area ratio A is 20% or more and the volume ratio (hereinafter referred to as volume ratio B) of the non-crystalline part of the laminated structure portion to the entire laminated structure part is 20% or more and 80% or less, rubber Thus, a brass-plated steel wire 10 having excellent initial adhesion performance and adhesion durability performance was obtained.
When the area ratio A was less than 20%, the effect described in the above effect (1), that is, excellent initial adhesion performance was not obtained. When the volume ratio B was less than 20%, the effects described in the above effects (1) and (2), that is, excellent initial adhesion performance and adhesion durability performance were not obtained. Furthermore, when the volume ratio B exceeded 80%, the effect described in the above effect (2), that is, excellent adhesion durability performance was not obtained. Further, when the volume ratio B was 25% or more and 75% or less, further excellent initial adhesion performance and durable adhesion performance were obtained.

Example Brass-plated steel wires of Examples 1 to 4 shown in FIG. 2 having different brass plating compositions, area ratios A and volume ratios B were produced, and the adhesion performance was evaluated. The area ratio A was calculated from the degree to which a clear Kikuchi pattern corresponding to the crystal orientation of Cu was obtained by taking a backscattered electron pattern on the surface of the produced brass-plated steel wire. The volume ratio B was calculated by image analysis of a cross-sectional observation image of the produced brass-plated steel wire. FIG. 2 shows data of each brass-plated steel wire according to Examples 1 to 4 in which the adhesive performance evaluation was performed. Regarding the adhesive performance evaluation, the initial adhesion was determined by preparing a steel cord by twisting brass plated steel wire with a wire diameter of 0.30 mm into a 1x3 structure, then arranging them in parallel at equal intervals, and coating with rubber from both sides Then, after vulcanization at 160 ° C. for 7 to 20 minutes, the steel cord was peeled off from the rubber for the obtained rubber-steel cord composite, and the rubber adhesion rate at that time was measured. The index is 100. It shows that adhesiveness is so favorable that a numerical value is large. In addition, the adhesive durability was the same as the initial adhesiveness, and after coating with rubber and vulcanizing at 160 ° C. for 20 minutes, the obtained rubber-steel cord composite was subjected to atmospheric pressure at a temperature of 75 ° C. and a humidity of 95%. The steel cord was left in the atmosphere for 7 to 14 days, and then the steel cord was peeled from the rubber. The rubber adhesion rate at that time was measured, and the result was shown as an index with Example 1 as 100. It shows that adhesiveness is so favorable that a numerical value is large. Moreover, the cross section of the brass plating steel wire 10 of Examples 1 to 4 is shown in FIG.
In Examples 2, 3, and 4, the area ratio A is 80% or more and the volume ratio B is 20% or more and 80% or less by drawing with the lubricity lowered to some extent as described above. Brass-plated steel wire 10 in which Example 1 is a brass-plated steel formed in a state where the area ratio A is less than 80% and the volume ratio B is less than 20% by drawing under good lubrication conditions. Line 10.

The following can be seen from FIG.
In Example 1, the composition of the brass plating layer 11 is 55 to 66% by weight of copper and 34 to 45% by weight of zinc, but does not satisfy the condition that the area ratio A is 80% or more, and the volume ratio B is 20%. % And 80% or less, the initial adhesion performance and adhesion durability performance are inferior to those of Examples 2 and 3.
In Examples 2 and 3, the composition of the brass plating layer 11 is 55 to 66% by weight of copper and 34 to 45% by weight of zinc, and the area ratio A is 80% or more and the volume ratio B is 20% or more and 80%. Since the following conditions were satisfied, the brass-plated steel wire 10 having good initial adhesion performance and adhesion durability performance was obtained.
In Example 4, the condition that the area ratio A is 80% or more and the volume ratio B is 20% or more and 80% or less is satisfied, but the copper is 68% by weight, the copper is 55 to 66% by weight, and the zinc 34 to Since the condition of 45% by weight is not satisfied, the adhesion durability performance is poor as compared with Examples 1, 2, and 3.

That is, the brass plating layer 11 has an amorphous portion 11a formed of crystal grains having a particle size of 20 nm or less, and the composition of the brass plating layer 11 is 55 to 66% by weight of copper and 34 to 45% by weight of zinc. % Examples 1, 2, and 3 were able to obtain a brass-plated steel wire 10 having better adhesion durability performance than that of Example 4 that did not satisfy the conditions.
In Examples 2 and 3 where the area ratio A satisfies the condition of 80% or more and the volume ratio B satisfies the condition of 20% or more and 80% or less, both the initial adhesive performance and the adhesive durability performance are good. A plated steel wire 10 could be obtained.

  Regardless of whether or not the laminated structure portion 13 is provided, the initial adhesion performance to rubber becomes better as the area ratio A is larger, so the area ratio A may be 100%.

It is a schematic diagram which shows the cross section of a brass plating steel wire (best form 1 or 2). The figure which shows the data of the brass plating steel wire by Examples 1-4. It is the figure which showed the cross section of the brass plating steel wire by Examples 1-4.

Explanation of symbols

10 brass-plated steel wire, 11 brass-plated layer, 11a amorphous part,
11b Crystalline part, 12 steel wire, 13 laminated structure part.

Claims (7)

  A brass-plated steel wire for reinforcing rubber articles having a brass plating layer on the surface, wherein the brass plating layer has an amorphous portion formed by crystal grains having a particle size of 20 nm or less, and the composition of the brass plating layer is A brass-plated steel wire for reinforcing rubber articles, comprising 55 to 66% by weight of copper and 34 to 45% by weight of zinc.   A brass-plated steel wire for reinforcing rubber articles having a brass plating layer on the surface, the brass plating layer comprising a laminated structure part in which a noncrystalline part on the surface side and an inner crystalline part are laminated, The amorphous part is formed of crystal grains having a particle diameter of 20 nm or less, the crystalline part is formed of crystal grains having a particle diameter exceeding 20 nm, and the composition of the brass plating layer is 55 to 66% by weight of copper, zinc A brass-plated steel wire for reinforcing rubber articles, characterized by being 34 to 45% by weight.   3. The brass-plated steel wire for reinforcing rubber articles according to claim 2, wherein the volume ratio of the laminated structure portion to the entire brass-plated layer is 50% or more.   The brass plating for reinforcing rubber articles according to any one of claims 1 to 3, wherein an area ratio of the surface of the amorphous portion to the entire surface of the brass plating layer is 80% or more. Steel wire.   The area ratio of the surface of the amorphous portion of the laminated structure portion to the entire surface of the brass plating layer is 20% or more, and the volume ratio of the amorphous portion of the laminated structure portion to the entire laminated structure portion is The brass-plated steel wire for reinforcing rubber articles according to claim 2, wherein the brass-plated steel wire is 20% or more and 80% or less.   A method for producing a brass-plated steel wire for reinforcing rubber articles according to any one of claims 1 to 5, wherein a crystalline brass-plated layer is formed on the surface of the steel wire, and then the crystalline brass is formed. By forming an amorphous brass plating layer on the surface of the plating layer, a brass plating layer having a laminated structure consisting of a lower crystalline portion and a non-crystalline portion of the surface layer is formed on the surface of the steel wire. A method of manufacturing a brass-plated steel wire for reinforcing rubber articles, characterized by being formed.   A method for producing a brass-plated steel wire for reinforcing rubber articles according to any one of claims 1 to 5, wherein a crystalline brass-plated layer is formed on the surface of the steel wire, and then the crystalline brass is formed. By carrying out strong processing only on the extreme surface layer of the plating layer, a brass plating layer having a laminated structure consisting of a crystalline part of the lower layer and an amorphous part of the surface layer was formed on the surface of the steel wire. A method for producing a brass-plated steel wire for reinforcing rubber articles.