JP2008063683A - Thread-containing print paper and printed product using the same - Google Patents

Thread-containing print paper and printed product using the same Download PDF

Info

Publication number
JP2008063683A
JP2008063683A JP2006241483A JP2006241483A JP2008063683A JP 2008063683 A JP2008063683 A JP 2008063683A JP 2006241483 A JP2006241483 A JP 2006241483A JP 2006241483 A JP2006241483 A JP 2006241483A JP 2008063683 A JP2008063683 A JP 2008063683A
Authority
JP
Japan
Prior art keywords
paper
thread
layer
printing paper
threaded
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2006241483A
Other languages
Japanese (ja)
Inventor
Mikihiko Sakakibara
幹彦 榊原
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dai Nippon Printing Co Ltd
Original Assignee
Dai Nippon Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dai Nippon Printing Co Ltd filed Critical Dai Nippon Printing Co Ltd
Priority to JP2006241483A priority Critical patent/JP2008063683A/en
Publication of JP2008063683A publication Critical patent/JP2008063683A/en
Pending legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide thread-containing print paper which prevents forgery and can be formed at a low cost, and to provide a printed product using the same. <P>SOLUTION: In the thread-containing print paper produced by adding threads at a step for making base paper for the prevention of forgery, the threads are formed between the front side paper layer and the back side paper layer of the base paper, and in the front and back side paper layers, unit openings having a size for exposing all the threads in a width direction are formed at thread-formed positions at a prescribed interval, and the unit openings formed on the front and back sides are arranged so that the unit openings are partially overlapped in a prescribed cycle. A printed product uses the thread-containing print paper in which the threads are formed along the shorter side of the printed product. <P>COPYRIGHT: (C)2008,JPO&INPIT

Description

本発明は、偽造防止のために基紙の抄紙段階でスレッドが抄きこまれたスレッド入り印刷用紙及びこのスレッド入り印刷用紙を使用した印刷物に関する。   The present invention relates to a threaded printing paper in which threads are made at the paper making stage of a base paper to prevent counterfeiting, and a printed matter using the threaded printing paper.

従来から、紙の層間にスレッドと呼ばれるプラスチックの薄い帯、または、金糸等を挿入した偽造防止用紙が紙幣をはじめとする有価証券類に多く使用されてきた。
有価証券のような認証のための証書には、偽造・改竄防止のために、その証書の面（以下、券面という）に細かい幾何学模様の印刷や、インキが盛り上がる凹版インキによる印刷が行われている。
また、普通の状態では目視できないが、ブラックライトにより紫外線を照射すると、蛍光を発色し、隠れていた図柄等が見えてくる蛍光インキを使用した印刷等も行われている。
さらに、高度な技術によって作製されたホログラムをプラスチックフィルム上に形成し、スレッド状にして用紙の間に抄き込んで偽造防止用紙として使用する方法や、紙の表面に前記ホログラム形成層を転写して偽造防止手段として使用する方法が実用され始めた。
前記スレッド入り用紙に関しては、偽造防止効果をより高めるために、スレッドの幅を広くしてスレッドを見やすくしたり、スレッドを複数にする試みが行われている。
しかし、スレッドの幅を広くすると、スレッドの価格が高くなりコストアップとなる。
また、商品券等において、スレッドが見えている面の裏面の偽造防止を強化するとなると、さらにホログラムの箔を設ける等をしなければならず、やはりコストアップとなる。
そこで、偽造防止用紙に窓を設け、スレッドを表裏両方の面から見えるようにした「スレッド入り偽造防止用紙」が提供されている（例えば、特許文献１参照）。
この「スレッド入り偽造防止用紙」は、図９に示すような、スレッド紙１００に、表裏を貫通する開口部（窓）３０を設け、表裏からスレッド２０を確認できるようにしたものである。また、窓の部分を独特な形状にすることで、意匠性を高めることにより偽造・改竄を一層困難にすることができるとしている。 2. Description of the Related Art Conventionally, anti-counterfeit paper in which a thin plastic band called a thread or a gold thread or the like is inserted between paper layers has been widely used for securities such as banknotes.
In order to prevent counterfeiting and falsification, securities such as securities are printed with a fine geometric pattern on the side of the certificate (hereinafter referred to as a ticket) or with intaglio ink that swells the ink. ing.
In addition, although it cannot be visually observed in a normal state, printing using fluorescent ink, which emits fluorescence when irradiated with ultraviolet light from a black light and allows a hidden pattern or the like to be seen, is also performed.
In addition, a hologram produced by advanced technology is formed on a plastic film, threaded into a sheet of paper and used as an anti-counterfeit paper, or the hologram forming layer is transferred to the surface of the paper. The method of using it as a means for preventing forgery has begun to be put into practical use.
With regard to the threaded paper, attempts have been made to increase the width of the thread so that the thread can be easily seen, or to use a plurality of threads in order to further enhance the forgery prevention effect.
However, if the width of the thread is widened, the price of the thread increases and the cost increases.
In addition, in a gift certificate or the like, if forgery prevention on the back side of the surface where the thread is visible is strengthened, it is necessary to further provide a foil of the hologram, which also increases the cost.
In view of this, there has been provided a “thread-forgery-preventing paper” in which a window is provided on the anti-counterfeit paper so that the thread can be seen from both the front and back surfaces (see, for example, Patent Document 1).
This “anti-counterfeit paper with a thread” is such that an opening (window) 30 penetrating the front and back is provided on the thread paper 100 as shown in FIG. 9 so that the thread 20 can be confirmed from the front and back. In addition, it is said that forging and tampering can be made more difficult by enhancing the design by making the window part unique.

特開２００１−１７２８９７号公報JP 2001-172897 A

特許文献１に開示されている技術は、表裏の偽造防止効果を高めるために用紙の表裏を貫通する開口部を設け、そこにスレッドを通したに過ぎない。
そこで本発明のスレッド入り印刷用紙及びこれを使用した印刷物は、さらに、偽造を困難にしたスレッド入り印刷用紙、および、これを使用した安価な印刷物を提供することを目的とするものである。 The technique disclosed in Patent Document 1 is merely provided with an opening penetrating the front and back sides of the paper in order to enhance the forgery prevention effect on the front and back sides, and a thread is passed therethrough.
Therefore, the threaded printing paper and the printed material using the same of the present invention are further intended to provide a threaded printing paper that is difficult to forge and an inexpensive printed material using the threaded printing paper.

前記課題の目的を達成するために、本発明のスレッド入り印刷用紙の第一の態様は、偽造防止のために基紙の抄紙段階でスレッドが抄きこまれたスレッド入り印刷用紙であって、スレッドは、基紙の表側紙層と裏側紙層の間に形成され、前記表側紙層と前記裏側紙層には、スレッドが形成された位置に、スレッドを幅方向に全て表出する大きさの単位開口部が所定の間隔で形成され、表裏に形成された単位開口部の一部が、所定の周期で重なり合うように配置されたことを特徴とするものである。   In order to achieve the above object, the first aspect of the threaded printing paper of the present invention is a threaded printing paper in which threads are engraved in the papermaking stage of the base paper to prevent counterfeiting. Is formed between the front side paper layer and the back side paper layer of the base paper, and the front side paper layer and the back side paper layer have a size that exposes all the threads in the width direction at the positions where the threads are formed. The unit openings are formed at a predetermined interval, and part of the unit openings formed on the front and back surfaces are arranged so as to overlap each other with a predetermined period.

また、第二の態様は、第一の態様において、スレッドはセキュリティ表示部が形成された透明なプラスチックフィルムからなり、スレッドの少なくとも表裏何れかの表出面に接着剤層が形成されたことを特徴とするものである。   The second aspect is characterized in that, in the first aspect, the thread is made of a transparent plastic film on which a security indicator is formed, and an adhesive layer is formed on at least one of the exposed surfaces of the thread. It is what.

また、第三の態様は、第一の態様において、セキュリティ表示部は、樹脂部と反射層からなる光回折構造又は文字を含むパターン、変色インキ、印刷図柄、の何れか又はこれらの組み合わせが形成されたことを特徴とするものである。   Further, the third aspect is the first aspect, in which the security display part is formed by any one of a light diffraction structure or a pattern including characters, a discoloration ink, a printed pattern, or a combination thereof composed of a resin part and a reflective layer. It is characterized by that.

また、第四の態様は、第一，第二，第三に記載のスレッド入り印刷用紙を使用した印刷物であって、スレッドは、印刷物の短辺に沿って形成されたことを特徴とするものである。   Further, a fourth aspect is a printed matter using the threaded printing paper described in the first, second, and third, wherein the thread is formed along the short side of the printed matter. It is.

１）本発明のスレッド入り印刷用紙の第一の態様のように、偽造防止のために基紙の抄紙段階でスレッドが抄きこまれたスレッド入り印刷用紙であって、スレッドは、基紙の表側紙層と裏側紙層の間に形成され、前記表側紙層と前記裏側紙層には、スレッドが形成された位置に、スレッドを幅方向に全て表出する大きさの単位開口部が所定の間隔で形成され、表裏に形成された単位開口部の一部が、所定の周期で重なり合うように配置されたことによって、片側だけにスレッドが表出するものや、単に表裏貫通する開口部が形成されたものと比較して極めて偽造困難なスレッド入り印刷用紙とすることができる。また、抄紙工程でスレッドが抄き込まれるためにスレッドによる凹凸が発生しないスレッド入り印刷用紙とすることができる。
２）また、第二の態様にように、第一の態様において、スレッドはセキュリティ表示部が形成された透明なプラスチックフィルムからなり、スレッドの少なくとも表裏何れかの表出面に接着剤層が形成されたことによって、基紙からスレッドを引き抜くことができなく、偽造困難なスレッド入り印刷用紙とすることができる。
３）また、第三の態様のように、第一の態様において、セキュリティ表示部は、樹脂部と反射層からなる光回折構造又は文字を含むパターン、変色インキ、印刷図柄、の何れか又はこれらの組み合わせが形成されたことによって、スレッドにバリエーションを与えることができる。
４）また、第四の態様のように、第一，第二，第三に記載のスレッド入り印刷用紙を使用した印刷物であって、スレッドは、印刷物の短辺に沿って形成されたことによって、スレッドの長さを短い状態で使用することができ、印刷物の単価を低く抑えることができる。 1) As in the first aspect of the threaded printing paper of the present invention, the threaded printing paper in which the thread is formed at the paper making stage of the base paper to prevent forgery, the thread being the front side of the base paper A unit opening portion is formed between the paper layer and the back side paper layer, and the front side paper layer and the back side paper layer have a unit opening having a size that exposes all the threads in the width direction at a position where the threads are formed. A part of unit openings formed on the front and back sides are arranged so as to overlap each other with a predetermined period, so that threads are exposed only on one side, or openings that pass through the front and back are formed. Therefore, it is possible to obtain a threaded printing paper that is extremely difficult to counterfeit compared to the printed one. In addition, since the thread is made in the paper making process, it is possible to obtain a threaded printing paper in which unevenness due to the thread does not occur.
2) Further, as in the second aspect, in the first aspect, the thread is made of a transparent plastic film on which a security indicator is formed, and an adhesive layer is formed on at least one of the exposed surfaces of the thread. As a result, the thread cannot be pulled out from the base paper, and a threaded printing paper that is difficult to forge can be obtained.
3) Further, as in the third aspect, in the first aspect, the security display portion is either a light diffraction structure or a pattern including characters, a discoloration ink, a printed design, or a print pattern composed of a resin portion and a reflective layer. As a result of forming the combination, variations can be given to the threads.
4) Further, as in the fourth aspect, the printed matter uses the threaded printing paper described in the first, second, and third, and the thread is formed along the short side of the printed matter. The thread can be used in a short state, and the unit price of the printed matter can be kept low.

以下、図面を参照して、本発明のスレッド入り印刷用紙及びこれを使用した印刷物について説明する。
図１は、本発明のスレッド入り印刷用紙の一例について説明するための図，図２は、図１のＡ−Ａ線断面図，図３は、本発明のスレッド入り印刷用紙の他の一例について説明するための図，図４は、図３のＸ−Ｘ線断面図，図５は、図３のＹ−Ｙ線断面図，図６は、スレッドの一例について説明するための図，図７は、抄紙機の一例について説明するための図，図８は、開口部及びスレッドの位置精度について説明するための図，図９は、従来のスレッド入り偽造防止用紙の一例について説明するための図，である。
以下の説明では、スレッドの一例として透明なプラスチックフィルムに光回折構造が形成され、反射層を伴ったスレッドの例で説明する。 Hereinafter, a threaded printing paper of the present invention and a printed matter using the same will be described with reference to the drawings.
1 is a diagram for explaining an example of a threaded printing paper of the present invention, FIG. 2 is a cross-sectional view taken along line AA of FIG. 1, and FIG. 3 is another example of the threaded printing paper of the present invention. FIG. 4 is a sectional view taken along line XX of FIG. 3, FIG. 5 is a sectional view taken along line YY of FIG. 3, and FIG. 6 is a diagram illustrating an example of a thread. FIG. 8 is a diagram for explaining an example of a paper machine, FIG. 8 is a diagram for explaining positional accuracy of an opening and a thread, and FIG. 9 is a diagram for explaining an example of a conventional anti-counterfeit paper with a thread. ,
In the following description, a light plastic structure is formed on a transparent plastic film as an example of a thread, and the example of a thread with a reflective layer will be described.

図１を参照して、本発明のスレッド入り印刷用紙の一例について説明する。
本発明のスレッド入り印刷用紙１は、帯状のスレッド２が基紙の表裏面に表出する状態で抄きこまれたスレッド入り印刷用紙である。
即ち、スレッド入り印刷用紙１の表から見た場合は、スレッド２が表開口部３ｂから裏側を構成する基紙（以下、裏側紙層という）１１上に、幅方向が全て視認される状態で表出し、スレッド入り印刷用紙１の裏から見た場合は、スレッド２が裏開口部３ｃから表側を構成する基紙（以下、表側紙層という）１２上に幅方向が全て視認される状態で表出する。
また、一定の周期で表裏を貫通した表裏開口部３ａの間に浮んだ状態で表出する。
表側紙層１２、裏側紙層１１に形成された開口部は、単位開口部３が１〜複数連なった状態で構成される。例えば、図１の表開口部３ｂは、表裏開口部３ａを含め、４つの単位開口部３で構成されて形成されており、裏開口部３ｃは、表裏開口部３ａを含め、１つの単位開口部３で構成され、形成されている。
図１において、表裏開口部３ａと裏開口部３ｃの間には、開口部が形成されておらず表裏からスレッド２が視認されない部分（１単位開口部で形成されている）になっている。 With reference to FIG. 1, an example of threaded printing paper of the present invention will be described.
The threaded printing paper 1 of the present invention is a threaded printing paper that has been engraved in a state where the belt-like thread 2 is exposed on the front and back surfaces of the base paper.
That is, when viewed from the front side of the threaded printing paper 1, the thread 2 is in a state where all the width directions are visually recognized on a base paper (hereinafter referred to as a back side paper layer) 11 constituting the back side from the front opening 3 b. When viewed from the back of the printing paper 1 with threading, the thread 2 is in a state where all the width directions are visually recognized on the base paper (hereinafter referred to as the front paper layer) 12 constituting the front side from the back opening 3c. Express.
Moreover, it appears in the state which floated between the front and back opening part 3a which penetrated the front and back with a fixed period.
The openings formed in the front-side paper layer 12 and the back-side paper layer 11 are configured in a state in which one or more unit openings 3 are connected. For example, the front opening 3b in FIG. 1 includes four unit openings 3 including the front and back openings 3a, and the back opening 3c includes one unit opening including the front and back openings 3a. It consists of part 3 and is formed.
In FIG. 1, an opening is not formed between the front and back opening 3a and the back opening 3c, and the thread 2 is not visible from the front and back (formed with one unit opening).

印刷部４には、図に示すような「商品券」の文字や、「１０，０００円」の金額が印刷されている。図示しないが、スレッド入り印刷用紙１の表裏にも上記の印刷部４の他にデザインや注意文言などの印刷部が形成される。
図に示すように、スレッド２は、印刷物の短辺に沿って形成されたことによって、スレッドの長さを短い状態で使用することができ、印刷物の単価を低く抑えることができる。 The printing unit 4 is printed with the characters “gift certificate” as shown in the figure and the amount of “10,000 yen”. Although not shown, in addition to the printing unit 4 described above, printing units such as designs and caution words are formed on the front and back sides of the threaded printing paper 1.
As shown in the figure, since the thread 2 is formed along the short side of the printed material, the thread 2 can be used in a short state, and the unit price of the printed material can be kept low.

図２を参照して、図１のＡ−Ａ線断面について説明する。
本発明のスレッド入り印刷用紙１に使用される基紙は、先ず、抄紙の最初のユニットで裏側紙層１１が抄紙機の毛布上に形成され、次のユニットで、表側紙層１２が裏側紙層１１の上に積層されて抄紙される。
裏側紙層１１が抄紙機の毛布上に形成される際に、開口部３ｃが同時に形成され、表側紙層１２が積層される際に、スレッド２を一緒に抄き込み、開口部３ｂが同時に形成される。 With reference to FIG. 2, the AA line cross section of FIG. 1 is demonstrated.
In the base paper used for the threaded printing paper 1 of the present invention, the back side paper layer 11 is first formed on the blanket of the paper machine in the first unit of paper making, and the front side paper layer 12 is the back side paper in the next unit. The paper is laminated on the layer 11 and made.
When the back side paper layer 11 is formed on the blanket of the paper machine, the opening 3c is formed at the same time, and when the front side paper layer 12 is laminated, the thread 2 is made together and the opening 3b is simultaneously formed. It is formed.

図２で、矢印３Ｂの方向には表開口部３ｂを通して、また、矢印３Ａの方向には表裏開口部３ａを通して、また、矢印３Ｃの方向には裏開口部３ｃを通して、スレッド２が視認される。
矢印１１ＡＣの方向には表側紙層１２，裏側紙層１１いずれにも開口部が形成されておらず、スレッド２を視認することができない。 In FIG. 2, the thread 2 is visually recognized through the front opening 3b in the direction of the arrow 3B, through the front and back opening 3a in the direction of the arrow 3A, and through the back opening 3c in the direction of the arrow 3C. .
No opening is formed in either the front paper layer 12 or the back paper layer 11 in the direction of the arrow 11AC, and the thread 2 cannot be visually recognized.

図３を参照して、本発明のスレッド入り印刷用紙の他の一例について説明する。
本発明のスレッド入り印刷用紙１は、帯状のスレッド２が基紙の表裏面に表出する状態で抄きこまれたスレッド入り印刷用紙である。
即ち、スレッド入り印刷用紙１の表から見た場合は、表開口部３ｂから裏側紙層１１上にスレッド２が幅方向が全て視認される状態で表出し、スレッド入り印刷用紙１の裏から見た場合は、裏開口部３ｃから表側紙層１２上にスレッド２が幅方向が全て視認される状態で表出する。
また、一定の周期で表裏を貫通した表裏開口部３ａの間にスレッド２が浮んだ状態で表出する。
表側紙層１２、裏側紙層１１に形成された開口部は、単位開口部３が２つ連なった状態で構成される。例えば、図３の表開口部３ｂ，裏開口部３ｃ共に、表裏開口部３ａを含め、２つの単位開口部３で構成されて形成されている。
図３に示すスレッド入り印刷用紙の例では、図１の例で説明したような、スレッド２が表裏いずれからも視認されない部分は存在しない。
即ち、図３に示す例のように表側紙層１２、裏側紙層１１に単位開口部３が２つ連なった状態で構成される開口部を形成する場合、抄紙の際に高い精度が要求され、精度が保たれない場合には、１単位開口部毎に１単位開口部より小さい大きさの表裏開口部３ａが発現する。 With reference to FIG. 3, another example of threaded printing paper of the present invention will be described.
The threaded printing paper 1 of the present invention is a threaded printing paper that has been engraved in a state where the belt-like thread 2 is exposed on the front and back surfaces of the base paper.
That is, when viewed from the front side of the threaded printing paper 1, the thread 2 is exposed from the front opening 3 b on the back side paper layer 11 in a state where all the width directions are visually recognized, and viewed from the back side of the threaded printing paper 1. In such a case, the thread 2 is exposed from the back opening 3c onto the front side paper layer 12 in a state where all the width directions are visually recognized.
Further, the thread 2 is exposed in a state where it floats between the front and back openings 3a penetrating the front and back at regular intervals.
The openings formed in the front-side paper layer 12 and the back-side paper layer 11 are configured in a state where two unit openings 3 are connected. For example, both the front opening 3b and the back opening 3c in FIG. 3 are formed of two unit openings 3 including the front and back openings 3a.
In the example of the threaded printing paper shown in FIG. 3, there is no portion where the thread 2 is not visually recognized from both the front and back sides as described in the example of FIG.
That is, when an opening composed of two unit openings 3 is formed in the front side paper layer 12 and the back side paper layer 11 as in the example shown in FIG. 3, high accuracy is required during paper making. When the accuracy cannot be maintained, the front and back opening 3a having a size smaller than one unit opening appears for each unit opening.

図４を参照して、図３のＡ−Ａ線断面について説明する。
図２で説明したように、本発明のスレッド入り印刷用紙１に使用される基紙は、先ず、抄紙の最初のユニットで裏側紙層１１が抄紙機の毛布上に形成され、次のユニットで表側紙層１２が裏側紙層１１の上に積層されて抄紙される。
裏側紙層１１が抄紙機の毛布上に形成される際に開口部３ｃが同時に形成され、表側紙層１２が積層される際にスレッド２を一緒に抄き込み開口部３ｂも同時に形成される。 With reference to FIG. 4, the AA line cross section of FIG. 3 is demonstrated.
As described with reference to FIG. 2, the base paper used for the threaded printing paper 1 of the present invention is the first unit of paper making, the back side paper layer 11 being formed on the blanket of the paper machine, and the next unit. The front side paper layer 12 is laminated on the back side paper layer 11 to make paper.
When the back side paper layer 11 is formed on the blanket of the paper machine, the opening 3c is formed at the same time, and when the front side paper layer 12 is laminated, the thread 2 is made together and the opening 3b is also formed at the same time. .

図４で、矢印３Ｂの方向には表開口部３ｂを通して、また、矢印３Ａの方向には表裏開口部３ａを通して、また、矢印３Ｃの方向には裏開口部３ｃを通して、スレッド２が視認される。   In FIG. 4, the thread 2 is visually recognized through the front opening 3b in the direction of the arrow 3B, through the front and back opening 3a in the direction of the arrow 3A, and through the back opening 3c in the direction of the arrow 3C. .

図５を参照して、図３のＹ−Ｙ線断面について説明する。
本発明のスレッド入り印刷用紙１は、表側紙層１２と、裏側紙層１１が積層された状態で形成されている。
開口部３ｂは、表側紙層１２と、裏側紙層１１が抄紙される際に同時に形成される。
また、スレッド２は、裏側紙層１１の上部に表側紙層１２が積層される際に、抄き込まれる。したがって、開口部３ｂの周縁は、紙の繊維が溶かされた構造になっているために直線状にはなっていない。
図示しないが、スレッド２は、裏側紙層１１に接着剤によって固定されている。 With reference to FIG. 5, the YY line cross section of FIG. 3 is demonstrated.
The threaded printing paper 1 of the present invention is formed in a state where a front side paper layer 12 and a back side paper layer 11 are laminated.
The opening 3b is formed simultaneously when the front side paper layer 12 and the back side paper layer 11 are made.
Further, the thread 2 is incorporated when the front side paper layer 12 is laminated on the upper side of the back side paper layer 11. Accordingly, the periphery of the opening 3b is not linear because the paper fibers are melted.
Although not shown, the thread 2 is fixed to the back paper layer 11 with an adhesive.

図６を参照して、スレッドの一例について説明する。
スレッド２は、透明なプラスチックフィルム２２の表出する面に接着剤層２１が形成され、その反対面に樹脂層２２が形成されている。
本実施の形態で説明するスレッドは、光回折構造であるために、樹脂層２２には微細な凹凸が形成され、樹脂層２２の表面には透明または不透明の反射層２４が形成される。さらに、反射層２４の表面には接着剤層２５が形成される。
接着剤層２１，２５には、水溶性又は熱可塑性の接着剤が形成され、スレッド２とスレッド入り印刷用紙基紙とを接着する役割を担う。
接着剤層２１は、スレッド２とスレッド入り印刷用紙基紙の表側紙層１２を接着する役割を担い、接着剤層２５は、スレッド２とスレッド入り印刷用紙基材の裏側紙層１１を接着する役割を担う。 An example of a thread will be described with reference to FIG.
The thread 2 has an adhesive layer 21 formed on the surface of the transparent plastic film 22 exposed, and a resin layer 22 formed on the opposite surface.
Since the thread described in this embodiment has an optical diffraction structure, fine irregularities are formed on the resin layer 22, and a transparent or opaque reflective layer 24 is formed on the surface of the resin layer 22. Further, an adhesive layer 25 is formed on the surface of the reflective layer 24.
A water-soluble or thermoplastic adhesive is formed on the adhesive layers 21 and 25 and serves to bond the thread 2 and the threaded printing paper base paper.
The adhesive layer 21 serves to bond the thread 2 and the front side paper layer 12 of the threaded printing paper base paper, and the adhesive layer 25 bonds the thread 2 and the back side paper layer 11 of the threaded printing paper base material. Take a role.

基紙とスレッド２の接着のための接着剤層が水溶性の接着剤で構成された場合は、基紙が製造されている途中で活性化されて接着性を発現する。
また、接着剤層が熱可塑性の接着剤で構成された場合は、基紙が乾燥装置の中で活性化され接着性を発現する。
抄紙の工程で、艶出し工程がある場合は、艶出しユニットでより接着を強固にする。 When the adhesive layer for bonding the base paper and the thread 2 is made of a water-soluble adhesive, the base paper is activated while the base paper is being manufactured and develops adhesiveness.
Further, when the adhesive layer is composed of a thermoplastic adhesive, the base paper is activated in the drying device and develops adhesiveness.
If there is a glazing process in the paper making process, the glazing unit will make the bond stronger.

ここで、スレッド２を構成する光回折構造について説明する。
光回折構造には、光回折構造が形成されたベースフィルム毎使用される場合と、光回折構造が形成された樹脂部だけが対象物に転写されて使用される二つの場合がある。
光回折構造がベースフィルム毎使用される場合は、ベースフィルムの片側に熱硬化性の樹脂層が形成され、熱硬化性の樹脂層に凹凸構造が形成され、凹凸構造の上に反射層が形成され、その上に粘着剤層または接着剤層が形成され、テープ状にスリットされ、またはラベル状に打ち抜かれて使用される。
光回折構造が形成された樹脂部だけが対象物に転写されて使用される場合は、耐熱性を有する基材フィルム上に剥離層が形成され、その上に、例えば、熱硬化性の樹脂層が形成され、熱硬化性の樹脂層に凹凸構造が形成され、反射層が形成され、その上に感熱接着剤層が形成されて、熱せられた金属の型等によって、接着剤層を含めた極めて薄い光回折構造形成層が紙などの印刷物上に転写されて使用される。 Here, the light diffraction structure constituting the thread 2 will be described.
There are two cases where the light diffraction structure is used for each base film on which the light diffraction structure is formed and where only the resin portion on which the light diffraction structure is formed is transferred to an object.
When the optical diffraction structure is used for each base film, a thermosetting resin layer is formed on one side of the base film, an uneven structure is formed on the thermosetting resin layer, and a reflective layer is formed on the uneven structure Then, an adhesive layer or an adhesive layer is formed thereon, slit into a tape shape, or punched into a label shape for use.
When only the resin part in which the light diffraction structure is formed is transferred to an object and used, a release layer is formed on a heat-resistant base film, and, for example, a thermosetting resin layer is formed thereon. An uneven structure is formed on a thermosetting resin layer, a reflective layer is formed, a heat-sensitive adhesive layer is formed thereon, and an adhesive layer is included depending on a heated metal mold or the like. An extremely thin light diffraction structure forming layer is used by being transferred onto a printed material such as paper.

前記反射層は、前述の光回折構造形成層の凹凸面に反射性を与えるために設けられる。反射層には、不透明な反射層と、透明性を有する反射層とがあるが、意匠効果を高める手段として使用する場合は、アルミニウムや、ニッケルなどの金属による不透明な反射層を形成する。反射層を形成する方法としては、真空蒸着法，スパッタリング法，イオンブレーティング法等があり、目的によって使い分ける。   The reflective layer is provided to provide reflectivity to the uneven surface of the light diffraction structure forming layer. The reflective layer includes an opaque reflective layer and a transparent reflective layer, but when used as a means for enhancing the design effect, an opaque reflective layer made of metal such as aluminum or nickel is formed. As a method for forming the reflective layer, there are a vacuum vapor deposition method, a sputtering method, an ion plating method, and the like, which are properly used depending on the purpose.

また、剥離層，熱硬化性樹脂層，接着剤層，粘着剤層等の形成手段として、グラビアコート，ダイコート，ナイフコート，ロールコート等の一般的なコーティング方法、および、シルクスクリーン等の印刷方法等があり、その中から選択して使用する。   In addition, as a means for forming a release layer, a thermosetting resin layer, an adhesive layer, an adhesive layer, etc., a general coating method such as gravure coating, die coating, knife coating, roll coating, etc., and a printing method such as silk screen Etc., and select from among them.

スレッド２の樹脂層２３，反射層２４の部分は、前述の光回折構造を形成する以外に、文字を含むパターン形成部、また、変色インキを使用した印刷部，通常の印刷図柄等を印刷した印刷部で構成することができる。
文字を含むパターン部と使用する場合、マイクロ文字をあしらったパターンや、これらパターンに反射層を付加し、金属光沢を付与したりして使用することができる。
変色インキを使用した印刷部として使用する場合は、例えば特殊な波長領域で発色するインキを用いたり、角度を変化させると異なる色で反射する液晶インキを用いて使用することができる。
また、通常の印刷図柄等を印刷した印刷部で構成する場合は、例えば、図１で例示した商品券に関連する印刷内容や、金額などを隠し文字として印刷し、使用することができる。 In addition to forming the light diffraction structure described above, the resin layer 23 and the reflective layer 24 of the thread 2 were printed with a pattern forming part including characters, a printing part using discoloration ink, a normal printing pattern, and the like. It can be composed of a printing unit.
When used with a pattern portion including characters, a pattern with micro characters or a reflective layer added to these patterns to give a metallic luster can be used.
When used as a printing section using a color-changing ink, for example, an ink that develops color in a special wavelength region can be used, or a liquid crystal ink that reflects in a different color when the angle is changed can be used.
Moreover, when it comprises with the printing part which printed the normal printing design etc., the printing content relevant to the gift certificate illustrated in FIG. 1, an amount, etc. can be printed and used as a hidden character, for example.

図７，図８を参照して、抄紙機の一例と開口部及びスレッドの位置精度について説明する。
図７は、本発明のスレッド入り印刷用紙基紙の製造に使用する円網型抄紙機の一例を示す概念図である。
紙料懸濁液が入った糟５１０の円網シリンダー５１の上網には、裏側紙層の開口部に相当する型を金属，樹脂，紙等で作製し、取り付ける。
開口部に相当する型の形状は、長方形，正方形，円等任意の形状とすることができる。
糟５１０の円網シリンダー５１の上網を装着した円網シリンダーで吸い上げた裏側紙層の紙料は毛布５４に転移され、円網シリンダー５２の槽５２０の上に運ばれ、円網シリンダー５２で吸い上げられた表側紙層がその上に重ねられ、２つの紙層が抄合わされてスレッド入り印刷用紙の基紙が抄造される。
スレッド２の挿入は、裏側紙層に表側紙層が積層される直前で行われる。
裏側紙層と裏側紙層とが積層された基紙１０は、毛布５４に転移された状態で抄紙機の乾燥装置５３の中に移動する。 With reference to FIGS. 7 and 8, an example of a paper machine and the positional accuracy of the opening and the thread will be described.
FIG. 7 is a conceptual diagram showing an example of a circular net type paper machine used for manufacturing a threaded printing paper base paper of the present invention.
A mold corresponding to the opening of the back paper layer is made of metal, resin, paper, and the like on the upper net of the circular cylinder 51 of the basket 510 containing the stock suspension.
The shape of the mold corresponding to the opening can be an arbitrary shape such as a rectangle, a square, or a circle.
The paper material of the back side paper layer sucked up by the circular net cylinder equipped with the upper net of the circular net cylinder 51 of 糟 510 is transferred to the blanket 54 and is carried onto the tank 520 of the circular net cylinder 52 and sucked up by the circular net cylinder 52. The obtained front side paper layer is overlaid thereon, and the two paper layers are combined to form the base paper of the threaded printing paper.
The insertion of the thread 2 is performed immediately before the front side paper layer is laminated on the back side paper layer.
The base paper 10 on which the back side paper layer and the back side paper layer are laminated moves into the drying device 53 of the paper machine while being transferred to the blanket 54.

図８に示す例は、裏側紙層１１と裏側紙層１２とが積層された時点で、開口部３ｂ，３ｃが微妙にずれて積層された状態を示している。また、スレッド２が抄き込まれた位置も、必ずしも開口部の中央部にはなっていない。したがって、基紙の断面は、図２，図４で説明したようなきれいな状態にはなっていないことが多い。
このことは、基紙の流れ方向に対しても言える。 The example shown in FIG. 8 shows a state in which the openings 3b and 3c are slightly shifted and laminated when the back paper layer 11 and the back paper layer 12 are laminated. Further, the position where the thread 2 is engraved is not necessarily the center of the opening. Therefore, the cross section of the base paper is often not in a clean state as described with reference to FIGS.
This is also true for the flow direction of the base paper.

（使用材料）
本発明のスレッド入り印刷用紙には、有価証券で利用される坪量７０〜１５０ｇ／ｍ2の基紙を使用される。そのため、表側紙層と裏側紙層のつけ比率は、１０：５０〜２５：１２０の範囲内で行う。
また、紙料は、ＮＢＫＰ，ＬＢＫＰに、白土，紙力増強剤，サイズ剤，硫酸バンドを適量加え調製する。
セキュリティ表示部分にホログラムを形成するスレッドは、厚さ１６〜２５μｍのプラスチックフィルムに、厚さ２〜６μｍの熱硬化性の樹脂層を形成し、樹脂層に光回折構造を形成し、光回折構造の表面に厚さ０．０４〜０．０８μｍのアルミニウム等による不透明な反射層を形成し、反射層上及びプラスチックフィルムの表面にビニル系の感熱接着剤を５〜１０μｍの厚さに塗工し、スリッターで帯状にスリットして作製する。 (Materials used)
As the threaded printing paper of the present invention, a base paper having a basis weight of 70 to 150 g / m 2 used for securities is used. Therefore, the attachment ratio of the front side paper layer and the back side paper layer is set within a range of 10:50 to 25: 120.
The paper stock is prepared by adding appropriate amounts of clay, paper strength enhancer, sizing agent and sulfuric acid band to NBKP and LBKP.
The thread for forming the hologram on the security display part is formed by forming a thermosetting resin layer having a thickness of 2 to 6 μm on a plastic film having a thickness of 16 to 25 μm, and forming a light diffraction structure on the resin layer. An opaque reflecting layer made of aluminum or the like having a thickness of 0.04 to 0.08 μm is formed on the surface of the coating, and a vinyl-based heat-sensitive adhesive is applied to the thickness of 5 to 10 μm on the reflecting layer and the surface of the plastic film. Then, it is made by slitting in a strip shape with a slitter.

（実施例）
スレッドとして、市販の２５μｍポリエチレンテレフタレートのフィルムに酢酸ビニル系の感熱接着剤を７μｍの厚さに塗工し、前記接着剤層の反対側に厚さ４μｍのアクリル系の樹脂層を形成し、前記樹脂層にホログラムを形成し、その上に０．０５μｍのアルミニウムによる反射層を形成し、反射層上に酢酸ビニル系の感熱接着剤を８μｍの厚さに塗工し、総厚約５０μｍのテープを作製した。
２槽式円網抄紙機の１槽目のシリンダーに、矩形状の開口部を形成するための樹脂板を取り付けた上網を装着し、２槽目の丸網シリンダーには帯状凹部を形成するための樹脂板を取り付けた上網を装着し、前記２槽の間から、上述のスレッドを供給して坪量１０５ｇ／ｍ2のスレッド入り印刷用紙を試作した。
試作したスレッド入り印刷用紙は、印刷適正も良好で、スレッド表出面の幅方向両端の紙繊維の被覆状態，接着状態共に良好で、また、スレッドと裏側基紙との接着も良好であった。
また、スレッド入り印刷用紙の表裏面に形成された矩形状の開口部から、および、表裏を貫通する開口部から、スレッドに形成されたホログラムを明瞭に視認することができた。 (Example)
As a thread, a commercially available 25 μm polyethylene terephthalate film was coated with a vinyl acetate heat-sensitive adhesive to a thickness of 7 μm, and an acrylic resin layer with a thickness of 4 μm was formed on the opposite side of the adhesive layer, A hologram is formed on the resin layer, a 0.05 μm aluminum reflective layer is formed thereon, a vinyl acetate heat-sensitive adhesive is applied on the reflective layer to a thickness of 8 μm, and a total thickness of about 50 μm tape. Was made.
In order to form a belt-like recess in the second tank of the round net cylinder, and the upper tank with a resin plate for forming a rectangular opening is mounted on the cylinder of the first tank of the two-tank paper machine. An upper net with a resin plate attached thereto was mounted, and the above-mentioned thread was supplied from between the two tanks to produce a threaded printing paper having a basis weight of 105 g / m 2 .
The prototyped threaded printing paper had good printing suitability, both the coated state and adhesion state of the paper fibers at both ends in the width direction of the thread exposed surface, and good adhesion between the thread and the back side base paper.
Further, the hologram formed on the thread could be clearly seen from the rectangular opening formed on the front and back surfaces of the threaded printing paper and from the opening penetrating the front and back surfaces.

本発明のスレッド入り印刷用紙は、商品券や株券などの有価証券，紙幣に利用される。   The threaded printing paper of the present invention is used for securities such as gift certificates and stock certificates, and banknotes.

本発明のスレッド入り印刷用紙の一例について説明するための図である。It is a figure for demonstrating an example of the threaded printing paper of this invention. 図１のＡ−Ａ線断面図である。It is the sectional view on the AA line of FIG. 本発明のスレッド入り印刷用紙の他の一例について説明するための図である。It is a figure for demonstrating another example of the threaded printing paper of this invention. 図３のＸ−Ｘ線断面図である。It is the XX sectional view taken on the line of FIG. 図３のＹ−Ｙ線断面図である。It is the YY sectional view taken on the line of FIG. スレッドの一例について説明するための図である。It is a figure for demonstrating an example of a thread | sled. 抄紙機の一例について説明するための図である。It is a figure for demonstrating an example of a paper machine. 開口部及びスレッドの位置精度について説明するための図である。It is a figure for demonstrating the positional accuracy of an opening part and a thread | sled. 従来のスレッド入り偽造防止用紙の一例について説明するための図である。It is a figure for demonstrating an example of the conventional forgery prevention paper with a thread | sled.

符号の説明Explanation of symbols

１，１００ スレッド入り印刷用紙
２，２０ スレッド
３ 単位開口部
３ａ，３ｂ，３ｃ，３０ 開口部
４ 印刷部
１０ スレッド入り印刷用紙基紙
１１ 裏側紙層
１２ 表側紙層
２１，２５ 接着剤層、接着剤
２２ 透明なプラスチックフィルム
２３ 樹脂層
２４ 反射層
５１ 裏側紙層形成ユニット
５２ 表側紙層形成ユニット
５３ 乾燥装置
５４ 毛布
５１０，５２０ 槽
1,100 Threaded printing paper 2,20 Thread 3 Unit opening 3a, 3b, 3c, 30 Opening 4 Printing section 10 Threaded printing paper base paper 11 Back side paper layer 12 Front side paper layer 21, 25 Adhesive layer, adhesive Agent 22 Transparent plastic film 23 Resin layer 24 Reflective layer 51 Back side paper layer forming unit 52 Front side paper layer forming unit 53 Drying device 54 Blanket 510,520 Tank

Claims (4)

偽造防止のために基紙の抄紙段階でスレッドが抄きこまれたスレッド入り印刷用紙であって、
スレッドは、基紙の表側紙層と裏側紙層の間に形成され、
前記表側紙層と前記裏側紙層には、スレッドが形成された位置に、スレッドを幅方向に全て表出する大きさの単位開口部が所定の間隔で形成され、
表裏に形成された単位開口部の一部が、所定の周期で重なり合うように配置されたことを特徴とするスレッド入り印刷用紙。 In order to prevent counterfeiting, it is a threaded printing paper in which threads are drawn at the base paper making stage,
The thread is formed between the front paper layer and the back paper layer of the base paper,
In the front side paper layer and the back side paper layer, unit openings of a size that exposes all the threads in the width direction are formed at predetermined intervals at positions where the threads are formed.
A threaded printing paper, wherein part of the unit openings formed on the front and back sides are arranged so as to overlap each other at a predetermined cycle. 請求項１に記載のスレッド入り印刷用紙において、
スレッドはセキュリティ表示部が形成された透明なプラスチックフィルムからなり、スレッドの少なくとも表裏何れかの表出面に接着剤層が形成されたことを特徴とするスレッド入り印刷用紙。 In the threaded printing paper according to claim 1,
A threaded printing paper, wherein the thread is made of a transparent plastic film on which a security display portion is formed, and an adhesive layer is formed on at least one of the front and back surfaces of the thread. 請求項１に記載のスレッド入り印刷用紙において、
セキュリティ表示部は、樹脂部と反射層からなる光回折構造又は文字を含むパターン、変色インキ、印刷図柄、の何れか又はこれらの組み合わせが形成されたことを特徴とするスレッド入り印刷用紙。 In the threaded printing paper according to claim 1,
A threaded printing paper, wherein the security display portion is formed with a light diffraction structure or a pattern including characters, a discoloration ink, a printed pattern, or a combination thereof, each including a resin portion and a reflective layer. 請求項１〜３に記載のスレッド入り印刷用紙を使用した印刷物であって、スレッドは、印刷物の短辺に沿って形成されたことを特徴とするスレッド入り印刷用紙を使用した印刷物。
A printed matter using the threaded printing paper according to claim 1, wherein the thread is formed along a short side of the printed matter.
JP2006241483A 2006-09-06 2006-09-06 Thread-containing print paper and printed product using the same Pending JP2008063683A (en)