JP2008030856A - Heat shrinkable tubular label - Google Patents

Heat shrinkable tubular label Download PDF

Info

Publication number
JP2008030856A
JP2008030856A JP2007146511A JP2007146511A JP2008030856A JP 2008030856 A JP2008030856 A JP 2008030856A JP 2007146511 A JP2007146511 A JP 2007146511A JP 2007146511 A JP2007146511 A JP 2007146511A JP 2008030856 A JP2008030856 A JP 2008030856A
Authority
JP
Japan
Prior art keywords
container
heat
base film
shrinkable
cylindrical label
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2007146511A
Other languages
Japanese (ja)
Other versions
JP4969321B2 (en
Inventor
Makoto Fukuhara
誠 福原
Tomohiro Yamaguchi
友弘 山口
Ryozo Sugiura
良三 杉浦
Takashi Odagiri
俊 小田切
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fuji Seal International Inc
Original Assignee
Fuji Seal International Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fuji Seal International Inc filed Critical Fuji Seal International Inc
Priority to JP2007146511A priority Critical patent/JP4969321B2/en
Publication of JP2008030856A publication Critical patent/JP2008030856A/en
Application granted granted Critical
Publication of JP4969321B2 publication Critical patent/JP4969321B2/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

<P>PROBLEM TO BE SOLVED: To prevent a tubular label from slipping when opening and closing a stopper of a container in a heat shrinkable tubular label which is mounted on a flexible container into which a stored object is enclosed at a pressure higher than atmospheric pressure. <P>SOLUTION: The flexible container 2 having a body section 22 and a screw cap 24 which can open and close a spout, and enclosed with a stored object at a pressure higher than atmospheric pressure, includes the heat shrinkable tubular label 1 mounted on the body section 22 of the container 2 of which the wall thickness at the center of the body section is thinner than the wall thickness at the lower part of the body section, wherein a tubular body which is obtained by forming a heat shrinkable base film provided with a sliding layer on the inside face into a tubular form, and a part of the inside face of the tubular body corresponding to the lower part of the body section of the container 2 is provided a blocking section 7 coated with a polymer softenable at a heat shrinking temperature of a base film. <P>COPYRIGHT: (C)2008,JPO&INPIT

Description

本発明は、加熱収縮させて容器に装着される熱収縮性筒状ラベルに関する。   The present invention relates to a heat-shrinkable cylindrical label that is heat-shrinked and attached to a container.

従来、飲料容器、食品容器などの様々な容器に、熱収縮性筒状ラベル(筒状シュリンク、シュリンクフィルムなどとも呼ばれる)が装着されている。
かかる熱収縮性筒状ラベルは、意匠印刷層が設けられた熱収縮性のベースフィルムを筒状に成形した筒状体から構成されている。さらに、この筒状体の内面には、熱収縮性筒状ラベルを容器に外嵌する際の動摩擦抵抗を下げるため、滑り層が設けられている。該滑り層は、例えば、滑剤を含有するメジウムインキをベースフィルムの最内面(容器接触面)にベタ状に塗工することによって形成されている。
Conventionally, heat-shrinkable cylindrical labels (also called cylindrical shrinks, shrink films, etc.) are attached to various containers such as beverage containers and food containers.
Such a heat-shrinkable cylindrical label is composed of a tubular body obtained by forming a heat-shrinkable base film provided with a design printing layer into a tubular shape. Furthermore, a sliding layer is provided on the inner surface of the cylindrical body in order to reduce the dynamic frictional resistance when the heat-shrinkable cylindrical label is fitted on the container. The sliding layer is formed, for example, by applying a medium ink containing a lubricant on the innermost surface (container contact surface) of the base film in a solid shape.

しかしながら、内面に滑り層が設けられている熱収縮性筒状ラベルは、胴部の周方向に回転させて開閉栓を行うネジキャップを有し且つ大気圧よりも高い状態で収納物が封入された容器に装着した場合、ネジキャップを回す際に空回りするという問題点がある。
具体的には、胴部と、該胴部の上方に開口された注出口と、該注出口を開閉栓するネジキャップと、を有する合成樹脂製の可撓性容器(例えば、ポリエチレンテレフタレート製のボトル型容器など)は、胴部を片手で持ちつつ、他方の手でネジキャップを胴部の周方向に回して開閉栓を行う。このうち、炭酸飲料などの昇圧性の収納物が封入された容器は、内圧が大気圧よりも高い状態となっているため、胴部が僅かに膨張している。従って、該容器の開栓時、内圧が下がると、容器の胴部は復元して僅かに小さくなる。このような容器の胴部に装着された熱収縮性筒状ラベルは、開閉栓に関わらず、その径が不変である。このため、容器が復元してその径が小さくなると、ネジキャップを回す際、筒状ラベルが胴部に対して空回りを起こすという問題がある。このように熱収縮性筒状ラベルが空回りすると、ネジキャップの開閉を容易に行えず、その改善が望まれている。
However, the heat-shrinkable cylindrical label provided with a sliding layer on the inner surface has a screw cap that rotates in the circumferential direction of the body and opens and closes the cap, and the stored items are enclosed in a state higher than atmospheric pressure. When it is attached to a container, there is a problem that the screw cap rotates freely when the screw cap is turned.
Specifically, a synthetic resin flexible container (for example, made of polyethylene terephthalate) having a barrel portion, a spout opening above the barrel portion, and a screw cap for opening and closing the spout. A bottle-shaped container or the like) is opened and closed by holding the barrel with one hand and turning the screw cap in the circumferential direction of the barrel with the other hand. Among these, since the internal pressure is in a state higher than the atmospheric pressure, the body portion of the container in which the pressurizing stored item such as carbonated drink is enclosed is slightly expanded. Therefore, when the internal pressure is reduced when the container is opened, the body of the container is restored and becomes slightly smaller. The diameter of the heat-shrinkable cylindrical label attached to the body of such a container is unchanged regardless of the opening / closing stopper. For this reason, when the container is restored and its diameter is reduced, there is a problem that when the screw cap is turned, the cylindrical label is idle with respect to the body portion. Thus, when the heat-shrinkable cylindrical label is idle, the screw cap cannot be easily opened and closed, and an improvement is desired.

熱収縮性筒状ラベルの空回りを防止するため、内面に不織布が積層された熱収縮性筒状ラベルの容器接触面に、感熱性接着剤を部分的に塗工した熱収縮性筒状ラベルが知られている(特許文献1)。   In order to prevent the heat-shrinkable cylindrical label from spinning around, a heat-shrinkable cylindrical label partially coated with a heat-sensitive adhesive is applied to the container contact surface of the heat-shrinkable cylindrical label laminated on the inner surface. Known (Patent Document 1).

しかしながら、容器接触面に感熱性接着剤を塗工すると、筒状ラベルを除去した後、該感熱性接着剤が容器に残存するため、容器をリサイクルする上で好ましくない。また、感熱性接着剤が設けられた筒状ラベルを扁平状にした際、筒状ラベルの内面同士が付着する現象(ブロッキング)を生じる虞がある。
特開2002−20705号公報
However, applying a heat-sensitive adhesive to the container contact surface is not preferable in recycling the container because the heat-sensitive adhesive remains in the container after the cylindrical label is removed. Moreover, when the cylindrical label provided with the heat sensitive adhesive is flattened, there is a possibility that a phenomenon (blocking) in which the inner surfaces of the cylindrical label adhere to each other may occur.
JP 2002-20705 A

そこで、本発明は、大気圧よりも高い状態で収納物が封入される可撓性の容器に装着される熱収縮性筒状ラベルに於いて、開閉栓の際、熱収縮性筒状ラベルの空回りを防止することを課題とする。   Therefore, the present invention relates to a heat-shrinkable cylindrical label attached to a flexible container in which a stored item is sealed in a state higher than atmospheric pressure. The problem is to prevent idling.

本発明は、胴部と、注出口を開閉栓可能なネジキャップとを有し、大気圧よりも高い状態で収納物が封入された合成樹脂製の可撓性容器であって、胴部中央に於ける肉厚が胴部下方に於ける肉厚よりも薄い容器の該胴部に装着される熱収縮性筒状ラベルに於いて、内面に滑り層が設けられた熱収縮性のベースフィルムを筒状に成形した筒状体を有し、容器の胴部下方に対応する筒状体の内面の一部分に、ベースフィルムの熱収縮温度で軟化しうるポリマーを塗工したブロッキング部、又は、ベースフィルムを露出させたブロッキング部の少なくとも何れか一方が設けられている熱収収縮性筒状ラベルを提供する。   The present invention is a flexible container made of a synthetic resin having a trunk portion and a screw cap capable of opening and closing a spout, and in which a stored item is sealed in a state higher than atmospheric pressure, A heat-shrinkable base film having a sliding layer on the inner surface of a heat-shrinkable cylindrical label attached to the barrel of a container whose thickness is thinner than the thickness below the barrel A blocking part in which a polymer that can be softened at the heat shrink temperature of the base film is applied to a part of the inner surface of the cylindrical body corresponding to the lower part of the body of the container, or Provided is a heat-shrinkable cylindrical label provided with at least one of blocking parts from which a base film is exposed.

上記熱収縮性筒状ラベルは、内面に滑り層が設けられているので、容器の胴部に外嵌する際、熱収縮性筒状ラベルの内面が容器外面に対してスムースに滑り、熱収縮性筒状ラベルを容器の所定位置に確実に位置させることができる。
外嵌後の熱収縮性筒状ラベルを加熱することにより、熱収縮性筒状ラベルは、容器に熱収縮装着される。
上記熱収縮性筒状ラベルは、容器の胴部下方に対応する内面の一部に、ベースフィルムの熱収縮温度で軟化しうるポリマーを塗工したブロッキング部、又は、ベースフィルムを露出させたブロッキング部の何れか一方が設けられているので、熱収縮性筒状ラベルを加熱した際、ポリマーの塗布部又はベースフィルムの露出部が軟化し、このブロッキング部が合成樹脂製容器の胴部下方の外面に強く密着する。胴部下方が胴部中央よりも厚肉状に形成されている容器は、開栓時、胴部下方の径変化が殆どない又は極めて小さい。このため、開栓時、ブロッキング部が胴部下方の外面に強く密着した状態を維持できる。従って、ラベル装着済みの容器を開閉栓する際、熱収縮性筒状ラベルが空回りすることを防止できる。
Since the above-mentioned heat-shrinkable cylindrical label is provided with a sliding layer on the inner surface, when it is externally fitted to the body of the container, the inner surface of the heat-shrinkable cylindrical label slides smoothly with respect to the outer surface of the container. The sticky cylindrical label can be reliably positioned at a predetermined position of the container.
By heating the heat-shrinkable cylindrical label after external fitting, the heat-shrinkable cylindrical label is heat-shrink mounted on the container.
The heat-shrinkable cylindrical label is a blocking part in which a polymer that can be softened at the heat-shrinking temperature of the base film is applied to a part of the inner surface corresponding to the lower part of the body part of the container, or a blocking in which the base film is exposed. Since either one of the parts is provided, when the heat-shrinkable cylindrical label is heated, the polymer application part or the exposed part of the base film is softened, and this blocking part is below the trunk part of the synthetic resin container. Strongly adheres to the outer surface. A container in which the lower portion of the body is formed thicker than the center of the body has little or very little change in diameter under the body when opened. For this reason, at the time of opening, the state in which the blocking part closely adhered to the outer surface below the trunk part can be maintained. Therefore, it is possible to prevent the heat-shrinkable cylindrical label from spinning around when the container with the label attached is opened and closed.

さらに、本発明は、胴部と、注出口を開閉栓可能なネジキャップとを有し、大気圧よりも高い状態で収納物が封入された合成樹脂製の可撓性容器であって、ネジキャップの開栓後に於ける胴部下方の周長さが、開栓前の同周長さの0.980〜1.000倍に縮小し、且つネジキャップの開栓後に於ける胴部中央の周長さが、前記胴部下方の周長さの縮小割合よりも大きく縮小する容器の胴部に装着される熱収縮性筒状ラベルに於いて、内面に滑り層が設けられた熱収縮性のベースフィルムを筒状に成形した筒状体を有し、容器の胴部下方に対応する筒状体の内面の一部分に、ベースフィルムの熱収縮温度で軟化しうるポリマーを塗工したブロッキング部、又は、ベースフィルムを露出させたブロッキング部の少なくとも何れか一方が設けられている熱収収縮性筒状ラベルを提供する。   Furthermore, the present invention is a flexible container made of a synthetic resin having a body portion and a screw cap capable of opening and closing a spout, and in which a stored item is enclosed in a state higher than atmospheric pressure, The circumferential length below the trunk after opening the cap is reduced to 0.980 to 1.000 times the same circumferential length before opening, and the middle of the trunk after opening the screw cap. The heat-shrinkable cylindrical label attached to the barrel of the container whose circumference is reduced to be larger than the reduction ratio of the circumference under the barrel, the heat-shrinkability provided with a sliding layer on the inner surface The blocking part has a cylindrical body formed by cylindrically forming the base film, and a polymer that can be softened at the heat shrink temperature of the base film is applied to a part of the inner surface of the cylindrical body corresponding to the lower part of the container body Or at least one of the blocking portions exposing the base film is provided. Providing NetsuOsamu shrinkable tubular label has.

上記熱収縮性筒状ラベルも同様に、容器の胴部に外嵌する際、熱収縮性筒状ラベルの内面が容器外面に対してスムースに滑り、熱収縮性筒状ラベルを容器の所定位置に確実に位置させることができる。
該熱収縮性筒状ラベルを熱収縮装着した際、上記ブロッキング部が軟化し、この部分が合成樹脂製容器の胴部下方の外面に強く密着する。開栓前後に於ける縮小割合が胴部下方に比して胴部中央の方が大きい上記容器は、胴部下方に於ける径変化が極めて小さい。このため、開栓時、ブロッキング部が胴部下方の外面に強く密着した状態を維持できる。従って、ラベル装着済みの容器を開閉栓する際、熱収縮性筒状ラベルが空回りすることを防止できる。
Similarly, when the heat-shrinkable cylindrical label is externally fitted to the body of the container, the inner surface of the heat-shrinkable cylindrical label smoothly slides with respect to the outer surface of the container, and the heat-shrinkable cylindrical label is moved to a predetermined position on the container. Can be reliably positioned.
When the heat-shrinkable cylindrical label is heat-shrink mounted, the blocking portion softens, and this portion strongly adheres to the outer surface below the trunk portion of the synthetic resin container. The above-mentioned container in which the reduction ratio before and after opening is larger in the middle of the trunk part than in the lower part of the trunk part has a very small diameter change in the lower part of the trunk part. For this reason, at the time of opening, the state in which the blocking part closely adhered to the outer surface below the trunk part can be maintained. Therefore, it is possible to prevent the heat-shrinkable cylindrical label from spinning around when the container with the label attached is opened and closed.

また、本発明は、胴部と、注出口を開閉栓可能なネジキャップとを有し、大気圧よりも高い状態で収納物が封入された合成樹脂製の可撓性容器の該胴部に装着される熱収縮性筒状ラベルに於いて、内面に滑り層が設けられた熱収縮性のベースフィルムの一側端部を他側端部の外面に重ね合わせてセンターシールすることにより筒状に成形されており、ベースフィルムの他側端部の側縁からセンターシール部までの間に、一側端部に非接着な余り代が確保されており、余り代の内面に、ベースフィルムを露出させたブロッキング部、又は、ベースフィルムの熱収縮温度で軟化しうるポリマーを塗工したブロッキング部の少なくとも何れか一方が設けられている熱収縮性筒状ラベルを提供する。   The present invention also includes a barrel and a screw cap capable of opening and closing the spout, and the barrel of a flexible container made of a synthetic resin in which a stored item is sealed in a state higher than atmospheric pressure. In the heat-shrinkable cylindrical label to be installed, the heat-shrinkable base film with a sliding layer on the inner surface is overlapped with one side end on the outer surface of the other end and center-sealed. A non-adhesive margin is secured at one side edge between the side edge of the other edge of the base film and the center seal, and the base film is placed on the inner surface of the margin. Provided is a heat-shrinkable cylindrical label provided with at least one of an exposed blocking portion or a blocking portion coated with a polymer that can be softened at the heat shrink temperature of a base film.

上記熱収縮性筒状ラベルも同様に、容器の胴部に外嵌する際、熱収縮性筒状ラベルの内面が容器外面に対してスムースに滑り、熱収縮性筒状ラベルを容器の所定位置に確実に位置させることができる。
上記熱収縮性筒状ラベルは、センターシール部に於いて一側端部に非接着な余り代が確保されており、この余り代の内面にベースフィルムの熱収縮温度で軟化しうるポリマーを塗工したブロッキング部、又は、ベースフィルムを露出させたブロッキング部の少なくとも何れか一方が設けられている。この余り代は、熱収縮性筒状ラベルを加熱した際、外側に重なったベースフィルムの一側端部の収縮によって、容器の外面側へと強く押圧されると共に、ブロッキング部が軟化する。ブロッキング部の軟化した余り代が容器に押圧されることにより、この部分が合成樹脂製容器の胴部の外面に強く密着する。このブロッキング部は、余り代全体(筒状ラベルの上縁から下縁まで帯状)に設けられていてもよいし、或いは、余り代に部分的に設けられていてもよい。ブロッキング部が、余り代全体に設けられている場合には、該熱収縮性筒状ラベルが開栓時に比較的大きく縮小する胴部中央を有する容器に装着されていても、ブロッキング部が容器の胴部の上下部分に於いて強く密着した状態を維持できる。従って、ラベル装着済みの容器を開閉栓する際、熱収縮性筒状ラベルが空回りすることを防止できる。
Similarly, when the heat-shrinkable cylindrical label is externally fitted to the body of the container, the inner surface of the heat-shrinkable cylindrical label smoothly slides with respect to the outer surface of the container, and the heat-shrinkable cylindrical label is moved to a predetermined position on the container. Can be reliably positioned.
The heat-shrinkable cylindrical label has a non-adhesive margin at one end at the center seal portion, and a polymer that can be softened at the heat shrink temperature of the base film is applied to the inner surface of the margin. At least one of the processed blocking part or the blocking part exposing the base film is provided. When the heat-shrinkable cylindrical label is heated, the remainder is strongly pressed toward the outer surface side of the container by the contraction of the one end portion of the base film overlapped on the outside, and the blocking portion is softened. When the softening margin of the blocking portion is pressed against the container, this portion strongly adheres to the outer surface of the body portion of the synthetic resin container. This blocking part may be provided in the entire remainder (a strip shape from the upper edge to the lower edge of the cylindrical label) or may be provided partially in the remainder. When the blocking portion is provided in the entire remainder, even if the heat-shrinkable cylindrical label is attached to a container having a barrel center that is relatively greatly reduced when opened, the blocking portion is not attached to the container. It is possible to maintain a tightly adhered state at the upper and lower portions of the trunk. Therefore, it is possible to prevent the heat-shrinkable cylindrical label from spinning around when the container with the label attached is opened and closed.

上記容器として、胴部下方に於いて内側へ凹む複数の凹状部が胴部の周方向に所定間隔を開けて形成されている容器に、上記熱収縮性筒状ラベルが装着される。   As the container, the heat-shrinkable cylindrical label is attached to a container in which a plurality of concave parts recessed inwardly at the lower part of the body part are formed at predetermined intervals in the circumferential direction of the body part.

本発明の熱収縮性筒状ラベルは、大気圧よりも高い状態で収納物が封入される可撓性の容器に装着される。該熱収縮性筒状ラベルは、容器に部分的に密着するので、容器を開閉栓する際、熱収縮性筒状ラベルが空回りを防止できる。   The heat-shrinkable cylindrical label of the present invention is attached to a flexible container in which stored items are enclosed in a state higher than atmospheric pressure. Since the heat-shrinkable cylindrical label partially adheres to the container, the heat-shrinkable cylindrical label can be prevented from spinning when the container is opened and closed.

以下、本発明について、図面を参照しつつ具体的に説明する。ただし、便宜上、方向を示す用語として、「外」は、装着される容器の中心から離れる側を、「内」は、容器の中心に近い側を指す。また、「上」とは、装着される容器の底面部から離れる側を、「下」とは、容器の底面部に近い側を指す。
<第1実施形態>
図1及び図2に於いて、1は、筒状に成形した熱収縮性のベースフィルム31を有する筒状体からなる熱収縮性筒状ラベルを示す。該熱収縮性筒状ラベル1は、大気圧よりも高い状態で収納物が封入された合成樹脂製の可撓性容器2の少なくとも胴部周りに装着される。尚、容器2については、図4に示している。
この熱収縮性筒状ラベル1は、内面(容器接触面)に滑り層33が設けられていると共に、容器2の胴部外面に密着するブロッキング部7が設けられている。
Hereinafter, the present invention will be specifically described with reference to the drawings. However, for convenience, as a term indicating a direction, “outside” indicates a side away from the center of the container to be mounted, and “inside” indicates a side close to the center of the container. Further, “upper” refers to the side away from the bottom surface of the container to be mounted, and “lower” refers to the side closer to the bottom surface of the container.
<First Embodiment>
1 and 2, reference numeral 1 denotes a heat-shrinkable cylindrical label comprising a tubular body having a heat-shrinkable base film 31 formed into a tubular shape. The heat-shrinkable cylindrical label 1 is mounted around at least a trunk portion of a synthetic resin-made flexible container 2 in which a stored item is sealed in a state higher than atmospheric pressure. The container 2 is shown in FIG.
The heat-shrinkable cylindrical label 1 is provided with a sliding layer 33 on the inner surface (container contact surface) and a blocking portion 7 that is in close contact with the outer surface of the body portion of the container 2.

具体的には、熱収縮性筒状ラベル1は、ラベル基材3の一側端部3aを他側端部3bの外面に重ね合わせ、溶剤又は接着剤を用いてセンターシール(接着)することにより筒状に成形された筒状体からなる。
図2に示すように、センターシール部4に於いて、内側に位置するラベル基材3の他側端部3bには、センターシール部4から周方向に延出された余り代5が確保されている。具体的には、センターシール部4は、ラベル基材3の一側端部3aを他側端部3bの外面に重ね合わせて、その重ね合わせた領域の所定幅を上下方向に帯状に接着することにより形成されている。このラベル基材3の他側端部3bの側縁3b’からセンターシール部4の縁までの間に、所定幅(例えば、3mm〜7mm程度)、余り代5が確保されている。この余り代5は、一側端部3aの内面に非接着な自由端とされている。
尚、ラベル基材3の一側端部3aの縁から所定幅の内面は、他側端部3bの外面にセンターシールするため、意匠印刷層32などが形成されておらず、ベースフィルム31の内面が露出している。
Specifically, the heat-shrinkable cylindrical label 1 is formed by superimposing one end portion 3a of the label base material 3 on the outer surface of the other end portion 3b and performing center sealing (adhesion) using a solvent or an adhesive. It consists of the cylindrical body shape | molded by this.
As shown in FIG. 2, in the center seal portion 4, a surplus margin 5 extending in the circumferential direction from the center seal portion 4 is secured at the other end 3 b of the label base material 3 positioned inside. ing. Specifically, the center seal portion 4 superimposes one side end portion 3a of the label base material 3 on the outer surface of the other side end portion 3b, and adheres a predetermined width of the overlapped region in the vertical direction. It is formed by. A predetermined width (for example, about 3 mm to 7 mm) and a margin of margin 5 are secured between the side edge 3 b ′ of the other end 3 b of the label base 3 and the edge of the center seal portion 4. The surplus margin 5 is a free end that is not bonded to the inner surface of the one side end 3a.
Since the inner surface of the predetermined width from the edge of the one side end portion 3a of the label base 3 is center-sealed to the outer surface of the other end portion 3b, the design print layer 32 or the like is not formed, and the base film 31 The inner surface is exposed.

ラベル基材3は、容器2の胴部22から肩部23にかけて覆うことができる所定長の矩形状に形成されている。ラベル基材3は、図3にも示すように、熱収縮性を有するベースフィルム31と、該ベースフィルム31の内面側に設けられた意匠印刷層32と、少なくとも意匠印刷層32の内面を被覆するようにベースフィルム31の内面側に設けられた滑り層33と、ベースフィルム31の内面側に設けられたブロッキング部7と、を有する。   The label base material 3 is formed in a rectangular shape having a predetermined length that can be covered from the body portion 22 to the shoulder portion 23 of the container 2. As shown in FIG. 3, the label substrate 3 covers a base film 31 having heat shrinkability, a design printing layer 32 provided on the inner surface side of the base film 31, and at least an inner surface of the design printing layer 32. Thus, the sliding layer 33 provided on the inner surface side of the base film 31 and the blocking portion 7 provided on the inner surface side of the base film 31 are included.

ベースフィルム31は、少なくとも一方向(筒状に形成した際に於ける周方向。以下同じ)に熱収縮性を有するものであれば特に限定されず、例えば、ポリエチレンテレフタレートなどのポリエステル系樹脂、ポリプロピレン、環状オレフィンなどのオレフィン系樹脂、ポリスチレン、スチレン−ブタジエン共重合体などのスチレン系樹脂、塩化ビニル系樹脂などの熱可塑性樹脂からから選ばれる1種、又は2種以上の混合物などからなる合成樹脂製フィルムなどを用いることができる。また、熱収縮性を有する2種以上の樹脂が積層された積層フィルムを用いることもできる。さらに、熱収縮性を有するフィルムに発泡樹脂シート等の断熱層やその他の機能層が積層された公知の積層フィルムを用いることもできる。中でも、ベースフィルム31は、収縮応力に優れていることから、ポリエステル系、ポリオレフィン系のフィルムを含むものが好ましく、特にポリエステル系フィルムを含むものが好ましい。   The base film 31 is not particularly limited as long as it has heat shrinkability in at least one direction (circumferential direction when formed into a cylindrical shape, hereinafter the same). For example, polyester-based resin such as polyethylene terephthalate, polypropylene Synthetic resins comprising one or a mixture selected from thermoplastic resins such as olefin resins such as cyclic olefins, styrene resins such as polystyrene and styrene-butadiene copolymers, and vinyl chloride resins A film or the like can be used. A laminated film in which two or more kinds of resins having heat shrinkability are laminated can also be used. Furthermore, the well-known laminated | multilayer film by which heat insulation layers, such as a foamed resin sheet, and another functional layer were laminated | stacked on the film which has heat-shrinkability can also be used. Especially, since the base film 31 is excellent in shrinkage stress, what contains a polyester-type and polyolefin-type film is preferable, and the thing containing a polyester-type film is especially preferable.

熱収縮性のフィルムは、公知の製法で製膜し延伸処理することにより得ることができる。延伸処理は、通常、70〜110℃程度の温度で、一方向に2.0〜8.0倍、好ましくは3.0〜7.0倍程度で主延伸することにより行われる。さらに、他方向(前記一方向に直交する方向。筒状に形成した際に於ける上下方向。以下同じ)にも、例えば1.5倍以下の低倍率で延伸処理を行ってもよい。得られたフィルムは、一軸延伸フィルム又は主延伸方向と直交する方向に若干延伸された二軸延伸フィルムとなる。フィルムの厚みは、特に限定されないが、通常、25〜80μm程度のものが用いられる。
フィルムの熱収縮率は、装着される容器2の胴部22及び肩部23の径差に応じて適宜設計できる。例えば、フィルムの一方向に於ける熱収縮率(90℃温水中に10秒間浸漬)は、約40%以上、好ましくは約50%以上のものが例示される。また、フィルムは他方向に若干熱収縮してもよく、かかる他方向に於ける熱収縮率(90℃温水中に10秒間浸漬)は、約−3〜15%程度のものが例示される。
但し、熱収縮率(%)=[{(一方向(又は他方向)の元の長さ)−(一方向(又は他方向)の浸漬後の長さ)}/(一方向(又は他方向)の元の長さ)]×100。
The heat-shrinkable film can be obtained by forming a film by a known manufacturing method and stretching the film. The stretching treatment is usually performed by main stretching at a temperature of about 70 to 110 ° C. in a direction of 2.0 to 8.0 times, preferably about 3.0 to 7.0 times. Furthermore, the stretching process may be performed at a low magnification of, for example, 1.5 times or less in the other direction (the direction orthogonal to the one direction. The vertical direction when formed into a cylindrical shape; the same applies hereinafter). The obtained film becomes a uniaxially stretched film or a biaxially stretched film slightly stretched in a direction orthogonal to the main stretch direction. Although the thickness of a film is not specifically limited, The thing of about 25-80 micrometers is used normally.
The heat shrinkage rate of the film can be appropriately designed according to the diameter difference between the body portion 22 and the shoulder portion 23 of the container 2 to be mounted. For example, the thermal shrinkage rate (immersion in 90 ° C. warm water for 10 seconds) in one direction of the film is about 40% or more, preferably about 50% or more. The film may be slightly heat-shrinked in the other direction, and the heat shrinkage rate (immersion in 90 ° C. warm water for 10 seconds) in the other direction is about −3 to 15%.
However, thermal shrinkage rate (%) = [{(original length in one direction (or other direction)) − (length after immersion in one direction (or other direction))} / (one direction (or other direction) ) Original length)] × 100.

意匠印刷層32は、センターシール部4となるベースフィルム31の一側端部3aの内面及び以下に詳述するブロッキング部7が設けられるベースフィルム31の内面の所定範囲を除き、ベースフィルム31の内面の所定範囲に設けられている。この意匠印刷層32は、例えば、商品名、絵柄、説明などの所定の表示などの表示印刷と白色等のベタ印刷などが、グラビア印刷などによって単色又は多色刷りにて設けられている。ただし、意匠印刷層32は、ベースフィルム31の内面の上記所定範囲全体にベタ状に設けてもよいし、上記所定範囲に於いて部分的に設けてもよい。
尚、意匠印刷層32は、ベースフィルム31の内面に設けることが好ましいが、ベースフィルム31の外面に設けてもよい。
The design printing layer 32 is formed on the base film 31 except for a predetermined range on the inner surface of the one side end portion 3a of the base film 31 serving as the center seal portion 4 and the inner surface of the base film 31 provided with the blocking portion 7 described in detail below. It is provided in a predetermined range on the inner surface. The design printing layer 32 is provided with display printing such as a predetermined display such as a product name, a pattern, and description, and solid printing such as white, for example, in a single color or multicolor printing by gravure printing or the like. However, the design print layer 32 may be provided in a solid shape over the entire predetermined range of the inner surface of the base film 31, or may be partially provided in the predetermined range.
The design print layer 32 is preferably provided on the inner surface of the base film 31, but may be provided on the outer surface of the base film 31.

滑り層33は、熱収縮性筒状ラベル1の容器2に対する動摩擦係数を小さくするために設けられているものである。滑り層33は、センターシール部4となるベースフィルム31の一側端部3aの内面及び以下に詳述するブロッキング部7が設けられるベースフィルム31の内面の所定範囲を除き、ベースフィルム31の内面側全体にベタ状に設けられている。従って、意匠印刷層32の内面は、滑り層33によって被覆されている。
滑り層33としては、例えば、メジウムインキを上記範囲にベタ状に塗工することにより設けることができる。該メジウムインキは、実質的に顔料(着色材料)を含まない透明なインキであって、ポリマーと、滑り成分とを含む。具体的には、該メジウムインキは、例えば、水(及び/又はアルコール)に、アクリル系樹脂、アクリル共重合体、ポリエステル系樹脂、ウレタン系樹脂、水性ポリアミド樹脂などを分散させたエマルジョン型;トルエン、メチルエチルケトン、酢酸エチル、イソプロピルアルコールなどの有機溶剤に、ロジン、ケトン系樹脂、塩化ビニル系樹脂、塩化ビニル−酢酸ビニル共重合体、アクリル系樹脂、ウレタン系樹脂、アクリル−ウレタン共重合体、ポリエステル系樹脂などを溶解させた溶剤型のポリマー溶液に、滑り成分を混合したものが例示できる。滑り成分としては、例えば、ワックス類、シリコーン、シリカなどの無機微粒子、有機微粒子などの滑剤が例示できる。メジウムインキには、必要に応じて、増粘剤、消泡剤、防かび剤などのその他の添加剤が混合されていてもよい。中でも、滑り層33は、アクリル系樹脂またはウレタン系樹脂をベースポリマーとし、ポリエチレンワックスなどのオレフィン系ワックス、4フッ化エチレン樹脂(テフロン(登録商標))などのフッ素系ワックス、フッ素樹脂粉末、シリカなどの滑り成分を1〜30質量%(固形分比率)として含むものが好ましい。特に、アクリル系樹脂に、ポリエチレンワックス5〜30質量%(固形分比率)含むものがより好ましい。
The sliding layer 33 is provided in order to reduce the dynamic friction coefficient of the heat-shrinkable cylindrical label 1 with respect to the container 2. The sliding layer 33 is formed on the inner surface of the base film 31 except for a predetermined range of the inner surface of the one side end 3a of the base film 31 serving as the center seal portion 4 and the inner surface of the base film 31 provided with the blocking portion 7 described in detail below. It is provided in a solid shape on the entire side. Therefore, the inner surface of the design printing layer 32 is covered with the sliding layer 33.
The sliding layer 33 can be provided, for example, by applying a medium ink in the above range in a solid form. The medium ink is a transparent ink substantially free of a pigment (coloring material), and includes a polymer and a sliding component. Specifically, the medium ink is, for example, an emulsion type in which an acrylic resin, an acrylic copolymer, a polyester resin, a urethane resin, an aqueous polyamide resin, or the like is dispersed in water (and / or alcohol); toluene , Rosin, ketone resin, vinyl chloride resin, vinyl chloride-vinyl acetate copolymer, acrylic resin, urethane resin, acrylic-urethane copolymer, polyester in organic solvents such as methyl ethyl ketone, ethyl acetate, isopropyl alcohol For example, a solvent-type polymer solution in which a system resin or the like is dissolved is mixed with a sliding component. Examples of the slip component include lubricants such as waxes, silicone fine particles, inorganic fine particles such as silica, and organic fine particles. The medium ink may be mixed with other additives such as a thickener, an antifoaming agent and an antifungal agent, if necessary. Among them, the sliding layer 33 is made of acrylic resin or urethane resin as a base polymer, olefin wax such as polyethylene wax, fluorine wax such as tetrafluoroethylene resin (Teflon (registered trademark)), fluorine resin powder, silica. What contains 1-30 mass% (solid content ratio) of slip components, such as these, is preferable. In particular, it is more preferable that the acrylic resin contains 5 to 30% by mass (solid content ratio) of polyethylene wax.

ブロッキング部7は、熱収縮性筒状ラベル1を容器2に対して強く密着させる(摩擦係数を高める)ために設けられている。該ブロッキング部7は、熱収縮性筒状ラベル1を容器2に装着した際、容器2の胴部下方22aに対応する位置に部分的に設けられている。
具体的には、ブロッキング部7は、筒状体の下端縁から上方側へと延びる帯状領域に形成されている。ブロッキング部7の上下長さHは、特に限定されないが、余りに短いと、容器2に対する装着位置によっては、ブロッキング部7全体が、胴部下方22aに形成された凹み部25に対面して、ブロッキング部7が容器2の外面と密着しない場合も考えられる。従って、ブロッキング部7の上下長さHは、図4に示す凹み部25の上下長さH1よりも長く形成されていることが好ましい。ブロッキング部7の幅W(周方向長さ)は、余りに短いと容器2に密着させて空回りを防止する効果を得ることができず、該効果を奏する範囲で適宜設計することができる。具体例を示すと、汎用的な0.5リットルのペタロイド状ボトル型容器に本発明の熱収縮性筒状ラベル1を装着する場合には、ブロッキング部7は、その上下長さHが、30〜40mm、幅Wが、10〜20mm程度に形成される。
The blocking part 7 is provided in order to make the heat-shrinkable cylindrical label 1 closely adhere to the container 2 (increase the friction coefficient). When the heat-shrinkable cylindrical label 1 is attached to the container 2, the blocking part 7 is partially provided at a position corresponding to the lower portion 22 a of the body 2 of the container 2.
Specifically, the blocking part 7 is formed in a belt-like region extending upward from the lower end edge of the cylindrical body. The vertical length H of the blocking portion 7 is not particularly limited, but if it is too short, depending on the mounting position on the container 2, the entire blocking portion 7 faces the recess 25 formed on the lower portion 22 a of the blocking portion, and blocking. It is also conceivable that the portion 7 does not adhere to the outer surface of the container 2. Therefore, it is preferable that the vertical length H of the blocking portion 7 is longer than the vertical length H1 of the recessed portion 25 shown in FIG. If the width W (circumferential length) of the blocking portion 7 is too short, it cannot be brought into close contact with the container 2 to obtain the effect of preventing idling, and can be designed as appropriate within the range where the effect is exhibited. As a specific example, when the heat-shrinkable cylindrical label 1 of the present invention is attached to a general-purpose 0.5-liter petaloid bottle-shaped container, the blocking portion 7 has a vertical length H of 30. -40 mm and width W are formed to be about 10-20 mm.

ブロッキング部7の形成材料は、ベースフィルム31の熱収縮温度で軟化しうるポリマーを用いることができる。具体的には、熱収縮性筒状ラベル1を容器に装着する際、雰囲気温度80〜100℃のスチームトンネルにて加熱する、或いは150〜250℃の熱風を吹き付ける熱風トンネルにて加熱することが多いため、ブロッキング部7の形成材料は、該加熱方式で軟化しうるポリマーが用いられる。かかるポリマーとしては、ガラス転移温度(DSC法により測定)が、100℃以下のものを用いることが好ましい。
ブロッキング部7の形成材料としては、実質的に滑り成分を除いた上記メジウムインキを用いることができる。具体的には、ブロッキング部7は、例えば、水(及び/又はアルコール)に分散させて塗布可能なポリマー(エマルジョン型)、例えば、アクリル系樹脂、アクリル共重合体、ウレタン系樹脂、ポリエステル系樹脂、水性ポリアミド樹脂などのエマルジョン型のポリマーを用いることができる。また、トルエン、メチルエチルケトン、酢酸エチル、イソプロピルアルコールなどの有機溶剤に溶解させて塗布するポリマー、例えば、アクリル系樹脂、ウレタン系樹脂、アクリル−ウレタン共重合体、ポリエステル系樹脂、ケトン系樹脂、塩化ビニル系樹脂、塩化ビニル−酢酸ビニル共重合体などの溶剤型のポリマーなどを用いて形成できる。中でも、比較的低温で軟化し易いことから、ポリマーとして、ウレタン系樹脂、アクリル系樹脂が好ましい。また、容器の主たる形成材料(合成樹脂)と同種のポリマーをブロッキング部7の形成材料として用いることも好ましい。
上記ポリマーは、水や溶剤に溶解させて適当な粘度に調整して溶液状とし、該溶液を公知の印刷方法等によってベースフィルム31の内面の所定範囲に塗布乾燥することにより、ブロッキング部7を形成することができる。
上記ポリマーの中でも、ガラス転移温度が、45〜100℃のアクリル系樹脂や、ガラス転移温度が、−10〜20℃のウレタン系樹脂を用いることがより好ましい。さらに、ブロッキング部7を設けた後にロール状に巻き取る場合にフィルム間のブロッキング現象を防止する観点から、前記アクリル系樹脂を用いることが特に好ましい。
ブロッキング部7は、上記ポリマーを90質量%(固形分比率)以上含むものが好ましく、さらに95質量%以上、特に99質量%以上含むものがより好ましい。ブロッキング部7は、実質的に滑り成分を含まないものが好ましく、具体的には滑り成分が1質量%以下である。また、ブロッキング部7の形成材料に粘着付与剤が含まれる場合、筒状ラベル1を容器2から除去する際、ブロッキング部7を構成するポリマーが容器2に付着した状態となることを防止する観点から、粘着付与剤の量は5質量%(固形分比率)以下であるが、特に、粘着付与剤が1質量%以下であるものが好ましい。
As a material for forming the blocking portion 7, a polymer that can be softened at the heat shrink temperature of the base film 31 can be used. Specifically, when the heat-shrinkable cylindrical label 1 is mounted on a container, it is heated in a steam tunnel having an atmospheric temperature of 80 to 100 ° C. or heated in a hot air tunnel that blows hot air of 150 to 250 ° C. Since there are many, the formation material of the blocking part 7 uses the polymer which can be softened by this heating system. As such a polymer, a polymer having a glass transition temperature (measured by DSC method) of 100 ° C. or less is preferably used.
As a forming material of the blocking part 7, the above-mentioned medium ink from which a slip component has been substantially removed can be used. Specifically, the blocking portion 7 is, for example, a polymer (emulsion type) that can be applied by being dispersed in water (and / or alcohol), such as an acrylic resin, an acrylic copolymer, a urethane resin, or a polyester resin. An emulsion type polymer such as an aqueous polyamide resin can be used. In addition, polymers applied by dissolving in organic solvents such as toluene, methyl ethyl ketone, ethyl acetate, isopropyl alcohol, such as acrylic resins, urethane resins, acrylic-urethane copolymers, polyester resins, ketone resins, vinyl chloride It can be formed using a solvent-type polymer such as a vinyl resin or a vinyl chloride-vinyl acetate copolymer. Among these, urethane resins and acrylic resins are preferable because they are easily softened at a relatively low temperature. Moreover, it is also preferable to use the same kind of polymer as the main forming material (synthetic resin) of the container as the forming material of the blocking portion 7.
The polymer is dissolved in water or a solvent to adjust to an appropriate viscosity to form a solution, and the solution is applied to a predetermined range on the inner surface of the base film 31 by a known printing method or the like, whereby the blocking portion 7 is formed. Can be formed.
Among the above polymers, it is more preferable to use an acrylic resin having a glass transition temperature of 45 to 100 ° C. or a urethane resin having a glass transition temperature of −10 to 20 ° C. Furthermore, it is particularly preferable to use the acrylic resin from the viewpoint of preventing a blocking phenomenon between films when the film is wound into a roll after providing the blocking portion 7.
The blocking part 7 preferably contains 90% by mass (solid content ratio) or more of the polymer, more preferably 95% by mass or more, and particularly preferably 99% by mass or more. The blocking part 7 is preferably substantially free of a slip component, and specifically, the slip component is 1% by mass or less. Moreover, when the tackifier is contained in the forming material of the blocking part 7, it is a viewpoint which prevents that the polymer which comprises the blocking part 7 will be in the state which adhered to the container 2, when removing the cylindrical label 1 from the container 2. Therefore, the amount of the tackifier is 5% by mass (solid content ratio) or less, and in particular, the tackifier is preferably 1% by mass or less.

上記ラベル基材3を筒状に成形した筒状体(熱収縮性筒状ラベル1)は、その最内面(容器接触面)の大半が滑り層33で構成されていると共に、該最内面のうち、容器2の胴部下方22aに対応する位置の一部分に、ブロッキング部7が形成されている。   The cylindrical body (heat-shrinkable cylindrical label 1) obtained by forming the label base material 3 into a cylindrical shape has a most part of the innermost surface (container contact surface) constituted by the sliding layer 33, and the innermost surface Among them, the blocking portion 7 is formed in a part of the position corresponding to the lower portion 22 a of the body 2 of the container 2.

本発明の熱収縮性筒状ラベル1は、大気圧よりも高い状態で収納物が封入された合成樹脂製の可撓性容器2に装着され、特に、円筒状の胴部を有する可撓性容器2に装着される場合に、本発明の効果を顕著に奏する。
該容器2の形状は、特に限定されないが、例えば、図4に示すように、円筒状外面を有する胴部22と注出口(図示せず)が形成され、この注出口に封緘用のネジキャップ24が取り付けられている。具体的には、容器2は、底面部21、これに続く円筒状外面を有する中空状の胴部22、胴部22から次第に細くなる肩部23が形成され、肩部23の上方に注出口が形成されている。容器2の胴部22及び肩部23の外面は、周方向に実質的に凹凸(リブ等)を有しない平滑曲面に形成されている。さらに、注出口は、外面に雄ネジ部が形成された略円筒状の周壁部と、この周壁部の上端に形成された開口部とからなり、開口部の中心軸が胴部22の中心軸上に一致するように形成されている。ネジキャップ24は、開口部を開閉栓可能であり、注出口の雄ネジ部に螺合する雌ネジ部が形成されている(何れも不図示)。従って、ネジキャップ24を中心軸周りに回転させることにより、注出口からネジキャップ24を取り外すことができる。
さらに、該容器2は、底面部21から胴部下方22aに亘って複数の凹み部25が形成されている。この凹み部25は、容器2の周方向に所定間隔を開けて形成されており、この凹み部25は、例えば、5箇所形成されている。一般に、このような凹み部25と該凹み部25間の円弧状の凸部は、ペダロイド型と呼ばれており、炭酸飲料などを収納するのに好適な耐圧容器形状として広く用いられている。容器2の容量は、特に限定されないが、通常、0.35リットル〜2リットル程度のものが例示される。特に、片手で胴部22を持ってネジキャップ24を開栓する容器、例えば、胴部22の周長さが、15cm〜30cm程度の容器に本発明の熱収縮性筒状ラベル1を装着した場合に、空回り防止効果を顕著に発揮する。
The heat-shrinkable cylindrical label 1 of the present invention is attached to a flexible container 2 made of a synthetic resin in which a stored item is enclosed in a state higher than atmospheric pressure, and in particular, a flexible body having a cylindrical body. When mounted on the container 2, the effect of the present invention is remarkably exhibited.
The shape of the container 2 is not particularly limited. For example, as shown in FIG. 4, a barrel 22 having a cylindrical outer surface and a spout (not shown) are formed, and a screw cap for sealing is formed at the spout. 24 is attached. Specifically, the container 2 is formed with a bottom surface portion 21, a hollow body portion 22 having a cylindrical outer surface following the bottom surface portion 21, and a shoulder portion 23 gradually narrowing from the body portion 22. Is formed. The outer surface of the trunk | drum 22 and the shoulder part 23 of the container 2 is formed in the smooth curved surface which does not have an unevenness | corrugation (rib etc.) substantially in the circumferential direction. Further, the spout is composed of a substantially cylindrical peripheral wall portion having a male screw portion formed on the outer surface and an opening portion formed at the upper end of the peripheral wall portion, and the central axis of the opening portion is the central axis of the trunk portion 22. It is formed to coincide with the top. The screw cap 24 is capable of opening and closing the opening, and is formed with a female screw portion that is screwed into the male screw portion of the spout (both not shown). Therefore, the screw cap 24 can be removed from the spout by rotating the screw cap 24 around the central axis.
Further, the container 2 has a plurality of recessed portions 25 formed from the bottom surface portion 21 to the lower body portion 22a. The recesses 25 are formed at predetermined intervals in the circumferential direction of the container 2, and the recesses 25 are formed at, for example, five locations. Generally, such an arcuate convex portion between the concave portion 25 and the concave portion 25 is called a pedaloid type, and is widely used as a pressure vessel shape suitable for storing carbonated beverages and the like. Although the capacity | capacitance of the container 2 is not specifically limited, Usually, the thing of about 0.35 liters-2 liters is illustrated. In particular, the heat-shrinkable cylindrical label 1 of the present invention is attached to a container that opens the screw cap 24 by holding the body part 22 with one hand, for example, a container having a circumferential length of about 15 cm to 30 cm. In this case, the effect of preventing idling is remarkably exhibited.

容器2は、胴部中央22bに於ける肉厚が胴部下方22aに於ける肉厚よりも薄く形成されている。該肉厚の具体的寸法は、一般に、胴部中央22bの肉厚が、0.35〜0.55mm程度、胴部下方22aの肉厚が、0.4〜0.6mm程度が例示される。尚、胴部中央22bとは、容器2の底面部21から胴部22の上端(次第に細くなる肩部23と直胴状の胴部22の境界)までの上下方向長さLの中間点を言う。また、胴部下方22aとは、容器2の底面部21から胴部22の上端までの上下方向長さLの1/4(底面部21から上方へ[L×1/4]長さ)の地点を言うが、上記ペダロイド型の容器の場合には、凹み部25の上端から上方10mmの地点を言う。
また、該容器2は、炭酸飲料などの昇圧性収納物を封入した状態からネジキャップ24を開栓した際に、該ネジキャップ24の開栓後に於ける胴部下方22aの周長さが開栓前の胴部下方22aの周長さの0.980〜1.000倍に縮小するものである。特に、前記胴部下方22aの縮小割合は、0.990〜1.000倍が好ましく、特に、0.995〜1.000倍がより好ましい。
さらに、容器2の胴部中央22bについては、昇圧性収納物を封入した状態からネジキャップ24を開栓した際に、該ネジキャップ24の開栓後に於ける胴部中央22bの周長さが、上記胴部下方22aの周長さの縮小割合(0.980〜1.000倍)よりも大きな割合で縮小するものである。具体的には、胴部下方22aが0.997〜0.999倍に縮小する容器2の場合、ネジキャップ24の開栓後に於ける胴部中央22bの周長さが開栓前の胴部中央22bの周長さの0.988〜0.993倍、容器2の形状などによっては0.992〜0.993倍に縮小するものである。
The container 2 is formed so that the wall thickness at the body center 22b is thinner than the wall thickness at the body lower part 22a. Specific examples of the thickness are generally such that the thickness of the barrel center 22b is about 0.35 to 0.55 mm, and the thickness of the barrel lower portion 22a is about 0.4 to 0.6 mm. . In addition, the trunk | drum center 22b is the intermediate point of the up-down direction length L from the bottom face part 21 of the container 2 to the upper end of the trunk | drum 22 (boundary of the shoulder part 23 and the straight trunk | drum 22 is gradually thinned). To tell. Further, the lower portion 22a of the body portion is 1/4 of the vertical length L from the bottom surface portion 21 of the container 2 to the upper end of the body portion 22 ([L × 1/4] length upward from the bottom surface portion 21). In the case of the above-mentioned Pedaloid type container, the point is 10 mm above the upper end of the recess 25.
In addition, when the screw cap 24 is opened from a state in which a pressurizing container such as a carbonated beverage is enclosed, the container 2 has the circumferential length of the lower portion 22a of the trunk portion after the screw cap 24 is opened. It is reduced to 0.980 to 1.000 times the circumferential length of the barrel lower part 22a before the stopper. In particular, the reduction ratio of the lower body portion 22a is preferably 0.990 to 1.000 times, and more preferably 0.995 to 1.000 times.
Further, with respect to the body center 22 b of the container 2, when the screw cap 24 is opened from the state in which the pressurization container is enclosed, the circumferential length of the body center 22 b after the screw cap 24 is opened is The body portion 22a is reduced at a rate larger than the reduction rate (0.980 to 1.000 times) of the circumferential length of the lower portion 22a. Specifically, in the case of the container 2 in which the lower portion 22a of the barrel portion is reduced by a factor of 0.997 to 0.999, the circumferential length of the barrel portion center 22b after the screw cap 24 is opened is the barrel portion before opening. It is reduced to 0.988 to 0.993 times the circumferential length of the center 22b and 0.992 to 0.993 times depending on the shape of the container 2 and the like.

容器2の材質は、合成樹脂製であれば特に限定されず、ポリエチレンテレフタレートなどのポリエステル系、ポリプロピレンなどのポリオレフィン系などが例示でき、通常、ポリエチレンテレフタレートなどのポリエステル系のブロー成形容器(いわゆるPETボトル)が用いられる。   The material of the container 2 is not particularly limited as long as it is made of synthetic resin, and examples thereof include polyesters such as polyethylene terephthalate, polyolefins such as polypropylene, and the like, and usually polyester-based blow molded containers such as polyethylene terephthalate (so-called PET bottles). ) Is used.

上記熱収縮性筒状ラベル1は、公知の製法に従い、長尺状のラベル基材の両側端部を重ね合わせて筒状に成形し、この筒状ラベル連続体を扁平状にしてロール状に巻き取られ、シュリンクラベラーに装填される。
該熱収縮性筒状ラベル1の最内面は、その大半が滑り層33で構成されているので、筒状ラベル連続体を扁平状にして巻き取っても、内面同士が付着する現象(ブロッキング)を起こす虞がない。
シュリンクラベラーでは、筒状ラベル連続体を所定長さに切断することによって1個の熱収縮性筒状ラベル1とし、これを容器2の胴部22から肩部23にかけて外嵌する。該熱収縮性筒状ラベル1の内面は、その大半が滑り層33で構成されているので、外嵌する際、熱収縮性筒状ラベル1は容器2に対してスムースに滑り、従って、該筒状ラベル1は、皺などを生じることなく、容器2の所定位置に外嵌できる。
The heat-shrinkable cylindrical label 1 is formed into a cylindrical shape by superimposing both side ends of a long label base material according to a known production method, and the cylindrical label continuous body is flattened into a roll shape. It is wound up and loaded into a shrink labeler.
Since most of the innermost surface of the heat-shrinkable cylindrical label 1 is composed of the sliding layer 33, the phenomenon that the inner surfaces adhere to each other even when the cylindrical label continuous body is wound in a flat shape (blocking). There is no risk of causing.
In the shrink labeler, the tubular label continuous body is cut into a predetermined length to form one heat-shrinkable tubular label 1, which is externally fitted from the body 22 to the shoulder 23 of the container 2. Since most of the inner surface of the heat-shrinkable cylindrical label 1 is composed of the sliding layer 33, the heat-shrinkable cylindrical label 1 smoothly slides with respect to the container 2 when fitted externally. The cylindrical label 1 can be fitted on a predetermined position of the container 2 without causing wrinkles or the like.

外嵌後、熱収縮性筒状ラベル1は所定温度に加熱され(例えば90℃のスチームを5秒間当てる等)、該熱収縮性筒状ラベル1は熱収縮して容器2に装着される。
この熱収縮性筒状ラベル1を収縮させるための熱によって、熱収縮性筒状ラベル1の内面に部分的に設けられたポリマー(ブロッキング部7)が軟化し、該ポリマーが、容器2の胴部下方22aの外面に密着する。このようにブロッキング部7が密着したラベル装着済みの容器2は、熱収縮性筒状ラベル1のブロッキング部7と容器2の胴部下方22aの間の摩擦係数が高くなる。
このラベル装着済み容器2のネジキャップ24を開栓すると、内圧が下がり、容器2の胴部22、特に胴部中央22bが比較的大きく縮小する。この点、ブロッキング部7が、開栓後に比較的縮小し難い胴部下方22aの外面に強く密着しているので、ネジキャップ24を回す際に、熱収縮性筒状ラベル1が空回りすることを防止できる。
After the external fitting, the heat-shrinkable cylindrical label 1 is heated to a predetermined temperature (for example, 90 ° C. steam is applied for 5 seconds), and the heat-shrinkable cylindrical label 1 is heat-shrinked and attached to the container 2.
The polymer (blocking portion 7) partially provided on the inner surface of the heat-shrinkable cylindrical label 1 is softened by heat for shrinking the heat-shrinkable cylindrical label 1, and the polymer becomes the body of the container 2. Close contact with the outer surface of the lower part 22a. As described above, the label-mounted container 2 with the blocking portion 7 in close contact has a high coefficient of friction between the blocking portion 7 of the heat-shrinkable cylindrical label 1 and the lower portion 22a of the body 2 of the container 2.
When the screw cap 24 of the container 2 with the label attached is opened, the internal pressure is reduced, and the body portion 22 of the container 2, particularly the body portion center 22b, is relatively greatly reduced. In this respect, since the blocking portion 7 is firmly adhered to the outer surface of the lower portion 22a of the trunk portion that is relatively difficult to reduce after opening, the heat-shrinkable cylindrical label 1 is idled when the screw cap 24 is turned. Can be prevented.

上記熱収縮性筒状ラベル1の容器2に対する装着位置は、特に限定されないが、好ましくは、図5に示すように、ブロッキング部7が、隣り合う凹み部25の間に位置するように装着するのが良い。なぜなら、ブロッキング部7全体が容器2の胴部下方22aの外面に密着して、より確実に空回り防止効果を奏するからである。もっとも、図6(a)、(b)に示すように、ブロッキング部7の下方部分が凹み部25に対面した位置に熱収縮性筒状ラベルを装着しても、ブロッキング部7の上方部分は容器2の外面に密着しているため、空回り防止効果が損なわれるわけではない。   The mounting position of the heat-shrinkable cylindrical label 1 with respect to the container 2 is not particularly limited, but preferably, the blocking section 7 is mounted so as to be positioned between adjacent recesses 25 as shown in FIG. Is good. This is because the entire blocking portion 7 is brought into close contact with the outer surface of the lower portion 22a of the body 2 of the container 2 and more reliably prevents the idling. However, as shown in FIGS. 6A and 6B, even if the heat-shrinkable cylindrical label is attached to the position where the lower part of the blocking part 7 faces the recess 25, the upper part of the blocking part 7 is Since it is in close contact with the outer surface of the container 2, the effect of preventing idling is not impaired.

次に、本実施形態の変形例を示す。
上記では、ブロッキング部7を構成するポリマーを塗工する部分には、意匠印刷層32が設けられておらず、ベースフィルム32の内面に直接ポリマーを塗工する構成を例示しているが、ポリマーを塗工する部分に意匠印刷層32が設けられていてもよい。
さらに、上記では、ブロッキング部7は、ポリマーを塗工した塗工部から構成されているが、例えば、図7に示すように、ブロッキング部7を設ける範囲に、ベースフィルム31の内面を露出させてもよい。すなわち、容器2の胴部下方22aに対応する筒状体の内面の一部分に、ベースフィルム32を露出させることによって、これをブロッキング部7とすることができる。かかるフィルム露出部(ブロッキング部7)は、熱収縮性筒状ラベル1を構成するベースフィルムであるから、熱収縮性筒状ラベル1の熱収縮温度で軟化しうる。従って、熱収縮性筒状ラベル1を熱収縮装着した際、該フィルム露出部が、容器2の胴部下方22aの外面に密着する。このようにフィルム露出部からなるブロッキング部7も、上記ポリマー塗工部からなるブロッキング部7と同様に、筒状ラベル1の空回りを防止できる。また、上記フィルム露出部に、コロナ放電処理などの表面処理を施してもよい。かかる処理を行うことで、ブロッキング部7に於ける容器2の外面に対する密着性を高めることができる。コロナ放電処理は、その処理面が好ましくは45ダイン以上、より好ましくは50ダイン以上、特に好ましくは52ダイン以上となるように実施される。本発明者らが実証したところ、コロナ放電処理後の処理面が40ダイン以下であると空回り防止効果は小さく、上記数値以上とすることにより、空回り防止効果の向上を図ることができるからである。
Next, a modification of this embodiment is shown.
In the above, the design printing layer 32 is not provided in the portion where the polymer constituting the blocking portion 7 is applied, and the configuration in which the polymer is directly applied to the inner surface of the base film 32 is exemplified. The design printing layer 32 may be provided in the part which coats.
Further, in the above, the blocking portion 7 is composed of a coating portion coated with a polymer. For example, as shown in FIG. 7, the inner surface of the base film 31 is exposed in a range where the blocking portion 7 is provided. May be. That is, by exposing the base film 32 to a part of the inner surface of the cylindrical body corresponding to the lower portion 22 a of the body 2 of the container 2, this can be used as the blocking portion 7. Since this film exposed part (blocking part 7) is a base film which comprises the heat-shrinkable cylindrical label 1, it can be softened at the heat shrink temperature of the heat-shrinkable cylindrical label 1. Therefore, when the heat-shrinkable cylindrical label 1 is heat-shrink mounted, the film exposed portion is in close contact with the outer surface of the lower portion 22a of the body 2 of the container 2. Thus, the blocking part 7 which consists of a film exposure part can prevent the idle rotation of the cylindrical label 1 similarly to the blocking part 7 which consists of the said polymer coating part. Further, the film exposed portion may be subjected to a surface treatment such as a corona discharge treatment. By performing such a process, the adhesion of the blocking portion 7 to the outer surface of the container 2 can be enhanced. The corona discharge treatment is carried out so that the treated surface is preferably 45 dynes or more, more preferably 50 dynes or more, particularly preferably 52 dynes or more. The present inventors have proved that when the treated surface after the corona discharge treatment is 40 dynes or less, the idling prevention effect is small, and by setting it to the above numerical value or more, the idling prevention effect can be improved. .

さらに、本実施形態に於いて、ブロッキング部7は、1カ所形成されているものを例示したが、胴部下方22aに対応する位置に設けられていれば良く、例えば、容器2の周方向に間隔を開けて複数のブロッキング部7を形成することもできる。
このように、ブロッキング部7を複数設ける場合においては、熱収縮性筒状ラベル1(筒状ラベル連続体)を扁平状にした際、ブロッキング部7同士が重ならないような位置に、複数のブロッキング部7が配置される。これは、扁平状の熱収縮性筒状ラベル1(筒状ラベル連続体)の開口不良を防止するためである。
また、本実施形態のブロッキング部7は、少なくとも胴部下方22aに対応する位置に形成されていれば良いので、例えば、ブロッキング部7は、センターシール部4の内面又は/及び余り代5の内面であってその内面の胴部下方22aに対応する位置に形成されていてもよい。
また、筒状ラベル1の上縁から下縁に亘って、帯状にブロッキング部7を形成してもよい。
Further, in the present embodiment, the blocking portion 7 is illustrated as being formed at one place, but it may be provided at a position corresponding to the lower portion 22a of the trunk portion, for example, in the circumferential direction of the container 2 A plurality of blocking portions 7 can also be formed at intervals.
Thus, in the case where a plurality of blocking portions 7 are provided, when the heat-shrinkable cylindrical label 1 (cylindrical label continuous body) is flattened, a plurality of blocking portions 7 are arranged at positions where the blocking portions 7 do not overlap each other. Part 7 is arranged. This is to prevent a defective opening of the flat heat-shrinkable cylindrical label 1 (tubular label continuous body).
Moreover, since the blocking part 7 of this embodiment should just be formed in the position corresponding to the trunk | drum lower part 22a at least, for example, the blocking part 7 is the inner surface of the center seal | sticker part 4, and / or the inner surface of the remainder margin 5. However, it may be formed at a position corresponding to the lower portion 22a of the inner surface of the body.
Moreover, you may form the blocking part 7 in strip shape ranging from the upper edge of the cylindrical label 1 to a lower edge.

<第2実施形態>
第2実施形態は、余り代の内面にブロッキング部が設けられている熱収縮性筒状ラベルに係る。以下、主として、上記第1実施形態と異なる構成及び作用効果について説明し、同様の構成などについては説明を省略し、用語及び図番を援用する場合がある。
<Second Embodiment>
2nd Embodiment concerns on the heat-shrinkable cylindrical label by which the blocking part is provided in the inner surface of the remainder. Hereinafter, the configuration and effects different from those of the first embodiment will be mainly described, and description of the same configuration and the like may be omitted, and terms and figure numbers may be used.

本実施形態の熱収縮性筒状ラベル1は、図8に示すように、センターシール部4に於ける少なくとも余り代5の内面にブロッキング部7が形成されている。この余り代5は、上記第1実施形態で示したように、一側端部3aの内側に位置するラベル基材3の他側端部3bが、センターシール部4から周方向に延出された部分であり、筒状体の上端縁から下端縁にかけて帯状に形成されている。この余り代5の幅は、通常、3mm〜7mm程度であるが、特にこの長さに限定されるものではない。   As shown in FIG. 8, the heat-shrinkable cylindrical label 1 of the present embodiment has a blocking portion 7 formed on the inner surface of at least the margin 5 in the center seal portion 4. As shown in the first embodiment, the surplus margin 5 is such that the other end portion 3b of the label base material 3 located inside the one end portion 3a extends from the center seal portion 4 in the circumferential direction. And is formed in a band shape from the upper end edge to the lower end edge of the cylindrical body. The width of the margin 5 is usually about 3 mm to 7 mm, but is not particularly limited to this length.

このブロッキング部7は、上下帯状の余り代5の内面全体に設けられていてもよいし、余り代5の上下方向に点状に連なって設けられていてもよい。
熱収縮性筒状ラベル1の製造や空回り防止の観点から、ブロッキング部7は、余り代5の内面全体に、帯状に設けられていることが好ましい。
このブロッキング部7は、上記第1実施形態で示したように、熱収縮温度で軟化しうるポリマーを塗工することにより形成されていてもよいし、或いは、ベースフィルム31の内面を露出させることにより形成されていてもよい。
ポリマーを塗工してブロッキング部7を形成する場合、図8に示すように、意匠印刷層32が、該ブロッキング部7の設けられる範囲にも、意匠印刷層32が設けられていることが好ましい。なぜなら、上述のようにラベル基材3の一側端部3aの内面には、意匠印刷層32が設けられていないため、余り代5の部分に意匠印刷層32が設けられていないと、熱収縮性筒状ラベルの外観上、意匠印刷のない部分が筋状に現れるからである。
もっとも、センターシール部4に於いて、センターシール部4に於いて、外側に位置する一側端部3aの施された意匠印刷層と内側に位置する他側端部3bに施された意匠印刷層とが、重なるように構成されていれば、外観上、上記筋状部分は現れない。従って、このように構成されている場合には、図8に示すように、余り代5全体に意匠印刷層32を設ける必要性はなく、例えば、余り代5の縁部側に意匠印刷層32を設けない構成に変更することも可能である。
The blocking portion 7 may be provided on the entire inner surface of the upper and lower belt-like surplus margin 5 or may be provided in a dotted manner in the vertical direction of the surplus margin 5.
From the viewpoint of manufacturing the heat-shrinkable cylindrical label 1 and preventing idling, it is preferable that the blocking portion 7 is provided in a strip shape on the entire inner surface of the remainder 5.
As shown in the first embodiment, the blocking portion 7 may be formed by applying a polymer that can be softened at a heat shrink temperature, or the inner surface of the base film 31 is exposed. May be formed.
When the blocking part 7 is formed by coating a polymer, it is preferable that the design printing layer 32 is provided in the range where the design printing layer 32 is provided as shown in FIG. . This is because, as described above, the design printing layer 32 is not provided on the inner surface of the one side end 3a of the label base material 3, and therefore, if the design printing layer 32 is not provided in the portion of the margin 5, This is because, on the appearance of the shrinkable cylindrical label, a portion without design printing appears in a streak shape.
However, in the center seal portion 4, the design printing layer applied to the outer side end portion 3 b positioned on the inner side and the outer side end portion 3 b positioned on the inner side in the center seal portion 4. If the layers are configured to overlap with each other, the streak portion does not appear in appearance. Accordingly, in the case of such a configuration, as shown in FIG. 8, it is not necessary to provide the design printing layer 32 on the entire remainder allowance 5, for example, the design printing layer 32 on the edge side of the remainder allowance 5. It is also possible to change to a configuration in which no is provided.

また、図9に示すように、余り代5の内面のみならず、センターシール部4に対応する他側端部3bの内面にまでブロッキング部7が形成されていてもよい。
また、特に図示しないが、ブロッキング部7は、余り代5全体(筒状ラベル1の上縁から下縁)に設けられているものに限られず、余り代5の一部、例えば、容器2の胴部下方22aに対応する位置や、筒状ラベル1の上縁部及び下縁部などに設けられていても良い。
尚、筒状体(熱収縮性筒状ラベル1)の最内面のうち、ブロッキング部7が設けられた範囲を除いて、滑り層32が設けられている。
Further, as shown in FIG. 9, the blocking portion 7 may be formed not only on the inner surface of the margin 5 but also on the inner surface of the other end portion 3 b corresponding to the center seal portion 4.
Further, although not particularly illustrated, the blocking portion 7 is not limited to the one provided in the entire margin 5 (from the upper edge to the lower edge of the cylindrical label 1), and a part of the margin 5, for example, the container 2 You may be provided in the position corresponding to the trunk | drum lower part 22a, the upper edge part of the cylindrical label 1, and a lower edge part.
In addition, the sliding layer 32 is provided except the range in which the blocking part 7 was provided among the innermost surfaces of a cylindrical body (heat-shrinkable cylindrical label 1).

本実施形態の熱収縮性筒状ラベル1は、上記第1実施形態と同様に、大気圧よりも高い状態で収納物が封入された合成樹脂製の可撓性容器2の少なくとも胴部22に装着される。
該熱収縮性筒状ラベル1も、内面の大半に滑り層33が設けられているので、容器2に対してスムースに外嵌できる。
そして、該熱収縮性筒状ラベル1を加熱した際、余り代5は、それ自身の収縮及び外側に重なった一側端部3aの収縮力によって、容器2の外面側へと強く押圧され、軟化したブロッキング部7が容器2の胴部22の外面に密着する。センターシール部4の近傍は、収縮力が強いため、ブロッキング部7が、容器胴部22の外面に強く押圧されて密着する。このブロッキング部7は、余り代5の上下方向に形成されているので、例えば、開栓時に比較的大きく縮小する胴部中央22bを有する容器2に装着しても、ブロッキング部7が、該容器胴部22の上下部分に於いて強く密着した状態を維持できる。従って、ラベル装着済みの容器を開閉栓する際、熱収縮性筒状ラベル1が空回りすることを防止できる。
As in the first embodiment, the heat-shrinkable cylindrical label 1 according to the present embodiment is attached to at least the trunk portion 22 of the synthetic resin-made flexible container 2 in which the stored items are sealed in a state higher than the atmospheric pressure. Installed.
Since the heat-shrinkable cylindrical label 1 is also provided with the sliding layer 33 on most of the inner surface, it can be smoothly fitted onto the container 2.
And when the heat-shrinkable cylindrical label 1 is heated, the surplus margin 5 is strongly pressed toward the outer surface side of the container 2 by the contraction of itself and the contraction force of the one side end portion 3a that overlaps the outside. The softened blocking portion 7 is in close contact with the outer surface of the body portion 22 of the container 2. Since the contraction force is strong in the vicinity of the center seal portion 4, the blocking portion 7 is strongly pressed against and closely contacts the outer surface of the container body portion 22. Since the blocking portion 7 is formed in the up and down direction of the margin of allowance 5, for example, even if the blocking portion 7 is attached to the container 2 having the trunk center 22b that is relatively greatly reduced when the cap is opened, the blocking portion 7 is not attached to the container. It is possible to maintain a tight contact state at the upper and lower portions of the body portion 22. Therefore, it is possible to prevent the heat-shrinkable cylindrical label 1 from idling when the container with the label attached is opened and closed.

以下、本発明の実施例を示す。ただし、本発明は、下記実施例に限定されるものではない。   Examples of the present invention will be described below. However, the present invention is not limited to the following examples.

(実施例1)
熱収縮性フィルムとして厚み50μmのポリスチレン系延伸フィルム(グンゼ包装システム社製、商品名:GMVS)を用い、そのフィルムの片面に、センターシール部を形成する範囲(フィルムの一縁から5mm幅の範囲)及びブロッキング部を形成する範囲(フィルムの下縁から高さ40mm、幅10mmの範囲)を除き、滑り成分を含むアクリル系メジウムインキ(大日精化工業社製、商品名:STR耐熱CSメジウム。ガラス転移温度約50℃)を塗工した。塗工方法は、グラビア印刷法(70線、塗工時の厚み2〜4μm)により行った。
次に、上記ブロッキング部を形成する範囲に、滑り成分を含まないアクリル系メジウムインキ(サカタインクス社製、商品名:エトナ調色用メジウム。ガラス転移温度約50℃)を、溶剤を用いて粘度調整した後、塗工した。なお、塗工方法は、グラビア印刷法(70線、塗工時の厚み2〜4μm)により行った。
このフィルムを、塗工面を内側にして筒状にし、両側端部を接着してセンターシール部を形成することにより、熱収縮性筒状ラベルを作製した。
得られた筒状ラベルを、500mlのペタロイド型PET製容器(東洋製罐製。但し、内部に炭酸飲料を充填したもの)の肩部から胴部下端縁にかけて外嵌し、90℃のスチームトンネルに5秒間曝して熱収縮装着した。
(Example 1)
Using a polystyrene stretched film with a thickness of 50 μm (trade name: GMVS, manufactured by Gunze Packaging System Co., Ltd.) as a heat-shrinkable film, a range in which a center seal portion is formed on one side of the film (a range of 5 mm width from one edge of the film) ) And a range where a blocking part is formed (a range of 40 mm in height and 10 mm in width from the lower edge of the film), and an acrylic medium ink containing a sliding component (trade name: STR heat-resistant CS medium manufactured by Dainichi Seika Kogyo Co., Ltd.). The glass transition temperature was about 50 ° C.). The coating method was performed by a gravure printing method (70 lines, coating thickness of 2 to 4 μm).
Next, in the range where the blocking part is formed, the viscosity of the acrylic medium ink containing no slipping component (manufactured by Sakata Inx Corporation, trade name: Etna toning medium. Glass transition temperature: about 50 ° C.) is adjusted using a solvent. And then coated. In addition, the coating method was performed by the gravure printing method (70 lines, thickness 2-4 micrometers at the time of coating).
A heat-shrinkable cylindrical label was produced by forming this film into a cylindrical shape with the coating surface on the inside, and bonding the end portions on both sides to form a center seal portion.
The obtained cylindrical label was externally fitted from the shoulder part to the lower end edge of the trunk part of a 500 ml petaloid type PET container (made by Toyo Sei, but filled with carbonated beverage), and a 90 ° C. steam tunnel. For 5 seconds to heat-shrink.

このラベル装着済み容器を、23℃で24時間養生して、容器と筒状ラベルの間に残存する水分を除去した。
その後、ラベル装着済み容器のネジキャップを一旦開栓して内圧を下げ、該キャップを再封した。再封後、直ぐに下記開栓トルク試験を行った。
なお、この容器は、開栓後、胴部中央(胴部の中間位置)の周長さが、開栓前の0.989倍に、胴部下方(凹み部の上端から10mm上方位置)の周長さが、開栓前の0.997倍に変形した。
This labeled container was cured at 23 ° C. for 24 hours to remove water remaining between the container and the cylindrical label.
Thereafter, the screw cap of the label-mounted container was once opened to reduce the internal pressure, and the cap was resealed. Immediately after resealing, the following opening torque test was conducted.
In addition, after opening the container, the circumference of the trunk part (middle position of the trunk part) is 0.989 times that before opening, and the container is below the trunk part (position 10 mm above the upper end of the recess). The perimeter was deformed 0.997 times before opening.

開栓トルク試験は、トルク試験機(型名:2TME450CN(最大4.5N・mまで測定可能)、株式会社東日製作所製)を測定した。このトルク試験機のチャック100に、上記ラベル装着済み容器10の注出部分を固定した(図10参照)。なお、この注出部分の固定とは、回転力を加えても開栓しないように固定したものである。
この容器の胴部を筒状ラベルの上から片手で握って、ネジキャップの回転中心軸周りに回転させ、筒状ラベルが空回りし始めた際の最大トルクを測定した。測定は、3サンプル行った。何れのサンプルも、トルク値450cN・m以上(トルク試験機の測定限界)であった。
The opening torque test was performed by measuring a torque tester (model name: 2TME450CN (measurable up to 4.5 N · m), manufactured by Tohnichi Corporation). The pouring portion of the label-equipped container 10 was fixed to the chuck 100 of this torque tester (see FIG. 10). In addition, fixing of this extraction | pouring part is fixed so that it may not open even if a rotational force is applied.
The body of the container was grasped with one hand from above the cylindrical label and rotated around the rotation center axis of the screw cap, and the maximum torque when the cylindrical label began to idle was measured. Three samples were measured. Each sample had a torque value of 450 cN · m or more (measurement limit of the torque tester).

(実施例2)
ブロッキング部を形成する範囲を、フィルムの他縁から10mm幅で且つフィルムの上下縁に亘った帯状の範囲としたこと以外は、実施例1と同様にして熱収縮性筒状ラベルを作製し、同様に、ペタロイド型PET製容器に装着し、開栓トルク試験を行った。なお、この実施例2は、上記第2実施形態に係る熱収縮性筒状ラベルに対応する。
その結果、何れのサンプルも、トルク値450cN・m以上(トルク試験機の測定限界)であった。
(Example 2)
A heat-shrinkable cylindrical label was produced in the same manner as in Example 1 except that the range for forming the blocking portion was a band-shaped range that was 10 mm wide from the other edge of the film and spanned the upper and lower edges of the film, Similarly, it was attached to a petaloid type PET container, and an opening torque test was conducted. In addition, this Example 2 respond | corresponds to the heat-shrinkable cylindrical label which concerns on the said 2nd Embodiment.
As a result, each sample had a torque value of 450 cN · m or more (measurement limit of the torque tester).

(実施例3)
滑り成分を含まないアクリル系メジウムインキを塗工しなかった(つまり、ブロッキング部を形成する範囲は、フィルム面が露出している)こと以外は、実施例1と同様にして熱収縮性筒状ラベルを作製し、同様に、ペタロイド型PET製容器に装着し、開栓トルク試験を行った。
その結果、何れのサンプルも、トルク値450cN・m以上(トルク試験機の測定限界)であった。
(Example 3)
A heat-shrinkable cylindrical shape in the same manner as in Example 1 except that the acrylic medium ink containing no sliding component was not applied (that is, the film surface was exposed in the area where the blocking portion was formed). A label was prepared and similarly mounted on a petaloid type PET container, and an opening torque test was performed.
As a result, each sample had a torque value of 450 cN · m or more (measurement limit of the torque tester).

(実施例4)
熱収縮性フィルムとして、厚み50μmのポリエチレンテレフタレート系延伸フィルム(東洋紡績社製、商品名:S7042)を用いたこと、及び、滑り成分を含まないインキとして、ウレタン系メジウムインキ(大日精化工業社製、商品名:NTハイラミック調色用メジウム)を用いたこと以外は、実施例1と同様にして熱収縮性筒状ラベルを作製し、同様に、ペタロイド型PET製容器に装着し、開栓トルク試験を行った。
その結果、何れのサンプルも、トルク値450cN・m以上(トルク試験機の測定限界)であった。
Example 4
As a heat-shrinkable film, a 50 μm thick polyethylene terephthalate-based stretched film (trade name: S7042 manufactured by Toyobo Co., Ltd.) was used, and urethane-based medium ink (Daiichi Seika Kogyo Co., Ltd.) containing no slip component. Manufactured under the trade name: NT Hiramic Toning Medium), a heat-shrinkable cylindrical label was prepared in the same manner as in Example 1, and similarly attached to a petaloid-type PET container and opened. A torque test was performed.
As a result, each sample had a torque value of 450 cN · m or more (measurement limit of the torque tester).

(比較例1)
熱収縮性フィルムとして厚み50μmのポリスチレン二軸延伸フィルム(グンゼ包装システム社製、商品名:GMVS)を用い、そのフィルムの片面に、センターシール部を形成する範囲(フィルムの一縁から5mm幅の範囲)を除き、滑り成分を含むアクリル系メジウムインキ(大日精化工業社製、商品名:STR耐熱CSメジウム。ガラス転移温度約50℃)を塗工した。塗工方法は、グラビア印刷法(70線、塗工時の厚み2〜4μm)により行った。
このフィルムを、塗工面を内側にして筒状にし、両側端部を接着してセンターシール部を形成することにより、熱収縮性筒状ラベルを作製した。
以下、実施例1と同様にして、ペタロイド型PET製容器に装着し、開栓トルク試験を行った。
その結果、3サンプルの平均値で、トルク値83cN・mであった。
(Comparative Example 1)
As a heat-shrinkable film, a polystyrene biaxially stretched film (Gunze Packaging System Co., Ltd., trade name: GMVS) having a thickness of 50 μm is used, and a range in which a center seal portion is formed on one side of the film (5 mm wide from one edge of the film) Except for the range, an acrylic medium ink containing a slip component (manufactured by Dainichi Seika Kogyo Co., Ltd., trade name: STR heat-resistant CS medium, glass transition temperature of about 50 ° C.) was applied. The coating method was performed by a gravure printing method (70 lines, coating thickness of 2 to 4 μm).
A heat-shrinkable cylindrical label was produced by forming this film into a cylindrical shape with the coating surface on the inside, and bonding the end portions on both sides to form a center seal portion.
Thereafter, in the same manner as in Example 1, it was attached to a petaloid type PET container, and an opening torque test was conducted.
As a result, the average value of the three samples was a torque value of 83 cN · m.

以上の結果から、実施例1〜4の熱収縮性筒状ラベルは、容器に装着した後、空回りし難いことが判り、一方、比較例1の熱収縮性筒状ラベルは、空回りし易いことが判る。   From the above results, it can be seen that the heat-shrinkable cylindrical labels of Examples 1 to 4 are difficult to idle after being attached to the container, while the heat-shrinkable cylindrical labels of Comparative Example 1 are easy to idle. I understand.

第1実施形態に係る熱収縮性筒状ラベルを示す斜視図。The perspective view which shows the heat-shrinkable cylindrical label which concerns on 1st Embodiment. 同A−A線に於いて、ラベルを周方向で切断した一部省略端面図。The partially abbreviated end view which cut | disconnected the label in the circumferential direction in the AA line. ラベル基材を内面側から示した斜視図。The perspective view which showed the label base material from the inner surface side. 本発明の熱収縮性筒状ラベルが装着される容器の一実施形態を示す正面図。The front view which shows one Embodiment of the container with which the heat-shrinkable cylindrical label of this invention is mounted | worn. ラベル装着済み容器を示す正面図。The front view which shows the label mounting | wearing container. 熱収縮性筒状ラベルの装着位置が異なったラベル装着済み容器を示す正面図。The front view which shows the label mounted container from which the mounting position of the heat-shrinkable cylindrical label differed. (a)は、第1実施形態の変形例に係る熱収縮性筒状ラベルを周方向で切断した一部省略端面図、(b)は、同(a)の熱収縮性筒状ラベルに用いられるラベル基材を内面側から示した斜視図。(A) is a partially omitted end view of a heat-shrinkable cylindrical label according to a modification of the first embodiment cut in the circumferential direction, and (b) is used for the heat-shrinkable cylindrical label of (a). The perspective view which showed the label base material used from the inner surface side. (a)は、第2実施形態に係る熱収縮性筒状ラベルを周方向で切断した一部省略端面図、(b)は、同(a)の熱収縮性筒状ラベルに用いられるラベル基材を内面側から示した斜視図。(A) is a partially omitted end view of the heat-shrinkable cylindrical label according to the second embodiment cut in the circumferential direction, and (b) is a label base used for the heat-shrinkable cylindrical label of (a). The perspective view which showed the material from the inner surface side. 第2実施形態の変形例に係る熱収縮性筒状ラベルを周方向で切断した一部省略端面図。The partial omission end view which cut | disconnected the heat-shrinkable cylindrical label which concerns on the modification of 2nd Embodiment in the circumferential direction. 開栓トルク試験の実施状況を示す参考正面図。The reference front view which shows the implementation status of the opening torque test.

符号の説明Explanation of symbols

1…熱収縮性筒状ラベル、2…容器、21…容器の底面部、22…容器の胴部、22a…容器の胴部下方、22b…容器の胴部中央、25…容器の凹み部、3…ラベル基材、31…ベースフィルム、32…意匠印刷層、33…滑り層、3a…一側端部、3b…他側端部、3b’…他側端部の側縁、4…センターシール部、5…余り代、7…ブロッキング部   DESCRIPTION OF SYMBOLS 1 ... Heat-shrinkable cylindrical label, 2 ... Container, 21 ... Container bottom part, 22 ... Container trunk | drum, 22a ... Container trunk | drum lower part, 22b ... Container trunk | drum center, 25 ... Container dent part, DESCRIPTION OF SYMBOLS 3 ... Label base material, 31 ... Base film, 32 ... Design printing layer, 33 ... Sliding layer, 3a ... One side edge part, 3b ... Other side edge part, 3b '... Side edge of the other side edge part, 4 ... Center Seal part, 5 ... remainder, 7 ... blocking part

Claims (4)

下記に示す容器の胴部に装着される熱収縮性筒状ラベルに於いて、
内面に滑り層が設けられた熱収縮性のベースフィルムを筒状に成形した筒状体を有し、容器の胴部下方に対応する筒状体の内面の一部分に、ベースフィルムの熱収縮温度で軟化しうるポリマーを塗工したブロッキング部、又は、ベースフィルムを露出させたブロッキング部の少なくとも何れか一方が設けられていることを特徴とする熱収収縮性筒状ラベル。
ただし、容器は、胴部と、注出口を開閉栓可能なネジキャップとを有し、大気圧よりも高い状態で収納物が封入された合成樹脂製の可撓性容器であって、胴部中央に於ける肉厚が胴部下方に於ける肉厚よりも薄く形成されているものである。
In the heat-shrinkable cylindrical label attached to the body of the container shown below,
It has a cylindrical body made of a heat shrinkable base film with a sliding layer provided on the inner surface, and the heat shrink temperature of the base film on a part of the inner surface of the cylindrical body corresponding to the lower part of the container body A heat-shrinkable cylindrical label, wherein at least one of a blocking part coated with a softening polymer and a blocking part exposing a base film is provided.
However, the container is a flexible container made of a synthetic resin having a trunk portion and a screw cap capable of opening and closing the spout, and in which a stored item is enclosed in a state higher than atmospheric pressure, The wall thickness at the center is formed thinner than the wall thickness below the trunk.
下記に示す容器の胴部に装着される熱収縮性筒状ラベルに於いて、
内面に滑り層が設けられた熱収縮性のベースフィルムを筒状に成形した筒状体を有し、容器の胴部下方に対応する筒状体の内面の一部分に、ベースフィルムの熱収縮温度で軟化しうるポリマーを塗工したブロッキング部、又は、ベースフィルムを露出させたブロッキング部の少なくとも何れか一方が設けられていることを特徴とする熱収収縮性筒状ラベル。
ただし、容器は、胴部と、注出口を開閉栓可能なネジキャップとを有し、大気圧よりも高い状態で収納物が封入された合成樹脂製の可撓性容器であって、ネジキャップの開栓後に於ける胴部下方の周長さが、開栓前の同周長さの0.980〜1.000倍に縮小し、且つネジキャップの開栓後に於ける胴部中央の周長さが、前記胴部下方の周長さの縮小割合よりも大きく縮小するものである。
In the heat-shrinkable cylindrical label attached to the body of the container shown below,
It has a cylindrical body made of a heat shrinkable base film with a sliding layer provided on the inner surface, and the heat shrink temperature of the base film on a part of the inner surface of the cylindrical body corresponding to the lower part of the container body A heat-shrinkable cylindrical label, wherein at least one of a blocking part coated with a softening polymer and a blocking part exposing a base film is provided.
However, the container is a flexible container made of a synthetic resin having a body portion and a screw cap capable of opening and closing the spout, and in which a stored item is sealed in a state higher than atmospheric pressure, and the screw cap The circumference of the lower part of the trunk after opening the plug is reduced to 0.980 to 1.000 times the circumference before opening, and the circumference of the middle of the trunk after opening the screw cap The length is reduced more than the reduction ratio of the circumferential length below the trunk.
下記に示す容器の胴部に装着される熱収縮性筒状ラベルに於いて、
内面に滑り層が設けられた熱収縮性のベースフィルムの一側端部を他側端部の外面に重ね合わせてセンターシールすることにより筒状に成形され、ベースフィルムの他側端部の側縁からセンターシール部までの間に、一側端部に非接着な余り代が確保されており、余り代の内面に、ベースフィルムの熱収縮温度で軟化しうるポリマーを塗工したブロッキング部、又は、ベースフィルムを露出させたブロッキング部の少なくとも何れか一方が設けられていることを特徴とする熱収縮性筒状ラベル。
ただし、容器は、胴部と、注出口を開閉栓可能なネジキャップとを有し、大気圧よりも高い状態で収納物が封入された合成樹脂製の可撓性容器である。
In the heat-shrinkable cylindrical label attached to the body of the container shown below,
One side end of heat-shrinkable base film provided with a sliding layer on the inner surface is overlapped with the outer surface of the other end and center-sealed to form a cylindrical shape. Between the edge and the center seal part, a non-adhesive margin is secured at one side end, and a blocking section coated with a polymer that can be softened at the heat shrink temperature of the base film on the inner surface of the margin, Or at least any one of the blocking part which exposed the base film is provided, The heat-shrinkable cylindrical label characterized by the above-mentioned.
However, the container is a flexible container made of a synthetic resin that has a body portion and a screw cap capable of opening and closing the spout and in which the stored item is sealed in a state higher than atmospheric pressure.
前記容器は、胴部下方に於いて、内側へ凹む複数の凹状部が胴部の周方向に所定間隔を開けて形成されている請求項1〜3のいずれかに記載の熱収縮性筒状ラベル。   The heat-shrinkable cylindrical shape according to any one of claims 1 to 3, wherein the container is formed with a plurality of concave portions recessed inward at a predetermined interval in a circumferential direction of the body portion below the body portion. label.
JP2007146511A 2006-06-29 2007-06-01 Heat-shrinkable cylindrical label Expired - Fee Related JP4969321B2 (en)