JP2008006708A - The hard coat layer transfer foil - Google Patents

The hard coat layer transfer foil Download PDF

Info

Publication number
JP2008006708A
JP2008006708A JP2006179567A JP2006179567A JP2008006708A JP 2008006708 A JP2008006708 A JP 2008006708A JP 2006179567 A JP2006179567 A JP 2006179567A JP 2006179567 A JP2006179567 A JP 2006179567A JP 2008006708 A JP2008006708 A JP 2008006708A
Authority
JP
Grant status
Application
Patent type
Prior art keywords
hard coat
coat layer
layer
transfer foil
transfer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2006179567A
Other languages
Japanese (ja)
Other versions
JP4930764B2 (en )
Inventor
Shinji Tajima
真治 田島
Original Assignee
Dainippon Printing Co Ltd
大日本印刷株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

<P>PROBLEM TO BE SOLVED: To provide a hard coat layer transfer foil having good transparency, protecting an image from a solvent, mechanical friction and abrasion, excellent in durability hard to damage, improved in foil cutting and enabling transfer at a time. <P>SOLUTION: The hard coat layer transfer foil is composed of a base material 11, a mold release layer 13, a hard coat layer 15 and an adhesive layer 19. The hard coat layer 15 contains a cured material of an ionizing radiation curable resin containing a urethane (meth)acrylate oligomer and polyethylene wax, and the mold release layer 13 comprises a melamine resin. The content ratio of polyethylene wax of the hard coat layer 15 is 0.01-5 mass%, the thickness of the hard coat layer 15 is 10 μm or above and the scratch strength of the hard coat layer 15 is 150 g or above as sapphire. <P>COPYRIGHT: (C)2008,JPO&INPIT

Description

本発明は、ハードコート層転写箔に関し、さらに詳しくは、転写画像を有する媒体などへ優れた耐摩擦性、耐溶剤性などの耐久性を付与し、媒体へ転写する際には、箔切れがよく転写性に優れるハードコート層転写箔に関するものである。 The present invention relates to a hard coat layer transfer foil, more particularly, wear resistance superior to such media having a transferred image, to impart durability, such as solvent resistance, in transferring the medium, the foil breakage It may relate hard coat layer transfer foil which is excellent in transferability.

本明細書において、配合を示す「比」、「部」、「%」などは特に断わらない限り質量基準であり、「/」印は一体的に積層されていることを示す。 Herein denotes formulation "ratio", "part" and "%" are by weight unless otherwise indicated, "/" mark indicates that it is integrally laminated.

(主なる用途)本発明のハードコート層転写箔を用いて、支持体へハードコート層を転写した媒体の用途としては、例えばクレジットカード、キャッシュカード、IDカードなどのカード類、パスポート、会員証、免許証、あるいは預金通帳、などの冊子類の、昇華性染料の顔写真に代表される個人識別用情報などを記録された媒体などのセキリティ性を求められる媒体に好適に使用できる。 Using the hard coat layer transfer foil (Lord use) the present invention, the use of the transferred medium hard coat layer to a support, for example a credit card, cash card, cards such as ID cards, passports, membership card , license, or a booklet such bankbook, etc., can be suitably used for medium asked to Sekiriti of such medium that have personal identification information represented by the face photograph of sublimable dyes. しかしながら、表面に耐久性を必要とする用途であれば、特に限定されるものではない。 However, if applications requiring durability on the surface, but is not particularly limited.

(背景技術)簡便な印刷方法として熱転写方法が広く使用される様になった。 It became (background art) as a thermal transfer method is widely used as a simple printing method. これらの熱転写方法では、各種の画像が簡便に形成されるので、印刷枚数が比較的少なくてもよい印刷物、例えば、身分証明書等のIDカードの作成等に利用される様になっている。 In these thermal transfer method, since various images are conveniently formed, relatively small which may be printed material printed sheets, for example, has become as utilized to create such an ID card identification and the like. 又、顔写真等の如くカラー画像が好ましい場合には、連続した基材フイルム上に、例えば、イエロー、マゼンダ及びシアン(更に必要に応じてブラック)の着色熱転写層を面順次に繰返し多数設けた長尺熱転写フイルムを用いる熱転写方法が行なわれている。 Further, when a color image is preferred as such a face photograph, on a substrate film a continuous, for example, yellow, provided many repeated colored thermal transfer layer sequentially face (black, if necessary) magenta and cyan thermal transfer method using a long thermal transfer film has been performed. この様な熱転写フイルムは大別すると、それらの熱転写層が加熱によって軟化して画像状に被熱転写材に熱転写される、所謂溶融転写タイプの熱転写フイルムと、加熱によって熱転写層中の染料が昇華(熱移行)して染料のみが画像状に被熱転写材上に熱転写する、所謂昇華タイプの熱転写フイルムとに大別される。 When such thermal transfer film is roughly classified into those of the thermal transfer layer is thermally transferred onto the thermal transfer material to soften the image shape by heating, and the so-called melt transfer type thermal transfer film, the dye of the thermal transfer layer by heating sublimation ( only thermal migration) to dye thermally transferred onto the thermal transfer material to the image shape, are classified into a so-called sublimation type thermal transfer film.
以上の如き熱転写フイルムで、身分証明書等のIDカードを作成する場合、溶融転写タイプの熱転写フイルムの場合は、文字や数字等の如き画像の形成は容易であるが、これらの画像は耐久性、特に耐摩擦性が劣るという欠点がある。 In above-described thermal transfer film, when creating the ID card identification, etc., in the case of melt transfer type thermal transfer film, but formation of such image such as characters and figures is easy, these images durability , there is a disadvantage that particularly abrasion resistance is poor. 一方、昇華転写型の熱転写フイルムの場合には、顔写真等の階調性画像を形成することが出来るが、形成された画像は通常の印刷インキとは異なり、ビヒクルが無い為、耐光性、耐候性、耐摩擦性等の耐久性に劣るという問題がある。 On the other hand, in the case of a sublimation transfer type thermal transfer film is capable of forming a gradation image such as face photograph, unlike the formed image usual printing inks, since the vehicle is not, light resistance, weather resistance, there is a problem of poor durability of the abrasion resistance and the like.
上記問題を解決する方法として、透明樹脂層や硬化樹脂層などの保護層(本発明のハードコート層に相当する)を転写する方法が多数提案されている。 As a method for solving the above problems, a method of transferring a protective layer such as a transparent resin layer and the cured resin layer (corresponding to the hard coat layer of the present invention) have been proposed. しかしながら、画像は最表面に存在する為、長期間の間には機械的な摩擦、溶剤やその他の薬品或は環境の影響を受け経時的に耐久性が低下し、また、極めて過酷な環境で使用されるガソリンスタンドカードや工事現場カード、及び、使用期限がなかったり、長期にわたる入退室カードやポイントカード、金融機関などの多数のセキュリティ管理された部屋への入退室を繰り返す入退室カードなどが増加しており、未だ充分な耐久性が得られていない。 However, the image to present on the outermost surface, between the long-term mechanical friction, over time durable affected solvents or other chemicals or environmental decreased, also, in an extremely harsh environment gas station cards and construction site card is used, and, or there is no expiration date, long-term entry and exit card and point card, repeat the entry and exit to a large number of security management has been the room, such as financial institutions such as the entry and exit card increased and, not yet sufficient durability can not be obtained. しかしながら、保護層を厚くすると箔切れが著しく悪くなるので、2回重ねて転写したりしている。 However, since the cutting foil when the thickness of the protective layer is significantly deteriorated, and or transfer superposed twice.
従って、ハードコート層(保護層)転写箔は、極めて過酷な環境での使用、使用期限がなかったり、長期にわたる使用、及び/又は多数回の繰り返し使用などでも、透明性がよく、溶剤、機械的な摩擦、及び摩耗から画像を保護し、傷付きにくい耐久性に優れ、しかも、箔切れがよく1回で転写できることが求められている。 Accordingly, the hard coat layer (protective layer) transfer foil, for use in extremely harsh environments, or no expiration date, long-term use, and / or the like many times repeated use, good transparency, solvent, mechanical frictional, and protects the image from abrasion, excellent hard scratched durability, moreover, it is required to be transferred by the foil breakage may once.

(先行技術)従来、社員証カードの顔写真画像の表面の摩耗性などの耐久性を高めるために、剥離層を有する支持体から、少なくとも、剥離層、特定樹脂の硬化層、光学変化素子層、中間層、接着層を、顔写真上へ転写することが知られている(例えば、特許文献1参照。)。 (Prior art) Conventionally, in order to improve the durability such as surface abrasion resistance of the facial photograph image of the employee ID card, a support having a release layer, at least, the release layer, cured layer of a specific resin, optical variable device layer , an intermediate layer, an adhesive layer, it is known to transfer onto the face photograph (e.g., see Patent Document 1.).
本出願人も、熱転写画像等に耐光性、耐摩擦性、耐可塑剤性、耐薬品性等の各種耐久性を付与できる保護層転写フィルムとして、基材フィルム/透明性樹脂層/極性基を有する成分を含有するアクリル系共重合樹脂で、且つ帯電防止性を有する樹脂で構成した耐可塑剤性樹脂層/熱接着性樹脂層の順に積層した積層体を開示している(例えば、特許文献2参照。)。 The applicant also light resistance in the thermal transfer image or the like, abrasion resistance, plasticizer resistance, the protective layer transfer film capable of imparting various durability such as chemical resistance, the substrate film / transparent resin layer / a polar group an acrylic copolymer resin containing a component having and discloses a laminate formed by laminating in this order plasticizer resistant resin layer / heat-adhesive resin layer of a resin having antistatic properties (e.g., Patent documents 2 reference.).
さらに、本出願人は、熱転写画像の各種耐久性、特に耐薬品性、耐光性及び耐候性等が長期間維持される保護層転写フイルムとして、基材フイルム/透明樹脂層(剥離可能)/耐薬品性付与層、紫外線遮断層及びセキュリティ層のうちの少なくとも1層が設けられているものを開示している(例えば、特許文献3参照。)。 Moreover, the Applicant has various durability of the thermal transfer image, especially chemical resistance, as a protective layer transfer film of light resistance and weather resistance and the like can be maintained for a long period of time, substrate film / transparent resin layer (peelable) / resistant drug-imparting layer, at least one layer of the ultraviolet blocking layer and the security layer is disclosed which is provided (for example, see Patent Document 3.).
しかしながら、上記いずれでも、画像表面の耐久性が厳しい使用条件下では未だ不足しているという問題点がある。 However, the either, there is a problem that is insufficient still in durability severe use conditions of the image surface.

特開2001−138674号公報 JP 2001-138674 JP 特開平07−156567号公報 JP 07-156567 discloses 特開平05−330259号公報 JP 05-330259 discloses

そこで、本発明はこのような問題点を解消するためになされたものである。 The present invention has been made to solve the above problems. その目的は、透明性がよく、溶剤、機械的な摩擦、及び摩耗から画像を保護し、傷付きにくい耐久性に優れ、しかも、箔切れがよく1回で転写できるハードコート層転写箔を提供することである。 Its purpose is good transparency, solvent, mechanical friction, and to protect the image from abrasion, excellent hard scratched durability, moreover, provide a hard coat layer transfer foil capable of transferring a foil breakage may once It is to be.

上記の課題を解決するために、請求項1の発明に係わるハードコート層転写箔は、基材と、該基材の一方の面へ離型層、ハードコート層及び接着層を設けてなるハードコート層転写箔において、上記離型層がメラミン系樹脂であり、上記ハードコート層が電離放射線硬化性樹脂の硬化物及びポリエチレンワックスを含んでいるように、したものである。 In order to solve the above problem, the hard coat layer transfer foil according to the present invention as claimed in claim 1, formed by providing a substrate, the release layer to one surface of the substrate, a hard coat layer and the adhesive layer hard in coating layer transfer foil is the release layer is a melamine-based resin, as the hard coat layer contains a cured product and polyethylene wax ionizing radiation curable resin is obtained by.
請求項2の発明に係わるハードコート層転写箔は、上記電離放射線硬化性樹脂の硬化物が(1)分子中にイソシアネート基を3個以上有するイソシアネート類、(2)分子中に水酸基を少なくとも1個と(メタ)アクリロイルオキシ基を少なくとも2個有する多官能(メタ)アクリレート類、又は(3)分子中に水酸基を少なくとも2個有する多価アルコール類の反応生成物であるウレタン(メタ)アクリレートオリゴマーを含有する電離放射線硬化性樹脂の硬化物であるように、したものである。 Hard coat layer transfer foil according to the second aspect of the present invention, isocyanates having a cured product of the ionizing radiation curable resin (1) 3 or more isocyanate groups in the molecule, (2) at least one hydroxyl group in the molecule number and (meth) acrylate polyfunctional (meth) acrylates having at least two acryloyloxy group, or (3) a urethane which is the reaction product of polyhydric alcohols having at least two hydroxyl groups in the molecule (meth) acrylate oligomer as a cured product of an ionizing radiation curable resin containing a is obtained by.
請求項3の発明に係わるハードコート層転写箔は、上記ハードコート層のポリエチレンワックスの含有が質量基準で、電離放射線硬化樹脂:ポリエチレンワックス=100:0.01〜10であるように、したものである。 Hard coat layer transfer foil according to the present invention as claimed in claim 3, in the mass content of the polyethylene wax of the hard coat layer, an ionizing radiation curable resin: polyethylene wax = 100: As is 0.01 to 10, the ones it is.
請求項4の発明に係わるハードコート層転写箔は、上記ハードコート層の厚味が10μm以上であるように、したものである。 Hard coat layer transfer foil according to the present invention as claimed in claim 4, as thickness of the hard coat layer is 10μm or more, it is obtained by.
請求項5の発明に係わるハードコート層転写箔は、スクラッチ強度がサファイア150g以上であるように、したものである。 Hard coat layer transfer foil according to the invention of claim 5 is a scratch strength such that sapphire 150g or more, which was.
請求項6の発明に係わるハードコート層転写箔は、上記ハードコート層と接着層との間に紫外線吸収層を有するように、したものである。 Hard coat layer transfer foil according to the present invention as claimed in claim 6, so as to have an ultraviolet absorbing layer between the hard coat layer and the adhesive layer is obtained by.

請求項1の本発明によれば、極めて過酷な環境での使用、使用期限がなかったり、長期にわたる使用、及び/又は多数回の繰り返し使用などでも、透明性がよく、溶剤、機械的な摩擦、及び摩耗、特に引掻きから画像を保護し、傷付きにくい耐久性に優れ、しかも、箔切れがよく1回で転写できるハードコート層転写箔が提供される。 According to the present invention of claim 1, very used in harsh environments, or no expiration date, long-term use, and / or the like many times repeated use, good transparency, solvent, mechanical friction , and wear, and protects the image from particular scratch, excellent hard scratched durability, moreover, a hard coat layer transfer foil capable of transferring a foil breakage often one is provided.
請求項2〜4の本発明によれば、転写時に箔切れがよりよく、厚いハードコート層でも1回の転写操作で容易に転写させることができるハードコート層転写箔が提供される。 According to the present invention of claims 2 to 4, better foils breakage at the time of transfer, a hard coat layer transfer foil can also be easily transferred in a single transfer operation in the thick hard coat layer.
請求項5の本発明によれば、極めて過酷な環境、長期にわたる使用、及び/又は多数回の繰り返し使用でも、画像を保護し耐久性に優れるハードコート層転写箔が提供される。 According to the present invention of claim 5, very harsh environment, long-term use, and / or in multiple repeated use of the hard coat layer transfer foil superior in durability to protect the image is provided.
請求項6の本発明によれば、請求項1〜5の発明の効果に加えて、紫外線からも画像を保護し、画像を退色しにくくさせるハードコート層転写箔が提供される。 According to the present invention of claim 6, in addition to the effect of the invention of claims 1 to 5, also to protect the image from the ultraviolet, the hard coat layer transfer foil to hardly discolored images is provided.

以下、本発明の実施形態について、図面を参照しながら、詳細に説明する。 Hereinafter, embodiments of the present invention, with reference to the accompanying drawings, will be described in detail.
図1は、本発明の1実施例を示すハードコート層転写箔の断面図である。 Figure 1 is a cross-sectional view of the hard coat layer transfer foil showing an embodiment of the present invention.
図2は、本発明のハードコート層転写箔を用いて、支持体へ転写し画像を保護した状態を示す断面図である。 2, using the hard coat layer transfer foil of the present invention, is a cross-sectional view showing a transferring state of protecting the image to the support.

(ハードコート層転写箔)本発明のハードコート層転写箔10は、図1に示すように、基材11と、該基材11の一方の面へ、少なくとも離型層13、ハードコート層15、必要に応じて紫外線吸収層21及び接着層19が積層され、基材11/離型層13/ハードコート層15/接着層19を必須とする構成である。 (Hard coat layer transfer foil) hard coat layer transfer foil 10 of the present invention, as shown in FIG. 1, a substrate 11, to one surface of the substrate 11, at least the release layer 13, the hard coat layer 15 , ultraviolet absorbing layer 21 and the adhesive layer 19 if necessary are laminated, a configuration that the substrate 11 / the release layer 13 / hardcoat layer 15 / adhesive layer 19 as required. ハードコート層15を後述する材料と、ポリエチレンワックスを含み、好ましくはポリエチレンワックスの添加割合、ハードコート層15の厚味を制御することで、課題を解消することができた。 And material described below the hard coat layer 15 comprises a polyethylene wax, preferably by controlling the addition rate, thickness of the hard coat layer 15 of polyethylene wax, it was possible to solve the problem. 図2は、本発明のハードコート層転写箔10を用いて、ハードコート層15、紫外線吸収層21(必要に応じて)及び接着層19を、支持体101に形成された画像105の表面へ転写した状態を示す。 2, using the hard coat layer transfer foil 10 of the present invention, the hard coat layer 15, an ultraviolet absorbing layer 21 (if necessary) and an adhesive layer 19, to the surface of the formed image 105 on a support 101 It shows transcriptional state. ハードコート層15が最表面に位置し、画像を保護し耐久性を高める。 Located hard coat layer 15 on the top surface, to protect the image enhancing durability.

(基材)基材11としては、耐熱性、機械的強度、製造に耐える機械的強度、耐溶剤性などがあれば、用途に応じて種々の材料が適用できる。 The (base) substrate 11, heat resistance, mechanical strength, mechanical strength to withstand manufacturing, if any such solvent resistance, various materials can be applied depending on the application. 例えば、ポリエチレンテレフタレート、ポリエチレンナフタレートなどのポリエステル系樹脂、ナイロン6などのポリアミド系樹脂、ポリプロピレン、ポリノルボルネンなどのポリオレフィン系樹脂、ポリ塩化ビニルなどのビニル系樹脂、ポリメチルメタアクリレートなどのアクリル系樹脂、ポリカーボネート、高衝撃ポリスチレンなどのスチレン系樹脂、セロファン、セルロースアセテートなどのセルロース系フィルム、ポリイミドなどのイミド系樹脂などがある。 For example, polyethylene terephthalate, polyester resins such as polyethylene naphthalate, polyamide resins such as nylon 6, polypropylene, polyolefin resins such as polynorbornene, vinyl resins such as polyvinyl chloride, acrylic resins such as polymethyl methacrylate , polycarbonate, styrene resins such as high impact polystyrene, cellophane, and the like imide resin, such as cellulose-based film, a polyimide, such as cellulose acetate.
好ましくは、耐熱性、機械的強度の点で、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレートなどのポリエステル系樹脂のフィルムで、ポリエチレンテレフタレートが最適である。 Preferably, the heat resistance in terms of mechanical strength, polyethylene terephthalate, polybutylene terephthalate, a film of polyester resins such as polyethylene naphthalate, is optimal polyethylene terephthalate. 該基材の厚さは、通常、2.5〜50μm程度が適用できるが、4〜25μmが転写性の点で好ましい。 The thickness of the substrate is usually applicable about 2.5~50Myuemu, preferred in terms 4~25μm of transferability.

該基材は、これら樹脂を主成分とする共重合樹脂、または、混合体(アロイを含む)、若しくは複数層からなる積層体であっても良い。 The substrate, a copolymer resin composed mainly of these resins, or, (including alloy) mixture, or it may be a laminate comprising a plurality of layers. また、該基材は、延伸フィルムでも、未延伸フィルムでも良いが、強度を向上させる目的で、一軸方向または二軸方向に延伸したフィルムが好ましい。 Further, the substrate may be a stretched film or may be a non-oriented film, but for the purpose of improving the strength, film stretched uniaxially or biaxially are preferred. 該基材は、これら樹脂の少なくとも1層からなるフィルム、シート、ボード状として使用する。 The substrate, a film consisting of at least one layer of these resins, used sheet, as board-shaped. 該基材は、塗布に先立って塗布面へ、コロナ放電処理、プラズマ処理、オゾン処理、フレーム処理、プライマー(アンカーコート、接着促進剤、易接着剤とも呼ばれる)塗布処理、予熱処理、除塵埃処理、蒸着処理、アルカリ処理、などの易接着処理を行ってもよい。 The substrate, the coating surface prior to coating, corona discharge treatment, plasma treatment, ozone treatment, frame treatment, primer (anchor coat, adhesive promoter, also called easy adhesion) coating treatment, preheating, dust-removing treatment , the deposition process may be carried out an easy-adhesion treatment of alkali treatment, etc.. また、必要に応じて、充填剤、可塑剤、着色剤、帯電防止剤などの添加剤を加えても良い。 If necessary, fillers, plasticizers, colorants, may be added an additive such as an antistatic agent.

(離型層)離型層13としては、通常、離型性樹脂、離型剤を含んだ樹脂、電離放射線で架橋する硬化性樹脂などがあるが、本発明ではメラミン系樹脂を用い、後述するハードコート層15と組合わせることで、離型層13とハードコート層15と間の剥離が安定し、転写時の箔切れ性を著しく向上させることができる。 The (release layer) a release layer 13, normally, releasable resin, resin containing a releasing agent, there is a like curable resin crosslinking with ionizing radiation, using a melamine resin in the present invention, described later by combining the hard coat layer 15, delamination between the release layer 13 and the hard coat layer 15 can be improved remarkably stable, foil cutting property during transfer.

離型層13の形成は、該樹脂を溶媒へ分散又は溶解して、ロールコート、グラビアコートなどの公知のコーティング方法で、塗布し乾燥して、温度150℃〜200℃程度で焼き付ける。 Formation of the release layer 13 is dispersed or dissolved in the resin to the solvent, roll coating, a known coating method such as gravure coating, coated and dried, baked at a temperature 0.99 ° C. to 200 DEG ° C. approximately. 離型層13の厚さとしては、通常は0.01μm〜5.0μm程度、好ましくは0.5μm〜3.0μm程度である。 The thickness of the release layer 13, typically about 0.01Myuemu~5.0Myuemu, preferably about 0.5Myuemu~3.0Myuemu.

(ハードコート層)ハードコート層15は、電離放射線硬化性樹脂の硬化物及びポリエチレンワックスを含むようにする。 (Hard Coat Layer) The hard coat layer 15 is to include a cured product and polyethylene wax ionizing radiation curable resin. 該電離放射線硬化性樹脂としては、好ましくは、(1)分子中にイソシアネート基を3個以上有するイソシアネート類、(2)分子中に水酸基を少なくとも1個と(メタ)アクリロイルオキシ基を少なくとも2個有する多官能(メタ)アクリレート類、又は(3)分子中に水酸基を少なくとも2個有する多価アルコール類の反応生成物であるウレタン(メタ)アクリレートオリゴマーを含有する電離放射線硬化性樹脂を用い、ポリエチレンワックスを含ませて、塗布し乾燥して電離放射線で硬化させればよい。 The ionizing radiation-curable resin, preferably, (1) an isocyanate compound having 3 or more isocyanate groups in the molecule, at least two hydroxyl groups at least one and a (meth) acryloyloxy groups in (2) Molecular polyfunctional (meth) acrylates, or (3) hydroxyl group using a polyhydric alcohol ionizing radiation curable resin containing a urethane (meth) acrylate oligomer is the reaction product of having at least two in the molecule, the polyethylene having moistened with wax, it is only necessary coating and drying to cure with ionizing radiation.

前記ウレタン(メタ)アクリレートオリゴマーを含有する電離放射線硬化性樹脂(本明細書では電離放射線硬化性樹脂組成物Mと呼称する)は、ウレタン(メタ)アクリレートオリゴマーを含有する電離放射線硬化性樹脂の硬化物、具体的には、特開2001−329031号公報で開示されている光硬化性樹脂などが例示できる。 The urethane (herein referred to as the ionizing radiation curable resin composition M) ionizing radiation curable resin containing a (meth) acrylate oligomer, curing the ionizing radiation-curable resin containing a urethane (meth) acrylate oligomer objects, specifically, such as light curing resin disclosed in JP-a-2001-329031 can be exemplified.

(ポリエチレンワックス)ポリエチレンワックスとしては、ポリエチレン系樹脂の粒子やビーズが挙げられるが、好ましくは球状ビーズである。 The (polyethylene wax) polyethylene wax, including but particles or beads of the polyethylene resin, preferably spherical beads. 但し、ポリエチレンワックスを添加すると、箔切れ性は低下するので、その添加量は、電離放射線硬化樹脂100質量部に対して、0.01〜10質量部程度、好ましくは0.1〜5質量部とする。 However, the addition of polyethylene wax, because the foil cutting property decreases, the amount added with respect to 100 parts by mass of the ionizing radiation curing resin, 0.01 to 10 parts by weight, preferably 0.1 to 5 parts by weight to.

(ハードコート層の形成)ハードコート層15の形成は、上記の電離放射線硬化性樹脂にポリエチレンワックス、必要に応じて光重合開始剤、可塑剤、安定剤、界面活性剤等を加え、溶媒へ分散または溶解して、ロールコート、グラビアコート、コンマコート、ダイコートなどの公知のコーティング方法で塗布し乾燥して、電離放射線で反応(硬化)させればよい。 (Formation of hard coat layer) formed on the hard coat layer 15 is a polyethylene wax to the ionizing radiation curable resin, if necessary a photopolymerization initiator, a plasticizer, a stabilizer, surfactant and the like is added, the solvent dispersed or dissolved, roll coating, gravure coating, comma coating, was applied and dried by a known coating method such as die coating, it may be reacted (cured) by ionizing radiation. また、ハードコート層15の厚味が厚いときには、複数回に分けて形成してもよい。 Further, when the thickness of the hard coat layer 15 is thick, it may be formed in a plurality of times.

(ハードコート層の厚味)ハードコート層15の厚さは、通常、1〜10μm程度であるが、本発明では、極めて過酷な環境での使用、使用期限がなかったり、長期にわたる使用、及び/又は多数回の繰り返し使用などでも、溶剤や機械的な摩擦及び摩耗、特に引掻きから画像を保護し、傷付きにくい耐久性を付与するために、好ましくは10μm以上で、好ましくは15μm以上とする。 The thickness of the hard coat layer 15 (thickness of the hard coat layer) is usually about 1 to 10 [mu] m, in the present invention, a very harsh in environments, or no expiration date, long-term use, and in such / or multiple repeated use, solvents and mechanical friction and wear, and protects the image from particular scratch, in order to impart scratch per hard durable, preferably 10μm or more, preferably more than 15μm . 上限は特に限定されないが、価格や箔切れ性から30μm以下程度である。 The upper limit is not particularly limited, it is much 30μm or less from the price and foil cutting property. ハードコート層15の厚味が10μm以上で、好ましくは15μm以上であるようにすることで耐久性が高まり、極めて過酷な環境での使用、使用期限がなかったり、長期にわたる使用、及び/又は多数回の繰り返し使用などでも、化学的機械的な外力から画像を保護できるハードコート層転写箔が得られる。 In thickness of the hard coat layer 15 is 10μm or more, preferably increased durability to ensure that is 15μm or more, the use of an extremely harsh environment, or no expiration date, long-term use, and / or multiple in such times of repeated use, the hard coat layer transfer foil is obtained which can protect the images from chemical mechanical external force.

このように、離型層13としてメラミン系樹脂を、ハードコート層15として少なくとも「電離放射線硬化性樹脂組成物M」の硬化物及びポリエチレンワックスとすることで、次の作用効果を兼ねさせることができるのである。 Thus, the melamine resin as the release layer 13, by a cured product and polyethylene wax of at least "ionizing radiation-curable resin composition M" as a hard coat layer 15, can serve also as the following advantages than is possible. (1)電離放射線硬化前の塗布状態のハードコート層塗膜は指乾状態でべとつかず、ブロッキングせずに巻き取ることができるので、ロールツーロール加工ができ、製造が容易であり、コストも低い。 (1) a hard coat layer coating film of the coating state before ionizing radiation curing is not sticky at the finger dry state, can be wound without blocking, roll-to-roll processing is possible, is easy to manufacture, cost Low. (2)ハードコート層15が破断しやすくなり、箔切れ性を著しく向上できる。 (2) a hard coat layer 15 is easily broken, it can significantly improve the foil cutting property. (3)転写後は、画像を有する支持体の最表面へ位置し、機械的及び/又は化学的な環境から耐久性を発現する。 (3) After the transfer is located to the outermost surface of the support having an image expressing the durability against mechanical and / or chemical environments.

(紫外線吸収層)紫外線吸収層21は必要に応じて、ハードコート層15と接着層19との間に設ければよく、また、必要に応じて他の層をも設けてもよい。 (Ultraviolet absorbing layer) UV-absorbing layer 21 is optionally may be provided between the adhesive layer 19 and the hard coat layer 15, or may be provided also other layers as necessary. 紫外線吸収層21を設けることで、特に昇華転写型インクリボンを用いて形成した顔写真などの画像は主に耐光性の悪い染料で構成されているが、耐光性を向上させ長期間にわたって画像を維持できる。 By providing the ultraviolet absorbing layer 21, in particular the image, such as forming the face photograph with sublimation transfer type ink ribbon is composed primarily of light resistance poor dye image over a long period of time to improve the light resistance It can be maintained. 紫外線吸収層21としては、バインダ中へ、ベンゾトリアゾール類、ベンゾフェノン類、置換オキザニリド類、シアノアクリレート類、又はトリアリールトリアジン類などの紫外線吸収剤を含む組成物へ、必要に応じて硬化剤、光重合開始剤、可塑剤、安定剤、界面活性剤等を加え、溶媒へ分散または溶解して、ロールコート、グラビアコート、コンマコート、ダイコートなどの公知のコーティング方法で塗布し乾燥するか、乾燥、若しくは乾燥した後のエージング(硬化)処理、又は電離放射線で反応(硬化)させればよい。 The ultraviolet absorbing layer 21, into the binder, benzotriazoles, benzophenones, substituted Okizanirido acids, cyano acrylates, or the composition containing the ultraviolet absorbent such as triaryl triazines, curing agent, if necessary, light polymerization initiator, a plasticizer, a stabilizer, a surfactant or the like added and dispersed or dissolved in a solvent, roll coating, gravure coating, comma coating, or coated and dried by a known coating method such as die coating, drying, or dry aging after (hardening) process, or it may be reacted (cured) by ionizing radiation.

(接着層)接着層19としては、公知の加熱されると溶融または軟化して接着効果を発揮する感熱接着剤が適用でき、具体的には、塩化ビニル系樹脂、酢酸ビニル系樹脂、塩化ビニル酢酸ビニル共重合樹脂、アクリル系樹脂、ポリエステル系樹脂などが挙げられる。 The (adhesive layer) The adhesive layer 19 can be applied is heat-sensitive adhesive which exhibits adhesive effect by melting or softening to be known heating, specifically, vinyl chloride resin, vinyl acetate resin, vinyl chloride vinyl acetate copolymer resin, acrylic resin, and polyester resin. 該接着層19には、マイクロシリカなどのフィラーを含むことが、箔切れ性の点で好ましい。 The adhesive layer 19, it is preferable in view of the foil cutting of including filler such as microsilica. また、接着層19の樹脂としては、95℃程度の低温で溶融接着し、60℃程度になると固化して接着する融点が60〜95℃ものが好ましい。 The resin of the adhesive layer 19, melt bonded at a low temperature of about 95 ° C., a melting point of bonding to solidify to be around 60 ° C. preferably has 60 to 95 ° C.. 融点が上記範囲未満であると、支持体との接着性が不十分であり、形成された画像を使用する温度が制限される。 When the melting point is less than the above range, adhesion to the support is insufficient, the temperatures used to form images is limited. また、融点が上記範囲を越えるとサーマルヘッドによる加熱では転写性が不十分となり、又、ハードコート層の箔切れ性が低下し、解像性の良い転写が困難となる。 The melting point transferability becomes insufficient by heating with a thermal head exceeds the above range, also reduces the foil cutting property of the hard coat layer, it is difficult to be transferred of resolution. 該材料樹脂を溶剤に溶解または分散させて、適宜顔料などの添加剤を添加して、公知のロールコーティング、グラビアコーティング、コンマコーティングなどの方法で塗布し乾燥させて、厚さ1〜30μmの層を得る。 The material resin is dissolved or dispersed in a solvent, by adding an additive such as suitable pigments, known roll coating, gravure coating, is coated and dried by a method such as comma coating, a layer having a thickness of 1~30μm obtained.

(転写)このようにして得られた本発明のハードコート層転写箔10を用いて、図2のように、ハードコート層15、紫外線吸収層21(必要に応じて)、及び接着層19を、支持体101に形成された画像105の表面へ転写する。 (Transcription) using the hard coat layer transfer foil 10 of the present invention obtained in this manner, as shown in FIG. 2, the hard coat layer 15, an ultraviolet absorbing layer 21 (if necessary), and an adhesive layer 19 It is transferred to the surface of the formed image 105 to the support 101. ハードコート層15が最表面に位置し、両者が画像を保護し耐久性を高める。 Hard coat layer 15 is positioned on the outermost surface, both enhance the durability to protect the image. 転写時には離型層13とハードコート層15との間で剥離するが、若干離型層13の1部がハードコート層15へ移行する場合もあるが、本発明の範囲内である。 Although delamination between the release layer 13 and the hard coat layer 15 at the time of transfer, but a portion of slightly releasing layer 13 is sometimes moves to the hard coat layer 15 is within the scope of the present invention.

(転写法)支持体101への形成方法としては、公知の転写法でよく、例えば、熱刻印によるホットスタンプ(箔押)、熱ロールによる全面又はストライプ転写、サーマルヘッド(感熱印画ヘッド)によるサーマルプリンタ(熱転写プリンタともいう)などの公知の方法が適用できる。 The method of forming the (transfer method) support 101 may be a known transfer method, for example, hot stamping by hot embossing (hot stamping), the entire surface or stripe transfer by heat roll, a thermal by a thermal head (thermal printing head) printer (also referred to as a thermal transfer printer) a known method such as is applicable. スポット状、文字、数字、イラストなどの任意の形状を転写してもよい。 Spots, letters, numbers, may be transferred to any shape, such as illustrations. 異なる任意の形状を連続操作できたり、オンデマンドで印画できるサーマルプリンタが好ましい。 Or you can successively operate different arbitrary shape, a thermal printer capable of printing on demand is preferred.

また、背景技術で説明したように、極めて過酷な環境での使用、長期にわたる使用期限、及び/又は多数回の繰り返し使用などでは、未だ充分な耐久性が得られていなかった。 Further, as described in the background art, the use of an extremely harsh environment, long-term expiration date, and / or the like many times repeated use, was not yet sufficient durability can not be obtained. 保護層(本発明のハードコート層)を厚くすればよいが、厚くすると箔切れが著しく悪くなるので、保護層を2回重ねて転写していた。 May be thicker protective layer (hard coat layer of the present invention), but since the foil breakage considerably deteriorated when the thickness, were transferred superimposed protective layer twice. 本発明のハードコート層転写箔10によれば、画像の保護性の高いハードコート層15を、厚さが厚くても剥離性及び箔切れ性がよく、1回で転写することができる。 According to the hard coat layer transfer foil 10 of the present invention, the protective highly hard coat layer 15 of the image, the thickness peelable and foil cutting property even thick is well, it can be transferred at once. ハードコート層15は、画像の表面に存在し、機械的化学的な損傷から長期間にわたって保護し、極めて過酷な環境で使用されるガソリンスタンドカードや工事現場カード、及び、使用期限がなかったり、長期にわたる入退室カードやポイントカード、金融機関などの多数のセキュリティ管理された部屋への入退室を繰り返す入退室カードなどにも好適に使用することができる。 The hard coat layer 15 is present on the surface of the image, and protection over a long period of time from mechanical and chemical damage, extremely harsh environment gas station card and the construction site card is used in, and, or there is no expiration date, long-term entry and exit card and point card, can also be suitably used, such as the entry and exit card to repeat the entry and exit to a large number of security management has been the room, such as financial institutions.

(支持体)支持体101としては、特に限定されず、例えば天燃繊維紙、コート紙、トレーシングペーパー、転写時の熱で変形しないプラスチックフイルム、ガラス、金属、セラミックス、木材、布あるいは染料受容性のある媒体等いずれのものでもよい。 The (support) support 101 is not particularly limited, for example, Natural fiber paper, coated paper, tracing paper, plastic film which is not deformed by the heat during transfer, glass, metal, ceramics, wood, cloth or dye receiving medium or the like with a sexually may be any one. また、支持体101の媒体はその少なくとも1部が、画像、着色、印刷、その他の加飾が施されていてもよい。 Further, the medium of the support 101 is at least 1 part, image, colored, printed, or may be other decorative is performed. なお、図2では昇華転写タイプの熱転写方法による画像で、受像層103へ形成した画像を例示しているが、受像層103の有無には限定されない。 Incidentally, in the image by the thermal transfer method of the sublimation transfer type in FIG. 2 that although the image formed to the image-receiving layer 103, the presence or absence of the image receiving layer 103 is not limited.

(画像)特に好ましい画像105としては、耐久性に劣る画像で、例えば、イエロー、マゼンダ及びシアン(更に必要に応じてブラック)の着色熱転写層を面順次に繰返し多数設けた長尺熱転写フイルムを用いる、溶融転写タイプ、昇華転写タイプの熱転写方法による画像である。 (Image) as a particularly preferred image 105 is an image inferior in durability, for example, yellow, using magenta and cyan elongate thermal transfer film provided with a number repeatedly colored thermal transfer layer sequentially face (black if necessary) is an image by the melt transfer type, sublimation transfer type thermal transfer method. 該画像は、身分証明書等のIDカードを作成する場合、溶融転写タイプの場合は、文字や数字等の如き画像の形成は容易であるが、これらの画像は耐久性、特に耐摩擦性が劣るという欠点がある。 The image, when creating the ID card identification, etc., in the case of melt transfer type, although the formation of such an image such as characters and figures is easy, these images durability, abrasion resistance is particularly there is a drawback that it is inferior. 一方、昇華転写タイプの場合には、顔写真等の階調性画像を形成することが出来るが、形成された画像は通常の印刷インキとは異なり、ビヒクルが無い為、耐光性、耐候性、耐摩擦性等の耐久性に劣るという問題がある。 On the other hand, in the case of the sublimation transfer type, although it is possible to form a gradation image such as face photograph, unlike the formed image to the usual printing inks, since the vehicle is not, light resistance, weather resistance, there is a problem of poor durability of the abrasion resistance and the like. 該画像は、本発明のハードコート層転写箔10を用いて表面へ転写することで、ハードコート層15が最表面に位置し、画像を保護し耐久性を高める。 The image, by transferring to the surface using a hard coat layer transfer foil 10 of the present invention, the hard coat layer 15 is positioned on the outermost surface, to protect the image enhancing durability.

(耐久性)ハードコート層15の鉛筆硬度試験は、JIS−K5400に準拠して測定し、H以上の硬度を有していた。 Pencil hardness test of (durability) hard coat layer 15, measured in accordance with JIS-K5400, had higher hardness H. また、ハードコート層15のスクラッチ強度は、表面の充分な耐摩擦性の点から、サファイア150g以上、好ましくは200g以上である。 Further, scratch strength of the hard coat layer 15, from the viewpoint of sufficient abrasion resistance of the surface, sapphire 150g or more, preferably 200g or more. なお、スクラッチ強度の測定方法は、23℃、55%RHの条件下で24時間調湿した試料に対して、耐摩耗性試験機(HEIDON−18)を用い、0.8mmφサファイア針を直角にあてがい、サファイア針に掛かる荷重を0gから200gまで徐々に増加させ、60cm/minで試料表面を摺動して移動させながら、表面に傷が付き始める時の荷重の測定を行った。 The method of measuring the scratch strength, 23 ° C., the sample was moistened 24 hours adjusted under the conditions of RH 55%, using the wear resistance tester (HEIDON-18), 0.8mmφ sapphire needle at a right angle Ategai, the load applied to the sapphire needle gradually increased from 0g to 200 g, while moving sliding surface of the sample at 60cm / min, it was measured load at start scratched surface. 荷重が大きいほど良好であることを表す。 Indicating that higher loading is greater the better.

以下、実施例及び比較例により、本発明を更に詳細に説明するが、これに限定されるものではない。 Hereinafter, examples and comparative examples, the present invention will be described in more detail, but is not limited thereto.

(実施例1)基材11として厚さ25μmのPETフィルムを用い、該基材11の一方の面へ、グラビアコート法で、TCM01メジューム(大日本インキ社製、メラミン樹脂商品名)塗工液を乾燥後2μmになるように塗布し乾燥して、080℃20秒間焼き付けて、離型層13を形成した。 A PET film having a thickness of 25μm (Example 1) a base 11, to one surface of the substrate 11, a gravure coating method, TCM01 Mejumu (Dainippon Ink Co., a melamine resin tradename) Coating Solution and it was applied to a dry post-2μm drying, baking 080 ° C. 20 seconds to form a release layer 13.
該離型層13面へ、下記の電離放射線硬化性樹脂組成物をグラビアリバースコーターで乾燥後の塗布厚さが5μmになるように塗工し100℃で乾燥させる工程を3回繰返して、合計15μmとしてから、高圧水銀灯を用いて紫外線を照射して硬化させて、ハードコート層15を形成した。 To the releasing layer 13 side, is repeated 3 times a process of the ionizing radiation-curable resin composition of the following coating thickness after drying at a gravure reverse coater and dried at coated such that the 5 [mu] m 100 ° C., a total of after a 15 [mu] m, and then cured by irradiation with ultraviolet rays using a high pressure mercury lamp, to form a hard coat layer 15.
・<電離放射線硬化性樹脂組成物の作製手順> - <Fabrication procedure ionizing radiation-curable resin composition>
まず、反応性生物(A)は以下の手順で、生成した。 First, reaction product (A) in the following procedures afforded. 撹拌機、還流冷却器、滴下漏斗及び温度計を取り付けた反応器に、酢酸エチル206.1g及びイソホロンジイソシアネートの三量体(HULS社製品、VESTANAT T1890、融点110℃)133.5gを仕込み、80℃に昇温して溶解させた。 A stirrer, a reflux condenser, were charged into a reactor equipped with a dropping funnel and a thermometer, trimers of ethyl acetate 206.1g and isophorone diisocyanate (HULS's products, VESTANAT T1890, mp 110 ° C.) and 133.5 g, 80 ℃ dissolved the temperature was raised to. 溶液中に空気を吹き込んだのち、ハイドロキノンモノメチルエーテル0.38g、ペンタエリスリトールトリアクリレート(大阪有機化学工業社製品、ビスコート300)249.3g及びジブチル錫ジラウレート0.38gを仕込んだ。 After air was blown into the solution, it was charged hydroquinone monomethyl ether 0.38 g, pentaerythritol triacrylate (manufactured by Osaka Organic Chemical Industry products, Viscoat 300) to 249.3g and dibutyltin dilaurate 0.38 g. 80℃で5時間反応させたのち酢酸エチル688.9gを添加して冷却した。 Ethyl acetate 688.9g After reacted for 5 hours at 80 ° C. and cooled added.
該反応生成物(A)と、ポリエチレンワックス、光重合開始剤、及び溶媒を下記の組成で配合して電離放射線硬化性樹脂組成物を調製した。 The reaction product with (A), a polyethylene wax, a photopolymerization initiator, and the solvent was compounded with the following composition was prepared an ionizing radiation curable resin composition.
・<電離放射線硬化性樹脂組成物> - <ionizing radiation-curable resin composition>
反応性生物(A) 30質量部 ポリエチレンワックス(平均粒径5μm) 0.3質量部 光重合開始剤(チバ社製、商品名イルガキュア907) 0.9質量部 溶媒(酢酸エチル:メチルイソブチルケトン=1:1) 70質量部 次に、該ハードコート層15面へ、下記の接着層組成物をグラビアコーターで乾燥後の塗布厚さが2μmになるように、塗工し100℃で乾燥させて、接着層19を形成して、実施例1のハードコート層転写箔10を得た。 Reaction product (A) 30 parts by mass Polyethylene wax (average particle size 5 [mu] m) 0.3 parts by mass Photopolymerization initiator (Ciba Corporation, trade name: Irgacure 907) 0.9 parts by weight solvent (ethyl acetate: methyl isobutyl ketone = 1: 1) 70 parts by mass Next, to said hard coat layer 15 side, an adhesive layer composition having the following as the coating thickness after drying at a gravure coater is 2 [mu] m, dried coating was 100 ° C. , to form an adhesive layer 19, to obtain a hard coat layer transfer foil 10 of the first embodiment.
・<接着層組成物> · <Adhesive layer composition>
ポリエステル樹脂P−170(日本合成化学社製、商品名) 20質量部 マイクロシリカ(平均粒子径0.5μ) 10質量部 溶媒(MEK:トルエン=1:1) 70質量部 Polyester resin P-170 (Nippon Synthetic Chemical Industry Co., Ltd., trade name) 20 parts by weight microsilica (average particle diameter 0.5 [mu]) 10 parts by weight solvent (MEK: toluene = 1: 1) 70 parts by weight

(実施例2)ハードコート層15面へ、紫外線吸収層組成物としてUVA(昭和インク工業所社製、商品名)をグラビアコーターで乾燥後の塗布厚さが4μmになるように、塗工し100℃で乾燥させ、50℃で1週間エージングして、紫外線吸収層21を形成する以外は実施例1のと同様にして、ハードコート層転写箔10を得た。 To (Example 2) the hard coat layer 15 side, UVA ultraviolet absorbing layer composition (Showa Ink Kogyosho Co., Ltd., trade name) as the coating thickness after drying at a gravure coater is 4 [mu] m, coated dried at 100 ° C., and aged for 1 week at 50 ° C., except for forming the ultraviolet absorbing layer 21 in the same manner as in example 1 to obtain a hard coat layer transfer foil 10.

(比較例1)ハードコート層15の組成物にポリエチレンワックスを用いない以外は実施例1と同様にして、ハードコート層転写箔10を得た。 Except using no polyethylene wax in the composition of (Comparative Example 1) The hard coat layer 15 in the same manner as in Example 1 to obtain a hard coat layer transfer foil 10.

(評価)評価は支持体への転写試験で行った。 (Evaluation) The evaluation was carried out in the transfer test of the support. 転写試験は、支持体101としてポリ塩化ビニール製のクレジットカード仕様のカードを用い、該支持体101の表面へ、FARGO製のカード用プリンタHDP820で、カラー昇華性インクリボンを用いて顔写真を印画した後に、同じくFARGO製のカード用プリンタHDP820で、実施例及び比較例のハードコート層転写箔10の接着層19面を重ねて熱転写し、カードへの転写状況を観察した。 Transfer tests, using a card of a credit card specifications made PVC as the support 101, to the surface of the support 101, the card printer HDP820 made FARGO, printing a facial portrait using a color sublimation ink ribbon after, also in FARGO made card printer HDP820, and thermal transfer superimposed adhesive layer 19 side of the hard coat layer transfer foil 10 of the examples and Comparative examples were observed transcription status of the card.

(評価結果)実施例1〜2では、転写時の剥離性もよく、箔切れ性もよく、正常に転写できた。 In Evaluation Results Examples 1-2, can be peeled off at the time of transfer may foil cutting property, it was transferred successfully. しかしながら、比較例1では剥離性が悪く剥離しにくく、転写時にバリが発生して正常に転写できなかった。 However, hardly peeled poor in releasability Comparative Example 1, burrs could not be transferred correctly generated at the time of transfer. また、実施例1〜2の第1ハードコート層15面の鉛筆硬度試験を、JIS−K−5400に準拠して測定したところ、2H以上の硬度を有し、さらに、実施例1〜2の第1ハードコート層15面のスクラッチ強度はサファイア200g以上であり、充分な耐久性を有していた。 Also, the pencil hardness test of the first hard coat layer 15 side of Examples 1-2, was measured in accordance with JIS-K-5400, it has a hardness of at least 2H, furthermore, of Examples 1-2 scratch strength of the first hard coat layer 15 side is at least sapphire 200 g, it had sufficient durability. しかしながら、比較例1ではスクラッチ強度が悪く、充分な耐久性を有していなかった。 However, scratch strength in Comparative Example 1 is poor, did not have sufficient durability.

本発明の1実施例を示すハードコート層転写箔の断面図である。 It is a cross-sectional view of the hard coat layer transfer foil showing an embodiment of the present invention. 本発明のハードコート層転写箔を用いて、支持体へ転写し画像を保護した状態を示す断面図である。 Using the hard coat layer transfer foil of the present invention, it is a cross-sectional view showing a transferring state of protecting the image to the support.

符号の説明 DESCRIPTION OF SYMBOLS

10:ハードコート層転写箔 11:基材 13:離型層 15:ハードコート層 19:接着層 21:紫外線吸収層 100:媒体 103:受像層 105:画像 10: hard coat layer transfer foil 11: substrate 13: release layer 15: hard coat layer 19: adhesive layer 21: UV-absorbing layer 100: medium 103: image-receiving layer 105: Image

Claims (6)

  1. 基材と、該基材の一方の面へ離型層、ハードコート層及び接着層を設けてなるハードコート層転写箔において、上記離型層がメラミン系樹脂であり、上記ハードコート層が電離放射線硬化性樹脂の硬化物及びポリエチレンワックスを含んでいることを特徴とするハードコート層転写箔。 A substrate, the release layer to one surface of the substrate, the hard coat layer transfer foil formed by providing a hard coat layer and the adhesive layer, the release layer is a melamine resin, the hard coat layer is ionized hard coat layer transfer foil characterized in that it comprises a cured product and polyethylene wax of the radiation curable resin.
  2. 上記電離放射線硬化性樹脂の硬化物が(1)分子中にイソシアネート基を3個以上有するイソシアネート類、(2)分子中に水酸基を少なくとも1個と(メタ)アクリロイルオキシ基を少なくとも2個有する多官能(メタ)アクリレート類、又は(3)分子中に水酸基を少なくとも2個有する多価アルコール類の反応生成物であるウレタン(メタ)アクリレートオリゴマーを含有する電離放射線硬化性樹脂の硬化物であることを特徴とする請求項1に記載のハードコート層転写箔。 Isocyanates having a cured product of the ionizing radiation curable resin (1) 3 or more isocyanate groups in the molecule, (2) at least one hydroxyl group in the molecule and (meth) acryloyloxy groups multi having at least two functional (meth) acrylates, or (3) a cured product of an ionizing radiation curable resin hydroxyl group containing urethane (meth) acrylate oligomer is a reaction product of polyhydric alcohols having at least two in the molecule hard coat layer transfer foil according to claim 1, wherein the.
  3. 上記ハードコート層のポリエチレンワックスの含有が質量基準で、電離放射線硬化樹脂:ポリエチレンワックス=100:0.01〜10であることを特徴とする請求項1〜2のいずれかに記載のハードコート層転写箔。 In the mass content of the polyethylene wax of the hard coat layer, an ionizing radiation curable resin: polyethylene wax = 100: hard coat layer according to any one of claims 1-2, characterized in that from 0.01 to 10 transfer foil.
  4. 上記ハードコート層の厚味が10μm以上であることを特徴とする請求項1〜3のいずれかに記載のハードコート層転写箔。 Hard coat layer transfer foil according to any one of claims 1 to 3, wherein the thickness of the hard coat layer is 10μm or more.
  5. スクラッチ強度がサファイア150g以上であることを特徴とする請求項1〜4のいずれかに記載のハードコート層転写箔。 Hard coat layer transfer foil according to claim 1, wherein the scratch strength of sapphire 150g or more.
  6. 上記ハードコート層と接着層との間に紫外線吸収層を有することを特徴とする請求項1〜4のいずれかに記載のハードコート層転写箔。 Hard coat layer transfer foil according to claim 1, characterized in that it comprises an ultraviolet absorbing layer between the hard coat layer and the adhesive layer.
JP2006179567A 2006-06-29 2006-06-29 The hard coat layer transfer foil Active JP4930764B2 (en)