JP2007303057A - Asbestos-surrounding and solidifying treatment material and asbestos-surrounding and solidifying treatment method using the same - Google Patents
Asbestos-surrounding and solidifying treatment material and asbestos-surrounding and solidifying treatment method using the same Download PDFInfo
- Publication number
- JP2007303057A JP2007303057A JP2006323617A JP2006323617A JP2007303057A JP 2007303057 A JP2007303057 A JP 2007303057A JP 2006323617 A JP2006323617 A JP 2006323617A JP 2006323617 A JP2006323617 A JP 2006323617A JP 2007303057 A JP2007303057 A JP 2007303057A
- Authority
- JP
- Japan
- Prior art keywords
- asbestos
- treatment material
- weight
- parts
- treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
この発明は、アスベスト繊維成分を含む建造物構造体などから発生するアスベスト繊維成分、岩綿あるいはセメントなどの粉塵の飛散防止にとどまらず、該アスベスト繊維を確実に包囲して強固に固化し、最終的には、大気中の炭酸ガスとの反応により経時的に石灰岩化して、無害化し、且つ、再資源化するという全く新しいテーマを包含するアスベスト包囲固化処理材およびこれを用いたアスベスト包囲固化処理工法に関するものである。 This invention is not limited to the prevention of scattering of dust such as asbestos fiber components, rock wool or cement generated from building structures containing asbestos fiber components, but securely surrounds and solidifies the asbestos fibers. In particular, asbestos-enclosed solidification processing material that includes a completely new theme of limestone, detoxification, and recycling, over time by reaction with carbon dioxide in the atmosphere, and asbestos-enclosed solidification treatment using the same It relates to the construction method.
周知のように、既存のコンクリート建造物（公共施設建造物、会社工場、学舎、駅舎など）あるいは一般家屋などでは、断熱性、耐火性あるいは吸音性建材として、石綿、岩綿、 セメントなどの粉塵性物質を含む耐火被覆材が多用されてきている。特に、従来多用されてきた石綿を含有する既設の断熱性、耐火性あるいは吸音性建材については、当該建材中の石綿が粉塵化し、飛散して人体に侵入することによる有害性が指摘され、極めて大きな問題として提起されている。 As is well known, in existing concrete buildings (public facilities buildings, company factories, school buildings, station buildings, etc.) or ordinary houses, etc., dust such as asbestos, rock wool, cement, etc. is used as a heat insulating, fire resistant or sound absorbing building material. Fire-resistant coating materials containing volatile substances have been frequently used. In particular, for existing heat insulation, fire resistance or sound absorbing building materials containing asbestos, which has been frequently used in the past, the asbestos in the building material is dusted, scattered and invaded into the human body, and extremely harmful It has been raised as a major problem.
従来、上記する問題を解決するものとして、既設の粉塵含有建材に、(1) 酢酸ビニル系エマルジョンを吹き付けて、その表面を遮蔽する方法、あるいは、(2) アクリル系合成樹脂などの水溶性高分子を吹き付けて浸透させ、粉塵を封じ込める方法などが試みられている。 Conventionally, in order to solve the above problems, existing dust-containing building materials are either (1) sprayed with a vinyl acetate emulsion to shield the surface, or (2) highly soluble in water such as an acrylic synthetic resin. Attempts have been made to spray molecules to infiltrate them and contain dust.
しかしながら、上記する従来技術において、酢酸ビニル系エマルジョンを用いる方法では、石綿含有建材の表面を遮蔽する点においては効果があるものの、内部への浸透性がないため、吹き付け層と石綿含有建材表面との間で剥離が生じるという欠点を有するものであった。内部への浸透性がないため、当該石綿含有建材を解体あるいは改修する場合に、建材内部の石綿が飛散してしまうという大きな欠点を有していた。 However, in the prior art described above, the method using a vinyl acetate emulsion is effective in shielding the surface of the asbestos-containing building material, but has no permeability to the inside, so that the spray layer and the asbestos-containing building material surface It had the disadvantage that peeling occurred between the two. Due to the lack of penetration into the interior, when the asbestos-containing building material was disassembled or repaired, the asbestos inside the building material was scattered.
一方また、上記する従来技術において、アクリル系合成樹脂などの水溶性高分子を用いる方法では、その濃度を調整して施工しても、その建材内への浸透性に限度があり、封じ込めた場合の封じ込めの耐久性が弱く、建材の粉塵化防止効果が不十分であった。さらに、その材料コストが非常に高くなるという問題点を有していた。 On the other hand, in the above-described conventional technology, in the method using a water-soluble polymer such as an acrylic synthetic resin, even if the concentration is adjusted, there is a limit to the permeability into the building material, and it is contained The durability of containment was weak, and the effect of preventing building materials from becoming dust was insufficient. Further, the material cost is very high.
そこで、この発明は、上記する従来技術における欠点並びに問題点を解消するに適したアスベスト包囲固化処理材を提供するものであり、且つ、周囲にも作業者にも極めて安全性の高いアスベスト包囲固化処理システムを提供するものである。すなわち、この発明では、特に、重大な被害をもたらすアスベスト繊維の飛散を防止し、該アスベスト繊維を確実に包囲して強固に固化し、最終的には、大気中の炭酸ガスとの反応により石灰岩化して、無害化しようとするアスベスト包囲固化処理材およびこれを用いたアスベスト包囲固化処理工法を提供するものである。 Therefore, the present invention provides an asbestos-enclosed solidification material suitable for solving the above-described drawbacks and problems in the prior art, and asbestos-enclosed solidification that is extremely safe for the surroundings and workers. A processing system is provided. That is, in the present invention, in particular, the scattering of asbestos fibers causing serious damage is prevented, the asbestos fibers are surely surrounded and firmly solidified, and finally, the reaction with the carbon dioxide in the atmosphere results in limestone. An asbestos-enclosed solidification treatment material to be rendered harmless and an asbestos-enclosed solidification treatment method using the same are provided.
さらに、この発明では、排出アスベストを最小のエネルギーで再資源化すること、並びに、当該アスベスト使用時に、建造物構造体内のアスベストをエステル結合して石灰化して、無害化しようとするアスベスト包囲固化処理工法を提供するものである。 Further, according to the present invention, exhausted asbestos is recycled with a minimum amount of energy, and when asbestos is used, asbestos in the building structure is esterified and calcified to detoxify the asbestos surrounding solidification process. The construction method is provided.
この発明は、上記する目的を達成するにあたって、請求項１に記載の発明は、アスベスト繊維を含む建造物構造体からのアスベスト繊維の飛散を防止し、前記アスベスト繊維を包囲して固化するべく、主として、金属イオンを含むアルカリ性の水溶液またはスラリー、植物性または動物性の油と、植物性または動物性の糊とを混合してなるアスベスト処理材であり、第１のアスベスト処理材と、第２のアスベスト処理材との組み合わせでなり、第１のアスベスト処理材が、前記アスベスト繊維を含む建造物構造体の表面に塗布ないしは吹き付けにより内部に浸透させ、乾燥後に有機金属化合物を形成するに適した浸透性の高い処理材からなり、第２のアスベスト処理材が、前記第１のアスベスト処理材の処理後の建造物構造体に吹き付けて、凝結固化するに適した封着性の高い処理剤からなることを特徴とするアスベスト包囲固化処理材を構成するものである。 In order to achieve the above object, the invention according to claim 1 is to prevent scattering of asbestos fibers from a building structure including asbestos fibers and to surround and solidify the asbestos fibers. An asbestos treatment material mainly comprising an alkaline aqueous solution or slurry containing metal ions, a vegetable or animal oil, and a vegetable or animal glue, a first asbestos treatment material, and a second In combination with the asbestos treatment material, the first asbestos treatment material is applied to or sprayed on the surface of the building structure containing the asbestos fibers, and is suitable for forming an organometallic compound after drying. It consists of a highly permeable treatment material, and the second asbestos treatment material is sprayed onto the building structure after treatment of the first asbestos treatment material, It constitutes a asbestos surrounding solidification material characterized by comprising a sealable high treatment agent suitable for forming solidification.
さらに、この発明において、請求項２に記載の発明は、請求項１に記載のアスベスト包囲固化処理材であって、第１のアスベスト処理材が、水１００重量部に対して、０．１〜５重量部の金属の水酸化物および／または強塩基と弱酸の金属塩と、０．１〜５重量部の植物性または動物性の油と、０．１〜１０重量部の植物性または動物性の糊とを混合してなる浸透性の高い処理剤であり、第２のアスベスト処理材が、水１００重量部に対して、５〜４０重量部の金属の水酸化物および／または強塩基と弱酸の金属塩と、０．１〜５重量部の植物性または動物性の油と、０．１〜１０重量部の植物性または動物性の糊と、０．１〜５重量部の有機または無機の繊維と、１〜３０重量部の骨材とを混合してなる封着性の高い処理材であることを特徴とするものである。
Furthermore, in this invention, invention of
さらに、この発明において、請求項３に記載の発明は、請求項１あるいは請求項２に記載のアスベスト包囲固化処理材であって、前記金属の水酸化物が、水酸化カルシウム、水酸化マグネシウム、水酸化アルミニウム、水酸化亜鉛あるいは水酸化鉄などであることを特徴とするものである。
Furthermore, in this invention, the invention according to claim 3 is the asbestos-enclosed solidification treatment material according to
さらに、この発明において、請求項４に記載の発明は、請求項１あるいは請求項２に記載のアスベスト包囲固化処理材であって、前記強塩基と弱酸の金属塩が、珪酸ナトリウム、珪酸カリウム、珪酸カルシウム、硼酸ナトリウムあるいはリン酸ナトリウムなどであることを特徴とするものである。 Furthermore, in this invention, the invention according to claim 4 is the asbestos-enclosed solidification material according to claim 1 or 2, wherein the metal salt of the strong base and the weak acid is sodium silicate, potassium silicate, It is characterized by being calcium silicate, sodium borate or sodium phosphate.
さらに、この発明において、請求項５に記載の発明は、請求項１あるいは請求項２に記載のアスベスト包囲固化処理材であって、前記植物性または動物性の油が、菜種油、ごま油、大豆油あるいはやし油などの植物性の油、または、魚油などの動物性の油であることを特徴とするものである。 Furthermore, in this invention, the invention according to claim 5 is the asbestos-enclosed solidified material according to claim 1 or 2, wherein the vegetable or animal oil is rapeseed oil, sesame oil, soybean oil. Alternatively, it is a vegetable oil such as palm oil or an animal oil such as fish oil.
さらに、この発明において、請求項６に記載の発明は、請求項１あるいは請求項２に記載のアスベスト包囲固化処理材であって、前記植物性または動物性の糊が、澱粉、銀杏あるいはつのまたなどの植物性の糊、または、ゼラチン、コラーゲンあるいはにかわなどの動物性の糊であることを特徴とするものである。
Further, in this invention, the invention according to
さらに、この発明において、請求項７に記載の発明は、請求項１〜請求項６のいずれかに記載のアスベスト包囲固化処理材であって、前記アスベスト包囲固化処理材に、合成樹脂を添加してなることを特徴とするものである。
Furthermore, in this invention, the invention according to
さらにまた、この発明において、請求項８に記載の発明は、請求項１〜請求項７のいずれかに記載のいずれかに記載のアスベスト包囲固化処理材であって、前記アスベスト包囲固化処理材に、天然ゴムあるいは合成ゴムを添加してなることを特徴とするものである。 Furthermore, in this invention, the invention according to claim 8 is the asbestos-enclosed solidified material according to any one of claims 1-7, wherein the asbestos-enclosed solidified material is the asbestos-enclosed solidified material. Further, natural rubber or synthetic rubber is added.
さらにまた、この発明において、請求項９に記載の発明は、請求項１〜請求項８のいずれかに記載のいずれかに記載のアスベスト包囲固化処理材であって、前記アスベスト包囲固化処理材に、有機または無機の繊維を混合してなることを特徴とするものでもある。 Furthermore, in this invention, the invention described in claim 9 is the asbestos-enclosed solidified material according to any one of claims 1-8, wherein the asbestos-enclosed solidified material is It is also characterized by mixing organic or inorganic fibers.
さらにまた、この発明において、請求項１０に記載の発明は、請求項９に記載のアスベスト包囲固化処理材であって、前記有機または無機の繊維が、麻、マニラ麻あるいはセルロースなどの天然繊維、レーヨン、ナイロン、ポリプロピレンあるいはアラミド繊維などの有機繊維、または、ガラス繊維あるいは炭素繊維などの無機繊維であることを特徴とするものである。 Furthermore, in this invention, the invention according to claim 10 is the asbestos-enclosed solidification material according to claim 9, wherein the organic or inorganic fiber is a natural fiber such as hemp, manila hemp or cellulose, or rayon. It is an organic fiber such as nylon, polypropylene or aramid fiber, or an inorganic fiber such as glass fiber or carbon fiber.
さらにまた、この発明において、請求項１１に記載の発明は、アスベスト繊維を含む建造物構造体からのアスベスト繊維の飛散を防止し、該アスベスト繊維を包囲して固化するためのアスベスト包囲固化処理工法であって、
主として、金属イオンを含むアルカリ性の水溶液またはスラリー、植物性または動物性の油、植物性または動物性の糊とを混合してなる浸透性の高い第１のアスベスト処理材を準備する工程と、
主として、金属イオンを含むアルカリ性の水溶液またはスラリー、植物性または動物性の油、植物性または動物性の糊、有機または無機の繊維および骨材とを混合してなる封着性の高い第２のアスベスト処理材を準備する工程と、
前記第１のアスベスト処理材を前記建造物構造体の表面に塗布ないしは吹き付けにより内部に浸透させ、乾燥後に有機金属化合物を形成する第１の処理工程と、
しかる後、石灰を主成分とする封着性の高い第２のアスベスト処理材を吹き付けて、アスベスト繊維表面にカルシウムイオンを作用させて、アスベスト繊維と強固に結合させ、大気中の炭酸ガス作用により経時的に石灰岩化する第２の処理工程とからなることを特徴とするアスベスト包囲固化処理工法を構成するものである。
Furthermore, in this invention, the invention according to claim 11 is an asbestos surrounding solidification processing method for preventing scattering of asbestos fibers from a building structure containing asbestos fibers and surrounding and solidifying the asbestos fibers. Because
A step of preparing a first asbestos treatment material having a high permeability formed by mixing mainly an alkaline aqueous solution or slurry containing metal ions, vegetable or animal oil, vegetable or animal glue;
A second highly sealing product comprising a mixture of an alkaline aqueous solution or slurry containing metal ions, vegetable or animal oil, vegetable or animal glue, organic or inorganic fibers and aggregate. Preparing asbestos treatment material;
A first treatment step in which the first asbestos treatment material is applied or sprayed on the surface of the building structure to form an organometallic compound after drying;
After that, a second asbestos treatment material having a high sealing property mainly composed of lime is sprayed to cause calcium ions to act on the surface of the asbestos fibers, thereby firmly bonding with the asbestos fibers, and by the action of carbon dioxide in the atmosphere. It comprises an asbestos-enclosed solidification treatment method characterized by comprising a second treatment step that limestones with time.
さらにまた、この発明において、請求項１２に記載の発明は、請求項１１に記載のアスベスト包囲固化処理工法であって、前記第１のアスベスト処理材が、水１００重量部に対して、０．１〜５重量部の金属の水酸化物および／または強塩基と弱酸の金属塩と、０．１〜５重量部の植物性または動物性の油と、０．１〜１０重量部の植物性または動物性の糊とを混合してなる浸透性の高い処理剤であり、
前記第２のアスベスト処理材が、水１００重量部に対して、５〜４０重量部の金属の水酸化物および／または強塩基と弱酸の金属塩と、０．１〜５重量部の植物性または動物性の油と、０．１〜１０重量部の植物性または動物性の糊と、０．１〜５重量部の有機または無機の繊維と、１〜３０重量部の骨材とを混合してなる封着性の高い処理材であることを特徴とするものである。
Furthermore, in this invention, the invention according to claim 12 is the asbestos-enclosed solidification processing method according to claim 11, wherein the first asbestos treatment material is added in an amount of 0. 0 to 100 parts by weight of water. 1 to 5 parts by weight of metal hydroxide and / or metal salt of strong base and weak acid, 0.1 to 5 parts by weight of vegetable or animal oil, and 0.1 to 10 parts by weight of vegetable Alternatively, it is a highly permeable treatment agent that is mixed with animal glue.
The second asbestos treatment material is 5 to 40 parts by weight of metal hydroxide and / or strong base and weak acid metal salt, and 0.1 to 5 parts by weight of plant based on 100 parts by weight of water. Or animal oil, 0.1 to 10 parts by weight of vegetable or animal glue, 0.1 to 5 parts by weight of organic or inorganic fiber, and 1 to 30 parts by weight of aggregate are mixed. It is characterized by being a treatment material with high sealing properties.
さらにまた、この発明において、請求項１３に記載の発明は、請求項１１あるいは請求項１２に記載のアスベスト包囲処理工法であって、前記第１の処理材による第１の処理工程が、前記第１のアスベスト処理材を、前記建造物構造体の表面に塗布する塗布処理と、前記建造物構造体の内部に注入する注入処理とを含むものからなることを特徴とするものである。 Furthermore, in this invention, the invention according to claim 13 is the asbestos surrounding treatment method according to claim 11 or claim 12, wherein the first treatment step by the first treatment material is the first treatment step. The asbestos treatment material according to claim 1 includes a coating treatment for coating the surface of the building structure and an injection treatment for injecting the asbestos treatment material into the building structure.
さらにまた、この発明において、請求項１４に記載の発明は、請求項１３に記載のアスベスト包囲処理工法であって、 前記第１の処理材による処理における前記注入処理に、アスベスト処理材注入器具を用い、該アスベスト処理材注入器具が、前記建造物構造体に対して、その表面から内部に突き刺さる複数本の注入針を備え、前記注入針を介して前記アスベスト処理材を前記建造物構造体の内部に加圧注入するものからなることを特徴とするものである。 Furthermore, in this invention, the invention according to claim 14 is the asbestos surrounding treatment method according to claim 13, wherein an asbestos treatment material injection tool is used for the injection treatment in the treatment with the first treatment material. The asbestos treatment material injection device includes a plurality of injection needles that pierce the building structure from the surface thereof, and the asbestos treatment material is supplied to the building structure through the injection needle. It consists of what is pressure-injected inside.
以上の構成になるこの発明のアスベスト包囲固化処理材によれば、主として、金属イオンを含むアルカリ性の水溶液またはスラリー、植物性または動物性の油と、植物性または動物性の糊とを混合してなり、あるいはこれに有機または無機の繊維を混合してなる第１および第２のアスベスト処理材の組み合わせにより構成し、まず、第１のアスベスト処理材を建造物構造体の表面から内部に浸透させて、乾燥後に有機金属化合物を形成し、しかる後、第２のアスベスト処理材を、前記第１のアスベスト処理材の処理後の建造物構造体に吹き付けて、凝結固化するものであり、浸透性並びに封着性に極めて優れており、該建造物構造体内にアスベスト繊維を石灰岩化して確実に且つ安全に封鎖するという点において極めて有効に作用するものといえる。 According to the asbestos-enclosed solidification material of the present invention having the above-described configuration, mainly an alkaline aqueous solution or slurry containing metal ions, vegetable or animal oil, and vegetable or animal glue are mixed. Or a combination of the first and second asbestos treatment materials obtained by mixing organic or inorganic fibers therein, and firstly infiltrate the first asbestos treatment material from the surface of the building structure to the inside. Then, an organometallic compound is formed after drying, and then the second asbestos-treated material is sprayed on the building structure after the treatment with the first asbestos-treated material to be solidified and permeable. In addition, it is extremely excellent in sealing properties, and acts extremely effectively in terms of securely and safely sealing asbestos fibers into the building structure. Obtain.
一方、この発明になるアスベスト包囲固化処理工法では、アスベスト繊維を含む建造物構造体の内部に、浸透性の高い第１のアスベスト処理材を浸透させて、乾燥後に有機金属化合物を形成し、しかる後、石灰を主成分とする封着性の高い第２のアスベスト処理材を吹き付けて、カルシウムイオンをアスベスト繊維表面に作用させて、アスベスト繊維と強固に結合させ、大気中の炭酸ガス作用により経時的に石灰岩化するようにしたものであり、周囲環境に対し、作業者に対して極めて安全であり、最終的には、石灰岩化することにより、再資源化をも可能とする点において、極めて有効に作用するものといえる。 On the other hand, in the asbestos enclosure solidification processing method according to the present invention, the first asbestos treatment material having high permeability is infiltrated into the structure of the building containing asbestos fibers, and an organometallic compound is formed after drying. After that, a second asbestos treatment material having a high sealing property mainly composed of lime is sprayed to cause calcium ions to act on the surface of the asbestos fibers so that they are firmly bonded to the asbestos fibers. Limestone, which is extremely safe for the surrounding environment, and extremely safe for workers. Finally, it can be recycled by limestone. It can be said that it works effectively.
以下、この発明になるアスベスト包囲固化処理材およびこれを用いたアスベスト包囲固化処理工法について詳細に説明する。
まず、この発明になるアスベスト包囲固化処理材の具体的な実施例によれば、当該アスベスト包囲固化処理材は、次のようなものからなっている。当該アスベスト包囲固化処理材は、主として、金属イオンを含むアルカリ性の水溶液またはスラリー、植物性または動物性の油と、植物性または動物性の糊とを混合した浸透性の高い第１のアスベスト処理材と、主として、金属イオンを含むアルカリ性の水溶液またはスラリー、植物性または動物性の油と、植物性または動物性の糊と、有機または無機の繊維と、骨材とを混合した封着性の高い第２のアスベスト処理材との組み合わせからなっている。
Hereinafter, the asbestos-enclosed solidification treatment material and the asbestos-enclosed solidification treatment method using the same will be described in detail.
First, according to the specific Example of the asbestos enclosure solidification processing material which becomes this invention, the said asbestos enclosure solidification processing material consists of the following. The asbestos-enclosed solidification treatment material is mainly a first asbestos treatment material having a high permeability obtained by mixing an alkaline aqueous solution or slurry containing metal ions, vegetable or animal oil, and vegetable or animal glue. And, mainly, an alkaline aqueous solution or slurry containing metal ions, vegetable or animal oil, vegetable or animal glue, organic or inorganic fiber, and aggregate are highly sealed. It consists of a combination with a second asbestos treatment material.
この第１のアスベスト処理材は、浸透性の高い溶液からなっているので、アスベスト繊維を含む建造物構造体の表面に塗布、吹き付けあるいは注入することにより、次第に建造物構造体内部に浸透していき、乾燥後に有機金属化合物を形成する。第２のアスベスト処理材は、石灰を主成分とする封着性の高い溶液からなっているので、第１のアスベスト処理材の処理後の建造物構造体に吹き付けることにより、カルシウムイオンをアスベスト繊維表面に作用させて、アスベスト繊維と強固に結合させ、大気中の炭酸ガス作用により経時的に石灰岩化する。 Since this first asbestos treatment material is made of a highly permeable solution, it gradually penetrates into the building structure by applying, spraying or injecting it onto the surface of the building structure containing asbestos fibers. Then, after drying, an organometallic compound is formed. Since the 2nd asbestos processing material consists of a highly sealing solution which has lime as a main component, it sprays on the building structure after processing of the 1st asbestos processing material, and calcium ion is asbestos fiber. It is made to act on the surface and is firmly bonded to asbestos fibers, and limestone is formed over time by the action of carbon dioxide in the atmosphere.
この発明において、金属イオンを含むアルカリ性の水溶液またはスラリーは、金属の水酸化物および／または強塩基と弱酸の金属塩によるものであり、前記金属の水酸化物としては、水酸化カルシウム、水酸化マグネシウム、水酸化アルミニウム、水酸化亜鉛あるいは水酸化鉄などが有効であり、前記強塩基と弱酸の金属塩としては、珪酸ナトリウム、珪酸カリウム、珪酸カルシウム、硼酸ナトリウムあるいはリン酸ナトリウムなどが有効である。 In the present invention, the alkaline aqueous solution or slurry containing metal ions is based on a metal hydroxide and / or a metal salt of a strong base and a weak acid, and examples of the metal hydroxide include calcium hydroxide and hydroxide. Magnesium, aluminum hydroxide, zinc hydroxide or iron hydroxide is effective, and as the metal salt of the strong base and weak acid, sodium silicate, potassium silicate, calcium silicate, sodium borate or sodium phosphate is effective. .
一方、この発明において、前記植物性または動物性の油としては、菜種油、ごま油、大豆油、やし油などの植物性の油、または、魚油などの動物性の油が有効であり、前記植物性または動物性の糊としては、澱粉、銀杏、つのまたなどの植物性の糊、または、ゼラチン、コラーゲン、にかわなどの動物性の糊が有効であり、前記有機または無機の繊維としては、麻、マニラ麻、セルロースなどの天然繊維、レーヨン、ナイロン、ポリプロピレン、アラミド繊維などの有機繊維、または、ガラス繊維、炭素繊維などの無機繊維が有効である。 On the other hand, in the present invention, as the vegetable or animal oil, vegetable oils such as rapeseed oil, sesame oil, soybean oil, and palm oil, or animal oils such as fish oil are effective. As the organic or animal glue, a vegetable glue such as starch, ginkgo, or vine, or an animal glue such as gelatin, collagen or glue is effective. As the organic or inorganic fiber, hemp Natural fibers such as manila hemp and cellulose, organic fibers such as rayon, nylon, polypropylene, and aramid fibers, or inorganic fibers such as glass fibers and carbon fibers are effective.
さらに、この発明においては、上記する構成により得られるアスベスト包囲固化処理材に対して、適量の合成樹脂を添加したものであってもよいし、あるいは、さらに、微量の天然ゴムあるいは合成ゴムを添加したものであってもよい。 Furthermore, in the present invention, an appropriate amount of synthetic resin may be added to the asbestos-enclosed solidified material obtained by the above-described configuration, or a small amount of natural rubber or synthetic rubber may be added. It may be what you did.
前記合成樹脂としては、例えば、酢酸ビニル、エチレン−酢酸ビニル共重合体などが有効であり、合成ゴムとしては、スチレンブタジエンゴムなどが有効である。 As the synthetic resin, for example, vinyl acetate, ethylene-vinyl acetate copolymer and the like are effective, and as the synthetic rubber, styrene butadiene rubber and the like are effective.
前記第２のアスベスト処理材には骨材が混入される。この骨材としては、例えば、パーライト、シラスバルーン、ビーズ発泡スチロールなどが有効である。 Aggregate is mixed into the second asbestos treatment material. As this aggregate, for example, pearlite, shirasu balloon, and polystyrene foam are effective.
この発明になるアスベスト包囲固化処理材の具体的な実施例において、当該アスベスト包囲固化処理材材は、以下に示す成分からなっている。第１のアスベスト処理材は、 水１００重量部に対して、
０．１〜５重量部の金属の水酸化物および／または強塩基と弱酸の金属塩
０．１〜５重量部の植物性または動物性の油
０．１〜１０重量部の植物性または動物性の糊とを混合してなる浸透性の高い処理剤としたものである。他方、第２のアスベスト処理材は、
水１００重量部に対して、
５〜４０重量部の金属の水酸化物および／または強塩基と弱酸の金属塩
０．１〜５重量部の植物性または動物性の油
０．１〜１０重量部の植物性または動物性の糊
０．１〜５重量部の有機または無機の繊維
１〜３０重量部の骨材とを混合してなる封着性の高い処理剤としたものである。
あるいは、この構成のものに、微量の合成樹脂、界面活性剤並びに天然ゴム、合成ゴムなどを添加したものであってもよい。
In the specific example of the asbestos-enclosed solidified material according to the present invention, the asbestos-enclosed solidified material comprises the following components. The first asbestos treatment material is 100 parts by weight of water,
0.1 to 5 parts by weight of metal hydroxide and / or metal salt of strong base and weak acid 0.1 to 5 parts by weight of vegetable or animal oil 0.1 to 10 parts by weight of vegetable or animal It is made into the processing agent with the high permeability formed by mixing the adhesive paste. On the other hand, the second asbestos treatment material is
For 100 parts by weight of water,
5 to 40 parts by weight of metal hydroxide and / or metal salt of strong base and weak acid 0.1 to 5 parts by weight of vegetable or animal oil 0.1 to 10 parts by weight of vegetable or animal It is a processing agent having a high sealing property obtained by mixing 0.1 to 5 parts by weight of an organic or inorganic fiber and 1 to 30 parts by weight of an aggregate.
Alternatively, a material obtained by adding a small amount of a synthetic resin, a surfactant, natural rubber, synthetic rubber, or the like to this structure may be used.
上記する構成成分において、前記金属の水酸化物または／および強塩基と弱酸の金属塩に関して、前記第１のアスベスト処理材では、これが、０．１重量部以下である場合には、濃度が薄すぎて機能せず、５重量部以上である場合には、浸透性が落ちるため好ましくなかった。一方、前記第２のアスベスト処理材では、これが、５重量部以下である場合には、形成される有機金属化合物が少なすぎ、被膜が薄くなってしまい、粉塵封鎖に効果がない。一方、これが４０重量部以上の場合には、混合物液体の粘度が高くなりすぎて、吹き付けなどにおいて問題があった。 In the constituents described above, regarding the metal hydroxide or / and the metal salt of a strong base and a weak acid, in the first asbestos-treated material, when this is 0.1 part by weight or less, the concentration is low. If it is too much and does not function, and the amount is 5 parts by weight or more, the permeability is not preferable. On the other hand, when the amount of the second asbestos treatment material is 5 parts by weight or less, the amount of the organometallic compound formed is too small, the coating becomes thin, and there is no effect on dust sealing. On the other hand, when the amount is 40 parts by weight or more, the viscosity of the mixture liquid becomes too high, which causes a problem in spraying.
さらに、上記する構成成分において、前記植物性または動物性の油に関して、これが０．１重量部以下である場合には、形成される有機金属化合物が少なすぎて粉塵を封鎖できない。一方、これが５重量部以上の場合には、反応に寄与しない油が流出することにより逆に封鎖の妨げになる。 Furthermore, in the above-described constituent components, when the amount of the vegetable or animal oil is 0.1 parts by weight or less, the amount of the organometallic compound formed is too small to block dust. On the other hand, when the amount is 5 parts by weight or more, oil that does not contribute to the reaction flows out, which hinders blocking.
さらにまた、上記する構成成分において、前記植物性または動物性の糊に関して、これが０．１重量部以下である場合には、封鎖状態を長期間にわたり固定できない。一方、これが１０重量部以上の場合には、粘度が高くなりすぎて建造物構造体内に充分に浸透できない。 Furthermore, in the constituents described above, when the vegetable or animal glue is 0.1 parts by weight or less, the blocked state cannot be fixed for a long period of time. On the other hand, when the amount is 10 parts by weight or more, the viscosity becomes too high to sufficiently penetrate into the building structure.
さらにまた、上記する構成成分において、前記有機または無機の繊維の混合量に関しては、当該有機または無機の繊維を混合しない第１のアスベスト処理材の場合、建造物構造体内への浸透性を高める効果を奏し、当該有機または無機の繊維を混合した第２のアスベスト処理材の場合、建造物構造体内での粉塵の封着性を高める効果を奏する。 Furthermore, in the component described above, with respect to the mixing amount of the organic or inorganic fiber, in the case of the first asbestos treatment material that does not mix the organic or inorganic fiber, the effect of increasing the permeability into the structure of the building. In the case of the 2nd asbestos processing material which mixed the said organic or inorganic fiber, there exists an effect which improves the sealing property of the dust in a building structure.
以下、この発明になるアスベスト包囲固化処理材の具体的な実施例である〔実施例１〕、〔実施例２〕および〔実施例３〕と、特許文献１に記載の発明に係る石綿飛散防止処理剤（主として、アクリル樹脂エマルジョンを成分とするもの）である〔比較例１〕および〔比較例２〕とを表１において比較して示す。 Hereinafter, [Example 1], [Example 2] and [Example 3], which are specific examples of the asbestos-enclosed solidification treatment material according to the present invention, and asbestos scattering prevention according to the invention described in Patent Document 1 [Comparative Example 1] and [Comparative Example 2], which are treatment agents (mainly containing an acrylic resin emulsion as a component), are shown in Table 1 for comparison.
上記表１からも明らかなように、この発明になる〔実施例１〕、〔実施例２〕および〔実施例３〕に挙げるアスベスト包囲固化処理材は、いずれも、浸透性並びに封鎖性が最良であるのに対し、主として、アクリル樹脂エマルジョンを成分とする〔比較例１〕および〔比較例２〕のものは、〔比較例１〕のものにおいて、浸透性が良であるに過ぎず、封鎖性は不良であり、〔比較例２〕のものにおいては、浸透性並びに封鎖性の双方が不良であった。 As is clear from Table 1 above, the asbestos-enclosed solidified materials listed in [Example 1], [Example 2] and [Example 3] according to the present invention all have the best permeability and sealing property. On the other hand, those of [Comparative Example 1] and [Comparative Example 2] mainly composed of an acrylic resin emulsion are only good in permeability in [Comparative Example 1], and are blocked. The properties of [Comparative Example 2] were poor in both permeability and blocking properties.
次いで、この発明になるアスベスト包囲固化処理材を用いたアスベスト包囲固化処理システムについて、その手順にそって詳細に説明する。
この発明では、上記する構成になる第１および第２のアスベスト処理材が予め準備される。一例において、前記第１のアスベスト処理材は、主として、金属イオンを含むアルカリ性の水溶液またはスラリー、植物性または動物性の油と、植物性または動物性の糊とを混合してなる浸透性の高いアスベスト処理材であり、前記第２のアスベスト処理材は、主として、金属イオンを含むアルカリ性の水溶液またはスラリー、植物性または動物性の油と、植物性または動物性の糊と、有機または無機の繊維とを混合してなる封着性の高いアスベスト処理材である。この発明になるアスベスト包囲固化処理システムでは、前記第１のアスベスト処理材を建造物構造体に吹き付けることによって、当該第１のアスベスト処理材を建造物構造体内に充分浸透させ、しかる後に、前記第２のアスベスト処理材を吹き付けることによって、当該第２のアスベスト処理材により建造物構造体内のアスベスト繊維を強固に封着する。
Next, the asbestos-enclosed solidification processing system using the asbestos-enclosed solidified treatment material according to the present invention will be described in detail along the procedure.
In this invention, the 1st and 2nd asbestos processing material which becomes the above-mentioned structure is prepared previously. In one example, the first asbestos-treated material is a highly permeable product mainly formed by mixing an alkaline aqueous solution or slurry containing metal ions, vegetable or animal oil, and vegetable or animal glue. It is an asbestos treatment material, and the second asbestos treatment material is mainly composed of an alkaline aqueous solution or slurry containing metal ions, vegetable or animal oil, vegetable or animal glue, and organic or inorganic fibers. Is an asbestos treatment material having a high sealing property. In the asbestos surrounding solidification processing system according to the present invention, the first asbestos treatment material is sufficiently permeated into the building structure by spraying the first asbestos treatment material onto the building structure. By spraying the second asbestos treatment material, the asbestos fibers in the building structure are firmly sealed by the second asbestos treatment material.
この発明において、アスベスト繊維を含む建造物構造体に対するアスベスト包囲固化処理材の反応の様子を図１に基づいて説明する。図１Ａは、該アスベスト包囲固化処理材による処理をする前のアスベスト繊維を含む建造物構造体内部の様子を示すものであり、セメント、ロックウール、アスベスト繊維が混在しており、経時的には、特に、アスベスト繊維が遊離している状態にあり、当該アスベスト繊維の飛散が生じるような状態となっている。 In this invention, the state of the reaction of the asbestos-enclosed solidifying material with respect to the building structure containing asbestos fibers will be described with reference to FIG. FIG. 1A shows the inside of a building structure including asbestos fibers before being treated with the asbestos-enclosed solidification treatment material, and cement, rock wool, and asbestos fibers are mixed. In particular, the asbestos fibers are in a free state, and the asbestos fibers are scattered.
図１Ｂは、図１Ａに示す状態にある建造物構造体に対して、この発明になる第１のアスベスト処理材を、例えば、塗布により処理した状態を示すものである。この場合、前記第１のアスベスト処理材は、浸透性が高いことから、建造物構造体の内部に浸透していく。さらに、この第１のアスベスト処理材は、カルシウムイオン、並びに、植物油などを含有しているため、乾燥するとともに、有機金属化合物を形成し、アスベスト繊維の封鎖の効果を高めるのに貢献する。 FIG. 1B shows a state in which the first asbestos treatment material according to the present invention is treated by, for example, coating the building structure in the state shown in FIG. 1A. In this case, since the first asbestos treatment material has high permeability, the first asbestos treatment material penetrates into the building structure. Furthermore, since the first asbestos treatment material contains calcium ions, vegetable oil, and the like, the first asbestos treatment material is dried and forms an organometallic compound, which contributes to enhancing the effect of blocking asbestos fibers.
しかる後、この発明になる第２のアスベスト処理材を、建造物構造体の表面に吹き付ける。この段階で、第２のアスベスト処理材におけるカルシウムイオンが、アスベスト繊維表面に作用して、アスベスト繊維と強固に結合させる（図１Ｃ参照）。 Thereafter, the second asbestos treatment material according to the present invention is sprayed on the surface of the building structure. At this stage, calcium ions in the second asbestos treatment material act on the surface of the asbestos fibers and are firmly bonded to the asbestos fibers (see FIG. 1C).
上記するように処理することによって、アスベスト繊維は、図１Ｄに示すように、石灰に包み込まれた形で凝結し、経時的には、大気中の炭酸ガスを取り込んで、最終的には石灰岩化し、無害化する。この状態で、当該建造物構造体を解体したとしても、無害化されていることから、当該解体作業は極めて安全であり、尚かつ、解体後、排出されたものを再資源化することもできる。 By treating as described above, asbestos fibers are condensed in the form of being encapsulated in lime as shown in FIG. 1D, and over time, carbon dioxide in the atmosphere is taken in and finally limestone is formed. , Detoxify. Even if the building structure is dismantled in this state, it is detoxified, so the dismantling operation is extremely safe, and after the dismantling, the discharged materials can be recycled. .
図２は、この発明になるアスベスト包囲固化処理材を用いたアスベスト包囲固化処理の施工手順をフローチャート化した図である。以下、このフローチャート図に基づいて説明する。このアスベスト包囲固化処理のための準備作業としては、アスベスト構造体の吹き付け厚を計測する事前調査、周辺環境の設備・備品・壁・床・天井などの作業前清掃、アスベスト包囲固化処理に必要な諸機器の設置などが行われる。この準備作業段階で、作業前の粉塵濃度測定がなされる。 FIG. 2 is a flowchart showing the construction procedure of asbestos surrounding solidification processing using the asbestos surrounding solidification processing material according to the present invention. Hereinafter, description will be given based on this flowchart. As preparatory work for this asbestos enclosure solidification treatment, it is necessary to conduct preliminary surveys to measure the spray thickness of the asbestos structure, clean the surrounding environment equipment, fixtures, walls, floors, ceilings, etc., and asbestos enclosure solidification treatment. Various devices are installed. In this preparatory work stage, the dust concentration before work is measured.
この発明になる第１のアスベスト処理材の塗布作業としては、まず、第１のアスベスト処理材の試験吹きが行われ、飛散防止処理を介在して、第１のアスベスト処理材の吹き付け処理が行われ、浸透チェックが行われる。この段階で、作業中の粉塵濃度測定がなされる。この第１のアスベスト処理材の処理に関しては、後述するアスベスト処理材注入器具１を用いて、前記第１のアスベスト処理材を施工すべき建造物構造体内に圧入するものであってもよい。この第１のアスベスト処理材塗布作業段階において、Ｚ形アンカー取り付け、剥落防止メッシュ取り付けが行われる。 In the first asbestos treatment material coating operation according to the present invention, first, the first asbestos treatment material is subjected to test spraying, and the first asbestos treatment material is sprayed through the scattering prevention treatment. A penetration check is performed. At this stage, the dust concentration during work is measured. As for the treatment of the first asbestos treatment material, the first asbestos treatment material injection tool 1 described later may be used to press-fit the first asbestos treatment material into the building structure to be constructed. In this first asbestos treatment material application work stage, Z-shaped anchor attachment and peeling prevention mesh attachment are performed.
次いで、第２のアスベスト処理材の塗布作業としては、まず、第２のアスベスト処理材並びに第２のアスベスト処理のための機材が準備される。その後、第２のアスベスト処理材の試験吹きが行われ、第２のアスベスト処理材の吹き付け処理が行われる。 Next, as the application work of the second asbestos treatment material, first, the second asbestos treatment material and the equipment for the second asbestos treatment are prepared. Then, the test blow of the 2nd asbestos processing material is performed, and the spraying process of the 2nd asbestos processing material is performed.
最終的に、検査・片付け作業がなされる。この段階では、アスベスト包囲固化処理の検査・確認がなされ、諸機材の片付け作業が行われる。この検査・片付け作業中に、作業後の粉塵濃度測定がなされる。 Finally, inspection and tidying work is done. At this stage, inspection and confirmation of the asbestos sieving and solidification process are carried out, and the equipment is cleaned up. During this inspection and tidying work, the dust concentration after the work is measured.
図３は、この発明になる第１のアスベスト処理材を建造物構造体内に圧入するためのアスベスト処理材注入器具１の具体的な実施例を示すものである。このアスベスト処理材注入器具１は、前記建造物構造体Ｓに対して、その表面から内部に突き刺さる複数本の注入針２を備え、前記注入針２を介して第１のアスベスト処理材を建造物構造体Ｓの内部に加圧注入するものからなっている。図３に示す例のものでは、基板３に対して複数の注入針２が固定されていて、前記各注入針２の一端２ａには、第１のアスベスト処理材源４からの第１のアスベスト処理材を受け入れる受入口５が設けてあり、他端２ｂには、第１のアスベスト処理材を吐出する吐出口６が設けてある。
FIG. 3 shows a specific embodiment of the asbestos treatment material injection device 1 for press-fitting the first asbestos treatment material according to the present invention into a building structure. This asbestos treatment material injection device 1 includes a plurality of injection needles 2 that pierce the building structure S from the surface to the inside, and the first asbestos treatment material is built through the injection needles 2. It consists of what is pressurized and injected into the structure S. In the example shown in FIG. 3, a plurality of injection needles 2 are fixed to the substrate 3, and the first asbestos from the first asbestos treatment material source 4 is attached to one
前記基板３の一方の面側３ａには、例えば、コイルスプリング７などにより、拡張方向に付勢された可動プレート８が進退自在に組み合わされており、当該基板３の他方の面側３ｂには、ハンドル９が取り付けられている。このハンドル９は、必要に応じてポール状の部材によって構成したものであってもよい。
On one surface side 3a of the substrate 3, for example, a movable plate 8 urged in the expansion direction by a
Ｓ 建造物構造体
１ アスベスト処理材注入器具
２ 注入針
２ａ 注入針の一端
２ｂ 注入針の他端
３ 基板
４ 第１のアスベスト処理材源
５ 注入針の受入口
６ 注入針の吐出口
７ コイルスプリング
８ 可動プレート
９ ハンドル
S Building Structure 1 Asbestos Treatment
Claims (14)
前記第１のアスベスト処理材が、前記アスベスト繊維を含む建造物構造体の表面に塗布ないしは吹き付けにより内部に浸透させ、乾燥後に有機金属化合物を形成するに適した浸透性の高い処理材からなり、
前記第２のアスベスト処理材が、前記第１のアスベスト処理材の処理後の建造物構造体に吹き付けて、凝結固化するに適した封着性の高い処理剤からなることを特徴とするアスベスト包囲固化処理材。 In order to prevent scattering of asbestos fibers from the building structure containing asbestos fibers and to surround and solidify the asbestos fibers, mainly an alkaline aqueous solution or slurry containing metal ions, vegetable or animal oils, and It is an asbestos treatment material formed by mixing vegetable or animal glue, and consists of a combination of a first asbestos treatment material and a second asbestos treatment material,
The first asbestos treatment material is made of a highly permeable treatment material suitable for forming an organometallic compound after drying by allowing the first asbestos treatment material to penetrate into the surface of the building structure containing the asbestos fibers by spraying or spraying.
The asbestos enclosure characterized in that the second asbestos treatment material is made of a treatment agent having a high sealing property suitable for spraying and solidifying the building structure after the treatment with the first asbestos treatment material. Solidified material.
前記第２のアスベスト処理材が、水１００重量部に対して、５〜４０重量部の金属の水酸化物および／または強塩基と弱酸の金属塩と、０．１〜５重量部の植物性または動物性の油と、０．１〜１０重量部の植物性または動物性の糊と、０．１〜５重量部の有機または無機の繊維と、１〜３０重量部の骨材とを混合してなる封着性の高い処理材であることを特徴とする請求項１に記載のアスベスト包囲固化処理材。 The first asbestos treatment material is 0.1 to 5 parts by weight of metal hydroxide and / or strong base and weak acid metal salt, and 0.1 to 5 parts by weight of 100 parts by weight of water. A highly permeable treatment agent comprising a mixture of vegetable or animal oil and 0.1 to 10 parts by weight of vegetable or animal glue,
The second asbestos treatment material is 5 to 40 parts by weight of metal hydroxide and / or strong base and weak acid metal salt, and 0.1 to 5 parts by weight of plant based on 100 parts by weight of water. Or animal oil, 0.1 to 10 parts by weight of vegetable or animal glue, 0.1 to 5 parts by weight of organic or inorganic fiber, and 1 to 30 parts by weight of aggregate are mixed. The asbestos-enclosed solidification treatment material according to claim 1, wherein the treatment material has high sealing properties.
主として、金属イオンを含むアルカリ性の水溶液またはスラリー、植物性または動物性の油、植物性または動物性の糊とを混合してなる浸透性の高い第１のアスベスト処理材を準備する工程と、
主として、金属イオンを含むアルカリ性の水溶液またはスラリー、植物性または動物性の油、植物性または動物性の糊、有機または無機の繊維および骨材とを混合してなる封着性の高い第２のアスベスト処理材を準備する工程と、
前記第１のアスベスト処理材を前記建造物構造体の表面に塗布ないしは吹き付けにより内部に浸透させ、乾燥後に有機金属化合物を形成する第１の処理工程と、
しかる後、石灰を主成分とする封着性の高い第２のアスベスト処理材を吹き付けて、アスベスト繊維表面にカルシウムイオンを作用させて、アスベスト繊維と強固に結合させ、大気中の炭酸ガス作用により経時的に石灰岩化する第２の処理工程とからなることを特徴とするアスベスト包囲固化処理工法。 Asbestos surrounding solidification processing method for preventing scattering of asbestos fibers from a building structure containing asbestos fibers and surrounding and solidifying the asbestos fibers,
A step of preparing a first asbestos treatment material having a high permeability formed by mixing mainly an alkaline aqueous solution or slurry containing metal ions, vegetable or animal oil, vegetable or animal glue;
A second highly sealing product comprising a mixture of an alkaline aqueous solution or slurry containing metal ions, vegetable or animal oil, vegetable or animal glue, organic or inorganic fibers and aggregate. Preparing asbestos treatment material;
A first treatment step in which the first asbestos treatment material is applied or sprayed on the surface of the building structure to form an organometallic compound after drying;
After that, a second asbestos treatment material having a high sealing property mainly composed of lime is sprayed to cause calcium ions to act on the surface of the asbestos fibers, thereby firmly bonding with the asbestos fibers, and by the action of carbon dioxide in the atmosphere. An asbestos-enclosed solidification processing method characterized by comprising a second processing step that limestones over time.
前記第２のアスベスト処理材が、水１００重量部に対して、５〜４０重量部の金属の水酸化物および／または強塩基と弱酸の金属塩と、０．１〜５重量部の植物性または動物性の油と、０．１〜１０重量部の植物性または動物性の糊と、０．１〜５重量部の有機または無機の繊維と、１〜３０重量部の骨材とを混合してなる封着性の高い処理材であることを特徴とする請求項１１に記載のアスベスト包囲固化処理工法。 The first asbestos treatment material is 0.1 to 5 parts by weight of metal hydroxide and / or strong base and weak acid metal salt, and 0.1 to 5 parts by weight of 100 parts by weight of water. A highly permeable treatment agent comprising a mixture of vegetable or animal oil and 0.1 to 10 parts by weight of vegetable or animal glue,
The second asbestos treatment material is 5 to 40 parts by weight of metal hydroxide and / or strong base and weak acid metal salt, and 0.1 to 5 parts by weight of plant based on 100 parts by weight of water. Or animal oil, 0.1 to 10 parts by weight of vegetable or animal glue, 0.1 to 5 parts by weight of organic or inorganic fiber, and 1 to 30 parts by weight of aggregate are mixed. The asbestos-enclosed solidification processing method according to claim 11, wherein the asbestos-enclosed solidification processing method is a processing material having high sealing properties.