JP2007262614A - Paper for carrier tape and carrier tape - Google Patents
Paper for carrier tape and carrier tape Download PDFInfo
- Publication number
- JP2007262614A JP2007262614A JP2006089488A JP2006089488A JP2007262614A JP 2007262614 A JP2007262614 A JP 2007262614A JP 2006089488 A JP2006089488 A JP 2006089488A JP 2006089488 A JP2006089488 A JP 2006089488A JP 2007262614 A JP2007262614 A JP 2007262614A
- Authority
- JP
- Japan
- Prior art keywords
- paper
- carrier tape
- layer
- pulp
- stiffness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、電子回路を製造する際に使用する、チップ状の表面実装電子部品を収納し、表面実装機(マウンター)に搬送するためのキャリアテープおよびこれに用いるキャリアテープ用紙に関する。 The present invention relates to a carrier tape for storing chip-shaped surface-mounted electronic components and transporting them to a surface-mounting machine (mounter) and a carrier tape sheet used therefor, which are used when manufacturing an electronic circuit.
電子機器の自動生産を行うにあたっては、表面実装タイプの電子部品を表面実装機により基板に自動装着する技術が用いられる。表面実装機に対して電子部品を供給するためには、電子部品収納用のキャビティ部と表面実装機内への送り用のマージナル部とを備える幅6〜9mm、基紙厚0.4〜1.0mmのキャリアテープが用いられている。特に一般的には幅8mm、厚さが0.7〜1.0mmのものがよく用いられる。
このキャリアテープは、紙製およびプラスチック製のものがあるが、コスト安であり、軽量であり、廃棄容易であり、非帯電性であることから紙製とするのが望ましいとされている。
キャリアテープの具体的な形態としては、部品収納用のキャビティ部とキャリアテープ送り用のマージナル部とが貫通孔であり、表面実装部品を収納した状態で、表面がトップカバーテープでシールされ、下面がボトムテープによりシールされるパンチキャリアテープや、キャビティ部がエンボス加工により形成された凹部であり、表面のみがトップカバーテープでシールされるエンボスキャリアテープや、表面実装部品の挿入直前にこれらキャビティ部等を形成するアンパンチキャリアテープなどが知られる。
これらのキャリアテープはキャビティ部に電子部品が装填されトップカバーテープでシールされた状態で、直径5cm程度のカセットリールに捲きつられた状態(レコード巻方式)、あるいは直径20cm程度巾10cm程度の紙管にスパイラル状に捲きつられた状態(トラバース巻)で出荷され、最終ユーザーが表面実装機に装着して使用される。
近年では、レコード巻方式と比較して1巻当りの巻長さを長くすることができるために継ぎ手作業が軽減され、電子部品装填工程の高速化及び作業効率向上のメリットがあるトラバース巻方式が多用されるようになっている。
There are paper and plastic carrier tapes. However, it is desirable that the carrier tape be made of paper because of its low cost, light weight, easy disposal, and non-charging properties.
As a specific form of the carrier tape, the cavity for storing the parts and the marginal part for feeding the carrier tape are through holes, and the surface is sealed with the top cover tape in a state where the surface mount parts are stored, and the bottom surface. Is a punch carrier tape that is sealed with a bottom tape, or an embossed carrier tape whose cavity part is formed by embossing and whose surface is sealed with a top cover tape. An unpunched carrier tape or the like is known.
These carrier tapes are loaded with electronic parts in the cavity and sealed with a top cover tape, and are wound around a cassette reel having a diameter of about 5 cm (record winding method), or a paper tube having a diameter of about 20 cm and a width of about 10 cm. It is shipped in a state of being wound in a spiral shape (traverse winding), and used by the end user by mounting it on a surface mounter.
In recent years, the traverse winding method has the advantages of reducing the joint work because the winding length per turn can be increased compared to the record winding method, speeding up the electronic component loading process, and improving work efficiency. It has come to be used frequently.
しかしながら、従来キャリアテープは、カセットリール等に捲き付ける際に、リールあるいは管の外周面に沿って湾曲せずに折れてしまうことがあった。
折れの現象は一般的に用いられる紙厚が700μm以上のもので顕著となり、またカセットリール径が5〜6cmと小径の場合に顕著となる。そして、このように折れが生ずると、その折れ部分の表面に凸部が発現し、この凸部が次工程の表面実装機のガイド部分に引っ掛かって部品を表面実装機内に安定して装填することができない。また、表面実装機では、トップシールを一定張力で引張しつつキャリアテープから剥離してキャビティ内の電子部品を取り出すが、キャリアテープが折れるとその折れ部分でキャリアテープからトップカバーシールが剥離して浮いてしまう。そうすると、表面実装機がトップカバーシールを一定張力で引張することができず、表面実装機に引っ張られるキャリアテープがばたつきキャビティ内の電子部品の脱落や所望位置への装填ができなくなる。
そこで、本発明の解決課題は、厚さ700μm以上の多層抄き板紙を効率良く生産することができ、かつ、リール捲き付け時あるいは捲き付け状態において、折れの発生が防止されたキャリアテープおよびキャリアテープ用紙を提供することにある。
However, when a conventional carrier tape is rubbed against a cassette reel or the like, the carrier tape may be bent without being bent along the outer peripheral surface of the reel or tube.
The phenomenon of folding becomes significant when the generally used paper thickness is 700 μm or more, and becomes remarkable when the cassette reel diameter is as small as 5 to 6 cm. And when a fold occurs in this way, a convex portion appears on the surface of the fold portion, and this convex portion is hooked on the guide portion of the surface mounting machine in the next process to stably load the component into the surface mounting machine. I can't. In surface mounters, the top seal is pulled from the carrier tape while pulling it at a constant tension, and the electronic components inside the cavity are taken out. However, when the carrier tape is broken, the top cover seal is peeled from the carrier tape at the folded portion. It will float. Then, the surface mounter cannot pull the top cover seal with a constant tension, and the carrier tape pulled by the surface mounter flutters, so that the electronic components in the cavity cannot be dropped off or loaded at a desired position.
SUMMARY OF THE INVENTION Accordingly, a problem to be solved by the present invention is that a carrier tape and a carrier capable of efficiently producing a multilayer paperboard having a thickness of 700 μm or more, and preventing the occurrence of folds at the time of reel winding or in the winding state. To provide tape paper.
上記課題を解決した本発明は次記のとおりである。
<請求項1記載の発明>
巻取りの外面となる表面層と、巻取りの内面となる裏面層と、それらの間の中間層を有する多層抄きのキャリアテープ用紙であって、
紙厚が700〜1200μmであり、
裏面側から表面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさに対する、表面側から裏面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさの比率が、80〜90%である、ことを特徴とするキャリアテープ用紙。
The present invention that has solved the above problems is as follows.
<Invention of Claim 1>
A multi-layered carrier tape paper having a surface layer as an outer surface of winding, a back layer as an inner surface of winding, and an intermediate layer therebetween,
The paper thickness is 700-1200 μm,
Paper stipulated in JIS-P8125 when a load is applied from the front side to the back side against the stiffness in the vertical direction of the paper stipulated in JIS-P8125 when a load is applied from the back side to the front side A carrier tape sheet characterized in that the ratio of stiffness in the vertical direction is 80 to 90%.
<請求項2記載の発明>
表面層および裏面層に水溶性高分子が塗工または含浸され、
裏層面に塗工または含浸された水溶性高分子量に対する、表面層に塗工または含浸された水溶性高分子量の質量比率が120〜250%である、請求項1に記載のキャリアテープ用紙。
<Invention of Claim 2>
The surface layer and the back layer are coated or impregnated with a water-soluble polymer,
The carrier tape paper according to claim 1, wherein a mass ratio of the water-soluble high molecular weight coated or impregnated on the surface layer to the water-soluble high molecular weight coated or impregnated on the back layer surface is 120 to 250%.
<請求項3記載の発明>
中間層に機械パルプが5〜30%含有されている、請求項1または請求項2に記載のキャリアテープ用紙。
<Invention of Claim 3>
The carrier tape paper according to claim 1 or 2, wherein 5 to 30% of mechanical pulp is contained in the intermediate layer.
<請求項4記載の発明>
隣接する層間のJIS−P8121に基づくカナダ標準濾水度の差が50cc以下である請求項1〜3の何れか1項に記載のキャリアテープ用紙。
<Invention of Claim 4>
The carrier tape paper according to any one of claims 1 to 3, wherein a difference in Canadian standard freeness based on JIS-P8121 between adjacent layers is 50 cc or less.
<請求項5記載の発明>
請求項1〜4記載のキャリアテープ用紙に対し、搬送対象部品収納用のキャビティ部とテープ送り用のマージナル部を加工形成してなる、ことを特徴とするキャリアテープ。
<Invention of Claim 5>
5. A carrier tape, comprising a carrier tape sheet according to any one of claims 1 to 4 having a cavity portion for storing a component to be conveyed and a marginal portion for feeding a tape.
本発明に係るキャリアテープ用紙は、多層抄きで各層間にある程度の一体性があり、さらに表裏面層間におけるこわさに適当な差を設けたことにより、キャリアテープとしてリール等に捲き付け時に、リールあるいは管に捲き付ける時あるいは捲き付けた状態において、巻取り内面に向いた側の折れの発生が格段に防止される。 The carrier tape paper according to the present invention has a certain degree of integrity between the layers in the multi-layer paper making, and further, by providing an appropriate difference in stiffness between the front and back layers, Alternatively, the occurrence of folds on the side facing the take-up inner surface is greatly prevented when the tube is rubbed against the tube or in the rubbed state.
そして、水溶性高分子の塗布、含浸により表裏面層間のこわさの差を好適に発生させることができる。 Then, a difference in stiffness between the front and back surfaces can be suitably generated by applying and impregnating the water-soluble polymer.
また、中間層に機械パルプが5〜30%含有されていると地合が良好になり、地合ムラによる折れ起点の発生が防止される。さらに機械パルプは、中間層の柔軟性も向上され、表裏面層間のこわさの差による作用効果をいっそう発揮させやすくなる。 Moreover, when 5-30% of mechanical pulp is contained in the intermediate layer, the formation becomes good, and the occurrence of the folding start point due to uneven formation is prevented. Furthermore, the mechanical pulp also improves the flexibility of the intermediate layer, making it easier to exert the effect of the difference in stiffness between the front and back layers.
さらに、隣接する各層のJIS−P8121に基づくカナダ標準濾水度(以下、単にフリーネスともいう)の差が50cc以下であると、隣接する各層間の繊維の絡み合いが良く、層間強度が高く、リール等に捲き付ける時あるいは捲き付けた状態における巻面に折れや各層間の分離の発生が防止される。 Furthermore, if the difference in Canadian standard freeness (hereinafter also simply referred to as “freeness”) based on JIS-P8121 of each adjacent layer is 50 cc or less, the entanglement of fibers between adjacent layers is good, the interlayer strength is high, and the reel Occurrence of folds on the winding surface and separation between the layers when it is rubbed or the like is prevented.
以上の本発明のキャリアテープ用紙からなるキャリアテープは、折れが極めて発生しづらいなどの利点があり、トップテープを安定的に剥離することができ、電子部品取り出し時の安定生産に優れ生産効率の向上に寄与する。 The carrier tape made of the carrier tape sheet of the present invention has advantages such as being extremely difficult to bend, and the top tape can be stably peeled off. Contributes to improvement.
本発明の実施の形態を、具体例を示しながら以下に詳説する。
本発明のキャリアテープ用紙は、多層抄きで製造される表面層、中間層、裏面層を備える用紙であればよく、3層構造に限らず中間層を複数層有する4層あるいはそれ以上の多層構造であってもよい。ここで、多層抄きとするのは、各層間でパルプ繊維同士に適度な絡みあいが生ずるため各層の適度な一体性が得られるからである。また、多層抄きでは、各層の原料の構成を自由にでき、例えば、古紙パルプを中間層に配合しつつ表面層および裏面層にバージンパルプを使用することが容易で、リサイクルに貢献する古紙パルプを使用しつつ品質の確保を達成しやすいといった利点がある。
Embodiments of the present invention will be described in detail below with specific examples.
The carrier tape paper of the present invention may be a paper having a surface layer, an intermediate layer, and a back layer manufactured by multilayer papermaking, and is not limited to a three-layer structure, but a multilayer of four or more layers having a plurality of intermediate layers. It may be a structure. Here, the reason for making the multi-layer paper is that moderate entanglement between the pulp fibers occurs between the layers, so that appropriate integrity of the layers can be obtained. In addition, in the multi-layer papermaking, the composition of the raw material of each layer can be made freely. For example, it is easy to use virgin pulp for the front and back layers while blending the used paper pulp in the intermediate layer, and contribute to recycling. There is an advantage that it is easy to achieve quality assurance while using.
ここで、本発明に係るキャリアテープ用紙の各層に用いる原料パルプとしては、例えば、広葉樹晒クラフトパルプ(LBKP)、針葉樹晒クラフトパルプ(NBKP)、広葉樹未晒クラフトパルプ(LUKP)、針葉樹未晒クラフトパルプ(NUKP)、広葉樹半晒クラフトパルプ(LSBKP)、針葉樹半晒クラフトパルプ(NSBKP)、広葉樹亜硫酸パルプ、針葉樹亜硫酸パルプ等の化学パルプ、ストーングランドパルプ(SGP)、加圧ストーングランドパルプ(PGW)、リファイナーグランドパルプ(RGP)、サーモメカニカルパルプ(TMP)、ケミグランドパルプ(CGP)、砕木パルプ(GP)、サーモメカニカルパルプ(TMP)等の機械パルプ、茶古紙、クラフト封筒古紙、雑誌古紙、新聞古紙、チラシ古紙、オフィス古紙、段ボール古紙、上白古紙、ケント古紙、模造古紙、地券古紙等から製造される離解古紙パルプ、離解・脱墨古紙パルプ、または離解・脱墨・漂白古紙パルプ、あるいは、ケナフ、麻、葦等の非木材繊維から化学的にまたは機械的に製造されたパルプ等の公知の種々のパルプを一種または数種を適宜選択して使用することができる。ただし、表面実装部品への影響を考慮し填料を減少させる必要がある場合は、ディインキングパルプ、ウエストパルプ等の古紙パルプよりもバージンパルプを使用することが好ましい。 Here, as the raw material pulp used for each layer of the carrier tape paper according to the present invention, for example, hardwood bleached kraft pulp (LBKP), softwood bleached kraft pulp (NBKP), hardwood unbleached kraft pulp (LUKP), softwood unbleached kraft Pulp (NUKP), hardwood semi-bleached kraft pulp (LSBKP), softwood semi-bleached kraft pulp (NSBKP), hardwood sulfite pulp, softwood sulfite pulp, etc., chemical stone, stone grand pulp (SGP), pressurized stone grand pulp (PGW) , Refiner Grand Pulp (RGP), Thermomechanical Pulp (TMP), Chemi-Grand Pulp (CGP), Ground Pulp (GP), Thermomechanical Pulp (TMP), etc. Mechanical Pulp, Tea Waste Paper, Craft Envelope Waste Paper, Magazine Waste Paper, Newspaper Waste paper, flyer waste paper, off Waste paper, corrugated waste paper, Koji white waste paper, Kent waste paper, imitation waste paper, waste paper waste paper, etc. One or several kinds of known various pulps such as pulps chemically or mechanically produced from non-wood fibers such as straw can be appropriately selected and used. However, when it is necessary to reduce the filler in consideration of the influence on the surface mount component, it is preferable to use virgin pulp rather than used paper pulp such as diinking pulp and waist pulp.
特にキャリアテープ用紙の表面層、裏面層においては、その役割、各種品質特性等をバランスよく、効率的に達成するために、LBKP、NBKPが適する。特に、LBKPを70〜95質量%含有することが好ましい。LBKPの含有量が70〜95質量%であると、キャリアテープ用紙として必要な表面強度や剛度を保ちながら、良好な地合いが得られるとともに、トップシールテープとの接着性がより良好となり、トップシールテープを剥離する際に安定したピールオフ強度がることができる。なお、表層の原料パルプのLBKPの含有量が70質量%未満であると、良好な地合いを得ることが難しくなり、トップシールテープとの接着性にバラツキが生じやすく、トップシールテープを剥離する際にキャリアテープの走行が安定しないことがあり、生産効率が低下するおそれもある。一方、LBKPの含有量が95質量%を超えると、表面強度や剛度が低下し、トップシールテープを剥離する際に毛羽立ちや紙粉が発生し、生産効率が低下する原因となる。 In particular, LBKP and NBKP are suitable for the front surface layer and the back surface layer of the carrier tape paper in order to achieve their roles and various quality characteristics in a balanced and efficient manner. In particular, it is preferable to contain 70 to 95% by mass of LBKP. When the content of LBKP is 70 to 95% by mass, while maintaining the surface strength and rigidity necessary for carrier tape paper, a good texture can be obtained and the adhesiveness to the top seal tape becomes better, and the top seal A stable peel-off strength can be obtained when the tape is peeled off. In addition, when the content of LBKP in the raw material pulp of the surface layer is less than 70% by mass, it becomes difficult to obtain a good texture, and the adhesiveness with the top seal tape tends to vary, and when the top seal tape is peeled off In addition, the carrier tape may not be stable, and production efficiency may be reduced. On the other hand, when the content of LBKP exceeds 95% by mass, the surface strength and the rigidity are lowered, and when the top seal tape is peeled off, fluffing and paper dust are generated, which causes a decrease in production efficiency.
特に中間層においては、その役割、リサイクルへの寄与、各種品質特性等をバランスよく、効率的に達成するために、機械パルプが適する。機械パルプとしては、グランドウッドパルプ(GP)、サーモメカニカルパルプ(TMP)、ケミサーモメカニカルパルプ(CTMP)、プレッシャライズドグランドウッドパルプ(PGW)などを使用することができる。これら機械パルプの中でも結束繊維や紙粉の発生が少ないサーモメカニカルパルプ(TMP)、プレッシャライズドグランドウッドパルプ(PGW)が好ましい。 In particular, in the intermediate layer, mechanical pulp is suitable for achieving its role, contribution to recycling, various quality characteristics, etc. in a balanced and efficient manner. As the mechanical pulp, grandwood pulp (GP), thermomechanical pulp (TMP), chemithermomechanical pulp (CTMP), pressured groundwood pulp (PGW), or the like can be used. Among these mechanical pulps, thermomechanical pulp (TMP) and pressured ground wood pulp (PGW) that generate less binding fibers and paper dust are preferable.
また、機械パルプの含有量は5%以上が好ましく、更には10%以上とすることが中間層にクッション性を持たせ、表面の折れ、しわを防止する点でより好ましい。配合量が多いと、強度が低くなり、断面からの紙粉発生や中間層での層間剥離の懸念があるため、30%以下が好ましい。なお、抄紙後の中間層の機械パルプ量は、JIS−P8120に記載の「紙、板紙及びパルプ繊維組成試験方法」により特定できる。 Further, the content of mechanical pulp is preferably 5% or more, and more preferably 10% or more from the viewpoint of imparting cushioning properties to the intermediate layer and preventing surface folding and wrinkling. When the blending amount is large, the strength is lowered, and there is a concern about generation of paper dust from the cross section or delamination in the intermediate layer, so 30% or less is preferable. In addition, the mechanical pulp amount of the intermediate layer after papermaking can be specified by “Paper, paperboard and pulp fiber composition test method” described in JIS-P8120.
一方、中間層に機械パルプを含有するにあたり、中間層の原料として古紙パルプを使用することができる。古紙パルプとしては、茶古紙、クラフト封筒古紙、雑誌古紙、新聞古紙、チラシ古紙、オフィス古紙、段ボール古紙、上白古紙、ケント古紙、模造古紙、地券古紙等から製造される離解古紙パルプ、離解・脱墨古紙パルプ、または離解・脱墨・漂白古紙パルプ等を使用することができる。これらの古紙パルプの中でも、特に中間層の原料としては、キャリアテープ用紙としての各種品質特性をバランスよく、効率的に得るために、表面強度や剛度、引張強度や層間強度などが高く、かつ機械パルプを含みクッション性に優れる、オフィス古紙、茶古紙、クラフト封筒古紙から製造される古紙パルプを用いることが好ましい。 On the other hand, when the intermediate layer contains mechanical pulp, waste paper pulp can be used as a raw material for the intermediate layer. Used paper pulp includes tea waste paper, kraft envelope waste paper, magazine waste paper, newspaper waste paper, flyer waste paper, office waste paper, corrugated waste paper, Kamihaku waste paper, Kent waste paper, imitation waste paper, and old paper waste paper, etc.・ Deinked waste paper pulp or disaggregation / deinking / bleached waste paper pulp can be used. Among these waste paper pulps, especially as the raw material of the intermediate layer, in order to obtain various quality characteristics as carrier tape paper in a balanced and efficient manner, the surface strength, rigidity, tensile strength, interlayer strength, etc. are high, and the machine It is preferable to use waste paper pulp produced from office waste paper, tea waste paper, and craft envelope waste paper that contains pulp and has excellent cushioning properties.
他方、本発明のキャリアテープ用紙は、隣接する各層間のフリーネスの差が50cc以下であるのが望ましい。差が50ccを超える場合は、隣接する層のパルプ繊維同士の絡み合いが弱くなり、直径約50mmのコアに捲き取られる際、あるいは捲き戻される際にかかる曲げやしごきの力によって、各層間で剥離が生じたてトップシールテープを剥離する際にキャリアテープの走行が安定しないことがある。 On the other hand, the carrier tape sheet of the present invention desirably has a difference in freeness between adjacent layers of 50 cc or less. When the difference exceeds 50 cc, the entanglement between the pulp fibers in adjacent layers becomes weak, and peeling occurs between the layers due to the bending and ironing force applied when the core is wound or wound back by a core having a diameter of about 50 mm. When the top seal tape is peeled off, the running of the carrier tape may not be stable.
なお、本発明にかかる各層のフリーネスは、キャリアテープ用紙を各層に分離し、その後にこれをJIS−P8220に基づいて離解処理して測定した値である。ただし、この値は、原料パルプスラリーのフリーネスとほとんど変わらない。ここで、各層の分離方法としては、キャリアテープ用紙を水に浸漬したのち、しごきの力を加えて層間剥離させればよい。その他の測定層以外の層を削りとるなどしてもよく、要は各層を他の層から分離できる方法であれば特に限定されない。 The freeness of each layer according to the present invention is a value measured by separating the carrier tape paper into each layer and then performing disaggregation processing based on JIS-P8220. However, this value is almost the same as the freeness of the raw pulp slurry. Here, as a method for separating each layer, the carrier tape sheet is immersed in water, and then the delamination is performed by applying a squeezing force. Other layers other than the measurement layer may be scraped off, and the point is not particularly limited as long as each layer can be separated from the other layers.
さらに、各層に用いる原料パルプのフリーネスは300〜500ccとすることが好ましく、350〜450ccとすることがより好ましい。すなわち、フリーネスが300cc未満であると、繊維長が短くなるため、キャリアテープとしたときの折れのおそれが高くなり、フリーネスが500ccを超えると、用紙の表面強度や剛度が低下傾向となるため、紙粉が発生しやすくキャリアテープとして加工適性に劣るようになる。 Furthermore, the freeness of the raw material pulp used for each layer is preferably 300 to 500 cc, and more preferably 350 to 450 cc. That is, if the freeness is less than 300 cc, the fiber length is shortened, so there is a high risk of bending when the carrier tape is used, and if the freeness exceeds 500 cc, the surface strength and stiffness of the paper tends to decrease. Paper dust is likely to be generated, and it becomes inferior in processability as a carrier tape.
なお、本発明のおける原料パルプあるいはパルプスラリー中には、内添薬品を必要に応じて添加することができる。例えば、硫酸バンド等の薬品定着剤、ロジン等のサイズ剤、ポリアクリルアマイド、澱粉等の紙力増強剤、ポリアマイド等の濾水・歩留り向上剤、ポリアミド、ポリアミン、エピクロルヒドリン等の耐水化剤、消泡剤、塩基性染料、酸性染料、アニオン性直接染料、カチオン性直接染料等の染料等がある。 In the raw material pulp or pulp slurry in the present invention, an internal additive chemical can be added as necessary. For example, chemical fixing agents such as sulfuric acid bands, sizing agents such as rosin, paper strength enhancers such as polyacrylamide and starch, drainage / yield improvers such as polyamide, waterproofing agents such as polyamide, polyamine and epichlorohydrin, Examples include foaming agents, basic dyes, acid dyes, anionic direct dyes, and cationic direct dyes.
他方、本発明のキャリアテープ用紙は、裏面側から表面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさに対する、表面側から裏面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさの比率が、80〜90%である。好適には82〜88%である。比率が90%を超えると、キャリアテープとしたのち通常使用される直径5cm程度のカセットリールや管に捲き取る際や、捲き戻されて使用される際などに、キャリアテープの表面に折れやしわが生じるようになり、比率が80%未満であるとキャリアテープとしたときの剛性が不足し、曲げ、しごきの力に対して、キャリアテープ裏面に折れが発生して、その部分の表面に、折れやしわが発生するようになる。ここで、表面側から裏面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさは、78mN・m以上、好適には85mN・m以上、140mN・m未満とするのが望ましい。また、裏面側から表面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさは、87mN・m以上、好適には95mN・m以上、155mN・m未満とするのが望ましい。 On the other hand, the carrier tape paper of the present invention applied a load from the front surface side to the back surface side against the stiffness in the paper vertical direction defined in JIS-P8125 when a load was applied from the back surface side to the front surface side. The ratio of stiffness in the vertical direction of the paper defined in JIS-P8125 is 80 to 90%. Preferably it is 82 to 88%. If the ratio exceeds 90%, the carrier tape may fold on the surface of the carrier tape when it is scraped on a cassette reel or tube having a diameter of about 5 cm after being used as a carrier tape or when it is used after being rolled back. When the ratio is less than 80%, the rigidity when the carrier tape is used is insufficient, and the bending of the carrier tape causes bending on the back surface of the carrier tape against the bending and ironing force. Breaks and wrinkles will occur. Here, the stiffness in the longitudinal direction of the paper as defined in JIS-P8125 when a load is applied from the front side to the back side is 78 mN · m or more, preferably 85 mN · m or more and less than 140 mN · m. Is desirable. Further, the stiffness in the vertical direction of the paper as defined in JIS-P8125 when a load is applied from the back side to the front side is 87 mN · m or more, preferably 95 mN · m or more and less than 155 mN · m. Is desirable.
なお、試験片を8mm幅で測定する場合には、表面側から裏面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさは16mN・m以上、好適には17mN・m以上とするのが望ましく、裏面側から表面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさは18mN・m以上、好適には20mN・m以上とするのが望ましい。 When measuring a test piece with a width of 8 mm, the stiffness in the vertical direction of the paper defined in JIS-P8125 when a load is applied from the front side to the back side is 16 mN · m or more, preferably 17 mN. -It is desirable to set it to m or more, and when the load is applied from the back side to the front side, the stiffness in the paper vertical direction defined in JIS-P8125 is 18 mN · m or more, preferably 20 mN · m or more. Is desirable.
キャリアテープ用紙のこわさを本発明の範囲にするにあたっては、表面層、裏面層に水溶性高分子を塗工あるいは含浸させることにより達成するのが簡易で適する。そして、この場合表面層に塗工または含浸された水溶性高分子量に対する、裏層面に塗工または含浸された水溶性高分子量の質量比率が120〜250%とするのが望ましい。表面層、裏面層に塗工あるいは含浸させる水溶性高分子としては、澱粉、ポリビニールアルコール(PVA)、ポリアクリルアミド(PAM)等から、1種又は2種以上の水溶性高分子を使用することができる。なかでも、表面強度やトップカバーテープとの接着性、耐熱性などの点からポリビニールアルコール(PVA)を使用するのが好ましい。 In order to make the stiffness of the carrier tape paper within the scope of the present invention, it is simple and suitable to achieve by applying or impregnating a water-soluble polymer to the surface layer and the back surface layer. In this case, the mass ratio of the water-soluble high molecular weight coated or impregnated on the back layer surface to the water-soluble high molecular weight coated or impregnated on the surface layer is preferably 120 to 250%. As the water-soluble polymer to be coated or impregnated on the surface layer and the back layer, one or more water-soluble polymers from starch, polyvinyl alcohol (PVA), polyacrylamide (PAM), etc. should be used. Can do. Among these, it is preferable to use polyvinyl alcohol (PVA) from the viewpoints of surface strength, adhesion to the top cover tape, heat resistance, and the like.
表面層への塗工または含浸量は、固形分で1.5〜4.0g/m2塗工することが好ましい。より好ましくは1.5〜2.5g/m2である。水溶性高分子の塗工・含浸量が1.5g/m2未満であると、用紙の裏面層側から表面層側へ向かって荷重を掛けた時のこわさに対する、表面層側から裏面層側へ向かって荷重を掛けたときのこわさの比率を80〜90%とすることが難しくなる。また、4.0g/m2を超えると塗工、含浸後の乾燥性が悪化し、生産性が低下するとともに後の工程の汚れを生じる。表裏面各層に水溶性高分子を内添する方法もあるが、コスト面や操業性などから外添するのが好ましい。 The coating or impregnation amount on the surface layer is preferably 1.5 to 4.0 g / m 2 in terms of solid content. More preferably, it is 1.5-2.5 g / m < 2 >. If the coating / impregnation amount of the water-soluble polymer is less than 1.5 g / m 2 , the surface layer side to the back layer side against the stiffness when a load is applied from the back layer side to the surface layer side of the paper It becomes difficult to make the ratio of stiffness when applying a load toward 80 to 90%. On the other hand, if it exceeds 4.0 g / m 2 , the drying property after coating and impregnation is deteriorated, the productivity is lowered and soiling in the subsequent step is caused. Although there is a method of internally adding a water-soluble polymer to each of the front and back layers, it is preferable to externally add from the viewpoint of cost and operability.
特に、裏面層に対する塗工・含浸量は、固形分で0.5〜2.0g/m2とするのが好ましい。より好ましくは0.5〜1.5g/m2である。裏面層への塗工・含浸量が0.5g/m2未満であると、キャリアテープとしたときの表面強度、層間強度が不足するおそれがある。2.0g/m2を超えると、こわさの比率を上記範囲(80〜90%)とすることが難しくなる。また、塗工・含浸後の乾燥性が悪化し、生産性が低下するとともに後の工程で汚れが生じることもある。 In particular, the coating / impregnation amount for the back layer is preferably 0.5 to 2.0 g / m 2 in terms of solid content. More preferably, it is 0.5-1.5 g / m < 2 >. If the coating / impregnation amount on the back layer is less than 0.5 g / m 2 , the surface strength and interlayer strength of the carrier tape may be insufficient. When it exceeds 2.0 g / m 2 , it becomes difficult to set the stiffness ratio within the above range (80 to 90%). Moreover, the drying property after coating and impregnation is deteriorated, the productivity is lowered, and dirt may be produced in the subsequent process.
水溶性高分子を表面層、裏面層へ塗工・含浸するために用いる塗工装置は特に限定されるものではなく、例えばエアナイフコーター、ブレードコーター、ロッドコーター、バーコーター及びゲートロールコーター、サイズプレス等のロールコーター、ベルバパコーター、カレンダー塗工等を適宜使用することができる。 The coating apparatus used for coating / impregnating the water-soluble polymer on the surface layer and the back layer is not particularly limited. For example, air knife coater, blade coater, rod coater, bar coater, gate roll coater, size press A roll coater such as velvapa coater, calendar coating and the like can be used as appropriate.
裏面層への塗工・含浸量を、表面層への塗工・含浸量よりも少なくするにあたっては、例えば、表裏層に塗工・含浸させる塗工液中の水溶性高分子濃度に変化をもたせたり、各層に対する塗工回数を異ならしめたりすればよい。例えば、カレンダー塗工機によって表面層に2回塗工し、裏面層に1回塗工するなどすればよい。 In order to reduce the amount of coating / impregnation to the back layer to less than the amount of coating / impregnation to the front layer, for example, change the concentration of water-soluble polymer in the coating solution to be coated / impregnated on the front and back layers. It may be provided or the number of coatings for each layer may be made different. For example, it may be applied to the surface layer twice by a calender coating machine and once to the back layer.
水溶性高分子を塗工・含浸させた後には、カレンダー装置にて表裏面を平滑化処理することができる。表面平滑化処理するためのカレンダー装置としては特に限定されるものではなく、例えばマシンカレンダー、ソフトカレンダー、又はヤンキードライヤー等が適宜使用される。表面平滑化処理は、JIS P 8151 プリント・サーフ試験機法(面積式流量計形プリント・サーフ試験機)にて、ソフトバッキングを用いてクランプ装置のバッキングを1.0MPAとして測定したときの平滑度が5.0〜8.0μmとなるようにするのが望ましい。 After coating and impregnating the water-soluble polymer, the front and back surfaces can be smoothed by a calendar device. The calendar device for performing the surface smoothing treatment is not particularly limited, and for example, a machine calendar, a soft calendar, a Yankee dryer, or the like is used as appropriate. Surface smoothing treatment is smoothness when the backing of the clamping device is measured as 1.0 MPA using soft backing in accordance with JIS P 8151 print surf tester method (area type flow meter type print surf tester). Is preferably 5.0 to 8.0 μm.
さらに、本発明のキャリアテープ用紙では、表面層の、TAPPI T459 om−83に準じて測定した表面強度が12A以上であるの好ましく、14Aであるのがより好ましい。表面強度を12A以上とするためには、原料配合率や原料パルプスラリーのスリーネス、水溶性高分子を塗工・含浸するなどの方法により達成することができる。トップカバーテープを接着する側の表面の表面強度が12A未満の場合には、トッパカバーテープを剥離する工程にて、キャリアテープ用紙表面のパルプ繊維がとられ、紙粉となって操業性を悪化させる原因となる。 Furthermore, in the carrier tape paper of the present invention, the surface strength of the surface layer measured according to TAPPI T459 om-83 is preferably 12A or more, and more preferably 14A. In order to make the surface strength 12A or more, it can be achieved by a method such as coating / impregnation with a raw material blending ratio, a raw pulp slurry's threeness, and a water-soluble polymer. When the surface strength of the surface to which the top cover tape is bonded is less than 12A, the pulp fiber on the surface of the carrier tape paper is taken in the process of peeling the topper cover tape, and it becomes paper dust and deteriorates operability. Cause it.
以上詳述のキャリアテープ用紙は、15〜20cm程度の幅の中原反に裁断したのちに、製品巾(例えば8mm巾)に裁断し、パンチ加工やエンボス加工等の適宜の加工をほどこして搬送対象部品収納用のキャビティ部やテープ送り用のマージナル部等を形成し、本発明のキャリアテープとする。 The carrier tape paper described in detail above is cut into a medium thickness of about 15 to 20 cm, then cut into a product width (for example, 8 mm width), and subjected to appropriate processing such as punching or embossing to be conveyed. A cavity portion for storing components, a marginal portion for tape feeding, and the like are formed to obtain the carrier tape of the present invention.
次に、本発明の実施例と比較例を説明することにより本発明の効果を明らかにする。なお、当然、本発明を以下の実施例のものに限定する趣旨ではない。また、以下の試験例においては、特に説明ない限り、「部」及び「%」とは、それぞれ「質量部」及び「質量%」を意味し、「kg/t」とは、パルプトンあたりの量(kg)を意味する。 Next, the effects of the present invention will be clarified by describing examples and comparative examples of the present invention. Of course, the present invention is not intended to be limited to the following examples. In the following test examples, unless otherwise specified, “parts” and “%” mean “parts by mass” and “% by mass”, respectively, and “kg / t” means the amount per pulp ton. (Kg).
〔実施例1〕
表面層及び裏面層については、針葉樹晒クラフトパルプ(NBKP)15%、広葉樹晒クラフトパルプ(LBKP)85%からなるフリーネス420mlのパルプスラリーに、サイズ剤(近代化学工業株式会社製R50)を固形分換算で0.25%、PAM(ハリマ化成株式会社製、ハーマイドB−15)を固形分換算で0.15%内添し、硫酸バンドを添加してPHを5に調整した原料を使用した。
一方、中間層(2〜4層)としては、NBKP50%、LBKP40%、サーモメカニカルパルプ(TMP)10%からなるフリーネス410mlのパルプスラリーに、サイズ剤(近代化学工業株式会社製R50)を固形分換算で0.30%、PAM(ハリマ化成株式会社製、ハーマイドB−15)を固形分換算で0.5%内添し、硫酸バンドを添加してPHを5に調整した原料を使用した。
これらを円網多層抄紙機にて、表層の付け量を60g/m2、中層(2〜4層)の付け量を460g/m2、裏層の付け量を60g/m2として、5層構造で抄き合わせ、PVA(日本合成化学株式会社製、ゴーセノールN300)をカレンダー塗工で表面に塗工量1.0g/m2、裏面に1.0g/m2塗工してキャリアテープ用紙を得た。
[Example 1]
For the surface layer and the back layer, sizing agent (R50 manufactured by Modern Chemical Industry Co., Ltd.) is added to the pulp slurry of 420 ml freeness consisting of 15% softwood bleached kraft pulp (NBKP) and 85% hardwood bleached kraft pulp (LBKP). A raw material in which 0.25% in terms of conversion and 0.15% in terms of solid content of PAM (manufactured by Harima Kasei Co., Ltd., Hermide B-15) was internally added, and a pH adjusted to 5 by adding a sulfuric acid band was used.
On the other hand, as an intermediate layer (2-4 layers), a sizing agent (R50 manufactured by Modern Chemical Industry Co., Ltd.) is added to a pulp slurry of 410 ml of freeness composed of NBKP 50%, LBKP 40%, and thermomechanical pulp (TMP) 10%. A raw material having 0.30% in terms of conversion and 0.5% PAM (Harmide B-15, manufactured by Harima Kasei Co., Ltd.) in terms of solid content and adjusting the pH to 5 by adding a sulfuric acid band was used.
These are 5 layers with a circular multi-layer paper machine, with a surface layer weight of 60 g / m 2 , a middle layer (2-4 layers) weight of 460 g / m 2 , and a back layer weight of 60 g / m 2. Paper with a structure, PVA (Nippon Synthetic Chemical Co., Ltd., Gohsenol N300) is calender coated on the surface with a coating amount of 1.0 g / m 2 , and on the back with 1.0 g / m 2 carrier tape paper Got.
〔実施例2〜5〕
表層表面に塗工するPVAの塗工量を表1に示す値に調整したことを除き、その他の点を実施例1と同様にしてキャリアテープ用紙を得た。
[Examples 2 to 5]
A carrier tape paper was obtained in the same manner as in Example 1 except that the amount of PVA applied on the surface of the surface layer was adjusted to the value shown in Table 1.
〔実施例6〜12〕
中層に使用する原料パルプ配合率を表1に示す値に調整したことを除き、その他の点を実施例1と同様にしてキャリアテープ用紙を得た。
[Examples 6 to 12]
A carrier tape paper was obtained in the same manner as in Example 1 except that the raw material pulp content used in the middle layer was adjusted to the values shown in Table 1.
〔実施例13〜18〕
表層、裏層、および中層に使用するパルプスラリーのフリーネスを表1に示した値としたことを除き、その他の点を実施例1と同様にしてキャリアテープ用紙を得た。
[Examples 13 to 18]
A carrier tape paper was obtained in the same manner as in Example 1 except that the freeness of the pulp slurry used for the surface layer, the back layer, and the middle layer was set to the values shown in Table 1.
〔実施例19〜23〕
表層、裏層に使用する原料パルプの配合率を表1に示す値に調整したことを除き、その他の点を実施例1と同様にしてキャリアテープ用紙を得た。
[Examples 19 to 23]
A carrier tape paper was obtained in the same manner as in Example 1 except that the blending ratio of the raw material pulp used for the surface layer and the back layer was adjusted to the values shown in Table 1.
〔比較例1〜2〕
表層表面に塗工するPVAの塗工量を表1に示す値に調整したことを除き、その他の点を実施例1と同様にしてキャリアテープ用紙を得た。
[Comparative Examples 1-2]
A carrier tape paper was obtained in the same manner as in Example 1 except that the amount of PVA applied on the surface of the surface layer was adjusted to the value shown in Table 1.
以上の実施例および比較例について米坪、厚さ、こわさ、平滑度、表面強度、層間強度の物性測定と、折れについて評価試験を行った。結果は、表1中に示す。なお、物性測定およびこの評価試験は、JIS−P8111に準拠して温度23℃±1℃、湿度50±2%の環境条件で行った。 About the above Example and the comparative example, the evaluation test was done about the physical-property measurement of a tsubo, thickness, stiffness, smoothness, surface strength, and interlayer strength, and a crease. The results are shown in Table 1. The physical property measurement and this evaluation test were performed under environmental conditions of a temperature of 23 ° C. ± 1 ° C. and a humidity of 50 ± 2% in accordance with JIS-P8111.
各測定方法および試験方法についての詳細は以下のとおりである。
(厚さ)
JIS P 8118 紙及び板紙−厚さ及び密度の試験方法に準じて厚さを測定した。
Details of each measurement method and test method are as follows.
(thickness)
JIS P 8118 Paper and paperboard—Thickness was measured according to thickness and density test methods.
(こわさ)
JIS P 8125 紙及び板紙−こわさ試験方法−テーバーこわさ試験機法に準じて縦方向のこわさを測定した。表中では、表面側から裏面側へ向かって荷重を掛けた時の縦方向のこわさを(X)とし、裏面側から表面側へ向かって荷重を掛けた時の縦方向のこわさを(Y)とした。
(Stiffness)
In accordance with JIS P 8125 paper and paperboard-stiffness test method-Taber stiffness tester method, the stiffness in the vertical direction was measured. In the table, (X) is the vertical stiffness when a load is applied from the front side to the back side, and (Y) is the vertical stiffness when a load is applied from the back side to the front side. It was.
(平滑度)
JIS P 8151 紙及び板紙−表面粗さ及び平滑度試験方法(エア・リーク法)−プリント・サーフ試験機法(面積式流量計形プリント・サーフ試験機)にて、ソフトバッキングを用い、クランプ装置のバッキングを1.0MPAとして表面、裏面それぞれの平滑度を測定した。
(Smoothness)
JIS P 8151 Paper and paperboard-Surface roughness and smoothness test method (air leak method)-Print surf tester method (area type flow meter type print surf tester), using soft backing, clamping device The smoothness of each of the front and back surfaces was measured with a backing of 1.0MPA.
(表面強度)
TAPPI T459 om−83に基づき、表面側、裏面側のそれぞれの表面強度を測定した。
(Surface strength)
Based on TAPPI T459 om-83, the surface strengths on the front and back sides were measured.
(層間強度)
TAPPI UM522に従い、Z軸方向の層間強度を測定した。
(Interlayer strength)
According to TAPPI UM522, the interlayer strength in the Z-axis direction was measured.
(各層の分離方法)
抄紙後の用紙の各層の物性を測定すべく、抄紙後の用紙から次記の方法で各層に分離した。まず、試料を室温の水に約1時間浸漬したのち、試料の角を起点として10mmΦ程度の丸棒に捲き付け、その状態で丸棒を転がして試料をしごく。この操作を試料の四隅の全ての角を起点に繰り返し、各方向から試料にしごきの力を加える。これにより、試料の層間の一部が剥離してくるので、これを利用して、試料を表層、中層、及び裏層に分離する。
(Separation method of each layer)
In order to measure the physical properties of each layer of the paper after paper making, each layer was separated from the paper after paper making by the following method. First, after immersing the sample in water at room temperature for about 1 hour, the sample is rubbed on a round bar of about 10 mmΦ starting from the corner of the sample, and the round bar is rolled in this state to squeeze the sample. This operation is repeated starting from all four corners of the sample, and an ironing force is applied to the sample from each direction. As a result, part of the layer between the samples is peeled off, and this is used to separate the sample into a surface layer, a middle layer, and a back layer.
(フリーネス)
分離された各層を裁断して約3cm2、約25gの試験片とし、この試験片を1リットルの水に24時間浸漬したのちにJIS−P8220に基づき標準離解機で15分間離解処理し、試験片が完全に離解していることを目視で確認した後、JIS−P8121に準拠してカナダ標準濾水度試験機にて測定した。
(Freeness)
Each separated layer is cut to obtain a test piece of about 3 cm 2 and about 25 g. After the test piece is immersed in 1 liter of water for 24 hours, it is subjected to a disaggregation treatment for 15 minutes with a standard disintegrator based on JIS-P8220. After visually confirming that the piece was completely disaggregated, it was measured with a Canadian standard freeness tester according to JIS-P8121.
(折れ)
折れの評価は、流れ方向30cm、幅8mmのサンプルを10本用意し、直径6cmの円柱に捲きつけ、折れの発生個数を目視判定し、1本のあたりの平均個数を次の基準で評価した。評価は、1個未満を◎、1個以上2個未満を○、2以上5個未満△、5個以上を×と評価した。
(Break)
For the evaluation of folding, ten samples having a flow direction of 30 cm and a width of 8 mm were prepared, placed on a cylinder having a diameter of 6 cm, the number of occurrences of folding was visually determined, and the average number per one was evaluated according to the following criteria. . In the evaluation, less than 1 was evaluated as ◎, 1 or more and less than 2 as ○, 2 or more and less than 5 Δ, and 5 or more as ×.
表1から、本発明のキャリアテープ用紙である実施例1〜23は品質評価に優れることが分かる。それに対して、比較例1〜2は、品質評価において実施例1〜23よりも劣る結果となっている。してみると、本発明のキャリアテープ用紙からは、カセットリールや管に捲き取るときや捲き取り後に、折れやしわの発生が防止されているといえる、これにより、トップテープを安定的に剥離することができ、電子部品取り出し時の安定生産に優れ、生産効率のよいキャリアテープを得ることができるといえる。 From Table 1, it can be seen that Examples 1 to 23, which are carrier tape sheets of the present invention, are excellent in quality evaluation. On the other hand, Comparative Examples 1-2 are inferior to Examples 1-23 in quality evaluation. As a result, it can be said that the carrier tape sheet of the present invention prevents creases and wrinkles from occurring when the cassette tape or tube is scraped off or after scraping. It can be said that it is possible to obtain a carrier tape that is excellent in stable production at the time of taking out electronic components and has high production efficiency.
本発明は、電子回路を製造する際に使用する、チップ状の表面実装電子部品を収納し、表面実装機(マウンター)に搬送するためのキャリアテープおよびこれに用いるキャリアテープ用紙に関する。 The present invention relates to a carrier tape for storing chip-shaped surface-mounted electronic components and transporting them to a surface-mounting machine (mounter) and a carrier tape sheet used therefor, which are used when manufacturing an electronic circuit.
電子機器の自動生産を行うにあたっては、表面実装タイプの電子部品を表面実装機により基板に自動装着する技術が用いられる。表面実装機に対して電子部品を供給するためには、電子部品収納用のキャビティ部と表面実装機内への送り用のマージナル部とを備える幅6〜9mm、基紙厚0.4〜1.0mmのキャリアテープが用いられている。特に一般的には幅8mm、厚さが0.7〜1.0mmのものがよく用いられる。
このキャリアテープは、紙製およびプラスチック製のものがあるが、コスト安であり、軽量であり、廃棄容易であり、非帯電性であることから紙製とするのが望ましいとされている。
キャリアテープの具体的な形態としては、部品収納用のキャビティ部とキャリアテープ送り用のマージナル部とが貫通孔であり、表面実装部品を収納した状態で、表面がトップカバーテープでシールされ、下面がボトムテープによりシールされるパンチキャリアテープや、キャビティ部がエンボス加工により形成された凹部であり、表面のみがトップカバーテープでシールされるエンボスキャリアテープや、表面実装部品の挿入直前にこれらキャビティ部等を形成するアンパンチキャリアテープなどが知られる。
これらのキャリアテープはキャビティ部に電子部品が装填されトップカバーテープでシールされた状態で、直径5cm程度のカセットリールに捲きつられた状態(レコード巻方式)、あるいは直径20cm程度巾10cm程度の紙管にスパイラル状に捲きつられた状態(トラバース巻)で出荷され、最終ユーザーが表面実装機に装着して使用される。
近年では、レコード巻方式と比較して1巻当りの巻長さを長くすることができるために継ぎ手作業が軽減され、電子部品装填工程の高速化及び作業効率向上のメリットがあるトラバース巻方式が多用されるようになっている。
There are paper and plastic carrier tapes. However, it is desirable that the carrier tape be made of paper because of its low cost, light weight, easy disposal, and non-charging properties.
As a specific form of the carrier tape, the cavity for storing the parts and the marginal part for feeding the carrier tape are through holes, and the surface is sealed with the top cover tape in a state where the surface mount parts are stored, and the bottom surface. Is a punch carrier tape that is sealed with a bottom tape, or an embossed carrier tape whose cavity part is formed by embossing and whose surface is sealed with a top cover tape. An unpunched carrier tape or the like is known.
These carrier tapes are loaded with electronic parts in the cavity and sealed with a top cover tape, and are wound around a cassette reel having a diameter of about 5 cm (record winding method), or a paper tube having a diameter of about 20 cm and a width of about 10 cm. It is shipped in a state of being wound in a spiral shape (traverse winding), and used by the end user by mounting it on a surface mounter.
In recent years, the traverse winding method has the advantages of reducing the joint work because the winding length per turn can be increased compared to the record winding method, speeding up the electronic component loading process, and improving work efficiency. It has come to be used frequently.
しかしながら、従来キャリアテープは、カセットリール等に捲き付ける際に、リールあるいは管の外周面に沿って湾曲せずに折れてしまうことがあった。
折れの現象は一般的に用いられる紙厚が700μm以上のもので顕著となり、またカセットリール径が5〜6cmと小径の場合に顕著となる。そして、このように折れが生ずると、その折れ部分の表面に凸部が発現し、この凸部が次工程の表面実装機のガイド部分に引っ掛かって部品を表面実装機内に安定して装填することができない。また、表面実装機では、トップシールを一定張力で引張しつつキャリアテープから剥離してキャビティ内の電子部品を取り出すが、キャリアテープが折れるとその折れ部分でキャリアテープからトップカバーシールが剥離して浮いてしまう。そうすると、表面実装機がトップカバーシールを一定張力で引張することができず、表面実装機に引っ張られるキャリアテープがばたつきキャビティ内の電子部品の脱落や所望位置への装填ができなくなる。
そこで、本発明の解決課題は、厚さ700μm以上の多層抄き板紙を効率良く生産することができ、かつ、リール捲き付け時あるいは捲き付け状態において、折れの発生が防止されたキャリアテープおよびキャリアテープ用紙を提供することにある。
However, when a conventional carrier tape is rubbed against a cassette reel or the like, the carrier tape may be bent without being bent along the outer peripheral surface of the reel or tube.
The phenomenon of folding becomes significant when the generally used paper thickness is 700 μm or more, and becomes remarkable when the cassette reel diameter is as small as 5 to 6 cm. And when a fold occurs in this way, a convex portion appears on the surface of the fold portion, and this convex portion is hooked on the guide portion of the surface mounting machine in the next process to stably load the component into the surface mounting machine. I can't. In surface mounters, the top seal is pulled from the carrier tape while pulling it at a constant tension, and the electronic components inside the cavity are taken out. However, when the carrier tape is broken, the top cover seal is peeled from the carrier tape at the folded portion. It will float. Then, the surface mounter cannot pull the top cover seal with a constant tension, and the carrier tape pulled by the surface mounter flutters, so that the electronic components in the cavity cannot be dropped off or loaded at a desired position.
SUMMARY OF THE INVENTION Accordingly, a problem to be solved by the present invention is that a carrier tape and a carrier capable of efficiently producing a multilayer paperboard having a thickness of 700 μm or more, and preventing the occurrence of folds at the time of reel winding or in the winding state. To provide tape paper.
上記課題を解決した本発明は次記のとおりである。
<請求項1記載の発明>
巻取りの外面となる表面層と、巻取りの内面となる裏面層と、それらの間の中間層を有する多層抄きのキャリアテープ用紙であって、
紙厚が700〜1200μmであり、
裏面側から表面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさに対する、表面側から裏面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさの比率が、80〜90%である、ことを特徴とするキャリアテープ用紙。
The present invention that has solved the above problems is as follows.
<Invention of Claim 1>
A multi-layered carrier tape paper having a surface layer as an outer surface of winding, a back layer as an inner surface of winding, and an intermediate layer therebetween,
The paper thickness is 700-1200 μm,
Paper stipulated in JIS-P8125 when a load is applied from the front side to the back side against the stiffness in the vertical direction of the paper stipulated in JIS-P8125 when a load is applied from the back side to the front side A carrier tape sheet characterized in that the ratio of stiffness in the vertical direction is 80 to 90%.
<請求項2記載の発明>
表面層および裏面層に水溶性高分子が塗工または含浸され、
裏面層に塗工または含浸された水溶性高分子量に対する、表面層に塗工または含浸された水溶性高分子量の質量比率が120〜250%である、請求項1に記載のキャリアテープ用紙。
<Invention of Claim 2>
The surface layer and the back layer are coated or impregnated with a water-soluble polymer,
The carrier tape paper according to claim 1, wherein a mass ratio of the water-soluble high molecular weight coated or impregnated on the surface layer to the water-soluble high molecular weight coated or impregnated on the back layer is 120 to 250%.
<請求項3記載の発明>
中間層に機械パルプが5〜30%含有されている、請求項1または請求項2に記載のキャリアテープ用紙。
<Invention of Claim 3>
The carrier tape paper according to claim 1 or 2, wherein 5 to 30% of mechanical pulp is contained in the intermediate layer.
<請求項4記載の発明>
隣接する層間のJIS−P8121に基づくカナダ標準濾水度の差が50cc以下である請求項1〜3の何れか1項に記載のキャリアテープ用紙。
<Invention of Claim 4>
The carrier tape paper according to any one of claims 1 to 3, wherein a difference in Canadian standard freeness based on JIS-P8121 between adjacent layers is 50 cc or less.
<請求項5記載の発明>
請求項1〜4記載のキャリアテープ用紙に対し、搬送対象部品収納用のキャビティ部とテープ送り用のマージナル部を加工形成してなる、ことを特徴とするキャリアテープ。
<Invention of Claim 5>
5. A carrier tape, comprising a carrier tape sheet according to any one of claims 1 to 4 having a cavity portion for storing a component to be conveyed and a marginal portion for feeding a tape.
本発明に係るキャリアテープ用紙は、多層抄きで各層間にある程度の一体性があり、さらに表裏面層間におけるこわさに適当な差を設けたことにより、キャリアテープとしてリール等に捲き付け時に、リールあるいは管に捲き付ける時あるいは捲き付けた状態において、巻取り内面に向いた側の折れの発生が格段に防止される。 The carrier tape paper according to the present invention has a certain degree of integrity between the layers in the multi-layer paper making, and further, by providing an appropriate difference in stiffness between the front and back layers, Alternatively, the occurrence of folds on the side facing the take-up inner surface is greatly prevented when the tube is rubbed against the tube or in the rubbed state.
そして、水溶性高分子の塗布、含浸により表裏面層間のこわさの差を好適に発生させることができる。 Then, a difference in stiffness between the front and back surfaces can be suitably generated by applying and impregnating the water-soluble polymer.
また、中間層に機械パルプが5〜30%含有されていると地合が良好になり、地合ムラによる折れ起点の発生が防止される。さらに機械パルプは、中間層の柔軟性も向上され、表裏面層間のこわさの差による作用効果をいっそう発揮させやすくなる。 Moreover, when 5-30% of mechanical pulp is contained in the intermediate layer, the formation becomes good, and the occurrence of the folding start point due to uneven formation is prevented. Furthermore, the mechanical pulp also improves the flexibility of the intermediate layer, making it easier to exert the effect of the difference in stiffness between the front and back layers.
さらに、隣接する各層のJIS−P8121に基づくカナダ標準濾水度(以下、単にフリーネスともいう)の差が50cc以下であると、隣接する各層間の繊維の絡み合いが良く、層間強度が高く、リール等に捲き付ける時あるいは捲き付けた状態における巻面に折れや各層間の分離の発生が防止される。 Furthermore, if the difference in Canadian standard freeness (hereinafter also simply referred to as “freeness”) based on JIS-P8121 of each adjacent layer is 50 cc or less, the entanglement of fibers between adjacent layers is good, the interlayer strength is high, and the reel Occurrence of folds on the winding surface and separation between the layers when it is rubbed or the like is prevented.
以上の本発明のキャリアテープ用紙からなるキャリアテープは、折れが極めて発生しづらいなどの利点があり、トップテープを安定的に剥離することができ、電子部品取り出し時の安定生産に優れ生産効率の向上に寄与する。 The carrier tape made of the carrier tape sheet of the present invention has advantages such as being extremely difficult to bend, and the top tape can be stably peeled off. Contributes to improvement.
本発明の実施の形態を、具体例を示しながら以下に詳説する。
本発明のキャリアテープ用紙は、多層抄きで製造される表面層、中間層、裏面層を備える用紙であればよく、3層構造に限らず中間層を複数層有する4層あるいはそれ以上の多層構造であってもよい。ここで、多層抄きとするのは、各層間でパルプ繊維同士に適度な絡みあいが生ずるため各層の適度な一体性が得られるからである。また、多層抄きでは、各層の原料の構成を自由にでき、例えば、古紙パルプを中間層に配合しつつ表面層および裏面層にバージンパルプを使用することが容易で、リサイクルに貢献する古紙パルプを使用しつつ品質の確保を達成しやすいといった利点がある。
Embodiments of the present invention will be described in detail below with specific examples.
The carrier tape paper of the present invention may be a paper having a surface layer, an intermediate layer, and a back layer manufactured by multilayer papermaking, and is not limited to a three-layer structure, but a multilayer of four or more layers having a plurality of intermediate layers. It may be a structure. Here, the reason for making the multi-layer paper is that moderate entanglement between the pulp fibers occurs between the layers, so that appropriate integrity of the layers can be obtained. In addition, in the multi-layer papermaking, the composition of the raw material of each layer can be made freely. For example, it is easy to use virgin pulp for the front and back layers while blending the used paper pulp in the intermediate layer, and contribute to recycling. There is an advantage that it is easy to achieve quality assurance while using.
ここで、本発明に係るキャリアテープ用紙の各層に用いる原料パルプとしては、例えば、広葉樹晒クラフトパルプ(LBKP)、針葉樹晒クラフトパルプ(NBKP)、広葉樹未晒クラフトパルプ(LUKP)、針葉樹未晒クラフトパルプ(NUKP)、広葉樹半晒クラフトパルプ(LSBKP)、針葉樹半晒クラフトパルプ(NSBKP)、広葉樹亜硫酸パルプ、針葉樹亜硫酸パルプ等の化学パルプ、ストーングランドパルプ(SGP)、加圧ストーングランドパルプ(PGW)、リファイナーグランドパルプ(RGP)、サーモメカニカルパルプ(TMP)、ケミグランドパルプ(CGP)、砕木パルプ(GP)、サーモメカニカルパルプ(TMP)等の機械パルプ、茶古紙、クラフト封筒古紙、雑誌古紙、新聞古紙、チラシ古紙、オフィス古紙、段ボール古紙、上白古紙、ケント古紙、模造古紙、地券古紙等から製造される離解古紙パルプ、離解・脱墨古紙パルプ、または離解・脱墨・漂白古紙パルプ、あるいは、ケナフ、麻、葦等の非木材繊維から化学的にまたは機械的に製造されたパルプ等の公知の種々のパルプを一種または数種を適宜選択して使用することができる。ただし、表面実装部品への影響を考慮し填料を減少させる必要がある場合は、ディインキングパルプ、ウエストパルプ等の古紙パルプよりもバージンパルプを使用することが好ましい。 Here, as the raw material pulp used for each layer of the carrier tape paper according to the present invention, for example, hardwood bleached kraft pulp (LBKP), softwood bleached kraft pulp (NBKP), hardwood unbleached kraft pulp (LUKP), softwood unbleached kraft Pulp (NUKP), hardwood semi-bleached kraft pulp (LSBKP), softwood semi-bleached kraft pulp (NSBKP), hardwood sulfite pulp, softwood sulfite pulp, etc., chemical stone, stone grand pulp (SGP), pressurized stone grand pulp (PGW) , Refiner Grand Pulp (RGP), Thermomechanical Pulp (TMP), Chemi-Grand Pulp (CGP), Ground Pulp (GP), Thermomechanical Pulp (TMP), etc. Mechanical Pulp, Tea Waste Paper, Craft Envelope Waste Paper, Magazine Waste Paper, Newspaper Waste paper, flyer waste paper, off Waste paper, corrugated waste paper, Koji white waste paper, Kent waste paper, imitation waste paper, waste paper waste paper, etc. One or several kinds of known various pulps such as pulps chemically or mechanically produced from non-wood fibers such as straw can be appropriately selected and used. However, when it is necessary to reduce the filler in consideration of the influence on the surface mount component, it is preferable to use virgin pulp rather than used paper pulp such as diinking pulp and waist pulp.
特にキャリアテープ用紙の表面層、裏面層においては、その役割、各種品質特性等をバランスよく、効率的に達成するために、LBKP、NBKPが適する。特に、LBKPを70〜95質量%含有することが好ましい。LBKPの含有量が70〜95質量%であると、キャリアテープ用紙として必要な表面強度や剛度を保ちながら、良好な地合いが得られるとともに、トップシールテープとの接着性がより良好となり、トップシールテープを剥離する際に安定したピールオフ強度がることができる。なお、表面層の原料パルプのLBKPの含有量が70質量%未満であると、良好な地合いを得ることが難しくなり、トップシールテープとの接着性にバラツキが生じやすく、トップシールテープを剥離する際にキャリアテープの走行が安定しないことがあり、生産効率が低下するおそれもある。一方、LBKPの含有量が95質量%を超えると、表面強度や剛度が低下し、トップシールテープを剥離する際に毛羽立ちや紙粉が発生し、生産効率が低下する原因となる。 In particular, LBKP and NBKP are suitable for the front surface layer and the back surface layer of the carrier tape paper in order to achieve their roles and various quality characteristics in a balanced and efficient manner. In particular, it is preferable to contain 70 to 95% by mass of LBKP. When the content of LBKP is 70 to 95% by mass, while maintaining the surface strength and rigidity necessary for carrier tape paper, a good texture can be obtained and the adhesiveness to the top seal tape becomes better, and the top seal A stable peel-off strength can be obtained when the tape is peeled off. In addition, when the content of LBKP in the raw material pulp of the surface layer is less than 70% by mass, it becomes difficult to obtain a good texture, the adhesiveness with the top seal tape tends to vary, and the top seal tape is peeled off. In some cases, the running of the carrier tape may not be stable, and production efficiency may be reduced. On the other hand, when the content of LBKP exceeds 95% by mass, the surface strength and the rigidity are lowered, and when the top seal tape is peeled off, fluffing and paper dust are generated, which causes a decrease in production efficiency.
特に中間層においては、その役割、リサイクルへの寄与、各種品質特性等をバランスよく、効率的に達成するために、機械パルプが適する。機械パルプとしては、グランドウッドパルプ(GP)、サーモメカニカルパルプ(TMP)、ケミサーモメカニカルパルプ(CTMP)、プレッシャライズドグランドウッドパルプ(PGW)などを使用することができる。これら機械パルプの中でも結束繊維や紙粉の発生が少ないサーモメカニカルパルプ(TMP)、プレッシャライズドグランドウッドパルプ(PGW)が好ましい。 In particular, in the intermediate layer, mechanical pulp is suitable for achieving its role, contribution to recycling, various quality characteristics, etc. in a balanced and efficient manner. As the mechanical pulp, groundwood pulp (GP), thermomechanical pulp (TMP), chemithermomechanical pulp (CTMP), pressured groundwood pulp (PGW), or the like can be used. Among these mechanical pulps, thermomechanical pulp (TMP) and pressured ground wood pulp (PGW) that generate less binding fibers and paper dust are preferable.
また、機械パルプの含有量は5%以上が好ましく、更には10%以上とすることが中間層にクッション性を持たせ、表面の折れ、しわを防止する点でより好ましい。配合量が多いと、強度が低くなり、断面からの紙粉発生や中間層での層間剥離の懸念があるため、30%以下が好ましい。なお、抄紙後の中間層の機械パルプ量は、JIS−P8120に記載の「紙、板紙及びパルプ繊維組成試験方法」により特定できる。 Further, the content of mechanical pulp is preferably 5% or more, and more preferably 10% or more from the viewpoint of imparting cushioning properties to the intermediate layer and preventing surface folding and wrinkling. When the blending amount is large, the strength is lowered, and there is a concern about generation of paper dust from the cross section or delamination in the intermediate layer, so 30% or less is preferable. In addition, the mechanical pulp amount of the intermediate layer after papermaking can be specified by “Paper, paperboard and pulp fiber composition test method” described in JIS-P8120.
一方、中間層に機械パルプを含有するにあたり、中間層の原料として古紙パルプを使用することができる。古紙パルプとしては、茶古紙、クラフト封筒古紙、雑誌古紙、新聞古紙、チラシ古紙、オフィス古紙、段ボール古紙、上白古紙、ケント古紙、模造古紙、地券古紙等から製造される離解古紙パルプ、離解・脱墨古紙パルプ、または離解・脱墨・漂白古紙パルプ等を使用することができる。これらの古紙パルプの中でも、特に中間層の原料としては、キャリアテープ用紙としての各種品質特性をバランスよく、効率的に得るために、表面強度や剛度、引張強度や層間強度などが高く、かつ機械パルプを含みクッション性に優れる、オフィス古紙、茶古紙、クラフト封筒古紙から製造される古紙パルプを用いることが好ましい。 On the other hand, when the intermediate layer contains mechanical pulp, waste paper pulp can be used as a raw material for the intermediate layer. Used paper pulp includes tea waste paper, kraft envelope waste paper, magazine waste paper, newspaper waste paper, flyer waste paper, office waste paper, corrugated waste paper, Kamihaku waste paper, Kent waste paper, imitation waste paper, and old paper waste paper, etc.・ Deinked waste paper pulp or disaggregation / deinking / bleached waste paper pulp can be used. Among these waste paper pulps, especially as the raw material of the intermediate layer, in order to obtain various quality characteristics as carrier tape paper in a balanced and efficient manner, the surface strength, rigidity, tensile strength, interlayer strength, etc. are high, and the machine It is preferable to use waste paper pulp produced from office waste paper, tea waste paper, and craft envelope waste paper that contains pulp and has excellent cushioning properties.
他方、本発明のキャリアテープ用紙は、隣接する各層間のフリーネスの差が50cc以下であるのが望ましい。差が50ccを超える場合は、隣接する層のパルプ繊維同士の絡み合いが弱くなり、直径約50mmのコアに捲き取られる際、あるいは捲き戻される際にかかる曲げやしごきの力によって、各層間で剥離が生じてトップシールテープを剥離する際にキャリアテープの走行が安定しないことがある。 On the other hand, the carrier tape sheet of the present invention desirably has a difference in freeness between adjacent layers of 50 cc or less. When the difference exceeds 50 cc, the entanglement between the pulp fibers in adjacent layers becomes weak, and peeling occurs between the layers due to the bending and ironing force applied when the core is wound or wound back by a core having a diameter of about 50 mm. travel of the carrier tape when it is peeled off the top seal tape Ji live may not be stable.
なお、本発明にかかる各層のフリーネスは、キャリアテープ用紙を各層に分離し、その後にこれをJIS−P8220に基づいて離解処理して測定した値である。ただし、この値は、原料パルプスラリーのフリーネスとほとんど変わらない。ここで、各層の分離方法としては、キャリアテープ用紙を水に浸漬したのち、しごきの力を加えて層間剥離させればよい。その他の測定層以外の層を削りとるなどしてもよく、要は各層を他の層から分離できる方法であれば特に限定されない。 The freeness of each layer according to the present invention is a value measured by separating the carrier tape paper into each layer and then performing disaggregation processing based on JIS-P8220. However, this value is almost the same as the freeness of the raw pulp slurry. Here, as a method for separating each layer, the carrier tape sheet is immersed in water, and then the delamination is performed by applying a squeezing force. Other layers other than the measurement layer may be scraped off, and the point is not particularly limited as long as each layer can be separated from the other layers.
さらに、各層に用いる原料パルプのフリーネスは300〜500ccとすることが好ましく、350〜450ccとすることがより好ましい。すなわち、フリーネスが300cc未満であると、繊維長が短くなるため、キャリアテープとしたときの折れのおそれが高くなり、フリーネスが500ccを超えると、用紙の表面強度や剛度が低下傾向となるため、紙粉が発生しやすくキャリアテープとして加工適性に劣るようになる。 Furthermore, the freeness of the raw material pulp used for each layer is preferably 300 to 500 cc, and more preferably 350 to 450 cc. That is, if the freeness is less than 300 cc, the fiber length is shortened, so there is a high risk of bending when the carrier tape is used, and if the freeness exceeds 500 cc, the surface strength and stiffness of the paper tends to decrease. Paper dust is likely to be generated, and it becomes inferior in processability as a carrier tape.
なお、本発明における原料パルプあるいはパルプスラリー中には、内添薬品を必要に応じて添加することができる。例えば、硫酸バンド等の薬品定着剤、ロジン等のサイズ剤、ポリアクリルアマイド、澱粉等の紙力増強剤、ポリアマイド等の濾水・歩留り向上剤、ポリアミド、ポリアミン、エピクロルヒドリン等の耐水化剤、消泡剤、塩基性染料、酸性染料、アニオン性直接染料、カチオン性直接染料等の染料等がある。 Incidentally, the pulp or pulp slurry definitive to the present invention may be added as required inner添薬products. For example, chemical fixing agents such as sulfuric acid bands, sizing agents such as rosin, paper strength enhancers such as polyacrylamide and starch, drainage / yield improvers such as polyamide, waterproofing agents such as polyamide, polyamine and epichlorohydrin, Examples include foaming agents, basic dyes, acid dyes, anionic direct dyes, and cationic direct dyes.
他方、本発明のキャリアテープ用紙は、裏面側から表面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさに対する、表面側から裏面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさの比率が、80〜90%である。好適には82〜88%である。比率が90%を超えると、キャリアテープとしたのち通常使用される直径5cm程度のカセットリールや管に捲き取る際や、捲き戻されて使用される際などに、キャリアテープの表面に折れやしわが生じるようになり、比率が80%未満であるとキャリアテープとしたときの剛性が不足し、曲げ、しごきの力に対して、キャリアテープ裏面に折れが発生して、その部分の表面に、折れやしわが発生するようになる。ここで、表面側から裏面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさは、78mN・m以上、好適には85mN・m以上、140mN・m未満とするのが望ましい。また、裏面側から表面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさは、87mN・m以上、好適には95mN・m以上、155mN・m未満とするのが望ましい。 On the other hand, the carrier tape paper of the present invention applied a load from the front surface side to the back surface side against the stiffness in the paper vertical direction defined in JIS-P8125 when a load was applied from the back surface side to the front surface side. The ratio of stiffness in the vertical direction of the paper defined in JIS-P8125 is 80 to 90%. Preferably it is 82 to 88%. If the ratio exceeds 90%, the carrier tape may fold on the surface of the carrier tape when it is scraped on a cassette reel or tube having a diameter of about 5 cm after being used as a carrier tape or when it is used after being rolled back. When the ratio is less than 80%, the rigidity when the carrier tape is used is insufficient, and the bending of the carrier tape causes bending on the back surface of the carrier tape against the bending and ironing force. Breaks and wrinkles will occur. Here, the stiffness in the longitudinal direction of the paper as defined in JIS-P8125 when a load is applied from the front side to the back side is 78 mN · m or more, preferably 85 mN · m or more and less than 140 mN · m. Is desirable. Further, the stiffness in the vertical direction of the paper as defined in JIS-P8125 when a load is applied from the back side to the front side is 87 mN · m or more, preferably 95 mN · m or more and less than 155 mN · m. Is desirable.
なお、試験片を8mm幅で測定する場合には、表面側から裏面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさは16mN・m以上、好適には17mN・m以上とするのが望ましく、裏面側から表面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさは18mN・m以上、好適には20mN・m以上とするのが望ましい。 When measuring a test piece with a width of 8 mm, the stiffness in the vertical direction of the paper defined in JIS-P8125 when a load is applied from the front side to the back side is 16 mN · m or more, preferably 17 mN. -It is desirable to set it to m or more, and when the load is applied from the back side to the front side, the stiffness in the paper vertical direction defined in JIS-P8125 is 18 mN · m or more, preferably 20 mN · m or more. Is desirable.
キャリアテープ用紙のこわさを本発明の範囲にするにあたっては、表面層、裏面層に水溶性高分子を塗工あるいは含浸させることにより達成するのが簡易で適する。そして、この場合表面層に塗工または含浸された水溶性高分子量に対する、裏面層に塗工または含浸された水溶性高分子量の質量比率が120〜250%とするのが望ましい。表面層、裏面層に塗工あるいは含浸させる水溶性高分子としては、澱粉、ポリビニールアルコール(PVA)、ポリアクリルアミド(PAM)等から、1種又は2種以上の水溶性高分子を使用することができる。なかでも、表面強度やトップカバーテープとの接着性、耐熱性などの点からポリビニールアルコール(PVA)を使用するのが好ましい。 In order to make the stiffness of the carrier tape paper within the scope of the present invention, it is simple and suitable to achieve by applying or impregnating a water-soluble polymer to the surface layer and the back surface layer. In this case, the mass ratio of the water-soluble high molecular weight coated or impregnated on the back surface layer to the water-soluble high molecular weight coated or impregnated on the surface layer is preferably 120 to 250%. As the water-soluble polymer to be coated or impregnated on the surface layer and the back layer, one or more water-soluble polymers from starch, polyvinyl alcohol (PVA), polyacrylamide (PAM), etc. should be used. Can do. Among these, it is preferable to use polyvinyl alcohol (PVA) from the viewpoints of surface strength, adhesion to the top cover tape, heat resistance, and the like.
表面層への塗工または含浸量は、固形分で1.5〜4.0g/m2塗工することが好ましい。より好ましくは1.5〜2.5g/m2である。水溶性高分子の塗工・含浸量が1.5g/m2未満であると、用紙の裏面層側から表面層側へ向かって荷重を掛けた時のこわさに対する、表面層側から裏面層側へ向かって荷重を掛けたときのこわさの比率を80〜90%とすることが難しくなる。また、4.0g/m2を超えると塗工、含浸後の乾燥性が悪化し、生産性が低下するとともに後の工程の汚れを生じる。表裏面各層に水溶性高分子を内添する方法もあるが、コスト面や操業性などから外添するのが好ましい。 The coating or impregnation amount on the surface layer is preferably 1.5 to 4.0 g / m 2 in terms of solid content. More preferably, it is 1.5-2.5 g / m < 2 >. If the coating / impregnation amount of the water-soluble polymer is less than 1.5 g / m 2 , the surface layer side to the back layer side against the stiffness when a load is applied from the back layer side to the surface layer side of the paper It becomes difficult to make the ratio of stiffness when applying a load toward 80 to 90%. On the other hand, if it exceeds 4.0 g / m 2 , the drying property after coating and impregnation is deteriorated, the productivity is lowered and soiling in the subsequent step is caused. Although there is a method of internally adding a water-soluble polymer to each of the front and back layers, it is preferable to externally add from the viewpoint of cost and operability.
特に、裏面層に対する塗工・含浸量は、固形分で0.5〜2.0g/m2とするのが好ましい。より好ましくは0.5〜1.5g/m2である。裏面層への塗工・含浸量が0.5g/m2未満であると、キャリアテープとしたときの表面強度、層間強度が不足するおそれがある。2.0g/m2を超えると、こわさの比率を上記範囲(80〜90%)とすることが難しくなる。また、塗工・含浸後の乾燥性が悪化し、生産性が低下するとともに後の工程で汚れが生じることもある。 In particular, the coating / impregnation amount for the back layer is preferably 0.5 to 2.0 g / m 2 in terms of solid content. More preferably, it is 0.5-1.5 g / m < 2 >. If the coating / impregnation amount on the back layer is less than 0.5 g / m 2 , the surface strength and interlayer strength of the carrier tape may be insufficient. When it exceeds 2.0 g / m 2 , it becomes difficult to set the stiffness ratio within the above range (80 to 90%). Moreover, the drying property after coating and impregnation is deteriorated, the productivity is lowered, and dirt may be produced in the subsequent process.
水溶性高分子を表面層、裏面層へ塗工・含浸するために用いる塗工装置は特に限定されるものではなく、例えばエアナイフコーター、ブレードコーター、ロッドコーター、バーコーター及びゲートロールコーター、サイズプレス等のロールコーター、ベルバパコーター、カレンダー塗工等を適宜使用することができる。 The coating apparatus used for coating / impregnating the water-soluble polymer on the surface layer and the back layer is not particularly limited. For example, air knife coater, blade coater, rod coater, bar coater, gate roll coater, size press A roll coater such as velvapa coater, calendar coating and the like can be used as appropriate.
裏面層への塗工・含浸量を、表面層への塗工・含浸量よりも少なくするにあたっては、例えば、表裏層に塗工・含浸させる塗工液中の水溶性高分子濃度に変化をもたせたり、各層に対する塗工回数を異ならしめたりすればよい。例えば、カレンダー塗工機によって表面層に2回塗工し、裏面層に1回塗工するなどすればよい。 In order to reduce the amount of coating / impregnation to the back layer to less than the amount of coating / impregnation to the front layer, for example, change the concentration of water-soluble polymer in the coating solution to be coated / impregnated on the front and back layers. It may be provided or the number of coatings for each layer may be made different. For example, it may be applied to the surface layer twice by a calender coating machine and once to the back layer.
水溶性高分子を塗工・含浸させた後には、カレンダー装置にて表裏面を平滑化処理することができる。表面平滑化処理するためのカレンダー装置としては特に限定されるものではなく、例えばマシンカレンダー、ソフトカレンダー、又はヤンキードライヤー等が適宜使用される。表面平滑化処理は、JIS P 8151 プリント・サーフ試験機法(面積式流量計形プリント・サーフ試験機)にて、ソフトバッキングを用いてクランプ装置のバッキングを1.0MPAとして測定したときの平滑度が5.0〜8.0μmとなるようにするのが望ましい。 After coating and impregnating the water-soluble polymer, the front and back surfaces can be smoothed by a calendar device. The calendar device for performing the surface smoothing treatment is not particularly limited, and for example, a machine calendar, a soft calendar, a Yankee dryer, or the like is used as appropriate. Surface smoothing treatment is smoothness when the backing of the clamping device is measured as 1.0 MPA using soft backing in accordance with JIS P 8151 print surf tester method (area type flow meter type print surf tester). Is preferably 5.0 to 8.0 μm.
さらに、本発明のキャリアテープ用紙では、表面層の、TAPPI T459 om−83に準じて測定した表面強度が12A以上であるの好ましく、14Aであるのがより好ましい。表面強度を12A以上とするためには、原料配合率や原料パルプスラリーのスリーネス、水溶性高分子を塗工・含浸するなどの方法により達成することができる。トップカバーテープを接着する側の表面の表面強度が12A未満の場合には、トッパカバーテープを剥離する工程にて、キャリアテープ用紙表面のパルプ繊維がとられ、紙粉となって操業性を悪化させる原因となる。 Furthermore, in the carrier tape paper of the present invention, the surface strength of the surface layer measured according to TAPPI T459 om-83 is preferably 12A or more, and more preferably 14A. In order to make the surface strength 12A or more, it can be achieved by a method such as coating / impregnation with a raw material blending ratio, a raw pulp slurry's threeness, and a water-soluble polymer. When the surface strength of the surface to which the top cover tape is bonded is less than 12A, the pulp fiber on the surface of the carrier tape paper is taken in the process of peeling the topper cover tape, and it becomes paper dust and deteriorates operability. Cause it.
以上詳述のキャリアテープ用紙は、15〜20cm程度の幅の中原反に裁断したのちに、製品巾(例えば8mm巾)に裁断し、パンチ加工やエンボス加工等の適宜の加工をほどこして搬送対象部品収納用のキャビティ部やテープ送り用のマージナル部等を形成し、本発明のキャリアテープとする。 The carrier tape paper described in detail above is cut into a medium thickness of about 15 to 20 cm, then cut into a product width (for example, 8 mm width), and subjected to appropriate processing such as punching or embossing to be conveyed. A cavity portion for storing components, a marginal portion for tape feeding, and the like are formed to obtain the carrier tape of the present invention.
次に、本発明の実施例と比較例を説明することにより本発明の効果を明らかにする。なお、当然、本発明を以下の実施例のものに限定する趣旨ではない。また、以下の試験例においては、特に説明しない限り、「部」及び「%」とは、それぞれ「質量部」及び「質量%」を意味し、「kg/t」とは、パルプトンあたりの量(kg)を意味する。 Next, the effects of the present invention will be clarified by describing examples and comparative examples of the present invention. Of course, the present invention is not intended to be limited to the following examples. In the following test examples, unless otherwise noted, "parts" and "%" respectively mean "parts by weight" and "% by mass", and "kg / t" per Paruputon Means amount (kg).
〔実施例1〕
表面層及び裏面層については、針葉樹晒クラフトパルプ(NBKP)15%、広葉樹晒クラフトパルプ(LBKP)85%からなるフリーネス420mlのパルプスラリーに、サイズ剤(近代化学工業株式会社製R50)を固形分換算で0.25%、PAM(ハリマ化成株式会社製、ハーマイドB−15)を固形分換算で0.15%内添し、硫酸バンドを添加してPHを5に調整した原料を使用した。
一方、中間層(2〜4層)としては、NBKP50%、LBKP40%、サーモメカニカルパルプ(TMP)10%からなるフリーネス410mlのパルプスラリーに、サイズ剤(近代化学工業株式会社製R50)を固形分換算で0.30%、PAM(ハリマ化成株式会社製、ハーマイドB−15)を固形分換算で0.5%内添し、硫酸バンドを添加してPHを5に調整した原料を使用した。
これらを円網多層抄紙機にて、表面層の付け量を60g/m2、中間層(2〜4層)の付け量を460g/m2、裏面層の付け量を60g/m2として、5層構造で抄き合わせ、PVA(日本合成化学株式会社製、ゴーセノールN300)をカレンダー塗工で表面に塗工量1.0g/m2、裏面に1.0g/m2塗工してキャリアテープ用紙を得た。
[Example 1]
For the surface layer and the back layer, sizing agent (R50 manufactured by Modern Chemical Industry Co., Ltd.) is added to the pulp slurry of 420 ml freeness consisting of 15% softwood bleached kraft pulp (NBKP) and 85% hardwood bleached kraft pulp (LBKP). A raw material in which 0.25% in terms of conversion and 0.15% in terms of solid content of PAM (manufactured by Harima Kasei Co., Ltd., Hermide B-15) was internally added, and a pH adjusted to 5 by adding a sulfuric acid band was used.
On the other hand, as an intermediate layer (2-4 layers), a sizing agent (R50 manufactured by Modern Chemical Industry Co., Ltd.) is added to a pulp slurry of 410 ml of freeness composed of NBKP 50%, LBKP 40%, and thermomechanical pulp (TMP) 10%. A raw material having 0.30% in terms of conversion and 0.5% PAM (Harmide B-15, manufactured by Harima Kasei Co., Ltd.) in terms of solid content and adjusting the pH to 5 by adding a sulfuric acid band was used.
At these round net multilayer paper machine, with the amount of 60 g / m 2 of the surface layer, 460 g / m 2 Paste amount of the intermediate layer (2-4 layers), Paste amount of the back layer as a 60 g / m 2, A sheet of paper with a five-layer structure, PVA (manufactured by Nippon Synthetic Chemical Co., Ltd., Gohsenol N300) is calendered and coated on the surface with a coating amount of 1.0 g / m 2 and on the back surface with 1.0 g / m 2. Tape paper was obtained.
〔実施例2〜5〕
表面層表面に塗工するPVAの塗工量を表1に示す値に調整したことを除き、その他の点を実施例1と同様にしてキャリアテープ用紙を得た。
[Examples 2 to 5]
A carrier tape paper was obtained in the same manner as in Example 1 except that the amount of PVA applied to the surface layer surface was adjusted to the values shown in Table 1.
〔実施例6〜12〕
中間層に使用する原料パルプ配合率を表1に示す値に調整したことを除き、その他の点を実施例1と同様にしてキャリアテープ用紙を得た。
[Examples 6 to 12]
A carrier tape paper was obtained in the same manner as in Example 1 except that the raw material pulp content used in the intermediate layer was adjusted to the values shown in Table 1.
〔実施例13〜18〕
表面層、裏面層、および中間層に使用するパルプスラリーのフリーネスを表1に示した値としたことを除き、その他の点を実施例1と同様にしてキャリアテープ用紙を得た。
[Examples 13 to 18]
A carrier tape paper was obtained in the same manner as in Example 1 except that the freeness of the pulp slurry used for the front surface layer , the back surface layer , and the intermediate layer was set to the values shown in Table 1.
〔実施例19〜23〕
表面層、裏面層に使用する原料パルプの配合率を表1に示す値に調整したことを除き、その他の点を実施例1と同様にしてキャリアテープ用紙を得た。
[Examples 19 to 23]
A carrier tape paper was obtained in the same manner as in Example 1 except that the blending ratio of the raw material pulp used for the surface layer and the back surface layer was adjusted to the values shown in Table 1.
〔比較例1〜2〕
表面層表面に塗工するPVAの塗工量を表1に示す値に調整したことを除き、その他の点を実施例1と同様にしてキャリアテープ用紙を得た。
[Comparative Examples 1-2]
A carrier tape paper was obtained in the same manner as in Example 1 except that the amount of PVA applied to the surface layer surface was adjusted to the values shown in Table 1.
以上の実施例および比較例について米坪、厚さ、こわさ、平滑度、表面強度、層間強度の物性測定と、折れについて評価試験を行った。結果は、表1中に示す。なお、物性測定およびこの評価試験は、JIS−P8111に準拠して温度23℃±1℃、湿度50±2%の環境条件で行った。 About the above Example and the comparative example, the evaluation test was done about the physical-property measurement of a tsubo, thickness, stiffness, smoothness, surface strength, and interlayer strength, and a crease. The results are shown in Table 1. The physical property measurement and this evaluation test were performed under environmental conditions of a temperature of 23 ° C. ± 1 ° C. and a humidity of 50 ± 2% in accordance with JIS-P8111.
各測定方法および試験方法についての詳細は以下のとおりである。
(厚さ)
JIS P 8118 紙及び板紙−厚さ及び密度の試験方法に準じて厚さを測定した。
Details of each measurement method and test method are as follows.
(thickness)
JIS P 8118 Paper and paperboard—Thickness was measured according to thickness and density test methods.
(こわさ)
JIS P 8125 紙及び板紙−こわさ試験方法−テーバーこわさ試験機法に準じて縦方向のこわさを測定した。表中では、表面側から裏面側へ向かって荷重を掛けた時の縦方向のこわさを(X)とし、裏面側から表面側へ向かって荷重を掛けた時の縦方向のこわさを(Y)とした。
(Stiffness)
In accordance with JIS P 8125 paper and paperboard-stiffness test method-Taber stiffness tester method, the stiffness in the vertical direction was measured. In the table, (X) is the vertical stiffness when a load is applied from the front side to the back side, and (Y) is the vertical stiffness when a load is applied from the back side to the front side. It was.
(平滑度)
JIS P 8151 紙及び板紙−表面粗さ及び平滑度試験方法(エア・リーク法)−プリント・サーフ試験機法(面積式流量計形プリント・サーフ試験機)にて、ソフトバッキングを用い、クランプ装置のバッキングを1.0MPAとして表面、裏面それぞれの平滑度を測定した。
(Smoothness)
JIS P 8151 Paper and paperboard-Surface roughness and smoothness test method (air leak method)-Print surf tester method (area type flow meter type print surf tester), using soft backing, clamping device The smoothness of each of the front and back surfaces was measured with a backing of 1.0MPA.
(表面強度)
TAPPI T459 om−83に基づき、表面側、裏面側のそれぞれの表面強度を測定した。
(Surface strength)
Based on TAPPI T459 om-83, the surface strengths on the front and back sides were measured.
(層間強度)
TAPPI UM522に従い、Z軸方向の層間強度を測定した。
(Interlayer strength)
According to TAPPI UM522, the interlayer strength in the Z-axis direction was measured.
(各層の分離方法)
抄紙後の用紙の各層の物性を測定すべく、抄紙後の用紙から次記の方法で各層に分離した。まず、試料を室温の水に約1時間浸漬したのち、試料の角を起点として10mmΦ程度の丸棒に捲き付け、その状態で丸棒を転がして試料をしごく。この操作を試料の四隅の全ての角を起点に繰り返し、各方向から試料にしごきの力を加える。これにより、試料の層間の一部が剥離してくるので、これを利用して、試料を表面層、中間層、及び裏面層に分離する。
(Separation method of each layer)
In order to measure the physical properties of each layer of the paper after paper making, each layer was separated from the paper after paper making by the following method. First, after immersing the sample in water at room temperature for about 1 hour, the sample is rubbed on a round bar of about 10 mmΦ starting from the corner of the sample, and the round bar is rolled in this state to squeeze the sample. This operation is repeated starting from all four corners of the sample, and an ironing force is applied to the sample from each direction. As a result, a part of the layer between the samples is peeled off, and this is used to separate the sample into a front surface layer , an intermediate layer , and a back surface layer .
(フリーネス)
分離された各層を裁断して約3cm2、約25gの試験片とし、この試験片を1リットルの水に24時間浸漬したのちにJIS−P8220に基づき標準離解機で15分間離解処理し、試験片が完全に離解していることを目視で確認した後、JIS−P8121に準拠してカナダ標準濾水度試験機にて測定した。
(Freeness)
Each separated layer is cut to obtain a test piece of about 3 cm 2 and about 25 g. After the test piece is immersed in 1 liter of water for 24 hours, it is subjected to a disaggregation treatment for 15 minutes with a standard disintegrator based on JIS-P8220. After visually confirming that the piece was completely disaggregated, it was measured with a Canadian standard freeness tester according to JIS-P8121.
(折れ)
折れの評価は、流れ方向30cm、幅8mmのサンプルを10本用意し、直径6cmの円柱に捲きつけ、折れの発生個数を目視判定し、1本のあたりの平均個数を次の基準で評価した。評価は、1個未満を◎、1個以上2個未満を○、2以上5個未満△、5個以上を×と評価した。
(Break)
For the evaluation of folding, ten samples having a flow direction of 30 cm and a width of 8 mm were prepared, placed on a cylinder having a diameter of 6 cm, the number of occurrences of folding was visually determined, and the average number per one was evaluated according to the following criteria. . In the evaluation, less than 1 was evaluated as ◎, 1 or more and less than 2 as ○, 2 or more and less than 5 Δ, and 5 or more as ×.
表1から、本発明のキャリアテープ用紙である実施例1〜23は品質評価に優れることが分かる。それに対して、比較例1〜2は、品質評価において実施例1〜23よりも劣る結果となっている。してみると、本発明のキャリアテープ用紙からは、カセットリールや管に捲き取るときや捲き取り後に、折れやしわの発生が防止されているといえる、これにより、トップテープを安定的に剥離することができ、電子部品取り出し時の安定性に優れ、生産効率のよいキャリアテープを得ることができるといえる。 From Table 1, it can be seen that Examples 1 to 23, which are carrier tape sheets of the present invention, are excellent in quality evaluation. On the other hand, Comparative Examples 1-2 are inferior to Examples 1-23 in quality evaluation. As a result, it can be said that the carrier tape sheet of the present invention prevents creases and wrinkles from occurring when the cassette tape or tube is scraped off or after scraping. It can be said that it is possible to obtain a carrier tape that is excellent in stability at the time of taking out an electronic component and has high production efficiency.
本発明は、電子回路を製造する際に使用する、チップ状の表面実装電子部品を収納し、表面実装機(マウンター)に搬送するためのキャリアテープおよびこれに用いるキャリアテープ用紙に関する。 The present invention relates to a carrier tape for storing chip-shaped surface-mounted electronic components and transporting them to a surface-mounting machine (mounter) and a carrier tape sheet used therefor, which are used when manufacturing an electronic circuit.
電子機器の自動生産を行うにあたっては、表面実装タイプの電子部品を表面実装機により基板に自動装着する技術が用いられる。表面実装機に対して電子部品を供給するためには、電子部品収納用のキャビティ部と表面実装機内への送り用のマージナル部とを備える幅6〜9mm、基紙厚0.4〜1.0mmのキャリアテープが用いられている。特に一般的には幅8mm、厚さが0.7〜1.0mmのものがよく用いられる。
このキャリアテープは、紙製およびプラスチック製のものがあるが、コスト安であり、軽量であり、廃棄容易であり、非帯電性であることから紙製とするのが望ましいとされている。
キャリアテープの具体的な形態としては、部品収納用のキャビティ部とキャリアテープ送り用のマージナル部とが貫通孔であり、表面実装部品を収納した状態で、表面がトップカバーテープでシールされ、下面がボトムテープによりシールされるパンチキャリアテープや、キャビティ部がエンボス加工により形成された凹部であり、表面のみがトップカバーテープでシールされるエンボスキャリアテープや、表面実装部品の挿入直前にこれらキャビティ部等を形成するアンパンチキャリアテープなどが知られる。
これらのキャリアテープはキャビティ部に電子部品が装填されトップカバーテープでシールされた状態で、直径5cm程度のカセットリールに捲きつられた状態(レコード巻方式)、あるいは直径20cm程度巾10cm程度の紙管にスパイラル状に捲きつられた状態(トラバース巻)で出荷され、最終ユーザーが表面実装機に装着して使用される。
近年では、レコード巻方式と比較して1巻当りの巻長さを長くすることができるために継ぎ手作業が軽減され、電子部品装填工程の高速化及び作業効率向上のメリットがあるトラバース巻方式が多用されるようになっている。
There are paper and plastic carrier tapes. However, it is desirable that the carrier tape be made of paper because of its low cost, light weight, easy disposal, and non-charging properties.
As a specific form of the carrier tape, the cavity portion for storing the component and the marginal portion for feeding the carrier tape are through holes, and the surface is sealed with the top cover tape in the state where the surface mount component is stored, and the bottom surface. Is a punch carrier tape that is sealed with a bottom tape, or an embossed carrier tape whose cavity part is formed by embossing and whose surface is sealed with a top cover tape. An unpunched carrier tape or the like is known.
These carrier tapes are loaded with electronic parts in the cavity and sealed with a top cover tape, and are wound around a cassette reel having a diameter of about 5 cm (record winding method), or a paper tube having a diameter of about 20 cm and a width of about 10 cm. It is shipped in a state of being wound in a spiral shape (traverse winding), and used by the end user by mounting it on a surface mounter.
In recent years, the traverse winding method has the advantages of reducing the joint work because the winding length per turn can be increased compared to the record winding method, speeding up the electronic component loading process, and improving work efficiency. It has come to be used frequently.
しかしながら、従来キャリアテープは、カセットリール等に捲き付ける際に、リールあるいは管の外周面に沿って湾曲せずに折れてしまうことがあった。
折れの現象は一般的に用いられる紙厚が700μm以上のもので顕著となり、またカセットリール径が5〜6cmと小径の場合に顕著となる。そして、このように折れが生ずると、その折れ部分の表面に凸部が発現し、この凸部が次工程の表面実装機のガイド部分に引っ掛かって部品を表面実装機内に安定して装填することができない。また、表面実装機では、トップシールを一定張力で引張しつつキャリアテープから剥離してキャビティ内の電子部品を取り出すが、キャリアテープが折れるとその折れ部分でキャリアテープからトップカバーシールが剥離して浮いてしまう。そうすると、表面実装機がトップカバーシールを一定張力で引張することができず、表面実装機に引っ張られるキャリアテープがばたつきキャビティ内の電子部品の脱落や所望位置への装填ができなくなる。
そこで、本発明の解決課題は、厚さ700μm以上の多層抄き板紙を効率良く生産することができ、かつ、リール捲き付け時あるいは捲き付け状態において、折れの発生が防止されたキャリアテープおよびキャリアテープ用紙を提供することにある。
However, when a conventional carrier tape is rubbed against a cassette reel or the like, the carrier tape may be bent without being bent along the outer peripheral surface of the reel or tube.
The phenomenon of folding becomes significant when the generally used paper thickness is 700 μm or more, and becomes remarkable when the cassette reel diameter is as small as 5 to 6 cm. And when a fold occurs in this way, a convex portion appears on the surface of the fold portion, and this convex portion is hooked on the guide portion of the surface mounting machine in the next process to stably load the component into the surface mounting machine. I can't. In surface mounters, the top seal is pulled from the carrier tape while pulling it at a constant tension, and the electronic components inside the cavity are taken out. However, when the carrier tape is broken, the top cover seal is peeled from the carrier tape at the folded portion. It will float. As a result, the surface mounter cannot pull the top cover seal with a constant tension, and the carrier tape pulled by the surface mounter flutters, and the electronic components in the cavity cannot be detached or loaded at a desired position.
SUMMARY OF THE INVENTION Accordingly, a problem to be solved by the present invention is that a carrier tape and a carrier capable of efficiently producing a multilayer paperboard having a thickness of 700 μm or more, and preventing the occurrence of folds at the time of reel winding or in the winding state. To provide tape paper.
上記課題を解決した本発明は次記のとおりである。
<請求項1記載の発明>
巻取りの外面となる表面層と、巻取りの内面となる裏面層と、それらの間の中間層を有する多層抄きのキャリアテープ用紙であって、
紙厚が700〜1200μmであり、
表面層および裏面層に水溶性高分子が塗工または含浸され、
裏面層に塗工または含浸された水溶性高分子量に対する、表面層に塗工または含浸された水溶性高分子量の質量比率が120〜250%であり、かつ
裏面側から表面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさに対する、表面側から裏面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさの比率が、82〜88%である、ことを特徴とするキャリアテープ用紙。
The present invention that has solved the above problems is as follows.
<Invention of Claim 1>
A multi-layered carrier tape paper having a surface layer as an outer surface of winding, a back layer as an inner surface of winding, and an intermediate layer therebetween,
The paper thickness is 700-1200 μm,
The surface layer and the back layer are coated or impregnated with a water-soluble polymer,
The weight ratio of the water-soluble polymer coated or impregnated on the surface layer to the water-soluble polymer coated or impregnated on the back layer is 120 to 250%, and a load is applied from the back side to the surface side. The ratio of the vertical stiffness of the paper defined in JIS-P8125 when a load is applied from the front side to the back side with respect to the vertical stiffness of the paper defined in JIS-P8125 when applied is 82 to Carrier tape paper characterized by 88%.
<請求項2記載の発明>
中間層に機械パルプが5〜30%含有されている、請求項1記載のキャリアテープ用紙。
<Invention of Claim 2>
The carrier tape paper according to claim 1, wherein the intermediate layer contains 5 to 30% of mechanical pulp.
<請求項3記載の発明>
隣接する層間のJIS−P8121に基づくカナダ標準濾水度の差が50cc以下である請求項1又は2記載のキャリアテープ用紙。
<Invention of Claim 3>
The carrier tape paper according to claim 1 or 2, wherein a difference in Canadian standard freeness based on JIS-P8121 between adjacent layers is 50 cc or less.
<請求項4記載の発明>
請求項1〜3記載のキャリアテープ用紙に対し、搬送対象部品収納用のキャビティ部とテープ送り用のマージナル部を加工形成してなる、ことを特徴とするキャリアテープ。
<Invention of Claim 4>
4. A carrier tape, comprising: a carrier tape storage cavity part and a tape feeding marginal part formed on the carrier tape sheet according to claim 1;
本発明に係るキャリアテープ用紙は、多層抄きで各層間にある程度の一体性があり、さらに表裏面層間におけるこわさに適当な差を設けたことにより、キャリアテープとしてリール等に捲き付け時に、リールあるいは管に捲き付ける時あるいは捲き付けた状態において、巻取り内面に向いた側の折れの発生が格段に防止される。 The carrier tape paper according to the present invention has a certain degree of integrity between the layers in the multi-layer paper making, and further, by providing an appropriate difference in stiffness between the front and back layers, Alternatively, the occurrence of folds on the side facing the take-up inner surface is greatly prevented when the tube is rubbed against the tube or in the rubbed state.
そして、水溶性高分子の塗布、含浸により表裏面層間のこわさの差を好適に発生させることができる。 Then, a difference in stiffness between the front and back surfaces can be suitably generated by applying and impregnating the water-soluble polymer.
また、中間層に機械パルプが5〜30%含有されていると地合が良好になり、地合ムラによる折れ起点の発生が防止される。さらに機械パルプは、中間層の柔軟性も向上され、表裏面層間のこわさの差による作用効果をいっそう発揮させやすくなる。 Moreover, when 5-30% of mechanical pulp is contained in the intermediate layer, the formation becomes good, and the occurrence of the folding start point due to uneven formation is prevented. Furthermore, the mechanical pulp also improves the flexibility of the intermediate layer, making it easier to exert the effect of the difference in stiffness between the front and back layers.
さらに、隣接する各層のJIS−P8121に基づくカナダ標準濾水度(以下、単にフリーネスともいう)の差が50cc以下であると、隣接する各層間の繊維の絡み合いが良く、層間強度が高く、リール等に捲き付ける時あるいは捲き付けた状態における巻面に折れや各層間の分離の発生が防止される。 Furthermore, if the difference in Canadian standard freeness (hereinafter also simply referred to as “freeness”) based on JIS-P8121 of each adjacent layer is 50 cc or less, the entanglement of fibers between adjacent layers is good, the interlayer strength is high, and the reel Occurrence of folds on the winding surface and separation between the layers when it is rubbed or the like is prevented.
以上の本発明のキャリアテープ用紙からなるキャリアテープは、折れが極めて発生しづらいなどの利点があり、トップテープを安定的に剥離することができ、電子部品取り出し時の安定生産に優れ生産効率の向上に寄与する。 The carrier tape made of the carrier tape sheet of the present invention has advantages such as being extremely difficult to bend, and the top tape can be stably peeled off. Contributes to improvement.
本発明の実施の形態を、具体例を示しながら以下に詳説する。
本発明のキャリアテープ用紙は、多層抄きで製造される表面層、中間層、裏面層を備える用紙であればよく、3層構造に限らず中間層を複数層有する4層あるいはそれ以上の多層構造であってもよい。ここで、多層抄きとするのは、各層間でパルプ繊維同士に適度な絡みあいが生ずるため各層の適度な一体性が得られるからである。また、多層抄きでは、各層の原料の構成を自由にでき、例えば、古紙パルプを中間層に配合しつつ表面層および裏面層にバージンパルプを使用することが容易で、リサイクルに貢献する古紙パルプを使用しつつ品質の確保を達成しやすいといった利点がある。
Embodiments of the present invention will be described in detail below with specific examples.
The carrier tape paper of the present invention may be a paper having a surface layer, an intermediate layer, and a back layer manufactured by multilayer papermaking, and is not limited to a three-layer structure, but a multilayer of four or more layers having a plurality of intermediate layers. It may be a structure. Here, the reason for making the multi-layer paper is that moderate entanglement between the pulp fibers occurs between the layers, so that appropriate integrity of the layers can be obtained. In addition, in the multi-layer papermaking, the composition of the raw material of each layer can be made freely. For example, it is easy to use virgin pulp for the front and back layers while blending the used paper pulp in the intermediate layer, and contribute to recycling. There is an advantage that it is easy to achieve quality assurance while using.
ここで、本発明に係るキャリアテープ用紙の各層に用いる原料パルプとしては、例えば、広葉樹晒クラフトパルプ(LBKP)、針葉樹晒クラフトパルプ(NBKP)、広葉樹未晒クラフトパルプ(LUKP)、針葉樹未晒クラフトパルプ(NUKP)、広葉樹半晒クラフトパルプ(LSBKP)、針葉樹半晒クラフトパルプ(NSBKP)、広葉樹亜硫酸パルプ、針葉樹亜硫酸パルプ等の化学パルプ、ストーングランドパルプ(SGP)、加圧ストーングランドパルプ(PGW)、リファイナーグランドパルプ(RGP)、サーモメカニカルパルプ(TMP)、ケミグランドパルプ(CGP)、砕木パルプ(GP)、サーモメカニカルパルプ(TMP)等の機械パルプ、茶古紙、クラフト封筒古紙、雑誌古紙、新聞古紙、チラシ古紙、オフィス古紙、段ボール古紙、上白古紙、ケント古紙、模造古紙、地券古紙等から製造される離解古紙パルプ、離解・脱墨古紙パルプ、または離解・脱墨・漂白古紙パルプ、あるいは、ケナフ、麻、葦等の非木材繊維から化学的にまたは機械的に製造されたパルプ等の公知の種々のパルプを一種または数種を適宜選択して使用することができる。ただし、表面実装部品への影響を考慮し填料を減少させる必要がある場合は、ディインキングパルプ、ウエストパルプ等の古紙パルプよりもバージンパルプを使用することが好ましい。 Here, as the raw material pulp used for each layer of the carrier tape paper according to the present invention, for example, hardwood bleached kraft pulp (LBKP), softwood bleached kraft pulp (NBKP), hardwood unbleached kraft pulp (LUKP), softwood unbleached kraft Pulp (NUKP), hardwood semi-bleached kraft pulp (LSBKP), softwood semi-bleached kraft pulp (NSBKP), hardwood sulfite pulp, softwood sulfite pulp, etc., chemical stone, stone grand pulp (SGP), pressurized stone grand pulp (PGW) , Refiner Grand Pulp (RGP), Thermomechanical Pulp (TMP), Chemi-Grand Pulp (CGP), Ground Pulp (GP), Thermomechanical Pulp (TMP), etc. Mechanical Pulp, Tea Waste Paper, Craft Envelope Waste Paper, Magazine Waste Paper, Newspaper Waste paper, flyer waste paper, off Waste paper, corrugated waste paper, Koji white waste paper, Kent waste paper, imitation waste paper, waste paper waste paper, etc. One or several kinds of known various pulps such as pulps chemically or mechanically produced from non-wood fibers such as straw can be appropriately selected and used. However, when it is necessary to reduce the filler in consideration of the influence on the surface mount component, it is preferable to use virgin pulp rather than used paper pulp such as diinking pulp and waist pulp.
特にキャリアテープ用紙の表面層、裏面層においては、その役割、各種品質特性等をバランスよく、効率的に達成するために、LBKP、NBKPが適する。特に、LBKPを70〜95質量%含有することが好ましい。LBKPの含有量が70〜95質量%であると、キャリアテープ用紙として必要な表面強度や剛度を保ちながら、良好な地合いが得られるとともに、トップシールテープとの接着性がより良好となり、トップシールテープを剥離する際に安定したピールオフ強度がることができる。なお、表面層の原料パルプのLBKPの含有量が70質量%未満であると、良好な地合いを得ることが難しくなり、トップシールテープとの接着性にバラツキが生じやすく、トップシールテープを剥離する際にキャリアテープの走行が安定しないことがあり、生産効率が低下するおそれもある。一方、LBKPの含有量が95質量%を超えると、表面強度や剛度が低下し、トップシールテープを剥離する際に毛羽立ちや紙粉が発生し、生産効率が低下する原因となる。 In particular, LBKP and NBKP are suitable for the front surface layer and the back surface layer of the carrier tape paper in order to achieve their roles and various quality characteristics in a balanced and efficient manner. In particular, it is preferable to contain 70 to 95% by mass of LBKP. When the content of LBKP is 70 to 95% by mass, while maintaining the surface strength and rigidity necessary for carrier tape paper, a good texture can be obtained and the adhesiveness to the top seal tape becomes better, and the top seal A stable peel-off strength can be obtained when the tape is peeled off. In addition, when the content of LBKP in the raw material pulp of the surface layer is less than 70% by mass, it becomes difficult to obtain a good texture, the adhesiveness with the top seal tape tends to vary, and the top seal tape is peeled off. In some cases, the running of the carrier tape may not be stable, and production efficiency may be reduced. On the other hand, when the content of LBKP exceeds 95% by mass, the surface strength and the rigidity are lowered, and when the top seal tape is peeled off, fluffing and paper dust are generated, which causes a decrease in production efficiency.
特に中間層においては、その役割、リサイクルへの寄与、各種品質特性等をバランスよく、効率的に達成するために、機械パルプが適する。機械パルプとしては、グランドウッドパルプ(GP)、サーモメカニカルパルプ(TMP)、ケミサーモメカニカルパルプ(CTMP)、プレッシャライズドグランドウッドパルプ(PGW)などを使用することができる。これら機械パルプの中でも結束繊維や紙粉の発生が少ないサーモメカニカルパルプ(TMP)、プレッシャライズドグランドウッドパルプ(PGW)が好ましい。 In particular, in the intermediate layer, mechanical pulp is suitable for achieving its role, contribution to recycling, various quality characteristics, etc. in a balanced and efficient manner. As the mechanical pulp, grandwood pulp (GP), thermomechanical pulp (TMP), chemithermomechanical pulp (CTMP), pressured groundwood pulp (PGW), or the like can be used. Among these mechanical pulps, thermomechanical pulp (TMP) and pressured ground wood pulp (PGW) that generate less binding fibers and paper dust are preferable.
また、機械パルプの含有量は5%以上が好ましく、更には10%以上とすることが中間層にクッション性を持たせ、表面の折れ、しわを防止する点でより好ましい。配合量が多いと、強度が低くなり、断面からの紙粉発生や中間層での層間剥離の懸念があるため、30%以下が好ましい。なお、抄紙後の中間層の機械パルプ量は、JIS−P8120に記載の「紙、板紙及びパルプ繊維組成試験方法」により特定できる。 Further, the content of mechanical pulp is preferably 5% or more, and more preferably 10% or more from the viewpoint of imparting cushioning properties to the intermediate layer and preventing surface folding and wrinkling. When the blending amount is large, the strength is lowered, and there is a concern about generation of paper dust from the cross section or delamination in the intermediate layer, so 30% or less is preferable. In addition, the mechanical pulp amount of the intermediate layer after papermaking can be specified by “Paper, paperboard and pulp fiber composition test method” described in JIS-P8120.
一方、中間層に機械パルプを含有するにあたり、中間層の原料として古紙パルプを使用することができる。古紙パルプとしては、茶古紙、クラフト封筒古紙、雑誌古紙、新聞古紙、チラシ古紙、オフィス古紙、段ボール古紙、上白古紙、ケント古紙、模造古紙、地券古紙等から製造される離解古紙パルプ、離解・脱墨古紙パルプ、または離解・脱墨・漂白古紙パルプ等を使用することができる。これらの古紙パルプの中でも、特に中間層の原料としては、キャリアテープ用紙としての各種品質特性をバランスよく、効率的に得るために、表面強度や剛度、引張強度や層間強度などが高く、かつ機械パルプを含みクッション性に優れる、オフィス古紙、茶古紙、クラフト封筒古紙から製造される古紙パルプを用いることが好ましい。 On the other hand, when the intermediate layer contains mechanical pulp, waste paper pulp can be used as a raw material for the intermediate layer. Used paper pulp includes tea waste paper, kraft envelope waste paper, magazine waste paper, newspaper waste paper, flyer waste paper, office waste paper, corrugated waste paper, Kamihaku waste paper, Kent waste paper, imitation waste paper, and old paper waste paper, etc.・ Deinked waste paper pulp or disaggregation / deinking / bleached waste paper pulp can be used. Among these waste paper pulps, especially as the raw material of the intermediate layer, in order to obtain various quality characteristics as carrier tape paper in a balanced and efficient manner, the surface strength, rigidity, tensile strength, interlayer strength, etc. are high, and the machine It is preferable to use waste paper pulp produced from office waste paper, tea waste paper, and craft envelope waste paper that contains pulp and has excellent cushioning properties.
他方、本発明のキャリアテープ用紙は、隣接する各層間のフリーネスの差が50cc以下であるのが望ましい。差が50ccを超える場合は、隣接する層のパルプ繊維同士の絡み合いが弱くなり、直径約50mmのコアに捲き取られる際、あるいは捲き戻される際にかかる曲げやしごきの力によって、各層間で剥離が生じてトップシールテープを剥離する際にキャリアテープの走行が安定しないことがある。 On the other hand, the carrier tape sheet of the present invention desirably has a difference in freeness between adjacent layers of 50 cc or less. When the difference exceeds 50 cc, the entanglement between the pulp fibers in adjacent layers becomes weak, and peeling occurs between the layers due to the bending and ironing force applied when the core is wound or wound back by a core having a diameter of about 50 mm. When the top seal tape is peeled off, the running of the carrier tape may not be stable.
なお、本発明にかかる各層のフリーネスは、キャリアテープ用紙を各層に分離し、その後にこれをJIS−P8220に基づいて離解処理して測定した値である。ただし、この値は、原料パルプスラリーのフリーネスとほとんど変わらない。ここで、各層の分離方法としては、キャリアテープ用紙を水に浸漬したのち、しごきの力を加えて層間剥離させればよい。その他の測定層以外の層を削りとるなどしてもよく、要は各層を他の層から分離できる方法であれば特に限定されない。 The freeness of each layer according to the present invention is a value measured by separating the carrier tape paper into each layer and then performing disaggregation processing based on JIS-P8220. However, this value is almost the same as the freeness of the raw pulp slurry. Here, as a method for separating each layer, the carrier tape sheet is immersed in water, and then the delamination is performed by applying a squeezing force. Other layers other than the measurement layer may be scraped off, and the point is not particularly limited as long as each layer can be separated from the other layers.
さらに、各層に用いる原料パルプのフリーネスは300〜500ccとすることが好ましく、350〜450ccとすることがより好ましい。すなわち、フリーネスが300cc未満であると、繊維長が短くなるため、キャリアテープとしたときの折れのおそれが高くなり、フリーネスが500ccを超えると、用紙の表面強度や剛度が低下傾向となるため、紙粉が発生しやすくキャリアテープとして加工適性に劣るようになる。 Furthermore, the freeness of the raw material pulp used for each layer is preferably 300 to 500 cc, and more preferably 350 to 450 cc. That is, if the freeness is less than 300 cc, the fiber length is shortened, so there is a high risk of bending when the carrier tape is used, and if the freeness exceeds 500 cc, the surface strength and stiffness of the paper tends to decrease. Paper dust is likely to be generated, and it becomes inferior in processability as a carrier tape.
なお、本発明における原料パルプあるいはパルプスラリー中には、内添薬品を必要に応じて添加することができる。例えば、硫酸バンド等の薬品定着剤、ロジン等のサイズ剤、ポリアクリルアマイド、澱粉等の紙力増強剤、ポリアマイド等の濾水・歩留り向上剤、ポリアミド、ポリアミン、エピクロルヒドリン等の耐水化剤、消泡剤、塩基性染料、酸性染料、アニオン性直接染料、カチオン性直接染料等の染料等がある。 In addition, an internal additive chemical | medical agent can be added to the raw material pulp or pulp slurry in this invention as needed. For example, chemical fixing agents such as sulfuric acid bands, sizing agents such as rosin, paper strength enhancers such as polyacrylamide and starch, drainage / yield improvers such as polyamide, waterproofing agents such as polyamide, polyamine and epichlorohydrin, Examples include foaming agents, basic dyes, acid dyes, anionic direct dyes, and cationic direct dyes.
他方、本発明のキャリアテープ用紙は、裏面側から表面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさに対する、表面側から裏面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさの比率が、80〜90%である。好適には82〜88%である。比率が90%を超えると、キャリアテープとしたのち通常使用される直径5cm程度のカセットリールや管に捲き取る際や、捲き戻されて使用される際などに、キャリアテープの表面に折れやしわが生じるようになり、比率が80%未満であるとキャリアテープとしたときの剛性が不足し、曲げ、しごきの力に対して、キャリアテープ裏面に折れが発生して、その部分の表面に、折れやしわが発生するようになる。ここで、表面側から裏面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさは、78mN・m以上、好適には85mN・m以上、140mN・m未満とするのが望ましい。また、裏面側から表面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさは、87mN・m以上、好適には95mN・m以上、155mN・m未満とするのが望ましい。 On the other hand, the carrier tape paper of the present invention applied a load from the front surface side to the back surface side against the stiffness in the paper vertical direction defined in JIS-P8125 when a load was applied from the back surface side to the front surface side. The ratio of stiffness in the vertical direction of the paper defined in JIS-P8125 is 80 to 90%. Preferably it is 82 to 88%. If the ratio exceeds 90%, the carrier tape may fold on the surface of the carrier tape when it is scraped on a cassette reel or tube having a diameter of about 5 cm after being used as a carrier tape or when it is used after being rolled back. When the ratio is less than 80%, the rigidity when the carrier tape is used is insufficient, and the bending of the carrier tape causes bending on the back surface of the carrier tape against the bending and ironing force. Breaks and wrinkles will occur. Here, the stiffness in the longitudinal direction of the paper as defined in JIS-P8125 when a load is applied from the front side to the back side is 78 mN · m or more, preferably 85 mN · m or more and less than 140 mN · m. Is desirable. Further, the stiffness in the vertical direction of the paper as defined in JIS-P8125 when a load is applied from the back side to the front side is 87 mN · m or more, preferably 95 mN · m or more and less than 155 mN · m. Is desirable.
なお、試験片を8mm幅で測定する場合には、表面側から裏面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさは16mN・m以上、好適には17mN・m以上とするのが望ましく、裏面側から表面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさは18mN・m以上、好適には20mN・m以上とするのが望ましい。 When measuring a test piece with a width of 8 mm, the stiffness in the vertical direction of the paper defined in JIS-P8125 when a load is applied from the front side to the back side is 16 mN · m or more, preferably 17 mN. -It is desirable to set it to m or more, and when the load is applied from the back side to the front side, the stiffness in the paper vertical direction defined in JIS-P8125 is 18 mN · m or more, preferably 20 mN · m or more. Is desirable.
キャリアテープ用紙のこわさを本発明の範囲にするにあたっては、表面層、裏面層に水溶性高分子を塗工あるいは含浸させることにより達成するのが簡易で適する。そして、この場合表面層に塗工または含浸された水溶性高分子量に対する、裏面層に塗工または含浸された水溶性高分子量の質量比率が120〜250%とするのが望ましい。表面層、裏面層に塗工あるいは含浸させる水溶性高分子としては、澱粉、ポリビニールアルコール(PVA)、ポリアクリルアミド(PAM)等から、1種又は2種以上の水溶性高分子を使用することができる。なかでも、表面強度やトップカバーテープとの接着性、耐熱性などの点からポリビニールアルコール(PVA)を使用するのが好ましい。 In order to make the stiffness of the carrier tape paper within the scope of the present invention, it is simple and suitable to achieve by applying or impregnating a water-soluble polymer to the surface layer and the back surface layer. In this case, the mass ratio of the water-soluble high molecular weight coated or impregnated on the back surface layer to the water-soluble high molecular weight coated or impregnated on the surface layer is preferably 120 to 250%. As the water-soluble polymer to be coated or impregnated on the surface layer and the back layer, one or more water-soluble polymers from starch, polyvinyl alcohol (PVA), polyacrylamide (PAM), etc. should be used. Can do. Among these, it is preferable to use polyvinyl alcohol (PVA) from the viewpoints of surface strength, adhesion to the top cover tape, heat resistance, and the like.
表面層への塗工または含浸量は、固形分で1.5〜4.0g/m2塗工することが好ましい。より好ましくは1.5〜2.5g/m2である。水溶性高分子の塗工・含浸量が1.5g/m2未満であると、用紙の裏面層側から表面層側へ向かって荷重を掛けた時のこわさに対する、表面層側から裏面層側へ向かって荷重を掛けたときのこわさの比率を80〜90%とすることが難しくなる。また、4.0g/m2を超えると塗工、含浸後の乾燥性が悪化し、生産性が低下するとともに後の工程の汚れを生じる。表裏面各層に水溶性高分子を内添する方法もあるが、コスト面や操業性などから外添するのが好ましい。 The coating or impregnation amount on the surface layer is preferably 1.5 to 4.0 g / m 2 in terms of solid content. More preferably, it is 1.5-2.5 g / m < 2 >. If the coating / impregnation amount of the water-soluble polymer is less than 1.5 g / m 2 , the surface layer side to the back layer side against the stiffness when a load is applied from the back layer side to the surface layer side of the paper It becomes difficult to make the ratio of stiffness when applying a load toward 80 to 90%. On the other hand, if it exceeds 4.0 g / m 2 , the drying property after coating and impregnation is deteriorated, the productivity is lowered and soiling in the subsequent step is caused. Although there is a method of internally adding a water-soluble polymer to each of the front and back layers, it is preferable to externally add from the viewpoint of cost and operability.
特に、裏面層に対する塗工・含浸量は、固形分で0.5〜2.0g/m2とするのが好ましい。より好ましくは0.5〜1.5g/m2である。裏面層への塗工・含浸量が0.5g/m2未満であると、キャリアテープとしたときの表面強度、層間強度が不足するおそれがある。2.0g/m2を超えると、こわさの比率を上記範囲(80〜90%)とすることが難しくなる。また、塗工・含浸後の乾燥性が悪化し、生産性が低下するとともに後の工程で汚れが生じることもある。 In particular, the coating / impregnation amount for the back layer is preferably 0.5 to 2.0 g / m 2 in terms of solid content. More preferably, it is 0.5-1.5 g / m < 2 >. If the coating / impregnation amount on the back layer is less than 0.5 g / m 2 , the surface strength and interlayer strength of the carrier tape may be insufficient. When it exceeds 2.0 g / m 2 , it becomes difficult to set the stiffness ratio within the above range (80 to 90%). Moreover, the drying property after coating and impregnation is deteriorated, the productivity is lowered, and dirt may be produced in the subsequent process.
水溶性高分子を表面層、裏面層へ塗工・含浸するために用いる塗工装置は特に限定されるものではなく、例えばエアナイフコーター、ブレードコーター、ロッドコーター、バーコーター及びゲートロールコーター、サイズプレス等のロールコーター、ベルバパコーター、カレンダー塗工等を適宜使用することができる。 The coating apparatus used for coating / impregnating the water-soluble polymer on the surface layer and the back layer is not particularly limited. For example, air knife coater, blade coater, rod coater, bar coater, gate roll coater, size press A roll coater such as velvapa coater, calendar coating and the like can be used as appropriate.
裏面層への塗工・含浸量を、表面層への塗工・含浸量よりも少なくするにあたっては、例えば、表裏層に塗工・含浸させる塗工液中の水溶性高分子濃度に変化をもたせたり、各層に対する塗工回数を異ならしめたりすればよい。例えば、カレンダー塗工機によって表面層に2回塗工し、裏面層に1回塗工するなどすればよい。 In order to reduce the amount of coating / impregnation to the back layer to less than the amount of coating / impregnation to the front layer, for example, change the concentration of water-soluble polymer in the coating solution to be coated / impregnated on the front and back layers. It may be provided or the number of coatings for each layer may be made different. For example, it may be applied to the surface layer twice by a calender coating machine and once to the back layer.
水溶性高分子を塗工・含浸させた後には、カレンダー装置にて表裏面を平滑化処理することができる。表面平滑化処理するためのカレンダー装置としては特に限定されるものではなく、例えばマシンカレンダー、ソフトカレンダー、又はヤンキードライヤー等が適宜使用される。表面平滑化処理は、JIS P 8151 プリント・サーフ試験機法(面積式流量計形プリント・サーフ試験機)にて、ソフトバッキングを用いてクランプ装置のバッキングを1.0MPAとして測定したときの平滑度が5.0〜8.0μmとなるようにするのが望ましい。 After coating and impregnating the water-soluble polymer, the front and back surfaces can be smoothed by a calendar device. The calendar device for performing the surface smoothing treatment is not particularly limited, and for example, a machine calendar, a soft calendar, a Yankee dryer, or the like is used as appropriate. Surface smoothing treatment is smoothness when the backing of the clamping device is measured as 1.0 MPA using soft backing in accordance with JIS P 8151 print surf tester method (area type flow meter type print surf tester). Is preferably 5.0 to 8.0 μm.
さらに、本発明のキャリアテープ用紙では、表面層の、TAPPI T459 om−83に準じて測定した表面強度が12A以上であるの好ましく、14Aであるのがより好ましい。表面強度を12A以上とするためには、原料配合率や原料パルプスラリーのスリーネス、水溶性高分子を塗工・含浸するなどの方法により達成することができる。トップカバーテープを接着する側の表面の表面強度が12A未満の場合には、トッパカバーテープを剥離する工程にて、キャリアテープ用紙表面のパルプ繊維がとられ、紙粉となって操業性を悪化させる原因となる。 Furthermore, in the carrier tape paper of the present invention, the surface strength of the surface layer measured according to TAPPI T459 om-83 is preferably 12A or more, and more preferably 14A. In order to make the surface strength 12A or more, it can be achieved by a method such as coating / impregnation with a raw material blending ratio, a raw pulp slurry's threeness, and a water-soluble polymer. When the surface strength of the surface to which the top cover tape is bonded is less than 12A, the pulp fiber on the surface of the carrier tape paper is taken in the process of peeling the topper cover tape, and it becomes paper dust and deteriorates operability. Cause it.
以上詳述のキャリアテープ用紙は、15〜20cm程度の幅の中原反に裁断したのちに、製品巾(例えば8mm巾)に裁断し、パンチ加工やエンボス加工等の適宜の加工をほどこして搬送対象部品収納用のキャビティ部やテープ送り用のマージナル部等を形成し、本発明のキャリアテープとする。 The carrier tape paper described in detail above is cut into a medium thickness of about 15 to 20 cm, then cut into a product width (for example, 8 mm width), and subjected to appropriate processing such as punching or embossing to be conveyed. A cavity portion for storing components, a marginal portion for tape feeding, and the like are formed to obtain the carrier tape of the present invention.
次に、本発明の実施例と比較例を説明することにより本発明の効果を明らかにする。なお、当然、本発明を以下の実施例のものに限定する趣旨ではない。また、以下の試験例においては、特に説明しない限り、「部」及び「%」とは、それぞれ「質量部」及び「質量%」を意味し、「kg/t」とは、パルプトンあたりの量(kg)を意味する。 Next, the effects of the present invention will be clarified by describing examples and comparative examples of the present invention. Of course, the present invention is not intended to be limited to the following examples. In the following test examples, unless otherwise specified, “part” and “%” mean “part by mass” and “% by mass”, respectively, and “kg / t” means the amount per pulp ton. (Kg).
〔実施例1〕
表面層及び裏面層については、針葉樹晒クラフトパルプ(NBKP)15%、広葉樹晒クラフトパルプ(LBKP)85%からなるフリーネス420mlのパルプスラリーに、サイズ剤(近代化学工業株式会社製R50)を固形分換算で0.25%、PAM(ハリマ化成株式会社製、ハーマイドB−15)を固形分換算で0.15%内添し、硫酸バンドを添加してPHを5に調整した原料を使用した。
一方、中間層(2〜4層)としては、NBKP50%、LBKP40%、サーモメカニカルパルプ(TMP)10%からなるフリーネス410mlのパルプスラリーに、サイズ剤(近代化学工業株式会社製R50)を固形分換算で0.30%、PAM(ハリマ化成株式会社製、ハーマイドB−15)を固形分換算で0.5%内添し、硫酸バンドを添加してPHを5に調整した原料を使用した。
これらを円網多層抄紙機にて、表面層の付け量を60g/m2、中間層(2〜4層)の付け量を460g/m2、裏面層の付け量を60g/m2として、5層構造で抄き合わせ、PVA(日本合成化学株式会社製、ゴーセノールN300)をカレンダー塗工で表面に塗工量1.2g/m2、裏面に1.0g/m2塗工してキャリアテープ用紙を得た。
[Example 1]
For the surface layer and the back layer, sizing agent (R50 manufactured by Modern Chemical Industry Co., Ltd.) is added to the pulp slurry of 420 ml freeness consisting of 15% softwood bleached kraft pulp (NBKP) and 85% hardwood bleached kraft pulp (LBKP). A raw material in which 0.25% in terms of conversion and 0.15% in terms of solid content of PAM (manufactured by Harima Kasei Co., Ltd., Hermide B-15) was internally added, and a pH adjusted to 5 by adding a sulfuric acid band was used.
On the other hand, as an intermediate layer (2-4 layers), a sizing agent (R50 manufactured by Modern Chemical Industry Co., Ltd.) is added to a pulp slurry of 410 ml of freeness composed of NBKP 50%, LBKP 40%, and thermomechanical pulp (TMP) 10%. A raw material having 0.30% in terms of conversion and 0.5% PAM (Harmide B-15, manufactured by Harima Kasei Co., Ltd.) in terms of solid content and adjusting the pH to 5 by adding a sulfuric acid band was used.
At these round net multilayer paper machine, with the amount of 60 g / m 2 of the surface layer, 460 g / m 2 Paste amount of the intermediate layer (2-4 layers), Paste amount of the back layer as a 60 g / m 2, A sheet of paper with a five-layer structure, PVA (manufactured by Nippon Synthetic Chemical Co., Ltd., GOHSENOL N300) is calendered and coated on the surface with a coating amount of 1.2 g / m 2 and on the back with 1.0 g / m 2. Tape paper was obtained.
〔実施例2〜4〕
表面層表面に塗工するPVAの塗工量を表1に示す値に調整したことを除き、その他の点を実施例1と同様にしてキャリアテープ用紙を得た。
[Examples 2 to 4]
A carrier tape paper was obtained in the same manner as in Example 1 except that the amount of PVA applied to the surface layer surface was adjusted to the values shown in Table 1.
〔実施例5〜11〕
表面層表面に塗工するPVAの塗工量、中間層に使用する原料パルプ配合率を表1に示す値に調整したことを除き、その他の点を実施例1と同様にしてキャリアテープ用紙を得た。
[Examples 5 to 11]
The carrier tape paper is the same as in Example 1 except that the coating amount of PVA applied to the surface layer surface and the raw material pulp blending ratio used for the intermediate layer are adjusted to the values shown in Table 1. Obtained.
〔実施例12〜17〕
表面層、裏面層、および中間層に使用するパルプスラリーのフリーネスを表1に示した値としたことを除き、その他の点を実施例1と同様にしてキャリアテープ用紙を得た。
[Examples 12 to 17]
A carrier tape paper was obtained in the same manner as in Example 1 except that the freeness of the pulp slurry used for the front surface layer, the back surface layer, and the intermediate layer was set to the values shown in Table 1.
〔実施例18〜22〕
表面層、裏面層に使用する原料パルプの配合率を表1に示す値に調整したことを除き、その他の点を実施例1と同様にしてキャリアテープ用紙を得た。
[Examples 18 to 22]
A carrier tape paper was obtained in the same manner as in Example 1 except that the blending ratio of the raw material pulp used for the surface layer and the back surface layer was adjusted to the values shown in Table 1.
〔比較例1〜2〕
表面層表面に塗工するPVAの塗工量を表1に示す値に調整したことを除き、その他の点を実施例1と同様にしてキャリアテープ用紙を得た。
[Comparative Examples 1-2]
A carrier tape paper was obtained in the same manner as in Example 1 except that the amount of PVA applied to the surface layer surface was adjusted to the values shown in Table 1.
以上の実施例および比較例について米坪、厚さ、こわさ、平滑度、表面強度、層間強度の物性測定と、折れについて評価試験を行った。結果は、表1中に示す。なお、物性測定およびこの評価試験は、JIS−P8111に準拠して温度23℃±1℃、湿度50±2%の環境条件で行った。 About the above Example and the comparative example, the evaluation test was done about the physical-property measurement of a tsubo, thickness, stiffness, smoothness, surface strength, and interlayer strength, and a crease. The results are shown in Table 1. The physical property measurement and this evaluation test were performed under environmental conditions of a temperature of 23 ° C. ± 1 ° C. and a humidity of 50 ± 2% in accordance with JIS-P8111.
各測定方法および試験方法についての詳細は以下のとおりである。
(厚さ)
JIS P 8118 紙及び板紙−厚さ及び密度の試験方法に準じて厚さを測定した。
Details of each measurement method and test method are as follows.
(thickness)
JIS P 8118 Paper and paperboard—Thickness was measured according to thickness and density test methods.
(こわさ)
JIS P 8125 紙及び板紙−こわさ試験方法−テーバーこわさ試験機法に準じて縦方向のこわさを測定した。表中では、表面側から裏面側へ向かって荷重を掛けた時の縦方向のこわさを(X)とし、裏面側から表面側へ向かって荷重を掛けた時の縦方向のこわさを(Y)とした。
(Stiffness)
In accordance with JIS P 8125 paper and paperboard-stiffness test method-Taber stiffness tester method, the stiffness in the vertical direction was measured. In the table, (X) is the vertical stiffness when a load is applied from the front side to the back side, and (Y) is the vertical stiffness when a load is applied from the back side to the front side. It was.
(平滑度)
JIS P 8151 紙及び板紙−表面粗さ及び平滑度試験方法(エア・リーク法)−プリント・サーフ試験機法(面積式流量計形プリント・サーフ試験機)にて、ソフトバッキングを用い、クランプ装置のバッキングを1.0MPAとして表面、裏面それぞれの平滑度を測定した。
(Smoothness)
JIS P 8151 Paper and paperboard-Surface roughness and smoothness test method (air leak method)-Print surf tester method (area type flow meter type print surf tester), using soft backing, clamping device The smoothness of each of the front and back surfaces was measured with a backing of 1.0MPA.
(表面強度)
TAPPI T459 om−83に基づき、表面側、裏面側のそれぞれの表面強度を測定した。
(Surface strength)
Based on TAPPI T459 om-83, the surface strengths on the front and back sides were measured.
(層間強度)
TAPPI UM522に従い、Z軸方向の層間強度を測定した。
(Interlayer strength)
According to TAPPI UM522, the interlayer strength in the Z-axis direction was measured.
(各層の分離方法)
抄紙後の用紙の各層の物性を測定すべく、抄紙後の用紙から次記の方法で各層に分離した。まず、試料を室温の水に約1時間浸漬したのち、試料の角を起点として10mmΦ程度の丸棒に捲き付け、その状態で丸棒を転がして試料をしごく。この操作を試料の四隅の全ての角を起点に繰り返し、各方向から試料にしごきの力を加える。これにより、試料の層間の一部が剥離してくるので、これを利用して、試料を表面層、中間層、及び裏面層に分離する。
(Separation method of each layer)
In order to measure the physical properties of each layer of the paper after paper making, each layer was separated from the paper after paper making by the following method. First, after immersing the sample in water at room temperature for about 1 hour, the sample is rubbed on a round bar of about 10 mmΦ starting from the corner of the sample, and the round bar is rolled in this state to squeeze the sample. This operation is repeated starting from all four corners of the sample, and an ironing force is applied to the sample from each direction. As a result, a part of the layer between the samples is peeled off, and this is used to separate the sample into a front surface layer, an intermediate layer, and a back surface layer.
(フリーネス)
分離された各層を裁断して約3cm2、約25gの試験片とし、この試験片を1リットルの水に24時間浸漬したのちにJIS−P8220に基づき標準離解機で15分間離解処理し、試験片が完全に離解していることを目視で確認した後、JIS−P8121に準拠してカナダ標準濾水度試験機にて測定した。
(Freeness)
Each separated layer is cut to obtain a test piece of about 3 cm 2 and about 25 g. After the test piece is immersed in 1 liter of water for 24 hours, it is subjected to a disaggregation treatment for 15 minutes with a standard disintegrator based on JIS-P8220. After visually confirming that the piece was completely disaggregated, it was measured with a Canadian standard freeness tester according to JIS-P8121.
(折れ)
折れの評価は、流れ方向30cm、幅8mmのサンプルを10本用意し、直径6cmの円柱に捲きつけ、折れの発生個数を目視判定し、1本のあたりの平均個数を次の基準で評価した。評価は、1個未満を◎、1個以上2個未満を○、2以上5個未満△、5個以上を×と評価した。
(Break)
For the evaluation of folding, ten samples having a flow direction of 30 cm and a width of 8 mm were prepared, placed on a cylinder having a diameter of 6 cm, the number of occurrences of folding was visually determined, and the average number per one was evaluated according to the following criteria. . In the evaluation, less than 1 was evaluated as ◎, 1 or more and less than 2 as ○, 2 or more and less than 5 Δ, and 5 or more as ×.
表1から、本発明のキャリアテープ用紙である実施例1〜23は品質評価に優れることが分かる。それに対して、比較例1〜2は、品質評価において実施例1〜23よりも劣る結果となっている。してみると、本発明のキャリアテープ用紙からは、カセットリールや管に捲き取るときや捲き取り後に、折れやしわの発生が防止されているといえる、これにより、トップテープを安定的に剥離することができ、電子部品取り出し時の安定性に優れ、生産効率のよいキャリアテープを得ることができるといえる。 From Table 1, it can be seen that Examples 1 to 23 which are carrier tape sheets of the present invention are excellent in quality evaluation. On the other hand, Comparative Examples 1-2 are inferior to Examples 1-23 in quality evaluation. As a result, it can be said that the carrier tape sheet of the present invention prevents creases and wrinkles from occurring when the cassette tape or tube is scraped off or after scraping. It can be said that it is possible to obtain a carrier tape that is excellent in stability at the time of taking out an electronic component and has high production efficiency.
Claims (5)
紙厚が700〜1200μmであり、
裏面側から表面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさに対する、表面側から裏面側へ向かって荷重を掛けたときのJIS−P8125に規定される用紙縦方向のこわさの比率が、80〜90%である、ことを特徴とするキャリアテープ用紙。 A multi-layered carrier tape paper having a surface layer as an outer surface of winding, a back layer as an inner surface of winding, and an intermediate layer therebetween,
The paper thickness is 700-1200 μm,
Paper stipulated in JIS-P8125 when a load is applied from the front side to the back side against the stiffness in the vertical direction of the paper stipulated in JIS-P8125 when a load is applied from the back side to the front side A carrier tape sheet characterized in that the ratio of stiffness in the vertical direction is 80 to 90%.
裏層面に塗工または含浸された水溶性高分子量に対する、表面層に塗工または含浸された水溶性高分子量の質量比率が120〜250%である、請求項1に記載のキャリアテープ用紙。 The surface layer and the back layer are coated or impregnated with a water-soluble polymer,
The carrier tape paper according to claim 1, wherein a mass ratio of the water-soluble high molecular weight coated or impregnated on the surface layer to the water-soluble high molecular weight coated or impregnated on the back layer surface is 120 to 250%.