JP2007111115A - Makeup cotton and its manufacturing method - Google Patents

Makeup cotton and its manufacturing method Download PDF

Info

Publication number
JP2007111115A
JP2007111115A JP2005303198A JP2005303198A JP2007111115A JP 2007111115 A JP2007111115 A JP 2007111115A JP 2005303198 A JP2005303198 A JP 2005303198A JP 2005303198 A JP2005303198 A JP 2005303198A JP 2007111115 A JP2007111115 A JP 2007111115A
Authority
JP
Japan
Prior art keywords
cotton
cotton fiber
sheet
fiber sheet
cosmetic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2005303198A
Other languages
Japanese (ja)
Other versions
JP4796371B2 (en
Inventor
Masataka Iwamoto
正孝 岩元
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kakui Co Ltd
Original Assignee
Kakui Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kakui Co Ltd filed Critical Kakui Co Ltd
Priority to JP2005303198A priority Critical patent/JP4796371B2/en
Publication of JP2007111115A publication Critical patent/JP2007111115A/en
Application granted granted Critical
Publication of JP4796371B2 publication Critical patent/JP4796371B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

<P>PROBLEM TO BE SOLVED: To provide makeup cotton consisting of a plurality of layers and allowing a user to easily peel or take out the makeup cotton in a laminated state from non-joined part which is not joined one at a time; and its manufacturing method. <P>SOLUTION: This multilayer-structure makeup cotton 1 formed by superposing cotton fiber sheets 2 containing thermomelting fibers one on another is characterized in embossing the cotton fiber sheet 2 peelably one at a time and having one or more linear recessed parts 4 near the circumferential edge of the laminated cotton fiber sheet 2. <P>COPYRIGHT: (C)2007,JPO&INPIT

Description

本発明は、熱溶融繊維を含有する綿繊維シートを積層する化粧綿に関するものであり、詳しくは、シート状に成形した綿繊維シートを1枚ずつ剥離可能にした化粧綿およびその製造方法に関するものである。   TECHNICAL FIELD The present invention relates to a decorative cotton in which cotton fiber sheets containing hot-melt fibers are laminated, and more specifically, to a decorative cotton in which cotton fiber sheets formed into a sheet shape can be peeled one by one and a method for producing the same. It is.

従来、複数層からなる化粧綿は、化粧水を含ませ、顔の下から上へなで押さえる動作(以下、「パッティング」という)をした後、数層の化粧綿に剥離させてパック用シートとして使用されているが、何十層からなる化粧綿を1枚ずつ剥離させようとすると、数枚が一緒になって、剥がれてしまう問題があった。   Conventionally, a multi-layered cosmetic cotton contains a lotion, and after pressing from the bottom of the face to the top (hereinafter referred to as “putting”), it is peeled off to a few layers of the cotton to make a pack sheet However, there was a problem that several sheets were peeled together when peeled off one by one from dozens of layers of decorative cotton.

また、化粧綿を1枚ずつ剥離させると、剥離された化粧綿の表面は、毛羽立った状態になり、化粧水を含ませた化粧綿でパッティングする際に、肌に綿繊維の付着が生じるという問題があった。   Moreover, when the cosmetic cotton is peeled one by one, the surface of the peeled cosmetic cotton becomes fuzzy, and the cotton fibers adhere to the skin when putting on the cosmetic cotton soaked with lotion. There was a problem.

これらの問題に対して、容易に引き剥がせるようにした不織布積層体またはパック用シートが下記の特許文献に提案されている。   In order to solve these problems, a nonwoven fabric laminate or a pack sheet that can be easily peeled is proposed in the following patent documents.

特許文献1には、不織布シートを上下に複数枚積層して積層体を製作し、この積層体に対して、不織布シートの繊維に係合するアゴ部を有するニードルを突き刺しては抜き取る操作を繰り返し行う。   In Patent Document 1, a plurality of nonwoven fabric sheets are stacked one above the other to produce a laminate, and a needle having an jaw portion that engages with the fibers of the nonwoven fabric sheet is pierced and removed from the laminate. Do.

そして、上下の不織布シートの繊維を相互に絡ませて、複数の不織布シートを1枚ずつ引き剥がし可能に結合した不織布積層体が提案されている。   And the nonwoven fabric laminated body which entangled the fiber of an upper and lower nonwoven fabric sheet mutually and couple | bonded the several nonwoven fabric sheet one by one so that peeling was possible is proposed.

また、特許文献2には、複数枚のそれぞれの周縁部における互いに異なる位置に少なくとも一つの延出部を形成させ、積層して収納されるパック用シートを簡単に引き剥がすことができるパック用シートが提案されている。   Further, Patent Document 2 discloses a pack sheet in which at least one extending portion is formed at different positions on the peripheral portions of each of a plurality of sheets, and a pack sheet stored in a stacked manner can be easily peeled off. Has been proposed.

特開2002−266218号公報(請求項1,2)JP 2002-266218 A (Claims 1, 2) 特開2000−325143号公報(請求項1)JP 2000-325143 A (Claim 1)

しかしながら、上記特許文献1に記載の不織布積層体は、ニードルの突き刺す回数と加熱温度及び圧接ローラによる圧接力に応じて、不織布積層体における不織布シートの結合強度を微妙に調整するもので、適度の結合強度に設定することが困難であった。   However, the nonwoven fabric laminate described in the above-mentioned Patent Document 1 finely adjusts the bonding strength of the nonwoven fabric sheet in the nonwoven fabric laminate according to the number of times the needle is pierced, the heating temperature and the pressure contact force by the pressure roller. It was difficult to set the bond strength.

また、上記特許文献2に記載のパック用シートは、紙または不織布等のシートであり、延出部を積層して収納される複数枚のシートの周縁部に互いに異なる位置に形成する必要があるため、製造工程が複雑となり、製造コストが高くなるという問題があった。   Further, the pack sheet described in Patent Document 2 is a sheet of paper or non-woven fabric, and needs to be formed at different positions on the peripheral edges of a plurality of sheets stored by stacking extending portions. Therefore, there is a problem that the manufacturing process becomes complicated and the manufacturing cost increases.

上述の問題点に鑑みて、本発明は、複数の層状からなる化粧綿を、使用者が積層した状態の化粧綿を接合していない非接合部から容易に1枚ずつ剥離または取り外しすることを可能にした化粧綿およびその製造方法の提供を目的とするものである。   In view of the above-mentioned problems, the present invention is intended to easily peel or remove one-by-one a single layer of decorative cotton from a non-joined part where a user has laminated the decorative cotton in a stacked state. An object of the present invention is to provide a decorative cotton made possible and a method for producing the same.

前記目的を達成するため、第1の発明の構成は、熱溶融繊維を含有する綿繊維シートが積層される多層構造の化粧綿であって、
1枚ずつ剥離可能に前記綿繊維シートにエンボス加工が施され、積層された前記綿繊維シートの周縁近傍部に1つ以上の線状凹部を設けることを特徴とする。
を特徴としている。
In order to achieve the above object, the structure of the first invention is a multi-layered decorative cotton in which cotton fiber sheets containing hot-melt fibers are laminated,
The cotton fiber sheets are embossed so as to be peeled one by one, and one or more linear recesses are provided in the vicinity of the periphery of the laminated cotton fiber sheets.
It is characterized by.

第2の発明の構成は、第1の発明の化粧綿において、前記線状凹部が前記綿繊維シートの周縁部と交差することを特徴とする。   The configuration of the second invention is characterized in that, in the decorative cotton of the first invention, the linear recess intersects a peripheral edge of the cotton fiber sheet.

第3の発明の構成は、第1または第2の発明の化粧綿において、前記積層された綿繊維シート相互が前記線状凹部で接合されることを特徴とする。   According to a third aspect of the present invention, in the decorative cotton of the first or second aspect, the laminated cotton fiber sheets are joined to each other at the linear recesses.

第4の発明の構成は、第1〜第3のいずれかの発明の化粧綿において、前記綿繊維シートは、熱溶融繊維を5〜15重量%含有することを特徴とする。   According to a fourth aspect of the present invention, in the decorative cotton according to any one of the first to third aspects, the cotton fiber sheet contains 5 to 15% by weight of a hot-melt fiber.

第5の発明の構成は、第1〜第4のいずれかの発明の化粧綿において、前記綿繊維シートの1枚の目付量が60〜240g/m2であることを特徴とする。 According to a fifth aspect of the invention, in the cosmetic cotton of any one of the first to fourth aspects, the basis weight of one of the cotton fiber sheets is 60 to 240 g / m 2 .

第6の発明の構成は、綿のエンボス加工、積層、接合・切断の各工程を有する化粧綿の製造方法であって、
前記綿繊維シートにエンボス加工を施すステップと、
前記綿繊維シートを多層構造に積層するステップと、
前記綿繊維シートの周縁近傍部に周縁部と交差する1つ以上の線状凹部を設けるステップと、
前記綿繊維シート相互が前記線状凹部で接合するステップと、
を有することを特徴とする化粧綿の製造方法である。
The configuration of the sixth invention is a method for producing decorative cotton having the steps of embossing cotton, laminating, joining and cutting,
Embossing the cotton fiber sheet;
Laminating the cotton fiber sheet into a multilayer structure;
Providing one or more linear recesses intersecting the peripheral edge in the peripheral vicinity of the cotton fiber sheet;
Bonding the cotton fiber sheets to each other at the linear recesses;
It is a manufacturing method of cosmetic cotton characterized by having.

第7の発明の構成は、第6の発明の化粧綿の製造方法において、前記エンボス加工ステップが、前記綿繊維シートの片面若しくは両面に施されたことを特徴とする。   According to a seventh aspect of the present invention, in the method for producing decorative cotton according to the sixth aspect of the invention, the embossing step is performed on one side or both sides of the cotton fiber sheet.

第8の発明の構成は、第6または第7の発明の化粧綿の製造方法において、前記エンボス加工ステップのプレス圧は、0.1〜5kg/cm2であることを特徴とする。 According to an eighth aspect of the present invention, there is provided the method for producing a decorative cotton according to the sixth or seventh aspect, wherein the embossing step has a press pressure of 0.1 to 5 kg / cm 2 .

請求項1〜3の発明によれば、1枚ずつ剥離可能に前記綿繊維シートがエンボス加工が施され、前記綿繊維シートの周縁近傍部に周縁部と交差する1つ以上の線状凹部を設け、前記綿繊維シート相互が前記線状凹部で接合されるように積層されたので、線状凹部のみが接合され、剥離可能に積層した化粧綿を製造することができる。   According to invention of Claims 1-3, the said cotton fiber sheet is embossed so that peeling can be carried out one by one, and the one or more linear recessed part which cross | intersects a peripheral part in the peripheral part of the said cotton fiber sheet is provided. Since it is provided and laminated so that the cotton fiber sheets are joined to each other by the linear recesses, only the linear recesses are joined, and the laminated cotton that can be peeled can be manufactured.

しかも使用者が接合されていない非接合部から綿繊維シートを1枚ずつ剥離することを容易にすることができる。比較的容易に剥離させる程度の接合強度にすることが可能となる。   Moreover, it is possible to easily peel the cotton fiber sheets one by one from the non-joined portion where the user is not joined. It is possible to achieve a bonding strength that can be relatively easily peeled off.

請求項4の発明によれば、請求項1〜3のいずれかの化粧綿において、熱溶融繊維を5〜15重量%含有することにより、綿繊維間の間隙を固定して、型くずれの防止と積層した綿繊維シートの熱溶着による接合を可能とする。   According to the invention of claim 4, in the decorative cotton according to any one of claims 1 to 3, by containing 5 to 15% by weight of the hot melt fiber, the gap between the cotton fibers is fixed, and the deformation of the mold is prevented. It enables joining by thermal welding of the laminated cotton fiber sheets.

請求項5の発明によれば、請求項1〜4のいずれかの化粧綿において、1枚の綿繊維シートの単位面積当たりの質量(以下、「目付量」という)を60〜240g/m2にすると、パック用シートとしての引張強度があり、経済的であるという効果が得られる。 According to the invention of claim 5, in the decorative cotton according to any one of claims 1 to 4, the mass per unit area (hereinafter referred to as “weight per unit area”) of one cotton fiber sheet is 60 to 240 g / m 2. If it makes it, there exists the tensile strength as a sheet | seat for packs, and the effect that it is economical will be acquired.

請求項6の発明によれば、積層された線状凹部のみが接合され、使用者が接合されていない非接合部から綿繊維シートを1枚ずつ剥離可能に積層した化粧綿を製造することができる。   According to invention of Claim 6, only the laminated linear recessed part is joined and the cosmetic cotton which laminated | stacked the cotton fiber sheet | seat one by one from the non-joining part which is not joined can be manufactured. it can.

請求項7の発明によれば、請求項6の化粧綿の製造方法で、前記エンボス加工ステップが、前記綿繊維シートの片面若しくは両面に施されたことにより、コンパクト化ができて、ソフトな肌触りを損なわず、かつ拭き取り効果を高めることができる。   According to a seventh aspect of the present invention, in the cosmetic cotton manufacturing method according to the sixth aspect, the embossing step is performed on one or both sides of the cotton fiber sheet, so that it can be made compact and has a soft touch. And the wiping effect can be enhanced.

請求項8の発明によれば、請求項6又は7の化粧綿の製造方法で、エンボス加工ステップのプレス圧は、0.1〜5kg/cm2にすることで綿繊維の風合いを残しつつ、剥離させる際の毛羽立ちがより抑えられ、化粧水の吸水性を高めて、化粧水を無駄に使用しないパック用シートを作製することができる。 According to the invention of claim 8, in the manufacturing method of the decorative cotton of claim 6 or 7, the press pressure of the embossing step is 0.1 to 5 kg / cm 2 while leaving the texture of the cotton fiber, The fluffing at the time of peeling is further suppressed, the water absorption of the lotion is increased, and a pack sheet that does not use the lotion wastefully can be produced.

以下、本発明の実施形態における化粧綿及び製造方法について、図面を参照しながら、詳細に説明する。   Hereinafter, cosmetic cotton and a manufacturing method in an embodiment of the present invention will be described in detail with reference to the drawings.

(第1の実施形態)
図1(a)は、長方形シートタイプ化粧綿の斜視図で、図1(b)は、 図1(a)のA−A線で切断した拡大断面図である。
(First embodiment)
Fig.1 (a) is a perspective view of a rectangular sheet type cosmetic cotton, FIG.1 (b) is the expanded sectional view cut | disconnected by the AA line of Fig.1 (a).

図1(a)に示すように、1は、本実施形態の化粧綿であり、長方形の綿繊維シート2が4枚積層されて、長方形の長辺側縁にそれぞれ1つの線状凹部4が設けられ、その線状凹部4で接合された構成となっている。   As shown to Fig.1 (a), 1 is the makeup | decoration cotton of this embodiment, 4 rectangular cotton fiber sheets 2 are laminated | stacked, and one linear recessed part 4 is each in the rectangular long side edge. It is the structure which was provided and was joined by the linear recessed part 4. FIG.

化粧綿1は、平面視で長方形(横60×縦80mm)の形状で、その厚さは、2mmに形成されている。素材としては、熱溶融繊維を含有した綿繊維を使用している。     The decorative cotton 1 has a rectangular shape (width 60 × length 80 mm) in plan view, and the thickness thereof is 2 mm. As the material, cotton fibers containing hot melt fibers are used.

化粧綿の寸法は、横45〜80×縦60〜100mmの範囲から選択され、厚さは、2〜4mmが好ましい。   The dimensions of the decorative cotton are selected from the range of 45 to 80 × 60 to 100 mm in length, and the thickness is preferably 2 to 4 mm.

顔面用のパック用シートとして使用する化粧綿の寸法は、横60×縦80mmがより好ましい。   The dimensions of the decorative cotton used as the pack sheet for the face are more preferably 60 × 80 mm.

1枚の綿繊維シートの目付量は、好ましくは、60〜240g/m2であり、その目付量が60g/m2未満では、綿繊維シートの厚みが薄くなり、引張強度が弱くなる。 Basis weight of a sheet of cotton fiber sheet is preferably a 60~240g / m 2, in its basis weight is less than 60 g / m 2, the thickness of the cotton fiber sheet becomes thin, the tensile strength is weakened.

一方、その目付量が240g/m2を超えると、綿繊維シートの厚みが厚くなり、化粧水を多量に吸収するので化粧水を無駄に使用して、経済的でない。 On the other hand, when the weight per unit area exceeds 240 g / m 2 , the thickness of the cotton fiber sheet becomes thick and a lot of lotion is absorbed, so the lotion is wasted and not economical.

熱溶融繊維としては、ポリオレフィン系繊維が挙げられる。好ましくは、ポリエステルステープルファイバー(東洋紡績(株)製品)、商品名 メルティ(ユニチカ(株)製品)やES繊維(チッソ(株)製品)等を使用することができる。   Examples of the hot melt fiber include polyolefin fibers. Preferably, polyester staple fiber (product of Toyobo Co., Ltd.), trade name Melty (product of Unitika Ltd.), ES fiber (product of Chisso Corp.), etc. can be used.

熱溶融繊維の含有量は、5〜15重量%が好ましい。綿繊維に熱溶融繊維を含有させることで、綿繊維間の間隙を固定して、型くずれの防止を図ると共に、綿繊維間融着を主な結合力として、十分な強度を有することができる。   The content of the hot melt fiber is preferably 5 to 15% by weight. By containing the hot-melt fiber in the cotton fiber, it is possible to fix the gap between the cotton fibers to prevent the deformation of the mold and to have a sufficient strength with the inter-cotton fiber fusion as a main bonding force.

また、熱溶融繊維の含有量が、5重量%未満では、熱融着による接合不足となり、積層した綿繊維シートの接合が不十分である。   Moreover, when the content of the hot-melt fiber is less than 5% by weight, bonding due to heat fusion is insufficient, and bonding of the laminated cotton fiber sheets is insufficient.

一方、熱溶融繊維の含有量が、15重量%を超えると、綿繊維シート自体が硬くなり、化粧綿としての肌の感触が悪くなる。   On the other hand, if the content of the hot-melt fiber exceeds 15% by weight, the cotton fiber sheet itself becomes hard, and the skin feel as cosmetic cotton becomes worse.

綿繊維に混合する熱溶融繊維の種類や混合比は、化粧綿の用途等に応じて、適宜選択することができる。   The kind and mixing ratio of the hot-melt fiber mixed with the cotton fiber can be appropriately selected according to the use of the decorative cotton.

綿繊維シート2の表面には、凹凸模様が施されたエンボスローラーにより、格子模様の凹凸模様3が形成されている。   On the surface of the cotton fiber sheet 2, an uneven pattern 3 having a lattice pattern is formed by an embossing roller having an uneven pattern.

エンボス加工ステップのプレス圧は、0.1〜5kg/cm2の範囲内であることが好ましい。上記のプレス圧でエンボス加工することにより、綿繊維シートを剥離させた際の化粧綿の毛羽立ち防止に有効であり、ソフトな肌触りを損なわず、かつ、吸水性を高めることができる。 The pressing pressure in the embossing step is preferably in the range of 0.1 to 5 kg / cm 2 . Embossing with the above-mentioned press pressure is effective in preventing fuzz of cosmetic cotton when the cotton fiber sheet is peeled off, and does not impair the soft touch and can increase water absorption.

また、エンボス加工ステップのプレス圧が、0.1kg/cm2未満では、化粧水等の保水量が多くなり、化粧綿は、形くずれが起きる。 In addition, when the press pressure of the embossing step is less than 0.1 kg / cm 2 , the amount of water to be retained such as lotion increases, and the cosmetic cotton is deformed.

一方、エンボス加工ステップのプレス圧が、5kg/cm2を超えると、化粧水等の保水量が少なくなり、化粧綿として、肌当たり感もよくない。 On the other hand, when the press pressure of the embossing step exceeds 5 kg / cm 2 , the amount of water retained such as skin lotion is reduced, and the skin feel is not good as cosmetic cotton.

尚、エンボス加工ステップのプレス圧は、化粧綿の使用目的及び用途に合わせて、変化させることにより、化粧水等の保水量や肌触りの調整を図ることがより好ましい。   In addition, it is more preferable to aim at adjustment of the water retention amount and the touch of the skin lotion, etc., by changing the press pressure of the embossing step according to the intended purpose and application of the cosmetic cotton.

綿繊維シート2の周縁近傍部、すなわち、長辺側縁に線状凹部4が、それぞれ1つずつ設けられ、周縁部である短辺側縁を交差して平行に形成されている。   One linear concave portion 4 is provided in the vicinity of the peripheral edge of the cotton fiber sheet 2, that is, the long side edge, and is formed in parallel by crossing the short side edge that is the peripheral edge.

線状凹部4は、線状凸部を有するヒートプレス機付き裁断機の加熱加圧により形成され、図1(b)に示すように、その厚みは、全体の厚みの1/4に形成されている。   The linear concave portion 4 is formed by heating and pressurizing a cutting machine with a heat press machine having linear convex portions, and as shown in FIG. 1B, the thickness thereof is formed to ¼ of the total thickness. ing.

綿繊維シート2相互が接合していない短辺側縁の非接合部5では、綿繊維シート2は、単に積層された状態に保持されている。   In the non-joining part 5 of the short side edge where the cotton fiber sheets 2 are not joined to each other, the cotton fiber sheet 2 is simply held in a laminated state.

また、図1では、長方形の長辺側縁に線状凹部4が、それぞれ1つずつ設けられているが、長辺側縁に線状凹部を設けないで、短辺側縁に線状凹部を設けて接合させてもよい
Further, in FIG. 1, one linear recess 4 is provided on each long side edge of the rectangle, but no linear recess is provided on the long side edge, and the linear recess is provided on the short side edge. And may be joined.

次に、本発明を適用した化粧綿の製造方法について、各工程を図4を参照しながら、詳細に説明する。   Next, the manufacturing method of the cosmetic cotton to which the present invention is applied will be described in detail with reference to FIG.

図4において、本発明の製造工程は、(1)熱溶融繊維を混合して開繊する混綿・開繊工程(ステップS101)と、(2)繊維の方向を揃えてシート状にするカード工程(ステップS102)と、(3)不純物を除去する精練工程(ステップS103)と、(4)漂白する漂白工程(ステップS104)と、(5)凹凸模様を施すエンボス加工工程(ステップS105)と、(6)乾燥させる乾燥工程(ステップS106)と、(7)巻取りする巻取り工程(ステップS107)と、(8)積層する積層工程(ステップS108)と、(9)接合・切断する接合・切断工程(ステップS109)から構成される。   In FIG. 4, the manufacturing process of the present invention includes (1) a mixed cotton / opening process (step S101) in which heat-melted fibers are mixed and opened, and (2) a card process in which the fiber directions are aligned to form a sheet. (Step S102), (3) a scouring process for removing impurities (Step S103), (4) a bleaching process for bleaching (Step S104), and (5) an embossing process for applying an uneven pattern (Step S105), (6) Drying process to be dried (step S106), (7) Winding process to wind up (step S107), (8) Laminating process to stack (step S108), (9) Joining / cutting It consists of a cutting process (step S109).

(1)ステップS101:混綿・開繊工程
混綿・開繊工程S101では、綿繊維に適宜の割合で熱溶融繊維を混合して混綿され、空気流で開繊した繊維集合体をベルトコンベア上に供給する。
(1) Step S101: Cotton blending / opening step In the cotton blending / opening step S101, a fiber assembly that is mixed with hot-melt fibers and mixed with cotton fibers at an appropriate ratio and opened by airflow is placed on a belt conveyor. Supply.

(2)ステップS102:カード工程
次に、カード工程S102では、コンベアの途中に設けられ、熱溶融繊維を含有した繊維集合体を薄く延ばしながら、何回も繰り返し細かい無数の針の間を通し、あたかも、くしで髪を梳くかのようにして、繊維の方向を揃えてシート状に成形する装置、即ち、梳棉機(以下、「カード機」という)でシート状に成形した綿繊維シートを一定量・一定方向にコンベア上に送り出す。
(2) Step S102: Carding process Next, in the carding process S102, the fiber assembly containing the heat-melting fibers is provided in the middle of the conveyor, and is repeatedly passed through numerous countless needles repeatedly. A cotton fiber sheet formed into a sheet shape with a machine (hereinafter referred to as a “card machine”) that forms a sheet with the direction of the fibers aligned as if combing hair. A certain amount is sent out on the conveyor in a certain direction.

(3)ステップS103:精練工程
また、精練工程S103では、綿繊維シート中に存在するタンパク、ペクチンおよびゴミ等の不純物を除去する。
(3) Step S103: Scouring Step In the scouring step S103, impurities such as proteins, pectin and dust existing in the cotton fiber sheet are removed.

(4)ステップS104:漂白工程
また、漂白工程S104では、漂白剤で綿繊維シートの色素脱色を行い、純粋に近い綿繊維の状態に漂白する。
(4) Step S104: Bleaching step In the bleaching step S104, the dyeing of the cotton fiber sheet is performed with a bleaching agent to bleach the cotton fiber into a nearly pure state.

(5)ステップS105:エンボス加工工程
次に、エンボス加工工程S105では、綿繊維シートをコンベアの下側に配置されたゴム製ローラーと、コンベアの上側に配置された凹凸加工を施した金属製ローラーとの間に通して、上下のローラーで綿繊維シートを圧接させて、綿繊維シートの片面に凹凸模様を形成させる。
(5) Step S105: Embossing Step Next, in the embossing step S105, a rubber roller having a cotton fiber sheet disposed on the lower side of the conveyor, and a metal roller having an uneven surface disposed on the upper side of the conveyor. The cotton fiber sheet is pressed with upper and lower rollers to form a concavo-convex pattern on one side of the cotton fiber sheet.

尚、綿繊維シートの両面に凹凸模様を形成させるには、上下側に配置された凹凸加工を施した金属製ローラーで、綿繊維シートを圧接させて、両面に凹凸模様を形成させる。   In addition, in order to form a concavo-convex pattern on both surfaces of a cotton fiber sheet, the rugged pattern is formed on both surfaces by pressing the cotton fiber sheet with a metal roller having a concavo-convex process disposed on the upper and lower sides.

(6)ステップS106:乾燥工程
さらに、乾燥工程S106では、綿繊維シートを電熱機または熱風で150℃の温度で80秒間乾燥させて、綿繊維シートに付着した水分を蒸発させる。
(6) Step S106: Drying Process Furthermore, in the drying process S106, the cotton fiber sheet is dried at a temperature of 150 ° C. for 80 seconds with an electric heater or hot air to evaporate water adhering to the cotton fiber sheet.

(7)ステップS107:巻取り工程
そして、巻取り工程S107では、綿繊維シートを複数の巻取り機にロール状に巻取る。
(7) Step S107: Winding Process And in the winding process S107, the cotton fiber sheet is wound in a roll shape on a plurality of winders.

(8)ステップS108:積層工程
また、積層工程S108では、巻取られた複数のロールから綿繊維シートを順次引き出して、綿繊維シートを複数枚揃えて重ね合わせて、積層シートを作製する。
(8) Step S108: Lamination process In addition, in the lamination process S108, a cotton fiber sheet is sequentially pulled out from a plurality of wound rolls, and a plurality of cotton fiber sheets are aligned and overlapped to produce a laminated sheet.

(9)ステップS109:接合・切断工程
さらに、接合・切断工程S109では、線状凸部を有するヒートプレス機付き裁断機は、ヒートプレス機の線状凸部が120〜126℃の設定温度に加熱され、積層した綿繊維シートの所望形状の周縁近傍部を加熱加圧すると、積層した綿繊維シートの周縁近傍部に線状凹部が形成され、綿繊維シート相互が線状凹部で接合される。それと同時に裁断機で、線状凹部が形成された積層シートを所望形状に切断する。
(9) Step S109: Joining / Cutting Process Furthermore, in the joining / cutting process S109, the cutting machine with a heat press machine having a linear convex part has a linear convex part of the heat press machine at a set temperature of 120 to 126 ° C. When heated and pressed in the vicinity of the periphery of the desired shape of the laminated cotton fiber sheets, a linear recess is formed in the vicinity of the periphery of the stacked cotton fiber sheet, and the cotton fiber sheets are joined to each other by the linear recess. . At the same time, the laminated sheet in which the linear recesses are formed is cut into a desired shape by a cutter.

積層した綿繊維シートの接合は、綿繊維シートの周縁近傍部に1つ以上の線状凹部を設けて接合すればよい。   The laminated cotton fiber sheets may be joined by providing one or more linear recesses in the vicinity of the periphery of the cotton fiber sheet.

また、線状凸部を有するヒートプレス機付き裁断機による加熱融着時の温度条件や綿繊維シートに形成される線状凹部の数を調整することで、綿繊維シート相互の接合強度を微妙に調整することが可能である。   In addition, by adjusting the temperature conditions at the time of heat-sealing by a cutting machine with a heat press machine having linear convex parts and the number of linear concave parts formed on the cotton fiber sheet, the bonding strength between the cotton fiber sheets is delicately adjusted. It is possible to adjust to.

次に、所望形状に切断された積層した綿繊維シートは、検査工程を経て、包装体に梱包されて、化粧綿として出荷される。   Next, the laminated cotton fiber sheet cut into a desired shape is packed in a package through an inspection process and shipped as cosmetic cotton.

(第2の実施形態)
図2(a)は、円形シートタイプの化粧綿の斜視図で、図2(b)は、図2(a)のA−A線で切断した拡大断面図である。
(Second Embodiment)
Fig.2 (a) is a perspective view of a circular sheet type cosmetic cotton, FIG.2 (b) is an expanded sectional view cut | disconnected by the AA line of Fig.2 (a).

上述の製造工程で成形された化粧綿の第2の実施形態では、図2(a)に示すように、1aは、本実施形態の化粧綿であり、円形の綿繊維シート2aを3枚積層して、円形の周縁近傍部に1つの線状凹部4aが設けられ、その線状凹部で接合された構成となっている。   In the second embodiment of the decorative cotton molded in the above-described manufacturing process, as shown in FIG. 2A, 1a is the decorative cotton of this embodiment, and three circular cotton fiber sheets 2a are laminated. And one linear recessed part 4a is provided in the circular periphery vicinity part, and it has the structure joined by the linear recessed part.

化粧綿1aは、平面視で円形(直径60mm)の形状で、その厚さは、3mmに形成されている。   The cosmetic cotton 1a has a circular shape (diameter 60 mm) in a plan view and a thickness of 3 mm.

綿繊維シート2aの表面には、凹凸模様が施されたエンボスローラーにより、水玉模様の凹凸模様3aが形成されている。   On the surface of the cotton fiber sheet 2a, a concavo-convex pattern 3a having a polka dot pattern is formed by an embossing roller having a concavo-convex pattern.

綿繊維シート2aの周縁近傍部に、すなわち、円形の一端から他端にわたって、線状凸部を有するヒートプレス機付き裁断機により、1つの線状凹部4aが設けられ、周縁部である円周を交差して形成されている。   In the vicinity of the peripheral edge of the cotton fiber sheet 2a, that is, from one end of the circular shape to the other end, one linear concave portion 4a is provided by a cutting machine with a heat-pressing machine having a linear convex portion. It is formed to intersect.

線状凹部4aは、線状凸部を有するヒートプレス機付き裁断機の加熱加圧により形成され、図2(b)に示すように、その厚みは、全体の厚みの1/3に形成されている。   The linear concave portion 4a is formed by heating and pressurizing a cutting machine with a heat press machine having linear convex portions, and as shown in FIG. 2 (b), the thickness is formed to 1/3 of the total thickness. ing.

綿繊維シート2a相互が接合していない非接合部5aでは、綿繊維シート2aは、単に積層された状態に保持されている。   In the non-joining part 5a in which the cotton fiber sheets 2a are not joined to each other, the cotton fiber sheet 2a is simply held in a laminated state.

したがって、使用者が接合されていない非接合部5aから容易に1枚ずつ剥離することが可能である。   Therefore, it is possible to easily peel one by one from the non-joined portion 5a that is not joined by the user.

本実施形態では、エンボス加工による凹凸模様を、図1(a)では格子模様に、図2(a)では水玉模様にして実施したが、これらの模様に限られず、凹凸模様が市松模様、多角形凹部模様、亀甲模様等であってもよい。   In this embodiment, the concavo-convex pattern formed by embossing is a lattice pattern in FIG. 1A and a polka dot pattern in FIG. 2A. However, the concavo-convex pattern is not limited to these patterns. A square concave pattern, a tortoiseshell pattern, etc. may be sufficient.

積層する綿繊維シートの枚数は、任意に設定することが可能であるが、2枚以上であれば良く、好ましくは、2〜4枚が最適である。綿繊維シートを5枚以上重ねて積層すると化粧綿自体が嵩張り、製品コストが高くなる。   The number of the cotton fiber sheets to be laminated can be arbitrarily set, but may be two or more, preferably 2 to 4 is optimal. When five or more cotton fiber sheets are stacked and laminated, the decorative cotton itself is bulky and the product cost is increased.

複数枚のシート状に成形した綿繊維シートからなる化粧綿を1パックとして、1パックの化粧綿を複数個ビニール袋等の包装体(不図示)に梱包することにより、複数回分の化粧綿を利用することができ、従来の1回分使い切りのシートタイプ化粧品と比較して、経済的である。   A single pack of cosmetic cotton made of cotton fiber sheets formed into a plurality of sheets is packed in a package (not shown) such as a plastic bag to pack multiple pieces of cosmetic cotton. It can be used and is economical compared to conventional single-use sheet-type cosmetics.

(第3の実施形態)
上述の製造工程で成形された化粧綿の第3の実施形態では、図3に示すように、化粧綿が円形、楕円形、ハート形、三角形の線対称な形状にした場合の接合箇所を表した一例の平面図である。
(Third embodiment)
In the third embodiment of the decorative cotton molded in the above-described manufacturing process, as shown in FIG. 3, the joint portion in the case where the decorative cotton has a circular, oval, heart-shaped, triangular line-symmetric shape is represented. It is a top view of an example.

円形の綿繊維シート2bからなる化粧綿1bは、接合部分を周縁近傍部に2箇所設け、二つの線状凹部4bがそれぞれ平行して形成されている。   The decorative cotton 1b made of a circular cotton fiber sheet 2b has two joint portions in the vicinity of the peripheral edge, and two linear recesses 4b are formed in parallel.

楕円形の綿繊維シート2cからなる化粧綿1cとハート形の綿繊維シート2dからなる化粧綿1dは、円形の綿繊維シート2bと同様に接合部分を周縁近傍部に2箇所設け、楕円形の綿繊維シート2cには、二つの線状凹部4cが、またハート形の綿繊維シート2dには、二つの線状凹部4dが、それぞれ平行して形成されている。   The decorative cotton 1c made of the oval-shaped cotton fiber sheet 2c and the decorative cotton 1d made of the heart-shaped cotton fiber sheet 2d are provided with two joint portions in the vicinity of the periphery in the same manner as the circular cotton fiber sheet 2b. Two linear recesses 4c are formed in the cotton fiber sheet 2c, and two linear recesses 4d are formed in parallel in the heart-shaped cotton fiber sheet 2d.

また、三角形の綿繊維シート2eからなる化粧綿1eは、接合部分を周縁近傍部に1箇所設け、1つの線状凹部4eが周縁部の一辺に平行して形成されている。   Further, the decorative cotton 1e made of the triangular cotton fiber sheet 2e is provided with one joining portion in the vicinity of the peripheral edge, and one linear recess 4e is formed in parallel with one side of the peripheral edge.

さらに、化粧綿は、エンボス加工ステップのプレス圧を強くすることにより、ペーパーライク(化粧紙)のように薄くなって、毛羽立ちが抑えられ、マニキュアの拭き取り除去に使用することができる。   Furthermore, cosmetic cotton is thin like paper-like (decorative paper) by increasing the pressing pressure in the embossing step, and can be used for wiping and removing nail polish.

そして、化粧綿は、顔全体をパッティングした後、綿繊維シートを1枚ずつ剥離して、顔の気になる乾燥部分に貼って、パック用シートとして利用することができる。   Then, after putting the entire face, the cosmetic cotton can be used as a pack sheet by peeling the cotton fiber sheets one by one and pasting them on the dry part of the face.

なお、化粧綿は、複数枚の綿繊維シートを1枚ずつ取り出し可能とするとともに1枚の綿繊維シートの引張強度を保持する機能を有している。   In addition, cosmetic cotton has a function of making it possible to take out a plurality of cotton fiber sheets one by one and maintaining the tensile strength of one cotton fiber sheet.

本発明の化粧綿は、綿繊維素材で構成されているにも拘わらず、使用時に綿繊維の脱落がなく、綿繊維素材の風合いを残しつつ、柔軟性があり、肌触りがよい。   Although the cosmetic cotton of the present invention is composed of a cotton fiber material, the cotton fiber does not fall off during use, and the texture of the cotton fiber material remains, and the fabric is soft and soft to the touch.

また、本発明の化粧綿は、コンパクト化ができて、保管・持ち運びが容易となる。   Moreover, the cosmetic cotton of the present invention can be made compact, and can be easily stored and carried.

さらに、本発明の化粧綿の製造方法は、製造工程が簡単で、材料費・製品コストの安価な化粧綿を製造することができる。   Furthermore, the manufacturing method of the cosmetic cotton of the present invention can manufacture cosmetic cotton having a simple manufacturing process and low material cost and product cost.

綿繊維95重量%とポリエステルステープルファイバー(東洋紡績(株)製品)5重量%を含有した繊維集合体をカード機で成形した幅70cm、厚さ30mmのシート状長尺の綿帯を、精練工程で不純物を除去し、そのシート状の綿帯を漂白工程を得て、純白に漂白させた。次に、シート状の綿帯をプレス圧3kg/cm2でエンボス加工を施し、乾燥工程で電熱機で乾燥させた。そして、シート状の綿帯を巻取り工程でロール状に巻き取った後に、目付量が60g/m2の綿繊維シートを4枚重ねて積層した。そして、120℃に設定されたヒートプレス機付き裁断機で対向する一対の周縁近傍部をプレスして、2つの線状凹部を形成させ、熱溶着で接合させた。同時に所定寸法が横60×縦80mmの綿繊維シートに切断し、長方形で4層の綿繊維シートからなる厚さ2.5mmの化粧綿を得た。 A scouring process for a sheet-like long cotton band with a width of 70 cm and a thickness of 30 mm, which is a card assembly formed from a fiber assembly containing 95% by weight of cotton fiber and 5% by weight of polyester staple fiber (Toyobo Co., Ltd.) Then, the impurities were removed, and the sheet-like cotton band was bleached to be bleached to pure white. Next, the sheet-like cotton band was embossed at a press pressure of 3 kg / cm 2 and dried with an electric heater in the drying step. And after winding a sheet-like cotton band in the roll shape at the winding-up process, four cotton fiber sheets with a fabric weight of 60 g / m < 2 > were piled up and laminated | stacked. And a pair of peripheral peripheral part which opposes with the cutting machine with a heat press set to 120 degreeC was formed, two linear recessed parts were formed, and it joined by heat welding. At the same time, the cotton was cut into a cotton fiber sheet having a predetermined dimension of 60 × 80 mm to obtain a 2.5-mm-thick cosmetic cotton made of four layers of rectangular cotton fiber sheets.

実施例1の化粧綿は、綿繊維シートが平滑な構造を有していることから、剥離性は非常によく、さらりとした肌当たり感が得られ、毛羽立ちが非常に抑えられた。拭き取り具合は、通常のエンボス加工しないカット綿体と比べて大幅に向上していた。   Since the cotton fabric sheet of Example 1 had a smooth structure, the peelability was very good, a feeling of dry skin contact was obtained, and fuzz was extremely suppressed. The wiping condition was greatly improved compared to a cut cotton body that was not embossed.

綿繊維95重量%とポリエステルステープルファイバー(東洋紡績(株)製品)5重量%を含有した繊維集合体を実施例1と同様な工程を経て、プレス圧は、0.1kg/cm2でエンボス加工を施し、巻取り工程でロール状に巻き取った。目付量が120g/m2の綿繊維シートを2枚重ねて積層して、実施例1と同様な工程を経て、所定寸法が横50×縦70mmの綿繊維シートに切断し、長方形で2層の綿繊維シートからなる厚さ4.5mmの化粧綿を得た。 A fiber assembly containing 95% by weight of cotton fibers and 5% by weight of polyester staple fibers (product of Toyobo Co., Ltd.) is subjected to the same steps as in Example 1, and is embossed at a press pressure of 0.1 kg / cm 2. And wound up into a roll in the winding process. Two cotton fiber sheets with a basis weight of 120 g / m 2 are stacked and laminated, cut into a cotton fiber sheet having a predetermined dimension of 50 × 70 mm, and rectangular in two layers through the same process as in Example 1. A 4.5 mm-thick cosmetic cotton made of a cotton fiber sheet was obtained.

実施例2の化粧綿は、剥離性及び毛羽立ちは普通であるが、ふんわりとした肌当たり感が得られた。   The cosmetic cotton of Example 2 had normal peelability and fluffiness, but gave a soft touch to the skin.

綿繊維95重量%とポリエステルステープルファイバー(東洋紡績(株)製品)5重量%を含有した繊維集合体を実施例1と同様な工程を経て、プレス圧は、3kg/cm2でエンボス加工を施し、巻取り工程でロール状に巻き取った。目付量が180g/m2の綿繊維シートを3枚重ねて積層して、実施例1と同様な工程を経て、所定寸法が横60×縦80mmの綿繊維シートに切断し、長方形で3層の綿繊維シートからなる厚さ3.5mmの化粧綿を得た。 A fiber assembly containing 95% by weight of cotton fibers and 5% by weight of polyester staple fibers (product of Toyobo Co., Ltd.) was subjected to the same process as in Example 1 and embossed at a press pressure of 3 kg / cm 2. In the winding process, it was wound into a roll. Three cotton fiber sheets having a weight per unit area of 180 g / m 2 are stacked and laminated, cut into cotton fiber sheets having a predetermined dimension of 60 × 80 mm in length through the same steps as in Example 1, and three layers in a rectangular shape A 3.5 mm-thick cosmetic cotton made of a cotton fiber sheet was obtained.

実施例3の化粧綿は、表1に示す通り、剥離性は非常によく、毛羽立ちは非常に抑えられ、クッション性があり、ふんわりとした肌当たり感があり、保水性が大幅に向上していた。化粧水等に使用する場合に好適な化粧綿であった。   As shown in Table 1, the cosmetic cotton of Example 3 has very good peelability, very little fluffing, cushioning, soft skin feel, and water retention is greatly improved. It was. It was a cosmetic cotton suitable for use in lotions and the like.

綿繊維85重量%とポリエステルステープルファイバー(東洋紡績(株)製品)15重量%を含有した繊維集合体を実施例1と同様な工程を経て、プレス圧は、2kg/cm2でエンボス加工を施し、巻取り工程でロール状に巻き取った。目付量が120g/m2の綿繊維シートを4枚重ねて積層して、実施例1と同様な工程を経て、所定寸法が横50×縦60mmの綿繊維シートに切断し、長方形で4層の綿繊維シートからなる厚さ3mmの化粧綿を得た。 A fiber assembly containing 85% by weight of cotton fibers and 15% by weight of polyester staple fibers (Toyobo Co., Ltd.) was subjected to the same process as in Example 1 and embossed at a pressing pressure of 2 kg / cm 2. In the winding process, it was wound into a roll. Four cotton fiber sheets having a weight per unit area of 120 g / m 2 are stacked and laminated, cut into cotton fiber sheets having a predetermined dimension of 50 × 60 mm, and rectangular in four layers through the same steps as in Example 1. A 3 mm-thick cosmetic cotton made of a cotton fiber sheet was obtained.

実施例4の化粧綿は、剥離性は非常によく、クッション性があり、さらりとした肌当たり感があり、保水性及び拭き取り具合が大幅に向上していた。   The cosmetic cotton of Example 4 had very good peelability, cushioning properties, a feeling of dry skin contact, and water retention and wiping conditions were greatly improved.

綿繊維85重量%とポリエステルステープルファイバー(東洋紡績(株)製品)15重量%を含有した繊維集合体を実施例1と同様な工程を経て、プレス圧は、5kg/cm2でエンボス加工を施し、巻取り工程でロール状に巻き取った。目付量が240g/m2の綿繊維シートを4枚重ねて積層して、実施例1と同様な工程を経て、所定寸法が横45×縦65mmの綿繊維シートに切断し、長方形で4層の綿繊維シートからなる厚さ3.5mmの化粧綿を得た。 A fiber assembly containing 85% by weight of cotton fiber and 15% by weight of polyester staple fiber (product of Toyobo Co., Ltd.) was subjected to the same process as in Example 1 and embossed at a pressing pressure of 5 kg / cm 2. In the winding process, it was wound into a roll. Four cotton fiber sheets having a basis weight of 240 g / m 2 are stacked and laminated, cut into cotton fiber sheets having a predetermined dimension of 45 × 65 mm in length through the same steps as in Example 1, and are rectangular in four layers. A 3.5 mm-thick cosmetic cotton made of a cotton fiber sheet was obtained.

実施例5の化粧綿は、剥離性は非常によく、さらりとした肌当たり感があり、毛羽立ち、保水性及び拭き取り具合が大幅に向上していた。
(比較例1)
The cosmetic cotton of Example 5 had very good peelability, a feeling of smooth skin contact, and fuzziness, water retention and wiping conditions were greatly improved.
(Comparative Example 1)

綿繊維95重量%とポリエステルステープルファイバー(東洋紡績(株)製品)5重量%を含有した繊維集合体を実施例1と同様な工程を経て、エンボス加工による凹凸模様を施さないで、巻取り工程でロール状に巻き取った。目付量が60g/m2の綿繊維シートを4枚重ねて積層して、実施例1と同様な工程を経て、所定寸法が横60×縦80mmの綿繊維シートに切断し、長方形で4層の綿繊維シートからなる厚さ5mmの化粧綿を得た。 A fiber assembly containing 95% by weight of cotton fibers and 5% by weight of polyester staple fibers (product of Toyobo Co., Ltd.) is subjected to the same process as in Example 1 and the winding process without embossing the uneven pattern. And rolled up into a roll. Four cotton fiber sheets with a basis weight of 60 g / m 2 are stacked and laminated, cut into a cotton fiber sheet having a predetermined dimension of 60 × 80 mm in length through the same steps as in Example 1, and 4 layers in a rectangular shape A 5 mm-thick cosmetic cotton made of a cotton fiber sheet was obtained.

比較例1の化粧綿は、表1に示す通り、ふんわりとした肌当たり感があったが、剥離性がやや悪く、毛羽立ち及び保水性があまりよくなかった。
(比較例2)
As shown in Table 1, the cosmetic cotton of Comparative Example 1 had a soft touch per skin, but the peelability was slightly poor and the fuzziness and water retention were not very good.
(Comparative Example 2)

綿繊維100重量%からなる綿繊維を実施例1と同様な工程を経て、比較例1と同様にエンボス加工による凹凸模様を施さないで、巻取り工程でロール状に巻き取った。目付量が180g/m2の綿繊維シートを4枚重ねて積層して、実施例1と同様な工程を経て、所定寸法が横60×縦80mmの綿繊維シートに切断し、長方形で4層の綿繊維シートからなる厚さ7mmの化粧綿を得た。 A cotton fiber composed of 100% by weight of cotton fiber was wound in the form of a roll in the winding step without giving an uneven pattern by embossing as in Comparative Example 1 through the same steps as in Example 1. Four cotton fiber sheets having a weight per unit area of 180 g / m 2 are stacked and laminated, cut into cotton fiber sheets having a predetermined dimension of 60 × 80 mm, and rectangular in four layers through the same steps as in Example 1. A 7-mm-thick cosmetic cotton made of a cotton fiber sheet was obtained.

比較例2の化粧綿は、肌当たり感や保水性はよかったが、剥離性がやや悪く、熱溶融繊維を含有していないので、積層した綿繊維シートを強固に接合することができなくて型くずれが起きた。   The cosmetic cotton of Comparative Example 2 had good skin feel and water retention, but the peelability was slightly poor and it did not contain hot melt fibers, so the laminated cotton fiber sheets could not be firmly joined and lost shape. Happened.

<パック用シートの評価>
まず、貼付部位となる顔面に、化粧水を適量塗布し、そこにカットしたパック用シートを押さえ、乾燥した後、パック用シートを剥離した。
<Evaluation of pack sheet>
First, an appropriate amount of lotion was applied to the face to be affixed, and the pack sheet cut there was pressed and dried, and then the pack sheet was peeled off.

そして、パック用シートの剥離性、肌当たり感、毛羽立ち、保水性及び拭き取り具合について、評価した。   And the peelability of the sheet | seat for packs, a feeling of skin contact, fluffing, water retention, and the wiping condition were evaluated.

表1は、熱溶融繊維を含有し、エンボス加工のプレス圧を変化させた化粧綿を使用した本実施例とエンボス加工による凹凸模様を施さない化粧綿を使用した比較例である。   Table 1 is a comparative example using the present embodiment using the decorative cotton containing hot melt fibers and changing the pressing pressure of the embossing and the comparative cotton using the embossed decorative cotton.

実施例1〜5の化粧綿と比較例1,2の化粧綿について、剥離性、肌当たり感、毛羽立ち、保水性及び拭き取り具合の特性を、以下の評価基準に基づいて、◎、〇、△の3段階の評価を表1に示した。   About the cosmetic cotton of Examples 1 to 5 and the cosmetic cotton of Comparative Examples 1 and 2, the properties of peelability, skin contact feeling, fuzziness, water retention and wiping condition were evaluated based on the following evaluation criteria: ◎, ○, △ Table 1 shows the three-stage evaluation.

(剥離性、肌当たり感、保水性、拭き取り具合)
評 価 基 準 評 価
非 常 に 良 い ◎
普 通 〇
や や 悪 い △
(毛羽立ち)
評 価 基 準 評 価
非常に抑えられている ◎
抑えられている 〇
やや抑えられていない △
(Peelability, skin feel, water retention, wiping condition)
Evaluation criteria Evaluation
Very good ◎
Normal 〇
Somewhat bad △
(Fluffing)
Evaluation criteria Evaluation
Very suppressed ◎
Is suppressed 〇
Somewhat uncontrollable △

Figure 2007111115
Figure 2007111115

本発明の第1の実施形態を示した長方形シートタイプの化粧綿の斜視図とA−A線拡大断面図である。It is the perspective view and AA line expanded sectional view of the rectangular sheet type cosmetic cotton which showed the 1st Embodiment of this invention. 本発明の第2の実施形態を示した円形シートタイプの化粧綿の斜視図とA−A線拡大断面図である。It is the perspective view and AA line expanded sectional view of the circular sheet type cosmetic cotton which showed the 2nd Embodiment of this invention. 本発明の第3の実施形態を示した化粧綿の平面図である。It is a top view of the cosmetic cotton which showed the 3rd Embodiment of this invention. 本発明を適用した化粧綿の製造工程を説明するための工程図である。It is process drawing for demonstrating the manufacturing process of the cosmetic cotton to which this invention is applied.

符号の説明Explanation of symbols

1,1a,1b,1c,1d,1e ………化粧綿
2,2a,2b,2c,2d,2e ………綿繊維シート
3,3a ………凹凸模様
4,4a,4b,4c,4d,4e ………線状凹部
5,5a ………非接合部

1, 1a, 1b, 1c, 1d, 1e ......... Cosmetic cotton 2,2a, 2b, 2c, 2d, 2e ......... Cotton fiber sheet 3,3a ......... Uneven pattern 4,4a, 4b, 4c, 4d , 4e ......... Linear recess 5,5a ......... Non-joined part

Claims (8)

熱溶融繊維を含有する綿繊維シートが積層される多層構造の化粧綿であって、
1枚ずつ剥離可能に前記綿繊維シートにエンボス加工が施され、積層された前記綿繊維シートの周縁近傍部に1つ以上の線状凹部を設けることを特徴とする化粧綿。
A multi-layered decorative cotton in which cotton fiber sheets containing hot-melt fibers are laminated,
Embossing is performed on the cotton fiber sheets so that they can be peeled one by one, and one or more linear recesses are provided in the vicinity of the peripheral edge of the laminated cotton fiber sheets.
前記線状凹部が前記綿繊維シートの周縁部と交差することを特徴とする請求項1に記載の化粧綿。   2. The decorative cotton according to claim 1, wherein the linear recess intersects a peripheral edge of the cotton fiber sheet. 前記積層された綿繊維シート相互が前記線状凹部で接合されることを特徴とする請求項1又は2に記載の化粧綿。   The decorative cotton according to claim 1 or 2, wherein the laminated cotton fiber sheets are joined to each other at the linear recesses. 前記綿繊維シートは、熱溶融繊維を5〜15重量%含有することを特徴とする請求項1〜3のいずれか1項に記載の化粧綿。   The said cotton fiber sheet contains 5-15 weight% of hot melt fibers, The cosmetic cotton of any one of Claims 1-3 characterized by the above-mentioned. 前記綿繊維シートの1枚の目付量が60〜240g/m2であることを特徴とする請求項1〜4のいずれか1項に記載の化粧綿。 5. The decorative cotton according to claim 1, wherein the basis weight of one of the cotton fiber sheets is 60 to 240 g / m 2 . 綿のエンボス加工、積層、接合・切断の各工程を有する化粧綿の製造方法であって、
前記綿繊維シートにエンボス加工を施すステップと、
前記綿繊維シートを多層構造に積層するステップと、
前記綿繊維シートの周縁近傍部に周縁部と交差する1つ以上の線状凹部を設けるステップと、
前記綿繊維シート相互が前記線状凹部で接合するステップと、
を有することを特徴とする化粧綿の製造方法。
A method for producing decorative cotton having embossing, laminating, joining and cutting steps of cotton,
Embossing the cotton fiber sheet;
Laminating the cotton fiber sheet into a multilayer structure;
Providing one or more linear recesses intersecting the peripheral edge in the peripheral vicinity of the cotton fiber sheet;
Bonding the cotton fiber sheets to each other at the linear recesses;
A method for producing cosmetic cotton, comprising:
前記エンボス加工ステップが、前記綿繊維シートの片面若しくは両面に施されたことを特徴とする請求項6項に記載の化粧綿の製造方法。   The said embossing step was given to the single side | surface or both surfaces of the said cotton fiber sheet, The manufacturing method of the cosmetic cotton of Claim 6 characterized by the above-mentioned. 前記エンボス加工ステップのプレス圧は、0.1〜5kg/cm2であることを特徴とする請求項6又は7に記載の化粧綿の製造方法。
Pressing pressure of the embossing step, cosmetic method for producing cotton according to claim 6 or 7, characterized in that a 0.1 to 5 kg / cm 2.
JP2005303198A 2005-10-18 2005-10-18 Cosmetic cotton and method for producing the same Active JP4796371B2 (en)