JP2007062138A - Embossed decorative paper, its manufacturing method, and paper container using using it - Google Patents
Embossed decorative paper, its manufacturing method, and paper container using using it Download PDFInfo
- Publication number
- JP2007062138A JP2007062138A JP2005250957A JP2005250957A JP2007062138A JP 2007062138 A JP2007062138 A JP 2007062138A JP 2005250957 A JP2005250957 A JP 2005250957A JP 2005250957 A JP2005250957 A JP 2005250957A JP 2007062138 A JP2007062138 A JP 2007062138A
- Authority
- JP
- Japan
- Prior art keywords
- paper
- embossed
- embossed decorative
- decorative paper
- glossy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、板紙等紙基材の表面にエンボス加工で微細な凹凸を施して加飾し、その商品価値を高めるエンボス加飾紙およびその製造方法、それを用いたエンボス加飾紙製容器に関するものであり、特に、高級清酒や高級菓子類等の紙箱用として、特殊な高級感と光の微細な動き（シズル感）を表現するエンボス加飾紙及びその製造方法並びにそれを用いた紙製容器に関する。 TECHNICAL FIELD The present invention relates to embossed decorative paper for embellishing the surface of a paper base material such as paperboard by embossing and decorating it, increasing its commercial value, a method for producing the same, and an embossed decorative paper container using the embossed decorative paper In particular, for paper boxes such as high-quality sake and high-class confectionery, embossed decorative paper that expresses a special high-class feeling and fine movement of light (sizzle feeling), a manufacturing method thereof, and a paper made using the same Concerning the container.
従来、例えば高級清酒やウイスキーあるいは菓子類などの紙箱として、その側壁面にエンボス加工で模様状の微細な凹凸を施し、その紙箱の商品価値を高めたエンボス加飾紙が知られ、各分野の紙箱として利用されている。 Conventionally, for example, high-quality sake, whiskey or confectionery paper boxes, embossed decorative paper that has been embossed on the side wall surface to increase the product value of the paper box has been known. It is used as a paper box.
さらに、それら紙箱を美麗化するため、例えば、図４の側断面図に示すように、紙基材（１１０）の表面にアルミニウム箔などでなる金属光沢層（１８０）を施し、それに印刷層（１３０）とエンボス加工で模様状の微細な凹凸パターン（１７０）とが見当が合った状態でエンボス加工が施されたエンボス加工紙（３０）がある（例えば、特許文献１参照。）。 Furthermore, in order to beautify these paper boxes, for example, as shown in the side sectional view of FIG. 4, a metallic luster layer (180) made of aluminum foil or the like is applied to the surface of the paper substrate (110), and a printed layer ( 130) and embossed paper (30) embossed in a state in which the pattern of fine concavo-convex pattern (170) formed by embossing is in register (see, for example, Patent Document 1).
以下に、上記先行技術文献を示す。
しかしながら、上記の従来技術、すなわち紙基材の表面にアルミニウム箔などで金属光沢層が施された金属光沢原紙を用い、その金属光沢層面にエンボス加工により模様状（万線状等）の微細な凹凸パターンを施したものは、その金属光沢の部分においてはエンボス加工によるきらきらした表現の高級感には向いているが、これとは異なるきらきらせず落ち着いた重厚感のある高級感に乏しいものであった。 However, the above-mentioned conventional technique, that is, a metallic glossy base paper having a metallic gloss layer coated with an aluminum foil or the like on the surface of a paper substrate, and the metallic gloss layer surface is embossed to form a fine pattern (such as a line). The one with the concavo-convex pattern is suitable for the high-class feeling of the glittering expression by embossing in the metallic luster part, but it is different from this and it is poor in the high-class feeling with a calm and solid feeling. there were.
さらにエンボス加工による文字やパターンを表現する凹凸のピッチが、０．８ｍｍ以上の粗いものであり、光の微細な動きを表現する所謂「シズル感」に欠けるという問題点があった。 Furthermore, the pitch of the unevenness expressing characters and patterns by embossing is a rough pitch of 0.8 mm or more, and there is a problem that the so-called “sizzle feeling” expressing fine movement of light is lacking.
本発明は、かかる従来技術の問題点を解決するものであり、その課題とするところは、紙基材上の印刷面にエンボス加工で文字やパターンでなる模様状の微細な凹凸を施したエンボス加飾紙において、特に落ち着きのある高級感とシズル感のあるエンボス加飾紙及びその製造方法並びにそれを用いた紙製容器を提供することにある。 The present invention solves such problems of the prior art, and the problem is that the embossing has a printed surface on a paper base material with embossed fine irregularities made of letters and patterns. An object of the present invention is to provide an embossed decorative paper having a high-class feeling and a sizzling feeling, a manufacturing method thereof, and a paper container using the decorative decorative paper.
本発明に於いて上記課題を達成するために、まず請求項１の発明では、紙基材の表面に少なくとも印刷層と光沢コート層が順に施されているエンボス加飾光沢原紙の所定の印刷部分に、エンボス加工による微細な凹凸状パターンが施されていることを特徴とするエンボス加飾紙としたものである。
In order to achieve the above object in the present invention, first, in the invention of
また、請求項２の発明では、前記エンボス加工されるエンボス加飾光沢原紙の所定の印刷部分は、明度が低く、かつ表面光沢度が高いことを特徴とする請求項１記載のエンボス
加飾紙としたものである。
The embossed decorative paper according to
また、請求項３の発明では、前記微細な凹凸状パターンの凸部は、ピッチが０．０５〜０．８ｍｍ、高さが１５〜２００μｍの範囲であることを特徴とする請求項１または２記載のエンボス加飾紙としたものである。 According to a third aspect of the present invention, the convex portions of the fine concavo-convex pattern have a pitch of 0.05 to 0.8 mm and a height of 15 to 200 μm. The embossed decorative paper is described.
また、請求項４の発明では、紙基材の表面に少なくとも印刷層と光沢コート層が順に施されているエンボス加飾光沢原紙の所定の印刷部分に、上下に往復運動する空押し版の面でエンボス加工して微細な凹凸状パターンを施すことを特徴とするエンボス加飾紙の製造方法としたものである。 In the invention of claim 4, the surface of the empty press plate that reciprocates up and down on a predetermined printed portion of the embossed glossy base paper in which at least the printing layer and the gloss coat layer are sequentially applied on the surface of the paper substrate. And embossing to give a fine concavo-convex pattern.
また、請求項５の発明では、前記エンボス加工するエンボス加飾光沢原紙の所定の印刷部分は、明度が低く、かつ表面光沢度が高いことを特徴とする請求項４記載のエンボス加飾紙の製造方法としたものである。
Further, in the invention of
また、請求項６の発明では、前記微細な凹凸状パターンの凸部は、ピッチを０．０５〜０．８ｍｍ、高さを１５〜２００μｍの範囲とすることを特徴とする請求項４または５記載のエンボス加飾紙の製造方法としたものである。 In the invention of claim 6, the convex portions of the fine concavo-convex pattern have a pitch of 0.05 to 0.8 mm and a height of 15 to 200 μm. It is set as the manufacturing method of the embossed decorative paper of description.
さらにまた、請求項７の発明では、上記請求項１乃至３のいずれかに記載のエンボス加飾紙および上記請求項４乃至６のいずれかに記載のエンボス加飾紙の製造方法を用いたエンボス加飾紙製容器としたものである。
Furthermore, in invention of Claim 7, the emboss using the embossed decorative paper in any one of the said
本発明は以上の構成であるから、下記に示す如き効果がある。 Since this invention is the above structure, there exist the following effects.
即ち、上記請求項１に係る発明によれば、紙基材の表面に少なくとも印刷層と光沢コート層が順に施されているエンボス加飾光沢原紙の所定の印刷部分に、エンボス加工による微細な凹凸状パターンが施されていることによって、高級感と光の微細な動きを表現する（シズル感のある）エンボス加飾紙とすることができる。 That is, according to the first aspect of the present invention, fine embossing by embossing is performed on a predetermined printed portion of the embossed glossy base paper in which at least a printing layer and a glossy coating layer are sequentially applied to the surface of the paper substrate. The embossed decorative paper that expresses a high-class feeling and fine movement of light (with a sizzle feeling) can be obtained by applying the shape pattern.
また、上記請求項２に係る発明によれば、エンボス加工されるエンボス加飾光沢原紙の所定の印刷部分は、明度が低く、かつ表面光沢度が高いことによって、より落ち着いた高級感のあるエンボス加飾紙とすることができる。 According to the second aspect of the present invention, the predetermined printed portion of the embossed glossy glossy base paper to be embossed has a low brightness and a high surface gloss, so that the embossing has a more calm and high-class feeling. It can be decorated paper.
上記明度の目安としては２５以下（ＪＩＳ Ｚ８７２９ Ｌ＊ａ＊ｂ 表色系）で、かつ入射角６０°における表面光沢度の目安としては４５以上程度であり、光る部分と影になる部分の見掛け上の差が大きいほどより落ち着いた高級感のあるエンボス加飾紙とすることができる。 The lightness standard is 25 or less (JIS Z8729 L * a * b color system), and the surface glossiness standard at an incident angle of 60 ° is about 45 or more. The larger the difference, the more embossed decorative paper with a more luxurious feel.
また、上記請求項３に係る発明によれば、微細な凹凸状パターンの凸部は、ピッチが０．０５〜０．８ｍｍ、高さが１５〜２００μｍの範囲とするもので、このような形状の微細な凹凸状パターンとすることによって、より落ち着いた高級感とよりシズル感のあるエンボス加飾紙とすることができる。 According to the third aspect of the invention, the convex portions of the fine concavo-convex pattern have a pitch in the range of 0.05 to 0.8 mm and a height in the range of 15 to 200 μm. By using a fine concavo-convex pattern, embossed decorative paper with a more relaxed luxury and sizzle can be obtained.
上記微細な凹凸状パターンの凸部のピッチが０．０５ｍｍに満たないと、一般的な腐食によるエンボス版の加工が困難で、逆にピッチが０．８ｍｍを越えると、光の細かな動き（シズル感という）を表現する効果が得られないので好ましくない。 If the pitch of the convex portions of the fine concavo-convex pattern is less than 0.05 mm, it is difficult to process an embossed plate by general corrosion. Conversely, if the pitch exceeds 0.8 mm, a fine movement of light ( This is not preferable because an effect of expressing a sizzle feeling) cannot be obtained.
また、上記微細な凹凸状パターンの凸部の高さが１５μｍに満たないと加飾効果、すな
わち高級感とシズル感を表現する効果が得られず、上記のように凸部のピッチが０．０５〜０．８ｍｍでは凸部の高さが２００μｍを越えることは困難である。
Further, if the height of the convex portions of the fine concavo-convex pattern is less than 15 μm, a decorative effect, that is, an effect of expressing a high-class feeling and a sizzle feeling cannot be obtained, and the pitch of the convex portions is 0. When the height is from 05 to 0.8 mm, it is difficult for the height of the convex portion to exceed 200 μm.
また、上記請求項４に係る発明によれば、紙基材の表面に少なくとも印刷層と光沢コート層が順に施されているエンボス加飾光沢原紙の所定の印刷部分に、上下に往復運動する平板タイプの空押し版の面でエンボス加工して微細な凹凸状パターンを施すことによって、高級感と光の微細な動きを表現する（シズル感のある）エンボス加飾紙の製造方法とすることができる。 According to the fourth aspect of the present invention, a flat plate that reciprocates up and down on a predetermined printed portion of an embossed glossy base paper in which at least a printed layer and a glossy coat layer are sequentially provided on the surface of the paper base. By embossing on the surface of the type of blank press plate to give a fine concavo-convex pattern, a method for producing embossed decorative paper that expresses a sense of luxury and fine movement of light (with a sizzle) it can.
また、上記請求項５に係る発明によれば、エンボス加工するエンボス加飾光沢原紙の所定の印刷部分を、明度が低く、かつ表面光沢度が高いものとすることによって、より落ち着いた高級感のあるエンボス加飾紙の製造方法とすることができる。
Further, according to the invention according to
上記明度の目安としては２５以下で、かつ入射角６０°における表面光沢度の目安としては４５以上程度であり、光る部分と影になる部分の見掛け上の差を大きくするほどより落ち着いた高級感のあるエンボス加飾紙の製造方法とすることができる。 The above lightness is 25 or less and the surface glossiness at an incident angle of 60 ° is about 45 or more, and the higher the apparent difference between the shining part and the shadowing part, the more luxurious the feeling of calmness. It can be set as the manufacturing method of embossed decorative paper.
また、上記請求項６に係る発明によれば、微細な凹凸状パターンの凸部を、ピッチが０．０５〜０．８ｍｍ、高さが１５〜２００μｍの範囲のものとすることによって、より落ち着いた高級感とよりシズル感のあるエンボス加飾紙の製造方法とすることができる効果がある。 According to the invention of claim 6 described above, the convex portions of the fine concavo-convex pattern are more settled by having a pitch of 0.05 to 0.8 mm and a height of 15 to 200 μm. There is the effect that it can be set as the manufacturing method of embossed decorative paper with a sense of luxury and a more sizzle.
上記微細な凹凸状パターンの凸部のピッチが０．０５ｍｍに満たないと、一般的な腐食によるエンボス版の加工が困難で、逆にピッチが０．８ｍｍを越えると、光の細かな動き（シズル感という）を表現する効果が得られないので好ましくない。 If the pitch of the convex portions of the fine concavo-convex pattern is less than 0.05 mm, it is difficult to process an embossed plate by general corrosion. Conversely, if the pitch exceeds 0.8 mm, a fine movement of light ( This is not preferable because an effect of expressing a sizzle feeling) cannot be obtained.
また、上記微細な凹凸状パターンの凸部の高さが１５μｍに満たないと加飾効果、すなわち高級感とシズル感を表現する効果が得られず、上記のように凸部のピッチが０．０５〜０．８ｍｍでは凸部の高さが２００μｍを越えることは困難となる。 Further, if the height of the convex portions of the fine concavo-convex pattern is less than 15 μm, a decorative effect, that is, an effect of expressing a high-class feeling and a sizzle feeling cannot be obtained, and the pitch of the convex portions is 0. If the height is from 05 to 0.8 mm, it is difficult for the height of the convex portion to exceed 200 μm.
さらにまた、上記請求項７に係る発明によれば、上記請求項１乃至３のいずれかに記載のエンボス加飾紙および上記請求項４乃至６のいずれかに記載のエンボス加飾紙の製造方法を用いたエンボス加飾紙製容器とすることによって、従来のアルミニウム箔等を用いた金属光沢層を有する原紙にエンボス加工したエンボス加飾紙を用いた紙容器とは異なり落ち着いた重厚感のある高級感と光の細かな動きを表現する「シズル感」に優れる紙製容器を提供できる効果がある。
Furthermore, according to the invention which concerns on the said Claim 7, the manufacturing method of the embossed decorative paper in any one of the said
従って本発明は、高級清酒や菓子類等の紙箱用として、特殊な高級感と光の微細な動きを表現を可能にするエンボス加飾紙およびその製造方法並びにそれを用いた紙製容器として、優れた実用上の効果を発揮する。 Therefore, the present invention, for paper boxes such as high-quality sake and confectionery, embossed decorative paper that enables the expression of a special high-class feeling and fine movement of light, a method for producing the same, and a paper container using the embossed decorative paper, Exhibits excellent practical effects.
以下本発明を実施するための最良の形態を図面を用いて詳細に説明する。 The best mode for carrying out the present invention will be described below in detail with reference to the drawings.
図１は、本発明のエンボス加飾紙の製造方法の一事例を示すもので、その側断面を拡大した説明図であり、図２は、本発明のエンボス加飾紙の一事例を示すもので、その側断面拡大図である。また図３は、本発明のエンボス加飾紙を用いた紙製容器の一事例を説明する斜視図である。 FIG. 1 shows an example of a method for producing embossed decorative paper according to the present invention, and is an explanatory view showing an enlarged side section thereof. FIG. 2 shows an example of embossed decorative paper according to the present invention. FIG. FIG. 3 is a perspective view for explaining an example of a paper container using the embossed decorative paper of the present invention.
本発明は、例えば、図１（ｂ）の側断面拡大図に示すように、紙基材（１０）の表面に
印刷層（１３）と光沢コート層（１４）が順に施されているエンボス加飾光沢原紙（２）を用い、その印刷層（１３）のある部分に、図１（ａ）の側断面拡大図に示すように、微細な凸凹状パターン（２７）が施された平板タイプの空押し版（２０）の加圧により、例えば、図２の側断面拡大図に示すように、微細な凹凸状パターン（１７）が施されているエンボス加飾紙（１）と、その製造方法に関するものであり、並びに、例えば、図３の斜視図に示すように、胴部側壁面の印刷層（図示せず）の部分に、エンボス加工によりこの微細な凹凸状パターン（１７）が施された高級感と光の微細な動きを表現する（シズル感のある）紙製容器（３）とすることに関するものである。
In the present invention, for example, as shown in the enlarged side sectional view of FIG. 1 (b), an embossing process in which a printing layer (13) and a gloss coating layer (14) are sequentially applied to the surface of a paper substrate (10). As shown in the enlarged side sectional view of FIG. 1 (a), a flat-plate type of decorative glossy base paper (2) is used, as shown in the enlarged side sectional view of FIG. The embossed decorative paper (1) on which a fine uneven pattern (17) is applied, as shown in the enlarged side sectional view of FIG. In addition, as shown in the perspective view of FIG. 3, for example, the fine concavo-convex pattern (17) is embossed on the printed layer (not shown) on the side wall surface of the body. A high-quality paper and a paper container (3) that expresses the fine movement of light. The present invention relates to door.
上記請求項１に係る発明は、例えば、図１（ｂ）に示すように、コートボール等板紙で紙層（１１）の表面に塗工層（１２）のある紙基材（１０）を用い、その上に絵柄等の印刷層（１３）を形成し、その上全面に高光沢ニス等による光沢コート層（１４）を施してエンボス加飾光沢原紙（２）を得る。
The invention according to
上記で得られるエンボス加飾光沢原紙（２）は、高光沢印刷物として一般の紙製容器としてそのまま使用されることがある。 The embossed glossy base paper (2) obtained above may be used as a general paper container as a high gloss printed matter.
本発明では、図１（ｂ）に示す上記エンボス加飾光沢原紙（２）の印刷層（１３）の部分に、図２に示すように、エンボス加工により微細な凹凸状パターン（１７）が施されたエンボス加飾紙（１）である。 In the present invention, a fine concavo-convex pattern (17) is applied to the printed layer (13) of the embossed glossy base paper (2) shown in FIG. 1 (b) by embossing as shown in FIG. Embossed decorative paper (1).
また、上記請求項２に係る発明では、図１（ｂ）に示すように、エンボス加工されるエンボス加飾光沢原紙（２）の印刷層（１３）の部分は、明度が低く、かつ表面光沢度が高いことを特徴とするもので、例えば、明度の目安としては２５以下（ＪＩＳ Ｚ８７２９
Ｌ＊ａ＊ｂ 表色系）と暗い方が好ましく、かつ入射角６０°における表面光沢度（ＪＩＳ Ｋ ７１０５のプラスチックの光学的特性試験方法に準拠した測定値）の目安としては４５以上、好ましくは６０以上であり、光る部分と影になる部分の見掛け上の差を大きくするほど良く、それにより落ち着いた重厚な高級感のあるエンボス加飾紙（１）とするものである。
In the invention according to
L * a * b color system) and darker are preferable, and the surface glossiness (measured value based on the plastic optical property test method of JIS K 7105) at an incident angle of 60 ° is preferably 45 or more, preferably Is 60 or more, and it is better to increase the apparent difference between the shining part and the shadowed part, thereby making the embossed decorative paper (1) with a calm and luxurious feeling.
また、上記請求項３に係る発明では、図２に示すように、微細な凹凸状パターン（１７）の凸部のピッチ（Ｐ）が０．０５〜０．８ｍｍ、その高さ（Ｈ）が１５〜２００μｍの範囲とするものである。 In the invention according to claim 3, as shown in FIG. 2, the pitch (P) of the convex portions of the fine concavo-convex pattern (17) is 0.05 to 0.8 mm, and the height (H) is The range is 15 to 200 μm.
上記のような形状、すなわち凸部のピッチ（Ｐ）とその高さ（Ｈ）でなる微細な凹凸状パターン（１７）とすることによって、より落ち着いた高級感とより「シズル感」のあるエンボス加飾紙（１）とすることができるものである。 Embossing with a more relaxed luxury and more “sizzle” by using the above-mentioned shape, that is, a fine uneven pattern (17) consisting of the pitch (P) and height (H) of the protrusions. The decorative paper (1) can be used.
上記のように微細な凹凸状パターン（１７）の凸部のピッチ（Ｐ）が０．０５ｍｍに満たないと、図１（ａ）に示すような凸凹状パターン（２７）を通常の技術による一般的な腐食によっては空押し板（２０）に施すことが困難で、逆にピッチ（Ｐ）が０．８ｍｍを越えると、光の細かな動き（シズル感という）を表現する効果が得られないので好ましくない。 If the pitch (P) of the convex portions of the fine concavo-convex pattern (17) is less than 0.05 mm as described above, the concavo-convex pattern (27) as shown in FIG. It is difficult to apply to the empty push plate (20) due to the general corrosion, and conversely, if the pitch (P) exceeds 0.8 mm, the effect of expressing fine movement of light (squeezed feeling) cannot be obtained. Therefore, it is not preferable.
また、図２に示すように、微細な凹凸状パターン（１７）の凸部の高さ（Ｈ）が１５μｍに満たないと細か過ぎて加飾効果、すなわち高級感と「シズル感」を表現する効果が得られず、上記のように凸部のピッチ（Ｐ）が０．０５〜０．８ｍｍの範囲では凸部の高さ（Ｈ）が２００μｍを越えることは殆どない。 Further, as shown in FIG. 2, if the height (H) of the convex portion of the fine concavo-convex pattern (17) is less than 15 μm, it is too fine to express a decoration effect, that is, a high-class feeling and a “sizzle feeling”. No effect is obtained, and the height (H) of the convex portion hardly exceeds 200 μm when the pitch (P) of the convex portion is in the range of 0.05 to 0.8 mm as described above.
上記微細な凹凸状パターン（１７）の形状は、特に限定するものではないが、例えば、
図３の斜視図の一部に示すように、凸部が万線状で構成される凹凸状パターン（１７ａ）としたり、凸部が網点状で構成される凹凸状パターン（１７ｂ）とすることもでき、その他波形万線状、点線状、点線万線状、それらの組合せなどでなる凹凸状パターンとすることもできる。
The shape of the fine concavo-convex pattern (17) is not particularly limited.
As shown in a part of the perspective view of FIG. 3, a convex / concave pattern (17a) in which convex portions are formed in a line shape, or an uneven pattern (17b) in which convex portions are formed in a dot shape. In addition, it can also be a concavo-convex pattern made up of corrugated lines, dotted lines, dotted lines, combinations thereof, or the like.
また、上記請求項４、５、６に係る発明は、図２に示すようなエンボス加飾紙（１）の製造方法であって、例えば、図１（ｂ）に示すように、紙基材（１０）の表面に印刷層（１３）と光沢コート層（１４）が順に施されているエンボス加飾光沢原紙（２）の印刷層（１３）のある部分に、下面に微細な凸凹状パターン（２７）が刻設されていて、上下に往復運動する空押し版（２０）を用い、その下面で加圧して、図２に示すような微細な凹凸状パターン（１７）をエンボス加飾光沢原紙（２）の表面に施すことを特徴とするエンボス加飾紙の製造方法である。
The invention according to
上記加圧の条件として、その温度の幅は、５〜１８０℃で、５℃以下でも加飾効果が得られる場合があるが、温度が高い方が加飾効果、すなわち微細な凹凸状パターン（１７）が再現されやすく、よって５℃以下の温度にするメリットはない。このように温度が高い方が加飾効果が出やすいが、温度が高くなり過ぎると紙基材（１０）が歪んだり、印刷層（１３）のインキがはぎ取られたりする危惧があり、上記温度１８０℃を越すことのメリットはない。 As a condition for the pressurization, the temperature range is 5 to 180 ° C., and a decoration effect may be obtained even at 5 ° C. or less, but the higher the temperature, the higher the decoration effect, that is, a fine uneven pattern ( 17) is easy to reproduce, so there is no merit of setting the temperature to 5 ° C. or lower. In this way, the higher the temperature, the easier the decorative effect is. However, if the temperature is too high, the paper substrate (10) may be distorted or the ink of the printing layer (13) may be stripped. There is no merit of exceeding the temperature of 180 ° C.
また、圧力の幅は、０．５〜４００ＭＰａで、０．５ＭＰａ以下では、加飾効果が低く、４００ＭＰａを越えると想定している紙基材（１０）の変形が大きくなり過ぎ、さらに空押し板（２０）の微細な凸凹状パターン（２７）が破壊される危惧があり好ましくはない。 Further, the pressure range is 0.5 to 400 MPa, and if it is 0.5 MPa or less, the decoration effect is low, and the deformation of the paper base material (10) that is assumed to exceed 400 MPa becomes too large. There is a risk that the fine uneven pattern (27) of the plate (20) is destroyed, which is not preferable.
さらにまた、上記請求項７に係る発明は、例えば、図３の斜視図に示すように、上記のようなエンボス加飾紙の製造方法で得られたエンボス加飾紙（１）を用いて、エンボス加飾された紙製容器（５）とするもので、この紙製容器（５）の胴部側壁の明度が低く、光沢度が高い印刷層（図示せず）と、その上の光沢コート層のある部分に種々の微細な凹凸状パターン（１７）が施され、従来の金属光沢層を有する原紙を用いたものとは異なり、特殊な重厚感のある高級感と「シズレ感」に優れた美粧性の紙製容器（５）とするものである。 Furthermore, as shown in the perspective view of FIG. 3, for example, the invention according to claim 7 uses an embossed decorative paper (1) obtained by the above-described embossed decorative paper manufacturing method, An embossed paper container (5), a printed layer (not shown) having a low brightness and a high gloss on the side wall of the body of the paper container (5), and a gloss coat thereon Various fine concavo-convex patterns (17) are applied to the part where the layer is, and unlike the conventional one using the base paper having the metallic gloss layer, it is excellent in a special sense of luxury and "squealing" A cosmetic paper container (5).
以下に本発明のエンボス加飾紙（１）を構成するエンボス加飾光沢原紙（２）について説明する。 The embossed decorative glossy base paper (2) constituting the embossed decorative paper (1) of the present invention will be described below.
まず、図１（ｂ）に示す上記エンボス加飾紙（１）を構成する紙基材（１０）としては、例えば、坪量２１０ｇ／ｍ2 〜５００ｇ／ｍ2 程度のコートボール、ノーコートボール、アイボリーやカード紙のマニラボール、特殊マニラボールなどの板紙が使用されるが、エンボス加飾光沢原紙（２）としては表面光沢度が高い方が好ましいことから、紙層（１１）の表面に塗工層（１２）が施されたコートボールやカード紙などが好ましく使用される。 First, as the paper substrate (10) constituting the embossed decorative paper (1) shown in FIG. 1 (b), for example, basis weight 210g / m 2 ~500g / m 2 about coated board, no coated cardboard Paper boards such as ivory and cardboard manila balls and special manila balls are used, but as the embossed decorative glossy base paper (2), it is preferable that the surface gloss is high, so that the surface of the paper layer (11) Coated balls, card paper and the like to which the coating layer (12) has been applied are preferably used.
また、上記紙基材（１０）上に印刷層（１３）と光沢コート層（１４）を形成するエンボス加飾光沢原紙（２）とする高光沢印刷物としては、その光沢コート層（１４）に紫外線硬化型のコート材を用いる方法と水性のコート材を用いる方法がある。 Moreover, as a high glossy printed material used as the embossed glossy base paper (2) for forming the print layer (13) and the gloss coat layer (14) on the paper substrate (10), the gloss coat layer (14) There are a method using an ultraviolet curable coating material and a method using an aqueous coating material.
前者の紫外線硬化型のコート剤を用いる方法としては、例えば、色材としての顔料と、ポリエステル、ポリオール、エポキシ等の各アクリル酸エステルでなる光重合性素材やケトン樹脂等とでなるビヒクルと、光重合開始剤等の添加剤とで構成される紫外線硬化型の
オフセットインキ（以下ＵＶオフセットインキという）を用い、紙基材（１０）上にオフセット印刷方式により印刷層（１３）を形成し、このＵＶオフセットインキからほぼ色材としての顔料を除いた構成の紫外線硬化型コート材（以下ＵＶニスという）を用い、この印刷層（１３）を覆うようにオフセット印刷方式で光沢コート層（１４）を形成した構成のものが、乾燥性などの点から印刷と光沢コート層の形成がインラインで高効率な製造が可能なので一般化されている方法である。
As a method of using the former ultraviolet curable coating agent, for example, a pigment and a vehicle made of a photopolymerizable material made of each acrylic ester such as polyester, polyol, epoxy, or a ketone resin, Using a UV curable offset ink (hereinafter referred to as UV offset ink) composed of additives such as a photopolymerization initiator, a printing layer (13) is formed on a paper substrate (10) by an offset printing method, A UV curable coating material (hereinafter referred to as UV varnish) having a configuration in which the pigment as a coloring material is substantially removed from the UV offset ink, and a glossy coating layer (14) by an offset printing method so as to cover the printing layer (13). Is a generalized product that can be printed and gloss coated layers can be produced in-line and highly efficiently from the viewpoint of dryness. It is.
これに対し、上記のＵＶオフセットインキ、ＵＶニスを用いたエンボス加飾光沢原紙（２）は、紙製容器等の使用後、再生紙として再利用するに際し、再生紙の製造工程における脱墨性（古紙のインキがパルパー中の温水と薬品で剥がされ、泡とともに浮上させそのインキを除去すること）に劣ることから、後者の水性コート材を用いる方法は、この脱墨性に優れ、かつ有機溶剤を用いない、いわゆる環境に配慮された水性の光沢コート剤による光沢コート層（１４）を形成する方法で、この光沢コート剤として、例えばアクリル系樹脂のエマルジョンでなる水性コート材があり、この水性コート材をロールコート法あるいはアニロックスロールを介してコート材を転移するフレキソコート法、グラビアコート法などで塗布し、次いでこの上からプレス加工を行って光沢コート層（１４）とする方法である。 On the other hand, the embossed glossy base paper (2) using the UV offset ink and UV varnish described above is used as a recycled paper after the use of a paper container or the like, and is used for deinking in the manufacturing process of the recycled paper. (The waste paper ink is peeled off with warm water and chemicals in the pulper and floats along with bubbles to remove the ink.) The latter method using a water-based coating material is excellent in deinking and organic. A method for forming a glossy coat layer (14) with a so-called environment-friendly water-based glossy coating agent that does not use a solvent. As this glossy coating agent, for example, there is an aqueous coating material made of an acrylic resin emulsion. Apply a water-based coating material by the roll coating method or flexographic coating method that transfers the coating material via an anilox roll, gravure coating method, etc. A method for the glossy coating layer (14) performing Luo pressing.
また、上記印刷層（１３）としては、前述のようにＵＶオフセットインキを用いて形成する方法の他に、通常の油性枚葉インキ（色材としての顔料と、ビヒクルとしてのロジン変性フェノール樹脂、アルキッド樹脂等樹脂、大豆油等植物油と、添加剤としてのドライヤー等で構成されるインキ）を使用し、オフセット印刷法によって得ることもでき、あるいは水性または油性（有機溶剤使用）のグラビアインキを使用し、グラビア印刷法によって得ることもできる。 As the printing layer (13), in addition to the method of forming using UV offset ink as described above, ordinary oil-based sheet-fed ink (pigment as a coloring material and rosin-modified phenolic resin as a vehicle, It can be obtained by offset printing using resin such as alkyd resin, vegetable oil such as soybean oil and dryer as additive, etc., or using water or oil-based (organic solvent) gravure ink However, it can also be obtained by a gravure printing method.
以下に、本発明の具体的実施例について説明する。 Specific examples of the present invention will be described below.
図１（ｂ）に示す紙基材（１０）として、
坪量３１０ｇ／ｍ2 のカード紙：ニューＤＶ（北越製紙社製）を用い、
その表面にＵＶオフセットインキ：ＵＰＴＯＰ（東洋インキ製造社製）によりオフセット印刷法で印刷層（１３）を形成し、
この印刷層（１３）上にＵＶニス：ＵＶハイグロスニス（東洋インキ製造社製）を用いて、
オフセット印刷法で光沢コート層（１４）を形成して、試験用のエンボス加飾原紙（２）を得た。
As the paper substrate (10) shown in FIG.
Card paper having a basis weight of 310 g / m 2 : New DV (made by Hokuetsu Paper Co., Ltd.)
A printing layer (13) is formed on the surface by an offset printing method using UV offset ink: UPTOP (manufactured by Toyo Ink Manufacturing Co., Ltd.)
By using UV varnish: UV high gloss varnish (manufactured by Toyo Ink Co., Ltd.) on this printed layer (13),
A gloss coat layer (14) was formed by an offset printing method to obtain a test embossed decorative base paper (2).
得られたエンボス加飾原紙（２）の入射角６０°における表面光沢度（ＪＩＳ Ｋ ７１０５のプラスチックの光学的特性試験方法に準拠した測定値）は、４８で、エンボス加工される印刷層（１３）の明度は、暗いところで５程度であり、比較的明るいところでも２５程度のエンボス加飾原紙（２）であった。 The embossed decorative base paper (2) thus obtained had a surface glossiness (measured value in accordance with the plastic optical property test method of JIS K 7105) at an incident angle of 60 °, and was 48 (13) The brightness of the embossed decorative paper (2) was about 5 in a dark place and about 25 in a relatively bright place.
一方、図１（ａ）に示すような、凸部のピッチ（ＥＰ）が０．３０ｍｍで、その高さが０．３０ｍｍの微細な凸凹状パターン（２７）が部分的に腐食により刻設された空押し版（２０）を準備した。 On the other hand, as shown in FIG. 1 (a), a fine uneven pattern (27) having a protrusion pitch (EP) of 0.30 mm and a height of 0.30 mm is partially engraved by corrosion. An empty press plate (20) was prepared.
上記で準備された空押し版（２０）を、
箔押し機：ＳＰ１２６−ＢＭＡ型（ボブスト社製）に取付け、
版圧；１０ＭＰａ、
版温度；７０℃で、
上記で得られたエンボス加飾原紙（２）の光沢コート層（１４）面にエンボス加工して微細な凸凹状パターン（２７）が施されたエンボス加飾紙（１）を得た。
The empty press plate (20) prepared above is
Foil stamping machine: attached to SP126-BMA type (Bobst)
Plate pressure: 10 MPa,
Plate temperature: 70 ° C
The embossed decorative paper (1) was obtained by embossing the glossy coated layer (14) surface of the embossed decorative base paper (2) obtained above and having a fine uneven pattern (27).
以下に、本発明の比較例について説明する。 Below, the comparative example of this invention is demonstrated.
図４に示すように紙基材（１１０）として、坪量３１０ｇ／ｍ2 のカード紙：ニューＤＶ（北越製紙社製）を用い、
その表面にポリウレタン系のドライラミネーション用接着剤を介して厚み１２μｍのアルミニウム箔をラミネートして金属光沢層（１８０）とし、
その上にＵＶオフセットインキ：ＵＶトップ（東洋インキ製造社製）によりオフセット印刷法で印刷層（１３０）を形成し、
上記エンボス版を加熱せず常温とした以外は、実施例１と同様にしてエンボス加飾紙を得た。
As shown in FIG. 4, as a paper substrate (110), a card paper having a basis weight of 310 g / m 2 : New DV (made by Hokuetsu Paper Co., Ltd.)
The surface is laminated with a 12 μm thick aluminum foil via a polyurethane dry lamination adhesive to form a metallic luster layer (180),
On top of that, a printing layer (130) is formed by an offset printing method using UV offset ink: UV top (manufactured by Toyo Ink Manufacturing Co., Ltd.)
An embossed decorative paper was obtained in the same manner as in Example 1 except that the embossed plate was heated to room temperature without heating.
上記実施例１で得られたエンボス加飾紙は、明度が低く、表面光沢度が高い部分に微細な凸凹状パターンが施されているので、上記実施例２のアルミニウム箔による金属光沢層を有する原紙を用いたものとは異なり、落ち着いた重厚感のある高級感と光の細かい動きを表現する「シズル感」に優るエンボス加飾紙であった。 The embossed decorative paper obtained in Example 1 has a metallic luster layer made of the aluminum foil of Example 2 because the fine uneven pattern is applied to the portion having low brightness and high surface gloss. Unlike the base paper, this embossed decorative paper is superior to a “sizzle” that expresses a calm and luxurious feeling and fine movement of light.
１‥‥エンボス加飾紙
２‥‥エンボス加飾光沢原紙
５‥‥エンボス加飾紙製容器
１０‥‥紙基材
１１‥‥紙層
１２‥‥塗工層
１３‥‥印刷層
１４‥‥光沢コート層
１７‥‥エンボス加工された凹凸状パターン
１７ａ‥‥凸部が万線状でなる凹凸状パターン
１７ｂ‥‥凸部が網点状でなる凹凸状パターン
２０‥‥空押し版
２７‥‥刻設された凸凹状パターン
３０‥‥従来のエンボス加飾紙
１１０‥‥紙基材
１３０‥‥金属光沢層
１８０‥‥印刷層
ＥＨ‥‥空押し版の凸凹状パターンの凸部の高さ
ＥＰ‥‥エンボス版の凸凹状パターンの凸部のピッチ
Ｈ‥‥エンボス加飾紙の凹凸状パターンの凸部の高さ
Ｐ‥‥エンボス加飾紙の凹凸状パターンの凸部のピッチ
1 ... Embossed
Claims (7)