JP2006334361A - Solid deodorant composition - Google Patents
Solid deodorant composition Download PDFInfo
- Publication number
- JP2006334361A JP2006334361A JP2005190593A JP2005190593A JP2006334361A JP 2006334361 A JP2006334361 A JP 2006334361A JP 2005190593 A JP2005190593 A JP 2005190593A JP 2005190593 A JP2005190593 A JP 2005190593A JP 2006334361 A JP2006334361 A JP 2006334361A
- Authority
- JP
- Japan
- Prior art keywords
- deodorant composition
- solid deodorant
- compound
- essential oil
- natural essential
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、固形タイプの固形消臭性組成物に関するものである。 The present invention relates to a solid-type solid deodorant composition.
従来、消臭剤関係の製品、特許は各種類のものが製造、特許出願されているが、液状タイプ、霧状タイプのものは、固形タイプのものと比較して効果は大きいが、液が他のものに付着したり、液がこぼれたりするという欠点がある。
また、固形タイプの固形消臭剤も各種製造、特許出願されてはいるが、液状タイプ、霧状タイプのものに比べて、効果が十分でなく、また価格的にも高いもの多いというのが実状である。（特許文献１）
In addition, various types of solid-type deodorants have been manufactured and patent applications have been filed, but many of them are less effective and more expensive than liquid-type and mist-type types. It's real. (Patent Document 1)
本発明は、消臭性能を十分発揮し、芳香性も付与した、固形タイプの、廃棄物を利用した、安価で、環境問題にも配慮した固形消臭性組成物を提供する事を目的とする。 An object of the present invention is to provide a solid deodorant composition that exhibits solid deodorization performance and imparts fragrance, is solid, uses waste, is inexpensive, and is environmentally friendly. To do.
本発明者らは、上記問題点を解決するために鋭意検討した結果、天然精油、木酢酸、竹酢の少なくとも１種類の化合物と水酸化カルシウムを含む成形体により上記目的を達成しうることを見いだし本発明を完成した。
さらに、本発明は、酸化カルシウムおよび水を混合し反応させ、水酸化カルシウムを生成させた後、天然精油、木酢酸、竹酢の少なくとも１種類の化合物と混合したものからなる固形消臭性組成物を見いだし本発明を完成した。As a result of intensive studies to solve the above problems, the present inventors have found that the above object can be achieved by a molded product containing at least one compound of natural essential oil, wood acetic acid, bamboo vinegar and calcium hydroxide. The present invention has been completed.
Further, the present invention provides a solid deodorant composition comprising a mixture of calcium oxide and water to react to form calcium hydroxide and then mixed with at least one compound of natural essential oil, wood acetic acid and bamboo vinegar. I found something and completed the present invention.
ここで、上記酸化カルシウムとしては、廃棄物である貝殻を粉砕し、５００℃〜１８００℃で焼成した粉末を使用してもよい。
天然精油としては、オレンジ油の成分であるリモネンが挙げられる。
また、上記固形消臭性組成物と、アクリル酸ソーダ系ポリマーのような高吸水性樹脂を配合した固形消臭性組成物を使用してもよい。Here, as said calcium oxide, you may use the powder which grind | pulverized the shell which is a waste, and baked at 500 to 1800 degreeC.
Examples of natural essential oils include limonene, which is a component of orange oil.
Moreover, you may use the solid deodorant composition which mix | blended the said solid deodorant composition and superabsorbent resin like a sodium acrylate type polymer.
本発明の固形消臭性組成物は、その消臭性、芳香性等の性能が良好であるばかりでなく、廃棄物である貝殻を利用した、環境問題にも配慮したものであり、従来の固形消臭性組成物に比べて比較的安価に製造可能である。 The solid deodorant composition of the present invention is not only good in its deodorant performance, aromaticity, etc., but also in consideration of environmental problems using shells that are waste, Compared with a solid deodorant composition, it can be produced at a relatively low cost.
本発明の固形消臭性組成物について説明する。
本発明で使用される天然精油について説明する。
天然精油は、植物から得られる油であるが、その種類は非常に多く、高価なものも多い。天然精油の中でも、安価で、工業的にも大量に入手可能なテルペン化合物についてさらに説明する。
テルペン化合物は天然の植物系の精油中に多く含まれ、安全性に優れた化合物である。
工業的には、植物の幹、葉、実から抽出される。中でも松ヤニやオレンジの果皮から得られるものが多く利用されている。The solid deodorant composition of the present invention will be described.
The natural essential oil used in the present invention will be described.
Natural essential oils are oils obtained from plants, but there are many types and many expensive ones. Among natural essential oils, terpene compounds that are inexpensive and available in large quantities industrially will be further described.
Terpene compounds are abundant in natural plant-based essential oils and are excellent in safety.
Industrially, it is extracted from plant trunks, leaves and fruits. Of these, many are obtained from pine crabs and orange peels.
テルペン化合物としては、炭素数１０のモノテルペン化合物、炭素数１５のセスキテルペン化合物、炭素数２０のジテルペン化合物、炭素数３０のトリテルペン化合物、モノテルペン化合物の多量体等が挙げられる。これらのテルペン化合物には、鎖状構造のものや単環のもの、更に多環のものがある。また、その種類は炭化水素の他に、アルコール体、アルデヒド体、ケトン体、エーテル体、およびカルボキシル基体等があり、その何れも使用することができる。その具体的な例として例えば次のものが挙げられるがこれらに限定されるものではない。 Examples of the terpene compound include a monoterpene compound having 10 carbon atoms, a sesquiterpene compound having 15 carbon atoms, a diterpene compound having 20 carbon atoms, a triterpene compound having 30 carbon atoms, and a multimer of monoterpene compounds. These terpene compounds include those having a chain structure, monocyclic ones, and further polycyclic ones. In addition to hydrocarbons, there are alcohols, aldehydes, ketones, ethers, carboxyl bases, etc., any of which can be used. Specific examples thereof include the following, but are not limited thereto.
１）モノテルペン化合物の例
α−ピネン、β−ピネン、ジペンテン、リモネン、フェランドレン、α−テルピネン、γ−テルピネン、テルピノレン、ミルセン、アロオシメン、カンフェン、ボルニレン、パラメンテン−１、パラメンテン−２、パラメンテン−３、パラメンタジエン類、パラメンタン、２−カレン、３−カレン、ツジャン等のモノテルペン炭化水素類、α、βおよびγターピネオール、４−ターピネオール、パラメンテノール、パラメンタノール、ゲラニオール、リナロール、ネロール、シトロネロール、アロシメノール、ミルセノール、カルベオール、メントール、ボルネオール、イソボルネオール、フェンチルアルコール、ベルベノール等のモノテルペンアルコール類、シトラール、シトロネラール等のテルペンアルデヒド類、イソプレゴン、カルボン、カンファー等のテルペンケトン類、飽水テレピン、パラメンタンジオール等のテルペンジオール類、１，４−シネオール、１，８−シネオール等のテルペンエーテル等である。1) Examples of monoterpene compounds α-pinene, β-pinene, dipentene, limonene, ferrandolene, α-terpinene, γ-terpinene, terpinolene, myrcene, alloocimene, camphene, bornylene, paramenten-1, paramenten-2, paramenten- 3. Paratertadiene, paramentane, 2-carene, 3-carene, monoterpene hydrocarbons such as tujan, α, β and γ terpineol, 4-terpineol, paramentenol, paramentanol, geraniol, linalool, nerol Monoterpene alcohols such as citronellol, arosimenol, myrsenol, carveol, menthol, borneol, isoborneol, fentil alcohol, berbenol, and terpene aldehydes such as citral, citronellal Isopuregon, carboxylic, terpene ketones such as camphor, water-saturated turpentine, a terpene diols such as p-menthane diol, 1,4-cineole, 1,8-terpene ethers such as cineole, or the like.
２）セスキテルペン化合物の例
ロンギホレン、カリオフィレン、カジネン、ツヨプセン、セドレン、クロベン、ロンギピネン等のセスキテルペン炭化水素類、エレモール、カジノール、ユーデスモール等のセスキテルペンアルコール類等である。2) Examples of sesquiterpene compounds Sesquiterpene hydrocarbons such as longifolene, caryophyllene, kadinene, tsuyopsen, cedrene, cloben, and longgipinene, and sesquiterpene alcohols such as elemol, casinol, and eudesmol.
３）ジテルペン・トリテルペン化合物の例
カンフォレン、カウレン、アビエチノール、アビエチン酸、ピマール酸、イソピマール酸、レボピマール酸、ネオアビエチン酸等のロジン化合物、スクワレン等である。3) Examples of diterpene / triterpene compounds Rosin compounds such as camphorene, kaurene, abietinol, abietic acid, pimaric acid, isopimaric acid, levopimaric acid, neoabietic acid, and squalene.
４）モノテルペン化合物の多量体の例
ピネンダイマー、リモネンダイマー、アロオシメンダイマー等のモノテルペン化合物の２量体、ピネン重合体、ジペンテン重合体等のモノテルペンの重合体等である。4) Examples of multimers of monoterpene compounds Dimers of monoterpene compounds such as pinene dimer, limonene dimer, and alloocimene dimer, and polymers of monoterpenes such as pinene polymer and dipentene polymer.
これらのテルペン化合物は単独で使用しても良いし、また２種類以上組み合わせて使用することもできる。
テルペン化合物を含む天然精油は、消臭性を付与できると共に、芳香性も付与できる。
テルペン化合物の中でも、好ましくはリモネンである。These terpene compounds may be used alone or in combination of two or more.
A natural essential oil containing a terpene compound can impart deodorizing properties as well as fragrance.
Among the terpene compounds, limonene is preferable.
本発明の木酢液について説明する。
一般に木酢液は、樹木の幹や枝を無酸素あるいは低酸素状態で不完全燃焼して、その際発生する煙を冷却して液状物を生じさせ、さらに数ヶ月間静置させてタール分を沈降させて得られる。本発明の木酢液もこのようにして得られたものを使用してもよい。
具体的には、各種製品が市販されているが、（株）関東ウッドケミカル製木酢液原液や（株）関東ウッドケミカル製木酢液蒸留品等がある。The wood vinegar solution of the present invention will be described.
In general, wood vinegar liquid burns the trunks and branches of trees in an oxygen-free or low-oxygen state and cools the smoke that is generated to produce a liquid material. Obtained by settling. What was obtained in this way may also be used for the wood vinegar of this invention.
Specifically, various products are commercially available, such as Kanto Wood Chemical Co., Ltd. wood vinegar liquor stock and Kanto Wood Chemical Co., Ltd. wood vinegar liquor distilled products.
本発明の竹酢液について説明する。
一般に竹酢液は、竹の稈を無酸素あるいは低酸素状態で不完全燃焼して、その際発生する煙を冷却して液状物を生じさせ、さらに数ヶ月間静置させてタール分を沈降させて得られる。本発明の竹酢液もこのようにして得られたものを使用してもよい。
具体的には、各種製品が市販されているが、（株）関東ウッドケミカル製竹酢液原液や（株）関東ウッドケミカル製竹酢液蒸留品等がある。The bamboo vinegar of the present invention will be described.
In general, bamboo vinegar liquid burns bamboo shoots incompletely in an oxygen-free or low-oxygen state, cools the smoke generated at that time to produce a liquid material, and then settles for several months to settle the tar content. Can be obtained. The bamboo vinegar solution of the present invention may be obtained as described above.
Specifically, various products are commercially available, such as a bamboo vinegar stock solution manufactured by Kanto Wood Chemical Co., Ltd., a bamboo vinegar liquid distilled product manufactured by Kanto Wood Chemical Co., Ltd., and the like.
本発明で使用される水酸化カルシウムは、天然精油、木酢酸、竹酢の少なくとも１種類の化合物が水酸化カルシウムに吸着保持された状態ものである。
水酸化カルシウムと天然精油、木酢酸、竹酢の少なくとも１種類の化合物の使用割合は、通常、水酸化カルシウム１００重量部に対して、天然精油、木酢酸、竹酢の少なくとも１種類の化合物が０．１〜２４０重量部、好ましくは、１〜１２０重量部である。
０．１重量部未満であると、消臭性の効果がなくなり、２４０重量部を超えると、水酸化カルシュウムが、天然精油、木酢酸、竹酢の少なくとも１種類の化合物を含有する含有出来る限度を超える。
さらに、その好ましい例として、天然精油、木酢酸、竹酢の少なくとも１種類の化合物が水酸化カルシウムをシェルとするカプセル中に捕獲されたものを挙げることができる。
即ち、天然精油、木酢酸、竹酢の少なくとも１種類の化合物を水酸化カルシウムでカプセル化することにより、天然精油、木酢酸、竹酢の少なくとも１種類の化合物の浸出や飛散および酸素による変質を防止すること、および消臭性効果を持続させることができる。また、天然精油、木酢酸、竹酢の少なくとも１種類の化合物が直接製品に触れることがないので安全性が向上する。The calcium hydroxide used in the present invention is a state in which at least one compound of natural essential oil, wood acetic acid, and bamboo vinegar is adsorbed and held in calcium hydroxide.
The use ratio of at least one compound of calcium hydroxide and natural essential oil, wood acetic acid, bamboo vinegar is usually at least one compound of natural essential oil, wood acetic acid, bamboo vinegar per 100 parts by weight of calcium hydroxide. 0.1 to 240 parts by weight, preferably 1 to 120 parts by weight.
When the amount is less than 0.1 parts by weight, the deodorizing effect is lost. When the amount exceeds 240 parts by weight, calcium hydroxide contains at least one compound of natural essential oil, wood acetic acid, and bamboo vinegar. Over.
Furthermore, as a preferable example, there can be mentioned one in which at least one compound of natural essential oil, wood acetic acid and bamboo vinegar is captured in a capsule having calcium hydroxide as a shell.
That is, by encapsulating at least one compound of natural essential oil, wood acetic acid, and bamboo vinegar with calcium hydroxide, leaching and scattering of at least one compound of natural essential oil, wood acetic acid, and bamboo vinegar, and alteration by oxygen Preventing and deodorizing effects can be sustained. Moreover, since at least one compound of natural essential oil, wood acetic acid, and bamboo vinegar does not directly touch the product, safety is improved.
また、本発明で使用される水酸化カルシウムは、酸化カルシウムならびに水を混合し反応させることにより得られる水酸化カルシウムであってもよい。
その固形消臭性組成物の製法としては、天然精油、木酢酸、竹酢の少なくとも１種類の化合物と、貝殻等を粉砕して焼成した酸化カルシウムならびに水を混合し反応させることにより得られる。The calcium hydroxide used in the present invention may be calcium hydroxide obtained by mixing and reacting calcium oxide and water.
A method for producing the solid deodorant composition is obtained by mixing and reacting at least one compound of natural essential oil, wood acetic acid, bamboo vinegar, calcium oxide obtained by pulverizing shells and the like, and water.
本発明の貝殻は、天然の貝殻であれば、特に問題ないが、本発明では、具体的には、食用貝加工業者から排出される廃棄物である貝殻を使用している。例えば、赤貝、イガイ、牡蠣、ハマグリ、アワビ類、サザエ等の食用貝である。
これら貝殻の主成分は炭酸カルシウムであるが、本発明では、この貝殻を粉砕し、５００〜１８００℃、好ましくは８００〜１１００℃、より好ましくは９５０〜１０００℃で焼成した粉末を使用するものである。
炭酸カルシウム等は、上記温度で焼成することにより、大部分は、酸化カルシウム等に変化する。
酸化カルシウムは水と容易に水和反応し、発熱をともなって水酸化カルシウムとなる。その際、抗菌性または忌避性を有する化合物を存在させておくと水和反応の際、その化合物が水酸化カルシウムに吸着保持される。ここで、天然精油、木酢酸、竹酢の少なくとも１種類の化合物と酸化カルシウムおよび水の割合を変えることにより良好な成形体を得ることができる。即ち、これらの割合を最適化させると、抗菌性または忌避性を有する化合物を水酸化カルシウムをシェルとするカプセル中に完全に捕獲することができる。さらにこれらの割合はカプセルの粒径や、シェルの厚みに影響を与える。カプセルの粒径やシェルの厚みは、中に捕獲されている抗菌性または忌避性を有する化合物の浸出量や浸出速度に影響を与えるので本発明の成形体の重要な要素である。The shell of the present invention is not particularly problematic as long as it is a natural shell, but in the present invention, specifically, a shell that is waste discharged from an edible shell processor is used. For example, edible shellfish such as red shellfish, mussels, oysters, clams, abalone, and turban shells.
The main component of these shells is calcium carbonate. In the present invention, the shells are pulverized and used at 500 to 1800 ° C, preferably 800 to 1100 ° C, more preferably 950 to 1000 ° C. is there.
Most of calcium carbonate or the like changes to calcium oxide or the like by firing at the above temperature.
Calcium oxide easily hydrates with water and becomes calcium hydroxide with heat generation. At that time, if a compound having antibacterial or repellent properties is present, the compound is adsorbed and held by calcium hydroxide during the hydration reaction. Here, a favorable molded object can be obtained by changing the ratio of at least one compound of natural essential oil, wood acetic acid and bamboo vinegar, calcium oxide and water. That is, when these ratios are optimized, a compound having antibacterial or repellent properties can be completely trapped in a capsule having calcium hydroxide as a shell. Further, these ratios affect the capsule particle size and the shell thickness. The particle size of the capsule and the thickness of the shell are important elements of the molded article of the present invention because they affect the leaching amount and leaching rate of the antibacterial or repellent compound trapped therein.
上記製法で使われる天然精油、木酢酸、竹酢の少なくとも１種類の化合物、酸化カルシウムおよび水の使用割合は、通常、酸化カルシウム１００重量部に対して抗菌性または忌避性を有する化合物が０．１〜１８０重量部、好ましくは、１〜１２０重量部、水が５〜６０重量部、好ましくは、１０〜５０重量部である。天然精油、木酢酸、竹酢の少なくとも１種類の化合物が０．１重量部未満だと消臭性の効果が小さく、また１８０重量部を越えると強度が劣るため好ましくない。また、水が５重量部未満だと水和反応が不十分となり、また６０重量部を越えると気密性や強度が劣り好ましくない。 The proportion of natural essential oil, wood acetic acid, bamboo vinegar, calcium oxide and water used in the above production method is usually 0. 100 parts by weight of calcium oxide for antibacterial or repellent compounds. 1 to 180 parts by weight, preferably 1 to 120 parts by weight, and 5 to 60 parts by weight of water, preferably 10 to 50 parts by weight. If the amount of at least one compound of natural essential oil, wood acetic acid, and bamboo vinegar is less than 0.1 parts by weight, the deodorizing effect is small, and if it exceeds 180 parts by weight, the strength is inferior. On the other hand, if the amount of water is less than 5 parts by weight, the hydration reaction is insufficient, and if it exceeds 60 parts by weight, the airtightness and strength are inferior.
本発明の製法で使われる酸化カルシウムは、粉末状のものでも粒状のもの、破砕品のいずれも使用できる。また、保存性を持たせるために粉末状または粒状のものの表面を撥水性の化合物でコーティングしたものを使用することもできる。 Calcium oxide used in the production method of the present invention can be powdery, granular or crushed. In addition, a powdery or granular surface coated with a water-repellent compound can be used in order to provide storage stability.
また、本発明の固形消臭剤組成物中には、必要に応じて、酸化防止剤、染料、香料等の各種添加剤を含有させてもよい。 Moreover, in the solid deodorant composition of this invention, you may contain various additives, such as antioxidant, a dye, and a fragrance | flavor, as needed.
本発明の固形消臭剤組成物は、そのまま使用することもできるが、固形消臭剤組成物をアクリル酸ソーダ系ポリマーのような高吸水性樹脂で包装して使用することもできる。特に製品が直接成形体に触れるような商品に使用する場合は後者が好ましい。通気性の包装材料としては通気性の気孔を有する素材であればどのような素材でも使用できる。例えば、低密度ポリエチレンフィルム、低密度ポリエチレンに炭酸カルシウムを混練したフィルム、通気性の紙、不織布等が挙げられる。 The solid deodorant composition of the present invention can be used as it is, but the solid deodorant composition can also be used after being packaged with a superabsorbent resin such as sodium acrylate polymer. In particular, when the product is used for a product in which the product directly touches the molded body, the latter is preferable. As the air-permeable packaging material, any material having air-permeable pores can be used. Examples thereof include a low density polyethylene film, a film in which calcium carbonate is kneaded with low density polyethylene, breathable paper, and a nonwoven fabric.
また、本発明の成形体の使用形態として、他の材料と組み合わせて使用することができる。例えば、紙製品やゴム製品、プラスチック製フィルム等に混合させたり、プラスチック成形材料の原料成分としても使用できる。得られた製品は消臭性が付与された機能性製品として利用できる。 Moreover, it can use in combination with another material as a usage form of the molded object of this invention. For example, it can be mixed with paper products, rubber products, plastic films, etc., or used as a raw material component of plastic molding materials. The obtained product can be used as a functional product with a deodorizing property.
また、本発明の固体消臭剤組成物の使用形態として、他の機能性製品、例えば脱酸素剤と組み合わせて使用してもよい。 Moreover, you may use it as a usage form of the solid deodorant composition of this invention in combination with another functional product, for example, an oxygen scavenger.
実施例１
ヤスハラケミカル（株）製ｄ−リモネン（純度：９９％）４０ｇと粉末状水酸化カルシウム１００ｇを室温下で混合し、白色粒状体を得た。この白色粒状体組成物１００ｇを男子トイレの尿用容器下部に設置したところ、約１か月、消臭効果を維持した。Example 1
40 g of d-limonene (purity: 99%) manufactured by Yasuhara Chemical Co., Ltd. and 100 g of powdered calcium hydroxide were mixed at room temperature to obtain a white granular material. When 100 g of this white granular composition was installed in the lower part of a urine container of a men's toilet, the deodorizing effect was maintained for about one month.
実施例２
（株）ウッドケミカル製木酢液原液４０ｇと粉末状水酸化カルシウム１００ｇを室温下で混合し、白色粒状体を得た。この白色粒状体組成物１００ｇを男子トイレの尿用容器下部に設置したところ、約１か月、消臭効果を維持した。Example 2
40 g of a wood vinegar stock solution manufactured by Wood Chemical Co., Ltd. and 100 g of powdered calcium hydroxide were mixed at room temperature to obtain a white granular material. When 100 g of this white granular composition was installed in the lower part of a urine container of a men's toilet, the deodorizing effect was maintained for about one month.
実施例３
（株）ウッドケミカル製竹酢液原液４０ｇと粉末状水酸化カルシウム１００ｇを室温下で混合し、白色粒状体を得た。この白色粒状体組成物１００ｇを男子トイレの尿用容器下部に設置したところ、約１か月、消臭効果を維持した。Example 3
40 g of bamboo vinegar stock solution manufactured by Wood Chemical Co., Ltd. and 100 g of powdered calcium hydroxide were mixed at room temperature to obtain a white granular material. When 100 g of this white granular composition was installed in the lower part of a urine container of a men's toilet, the deodorizing effect was maintained for about one month.
実施例４
主成分が炭酸カルシウムである廃棄物となっている牡蠣殻をボールミル粉砕機を使用して粉砕した後、径４ｍ、長さ６０ｍの鋼鉄製円筒管であるロータリーキルンを使用して、９５０〜１０００℃で焼成し、主成分の酸化カルシウムを得た。
この粉末状酸化カルシュウム８０ｇとｄ−リモネン４０ｇとを室温下混合し、撹拌しながら、これに水を１０分間で３０ｇ滴下し、さらに２時間撹拌したところ、白色粒状成形体が得られた。この組成物１００ｇを男子トイレの尿用容器下部に設置したところ、約１か月、消臭効果を維持した。Example 4
After pulverizing the oyster shell, which is a waste whose main component is calcium carbonate, using a ball mill pulverizer, using a rotary kiln which is a steel cylindrical tube having a diameter of 4 m and a length of 60 m, 950 to 1000 ° C. The main component calcium oxide was obtained.
When 80 g of this powdered calcium oxide and 40 g of d-limonene were mixed at room temperature, 30 g of water was added dropwise to the mixture over 10 minutes while stirring, and the mixture was further stirred for 2 hours to obtain a white granular molded product. When 100 g of this composition was installed in the lower part of a urine container of a men's toilet, the deodorizing effect was maintained for about one month.
実施例５
実施例１で得られた白色粒状体組成物１００ｇに高級水樹脂のアクリル酸ソーダ系ポリマーである三洋化成（株）製アクアパールＳを１０ｇ加え、白色粒状体を得た。この白色粒状体組成物１００ｇに、人尿１０ｇをしみ込ませたところ、約１か月、消臭効果を維持した。Example 5
10 g of Aqua Pearl S manufactured by Sanyo Chemical Co., Ltd., which is a sodium acrylate polymer of a high-grade water resin, was added to 100 g of the white granule composition obtained in Example 1 to obtain a white granule. When 100 g of this white granular composition was soaked with 10 g of human urine, the deodorizing effect was maintained for about one month.
実施例６
実施例４で得られた白色粒状体組成物１００ｇに高級水樹脂のアクリル酸ソーダ系ポリマーである三洋化成（株）製アクアパールＳを１０ｇ加え、白色粒状体を得た。この白色粒状体組成物１００ｇに、人尿１０ｇをしみ込ませたところ、約１か月、消臭効果を維持した。Example 6
10 g of Aqua Pearl S manufactured by Sanyo Chemical Co., Ltd., which is a sodium acrylate polymer of a high-grade water resin, was added to 100 g of the white granule composition obtained in Example 4 to obtain a white granule. When 100 g of this white granular composition was soaked with 10 g of human urine, the deodorizing effect was maintained for about one month.
比較例１
実施例５で使用した三洋化成（株）製アクアパールＳ１０ｇに、人尿１０ｇをしみ込ませたところ、全く消臭効果は見られなかった。Comparative Example 1
When 10 g of human urine was soaked into 10 g of Aqua Pearl S10g manufactured by Sanyo Chemical Co., Ltd. used in Example 5, no deodorizing effect was observed.
本発明により製造される固体消臭剤組成物は安全性が高く、消臭性能に優れ、最近問題になっている環境問題にも適用したものであり、自動車車内等の消臭剤や住居用消臭剤として利用可能である。また、本発明の組成物は消臭性だけでなく、抗菌性や忌避性も有するものであり、そういった意味での利用の可能性も考えられる。 The solid deodorant composition produced by the present invention has high safety, excellent deodorization performance, and is applied to environmental problems that have recently become a problem. It can be used as a deodorant. Further, the composition of the present invention has not only deodorant properties but also antibacterial properties and repellent properties, and the possibility of use in such meaning is also conceivable.
Claims (5)