JP2006220863A - Pattern formation material, pattern formation apparatus and pattern formation method - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a pattern formation material which suppresses coloration and sensitivity lowering during storage, excels in development of a visible image in an exposed region because of good color formation property in exposure, and excels in sensitivity stability, and to provide a pattern formation apparatus provided with the pattern formation material and a pattern formation method using the pattern formation material. <P>SOLUTION: The pattern formation material has at least a photosensitive layer on a support and absorbance of the unexposed photosensitive layer to light of 600 nm satisfies a relationship of B-A≤0.1 wherein B is absorbance after treatment at 60°C for 72 h and A is absorbance before the treatment. The pattern formation apparatus provided with the pattern formation material and the pattern formation method using the pattern formation material are also provided. The photosensitive layer preferably contains a binder, a polymerizable compound, a photoinitiator and a color former compound having at least one substituent in the ortho-position with respect to the carbon atom of methane, which is a triarylmethane dye having a substituted amino group in each 4-position. <P>COPYRIGHT: (C)2006,JPO&NCIPI

Description

  The present invention relates to a pattern forming material suitable for dry film resist (DFR) and the like, and a pattern forming method using the pattern forming material.

  When forming a permanent pattern such as a wiring pattern, a pattern forming material in which a photosensitive layer is formed by applying and drying a photosensitive resin composition on a support is used. As the method for producing the permanent pattern, for example, a laminate is formed by laminating the pattern forming material on a substrate such as a copper clad laminate on which the permanent pattern is formed, and the photosensitive layer in the laminate is formed on the photosensitive layer. The permanent pattern is formed by exposing to light, developing the photosensitive layer after the exposure to form a pattern, and then performing an etching process or the like.

  The pattern forming material includes, for example, a leuco crystal as a color former that develops color by irradiation with actinic rays such as ultraviolet rays in order to obtain a printed image that can distinguish between an exposed portion and an unexposed portion in order to prevent overlapping exposure. A photosensitive composition containing a leuco dye such as violet and an organic halogen compound is used (see, for example, Patent Documents 1 and 2). However, in these photosensitive compositions, even under light-shielding conditions, a part of the leuco dye, which is a printing dye, develops color due to oxidation, the photosensitive layer is contaminated, and the sensitivity decreases (so-called “fogging”). Occurs).

  For this problem, it has been reported that a method of adding a basic dye such as malachite green is effective for stabilizing the leuco dye and contains alkanolamine and malachite green together with the leuco dye. A photosensitive resin composition has been proposed (see, for example, Patent Document 3). However, in this case, it is necessary to add a relatively large amount of malachite green, and in addition, the dye added for the purpose of stabilization may cause a change in color tone depending on manufacturing conditions, and exposure of the photosensitive layer. There is a problem of lowering the sensitivity.

  On the other hand, in order to suppress fogging before use of proof paper or the like, as a color former, a microcapsule encapsulating triphenylmethane having an aminophenoxyalkyl group which may have a substituent and a photooxidant, And an image forming material in which a coating layer containing a reducing agent is formed on a support has been proposed (for example, see Patent Document 4). However, in the above-mentioned Patent Document 4, application to a dry film resist has not been studied, and when applied, sufficient exposure sensitivity cannot be obtained, and there is a high possibility that adverse effects will occur due to the use of microcapsules, There is a problem that it cannot be used.

  Therefore, a pattern forming material that suppresses coloring during storage and a decrease in sensitivity and has excellent color development at the time of exposure and is excellent in visualizing an exposed region, and has excellent sensitivity stability, and the pattern forming material. A pattern forming apparatus provided and a pattern forming method using the pattern forming material have not been provided yet, and further improvements and developments are desired.

JP 59-107344 A JP 60-57340 A Japanese Patent Laid-Open No. 6-148883 JP-A-5-127300

  This invention is made | formed in view of this present condition, and makes it a subject to solve the said various problems in the past and to achieve the following objectives. That is, the present invention is a pattern forming material that suppresses coloring during storage and sensitivity reduction, and is excellent in visualizing exposed areas due to good color development during exposure, and has excellent sensitivity stability, and the pattern formation It aims at providing the pattern formation apparatus provided with the material, and the pattern formation method using the said pattern formation material.

  As a result of intensive studies in view of the above problems, the inventors of the present invention are triarylmethane dyes having a substituted amino group at the 4-position as a color former compound capable of oxidative color development, which is ortho to the carbon atom of methane. By using a color former compound having at least one substituent at the position, coloring during storage and sensitivity reduction are suppressed, and excellent exposure to visible images is achieved due to good color development during exposure, and sensitivity stability. It was found that an excellent pattern forming material can be obtained.

The present invention is based on the above knowledge, and means for solving the above problems are as follows. That is,
<1> The support has at least a photosensitive layer, and the absorbance of the unexposed photosensitive layer with respect to 600 nm light is B after the treatment for 72 hours under the temperature condition of 60 ° C., the absorbance before the treatment. Is a pattern forming material characterized by satisfying the relationship of B−A ≦ 0.1.
<2> The pattern forming material according to <1>, wherein the photosensitive layer includes at least a binder, a polymerizable compound, a photopolymerization initiator, and a color former compound represented by the following structural formula (I). .
However, in said structural formula (I), R < ₁ >, R < ₂ >, R < ₃ >, R < ₄ >, R < ₅ >, and R < ₆ > represent either the alkyl group and aryl group which may have a substituent,
Any pair of R ₁ and R ₂ , R ₃ and R ₄ , and R ₅ and R ₆ may form a saturated 5- to 8-membered ring together with the nitrogen atom to be bonded,
R ₇ , R ₈ and R _{9 each} represent a hydrogen atom, an alkyl group, an alkyloxy group, an alkylthio group, an alkyloxycarbonyl group, an acylamino group, or a hydroxy group, and R ₇ , R ₈ and R ₉ At least one represents any of an alkyl group, an alkyloxy group, an alkylthio group, an alkyloxycarbonyl group, an acylamino group, and a hydroxy group.
<3> In Structural Formula (I), any one of R ₇ , R ₈ , and R ₉ is any one of an alkyl group, an alkyloxy group, an alkylthio group, an alkyloxycarbonyl group, an acylamino group, and a hydroxy group. The pattern forming material according to <2>, wherein the other two are hydrogen atoms.
<4> The pattern forming material according to any one of <2> to <3>, wherein the photosensitive layer contains 0.01 to 20% by mass of a color former compound represented by Structural Formula (I).
<5> The content of the color former compound represented by the structural formula (I) is 50% by mass or more based on the total amount of the color former compound contained in the photosensitive layer. It is a pattern formation material of description.
<6> The pattern forming material according to any one of <1> to <5>, wherein the support has a cushion layer and a photosensitive layer in this order.
<7> The pattern forming material according to any one of <1> to <6>, further including a cushion layer, a barrier layer capable of suppressing movement of the substance, and a photosensitive layer in this order on the support.
<8> The pattern forming material according to any one of <1> to <7>, wherein the support has a plurality of photosensitive layers having relatively different photosensitivities.
<9> The pattern forming material according to <8>, wherein a barrier layer is provided between the photosensitive layers having relatively different photosensitivities.

<10> The pattern forming material according to any one of <1> to <9>, wherein the binder has an acidic group.
<11> The pattern forming material according to any one of <1> to <10>, wherein the binder includes a vinyl copolymer.
<12> The pattern forming material according to any one of <1> to <11>, wherein the binder includes a copolymer of at least one of styrene and a styrene derivative.
<13> The pattern forming material according to any one of <1> to <12>, wherein the binder has an acid value of 70 to 250 (mgKOH / g).
<14> The pattern forming material according to any one of <1> to <13>, wherein the binder has a glass transition temperature of 80 ° C. or higher.
<15> The pattern forming material according to any one of <1> to <14>, wherein the polymerizable compound includes a monomer having at least one of a urethane group and an aryl group.
<16> The photopolymerization initiator includes at least one selected from halogenated hydrocarbon derivatives, hexaarylbiimidazoles, oxime derivatives, organic peroxides, thio compounds, ketone compounds, aromatic onium salts, and metallocenes. The pattern forming material according to any one of <1> to <15>.
<17> The pattern forming material according to any one of <1> to <16>, wherein the photosensitive layer has a thickness of 1 to 100 μm.
<18> The photosensitive layer contains 30 to 90% by mass of a binder, 5 to 60% by mass of a polymerizable compound, and 0.1 to 30% by mass of a photopolymerization initiator. > The pattern forming material according to any one of the above.
<19> The pattern forming material according to any one of <1> to <18>, wherein the support includes a synthetic resin and is transparent.
<20> The pattern forming material according to any one of <1> to <19>, wherein the support has an elongated shape.
<21> The pattern forming material according to any one of <1> to <20>, wherein the pattern forming material has a long shape and is wound in a roll shape.
<22> The pattern forming material according to any one of <1> to <21>, wherein the pattern forming material has a protective film on the photosensitive layer.

<23> The pattern forming material according to any one of <1> to <22> is provided,
A pattern forming apparatus comprising at least light irradiating means capable of irradiating light, and light modulating means for modulating light from the light irradiating means and exposing the photosensitive layer in the pattern forming material. is there. In the pattern forming apparatus according to <23>, the light irradiation unit irradiates light toward the light modulation unit. The light modulation unit modulates light received from the light irradiation unit. The light modulated by the light modulator is exposed to the photosensitive layer. For example, when the photosensitive layer is subsequently developed, a high-definition pattern is formed.
<24> The light modulation means further includes a pattern signal generation means for generating a control signal based on the pattern information to be formed, and the control signal generated by the pattern signal generation means is emitted from the light irradiation means. It is a pattern formation apparatus as described in said <23> modulated according to. In the pattern forming apparatus according to <24>, since the light modulation unit includes the pattern signal generation unit, light emitted from the light irradiation unit corresponds to a control signal generated by the pattern signal generation unit. Modulated.
<25> The light modulation means has n pixel parts, and forms any less than n pixel elements arranged continuously from the n pixel parts. The pattern forming apparatus according to any one of <23> to <24>, which can be controlled according to pattern information. In the pattern forming apparatus according to <25>, any less than n pixel portions arranged continuously from the n pixel portions in the light modulation unit are controlled according to pattern information. Thereby, the light from the light irradiation means is modulated at high speed.
<26> The pattern forming apparatus according to any one of <23> to <25>, wherein the light modulation unit is a spatial light modulation element.
<27> The pattern forming apparatus according to <26>, wherein the spatial light modulation element is a digital micromirror device (DMD).
<28> The pattern forming apparatus according to any one of <25> to <27>, wherein the drawing element portion is a micromirror.
<29> The pattern forming apparatus according to any one of <23> to <28>, wherein the light irradiation unit is capable of combining and irradiating two or more lights. In the pattern forming apparatus according to <29>, since the light irradiation unit can synthesize and irradiate two or more lights, exposure is performed with exposure light having a deep focal depth. As a result, the pattern forming material is exposed with extremely high definition. For example, when the photosensitive layer is subsequently developed, an extremely fine pattern is formed.
<30> The light irradiation means includes a plurality of lasers, a multimode optical fiber, and a collective optical system that condenses the laser light irradiated from each of the plurality of lasers and couples the laser light to the multimode optical fiber. <23> to the pattern forming apparatus according to any one of <29>. In the pattern forming apparatus according to <30>, the light irradiation unit can condense the laser light emitted from each of the plurality of lasers by the collective optical system and be coupled to the multimode optical fiber. Thus, exposure is performed with exposure light having a deep focal depth. As a result, the pattern forming material is exposed with extremely high definition. For example, when the photosensitive layer is subsequently developed, an extremely fine pattern is formed.

<31> A pattern forming method comprising at least exposing the photosensitive layer in the pattern forming material according to any one of <1> to <22>. In the pattern forming method according to <31>, exposure is performed on the pattern forming material. For example, when the photosensitive layer is subsequently developed, a high-definition pattern is formed.
<32> The pattern forming method according to <31>, wherein the pattern forming material is laminated on the substrate while being heated and pressurized and exposed.
<33> The pattern forming method according to <32>, wherein the base is a printed wiring board.
<34> The pattern forming method according to any one of <31> to <33>, wherein the exposure is performed imagewise based on pattern information to be formed.
<35> The pattern formation according to any one of <31> to <34>, wherein the exposure is performed using a light generated by generating a control signal based on pattern information to be formed and modulated in accordance with the control signal Is the method. In the pattern formation method according to <35>, a control signal is generated based on pattern formation information to be formed, and light is modulated in accordance with the control signal.
<36> From <31> to <35, wherein the exposure is performed using light irradiation means for irradiating light and light modulation means for modulating light emitted from the light irradiation means based on pattern information to be formed. > The pattern forming method according to any one of the above.
<37> After the light is modulated by the light modulating means having n number of picture element portions that receive and emit light from the light irradiating means, the light is emitted from the light irradiating means. The pattern forming method according to any one of <31> to <36>, wherein the pattern forming method includes at least a microlens array in which microlenses having aspheric surfaces capable of correcting aberration due to distortion are arranged. In the pattern forming method according to <37>, the light modulated by the light modulation unit passes through the aspheric surface in the microlens array, so that the aberration due to the distortion of the emission surface in the pixel portion is corrected. The As a result, distortion of the image formed on the pattern forming material is suppressed, and exposure to the pattern forming material is performed with extremely high definition. For example, when the photosensitive layer is subsequently developed, an extremely fine pattern is formed.
<38> The pattern forming method according to <37>, wherein the aspherical surface is a toric surface. In the pattern forming method according to <38>, since the aspherical surface is a toric surface, aberration due to distortion of the radiation surface in the pixel portion is efficiently corrected, and an image formed on the pattern forming material is formed. Is effectively suppressed. As a result, the pattern forming material is exposed with extremely high definition. For example, when the photosensitive layer is subsequently developed, an extremely fine pattern is formed.
<39> The pattern forming method according to any one of <31> to <38>, wherein the exposure is performed through an aperture array. In the pattern forming method according to <39>, the extinction ratio is improved by performing exposure through the aperture array. As a result, the exposure is performed with extremely high definition. For example, when the photosensitive layer is subsequently developed, an extremely fine pattern is formed.
<40> The pattern forming method according to any one of <31> to <39>, wherein the exposure is performed while relatively moving the exposure light and the photosensitive layer. In the pattern forming method according to <40>, exposure is performed at a high speed by performing exposure while relatively moving the modulated light and the photosensitive layer. For example, when the photosensitive layer is subsequently developed, a high-definition pattern is formed.
<41> The pattern forming method according to any one of <31> to <40>, wherein the exposure is performed on a partial region of the photosensitive layer.
<42> The pattern forming method according to any one of <31> to <41>, wherein the photosensitive layer is developed after the exposure.
<43> The pattern forming method according to any one of <31> to <42>, wherein a permanent pattern is formed after development.
<44> The pattern forming method according to <43>, wherein the permanent pattern is a wiring pattern, and the formation of the permanent pattern is performed by at least one of an etching process and a plating process.

  According to the present invention, conventional problems can be solved, coloring during storage and reduction in sensitivity are suppressed, and excellent exposure to visible images due to good color development during exposure, and excellent sensitivity stability. The pattern forming material, the pattern forming apparatus provided with the pattern forming material, and the pattern forming method using the pattern forming material can be provided.

(Pattern forming material)
The pattern forming material of the present invention has at least a photosensitive layer on a support, and the absorbance of the unexposed photosensitive layer with respect to light of 600 nm is B after the treatment for 72 hours under a temperature condition of 60 ° C. Assuming that the absorbance before the treatment is A, there is no particular limitation as long as the relationship of B−A ≦ 0.1 is satisfied, and it can be appropriately selected according to the purpose.
In the pattern forming material, a cushion layer may be provided between the support and the photosensitive layer, a barrier layer may be provided together with the cushion layer, or a protective film may be formed on the photosensitive layer. Furthermore, other layers appropriately selected may be provided.
The photosensitive layer may be a single layer or two or more layers.

<Photosensitive layer>
The absorbance of the unexposed photosensitive layer with respect to 600 nm light is B-A, where B is the absorbance after processing for 72 hours at 60 ° C. and A is the absorbance before processing. As long as the relationship of ≦ 0.1 is satisfied, there is no particular limitation, and it can be appropriately selected according to the purpose. The value B−A is more preferably 0.05 or less.
When the value of B-A is 0.1 or more, the exposure sensitivity is low, and the absorbance of the unexposed photosensitive layer due to change with time is increased (the density is increased). The difference becomes small, and it may be difficult to distinguish between an exposed area and an unexposed area.

  The absorbance (density) of the unexposed photosensitive layer with respect to 600 nm light is preferably 0.003 to 0.02 / μm. For example, when the thickness of the photosensitive layer is 15 μm, the concentration is preferably 0.05 to 0.3, and more preferably 0.1 to 0.3.

  The photosensitive layer is a binder, a polymerizable compound, a photopolymerization initiator, and a triarylmethane dye having a substituted amino group at the 4-position, and at least one substituent at an ortho-position to the carbon atom of methane. And a color former compound represented by the following structural formula (I), and may contain other components appropriately selected according to the purpose.

However, in said structural formula (I), R < ₁ >, R < ₂ >, R < ₃ >, R < ₄ >, R < ₅ >, and R < ₆ > represent either the alkyl group and aryl group which may have a substituent,
Any pair of R ₁ and R ₂ , R ₃ and R ₄ , and R ₅ and R ₆ may form a saturated 5- to 8-membered ring together with the nitrogen atom to be bonded,
R ₇ , R ₈ and R _{9 each} represent a hydrogen atom, an alkyl group, an alkyloxy group, an alkylthio group, an alkyloxycarbonyl group, an acylamino group, or a hydroxy group, and R ₇ , R ₈ and R ₉ At least one represents any of an alkyl group, an alkyloxy group, an alkylthio group, an alkyloxycarbonyl group, an acylamino group, and a hydroxy group.

<< Color former compound >>
The color former compound includes a color former compound represented by the structural formula (I), and may further contain another color former compound.

In the structural formula (I), R ₁ , R ₂ , R ₃ , R ₄ , R ₅ , and R ₆ represent either an alkyl group or an aryl group which may have a substituent, and are the same May be different.
Examples of the alkyl group include a saturated alkyl group, an unsaturated alkyl group, and a cycloalkyl group, and these include an aryl group, an alkyloxy group, an aryloxy group, an acyloxy group, a halogen atom, an acylamino group, and an alkyloxycarbonyl group. May have a substituent such as an aminocarbonyl group or a cyano group.
The aryl group represents a phenyl group, a naphthyl group, and a heterocyclic group, and these include an alkyl group, an alkyloxy group, an aryloxy group, a halogen atom, a nitro group, a cyano group, a substituted carbamoyl group, a substituted sulfamoyl group, and a substituted group. It may have a substituent such as an amino group, a substituted oxycarbonyl group, a substituted oxysulfonyl group, an alkylthio group, an arylsulfonyl group, and a phenyl group.
Among these, an alkyl group having 1 to 18 carbon atoms is preferable, and an alkyl group having 1 to 12 carbon atoms is more preferable.

In the structural formula (I), R ₁ , R ₂ , R ₃ , R ₄ , R ₅ , and R ₆ are each a halogen atom, an alkyloxy group, an aryl group, an aryloxy group, an alkyl group, an acyl group, It may be substituted with a cyano group, a hydroxy group, a furfuryl group, or the like.

Furthermore, in the structural formula (I), any combination of R ₁ and R ₂ , R ₃ and R ₄ , and R ₅ and R ₆ forms a saturated 5- to 8-membered ring together with the nitrogen atom to be bonded. Examples of the ring include piperidine, morpholine, pyrrolidine, piperazine, and hexamethyleneimine. Examples of the substituent represented by R ₁ R ₂ N—, R ₃ R ₄ N—, and R ₅ R ₆ N— include, for example, a pyrrolidino group, a piperazino group, a morpholino group, an N-ethylpiperazino group, Dimethylamino group, diethylamino group, dipropylamino group, dibutylamino group, N-ethyl-N-isobutylamino group, N-ethyl-benzylamino group, diamylamino group, dihexylamino group, dioctylamino group, N-ethyl-N -Tetrafurfurylamino group, dibenzylamino group, etc. are mentioned.
Among these, a 5-membered ring and a 6-membered ring are preferable.

In the structural formula (I), R ₇ , R ₈ and R ₉ represent any one of a hydrogen atom, an alkyl group, an alkyloxy group, an alkylthio group, an alkyloxycarbonyl group, an acylamino group, and a hydroxy group, and R ₇ , at least one of R ₈ and R ₉ represents any of an alkyl group, an alkyloxy group, an alkylthio group, an alkyloxycarbonyl group, an acylamino group, and a hydroxy group, and any one of R ₇ , R ₈ , and R ₉ One is preferably an alkyl group, an alkyloxy group, an alkylthio group, an alkyloxycarbonyl group, an acylamino group, or a hydroxy group, and the other two are preferably hydrogen atoms.
When R ₇ , R ₈ , and R ₉ are not a hydrogen atom, they are preferably an alkyl group having 1 to 18 carbon atoms or an alkyloxy group, and an alkyl group or alkyloxy having 1 to 12 carbon atoms. More preferably, it is a group. These may be substituted with a halogen atom, an alkyloxy group, an aryl group, an aryloxy group, an alkyl group, a cyano group, a hydroxy group, a furfuryl group, or the like.

  Examples of the color former compound represented by the structural formula (I) include compounds represented by the following structural formulas (1) to (32).

  Among the compounds represented by the structural formulas (1) to (32), those having one phenyl group having a substituent in the ortho position with respect to the carbon atom of methane are preferable. For example, the structural formula (1) , (2), (6), (7), (14) to (29), (31), and (32) are preferred, and structural formulas (1), (2), (6), (7 ), (16), and (21) are more preferred.

The content of the color former compound represented by the structural formula (I) is preferably 50% by mass or more, more preferably 70% by mass or more, and 90% by mass with respect to the total amount of the color former compound. The above is particularly preferable.
The content of the color former compound represented by the structural formula (I) in the photosensitive layer is preferably 0.01 to 20% by mass, more preferably 0.05 to 10% by mass, 5% by mass is particularly preferred.

The other color former compound is not particularly limited as long as it gives a visible image to the photosensitive layer after exposure, and can be appropriately selected according to the purpose. For example, tris (4-dimethylaminophenyl) ) Methane (leuco crystal violet), tris (4-diethylaminophenyl) methane, tris (4-dimethylamino-2-methylphenyl) methane, tris (4-diethylamino-2-methylphenyl) methane, bis (4-dibutylamino) Aminotriarylmethanes such as phenyl)-[4- (2-cyanoethyl) methylaminophenyl] methane, bis (4-dimethylaminophenyl) -2-quinolylmethane, tris (4-dipropylaminophenyl) methane; 6-bis (dimethylamino) -9-phenylxanthine, 3-amino-6- Aminoxanthines such as methylamino-2-methyl-9- (2-chlorophenyl) xanthine; 3,6-bis (diethylamino) -9- (2-ethoxycarbonylphenyl) thioxanthene, 3,6-bis (dimethylamino) ) Aminothioxanthenes such as thioxanthene; 3,6-bis (diethylamino) -9,10-dihydro-9-phenylacridine, 3,6-bis (benzylamino) -9,10-dividro-9-methylacridine Amino-9,10-dihydroacridines such as; aminophenoxazines such as 3,7-bis (diethylamino) phenoxazine; aminophenothiazines such as 3,7-bis (ethylamino) phenothizone; Aminodi, such as (diethylamino) -5-hexyl-5,10-dihydrophenazine Drophenazines; aminophenylmethanes such as bis (4-dimethylaminophenyl) anilinomethane; aminohydrols such as 4-amino-4′-dimethylaminodiphenylamine, 4-amino-α, β-dicyanohydrocinnamic acid methyl ester Cinnamic acids; hydrazines such as 1- (2-naphthyl) -2-phenylhydrazine; amino-2,3-dihydroanthraquinones of 1,4-bis (ethylamino) -2,3-dihydroanthraquinones; N Phenethylanilines such as N, diethyl-4-phenethylaniline; acyl derivatives of leuco dyes containing basic NH such as 10-acetyl-3,7-bis (dimethylamino) phenothiazine; tris (4-diethylamino-2- Tolyl) does not have oxidizable hydrogen such as ethoxycarbonylmentane Leuco-like compounds that can be oxidized to coloring compounds; leucoin digoid dyes; organic amines that can be oxidized to coloring forms as described in US Pat. Nos. 3,042,515 and 3,042,517 (For example, 4,4′-ethylenediamine, diphenylamine, N, N-dimethylaniline, 4,4′-methylenediaminetriphenylamine, N-vinylcarbazole).
The content of these color former compounds is preferably less than 50% by mass, more preferably less than 30% by mass, and particularly preferably less than 10% by mass with respect to the total amount of the color former compound.

  Furthermore, it is known to add a halogen compound for the purpose of coloring these color former compounds. Examples of the halogen compound include halogenated hydrocarbons (for example, carbon tetrabromide, iodoform, ethylene bromide, methylene bromide, amyl bromide, isoamyl bromide, amyl iodide, isobutylene bromide, butyl iodide, odor Diphenylmethyl, hexachloroethane, 1,2-dibromoethane, 1,1,2,2-tetrabromoethane, 1,2-dibromo-1,1,2-trichloroethane, 1,2,3 tribromopropane, 1 -Bromo-4-chlorobutane, 1,2,3,4-tetrabromobutane, tetrachlorocyclopropene, hexachlorocyclopentadiene, dibromocyclohexane, 1,1,1-trichloro-2,2-bis (4-chlorophenyl) ) Ethane); halogenated alcohol compounds (eg, 2,2,2-trichloroethanol, tri Lomoethanol, 1,3-dichloro-2-propanol, 1,1,1-trichloro-2-propanol, di (iodohexamethylene) aminoisopropanol, tribromo-t-butyl alcohol, 2,2,3-trichlorobutane 1,4-diol, etc .; halogenated carbonyl compounds (for example, 1,1-dichloroacetone, 1,3-dichloroacetone, hexachloroacetone, hexabromoacetone, 1,1,3,3-tetrachloroacetone, 1,1 , 1-trichloroacetone, 3,4-dibromo-2-butanone, 1,4-dichloro-2-butanone-dibromocyclohexanone, etc .; halogenated ether compounds (eg 2-bromoethyl methyl ether, 2-bromoethyl ethyl ether) Di (2-bromoethyl) ether, 1,2- Halogenated ester compounds (eg, bromoethyl acetate, ethyl trichloroacetate, trichloroethyl trichloroacetate, homopolymers and copolymers of 2,3-dibromopropyl acrylate, trichloroethyl dibromopropionate, α, β- Halogenated amide compounds (eg, chloroacetamide, bromoacetamide, dichloroacetamide, trichloroacetamide, tribromoacetamide, trichloroethyltrichloroacetamide, 2-bromoisopropionamide, 2,2,2-trichloropropion) Amide, N-chlorosuccinimide, N-bromosuccinimide, etc.); a compound having sulfur or phosphorus (for example, tribromomethylphenylsulfone, 4-nitro E sulfonyl tribromomethyl sulfone, 4-chlorophenyl tribromomethyl sulfone, tris (2,3-dibromopropyl) phosphate, etc.), 2,4-bis (such as trichloromethyl) 6-phenyl triazole and the like. Of the organic halogen compounds, a halide having two or more halogen atoms bonded to the same carbon atom is preferable, and a halide having three halogen atoms in one carbon atom is particularly preferable. The organic halogen compounds may be used alone or in combination of two or more. Of these, particularly preferred organic halogen compounds are tribromomethylphenylsulfone and 2,4-bis (trichloromethyl) -6-phenyltriazole.

The content of the color former compound is preferably 0.01 to 20% by mass, more preferably 0.05 to 10% by mass, and more preferably 0.1 to 5% by mass with respect to all components of the photosensitive layer. Particularly preferred.
Further, the content of the halogen compound is preferably 0.001 to 5% by mass, more preferably 0.005 to 1% by mass with respect to all components of the photosensitive layer.

<< Binder >>
There is no restriction | limiting in particular as said binder, Although it can select suitably according to the objective, For example, it is preferable that it is swellable with respect to an alkaline liquid, and it is more preferable that it is soluble with respect to an alkaline liquid.
As the binder exhibiting swellability or solubility with respect to the alkaline liquid, for example, those having an acidic group are preferably mentioned.

There is no restriction | limiting in particular as said acidic group, According to the objective, it can select suitably, For example, a carboxyl group, a sulfonic acid group, a phosphoric acid group etc. are mentioned, Among these, a carboxyl group is preferable.
Examples of the binder having a carboxyl group include a vinyl copolymer having a carboxyl group, a polyurethane resin, a polyamic acid resin, and a modified epoxy resin. Among these, the solubility in a coating solvent, the solubility in an alkali developer, and the like. A vinyl copolymer having a carboxyl group is preferable from the viewpoint of solubility, suitability for synthesis, ease of adjustment of film properties, and the like.

  The vinyl copolymer having a carboxyl group can be obtained by copolymerization of at least (1) a vinyl monomer having a carboxyl group, and (2) a monomer copolymerizable therewith.

Examples of the vinyl monomer having a carboxyl group (1) include (meth) acrylic acid, vinyl benzoic acid, maleic acid, maleic acid monoalkyl ester, fumaric acid, itaconic acid, crotonic acid, cinnamic acid, acrylic acid dimer, An addition reaction product of a monomer having a hydroxyl group (for example, 2-hydroxyethyl (meth) acrylate) and a cyclic anhydride (for example, maleic anhydride, phthalic anhydride, cyclohexanedicarboxylic anhydride), ω-carboxy- Examples include polycaprolactone mono (meth) acrylate. Among these, (meth) acrylic acid is particularly preferable from the viewpoints of copolymerizability, cost, solubility, and the like.
Moreover, you may use the monomer which has anhydrides, such as maleic anhydride, itaconic anhydride, and citraconic anhydride, as a precursor of a carboxyl group.

  The monomer copolymerizable with the carboxyl group (2) is not particularly limited and may be appropriately selected depending on the intended purpose. Examples thereof include styrenes, (meth) acrylic acid esters, crotonic acid esters, Vinyl esters, maleic diesters, fumaric diesters, itaconic diesters, (meth) acrylamides, vinyl ethers, vinyl alcohol esters, (meth) acrylonitrile, heterocyclic groups substituted with vinyl groups (eg , Vinylpyridine, vinylpyrrolidone, vinylcarbazole, etc.), N-vinylformamide, N-vinylacetamide, N-vinylimidazole, vinylcaprolactone, 2-acrylamido-2-methylpropanesulfonic acid, mono (2-acryloyloxyethyl phosphate) Esther), Li Acid mono (1-methyl-2-acryloyloxyethyl ester), functional groups (e.g., a urethane group, a urea group, a sulfonamide group, a phenol group, an imido group), vinyl monomers and the like having a. Among these, styrenes (styrene and styrene derivatives) are preferable from the viewpoint that permanent patterns such as wiring patterns can be formed with high definition and the tent property of the formed cured film can be improved.

  Examples of the styrenes (styrene and styrene derivatives) include styrene, methylstyrene, dimethylstyrene, trimethylstyrene, ethylstyrene, isopropylstyrene, butylstyrene, hydroxystyrene, methoxystyrene, butoxystyrene, acetoxystyrene, chlorostyrene, Examples thereof include dichlorostyrene, bromostyrene, chloromethylstyrene, hydroxystyrene protected with a group deprotectable by an acidic substance (for example, t-Boc and the like), methyl vinylbenzoate, α-methylstyrene, and the like.

  Examples of the (meth) acrylic acid esters include methyl (meth) acrylate, ethyl (meth) acrylate, n-propyl (meth) acrylate, isopropyl (meth) acrylate, n-butyl (meth) acrylate, and isobutyl (meth) ) Acrylate, t-butyl (meth) acrylate, n-hexyl (meth) acrylate, cyclohexyl (meth) acrylate, t-butylcyclohexyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, t-octyl (meth) acrylate, Dodecyl (meth) acrylate, octadecyl (meth) acrylate, acetoxyethyl (meth) acrylate, phenyl (meth) acrylate, 2-hydroxyethyl (meth) acrylate, 2-methoxyethyl (meth) acrylate 2-ethoxyethyl (meth) acrylate, 2- (2-methoxyethoxy) ethyl (meth) acrylate, 3-phenoxy-2-hydroxypropyl (meth) acrylate, benzyl (meth) acrylate, diethylene glycol monomethyl ether (meta ) Acrylate, diethylene glycol monoethyl ether (meth) acrylate, diethylene glycol monophenyl ether (meth) acrylate, triethylene glycol monomethyl ether (meth) acrylate, triethylene glycol monoethyl ether (meth) acrylate, polyethylene glycol monomethyl ether (meth) acrylate , Polyethylene glycol monoethyl ether (meth) acrylate, β-phenoxyethoxyethyl acrylate, Nylphenoxypolyethylene glycol (meth) acrylate, dicyclopentanyl (meth) acrylate, dicyclopentenyl (meth) acrylate, dicyclopentenyloxyethyl (meth) acrylate, trifluoroethyl (meth) acrylate, octafluoropentyl (meth) Examples thereof include acrylate, perfluorooctylethyl (meth) acrylate, tribromophenyl (meth) acrylate, and tribromophenyloxyethyl (meth) acrylate.

  Examples of the crotonic acid esters include butyl crotonate and hexyl crotonate.

  Examples of the vinyl esters include vinyl acetate, vinyl propionate, vinyl butyrate, vinyl methoxyacetate, vinyl benzoate, and the like.

  Examples of the maleic acid diesters include dimethyl maleate, diethyl maleate, and dibutyl maleate.

  Examples of the fumaric acid diesters include dimethyl fumarate, diethyl fumarate, dibutyl fumarate and the like.

  Examples of the itaconic acid diesters include dimethyl itaconate, diethyl itaconate, and dibutyl itaconate.

  Examples of the (meth) acrylamides include (meth) acrylamide, N-methyl (meth) acrylamide, N-ethyl (meth) acrylamide, N-propyl (meth) acrylamide, N-isopropyl (meth) acrylamide, N- n-butylacryl (meth) amide, Nt-butyl (meth) acrylamide, N-cyclohexyl (meth) acrylamide, N- (2-methoxyethyl) (meth) acrylamide, N, N-dimethyl (meth) acrylamide, Examples thereof include N, N-diethyl (meth) acrylamide, N-phenyl (meth) acrylamide, N-benzyl (meth) acrylamide, (meth) acryloylmorpholine, diacetone acrylamide and the like.

  Examples of the vinyl ethers include methyl vinyl ether, butyl vinyl ether, hexyl vinyl ether, and methoxyethyl vinyl ether.

  Examples of the method for synthesizing a vinyl monomer having a urethane group or a urea group as the functional group include an addition reaction of an isocyanate group and a hydroxyl group or an amino group. Specifically, a monomer having an isocyanate group, and a hydroxyl group An addition reaction with a compound containing 1 or a compound having one primary or secondary amino group, an addition reaction between a monomer having a hydroxyl group or a monomer having a primary or secondary amino group, and a monoisocyanate. .

  Examples of the monomer having an isocyanate group include compounds represented by the following structural formulas (33) to (35).

However, in the structural formulas (33) to (35), R ¹ represents a hydrogen atom or a methyl group.

  Examples of the monoisocyanate include cyclohexyl isocyanate, n-butyl isocyanate, toluyl isocyanate, benzyl isocyanate, and phenyl isocyanate.

  Examples of the monomer having a hydroxyl group include compounds represented by the following structural formulas (36) to (44).

However, in the structural formulas (36) to (44), R ¹ represents a hydrogen atom or a methyl group, and n, n1, and n2 represent an integer of 1 or more.

  Examples of the compound containing one hydroxyl group include alcohols (for example, methanol, ethanol, n-propanol, i-propanol, n-butanol, sec-butanol, t-butanol, n-hexanol, 2-ethylhexanol). , N-decanol, n-dodecanol, n-octadecanol, cyclopentanol, cyclohexanol, benzyl alcohol, phenylethyl alcohol, etc.), phenols (eg, phenol, cresol, naphthol, etc.), and further containing substituents Examples thereof include fluoroethanol, trifluoroethanol, methoxyethanol, phenoxyethanol, chlorophenol, dichlorophenol, methoxyphenol, acetoxyphenol, and the like.

  Examples of the monomer having a primary or secondary amino group include vinylbenzylamine.

  Examples of the compound containing one primary or secondary amino group include alkylamines (methylamine, ethylamine, n-propylamine, i-propylamine, n-butylamine, sec-butylamine, t-butylamine, hexyl). Amine, 2-ethylhexylamine, decylamine, dodecylamine, octadecylamine, dimethylamine, diethylamine, dibutylamine, dioctylamine), cyclic alkylamine (cyclopentylamine, cyclohexylamine, etc.), aralkylamine (benzylamine, phenethylamine, etc.), Arylamines (aniline, toluylamine, xylylamine, naphthylamine, etc.), combinations thereof (N-methyl-N-benzylamine, etc.), and amines containing substituents (trifluoroethylamino , Hexafluoro isopropyl amine, methoxyaniline, methoxypropylamine and the like) and the like.

  Examples of the other copolymerizable monomers other than those described above include, for example, methyl (meth) acrylate, ethyl (meth) acrylate, butyl (meth) acrylate, benzyl (meth) acrylate, and (meth) acrylic. Preferable examples include 2-ethylhexyl acid, styrene, chlorostyrene, bromostyrene, and hydroxystyrene.

  The said other copolymerizable monomer may be used individually by 1 type, and may use 2 or more types together.

  The vinyl copolymer can be prepared by copolymerizing the corresponding monomers by a known method according to a conventional method. For example, it can be prepared by using a method (solution polymerization method) in which the monomer is dissolved in a suitable solvent and a radical polymerization initiator is added thereto to polymerize in a solution. Moreover, it can prepare by utilizing superposition | polymerization by what is called emulsion polymerization etc. in the state which disperse | distributed the said monomer in the aqueous medium.

  The suitable solvent used in the solution polymerization method is not particularly limited and may be appropriately selected depending on the monomer used and the solubility of the copolymer to be produced. For example, methanol, ethanol, propanol, Examples include isopropanol, 1-methoxy-2-propanol, acetone, methyl ethyl ketone, methyl isobutyl ketone, methoxypropyl acetate, ethyl lactate, ethyl acetate, acetonitrile, tetrahydrofuran, dimethylformamide, chloroform, toluene and the like. These solvents may be used alone or in combination of two or more.

  The radical polymerization initiator is not particularly limited, and examples thereof include 2,2′-azobis (isobutyronitrile) (AIBN) and 2,2′-azobis- (2,4′-dimethylvaleronitrile). Examples thereof include peroxides such as azo compounds and benzoyl peroxide, and persulfates such as potassium persulfate and ammonium persulfate.

There is no restriction | limiting in particular as content rate of the polymeric compound which has a carboxyl group in the said vinyl copolymer, Although it can select suitably according to the objective, For example, 5-50 mol% is preferable, 10-40 mol % Is more preferable, and 15 to 35 mol% is particularly preferable.
If the content is less than 5 mol%, the developability to alkaline water may be insufficient, and if it exceeds 50 mol%, the developer resistance of the cured portion (image portion) may be insufficient.

There is no restriction | limiting in particular as molecular weight of the binder which has the said carboxyl group, Although it can select suitably according to the objective, For example, 2,000-300,000 are preferable as a mass mean molecular weight, 4,000-150 1,000 is more preferable.
When the mass average molecular weight is less than 2,000, the strength of the film tends to be insufficient and stable production may be difficult, and when it exceeds 300,000, developability may be deteriorated.

  The binder which has the said carboxyl group may be used individually by 1 type, and may use 2 or more types together. Examples of the case where two or more binders are used in combination include, for example, a combination of two or more binders composed of different copolymer components, two or more binders having different mass average molecular weights, and two or more binders having different dispersities. Is mentioned.

  The binder having a carboxyl group may be partially or entirely neutralized with a basic substance. The binder may be used in combination with resins having different structures such as polyester resin, polyamide resin, polyurethane resin, epoxy resin, polyvinyl alcohol, and gelatin.

  Moreover, as the binder, a resin soluble in an alkaline liquid described in Japanese Patent No. 2873890 and the like can be used.

The acid value of the binder is not particularly limited and may be appropriately selected depending on the intended purpose. For example, it is preferably 70 to 250 (mgKOH / g), more preferably 90 to 200 (mgKOH / g), 100 to 180 (mg KOH / g) is particularly preferable.
When the acid value is less than 70 (mgKOH / g), developability may be insufficient, resolution may be inferior, and permanent patterns such as wiring patterns may not be obtained with high definition. / G), at least one of the developer resistance and adhesion of the pattern deteriorates, and a permanent pattern such as a wiring pattern may not be obtained with high definition.

When the binder is a substance having a glass transition temperature, the glass transition temperature is not particularly limited and may be appropriately selected depending on the intended purpose.For example, tackiness of the pattern forming material, edge fusion, And from either viewpoint of the peelability of the said support body, 80 degreeC or more is preferable, 100 degreeC or more is more preferable, and 120 degreeC or more is especially preferable.
When the glass transition temperature is less than 80 ° C., the tackiness of the pattern forming material may increase, edge fusion may easily occur, and the peelability of the support may deteriorate.

There is no restriction | limiting in particular as content of the said binder in the said photosensitive layer, Although it can select suitably according to the objective, For example, 10-90 mass% is preferable, 20-80 mass% is more preferable, 40- 80% by mass is particularly preferred.
When the content is less than 10% by mass, alkali developability and adhesion to a printed wiring board forming substrate (for example, a copper-clad laminate) may be deteriorated. Stability and strength of the cured film (tent film) may be reduced. The content may be the total content of the binder and the polymer binder used in combination as necessary.

<< polymerizable compound >>
There is no restriction | limiting in particular as said polymeric compound, Although it can select suitably according to the objective, For example, the monomer or oligomer which has at least any one of a urethane group and an aryl group is mentioned suitably. Moreover, it is preferable that these have 2 or more types of polymeric groups.

  Examples of the polymerizable group include an ethylenically unsaturated bond (for example, (meth) acryloyl group, (meth) acrylamide group, styryl group, vinyl group such as vinyl ester and vinyl ether, allyl group such as allyl ether and allyl ester). Etc.) and a polymerizable cyclic ether group (for example, epoxy group, oxetane group, etc.) and the like. Among these, an ethylenically unsaturated bond is preferable.

-Monomer having a urethane group-
The monomer having a urethane group is not particularly limited as long as it has a urethane group, and can be appropriately selected depending on the purpose. For example, JP-B-48-41708, JP-A-51-37193, JP-B-5 -50737, Japanese Patent Publication No. 7-7208, Japanese Patent Application Laid-Open No. 2001-154346, Japanese Patent Application Laid-Open No. 2001-356476, and the like. For example, a polyisocyanate compound having two or more isocyanate groups in the molecule And an adduct of a vinyl monomer having a hydroxyl group in the molecule.

  Examples of the polyisocyanate compound having two or more isocyanate groups in the molecule include hexamethylene diisocyanate, trimethylhexamethylene diisocyanate, isophorone diisocyanate, xylene diisocyanate, toluene diisocyanate, phenylene diisocyanate, norbornene diisocyanate, diphenyl diisocyanate, diphenylmethane diisocyanate, A diisocyanate such as 3,3′dimethyl-4,4′-diphenyl diisocyanate; a polyaddition product of the diisocyanate with a bifunctional alcohol (in this case, both ends are isocyanate groups); a burette or isocyanurate of the diisocyanate; Trimer; the diisocyanate or diisocyanates and trimethylolpropane, pe Taerisurutoru, polyfunctional alcohols such as glycerin, or the like adducts of other functional alcohol obtained of such these ethylene oxide adducts and the like.

  Examples of the vinyl monomer having a hydroxyl group in the molecule include 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate, diethylene glycol mono (meth) acrylate, and triethylene. Glycol mono (meth) acrylate, tetraethylene glycol mono (meth) acrylate, octaethylene glycol mono (meth) acrylate, polyethylene glycol mono (meth) acrylate, dipropylene glycol mono (meth) acrylate, tripropylene glycol mono (meth) acrylate , Tetrapropylene glycol mono (meth) acrylate, octapropylene glycol mono (meth) acrylate, polypropylene glycol mono (meth) Chryrate, dibutylene glycol mono (meth) acrylate, tributylene glycol mono (meth) acrylate, tetrabutylene glycol mono (meth) acrylate, octabutylene glycol mono (meth) acrylate, polybutylene glycol mono (meth) acrylate, trimethylolpropane Examples include di (meth) acrylate and pentaerythritol tri (meth) acrylate. Moreover, the one terminal (meth) acrylate body of the diol body which has different alkylene oxide parts, such as a copolymer (random, a block, etc.) of ethylene oxide and propylene oxide, etc. are mentioned.

  In addition, examples of the monomer having a urethane group include compounds having an isocyanurate ring such as tri ((meth) acryloyloxyethyl) isocyanurate, di (meth) acrylated isocyanurate, and tri (meth) acrylate of ethylene oxide-modified isocyanuric acid. Is mentioned. Among these, the compound represented by the following structural formula (45) or the structural formula (46) is preferable, and at least the compound represented by the structural formula (46) is particularly preferable from the viewpoint of tent properties. Moreover, these compounds may be used individually by 1 type, and may use 2 or more types together.

In the structural formulas (45) and (46), R ^{1 to} R ³ each represent a hydrogen atom or a methyl group. X ₁ to X ₃ represents an alkylene oxide, may be alone or in combination of two or more thereof.

  Examples of the alkylene oxide group include an ethylene oxide group, a propylene oxide group, a butylene oxide group, a pentylene oxide group, a hexylene oxide group, and a group in which these are combined (may be combined in any of random or block). Among these, an ethylene oxide group, a propylene oxide group, a butylene oxide group, or a combination thereof is preferable, and an ethylene oxide group and a propylene oxide group are more preferable.

  In the structural formulas (45) and (46), m1 to m3 represent an integer of 1 to 60, preferably 2 to 30, and more preferably 4 to 15.

In the structural formulas (45) and (46), Y ¹ and Y ² represent a divalent organic group having 2 to 30 carbon atoms, for example, an alkylene group, an arylene group, an alkenylene group, an alkynylene group, a carbonyl group. (—CO—), an oxygen atom (—O—), a sulfur atom (—S—), an imino group (—NH—), a substituted imino group in which the hydrogen atom of the imino group is substituted with a monovalent hydrocarbon group, Preferred examples include a sulfonyl group (—SO ₂ —) or a combination thereof, and among these, an alkylene group, an arylene group, or a combination thereof is preferable.

  The alkylene group may have a branched structure or a cyclic structure, for example, methylene group, ethylene group, propylene group, isopropylene group, butylene group, isobutylene group, pentylene group, neopentylene group, hexylene group, trimethyl hexene. Preferable examples include a xylene group, a cyclohexylene group, a heptylene group, an octylene group, a 2-ethylhexylene group, a nonylene group, a decylene group, a dodecylene group, an octadecylene group, or any of the groups shown below.

  The arylene group may be substituted with a hydrocarbon group, and examples thereof include a phenylene group, a tolylene group, a diphenylene group, a naphthylene group, and the groups shown below.

  Examples of the group in which these are combined include a xylylene group.

  The alkylene group, arylene group, or a combination thereof may further have a substituent. Examples of the substituent include a halogen atom (for example, fluorine atom, chlorine atom, bromine atom, iodine). Atom), aryl group, alkoxy group (for example, methoxy group, ethoxy group, 2-ethoxyethoxy group), aryloxy group (for example, phenoxy group), acyl group (for example, acetyl group, propionyl group), acyloxy group (for example, , Acetoxy group, butyryloxy group), alkoxycarbonyl group (for example, methoxycarbonyl group, ethoxycarbonyl group), aryloxycarbonyl group (for example, phenoxycarbonyl group) and the like.

  In the structural formulas (45) and (46), n represents an integer of 3 to 6, and 3, 4 or 6 is preferable from the viewpoint of raw material supply for synthesizing a polymerizable monomer.

  In the structural formulas (45) and (46), Z represents an n-valent (trivalent to hexavalent) linking group, and examples thereof include any of the groups shown below.

However, _{X 4} represents an alkylene oxide. m4 represents an integer of 1 to 20. n represents an integer of 3 to 6. A represents an n-valent (trivalent to hexavalent) organic group.

  Examples of A include an n-valent aliphatic group, an n-valent aromatic group, and an alkylene group, an arylene group, an alkenylene group, an alkynylene group, a carbonyl group, an oxygen atom, a sulfur atom, an imino group, and an imino group. Are preferably a combination of a substituted imino group in which the hydrogen atom is substituted with a monovalent hydrocarbon group or a sulfonyl group, an n-valent aliphatic group, an n-valent aromatic group, or an alkylene group or arylene A group in which a group and an oxygen atom are combined is more preferable, and an n-valent aliphatic group, and a group in which an n-valent aliphatic group is combined with an alkylene group and an oxygen atom are particularly preferable.

  The number of carbon atoms of A is, for example, preferably an integer of 1 to 100, more preferably an integer of 1 to 50, and particularly preferably an integer of 3 to 30.

The n-valent aliphatic group may have a branched structure or a cyclic structure.
As a carbon atom number of the said aliphatic group, the integer of 1-30 is preferable, for example, the integer of 1-20 is more preferable, and the integer of 3-10 is especially preferable.
The number of carbon atoms of the aromatic group is preferably an integer of 6 to 100, more preferably an integer of 6 to 50, and particularly preferably an integer of 6 to 30.

  The n-valent aliphatic group or aromatic group may further have a substituent. Examples of the substituent include a hydroxyl group, a halogen atom (for example, a fluorine atom, a chlorine atom, a bromine atom, Iodine atom), aryl group, alkoxy group (for example, methoxy group, ethoxy group, 2-ethoxyethoxy group), aryloxy group (for example, phenoxy group), acyl group (for example, acetyl group, propionyl group), acyloxy group ( Examples thereof include an acetoxy group, a butyryloxy group), an alkoxycarbonyl group (for example, a methoxycarbonyl group, an ethoxycarbonyl group), an aryloxycarbonyl group (for example, a phenoxycarbonyl group), and the like.

The alkylene group may have a branched structure or a cyclic structure.
As a carbon atom number of the said alkylene group, the integer of 1-18 is preferable, for example, and the integer of 1-10 is more preferable.

The arylene group may be further substituted with a hydrocarbon group.
As the number of carbon atoms of the arylene group, an integer of 6 to 18 is preferable, and an integer of 6 to 10 is more preferable.

  As a carbon atom number of the monovalent hydrocarbon group of the said substituted imino group, the integer of 1-18 is preferable and the integer of 1-10 is more preferable.

  Below, the preferable example of said A is as follows.

  Examples of the compounds represented by the structural formulas (45) and (46) include compounds represented by the following structural formulas (47) to (69).

  However, in said structural formula (47)-(69), n, n1, n2 and m mean 1-60, l means 1-20, R represents a hydrogen atom or a methyl group. .

-Monomer having an aryl group-
The monomer having an aryl group is not particularly limited as long as it has an aryl group, and can be appropriately selected depending on the purpose. For example, a polyhydric alcohol compound having a aryl group, a polyvalent amine compound, and a polyvalent Examples thereof include esters or amides of at least one of amino alcohol compounds and unsaturated carboxylic acid.

  Examples of the polyhydric alcohol compound, polyamine compound or polyhydric amino alcohol compound having an aryl group include polystyrene oxide, xylylene diol, di- (β-hydroxyethoxy) benzene, 1,5-dihydroxy-1, 2,3,4-tetrahydronaphthalene, 2,2-diphenyl-1,3-propanediol, hydroxybenzyl alcohol, hydroxyethyl resorcinol, 1-phenyl-1,2-ethanediol, 2,3,5,6-tetra Methyl-p-xylene-α, α′-diol, 1,1,4,4-tetraphenyl-1,4-butanediol, 1,1,4,4-tetraphenyl-2-butyne-1,4- Diol, 1,1′-bi-2-naphthol, dihydroxynaphthalene, 1,1′-methylene-di-2-naphth 1,2,4-benzenetriol, biphenol, 2,2′-bis (4-hydroxyphenyl) butane, 1,1-bis (4-hydroxyphenyl) cyclohexane, bis (hydroxyphenyl) methane, catechol, 4-chlororesorcinol, hydroquinone, hydroxybenzyl alcohol, methyl hydroquinone, methylene-2,4,6-trihydroxybenzoate, phloroglicinol, pyrogallol, resorcinol, α- (1-aminoethyl) -p-hydroxybenzyl alcohol, α -(1-aminoethyl) -p-hydroxybenzyl alcohol, 3-amino-4-hydroxyphenylsulfone and the like can be mentioned. In addition, compounds obtained by adding α, β-unsaturated carboxylic acid to glycidyl compounds such as xylylene bis (meth) acrylamide, novolac epoxy resin and bisphenol A diglycidyl ether, phthalic acid, trimellitic acid, etc. Esterified products obtained from vinyl monomers containing hydroxyl groups in the molecule, diallyl phthalate, triallyl trimellitic acid, diallyl benzenedisulfonate, cationically polymerizable divinyl ethers (for example, bisphenol A divinyl ether), epoxy as a polymerizable monomer Compound (for example, novolac type epoxy resin, bisphenol A diglycidyl ether, etc.), vinyl ester (for example, divinyl phthalate, divinyl terephthalate, divinylbenzene-1,3-disulfonate, etc.), styrene Compounds such as divinylbenzene, p-allylstyrene, p-isopropenestyrene, and the like. Among these, the compound represented by the following structural formula (70) is preferable.

In the structural formula (70), R ⁴ and R ⁵ represent a hydrogen atom or an alkyl group.

In the structural formula (70), X ₅ and X ₆ represent an alkylene oxide group, which may be used alone or in combination of two or more. As the alkylene oxide group, for example, an ethylene oxide group, a propylene oxide group, a butylene oxide group, a pentylene oxide group, a hexylene oxide group, a group combining these (which may be combined in any of random and block), Among these, an ethylene oxide group, a propylene oxide group, a butylene oxide group, or a group combining these is preferable, and an ethylene oxide group and a propylene oxide group are more preferable.

  In the structural formula (70), m5 and m6 are preferably an integer of 1 to 60, more preferably an integer of 2 to 30, and particularly preferably an integer of 4 to 15.

In the structural formula (70), T represents a divalent linking group, and examples thereof include methylene, ethylene, MeCMe, CF ₃ CCF ₃ , CO, and SO ₂ .

In the structural formula (70), Ar ¹ and Ar ² represent an aryl group which may have a substituent, and examples thereof include phenylene and naphthylene. Examples of the substituent include an alkyl group, an aryl group, an aralkyl group, a halogen group, an alkoxy group, or a combination thereof.

  Specific examples of the monomer having an aryl group include 2,2-bis [4- (3- (meth) acryloxy-2-hydroxypropoxy) phenyl] propane, 2,2-bis [4-((meth)). (Acryloxyethoxy) phenyl] propane, 2,2-bis (4-((meth) acryloyloxypolyethoxy) phenyl) propane having 2 to 20 ethoxy groups substituted with one phenolic OH group (For example, 2,2-bis (4-((meth) acryloyloxydiethoxy) phenyl) propane, 2,2-bis (4-((meth) acryloyloxytetraethoxy) phenyl) propane, 2,2-bis (4-((Meth) acryloyloxypentaethoxy) phenyl) propane, 2,2-bis (4-((meth) acryloyloxydecae) Xyl) phenyl) propane, 2,2-bis (4-((meth) acryloyloxypentadecaethoxy) phenyl) propane), 2,2-bis [4-((meth) acryloxypropoxy) phenyl] propane, 2,2-bis (4-((meth) acryloyloxypolypropoxy) phenyl) propane (e.g. 2,2-bis (2) having 2 to 20 ethoxy groups substituted with one phenolic OH group 4-((meth) acryloyloxydipropoxy) phenyl) propane, 2,2-bis (4-((meth) acryloyloxytetrapropoxy) phenyl) propane, 2,2-bis (4-((meth) acryloyloxy) Pentapropoxy) phenyl) propane, 2,2-bis (4-((meth) acryloyloxydecapropoxy) pheny ) Propane, 2,2-bis (4-((meth) acryloyloxypentadecapropoxy) phenyl) propane, or the like, or both the polyethylene oxide skeleton and the polypropylene oxide skeleton in the same molecule as the polyether moiety Compounds (for example, compounds described in WO01 / 98832 etc., or commercially available, Shin-Nakamura Chemical Co., Ltd., BPE-200, BPE-500, BPE-1000), bisphenol skeleton and urethane group Examples thereof include a polymerizable compound. These compounds may be compounds obtained by changing the part derived from the bisphenol A skeleton to bisphenol F or bisphenol S.

  Examples of the polymerizable compound having a bisphenol skeleton and a urethane group include an isocyanate group and a polymerizable group in a compound having a hydroxyl group at the terminal obtained as an adduct such as bisphenol and ethylene oxide or propylene oxide, or a polyaddition product. Examples thereof include compounds (for example, 2-isocyanatoethyl (meth) acrylate, α, α-dimethyl-vinylbenzyl isocyanate, etc.).

-Other polymerizable monomers-
In the pattern forming material of the present invention, a polymerizable monomer other than the monomer having the urethane group and the monomer having the aryl group may be used.

  Examples of the polymerizable monomer other than the monomer containing the urethane group and the monomer containing the aromatic ring include an unsaturated carboxylic acid (for example, acrylic acid, methacrylic acid, itaconic acid, crotonic acid, isocrotonic acid, maleic acid). Etc.) and an aliphatic polyhydric alcohol compound, an amide of an unsaturated carboxylic acid and a polyvalent amine compound, and the like.

  Examples of the monomer of the ester of the unsaturated carboxylic acid and the aliphatic polyhydric alcohol compound include (meth) acrylic acid ester, ethylene glycol di (meth) acrylate, and polyethylene glycol having 2 to 18 ethylene groups. Di (meth) acrylate (for example, diethylene glycol di (meth) acrylate, triethylene glycol di (meth) acrylate, tetraethylene glycol di (meth) acrylate, nonaethylene glycol di (meth) acrylate, dodecaethylene glycol di (meth) acrylate , Tetradecaethylene glycol di (meth) acrylate, etc.), propylene glycol di (meth) acrylate, polypropylene glycol di (meth) acrylate having 2 to 18 propylene groups (for example, , Dipropylene glycol di (meth) acrylate, tripropylene glycol di (meth) acrylate, tetrapropylene glycol di (meth) acrylate, dodecapropylene glycol di (meth) acrylate, etc.), neopentyl glycol di (meth) acrylate, ethylene oxide modified Neopentyl glycol di (meth) acrylate, propylene oxide modified neopentyl glycol di (meth) acrylate, trimethylolpropane tri (meth) acrylate, trimethylolpropane di (meth) acrylate, trimethylolpropane tri ((meth) acryloyloxypropyl) ) Ether, trimethylolethane tri (meth) acrylate, 1,3-propanediol di (meth) acrylate, 1,3-butanediol (Meth) acrylate, 1,4-butanediol di (meth) acrylate, 1,6-hexanediol di (meth) acrylate, tetramethylene glycol di (meth) acrylate, 1,4-cyclohexanediol di (meth) acrylate, 1,2,4-butanetriol tri (meth) acrylate, 1,5-bentanediol (meth) acrylate, pentaerythritol di (meth) acrylate, pentaerythritol tri (meth) acrylate, pentaerythritol tetra (meth) acrylate, di Pentaerythritol penta (meth) acrylate, dipentaerythritol hexa (meth) acrylate, sorbitol tri (meth) acrylate, sorbitol tetra (meth) acrylate, sorbitol penta (meth) acrylate Rate, sorbitol hexa (meth) acrylate, dimethylol dicyclopentane di (meth) acrylate, tricyclodecane di (meth) acrylate, neopentyl glycol di (meth) acrylate, neopentyl glycol modified trimethylolpropane di (meth) acrylate A di (meth) acrylate of an alkylene glycol chain having at least one ethylene glycol chain / propylene glycol chain (for example, a compound described in WO01 / 98832), at least one of ethylene oxide and propylene oxide Trimethylolpropane tri (meth) acrylate, polybutylene glycol di (meth) acrylate, glycerol di (meth) acrylate, glycerol tri (meth) acrylate Examples include relate and xylenol di (meth) acrylate.

  Among the (meth) acrylic acid esters, ethylene glycol di (meth) acrylate, polyethylene glycol di (meth) acrylate, propylene glycol di (meth) acrylate, polypropylene glycol di (meta) from the viewpoint of easy availability. ) Acrylate, di (meth) acrylate of alkylene glycol chain each having at least one ethylene glycol chain / propylene glycol chain, trimethylolpropane tri (meth) acrylate, pentaerythritol tetra (meth) acrylate, pentaerythritol triacrylate, penta Erythritol di (meth) acrylate, dipentaerythritol penta (meth) acrylate, dipentaerythritol hexa (meth) acrylate, glycerin tri (Meth) acrylate, diglycerin di (meth) acrylate, 1,3-propanediol di (meth) acrylate, 1,2,4-butanetriol tri (meth) acrylate, 1,4-cyclohexanediol di (meth) acrylate, 1, Preference is given to 5-pentanediol (meth) acrylate, neopentyl glycol di (meth) acrylate, trimethylolpropane tri (meth) acrylate added with ethylene oxide, and the like.

  Examples of the ester (itaconic acid ester) of the itaconic acid and the aliphatic polyhydric alcohol compound include ethylene glycol diitaconate, propylene glycol diitaconate, 1,3-butanediol diitaconate, 1,4- Examples include butanediol diitaconate, tetramethylene glycol diitaconate, pentaerythritol diitaconate, and sorbitol tetritaconate.

  Examples of the ester (crotonic acid ester) of the crotonic acid and the aliphatic polyhydric alcohol compound include ethylene glycol dicrotonate, tetramethylene glycol dicrotonate, pentaerythritol dicrotonate, and sorbitol tetradicrotonate. Can be mentioned.

  Examples of the ester (isocrotonic acid ester) of the isocrotonic acid and the aliphatic polyhydric alcohol compound include ethylene glycol diisocrotonate, pentaerythritol diisocrotonate, and sorbitol tetraisocrotonate.

  Examples of the ester of maleic acid and the aliphatic polyhydric alcohol compound (maleic acid ester) include ethylene glycol dimaleate, triethylene glycol dimaleate, pentaerythritol dimaleate, and sorbitol tetramaleate.

  Examples of the amide derived from the polyvalent amine compound and the unsaturated carboxylic acid include methylene bis (meth) acrylamide, ethylene bis (meth) acrylamide, 1,6-hexamethylene bis (meth) acrylamide, and octamethylene bis ( And (meth) acrylamide, diethylenetriamine tris (meth) acrylamide, and diethylenetriamine bis (meth) acrylamide.

  In addition to the above, as the polymerizable monomer, for example, butanediol-1,4-diglycidyl ether, cyclohexanedimethanol glycidyl ether, ethylene glycol diglycidyl ether, diethylene glycol diglycidyl ether, dipropylene glycol diglycidyl ether, Compounds obtained by adding an α, β-unsaturated carboxylic acid to a glycidyl group-containing compound such as hexanediol diglycidyl ether, trimethylolpropane triglycidyl ether, pentaerythritol tetraglycidyl ether, glycerin triglycidyl ether, Polyester acrylate and polyester (meth) acrylate as described in JP-B-6183, JP-B-49-43191 and JP-B-52-30490. Rate oligomers, epoxy compounds (eg, butanediol-1,4-diglycidyl ether, cyclohexanedimethanol glycidyl ether, diethylene glycol diglycidyl ether, dipropylene glycol diglycidyl ether, hexanediol diglycidyl ether, trimethylolpropane triglycidyl ether , Pentaerythritol tetraglycidyl ether, glycerin triglycidyl ether and the like) and polyfunctional acrylates and methacrylates such as epoxy acrylates obtained by reacting (meth) acrylic acid, Japan Adhesion Association Vol. 20, No. 7, 300-308 Photocurable monomers and oligomers and allyl esters described in page (1984) (eg diallyl phthalate, diallyl adipate, malonic acid) Allyl, diallylamide (eg, diallylacetamide), cationically polymerizable divinyl ethers (eg, butanediol-1,4-divinyl ether, cyclohexanedimethanol divinyl ether, ethylene glycol divinyl ether, diethylene glycol divinyl ether, dipropylene glycol) Divinyl ether, hexanediol divinyl ether, trimethylolpropane trivinyl ether, pentaerythritol tetravinyl ether, glycerin trivinyl ether, etc.), epoxy compounds (for example, butanediol-1,4-diglycidyl ether, cyclohexanedimethanol glycidyl ether, ethylene glycol di) Glycidyl ether, diethylene glycol diglycidyl ether, dipropylene group Recall diglycidyl ether, hexanediol diglycidyl ether, trimethylolpropane triglycidyl ether, pentaerythritol tetraglycidyl ether, glycerin triglycidyl ether, etc.), oxetanes (for example, 1,4-bis [(3-ethyl-3-oxetanylmethoxy) ) Methyl] benzene, etc.), epoxy compounds, oxetanes (for example, compounds described in WO01 / 22165), N-β-hydroxyethyl-β- (methacrylamide) ethyl acrylate, N, N-bis (β- And compounds having two or more different ethylenically unsaturated double bonds, such as methacryloxyethyl) acrylamide and allyl methacrylate.

  Examples of the vinyl esters include divinyl succinate and divinyl adipate.

  These polyfunctional monomers or oligomers may be used alone or in combination of two or more.

If necessary, the polymerizable monomer may be used in combination with a polymerizable compound (monofunctional monomer) containing one polymerizable group in the molecule.
Examples of the monofunctional monomer include the compounds exemplified as the raw material of the binder, and the dibasic mono ((meth) acryloyloxyalkyl ester) mono (halohydroxyalkyl ester) described in JP-A-6-236031. Monofunctional monomers such as γ-chloro-β-hydroxypropyl-β′-methacryloyloxyethyl-o-phthalate, etc., compounds described in Japanese Patent No. 2744443, WO00 / 52529, Japanese Patent No. 2548016, etc. Is mentioned.

As content of the polymeric compound in the said photosensitive layer, 5-90 mass% is preferable, for example, 15-60 mass% is more preferable, and 20-50 mass% is especially preferable.
If the content is 5% by mass, the strength of the tent film may be reduced, and if it exceeds 90% by mass, edge fusion during storage (exudation failure from the end of the roll) may be deteriorated. .
Moreover, as content of the polyfunctional monomer which has 2 or more of the said polymeric groups in a polymeric compound, 5-100 mass% is preferable, 20-100 mass% is more preferable, 40-100 mass% is especially preferable. .

<< photopolymerization initiator >>
The photopolymerization initiator is not particularly limited as long as it has the ability to initiate polymerization of the polymerizable compound, and can be appropriately selected from known photopolymerization initiators. For example, it is visible from the ultraviolet region. It is preferable to have photosensitivity to the light of the photocatalyst, and may be an activator that generates an active radical by generating some action with a photoexcited sensitizer, and initiates cationic polymerization depending on the type of monomer. Initiator may be used.
The photopolymerization initiator preferably contains at least one component having a molecular extinction coefficient of at least about 50 within a range of about 300 to 800 nm (more preferably 330 to 500 nm).

  Examples of the photopolymerization initiator include halogenated hydrocarbon derivatives (for example, those having a triazine skeleton, those having an oxadiazole skeleton), hexaarylbiimidazoles, oxime derivatives, organic peroxides, thio compounds, Examples include ketone compounds, aromatic onium salts, and metallocenes. Among these, halogenated hydrocarbons having a triazine skeleton, oxime derivatives, ketone compounds, hexaarylbiimidazoles from the viewpoints of sensitivity and storage stability of the photosensitive layer, and adhesion between the photosensitive layer and the printed wiring board forming substrate. System compounds are preferred.

  Examples of the hexaarylbiimidazole include 2,2′-bis (2-chlorophenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole, 2,2′-bis (o-fluorophenyl)- 4,4 ', 5,5'-tetraphenylbiimidazole, 2,2'-bis (2-bromophenyl) -4,4', 5,5'-tetraphenylbiimidazole, 2,2'-bis ( 2,4-dichlorophenyl) -4,4 ', 5,5'-tetraphenylbiimidazole, 2,2'-bis (2-chlorophenyl) -4,4', 5,5'-tetra (3-methoxyphenyl) ) Biimidazole, 2,2'-bis (2-chlorophenyl) -4,4 ', 5,5'-tetra (4-methoxyphenyl) biimidazole, 2,2'-bis (4-methoxyphenyl) -4 , 4 ', , 5'-tetraphenylbiimidazole, 2,2'-bis (2,4-dichlorophenyl) -4,4 ', 5,5'-tetraphenylbiimidazole, 2,2'-bis (2-nitrophenyl) -4,4 ', 5,5'-tetraphenylbiimidazole, 2,2'-bis (2-methylphenyl) -4,4', 5,5'-tetraphenylbiimidazole, 2,2'-bis (2-Trifluoromethylphenyl) -4,4 ', 5,5'-tetraphenylbiimidazole, compounds described in WO00 / 52529, and the like.

  The biimidazoles are described in, for example, Bull. Chem. Soc. Japan, 33, 565 (1960); Org. It can be easily synthesized by the method disclosed in Chem, 36 (16) 2262 (1971).

  Examples of the halogenated hydrocarbon compound having a triazine skeleton include those described in Wakabayashi et al., Bull. Chem. Soc. Japan, 42, 2924 (1969), a compound described in British Patent 1388492, a compound described in JP-A-53-133428, a compound described in German Patent 3337024, F.I. C. J. Schaefer et al. Org. Chem. 29, 1527 (1964), compounds described in JP-A-62-258241, compounds described in JP-A-5-281728, compounds described in JP-A-5-34920, US Pat. No. 4,221,976 And the compounds described in the book.

  Wakabayashi et al., Bull. Chem. Soc. As a compound described in Japan, 42, 2924 (1969), for example, 2-phenyl-4,6-bis (trichloromethyl) -1,3,5-triazine, 2- (4-chlorophenyl) -4,6 -Bis (trichloromethyl) -1,3,5-triazine, 2- (4-tolyl) -4,6-bis (trichloromethyl) -1,3,5-triazine, 2- (4-methoxyphenyl)- 4,6-bis (trichloromethyl) -1,3,5-triazine, 2- (2,4-dichlorophenyl) -4,6-bis (trichloromethyl) -1,3,5-triazine, 2, 4,6-tris (trichloromethyl) -1,3,5-triazine, 2-methyl-4,6-bis (trichloromethyl) -1,3,5-triazine, 2-n-nonyl-4,6- Bis (trichloromethyl) 1,3,5-triazine, and 2-(alpha, alpha, beta-trichloroethyl) -4,6-bis (trichloromethyl) -1,3,5-triazine.

  Examples of the compound described in the British Patent 1388492 include 2-styryl-4,6-bis (trichloromethyl) -1,3,5-triazine, 2- (4-methylstyryl) -4,6- Bis (trichloromethyl) -1,3,5-triazine, 2- (4-methoxystyryl) -4,6-bis (trichloromethyl) -1,3,5-triazine, 2- (4-methoxystyryl)- 4-amino-6-trichloromethyl-1,3,5-triazine and the like can be mentioned.

  Examples of the compounds described in JP-A-53-133428 include 2- (4-methoxy-naphth-1-yl) -4,6-bis (trichloromethyl) -1,3,5-triazine, 2 -(4-Ethoxy-naphth-1-yl) -4,6-bis (trichloromethyl) -1,3,5-triazine, 2- [4- (2-ethoxyethyl) -naphth-1-yl]- 4,6-bis (trichloromethyl) -1,3,5-triazine, 2- (4,7-dimethoxy-naphth-1-yl) -4,6-bis (trichloromethyl) -1,3,5- Examples include triazine and 2- (acenaphtho-5-yl) -4,6-bis (trichloromethyl) -1,3,5-triazine.

  Examples of the compound described in the specification of German Patent 3333724 include 2- (4-styrylphenyl) -4,6-bis (trichloromethyl) -1,3,5-triazine, 2- (4- (4 -Methoxystyryl) phenyl) -4,6-bis (trichloromethyl) -1,3,5-triazine, 2- (1-naphthylvinylenephenyl) -4,6-bis (trichloromethyl) -1,3,5 -Triazine, 2-chlorostyrylphenyl-4,6-bis (trichloromethyl) -1,3,5-triazine, 2- (4-thiophen-2-vinylenephenyl) -4,6-bis (trichloromethyl)- 1,3,5-triazine, 2- (4-thiophene-3-vinylenephenyl) -4,6-bis (trichloromethyl) -1,3,5-triazine, 2- (4-furan-2 Vinylenephenyl) -4,6-bis (trichloromethyl) -1,3,5-triazine, and 2- (4-benzofuran-2-vinylenephenyl) -4,6-bis (trichloromethyl) -1,3 5-triazine etc. are mentioned.

  F. above. C. J. Schaefer et al. Org. Chem. 29, 1527 (1964) include, for example, 2-methyl-4,6-bis (tribromomethyl) -1,3,5-triazine, 2,4,6-tris (tribromomethyl); -1,3,5-triazine, 2,4,6-tris (dibromomethyl) -1,3,5-triazine, 2-amino-4-methyl-6-tri (bromomethyl) -1,3,5- Examples include triazine and 2-methoxy-4-methyl-6-trichloromethyl-1,3,5-triazine.

  Examples of the compounds described in JP-A-62-258241 include 2- (4-phenylethynylphenyl) -4,6-bis (trichloromethyl) -1,3,5-triazine, 2- (4- Naphthyl-1-ethynylphenyl-4,6-bis (trichloromethyl) -1,3,5-triazine, 2- (4- (4-tolylethynyl) phenyl) -4,6-bis (trichloromethyl) -1 , 3,5-triazine, 2- (4- (4-methoxyphenyl) ethynylphenyl) -4,6-bis (trichloromethyl) -1,3,5-triazine, 2- (4- (4-isopropylphenyl) Ethynyl) phenyl) -4,6-bis (trichloromethyl) -1,3,5-triazine, 2- (4- (4-ethylphenylethynyl) phenyl) -4,6-bis (trichloromethyl) Le) -1,3,5-triazine.

  Examples of the compound described in JP-A-5-281728 include 2- (4-trifluoromethylphenyl) -4,6-bis (trichloromethyl) -1,3,5-triazine, 2- (2, 6-difluorophenyl) -4,6-bis (trichloromethyl) -1,3,5-triazine, 2- (2,6-dichlorophenyl) -4,6-bis (trichloromethyl) -1,3,5- Examples include triazine, 2- (2,6-dibromophenyl) -4,6-bis (trichloromethyl) -1,3,5-triazine.

  Examples of the compound described in JP-A-5-34920 include 2,4-bis (trichloromethyl) -6- [4- (N, N-diethoxycarbonylmethylamino) -3-bromophenyl] -1, 3,5-triazine, trihalomethyl-s-triazine compounds described in US Pat. No. 4,239,850, 2,4,6-tris (trichloromethyl) -s-triazine, 2- (4-chlorophenyl) Examples include -4,6-bis (tribromomethyl) -s-triazine.

  Examples of the compound described in US Pat. No. 4,221,976 include compounds having an oxadiazole skeleton (for example, 2-trichloromethyl-5-phenyl-1,3,4-oxadiazole, 2- Trichloromethyl-5- (4-chlorophenyl) -1,3,4-oxadiazole, 2-trichloromethyl-5- (1-naphthyl) -1,3,4-oxadiazole, 2-trichloromethyl-5 -(2-naphthyl) -1,3,4-oxadiazole, 2-tribromomethyl-5-phenyl-1,3,4-oxadiazole, 2-tribromomethyl-5- (2-naphthyl) -1,3,4-oxadiazole; 2-trichloromethyl-5-styryl-1,3,4-oxadiazole, 2-trichloromethyl-5- (4-chlorostyryl) -1,3,4-oxadiazole, 2-trichloromethyl-5- (4-methoxystyryl) -1,3,4-oxadiazole, 2-trichloromethyl-5- (1-naphthyl) -1, 3,4-oxadiazole, 2-trichloromethyl-5- (4-n-butoxystyryl) -1,3,4-oxadiazole, 2-tribromomethyl-5-styryl-1,3,4 Oxadiazole and the like).

  Examples of the oxime derivative suitably used in the present invention include compounds represented by the following structural formulas (71) to (104).

  Examples of the ketone compound include benzophenone, 2-methylbenzophenone, 3-methylbenzophenone, 4-methylbenzophenone, 4-methoxybenzophenone, 2-chlorobenzophenone, 4-chlorobenzophenone, 4-bromobenzophenone, 2-carboxybenzophenone, 2-ethoxycarbonylbenzolphenone, benzophenonetetracarboxylic acid or tetramethyl ester thereof, 4,4′-bis (dialkylamino) benzophenone (for example, 4,4′-bis (dimethylamino) benzophenone, 4,4′- Bisdicyclohexylamino) benzophenone, 4,4′-bis (diethylamino) benzophenone, 4,4′-bis (dihydroxyethylamino) benzophenone, 4-methoxy-4′-dimethylamino Nzophenone, 4,4'-dimethoxybenzophenone, 4-dimethylaminobenzophenone, 4-dimethylaminoacetophenone, benzyl, anthraquinone, 2-t-butylanthraquinone, 2-methylanthraquinone, phenanthraquinone, xanthone, thioxanthone, 2-chloro -Thioxanthone, 2,4-diethylthioxanthone, fluorenone, 2-benzyl-dimethylamino-1- (4-morpholinophenyl) -1-butanone, 2-methyl-1- [4- (methylthio) phenyl] -2-morpholino -1-propanone, 2-hydroxy-2-methyl- [4- (1-methylvinyl) phenyl] propanol oligomer, benzoin, benzoin ethers (for example, benzoin methyl ether, benzoin ethyl ether, In propyl ether, benzoin isopropyl ether, benzoin phenyl ether, benzyl dimethyl ketal), acridone, chloro acridone, N- methyl acridone, N- butyl acridone, N- butyl - such as chloro acrylic pyrrolidone.

  Examples of the metallocenes include bis (η5-2,4-cyclopentadien-1-yl) -bis (2,6-difluoro-3- (1H-pyrrol-1-yl) -phenyl) titanium, η5- Cyclopentadienyl-η6-cumenyl-iron (1 +)-hexafluorophosphate (1-), JP-A-53-133428, JP-B-57-1819, JP-A-57-6096, and US Pat. Examples thereof include compounds described in the specification of 3615455.

  Further, as photopolymerization initiators other than the above, acridine derivatives (for example, 9-phenylacridine, 1,7-bis (9,9′-acridinyl) heptane, etc.), N-phenylglycine, and the like, polyhalogen compounds (for example, Carbon tetrabromide, phenyltribromomethylsulfone, phenyltrichloromethylketone, etc.), coumarins (for example, 3- (2-benzofuroyl) -7-diethylaminocoumarin, 3- (2-benzofuroyl) -7- (1-pyrrolidinyl) ) Coumarin, 3-benzoyl-7-diethylaminocoumarin, 3- (2-methoxybenzoyl) -7-diethylaminocoumarin, 3- (4-dimethylaminobenzoyl) -7-diethylaminocoumarin, 3,3′-carbonylbis (5 , 7-di-n-propoxycoumarin), 3,3′-carbonylbis (7-diethylaminocoumarin), 3-benzoyl-7-methoxycoumarin, 3- (2-furoyl) -7-diethylaminocoumarin, 3- (4-diethylaminocinnamoyl) -7-diethylaminocoumarin, 7-methoxy-3- (3-pyridylcarbonyl) coumarin, 3-benzoyl-5,7-dipropoxycoumarin, 7-benzotriazol-2-ylcoumarin, JP-A-5-19475, JP-A-7-271028, JP-A-2002-363206 No., JP-A-2002-363207, JP-A-2002-363208, JP-A-2002-363209, etc.), amines (for example, ethyl 4-dimethylaminobenzoate, 4-dimethylaminobenzoate) N-butyl acid, 4-dimethylaminobenzoic acid phenethyl, 4-dimethyl 2-phthalimidoethyl tilaminobenzoate, 2-methacryloyloxyethyl 4-dimethylaminobenzoate, pentamethylenebis (4-dimethylaminobenzoate), phenethyl of 3-dimethylaminobenzoic acid, pentamethylene ester, 4-dimethylaminobenzaldehyde, 2-chloro-4-dimethylaminobenzaldehyde, 4-dimethylaminobenzyl alcohol, ethyl (4-dimethylaminobenzoyl) acetate, 4-piperidinoacetophenone, 4-dimethylaminobenzoin, N, N-dimethyl-4-toluidine, N, N-diethyl-3-phenetidine, tribenzylamine, dibenzylphenylamine, N-methyl-N-phenylbenzylamine, 4-bromo-N, N-dimethylaniline, tridodecylamine, amino Nofluoranes (ODB, ODBII, etc.), crystal violet lactone, leuco crystal violet, etc., acylphosphine oxides (for example, bis (2,4,6-trimethylbenzoyl) -phenylphosphine oxide, bis (2,6-dimethoxybenzoyl) ) -2,4,4-trimethyl-pentylphenylphosphine oxide, Lucirin TPO, etc.).

  Further, vicinal polyketaldonyl compounds described in US Pat. No. 2,367,660, acyloin ether compounds described in US Pat. No. 2,448,828, and US Pat. No. 2,722,512 are described. An aromatic acyloin compound substituted with α-hydrocarbon, a polynuclear quinone compound described in US Pat. Nos. 3,046,127 and 2,951,758, an organoboron compound described in JP-A-2002-229194, and a radical Generator, triarylsulfonium salt (for example, salt with hexafluoroantimony or hexafluorophosphate), phosphonium salt compound (for example, (phenylthiophenyl) diphenylsulfonium salt, etc.) (effective as a cationic polymerization initiator), WO01 / 71428 Onium Such compounds.

  The said photoinitiator may be used individually by 1 type, and may use 2 or more types together. Examples of the combination of two or more include, for example, a combination of hexaarylbiimidazole and 4-aminoketone described in US Pat. No. 3,549,367, a benzothiazole compound described in Japanese Patent Publication No. 51-48516, and trihalomethyl- Combinations of s-triazine compounds, combinations of aromatic ketone compounds (such as thioxanthone) and hydrogen donors (such as dialkylamino-containing compounds and phenol compounds), combinations of hexaarylbiimidazole and titanocene, and coumarins And combinations of titanocene and phenylglycines.

  As content of the photoinitiator in the said photosensitive layer, 0.1-30 mass% is preferable, 0.5-20 mass% is more preferable, 0.5-15 mass% is especially preferable.

<< Other ingredients >>
Examples of the other components include sensitizers, thermal polymerization inhibitors, plasticizers, colorants, and the like, and further adhesion promoters and other auxiliaries (for example, pigments, conductive particles). , Fillers, antifoaming agents, flame retardants, leveling agents, peeling accelerators, antioxidants, fragrances, thermal crosslinking agents, surface tension modifiers, chain transfer agents, etc.) may be used in combination. By appropriately containing these components, it is possible to adjust properties such as stability, photographic properties, print-out properties, and film properties of the target pattern forming material.

-Sensitizer-
The sensitizer can be appropriately selected by visible light, ultraviolet light, visible light laser, or the like as a light irradiation means to be described later.
The sensitizer is excited by active energy rays and interacts with other substances (for example, radical generator, acid generator, etc.) (for example, energy transfer, electron transfer, etc.), thereby generating radicals, acids, etc. It is possible to generate a useful group of

  The sensitizer is not particularly limited and may be appropriately selected from known sensitizers. For example, known polynuclear aromatics (for example, pyrene, perylene, triphenylene), xanthenes (for example, , Fluorescein, eosin, erythrosine, rhodamine B, rose bengal), cyanines (eg, indocarbocyanine, thiacarbocyanine, oxacarbocyanine), merocyanines (eg, merocyanine, carbomerocyanine), thiazines (eg, thionine, Methylene blue, toluidine blue), acridines (eg, acridine orange, chloroflavin, acriflavine), anthraquinones (eg, anthraquinone), squariums (eg, squalium), acridones (eg, acridone, chloroacrine) Don, N-methylacridone, N-butylacridone, N-butyl-chloroacridone, etc.), coumarins (for example, 3- (2-benzofuroyl) -7-diethylaminocoumarin, 3- (2-benzofuroyl)- 7- (1-pyrrolidinyl) coumarin, 3-benzoyl-7-diethylaminocoumarin, 3- (2-methoxybenzoyl) -7-diethylaminocoumarin, 3- (4-dimethylaminobenzoyl) -7-diethylaminocoumarin, 3,3 '-Carbonylbis (5,7-di-n-propoxycoumarin), 3,3'-carbonylbis (7-diethylaminocoumarin), 3-benzoyl-7-methoxycoumarin, 3- (2-furoyl) -7- Diethylaminocoumarin, 3- (4-diethylaminocinnamoyl) -7-diethylaminocoumarin Examples thereof include 7-methoxy-3- (3-pyridylcarbonyl) coumarin, 3-benzoyl-5,7-dipropoxycoumarin, and others, and JP-A-5-19475, JP-A-7-271028, JP-A-2002-. No. 363206, JP-A No. 2002-363207, JP-A No. 2002-363208, JP-A No. 2002-363209, and the like.

  Examples of the combination of the photopolymerization initiator and the sensitizer include, for example, an electron transfer start system described in JP-A-2001-305734 [(1) an electron donating initiator and a sensitizing dye, (2) A combination of an electron-accepting initiator and a sensitizing dye, (3) an electron-donating initiator, a sensitizing dye and an electron-accepting initiator (ternary initiation system), and the like.

As content of the said sensitizer, 0.05-30 mass% is preferable with respect to all the components of the photosensitive resin composition, 0.1-20 mass% is more preferable, 0.2-10 mass% is Particularly preferred.
When the content is less than 0.05% by mass, the sensitivity to active energy rays decreases, the exposure process takes time, and the productivity may decrease. When the content exceeds 30% by mass, the photosensitive layer May precipitate during storage.

-Thermal polymerization inhibitor-
The thermal polymerization inhibitor may be added to prevent thermal polymerization or temporal polymerization of the polymerizable compound in the photosensitive layer.
Examples of the thermal polymerization inhibitor include 4-methoxyphenol, hydroquinone, alkyl or aryl-substituted hydroquinone, t-butylcatechol, pyrogallol, 2-hydroxybenzophenone, 4-methoxy-2-hydroxybenzophenone, cuprous chloride, phenothiazine. , Chloranil, naphthylamine, β-naphthol, 2,6-di-tert-butyl-4-cresol, 2,2′-methylenebis (4-methyl-6-tert-butylphenol), pyridine, nitrobenzene, dinitrobenzene, picric acid 4-toluidine, methylene blue, copper and organic chelating agent reactant, methyl salicylate, phenothiazine, nitroso compound, chelate of nitroso compound and Al, and the like.

As content of the said thermal-polymerization inhibitor, 0.001-5 mass% is preferable with respect to the said polymeric compound of the said photosensitive layer, 0.005-2 mass% is more preferable, 0.01-1 mass% Is particularly preferred.
When the content is less than 0.001% by mass, stability during storage may be reduced, and when it exceeds 5% by mass, sensitivity to active energy rays may be reduced.

-Plasticizer-
The plasticizer may be added to control film physical properties (flexibility) of the photosensitive layer.
Examples of the plasticizer include dimethyl phthalate, dibutyl phthalate, diisobutyl phthalate, diheptyl phthalate, dioctyl phthalate, dicyclohexyl phthalate, ditridecyl phthalate, butyl benzyl phthalate, diisodecyl phthalate, diphenyl phthalate, diallyl phthalate, octyl capryl phthalate, and the like. Phthalic acid esters: Triethylene glycol diacetate, tetraethylene glycol diacetate, dimethylglycol phthalate, ethyl phthalyl ethyl glycolate, methyl phthalyl ethyl glycolate, butyl phthalyl butyl glycolate, triethylene glycol dicabrylate, etc. Glycol esters of tricresyl phosphate, triphenyl phosphate, etc. Acid esters; Amides such as 4-toluenesulfonamide, benzenesulfonamide, Nn-butylbenzenesulfonamide, Nn-butylacetamide; diisobutyl adipate, dioctyl adipate, dimethyl sebacate, dibutyl sepacate, dioctyl Aliphatic dibasic acid esters such as sepacate, dioctyl azelate, dibutyl malate; triethyl citrate, tributyl citrate, glycerin triacetyl ester, butyl laurate, 4,5-diepoxycyclohexane-1,2-dicarboxylic acid Examples include glycols such as dioctyl acid, polyethylene glycol, and polypropylene glycol.

  As content of the said plasticizer, 0.1-50 mass% is preferable with respect to all the components of the said photosensitive layer, 0.5-40 mass% is more preferable, 1-30 mass% is especially preferable.

-Colorant-
The colorant is not particularly limited and may be appropriately selected depending on the intended purpose. For example, a known pigment such as red, green, blue, yellow, purple, magenta, cyan, black, Examples include dyes such as Victoria Pure Blue BO (C.I. 42595), Auramine (C.I. 41000), Fat Black HB (C.I. 26150), Monolite Yellow GT ( CI Pigment Yellow 12), Permanent Yellow GR (C.I. Pigment Yellow 17), Permanent Yellow HR (C.I. Pigment Yellow 83), Permanent Carmine FBB (C.I. Pigment)・ Red 146), Hoster Balm Red ESB (CI Pigment Violet 19), Permanent Le -FBH (CI Pigment Red 11), Fastel Pink B Supra (CI Pigment Red 81), Monastral First Blue (CI Pigment Blue 15), Monolite First Black B (CI Pigment Black 1) and carbon black can be mentioned.

  Examples of the colorant suitable for producing a color filter include C.I. I. Pigment red 97, C.I. I. Pigment red 122, C.I. I. Pigment red 149, C.I. I. Pigment red 168, C.I. I. Pigment red 177, C.I. I. Pigment red 180, C.I. I. Pigment red 192, C.I. I. Pigment red 215, C.I. I. Pigment green 7, C.I. I. Pigment green 36, C.I. I. Pigment blue 15: 1, C.I. I. Pigment blue 15: 4, C.I. I. Pigment blue 15: 6, C.I. I. Pigment blue 22, C.I. I. Pigment blue 60, C.I. I. Pigment blue 64, C.I. I. Pigment yellow 139, C.I. I. Pigment yellow 83, C.I. I. Pigment violet 23, and those described in JP-A-2002-162752 (0138) to (0141). There is no restriction | limiting in particular as an average particle diameter of the said coloring agent, Although it can select suitably according to the objective, For example, 5 micrometers or less are preferable and 1 micrometer or less is more preferable. Moreover, when producing a color filter, as said average particle diameter, 0.5 micrometer or less is preferable.

-Dye-
In the photosensitive layer, a dye can be used for the purpose of coloring the photosensitive resin composition for improving the handleability or imparting storage stability.
Examples of the dye include brilliant green (for example, sulfate thereof), eosin, ethyl violet, erythrosine B, methyl green, crystal violet, basic fuchsin, phenolphthalein, 1,3-diphenyltriazine, alizarin red S, thymolphthalein. , Methyl violet 2B, quinaldine red, rose bengal, metanil-yellow, thymol sulfophthalein, xylenol blue, methyl orange, orange IV, diphenyltylocarbazone, 2,7-dichlorofluorescein, paramethyl red, congo red, benzo Purpurin 4B, α-naphthyl-red, Nile blue A, phenacetalin, methyl violet, malachite green, parafuxin, oil blue # 603 (Orien Chemical Co., Ltd.), Rhodamine B, Rhodamine 6G, and the like can be illustrated Victoria Pure Blue BOH, Among these cationic dyes (e.g., Malachite Green oxalate, malachite green sulfates) are preferable. The counter anion of the cationic dye may be a residue of an organic acid or an inorganic acid, for example, a residue such as bromic acid, iodic acid, sulfuric acid, phosphoric acid, oxalic acid, methanesulfonic acid, toluenesulfonic acid ( Anion) and the like.

  As content of the said dye, 0.001-10 mass% is preferable with respect to all the components of the said photosensitive layer, 0.01-5 mass% is more preferable, 0.1-2 mass% is especially preferable.

-Adhesion promoter-
In order to improve the adhesion between the layers or the adhesion between the pattern forming material and the substrate, a known so-called adhesion promoter can be used for each layer.

  Preferable examples of the adhesion promoter include adhesion promoters described in JP-A Nos. 5-11439, 5-341532, and 6-43638. Specifically, benzimidazole, benzoxazole, benzthiazole, 2-mercaptobenzimidazole, 2-mercaptobenzoxazole, 2-mercaptobenzthiazole, 3-morpholinomethyl-1-phenyl-triazole-2-thione, 3-morpholino Methyl-5-phenyl-oxadiazole-2-thione, 5-amino-3-morpholinomethyl-thiadiazole-2-thione, and 2-mercapto-5-methylthio-thiadiazole, triazole, tetrazole, benzotriazole, carboxybenzotriazole Amino group-containing benzotriazole, silane coupling agents, and the like.

  As content of the said adhesion promoter, 0.001 mass%-20 mass% are preferable with respect to all the components of the said photosensitive layer, 0.01-10 mass% is more preferable, 0.1 mass%-5 mass% % Is particularly preferred.

  The photosensitive layer is, for example, J.I. It may contain organic sulfur compounds, peroxides, redox compounds, azo or diazo compounds, photoreducible dyes, organic halogen compounds, etc. as described in Chapter 5 of “Light Sensitive Systems” Good.

  Examples of the organic sulfur compound include di-n-butyl disulfide, dibenzyl disulfide, 2-mercaptobenzthiazole, 2-mercaptobenzoxazole, thiophenol, ethyltrichloromethane sulfenate, and 2-mercaptobenzimidazole. Is mentioned.

  Examples of the peroxide include di-t-butyl peroxide, benzoyl peroxide, and methyl ethyl ketone peroxide.

  The redox compound is a combination of a peroxide and a reducing agent, and examples thereof include ferrous ions and persulfate ions, ferric ions and peroxides.

  Examples of the azo and diazo compounds include α, α'-azobisiributyronitrile, 2-azobis-2-methylbutyronitrile, and diazonium such as 4-aminodiphenylamine.

  Examples of the photoreducible dye include rose bengal, erythrosine, eosin, acriflavine, lipoflavin, and thionine.

--Surfactant--
In order to improve the surface unevenness generated when the pattern forming material of the present invention is produced, a known surfactant can be used in combination.
The surfactant can be appropriately selected from, for example, an anionic surfactant, a cationic surfactant, a nonionic surfactant, an amphoteric surfactant, and a fluorine-containing surfactant.

As content of the said surfactant, 0.001-10 mass% is preferable with respect to solid content of the photosensitive resin composition.
When the content is less than 0.001% by mass, the effect of improving the surface shape may not be obtained, and when it exceeds 10% by mass, the adhesion may be deteriorated.

  There is no restriction | limiting in particular as thickness of the said photosensitive layer, Although it can select suitably according to the objective, For example, 1-100 micrometers is preferable, 2-50 micrometers is more preferable, and 4-30 micrometers is especially preferable.

The photosensitive layer may be a plurality of photosensitive layers having relatively different photosensitivities.
For example, when the photosensitive layer has a first photosensitive layer and a second photosensitive layer in this order on a support, the photosensitivity of the second photosensitive layer is the photosensitivity of the first photosensitive layer. More specifically, when the light having a wavelength of 405 nm is irradiated, the minimum exposure amount at which the pattern of the first photosensitive layer can be formed is smaller than the minimum exposure amount at which the pattern of the second photosensitive layer can be formed. Is also preferably large.
The light irradiated from the support side during exposure proceeds in the order of the support, the first photosensitive layer, and the second photosensitive layer when the support is provided, and the curing of the second photosensitive layer is Before the first photosensitive layer, the process starts with a small amount of light energy. When the amount of light energy is increased after the entire second photosensitive layer is cured, the curing of the first photosensitive layer starts. When the amount of light energy is further increased, the entire first photosensitive layer is cured.

Amount of light energy hardening begins the second photosensitive layer is preferably in the range of 0.05~10mJ / cm ^2, more preferably in the range of 0.1~5mJ / cm ^2, 0.15 It is particularly preferably in the range of ˜2.5 mJ / cm ² .
Further, the second photosensitive layer of light energy required for curing the is preferably in the range of 0.1~20mJ / cm ^2, more in the range of 0.2~15mJ / cm ² A range of 0.4 to 10 mJ / cm ² is particularly preferable.

The ratio (A / B) between the amount of light energy A necessary for curing the second photosensitive layer and the amount of light energy B necessary for curing the first photosensitive layer is 0.005 to 0.00. It is preferably in the range of 5, more preferably in the range of 0.01 to 0.4, and particularly preferably in the range of 0.02 to 0.35.
The ratio (C / A) between the amount of light energy A required to cure the second photosensitive layer and the amount of light energy C required until the first photosensitive layer begins to be cured is in the range of 1-10. Preferably, it is preferably in the range of 1.1 to 9, more preferably in the range of 1.3 to 8. The light energy C is preferably in the range of 0.1~200mJ / cm ^2, more preferably in the range of 1 to 100 mJ / cm ^2, in the range of 2~50mJ / cm ² Particularly preferred.

When the photosensitive layer is a plurality of photosensitive layers having relatively different photosensitivities, it is preferable to have the barrier layer between the photosensitive layers.
For example, when the photosensitive layer is composed of a first photosensitive layer and a second photosensitive layer, the first photosensitive layer, the barrier layer, and the second photosensitive layer are provided on the support in this order. Is preferred.

<Cushion layer>
The pattern forming material may be provided with a cushion layer between the support and the photosensitive layer.
There is no restriction | limiting in particular as said cushion layer, Although it can select suitably according to the objective, For example, the thing containing a thermoplastic resin is preferable. Further, the cushion layer may be swellable or soluble in an alkaline liquid, or may be insoluble.

-Thermoplastic resin-
When the cushion layer is swellable or soluble in an alkaline liquid, the thermoplastic resin mainly contains an alkali-soluble thermoplastic polymer, and optionally contains other components. Also good.

  The acid value (mgKOH / g) of the thermoplastic polymer is not particularly limited and may be appropriately selected depending on the intended purpose, but is preferably 50 to 300, more preferably 60 to 270, and particularly preferably 70 to 250. . When the acid value is in the above range, the developability of the cushion layer can be ensured. When the acid value is less than 50, development failure may occur. When the acid value exceeds 300, the cushion layer may become too hard, and the unevenness followability and laminate property may be deteriorated.

The weight average molecular weight of the thermoplastic polymer is not particularly limited and may be appropriately selected depending on the intended purpose. It is preferably 1000 to 300000, more preferably 3000 to 200000, and particularly preferably 5000 to 150,000. When the weight average molecular weight is in the above range, the developability of the cushion layer can be ensured, and the viscosity η ₁ can be easily adjusted. Further, the effect can be further obtained by the combination with the acid value range. If the weight average molecular weight is less than 1000, the membrane may become brittle or the cushion layer may ooze out during lamination. When it exceeds 300,000, the cushion layer becomes too hard, and uneven followability and laminating properties may be deteriorated.

  The content of the thermoplastic polymer in the cushion layer is not particularly limited and can be appropriately selected according to the purpose. For example, the content is 35% by mass or more based on the total solid content of the cushion layer. It is preferably contained, more preferably 55% by mass or more.

  The softening point (Vicat) of the thermoplastic polymer is not particularly limited and may be appropriately selected depending on the intended purpose. For example, the softening point of the cushion layer may be substantially less than 80 ° C. Those having a softening point of 80 ° C. or lower are preferred. Examples of alkali-soluble thermoplastic polymers having a softening point of 80 ° C. or less include saponified products of ethylene and acrylate copolymers, saponified products of styrene and (meth) acrylate copolymers, vinyltoluene and (meta ) Saponified products of acrylic acid ester copolymers, poly (meth) acrylic acid esters, saponified products such as (meth) acrylic acid ester copolymers such as butyl (meth) acrylate and vinyl acetate, (meth) acrylic acid esters And a copolymer of (meth) acrylic acid, a copolymer of styrene, (meth) acrylic acid ester and (meth) acrylic acid, a copolymer of styrene and (meth) acrylic acid, and the like.

  As the thermoplastic resin having a softening point of 80 ° C. or less, in addition to the above-mentioned thermoplastic resin, “Plastic Performance Handbook” (edited by the Japan Plastics Industry Federation, All Japan Plastics Molding Industry Federation, published by the Industrial Research Council, October 1968) Among those organic polymers having a softening point of about 80 ° C. or less, which are soluble in an alkaline solution. In addition, even in an organic polymer substance having a softening point of 80 ° C. or higher, various plasticizers compatible with the organic polymer substance are added to the organic polymer substance so that a substantial softening point is 80 ° C. or lower. It is also possible to lower it.

  The plasticizer is not particularly limited and may be appropriately selected depending on the intended purpose.For example, polypropylene glycol, polyethylene glycol, dioctyl phthalate, diheptyl phthalate, dibutyl phthalate, tricresyl phosphate, cresyl diphenyl Examples thereof include alcohols and esters such as phosphate and biphenyldiphenyl phosphate, and amides such as toluenesulfonamide.

  In addition, when the cushion layer is swellable or soluble in an alkaline liquid, the interlayer adhesive force of the pattern forming material is not particularly limited and can be appropriately selected according to the purpose. Of the interlayer adhesive strength of each layer, it is preferable that the interlayer adhesive strength between the support and the cushion layer is the smallest. With such an interlayer adhesive strength, only the support is peeled off from the laminate, the photosensitive layer is exposed through the cushion layer, and then the photosensitive layer is developed using an alkaline developer. be able to. Further, after exposing the photosensitive layer while leaving the support, only the support is peeled off from the laminate, and the photosensitive layer can be developed using an alkaline developer.

  The method for adjusting the interlayer adhesion is not particularly limited and can be appropriately selected according to the purpose. For example, a known polymer, supercooling substance, adhesion improver, surfactant in the thermoplastic resin, The method of adding a mold release agent etc. is mentioned.

When the cushion layer is insoluble in an alkaline liquid, examples of the thermoplastic resin include a copolymer whose main component is ethylene as an essential copolymer component.
The copolymer having ethylene as an essential copolymer component is not particularly limited and may be appropriately selected depending on the intended purpose. Examples thereof include ethylene-vinyl acetate copolymer (EVA) and ethylene-ethyl acrylate. A copolymer (EEA) etc. are mentioned.

  When the cushion layer is insoluble in the alkaline liquid, the interlayer adhesion of the pattern forming material is not particularly limited and can be appropriately selected depending on the purpose. Of the adhesive strength, it is preferable that the adhesive force between the photosensitive layer and the cushion layer is the smallest. By setting such an interlayer adhesive strength, the support and the cushion layer are peeled from the laminate, and the photosensitive layer is exposed, and then the photosensitive layer can be developed using an alkaline developer. Further, after exposing the photosensitive layer while leaving the support, the support and the cushion layer can be peeled from the laminate, and the photosensitive layer can be developed using an alkaline developer.

  The method for adjusting the interlayer adhesion is not particularly limited and can be appropriately selected depending on the purpose. For example, various polymers, supercooling substances, adhesion improvers, surfactants in the thermoplastic resin, Examples thereof include a method of adding a release agent and the like, and a method of adjusting an ethylene copolymerization ratio described below.

There is no restriction | limiting in particular as an ethylene copolymerization ratio in the copolymer which uses the said ethylene as an essential copolymerization component, Although it can select suitably according to the objective, For example, 60-90 mass% is preferable, 60- 80 mass% is more preferable, and 65-80 mass% is especially preferable.
When the ethylene copolymerization ratio is less than 60% by mass, the interlayer adhesive force between the cushion layer and the photosensitive layer increases, and it becomes difficult to peel off at the interface between the cushion layer and the photosensitive layer. When the amount exceeds 90% by mass, the interlayer adhesive force between the cushion layer and the photosensitive layer becomes too small, so that the cushion layer and the photosensitive layer are very easily peeled off. It may be difficult to manufacture the pattern forming material.

  When the cushion layer is insoluble in an alkaline solution and a barrier layer is present between the cushion layer and the photosensitive layer, the photosensitive layer and the barrier are included in the interlayer adhesion of each layer. It is preferable that the interlayer adhesive strength with the layer is the smallest. By setting such an interlayer adhesive force, the support, the cushion layer, and the barrier layer are peeled from the laminate, the photosensitive layer is exposed, and then the photosensitive layer is used with an alkaline developer. Can be developed. In addition, after exposing the photosensitive layer through the cushion layer while leaving the support without peeling, the support, the cushion layer, and the barrier layer are peeled from the laminate, The photosensitive layer can also be developed using a developer.

  The method for adjusting the interlayer adhesive force is not particularly limited and may be appropriately selected depending on the intended purpose.For example, a method in which a release agent is contained in the photosensitive layer, the cushion layer and the barrier layer A method for surface-treating an adhesive surface, a method for surface-treating an adhesive surface between the support and the cushion layer, and a method for adjusting the content of at least one selected from components contained in at least one of the layers And the method of containing thru | or apply | coating etc. which contain the component which improves an adhesive force is mentioned, These methods may be used individually by 1 type, and may use 2 or more types together.

  There is no restriction | limiting in particular as said mold release agent, It can select suitably from well-known mold release agents, For example, a silicone compound, the compound which has a fluorinated alkyl group, etc. are mentioned.

  Examples of the silicone compound include Daicel UCB, Ebeacryl 1360, 350, Toshiba Silicone dimethyl silicone oil TSF400, methylphenylsilicone oil TSF4300, silicone polyether copolymers TSF4445, TSF4446, TSF4460, TSF4452, and the like. It is done.

  Examples of the compound having a fluorinated alkyl group include a fluorine-based surfactant (for example, perfluoroalkyl group / hydrophilic group-containing oligomer F-171, perfluoroalkyl group / lipophilic group manufactured by Dainippon Ink & Chemicals, Inc. -Containing oligomer F-173, perfluoroalkyl group / hydrophilic group / lipophilic group-containing oligomer F-177, perfluoroalkyl group / lipophilic group-containing urethane F-183, F-184, fluorine-based graft polymer, etc.), fluorine System graft polymer (for example, Aron GF-300, GF-150, etc., manufactured by Toagosei Co., Ltd.).

  Examples of the surface treatment include plasma treatment, electron beam treatment, glow discharge treatment, corona discharge treatment, and ultraviolet irradiation treatment.

  As a method for adjusting the content, for example, when the cushion layer contains a copolymer essential for the ethylene, a method for setting the ethylene copolymerization ratio in the copolymer to less than 60% by mass is mentioned. It is done.

  Examples of the component for improving the adhesive strength include phenolic substances (for example, cresol novolac resin, phenol resin, etc.), polyvinylidene chloride resin, styrene butadiene rubber, gelatin, polyvinyl alcohol, and celluloses. These may be included in at least one of the support, the cushion layer, and the barrier layer as necessary, and the contact surface between the support and the cushion layer, the cushion layer and the barrier layer. You may apply | coat with respect to a contact surface.

Examples of the crosslinking agent include borax, boric acid, borates (for example, orthoborate, InBO ₃ , ScBO ₃ , YBO ₃ , LaBO ₃ , Mg ₃ (BO ₃ ) ₂ , Co ₃ (BO ₃ ) ₂ , two Borate (eg, Mg ₂ B ₂ O ₅ , Co ₂ B ₂ O ₅ ), metaborate (eg, LiBO ₂ , Ca (BO ₂ ) ₂ , NaBO ₂ , KBO ₂ ), tetraborate (eg, Na ₂ B ₄ O ₇ · 10H ₂ O) and boron compounds such as pentaborate (for example, KB ₅ O ₈ · 4H ₂ O, Ca ₂ B ₆ O ₁₁ · 7H ₂ O, CsB ₅ O ₅ ). Among these, borax, boric acid, and borate are preferable, and boric acid is more preferable in that a crosslinking reaction can be rapidly caused, and aldehydes such as formaldehyde, glyoxal, and glutaraldehyde are also preferable. Compounds; ketone compounds such as diacetyl and cyclopentanedione; bis (2-chloroethylurea) -2-hydroxy-4,6-dichloro-1,3,5-triazine, 2,4-dichloro-6-S— Active halogen compounds such as triazine sodium salt; divinylsulfonic acid, 1,3-vinylsulfonyl-2-propanol, N, N′-ethylenebis (vinylsulfonylacetamide), 1,3,5-triacryloyl-hexahydro -Active vinyl compounds such as S-triazine; N-methylol compounds such as dimethylolurea and methyloldimethylhydantoin; Melamine resins (for example, methylolmelamine, alkylated methylolmelamine); Epoxy resins; 1,6-hexamethylene diisocyanate, etc. Isocyanate compounds; US Patent Specification No. Aziridine compounds described in US Pat. Nos. 017280 and 2983611; Carboximide compounds described in US Pat. No. 3,100,704; Epoxy compounds such as glycerol triglycidyl ether; 1,6-hexamethylene-N, N ′ -Ethyleneimino compounds such as bisethyleneurea; Halogenated carboxaldehyde compounds such as mucochloric acid and mucophenoxycyclolic acid; Dioxane compounds such as 2,3-dihydroxydioxane and 2,3-dihydroxy-1,4-dioxane Contains metal-containing compounds such as titanium lactate, aluminum sulfate, chromium alum, potash alum, zirconyl acetate and chromium acetate, polyamine compounds such as tetraethylenepentamine, hydrazide compounds such as adipic acid dihydrazide, and two or more oxazoline groups Low molecular weight Polymer, and the like. These may be used alone or in combination of two or more.

  Examples of the silane coupling agent include N-2 (aminoethyl) 3-aminopropylmethyldimethoxysilane, N-2 (aminoethyl) 3-aminopropyltrimethoxysilane, and N-2 (aminoethyl) 3-amino. Propyltriethoxysilane, 3-aminopropyltrimethoxysilane, 3-aminopropyltriethoxysilane, 3-triethoxysilyl-N- (1,3-dimethyl-butylidene) propylamine, N-phenyl-3-aminopropyltrime Toxylsilane, N- (vinylbenzyl) -2-aminoethyl-3-aminopropyltrimethoxysilane and the like can be mentioned. A silane coupling agent manufactured by Shin-Etsu Chemical Co., Ltd. can also be suitably used.

  The layer containing at least one of the crosslinking agent and the silane coupling agent is not particularly limited and may be appropriately selected depending on the intended purpose. For example, the cushion layer and the barrier layer are preferable, and the cushion A layer alone is more preferred.

  In addition to the method described above, at least one selected from the components contained in the cushion layer, at least one selected from the components contained in the cushion layer, and at least one selected from the components contained in the barrier layer. A method of making one kind of hydrophilic substance and at least one kind selected from the ingredients contained in the photosensitive layer a hydrophobic substance, at least one kind of ingredients contained in the support, and the cushion layer At least one selected from the components included and at least one selected from the components included in the barrier layer are made hydrophobic, and at least one selected from the components included in the photosensitive layer is hydrophilic. The method of making it a sex substance is mentioned.

When the component is polyvinyl alcohol, a polyvinyl alcohol having a saponification degree of 85% or less or modified polyvinyl alcohol can be appropriately selected and used. Moreover, you may use the said polyvinyl alcohol together with the said crosslinking agent, the said silane coupling agent, etc.
Examples of the modified polyvinyl alcohol include anion-modified polyvinyl alcohol (for example, carboxy-modified polyvinyl alcohol), cation-modified polyvinyl alcohol, acetoacetylated polyvinyl alcohol, silanol-modified polyvinyl alcohol, and hydrophobic group-modified polyvinyl alcohol (for example, terminal alkyl polyvinyl). Alcohol), hydrophilic group-modified polyvinyl alcohol (for example, ethylene oxide-modified polyvinyl alcohol), terminal thiol polyvinyl alcohol, EXEVAL (manufactured by Kuraray Co., Ltd.), and the like.

  The cushion layer is prepared by dissolving the thermoplastic resin and, if necessary, other components in an organic solvent to prepare a coating solution (a coating solution for a thermoplastic resin layer), and coating the temporary support by a known coating method. Etc. can be formed. Examples of the organic solvent include methyl ethyl ketone and 1-methoxy-2-propanol.

<Barrier layer>
The pattern forming material may be provided with a barrier layer between the photosensitive layer and the cushion layer when the cushion layer is provided between the support and the photosensitive layer.
The barrier layer is not particularly limited as long as the movement of the substance can be suppressed, and can be appropriately selected according to the purpose. The barrier layer may be water-soluble or water-dispersible, and is soluble in an alkaline liquid. It may be present or insoluble. Note that the suppression of the movement of the substance means that the increase or decrease in the content of the target substance in the layer adjacent to the barrier layer is suppressed as compared to the case where the barrier layer is not provided. To do.

  There is no restriction | limiting in particular as said substance, Although it can select suitably according to the objective, For example, the substance contained in at least any one of oxygen, water, the said photosensitive layer, and a cushion layer is mentioned.

  When the barrier layer is water-soluble or water-dispersible, it preferably contains a water-soluble or water-dispersible resin, and when it is soluble in an alkaline liquid, it is soluble in an alkaline liquid. It is preferable that resin is included. In addition, as said water solubility degree, what melt | dissolves 0.1 mass% or more with respect to 25 degreeC water, for example, and what melt | dissolves 1 mass% or more is more preferable.

  The resin is not particularly limited and may be appropriately selected depending on the intended purpose. Examples thereof include various alcohol-soluble resins, water-soluble resins, alcohol-dispersible resins, water-dispersible resins, emulsifiable resins, and alkaline liquids. Examples include vinyl polymers (for example, polyvinyl alcohol (including modified polyvinyl alcohols), polyvinylpyrrolidone, etc.), the above-mentioned vinyl copolymers, water-soluble polyamides, and gelatins. , Cellulose, and derivatives thereof. In addition, the thermoplastic resin described in Japanese Patent No. 2794242, the compound used in the intermediate layer, the binder, and the like can also be used. These may be used alone or in combination of two or more.

When the barrier layer is insoluble in the alkaline liquid, it is preferable to include a resin insoluble in the alkaline liquid.
Examples of the resin insoluble in the alkaline liquid include a copolymer whose main component is ethylene as an essential copolymer component.
The copolymer having ethylene as an essential copolymer component is not particularly limited and may be appropriately selected depending on the intended purpose. Examples thereof include ethylene-vinyl acetate copolymer (EVA) and ethylene-ethyl acrylate. A copolymer (EEA) etc. are mentioned.

There is no restriction | limiting in particular as thickness of the said barrier layer, Although it can select suitably according to the objective, For example, less than 10 micrometers is preferable, 0.1-6 micrometers is more preferable, and 1-5 micrometers is especially preferable.
When the thickness is 10 μm or more, light scattering occurs in the barrier layer during exposure, and at least one of resolution and adhesion may be deteriorated.

<Support>
There is no restriction | limiting in particular as said support body, Although it can select suitably according to the objective, The thing with favorable light transmittance is preferable, and also it is more preferable that the smoothness of surface is also favorable.

  The support is preferably made of synthetic resin and transparent, for example, polyethylene terephthalate, polyethylene naphthalate, polypropylene, polyethylene, cellulose triacetate, cellulose diacetate, poly (meth) acrylic acid alkyl ester, poly ( (Meth) acrylic acid ester copolymer, polyvinyl chloride, polyvinyl alcohol, polycarbonate, polystyrene, cellophane, polyvinylidene chloride copolymer, polyamide, polyimide, vinyl chloride / vinyl acetate copolymer, polytetrafluoroethylene, polytrifluoro Various plastic films, such as ethylene, a cellulose film, and a nylon film, are mentioned, Among these, polyethylene terephthalate is particularly preferable. These may be used alone or in combination of two or more.

  There is no restriction | limiting in particular as thickness of the said support body, Although it can select suitably according to the objective, For example, 2-150 micrometers is preferable, 5-100 micrometers is more preferable, and 8-50 micrometers is especially preferable.

  There is no restriction | limiting in particular as a shape of the said support body, Although it can select suitably according to the objective, A long shape is preferable. There is no restriction | limiting in particular as the length of the said elongate support body, For example, the thing of length 10m-20000m is mentioned.

<Protective film>
The pattern forming material may form a protective film on the photosensitive layer.
Examples of the protective film include those used for the support, paper, paper laminated with polyethylene, polypropylene, and the like. Among these, polyethylene film and polypropylene film are preferable.
There is no restriction | limiting in particular as thickness of the said protective film, Although it can select suitably according to the objective, For example, 5-100 micrometers is preferable, 8-50 micrometers is more preferable, 10-30 micrometers is especially preferable.
When the protective film is used, it is preferable that the interlayer adhesive strength between the protective film and the photosensitive layer is the smallest among the interlayer adhesive strengths of the other layers.
Examples of the combination of the support and the protective film (support / protective film) include polyethylene terephthalate / polypropylene, polyethylene terephthalate / polyethylene, polyvinyl chloride / cellophane, polyimide / polypropylene, polyethylene terephthalate / polyethylene terephthalate, and the like. . Moreover, the relationship of the above adhesive forces can be satisfy | filled by surface-treating at least any one of a support body and a protective film. The surface treatment of the support may be performed in order to increase the adhesive force with the photosensitive layer. For example, coating of a primer layer, corona discharge treatment, flame treatment, ultraviolet irradiation treatment, high frequency irradiation treatment, glow treatment Examples thereof include discharge irradiation treatment, active plasma irradiation treatment, and laser beam irradiation treatment.

Moreover, as a static friction coefficient of the said support body and the said protective film, 0.3-1.4 are preferable and 0.5-1.2 are more preferable.
When the coefficient of static friction is less than 0.3, slipping is excessive, so that winding deviation may occur when the roll is formed, and when it exceeds 1.4, it is difficult to wind into a good roll. Sometimes.

  It is preferable that the pattern forming material is wound around a cylindrical core, wound into a long roll, and stored. There is no restriction | limiting in particular as length of the said elongate pattern formation material, For example, it can select suitably from the range of 10m-20,000m. Further, slitting may be performed so that the user can easily use, and a long body in the range of 100 m to 1,000 m may be formed into a roll. In this case, it is preferable that the support is wound up so as to be the outermost side. The roll-shaped pattern forming material may be slit into a sheet shape. From the viewpoint of protecting the end face and preventing edge fusion during storage, it is preferable to install a separator (especially moisture-proof and desiccant-containing) on the end face, and use a low moisture-permeable material for packaging. Things are preferable.

  The protective film may be surface-treated in order to adjust the adhesion between the protective film and the photosensitive layer. In the surface treatment, for example, an undercoat layer made of a polymer such as polyorganosiloxane, fluorinated polyolefin, polyfluoroethylene, or polyvinyl alcohol is formed on the surface of the protective film. The undercoat layer can be formed by applying the polymer coating solution to the surface of the protective film and then drying at 30 to 150 ° C. (especially 50 to 120 ° C.) for 1 to 30 minutes. Moreover, you may have layers, such as a peeling layer, an adhesive layer, a light absorption layer, a surface protective layer, in addition to the said photosensitive layer, the said support body, and the said protective film. Each of the layers may have one layer or two or more layers.

[Manufacture of pattern forming materials]
The pattern forming material can be manufactured, for example, as follows.
First, materials contained in the photosensitive layer, cushion layer, and barrier layer are dissolved, emulsified or dispersed in water or a solvent to prepare a photosensitive resin composition solution, a cushion layer coating solution, and a barrier layer coating solution. To do.

  There is no restriction | limiting in particular as a solvent of the said photosensitive resin composition solution, the coating liquid for cushion layers, or the coating liquid for barrier layers, According to the objective, it can select suitably, For example, methanol, ethanol, n-propanol , Isopropanol, n-butanol, sec-butanol, n-hexanol, etc .; ketones such as acetone, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone, diisobutyl ketone; ethyl acetate, butyl acetate, acetic acid-n-amyl sulfate, methyl sulfate , Esters such as ethyl propionate, dimethyl phthalate, ethyl benzoate, and methoxypropyl acetate; aromatic hydrocarbons such as toluene, xylene, benzene, ethylbenzene; carbon tetrachloride, trichloroethylene, chloroform, 1,1,1 -Birds Halogenated hydrocarbons such as loroethane, methylene chloride, monochlorobenzene; ethers such as tetrahydrofuran, diethyl ether, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, 1-methoxy-2-propanol; dimethylformamide, dimethylacetamide, dimethyl Examples include sulfooxide and sulfolane. These may be used alone or in combination of two or more. Moreover, you may add a well-known surfactant.

  Next, the cushion layer coating solution is applied onto the support and dried to form a cushion layer, and the barrier layer coating solution is applied onto the cushion layer and dried to form a barrier layer. The photosensitive resin composition solution is applied onto the barrier layer and dried to form a photosensitive layer, whereby a pattern forming material can be produced.

The method for coating the photosensitive resin composition solution, the cushion layer coating solution, or the barrier layer coating solution is not particularly limited and may be appropriately selected depending on the intended purpose. Various coating methods such as a coating method, a spin coating method, a slit coating method, an extrusion coating method, a curtain coating method, a die coating method, a gravure coating method, a wire bar coating method, and a knife coating method can be mentioned.
The drying conditions vary depending on each component, the type of solvent, the use ratio, and the like, but are usually about 60 to 110 ° C. for about 30 seconds to 15 minutes.

The pattern forming material of the present invention preferably has the cushion layer and the photosensitive resin layer in this order on the support.
Since the pattern forming material of the present invention uses a polymacromonomer in at least one of the cushion layer and the photosensitive layer, the melt viscosity of the cushion layer has a sharp melt property that changes rapidly due to a temperature change. Excellent transferability and suppression of edge fusion phenomenon are compatible.

  The pattern forming material of the present invention is excellent in uneven followability, can suppress a decrease in sensitivity of the photosensitive layer, can be laminated at a low temperature, and does not require preheating of the substrate, so that the substrate can be laminated in a short time. Since the edge fusion phenomenon can be suppressed, it can be suitably used for the production of a printed wiring board, and can be particularly suitably used for the pattern forming method and pattern forming apparatus of the present invention.

(Pattern forming apparatus and pattern forming method)
The pattern forming apparatus of the present invention includes the pattern forming material of the present invention, and has at least light irradiation means and light modulation means.
The pattern forming method of the present invention includes at least an exposure step and includes other appropriately selected steps.
In addition, the said pattern formation apparatus of this invention is clarified through description of the said pattern formation method of this invention.

[Exposure process]
The said exposure process is a process of exposing with respect to the photosensitive layer in the pattern formation material of this invention. The pattern forming material of the present invention is as described above.

  The object of exposure is not particularly limited as long as it is a photosensitive layer in the pattern forming material, and can be appropriately selected according to the purpose. For example, a laminate formed by forming the pattern forming material on a substrate It is preferably performed on the body.

  The substrate is not particularly limited, and can be appropriately selected from known materials having high surface smoothness to those having an uneven surface. A plate-like substrate (substrate) is preferable, and Specifically, a known printed wiring board forming substrate (for example, a copper-clad laminate), a glass plate (for example, a soda glass plate), a synthetic resin film, paper, a metal plate, and the like can be given.

As the printed wiring board forming substrate, for example, a glass epoxy substrate, an epoxy-impregnated aramid nonwoven fabric, or a surface of an insulating layer such as polyimide is preferably provided with a copper foil layer as a plating foil or a sputtered foil. When the sputter foil is provided, another metal foil (Ni, Cr, etc.) may be provided as a base layer for the purpose of improving the adhesion between the copper foil and the insulating layer.
The surface of the substrate may be formed with unevenness of about 0.5 to 2 μm by a method such as chemical polishing for the purpose of improving adhesion with the pattern forming material to be laminated.
There is no restriction | limiting in particular as a layer structure in the said laminated body, Although it can select suitably according to the objective, For example, the layer structure which has the said base | substrate, the said photosensitive layer, and the said support body in this order is preferable.

The method for forming the laminate is not particularly limited and may be appropriately selected depending on the purpose. However, the pattern forming material may be laminated on the substrate while performing at least one of heating and pressing. preferable.
There is no restriction | limiting in particular as said heating temperature, Although it can select suitably according to the objective, For example, 15-180 degreeC is preferable and 60-140 degreeC is more preferable.
There is no restriction | limiting in particular as a pressure of the said pressurization, Although it can select suitably according to the objective, For example, 0.1-1.0 MPa is preferable and 0.2-0.8 MPa is more preferable.

  There is no restriction | limiting in particular as an apparatus which performs at least any one of the said heating and pressurization, According to the objective, it can select suitably, For example, a laminator, a vacuum laminator, etc. are mentioned suitably.

  There is no restriction | limiting in particular as an apparatus which performs at least any one of the said heating and pressurization, According to the objective, it can select suitably, For example, a laminator (For example, Taisei Laminator company make, VP-II) etc. are suitable. Can be mentioned.

  There is no restriction | limiting in particular as said exposure, According to the objective, it can select suitably, Digital exposure, analog exposure, etc. are mentioned, Among these, digital exposure is preferable.

  The digital exposure is not particularly limited and can be appropriately selected depending on the purpose.For example, a control signal is generated based on pattern formation information to be formed, and light modulated in accordance with the control signal is generated. It is preferable to use.

  The digital exposure means is not particularly limited and may be appropriately selected depending on the purpose. For example, the light irradiation means for irradiating light, and the light irradiation means for irradiating based on the pattern information to be formed. Examples thereof include light modulation means for modulating light.

<Light modulation means>
The light modulation means is not particularly limited as long as it can modulate light, and can be appropriately selected according to the purpose. For example, it preferably has n pixel portions.
The light modulation means having the n picture elements is not particularly limited and can be appropriately selected according to the purpose. For example, a spatial light modulation element is preferable.

  Examples of the spatial light modulator include a digital micromirror device (DMD), a MEMS (Micro Electro Mechanical Systems) type spatial light modulator (SLM), and modulates transmitted light by an electro-optic effect. An optical element (PLZT element), a liquid crystal optical shutter (FLC), etc. are mentioned, Among these, DMD is mentioned suitably.

Moreover, it is preferable that the said light modulation means has a pattern signal generation means which produces | generates a control signal based on the pattern information to form. In this case, the light modulation unit modulates light according to the control signal generated by the pattern signal generation unit.
There is no restriction | limiting in particular as said control signal, According to the objective, it can select suitably, For example, a digital signal is mentioned suitably.

Hereinafter, an example of the light modulation means will be described with reference to the drawings.
As shown in FIG. 1, in the DMD 50, a large number (eg, 1024 × 768) of micromirrors (micromirrors) 62, each constituting a pixel (pixel), are arranged in a lattice pattern on an SRAM cell (memory cell) 60. It is a mirror device arranged. In each pixel, a micromirror 62 supported by a support column is provided at the top, and a material having high reflectance such as aluminum is deposited on the surface of the micromirror 62. The reflectance of the micromirror 62 is 90% or more, and the arrangement pitch is 13.7 μm as an example in both the vertical and horizontal directions. A silicon gate CMOS SRAM cell 60 manufactured in a normal semiconductor memory manufacturing line is disposed directly below the micromirror 62 via a support including a hinge and a yoke, and the entire structure is monolithic. ing.

  When a digital signal is written in the SRAM cell 60 of the DMD 50, the micromirror 62 supported by the support is tilted in a range of ± α degrees (for example, ± 12 degrees) with respect to the substrate side on which the DMD 50 is disposed with the diagonal line as the center. It is done. 2A shows a state where the micromirror 62 is tilted to + α degrees when the micromirror 62 is in the on state, and FIG. 2B shows a state where the micromirror 62 is tilted to −α degrees when the micromirror 62 is in the off state. Therefore, by controlling the inclination of the micromirror 62 in each pixel of the DMD 50 according to the pattern information as shown in FIG. The

  FIG. 1 shows an example of a state in which a part of the DMD 50 is enlarged and the micromirror 62 is controlled to + α degrees or −α degrees. The on / off control of each micromirror 62 is performed by a controller 302 (see FIG. 12) connected to the DMD 50. Further, a light absorber (not shown) is arranged in the direction in which the laser beam B reflected by the off-state micromirror 62 travels.

  Further, it is preferable that the DMD 50 is arranged with a slight inclination so that the short side forms a predetermined angle θ (for example, 0.1 ° to 5 °) with the sub-scanning direction. 3A shows the scanning trajectory of the reflected light image (exposure beam) 53 by each micromirror when the DMD 50 is not tilted, and FIG. 3B shows the scanning trajectory of the exposure beam 53 when the DMD 50 is tilted. Show.

In the DMD 50, a number of micromirror arrays in which a number of micromirrors are arranged in the longitudinal direction (for example, 1024) are arranged in a short direction (for example, 756 pairs). as shown, by tilting the DMD 50, the pitch P ₂ of the scanning locus of the exposure beams 53 from each micromirror (scan line), it becomes narrower than the pitch P ₁ of the scanning line in the case of not tilting the DMD 50, significant resolution Can be improved. On the other hand, the inclination angle of the DMD 50 is small, the scanning width _{W 2} in the case of tilting the DMD 50, which is substantially equal to the scanning width _{W 1} when not inclined DMD 50.

Next, a method for increasing the modulation speed in the optical modulation means (hereinafter referred to as “high-speed modulation”) will be described.
It is preferable that the light modulation unit is capable of controlling any less than n pixel elements arranged continuously from the n pixel elements according to pattern information. There is a limit to the data processing speed of the light modulation means, and the modulation speed per line is determined in proportion to the number of pixels to be used. By using, the modulation speed per line is increased.

Hereinafter, the high-speed modulation will be further described with reference to the drawings.
When the laser light B is irradiated from the fiber array light source 66 to the DMD 50, the laser light reflected when the micromirror of the DMD 50 is in an on state is imaged on the pattern forming material 150 by the lens systems 54 and 58. In this manner, the laser light emitted from the fiber array light source 66 is turned on / off for each pixel, and the pattern forming material 150 is exposed in the number of pixel units (exposure area 168) substantially equal to the number of used pixel elements of the DMD 50. . Further, when the pattern forming material 150 is moved at a constant speed together with the stage 152, the pattern forming material 150 is sub-scanned in the direction opposite to the stage moving direction by the scanner 162, and a strip-shaped exposed region 170 is provided for each exposure head 166. Is formed.

  In this example, as shown in FIGS. 4A and 4B, in the DMD 50, 768 sets of micromirror arrays in which 1024 micromirrors are arranged in the main scanning direction are arranged in the subscanning direction. In this example, the controller 302 (see FIG. 12) controls so that only a part of the micromirror rows (eg, 1024 × 256 rows) are driven.

  In this case, a micromirror array arranged at the center of the DMD 50 as shown in FIG. 4 (A) may be used, and a micromirror arranged at the end of the DMD 50 as shown in FIG. 4 (B). A column may be used. In addition, when a defect occurs in some of the micromirrors, the micromirror array to be used may be appropriately changed depending on the situation, such as using a micromirror array in which no defect has occurred.

  Since the data processing speed of the DMD 50 is limited and the modulation speed per line is determined in proportion to the number of pixels used, the modulation speed per line can be increased by using only a part of the micromirror array. Get faster. On the other hand, in the case of an exposure method in which the exposure head is continuously moved relative to the exposure surface, it is not necessary to use all the pixels in the sub-scanning direction.

  When the sub-scan of the pattern forming material 150 by the scanner 162 is finished and the rear end of the pattern forming material 150 is detected by the sensor 164, the stage 152 is moved upstream of the gate 160 along the guide 158 by the stage driving device 304. It returns to the origin on the side and is moved again along the guide 158 from the upstream side to the downstream side of the gate 160 at a constant speed.

  For example, when only 384 sets of 768 sets of micromirror arrays are used, modulation can be performed twice as fast per line as compared with the case of using all 768 sets. Also, when only 256 pairs are used in the 768 sets of micromirror arrays, modulation can be performed three times faster per line than when all 768 sets are used.

  As described above, according to the pattern forming method of the present invention, the micromirror array in which 1,024 micromirrors are arranged in the main scanning direction includes the DMD in which 768 sets are arranged in the subscanning direction. By controlling so that only a part of the micromirror rows are driven by the controller, the modulation rate per line becomes faster than when all the micromirror rows are driven.

  In addition, an example in which the DMD micromirror is partially driven has been described, but the length of the direction corresponding to the predetermined direction is reflected on the substrate longer than the length of the direction intersecting the predetermined direction according to the control signal. Even if a long and narrow DMD in which a large number of micromirrors capable of changing the surface angle are arranged in a two-dimensional manner is used, the number of micromirrors for controlling the angle of the reflecting surface is reduced. Can do.

  The exposure method is preferably performed while relatively moving the exposure light and the photosensitive layer, and in this case, it is preferable to use the high-speed modulation together. Thereby, high-speed exposure can be performed in a short time.

  In addition, as shown in FIG. 5, the entire surface of the pattern forming material 150 may be exposed by a single scan in the X direction by the scanner 162, and as shown in FIGS. 6A and 6B, the scanner 162. After scanning the pattern forming material 150 in the X direction, the scanner 162 is moved one step in the Y direction, and scanning is performed in the X direction. Thus, the pattern forming material 150 is scanned a plurality of times. Alternatively, the entire surface may be exposed. In this example, the scanner 162 includes 18 exposure heads 166. Note that the exposure head includes at least the light irradiation unit and the light modulation unit.

  The exposure is performed on a partial area of the photosensitive layer to cure the partial area, and uncured areas other than the cured partial area are removed in a development step described later. A pattern is formed.

Next, an example of a pattern forming apparatus including the light modulation means will be described with reference to the drawings.
As shown in FIG. 7, the pattern forming apparatus including the light modulation means includes a flat plate stage 152 that holds a sheet-like pattern forming material 150 by adsorbing to the surface.
Two guides 158 extending along the stage moving direction are installed on the upper surface of the thick plate-shaped installation table 156 supported by the four legs 154. The stage 152 is arranged so that the longitudinal direction thereof faces the stage moving direction, and is supported by a guide 158 so as to be reciprocally movable. The pattern forming apparatus has a drive device (not shown) for driving the stage 152 along the guide 158.

  A U-shaped gate 160 is provided at the center of the installation table 156 so as to straddle the movement path of the stage 152. Each of the ends of the U-shaped gate 160 is fixed to both side surfaces of the installation table 156. A scanner 162 is provided on one side of the gate 160, and a plurality of (for example, two) detection sensors 164 for detecting the front and rear ends of the pattern forming material 150 are provided on the other side. . The scanner 162 and the detection sensor 164 are respectively attached to the gate 160 and fixedly arranged above the moving path of the stage 152. The scanner 162 and the detection sensor 164 are connected to a controller (not shown) that controls them.

As shown in FIGS. 8 and 9B, the scanner 162 includes a plurality of (for example, 14) exposure heads 166 arranged in a substantially matrix of m rows and n columns (for example, 3 rows and 5 columns). ing. In this example, four exposure heads 166 are arranged in the third row in relation to the width of the pattern forming material 150. In addition, when showing each exposure head arranged in the m-th row and the n-th column, it is expressed as an exposure head 166 _mn .

An exposure area 168 by the exposure head 166 has a rectangular shape with a short side in the sub-scanning direction. Accordingly, as the stage 152 moves, a strip-shaped exposed region 170 is formed in the pattern forming material 150 for each exposure head 166. In addition, when showing the exposure area by each exposure head arranged in the m-th row and the n-th column, it is expressed as an exposure area 168 _mn .

Further, as shown in FIGS. 9A and 9B, each of the exposure heads in each row arranged in a line so that the strip-shaped exposed regions 170 are arranged in the direction orthogonal to the sub-scanning direction without gaps. These are arranged with a predetermined interval (natural number times the long side of the exposure area, twice in this example) in the arrangement direction. Therefore, can not be exposed portion between the exposure area _{168 11} in the first row and the exposure area _{168 12,} it can be exposed by the second row of the exposure area _{168 21} and the exposure area _{168 31} in the third row.

As shown in FIGS. 10 and 11, each of the exposure heads 166 _{11 to} 166 _mn serves as the light modulation means (spatial light modulation element that modulates each pixel) according to the pattern information. A digital micromirror device (DMD) 50 manufactured by Texas Instruments, USA is provided. The DMD 50 is connected to the controller 302 (see FIG. 12) including a data processing unit and a mirror drive control unit. The data processing unit of the controller 302 generates a control signal for driving and controlling each micromirror in the area to be controlled by the DMD 50 for each exposure head 166 based on the input pattern information. The area to be controlled will be described later. The mirror drive control unit controls the angle of the reflection surface of each micromirror of the DMD 50 for each exposure head 166 based on the control signal generated by the pattern information processing unit. The control of the angle of the reflecting surface will be described later.

  On the light incident side of the DMD 50, a fiber array light source 66 including a laser emitting section in which emission ends (light emitting points) of an optical fiber are arranged in a line along a direction corresponding to the long side direction of the exposure area 168, a fiber A lens system 67 for correcting the laser light emitted from the array light source 66 and condensing it on the DMD, and a mirror 69 for reflecting the laser light transmitted through the lens system 67 toward the DMD 50 are arranged in this order. In FIG. 10, the lens system 67 is schematically shown.

  As shown in detail in FIG. 11, the lens system 67 is inserted into the optical path of the light passing through the condenser lens 71 and the condenser lens 71 that collects the laser light B as the illumination light emitted from the fiber array light source 66. A rod-shaped optical integrator (hereinafter referred to as a rod integrator) 72 and an imaging lens 74 disposed in front of the rod integrator 72, that is, on the mirror 69 side. The condensing lens 71, the rod integrator 72, and the imaging lens 74 cause the laser light emitted from the fiber array light source 66 to enter the DMD 50 as a light beam that is close to parallel light and has a uniform beam cross-sectional intensity. The shape and action of the rod integrator 72 will be described in detail later.

  The laser beam B emitted from the lens system 67 is reflected by the mirror 69 and irradiated to the DMD 50 via the TIR (total reflection) prism 70. In FIG. 10, the TIR prism 70 is omitted.

  An imaging optical system 51 that images the laser beam B reflected by the DMD 50 on the pattern forming material 150 is disposed on the light reflection side of the DMD 50. The imaging optical system 51 is schematically shown in FIG. 10, but as shown in detail in FIG. 11, the imaging optical system 51 includes a first imaging optical system including lens systems 52 and 54 and lens systems 57 and 58. A second imaging optical system, a microlens array 55 inserted between these imaging optical systems, and an aperture array 59 are included.

The microlens array 55 is formed by two-dimensionally arranging a large number of microlenses 55a corresponding to the pixels of the DMD 50. In this example, as will be described later, only 1024 × 256 rows of the 1024 × 768 rows of micromirrors of the DMD 50 are driven, and accordingly, 1024 × 256 rows of microlenses 55a are arranged. The arrangement pitch of the micro lenses 55a is 41 μm in both the vertical and horizontal directions. As an example, the microlens 55a has a focal length of 0.19 mm, an NA (numerical aperture) of 0.11, and is formed from the optical glass BK7. The shape of the micro lens 55a will be described in detail later.
The beam diameter of the laser beam B at the position of each microlens 55a is 41 μm.

  The aperture array 59 is formed by forming a large number of apertures (openings) 59 a corresponding to the respective micro lenses 55 a of the micro lens array 55. The diameter of the aperture 59a is, for example, 10 μm.

  The first imaging optical system enlarges the image by the DMD 50 three times and forms an image on the microlens array 55. The second imaging optical system enlarges the image that has passed through the microlens array 55 by 1.6 times, and forms and projects the image on the pattern forming material 150. Therefore, as a whole, the image formed by the DMD 50 is enlarged and enlarged by 4.8 times, and is imaged and projected on the pattern forming material 150.

  A prism pair 73 is disposed between the second imaging optical system and the pattern forming material 150. By moving the prism pair 73 in the vertical direction in FIG. 11, an image on the pattern forming material 150 is obtained. The focus can be adjusted. In the figure, the pattern forming material 150 is sub-scanned in the direction of arrow F.

The pixel portion is not particularly limited as long as it can receive and emit light from the light irradiation means, and can be appropriately selected according to the purpose. For example, the pattern forming method of the present invention When the pattern to be formed is an image pattern, it is a pixel, and when the light modulation means includes a DMD, it is a micromirror.
There is no restriction | limiting in particular as the number (the said n) of picture element parts which the said light modulation element has, It can select suitably according to the objective.
The arrangement of the picture element portions in the light modulation element is not particularly limited and may be appropriately selected depending on the intended purpose. For example, it is preferably arranged in a two-dimensional form, and arranged in a lattice form. More preferably.

<Light irradiation means>
The light irradiation means is not particularly limited and may be appropriately selected depending on the purpose. For example, (ultra) high pressure mercury lamp, xenon lamp, carbon arc lamp, halogen lamp, copier, fluorescent tube, LED, etc. , A known light source such as a semiconductor laser, or means capable of synthesizing and irradiating two or more lights. Among these, means capable of synthesizing and irradiating two or more lights are preferable.
The light emitted from the light irradiation means is, for example, an electromagnetic wave that passes through the support and activates the photopolymerization initiator and sensitizer used when the light is irradiated through the support. In particular, ultraviolet to visible light, electron beam, X-ray, laser beam, and the like can be mentioned. Of these, laser beam is preferable, and a laser combining two or more lights (hereinafter, referred to as “combined laser”). More preferred. Even when light irradiation is performed after the support is peeled off, the same light can be used.

As a wavelength of the ultraviolet to visible light, for example, 300 to 1500 nm is preferable, 320 to 800 nm is more preferable, and 330 nm to 650 nm is particularly preferable.
As a wavelength of the said laser beam, 200-1500 nm is preferable, for example, 300-800 nm is more preferable, 330 nm-500 nm is still more preferable, 400 nm-450 nm is especially preferable.

  Examples of means capable of irradiating the combined laser include, for example, a plurality of lasers, a multimode optical fiber, and collective optics for condensing and coupling the laser beams respectively emitted from the plurality of lasers to the multimode optical fiber. Means having a system are preferred.

  Hereinafter, means (fiber array light source) capable of irradiating the combined laser will be described with reference to the drawings.

  As shown in FIG. 27 a, the fiber array light source 66 includes a plurality of (for example, 14) laser modules 64, and one end of the multimode optical fiber 30 is coupled to each laser module 64. An optical fiber 31 having the same core diameter as that of the multimode optical fiber 30 and a smaller cladding diameter than the multimode optical fiber 30 is coupled to the other end of the multimode optical fiber 30. As shown in detail in FIG. 27b, seven end portions of the multimode optical fiber 31 opposite to the optical fiber 30 are arranged along the main scanning direction orthogonal to the sub-scanning direction, and they are arranged in two rows to form a laser. An emission unit 68 is configured.

  As shown in FIG. 27b, the laser emitting portion 68 configured by the end portion of the multimode optical fiber 31 is sandwiched and fixed between two support plates 65 having a flat surface. In addition, a transparent protective plate such as glass is preferably disposed on the light emitting end face of the multimode optical fiber 31 for protection. The light exit end face of the multimode optical fiber 31 has high light density and is likely to collect dust and easily deteriorate. However, the protective plate as described above prevents the dust from adhering to the end face and deteriorates. Can be delayed.

  In this example, in order to arrange the emission ends of the optical fibers 31 with a small cladding diameter in a line without any gaps, the multimode optical fiber 30 is placed between two adjacent multimode optical fibers 30 at a portion with a large cladding diameter. Two exit ends of the optical fiber 31 coupled to the two multimode optical fibers 30 adjacent to each other at the portion where the cladding diameter is large are the exit ends of the optical fiber 31 coupled to the stacked and stacked multimode optical fibers 30. Are arranged so as to be sandwiched between them.

  For example, as shown in FIG. 28, an optical fiber 31 having a length of 1 to 30 cm and having a small cladding diameter is coaxially connected to the tip portion of the multimode optical fiber 30 having a large cladding diameter on the laser light emission side. Can be obtained by linking them together. In the two optical fibers, the incident end face of the optical fiber 31 is fused and joined to the outgoing end face of the multimode optical fiber 30 so that the central axes of both optical fibers coincide. As described above, the diameter of the core 31 a of the optical fiber 31 is the same as the diameter of the core 30 a of the multimode optical fiber 30.

  In addition, a short optical fiber in which an optical fiber having a short cladding diameter and a large cladding diameter is fused to an optical fiber having a short cladding diameter and a large cladding diameter may be coupled to the output end of the multimode optical fiber 30 via a ferrule or an optical connector. Good. By detachably coupling using a connector or the like, the tip portion can be easily replaced when an optical fiber having a small cladding diameter is broken, and the cost required for exposure head maintenance can be reduced. Hereinafter, the optical fiber 31 may be referred to as an emission end portion of the multimode optical fiber 30.

  The multimode optical fiber 30 and the optical fiber 31 may be any of a step index type optical fiber, a graded index type optical fiber, and a composite type optical fiber. For example, a step index type optical fiber manufactured by Mitsubishi Cable Industries, Ltd. can be used. In the present embodiment, the multimode optical fiber 30 and the optical fiber 31 are step index type optical fibers, and the multimode optical fiber 30 has a cladding diameter = 125 μm, a core diameter = 50 μm, NA = 0.2, an incident end face. The transmittance of the coat is 99.5% or more, and the optical fiber 31 has a cladding diameter = 60 μm, a core diameter = 50 μm, and NA = 0.2.

  In general, in laser light in the infrared region, propagation loss increases as the cladding diameter of the optical fiber is reduced. For this reason, a suitable cladding diameter is determined according to the wavelength band of the laser beam. However, the shorter the wavelength, the smaller the propagation loss. In the case of laser light having a wavelength of 405 nm emitted from a GaN-based semiconductor laser, the cladding thickness {(cladding diameter−core diameter) / 2} is set to an infrared light having a wavelength band of 800 nm. The propagation loss hardly increases even if it is about ½ of the case of propagating infrared light and about ¼ of the case of propagating infrared light in the 1.5 μm wavelength band for communication. Therefore, the cladding diameter can be reduced to 60 μm.

  However, the clad diameter of the optical fiber 31 is not limited to 60 μm. The clad diameter of the optical fiber used in the conventional fiber array light source is 125 μm, but the depth of focus becomes deeper as the clad diameter becomes smaller. More preferably, it is 40 μm or less. On the other hand, since the core diameter needs to be at least 3 to 4 μm, the cladding diameter of the optical fiber 31 is preferably 10 μm or more.

  The laser module 64 includes a combined laser light source (fiber array light source) shown in FIG. This combined laser light source includes a plurality of (for example, seven) chip-like lateral multimode or single mode GaN-based semiconductor lasers LD1, LD2, LD3, LD4, LD5, LD6, arrayed and fixed on the heat block 10. And LD7, collimator lenses 11, 12, 13, 14, 15, 16, and 17 provided corresponding to each of the GaN-based semiconductor lasers LD1 to LD7, one condenser lens 20, and one multi-lens. Mode optical fiber 30. The number of semiconductor lasers is not limited to seven. For example, as many as 20 semiconductor laser beams can be incident on a multimode optical fiber having a cladding diameter = 60 μm, a core diameter = 50 μm, and NA = 0.2. In addition, the number of optical fibers can be further reduced.

  The GaN-based semiconductor lasers LD1 to LD7 all have the same oscillation wavelength (for example, 405 nm), and the maximum output is also all the same (for example, 100 mW for the multimode laser and 30 mW for the single mode laser). As the GaN-based semiconductor lasers LD1 to LD7, lasers having an oscillation wavelength other than the above 405 nm in a wavelength range of 350 nm to 450 nm may be used.

  As shown in FIGS. 30 and 31, the combined laser light source is housed in a box-shaped package 40 having an upper opening together with other optical elements. The package 40 includes a package lid 41 created so as to close the opening thereof. After the deaeration process, a sealing gas is introduced, and the package 40 and the package lid 41 are closed by closing the opening of the package 40 with the package lid 41. 41. The combined laser light source is hermetically sealed in a closed space (sealed space) formed by 41.

  A base plate 42 is fixed to the bottom surface of the package 40, and the heat block 10, a condensing lens holder 45 that holds the condensing lens 20, and the multimode optical fiber 30 are disposed on the top surface of the base plate 42. A fiber holder 46 that holds the incident end is attached. The exit end of the multimode optical fiber 30 is drawn out of the package from an opening formed in the wall surface of the package 40.

  Further, a collimator lens holder 44 is attached to the side surface of the heat block 10, and the collimator lenses 11 to 17 are held. An opening is formed in the lateral wall surface of the package 40, and wiring 47 for supplying a driving current to the GaN-based semiconductor lasers LD1 to LD7 is drawn out of the package through the opening.

  In FIG. 31, in order to avoid complication of the figure, only the GaN-based semiconductor laser LD7 among the plurality of GaN-based semiconductor lasers is numbered, and only the collimator lens 17 among the plurality of collimator lenses is numbered. is doing.

  FIG. 32 shows the front shape of the attachment part of the collimator lenses 11-17. Each of the collimator lenses 11 to 17 is formed in a shape obtained by cutting a region including the optical axis of a circular lens having an aspherical surface into a long and narrow plane. This elongated collimator lens can be formed, for example, by molding resin or optical glass. The collimator lenses 11 to 17 are closely arranged in the arrangement direction of the light emitting points so that the length direction is orthogonal to the arrangement direction of the light emitting points of the GaN-based semiconductor lasers LD1 to LD7 (left and right direction in FIG. 32).

  On the other hand, each of the GaN-based semiconductor lasers LD1 to LD7 includes an active layer having a light emission width of 2 μm, and each of the laser beams B1 in a state in which the divergence angles in a direction parallel to and perpendicular to the active layer are, for example A laser emitting ~ B7 is used. These GaN-based semiconductor lasers LD1 to LD7 are arranged so that the light emitting points are arranged in a line in a direction parallel to the active layer.

Therefore, in the laser beams B1 to B7 emitted from the respective light emitting points, the direction in which the divergence angle is large coincides with the length direction and the divergence angle is small with respect to the elongated collimator lenses 11 to 17 as described above. Incident light is incident in a state where the direction coincides with the width direction (direction perpendicular to the length direction). That is, the collimator lenses 11 to 17 have a width of 1.1 mm and a length of 4.6 mm, and the horizontal and vertical beam diameters of the laser beams B1 to B7 incident thereon are 0.9 mm and 2. 6 mm. Each of the collimator lenses 11 to 17 has a focal length f ₁ = 3 mm, NA = 0.6, and a lens arrangement pitch = 1.25 mm.

The condensing lens 20 is formed by cutting a region including the optical axis of a circular lens having an aspheric surface into a long and narrow shape in parallel planes, and is long in the arrangement direction of the collimator lenses 11 to 17, that is, in a horizontal direction and short in a direction perpendicular thereto. Is formed. This condenser lens 20 has a focal length f ₂ = 23 mm and NA = 0.2. This condensing lens 20 is also formed by molding resin or optical glass, for example.

  In addition, since the light emitting means for illuminating the DMD uses a high-intensity fiber array light source in which the output ends of the optical fibers of the combined laser light source are arranged in an array, it has a high output and a deep depth of focus. A pattern forming apparatus can be realized. Furthermore, since the output of each fiber array light source is increased, the number of fiber array light sources required to obtain a desired output is reduced, and the cost of the pattern forming apparatus can be reduced.

  Further, since the cladding diameter of the output end of the optical fiber is smaller than the cladding diameter of the incident end, the diameter of the light emitting portion is further reduced, and the brightness of the fiber array light source can be increased. Thereby, a pattern forming apparatus having a deeper depth of focus can be realized. For example, even in the case of ultra-high resolution exposure with a beam diameter of 1 μm or less and a resolution of 0.1 μm or less, a deep depth of focus can be obtained, and high-speed and high-definition exposure is possible. Therefore, it is suitable for a thin film transistor (TFT) exposure process that requires high resolution.

  The light irradiating means is not limited to a fiber array light source including a plurality of the combined laser light sources, and for example, emits laser light incident from a single semiconductor laser having one light emitting point. A fiber array light source in which fiber light sources including optical fibers are arrayed can be used.

  Further, as the light irradiation means having a plurality of light emitting points, for example, as shown in FIG. 33, a laser in which a plurality of (for example, seven) chip-shaped semiconductor lasers LD1 to LD7 are arranged on the heat block 100. An array can be used. A chip-shaped multicavity laser 110 in which a plurality of (for example, five) light emitting points 110a shown in FIG. 34A is arranged in a predetermined direction is known. Since the multicavity laser 110 can arrange the light emitting points with high positional accuracy as compared with the case where the chip-shaped semiconductor lasers are arranged, it is easy to multiplex the laser beams emitted from the respective light emitting points. However, as the number of light emitting points increases, the multicavity laser 110 is likely to be bent at the time of laser manufacturing. Therefore, the number of light emitting points 110a is preferably 5 or less.

  As the light irradiation means, the multi-cavity laser 110 or a plurality of multi-cavity lasers 110 on the heat block 100 in the same direction as the arrangement direction of the light emitting points 110a of each chip as shown in FIG. An arrayed multi-cavity laser array can be used as a laser light source.

  The combined laser light source is not limited to one that combines laser beams emitted from a plurality of chip-shaped semiconductor lasers. For example, as shown in FIG. 21, a combined laser light source including a chip-shaped multicavity laser 110 having a plurality of (for example, three) light emitting points 110a can be used. This combined laser light source is configured to include a multi-cavity laser 110, one multi-mode optical fiber 130, and a condensing lens 120. The multi-cavity laser 110 can be composed of, for example, a GaN-based laser diode having an oscillation wavelength of 405 nm.

  In the above configuration, each of the laser beams B emitted from each of the plurality of light emitting points 110 a of the multicavity laser 110 is collected by the condenser lens 120 and enters the core 130 a of the multimode optical fiber 130. The laser light incident on the core 130a propagates in the optical fiber, is combined into one, and is emitted.

  A plurality of light emitting points 110 a of the multicavity laser 110 are arranged in parallel within a width substantially equal to the core diameter of the multimode optical fiber 130, and a focal point substantially equal to the core diameter of the multimode optical fiber 130 is formed as the condenser lens 120. By using a convex lens of a distance or a rod lens that collimates the outgoing beam from the multi-cavity laser 110 only in a plane perpendicular to the active layer, the coupling efficiency of the laser beam B to the multi-mode optical fiber 130 can be increased. it can.

  As shown in FIG. 35, a multi-cavity laser 110 having a plurality of (for example, three) emission points is used, and a plurality of (for example, nine) multi-cavity lasers 110 are equidistant from each other on the heat block 111. A combined laser light source including the laser array 140 arranged in (1) can be used. The plurality of multi-cavity lasers 110 are arranged and fixed in the same direction as the arrangement direction of the light emitting points 110a of each chip.

  This combined laser light source includes a laser array 140, a plurality of lens arrays 114 arranged corresponding to each multi-cavity laser 110, and a single rod arranged between the laser array 140 and the plurality of lens arrays 114. The lens 113, one multimode optical fiber 130, and a condenser lens 120 are provided. The lens array 114 includes a plurality of microlenses corresponding to the emission points of the multicavity laser 110.

  In the above configuration, each of the laser beams B emitted from each of the plurality of light emitting points 110a of the plurality of multi-cavity lasers 110 is collected in a predetermined direction by the rod lens 113, and then each microlens of the lens array 114. It becomes parallel light. The collimated laser beam L is condensed by the condenser lens 120 and enters the core 130a of the multimode optical fiber 130. The laser light incident on the core 130a propagates in the optical fiber, is combined into one, and is emitted.

  Still another example of the combined laser light source will be described. In this combined laser light source, as shown in FIGS. 36A and 36B, a heat block 182 having an L-shaped cross section in the optical axis direction is mounted on a substantially rectangular heat block 180, and two heats are provided. A storage space is formed between the blocks. On the upper surface of the L-shaped heat block 182, a plurality of (for example, two) multi-cavity lasers 110 in which a plurality of light emitting points (for example, five) are arranged in an array form the light emitting points 110a of each chip. It is arranged and fixed at equal intervals in the same direction as the arrangement direction.

  A concave portion is formed in the substantially rectangular heat block 180, and a plurality of (for example, two) light emitting points (for example, five) are arranged in an array on the upper surface of the space side of the heat block 180. The multi-cavity laser 110 is arranged such that its emission point is located on the same vertical plane as the emission point of the laser chip arranged on the upper surface of the heat block 182.

  On the laser beam emission side of the multi-cavity laser 110, a collimator lens array 184 in which collimator lenses are arranged corresponding to the light emission points 110a of the respective chips is arranged. In the collimating lens array 184, the length direction of each collimating lens coincides with the direction in which the divergence angle of the laser beam is large (fast axis direction), and the width direction of each collimating lens is in the direction in which the divergence angle is small (slow axis direction). They are arranged to match. Thus, by collimating and integrating the collimating lenses, the space utilization efficiency of the laser light can be improved, the output of the combined laser light source can be increased, and the number of parts can be reduced and the cost can be reduced. .

  Further, on the laser light emitting side of the collimating lens array 184, there is one multimode optical fiber 130 and a condensing lens 120 that condenses and couples the laser light to the incident end of the multimode optical fiber 130. Is arranged.

  In the above configuration, each of the laser beams B emitted from each of the plurality of light emitting points 110a of the plurality of multi-cavity lasers 110 arranged on the laser blocks 180 and 182 is collimated by the collimating lens array 184 and condensed. The light is condensed by the lens 120 and enters the core 130 a of the multimode optical fiber 130. The laser light incident on the core 130a propagates in the optical fiber, is combined into one, and is emitted.

  As described above, the combined laser light source can achieve particularly high output by the multistage arrangement of multicavity lasers and the array of collimating lenses. By using this combined laser light source, a higher-intensity fiber array light source or bundle fiber light source can be configured, so that it is particularly suitable as a fiber light source constituting the laser light source of the pattern forming apparatus of the present invention.

  It should be noted that a laser module in which each of the combined laser light sources is housed in a casing and the emission end of the multimode optical fiber 130 is pulled out from the casing can be configured.

  In addition, the other end of the multimode optical fiber of the combined laser light source is coupled with another optical fiber having the same core diameter as the multimode optical fiber and a cladding diameter smaller than the multimode optical fiber. However, for example, a multimode optical fiber having a cladding diameter of 125 μm, 80 μm, 60 μm or the like may be used without coupling another optical fiber to the emission end.

Here, the pattern forming method of the present invention will be further described.
In each exposure head 166 of the scanner 162, laser light B1, B2, B3, B4, B5, B6 emitted in a divergent light state from each of the GaN-based semiconductor lasers LD1 to LD7 constituting the combined laser light source of the fiber array light source 66. , And B7 are collimated by corresponding collimator lenses 11-17. The collimated laser beams B <b> 1 to B <b> 7 are collected by the condenser lens 20 and converge on the incident end face of the core 30 a of the multimode optical fiber 30.

  In this example, the collimator lenses 11 to 17 and the condenser lens 20 constitute a condensing optical system, and the condensing optical system and the multimode optical fiber 30 constitute a multiplexing optical system. That is, the laser beams B1 to B7 collected as described above by the condenser lens 20 enter the core 30a of the multimode optical fiber 30 and propagate through the optical fiber to be combined with one laser beam B. The light is emitted from the optical fiber 31 coupled to the output end of the multimode optical fiber 30.

  In each laser module, when the coupling efficiency of the laser beams B1 to B7 to the multimode optical fiber 30 is 0.85 and each output of the GaN-based semiconductor lasers LD1 to LD7 is 30 mW, the light arranged in an array For each of the fibers 31, a combined laser beam B with an output of 180 mW (= 30 mW × 0.85 × 7) can be obtained. Therefore, the output from the laser emitting unit 68 in which the six optical fibers 31 are arranged in an array is about 1 W (= 180 mW × 6).

  In the laser emitting portion 68 of the fiber array light source 66, light emission points with high luminance are arranged in a line along the main scanning direction as described above. A conventional fiber light source that couples laser light from a single semiconductor laser to a single optical fiber has a low output, so that a desired output cannot be obtained unless multiple rows are arranged. Since the laser light source has a high output, a desired output can be obtained even with a small number of columns, for example, one column.

For example, in a conventional fiber light source in which a semiconductor laser and an optical fiber are coupled on a one-to-one basis, a laser having an output of about 30 mW (milliwatt) is usually used as the semiconductor laser, and the core diameter is 50 μm and the cladding diameter is 125 μm. Since a multimode optical fiber having a numerical aperture (NA) of 0.2 is used, if an output of about 1 W (watt) is to be obtained, 48 multimode optical fibers (8 × 6) must be bundled. Since the area of the light emitting region is 0.62 mm ² (0.675 mm × 0.925 mm), the luminance at the laser emitting portion 68 is 1.6 × 10 ⁶ (W / m ² ) and one optical fiber is used. The luminance per hit is 3.2 × 10 ⁶ (W / m ² ).

On the other hand, when the light irradiating means is a means capable of irradiating a combined laser, an output of about 1 W can be obtained with six multimode optical fibers, and the area of the light emitting region at the laser emitting portion 68 can be obtained. Is 0.0081 mm ² (0.325 mm × 0.025 mm), the luminance at the laser emitting portion 68 is 123 × 10 ⁶ (W / m ² ), which is about 80 times higher than the conventional luminance. be able to. Further, the luminance per optical fiber is 90 × 10 ⁶ (W / m ² ), and the luminance can be increased by about 28 times compared with the conventional one.

  Here, with reference to FIGS. 37A and 37B, the difference in depth of focus between the conventional exposure head and the exposure head of the present embodiment will be described. The diameter of the light emission region of the bundled fiber light source of the conventional exposure head in the sub-scanning direction is 0.675 mm, and the diameter of the light emission region of the fiber array light source of the exposure head in the sub-scanning direction is 0.025 mm. As shown in FIG. 37A, in the conventional exposure head, since the light emitting area of the light irradiating means (bundle-shaped fiber light source) 1 is large, the angle of the light beam incident on the DMD 3 is increased, and as a result, the scanning surface 5 is moved. The angle of the incident light beam increases. For this reason, the beam diameter tends to increase with respect to the light condensing direction (shift in the focus direction).

  On the other hand, as shown in FIG. 37B, in the exposure head in the pattern forming apparatus of the present invention, the diameter of the light emitting region of the fiber array light source 66 in the sub-scanning direction is small, so that it passes through the lens system 67 and enters the DMD 50. As a result, the angle of the light beam incident on the scanning surface 56 is reduced. That is, the depth of focus becomes deep. In this example, the diameter of the light emitting region in the sub-scanning direction is about 30 times that of the conventional one, and a depth of focus substantially corresponding to the diffraction limit can be obtained. Therefore, it is suitable for exposure of a minute spot. This effect on the depth of focus is more prominent and effective as the required light quantity of the exposure head is larger. In this example, the size of one pixel projected on the exposure surface is 10 μm × 10 μm. The DMD is a reflective spatial light modulator, but FIGS. 37A and 37B are developed views for explaining the optical relationship.

  Pattern information corresponding to the exposure pattern is input to a controller (not shown) connected to the DMD 50 and temporarily stored in a frame memory in the controller. This pattern information is data representing the density of each pixel constituting the image as binary values (whether or not dots are recorded).

  The stage 152 having the pattern forming material 150 adsorbed on the surface thereof is moved at a constant speed from the upstream side to the downstream side of the gate 160 along the guide 158 by a driving device (not shown). When the leading edge of the pattern forming material 150 is detected by the detection sensor 164 attached to the gate 160 while the stage 152 passes under the gate 160, the pattern information stored in the frame memory is sequentially read out for a plurality of lines. Then, a control signal is generated for each exposure head 166 based on the pattern information read by the data processing unit. Then, each of the micromirrors of the DMD 50 is controlled on and off for each exposure head 166 based on the generated control signal by the mirror drive control unit.

  When the DMD 50 is irradiated with laser light from the fiber array light source 66, the laser light reflected when the micromirror of the DMD 50 is in the on state is coupled onto the exposed surface 56 of the pattern forming material 150 by the lens systems 54 and 58. Imaged. In this manner, the laser light emitted from the fiber array light source 66 is turned on / off for each pixel, and the pattern forming material 150 is exposed in the number of pixel units (exposure area 168) substantially equal to the number of used pixel elements of the DMD 50. . Further, when the pattern forming material 150 is moved at a constant speed together with the stage 152, the pattern forming material 150 is sub-scanned in the direction opposite to the stage moving direction by the scanner 162, and a strip-shaped exposed region 170 is provided for each exposure head 166. Is formed.

<Microlens array>
The exposure is preferably performed using the modulated light through a microlens array, and may be performed through an aperture array, an imaging optical system, or the like.

  The microlens array is not particularly limited and may be appropriately selected according to the purpose. For example, microlenses having an aspheric surface capable of correcting aberration due to distortion of the exit surface in the pixel portion are arranged. A thing is mentioned suitably.

  There is no restriction | limiting in particular as said aspherical surface, Although it can select suitably according to the objective, For example, a toric surface is preferable.

  Hereinafter, the microlens array, the aperture array, the imaging optical system, and the like will be described with reference to the drawings.

FIG. 13A shows each of DMD 50, light irradiation means 144 for irradiating the DMD 50 with laser light, lens systems (imaging optical systems) 454, 458, and DMD 50 for enlarging and imaging the laser light reflected by the DMD 50. A microlens array 472 in which a large number of microlenses 474 are arranged corresponding to the picture element portion, an aperture array 476 in which a large number of apertures 478 are provided corresponding to each microlens of the microlens array 472, and a laser that has passed through the aperture An exposure head composed of lens systems (imaging optical systems) 480 and 482 for forming an image of light on an exposed surface 56 is shown.
Here, FIG. 14 shows the result of measuring the flatness of the reflecting surface of the micromirror 62 constituting the DMD 50. In the figure, the same height positions of the reflecting surfaces are shown connected by contour lines, and the pitch of the contour lines is 5 nm. Note that the x direction and the y direction shown in the figure are two diagonal directions of the micromirror 62, and the micromirror 62 rotates around the rotation axis extending in the y direction as described above. 15A and 15B show the height position displacement of the reflecting surface of the micromirror 62 along the x direction and the y direction, respectively.

  As shown in FIGS. 14 and 15, there is distortion on the reflection surface of the micromirror 62, and when attention is paid particularly to the center of the mirror, distortion in one diagonal direction (y direction) is different from that in the other diagonal line. It is larger than the distortion in the direction (x direction). For this reason, the problem that the shape in the condensing position of the laser beam B condensed with the micro lens 55a of the micro lens array 55 may be distorted may occur.

  In the pattern forming method of the present invention, in order to prevent the above problem, the microlens 55a of the microlens array 55 has a special shape different from the conventional one. Hereinafter, this point will be described in detail.

  FIGS. 16A and 16B respectively show the front and side shapes of the entire microlens array 55 in detail. These drawings also show the dimensions of each part of the microlens array 55, and the unit thereof is mm. In the pattern forming method of the present invention, as described above with reference to FIG. 4, the 1024 × 256 rows of micromirrors 62 of the DMD 50 are driven. A row of 1024 microlenses 55a arranged in the direction is arranged in parallel in the vertical direction. In FIG. 9A, the arrangement order of the microlens array 55 is indicated by j in the horizontal direction and k in the vertical direction.

  17A and 17B show the front shape and the side shape of one microlens 55a in the microlens array 55, respectively. In FIG. 9A, the contour lines of the micro lens 55a are also shown. The end surface of each microlens 55a on the light emitting side has an aspherical shape that corrects aberration due to distortion of the reflecting surface of the micromirror 62. More specifically, the micro lens 55a is a toric lens, and has a radius of curvature Rx = −0.125 mm in a direction optically corresponding to the x direction and a radius of curvature Ry = − in a direction corresponding to the y direction. 0.1 mm.

  Therefore, the condensing state of the laser beam B in the cross section parallel to the x direction and the y direction is roughly as shown in FIGS. 18A and 18B, respectively. That is, when the cross section parallel to the x direction is compared with the cross section parallel to the y direction, the radius of curvature of the microlens 55a is smaller and the focal length is shorter in the latter cross section. .

  19A, 19B, 19D, and 19D show simulation results of the beam diameter in the vicinity of the condensing position (focal position) of the microlens 55a when the microlens 55a has the above shape. For comparison, FIGS. 20a, 20b, 20c, and 20d show the results of a similar simulation when the microlens 55a has a spherical shape with a radius of curvature Rx = Ry = −0.1 mm. In addition, the value of z in each figure has shown the evaluation position of the focus direction of the micro lens 55a with the distance from the beam emission surface of the micro lens 55a.

The surface shape of the microlens 55a used for the simulation is calculated by the following calculation formula.

  In the above formula, Cx means the curvature in the x direction (= 1 / Rx), Cy means the curvature in the y direction (= 1 / Ry), and X is the lens optical axis in the x direction. The distance from O means Y, and Y means the distance from the lens optical axis O in the y direction.

  19A to 19D and FIGS. 20A to 20D, in the pattern forming method of the present invention, the microlens 55a is focused on the micro lens 55a with a focal length in a cross section parallel to the y direction. By using a toric lens smaller than the distance, distortion of the beam shape in the vicinity of the condensing position is suppressed. If so, the pattern forming material 150 can be exposed to a higher-definition image without distortion. It can also be seen that the embodiment shown in FIGS. 19a to 19d has a wider region with a smaller beam diameter, that is, a greater depth of focus.

  In addition, when the magnitude relation of the distortion of the center part in the x direction and the y direction of the micromirror 62 is opposite to the above, the focal length in the cross section parallel to the x direction is in the cross section parallel to the y direction. If the microlens is formed of a toric lens that is smaller than the focal length, similarly, it is possible to expose the pattern forming material 150 with a higher definition image without distortion.

  In addition, the aperture array 59 disposed in the vicinity of the condensing position of the microlens array 55 is disposed such that only light having passed through the corresponding microlens 55a is incident on each aperture 59a. That is, by providing this aperture array 59, it is possible to prevent light from adjacent microlenses 55a not corresponding to each aperture 59a from entering, and to increase the extinction ratio.

  Originally, if the diameter of the aperture 59a of the aperture array 59 installed for the above purpose is reduced to some extent, an effect of suppressing the distortion of the beam shape at the condensing position of the microlens 55a can be obtained. However, in such a case, the amount of light blocked by the aperture array 59 is increased, and the light use efficiency is reduced. On the other hand, when the microlens 55a has an aspherical shape, the light utilization efficiency is kept high because the light is not blocked.

  In the pattern forming method of the present invention, the microlens 55a may have a secondary aspherical shape or a higher order (4th, 6th,...) Aspherical shape. By adopting the higher order aspherical shape, the beam shape can be further refined.

  In the embodiment described above, the end surface on the light emission side of the micro lens 55a is an aspherical surface (toric surface). However, one of the two light passing end surfaces is a spherical surface and the other is a cylindrical surface. Thus, the microlens array can be configured to obtain the same effect as the above embodiment.

  Furthermore, in the embodiment described above, the microlens 55a of the microlens array 55 has an aspherical shape that corrects aberration due to distortion of the reflecting surface of the micromirror 62. Such an aspherical shape is adopted. Instead, the same effect can be obtained even if each microlens constituting the microlens array has a refractive index distribution that corrects aberration due to distortion of the reflection surface of the micromirror 62.

  An example of such a microlens 155a is shown in FIG. (A) and (B) of the same figure respectively show the front shape and side shape of the micro lens 155a, and the external shape of the micro lens 155a is a parallel plate shape as shown in the figure. The x and y directions in the figure are as described above.

  23A and 23B schematically show the condensing state of the laser beam B in the cross section parallel to the x direction and the y direction by the micro lens 155a. The microlens 155a has a refractive index distribution that gradually increases outward from the optical axis O. In the drawing, the broken line shown in the microlens 155a indicates that the refractive index is predetermined from the optical axis O. The position changed with the pitch is shown. As shown in the figure, when the cross section parallel to the x direction and the cross section parallel to the y direction are compared, the ratio of the refractive index change of the microlens 155a is larger in the latter cross section, and the focal length is larger. It is shorter. Even when a microlens array composed of such a gradient index lens is used, it is possible to obtain the same effect as when the microlens array 55 is used.

  In addition, in the microlens whose surface shape is aspherical like the microlens 55a previously shown in FIGS. 17 and 18, the refractive index distribution as described above is given together, and both by the surface shape and the refractive index distribution. The aberration due to the distortion of the reflection surface of the micromirror 62 may be corrected.

  In the above embodiment, the aberration due to the distortion of the reflection surface of the micromirror 62 constituting the DMD 50 is corrected. However, in the pattern forming method of the present invention using the spatial light modulator other than the DMD, the spatial light is also corrected. If there is distortion on the surface of the picture element portion of the modulation element, the present invention can be applied to correct the aberration caused by the distortion and prevent the beam shape from being distorted.

Next, the imaging optical system will be further described.
In the exposure head, when the laser beam is irradiated from the light irradiation unit 144, the cross-sectional area of the light beam reflected in the ON direction by the DMD 50 is enlarged several times (for example, two times) by the lens systems 454 and 458. The The expanded laser light is condensed by each microlens of the microlens array 472 so as to correspond to each pixel part of the DMD 50, and passes through the corresponding aperture of the aperture array 476. The laser light that has passed through the aperture is imaged on the exposed surface 56 by the lens systems 480 and 482.

  In this imaging optical system, the laser light reflected by the DMD 50 is magnified several times by the magnifying lenses 454 and 458 and projected onto the exposed surface 56, so that the entire image area is widened. At this time, if the microlens array 472 and the aperture array 476 are not arranged, as shown in FIG. 13B, one pixel size (spot size) of each beam spot BS projected onto the exposed surface 56 is set. MTF (Modulation Transfer Function) characteristics representing the sharpness of the exposure area 468 are reduced depending on the size of the exposure area 468.

  On the other hand, when the microlens array 472 and the aperture array 476 are arranged, the laser light reflected by the DMD 50 is condensed corresponding to each pixel part of the DMD 50 by each microlens of the microlens array 472. Accordingly, as shown in FIG. 13C, even when the exposure area is enlarged, the spot size of each beam spot BS can be reduced to a desired size (for example, 10 μm × 10 μm), and the MTF characteristics are obtained. It is possible to perform high-definition exposure while preventing the deterioration of the above. The exposure area 468 is tilted because the DMD 50 is tilted and arranged in order to eliminate the gap between the pixels.

  In addition, the aperture array can shape the beam so that the spot size on the surface to be exposed 56 is constant even if the beam is thick due to the aberration of the micro lens. Thus, crosstalk between adjacent picture elements can be prevented by passing through the aperture array.

  Further, by using a high-intensity light source, which will be described later, as the light irradiating means 144, the angle of the light beam incident on each microlens of the microlens array 472 from the lens 458 becomes small. The incident can be prevented. That is, a high extinction ratio can be realized.

<Other optical systems>
In the pattern forming method of the present invention, it may be used in combination with other optical systems appropriately selected from known optical systems, for example, a light amount distribution correcting optical system composed of a pair of combination lenses.
The light amount distribution correcting optical system changes the light flux width at each exit position so that the ratio of the light flux width at the peripheral portion to the light flux width at the central portion close to the optical axis is smaller on the exit side than on the incident side. When the DMD is irradiated with the parallel light flux from the light irradiation means, the light amount distribution on the irradiated surface is corrected so as to be substantially uniform. Hereinafter, the light quantity distribution correcting optical system will be described with reference to the drawings.

  First, as shown in FIG. 24A, the case where the entire luminous flux widths (total luminous flux widths) H0 and H1 are the same for the incident luminous flux and the outgoing luminous flux will be described. In FIG. 24A, the portions denoted by reference numerals 51 and 52 virtually indicate the entrance surface and the exit surface in the light quantity distribution correction optical system.

  In the light quantity distribution correcting optical system, it is assumed that the light flux widths h0 and h1 of the light beam incident on the central portion near the optical axis Z1 and the light flux incident on the peripheral portion are the same (h0 = hl). The light quantity distribution correcting optical system expands the light flux width h0 of the incident light flux at the central portion with respect to the light having the same light flux width h0, h1 on the incident side, and conversely changes the incident light flux at the peripheral portion. On the other hand, the light beam width h1 is reduced. That is, the width h10 of the outgoing light beam at the center and the width h11 of the outgoing light beam at the periphery are set to satisfy h11 <h10. In terms of the ratio of the luminous flux width, the ratio “h11 / h10” of the luminous flux width in the peripheral portion to the luminous flux width in the central portion on the emission side is smaller than the ratio (h1 / h0 = 1) on the incident side ( (H11 / h10) <1).

  By changing the light flux width in this way, the light flux in the central part, which normally has a large light quantity distribution, can be utilized in the peripheral part where the light quantity is insufficient, and the overall light utilization efficiency is not reduced. In addition, the light quantity distribution on the irradiated surface is made substantially uniform. The degree of uniformity is, for example, such that the unevenness in the amount of light in the effective area is within 30%, preferably within 20%.

  The operations and effects of the light quantity distribution correcting optical system are the same when the entire luminous flux width is changed between the incident side and the exit side (FIGS. 24B and 24C).

  FIG. 24B shows a case where the entire light flux width H0 on the incident side is “reduced” to the width H2 and emitted (H0> H2). Even in such a case, the light quantity distribution correcting optical system has the same light beam width h0, h1 on the incident side, and the light beam width h10 in the central part is larger than that in the peripheral part on the emission side. Conversely, the luminous flux width h11 at the peripheral part is made smaller than that at the central part. Considering the reduction rate of the light beam, the reduction rate with respect to the incident light beam in the central part is made smaller than that in the peripheral part, and the reduction rate with respect to the incident light beam in the peripheral part is made larger than that in the central part. Also in this case, the ratio “H11 / H10” of the light flux width in the peripheral portion to the light flux width in the central portion is smaller than the ratio (h1 / h0 = 1) on the incident side ((h11 / h10) <1) .

  FIG. 24C shows a case where the entire light flux width H0 on the incident side is “enlarged” by the width Η3 and emitted (H0 <H3). Even in such a case, the light quantity distribution correcting optical system has the same light beam width h0, h1 on the incident side, and the light beam width h10 in the central part is larger than that in the peripheral part on the emission side. Conversely, the luminous flux width h11 at the peripheral part is made smaller than that at the central part. Considering the expansion rate of the light beam, the expansion rate for the incident light beam in the central portion is made larger than that in the peripheral portion, and the expansion rate for the incident light beam in the peripheral portion is made smaller than that in the central portion. Also in this case, the ratio “h11 / h10” of the light flux width in the peripheral portion to the light flux width in the central portion is smaller than the ratio (h1 / h0 = 1) on the incident side ((h11 / h10) <1). .

  As described above, the light quantity distribution correcting optical system changes the light beam width at each emission position, and the ratio of the light beam width in the peripheral part to the light beam width in the central part near the optical axis Z1 is larger on the outgoing side than on the incident side. Since the light having the same luminous flux width on the incident side is larger on the outgoing side, the luminous flux width in the central portion is larger than that in the peripheral portion, and the luminous flux width in the peripheral portion is smaller than that in the central portion. Become smaller. As a result, it is possible to make use of the light beam at the center part to the peripheral part, and it is possible to form a light beam cross-section with a substantially uniform light amount distribution without reducing the light use efficiency of the entire optical system.

Next, an example of specific lens data of a pair of combination lenses used as the light quantity distribution correcting optical system will be shown. In this example, lens data in the case where the light amount distribution in the cross section of the emitted light beam is a Gaussian distribution as in the case where the light irradiation means is a laser array light source is shown. When one semiconductor laser is connected to the incident end of the single mode optical fiber, the light quantity distribution of the emitted light beam from the optical fiber becomes a Gaussian distribution. The pattern forming method of the present invention can be applied to such a case. Further, the present invention can be applied to a case where the light amount in the central portion near the optical axis is larger than the light amount in the peripheral portion, for example, by reducing the core diameter of the multi-mode optical fiber and approaching the configuration of the single mode optical fiber.
Table 1 below shows basic lens data.

  As can be seen from Table 1, the pair of combination lenses is composed of two rotationally symmetric aspherical lenses. If the light incident side surface of the first lens disposed on the light incident side is the first surface and the light exit side surface is the second surface, the first surface is aspherical. In addition, when the surface on the light incident side of the second lens disposed on the light emitting side is the third surface and the surface on the light emitting side is the fourth surface, the fourth surface is aspherical.

In Table 1, the surface number Si indicates the number of the i-th surface (i = 1 to 4), the curvature radius ri indicates the curvature radius of the i-th surface, and the surface interval di indicates the i-th surface and the i + 1-th surface. The distance between surfaces on the optical axis is shown. The unit of the surface interval di value is millimeter (mm). The refractive index Ni indicates the value of the refractive index with respect to the wavelength of 405 nm of the optical element having the i-th surface.
Table 2 below shows the aspheric data of the first surface and the fourth surface.

  The aspheric data is expressed by a coefficient in the following formula (A) that represents the aspheric shape.

In the above formula (A), each coefficient is defined as follows.
Z: Length of a perpendicular line (mm) drawn from a point on the aspheric surface at a height ρ from the optical axis to the tangent plane (plane perpendicular to the optical axis) of the apex of the aspheric surface
ρ: Distance from optical axis (mm)
K: Conic coefficient C: Paraxial curvature (1 / r, r: Paraxial radius of curvature)
ai: i-th order (i = 3 to 10) aspheric coefficient In the numerical values shown in Table 2, the symbol “E” indicates that the subsequent numerical value is a “power index” with 10 as the base. The numerical value represented by the exponential function with the base of 10 is multiplied by the numerical value before “E”. For example, “1.0E-02” indicates “1.0 × 10 ⁻² ”.

  FIG. 26 shows a light amount distribution of illumination light obtained by the pair of combination lenses shown in Tables 1 and 2. The horizontal axis indicates coordinates from the optical axis, and the vertical axis indicates the light amount ratio (%). For comparison, FIG. 25 shows a light amount distribution (Gaussian distribution) of illumination light when correction is not performed. As can be seen from FIGS. 25 and 26, the light amount distribution correction optical system corrects the light amount distribution which is substantially uniform as compared with the case where the correction is not performed. Thereby, it is possible to perform exposure with uniform laser light without reducing the use efficiency of light, without causing any unevenness.

[Other processes]
There is no restriction | limiting in particular as said other process, Although selecting suitably from the process in well-known pattern formation is mentioned, For example, a image development process, an etching process, a plating process, etc. are mentioned. These may be used alone or in combination of two or more.
The development step is a step of forming a pattern by exposing the photosensitive layer in the pattern forming material by the exposure step, curing the exposed region of the photosensitive layer, and then developing by removing an uncured region. is there.

The developing step can be preferably performed by, for example, developing means.
The developing means is not particularly limited as long as it can be developed using a developer, and can be appropriately selected according to the purpose. For example, the means for spraying the developer and the developer are applied. And means for immersing in the developer. These may be used alone or in combination of two or more.
In addition, the developing unit may include a developer replacing unit that replaces the developer, a developer supplying unit that supplies the developer, and the like.

  There is no restriction | limiting in particular as said developing solution, Although it can select suitably according to the objective, For example, an alkaline solution, an aqueous developing solution, an organic solvent etc. are mentioned, Among these, weakly alkaline aqueous solution is preferable. Examples of the basic component of the weak alkaline liquid include lithium hydroxide, sodium hydroxide, potassium hydroxide, lithium carbonate, sodium carbonate, potassium carbonate, lithium hydrogen carbonate, sodium hydrogen carbonate, potassium hydrogen carbonate, sodium phosphate, phosphorus Examples include potassium acid, sodium pyrophosphate, potassium pyrophosphate, and borax.

The pH of the weak alkaline aqueous solution is, for example, preferably about 8 to 12, and more preferably about 9 to 11. Examples of the weak alkaline aqueous solution include a 0.1 to 5% by mass aqueous sodium carbonate solution or an aqueous potassium carbonate solution.
The temperature of the developer can be appropriately selected according to the developability of the photosensitive layer, and is preferably about 25 ° C. to 40 ° C., for example.

  The developer includes a surfactant, an antifoaming agent, an organic base (for example, ethylenediamine, ethanolamine, tetramethylammonium hydroxide, diethylenetriamine, triethylenepentamine, morpholine, triethanolamine, etc.) and accelerates development. Therefore, it may be used in combination with an organic solvent (for example, alcohols, ketones, esters, ethers, amides, lactones, etc.). The developer may be an aqueous developer obtained by mixing water or an aqueous alkali solution and an organic solvent, or may be an organic solvent alone.

The etching step can be performed by a method appropriately selected from known etching methods.
There is no restriction | limiting in particular as an etching liquid used for the said etching process, Although it can select suitably according to the objective, For example, when the said metal layer is formed with copper, a cupric chloride solution, Examples thereof include a ferric chloride solution, an alkali etching solution, and a hydrogen peroxide-based etching solution. Among these, a ferric chloride solution is preferable from the viewpoint of an etching factor.
A permanent pattern can be formed on the surface of the substrate by removing the pattern after performing the etching process in the etching step.
There is no restriction | limiting in particular as said permanent pattern, According to the objective, it can select suitably, For example, a wiring pattern etc. are mentioned suitably.

The plating step can be performed by an appropriately selected method selected from known plating processes.
Examples of the plating treatment include copper plating such as copper sulfate plating and copper pyrophosphate plating, solder plating such as high flow solder plating, watt bath (nickel sulfate-nickel chloride) plating, nickel plating such as nickel sulfamate, and hard gold plating. And gold plating such as soft gold plating.
A permanent pattern can be formed on the surface of the substrate by removing the pattern after the plating process in the plating process, and further removing unnecessary portions by an etching process or the like as necessary.

[Method of manufacturing printed wiring board]
The pattern forming method of the present invention can be suitably used for the production of a printed wiring board, particularly for the production of a printed wiring board having a hole such as a through hole or a via hole. Hereinafter, an example of the manufacturing method of the printed wiring board using the pattern formation method of this invention is demonstrated.

-Manufacturing method of printed wiring board-
In particular, as a method of manufacturing a printed wiring board having a hole portion such as a through hole or a via hole, (1) the pattern forming material is placed on the printed wiring board forming substrate having the hole portion as the base, and the photosensitive layer is (2) The photosensitive layer is cured by irradiating a desired region from the side opposite to the base of the laminate to cure the photosensitive layer. (3) If the laminate has the support in the pattern forming material and the cushion layer, the cushion layer is removed, and (4) the photosensitive layer in the laminate is developed to remove the uncured portion in the laminate. Thus, a pattern can be formed.

In addition, when the cushion layer is swellable or soluble in an alkaline liquid, the removal of the cushion layer is not particularly limited, and may be performed anywhere after (2). When it is insoluble in the alkaline liquid, it is preferably removed before (4).
Moreover, you may perform the removal of the said support body in said (3) between said (1) and said (2) instead of performing between said (2) and said (4).
Further, when the pattern forming material has a barrier layer, the barrier layer may be removed together with the support in (3), or may be removed during development in (4).

  Thereafter, in order to obtain a printed wiring board, a method of etching or plating the printed wiring board forming substrate using the formed pattern (for example, a known subtractive method or additive method (for example, a semi-additive method) And the full additive method)). Among these, in order to form a printed wiring board by industrially advantageous tenting, the subtractive method is preferable. After the treatment, the cured resin remaining on the printed wiring board forming substrate is peeled off. In the case of the semi-additive method, a desired printed wiring board can be manufactured by further etching the copper thin film portion after peeling. it can. A multilayer printed wiring board can also be manufactured in the same manner as the printed wiring board manufacturing method.

  Next, the manufacturing method of the printed wiring board which has a through hole using the said pattern formation material is further demonstrated.

  First, a printed wiring board forming substrate having through holes and having a surface covered with a metal plating layer is prepared. As the printed wiring board forming substrate, for example, a copper-clad laminate substrate and a substrate in which a copper plating layer is formed on an insulating base material such as glass-epoxy, or an interlayer insulating film is laminated on these substrates, and a copper plating layer is formed. A formed substrate (laminated substrate) can be used.

Next, when the protective film is provided on the pattern forming material, the protective film is peeled off, and the pressure-sensitive roll is placed so that the photosensitive layer in the pattern forming material is in contact with the surface of the printed wiring board forming substrate. Used for pressure bonding (lamination process). Thereby, the laminated body which has the said board | substrate for printed wiring board formation and the said laminated body in this order is obtained.
There is no restriction | limiting in particular as lamination | stacking temperature of the said pattern formation material, For example, room temperature (15-30 degreeC) or under heating (30-180 degreeC) is mentioned, Among these, under heating (60-140 degreeC) ) Is preferred.
There is no restriction | limiting in particular as roll pressure of the said crimping | compression-bonding roll, For example, 0.1-1 Mpa is preferable.
There is no restriction | limiting in particular as the speed | rate of the said crimping | compression-bonding, and 1-3 m / min is preferable.
The printed wiring board forming substrate may be preheated or laminated under reduced pressure.

  In the formation of the laminate, the pattern forming material may be laminated on the printed wiring board forming substrate, and a photosensitive resin composition solution for manufacturing the pattern forming material is used for forming the printed wiring board. The photosensitive layer, the cushion layer, and the support may be laminated on the printed wiring board forming substrate by applying directly to the surface of the substrate and drying. In the case where a barrier layer is provided, it is preferably formed between the photosensitive layer and the cushion layer.

  Next, the photosensitive layer is cured by irradiating light from the surface of the laminate opposite to the substrate. At this time, exposure may be performed after peeling off the support as necessary (for example, when the light transmittance of the support is insufficient). At this time, when the cushion layer and the barrier layer are formed together with the support, exposure may be performed after the barrier layer is peeled off.

  At this time, when the support, the cushion layer, and the barrier layer have not been peeled yet, at least the support is peeled from the laminate (peeling step).

  Next, the uncured region of the photosensitive layer on the printed wiring board forming substrate is dissolved and removed with an appropriate developer to form a pattern of the cured layer for forming the wiring pattern and the cured layer for protecting the metal layer of the through hole. And a metal layer is exposed on the surface of the printed wiring board forming substrate (developing step).

  Moreover, you may perform the process which further accelerates | stimulates the hardening reaction of a hardening part by post-heat processing or post-exposure processing as needed after image development. The development may be a wet development method as described above or a dry development method.

  Next, the metal layer exposed on the surface of the printed wiring board forming substrate is dissolved and removed with an etching solution (etching step). Since the opening of the through hole is covered with a cured resin composition (tent film), the metal plating of the through hole is predetermined without etching liquid entering the through hole and corroding the metal plating in the through hole. It will remain in the shape. Thus, a wiring pattern is formed on the printed wiring board forming substrate.

  There is no restriction | limiting in particular as said etching liquid, Although it can select suitably according to the objective, For example, when the said metal layer is formed with copper, a cupric chloride solution, a ferric chloride solution , Alkaline etching solutions, hydrogen peroxide-based etching solutions, and the like. Among these, ferric chloride solutions are preferable from the viewpoint of etching factors.

Next, it removes from the said board | substrate for printed wiring board formation by making the said hardened layer into a peeling piece with strong alkaline aqueous solution etc. (hardened | cured material removal process).
There is no restriction | limiting in particular as a base component in the said strong alkali aqueous solution, For example, sodium hydroxide, potassium hydroxide, etc. are mentioned.
As pH of the said strong alkali aqueous solution, about 12-14 are preferable, for example, and about 13-14 are more preferable.
There is no restriction | limiting in particular as said strong alkali aqueous solution, For example, 1-10 mass% sodium hydroxide aqueous solution or potassium hydroxide aqueous solution etc. are mentioned.

The printed wiring board may be a multilayer printed wiring board.
The pattern forming material may be used not only for the above etching process but also for a plating process. Examples of the plating method include copper plating such as copper sulfate plating and copper pyrophosphate plating, solder plating such as high throw solder plating, watt bath (nickel sulfate-nickel chloride) plating, nickel plating such as nickel sulfamate, and hard gold plating. And gold plating such as soft gold plating.

  Since the pattern forming method and the pattern forming apparatus of the present invention use a pattern forming material that can suppress a decrease in sensitivity of the photosensitive layer and can form a high-definition pattern, exposure can be performed with light of a smaller energy amount. This is advantageous in that the processing speed is increased because the exposure speed is increased.

Since the pattern forming method of the present invention uses the pattern forming material of the present invention, it can be suitably used for manufacturing a printed wiring board, and can be particularly suitably used for forming a high-definition wiring pattern.
Since the pattern forming apparatus of the present invention includes the pattern forming material of the present invention, it can be suitably used for the production of printed wiring boards, and can be particularly suitably used for the formation of high-definition wiring patterns. .

  EXAMPLES Hereinafter, the present invention will be described more specifically with reference to examples, but the present invention is not limited thereto.

Example 1
A photosensitive resin composition solution A having the following composition was applied to a polyethylene terephthalate film having a thickness of 19 μm as the support and dried to form a photosensitive layer having a thickness of 15 μm, thereby producing the pattern forming material.

[Composition of Photosensitive Resin Composition Solution A]
Methyl methacrylate / styrene / ethyl acrylate / methacrylic acid copolymer (copolymer composition (mass ratio): 25/39/11/25, mass average molecular weight: 90,000, acid value 163) 15 parts by mass 7.0 parts by mass of polymerizable monomer represented by formula (105): 1/2 molar ratio adduct of hexamethylene diisocyanate and tetraethylene oxide monomethacrylate 7.0 parts by mass: 0.11 part by mass of N-methylacridone -2,2-bis (o-chlorophenyl) -4,4 ', 5,5'-tetraphenylbiimidazole 2.17 parts by mass-0.23 parts by mass of 2-mercaptobenzimidazole-Malachite green oxalate 0. 02 parts by mass-color former compound represented by the following structural formula (1) 0.26 parts by mass-methyl ethyl ketone 40 parts by mass
・ 20 parts by mass of 1-methoxy-2-propanol

However, m + n represents 10 in Structural Formula (105). Structural formula (105) is an example of a compound represented by structural formula (70).

-Manufacture of laminates-
A 20 μm thick polyethylene film was laminated as the protective film on the photosensitive layer of the pattern forming material. Next, as the substrate, the surface of the pattern-forming material is protected on the surface of a copper-clad laminate (Copper-clad laminate R-1701 for National Printed Wiring Board, manufactured by Matsushita Electric Works) whose surface has been polished, washed and dried. While peeling off the film, the pattern forming material was pressure-bonded using a laminator (MODEL8B-720-PH, manufactured by Taisei Laminator Co., Ltd.) so that the photosensitive layer of the pattern forming material was in contact with the copper-clad laminate. The pressure bonding conditions were a substrate temperature of 70 ° C., a pressure roll temperature of 105 ° C., a pressure roll pressure of 3 kg / cm ² , and a laminating speed of 1.2 m / min. After the lamination, the laminate was allowed to stand at room temperature (23 ° C., 55% RH) for 10 minutes to prepare a laminate in which the copper-clad laminate, the photosensitive layer, and the support were laminated in this order.
The manufactured laminate is evaluated by the following methods for resolution, etching property, color density after exposure, exposure speed, change in clear sensitivity (number of steps) by thermo test, and change in color density before exposure. It was. The results are shown in Table 3.

<Measurement of resolution>
(1) Measuring method of shortest development time The support is peeled off from the laminate, and a 1 mass% sodium carbonate aqueous solution at 30 ° C. is sprayed on the entire surface of the photosensitive layer on the copper clad laminate at a pressure of 0.15 MPa. The time required from the start of spraying of the aqueous sodium carbonate solution until the photosensitive layer on the copper clad laminate was dissolved and removed was measured, and this was taken as the shortest development time.
As a result, the shortest development time was 10 seconds.

(2) Sensitivity measurement method With respect to the photosensitive layer of the pattern forming material in the laminate, from the support side, using a pattern forming apparatus having a 405 nm laser light source as the light irradiation means, 0.1 mJ / cm ² And exposed to light having different light energy amounts up to 100 mJ / cm ^{2 at} intervals of 2 ^1/2 times to cure a part of the photosensitive layer. After standing at room temperature for 10 minutes, the support is peeled off from the laminate, and an aqueous sodium carbonate solution (30 ° C., 1% by mass) is sprayed on the entire surface of the photosensitive layer on the copper clad laminate at a pressure of 0.15 MPa. And sprayed for twice the shortest development time determined in (1) above, the uncured area was dissolved and removed, and the thickness of the remaining cured area was measured. Next, a sensitivity curve is obtained by plotting the relationship between the light irradiation amount and the thickness of the cured layer. From the sensitivity curve thus obtained, the amount of light energy when the thickness of the cured region was 15 μm was determined as the amount of light energy necessary for curing the photosensitive layer. As a result, the amount of light energy necessary for curing the photosensitive layer was 3 mJ / cm ² .
In the sensitivity measurement method, a step wedge (Fuji Step Guide P, manufactured by Fuji Photo Film Co., Ltd., step: 0.15, density step: 1 to 15 steps) is disposed on the support of the laminate. wherein the photosensitive layer, when exposed through the step wedge from the support side, the first stage step wedge 10 mJ / ^cm 2, 10 stage is an exposure condition corresponding to 1.78mJ / cm ^2.

(3) Method of measuring resolution The laminate was prepared and allowed to stand at room temperature (23 ° C., 55% RH) for 10 minutes. From the obtained polyethylene terephthalate film (support) of the laminate, using the pattern forming apparatus, line / space = 1/1 and line widths of 5 μm to 20 μm are exposed in 1 μm increments, and the line width is exposed. Each line width was exposed in steps of 5 μm from 20 μm to 50 μm. The exposure amount at this time is the amount of light energy necessary for curing the photosensitive layer of the pattern forming material measured in the sensitivity measurement. After standing at room temperature for 10 minutes, the polyethylene terephthalate film (support) was peeled off from the laminate. Twice the shortest development time obtained in (1) above with a sodium carbonate aqueous solution (30 ° C., 1% by mass) as the developer at a spray pressure of 0.15 MPa on the entire surface of the photosensitive layer on the copper clad laminate. The uncured area was dissolved and removed by spraying. The surface of the copper-clad laminate with the cured resin pattern thus obtained was observed with an optical microscope, and the minimum line width without any abnormalities such as tsumari and twisting was measured on the cured resin pattern line. did. The smaller the numerical value, the better the resolution.

<Etching property>
Using a laminate having a pattern formed in the resolution measurement, an iron chloride etchant (ferric chloride-containing etching solution, 40 ° Baume, liquid temperature 40 ° C. is formed on the exposed copper-clad laminate in the laminate. ) Was sprayed at 0.25 MPa for 36 seconds to dissolve and remove the exposed copper layer not covered with the hardened layer. Next, the formed pattern was removed by spraying a 2% by mass aqueous sodium hydroxide solution to prepare a printed wiring board having a copper layer wiring pattern on the surface as the permanent pattern. The wiring pattern on the printed wiring board was observed with an optical microscope, and the minimum line width of the wiring pattern was measured. A smaller minimum line width means that a finer wiring pattern can be obtained and the etching property is better.

<Color density after exposure>
Using a pattern forming apparatus having a 405 nm laser light source as the light irradiating means, the photosensitive layer of the pattern forming material in the laminate is exposed by irradiating with light of 10 mJ / cm ² , A part of the photosensitive layer was cured. After leaving still at room temperature for 10 minutes, the said support body was peeled off from the said laminated body, and the light absorbency in 600 nm was measured using UV spectrometer (the Shimadzu Corporation make, UV-2400). As a result, the absorbance at 600 nm was 0.35.

<Exposure speed>
Using the pattern forming apparatus, the speed at which the exposure light and the photosensitive layer were moved relative to each other was changed to obtain the speed at which a general wiring pattern was formed. The exposure was performed on the photosensitive layer of the pattern forming material in the prepared laminate from the support side. Note that efficient pattern formation is possible when the set speed is high.

<Change in clear sensitivity (number of steps) by thermo test>
A laminate is produced by the above method using the produced pattern forming material stored for 72 hours under a temperature condition of 60 ° C. and the pattern forming material immediately after the production, and for each laminated body, The clear sensitivity (number of steps) of the photosensitive layer was measured by the following method.

−Measurement of the number of clear steps−
Step wedges (Fuji Step Guide P, manufactured by Fuji Photo Film Co., Ltd., level difference: 0.15, density level difference: 1 to 15 levels) were arranged on the support of the laminate. The photosensitive layer is exposed by irradiating light of 40 mJ / cm ² through the step wedge from the support side using a pattern forming apparatus having a laser light source of 405 nm as the light irradiation means, and the photosensitive layer Some areas of were cured. After standing at room temperature for 10 minutes, the support was peeled off from the laminate, and a sodium carbonate aqueous solution (30 ° C., 1% by mass) was sprayed onto the entire surface of the photosensitive layer on the copper clad laminate at a spray pressure of 1.03 kg. The film was sprayed for 80 seconds at / cm ² to dissolve and remove uncured areas. After development, the minimum number of steps at which the photosensitive layer was completely dissolved was read to determine the clear sensitivity. As a result, the number of clear stages was 10 stages. In addition, it shows that the sensitivity fall during preservation | save is suppressed, so that the difference in the number of clear steps is small.

<Color density change before exposure by thermo test>
The produced pattern forming material was stored for 72 hours under a temperature condition of 60 ° C., and the pattern forming material immediately after the production, respectively, using a UV spectrometer (manufactured by Shimadzu Corporation, UV-2400). The absorbance at 600 nm of each photosensitive layer was measured.
After the production, the absorbance at 600 nm of the unprocessed pattern forming material was designated as A, and the absorbance of the photosensitive layer of the pattern forming material stored at 60 ° C. for 72 hours as B, and the value of B−A was determined. . As a result, the value of B-A was 0.04. In addition, it shows that the coloring by the oxidation of the color former compound during preservation | save is suppressed, so that the value of B-A is small.

(Example 2)
In Example 1, except that the color former compound represented by the structural formula (1) was changed to the color former compound represented by the following structural formula (6), a pattern forming material was obtained in the same manner as in Example 1. Manufactured.
About the manufactured pattern forming material, in the same manner as in Example 1, resolution, etching property, color density after exposure, exposure speed, change in clear sensitivity (number of steps) by thermo test, and change in color density before exposure Evaluation was performed. The results are shown in Table 3.

(Example 3)
In Example 1, except that the color former compound represented by the structural formula (1) was changed to the color former compound represented by the following structural formula (8), a pattern forming material was obtained in the same manner as in Example 1. Manufactured.
About the manufactured pattern forming material, in the same manner as in Example 1, resolution, etching property, color density after exposure, exposure speed, change in clear sensitivity (number of steps) by thermo test, and change in color density before exposure Evaluation was performed. The results are shown in Table 3.

Example 4
In Example 1, except that the color former compound represented by the structural formula (1) was changed to the color former compound represented by the following structural formula (20), a pattern forming material was obtained in the same manner as in Example 1. Manufactured.
About the manufactured pattern forming material, in the same manner as in Example 1, resolution, etching property, color density after exposure, exposure speed, change in clear sensitivity (number of steps) by thermo test, and change in color density before exposure Evaluation was performed. The results are shown in Table 3.

(Example 5)
In Example 1, except that the color former compound represented by the structural formula (1) was changed to the color former compound represented by the following structural formula (28), a pattern forming material was obtained in the same manner as in Example 1. Manufactured.
About the manufactured pattern forming material, in the same manner as in Example 1, resolution, etching property, color density after exposure, exposure speed, change in clear sensitivity (number of steps) by thermo test, and change in color density before exposure Evaluation was performed. The results are shown in Table 3.

(Comparative Example 1)
In Example 1, the same procedure as in Example 1 was conducted except that the color former compound represented by the structural formula (1) was changed to the color former compound (leuco crystal violet) represented by the following structural formula (106). Thus, a pattern forming material was manufactured.
About the manufactured pattern forming material, in the same manner as in Example 1, resolution, etching property, color density after exposure, exposure speed, change in clear sensitivity (number of steps) by thermo test, and change in color density before exposure Evaluation was performed. The results are shown in Table 3.

(Example 6)
In Example 1, a cushioning layer coating liquid having the following composition was applied on the support and dried to form a 15 μm cushioning layer. Then, the photosensitive resin having the following composition was formed on the cushioning layer. A pattern forming material was produced in the same manner as in Example 1 except that the photosensitive layer was formed by applying the composition solution B to 5 μm.
About the manufactured pattern forming material, the resolution, the etching property, the color density after exposure, the exposure speed, and the same as in Example 1 except that the exposure was performed with light having an energy amount of 1.5 mJ / cm ^2. Changes in clear sensitivity (number of steps) due to a thermo test and changes in color density before exposure were evaluated. The results are shown in Table 3.
In the exposure and development, the cushion layer was removed together with the support for processing.

[Composition of cushion layer coating solution]
・ Methyl methacrylate / 2-ethylhexyl acrylate / benzyl methacrylate /
Methacrylic acid copolymer (copolymerization composition (molar ratio): 55/10/5/30, mass average molecular weight: 100,000) 60 parts by mass Styrene / acrylic acid (copolymerization composition (molar ratio): 65/35 , Mass average molecular weight: 10,
000) 140 parts by mass. 2,2-bis (4- (methacryloyloxypentaethoxy) phenyl) propane (manufactured by Shin-Nakamura Chemical Co., Ltd., BPE-500) 150 parts by mass
・ 700 parts by mass of methyl ethyl ketone

[Composition of Photosensitive Resin Composition Solution B]
Methyl methacrylate / styrene / ethyl acrylate / methacrylic acid copolymer (copolymer composition (mass ratio): 25/39/11/25, mass average molecular weight: 90,000, acid value 163) 13 parts by mass 5 parts by mass of a polymerizable monomer represented by the formula (105) 5 parts by mass of an adduct of hexamethylene diisocyanate and tetramethylene oxide monomethacrylate 5 parts by mass N-methylacridone 0.4 parts by mass 2, 2-bis (o-chlorophenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole 1.3 parts by mass, 2-mercaptobenzimidazole 0.4 parts by mass, malachite green oxalate 0.02 parts by mass -0.2 parts by mass of the color former compound represented by the structural formula (1)-10 parts by mass of methyl ethyl ketone
・ 20 parts by mass of 1-methoxy-2-propanol

(Comparative Example 2)
In Example 6, the color former compound represented by the structural formula (1) of the photosensitive resin composition solution B was changed to the color former compound (leuco crystal violet) represented by the structural formula (106). A pattern forming material was manufactured in the same manner as in Example 6 except for the above.
The produced pattern forming material was exposed to light having an energy amount of 1.5 mJ / cm ^{2 in} the same manner as in Example 6, and the resolution, etching property, color density after exposure, exposure speed, and clear by thermo test. Changes in sensitivity (number of steps) and changes in color density before exposure were evaluated. The results are shown in Table 3.

(Example 7)
In Example 6, a barrier layer coating solution having the following composition was applied onto the cushion layer and dried to form a 1.6 μm barrier layer. The photosensitive resin composition solution was formed on the barrier layer. A pattern forming material was produced in the same manner as in Example 6 except that the photosensitive layer was formed by applying B to a thickness of 5 μm. About the manufactured pattern forming material, in the same manner as in Example 1, resolution, etching property, color density after exposure, exposure speed, change in clear sensitivity (number of steps) by thermo test, and change in color density before exposure Evaluation was performed. The results are shown in Table 3.
Note that the cushion layer and the barrier layer were removed together with the support during the exposure and development.

[Composition of coating solution for barrier layer]
Polyvinyl alcohol (Kuraray Co., PVA205) 13 parts by mass Polyvinylpyrrolidone (ISP Co., K-30) 6 parts by mass Water 200 parts by mass
・ Methanol 180 parts by mass

(Comparative Example 3)
In Example 7, the color former compound represented by the structural formula (1) of the photosensitive resin composition solution B was changed to the color former compound (leuco crystal violet) represented by the structural formula (106). Except for the above, a pattern forming material was produced in the same manner as in Example 7.
About the manufactured pattern forming material, in the same manner as in Example 1, resolution, etching property, color density after exposure, exposure speed, change in clear sensitivity (number of steps) by thermo test, and change in color density before exposure Evaluation was performed. The results are shown in Table 3.

(Example 8)
In Example 1, a photosensitive resin composition solution obtained by removing the color former compound represented by the structural formula (1) from the photosensitive resin composition solution A was applied and dried to form a first layer having a thickness of 25 μm. (First photosensitive layer) is formed, and the barrier layer coating solution is applied onto the first layer (first photosensitive layer) and dried to form a 1.6 μm barrier layer. The photosensitive resin composition solution B was applied on the layer so as to have a thickness of 5 μm and dried to form a second layer (second photosensitive layer) having a thickness of 5 μm. Thus, a pattern forming material was manufactured.
About the manufactured pattern forming material, the resolution, the etching property, the color density after exposure, the exposure speed, and the same as in Example 1 except that the exposure was performed with light having an energy amount of 2.0 mJ / cm ^2. Changes in clear sensitivity (number of steps) due to a thermo test and changes in color density before exposure were evaluated. The results are shown in Table 3.

(Comparative Example 4)
In Example 8, the color former compound represented by the structural formula (1) of the photosensitive resin composition solution B was changed to the color former compound (leuco crystal violet) represented by the structural formula (106). A pattern forming material was manufactured in the same manner as Example 8 except for the above.
The produced pattern forming material was exposed to light with an energy amount of 2.0 mJ / cm ^{2 in} the same manner as in Example 8, and the resolution, etching property, color density after exposure, exposure speed, and clear by thermo test. Changes in sensitivity (number of steps) and changes in color density before exposure were evaluated. The results are shown in Table 3.

Example 9
In Example 1, except that the pattern forming apparatus was replaced with the pattern forming apparatus described below, the resolution, etching property, color density after exposure, exposure speed, and clear sensitivity by thermo test ( The change in the number of stages) and the change in color density before exposure were evaluated. The results are shown in Table 3.

<< Pattern Forming Apparatus >>
27 to 32 as the light irradiating means, and 768 pairs of micromirror arrays in which 1024 micromirrors are arranged in the main scanning direction shown in FIG. 4 as the light modulating means are arranged in the sub-scanning direction. The microlens array 472 in which the DMD 50 controlled to drive only 1024 × 256 rows and the microlenses 474 whose one surface is a toric surface shown in FIG. A pattern forming apparatus having optical systems 480 and 482 for imaging light passing through the array onto the pattern forming material was used. The DMD 50 is connected to the controller 302 including the data processing unit and the mirror drive control unit shown in FIG. Based on the input pattern information, the data processing unit of the controller 302 can generate a control signal for driving and controlling each micromirror in the region to be controlled by the DMD 50 for each exposure head 166. The drive control unit can control the angle of the reflection surface of each micromirror of the DMD 50 for each exposure head 166 based on the control signal generated by the pattern information processing unit.
The exposure in the pattern forming apparatus was performed while relatively moving the exposure light and the photosensitive layer in the pattern forming material.

The toric surface of the microlens described below was used.
First, in order to correct the distortion on the exit surface of the microlens 474 as the picture element portion of the DMD 50, the strain on the exit surface was measured. The results are shown in FIG. In FIG. 14, the same height positions of the reflecting surfaces are shown connected by contour lines, and the pitch of the contour lines is 5 nm. Note that the x direction and the y direction shown in the figure are two diagonal directions of the micromirror 62, and the micromirror 62 rotates around a rotation axis extending in the y direction. 15A and 15B show the height position displacement of the reflecting surface of the micromirror 62 along the x direction and the y direction, respectively.

  As shown in FIGS. 14 and 15, there is distortion on the reflection surface of the micromirror 62, and when attention is paid particularly to the center of the mirror, distortion in one diagonal direction (y direction) is different from that in the other diagonal line. It can be seen that the distortion is larger than the distortion in the direction (x direction). Therefore, it can be seen that the shape of the laser beam B collected by the microlens 55a of the microlens array 55 is distorted in this state.

  FIGS. 16A and 16B show the front shape and the side shape of the entire microlens array 55 in detail. In these drawings, the dimensions of each part of the microlens array 55 are also entered, and the unit thereof is mm. As described above with reference to FIG. 4, the 1024 × 256 micromirrors 62 of the DMD 50 are driven. Correspondingly, the microlens array 55 has 1024 microlenses arranged in the horizontal direction. The 55a rows are arranged in parallel in 256 rows in the vertical direction. In FIG. 9A, the arrangement order of the microlens array 55 is indicated by j in the horizontal direction and k in the vertical direction.

  17A and 17B show a front shape and a side shape of one microlens 55a in the microlens array 55, respectively. In FIG. 9A, the contour lines of the micro lens 55a are also shown. The end surface of each microlens 55a on the light emitting side has an aspherical shape that corrects aberration due to distortion of the reflecting surface of the micromirror 62. More specifically, the micro lens 55a is a toric lens, and has a radius of curvature Rx = −0.125 mm in a direction optically corresponding to the x direction and a radius of curvature Ry = − in a direction corresponding to the y direction. 0.1 mm.

  Therefore, the condensing state of the laser beam B in the cross section parallel to the x direction and the y direction is roughly as shown in FIGS. 18A and 18B, respectively. That is, when the cross section parallel to the x direction is compared with the cross section parallel to the y direction, the radius of curvature of the microlens 55a is smaller and the focal length is shorter in the latter cross section. I understand that.

  19A, 19B, 19C, and 19D show simulation results of the beam diameter in the vicinity of the condensing position (focal position) of the microlens 55a when the microlens 55a has the above shape. For comparison, FIGS. 20a, 20b, 20c, and 20d show the results of a similar simulation when the microlens 55a has a spherical shape with a radius of curvature Rx = Ry = −0.1 mm. In addition, the value of z in each figure has shown the evaluation position of the focus direction of the micro lens 55a with the distance from the beam emission surface of the micro lens 55a.

The surface shape of the microlens 55a used for the simulation is calculated by the following calculation formula.

  In the above formula, Cx means the curvature in the x direction (= 1 / Rx), Cy means the curvature in the y direction (= 1 / Ry), and X is the lens optical axis in the x direction. The distance from O means Y, and Y means the distance from the lens optical axis O in the y direction.

  As is apparent when comparing FIGS. 19a to 19d and FIGS. 20a to 20d, the microlens 55a includes a toric lens in which the focal length in the cross section parallel to the y direction is smaller than the focal length in the cross section parallel to the x direction. As a result, distortion of the beam shape in the vicinity of the condensing position is suppressed. As a result, the pattern forming material 150 can be exposed to a higher definition pattern without distortion. Moreover, it turns out that the area | region where a beam diameter is small is wider, ie, the depth of focus is larger in this embodiment shown to FIG.

  In addition, the aperture array 59 disposed in the vicinity of the condensing position of the microlens array 55 is disposed such that only light having passed through the corresponding microlens 55a is incident on each aperture 59a. That is, by providing this aperture array 59, it is possible to prevent light from adjacent microlenses 55a not corresponding to each aperture 59a from entering, and to increase the extinction ratio.

(Example 10)
In Example 2, except that the pattern forming apparatus was replaced with the pattern forming apparatus described below, the resolution, etching property, color density after exposure, exposure speed, and clear sensitivity by thermotest ( The change in the number of stages) and the change in color density before exposure were evaluated. The results are shown in Table 3.

(Example 11)
In Example 3, except that the pattern forming apparatus was replaced with the pattern forming apparatus described below, the resolution, the etching property, the color density after exposure, the exposure speed, and the clear sensitivity by thermo test ( The change in the number of stages) and the change in color density before exposure were evaluated. The results are shown in Table 3.

From the results of Table 3, the structural formulas (1), (6), which are triarylmethane dyes having a substituted amino group at the 4-position and having at least one substituent at the ortho-position to the carbon atom of methane, The pattern forming materials of Examples 1 to 11 using the color former compounds of (8), (20), and (28) are suppressed in coloring and sensitivity reduction even after being stored under high temperature and high humidity, In addition, it was found that the exposure area is excellent in the visible image due to good color developability at the time of exposure.
In Examples 9 to 11, since a pattern forming apparatus capable of high-speed modulation with a high-intensity light source and capable of correcting optical system distortion by a toric lens was used, it was recognized that the resolution and exposure speed were excellent, and high-definition It was confirmed that a permanent pattern was formed.

  The pattern-forming material of the present invention is capable of forming various patterns because it suppresses storability coloring and sensitivity reduction, and is excellent in visualizing exposed areas due to good color development during exposure and excellent in sensitivity stability. It can be used suitably for the formation of permanent patterns such as wiring patterns, color filters, pillar materials, rib materials, spacers, production of liquid crystal structural members such as partition walls, holograms, micromachines, proofs, etc. It can be suitably used for forming a wiring pattern. Since the pattern forming apparatus of the present invention includes the pattern forming material of the present invention, it forms various patterns, forms permanent patterns such as wiring patterns, color filters, column materials, rib materials, spacers, partition walls, and other liquid crystals. It can be suitably used for the production of structural members, the production of holograms, micromachines, proofs, etc., and can be particularly suitably used for the formation of high-definition wiring patterns. Since the pattern forming method of the present invention uses the pattern forming material of the present invention, liquid crystal structural members such as various patterns, permanent patterns such as wiring patterns, color filters, pillar materials, rib materials, spacers, partition walls, etc. It can be suitably used for the manufacture of holograms, micromachines, proofs, etc., and can be particularly suitably used for the formation of high-definition wiring patterns.

FIG. 1 is an example of a partially enlarged view showing a configuration of a digital micromirror device (DMD). 2A and 2B are examples of explanatory diagrams for explaining the operation of the DMD. FIGS. 3A and 3B are examples of plan views showing the arrangement of the exposure beam and the scanning line in a case where the DMD is not inclined and in a case where the DMD is inclined. 4A and 4B are examples of diagrams illustrating examples of DMD usage areas. FIG. 5 is an example of a plan view for explaining an exposure method in which the pattern forming material is exposed by one scanning by the scanner. 6A and 6B are examples of plan views for explaining an exposure method for exposing a pattern forming material by a plurality of scans by a scanner. FIG. 7 is an example of a schematic perspective view illustrating an appearance of an example of the pattern forming apparatus. FIG. 8 is an example of a schematic perspective view illustrating the configuration of the scanner of the pattern forming apparatus. FIG. 9A is an example of a plan view showing an exposed region formed in the pattern forming material, and FIG. 9B is an example of a diagram showing an array of exposure areas by each exposure head. FIG. 10 is an example of a perspective view showing a schematic configuration of an exposure head including light modulation means. FIG. 11 is an example of a sectional view in the sub-scanning direction along the optical axis showing the configuration of the exposure head shown in FIG. FIG. 12 is an example of a controller that controls DMD based on pattern information. FIG. 13A is an example of a cross-sectional view along the optical axis showing the configuration of another exposure head having a different coupling optical system, and FIG. 13B shows the exposure when a microlens array or the like is not used. FIG. 13C is an example of a plan view showing a light image projected on the surface to be exposed when a microlens array or the like is used. FIG. 14 is an example of a diagram showing the distortion of the reflection surface of the micromirror constituting the DMD with contour lines. FIG. 15 is an example of a graph showing distortion of the reflection surface of the micromirror in two diagonal directions of the mirror. FIG. 16 is an example of a front view (A) and a side view (B) of a microlens array used in the pattern forming apparatus. FIG. 17 is an example of a front view (A) and a side view (B) of the microlens constituting the microlens array. FIG. 18 is an example of a schematic diagram illustrating a condensing state by a microlens in one cross section (A) and another cross section (B). FIG. 19a is an example of a diagram showing the result of simulating the beam diameter in the vicinity of the condensing position of the microlens of the present invention. FIG. 19B is an example of a diagram showing the same simulation result as that in FIG. 19A at another position. FIG. 19c is an example of a diagram showing the same simulation result as in FIG. 19a at another position. FIG. 19d is an example of a diagram showing the same simulation result as in FIG. 19a at another position. FIG. 20a is an example of a diagram showing the result of simulating the beam diameter in the vicinity of the condensing position of the microlens in the conventional pattern forming method. FIG. 20b is an example of a diagram showing the same simulation result as in FIG. 20a at another position. FIG. 20c is an example of a diagram showing the same simulation result as in FIG. 20a for another position. FIG. 20d is an example of a diagram illustrating simulation results similar to those in FIG. 20a at different positions. FIG. 21 is an example of a plan view showing another configuration of the combined laser light source. FIG. 22 shows an example of a front view (A) and an example of a side view (B) of the microlens constituting the microlens array. FIG. 23 is an example of a schematic diagram illustrating a light condensing state by the microlens of FIG. 22 in one cross section (A) and another cross section (B). FIG. 24 is an example of an explanatory diagram about the concept of correction by the light amount distribution correction optical system. FIG. 25 is an example of a graph showing the light amount distribution when the light irradiation means has a Gaussian distribution and the light amount distribution is not corrected. FIG. 26 is an example of a graph showing the light amount distribution after correction by the light amount distribution correcting optical system. 27A (A) is a perspective view showing the configuration of the fiber array light source, FIG. 27A (B) is an example of a partially enlarged view of (A), and FIGS. 27A (C) and (D) are lasers. It is an example of the top view which shows the arrangement | sequence of the light emission point in an emission part. FIG. 27 b is an example of a front view showing the arrangement of light emitting points in the laser emission part of the fiber array light source. FIG. 28 is an example of a diagram illustrating a configuration of a multimode optical fiber. FIG. 29 is an example of a plan view showing the configuration of the combined laser light source. FIG. 30 is an example of a plan view showing the configuration of the laser module. FIG. 31 is an example of a side view showing the configuration of the laser module shown in FIG. 32 is a partial side view showing the configuration of the laser module shown in FIG. FIG. 33 is an example of a perspective view showing a configuration of a laser array. FIG. 34A is an example of a perspective view showing a configuration of a multi-cavity laser, and FIG. 34B is a perspective view of a multi-cavity laser array in which the multi-cavity lasers shown in FIG. It is an example. FIG. 35 is an example of a plan view showing another configuration of the combined laser light source. FIG. 36A is an example of a plan view illustrating another configuration of the combined laser light source, and FIG. 36B is an example of a cross-sectional view along the optical axis of FIG. FIGS. 37A and 37B are examples of cross-sectional views along the optical axis showing the difference between the depth of focus in the conventional exposure apparatus and the depth of focus by the pattern forming method (pattern forming apparatus) of the present invention.

Explanation of symbols

LD1-LD7 GaN-based semiconductor laser 10 Heat block 11-17 Collimator lens 20 Condensing lens 30-31 Multimode optical fiber 44 Collimator lens holder 45 Condensing lens holder 46 Fiber holder 50 Digital micromirror device (DMD)
52 Lens system 53 Reflected light image (exposure beam)
54 Lens of second imaging optical system 55 Micro lens array 55a Micro lens 56 Surface to be exposed (scanning surface)
57 Lens of second imaging optical system 58 Lens of second imaging optical system 59 Aperture array 64 Laser module 66 Fiber array light source 67 Lens system 68 Laser emitting unit 69 Mirror 70 Prism 71 Condensing lens 72 Rod integrator 73 Combination lens 74 Imaging lens 100 Heat block 110 Multi cavity laser 111 Heat block 113 Rod lens 120 Condensing lens 130 Multimode optical fiber 130a Core 140 Laser array 144 Light irradiation means 150 Pattern forming material 152 Stage 155a Micro lens 156 Installation table 158 Guide 160 Gate 162 Scanner 164 Sensor 166 Exposure head 168 Exposure area 170 Exposed area 180 Heat block 184 Collimating lens Ray 302 controller 304 stage driver 454 lens system 468 exposure area 472 microlens array 474 microlens 476 aperture array 478 aperture 480 lens system

Claims (15)

  The support has at least a photosensitive layer, and the absorbance of the unexposed photosensitive layer with respect to light of 600 nm is B after the treatment for 72 hours under the temperature condition of 60 ° C., and the absorbance before the treatment is A. A pattern forming material satisfying a relationship of B−A ≦ 0.1. The pattern forming material according to claim 1, wherein the photosensitive layer contains at least a binder, a polymerizable compound, a photopolymerization initiator, and a color former compound represented by the following structural formula (I).
However, in said structural formula (I), R < ₁ >, R < ₂ >, R < ₃ >, R < ₄ >, R < ₅ >, and R < ₆ > represent either the alkyl group and aryl group which may have a substituent,
Any pair of R ₁ and R ₂ , R ₃ and R ₄ , and R ₅ and R ₆ may form a saturated 5- to 8-membered ring together with the nitrogen atom to be bonded,
R ₇ , R ₈ and R _{9 each} represent a hydrogen atom, an alkyl group, an alkyloxy group, an alkylthio group, an alkyloxycarbonyl group, an acylamino group, or a hydroxy group, and R ₇ , R ₈ and R ₉ At least one represents any of an alkyl group, an alkyloxy group, an alkylthio group, an alkyloxycarbonyl group, an acylamino group, and a hydroxy group. In Structural Formula (I), any one of R ₇ , R ₈ , and R ₉ is any one of an alkyl group, an alkyloxy group, an alkylthio group, an alkyloxycarbonyl group, an acylamino group, and a hydroxy group; The pattern forming material according to claim 2, wherein two are hydrogen atoms.   The pattern forming material according to claim 2, wherein the photosensitive layer contains 0.01 to 20% by mass of a color former compound represented by Structural Formula (I).   The pattern forming material according to claim 1, further comprising a cushion layer and a photosensitive layer in this order on the support.   The pattern forming material according to any one of claims 1 to 5, further comprising a cushion layer, a barrier layer capable of suppressing movement of a substance, and a photosensitive layer in this order on the support.   The pattern forming material according to claim 1, comprising a plurality of photosensitive layers having relatively different photosensitivities on the support. The pattern forming material according to claim 1 is provided,
A pattern forming apparatus comprising: a light irradiating means capable of irradiating light; and a light modulating means for modulating light from the light irradiating means and exposing the photosensitive layer in the pattern forming material.   8. A pattern forming method comprising at least exposing the photosensitive layer in the pattern forming material according to claim 1 to exposure.   The pattern forming method according to claim 9, wherein the pattern forming material is laminated on the substrate while being heated and pressurized and exposed.   The exposure is performed by modulating light from the light irradiating means by light modulating means having n picture elements for receiving and emitting light from the light irradiating means, and then aberration due to distortion of the exit surface in the picture element. The pattern forming method according to claim 9, wherein the pattern forming method includes at least a microlens array in which microlenses having an aspheric surface capable of correcting the above are arranged.   The pattern forming method according to claim 11, wherein the aspherical surface is a toric surface.   The pattern forming method according to claim 9, wherein the photosensitive layer is developed after the exposure.   The pattern forming method according to claim 9, wherein a permanent pattern is formed after the development. The pattern forming method according to claim 14, wherein the permanent pattern is a wiring pattern, and the permanent pattern is formed by at least one of an etching process and a plating process.