JP2006206791A - Stripping and cleaning agent for fixtures for painting and pretreatment and cleaning method of fixtures for painting using the agent - Google Patents
Stripping and cleaning agent for fixtures for painting and pretreatment and cleaning method of fixtures for painting using the agent Download PDFInfo
- Publication number
- JP2006206791A JP2006206791A JP2005022624A JP2005022624A JP2006206791A JP 2006206791 A JP2006206791 A JP 2006206791A JP 2005022624 A JP2005022624 A JP 2005022624A JP 2005022624 A JP2005022624 A JP 2005022624A JP 2006206791 A JP2006206791 A JP 2006206791A
- Authority
- JP
- Japan
- Prior art keywords
- coating
- water
- cleaning agent
- cleaning
- peeling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、塗装用治具類の剥離洗浄剤、並びに塗装用治具類の前処理方法及び洗浄方法に関し、より詳しくは、塗装工程において使用される固定治具、マスク治具等の塗装用治具類に付着した塗料を剥離させて洗浄する洗浄方法に用いるための塗装用治具類の剥離洗浄剤、並びに、その剥離洗浄剤を用いた塗装用治具類の前処理方法及び洗浄方法に関する。 The present invention relates to a peeling cleaning agent for coating jigs, and a pretreatment method and a cleaning method for coating jigs, and more specifically, for coating fixed jigs, mask jigs, and the like used in a coating process. Stripping cleaning agent for coating jigs for use in a cleaning method for peeling and cleaning paint adhering to jigs, and a pretreatment method and a cleaning method for coating jigs using the stripping cleaning agent About.
塗装工程において使用される固定治具は、被塗装品を固定するために用いられる治具であり、金属等の材料を使用して形作られた治具である。また、塗装工程において使用されるマスク治具は、被塗装品の所望する領域だけに塗料を付着させるために塗装部位の形状に対応させて形作られた治具であり、塗装部位以外の部分を被覆するようにし、塗料が不必要な部位に付着しないようにするために用いられるものである。そのため、このような塗装用治具類は塗装工程において被塗装品と共に塗料が付着してしまうことが避けられないものであり、かかる塗装用治具類を繰り返し使用するために、従来より剥離洗浄剤を用いて塗装用治具類に付着した塗料の除去と洗浄が行われてきている。 The fixing jig used in the painting process is a jig used to fix the article to be coated, and is a jig formed using a material such as metal. In addition, the mask jig used in the painting process is a jig that is formed to correspond to the shape of the painting part in order to attach the paint only to the desired region of the article to be painted. It is used for covering and preventing the paint from adhering to unnecessary parts. For this reason, it is inevitable that such coating jigs adhere to the product to be coated in the painting process, and in order to use such coating jigs repeatedly, it is more difficult to remove and clean. Removal and cleaning of the paint adhering to the coating jigs have been performed using an agent.
このような塗装治具類の洗浄方法としては、有機塩素系溶剤であるジクロロメタン（塩化メチレン）やトリクレン等の有機溶剤中に塗装用治具類を浸漬させて付着した塗料を溶解し除去する方法、または、これらの溶剤に水酸化ナトリウム等のアルカリを添加して併用することで付着した塗料を溶解し除去する方法等が挙げられる。 As a cleaning method for such coating jigs, a method for dissolving and removing the coating material by immersing the coating jigs in an organic solvent such as dichloromethane (methylene chloride) or trichlene, which is an organic chlorine solvent. Alternatively, a method of dissolving and removing the paint attached by adding an alkali such as sodium hydroxide to these solvents and using them together may be used.
しかしながら、前述のような有機溶剤を使用する方法においては、ジクロロメタンが発ガン性物質であることが指摘されていること、有機塩素系溶剤による作業者への健康面への影響、更には、土壌汚染、オゾン層破壊、地球温暖化等の環境問題という点で問題があった。また、前述のような有機溶剤を使用する方法においては、塗装用治具類から剥離された塗料が溶剤中に溶解し、その溶解した塗料が塗装用治具類に再付着して洗浄力が低下することから、洗浄液の交換を比較的頻繁に、且つ定期的に行わなければならなかった。このため、作業効率が低下すること、有機溶剤の新液を大量に追加しなければならないこと、塗料が溶解した溶剤を処理するために必要なコストが生じること等からトータルランニングコストが高くなるという問題もあった。更に、非ハロゲン系の引火し易い溶剤を使用する場合には、火災にも留意する必要があり、防爆設備等の導入も必要となるという問題があった。 However, in the method using an organic solvent as described above, it has been pointed out that dichloromethane is a carcinogenic substance, the effect of organic chlorinated solvents on the health of workers, and further, soil There were problems with environmental issues such as pollution, ozone depletion, and global warming. Further, in the method using the organic solvent as described above, the paint peeled off from the coating jig is dissolved in the solvent, and the dissolved paint is reattached to the coating jig and has a cleaning power. Since it decreased, the cleaning liquid had to be replaced relatively frequently and periodically. For this reason, the total running cost will increase due to the reduction in work efficiency, the need to add a large amount of a new organic solvent, and the cost required to treat the solvent in which the paint is dissolved. There was also a problem. Furthermore, when using a non-halogen flammable solvent, there is a problem that it is necessary to pay attention to a fire, and it is necessary to introduce explosion-proof equipment.
このような問題を解決するために、特開平６−２６２１０６号公報（特許文献１）においては、マスク治具の表面にフッ素樹脂をコーティングして塗料の密着性を低下させることによって、付着した塗料の剥離を容易にし、溶剤を用いて完全に除去する方法が開示されている。しかしながら、このような特許文献１に記載の方法においては、塗料を剥離させる際に溶剤を使用するため、上記の廃溶剤の処理や作業環境の問題点が懸念されていた。 In order to solve such a problem, in JP-A-6-262106 (Patent Document 1), the surface of a mask jig is coated with a fluororesin to reduce the adhesion of the paint, thereby adhering paint. A method of facilitating peeling of the film and completely removing it using a solvent is disclosed. However, in such a method described in Patent Document 1, since a solvent is used when the paint is peeled off, there are concerns about the treatment of the waste solvent and problems in the working environment.
また、特開２００１−１０４８９５号公報（特許文献２）においては、グルコン酸ナトリウム、ポリアクリル酸ナトリウム、リン酸ナトリウムから構成された界面活性剤を溶解した水系の洗浄液をマスク治具に吹き付けて、前記マスク治具の表面に前記界面活性剤膜を形成する剥離膜形成工程と、塗装工程の後に、前記洗浄液を塗料が付着したマスク治具に吹き付けて、付着した塗料を前記界面活性剤膜とともに洗い落とす洗浄工程とを含むマスク治具の洗浄方法が開示されている。更に、特開２００２−１５９９２３号公報（特許文献３）においては、マスキング塗装により塗膜が付着された塗装用マスクに、ポリアクリル酸ナトリウム、グルコン酸ナトリウム、リン酸ナトリウムおよびホウ酸ナトリウムを含む加温された水性洗浄液を噴射して前記マスク表面の塗膜を剥離除去するマスクの塗装用洗浄方法が開示されている。しかしながら、このような特許文献２及び３に記載の水系の洗浄剤を用いるマスク治具の洗浄方法においては、マスク治具に付着した塗料の剥離洗浄性の向上に限界があり、未だ十分なものではなかった。
本発明は、上記従来技術の有する課題に鑑みてなされたものであり、前記従来の有機溶剤系の剥離洗浄剤の有する課題を解決できる水系の剥離洗浄剤であって、べたつきがない均一且つ緻密な水不溶性無機化合物の付着層を形成することができ、高水準の剥離洗浄性を達成することが可能な塗装用治具類の剥離洗浄剤、並びに、その剥離洗浄剤を用いた塗装用治具類の前処理方法及び洗浄方法を提供することを目的とする。 The present invention has been made in view of the above-described problems of the prior art, and is a water-based stripping cleaning agent that can solve the problems of the conventional organic solvent-based stripping cleaning agent, and is uniform and dense without stickiness. A water-insoluble inorganic compound adhesion layer that can form a high level of delamination cleaning properties, and a coating cleaning agent that can achieve a high level of delamination cleaning properties, and a coating treatment that uses the delamination cleaning agent. The object is to provide a pre-treatment method and a cleaning method for equipment.
本発明者らは、上記目的を達成すべく鋭意研究を重ねた結果、剥離洗浄剤の成分として水不溶性無機化合物を用いることにより、べたつきがない均一且つ緻密な水不溶性無機化合物の付着層を形成することができ、高水準の剥離洗浄性を達成することが可能な剥離洗浄剤が得られることを見出し、この知見に基づき本発明を完成させた。 As a result of intensive studies to achieve the above object, the present inventors have formed a uniform and dense water-insoluble inorganic compound adhesion layer without stickiness by using a water-insoluble inorganic compound as a component of a peeling cleaning agent. The present invention was completed based on this finding, and it was found that a release cleaning agent capable of achieving a high level of release cleaning performance can be obtained.
すなわち、本発明の塗装用治具類の剥離洗浄剤は、被塗装品を塗装またはマスク塗装する際に用いた塗装用治具類に付着した塗料を剥離させて洗浄する洗浄方法に用いるための塗装用治具類の剥離洗浄剤において、水不溶性無機化合物と水とを含有することを特徴とするものである。 That is, the stripping cleaning agent for the coating jigs of the present invention is used for a cleaning method for stripping and cleaning the paint adhering to the coating jigs used when painting or mask coating the article to be coated. The stripping cleaning agent for coating jigs contains a water-insoluble inorganic compound and water.
上記本発明にかかる前記水不溶性無機化合物としては、珪酸化合物、金属酸化物またはカルシウム化合物であることが好ましく、また、前記珪酸化合物が鉱産物であることがより好ましい。 The water-insoluble inorganic compound according to the present invention is preferably a silicate compound, a metal oxide, or a calcium compound, and more preferably the silicate compound is a mineral product.
上記本発明の塗装用治具類の剥離洗浄剤としては、高分子系分散剤を更に含有することが好ましく、また、前記高分子系分散剤の含有量が０．００１〜１０質量％であることがより好ましい。 As the peeling cleaning agent for the above-mentioned coating jigs of the present invention, it is preferable to further contain a polymer dispersant, and the content of the polymer dispersant is 0.001 to 10% by mass. It is more preferable.
上記本発明の塗装用治具類の剥離洗浄剤としては、非イオン界面活性剤及びアニオン界面活性剤からなる群から選択される少なくとも１種の界面活性剤を更に含有することが好ましく、また、前記界面活性剤の含有量が０．００５〜１０質量％であることがより好ましい。 As the peeling cleaning agent for the above-mentioned coating jigs of the present invention, it is preferable to further contain at least one surfactant selected from the group consisting of a nonionic surfactant and an anionic surfactant, It is more preferable that the content of the surfactant is 0.005 to 10% by mass.
上記本発明の塗装用治具類の剥離洗浄剤としては、水溶性高分子を更に含有することが好ましく、また、前記水溶性高分子がポリビニルアルコールであることがより好ましい。 As a peeling cleaning agent for the above-mentioned coating jigs of the present invention, it is preferable to further contain a water-soluble polymer, and it is more preferable that the water-soluble polymer is polyvinyl alcohol.
本発明の塗装治具類の前処理方法は、被塗装品を塗装またはマスク塗装する際に用いる塗装用治具類の表面に前記剥離洗浄剤を供給し、水不溶性無機化合物の付着層を形成させることを特徴とする方法である。 The pre-treatment method for coating jigs according to the present invention is to supply the above-mentioned peeling cleaning agent to the surface of the coating jigs used when painting or mask coating the article to be coated, thereby forming a water-insoluble inorganic compound adhesion layer. It is the method characterized by making it carry out.
また、本発明の塗装用治具類の洗浄方法は、被塗装品を塗装またはマスク塗装する際に用いた塗装用治具類に付着した塗料を剥離させて洗浄する洗浄方法であって、前記塗装治具類が、前記剥離洗浄剤により形成された水不溶性無機化合物の付着層を有するものであることを特徴とする方法である。 Further, the cleaning method of the coating jigs of the present invention is a cleaning method of peeling and cleaning the paint adhering to the coating jigs used when coating or mask coating the article to be coated, The coating jig is a method having an adhesion layer of a water-insoluble inorganic compound formed by the peeling cleaning agent.
本発明によれば、前記従来の有機溶剤系の剥離洗浄剤の有する課題を解決できる水系の剥離洗浄剤であって、べたつきがない均一且つ緻密な水不溶性無機化合物の付着層を形成することができ、高水準の剥離洗浄性を達成することが可能な塗装用治具類の剥離洗浄剤、並びに、その剥離洗浄剤を用いた塗装用治具類の前処理方法及び洗浄方法を提供することが可能となる。 According to the present invention, a water-based stripping cleaning agent that can solve the problems of the conventional organic solvent-based stripping cleaning agent can form a uniform and dense water-insoluble inorganic compound adhesion layer without stickiness. A stripping cleaning agent for coating jigs capable of achieving a high level of stripping cleaning performance, and a pretreatment method and a cleaning method for coating jigs using the stripping cleaning agent are provided. Is possible.
以下、本発明をその好適な実施形態に即して詳細に説明する。 Hereinafter, the present invention will be described in detail with reference to preferred embodiments thereof.
先ず、本発明の塗装用治具類の剥離洗浄剤について説明する。すなわち、本発明の塗装用治具類の剥離洗浄剤は、被塗装品を塗装またはマスク塗装する際に用いた塗装用治具類に付着した塗料を剥離させて洗浄する洗浄方法に用いるための塗装用治具類の剥離洗浄剤において、水不溶性無機化合物と水とを含有することを特徴とするものである。 First, the peeling cleaning agent for the coating jigs of the present invention will be described. That is, the stripping cleaning agent for the coating jigs of the present invention is used for a cleaning method for stripping and cleaning the paint adhering to the coating jigs used when painting or mask coating the article to be coated. The stripping cleaning agent for coating jigs contains a water-insoluble inorganic compound and water.
本発明にかかる水不溶性無機化合物は、２５℃以下の温度条件下において水に対する溶解度が１質量％以下の無機化合物である。このような水不溶性無機化合物としては、剥離洗浄性の向上という観点から、珪酸化合物、金属酸化物又はカルシウム化合物を用いることが好ましい。また、前記珪酸化合物としては、例えば、カオリン、活性白土、ケイ砂、ケイソウ土、タルク、パーライト、ベントナイト等の鉱産物を用いることが好ましく、前記金属酸化物としては、例えば、酸化チタン、酸化アルミニウム等を用いることが好ましく、前記カルシウム化合物としては、例えば、炭酸カルシウム、硫酸カルシウムを用いることが好ましい。また、このような水不溶性無機化合物は、１種を単独で用いることができ、または２種以上を混合して用いることもできる。 The water-insoluble inorganic compound according to the present invention is an inorganic compound having a solubility in water of 1% by mass or less under a temperature condition of 25 ° C. or less. As such a water-insoluble inorganic compound, it is preferable to use a silicic acid compound, a metal oxide, or a calcium compound from the viewpoint of improving the peelability. Further, as the silicic acid compound, it is preferable to use mineral products such as kaolin, activated clay, silica sand, diatomaceous earth, talc, perlite, bentonite and the like, and examples of the metal oxide include titanium oxide and aluminum oxide. It is preferable to use, for example, calcium carbonate and calcium sulfate as the calcium compound. Moreover, such a water-insoluble inorganic compound can be used individually by 1 type, or can also be used in mixture of 2 or more types.
本発明の剥離洗浄剤は、前述のように水不溶性無機化合物と水とを含有するものである。このような剥離洗浄剤における前記水不溶性無機化合物の含有量としては、１〜８０質量％であることが好ましく、１０〜５０質量％であることがより好ましい。前記含有量が前記下限未満では、含有量が不十分で得られる剥離洗浄剤の剥離洗浄性が低下する傾向にあり、他方、前記上限を超えると、水不溶性無機化合物が水に安定的に分散し難くなるとともに、高濃度となって乾燥時の付着層の形成性が低下する傾向にある。 The peeling cleaning agent of the present invention contains a water-insoluble inorganic compound and water as described above. As content of the said water-insoluble inorganic compound in such peeling cleaning agent, it is preferable that it is 1-80 mass%, and it is more preferable that it is 10-50 mass%. If the content is less than the lower limit, the release cleaning property of the resulting release cleaning agent tends to be reduced. On the other hand, if the content exceeds the upper limit, the water-insoluble inorganic compound is stably dispersed in water. In addition, the concentration tends to be high and the formability of the adhesion layer during drying tends to be reduced.
また、このような剥離洗浄剤は前記水不溶性無機化合物を水に分散させた分散液として剤型化されたものである。このような剤型化に際しては、剥離洗浄剤中における前記水不溶性無機化合物の水への分散性の向上及び分散状態の安定性を図る観点から、前記水不溶性無機化合物は微粒子化されていることが好ましい。このような微粒子化における前記水不溶性無機化合物の平均粒子径としては特に制限されないが、０．０１〜１００μｍであることが好ましく、０．１〜５０μｍであることがより好ましい。 Moreover, such a peeling cleaning agent is formulated as a dispersion in which the water-insoluble inorganic compound is dispersed in water. In such a dosage form, the water-insoluble inorganic compound must be finely divided from the viewpoint of improving the dispersibility of the water-insoluble inorganic compound in water and the stability of the dispersed state in the release cleaning agent. Is preferred. The average particle size of the water-insoluble inorganic compound in such micronization is not particularly limited, but is preferably 0.01 to 100 μm, and more preferably 0.1 to 50 μm.
このような剥離洗浄剤の製造方法としては特に制限されず、水不溶性無機化合物を水に分散させることで製造することができ、例えば、予め微粒子化された水不溶性無機化合物を水に分散させて製造する方法や、水不溶性無機化合物を水に分散させた後にサンドグラインドミル等の微粒子化機用いて微粒子化して製造する方法等が挙げられる。 The method for producing such a peeling cleaning agent is not particularly limited, and can be produced by dispersing a water-insoluble inorganic compound in water. For example, a water-insoluble inorganic compound that has been finely divided in advance is dispersed in water. Examples thereof include a production method and a method in which a water-insoluble inorganic compound is dispersed in water and then micronized using a micronizer such as a sand grind mill.
また、このような本発明の剥離洗浄剤においては、前記水不溶性無機化合物を水により均一に分散させるとともに、分散液の粘性をより適度に保つという観点から、高分子系分散剤を更に含有することが好ましい。 Further, in such a peeling cleaning agent of the present invention, from the viewpoint of uniformly dispersing the water-insoluble inorganic compound with water and maintaining the viscosity of the dispersion more appropriately, it further contains a polymer dispersant. It is preferable.
このような高分子系分散剤としては特に制限はないが、例えば、ナフタレンスルホン酸ナトリウムのホルマリン縮合物、スチレンマレイン酸共重合物の塩、ポリアクリル酸ナトリウム、アクリル酸と他の不飽和モノマーとの共重合物の塩、ポリスチレンスルホン酸ナトリウム、スチレンスルホン酸と不飽和モノマーとの共重合物の塩等が挙げられる。このような高分子系分散剤は、１種を単独で用いることも２種以上を混合して用いることも可能である。 Such a polymeric dispersant is not particularly limited. For example, a formalin condensate of sodium naphthalene sulfonate, a salt of a styrene maleic acid copolymer, sodium polyacrylate, acrylic acid and other unsaturated monomers And a copolymer salt of styrene sulfonic acid and an unsaturated monomer. Such polymeric dispersants can be used singly or in combination of two or more.
このような高分子系分散剤の含有量としては、剥離洗浄剤中に０．００１〜１０質量％であることが好ましく、０．０１〜５質量％であることがより好ましい。前記含有量が、前記下限未満では、水不溶性無機化合物の水への分散性の向上が不十分となる傾向にあり、他方、前記上限を超えると粘度が増大する傾向にある。 As content of such a polymeric dispersing agent, it is preferable that it is 0.001-10 mass% in a peeling cleaning agent, and it is more preferable that it is 0.01-5 mass%. When the content is less than the lower limit, the improvement of the dispersibility of the water-insoluble inorganic compound in water tends to be insufficient. On the other hand, when the content exceeds the upper limit, the viscosity tends to increase.
また、このような高分子系分散剤の平均分子量としては、水不溶性無機化合物の水への分散性の向上と分散液の粘性を適度に保つという観点から、５００〜３０００であることが好ましい。 In addition, the average molecular weight of such a polymeric dispersant is preferably 500 to 3000 from the viewpoint of improving the dispersibility of the water-insoluble inorganic compound in water and maintaining the viscosity of the dispersion appropriately.
さらに、本発明の剥離洗浄剤においては、前記水不溶性無機化合物に対する水の浸透性の向上、得られる剥離洗浄剤の濡れ性の向上、及び洗浄時における剥離洗浄剤の浸透性の向上という観点から、非イオン界面活性剤及びアニオン界面活性剤からなる群から選択される少なくとも１種の界面活性剤を更に含有することが好ましい。 Furthermore, in the peeling cleaning agent of the present invention, from the viewpoints of improving the water permeability to the water-insoluble inorganic compound, improving the wettability of the resulting peeling cleaning agent, and improving the permeability of the peeling cleaning agent during cleaning. It is preferable to further contain at least one surfactant selected from the group consisting of a nonionic surfactant and an anionic surfactant.
このような非イオン界面活性剤としては、例えば、高級アルコールのアルキレンオキサイド付加物、アルキルフェノールのアルキレンオキサイド付加物、脂肪酸のアルキレンオキサイド付加物、多価アルコール脂肪酸エステルのアルキレンオキサイド付加物、高級アルキルアミンのアルキレンオキサイド付加物、脂肪酸アミドのアルキレンオキサイド付加物、油脂のアルキレンオキサイド付加物、ポリプロピレングリコールのエチレンオキサイド付加物等の非イオン界面活性剤が挙げられる。また、アニオン界面活性剤としては脂肪酸セッケン等のカルボン酸塩、高級アルコール硫酸エステル塩（アルキル硫酸エステル塩）、高級アルキルポリアルキレングリコールエーテル硫酸エステル塩、硫酸化脂肪酸エステル、硫酸化オレフィン等の硫酸エステル塩、硫酸化油、アルキルベンゼンスルホン酸塩、アルキルナフタレンスルホン酸塩、α−オレフィンスルホン酸塩、パラフィンスルホン酸塩、イゲポンＴ型（商品名）、スルホコハク酸ジエステル塩等のスルホン酸塩、高級アルコールのリン酸エステル塩（アルキルリン酸エステル塩）、高級アルキルポリアルキレングリコールのリン酸エステル塩等のリン酸エステル塩等のアニオン界面活性剤が挙げられる。前記高級アルコールとしては、炭素数が６〜２０の高級アルコールが好ましく、前記アルキルとしては、炭素数が６〜２０のアルキル基であることが好ましく、前記アルキレンオキサイドとしては、炭素数が２〜４のアルキレン基であり、付加モル数が１〜２０モルであることが好ましい。 Examples of such nonionic surfactants include alkylene oxide adducts of higher alcohols, alkylene oxide adducts of alkylphenols, alkylene oxide adducts of fatty acids, alkylene oxide adducts of polyhydric alcohol fatty acid esters, and higher alkylamines. Nonionic surfactants such as alkylene oxide adducts, alkylene oxide adducts of fatty acid amides, alkylene oxide adducts of fats and oils, and ethylene oxide adducts of polypropylene glycol are exemplified. Anionic surfactants include carboxylates such as fatty acid soaps, higher alcohol sulfates (alkyl sulfates), higher alkyl polyalkylene glycol ether sulfates, sulfates such as sulfated fatty acid esters and sulfated olefins. Salt, sulfated oil, alkylbenzene sulfonate, alkyl naphthalene sulfonate, α-olefin sulfonate, paraffin sulfonate, Igepon T type (trade name), sulfosuccinic acid diester salt and other sulfonates, higher alcohols Anionic surfactants such as phosphoric acid ester salts (alkyl phosphoric acid ester salts) and phosphoric acid ester salts such as phosphoric acid ester salts of higher alkyl polyalkylene glycols. The higher alcohol is preferably a higher alcohol having 6 to 20 carbon atoms, the alkyl is preferably an alkyl group having 6 to 20 carbon atoms, and the alkylene oxide has 2 to 4 carbon atoms. The number of moles added is preferably 1 to 20 moles.
このような非イオン界面活性剤またはアニオン界面活性剤の中でも、高級アルコールのアルキレンオキサイド付加物、高級アルコール硫酸エステル塩又は高級アルコールリン酸エステル塩を用いることがより好ましい。また、このようなアニオン界面活性剤の中でも、得られる剥離洗浄剤の濡れ性及び密着強度をより向上するという観点からは、アルキル硫酸エステルナトリウムまたはアルキルリン酸エステルナトリウムを用いることが特に好ましい。このような非イオン界面活性剤またはアニオン界面活性剤は、１種を単独で用いることができ、または２種以上を混合して用いることもできる。 Among such nonionic surfactants or anionic surfactants, it is more preferable to use alkylene oxide adducts of higher alcohols, higher alcohol sulfates or higher alcohol phosphates. Among such anionic surfactants, sodium alkyl sulfate ester sodium or alkyl phosphate sodium salt is particularly preferably used from the viewpoint of further improving the wettability and adhesion strength of the resulting release cleaning agent. Such nonionic surfactants or anionic surfactants can be used alone or in combination of two or more.
このような非イオン界面活性剤またはアニオン界面活性剤の含有量としては、剥離洗浄剤中に０．００５〜１０質量％であることが好ましく、０．０１〜２質量％であることがより好ましい。前記配合量が、前記下限未満では得られる剥離洗浄剤の塗装用治具に対する濡れ性及び密着強度の向上が不十分な傾向にあり、前記上限を超えると、剥離洗浄剤への溶解性の低下や剥離洗浄剤の乾燥性の低下といった問題、洗浄時の泡立ちが多くなるといった問題等が生じる傾向にある。 As content of such a nonionic surfactant or anionic surfactant, it is preferable that it is 0.005-10 mass% in a peeling cleaning agent, and it is more preferable that it is 0.01-2 mass%. . If the blending amount is less than the lower limit, improvement in wettability and adhesion strength of the obtained peeling cleaning agent to the coating jig tends to be insufficient, and if the upper limit is exceeded, the solubility in the peeling cleaning agent decreases. There is a tendency that problems such as a decrease in the drying property of the peeling cleaning agent and problems that foaming during cleaning increases.
また、本発明の剥離洗浄剤においては、水溶性高分子を含有させることが好ましい。このような水溶性高分子を本発明の塗装用治具類の剥離洗浄剤に含有させることで、前記水不溶性無機化合物が塗装用治具類により均一に付着させることが可能となるとともに、形成される付着層の塗装用治具類への密着強度が向上する効果が得られるためである。なお、このような水溶性高分子は、得られる剥離洗浄剤がより高い濡れ性、均一付着性及び密着強度を示すという観点から、前述の界面活性剤と共に含有させることがより好ましい。 Moreover, in the peeling cleaning agent of this invention, it is preferable to contain water-soluble polymer. By including such a water-soluble polymer in the peeling cleaning agent of the coating jig of the present invention, the water-insoluble inorganic compound can be uniformly attached by the coating jig and formed. This is because the effect of improving the adhesion strength of the adhesion layer to the coating jigs can be obtained. In addition, it is more preferable to contain such a water-soluble polymer together with the above-described surfactant from the viewpoint that the obtained release cleaning agent exhibits higher wettability, uniform adhesion, and adhesion strength.
このような水溶性高分子としては特に制限されず、例えば、ポリビニルアルコール、水溶性ポリウレタン、水溶性アクリルポリマー、メチルセルロース等のセルロース誘導体、水溶性ポリエステル、水溶性ナイロン、水溶性ポリアミド、エチレン酢酸ビニル、ポリアクリルアミド、カゼイン、水溶性タンパク質、天然多糖類等の水溶性高分子が挙げられる。このような水溶性高分子の中でも、ポリビニルアルコールを用いることがより好ましい。 Such water-soluble polymer is not particularly limited, for example, polyvinyl alcohol, water-soluble polyurethane, water-soluble acrylic polymer, cellulose derivatives such as methyl cellulose, water-soluble polyester, water-soluble nylon, water-soluble polyamide, ethylene vinyl acetate, Examples thereof include water-soluble polymers such as polyacrylamide, casein, water-soluble protein, and natural polysaccharide. Among such water-soluble polymers, it is more preferable to use polyvinyl alcohol.
ここで、ポリビニルアルコールは、水溶性合成高分子としては特異な性質を持ち、ケン化度の違いによって、７５℃以上の温水には可溶であるが冷水には膨潤するだけで難溶性のものもある。また、ポリビニルアルコールの被膜は、引き裂き強度、伸張度、耐磨耗性に優れており、更に、生成した被膜は水蒸気を良く通す性質がある。このような性質を有することから、ポリビニルアルコールは、本発明の剥離洗浄剤に対する造膜助剤として好適に用いることができる。 Here, polyvinyl alcohol has a unique property as a water-soluble synthetic polymer, and is soluble in hot water of 75 ° C. or higher but hardly swelled in cold water depending on the degree of saponification. There is also. In addition, the polyvinyl alcohol film has excellent tear strength, elongation, and abrasion resistance, and the formed film has a property of allowing water vapor to pass well. Since it has such properties, polyvinyl alcohol can be suitably used as a film-forming aid for the peeling cleaning agent of the present invention.
このようなポリビニルアルコールの剥離洗浄剤への添加量としては、あまり過剰に添加すると造膜し難く、しかも取扱いが困難になるという観点から、本発明の剥離洗浄剤に含有される水不溶性無機化合物に対して０．０１〜１０質量％であることが好ましい。また、ポリビニルアルコールのケン化度の大きさについては水への溶解性と造膜性とを評価して選定しなければならないが、ケン化度が７０〜９５％程度であるものが好ましく、例えば、部分ケン化でケン化度８８％のものとして、クラレポバールＰＶＡ−２０３（商品名［株式会社クラレ製］）が水に対する溶解性が良く、造膜性も優れている点で有効的に使用できる。 The amount of such polyvinyl alcohol added to the release cleaning agent is such that the water-insoluble inorganic compound contained in the release cleaning agent of the present invention is difficult to form if added excessively, and handling becomes difficult. It is preferable that it is 0.01-10 mass% with respect to. Further, the degree of saponification degree of polyvinyl alcohol must be selected by evaluating the solubility in water and the film-forming property, but those having a saponification degree of about 70 to 95% are preferable. Kuraray Poval PVA-203 (trade name [manufactured by Kuraray Co., Ltd.]) is effective in that it has good solubility in water and excellent film-forming properties. it can.
なお、本発明の塗装用治具類の剥離洗浄剤には、本発明の効果を損なわない範囲において、他の成分を添加することが可能である。このような他の成分としては、特に制限されるものではないが、例えば、洗浄時の発泡を抑える消泡剤、治具又は槽の発錆を抑える防錆剤、水溶性高分子の腐敗を抑える防腐剤、消臭剤、香料等が挙げられる。また、このような他の成分の含有量としては、剥離洗浄剤中に０．００１〜１質量％程度であることが好ましい。 In addition, it is possible to add another component to the peeling cleaning agent for the coating jigs of the present invention as long as the effects of the present invention are not impaired. Such other components are not particularly limited, but include, for example, a defoaming agent that suppresses foaming during cleaning, a rust inhibitor that suppresses rusting of jigs or tanks, and a water-soluble polymer that decays. Antiseptics, deodorants, fragrances, and the like are included. Moreover, as content of such other components, it is preferable that it is about 0.001-1 mass% in peeling cleaning agent.
次に、本発明の塗装用治具類の前処理方法及び洗浄方法について説明する。 Next, a pretreatment method and a cleaning method for the coating jigs of the present invention will be described.
本発明の塗装用治具類の前処理方法は、被塗装品を塗装またはマスク塗装する際に用いる塗装用治具類の表面に、前記剥離洗浄剤を供給し、水不溶性無機化合物の付着層を形成させることを特徴とする方法である。 The pre-treatment method for a coating jig according to the present invention includes supplying the peeling cleaning agent to the surface of a coating jig used for coating or mask coating an article to be coated, and applying an adhesion layer of a water-insoluble inorganic compound. Is formed.
このような剥離洗浄剤を塗装用治具類の表面に供給する方法としては特に制限されず、適宜公知の方法を用いることができ、例えば、予め塗装用治具類に前記剥離洗浄剤を塗布する方法、塗装用治具類を前記剥離洗浄剤の分散液に浸漬させる方法等が挙げられる。また、このような剥離洗浄剤を塗装用治具類の表面に供給する際における前記剥離洗浄剤の供給量としては、特に制限はされないが１００〜５００ｇ／ｍ２程度であることが好ましい。そして、塗装用治具類の表面に前記剥離洗浄剤を供給した後に、乾燥させることで塗装用治具類の表面に水不溶性無機化合物が層状に付着した付着層を形成させることができる。 A method for supplying such a peeling cleaning agent to the surface of the coating jig is not particularly limited, and a known method can be used as appropriate. For example, the peeling cleaning agent is applied to the coating jig in advance. And a method of immersing a coating jig in the dispersion liquid of the peeling cleaning agent. The supply amount of the peeling cleaning agent when supplying such a peeling cleaning agent to the surface of the coating jig is not particularly limited, but is preferably about 100 to 500 g / m 2 . And after supplying the said peeling cleaning agent to the surface of the jig for coating, it can be made to dry and can form the adhesion layer in which the water-insoluble inorganic compound adhered to the surface of the jig for coating.
本発明の塗装用治具類の洗浄方法は、被塗装品を塗装またはマスク塗装する際に用いた塗装用治具類に付着した塗料を剥離させて洗浄する洗浄方法であって、前記塗装治具類が、前記剥離洗浄剤により形成された水不溶性無機化合物の付着層を有するものであることを特徴とする方法である。 The cleaning method for a coating jig according to the present invention is a cleaning method for peeling and cleaning the paint adhering to the coating jig used when painting or mask-coating the article to be coated. The tool is characterized in that it has an adhesion layer of a water-insoluble inorganic compound formed by the peeling cleaning agent.
このような本発明の塗装用治具類の洗浄方法は、塗装用治具類の表面に形成された水不溶性無機化合物の付着層に洗浄液の水が浸透していくことにより、前記水不溶性無機化合物とともに塗装用治具類に付着した塗料が剥離するというものである。そして、塗装用治具類から剥離した塗料（塗膜）は水に不溶であるため容易に分離できるものである。従って、前記洗浄液が前記剥離洗浄剤を希釈した液である場合には、かかる剥離洗浄剤を塗装用治具類の表面に予め付着層を形成させるためにも使用できるため、塗装用治具類の表面に付着した塗料の剥離洗浄と、塗装用治具類の表面における前記水不溶性無機化合物の付着層の形成とが同時に行えるという利点がある。 Such a cleaning method for a coating jig of the present invention is such that the water of the cleaning liquid penetrates into the adhesion layer of the water-insoluble inorganic compound formed on the surface of the coating jig, thereby The paint adhered to the coating jig together with the compound is peeled off. And since the coating material (coating film) peeled from the coating jigs is insoluble in water, it can be easily separated. Therefore, when the cleaning liquid is a solution obtained by diluting the peeling cleaning agent, the peeling cleaning agent can be used to form an adhesion layer on the surface of the coating jig in advance. There is an advantage that it is possible to simultaneously perform the peeling cleaning of the paint adhering to the surface and the formation of the adhesion layer of the water-insoluble inorganic compound on the surface of the coating jig.
前記剥離洗浄剤により形成された水不溶性無機化合物の付着層を有する塗装治具類を洗浄する方法としては特に制限されず、適宜公知の洗浄方法、例えば、浸漬法、超音波洗浄法、浸漬揺動法、スプレー法等の各種の洗浄方法が挙げられる。 There is no particular limitation on the method for cleaning the coating jigs having a water-insoluble inorganic compound adhesion layer formed by the above-described peeling cleaning agent, and appropriately known cleaning methods such as immersion method, ultrasonic cleaning method, immersion shaking Various cleaning methods, such as a dynamic method and a spray method, are mentioned.
塗装工程において使用される固定治具の具体的な洗浄方法としては、例えば、用いる固定治具に予め前記剥離洗浄剤を塗布し、乾燥させて前記水不溶性無機化合物の付着層を形成させた後、前記固定治具を使用して塗装を繰り返し、塗料の付着した固定治具を、水または前記剥離洗浄剤を含む洗浄液に浸漬することで前記固定治具から容易に塗料を剥離させて洗浄する方法が挙げられ、これによって洗浄液中の剥離させた塗料は容易に水と分離させることが可能となる。また、塗装工程において使用されるマスク治具の具体的な洗浄方法としては、例えば、前記剥離洗浄剤の希釈液にマスク治具を浸漬した後、乾燥することによって前記水不溶性無機化合物の付着層を前記マスク治具に形成させて、このマスク治具で被塗装品の非塗装部分を覆いマスキンング塗装を行い、マスキング塗装が１〜数十回繰り返されることで塗料が付着したマスク治具を、水または前記剥離洗浄剤を含む洗浄液に浸漬することで前記マスク治具から容易に塗料を剥離させて洗浄する方法が挙げられ、これによって剥離させた塗料は容易に水と分離させることが可能となる。このように、本発明の洗浄方法においては、水または前記剥離洗浄剤を含む洗浄液に前記塗装用冶具類を浸漬させることにより、前記塗装用冶具類から容易に塗料を剥離させて洗浄することが可能となる。 As a specific cleaning method for the fixing jig used in the painting process, for example, after applying the peeling cleaning agent to the fixing jig to be used in advance and drying it to form the adhesion layer of the water-insoluble inorganic compound The coating is repeatedly performed using the fixing jig, and the fixing jig to which the paint is attached is immersed in water or a cleaning solution containing the peeling cleaning agent so that the coating is easily peeled off from the fixing jig and cleaned. A method is mentioned, and this makes it possible to easily separate the peeled paint in the cleaning liquid from water. Further, as a specific cleaning method of the mask jig used in the painting process, for example, the mask jig is immersed in a diluting liquid of the peeling cleaning agent, and then dried to dry the adhesion layer of the water-insoluble inorganic compound. Is formed on the mask jig, and the mask jig is used to cover the non-coated portion of the article to be coated, and the masking coating is repeated 1 to several tens of times to apply the mask jig to which the paint adheres. It is possible to easily remove the paint from the mask jig and wash it by immersing it in water or a cleaning solution containing the release cleaning agent, and the paint thus peeled off can be easily separated from water. Become. As described above, in the cleaning method of the present invention, the paint jig can be easily peeled off from the paint jig and washed by immersing the paint jig in water or a cleaning liquid containing the peeling detergent. It becomes possible.
なお、本発明の剥離洗浄剤を用いて表面に前記水不溶性無機化合物の付着層を形成させた塗装用治具類を用いた塗装方法としては特に制限はなく、一般的なスプレー塗装であるエアースプレー方式、ホットエアースプレー方式、エアーレススプレー方式、ホットエアーレススプレー方式等の塗装方法が挙げられる。 In addition, there is no restriction | limiting in particular as a coating method using the jig for coating which formed the adhesion layer of the said water-insoluble inorganic compound on the surface using the peeling cleaning agent of this invention, The air which is general spray coating Examples of the coating method include a spray method, a hot air spray method, an airless spray method, and a hot airless spray method.
以下、実施例及び比較例に基づいて本発明をより具体的に説明するが、本発明は以下の実施例に限定されるものではない。 EXAMPLES Hereinafter, although this invention is demonstrated more concretely based on an Example and a comparative example, this invention is not limited to a following example.
（実施例１）
工業用填料として市販されているタルク（珪酸マグネシウム）２００ｇを水７９７ｇにナフタレンスルホン酸ナトリウムのホルマリン縮合物（高分子系分散剤）３ｇを加えて分散させて剥離洗浄剤を得た。
Example 1
200 g of talc (magnesium silicate) commercially available as an industrial filler was dispersed in 797 g of water by adding 3 g of a formalin condensate (polymeric dispersant) of sodium naphthalene sulfonate to obtain a peeling cleaning agent.
（実施例２）
炭酸カルシウム２００ｇを水８００ｇに分散させて剥離洗浄剤を得た。
(Example 2)
A peeling detergent was obtained by dispersing 200 g of calcium carbonate in 800 g of water.
（実施例３）
硫酸カルシウム２００ｇを水８００ｇに分散させて剥離洗浄剤を得た。
(Example 3)
A peeling detergent was obtained by dispersing 200 g of calcium sulfate in 800 g of water.
（実施例４）
工業用無機顔料として市販されている酸化チタン２００ｇを水７９５ｇにスチレンマレイン酸共重合物の塩（日華化学株式会社製の商品名「ディスパテックスＳＭＡ」）５ｇを加えて分散させて剥離洗浄剤を得た。
Example 4
200 g of titanium oxide, which is commercially available as an industrial inorganic pigment, is dispersed in 795 g of water by adding 5 g of a salt of a styrene maleic acid copolymer (trade name “Dispatex SMA” manufactured by Nikka Chemical Co., Ltd.) to disperse it. Got.
（実施例５）
工業用填料として市販されているタルク（珪酸マグネシウム）２００ｇを水７９６ｇにナフタレンスルホン酸ナトリウムのホルマリン縮合物（高分子系分散剤）３ｇを加えて分散させた後、更に（Ｃ１２）アルキル硫酸エステルナトリウム１ｇを加えて剥離洗浄剤を得た。
(Example 5)
200 g of talc (magnesium silicate) commercially available as an industrial filler was dispersed in 796 g of water by adding 3 g of a formalin condensate (polymeric dispersant) of sodium naphthalene sulfonate, and then (C 12 ) alkyl sulfate. 1 g of sodium was added to obtain a peeling cleaner.
（実施例６）
工業用填料として市販されているタルク（珪酸マグネシウム）２００ｇを水７９５ｇにナフタレンスルホン酸ナトリウムのホルマリン縮合物（高分子系分散剤）３ｇを加えて分散させた後、更に（Ｃ１２）アルキル硫酸エステルナトリウム１ｇ、ポリビニルアルコール（株式会社クラレ製の商品名「ＰＶＡ−２０３」）１０ｇ及びポリオキシエチレン（６モル）（Ｃ１２）アルキルエーテル１ｇを加えて剥離洗浄剤を得た。
(Example 6)
200 g of talc (magnesium silicate) commercially available as an industrial filler was dispersed in 795 g of water by adding 3 g of a formalin condensate of sodium naphthalene sulfonate (polymer dispersing agent), and then (C 12 ) alkyl sulfate. 1 g of sodium, 10 g of polyvinyl alcohol (trade name “PVA-203” manufactured by Kuraray Co., Ltd.) and 1 g of polyoxyethylene (6 mol) (C 12 ) alkyl ether were added to obtain a peeling cleaning agent.
（比較例１）
ポリアクリル酸ナトリウム（分子量＝１００００）２００ｇを水８００ｇに溶解させて剥離洗浄剤を得た。
(Comparative Example 1)
200 g of sodium polyacrylate (molecular weight = 10000) was dissolved in 800 g of water to obtain a peeling cleaning agent.
（比較例２）
（Ｃ１２）アルキルスルホン酸ナトリウム３００ｇを水７００ｇに溶解させて剥離洗浄剤を得た。
(Comparative Example 2)
(C 12 ) 300 g of sodium alkyl sulfonate was dissolved in 700 g of water to obtain a peeling cleaning agent.
１．試験片の濡れ性、べたつき性の評価
５０ｍｍ×８０ｍｍの冷間圧延鋼鈑（ＳＰＣＣ）を、容量比５０／５０で混合したトルエン／アセトンの混合溶剤中に浸漬し、その後乾燥して脱脂処理を行った試験片を得た。
1. Evaluation of wettability and stickiness of test piece A 50 mm x 80 mm cold rolled steel plate (SPCC) is immersed in a mixed solvent of toluene / acetone mixed at a volume ratio of 50/50, and then dried to be degreased. A test specimen was obtained.
次に、実施例１〜６及び比較例１〜２で得られた剥離洗浄剤中に前記試験片を１０秒間浸漬した後、引き上げて、試験片の濡れ性を下記の基準で評価した。その後、８０℃で１０分間乾燥した試験片のべたつき性を下記の基準で評価した。得られた結果を表１に示す。 Next, the test piece was dipped in the release cleaning agent obtained in Examples 1 to 6 and Comparative Examples 1 and 2 for 10 seconds and then pulled up, and the wettability of the test piece was evaluated according to the following criteria. Then, the stickiness of the test piece dried for 10 minutes at 80 ° C. was evaluated according to the following criteria. The obtained results are shown in Table 1.
［濡れ性］
◎：斑がなく全面均一に剥離洗浄剤が付着している
○：一部に斑があるが、ほぼ均一に剥離洗浄剤が付着している
×：剥離洗浄剤が斑付きしている。
[Wettability]
A: There is no spots, and the entire surface of the release cleaning agent is evenly attached. O: Some spots are present, but the release cleaning agent is attached almost uniformly. X: The release cleaning agent is spotted.
［べたつき性］
◎：べたつきがなく、全面均一に緻密な付着層を形成している
○：少しべたつきがあるが、ほぼ均一に付着層を形成している
×：べたつきがあり、一部に不均一な付着層を形成している。
[Stickness]
A: There is no stickiness, and a dense adhesion layer is formed uniformly on the entire surface. A: There is a little stickiness, but an adhesion layer is formed almost uniformly. X: There is stickiness, and a part of the adhesion layer is uneven. Is forming.
２．塗料の剥離洗浄性
（i）水による洗浄
前述のようにして得られた試験片にアクリル系塗料を塗工し、８０℃で１時間乾燥させた。その後、アクリル系塗料を塗工した試験片を水に浸漬し、塗装膜の剥離洗浄性を下記に示す評価基準で評価した。得られた結果を表１に示す。
2. (I) Cleaning with water An acrylic coating was applied to the test piece obtained as described above and dried at 80 ° C. for 1 hour. Thereafter, the test piece coated with the acrylic paint was immersed in water, and the peelability of the coating film was evaluated according to the following evaluation criteria. The obtained results are shown in Table 1.
（ii）実施例１〜６及び比較例１〜２の剥離洗浄剤による洗浄
前述のようにして得られたアクリル系塗料を塗工した試験片を実施例１〜６及び比較例１〜２の剥離洗浄剤中に浸漬し、塗装膜の剥離洗浄性を下記に示す評価基準で評価した。得られた結果を表１に示す。
(Ii) Cleaning with Examples 1 to 6 and Comparative Examples 1 and 2 Stripping cleaning agents The test pieces coated with the acrylic paint obtained as described above were used in Examples 1 to 6 and Comparative Examples 1 and 2. It was immersed in a peeling cleaning agent, and the peeling cleaning property of the coating film was evaluated according to the following evaluation criteria. The obtained results are shown in Table 1.
［剥離洗浄性］
◎：剥離性が良好で、塗料が全く残らない
○：剥離性は良いが、一部に塗料が残る
△：剥離性が弱く、塗料が斑点状に残る。
[Peeling cleanability]
A: Good peelability and no paint remains. ○: Good peelability but some paint remains. Δ: The peelability is weak and the paint remains in spots.
本発明の実施例１〜６の剥離洗浄剤によれば、塗料の剥離性及びべたつき性に優れることが分かる。特に高分子系分散剤を併用した実施例４で得られた剥離洗浄剤、高分子系分散剤と界面活性剤とを併用した実施例５で得られた剥離洗浄剤、及び高分子系分散剤と界面活性剤と水溶性高分子とを併用した実施例６で得られた剥離洗浄剤においては、塗装用治具類の表面に均一な付着層を形成させて、塗装用治具類に直接塗料が付着するのを有効に防止することができたため、塗料の剥離性に特に優れることが確認された。また、剥離させた塗料（塗膜）も水に溶解することが無く、塗料（塗膜）を容易に分離することが可能であったため、従来行われていた有機溶剤を用いて塗料を溶解させる洗浄方法とは異なり、排水（廃液）処理の負荷も少ないものとなることが分かった。 According to the peeling detergents of Examples 1 to 6 of the present invention, it can be seen that the paint has excellent peelability and stickiness. In particular, the release cleaning agent obtained in Example 4 in combination with a polymer dispersant, the release cleaning agent in Example 5 in which a polymer dispersant and a surfactant are used in combination, and the polymer dispersion agent In the release cleaning agent obtained in Example 6 in which a surfactant and a water-soluble polymer were used in combination, a uniform adhesion layer was formed on the surface of the coating jig and directly applied to the coating jig. Since it was possible to effectively prevent the paint from adhering, it was confirmed that the paint was particularly excellent in releasability. In addition, since the peeled paint (coating film) does not dissolve in water and the paint (coating film) can be easily separated, the paint is dissolved using a conventional organic solvent. It was found that, unlike the cleaning method, the load of wastewater (waste liquid) treatment is small.
以上説明したように、本発明によれば、前記従来の有機溶剤系の剥離洗浄剤の有する課題を解決できる水系の剥離洗浄剤であって、べたつきがない均一且つ緻密な水不溶性無機化合物の付着層を形成することができ、高水準の剥離洗浄性を達成することが可能な塗装用治具類の剥離洗浄剤、並びに、その剥離洗浄剤を用いた塗装用治具類の前処理方法及び洗浄方法を提供することが可能となる。 As described above, according to the present invention, a water-based stripping cleaning agent capable of solving the problems of the conventional organic solvent-based stripping cleaning agent, and adhesion of a uniform and dense water-insoluble inorganic compound without stickiness. A peeling cleaning agent for coating jigs capable of forming a layer and achieving a high level of peeling cleaning properties, a pretreatment method for coating jigs using the peeling cleaning agent, and A cleaning method can be provided.
すなわち、本発明の塗装用治具類の剥離洗浄剤を用いれば、固定治具やマスク治具等の塗装用治具類に付着した塗装を容易に、且つ確実に落とすことができる剥離洗浄方法を提供することが可能となる。また、本発明の塗装用治具類の剥離洗浄剤及びそれを用いた洗浄方法は、ジクロロメタン（塩化メチレン）や有機溶剤を使用しないため作業環境及び地球環境に優しく、更には、剥離された塗料の分離が容易であるため、剥離洗浄液を繰り返し使用することが可能となる。このように、本発明の塗装用治具類の剥離洗浄剤は、工業製品の塗装技術の向上、環境問題、コスト面等で有用なものである。 That is, if the stripping cleaning agent for the coating jigs of the present invention is used, the stripping cleaning method can easily and reliably drop the coating adhered to the coating jigs such as the fixing jig and the mask jig. Can be provided. In addition, the stripping cleaning agent and the cleaning method using the coating jig according to the present invention are gentle to the working environment and the global environment because dichloromethane (methylene chloride) and an organic solvent are not used. Therefore, the separation cleaning liquid can be used repeatedly. Thus, the peeling cleaning agent for the coating jigs of the present invention is useful in improving the coating technology of industrial products, environmental problems, cost and the like.
Claims (11)