JP2006045169A - Sheet-like cosmetic - Google Patents
Sheet-like cosmetic Download PDFInfo
- Publication number
- JP2006045169A JP2006045169A JP2004232352A JP2004232352A JP2006045169A JP 2006045169 A JP2006045169 A JP 2006045169A JP 2004232352 A JP2004232352 A JP 2004232352A JP 2004232352 A JP2004232352 A JP 2004232352A JP 2006045169 A JP2006045169 A JP 2006045169A
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- powder
- skin
- cosmetic
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、シート状化粧料、さらに詳しくは、シート状基材表面近傍に粉体が存在し、清拭後の肌に効率よく粉体が移行して快適な使用感を与えると共に、粉体による白残りを抑制し得るシート状化粧料に関する。 The present invention relates to a sheet-like cosmetic, more specifically, powder is present in the vicinity of the surface of the sheet-like base material, and the powder is efficiently transferred to the skin after wiping to give a comfortable feeling of use. It is related with the sheet-like cosmetics which can suppress the white residue by.
従来、顔、首、手足等の身体の清拭やシェービングに用いるウェットシートタイプの製品が種々実用化されている。これらは一枚ずつ個装された製品や１０数枚単位にしたポケットティッシュタイプの製品、数十枚〜数百枚単位のボックスタイプの製品等がある。これらの製品は、化粧成分や、洗浄剤、清涼剤、殺菌剤、香料等の成分をシートに含浸させたものであって、使用後の肌を清潔にしたり、清涼感を与えたり、シェービングのための水分を補給する目的で使用されている。 Conventionally, various wet sheet type products used for wiping and shaving the body such as the face, neck and limbs have been put into practical use. These include products that are individually packaged, pocket tissue type products that are in units of several dozens, and box type products that are in units of several tens to several hundreds. These products are made by impregnating sheets with cosmetic ingredients, cleaning agents, refreshing agents, disinfectants, fragrances, etc., to clean the skin after use, to give a refreshing feeling, It is used for the purpose of replenishing moisture.
しかしながら、従来の製品は、肌を清潔にしたり、湿潤にする目的では、効果を発揮するものの、肌上の油分や水分を必要以上に拭き除いてしまい、乾燥感や不快感を与えることが多かった。例えば、脇の下や首の周囲等ではウェットタイプの濡れティッシュで拭きすぎた場合、肌荒れ等を起こす場合があった。こうしたウェットタイプの製品では全身に使えるとされているものの、実質的には使用部位が手や足等、比較的汚れた部位の清拭に限定され、全身を日常的に清拭するには適さない。
例えば、水性媒体と共に、粉体をシート状基材に担持してなるシート状化粧料が提案されているが（例えば、特許文献１参照）、このものは、皮膚にさらさら感を与える粉体を移行させることを主目的とするものであり、乾いた後の皮膚上で粉体が白残りする場合があった。
However, while conventional products are effective for the purpose of cleansing and moisturizing the skin, they often wipe out oil and moisture on the skin more than necessary, and often give dryness and discomfort. It was. For example, rough wiping or the like may occur when the wet cloth of a wet type is wiped excessively on the armpit or around the neck. Although these wet type products can be used throughout the body, they are practically limited to cleaning relatively dirty parts such as hands and feet, and are not suitable for daily cleaning of the whole body. .
For example, a sheet-like cosmetic material in which a powder is supported on a sheet-like base material together with an aqueous medium has been proposed (see, for example, Patent Document 1), which is a powder that gives a dry feeling to the skin. The main purpose is to transfer the powder, and the powder may remain white on the skin after drying.
本発明は、シート状基材表面近傍に粉体が存在し、清拭後の肌に効率よく粉体が移行して快適な使用感を与えると共に、粉体による白残りを抑制し得るシート状化粧料を提供することを目的とする。 The present invention is a sheet form in which powder is present in the vicinity of the surface of the sheet-like base material, and the powder efficiently migrates to the skin after wiping and gives a comfortable feeling of use and can suppress white residue due to the powder. The purpose is to provide cosmetics.
本発明者らは、粉体を、不飽和脂肪酸、酸化防止剤を含有する水性媒体とともにシート状基材に含有させることにより、基材表面近傍に粉体が存在し、清拭後の肌に効率よく粉体が移行して快適な使用感を与え、かつ粉体による白残りが抑制されることを見出した。
すなわち、本発明は、粉体、不飽和脂肪酸、酸化防止剤及び水性媒体を含む液状組成物をシート状基材に担持してなるシート状化粧料を提供する。
The present inventors include powders in the sheet-like base material together with an aqueous medium containing an unsaturated fatty acid and an antioxidant, so that the powder exists near the surface of the base material, and the skin after wiping is removed. It was found that the powder migrates efficiently and gives a comfortable feeling of use, and the white residue due to the powder is suppressed.
That is, the present invention provides a sheet-like cosmetic comprising a sheet-like base material carrying a liquid composition containing powder, an unsaturated fatty acid, an antioxidant and an aqueous medium.
本発明によれば、シート状基材表面近傍に粉体が存在し、清拭後の肌に効率よく粉体が移行して快適な使用感を与えると共に、粉体による白残りを抑制し得るシート状化粧料を提供することができる。 According to the present invention, powder exists in the vicinity of the surface of the sheet-like base material, and the powder efficiently migrates to the skin after wiping, giving a comfortable feeling of use and suppressing white residue due to the powder. Sheet-like cosmetics can be provided.
本発明のシート状化粧料は、粉体、不飽和脂肪酸、酸化防止剤及び水性媒体を含む液状組成物をシート状基材に、噴霧や塗布などの方法により担持させることにより、作製することができる。前記水性媒体としては、水又は含水エタノールが好ましい。 The sheet-like cosmetic of the present invention can be produced by carrying a liquid composition containing powder, unsaturated fatty acid, antioxidant and aqueous medium on a sheet-like substrate by a method such as spraying or coating. it can. As the aqueous medium, water or hydrous ethanol is preferable.
本発明に用いられる粉体としては、合成高分子化合物及び天然鉱物から選ばれるものが好ましい。このうち、合成高分子化合物の粉体の例としては、シリコーン樹脂［信越化学 (株) 製ＫＭＰ−５９０、東芝シリコーン（株） 製トスパール１４５、トスパール２０００Ｂ等］、ポリオルガノシルセスキオキサン、シリコーンゴムパウダー［信越化学 (株) 製ＫＭＰ−５９７、ＫＭＰ−５９８、Ｘ−５２−８７５、東レ（株） 製トレフィル５０１、トレフィル５０５、トレフィル５０６、トレフィル６０１等］、シリコーン樹脂／ゴム複合パウダー［信越化学 (株) 製ＫＳＰ−１０５等］、及び片末端にラジカル重合性基を有するポリシロキサン化合物を分散剤として、溶媒中でビニルモノマーの分散重合を行うことにより得られたポリマー微粒子等の有機シリコーン基含有ポリマーなどが挙げられる。また、ナイロン樹脂［東レ（株） 製ＳＰ−５００等］、ポリスチレン系樹脂［住友化学工業（株） 製ファインパール、積水化成品工業（株） 製テクポリマーＳＢ、綜研化学（株） 製ファインパウダーＳＧＰ等］、ポリエチレン樹脂［住友精化（株） 製フロービーズ等］、ポリメタクリル酸メチル系樹脂［松本油脂製薬（株）製マツモトマイクロスフェアーＭ、積水化成品工業（株） 製テクポリマーＭＢ、綜研化学（株） 製ファインパウダーＭＰ等］、ジビニルベンゼン系樹脂、ポリウレタン系樹脂、ベンゾグアナミン樹脂、メラミン樹脂、フェノール系樹脂、フッ素系樹脂等の他、メチルハイドロジェンジメチルポリシロキサン、パーフルオロアルキルリン酸エステルジエタノールアミン塩等のケイ素やフッ素を含有する化合物で表面撥水化処理をした粉体［三好化成（株） 製ＳＩ−タルクＪＡ４６Ｒ、大東化成工業（株）製ＰＦ−３ＬＬ−５タルク］などが挙げられる。中でも上記有機シリコーン基含有ポリマーが肌残留時の動摩擦低下、肌の滑り感触（さらさら感触）付与及び肌上での残留性という点で好ましい。
また、アクリル酸エステル及びメタクリル酸エステルから選ばれる少なくとも１種の単量体とカルボキシル基を有する単量体を含む単量体成分を共重合してなる架橋（メタ）アクリル酸エステル系樹脂粉体も好ましい。
The powder used in the present invention is preferably selected from synthetic polymer compounds and natural minerals. Among these, examples of the synthetic polymer compound powder include silicone resins [KMP-590 manufactured by Shin-Etsu Chemical Co., Ltd., Tospearl 145 manufactured by Toshiba Silicone Co., Ltd., Tospearl 2000B, etc.], polyorganosilsesquioxane, and silicone. Rubber powder [Shin-Etsu Chemical Co., Ltd. KMP-597, KMP-598, X-52-875, Toray Industries, Inc. Trefil 501, Trefil 505, Trefil 506, Trefil 601 etc.], Silicone resin / rubber composite powder [Shin-Etsu Chemical Co., Ltd. KSP-105 etc.] and organosilicone such as polymer fine particles obtained by carrying out dispersion polymerization of vinyl monomer in a solvent using a polysiloxane compound having a radical polymerizable group at one end as a dispersant. And group-containing polymers. In addition, nylon resin [SP-500 etc. manufactured by Toray Industries, Inc.], polystyrene resin [Fine Pearl manufactured by Sumitomo Chemical Co., Ltd., Techpolymer SB manufactured by Sekisui Plastics Co., Ltd., Fine Powder manufactured by Soken Chemical Co., Ltd. SGP, etc.], polyethylene resin [Flow Beads manufactured by Sumitomo Seika Co., Ltd.], polymethyl methacrylate resin [Matsumoto Yushi Seiyaku Co., Ltd. Matsumoto Microsphere M, Sekisui Chemicals Co., Ltd. Techpolymer MB , Fine powder MP manufactured by Soken Chemical Co., Ltd.], divinylbenzene resin, polyurethane resin, benzoguanamine resin, melamine resin, phenol resin, fluorine resin, methyl hydrogen dimethylpolysiloxane, perfluoroalkyl phosphorus Surface repellent with compounds containing silicon and fluorine, such as acid ester diethanolamine salt Examples include hydrotreated powder [SI-talc JA46R manufactured by Miyoshi Kasei Co., Ltd., PF-3LL-5 talc manufactured by Daito Kasei Kogyo Co., Ltd.]. Among them, the above-mentioned organic silicone group-containing polymer is preferable in terms of lowering dynamic friction when the skin remains, imparting a slipping feeling (smooth feeling) to the skin, and persistence on the skin.
Further, a crosslinked (meth) acrylate resin powder obtained by copolymerizing at least one monomer selected from an acrylate ester and a methacrylate ester and a monomer component containing a monomer having a carboxyl group Is also preferable.
一方、天然鉱物からなる粉体としては、タルク、セリサイト、マイカ、カオリン、ベンガラ、クレー、ベントナイト、ケイ酸、無水ケイ酸、ケイ酸マグネシウム、雲母、酸化マグネシウム、酸化亜鉛、酸化チタン、酸化アルミニウム、硫酸アルミニウム、ミョウバン、硫酸カルシウム、硫酸バリウム、硫酸マグネシウム等が例示されるが、特にタルクは肌の上での滑りが良いので好ましい。 On the other hand, powders made of natural minerals include talc, sericite, mica, kaolin, bengara, clay, bentonite, silicic acid, silicic anhydride, magnesium silicate, mica, magnesium oxide, zinc oxide, titanium oxide, aluminum oxide. Aluminum sulfate, alum, calcium sulfate, barium sulfate, magnesium sulfate and the like are exemplified, but talc is particularly preferable because it has good slippage on the skin.
また、本発明の粉体の粒径としては、０．５〜３０μｍの範囲に全粉体の６０質量％以上が存在することが、肌感触を高める上で好ましく、粒径１〜１０μｍの粉体が全粉体の８０質量％以上であることが特に好ましい。一方、粒径が０．５μｍ未満の粉体は肌の感触に対してほとんど効果がないか、又はきしむような不快感を与えるため少ない方が好ましく、また粒径が３０μｍを超える粉体の混入は少ない方が良い。したがって、これらの粉体の量は全粉体の４０質量％未満であることが好ましく、１０質量％以下が更に好ましい。また、肌感触の観点からは粒径が２００μｍ以上の粉体を実質的に含まないことが望ましい。
本発明のシート状化粧料は、前記粉体のうち粒径０．５〜３０μｍの粉体をシート状基材の１平方メートル当たり０．１〜２０ｇ、特に０．５〜１０ｇ含有することが、肌に感触を与えながら且つ肌を白くさせないという点で好ましい。
In addition, the particle size of the powder of the present invention is preferably 60% by mass or more of the total powder in the range of 0.5 to 30 μm from the viewpoint of enhancing the skin feel, and the powder having a particle size of 1 to 10 μm. The body is particularly preferably 80% by mass or more of the total powder. On the other hand, a powder with a particle size of less than 0.5 μm has little effect on the feel of the skin, or is preferably less because it gives a squeaky discomfort, and a powder with a particle size of more than 30 μm is mixed. Is better. Therefore, the amount of these powders is preferably less than 40% by mass of the total powder, and more preferably 10% by mass or less. Further, from the viewpoint of skin feel, it is desirable that a powder having a particle size of 200 μm or more is not substantially contained.
The sheet-like cosmetic of the present invention contains 0.1 to 20 g, particularly 0.5 to 10 g, of a powder having a particle size of 0.5 to 30 μm per square meter of the sheet-like base material among the powders. This is preferable in that it gives the skin a touch and does not whiten the skin.
本発明のシート状化粧料において、シート状基材に担持される液状組成物の一成分として用いられる不飽和脂肪酸としては、炭素原子数が１４〜２２のものが好ましく、特に１４〜１８のものが好ましい。具体的には、ミリストレイン酸、パルミトレイン酸、オレイン酸、リノール酸、リノレン酸等が挙げられる。
これらの不飽和脂肪酸は、液状組成物中に一種含まれていてもよく、二種以上含まれていてもよい。該液状組成物中の前記不飽和脂肪酸の含有量は、０．０１〜１質量％とするのが好ましく、より好ましくは０．０５〜０．３質量％である。この範囲において、意図する効果が認知でき、１質量％を超える量の不飽和脂肪酸を含有させても、効果の向上は顕著ではなく、また１質量％以下であれば、特有の脂肪酸臭が生じず、製品処方上好ましい。
In the sheet-like cosmetic of the present invention, the unsaturated fatty acid used as one component of the liquid composition carried on the sheet-like base material preferably has 14 to 22 carbon atoms, particularly those having 14 to 18 carbon atoms. Is preferred. Specific examples include myristoleic acid, palmitoleic acid, oleic acid, linoleic acid, and linolenic acid.
One kind of these unsaturated fatty acids may be contained in the liquid composition, or two or more kinds thereof may be contained. The content of the unsaturated fatty acid in the liquid composition is preferably 0.01 to 1% by mass, more preferably 0.05 to 0.3% by mass. In this range, the intended effect can be recognized, and even when an unsaturated fatty acid in an amount exceeding 1% by mass is contained, the improvement in the effect is not remarkable. It is preferable in terms of product formulation.
また、粉体を含む液状組成物は、シート状基材１００質量部に対して、５０〜５００質量部を含浸させることが好ましく、特に使用感を高める上で１００〜４００質量部を含浸させることが好ましい。本発明においてはシート状基材として、天然繊維又は合成繊維の不織布又は織布の何れをも使用することができる。具体的には、例えばレーヨン、アセテート、アクリル、ポリエステル、ポリエチレン、ポリプロピレン、ポリウレタン、ポリアミドなどの繊維や、コットン及びこれらを混綿したものの不織布又は織布、更に湿式及び乾式パルプシート、熱可塑性樹脂（ポリエチレン、ポリプロピレン、ポリエチレンテレフタレート等）で強化したパルプシート等が挙げられる。これらの基材は、繊維間隔がなるべく密なほどシート表面に粉体が集合するので好ましい。また、製造時の加工のしやすさ等から、パルプ、コットンがシート基材として特に好ましい。パルプについては、やわらかさと強度を両立させるために薄いパルプを重ね合わせて用いることが好ましく、更に熱可塑性樹脂で強化したパルプは、エンボス処理により適度な厚み（嵩高さ）を付与でき、かつ肌を濡らしすぎないので好ましい。更にヒートシールにより複数枚のシートを部分的に貼り合わせることで、柔らかく、拭きごたえのある厚みのあるシートを得ることができ、より良好な使用感を提供できる。 Moreover, it is preferable to impregnate 50-500 mass parts with respect to 100 mass parts of sheet-like base materials, and especially the liquid composition containing powder impregnates 100-400 mass parts in order to improve a usability | use_condition. Is preferred. In the present invention, any of non-woven fabrics or woven fabrics of natural fibers or synthetic fibers can be used as the sheet-like substrate. Specifically, for example, fibers such as rayon, acetate, acrylic, polyester, polyethylene, polypropylene, polyurethane, polyamide, and nonwoven fabrics or woven fabrics made of cotton and blends thereof, wet and dry pulp sheets, thermoplastic resins (polyethylene) Pulp sheet reinforced with polypropylene, polyethylene terephthalate, etc.). These base materials are preferable because powders gather on the sheet surface as the fiber spacing is as close as possible. Further, pulp and cotton are particularly preferable as the sheet base material because of ease of processing during production. As for the pulp, it is preferable to use a thin pulp in order to achieve both softness and strength. Further, the pulp reinforced with a thermoplastic resin can impart an appropriate thickness (bulkness) by embossing treatment, and the skin. It is preferable because it does not get wet too much. Furthermore, by sticking together a plurality of sheets by heat sealing, a soft and wipingly thick sheet can be obtained, and a better usability can be provided.
また、本発明のシート状化粧料は、より感触を高めるため、動粘度が２５℃で１〜２００ｍｍ2／ｓのシリコーン油を含有することができる。シリコーン油は肌への吸着性が高いという性質があるが、上記粉体の肌への吸着をより高める上で好ましい効果をもたらす。シリコーン油としては、メチルポリシロキサン、ジメチルポリシロキサン、ジエチルポリシロキサン、メチルフェニルポリシロキサン、脂肪酸変性ポリシロキサン、高級アルコール変性ポリシロキサン、アミノ変性ポリシロキサンなどが挙げられる。これらの中で、メチルポリシロキサン、ジメチルポリシロキサンが特に好ましい。また、上記動粘度が１ｍｍ2／ｓ以上であると皮膚刺激性等の問題がなく、好ましい。このシリコーン油の配合量は粉体の質量に対して１００分の１量〜１０倍量が好ましく、５０分の１量〜１倍量が更に好ましい。 In addition, the sheet-like cosmetic of the present invention can contain a silicone oil having a kinematic viscosity of 1 to 200 mm 2 / s at 25 ° C. in order to enhance the touch. Silicone oil has a property of high adsorptivity to the skin, but brings about a favorable effect in further enhancing the adsorption of the powder to the skin. Examples of the silicone oil include methylpolysiloxane, dimethylpolysiloxane, diethylpolysiloxane, methylphenylpolysiloxane, fatty acid-modified polysiloxane, higher alcohol-modified polysiloxane, and amino-modified polysiloxane. Of these, methylpolysiloxane and dimethylpolysiloxane are particularly preferred. The kinematic viscosity is preferably 1 mm 2 / s or more because there is no problem such as skin irritation. The blending amount of the silicone oil is preferably 1/100 to 10 times, more preferably 1/50 to 1 times the mass of the powder.
シリコーン油以外にも本発明のシート状化粧料に含有させることができる油性物質としては、使用感を高める上から、アボカド油、ツバキ油、タートル油、トウモロコシ油、オリーブ油、小麦胚芽油、大豆油、ホホバ油、落花生油、カカオ脂、ラノリン、流動パラフィン、スクワラン、ワセリン、コレステリルエステル類等が好ましい。
本発明のシート状化粧料には、更にエタノール、プロピレングリコール、１，３−ブタンジオール、グリセリン、ソルビトール、ポリエチレングリコール等のアルコール類を配合することができる。
In addition to silicone oil, the oily substance that can be contained in the sheet-shaped cosmetic composition of the present invention includes avocado oil, camellia oil, turtle oil, corn oil, olive oil, wheat germ oil, soybean oil, in order to enhance the feeling of use. Jojoba oil, peanut oil, cacao butter, lanolin, liquid paraffin, squalane, petrolatum, cholesteryl esters and the like are preferable.
The sheet-like cosmetic of the present invention can further contain alcohols such as ethanol, propylene glycol, 1,3-butanediol, glycerin, sorbitol, and polyethylene glycol.
また、本発明のシート状化粧料には、酸化防止剤を配合する。酸化防止剤としては、ジブチルヒドロキシトルエン（ＢＨＴ）、ブチルヒドロキシアニソール、ビタミンＥ及びその誘導体、カテキン化合物、フラボノイド化合物、ポリフェノール化合物などを例示することができる。これらの酸化防止剤は、一種を単独で用いてもよく、二種以上を組み合わせて用いてもよい。 Moreover, antioxidant is mix | blended with the sheet-like cosmetics of this invention. Examples of the antioxidant include dibutylhydroxytoluene (BHT), butylhydroxyanisole, vitamin E and its derivatives, catechin compounds, flavonoid compounds, polyphenol compounds and the like. These antioxidants may be used individually by 1 type, and may be used in combination of 2 or more type.
さらに、本発明のシート状化粧料には、制汗塩及び／又は殺菌剤を配合することができる。
制汗塩としては、例えばアルミニウムクロロハイドレート、塩化アルミニウム、硫酸アルミニウム、塩基性臭化アルミニウム、アルミニウムフェノールスルホン酸、タンニン酸、アルミニウムナフタリンスルホン酸、塩基性ヨウ化アルミニウム、ジルコニウム塩、アルミニウム−ジルコニウム複合塩、ｐ−フェノールスルホン酸亜鉛等が挙げられる。これらの制汗塩は一種を単独で用いてもよく、二種以上を組み合わせて用いてもよい。
また、殺菌剤としては、例えば３，４，４−トリクロロカルバニリド（ＴＣＣ）、レゾルシン、フェノール、ヘキサクロロフェン、トリクロサン、イソプロピルメチルフェノール等のノニオン系殺菌剤、塩化ベンザルコニウム、塩化ベンゼトニウム、塩化アルキルトリメチルアンモニウム、ジンクピリチオン等のカチオン系殺菌剤、ソルビン酸、サリチル酸等のアニオン系殺菌剤が挙げられる。これらの殺菌剤は一種を単独で用いてもよく、二種以上を組み合わせて用いてもよいし、さらには、前記制汗塩一種以上と殺菌剤一種以上を組み合わせて用いてもよい。
Furthermore, an antiperspirant salt and / or a bactericidal agent can be blended in the sheet-like cosmetic of the present invention.
Examples of antiperspirant salts include aluminum chlorohydrate, aluminum chloride, aluminum sulfate, basic aluminum bromide, aluminum phenol sulfonic acid, tannic acid, aluminum naphthalene sulfonic acid, basic aluminum iodide, zirconium salt, and aluminum-zirconium composite. Examples thereof include salts and zinc p-phenolsulfonate. These antiperspirant salts may be used alone or in a combination of two or more.
Examples of the bactericides include nonionic bactericides such as 3,4,4-trichlorocarbanilide (TCC), resorcin, phenol, hexachlorophene, triclosan, isopropylmethylphenol, benzalkonium chloride, benzethonium chloride, and chloride. Examples include cationic fungicides such as alkyltrimethylammonium and zinc pyrithione, and anionic fungicides such as sorbic acid and salicylic acid. These disinfectants may be used alone or in combination of two or more, and moreover, one or more antiperspirant salts and one or more disinfectants may be used in combination.
本発明のシート状化粧料は、肌を拭くことにより汚れを取り除いて清潔にすると共に、粉体が効果的に肌に吸着して残留し、長時間にわたって肌にさらさらとした肌感触を与えることができる。また、保湿剤、抗炎症剤、美白剤、ＵＶケア剤、清涼剤、香料等を配合することにより、これらの成分を粉体と共に肌に長時間残留させ、使用後の肌を機能的にコンディショニングすることができ、潤いや清涼感、香りを楽しむこともできる。 The sheet-like cosmetic of the present invention removes dirt by wiping the skin and cleans it, and the powder effectively adsorbs and remains on the skin, giving a smooth skin feel for a long time. Can do. Also, by blending moisturizers, anti-inflammatory agents, whitening agents, UV care agents, refreshing agents, fragrances, etc., these components remain on the skin together with the powder for a long time, and the skin after use is functionally conditioned. You can enjoy moisture, refreshment and fragrance.
例えば、顔面に用いた場合、皮脂を効果的に除去すると共に粉体や保湿剤を残留させ快適に保つだけでなく、化粧直しのしやすさが著しく向上する。また、制汗塩、殺菌剤を配合した場合、肌を清浄にした上でこれらの有効成分を肌に長時間残留させるため、持続的な制汗・デオドラント効果が期待できる。また、身体のむだ毛処理部位に使用し、剃毛後の肌を整える用法でも、本発明品の有用性は高い。つまり、カミソリ使用前の肌に塗布することにより、当該部位を湿潤させるとともに粉体を残留させることで、カミソリの滑りを良好にして肌を痛めず、快適な肌感触に仕上げることができる。 For example, when it is used on the face, it not only effectively removes sebum but also keeps the powder and moisturizing agent to remain comfortable, and the retouching ease is remarkably improved. In addition, when antiperspirant salt and a bactericidal agent are blended, these active ingredients remain on the skin for a long time after cleansing the skin, so that a continuous antiperspirant / deodorant effect can be expected. Moreover, the usefulness of the product of the present invention is also high in a method of using it on the body's unwanted hair treatment site and preparing the skin after shaving. In other words, by applying to the skin before using the razor, the part is moistened and the powder remains, so that the razor can be made slippery without damaging the skin, and a comfortable skin feel can be achieved.
本発明のシート状化粧料は、上記粉体を、好ましくはその大部分を、シート状基材の表面近傍に偏在して担持することが好ましい。粉体を偏在させるためには、シート状基材に、粉体を配合した液状組成物を塗工する方法が挙げられるが、シート状基材の上から直接粉体を振りかけることもできる。また、本発明のシート状化粧料は、上記粉体を、摺動により肌に移行し得る状態で担持することが好ましい。 In the sheet-like cosmetic of the present invention, it is preferable that the powder, preferably most of the powder, is unevenly distributed near the surface of the sheet-like substrate. In order to make the powder unevenly distributed, a method of applying a liquid composition in which the powder is mixed to the sheet-like substrate can be mentioned, but the powder can also be sprinkled directly on the sheet-like substrate. Moreover, it is preferable to carry | support the said powder in the state which can transfer to the skin by sliding in the sheet-like cosmetics of this invention.
本発明のシート状化粧料は、水性媒体に本発明で用いる粉体及びその他の成分を含有させた液状組成物を、スプレーやエアーガン等を用いた噴霧や、スリット型のノズルやバーコーターを用いた塗布等の方法により、シート状基材に担持させることで調製できる。特に、積層されたシート状化粧料を得る方法としては、粉体と水性媒体とを含有する液状組成物を、シート状基材に塗布し又は含浸させて、前記粉体及び液状組成物を担持させた後、裁断して積層することからなる製造方法が好ましい。この方法によれば、粉体が均一に分布し、本発明の効果を十分に発揮する製品が得られる。 The sheet-like cosmetic of the present invention uses a liquid composition containing the powder and other components used in the present invention in an aqueous medium, spraying using a spray or an air gun, a slit type nozzle or a bar coater. It can be prepared by carrying it on a sheet-like base material by a method such as coating. In particular, as a method of obtaining a laminated sheet-like cosmetic, a liquid composition containing a powder and an aqueous medium is applied to or impregnated on a sheet-like substrate to carry the powder and the liquid composition. Then, a production method comprising cutting and laminating is preferable. According to this method, a product is obtained in which the powder is uniformly distributed and the effects of the present invention are sufficiently exhibited.
製造例１ ポリマー粒子Ａの製造
ｎ−ヘキサン２７６．９ｇ、トルエン９０ｇ、片末端にメタクリロキシ基を有するポリシロキサン化合物［チッソ（株）製サイラプレーンＦＭ−０７２５（登録商標）、数平均分子量１万］１．５８ｇを、窒素雰囲気下、反応容器に仕込み、７０℃に昇温した。メタクリル酸メチル３９．５０ｇ、スチレン１３．１７ｇ、ラウロイルパーオキシド１．０６ｇを加え、７０℃で１２時間反応させた。反応液を放冷後、ｎ−ヘキサン２００ｇで希釈し、遠心分離により固液分離した。固形物をｎ−ヘキサン３００ｇで再分散した後、遠心分離する洗浄工程を２回行い、５０℃の乾燥機で真空乾燥を行い、白色パウダー５４．０ｇを得た。得られたポリマー粒子の粒子径は２μｍの単分散粒子であった。これをポリマー粒子Ａとする。
Production Example 1 Production of Polymer Particle A 276.9 g of n-hexane, 90 g of toluene, polysiloxane compound having a methacryloxy group at one end [Chiraso Co., Ltd. Silaplane FM-0725 (registered trademark), number average molecular weight 10,000] 1.58 g was charged into a reaction vessel under a nitrogen atmosphere and heated to 70 ° C. 39.50 g of methyl methacrylate, 13.17 g of styrene and 1.06 g of lauroyl peroxide were added and reacted at 70 ° C. for 12 hours. The reaction solution was allowed to cool, diluted with 200 g of n-hexane, and solid-liquid separated by centrifugation. The solid was redispersed with 300 g of n-hexane and then subjected to a washing step of centrifuging twice, followed by vacuum drying with a dryer at 50 ° C. to obtain 54.0 g of white powder. The obtained polymer particles were monodisperse particles having a particle diameter of 2 μm. This is designated as polymer particle A.
製造例２ ポリマー粒子Ｂの製造
ビーカーにラウリルメタクリレート８２ｇ、メタクリル酸３ｇ、エチレングリコールジメタクリレート１５ｇ、ラウロイルパーオキサイド２ｇを仕込み混合攪拌して溶解させた。ここにＮ−ステアロイル−Ｎ−メチルタウリンナトリウムを０．７５ｇ溶解させたイオン交換水４００ｇを加え、ホモミキサーで粒径が２．２μｍになるまで分散させた。
４つ口フラスコにこの分散液を注ぎ込み、攪拌しながら窒素置換を３０分行った。オイルバスによりフラスコ内部の温度を８０℃まで加温し、８０℃に達してから５時間重合を行った後、室温まで冷却した。重合した粒子の分散液を凍結乾燥し、粒子を回収することによりポリマー粒子Ｂを得た。
Production Example 2 Production of Polymer Particle B 82 g of lauryl methacrylate, 3 g of methacrylic acid, 15 g of ethylene glycol dimethacrylate, and 2 g of lauroyl peroxide were charged in a beaker and dissolved by stirring. 400 g of ion-exchanged water in which 0.75 g of sodium N-stearoyl-N-methyltaurine was dissolved was added thereto and dispersed with a homomixer until the particle size became 2.2 μm.
The dispersion was poured into a four-necked flask and purged with nitrogen for 30 minutes while stirring. The temperature inside the flask was heated to 80 ° C. with an oil bath. After reaching 80 ° C., polymerization was performed for 5 hours, and then cooled to room temperature. The dispersion liquid of the polymerized particles was lyophilized and the particles were collected to obtain polymer particles B.
実施例１〜６、比較例１及び２
シート基材としてパルプシート（１２０ｇ／ｍ2）を用い、含浸率を設定し、所定量の液状組成物をスプレーにて該シート基材に噴霧して粉体をシート基材に担持させたのち、裁断して積層させ、ウェットタイプのシート状化粧料を作製した。液状組成物は、表１に示す量の原料成分を、ホモミキサーを用いて混合し、調製した。
（評価方法）
専門パネラー１０名が上腕部を各実施例及び比較例にて作製したシート状化粧料で清拭し、白残り、及びさらさら感の持続について、下記の基準に従い官能評価した。各パネラーの評点を集計し、平均評価スコアでランク分けした。評価結果を組成とともに表１に示す。
Examples 1-6, Comparative Examples 1 and 2
After using a pulp sheet (120 g / m 2 ) as the sheet substrate, setting the impregnation rate, spraying a predetermined amount of the liquid composition onto the sheet substrate by spraying, and then supporting the powder on the sheet substrate The sheet was cut and laminated to prepare a wet type sheet-shaped cosmetic. The liquid composition was prepared by mixing raw material components in the amounts shown in Table 1 using a homomixer.
(Evaluation methods)
Ten expert panelists wiped the upper arm with a sheet-like cosmetic prepared in each of the examples and comparative examples, and sensory-evaluated the remaining white and the continuity of the smooth feeling according to the following criteria. The score of each panel was tabulated and ranked according to the average evaluation score. The evaluation results are shown in Table 1 together with the composition.
＜評価基準＞
（１）白残り（塗布直後の見た目の白さを評価した）
４：白くならない
３：あまり白くならない
２：やや白くなる
１：白くなる
＜平均評価スコア＞
◎：３．５〜４．０
○：２．５〜３．４
△：１．５〜２．４
×：１．０〜１．４
（２）さらさら感の持続（塗布１時間後のさらさらした感触を評価した）
５：さらさらする
４：ややさらさらする
３：どちらともいえない
２：あまりさらさらしない
１：全くさらさらしない
＜平均評価スコア＞
◎ ：４．５〜５．０
○ ：３．５〜４．４
○△：２．５〜３．４
△ ：１．５〜２．４
× ：１．０〜１．４
<Evaluation criteria>
(1) White residue (Evaluation of apparent whiteness immediately after application)
4: Does not become white 3: Does not become very white 2: Becomes slightly white 1: Becomes white <Average evaluation score>
A: 3.5 to 4.0
○: 2.5 to 3.4
Δ: 1.5 to 2.4
X: 1.0-1.4
(2) Persistence of a smooth feeling (Evaluated for a smooth feel after 1 hour of application)
5: Slightly smooth 4: Slightly smooth 3: Neither say 2: Slightly free 1: Not completely free <Average rating score>
A: 4.5 to 5.0
○: 3.5 to 4.4
○ △: 2.5 to 3.4
Δ: 1.5 to 2.4
X: 1.0-1.4
表１より、実施例１〜６のシート状化粧料は比較例１及び２のシート状化粧料と比較して使用感に優れ、すなわち、さらさら感が実感でき、粉体により肌が白く見えなかった。 From Table 1, the sheet-like cosmetics of Examples 1 to 6 are superior in use feeling compared to the sheet-like cosmetics of Comparative Examples 1 and 2, that is, they can feel a smooth feeling and the skin does not look white due to the powder. It was.
本発明のシート状化粧料を使うことにより、汗ばんだ肌や垢で汚れた肌を清潔にすると共に、使用後の肌にさらさらした滑り感を提供し、今までのウェットシートにはない新しい快適な効果を与えることができる。
By using the sheet-like cosmetic of the present invention, it cleans sweaty skin and dirt-stained skin, and provides a feeling of slipperiness to the skin after use, a new comfort not found in conventional wet sheets Effects can be given.
Claims (6)
Furthermore, the sheet-form cosmetics in any one of Claims 1-5 containing an antiperspirant salt and / or a disinfectant.