JP2006017781A - Electrostatic charge image developing toner, developer, image forming apparatus and process cartridge - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide an electrostatic charge image developing toner and a developer having a stabilized particle size distribution of the toner, adaptable to a low-temperature fixing system, exhibiting proper offset resistance, staining neither fixing means not image, and capable of forming stable images, and to provide an electrophotographic system image forming apparatus and a process cartridge that use the developer. <P>SOLUTION: The electrostatic charge image developing toner is includes processes where; an organic solvent phase in which at least a functional group-containing polyester resin has been dissolved, an active hydrogen-containing compound and a colorant are dispersed in an aqueous medium phase, in which resin fine particles have been dissolved, the functional group-containing polyester resin and the active hydrogen-containing compound are brought into an extension reaction and/or a crosslinking reaction, and particles are formed from the resulting dispersion, wherein an organic acid compound is contained in the organic solvent phase. <P>COPYRIGHT: (C)2006,JPO&NCIPI

Description

  The present invention relates to an electrostatic latent image developing toner and developer used for image formation by an electrostatic copying process such as a copying machine, a facsimile, and a printer, and an image forming apparatus using the toner and developer. The present invention relates to a process cartridge.

  Conventionally, in an electrophotographic apparatus, an electrostatic recording apparatus, or the like, an electric or magnetic latent image is visualized with toner. For example, in electrophotography, an electrostatic charge image (latent image) is formed on a photoreceptor, and then the latent image is developed with toner to form a toner image. The toner image is usually transferred onto a transfer material such as paper and then fixed by a method such as heating. Toner used for electrostatic charge image development is generally colored particles in which a binder, a colorant, a charge control agent, and other additives are contained in a binder resin. There is a suspension polymerization method. In the pulverization method, a colorant, a charge control agent, an offset preventive agent, and the like are melt-mixed and uniformly dispersed in a thermoplastic resin, and the resulting composition is pulverized and classified to produce a toner. According to the pulverization method, a toner having some excellent characteristics can be produced, but there is a limitation in the selection of the toner material. For example, the composition obtained by melt mixing must be capable of being pulverized and classified by economically usable equipment. From this requirement, the melt-mixed composition must be made sufficiently brittle. For this reason, when the above composition is actually pulverized into particles, a high-range particle size distribution is likely to be formed, and when attempting to obtain a copy image with good resolution and gradation, for example, the particle size There is a disadvantage that the fine powder of 5 μm or less and the coarse powder of 20 μm or more must be removed by classification and the yield becomes very low. Further, in the pulverization method, it is difficult to uniformly disperse the colorant, the charge control agent, and the like in the thermoplastic resin. The uneven dispersion of the compounding agent adversely affects the fluidity, developability, durability, image quality and the like of the toner.

  In recent years, in order to overcome these problems in the pulverization method, a toner production method by a suspension polymerization method has been proposed and implemented. A technique for producing a toner for developing an electrostatic latent image by a polymerization method is known. For example, toner particles are obtained by a suspension polymerization method. However, the toner particles obtained by the suspension polymerization method are spherical and have a drawback of poor cleaning properties. Development / transfer with a low image area ratio results in a small amount of residual toner, and poor cleaning does not pose a problem. However, images with a high image area ratio, such as photographic images, and untransferred images formed due to poor paper feed, etc. Toner may be generated on the photoconductor as untransferred toner, and if accumulated, the image may be soiled. In addition, the charging roller that contacts and charges the photosensitive member is contaminated, and the original charging ability cannot be exhibited. For this reason, a method for obtaining resin particles having irregular shapes by associating resin fine particles obtained by an emulsion polymerization method is disclosed (for example, see Patent Document 1). However, in the toner particles obtained by the emulsion polymerization method, a large amount of the surfactant remains not only on the surface but also inside the particles even after the water washing step, and the environmental stability of the toner charging is impaired. The amount distribution is widened, and the background stain of the obtained image becomes poor. Further, the remaining surfactant contaminates the photoreceptor, the charging roller, the developing roller, etc., and the original charging ability cannot be exhibited.

On the other hand, a new production method called a dissolution suspension method (EA: Emulsion-Aggregation method) has recently been proposed (see, for example, Patent Document 2). This method is a method of granulating from a polymer dissolved in an organic solvent, etc., while the suspension polymerization method forms particles from monomers, and has advantages such as expansion of the resin selection range and polarity controllability. Cite. Although the toner structure control (core / shell structure control) is possible, the shell structure is a resin-only layer intended to reduce the exposure of pigments and wax to the surface. It is disclosed that the state is not devised and that it does not have such a structure (for example, Non-Patent Document 1). Therefore, although the shell structure is used, the surface of the toner is a normal resin and is not particularly devised. When aiming at fixing at a lower temperature, it is not sufficient in terms of heat-resistant storage stability and environmental charge stability.
Moreover, it is common to use a styrene-acrylate copolymer for any of the suspension polymerization method, emulsion polymerization method, and dissolution suspension method, and polyester resins have difficulty in particle formation and have a particle size and particle size distribution. It was difficult to control the shape. In addition, there was a limit to fixability when aiming at lower temperature fixing.
On the other hand, it is also known to use polyester modified with urea bonds for the purpose of heat-resistant storage stability and low-temperature fixing (Patent Document 3), but the surface is not particularly devised, and the conditions are particularly severe. The problem was not sufficient in terms of environmental charge stability.

  In the field of electrophotography, high image quality has been studied from various angles, and among them, the recognition that toner diameter reduction and spheroidization are extremely effective is increasing. However, as the diameter of the toner is reduced, the transferability and the fixing property are lowered, and a tendency to become a poor image is observed. On the other hand, it is known that transferability is improved by making toner spherical (Patent Document 4). Under such circumstances, further speeding up of image formation is desired in the field of color copiers and color printers. The “tandem method” is effective for speeding up (for example, Patent Document 5). The “tandem method” is a method of obtaining a full-color image on a transfer sheet by sequentially superimposing and transferring an image formed by an image forming unit onto a single transfer sheet conveyed to a transfer belt. A tandem color image forming apparatus has a variety of transfer papers that can be used, has high quality of a full color image, and has excellent characteristics that a full color image can be obtained at a high speed. In particular, the characteristic that a full color image can be obtained at a high speed is a characteristic that is not found in other color image forming apparatuses. On the other hand, attempts have been made to achieve high speed while improving image quality using spherical toner. However, in order to cope with higher speeds, quick fixability is required, but a toner having both good fixability and low temperature fixability with a spherical toner has not been realized so far.

Japanese Patent No. 2537503 Japanese Patent No. 3141784 Japanese Patent Laid-Open No. 11-133667 JP 9-258474 A JP-A-5-341617 Takao Ishiyama, two others “Characteristics and Future Prospects of Toner,” 4th Joint Imaging Symposium (July 29, 2002)

  Therefore, the present invention has been made in view of the above problems, and the problem is that the toner particle size distribution is stabilized, it is compatible with a low-temperature fixing system, has good offset resistance, and contaminates the fixing means and the image. An object of the present invention is to provide a toner and a developer for developing an electrostatic image capable of forming a stable and stable image, and to provide an electrophotographic image forming apparatus and a process cartridge using the same.

As a result of intensive studies to solve such problems, the present inventors have at least an organic solvent phase in which a functional group-containing polyester resin is dissolved, an active hydrogen-containing compound, and a colorant. Dispersed in a dispersed aqueous medium phase to cause elongation reaction and / or crosslinking reaction between the functional group-containing polyester resin and the active hydrogen-containing compound, thereby forming particles from the resulting dispersion An electrostatic charge image developing toner, in which an organic acid compound is dispersed in the organic solvent phase to stabilize the particle size distribution of the toner, correspond to a low-temperature fixing system, and provide a toner base having good offset resistance. Based on these findings, the present invention has been completed.
That is, the above-described problem is (1) “an aqueous medium in which resin fine particles are dispersed in an organic solvent phase in which at least a functional group-containing polyester resin is dissolved, an active hydrogen-containing compound, and a colorant. For electrostatic image development in which particles are formed from the dispersion obtained by causing an elongation reaction and / or a crosslinking reaction between the functional group-containing polyester resin and the active hydrogen-containing compound by dispersing in the phase A toner for developing an electrostatic charge image, wherein the organic solvent phase contains an organic acid compound ”, (2)“ the organic acid compound is a carboxylic acid compound and a carboxylic acid anhydride; (3) “The organic acid compound has a number average molecular weight in the range of 15 to 1500”. 2 ), (4) “Non-reactive polyester is further dissolved in the organic solvent phase together with the functional group-containing polyester resin, and the functional group-containing polyester system”. The toner for developing an electrostatic charge image according to any one of (1) or (2), wherein the weight ratio of the resin to the non-reactive polyester is 5/95 to 75/25 ", (5) “The toner for developing an electrostatic charge image according to any one of (1) to (3) above, wherein the toner particles have an average circularity of 0.900 to 0.980”, 6) “Toner for developing electrostatic image according to any one of items (1) to (4), wherein Dv / Dn of the toner particles is 1.25 or less”, (7 ) “The average circularity of the toner particles is 0.900 to 0.980. The electrostatic image developing toner according to any one of items (1) to (5), (8) “Toner according to at least the items (1) to (6)”. And a carrier comprising magnetic particles ”, (9)“ Static image carrier, charging means, exposure means, developing means, contact transfer means, heat fixing means, and cleaning means And an image forming apparatus using the toner for developing an electrostatic charge image according to item (1) or (6), and (10) “To an electrostatic image carrier”. The image forming apparatus according to (1), wherein the charging member is charged by bringing a charging member into contact with the charging member and applying a voltage to the charging member. The carrier is an amorphous silicon electrostatic image carrier The image forming apparatus according to any one of (8) and (9) above, (12) “The fixing device is in contact with a heating body including a heating element and the heating body. Heating that includes a film and a pressure member that is in pressure contact with the heating body via the film, and that heats and fixes a recording material on which an unfixed image is formed between the film and the pressure member The image forming apparatus according to any one of Items (8) to (10), wherein the image forming apparatus is a fixing unit, and (13) “At least the photosensitive member and the developing unit are integrally supported to form an image. In a process cartridge that is detachably attached to the forming apparatus main body, the developing means holds toner (developer), and the toner (developer) is at least as defined in items (1) to (6). A process comprising the toner according to any one of the above. Mosquitoes - are resolved by the cartridge ".

  The present invention provides an aqueous medium phase in which resin fine particles are dispersed by an organic solvent phase in which at least a functional group-containing polyester resin is dissolved, an active hydrogen-containing compound, and a colorant by means for solving the above-described problem. A toner for developing an electrostatic charge image, which is dispersed in to cause an elongation reaction and / or a crosslinking reaction between the functional group-containing polyester resin and the active hydrogen-containing compound, thereby forming particles from the resulting dispersion. In addition, by containing an organic acid compound in the organic solvent phase, the toner particle size distribution is stable, compatible with a low-temperature fixing system, good offset resistance, and does not contaminate the fixing device and the image. Toner can be provided. Further, even if the toner is attached to the process cartridge, the same excellent effect is obtained. Also, a charging device with reduced generation of ozone, a photoreceptor having high surface hardness, high sensitivity to long-wavelength light such as a semiconductor laser (770 to 800 nm), etc., and being hardly deteriorated by repeated use, and It is possible to provide an image forming apparatus using a fixing device that is efficient and can shorten the rise time.

  The best mode for carrying out the present invention will be described below with reference to the drawings. Note that it is easy for a person skilled in the art to make other embodiments by changing or correcting the present invention within the scope of the claims, and these changes and modifications are included in the scope of the claims. The following description is an example of the best mode of the present invention, and does not limit the scope of the claims.

[Organic solvent phase]
<Organic solvent>
The materials used for producing the toner of the present invention will be described. In the present invention, the organic solvent is not particularly limited as long as it is a solvent capable of dissolving and / or dispersing the toner composition. As a preferable thing, it is preferable from the point that removal is easy that the boiling point of this solvent is less than 150 degreeC. Examples of the solvent include toluene, xylene, benzene, carbon tetrachloride, methylene chloride, 1,2-dichloroethane, 1,1,2-trichloroethane, trichloroethylene, chloroform, monochlorobenzene, methyl acetate, ethyl acetate, methyl ethyl ketone, acetone. , Tetrahydrofuran and the like can be used alone or in combination of two or more. Of these, methyl acetate and ethyl acetate are preferred because they are particularly volatile to toner. The amount of the solvent used relative to 100 parts of the toner solid component is usually 40 to 300 parts, preferably 60 to 140 parts, and more preferably 80 to 120 parts.

<Functional group-containing polyester resin>
In the present invention, a polyester prepolymer having an isocyanate group can be used as the modified polyester resin. Examples of the polyester prepolymer (A) having an isocyanate group include a polycondensate of a polyol (1) and a polycarboxylic acid (2) and a polyester having an active hydrogen group, which is further reacted with a polyisocyanate (3). Can be mentioned. Examples of the active hydrogen group possessed by the polyester include hydroxyl groups (alcoholic hydroxyl groups and phenolic hydroxyl groups), amino groups, carboxyl groups, mercapto groups, and the like. Among these, alcoholic hydroxyl groups are preferred.
Examples of the polyol (1) include a diol (1-1) and a tri- or higher valent polyol (1-2). (1-1) alone or (1-1) and a small amount of (1-2) Mixtures are preferred. Diol (1-1) includes alkylene glycol (ethylene glycol, 1,2-propylene glycol, 1,3-propylene glycol, 1,4-butanediol, 1,6-hexanediol, etc.); alkylene ether glycol (diethylene glycol) ), Triethylene glycol, dipropylene glycol, polyethylene glycol, polypropylene glycol, polytetramethylene ether glycol, etc.); alicyclic diols (1,4-cyclohexanedimethanol, hydrogenated bisphenol A, etc.); bisphenols (bisphenol A, bisphenol) F, bisphenol S, etc.); alkylene oxide (ethylene oxide, propylene oxide, butylene oxide, etc.) adduct of the above alicyclic diol; Alkylene oxide Nord acids (ethylene oxide, propylene oxide, butylene oxide, etc.), etc. adducts. Among them, preferred are alkylene glycols having 2 to 12 carbon atoms and alkylene oxide adducts of bisphenols, and particularly preferred are alkylene oxide adducts of bisphenols and alkylene glycols having 2 to 12 carbon atoms. It is a combined use.
The trihydric or higher polyol (1-2) includes 3 to 8 or higher polyhydric aliphatic alcohols (glycerin, trimethylolethane, trimethylolpropane, pentaerythritol, sorbitol, etc.); trihydric or higher phenols (Trisphenol PA, phenol novolak, cresol novolak, etc.); and alkylene oxide adducts of the above trivalent or higher polyphenols.

Examples of the polycarboxylic acid (2) include dicarboxylic acid (2-1) and trivalent or higher polycarboxylic acid (2-2). (2-1) alone and (2-1) with a small amount of ( The mixture of 2-2) is preferred. Dicarboxylic acid (2-1) includes alkylene dicarboxylic acid (succinic acid, adipic acid, sebacic acid, etc.); alkenylene dicarboxylic acid (maleic acid, fumaric acid, etc.); aromatic dicarboxylic acid (phthalic acid, isophthalic acid, terephthalic acid) And naphthalenedicarboxylic acid). Of these, preferred are alkenylene dicarboxylic acids having 4 to 20 carbon atoms and aromatic dicarboxylic acids having 8 to 20 carbon atoms.
Examples of the trivalent or higher polycarboxylic acid (2-2) include aromatic polycarboxylic acids having 9 to 20 carbon atoms (trimellitic acid, pyromellitic acid, and the like). In addition, as polycarboxylic acid (2), you may make it react with polyol (1) using the acid anhydride or lower alkyl ester (methyl ester, ethyl ester, isopropyl ester, etc.) of the above-mentioned thing.
In order to adjust the polyester having an alcoholic hydroxyl group at the terminal by a polycondensation reaction, the ratio of the polyol (1) to the polycarboxylic acid (2) is equivalent to the equivalent ratio [OH] / [ COOH] is usually 2/1 to 1/1, preferably 1.5 / 1 to 1/1, and more preferably 1.3 / 1 to 1.02 / 1.
Examples of the polyisocyanate (3) used for preparing the polyester prepolymer by reacting with the alcoholic hydroxyl group of the polyester include aliphatic polyisocyanates (tetramethylene diisocyanate, hexamethylene diisocyanate, 2,6-diisocyanatomethyl carbonate). Proate, etc.); alicyclic polyisocyanates (isophorone diisocyanate, cyclohexylmethane diisocyanate, etc.); aromatic diisocyanates (tolylene diisocyanate, diphenylmethane diisocyanate, etc.); Xylylene diisocyanate); isocyanurates; the polyisocyanate blocked with a phenol derivative, oxime, caprolactam, etc .; and These two or more types can be used in combination.

The use ratio of the polyisocyanate is usually 5/1 to 1/1, preferably 4/1 to 1 as an equivalent ratio [NCO] / [OH] of the isocyanate group [NCO] and the hydroxyl group [OH] of the polyester having a hydroxyl group. 1.2 / 1, more preferably 2.5 / 1 to 1.5 / 1. When [NCO] / [OH] exceeds 5, low-temperature fixability deteriorates. If the molar ratio of [NCO] is less than 1, the urea content in the modified polyester will be low, and the hot offset resistance will deteriorate.
The number of isocyanate groups contained per molecule in the prepolymer (A) having an isocyanate group is usually 1 or more, preferably 1.5 to 3 on average, more preferably 1.8 to 2.5 on average. It is. If it is less than 1 per molecule, the molecular weight of the modified polyester after crosslinking and / or elongation becomes low, and the hot offset resistance deteriorates.

<Combination of non-reactive low molecular weight polyester>
In the present invention, it is important not only to use the modified polyester (A) alone, but also to contain an unmodified polyester (C) not modified with the (A) as a toner binder component. By using (C) in combination, low-temperature fixability and glossiness when used in a full-color device are improved. Examples of (C) include the same polycondensates of polyol (1) and polycarboxylic acid (2) as in the polyester component (A), and preferred ones are also the same as (C). (C) is not limited to unmodified polyester, but may be modified with a chemical bond other than a urea bond, and may be modified with, for example, a urethane bond. It is preferable that (A) and (C) are at least partially compatible in terms of low-temperature fixability and hot offset resistance. Accordingly, the polyester component (A) and (C) preferably have similar compositions. When (A) is contained, the weight ratio of (A) to (C) is usually 5/95 to 75/25, preferably 10/90 to 25/75, more preferably 12/88 to 25/75, Particularly preferred is 12/88 to 22/78. If the weight ratio of (A) is less than 5%, the hot offset resistance deteriorates, and it is disadvantageous in terms of both heat-resistant storage stability and low-temperature fixability.

  The peak molecular weight measured by GPC (gel permeation chromatography) of the polyester (C) is usually 1000 to 30000, preferably 1500 to 10000, more preferably 2000 to 8000. If it is less than 1000, heat-resistant storage stability will deteriorate, and if it exceeds 10,000, low-temperature fixability will deteriorate. The hydroxyl value of (C) is preferably 5 or more, more preferably 10 to 120, and particularly preferably 20 to 80. If it is less than 5, it is disadvantageous in terms of both heat-resistant storage stability and low-temperature fixability. The acid value of (C) is usually from 0.5 to 40, preferably from 5 to 35. If the acid value is too high, it tends to be negatively charged, which is not preferable. Those exceeding this range are susceptible to environmental influences under high temperature and high humidity and low temperature and low humidity environments, and are liable to cause image deterioration.

<Organic acid compound>
In the present invention, an organic acid compound can be used for the purpose of stabilizing the particle size distribution of the toner. Any organic acid compound can be used and is not particularly limited. When the organic acid compound is granulated in an aqueous solvent, in addition to the above, the emulsification / dispersion is affected. Therefore, even if the amount of the unmodified polyester in the emulsified particles varies, Oxidation can be adjusted so as not to affect. As the organic acid compound, a carboxylic acid compound and a carboxylic acid anhydride are preferable, and more preferably, methyl acetate, acetic acid that is a hydrolyzate of ethyl acetate mentioned in the organic solvent, and the modified polyester (A), It is polycarboxylic acid (2) used at the time of preparation of non-reactive polyester (C). These are contained in the emulsified formed particles. The organic acid compound has a number average molecular weight in the range of 15 to 1500. If the number average molecular weight is less than 15, the effect of adjusting the oxidation in the particles is small, and if it exceeds 1500, it is difficult to be contained in the particles.

[Active hydrogen-containing compounds]
As will be described later, the above-mentioned polyester prepolymer (A) having an isocyanate group is made to have a higher molecular weight by being subjected to elongation and / or crosslinking reaction with an active hydrogen compound.
In the present invention, amines can be used as a crosslinking agent and / or an extender. As amines (B), diamine (B1), trivalent or higher polyamine (B2), aminoalcohol (B3), aminomercaptan (B4), amino acid (B5), and amino acids B1-B5 blocked (B6) etc. are mentioned. Examples of the diamine (B1) include aromatic diamines (phenylenediamine, diethyltoluenediamine, 4,4′diaminodiphenylmethane, etc.); alicyclic diamines (4,4′-diamino-3,3′dimethyldicyclohexylmethane, diaminecyclohexane, Isophorone diamine etc.); and aliphatic diamines (ethylene diamine, tetramethylene diamine, hexamethylene diamine etc.) and the like. Examples of the trivalent or higher polyamine (B2) include diethylenetriamine and triethylenetetramine. Examples of amino alcohol (B3) include ethanolamine and hydroxyethylaniline. Examples of amino mercaptan (B4) include aminoethyl mercaptan and aminopropyl mercaptan. Examples of the amino acid (B5) include aminopropionic acid and aminocaproic acid. Examples of B1 to B5 blocked amino groups (B6) include ketimine compounds and oxazoline compounds obtained from the amines of B1 to B5 and ketones (acetone, methyl ethyl ketone, methyl isobutyl ketone, etc.). Among these amines (B), preferred are B1 and a mixture of B1 and a small amount of B2.

Furthermore, if necessary, the molecular weight of the modified polyester after completion of the reaction can be adjusted by using a terminator for crosslinking and / or elongation. Examples of the terminator include monoamines (diethylamine, dibutylamine, butylamine, laurylamine, etc.), and those blocked (ketimine compounds).
The ratio of amines (B) is the equivalent ratio [NCO] / [NHx] of isocyanate groups [NCO] in the prepolymer (A) having isocyanate groups and amino groups [NHx] in amines (B). The ratio is usually 1/2 to 2/1, preferably 1.5 / 1 to 1 / 1.5, more preferably 1.2 / 1 to 1 / 1.2. If [NCO] / [NHx] is greater than 2 or less than 1/2, the molecular weight of the urea-modified polyester (i) becomes low and the hot offset resistance deteriorates.

<Features of toner binder>
In the present invention, as described above, the polyester prepolymer (A) is characterized by using, as a toner binder, a urea-modified polyester resin obtained by a reaction between an amine (B) and a non-reactive polyester or the like. Other components (including the resin used for the colorant master batch) are also used. In the present invention, the glass transition point (Tg) of the toner binder is usually 40 to 70 ° C., preferably 45 to 55 ° C. If it is less than 40 ° C., the heat-resistant storage stability of the toner deteriorates, and if it exceeds 70 ° C., the low-temperature fixability becomes insufficient. Due to the coexistence of the crosslinked and / or elongated polyester resin, the toner for developing an electrostatic charge image of the present invention exhibits good storage stability even when the glass transition point is low, as compared with known polyester-based toners. As the storage elastic modulus of the toner, the temperature (TG ′) at which the measurement frequency is 20 Hz becomes 1000 Pa is usually 100 ° C. or higher, preferably 110 to 200 ° C. If it is less than 100 ° C., the resistance to hot offset deteriorates. As the viscosity of the toner, the temperature (Tη) at 100 Pa · s at a measurement frequency of 20 Hz is usually 180 ° C. or lower, preferably 90 to 160 ° C. If it exceeds 180 ° C., the low-temperature fixability deteriorates. That is, TG ′ is preferably higher than Tη from the viewpoint of achieving both low temperature fixability and hot offset resistance. In other words, the difference between TG ′ and Tη (TG′−Tη) is preferably 0 ° C. or higher. More preferably, it is 10 degreeC or more, Most preferably, it is 20 degreeC or more. The upper limit of the difference is not particularly limited. Further, from the viewpoint of achieving both heat-resistant storage stability and low-temperature fixability, the difference between Tη and Tg is preferably 0 to 100 ° C. More preferably, it is 10-90 degreeC, Most preferably, it is 20-80 degreeC.

[Aqueous medium phase]
<Aqueous medium>
In the present invention, the aqueous medium in which the resin fine particles described later are dispersed to form the aqueous medium phase may be water alone, or a solvent miscible with water may be used in combination. Examples of miscible solvents include alcohols (methanol, isopropanol, ethylene glycol, etc.), dimethylformamide, tetrahydrofuran, cellosolves, and lower ketones (acetone, methyl ethyl ketone, etc.). These can be used singly or in combination of two or more.

<Resin fine particles>
The resin fine particles in the toner of the present invention are added in the production process in order to control the toner shape (circularity, particle size distribution, etc.) described later. The fine particles are considered to be bonded to the surface portion when an organic solvent phase and an active hydrogen-containing compound (amines) are dispersed in an aqueous medium to form organic dispersed particles, as will be described later. As a result, like the external additive described later, it is considered that the toner base particles obtained are unevenly distributed mainly on the surface portion. In the present invention, it is necessary and important that the amount of resin fine particles contained in the obtained toner particles after the external additive treatment is 0.5 to 5.0 wt%. When the content is less than 0.5 wt%, the storage stability of the toner deteriorates, and blocking occurs during storage and in the developing machine. When the remaining amount is 5.0 wt% or more, the resin fine particles are not present. The exudation of the wax is obstructed, the effect of releasing the wax cannot be obtained, and the occurrence of offset is observed. Further, it is important that the glass transition point (Tg) of the resin fine particles is 40 to 100 ° C. and the weight average molecular weight is 9000 to 200,000. If the Tg of the resin fine particles is less than 40 ° C. and / or the weight average molecular weight is less than 9,000, the storage stability of the toner deteriorates, and blocking occurs during storage and in the developing machine. Is 80 ° C. or higher and / or the weight average molecular weight is 200,000 or higher, the resin fine particles inhibit the adhesiveness to the fixing paper, and an increase in the minimum fixing temperature is observed.

The residual rate of the resin fine particles can be measured by analyzing a substance caused by the resin fine particles, not by the toner particles, using a pyrolysis gas chromatograph mass spectrometer, and calculating from the peak area.
The detector is preferably a mass spectrometer, but is not particularly limited. The dispersion / blending amount of the resin fine particles in the aqueous medium may be set so as to satisfy the conditions relating to the above-mentioned content, but is usually in the range of about 0.5 to 10 wt%.
The resin fine particles may be any resin as long as it can form an aqueous dispersion, and may be a thermoplastic resin or a thermosetting resin. For example, vinyl resins, polyurethane resins, epoxy resins, polyester resins, polyamide resins, polyimides Examples thereof include resins, silicon-based resins, phenol resins, melamine resins, urea resins, aniline resins, ionomer resins, and polycarbonate resins. As the resin fine particles, two or more of the above resins may be used in combination. Of these, vinyl resins, polyurethane resins, epoxy resins, polyester resins, and combinations thereof are preferred because an aqueous dispersion of fine spherical resin particles is easily obtained.
The vinyl resin is a polymer obtained by homopolymerization or copolymerization of a vinyl monomer, such as a styrene- (meth) acrylate resin, a styrene-butadiene copolymer, a (meth) acrylic acid-acrylate polymer, Examples include styrene-acrylonitrile copolymers, styrene-maleic anhydride copolymers, styrene- (meth) acrylic acid copolymers, and the like.

[Other ingredients]
<Colorant>
As the colorant of the present invention, all known dyes and pigments can be used. For example, carbon black, nigrosine dye, iron black, naphthol yellow S, Hansa yellow (10G, 5G, G), cadmium yellow, yellow iron oxide , Ocher, yellow lead, titanium yellow, polyazo yellow, oil yellow, Hansa Yellow (GR, A, RN, R), Pigment Yellow L, Benzidine Yellow (G, GR), Permanent Yellow (NCG), Vulcan Fast Yellow ( 5G, R), Tartrazine Lake, Quinoline Yellow Lake, Anthrazan Yellow BGL, Isoindolinone Yellow, Bengala, Red Dan, Lead Zhu, Cadmium Red, Cadmium Mercury Red, Antimon Zhu, Permanent Red 4R, Para Red , Fais red, parachlorol Nitroaniline Red, Resol Fast Scarlet G, Brilliant Fast Scarlet, Brilliant Carmine B, Permanent Red (F2R, F4R, FRL, FRLL, F4RH), Fast Scarlet VD, Belkan Fast Rubin B, Brilliant Scarlet G, Resol Rubin GX, Permanent Red F5R, Brilliant Carmine 6B, Pigment Scarlet 3B, Bordeaux 5B, Tolujing Maroon, Permanent Bordeaux F2K, Helio Bordeaux BL, Bordeaux 10B, Bon Maroon Light, Bon Maroon Medium, Eosin Lake, Rhodamine Lake B, Rhodamine Lake Y, Alizarin Lake , Thioindigo red B, thioindigo maroon, oil red, quinacridone red, pyrazolone , Polyazo red, chrome vermillion, benzidine orange, perinone orange, oil orange, cobalt blue, cerulean blue, alkali blue rake, peacock blue rake, Victoria blue rake, metal free phthalocyanine blue, phthalocyanine blue, fast sky blue, in Dunslen Blue (RS, BC), Indigo, Ultramarine Blue, Bitumen, Anthraquinone Blue, Fast Violet B, Methyl Violet Lake, Cobalt Purple, Manganese Purple, Dioxane Violet, Anthraquinone Violet, Chrome Green, Zinc Green, Chrome Oxide, Pyridian, Emerald Green, Pigment Green B, Naphthol Green B, Green Gold, Acid Green Lake, Malachite Green Lake Phthalocyanine green, anthraquinone green, titanium oxide, zinc white, lithobon and mixtures thereof can be used. The content of the colorant is usually 1 to 15 wt%, preferably 3 to 10 wt% as the content in the toner base of the present invention.

The colorant used in the present invention can also be used as a master batch combined with a resin. Examples of the binder resin kneaded together with the production of the master batch or the master batch include, for example, the above-mentioned urea-modified polyester resin and non-reactive polyester resin, as well as the weight of styrene such as polystyrene, poly p-chlorostyrene, and polyvinyltoluene, and their substitutes. Copolymer: Styrene-p-chlorostyrene copolymer, styrene-propylene copolymer, styrene-vinyltoluene copolymer, styrene-vinylnaphthalene copolymer, styrene-methyl acrylate copolymer, styrene-ethyl acrylate copolymer Polymer, styrene-butyl acrylate copolymer, styrene-octyl acrylate copolymer, styrene-methyl methacrylate copolymer, styrene-ethyl methacrylate copolymer, styrene-butyl methacrylate copolymer, styrene- α-Chlormeta Methyl acrylate copolymer, styrene-acrylonitrile copolymer, styrene-vinyl methyl ketone copolymer, styrene-butadiene copolymer, styrene-isoprene copolymer, styrene-acrylonitrile-indene copolymer, styrene-maleic acid Styrene copolymers such as copolymers, styrene-maleic acid ester copolymers; polymethyl methacrylate, polybutyl methacrylate, polyvinyl chloride, polyvinyl acetate, polyethylene, polypropylene, polyester, epoxy resin, epoxy polyol resin, polyurethane , Polyamide, polyvinyl butyral, polyacrylic acid resin, rosin, modified rosin, terpene resin, aliphatic or alicyclic hydrocarbon resin, aromatic petroleum resin, chlorinated paraffin, paraffin wax, etc. Alternatively, they can be used in combination.
This master batch can be obtained by mixing and kneading a resin for a master batch and a colorant under a high shear force to obtain a master batch. At this time, an organic solvent can be used to enhance the interaction between the colorant and the resin. In addition, a so-called flushing method, which is a wet cake of a coloring agent, is a method of mixing and kneading an aqueous paste containing water of a coloring agent together with a resin and an organic solvent, transferring the coloring agent to the resin side, and removing moisture and organic solvent components. Can be used as it is, so that it is not necessary to dry and is preferably used. For mixing and kneading, a high shear dispersion device such as a three-roll mill is preferably used. The colorant or master batch can be dissolved or dispersed in the organic solvent phase, but is not limited thereto.

<Release agent>
Further, a wax may be contained together with the toner binder and the colorant. Known waxes can be used as the wax of the present invention, such as polyolefin wax (polyethylene wax, polypropylene wax, etc.); long chain hydrocarbon (paraffin wax, sasol wax, etc.); carbonyl group-containing wax, etc. It is done. Of these, carbonyl group-containing waxes are preferred. Carbonyl group-containing waxes include polyalkanoic acid esters (carnauba wax, montan wax, trimethylolpropane tribehenate, pentaerythritol tetrabehenate, pentaerythritol diacetate dibehenate, glycerin tribehenate, 1,18. -Octadecandiol diol distearate, etc.); polyalkanol esters (tristearyl trimellitic acid, distearyl maleate, etc.); polyalkanoic acid amides (ethylenediamine dibehenyl amide, etc.); polyalkylamides (trimellitic acid tristearyl amide, etc.) And dialkyl ketones (such as distearyl ketone). Among these carbonyl group-containing waxes, polyalkanoic acid esters are preferred. The melting point of the wax of the present invention is usually 40 to 160 ° C, preferably 50 to 120 ° C, more preferably 60 to 90 ° C. A wax having a melting point of less than 40 ° C. has an adverse effect on heat resistant storage stability, and a wax having a melting point of more than 160 ° C. tends to cause a cold offset when fixing at a low temperature. Further, the melt viscosity of the wax is preferably 5 to 1000 cps, more preferably 10 to 100 cps as a measured value at a temperature 20 ° C. higher than the melting point. Waxes exceeding 1000 cps have poor effects for improving hot offset resistance and low-temperature fixability. The amount of the wax (release agent) used is usually 0 to 40 wt%, preferably 3 to 30 wt% as the content in the toner base. Further, the wax (release agent) can be dissolved or dispersed in the organic solvent phase, but is not limited thereto.

<Charge control agent>
The toner of the present invention may contain a charge control agent as necessary. All known charge control agents can be used, such as nigrosine dyes, triphenylmethane dyes, chromium-containing metal complex dyes, molybdate chelate pigments, rhodamine dyes, alkoxy amines, quaternary ammonium salts (fluorine-modified). Quaternary ammonium salts), alkylamides, phosphorus simple substances or compounds, tungsten simple substances or compounds, fluorine-based activators, salicylic acid metal salts, and metal salts of salicylic acid derivatives. Specifically, Nitronine dye Bontron 03, Quaternary ammonium salt Bontron P-51, Metal-containing azo dye Bontron S-34, Oxynaphthoic acid metal complex E-82, Salicylic acid metal complex E- 84, E-89 of a phenol-based condensate (above, Orient Chemical Industry Co., Ltd.), TP-302 of a quaternary ammonium salt molybdenum complex, TP 1415 (above, Hodogaya Chemical Industry Co., Ltd.), quaternary ammonium Copy charge PSY VP2038 of salt, copy blue PR of triphenylmethane derivative, copy charge of quaternary ammonium salt NEG VP2036, copy charge NX VP434 (above, manufactured by Hoechst), LRA-901, LR-147 which is a boron complex (Nippon Carlit Co., Ltd.), copper phthalocyanine, perylene, quinacridone Azo pigments, sulfonate group, carboxyl group, and polymer compounds having a functional group such as a quaternary ammonium salt.

  In the present invention, the amount of charge control agent used is determined by the toner production method including the type of binder resin, the presence or absence of additives used as necessary, and the dispersion method, and is uniquely limited. However, it is preferably used in the range of 0.1 to 10 parts by weight with respect to 100 parts by weight of the binder resin. The range of 0.2 to 5 parts by weight is preferable. When the amount exceeds 10 parts by weight, the chargeability of the toner is too high, the effect of the main charge control agent is reduced, the electrostatic attractive force with the developing roller is increased, the flowability of the developer is reduced, and the image density is reduced. Incurs a decline. These charge control agents can be dissolved and dispersed after being melt-kneaded with a masterbatch and resin, and of course, they may be added directly when dissolved and dispersed in an organic solvent. It is preferable to make it.

[Toner particle adjustment]
The dry toner of the present invention can be produced by the following method, but is not limited thereto.
<Toner production method in aqueous medium>
The aqueous phase used in the present invention is used by adding resin fine particles in advance. The water used for the aqueous phase may be water alone, or a solvent miscible with water may be used in combination. Examples of miscible solvents include alcohol (methanol, isopropanol, ethylene glycol, etc.), dimethylformamide, tetrahydrofuran, cellosolves (methyl cellosolve, etc.), lower ketones (acetone, methyl ethyl ketone, etc.), and the like.

<Dispersion and reaction of organic solvent phase>
As described above, the toner particles are formed by dispersing the organic solvent phase containing the polyester prepolymer (A) in the aqueous medium phase together with the amines (B) and the organic acid compound, and extending and / or extending in the aqueous medium phase. It is formed through a step of crosslinking reaction to form a urea-modified polyester. As a method for stably forming a dispersion comprising a polyester prepolymer (A) in an aqueous phase, a composition of a toner raw material comprising a polyester prepolymer (A) dissolved or dispersed in an organic solvent in an aqueous phase is added. And a method of dispersing by shearing force. Polyester prepolymer (A) dissolved or dispersed in an organic solvent and other toner composition (hereinafter referred to as toner raw material), colorant masterbatch, release agent, charge control agent, unmodified The polyester resin or the like may be mixed when forming the dispersion in the aqueous phase, but after the toner raw material is mixed in advance and dissolved or dispersed in an organic solvent, the mixture is added to the aqueous phase and dispersed. Is more preferable. Further, in the present invention, other toner raw materials such as a colorant, a release agent, and a charge control agent do not necessarily have to be mixed when forming particles in the aqueous phase. After the particles are formed, It may be added. For example, after forming particles containing no colorant, the colorant can be added by a known dyeing method.

  The dispersion method is not particularly limited, and known equipment such as a low-speed shear method, a high-speed shear method, a friction method, a high-pressure jet method, and an ultrasonic wave can be applied. In order to make the particle size of the dispersion 2 to 20 μm, a high-speed shearing type is preferable. When a high-speed shearing disperser is used, the rotational speed is not particularly limited, but is usually 1000 to 30000 rpm, preferably 5000 to 20000 rpm. The dispersion time is not particularly limited, but in the case of a batch method, it is usually 0.1 to 5 minutes. The temperature during dispersion is usually 0 to 150 ° C. (under pressure), preferably 40 to 98 ° C. Higher temperatures are preferred in that the dispersion of the polyester prepolymer (A) has a low viscosity and is easy to disperse.

The usage-amount of the aqueous medium with respect to 100 parts of solid components contained in the organic solvent phase of a polyester prepolymer (A) is 50-2000 weight part normally, Preferably it is 100-1000 weight part. If the amount is less than 50 parts by weight, the dispersion state of the toner composition is poor, and toner particles having a predetermined particle diameter cannot be obtained. If it exceeds 20000 parts by weight, it is not economical. Moreover, a dispersing agent can also be used as needed. The use of a dispersant is preferable in that the particle size distribution becomes sharp and the dispersion is stable.
As a dispersant for emulsifying and dispersing the organic solvent phase containing the polyester prepolymer (A) and the like, anionic surfactants such as alkylbenzene sulfonate, α-olefin sulfonate, phosphate ester, alkylamine salts, Amine salt types such as aminoalcohol fatty acid derivatives, polyamine fatty acid derivatives, imidazoline, and quaternary alkyltrimethylammonium salts, dialkyldimethylammonium salts, alkyldimethylbenzylammonium salts, pyridinium salts, alkylisoquinolinium salts, benzethonium chloride, etc. Nonionic surfactants such as ammonium salt type cationic surfactants, fatty acid amide derivatives, polyhydric alcohol derivatives, such as alanine, dodecyldi (aminoethyl) glycine, di (octylaminoethyl) glycine and N-alkyl Over N, amphoteric surfactants such as N-dimethylammonium betaine.

  Further, by using a surfactant having a fluoroalkyl group, the effect can be obtained in a very small amount. Preferred anionic surfactants having a fluoroalkyl group include fluoroalkyl carboxylic acids having 2 to 10 carbon atoms and metal salts thereof, disodium perfluorooctanesulfonyl glutamate, 31- [omega-fluoroalkyl (C6-C11 ) Oxy] -1-alkyl (C3-C4) sodium sulfonate, 3- [omega-fluoroalkanoyl (C6-C8) mono-N-ethylamino] -1-propanesulfonic acid sodium, fluoroalkyl (C11-C20) carboxylic acid and metal Salt, perfluoroalkylcarboxylic acid (C7 to C13) and its metal salt, perfluoroalkyl (C4 to C12) sulfonic acid and its metal salt, perfluorooctanesulfonic acid diethanolamide, N-propyl-N- (2 hydroxyethyl) -Fluorooctanesulfonamide, perfluoroalkyl (C6-C10) sulfonamidopropyltrimethylammonium salt, perfluoroalkyl (C6-C10) -N-ethylsulfonylglycine salt, monoperfluoroalkyl (C6-C16) ethyl phosphate, etc. Is mentioned.

  Product names include Surflon S-111, S-112, S-113 (Asahi Glass Co., Ltd.), Florard FC-93, FC-95, FC-98, FC-l29 (Sumitomo 3M Co., Ltd.), Unidyne DS-1101 , DS-102, (Taikin Kogyo Co., Ltd.), Megafuck F-l0, F-l20, F-113, F-191, F-812, F-833 (Dainippon Ink Co., Ltd.), Xtop EF-ichi 102, 103, 104, 105, 112, 123A, 123B, 306A, 501, 201, 204 (manufactured by Tochem Products), and Fagento F-100, F150 (manufactured by Neos).

  Further, as the cationic surfactant, aliphatic quaternary ammonium salts such as aliphatic primary, secondary or secondary amic acid, perfluoroalkyl (C6 1 C10) sulfonamidopropyltrimethylammonium salt which right the fluoroalkyl group, Benzalkonium salts, benzethonium chloride, pyridinium salts, imidazolinium salts, trade names include Surflon S-21 (Asahi Glass Co., Ltd.), Florard FC-135 (Sumitomo 3M Co., Ltd.), Unidyne DS-202 (Daikin Industries Co., Ltd.) ), Megafuck F-150, F-824 (Dainippon Ink Co., Ltd.), Xtop EF-32 (Tochem Products Co., Ltd.), Footgent F 1300 (Neos Co., Ltd.), and the like.

Moreover, tricalcium phosphate, calcium carbonate, titanium oxide, colloidal silica, hydroxyapatite, etc. can be used as an inorganic compound dispersant which is hardly soluble in water.
Further, the dispersed droplets may be stabilized by a polymer protective colloid. For example, acrylic acid, methacrylic acid, α-cyanoacrylic acid, α-cyanomethacrylic acid, itaconic acid, crotonic acid, fumaric acid, maleic acid or maleic anhydride or other (meth) acrylic monomer containing a hydroxyl group, For example, β-hydroxyethyl acrylate, β-hydroxyethyl methacrylate, β-hydroxypropyl acrylate, β-hydroxypropyl methacrylate, γ-hydroxypropyl acrylate, γ-hydroxypropyl methacrylate, 3-chloro-2-acrylate -Hydroxypropyl, 3-chloro-2-methacrylic acid methacrylate, diethylene glycol monoacrylate, diethylene glycol monomethacrylate, glycerol monoacrylate, glycerol monomethacrylate, N -Methylol acrylamide, N-methylol methacrylamide, etc., vinyl alcohol or ethers with vinyl alcohol, such as vinyl methyl ether, vinyl ethyl ether, vinyl propyl ether, or esters of compounds containing vinyl alcohol and carboxyl groups For example, pinyl acetate, pinyl propionate, vinyl butyrate, acrylamide, methacrylamide, diacetone acrylamide or their methylol compounds, acid chlorides such as acrylic acid chloride, methacrylic acid chloride, pinylviridine, vinylpyrrolidone, vinylimidazole, ethyleneimine Homopolymers or copolymers such as those having a nitrogen atom or its heterocyclic ring, polyoxyethylene, polyoxypropylene, Oxyethylene alkylamine, polyoxypropylene alkylamine, polyoxyethylene alkylamide, polyoxypropylene alkylamide, polyoxyethylene nonyl phenyl ether, polyoxyethylene lauryl phenyl ether, polyoxyethylene stearyl phenyl ester, polyoxyethylene nonylphenyl Polyoxyethylenes such as esters, celluloses such as methyl cellulose, hydroxyethyl cellulose, and hydroxypropyl cellulose can be used.
In addition, when an acid such as calcium phosphate salt or an alkali-soluble substance is used as the dispersion stabilizer, the calcium phosphate salt is removed from the fine particles by a method such as dissolving the calcium phosphate salt with an acid such as hydrochloric acid and then washing with water. To do. It can also be removed by operations such as enzymatic degradation. When a dispersant is used, the dispersant can remain on the surface of the toner particles. However, it is preferable from the charged surface of the toner that the dispersant is washed and removed after the elongation and / or crosslinking reaction.

The elongation and / or crosslinking reaction time is selected depending on the reactivity of the isocyanate group structure of the prepolymer (A) and the amines (B), but is usually 10 minutes to 40 hours, preferably 2 to 24 hours. is there. The reaction temperature is generally 0 to 150 ° C, preferably 40 to 98 ° C. Moreover, a well-known catalyst can be used as needed. Specific examples include dibutyltin laurate and dioctyltin laurate.
In order to remove the organic solvent from the obtained emulsified dispersion, a method can be employed in which the temperature of the entire system is gradually raised and the organic solvent in the droplets is completely evaporated and removed. Alternatively, it is also possible to spray the emulsified dispersion in a dry atmosphere to completely remove the water-insoluble organic solvent in the droplets to form toner fine particles, and to evaporate and remove the aqueous dispersant together. . As a dry atmosphere in which the emulsified dispersion is sprayed, a gas obtained by heating air, nitrogen, carbon dioxide gas, combustion gas, or the like, in particular, various air streams heated to a temperature equal to or higher than the boiling point of the highest boiling solvent used are generally used. Sufficient quality can be obtained with a short processing time such as spray dryer, belt dryer, rotary kiln.

When the particle size distribution at the time of emulsification dispersion is wide, and washing and drying processes are performed while maintaining the particle size distribution, the particle size distribution can be adjusted by classification into a desired particle size distribution.
In the classification operation, the fine particle portion can be removed in the liquid by a cyclone, a decanter, centrifugation, or the like. Of course, the classification operation may be performed after obtaining the powder as a powder after drying, but it is preferably performed in a liquid in terms of efficiency. The obtained unnecessary fine particles or coarse particles can be returned to the kneading step and used for forming particles. At that time, fine particles or coarse particles may be wet. The dispersant used is preferably removed from the obtained dispersion as much as possible, but it is preferable to carry out it simultaneously with the classification operation described above.

  Mixing or giving mechanical impact force to the powder mixture after drying with different types of particles such as release agent fine particles, charge control fine particles, fluidizing agent fine particles, and colorant fine particles By immobilizing and fusing on the surface, it is possible to prevent detachment of foreign particles from the surface of the resulting composite particle. Specific means include a method of applying an impact force to the mixture by blades rotating at high speed, a method of injecting and accelerating the mixture in a high-speed air stream, and causing particles or composite particles to collide with an appropriate collision plate, etc. is there. As equipment, Ong mill (manufactured by Hosokawa Micron Co., Ltd.), I-type mill (manufactured by Nippon Pneumatic Co., Ltd.) has been modified to reduce the pulverization air pressure, hybridization system (manufactured by Nara Machinery Co., Ltd.), kryptron System (manufactured by Kawasaki Heavy Industries, Ltd.), automatic mortar, etc.

[Application of external additives]
As the external additive for assisting the fluidity, developability and chargeability of the colored particles obtained in the present invention, inorganic fine particles can be preferably used. The primary particle diameter of the inorganic fine particles is preferably 5 mμ to 2 μm, and particularly preferably 5 mμ to 500 mμ. Moreover, it is preferable that the specific surface area by BET method is 20-500 m < ² > / g. The use ratio of the inorganic fine particles is preferably 0.01 to 5 wt% of the toner, and particularly preferably 0.01 to 2.0 wt%.
Specific examples of the inorganic fine particles include, for example, silica, alumina, titanium oxide, barium titanate, magnesium titanate, calcium titanate, strontium titanate, zinc oxide, tin oxide, quartz sand, clay, mica, wollastonite, diatomaceous earth. Examples include soil, chromium oxide, cerium oxide, pengala, antimony trioxide, magnesium oxide, zirconium oxide, barium sulfate, barium carbonate, calcium carbonate, silicon carbide, and silicon nitride.
Other polymer fine particles such as polystyrene obtained by soap-free emulsion polymerization, suspension polymerization and dispersion polymerization, methacrylic acid ester and acrylic acid ester copolymer, polycondensation system such as silicone, benzoguanamine and nylon, and thermosetting resin Examples include polymer particles.
Such a fluidizing agent can be surface-treated to increase hydrophobicity and prevent deterioration of flow characteristics and charging characteristics even under high humidity. For example, silane coupling agents, silylating agents, silane coupling agents having a fluoroalkyl group, organic titanate coupling agents, aluminum coupling agents, silicone oils, modified silicone oils and the like are preferable surface treatment agents. .

  On the other hand, examples of the cleaning property improver for removing the developer after transfer remaining on the photoreceptor and the primary transfer medium include fatty acid metal salts such as zinc stearate, calcium stearate and stearic acid, such as polymethyl methacrylate fine particles, polystyrene. Examples thereof include fine polymer particles produced by soap-free emulsion polymerization of fine particles and the like. The polymer fine particles preferably have a relatively narrow particle size distribution and a volume average particle size of 0.01 to 1 μm.

[Toner shape, etc.]
<Circularity and circularity distribution>
It is important that the toner in the present invention has a specific shape and shape distribution. An toner having an average circularity of less than 0.90 and an irregular shape that is too far from a spherical shape exhibits satisfactory transferability and dust. A high-quality image with no image cannot be obtained. As a method for measuring the shape, an optical detection band method is suitable in which a suspension containing particles is passed through an imaging unit detection band on a flat plate, and a particle image is optically detected and analyzed by a CCD camera. Toner having an average circularity of 0.980 to 0.900, which is a value obtained by dividing the perimeter of an equivalent circle having the same projected area obtained by this method by the perimeter of the actual particle, has high reproducibility with an appropriate density reproducibility. It was found to be effective in forming a clear image. When the average circularity is 0.980 or more, in a system that employs blade cleaning or the like, poor cleaning occurs on the photosensitive member and the transfer belt, causing stain on the image. For example, development / transfer with a low image area ratio results in a small amount of residual toner and poor cleaning does not become a problem. The image-formed toner may be generated as a transfer residual toner on the photosensitive member, and if accumulated, the image may be soiled. In addition, the charging roller that contacts and charges the photosensitive member is contaminated, and the original charging ability cannot be exhibited. This value was measured as an average circularity by a flow type particle image analyzer FPIA-2100 (manufactured by Toa Medical Electronics Co., Ltd.). A specific measurement method will be described later.

<Volume average particle diameter, number average particle diameter>
The toner of the present invention preferably has a volume average particle diameter (Dv) of 3 to 8 μm, and more preferably 4 to 7 μm. The ratio (Dv / Dn) of the volume average particle diameter (Dv) to the number average particle diameter (Dn) is 1.25 or less, preferably 1.10 to 1.20. Here, the volume average particle diameter (Dv) is defined as Dv = [Σ (nD ³ ) / Σn] ^1/3 (where n is the number of particles and D is the particle diameter). In the present invention, by setting the value of (Dv / Dn) within the above range, it is excellent in all of heat resistant storage stability, low temperature fixing property, and hot offset resistance. Excellent two-component developer, even with long-term toner balance, fluctuations in toner particle diameter in the developer are reduced, and even with long-term agitation in the developing device, it is stable and stable. Developability is obtained. Even when used as a one-component developer, even if the balance of the toner is performed, the fluctuation of the toner particle diameter is reduced, and the toner is filmed on the developing roller and the toner is made thin. The toner is not fused to a member such as a blade, and good and stable developability and an image can be obtained even in the long-term use (stirring) of the developing device.

In general, it is said that the smaller the particle size of the toner, the more advantageous it is to obtain a high-resolution and high-quality image, but it is disadvantageous for transferability and cleaning properties. is there. Further, when the volume average particle diameter is smaller than the range of the present invention, in the case of the two-component developer, the toner is fused to the surface of the carrier during a long period of stirring in the developing device, and the charging ability of the carrier is reduced, When used as an agent, toner filming on the developing roller and toner fusion to a member such as a blade for thinning the toner are likely to occur. Further, these phenomena are the same for the toner having a fine powder content larger than the range of the present invention.
On the contrary, when the particle diameter of the toner is larger than the range of the present invention, it becomes difficult to obtain a high resolution and high quality image, and when the balance of the toner in the developer is performed, In many cases, the variation of the particle size becomes large. It was also clarified that the same applies when the volume average particle diameter / number average particle diameter (Dv / Dn) is too large. Further, if the volume average particle diameter / number average particle diameter (Dv / Dn) is too small, there are preferable aspects from the viewpoint of stabilizing the behavior of the toner and equalizing the charge amount, but the toner becomes insufficiently charged. In some cases, it was also found that the cleaning property may be deteriorated.
The volume average particle size / number average particle size (Dv / Dn) was measured using a particle size measuring device “Coulter Counter TAII” manufactured by Coulter Electronics Co., Ltd., with a volume average particle size (Dv ) And the number average particle diameter (Dn).

[Two-component carrier]
When the toner of the present invention is used for a two-component developer, it may be used by mixing it with a magnetic carrier. Part is preferable, and the range of 3 to 9 parts by weight is more preferable. As the magnetic carrier, conventionally known ones such as iron powder, ferrite powder, magnetite powder, magnetic resin carrier having a particle diameter of about 20 to 200 μm can be used. Examples of the coating material include amino resins such as urea-formaldehyde resin, melamine resin, benzoguanamine resin, urea resin, polyamide resin, and epoxy resin. Polyvinyl and polyvinylidene resins such as acrylic resins, polymethyl methacrylate resins, polyacrylonitrile resins, polyvinyl acetate resins, polyvinyl alcohol resins, polyvinyl butyral resins, polystyrene resins and styrene acrylic copolymer resins, Halogenated olefin resin such as vinyl, polyester resin such as polyethylene terephthalate resin and polybutylene terephthalate resin, polycarbonate resin, polyethylene resin, polyvinyl fluoride resin, polyvinylidene fluoride resin, polytrifluoroethylene resin, polyhexafluoro Propylene resin, copolymer of vinylidene fluoride and acrylic monomer, copolymer of vinylidene fluoride and vinyl fluoride, tetrafluoroethylene and vinylidene fluoride And fluoro such as terpolymers of non-fluoride monomers including, and silicone resins. Moreover, you may contain electrically conductive powder etc. in coating resin as needed. As the conductive powder, metal powder, carbon black, titanium oxide, tin oxide, zinc oxide or the like can be used. These conductive powders preferably have an average particle diameter of 1 μm or less. When the average particle diameter is larger than 1 μm, it becomes difficult to control electric resistance. The toner of the present invention can also be used as a one-component magnetic toner that does not use a carrier or a non-magnetic toner.

[Image forming equipment]
Hereinafter, an image forming apparatus using the electrophotographic toner of the present invention or a two-component developer composed of the toner and a carrier will be described.
-Intermediate transfer member-
An embodiment of an intermediate transfer member of a transfer system in the present invention will be described. FIG. 1 is a schematic configuration diagram of a copying machine according to the present embodiment. Around a photosensitive drum (hereinafter referred to as a photosensitive member) 10 as an image carrier, a charging roller 20 as a charging device, an exposure device 30, a cleaning device 60 having a cleaning blade, a static elimination lamp 70 as a static elimination device, and development. An apparatus 40 and an intermediate transfer member 50 as an intermediate transfer member are provided. The intermediate transfer member 50 is suspended by a plurality of suspension rollers 51 and is configured to run endlessly in the direction of the arrow by a driving unit such as a motor (not shown). A part of the suspension roller 51 also serves as a transfer bias roller for supplying a transfer bias to the intermediate transfer member, and a predetermined transfer bias voltage is applied from a power source (not shown). A cleaning device 90 having a cleaning blade for the intermediate transfer member 50 is also provided. Further, a transfer roller 80 is provided as a transfer means for transferring the developed image onto the transfer paper 100 as the final transfer material, facing the intermediate transfer body 50, and the transfer roller 80 is transferred by a power supply device (not shown). Supplied. A corona charger 52 is provided around the intermediate transfer member 50 as charge applying means.

The developing device 40 includes a developing belt 41 as a developer carrier, a black (hereinafter referred to as “Bk”) developing unit 45K, a yellow (hereinafter referred to as “Y”) developing unit 45Y, The developing unit 45M is hereinafter referred to as magenta and the cyan (hereinafter referred to as C) developing unit 45C. Further, the developing belt 41 is stretched between a plurality of belt rollers, and is configured to run endlessly in a direction indicated by an arrow by a driving unit such as a motor (not shown). Moves at approximately the same speed as 10.
Since the structure of each developing unit is common, the following description will be given only for the Bk developing unit 45K, and the other developing units 45Y, 45M, and 45C will be described in the parts corresponding to those in the Bk developing unit 45K in the drawing. Y, M, and C are added after the numbers given to the units, and the description is omitted. The developing unit 45K is disposed so as to immerse the developing tank 42K containing a high-viscosity, high-concentration liquid developer containing toner particles and a carrier liquid component, and the lower part in the liquid developer in the developing tank 42K. And a coating roller 44K for thinning the developer pumped from the pumping roller 43K and applying it to the developing belt 41. The application roller 44K has conductivity, and a predetermined bias is applied from a power source (not shown).
In addition to the apparatus configuration as shown in FIG. 1, the apparatus configuration of the copying machine according to the present embodiment is an apparatus configuration in which development units 45 for each color are provided around the photoconductor 10 as shown in FIG. It may be.

Next, the operation of the copying machine according to the present embodiment will be described. In FIG. 1, the photosensitive member 10 is uniformly charged by the charging roller 20 while being driven to rotate in the direction of the arrow, and then the reflected light from the original is imaged and projected by an optical system (not shown) by the exposure device 30. An electrostatic charge image is formed on the surface. This electrostatic charge image is developed by the developing device 40 to form a toner image as a visible image. The developer thin layer on the developing belt 41 is peeled off from the belt 41 in a thin layer state by contact with the photosensitive member in the developing region, and moves to a portion where a latent image is formed on the photosensitive member 10. The toner image developed by the developing device 40 is transferred to the surface of the intermediate transfer member 50 at the contact portion (primary transfer region) between the photosensitive member 10 and the intermediate transfer member 50 moving at a constant speed (primary transfer). Transcription). When transferring three or four colors to be superimposed, this process is repeated for each color to form a color image on the intermediate transfer member 50.
The corona charger 52 for applying an electric charge to the superimposed toner image on the intermediate transfer member is provided at a contact facing portion between the photosensitive member 10 and the intermediate transfer member 50 in the rotation direction of the intermediate transfer member 50. It is installed on the downstream side and on the upstream side of the contact facing portion between the intermediate transfer member 50 and the transfer paper 100. The corona charger 52 gives the toner image a true charge having the same polarity as the charge polarity of the toner particles forming the toner image, and is sufficient for good transfer to the transfer paper 100. Charge is applied to the toner image. The toner image is charged by the corona charger 52 and then transferred to the transfer paper 100 conveyed in the direction of the arrow from a paper supply unit (not shown) by a transfer bias from the transfer roller 80 (two). Next transfer). Thereafter, the transfer paper 100 onto which the toner image has been transferred is separated from the photoconductor 10 by a separation device (not shown), and after a fixing process is performed by a fixing device (not shown), the transfer paper 100 is discharged from the device. On the other hand, after the transfer, the untransferred toner is collected and removed by the cleaning device 60, and the residual charge is discharged by the discharging lamp 70 in preparation for the next charging.

As described above, the static friction coefficient of the intermediate transfer member is preferably 0.1 to 0.6, and more preferably 0.3 to 0.5. The volume resistance of the intermediate transfer member is preferably from several Ωcm to 10 ³ Ωcm. When the volume resistance is set to several Ωcm or more and 10 ³ Ωcm or less, the intermediate transfer member itself is prevented from being charged, and the charge imparted by the charge imparting means hardly remains on the intermediate transfer member. Transfer unevenness can be prevented. Further, it is possible to easily apply a transfer bias at the time of secondary transfer.
The material of the intermediate transfer member is not particularly limited, and all known materials can be used. An example is shown below. (1) A material having a high Young's modulus (tensile modulus) is used as a single-layer belt. PC (polycarbonate), PVDF (polyvinylidene fluoride), PAT (polyalkylene terephthalate), PC (polycarbonate) / PAT ( Polyalkylene terephthalate) blend material, ETFE (ethylene tetrafluoroethylene copolymer) / PC, ETFE / PAT, PC / PAT blend material, carbon black dispersed thermosetting polyimide, and the like. These single-layer belts with a high Young's modulus have the advantage that the amount of deformation with respect to stress during image formation is small, and in particular, there is little misregistration during color image formation. (2) A belt having a two- to three-layer structure in which a belt having a high Young's modulus is used as a base layer and a surface layer or an intermediate layer is provided on the outer periphery thereof. Therefore, the line image can be prevented from being lost due to the height. (3) Belts having a relatively low Young's modulus using rubber and elastomer, and these belts have the advantage that line images are hardly lost due to their softness. In addition, the width of the belt is made larger than that of the drive roll and the tension roll, and the elasticity of the belt ear protruding from the roll is used to prevent meandering, so that low cost can be realized without the need for ribs or meandering prevention devices. .
Conventionally, a fluorine-based resin, a polycarbonate resin, a polyimide resin, or the like has been used for the intermediate transfer belt, but in recent years, an elastic belt in which the entire belt layer or a part of the belt is used as an elastic member has been used. The transfer of a color image using a resin belt has the following problems.

A color image is usually formed with four colored toners. On one color image, toner layers of 1 to 4 layers are formed. The toner layer receives pressure by passing through the primary transfer (transfer from the photoreceptor to the intermediate transfer belt) and the secondary transfer (transfer from the intermediate transfer belt to the sheet), and the cohesive force between the toners increases. When the cohesive force between the toners increases, the phenomenon of missing characters in the characters and missing edges in the solid portion image tends to occur. Since the resin belt has a high hardness and does not deform according to the toner layer, the toner layer is easily compressed, and the character dropout phenomenon is likely to occur.
Recently, there is an increasing demand for forming full-color images on various papers, for example, Japanese paper, intentionally irregularities, and forming images on paper. However, a paper with poor smoothness is liable to generate toner and voids at the time of transfer, and transfer loss is likely to occur. When the transfer pressure at the secondary transfer portion is increased to improve the adhesion, the condensing power of the toner layer is increased, and the above-described character void is generated.

The elastic belt is used for the following purposes. The elastic belt is deformed corresponding to the toner layer and the paper having poor smoothness at the transfer portion. In other words, because the elastic belt deforms following local irregularities, the paper does not have excessive flatness and does not excessively increase the transfer pressure with respect to the toner layer. In contrast, a transfer image having excellent uniformity can be obtained.
The elastic belt resin is polycarbonate, fluororesin (ETFE, PVDF), polystyrene, chloropolystyrene, poly-α-methylstyrene, styrene-butadiene copolymer, styrene-vinyl chloride copolymer, styrene-vinyl acetate copolymer. Styrene-maleic acid copolymer, styrene-acrylic acid ester copolymer (for example, styrene-methyl acrylate copolymer, styrene-ethyl acrylate copolymer, styrene-butyl acrylate copolymer, styrene- Octyl acrylate copolymer and styrene-phenyl acrylate copolymer), styrene-methacrylic acid ester copolymer (for example, styrene-methyl methacrylate copolymer, styrene-ethyl methacrylate copolymer, styrene-methacrylic acid). Acid phenyl copolymer, etc.), styrene -Styrenic resins (monopolymer or copolymer containing styrene or styrene-substituted product) such as methyl α-chloroacrylate copolymer, styrene-acrylonitrile-acrylate ester copolymer, methyl methacrylate resin, methacrylic acid Butyl resin, ethyl acrylate resin, butyl acrylate resin, modified acrylic resin (for example, silicone-modified acrylic resin, vinyl chloride resin-modified acrylic resin, acrylic / urethane resin, etc.), vinyl chloride resin, styrene-vinyl acetate copolymer, Vinyl chloride-vinyl acetate copolymer, rosin-modified maleic acid resin, phenol resin, epoxy resin, polyester resin, polyester polyurethane resin, polyethylene, polypropylene, polybutadiene, polyvinylidene chloride, ionomer resin, polyurethane resin, silica One type or a combination of two or more types selected from the group consisting of carbon resins, ketone resins, ethylene-ethyl acrylate copolymers, xylene resins and polyvinyl butyral resins, polyamide resins, modified polyphenylene oxide resins and the like can be used. . However, it is a matter of course that the material is not limited to the above materials.

  Elastic rubber and elastomer include butyl rubber, fluorine rubber, acrylic rubber, EPDM, NBR, acrylonitrile-butadiene-styrene rubber natural rubber, isoprene rubber, styrene-butadiene rubber, butadiene rubber, ethylene-propylene rubber, ethylene-propylene ter Polymer, chloroprene rubber, chlorosulfonated polyethylene, chlorinated polyethylene, urethane rubber, syndiotactic 1,2-polybutadiene, epichlorohydrin rubber, ricone rubber, fluororubber, polysulfide rubber, polynorbornene rubber, hydrogenated nitrile rubber , Selected from the group consisting of thermoplastic elastomers (for example, polystyrene, polyolefin, polyvinyl chloride, polyurethane, polyamide, polyurea, polyester, fluororesin) It is possible to use one kind or two or more kinds of combinations that. However, it is a matter of course that the material is not limited to the above materials.

There are no particular restrictions on the conductive agent for adjusting the resistance value. For example, carbon black, graphite, metal powder such as aluminum and nickel, tin oxide, titanium oxide, antimony oxide, indium oxide, potassium titanate, antimony oxide-tin oxide composite Conductive metal oxides such as oxide (ATO) and indium oxide-tin oxide composite oxide (ITO), and conductive metal oxides are coated with insulating fine particles such as barium sulfate, magnesium silicate, and calcium carbonate. But you can. Of course, the conductive agent is not limited thereto.
Surface layer materials and surface layers are required to prevent contamination of the photoreceptor by elastic materials, reduce surface friction resistance to the surface of the transfer belt, reduce toner adhesion, and improve cleaning properties and secondary transfer properties. . For example, materials that use one or a combination of two or more of polyurethane, polyester, epoxy resin, etc. to reduce surface energy and increase lubricity, such as fluorine resin, fluorine compound, fluorocarbon, titanium dioxide, silicon carbide, etc. These powders and particles can be used by dispersing one type, two or more types, or a combination of particles having different particle sizes. Further, it is also possible to use a material having a surface energy reduced by forming a fluorine-rich layer on the surface by heat treatment, such as a fluorine-based rubber material.

The belt manufacturing method is not limited. For example, a centrifugal molding method in which a material is poured into a rotating cylindrical mold to form a belt, a spray coating method in which a liquid paint is sprayed to form a film, and a cylindrical mold are used. Examples include, but are not limited to, a dipping method in which the material is dipped in a solution of the material, a casting method in which it is injected into the inner mold and the outer mold, a method in which a compound is wound around a cylindrical mold and vulcanized and polished. In general, a belt is manufactured by combining a plurality of manufacturing methods.
As a method for preventing elongation as an elastic belt, there are a method of forming a rubber layer in a core resin layer with little elongation, a method of putting a material for preventing elongation into a core layer, and the like, but the method is limited to a specific production method is not.
The material constituting the core layer for preventing elongation includes, for example, natural fibers such as cotton and silk; polyester fibers, nylon fibers, acrylic fibers, polyolefin fibers, polyvinyl alcohol fibers, polyvinyl chloride fibers, polyvinylidene chloride fibers, One or two selected from the group consisting of synthetic fibers such as polyurethane fibers, polyacetal fibers, polyfluoroethylene fibers and phenol fibers; inorganic fibers such as carbon fibers, glass fibers and boron fibers; and metal fibers such as iron fibers and copper fibers A combination of two or more species is used to form a woven fabric or a yarn. Of course, the material is not limited to the above.

The yarn may be twisted in any manner, such as one or a plurality of filaments twisted, a single twisted yarn, various twisted yarns, a double yarn, or the like. Further, for example, fibers of a material selected from the above material group may be blended. Of course, the yarn can be used after being subjected to an appropriate conductive treatment. On the other hand, as the woven fabric, any woven fabric such as knitted fabric can be used. Of course, a cross-woven fabric can also be used, and naturally conductive treatment can be performed.
The production method for providing the core layer is not particularly limited. For example, a method of providing a coating layer on a woven fabric woven in a cylindrical shape on a mold or the like, or a liquid woven woven fabric in a cylindrical shape. Examples thereof include a method in which a coating layer is provided on one or both surfaces of a core layer by dipping in rubber or the like, and a method in which a thread is spirally wound around a mold or the like at an arbitrary pitch and a coating layer is provided thereon.
The thickness of the elastic layer depends on the hardness of the elastic layer, but if it is too thick, the surface expands and contracts and cracks are likely to occur on the surface layer. Also, it is not preferable that the thickness is too large (approximately 1 mm or more) because the amount of expansion and contraction becomes large and the image is stretched.

~ Charging device ~
FIG. 3 shows a schematic configuration of an example of an image forming apparatus using a contact-type charging device. The photosensitive member as the member to be charged and the image carrier is driven to rotate at a predetermined speed (process speed) in the direction of the arrow. The charging roller 52 as a charging member brought into contact with the photosensitive drum is basically composed of a cored bar 521 and a conductive rubber layer 522 formed concentrically on the outer periphery of the cored bar, and both ends of the cored bar are not shown. In addition to being held freely rotating by a bearing member or the like, the photosensitive drum is pressed with a predetermined pressing force by a pressing means (not shown). In this case, the charging roller 52 is used to drive the photosensitive drum 10 to rotate. Follow and rotate. The charging roller 52 is formed to have a diameter of 16 mm by coating a medium resistance rubber layer 522 of about 100,000 Ω · cm on a core metal 521 having a diameter of 9 mm.
The cored bar 521 of the charging roller 52 and the illustrated power source 53 are electrically connected, and a predetermined bias is applied to the charging roller 52 by the power source 53. As a result, the peripheral surface of the photoconductor is uniformly charged to a predetermined polarity and potential.

The shape of the charging member used in the present invention may take any form such as a magnetic brush or a fur brush in addition to the roller, and can be selected according to the specifications and form of the electrophotographic apparatus. When the magnetic brush is used, the magnetic brush is made up of various ferrite particles such as Zn-Cu ferrite as a charging member, a nonmagnetic conductive sleeve for supporting the ferrite member, and a magnet roll included in the nonmagnetic conductive sleeve. In addition, when using a fur brush, for example, as a material of the fur brush, a fur treated with carbon, copper sulfide, metal or metal oxide is used, and this is wound around a metal or other conductive core. By charging or pasting, it becomes a charger.
Of course, the charging device used in the present invention is not limited to the contact type charging device as described above, but an image forming apparatus in which ozone generated from the charging device is reduced can be obtained. Is preferably used.

-Photoconductor-
As the electrophotographic photoreceptor used in the present invention, a conductive support is heated to 50 ° C. to 400 ° C., and a vacuum deposition method, a sputtering method, an ion plating method, a thermal CVD method, a photo CVD is applied on the support. An amorphous silicon photoconductor (hereinafter referred to as “a-Si photoconductor”) having a photoconductive layer made of a-Si can be used by a film forming method such as a plasma CVD method. Among them, a plasma CVD method, that is, a method in which a source gas is decomposed by direct current, high frequency or microwave glow discharge to form an a-Si deposited film on a support is preferably used.
The layer structure of the amorphous silicon photoconductor is, for example, as follows. FIG. 4 is a schematic configuration diagram for explaining a layer configuration. In the electrophotographic photoreceptor 500 shown in FIG. 4A, a photoconductive layer 502 made of a-Si: H, X and having photoconductivity is provided on a support 501. An electrophotographic photosensitive member 500 shown in FIG. 4B includes a photoconductive layer 502 made of a-Si: H, X and having photoconductivity, and an amorphous silicon surface layer 503 on a support 501. It is configured. An electrophotographic photoreceptor 500 shown in FIG. 4C has a photoconductive layer 502 made of a-Si: H, X and having photoconductivity on a support 501, an amorphous silicon-based surface layer 503, and And an amorphous silicon based charge injection blocking layer 504. In an electrophotographic photoreceptor 500 shown in FIG. 4D, a photoconductive layer 502 is provided on a support 501. The photoconductive layer 502 includes a charge generation layer 505 made of a-Si: H, X and a charge transport layer 506, and an amorphous silicon surface layer 503 is provided thereon.

The support for the photoreceptor may be conductive or electrically insulating. Examples of the conductive support include metals such as Al, Cr, Mo, Au, In, Nb, Te, V, Ti, Pt, Pd, and Fe, and alloys thereof such as stainless steel. Also, at least the surface of the electrically insulating support such as polyester, polyethylene, polycarbonate, cellulose acetate, polypropylene, polyvinyl chloride, polystyrene, polyamide, etc. A conductively treated support can also be used.
The shape of the support can be a cylindrical or plate-like or endless belt with a smooth surface or an uneven surface, and the thickness is appropriately determined so that a desired photoreceptor for an image forming apparatus can be formed. When flexibility as a photoreceptor for an image forming apparatus is required, the thickness can be made as thin as possible within a range in which the function as a support can be sufficiently exhibited. However, the support is usually 10 μm or more from the viewpoints of production and handling, mechanical strength, and the like.

In the amorphous silicon photoconductor that can be used in the present invention, a charge injection blocking layer that functions to block charge injection from the conductive support side is provided between the conductive support and the photoconductive layer as necessary. It is more effective to provide this (FIG. 8C). That is, the charge injection blocking layer has a function of blocking charge injection from the support side to the photoconductive layer side when the photosensitive layer is subjected to a charging process with a certain polarity on its free surface. When charged, it has a so-called polarity dependency that does not exhibit such a function. In order to provide such a function, the charge injection blocking layer contains a relatively large number of atoms for controlling conductivity as compared with the photoconductive layer.
The layer thickness of the charge injection blocking layer is preferably 0.1 to 5 μm, more preferably 0.3 to 4 μm, and most preferably 0.5 to 0.5 from the viewpoints of obtaining desired electrophotographic characteristics and economic effects. It is desirable to be 3 μm.
The photoconductive layer is formed on the undercoat layer as necessary, and the layer thickness of the photoconductive layer 502 is appropriately determined as desired from the viewpoint of obtaining desired electrophotographic characteristics and economic effects, preferably It is desirable that the thickness is 1 to 100 μm, more preferably 20 to 50 μm, and most preferably 23 to 45 μm.

The charge transport layer is a layer mainly having a function of transporting charges when the photoconductive layer is functionally separated. The charge transport layer includes at least silicon atoms, carbon atoms, and fluorine atoms as constituent elements, and is formed of a-SiC (H, F, O) including hydrogen atoms and oxygen atoms as required. It has conductive properties, particularly charge retention properties, charge generation properties, and charge transport properties. In the present invention, it is particularly preferable to contain an oxygen atom.
The layer thickness of the charge transport layer is appropriately determined as desired from the viewpoint of obtaining desired electrophotographic characteristics and economic effects, and the charge transport layer is preferably 5 to 50 μm, more preferably 10 to 40 μm, Optimally, it is desirably 20 to 30 μm.
The charge generation layer is a layer mainly having a function of generating charges when the photoconductive layer is functionally separated. This charge generation layer is composed of a-Si: H containing at least silicon atoms as components and substantially no carbon atoms and, if necessary, hydrogen atoms, and has desired photoconductive properties, particularly charge generation properties. , Has charge transport properties.
The layer thickness of the charge generation layer is appropriately determined as desired from the viewpoint of obtaining desired electrophotographic characteristics and economic effects, etc., preferably 0.5 to 15 μm, more preferably 1 to 10 μm, optimally 1 ˜5 μm.

If necessary, the amorphous silicon photoreceptor that can be used in the present invention can be provided with a surface layer on the photoconductive layer formed on the support as described above. It is preferable to form a surface layer. This surface layer has a free surface and is provided to achieve the object of the present invention mainly in moisture resistance, continuous repeated use characteristics, electrical pressure resistance, use environment characteristics, and durability.
The thickness of the surface layer in the present invention is usually 0.01 to 3 μm, preferably 0.05 to 2 μm, and most preferably 0.1 to 1 μm. If the layer thickness is less than 0.01 μm, the surface layer is lost due to wear or the like during use of the photoreceptor, and if it exceeds 3 μm, electrophotographic characteristics such as an increase in residual potential are observed.
Amorphous silicon photoconductors have high surface hardness, high sensitivity to long-wavelength light such as semiconductor lasers (770 to 800 nm), etc., and almost no deterioration due to repeated use. Therefore, high-speed copying machines and laser beam printers are used. It is used as an electrophotographic photoreceptor such as (LBP).

-Fixing device (surf fixing device)-
As the fixing device 25 in the present invention, a so-called surf fixing device 250 that rotates and fixes a fixing film 251 as shown in FIG. 5 is used. More specifically, the fixing film 251 is an endless belt-like heat-resistant film, and is held by a driving roller 256 that is a supporting rotating body of the film, a driven roller 257, and a heater support provided below the two rollers. The heating body 252 is disposed so as to be fixedly supported.
The driven roller 257 also serves as a tension roller for the fixing film 251. The fixing film 251 is driven to rotate in the clockwise direction by the rotation of the driving roller 256 in the clockwise direction in the drawing. The rotational driving speed is adjusted to a speed at which the transfer material and the fixing film 251 have the same speed in the fixing nip region L where the pressure roller 254 and the fixing film 251 are in contact with each other.
Here, the pressure roller 254 is a roller having a rubber elastic layer having good releasability such as silicon rubber, and abutting against the fixing nip region L with a total pressure of 4 to 10 kg while rotating counterclockwise. It is pressed with pressure.
The fixing film 251 preferably has excellent heat resistance, releasability and durability, and a thin film having a total thickness of 100 μm or less, preferably 40 μm or less is used. For example, at least an image of a single layer film of a heat-resistant resin such as polyimide, polyetherimide, PES (polyether sulfide), PFA (tetrafluoroethylene barfluoroalkyl vinyl ether copolymer resin), or a composite layer film, for example, a 20 μm thick film The contact surface is coated with a release coating layer of PTFE (tetrafluoroethylene resin), PFA or other fluororesin with a conductive material added to a thickness of 10 μm, or an elastic layer such as fluororubber or silicon rubber. It is what.

In FIG. 5, the heating body 252 of this embodiment is composed of a flat substrate 255 and a fixing heater 253. The flat substrate 255 is made of a material having high thermal conductivity and high electrical resistivity, such as alumina, and a fixing film. A fixing heater composed of a resistance heating element is installed on the surface in contact with 251 in the longitudinal direction. The fixing heater 253 is obtained by coating an electric resistance material such as Ag / Pd or Ta ₂ N in a linear or belt shape by screen printing or the like. In addition, electrodes (not shown) are formed at both ends of the fixing heater 253, and the resistance heating element generates heat when energized between the electrodes. Further, a fixing temperature sensor 258 constituted by a thermistor is provided on the surface of the substrate 255 opposite to the surface on which the fixing heater 253 is provided.
The substrate temperature information detected by the fixing temperature sensor 258 is sent to a control unit (not shown), and the amount of electric power supplied to the fixing heater is controlled by the control unit, so that the heating body 252 is controlled to a predetermined temperature.
Of course, the fixing device used in the present invention is not limited to the surf fixing device 250 as described above. However, since the image forming apparatus 100 using the fixing device 25 capable of efficiently reducing the rise time can be obtained. It is preferable to use the surf fixing device 250.

-Fixing device (electromagnetic induction heating method (IH fixing device))-
In the fixing device according to the present invention, as shown in FIG. 6A, the heating unit generates Joule heat by eddy current generated in the magnetic metal member by an alternating magnetic field, and the heating body including the metal member is heated by electromagnetic induction. A so-called electromagnetic induction heating type fixing device (IH fixing device) is used.
The fixing device shown in FIG. 6A includes a heating roller 1 heated by electromagnetic induction of the induction heating unit 6, a fixing roller 2 arranged in parallel to the heating roller 1, and the heating roller 1 and the fixing roller 2. An endless belt-like heat-resistant belt (toner heating medium) 3 that is stretched and heated by the heating roller 1 and rotated in the direction of arrow A by at least one of these rollers, and a fixing roller via the belt 3 2 and a pressure roller 4 that rotates in the forward direction with respect to the belt 3. The heating roller 1 is made of a hollow cylindrical magnetic metal member such as iron, cobalt, nickel, or an alloy of these metals, and has a low heat capacity and a high temperature rise. The fixing roller 2 includes a metal core 2a made of, for example, stainless steel, and an elastic member 2b in which a heat-resistant silicone rubber is solid or foamed and covered with the core 2a. In order to form a contact portion having a predetermined width between the pressure roller 4 and the fixing roller 2 by the pressing force from the pressure roller 4, the outer diameter is made larger than that of the heating roller 1. With this configuration, the heat capacity of the heating roller 1 becomes smaller than the heat capacity of the fixing roller 2, and the heating roller 1 is rapidly heated to shorten the warm-up time. The belt 3 stretched between the heating roller 1 and the fixing roller 2 is heated at a contact portion W1 with the heating roller 1 heated by the induction heating means 6.

  The inner surface of the belt 3 is continuously heated by the rotation of the rollers 1 and 2, and as a result, the entire belt is heated. The pressure roller 4 includes a cored bar 4a made of a cylindrical member made of a metal having high thermal conductivity such as copper or aluminum, and an elastic member having high heat resistance and toner releasability provided on the surface of the cored bar 4a. 4b. In addition to the above metal, SUS may be used for the core metal 4a. The pressure roller 4 presses the fixing roller 2 via the belt 3 to form the fixing nip portion N, but in this embodiment, the pressure roller 4 is harder than the fixing roller 2. As a result, the pressure roller 4 bites into the fixing roller 2 (and the belt 3), and the recording material 11 follows the circumferential shape of the surface of the pressure roller 4 by this biting. Has the effect of facilitating.

  As shown in FIGS. 6 (a) and 6 (b) A and B, the induction heating means 6 for heating the heating roller 1 by electromagnetic induction includes an exciting coil 7 as a magnetic field generating means, and the exciting coil 7 is wound. And a rotated coil guide plate 8. The coil guide plate 8 has a semi-cylindrical shape arranged close to the outer peripheral surface of the heating roller 1, and as shown in FIG. 6B, the excitation coil 7 is a long excitation coil wire. It is wound alternately along the plate 8 in the axial direction of the heating roller 1. The exciting coil 7 is connected to a driving power source (not shown) whose oscillation circuit has a variable frequency. Outside the excitation coil 7, a semi-cylindrical excitation coil core 9 made of a ferromagnetic material such as ferrite is fixed to the excitation coil core support member 10 and is disposed close to the excitation coil 7. In the present embodiment, the exciting coil core 9 has a relative permeability of 2500. A high frequency alternating current of 10 kHz to 1 MHz, preferably a high frequency alternating current of 20 kHz to 800 kHz is supplied to the exciting coil 7 from a driving power source, thereby generating an alternating magnetic field. The alternating magnetic field acts on the heat generating layer of the heating roller 1 and the belt 3 in the contact area W1 between the heating roller 1 and the heat-resistant belt 3 and the vicinity thereof, and in the direction B that prevents the change of the alternating magnetic field inside these. Eddy current I flows. This eddy current I generates Joule heat corresponding to the resistance of the heat generating layer of the heating roller 1 and the belt 3, and the belt having the heating roller 1 and the heat generating layer mainly in the contact area between the heating roller 1 and the belt 3 and in the vicinity thereof. 3 is heated by electromagnetic induction.

The belt 3 heated in this way is detected by a temperature detecting means 5 comprising a thermosensitive element such as a thermistor disposed in contact with the inner surface side of the belt 3 in the vicinity of the entrance side of the fixing nip N. The belt inner surface temperature is detected.
Of course, the fixing device used in the present invention is not limited to the above-mentioned IH fixing device. However, the heat transfer efficiency is higher than that of the heat roller type fixing device, and the warm-up time can be shortened. Since an image forming apparatus using a fixing device capable of saving energy can be obtained, it is preferable to use an IH fixing device.

-Developer-
In the developing device used in the embodiment of the present invention, during development, a vibration bias voltage obtained by superimposing an AC voltage on a DC voltage is applied to the developing sleeve as a developing bias by a power source. The background portion potential and the image portion potential are located between the maximum value and the minimum value of the vibration bias potential. As a result, an alternating electric field whose direction changes alternately is formed in the developing portion. In this alternating electric field, the developer toner and carrier vibrate vigorously, and the toner flies off the electrostatic binding force on the developing sleeve and carrier and flies to the photosensitive drum, and adheres corresponding to the latent image on the photosensitive drum. To do.
The difference between the maximum value and the minimum value of the vibration bias voltage (voltage between peaks) is preferably 0.5 to 5 KV, and the frequency is preferably 1 to 10 KHz. As the waveform of the vibration bias voltage, a rectangular wave, a sine wave, a triangular wave, or the like can be used. As described above, the DC voltage component of the vibration bias is a value between the background part potential and the image part potential, but the value closer to the background part potential than the image part potential is more likely to cover the background part potential region. Or, it is preferable for preventing toner adhesion.
When the vibration bias voltage waveform is a rectangular wave, the duty ratio is preferably 50% or less. Here, the duty ratio is a ratio of time during which the toner is directed to the photoconductor in one cycle of the vibration bias. By doing so, the difference between the peak value at which the toner is directed to the photoreceptor and the time average value of the bias can be increased, so that the movement of the toner is further activated and the potential of the latent image surface is increased. It can adhere to the distribution and improve the roughness and resolution. In addition, since the difference between the peak value of the carrier having a charge opposite to that of the toner and the time average value of the bias toward the photosensitive member can be reduced, the movement of the carrier is reduced, and the background portion of the latent image is reduced. The probability of carriers adhering to the substrate can be greatly reduced.
Of course, the applied bias of the developing device used in the present invention is not limited as described above. However, in order to obtain a high-definition image without roughness, it is preferable to take the above-described form.

-Tandem type color image forming device-
An embodiment of a tandem color image forming apparatus of the present invention will be described. As shown in FIG. 7, the tandem type electrophotographic apparatus includes a direct transfer system that sequentially transfers an image on each photoconductor 1 to a sheet s conveyed by a sheet conveying belt 3 by a transfer apparatus 2. As shown in FIG. 8, the image on each photoconductor 1 is once transferred sequentially to the intermediate transfer body 4 by the primary transfer device 2, and then the image on the intermediate transfer body 4 is transferred to the sheet s by the secondary transfer device 5. There are indirect transfer systems that perform batch transfer. The transfer device 5 is a transfer conveyance belt, but there are also roller shapes and methods.
Comparing the direct transfer type and the indirect transfer type, the former arranges the paper feeding device 6 on the upstream side of the tandem type image forming apparatus T on which the photoconductors 1 are arranged, and the fixing device 7 on the downstream side. There is a drawback in that the size increases in the sheet conveying direction. On the other hand, the latter can set the secondary transfer position relatively freely. The paper feeding device 6 and the fixing device 7 can be arranged so as to overlap with the tandem image forming apparatus T, and there is an advantage that downsizing is possible.

In the former, in order not to increase the size in the sheet conveyance direction, the fixing device 7 is disposed close to the tandem type image forming apparatus T. For this reason, the fixing device 7 cannot be disposed with a sufficient margin that allows the sheet s to bend, and an impact when the leading edge of the sheet s enters the fixing device 7 (particularly with a thick sheet) or fixing. Due to the speed difference between the sheet conveying speed when passing through the apparatus 7 and the sheet conveying speed by the transfer conveying belt, there is a drawback that the fixing device 7 tends to affect the image formation on the upstream side. On the other hand, in the latter case, the fixing device 7 can be disposed with a sufficient margin that allows the sheet s to bend, so that the fixing device 7 hardly affects the image formation.
In view of the above, in recent years, indirect transfer type among tandem type electrophotographic apparatuses has been attracting attention.
In this type of color electrophotographic apparatus, as shown in FIG. 8, the transfer residual toner remaining on the photoreceptor 1 after the primary transfer is removed by the photoreceptor cleaning apparatus 8 to clean the surface of the photoreceptor 1. In preparation for image formation again. Further, the transfer residual toner remaining on the intermediate transfer body 4 after the secondary transfer is removed by the intermediate transfer body cleaning device 9 to clean the surface of the intermediate transfer body 4 to prepare for image formation again.

Hereinafter, embodiments of the present invention will be described with reference to the drawings.
FIG. 9 shows an embodiment of the present invention, which is a tandem indirect transfer type electrophotographic apparatus. In the figure, reference numeral 100 is a copying apparatus main body, 200 is a paper feed table on which it is placed, 300 is a scanner mounted on the copying apparatus main body 100, and 400 is an automatic document feeder (ADF) further mounted thereon. The copying machine main body 100 is provided with an endless belt-shaped intermediate transfer member 10 at the center.
Then, as shown in FIG. 9, in the illustrated example, it is wound around three support rollers 14, 15, and 16 so as to be able to rotate and convey clockwise in the figure.
In this illustrated example, an intermediate transfer body cleaning device 17 for removing residual toner remaining on the intermediate transfer body 10 after image transfer is provided on the left of the second support roller 15 among the three.
Further, among the three images, four images of yellow, cyan, magenta, and black are arranged on the intermediate transfer member 10 stretched between the first support roller 14 and the second support roller 15 along the conveyance direction. The tandem image forming apparatus 20 is configured by arranging the forming units 18 side by side.
An exposure device 21 is further provided on the tandem image forming apparatus 20 as shown in FIG. On the other hand, a secondary transfer device 22 is provided on the side opposite to the tandem image forming apparatus 20 with the intermediate transfer body 10 interposed therebetween. In the illustrated example, the secondary transfer device 22 is configured by spanning a secondary transfer belt 24, which is an endless belt, between two rollers 23, and is pressed against the third support roller 16 via the intermediate transfer body 10. The image on the intermediate transfer body 10 is transferred to a sheet.

A fixing device 25 for fixing the transfer image on the sheet is provided beside the secondary transfer device 22. The fixing device 25 is configured by pressing a pressure roller 27 against a fixing belt 26 that is an endless belt.
The secondary transfer device 22 described above is also provided with a sheet transport function for transporting the sheet after image transfer to the fixing device 25. Of course, a transfer roller or a non-contact charger may be arranged as the secondary transfer device 22, and in such a case, it is difficult to provide this sheet conveying function together.
In the illustrated example, under such a secondary transfer device 22 and a fixing device 25, a sheet reversing device 28 for reversing the sheet to record images on both sides of the sheet in parallel with the tandem image forming device 20 described above. Is provided.

Now, when making a copy using this color electrophotographic apparatus, a document is set on the document table 30 of the automatic document feeder 400. Alternatively, the automatic document feeder 400 is opened, a document is set on the contact glass 32 of the scanner 300, and the automatic document feeder 400 is closed and pressed by it.
When a start switch (not shown) is pressed, when the document is set on the automatic document feeder 400, the document is transported and moved onto the contact glass 32, and then the document is set on the other contact glass 32. At that time, the scanner 300 is immediately driven to travel the first traveling body 33 and the second traveling body 34. Then, the first traveling body 33 emits light from the light source and further reflects the reflected light from the document surface toward the second traveling body 34 and is reflected by the mirror of the second traveling body 34 and passes through the imaging lens 35. The document is placed in the reading sensor 36 and the original content is read.
When a start switch (not shown) is pressed, one of the support rollers 14, 15 and 16 is rotationally driven by a drive motor (not shown), the other two support rollers are driven to rotate, and the intermediate transfer body 10 is rotated and conveyed. To do. At the same time, the individual image forming means 18 rotates the photoconductors 40 to form black, yellow, magenta, and cyan single color images on the photoconductors 40, respectively. Then, along with the conveyance of the intermediate transfer member 10, the single color images are sequentially transferred to form a composite color image on the intermediate transfer member 10.
On the other hand, when a start switch (not shown) is pressed, one of the paper feed rollers 42 of the paper feed table 200 is selectively rotated, and the sheet is fed out from one of the paper feed cassettes 44 provided in multiple stages in the paper bank 43, and the separation roller 45. Then, the sheets are separated one by one into the paper feed path 46, transported by the transport roller 47, guided to the paper feed path 48 in the copying machine main body 100, and abutted against the registration roller 49 and stopped.

Alternatively, the sheet feed roller 50 is rotated to feed out the sheets on the manual feed tray 51, separated one by one by the separation roller 52, put into the manual feed path 53, and abutted against the registration roller 49 and stopped.
Then, the registration roller 49 is rotated in synchronization with the composite color image on the intermediate transfer body 10, the sheet is fed between the intermediate transfer body 10 and the secondary transfer device 22, and transferred by the secondary transfer device 22. A color image is recorded on the sheet.
The sheet after the image transfer is conveyed by the secondary transfer device 22 and sent to the fixing device 25, and heat and pressure are applied to the fixing device 25 to fix the transferred image. The paper is discharged at 56 and stacked on the paper discharge tray 57. Alternatively, it is switched by the switching claw 55 and put into the sheet reversing device 28, where it is reversed and guided again to the transfer position, and the image is recorded also on the back surface, and then discharged onto the discharge tray 57 by the discharge roller 56.

On the other hand, the intermediate transfer body 10 after the image transfer is removed by the intermediate transfer body cleaning device 17 to remove residual toner remaining on the intermediate transfer body 10 after the image transfer, so that the tandem image forming apparatus 20 can prepare for another image formation.
Here, the registration roller 49 is generally used while being grounded, but it is also possible to apply a bias for removing paper dust from the sheet.
In the tandem image forming apparatus 20 described above, the individual image forming means 18 includes, for example, a charging device 60, a developing device 61, and a primary transfer device around a drum-shaped photoconductor 40 as shown in FIG. 62, a photoconductor cleaning device 63, a charge removal device 64, and the like. The reference numerals shown in FIG. 10 are described. 65 is a developer on the developing sleeve, 68 is a stirring paddle, 69 is a partition plate, 71 is a toner concentration sensor, 72 is a developing sleeve, 73 is a doctor, 75 is a cleaning blade, and 76 is A cleaning brush, 77 is a cleaning roller, 78 is a cleaning blade, 79 is a toner discharge auger, and 80 is a driving device.

~ Process cartridge ~
FIG. 11 shows a schematic configuration of an image forming apparatus having a process cartridge used in the embodiment of the present invention. In the drawing, a represents the entire process cartridge, b represents a photosensitive member, c represents a charging unit, d represents a developing unit, and e represents a cleaning unit.
In the present invention, among the constituent elements such as the above-described photoreceptor b, charging device means c, developing means d, and cleaning means e, at least the photoreceptor b and the developing means d are integrally coupled as a process cartridge, The process cartridge is configured to be detachable from a main body of an image forming apparatus such as a copying machine or a printer.
In the image forming apparatus having the process cartridge using the electrophotographic toner of the present invention, the photosensitive member is rotationally driven at a predetermined peripheral speed. In the rotation process, the photosensitive member is uniformly charged with a predetermined positive or negative potential on its peripheral surface by the charging unit, and then receives image exposure light from an image exposing unit such as slit exposure or laser beam scanning exposure. An electrostatic image is sequentially formed on the circumferential surface of the body, and the formed electrostatic image is then developed with toner by a developing unit, and the developed toner image is exposed between the photosensitive member and the transfer unit from the paper feeding unit. The transfer material is sequentially transferred to the transfer material fed in synchronization with the rotation of the body. The transfer material that has received the image transfer is separated from the surface of the photosensitive member, introduced into the image fixing means, and fixed, and printed out as a copy (copy). The surface of the photoconductor after the image transfer is cleaned by removing the transfer residual toner by the cleaning means, and after being further discharged, it is repeatedly used for image formation.

EXAMPLES The present invention will be further described below with reference to examples, but the present invention is not limited thereto.
In the following, “part” means part by weight, and “%” means wt%.
Example 1
Hereinafter, the “organic solvent phase in which at least the functional group-containing polyester resin is dissolved, the active hydrogen-containing compound, and the colorant are dispersed in an aqueous medium phase in which resin fine particles are dispersed. An electrostatic charge image developing toner which causes an elongation reaction and / or a cross-linking reaction between the functional group-containing polyester resin and the active hydrogen-containing compound, and forms particles from the resulting dispersion. The specific production of the toner containing an organic acid compound in the organic solvent phase will be described step by step.

~ Synthesis of organic fine particle emulsion ~
In a reaction vessel in which a stir bar and a thermometer were set, 683 parts of water, 11 parts of sodium salt of ethylene oxide methacrylate adduct sulfate (Eleminol RS-30, manufactured by Sanyo Chemical Industries), 80 parts of styrene, 83 parts of methacrylic acid, When 110 parts of butyl acrylate, 12 parts of butyl thioglycolate, and 1 part of ammonium persulfate were added and stirred for 15 minutes at 400 rpm, a white emulsion was obtained. The system was heated to raise the temperature in the system to 75 ° C. and reacted for 5 hours. Further, 30 parts of a 1% ammonium persulfate aqueous solution was added, and the mixture was aged at 75 ° C. for 5 hours, and an aqueous vinyl resin (a copolymer of styrene-methacrylic acid-butyl acrylate-methacrylic acid ethylene oxide adduct sulfate sodium salt). A dispersion was obtained. This is designated as [fine particle dispersion 1]. The volume average particle diameter of the [fine particle dispersion 1] measured by a laser diffraction particle size distribution analyzer (LA-920, manufactured by Shimadzu Corp.) was 120 nm. A portion of [Fine Particle Dispersion 1] was dried to isolate the resin component. The Tg of the resin was 42 ° C., and the weight average molecular weight was 30,000.

~ Preparation of aqueous phase ~
990 parts of water, 65 parts of [fine particle dispersion 1], 37 parts of a 48.5% aqueous solution of sodium dodecyldiphenyl ether disulfonate (ELEMINOL MON-7, Sanyo Chemical Industries) and 90 parts of ethyl acetate were mixed and stirred to give a milky white color Obtained liquid. This is designated as [Aqueous Phase 1].

~ Synthesis of low molecular weight polyester ~
In a reaction vessel equipped with a condenser, a stirrer and a nitrogen inlet tube, 229 parts of bisphenol A ethylene oxide 2-mole adduct, 529 parts of bisphenol A propylene oxide 3-mole adduct, 208 parts terephthalic acid, 46 parts adipic acid and dibutyl Add 2 parts of tin oxide, react for 8 hours at 230 ° C. under normal pressure, and further react for 5 hours under reduced pressure of 10-15 mmHg, then put 44 parts of trimellitic anhydride into the reaction vessel, and at 180 ° C. under normal pressure. The mixture was reacted for 2 hours to obtain [Low molecular weight polyester 1]. [Low molecular polyester 1] had a number average molecular weight of 2500, a weight average molecular weight of 6700, a Tg of 43 ° C., and an acid value of 24.

~ Synthesis of intermediate polyester ~
In a reaction vessel equipped with a cooling pipe, a stirrer and a nitrogen introduction pipe, 682 parts of bisphenol A ethylene oxide 2-mole adduct, 81 parts of bisphenol A propylene oxide 2-mole adduct, 283 parts of terephthalic acid, trimellitic anhydride 22 And 2 parts of dibutyltin oxide were added, reacted at 230 ° C. for 8 hours at normal pressure, and further reacted for 5 hours at a reduced pressure of 10 to 15 mmHg to obtain [Intermediate Polyester 1]. [Intermediate Polyester 1] had a number average molecular weight of 2,100, a weight average molecular weight of 9,500, Tg of 55 ° C., an acid value of 0.5, and a hydroxyl value of 51.

-Synthesis of a modified polyester resin (referred to as prepolymer 1) capable of reacting with a compound having at least an active hydrogen group-
In a reaction vessel equipped with a cooling tube, a stirrer and a nitrogen introduction tube, 410 parts of the above [intermediate polyester 1], 89 parts of isophorone diisocyanate, and 500 parts of ethyl acetate were added and reacted at 100 ° C. for 5 hours. ] Was obtained. [Prepolymer 1] had a free isocyanate wt% of 1.53%.

~ Synthesis of ketimine ~
In a reaction vessel equipped with a stir bar and a thermometer, 170 parts of isophoronediamine and 75 parts of methyl ethyl ketone were charged and reacted at 50 ° C. for 5 hours to obtain [ketimine compound 1]. The amine value of [ketimine compound 1] was 418.

~ Master batch synthesis ~
1200 parts water, 40 parts carbon black (manufactured by Cabot, Regal 400R), 60 parts polyester resin (manufactured by Sanyo Kasei, RS801), 30 parts water, and mixed with a Henschel mixer (manufactured by Mitsui Mining) The mixture was kneaded at 150 ° C. for 30 minutes using two rolls, rolled and cooled, and pulverized with a pulverizer to obtain [Masterbatch 1].

-Production of toner composition containing oil phase, that is, inorganic fine particles-
In a container equipped with a stir bar and a thermometer, 400 parts of [Low molecular weight polyester 1], 110 parts of carnauba wax and 947 parts of ethyl acetate were charged, heated to 80 ° C. with stirring, and maintained at 80 ° C. for 5 hours. Thereafter, it was cooled to 30 ° C. at 1 hour. Next, 500 parts of [Masterbatch 1] and 500 parts of ethyl acetate were placed in a container and mixed for 1 hour to obtain [Raw material solution 1].
[Raw material solution 1] 1324 parts are transferred to a container, and using a bead mill (Ultra Visco Mill, manufactured by Imex Co., Ltd.), a liquid feed speed of 1 kg / hr, a disk peripheral speed of 6 m / sec, and 0.5 mm zirconia beads are 80% by volume. The wax was dispersed under the conditions of filling and 3 passes. Next, 1324 parts of a 65% ethyl acetate solution of [low molecular weight polyester 1] and 34 parts of [inorganic fine particles 1] were added, followed by one pass using a bead mill under the above conditions to obtain [Pigment / Wax Dispersion 1]. The solid content concentration of [Pigment / Wax Dispersion 1] (130 ° C., 30 minutes) was 50%.

~ Emulsification ~
[Pigment / Wax Dispersion 1] 648 parts, [Prepolymer 1] 154 parts, [Ketimine Compound 1] 8.5 parts, organic acid compound (acetic acid) 0.01 part in a container, TK homomixer (special After mixing at 5,000 rpm for 1 minute, the mixture was added with 1200 parts of [Aqueous phase 1] and mixed with a TK homomixer at a rotational speed of 10,000 rpm for 20 minutes to obtain [Emulsion slurry 1].
That is, it is dispersed in an aqueous medium containing resin fine particles and an elongation reaction is performed.

~ Solvent removal ~
[Emulsion slurry 1] was put into a container equipped with a stirrer and a thermometer, and after removing the solvent at 30 ° C. for 8 hours, aging was carried out at 45 ° C. for 4 hours to obtain [Dispersion slurry 1].

~ Washing and drying ~
[Dispersion Slurry 1] After filtering 100 parts under reduced pressure,
(1): 100 parts of ion-exchanged water was added to the filter cake, mixed with a TK homomixer (rotation speed: 12,000 rpm for 10 minutes), and then filtered.
(2): 100 parts of 10% sodium hydroxide aqueous solution was added to the filter cake of (1), mixed with a TK homomixer (30 minutes at 12,000 rpm), and then filtered under reduced pressure.
(3): 100 parts of 10% hydrochloric acid was added to the filter cake of (2), mixed with a TK homomixer (rotation speed: 12,000 rpm for 10 minutes), and then filtered.
(4): 300 parts of ion-exchanged water was added to the filter cake of (3), mixed with a TK homomixer (10 minutes at 12,000 rpm), and then filtered twice to obtain a cake. . This is designated as [filter cake 1].
[Filter cake 1] was dried at 45 ° C. for 48 hours in a circulating dryer. Thereafter, the mixture was sieved with a 75 μm mesh to obtain toner base particles. This is designated as [toner base particle 1].

~ External additive treatment ~
To 100 parts of [Toner Base Particle 1] obtained above, 0.7 part of hydrophobic silica and 0.3 part of hydrophobic titanium oxide as external additives are mixed with a Henschel mixer to obtain a toner. It was. This is referred to as [Toner 1]. The physical property values of [Toner 1] are listed in Table 1.

-Adjustment of developer-
[Toner base particle 1] A two-component developer composed of 5 wt% and a copper-zinc ferrite carrier 95 wt% with an average particle diameter of 40 µm coated with a silicone resin was prepared. Using this developer, continuous printing was carried out using Ricoh's imagio Neo 450, which can print 45 sheets of A4 size paper per minute, and the evaluation results shown below are shown in Table 2. It was.

(Example 2)
[Toner 2] was obtained in the same manner as in Example 1 except that the organic acid compound (acetic acid) was changed to 0.03 part in the emulsification of Example 1.

Example 3
[Toner 3] was obtained in the same manner as in Example 1 except that the organic acid compound (trimellitic anhydride) was changed to 0.01 part in the emulsification of Example 1.

Example 4
[Toner 4] was obtained in the same manner as in Example 1 except that the organic acid compound (trimellitic anhydride) was changed to 0.03 part in the emulsification of Example 1.

(Comparative Example 1)
[Toner 5] was obtained in the same manner as in Example 1 except that the organic acid compound was changed to 0 part in the emulsification in Example 1.

(Evaluation item)
(1) Measurement of Volume Average Particle Size and (Dv / Dn) The particle size of the toner was measured using a particle size measuring device “Coulter Counter TAII” manufactured by Coulter Electronics Co., Ltd., with an aperture diameter of 100 μm. The volume average particle size and the number average particle size were determined by the particle size measuring instrument. (Dv / Dn) was automatically calculated from the above values.
(2) Average circularity The average circularity can be measured by a flow type particle image analyzer FPIA-2100 (manufactured by Toa Medical Electronics Co., Ltd.). As a specific measuring method, 0.1 to 0.5 ml of a surfactant, preferably alkylbenzene sulfonate is added as a dispersant to 100 to 150 ml of water from which impure solids have been removed in advance, and further measurement is performed. Add about 0.1-0.5g of sample. The suspension in which the sample is dispersed is obtained by performing dispersion treatment for about 1 to 3 minutes with an ultrasonic disperser and measuring the shape and distribution of the toner with the above apparatus at a dispersion concentration of 3000 to 10,000 / μl. .
(3) Charge amount 6 g of developer is weighed, charged into a metal cylinder that can be sealed, and blown to obtain the charge amount. The toner concentration is adjusted to 4.5 to 5.5 wt%.
(4) Cleanability Using the evaluation machine A, the transfer residual toner on the photosensitive member that has passed the cleaning process after outputting 100 sheets is transferred to a white paper with a scotch tape (manufactured by Sumitomo 3M Co., Ltd.). Measured with RD514 type, ◎ if the difference from the blank is less than 0.005, ○ if 0.005 to 0.010, Δ if 0.011 to 0.02, and more than 0.02. Was evaluated as x.
(5) Image Density Using Evaluator A, 150,000 sheets of 50% image area image charts were output in a single color mode, and then a solid image was output to 6000 paper manufactured by Ricoh. Measurement was carried out by (manufactured by X-Rite). This was done for four colors alone and the average was determined. If this value is less than 1.2, x, if it is 1.2 or more and less than 1.4, Δ, if it is 1.4 or more and less than 1.8, ○, if it is 1.8 or more and less than 2.2 ◎.
(6) Image granularity and sharpness Using the evaluator B, a photographic image was output in a single color, and the degree of granularity and sharpness was visually evaluated. Evaluations were made from GOOD, ◎, ○, Δ, and ×.並 is equivalent to offset printing, ◯ is slightly worse than offset printing, Δ is much worse than offset printing, and × is very bad compared to conventional electrophotographic images.
(7) Background stain After using the evaluation machine A to run 30,000 image charts with a 50% image area in single color mode, the blank image is stopped during development, and the developer on the photoconductor after development is removed. The tape was transferred, and the difference from the image density of the untransferred tape was measured with a 938 spectrodensitometer (manufactured by X-Rite). The smaller the difference in image density, the better the background stains, and the higher the rank in the order of x, Δ, ○, ◎.
(8) White spots inside character images After running 30,000 image charts with 50% image area in monochrome mode using Evaluator A, the character images are printed in four colors on a Ricoh type DX OHP sheet. The frequency of untransferred toner that is output in a superimposed manner and the inside of the line image of the character portion is lost was compared with a step sample. Rank 1 is the lowest and rank 5 is the highest. Rank 1 or 2 was rated as x, Rank 3 was rated as △, Rank 4 was rated as ◯, and Rank 5 was rated as ◎.
(9) Toner fluidity A powder tester (PT-N type, manufactured by Hosokawa Micron) is loaded with meshes of 75 μm, 45 μm, and 22 μm openings in order from the top, and 2 g of the toner base is placed on the uppermost 75 μm mesh. Then, a vibration of 1 mm in the vertical direction was applied for 10 seconds, and the fluidity (cohesion degree) of the toner base was calculated from the residual amount of toner on each mesh.
Aggregation degree (%) = (5 × (remaining toner amount (g) on 75 μm mesh))
+ 3 × (residual toner amount on 45 μm mesh (g))
+ (Residual toner amount on 22 μm mesh (g))) × 10
When the degree of aggregation was 8% or less, ◎, when it was 8 to 16%, ◯, when it was 16 to 25%, Δ, and when it was 25% or more, ×.
(10) Fixability Using the evaluation machine A, a solid image and a 0.85 ± 0.1 mg / cm ² solid image on a transfer paper (made by Ricoh, type 6200 and NBS Ricoh copy printing paper <135>). Fixing was evaluated based on the toner adhesion amount. A fixing test was performed by changing the temperature of the fixing belt, and an upper limit temperature at which hot offset did not occur on plain paper was defined as an upper limit fixing temperature. Further, the minimum fixing temperature was measured with cardboard. The lower limit fixing temperature was determined as the fixing lower limit temperature at the fixing roll temperature at which the residual ratio of the image density after rubbing the obtained fixed image with a pad was 70% or more. The upper limit fixing temperature was ◎ for 190 ° C or higher, ○ for 190-180 ° C, △ for 180-170 ° C, and x for 170 ° C or lower. The lower limit fixing temperature was ◎ for 135 ° C. or less, ◯ for 135 to 145 ° C., Δ for 145 to 155 ° C., and × for 155 ° C. or more.

1 is a schematic configuration diagram illustrating an example of an image forming apparatus of the present invention. 1 is a schematic configuration diagram illustrating an example of an image forming apparatus of the present invention. It is explanatory drawing of the outline of a roller-type contact charging device. It is the schematic which shows the example of a structure of a photoreceptor. FIG. 2 is a schematic explanatory diagram of a surf fixing device. FIG. 2 is a schematic explanatory diagram of an IH fixing device. 1 is a schematic configuration diagram illustrating an example of an image forming apparatus of the present invention. 1 is a schematic configuration diagram illustrating an example of an image forming apparatus of the present invention. 1 is a schematic configuration diagram illustrating an example of an image forming apparatus of the present invention. 1 is a schematic configuration diagram illustrating an example of an image forming apparatus of the present invention. It is a schematic explanatory drawing which shows an example of the process cartridge of this invention.

Explanation of symbols

DESCRIPTION OF SYMBOLS 10 Photoconductor 20 Charging roller 30 Exposure apparatus 40 Developing apparatus 41 Developing belt 42 Developing tank 43 Pumping roller 44 Coating roller 45 Developing unit 50 Intermediate transfer body 51 Suspension roller 52 Corona charger 53 Constant current source 60 Cleaning device 70 Static elimination lamp 80 Transfer Roller 90 Cleaning device 100 Transfer paper

Claims (13)

An organic solvent phase in which at least a functional group-containing polyester resin is dissolved, an active hydrogen-containing compound, and a colorant are dispersed in an aqueous medium phase in which resin fine particles are dispersed,
An electrostatic charge image developing toner in which an elongation reaction and / or a crosslinking reaction between the functional group-containing polyester resin and the active hydrogen-containing compound is caused to form particles from the resulting dispersion. An electrostatic image developing toner comprising an organic acid compound in a solvent phase. The toner for developing an electrostatic charge image according to claim 1, wherein the organic acid compound is a carboxylic acid compound and a carboxylic acid anhydride. The electrostatic image developing toner according to claim 2, wherein the organic acid compound has a number average molecular weight in the range of 15 to 1500. In the organic solvent phase, a non-reactive polyester is dissolved together with the functional group-containing polyester resin, and a weight ratio of the functional group-containing polyester resin to the non-reactive polyester is 6/96 to 76/26. The electrostatic image developing toner according to claim 1, wherein the toner is an electrostatic charge image developing toner. The toner for electrostatic image development according to any one of claims 1 to 4, wherein the toner particles have a volume average particle diameter of 3 to 8 µm. 6. The electrostatic image developing toner according to claim 1, wherein Dv / Dn of the toner particles is 1.26 or less. 7. The electrostatic image developing toner according to claim 1, wherein the toner particles have an average circularity of 0.900 to 0.980. In a developer for developing an electrostatic image,
The two-component developer, wherein the developer includes at least a carrier comprising the toner according to any one of claims 1 to 7 and magnetic particles. 8. An electrostatic charge image developing member according to claim 1, further comprising an electrostatic charge image carrier, a charging means, an exposure means, a developing means, a contact transfer means, a heat fixing means, and a cleaning means. An image forming apparatus using toner. The image forming apparatus according to claim 9, further comprising a charging unit that performs charging by bringing a charging member into contact with the electrostatic charge image carrier and applying a voltage to the charging member. The image forming apparatus according to claim 9, wherein the electrostatic image carrier is an amorphous silicon electrostatic image carrier. The image forming apparatus includes a heating body including a heating element, a film that contacts the heating body, and a pressure member that presses the heating body via the film, and the film and the pressure member The image forming apparatus according to claim 9, further comprising a heat fixing unit that heats and fixes a recording material on which an unfixed image is formed between the recording materials. At least in the process cartridge that integrally supports the charge image carrier and the developing means and is detachable from the image forming apparatus main body,
The process cartridge using at least the toner according to any one of claims 1 to 7.