JP2005297244A - Easily tearable film - Google Patents
Easily tearable film Download PDFInfo
- Publication number
- JP2005297244A JP2005297244A JP2004113230A JP2004113230A JP2005297244A JP 2005297244 A JP2005297244 A JP 2005297244A JP 2004113230 A JP2004113230 A JP 2004113230A JP 2004113230 A JP2004113230 A JP 2004113230A JP 2005297244 A JP2005297244 A JP 2005297244A
- Authority
- JP
- Japan
- Prior art keywords
- film
- layer
- easily tearable
- amount
- easy tear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は包装用材料に用いられる易引裂き性フィルムに関するものであって、具体的には、易引裂き性に富んだ易引裂き性フィルムに関する。 The present invention relates to an easy tear film used for a packaging material, and specifically relates to an easy tear film rich in easy tear.
従来より、食品や医薬品、電子部品などの包装には、各種のプラスチックフィルムを材料とした包装材料による包装袋が用いられる。しかし内容物の保存が重視される場合においても単なるプラスチックフィルムを用いたのでは、酸素や水蒸気等はプラスチックフィルムを容易に透過してしまい、透過した酸素や水蒸気等が内容物と反応し、内容物の品質を損ねてしまうことになるので、この場合においてはプラスチックフィルムに対して酸素や水蒸気を透過しない性質、いわゆるガスバリア性を付与したガスバリア性フィルムを原材料として用いることが通常行われている。 Conventionally, packaging bags made of packaging materials made of various plastic films are used for packaging foods, pharmaceuticals, electronic parts and the like. However, even when the preservation of the contents is important, if a simple plastic film is used, oxygen, water vapor, etc. easily permeate the plastic film, and the permeated oxygen, water vapor, etc. react with the contents, and the contents In this case, a gas barrier film imparted with a property that does not transmit oxygen or water vapor, that is, a so-called gas barrier property, is usually used as a raw material.
例えばプラスチックフィルムにアルミニウムを蒸着してなるアルミニウム蒸着フィルム等のような、プラスチックフィルムに金属を蒸着してなる積層フィルムが用いられることが多いが、このフィルムの場合、視認性が悪く内容物が見えない、また特に最近では廃棄時において生じる環境問題がクローズアップされてきているので、これに代わるガスバリア性フィルムが強く望まれるようになってきている。 For example, a laminated film obtained by evaporating metal on a plastic film, such as an aluminum evaporated film obtained by evaporating aluminum on a plastic film, is often used. In recent years, environmental problems that occur at the time of disposal have been highlighted, and therefore, a gas barrier film as an alternative has been strongly desired.
そこで、このような金属蒸着フィルムに代わるガスバリアフィルムとして、透明プラスチックフィルムを基材とし、これに例えば酸化ケイ素や酸化アルミニウムよりなる蒸着層を積層したガスバリアフィルムが提案されている。 Therefore, as a gas barrier film replacing such a metal vapor deposition film, a gas barrier film is proposed in which a transparent plastic film is used as a base material and a vapor deposition layer made of, for example, silicon oxide or aluminum oxide is laminated thereon.
しかしこれらのフィルムでは、従来の金属蒸着フィルム、例えば広く普及している上述したアルミニウム蒸着フィルムほどにはガスバリア性を得ることができないので、さらに積層物（積層数）を増やしたり、フィルムや積層物の厚みを厚くすることで好適なガスバリア性を得ようとしているが、そうすると今度は、そのようなフィルムを原材料として包装用の袋と実際にしてみると、内容物の保存という観点からは有る程度の目的を達しているものの、これを開封しようとすると、手で引裂くことが非常に困難なものとなってしまい、その結果引裂きがうまくいかず、例えば内容物が飛散してしまう、といった実用的な問題が多発するようになってしまっている。 However, in these films, the gas barrier property cannot be obtained as much as the conventional metal vapor-deposited film, for example, the above-mentioned aluminum vapor-deposited film, which is widely used. I am trying to obtain a suitable gas barrier property by increasing the thickness of the film, but then, when I actually try to use it as a packaging bag with such a film as a raw material, it is a certain degree from the viewpoint of preservation of contents However, if you try to open it, it will be very difficult to tear by hand, and as a result, tearing will not work, for example, the contents will be scattered The problem has become frequent.
そこでこのような問題点を解消すべく、様々な易引裂き性積層体が提案されている。
例えば特許文献１に記載されている発明は、ポリエチレンテレフタレート（ＰＥＴ）フィルム／接着層／透明蒸着層／ＰＥＴフィルム／接着層／ヒートシール層、という構成を有する易引裂き性防湿包装材料に関する発明であるが、このように構成することで防湿性に優れ、かつ開封に際して手切れ性がよく、アルミニウムを用いていないので焼却時に環境問題を引き起こさない、という効果を得られる、となっている。
Therefore, various easily tearable laminates have been proposed in order to solve such problems.
For example, the invention described in Patent Document 1 relates to an easily tearable moisture-proof packaging material having a configuration of polyethylene terephthalate (PET) film / adhesive layer / transparent vapor deposition layer / PET film / adhesive layer / heat seal layer. However, with such a configuration, it is excellent in moisture resistance, has good hand-cutting properties when opened, and since it does not use aluminum, the effect of not causing environmental problems during incineration can be obtained.
また特許文献２においては、ＰＥＴフィルム／ＰＥＴフィルム／透明蒸着層／接着層／ヒートシール層、という構成を有する易引裂き性フィルムに関する発明が記載されているが、このように構成することで、特に食品包装に適した、ガスバリア性及び易引裂き性に優れたフィルムを容易に提供できる、という効果を得られる、となっている。 Moreover, in patent document 2, although the invention regarding the easily tearable film which has a structure of PET film / PET film / transparent vapor deposition layer / adhesion layer / heat seal layer is described, by comprising in this way, especially It is possible to obtain an effect that it is possible to easily provide a film excellent in gas barrier properties and easy tearing suitable for food packaging.
さらに特許文献３においては、ＰＥＴフィルム／透明蒸着層／接着層／エチレン−α−オレフィン共重合体ヒートシール層、という構成を有する易引裂き性フィルムに関する発明が記載されているが、このように構成することで、特に食品包装に適した、透明性、ガスバリア性及び易引裂き性に優れたフィルムを工業的に容易に提供できる、という効果を得られる、となっている。 Further, Patent Document 3 describes an invention relating to an easily tearable film having a configuration of PET film / transparent vapor deposition layer / adhesion layer / ethylene-α-olefin copolymer heat seal layer. By doing so, it is possible to obtain an effect that a film excellent in transparency, gas barrier property and easy tearing, particularly suitable for food packaging, can be easily provided industrially.
しかし、特許文献１に記載されたフィルムであれば、フィルムを３層に渡って使用している、しかも全て異なる種類のフィルムを用いる、さらにラミネート工数が多い、よって、実際に本発明に係るフィルムを製造する場合にはコスト的な問題が生じてしまい、必ずしも万全の解決策とはなりえていない。また特許文献２及び特許文献３に記載されたフィルムであれば、構成は簡素化されているために、特許文献１に比べて工数が少なくなり、また他種類のフィルムも用意しなくてよいのでこの点は特許文献１に比べて利点となりうるが、これらの文献に記載の発明においてＰＥＴフィルムの選定に制限があること、またヒートシール層として用いる部材も特殊なものとしなければ、これらの文献に記載の発明による効果を得ることができず、即ち使い勝手が必ずしも好適とは言えない発明であった。 However, in the case of the film described in Patent Document 1, the film is used in three layers, and all the different types of films are used, and the number of laminating steps is large. Therefore, the film according to the present invention is actually used. In the case of manufacturing, a cost problem arises, and it is not always a perfect solution. Moreover, since the structure is simplified if it is the film described in patent document 2 and patent document 3, compared with patent document 1, man-hours will decrease, and it is not necessary to prepare another kind of film. Although this point can be an advantage compared to Patent Document 1, there is a limitation in the selection of the PET film in the inventions described in these documents, and these documents unless the member used as the heat seal layer is also special. In other words, the effect of the invention described in 1) cannot be obtained, that is, the invention is not necessarily preferable in terms of usability.
そこで本発明はこのような問題点に鑑みて なされたものであり、その目的は、従来のガスバリア性フィルムに比べ、引裂き性が好適であって、特に手で引裂いても容易に引裂くことが出来るものであって、さらに簡潔な構成であるにもかかわらず従前通りのガスバリア性を確保することが出来る、ガスバリア性に優れた易引裂き性フィルムを提供することである。 Therefore, the present invention has been made in view of such problems, and its purpose is that tearability is better than conventional gas barrier films, and it can be easily torn even by tearing by hand. It is an object of the present invention to provide an easily tearable film excellent in gas barrier properties, which is capable of ensuring gas barrier properties as before, although it has a simpler structure.
上記課題を解決するため、本願発明の請求項１に記載の発明は、基材フィルムと、その表面に、透明蒸着層と、接着層と、ヒートシール層と、をこの記載順に積層してなる積層体であって、前記接着層が、主剤量ｘに対し硬化剤量をｙとする割合で混合することによって接着剤として作用する前記主剤と前記硬化剤とによりなる接着剤において、硬化剤量をｙの１．５倍以上３倍以下とし、これを主剤量ｘに対して混合することにより得られる樹脂により形成されてなること、を特徴とする。 In order to solve the above-mentioned problem, the invention according to claim 1 of the present invention is formed by laminating a base film and a transparent vapor-deposited layer, an adhesive layer, and a heat seal layer on the surface in the order described. In the adhesive comprising the main agent and the curing agent that act as an adhesive by mixing the adhesive layer at a ratio where the amount of the curing agent is y with respect to the main agent amount x. It is characterized in that it is formed of a resin obtained by mixing 1.5 to 3 times y with respect to the amount x of the main agent.
本願発明の請求項２に記載の発明は、請求項１に記載の易引裂き性フィルムにおいて、前記主剤は予め溶剤中に溶解されてなるものであり、かつ前記硬化剤は予め溶剤中に溶解されてなるものであり、前記主剤量ｘは前記主剤を溶解した溶液全体の量であり、前記硬化剤量ｙは前記硬化剤を溶解した溶液全体の量であること、を特徴とする。 The invention according to claim 2 of the present invention is the easily tearable film according to claim 1, wherein the main agent is previously dissolved in a solvent, and the curing agent is previously dissolved in the solvent. The main agent amount x is the total amount of the solution in which the main agent is dissolved, and the curing agent amount y is the total amount of the solution in which the curing agent is dissolved.
本願発明の請求項３に記載の発明は、請求項２に記載の易引裂き性フィルムにおいて、前記溶剤が、酢酸エチル、メチルエチルケトン、又はトルエンの何れか、もしくは複数であること、を特徴とする。 The invention according to claim 3 of the present invention is characterized in that in the easily tearable film according to claim 2, the solvent is any one or a plurality of ethyl acetate, methyl ethyl ketone, and toluene.
本願発明の請求項４に記載の発明は、請求項１ないし請求項３の何れか１項に記載の易引裂き性フィルムにおいて、前記基材フィルム表面に前記透明蒸着層を積層する前に、前記基材フィルムの前記透明蒸着層を積層する面に対し、予め何らかの表面処理してなること、を特徴とする。 Invention of Claim 4 of this invention is the easily tearable film of any one of Claim 1 thru | or 3, WHEREIN: Before laminating | stacking the said transparent vapor deposition layer on the said base film surface, The surface of the base film on which the transparent vapor deposition layer is laminated is subjected to some surface treatment in advance.
本願発明の請求項５に記載の発明は、請求項４に記載の易引裂き性フィルムにおいて、前記表面処理とは、コロナ放電処理、プラズマ処理、又はグロー放電処理の何れかの処理であること、若しくはアンカーコート層を設ける処理であること、を特徴とする。 The invention according to claim 5 of the present invention is the easily tearable film according to claim 4, wherein the surface treatment is any one of corona discharge treatment, plasma treatment, and glow discharge treatment. Or it is the process which provides an anchor-coat layer, It is characterized by the above-mentioned.
本願発明の請求項６に記載の発明は、請求項１ないし請求項５の何れか１項に記載の易引裂き性フィルムにおいて、前記透明蒸着層が、Ａｌ２Ｏ３、又はＳｉＯｘ（１≦ｘ≦２）の何れかにより形成されてなること、を特徴とする。 The invention described in claim 6 of the present invention is the easy tearable film according to any one of claims 1 to 5, wherein the transparent deposition layer, Al 2 O 3, or SiO x (1 ≦ x ≦ 2).
本願発明の請求項７に記載の発明は、請求項１ないし請求項６の何れか１項に記載の易引裂き性フィルムにおいて、前記透明蒸着層に前記接着層を積層する前に、前記透明蒸着層の表面にプライマー層を設けてなること、を特徴とする。 The invention according to claim 7 of the present invention is the easily tearable film according to any one of claims 1 to 6, wherein the transparent vapor deposition is performed before the adhesive layer is laminated on the transparent vapor deposition layer. A primer layer is provided on the surface of the layer.
本願発明の請求項８に記載の発明は、請求項７に記載の易引裂き性フィルムにおいて、前記プライマー層が、ウレタン系樹脂、ポリエステル系樹脂、セルロース系樹脂、又はアクリル系樹脂の何れか若しくは複数であること、を特徴とする。 The invention according to claim 8 of the present invention is the easily tearable film according to claim 7, wherein the primer layer is one or more of a urethane resin, a polyester resin, a cellulose resin, and an acrylic resin. It is characterized by.
本願発明の請求項９に記載の発明は、請求項１ないし請求項８の何れか１項に記載の易引裂き性フィルムにおいて、前記基材フィルムが、易直線引裂き性を備えたフィルムであること、を特徴とする。 The invention according to claim 9 of the present invention is the easily tearable film according to any one of claims 1 to 8, wherein the substrate film is a film having easy straight tearability. It is characterized by.
本願発明の請求項１０に記載の発明は、請求項１ないし請求項９の何れか１項に記載の易引裂き性フィルムにおいて、前記基材フィルムが、ポリエチレン（ＰＥ）フィルム、ポリエチレンテレフタレート（ＰＥＴ）フィルム、ナイロンフィルム、又はポリプロピレン（ＰＰ）フィルムの何れかであること、を特徴とする。 The invention according to claim 10 of the present invention is the easily tearable film according to any one of claims 1 to 9, wherein the base film is a polyethylene (PE) film, polyethylene terephthalate (PET). It is any one of a film, a nylon film, or a polypropylene (PP) film.
本願発明の請求項１１に記載の発明は、請求項１ないし請求項１０の何れか１項に記載の易引裂き性フィルムにおいて、前記ヒートシール層が、無延伸ポリプロピレン（ＣＰＰ）フィルム、低密度ポリエチレン（ＬＤＰＥ）フィルム、又はリニヤー低密度ポリエチレン（ＬＬＤＰＥ）フィルムの何れかにより形成されてなること、を特徴とする。 The invention according to claim 11 of the present invention is the easily tearable film according to any one of claims 1 to 10, wherein the heat seal layer is an unstretched polypropylene (CPP) film, low-density polyethylene. It is formed by either an (LDPE) film or a linear low density polyethylene (LLDPE) film.
本願発明の請求項１２に記載の発明は、請求項１ないし請求項１１の何れか１項に記載の易引裂き性フィルムにおいて、前記透明蒸着層と前記接着層との間、もしくは前記プライマー層と前記接着層との間に、前記接着層を設ける前に、その時点における最外層の表面に何らかの印刷をすることにより印刷層を設けてなること、を特徴とする。 Invention of Claim 12 of this invention is the easily tearable film of any one of Claim 1 thru | or 11, In the easily tearable film between the said transparent vapor deposition layer and the said adhesive layer, or the said primer layer, Before the adhesive layer is provided between the adhesive layer and the adhesive layer, a printing layer is provided by printing on the surface of the outermost layer at that time.
以上のように、本願発明に係る易引裂き性フィルムでは、主剤量ｘに対し硬化剤量をｙとする割合で混合することによって接着剤として作用する前記主剤と前記硬化剤とによりなる接着剤において、硬化剤量をｙの１．５倍以上３倍以下とし、これを主剤量ｘに対して混合することにより得られる樹脂により形成されてなる構成としたので、使用する硬化剤を増量することにより架橋密度が上がり、その結果接着層がより硬くなることにより、易引裂き性を容易に得られるようになる。 As described above, in the easily tearable film according to the present invention, in the adhesive comprising the main agent and the curing agent that act as an adhesive by mixing the main agent amount x at a ratio of setting the amount of the curing agent to y. The amount of the curing agent is 1.5 times to 3 times the amount of y, and the amount of the curing agent to be used is increased because it is made of a resin obtained by mixing this with the amount of the main agent x. As a result, the crosslink density is increased, and as a result, the adhesive layer becomes harder, so that easy tearability can be easily obtained.
以下、本願発明の実施の形態について説明する。尚、ここで示す実施の形態はあくまでも一例であって、必ずもこの実施の形態に限定されるものではない。 Embodiments of the present invention will be described below. The embodiment shown here is merely an example, and is not necessarily limited to this embodiment.
（実施の形態１）
本願発明に係る易引裂き性フィルムについて第１の実施の形態として説明する。
本実施の形態に係る易引裂き性フィルムは、基材フィルムと、その表面に、透明蒸着層と、接着層と、ヒートシール層と、をこの記載順に積層してなる積層体であって、前記接着層が、本来であれば、主剤量ｘに対し硬化剤量をｙとする割合で混合することによって接着剤として作用する前記主剤と前記硬化剤とによりなる接着剤において、硬化剤量をｙの１．５倍以上３倍以下とし、これを主剤量ｘに対して混合することにより得られる樹脂により形成されてなるものである。このように量を調整する理由については後述する。
(Embodiment 1)
The easily tearable film according to the present invention will be described as a first embodiment.
The easily tearable film according to the present embodiment is a laminate formed by laminating a base film and a transparent vapor-deposited layer, an adhesive layer, and a heat seal layer in this order on the surface thereof, If the adhesive layer is original, the amount of curing agent is set to y in the adhesive composed of the main agent and the curing agent acting as an adhesive by mixing the amount of the curing agent with respect to the amount x of the main agent. It is formed from a resin obtained by mixing this with respect to the main agent amount x. The reason for adjusting the amount in this way will be described later.
尚、主剤及び硬化剤は予め溶剤中に溶解されている場合もあるが、この場合は、前記主剤量ｘは前記主剤を溶解した溶液全体の量であり、前記硬化剤量ｙは前記硬化剤を溶解した溶液全体の量であることとすればよい。またこの場合において用いられる溶剤は特に限定しないが、本実施の形態では酢酸エチル、メチルエチルケトン、又はトルエンの何れか、もしくは複数であることとする。これらは通常広く利用されるものであり、実際にこれらを溶剤としている場合が多いため、本実施の形態でもこれらの溶剤を利用すればよい。 The main agent and the curing agent may be dissolved in the solvent in advance. In this case, the main agent amount x is the total amount of the solution in which the main agent is dissolved, and the curing agent amount y is the curing agent. The total amount of the solution in which is dissolved may be determined. In this case, the solvent used is not particularly limited, but in this embodiment, it is assumed that the solvent is any one or a plurality of ethyl acetate, methyl ethyl ketone, and toluene. Since these are usually widely used and in many cases they are actually used as solvents, these solvents may be used in the present embodiment.
本実施の形態に係る易引裂き性フィルムとしては、特に限定するものではないが、ここではポリエチレンフィルム、ポリエチレンテレフタレートフィルム。ナイロンフィルム、又はポリプロピレンフィルムの何れかを用いることが望ましい。これは、包装材料としてのみならず、蒸着フィルムを作製するときに広く用いられるフィルムであるからであり、またそれ故に入手もしやすく、取り扱いも容易である、という利点がある。 Although it does not specifically limit as an easily tearable film which concerns on this Embodiment, Here, a polyethylene film and a polyethylene terephthalate film. It is desirable to use either a nylon film or a polypropylene film. This is because it is a film that is widely used not only as a packaging material but also for producing a vapor-deposited film, and therefore has the advantage of being easily available and easy to handle.
また、本実施の形態に係る易引裂き性フィルムに用いる基材フィルムを易直線引裂き性を有するフィルムとすれば、全体としても直線的に引裂きやすいフィルムとすることが出来て好適である。このような直線的に引裂きやすい易直線引裂き性フィルムであれば、例えばレトルト食材の包装材料などに用いると、調理等がやりやすくなり大変好適な物とすることが出来る。 Moreover, if the base film used for the easily tearable film according to the present embodiment is a film having easy straight tearability, it is preferable that the film as a whole can be easily teared linearly. If it is such an easily linear tearable film that is easy to tear linearly, for example, when it is used as a packaging material for retort food, cooking and the like can be easily performed, and it can be made a very suitable product.
このようにして基材フィルムを選定すれば、次にその表面に透明蒸着層を設けるが、その前に基材フィルムの表面に対し、予め何らかの表面処理をすることも可能である。例えば、コロナ放電処理、プラズマ処理、又はグロー放電処理等に代表される処理であればよい。若しくはアンカーコート層を設ける処理を行うことも考えられる。これらの処理を行うことにより、後述の透明蒸着層の積層が容易となり、またいわゆる層間剥離を生じない積層体とすることが出来るのである。またこのような処理をしておけば、基材フィルムとそれに積層する透明蒸着層との相性、即ち積層のしやすさ、もしくは層間密着力の程度、等を詳細に検討する必要がなくなり、その結果素材の選択肢が広くなる。 If the base film is selected in this way, a transparent vapor deposition layer is then provided on the surface, but before that, it is possible to perform some surface treatment on the surface of the base film in advance. For example, a process represented by a corona discharge process, a plasma process, a glow discharge process, or the like may be used. Alternatively, a process of providing an anchor coat layer can be considered. By performing these treatments, lamination of a transparent vapor deposition layer, which will be described later, is facilitated, and a laminated body that does not cause so-called delamination can be obtained. If such a treatment is performed, it is not necessary to examine in detail the compatibility between the base film and the transparent vapor deposition layer laminated thereon, that is, the ease of lamination, the degree of interlayer adhesion, etc. As a result, the choice of material becomes wide.
基材フィルムに直接、もしくは上述の処理を施した後、に透明蒸着層を積層するのであるが、この透明蒸着層は、Ａｌ２Ｏ３、又はＳｉＯｘ（１≦ｘ≦２）の何れかにより形成されてなることが好ましい。これらであれば、その性質等も広く知れ渡っており、即ち取り扱いが容易であり、また製造に関するノウハウも十分にあるので好適と言えるが、必ずしもこれらの物質に限定されるものでないことを個々で断っておく。 A transparent vapor deposition layer is laminated on the base film directly or after performing the above-mentioned treatment. This transparent vapor deposition layer is either Al 2 O 3 or SiO x (1 ≦ x ≦ 2). It is preferable that it is formed by. These are suitable because their properties are widely known, that is, they are easy to handle and have sufficient manufacturing know-how, but they are not necessarily limited to these substances individually. Keep it.
尚、この透明蒸着層の積層方法については特に限定するものではないが、従来公知の手法であればどのような方法であってもよく、例えば真空蒸着法、電子ビーム蒸着法、スパッタリング法、といった手法によって積層されればよい。 In addition, although it does not specifically limit about the lamination | stacking method of this transparent vapor deposition layer, What kind of method may be used if it is a conventionally well-known method, for example, a vacuum evaporation method, an electron beam evaporation method, a sputtering method, etc. What is necessary is just to laminate | stack by the method.
透明蒸着層を積層すると、その表面に接着層を積層する。この接着層の積層についても上述同様、特にその手法をここで限定するものではないが、従来公知の手法であればどのような方法であってもよく、例えばグラビアロールコート、リバースロールコート、といった手法によって積層されればよい。重要なことは、接着層として用いる接着剤が、最初に説明したように、硬化剤の量を１．５倍以上、３倍以下の量で添加することである。１．５倍以下であると従来の接着剤と同程度の効果しか生じず、また３倍以上としてしまうと接着剤としての効果が弱くなり、易引裂き性を発揮することができなくなってしまう。 When a transparent vapor deposition layer is laminated | stacked, an adhesive layer will be laminated | stacked on the surface. Regarding the lamination of the adhesive layer, as described above, the method is not particularly limited here, but any method may be used as long as it is a conventionally known method, for example, gravure roll coating, reverse roll coating, etc. What is necessary is just to laminate | stack by the method. What is important is that the adhesive used as the adhesive layer is added in an amount of 1.5 times or more and 3 times or less the amount of the curing agent as explained at the beginning. If it is 1.5 times or less, only the same effect as a conventional adhesive will be produced, and if it is 3 times or more, the effect as an adhesive will be weakened and it will not be possible to exhibit easy tearability.
本実施の形態において従来の使用量に比べて硬化剤をこのように多くして用いることにより、接着剤における架橋密度が上がることが考えられる。その結果、接着層がより硬くなるために易引裂き性が発揮されるのである。 In this embodiment, it is conceivable that the crosslinking density in the adhesive is increased by using the curing agent in such a manner as compared with the conventional use amount. As a result, since the adhesive layer becomes harder, easy tearing is exhibited.
即ち、本実施の形態においては接着層に有る程度の硬度を付与することにより易引裂き性を付与することが出来るのであり、そのために上述の程度に硬化剤を通常より多めに使用するのである。 That is, in the present embodiment, easy tearability can be imparted by imparting a certain degree of hardness to the adhesive layer, and for this reason, the curing agent is used in a larger amount than usual.
このようにして接着層を積層すれば、その表面にヒートシール層を設ける。
このヒートシール層として用いる材料は、本実施の形態では特に限定しないが、例えば無延伸ポリプロピレン（ＣＰＰ）フィルム、低密度ポリエチレン（ＬＤＰＥ）フィルム、又はリニヤー低密度ポリエチレン（ＬＬＤＰＥ）フィルム、の何れかにより形成されてなることが考えられる。これらのフィルムはすでにヒートシール層としての利用に一定の実績があるので、本実施の形態で用いることが好適と言えるのである。
When the adhesive layer is laminated in this manner, a heat seal layer is provided on the surface.
The material used for the heat seal layer is not particularly limited in the present embodiment, but for example, any of an unstretched polypropylene (CPP) film, a low density polyethylene (LDPE) film, or a linear low density polyethylene (LLDPE) film. It may be formed. Since these films already have a certain track record in use as a heat seal layer, it can be said that it is preferable to use them in this embodiment.
このようにして本実施の形態における易引裂き性フィルムを得るのであるが、例えば透明蒸着層に前記接着層を積層する前に、前記透明蒸着層の表面にプライマー層を設けてなることも考えられる。そしてこの場合のプライマー層としては、ウレタン系樹脂、ポリエステル系樹脂、セルロース系樹脂、又はアクリル系樹脂の何れか若しくは複数であること、であることが考えられる。 In this way, the easily tearable film in the present embodiment is obtained. For example, it may be possible to provide a primer layer on the surface of the transparent vapor deposition layer before laminating the adhesive layer on the transparent vapor deposition layer. . In this case, the primer layer may be any one or more of a urethane resin, a polyester resin, a cellulose resin, and an acrylic resin.
プライマー層を設けることで、透明蒸着層と接着層との密着力が向上する、という利点が生じ、またこのように密着力が向上することにより、より易引裂き性が高いものとなるのである。 By providing the primer layer, there is an advantage that the adhesion between the transparent vapor deposition layer and the adhesive layer is improved, and the improvement in the adhesion makes it easier to tear.
また、本実施の形態に係る易引裂き性フィルムは、特に包装材料に広く用いることが出来るが、その際には通常何らかの印刷、例えば商品名や調理方法などを印刷することが行われる。そこで、本実施の形態に係る易引裂き性フィルムを製造するために基材フィルムの表面に透明蒸着層を積層したら、その次の段階で、透明蒸着層の表面に上述したような印刷を施して印刷層となし、そしてその印刷層の表面に接着層を積層することも考えられる。又は、透明蒸着層の表面に前述したプライマー層を設ける場合には、透明蒸着層の表面にプライマー層を積層した後に、プライマー層の表面に印刷層を設け、そしてその印刷層の表面に接着層を設ける、とすることも考えられる。 In addition, the easy tear film according to the present embodiment can be widely used particularly for packaging materials, and in that case, usually some kind of printing, for example, printing of a trade name or a cooking method is performed. Therefore, after laminating the transparent vapor deposition layer on the surface of the base film in order to produce the easy tear film according to the present embodiment, in the next stage, the surface as described above is applied to the surface of the transparent vapor deposition layer. It is also conceivable to form a printed layer and to laminate an adhesive layer on the surface of the printed layer. Or when providing the primer layer mentioned above on the surface of a transparent vapor deposition layer, after laminating | stacking a primer layer on the surface of a transparent vapor deposition layer, providing a printing layer on the surface of a primer layer, and adhering layer on the surface of the printing layer It is also conceivable to provide
いずれにせよ、接着層を積層する前に印刷層を設けるようにしておけば、これを例えばレトルト食材の包装材料とした場合であっても加熱処理等を施しても印刷層が劣化することがないので好適である。 In any case, if a printing layer is provided before laminating the adhesive layer, the printed layer may deteriorate even if it is subjected to heat treatment or the like even if it is used as a packaging material for retort food, for example. It is preferable because it is not present.
このように、本実施の形態に係る易引裂き性フィルムであれば、通常と同様の構成であるものの、通常利用する接着剤の硬化剤混合量を通常より多めに使用するようにするだけで、それまでは引裂き性がよくなかったガスバリア性フィルムであっても好適な引裂き性を得ることが出来るようになる。 Thus, if it is an easily tearable film according to the present embodiment, although it has the same configuration as usual, it is only necessary to use a larger amount of the curing agent mixture of the adhesive that is normally used than usual, Even if it is a gas barrier film that has not been good in tearing until then, suitable tearing can be obtained.
Claims (12)
その表面に、透明蒸着層と、接着層と、ヒートシール層と、をこの記載順に積層してなる積層体であって、
前記接着層が、主剤量ｘに対し硬化剤量をｙとする割合で混合することによって接着剤として作用する前記主剤と前記硬化剤とによりなる接着剤において、硬化剤量をｙの１．５倍以上３倍以下とし、これを主剤量ｘに対して混合することにより得られる樹脂により形成されてなること、
を特徴とする、易引裂き性フィルム。 A base film;
On the surface, a laminated body formed by laminating a transparent vapor deposition layer, an adhesive layer, and a heat seal layer in the order of description,
In the adhesive composed of the main agent and the curing agent that act as an adhesive by mixing the adhesive layer in a ratio where the amount of the curing agent is y with respect to the main agent amount x, the amount of the curing agent is 1.5 of y. It is made of a resin obtained by mixing it with the main agent amount x, not less than 3 times and not more than 3 times,
Easy tear film characterized by
前記主剤は予め溶剤中に溶解されてなるものであり、かつ前記硬化剤は予め溶剤中に溶解されてなるものであり、前記主剤量ｘは前記主剤を溶解した溶液全体の量であり、前記硬化剤量ｙは前記硬化剤を溶解した溶液全体の量であること、
を特徴とする、易引裂き性フィルム。 In the easily tearable film according to claim 1,
The main agent is preliminarily dissolved in a solvent, and the curing agent is preliminarily dissolved in a solvent, and the main agent amount x is the total amount of the solution in which the main agent is dissolved, The curing agent amount y is the total amount of the solution in which the curing agent is dissolved;
Easy tear film characterized by
前記溶剤が、酢酸エチル、メチルエチルケトン、又はトルエンの何れか、もしくは複数であること、
を特徴とする、易引裂き性フィルム。 In the easily tearable film according to claim 2,
The solvent is one or more of ethyl acetate, methyl ethyl ketone, and toluene,
Easy tear film characterized by
前記基材フィルム表面に前記透明蒸着層を積層する前に、
前記基材フィルムの前記透明蒸着層を積層する面に対し、予め何らかの表面処理してなること、
を特徴とする、易引裂き性フィルム。 In the easily tearable film according to any one of claims 1 to 3,
Before laminating the transparent vapor deposition layer on the substrate film surface,
For the surface on which the transparent vapor deposition layer of the base film is laminated, it has been subjected to some surface treatment in advance.
Easy tear film characterized by
前記表面処理とは、コロナ放電処理、プラズマ処理、又はグロー放電処理の何れかの処理であること、若しくはアンカーコート層を設ける処理であること、
を特徴とする、易引裂き性フィルム。 In the easily tearable film of Claim 4,
The surface treatment is a treatment of any one of corona discharge treatment, plasma treatment, and glow discharge treatment, or a treatment for providing an anchor coat layer.
Easy tear film characterized by
前記透明蒸着層が、Ａｌ２Ｏ３、又はＳｉＯｘ（１≦ｘ≦２）の何れかにより形成されてなること、
を特徴とする、易引裂き性フィルム。 In the easily tearable film according to any one of claims 1 to 5,
The transparent vapor deposition layer is formed of either Al 2 O 3 or SiO x (1 ≦ x ≦ 2),
Easy tear film characterized by
前記透明蒸着層に前記接着層を積層する前に、前記透明蒸着層の表面にプライマー層を設けてなること、
を特徴とする、易引裂き性フィルム。 In the easily tearable film according to any one of claims 1 to 6,
Before laminating the adhesive layer on the transparent vapor deposition layer, a primer layer is provided on the surface of the transparent vapor deposition layer,
Easy tear film characterized by
前記プライマー層が、ウレタン系樹脂、ポリエステル系樹脂、セルロース系樹脂、又はアクリル系樹脂の何れか若しくは複数であること、
を特徴とする、易引裂き性フィルム。 In the easily tearable film according to claim 7,
The primer layer is a urethane resin, a polyester resin, a cellulose resin, or an acrylic resin or a plurality thereof;
Easy tear film characterized by
前記基材フィルムが、易直線引裂き性を備えたフィルムであること、
を特徴とする、易引裂き性フィルム。 In the easily tearable film according to any one of claims 1 to 8,
The base film is a film having easy linear tearing;
Easy tear film characterized by
前記基材フィルムが、ポリエチレン（ＰＥ）フィルム、ポリエチレンテレフタレート（ＰＥＴ）フィルム、ナイロンフィルム、又はポリプロピレン（ＰＰ）フィルムの何れかであること、
を特徴とする、易引裂き性フィルム。 The easily tearable film according to any one of claims 1 to 9,
The base film is a polyethylene (PE) film, a polyethylene terephthalate (PET) film, a nylon film, or a polypropylene (PP) film;
Easy tear film characterized by
前記ヒートシール層が、無延伸ポリプロピレン（ＣＰＰ）フィルム、低密度ポリエチレン（ＬＤＰＥ）フィルム、又はリニヤー低密度ポリエチレン（ＬＬＤＰＥ）フィルムの何れかにより形成されてなること、
を特徴とする、易引裂き性フィルム。 In the easily tearable film according to any one of claims 1 to 10,
The heat seal layer is formed of any one of an unstretched polypropylene (CPP) film, a low density polyethylene (LDPE) film, or a linear low density polyethylene (LLDPE) film,
Easy tear film characterized by
前記透明蒸着層と前記接着層との間、もしくは前記プライマー層と前記接着層との間に、前記接着層を設ける前に、その時点における最外層の表面に何らかの印刷をすることにより印刷層を設けてなること、
を特徴とする、易引裂き性フィルム。 In the easily tearable film according to any one of claims 1 to 11,
Before providing the adhesive layer between the transparent vapor-deposited layer and the adhesive layer, or between the primer layer and the adhesive layer, a printing layer is formed by printing on the surface of the outermost layer at that time. To provide,
Easy tear film characterized by