JP2005159328A - Method of manufacturing wiring, method of manufacturing thin film transistor, and method of discharging droplet - Google Patents
Method of manufacturing wiring, method of manufacturing thin film transistor, and method of discharging droplet Download PDFInfo
- Publication number
- JP2005159328A JP2005159328A JP2004311240A JP2004311240A JP2005159328A JP 2005159328 A JP2005159328 A JP 2005159328A JP 2004311240 A JP2004311240 A JP 2004311240A JP 2004311240 A JP2004311240 A JP 2004311240A JP 2005159328 A JP2005159328 A JP 2005159328A
- Authority
- JP
- Japan
- Prior art keywords
- electrode
- film
- wiring
- plasma treatment
- dropping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、形成対象の材料が混入された組成物を滴下することによる配線の作製方法及び薄膜トランジスタ、またはそれを有する半導体装置の作製方法に関する。具体的には、液滴吐出(インクジェット)法による配線の作製方法及び薄膜トランジスタの作製方法に関する。
また、それらの液滴吐出方法に関する。
The present invention relates to a method for manufacturing a wiring by dropping a composition mixed with a material to be formed, a thin film transistor, and a method for manufacturing a semiconductor device having the thin film transistor. Specifically, the present invention relates to a method for manufacturing a wiring by a droplet discharge (inkjet) method and a method for manufacturing a thin film transistor.
Further, the present invention relates to a method for discharging those droplets.
ピエゾ方式やサーマルジェット方式に代表される液滴吐出技術、あるいは連続式の液滴吐出技術が注目を集めている。この液滴吐出技術は活字、画像の描画に使われてきたが、近年微細パターン形成などの半導体分野へ応用する試みが始まっている。 A droplet discharge technique represented by a piezo method or a thermal jet method, or a continuous droplet discharge technique has attracted attention. Although this droplet discharge technique has been used for printing characters and images, attempts to apply it to the semiconductor field such as fine pattern formation have recently started.
インクジェット法による膜パターンの形成方法を改善し、厚膜化を達成し、細線化の要請も満たし、導電膜とした場合に断線や短絡等の問題を生じない膜パターンの形成方法が提案されている(特許文献1参照)。
特許文献1によると、予め液滴との接触角が60degとなるように基板に処理を行い、第1の吐出工程では液滴を配線形成領域全体に、基板上に着弾した後の液滴の直径よりも大きいピッチで吐出する。第2の吐出工程では液滴を配線形成領域全体の第1吐出工程における吐出一と異なる位置に第1の吐出工程と同じピッチで吐出する。第3の吐出工程では、液滴を配線形成領域全体に第1の吐出工程におけるピッチよりも小さいピッチで吐出することが記載されている。 According to Patent Document 1, the substrate is processed in advance so that the contact angle with the droplet is 60 deg. In the first discharge process, the droplet is deposited on the substrate in the entire wiring formation region. Discharge at a pitch larger than the diameter. In the second ejection step, droplets are ejected at the same pitch as in the first ejection step at a position different from the ejection one in the first ejection step in the entire wiring formation region. In the third ejection step, it is described that droplets are ejected to the entire wiring formation region at a pitch smaller than the pitch in the first ejection step.
また接触角を制御するための表面処理の方法として、常圧又は真空中でプラズマ照射する方法が挙げられている。プラズマ処理に用いるガス種は、導電性配線を形成すべき基板の表面材料を考慮して選択することができ、例えば、4フッ化メタン、パーフルオロヘキサン、パーフルオロデカン等を処理ガスとして使用できることが記載されている。 Further, as a surface treatment method for controlling the contact angle, a method of irradiating plasma in normal pressure or vacuum is cited. The gas type used for the plasma treatment can be selected in consideration of the surface material of the substrate on which the conductive wiring is to be formed. For example, tetrafluoromethane, perfluorohexane, perfluorodecane, etc. can be used as the treatment gas. Is described.
上記のようなインクジェット法を代表とする方法により配線等を形成する場合、その線幅が太くなることを防ぎ、微細化することが要求されている。そこで、上記特許文献と異なる方法により、線幅を微細化する方法を提供することを課題とする。 In the case of forming a wiring or the like by a method typified by the ink jet method as described above, it is required to prevent the line width from becoming thicker and to make it finer. Therefore, an object of the present invention is to provide a method for reducing the line width by a method different from the above-mentioned patent document.
さらに本発明は、配線以外のもの、例えば半導体膜、絶縁膜、マスク等を、インクジェット法を代表とする方法により形成し、これらの線幅を微細化する方法を提供することを課題とする。 It is another object of the present invention to provide a method for forming a line width other than a wiring, for example, a semiconductor film, an insulating film, a mask, and the like by a method typified by an ink jet method and reducing the line width thereof.
上記課題を鑑み、本発明は、所望のパターンを形成する前に、パターンが形成される面(被形成面)に撥液性となる領域(撥液性領域)を形成することを特徴とする。すなわち、配線等を形成する前に、被形成面に対して撥液処理を行うことを特徴とする。その後、配線等の導電体材料が混入された組成物(溶媒に導電体が溶解又は分散させた組成物を含む)を滴下する方法(滴下法)により配線等のパターンを形成する。 In view of the above problems, the present invention is characterized in that before forming a desired pattern, a region (liquid repellent region) that becomes liquid repellent is formed on the surface on which the pattern is formed (formation surface). . That is, the liquid-repellent treatment is performed on the surface to be formed before the wiring or the like is formed. Thereafter, a pattern of wiring or the like is formed by a method (drop method) of dropping a composition mixed with a conductor material such as wiring (including a composition in which a conductor is dissolved or dispersed in a solvent).
導電体材料が混入された組成物を滴下する手段として、液滴吐出(インクジェット)法がある。インクジェット法としてピエゾ方式を用いることができる。ピエゾ方式は、液滴の制御性に優れインク選択の自由度の高いことからインクジェットプリンターでも利用されている。なお、ピエゾ方式には、MLP(Multi Layer Piezo)タイプとMLChip(Multi Layer Ceramic Hyper Integrated Piezo Segments)タイプがある。また溶媒の材料によっては、発熱体を発熱させ気泡を生じさせ溶液を押し出す、所謂サーマル方式を用いたインクジェット法でもよい。 As means for dropping a composition mixed with a conductor material, there is a droplet discharge (inkjet) method. A piezo method can be used as the ink jet method. The piezo method is also used in inkjet printers because of its excellent droplet controllability and high degree of freedom in ink selection. There are two types of piezo systems: MLP (Multi Layer Piezo) type and MLChip (Multi Layer Ceramic Hyper Integrated Piezo Segments) type. Depending on the material of the solvent, an ink jet method using a so-called thermal method in which a heating element generates heat to generate bubbles to push out the solution may be used.
撥液処理を行う手段として、被形成面に対してプラズマ処理を行う方法がある。プラズマ処理の条件は、空気、酸素又は窒素を処理ガスとして用い、圧力を数十Torr〜1000Torr(133000Pa)、好ましくは100(13300Pa)〜1000Torr(133000Pa)、より好ましくは700Torr(93100Pa)〜800Torr(106400Pa)、つまり大気圧又は大気圧近傍の圧力となる状態で、パルス状の電圧(パルス電圧)を印加する。このとき、プラズマ密度は、1×1010〜1×1014m-3、所謂コロナ放電やグロー放電の状態となるようにする。 As a means for performing liquid repellent treatment, there is a method of performing plasma treatment on a surface to be formed. The plasma treatment is performed using air, oxygen, or nitrogen as a treatment gas, and a pressure of several tens of Torr to 1000 Torr (133000 Pa), preferably 100 (13300 Pa) to 1000 Torr (133000 Pa), more preferably 700 Torr (93100 Pa) to 800 Torr ( 106400 Pa), that is, a pulsed voltage (pulse voltage) is applied in a state of atmospheric pressure or a pressure close to atmospheric pressure. At this time, the plasma density is set to 1 × 10 10 to 1 × 10 14 m −3 , so-called corona discharge or glow discharge.
また、特許文献1に記載のように、処理ガスにフッ素系ガスを用いる場合、半導体膜の表面に対して表面改質を行うことが難しい。これは、フッ素系のガスを用いると、珪素を有する半導体膜が除去されてしまうからである。またフッ素系のガスを用いると、アクリル等の有機材料の表面に対して表面改質を行うことも難しい。フッ素系のガスでは、有機材料の表面を傷つけたり、除去してしまうからである。 Further, as described in Patent Document 1, when a fluorine-based gas is used as a processing gas, it is difficult to perform surface modification on the surface of the semiconductor film. This is because if a fluorine-based gas is used, the semiconductor film containing silicon is removed. If a fluorine-based gas is used, it is difficult to perform surface modification on the surface of an organic material such as acrylic. This is because the fluorine-based gas damages or removes the surface of the organic material.
それに対して本発明は、空気、酸素又は窒素を用いてプラズマ処理を行っている。従って、形成面の材質を選ばず半導体膜や有機材料に対しても表面改質を行うことができ好ましい。さらに処理ガスが空気、酸素又は窒素であるため、コストが安く、排ガス処理も簡便である。 On the other hand, in the present invention, plasma treatment is performed using air, oxygen, or nitrogen. Therefore, the surface modification can be performed on the semiconductor film and the organic material regardless of the material of the formation surface, which is preferable. Further, since the processing gas is air, oxygen or nitrogen, the cost is low and the exhaust gas treatment is also simple.
また特に、処理ガスに酸素を用いて行うプラズマ処理は、半導体膜等をパターニングするためのマスク除去にも使うことができ好ましい。 In particular, plasma treatment using oxygen as a treatment gas is preferable because it can be used for removing a mask for patterning a semiconductor film or the like.
本発明のプラズマ処理に使われるプラズマ処理装置において、電極とプラズマ処理が行われる対象物(被処理物)との間には、誘電体が設けられており、誘電体は発生するプラズマに曝されることを特徴とする。誘電体として、テフロン(登録商標)を用いることができる。例えば、プラズマが生じる一面に、少なくとも誘電体が設けられた電極を用意し、誘電体がプラズマに曝されるように、被処理物と電極との間にプラズマを発生させればよい。そのため、誘電体は電極表面全体を覆う必要はない。 In the plasma processing apparatus used for the plasma processing of the present invention, a dielectric is provided between the electrode and an object (object to be processed) on which the plasma processing is performed, and the dielectric is exposed to the generated plasma. It is characterized by that. Teflon (registered trademark) can be used as the dielectric. For example, an electrode provided with at least a dielectric on one surface where plasma is generated may be prepared, and plasma may be generated between the workpiece and the electrode so that the dielectric is exposed to the plasma. Therefore, the dielectric does not need to cover the entire electrode surface.
本発明において、具体的なパルス電圧は、減衰振動波が間欠的に繰り返し生ずる減衰振動波形周期波として各減衰振動波のように共振された状態となるように印加する。例えば、正負一対のパルスを繰り返し周波数で高圧トランスの一次側に供給し、高圧トランスの二次側から各減衰振動波に共振した減衰振動波形周期波を出力して一対の電極に印加する。このとき共振した各減衰振動波の電圧立ち上がり時間は5μs以下であると好ましい。また減衰振動波の繰り返し周期が10〜100kHzであると好ましい。またパルスは100〜10000pps(1秒当たり10000回)であると好ましい。 In the present invention, a specific pulse voltage is applied so that a damped oscillation wave is resonated as a damped oscillation wave as a damped oscillation waveform periodic wave that is intermittently repeatedly generated. For example, a pair of positive and negative pulses is supplied to the primary side of the high-voltage transformer at a repetition frequency, and a damped oscillation waveform periodic wave resonated with each damped oscillation wave is output from the secondary side of the high-voltage transformer and applied to the pair of electrodes. At this time, the voltage rise time of each damped oscillation wave resonated is preferably 5 μs or less. Moreover, it is preferable that the repetition period of the damped vibration wave is 10 to 100 kHz. The pulse is preferably 100 to 10,000 pps (10,000 times per second).
以上のようなプラズマ処理を行う結果、導電膜が形成される面(被形成面)の表面が改質される。例えば、電極の一表面にテフロン(登録商標)が設けられている場合、導電膜の被形成面にCF2が形成され、水、アルコールや油等その他の液体に対して濡れ性の低い撥液性を示すようになる。 As a result of performing the plasma treatment as described above, the surface of the surface on which the conductive film is formed (formation surface) is modified. For example, when Teflon (registered trademark) is provided on one surface of the electrode, CF 2 is formed on the surface on which the conductive film is formed, and the liquid repellent has low wettability with respect to other liquids such as water, alcohol and oil. Shows sex.
その後、導電体材料を有する組成物を滴下し、配線を形成する。その結果、線幅が小さくなり、微細化を達成することができる。 Thereafter, a composition having a conductor material is dropped to form a wiring. As a result, the line width is reduced and miniaturization can be achieved.
すなわち本発明は、導電膜等のパターンの被形成面に対して撥液性領域を形成することを特徴とする。そのため、本発明は少なくとも、撥液処理を行った後、導電膜を形成し、微細な配線を形成する。例えば、撥液処理としてテフロン(登録商標)等のフッ素を有する膜を形成した後、導電体材料を有する組成物を滴下することにより微細な配線を形成してもよい。 That is, the present invention is characterized in that a liquid repellent region is formed on a surface on which a pattern such as a conductive film is formed. Therefore, at least after the liquid repellent treatment is performed in the present invention, a conductive film is formed and a fine wiring is formed. For example, a fine wiring may be formed by forming a film containing fluorine such as Teflon (registered trademark) as a liquid repellent treatment and then dropping a composition containing a conductive material.
また本発明は、溶媒に導電体(配線を構成する材料)が混入された組成物を吐出して配線を形成している。このような組成物を吐出する工程は、減圧下で行うと好ましい。組成物を吐出して被処理物に着弾するまでの間に、該組成物の溶媒が蒸発し、組成物の乾燥と焼成の工程を省略することができるからである。またさらに、減圧下で行うと、導電体の表面に酸化膜などが形成されないため好ましい。また組成物を滴下する工程は、窒素雰囲気中や有機ガス雰囲気中で行ってもよい。 In the present invention, the wiring is formed by discharging a composition in which a conductive material (material constituting the wiring) is mixed in a solvent. The step of discharging such a composition is preferably performed under reduced pressure. This is because the solvent of the composition evaporates and the steps of drying and firing the composition can be omitted before the composition is discharged and landed on the object to be processed. Furthermore, it is preferable to perform under reduced pressure because an oxide film or the like is not formed on the surface of the conductor. The step of dropping the composition may be performed in a nitrogen atmosphere or an organic gas atmosphere.
このとき、組成物はドット(液滴)状に吐出されたり、ドットが連なった柱状に吐出されたりする。すなわち、複数のドットが連続して吐出されるため、ドットとして認識されず線状に吐出されることもある。これのように組成物がドット状又は柱状に吐出されることを単にドット(液滴)を滴下と表記する。 At this time, the composition is ejected in the form of dots (droplets), or is ejected in the form of columns in which dots are connected. That is, since a plurality of dots are continuously ejected, they are not recognized as dots and may be ejected linearly. The discharge of the composition in the form of dots or columns like this is simply referred to as dots (droplets).
特に、導電体材料を有するドットを滴下する法により配線を形成する場合、該配線をパターニングするためのマスクの露光、現像といったフォトリソグラフィー工程、配線パターニングするエッチング工程を省略することができる。 In particular, when a wiring is formed by a method of dropping a dot having a conductive material, a photolithography process such as exposure and development of a mask for patterning the wiring and an etching process for patterning the wiring can be omitted.
導電体としては、金(Au)、銀(Ag)、銅(Cu)、白金(Pt)、パラジウム(Pd)、タングステン(W)、ニッケル(Ni)、タンタル(Ta)、ビスマス(Bi)、鉛(Pb)、インジウム(In)、錫(Sn)、亜鉛(Zn)、チタン(Ti)、若しくはアルミニウム(Al)、これらからなる合金、これらの分散性ナノ粒子、又はハロゲン化銀の微粒子を用いることができる。特に低抵抗な銀、銅を用いるとよい。但し銅を用いる場合、半導体膜中等に銅が拡散することを防止するため、窒素を有する絶縁膜をバリア膜として形成する必要がある。 As the conductor, gold (Au), silver (Ag), copper (Cu), platinum (Pt), palladium (Pd), tungsten (W), nickel (Ni), tantalum (Ta), bismuth (Bi), Lead (Pb), indium (In), tin (Sn), zinc (Zn), titanium (Ti), or aluminum (Al), alloys made of these, dispersible nanoparticles, or silver halide fine particles Can be used. In particular, low resistance silver or copper may be used. However, in the case of using copper, it is necessary to form an insulating film containing nitrogen as a barrier film in order to prevent copper from diffusing into the semiconductor film or the like.
また透明な導電体として、インジウム錫酸化物(ITO、Indium Tin Oxide)、酸化インジウムに2〜20%の酸化亜鉛(ZnO)を混合したIZO(indium zinc oxide)、酸化インジウムに2〜20%の酸化珪素(SiO2)を混合したITSO(便宜上ITSO又はNITOと表記する)、有機インジウム、有機スズ、窒化チタン(TiN)等を用いることもできる。 Further, as transparent conductors, indium tin oxide (ITO), indium oxide mixed with 2-20% zinc oxide (ZnO), indium zinc oxide (IZO), indium oxide 2-20% ITSO mixed with silicon oxide (SiO 2 ) (referred to as ITSO or NITO for convenience), organic indium, organic tin, titanium nitride (TiN), or the like can also be used.
このように本発明は、インクジェット法を代表とする滴下法により微細な配線を形成することを特徴としており、配線を形成する薄膜トランジスタの構造等は限定されない。すなわち、結晶性半導体膜及び非晶質半導体膜のいずれを有する薄膜トランジスタであってもよく、半導体膜より下方にゲート電極が設けられる所謂ボトムゲート型、及び半導体膜より上方にゲート電極が設けられる所謂トップゲート型のいずれの構造を有する薄膜トランジスタであってもよい。 As described above, the present invention is characterized in that fine wiring is formed by a dropping method typified by an inkjet method, and the structure of the thin film transistor for forming the wiring is not limited. That is, it may be a thin film transistor having either a crystalline semiconductor film or an amorphous semiconductor film, a so-called bottom gate type in which a gate electrode is provided below the semiconductor film, and a so-called gate electrode provided above the semiconductor film. A thin film transistor having any structure of a top gate type may be used.
また薄膜トランジスタが有する、ゲート電極、ソース電極、ドレイン電極、及びそれら電極に接続される配線のいずれにおいても、インクジェット法を代表とする滴下法により形成する場合、プラズマ処理を行って、微細化を達成することができる。すなわち薄膜トランジスタが有する導電膜を、インクジェット法を代表とする滴下法により形成する場合、導電膜の被形成面にプラズマ処理を行うことができる。 In addition, any of the gate electrode, the source electrode, the drain electrode, and the wiring connected to these electrodes, which the thin film transistor has, is formed by a dropping method typified by an ink jet method, and plasma processing is performed to achieve miniaturization. can do. That is, in the case where the conductive film included in the thin film transistor is formed by a dropping method typified by an ink jet method, plasma treatment can be performed on a surface where the conductive film is formed.
以上、導電膜について説明したが、本発明は、例えばマスク等の被形成面に対してプラズマ処理を行ってもよい。すなわち本発明は、微細化したい対象の被形成面に対してプラズマ処理を行うことを特徴とする。 Although the conductive film has been described above, in the present invention, for example, plasma treatment may be performed on a surface to be formed such as a mask. That is, the present invention is characterized in that plasma processing is performed on a target surface to be miniaturized.
このように本発明は、空気、酸素又は窒素の処理ガスを用いプラズマ処理を用いることにより、材質依存性なく、表面改質を行うことができる。その結果、あらゆる材料に対して表面改質を行うことができる。そのため、基板上に形成する配線であっても、絶縁膜上に形成する配線であっても微細化することができる。またさらに材料依存性がないため、有機材料上に形成するマスク等の微細化を達成することができる。 As described above, according to the present invention, surface modification can be performed without material dependence by using plasma treatment using a treatment gas of air, oxygen, or nitrogen. As a result, surface modification can be performed on any material. Therefore, even a wiring formed on a substrate or a wiring formed on an insulating film can be miniaturized. Further, since there is no material dependence, miniaturization of a mask or the like formed on the organic material can be achieved.
また本発明は、配線やマスク等の所望のパターンを、インクジェット法を代表とする滴下法により形成する一工程において、被形成面に対してプラズマ処理を行うことを特徴とする。すなわち、上記一工程においてプラズマ処理を行った後にインクジェット法を代表とする滴下法により形成される配線やマスク等が微細化するという本発明の効果を得ることができる。そのため本発明の薄膜トランジスタ作製工程において、必ずしもプラズマ処理後にインクジェット法を代表とする滴下法により配線を形成する必要はなく、インクジェット法を代表とする滴下法により微細化したパターンを形成する必要がある場合、プラズマ処理を行えばよい。 In addition, the present invention is characterized in that plasma processing is performed on a surface to be formed in one step of forming a desired pattern such as a wiring or a mask by a dropping method typified by an ink jet method. That is, it is possible to obtain the effect of the present invention that wirings, masks, and the like formed by a dropping method typified by an ink jet method after the plasma treatment in the one step are miniaturized. Therefore, in the thin film transistor manufacturing process of the present invention, it is not always necessary to form a wiring by a dropping method typified by an ink jet method after plasma treatment, and it is necessary to form a fine pattern by a dropping method typified by an ink jet method. Plasma treatment may be performed.
またインクジェット法を代表とする滴下法を用いることにより、マザーガラス基板が1000mm×1300mm、1000mm×1500mm、1800mm×2200mm以上とメータを超える第5世代以降のガラス基板のライン検討が進んでいる。この場合、マザーガラスから多数のパネルを作製することができ、パネルの価格が下がることが期待できる。この場合でも、インクジェット法を代表とする滴下法を用いることにより、採算を維持できる製造ラインを構築することができる。それは、インクジェット法を代表とする滴下法により配線等を形成すると、フォトプロセスの簡略化を行うことができるからである。その結果、フォトマスクが不要となり、設備投資コストの削減、コストの削減を達成することができる。さらにフォトリソグラフィー工程が不要となるため、製造時間を短縮することができる。またインクジェット法を代表とする滴下法により形成すると、材料の利用効率が向上し、コストの削減、廃液処理量の削減が可能となる。このようにインクジェット法を代表とする滴下法を、大面積基板への適用すると好適である。 Further, by using a dropping method typified by an ink jet method, line studies of glass substrates of the fifth generation and beyond, in which the mother glass substrate exceeds 1000 mm × 1300 mm, 1000 mm × 1500 mm, 1800 mm × 2200 mm or more, are proceeding. In this case, a large number of panels can be produced from the mother glass, and the panel price can be expected to decrease. Even in this case, a production line capable of maintaining profitability can be constructed by using a dropping method typified by the inkjet method. This is because if a wiring or the like is formed by a dropping method typified by an ink jet method, the photo process can be simplified. As a result, a photomask becomes unnecessary, and it is possible to achieve a reduction in capital investment cost and a reduction in cost. Furthermore, since a photolithography process is unnecessary, manufacturing time can be shortened. In addition, when formed by a dropping method typified by an ink jet method, the utilization efficiency of the material is improved, and the cost can be reduced and the amount of waste liquid processed can be reduced. As described above, it is preferable to apply the dropping method typified by the ink jet method to a large-area substrate.
以下に、本発明の実施の形態を図面に基づいて説明する。但し、本発明は多くの異なる態様で実施することが可能であり、本発明の趣旨及びその範囲から逸脱することなくその形態及び詳細を様々に変更し得ることは当業者であれば容易に理解される。従って、本実施の形態の記載内容に限定して解釈されるものではない。なお、実施の形態を説明するための全図において、同一部分又は同様な機能を有する部分には同一の符号を付し、その繰り返しの説明は省略する。 Embodiments of the present invention will be described below with reference to the drawings. However, the present invention can be implemented in many different modes, and those skilled in the art can easily understand that the modes and details can be variously changed without departing from the spirit and scope of the present invention. Is done. Therefore, the present invention is not construed as being limited to the description of this embodiment mode. Note that in all the drawings for describing the embodiments, the same portions or portions having similar functions are denoted by the same reference numerals, and repetitive description thereof is omitted.
以下の実施の形態において、滴下法にはインクジェット法を用いる。また断りのない限り、撥液処理にはプラズマ処理を用いる。 In the following embodiments, an ink jet method is used as the dropping method. Unless otherwise noted, plasma treatment is used for the liquid repellent treatment.
またTFTはゲート、ソース、ドレインの3端子を有するが、ソース端子(ソース電極)、ドレイン端子(ドレイン電極)に関しては、トランジスタの構造上、明確に区別が出来ない。よって、素子間の接続について説明する際は、ソース電極、ドレイン電極のうち一方を第1の電極、他方を第2の電極と表記する。 A TFT has three terminals, a gate, a source, and a drain. However, the source terminal (source electrode) and the drain terminal (drain electrode) cannot be clearly distinguished because of the structure of the transistor. Therefore, when describing connection between elements, one of a source electrode and a drain electrode is referred to as a first electrode, and the other is referred to as a second electrode.
(実施の形態1)
本実施の形態では、薄膜トランジスタの作製方法の一例について説明する。
(Embodiment 1)
In this embodiment, an example of a method for manufacturing a thin film transistor will be described.
まず図1(A)に示すように、絶縁表面を有する基板100上に下地膜101を形成する。基板100には、例えばバリウムホウケイ酸ガラスや、アルミノホウケイ酸ガラスなどのガラス基板、石英基板、ステンレス基板等を用いることができる。また、ポリエチレン-テレフタレート(PET)、ポリエチレンナフタレート(PEN)、ポリエーテルサルフォン(PES)に代表されるプラスチックや、アクリル等の可撓性を有する合成樹脂からなる基板は、一般的に他の基板と比較して耐熱温度が低い傾向にあるが、作製工程における処理温度に耐え得るのであれば用いることが可能である。特に、半導体膜を結晶化するための加熱工程を要しない非晶質半導体膜を有する薄膜トランジスタを形成する場合、可撓性を有する合成樹脂からなる基板を用いやすい。
First, as illustrated in FIG. 1A, a
下地膜101は基板100中に含まれるNaなどのアルカリ金属やアルカリ土類金属が、半導体膜中に拡散し、半導体素子の特性に悪影響を及ぼすのを防ぐために設ける。よってアルカリ金属やアルカリ土類金属の半導体膜への拡散を抑えることができる酸化珪素、窒化珪素、窒化酸化珪素、酸化チタン、窒化チタンなどの絶縁膜を用いて下地膜を形成することができる。またチタン等の導電膜を用いて下地膜を形成することもできる。この場合、導電膜は、作製工程における加熱処理等により、酸化されることがある。特に、下地膜の材料は、ゲート電極材料と密着性の高いものを選択するとよい。例えば、ゲート電極にAgを用いる場合、酸化チタン(TiOx)からなる下地膜を形成すると好ましい。なお下地膜101は単層構造又は積層構造を有してもよい。本実施の形態において、下地膜は第1の下地膜と第2の下地膜との積層構造とする。第1の下地膜として、プラズマCVD法を用い、原料ガスにSiH4、N2O、NH3、H2、圧力が0.3Torr(39.9Pa)、RFパワーが50W、RF周波数が60MHz、基板温度が400℃として形成する酸化窒化珪素膜を10〜200nm(好ましくは50〜200nm)形成する。第2の下地膜として、プラズマCVD法を用い、原料ガスにSiH4、N2O、圧力が0.3Torr(39.9Pa)、RFパワーが150W、RF周波数が60MHz、基板温度が400℃として形成する酸化窒化珪素膜を50〜200nm(好ましくは200〜150nm)形成する。
The
ガラス基板、ステンレス基板またはプラスチック基板のように、アルカリ金属やアルカリ土類金属が多少なりとも含まれている基板を用いる場合、不純物の拡散を防ぐという観点から下地膜を設けることは有効である。一方、石英基板など不純物の拡散がさして問題とならない場合は、必ずしも下地膜を設ける必要はない。すなわち不純物が半導体膜へ拡散することが防止できれば、下地膜は必ずしも設ける必要はない。例えば、ゲート電極上にゲート絶縁膜を介して半導体膜を形成する場合、ゲート絶縁膜が半導体膜へ不純物の拡散を防止する機能を果たすことができるため、下地膜を設ける必要はない。 In the case of using a substrate containing an alkali metal or an alkaline earth metal, such as a glass substrate, a stainless steel substrate, or a plastic substrate, it is effective to provide a base film from the viewpoint of preventing impurity diffusion. On the other hand, in the case where diffusion of impurities does not cause any problem such as a quartz substrate, it is not always necessary to provide a base film. That is, the base film is not necessarily provided if impurities can be prevented from diffusing into the semiconductor film. For example, in the case where a semiconductor film is formed over a gate electrode with a gate insulating film interposed therebetween, it is not necessary to provide a base film because the gate insulating film can function to prevent diffusion of impurities into the semiconductor film.
その後、ゲート電極の被形成面に対してプラズマ処理を行う。本実施の形態では、ゲート電極の被形成面が下地膜であるため、下地膜に対してプラズマ処理を行う。プラズマ処理は、ゲート電極の被形成面に対して非接触で行うとよい。 After that, plasma treatment is performed on the formation surface of the gate electrode. In this embodiment mode, since the formation surface of the gate electrode is a base film, plasma treatment is performed on the base film. The plasma treatment may be performed in a non-contact manner with respect to the formation surface of the gate electrode.
プラズマ処理は、空気、酸素又は窒素を処理ガスとして用い、圧力が数十Torr〜800Torr(106400Pa)、好ましくは700Torr(93100Pa)〜800Torr(大気圧又は大気圧近傍の圧力)の状態で行う。またプラズマ処理の電源にはRF電源やAC電源を用いることができる。例えば、AC電源を用い、交流電圧100V、周波数13.56MHz等の条件で印加し、パワーを変化させてプラズマを発生させる。このとき安定なプラズマを放電するため、電圧幅2〜4μsec間隔でパルスを印加する。このプラズマ処理を行う結果、アルコールや油等の液体に対して濡れ性の低い撥液性となるように表面改質が行われる。 The plasma treatment is performed using air, oxygen, or nitrogen as a treatment gas under a pressure of several tens of Torr to 800 Torr (106400 Pa), preferably 700 Torr (93100 Pa) to 800 Torr (atmospheric pressure or pressure near atmospheric pressure). An RF power source or an AC power source can be used as a power source for plasma processing. For example, an AC power source is used and applied under conditions such as an AC voltage of 100 V and a frequency of 13.56 MHz, and plasma is generated by changing the power. At this time, in order to discharge stable plasma, pulses are applied at intervals of 2 to 4 μsec. As a result of this plasma treatment, surface modification is performed so that the liquid repellency is low in wettability with respect to liquids such as alcohol and oil.
図1(B)に示すように、インクジェット法を用いて、溶媒中に導電体が混入したドットを滴下して、ゲート電極103として機能する導電膜を形成する。本実施の形態では、テトラデカンの溶媒中に銀(Ag)の導電体が分散しているドットを滴下する。テトラデカンは、プラズマ処理が行われた面に対して撥液性を示す溶媒である。そのためプラズマ処理を行った結果、インクジェット法により形成されたゲート電極を微細化することができる。
As shown in FIG. 1B, a conductive film functioning as the
その後、ドットの溶媒を除去する必要があるとき、焼成したり、乾燥させるため加熱処理を施す。具体的には、所定の温度、例えば200℃〜300℃で加熱すればよく、好ましくは酸素を有する雰囲気で加熱処理を行う。このときゲート電極表面に凹凸が生じないように加熱温度を設定する。本実施の形態のように銀(Ag)を有するドットを用いる場合、酸素及び窒素を有する雰囲気で加熱処理を行うと、溶媒中に含まれる接着剤等の熱硬化性樹脂などの有機物が分解されるため、有機物を含まない銀(Ag)を得ることができる。その結果、ゲート電極表面の平坦性を高め、比抵抗値を低くすることができる。 Then, when it is necessary to remove the solvent of a dot, it heat-processes in order to bake or to dry. Specifically, heating may be performed at a predetermined temperature, for example, 200 ° C. to 300 ° C., and heat treatment is preferably performed in an atmosphere containing oxygen. At this time, the heating temperature is set so that the gate electrode surface is not uneven. When using a dot containing silver (Ag) as in this embodiment, if heat treatment is performed in an atmosphere containing oxygen and nitrogen, organic substances such as a thermosetting resin such as an adhesive contained in the solvent are decomposed. Therefore, silver (Ag) which does not contain organic substances can be obtained. As a result, the flatness of the gate electrode surface can be improved and the specific resistance value can be lowered.
またゲート電極は、銀(Ag)以外にタンタル、タングステン、チタン、モリブデン、アルミニウム、銅から選ばれた元素、または前記元素を主成分とする合金材料もしくは化合物材料で形成することもできる。また導電膜は、インクジェット法以外に、スパッタリング法、プラズマCVD法により形成することができる。スパッタリング法、プラズマCVD法により形成する導電膜として、リン等の不純物元素をドーピングした多結晶シリコン膜に代表される半導体膜や、AgPdCu合金を用いることができる。 In addition to silver (Ag), the gate electrode can be formed of an element selected from tantalum, tungsten, titanium, molybdenum, aluminum, and copper, or an alloy material or a compound material containing the element as a main component. The conductive film can be formed by a sputtering method or a plasma CVD method in addition to the ink jet method. As a conductive film formed by a sputtering method or a plasma CVD method, a semiconductor film typified by a polycrystalline silicon film doped with an impurity element such as phosphorus, or an AgPdCu alloy can be used.
図1(C)に示すように、ゲート電極を覆ってゲート絶縁膜104として機能する絶縁膜を形成する。絶縁膜は積層構造又は単層構造を有することができる。絶縁膜として、プラズマCVD法により酸化珪素、窒化珪素又は窒化酸化珪素等の絶縁体を形成することができる。なおインクジェット法により絶縁膜の材料が混入されたドットを吐出してゲート絶縁膜を形成してもよい。本実施の形態のように、銀(Ag)をゲート電極として用いる場合、ゲート電極を覆う絶縁膜には窒化珪素膜を用いると好ましい。酸素を有する絶縁膜を用いると、銀(Ag)と反応し、酸化銀が形成されゲート電極表面が荒れる恐れがあるからである。
As shown in FIG. 1C, an insulating film functioning as the
ゲート絶縁膜上に、半導体膜105を形成する。半導体膜は、プラズマCVD法、スパッタリング法、インクジェット法等により形成することができる。半導体膜の膜厚は25〜200nm(好ましくは30〜60nm)とする。また半導体膜の材料は珪素だけではなくシリコンゲルマニウムも用いることができる。シリコンゲルマニウムを用いる場合、ゲルマニウムの濃度は0.01〜4.5atomic%程度であることが好ましい。また半導体膜は、非晶質半導体、非晶質半導体の中に結晶粒が分散するように存在しているセミアモルファス半導体、及び非晶質半導体中に0.5nm〜20nmの結晶粒を観察することができる微結晶半導体、から選ばれたいずれの状態を有してもよい。特に、0.5nm〜20nmの結晶を粒観察することができる微結晶状態は所謂マイクロクリスタル(μc)と呼ばれている。
A
セミアモルファス半導体の材料としてシリコンを用いたセミアモルファスシリコン(SASとも表記する)は、珪化物気体をグロー放電分解することにより得ることができる。代表的な珪化物気体としては、SiH4であり、その他にもSi2H6、SiH2Cl2、SiHCl3、SiCl4、SiF4などを用いることができる。珪化物気体を水素、水素とヘリウム、アルゴン、クリプトン、ネオンから選ばれた一種または複数種の希ガス元素で希釈して用いることによりSASの形成を容易なものとすることができる。このとき希釈率が10倍〜1000倍の範囲となるように、珪化物気体を希釈すると好ましい。またSi2H6及びGeF4を用い、ヘリウムガスで希釈する方法を用いてSASを形成することができる。グロー放電分解による被膜の反応生成は減圧下で行うと好ましく、圧力は概略0.1Pa〜133Paの範囲で行えばよい。グロー放電を形成するための電力は1MHz〜120MHz、好ましくは13MHz〜60MHzの高周波電力を供給すればよい。基板加熱温度は300度以下が好ましく、100〜250度の基板加熱温度が推奨される。 Semi-amorphous silicon (also referred to as SAS) using silicon as a semi-amorphous semiconductor material can be obtained by glow discharge decomposition of a silicide gas. A typical silicide gas is SiH 4 , and in addition, Si 2 H 6 , SiH 2 Cl 2 , SiHCl 3 , SiCl 4 , SiF 4 and the like can be used. The formation of the SAS can be facilitated by diluting the silicide gas with one or more kinds of rare gas elements selected from hydrogen, hydrogen and helium, argon, krypton, and neon. At this time, it is preferable to dilute the silicide gas so that the dilution rate is in the range of 10 to 1000 times. Further, the SAS can be formed by using Si 2 H 6 and GeF 4 and diluting with helium gas. The reaction generation of the coating by glow discharge decomposition is preferably performed under reduced pressure, and the pressure may be in the range of about 0.1 Pa to 133 Pa. The power for forming the glow discharge may be high frequency power of 1 MHz to 120 MHz, preferably 13 MHz to 60 MHz. The substrate heating temperature is preferably 300 ° C. or less, and a substrate heating temperature of 100 to 250 ° C. is recommended.
本実施の形態では、プラズマCVD法を用いて、珪素を主成分とする非晶質半導体膜(非晶質珪素膜、アモルファスシリコンとも表記する)を形成する。 In this embodiment, an amorphous semiconductor film containing silicon as a main component (also referred to as an amorphous silicon film or amorphous silicon) is formed by a plasma CVD method.
次いで、一導電型を有する半導体膜を形成する。一導電型を有する半導体膜は、プラズマCVD法、スパッタリング法、インクジェット法等を用いて形成することができる。なお一導電型を有する半導体膜を設ける場合、半導体膜と電極とのコンタクト抵抗が低くなり好ましいが、必要に応じて設ければよい。本実施の形態では、プラズマCVD法を用いてN型を有する半導体膜106を形成する。このように半導体とN型を有する半導体膜をプラズマCVD法により形成する場合、半導体膜105と、N型を有する半導体膜106、更にはゲート絶縁膜を連続形成すると好ましく、原料ガスの供給を変化させることにより大気開放せず、連続形成することができる。
Next, a semiconductor film having one conductivity type is formed. The semiconductor film having one conductivity type can be formed by a plasma CVD method, a sputtering method, an ink jet method, or the like. Note that in the case where a semiconductor film having one conductivity type is provided, the contact resistance between the semiconductor film and the electrode is preferably reduced, but may be provided as necessary. In this embodiment, the N-
図1(D)に示すように、半導体膜105及びN型を有する半導体膜106を所望の形状にパターニングする。図示しないが所望箇所にマスクを形成し、マスクを用いてエッチングすればよい。マスクは、材料の利用効率が向上し、コストの削減、廃液処理量の削減が可能となるためインクジェット法を用いて形成すると好ましいが、フォトリソグラフィー法により形成してもよい。更にインクジェット法によりマスクを形成すると、フォトリソグラフィー工程の簡略化を行うことができる。すなわち、フォトマスク形成、露光等が不要となり、設備投資コストの削減を達成でき、製造時間を短縮することができる。インクジェット法によりマスクを形成する場合、マスクの被形成面に対してプラズマ処理を行ってもよい。その結果、インクジェット法により形成されたマスクを微細化することができる。
As shown in FIG. 1D, the
マスク材料として、無機材料(酸化シリコン、窒化シリコン、酸化窒化シリコンなど)、感光性または非感光性の有機材料(ポリイミド、アクリル、ポリアミド、ポリイミドアミド、ポリビニルアルコール、レジストまたはベンゾシクロブテン)を用いることができる。例えばポリイミドを用いてインクジェット法によりマスクを形成する場合、所望箇所にインクジェット法によりポリイミドを吐出した後、焼成するため150〜300℃で加熱処理を行うとよい。その後、マスクを用いて半導体膜105及びN型を有する半導体膜106エッチングする。エッチング後、マスクを除去するため、プラズマ処理を行う。なお、インクジェット法を用いて形成されるマスクは除去せずに絶縁膜として機能させてもよい。
Inorganic materials (silicon oxide, silicon nitride, silicon oxynitride, etc.) and photosensitive or non-photosensitive organic materials (polyimide, acrylic, polyamide, polyimide amide, polyvinyl alcohol, resist or benzocyclobutene) are used as mask materials. Can do. For example, in the case where a mask is formed using an inkjet method using polyimide, heat treatment may be performed at 150 to 300 ° C. for firing after discharging polyimide to a desired portion by an inkjet method. After that, the
そして、図1(A)と同様にソース電極及びドレイン電極の被形成面に対してプラズマ処理を行う。本実施の形態では、ソース電極及びドレイン電極の被形成面であるN型を有する半導体膜、及びゲート絶縁膜に対してプラズマ処理を行う。プラズマ処理は、ソース電極及びドレイン電極の被形成面に対して非接触で行うとよい。このプラズマ処理を行う結果、アルコールや油等の液体に対して濡れ性の低い撥液性となるように表面改質が行われる。 Then, plasma treatment is performed on the formation surfaces of the source electrode and the drain electrode as in FIG. In this embodiment mode, plasma treatment is performed on an N-type semiconductor film, which is a formation surface of the source electrode and the drain electrode, and the gate insulating film. The plasma treatment may be performed in a non-contact manner on the formation surfaces of the source electrode and the drain electrode. As a result of this plasma treatment, surface modification is performed so that the liquid repellency is low in wettability with respect to liquids such as alcohol and oil.
図1(E)に示すように、ソース電極及びドレイン電極108として機能する導電膜を形成する。導電膜は、単層構造及び積層構造のいずれを有してもよい。導電膜として、金、銀、銅、アルミニウム、チタン、モリブデン、タングステンもしくはシリコンの元素からなる膜又はこれらの元素を用いた合金膜を用いることができる。また導電膜はインクジェット法、CVD法及びスパッタリング法のいずれかを用いて形成することができる。本実施の形態では、インクジェット法により銀(Ag)が混入されたドットを用いて形成する。具体的には、図1(B)に示したゲート電極と同様に行えばよい。プラズマ処理を行う結果、インクジェット法により形成されたソース電極及びドレイン電極を微細化することができる。
As shown in FIG. 1E, a conductive film functioning as the source and drain
その後、ドットの溶媒を除去する必要があるとき、焼成したり、乾燥させるため加熱処理を施す。 Then, when it is necessary to remove the solvent of a dot, it heat-processes in order to bake or to dry.
その後、ソース電極及びドレイン電極をマスクとして、N型を有する半導体膜106をエッチングする。N型を有する半導体膜が、ソース電極及びドレイン電極を短絡することを防止するためである。このとき、半導体膜105が多少エッチングされることがある。
After that, the n-
以上のように、ソース電極及びドレイン電極まで設けられた薄膜トランジスタが完成する。本実施の形態の薄膜トランジスタは、半導体膜より下方にゲート電極が設けられる、所謂ボトムゲート型の薄膜トランジスタである。より詳細には、半導体膜が多少エッチングされている、所謂チャネルエッチ型である。このような薄膜トランジスタが複数設けられた基板をTFT基板と表記する。 As described above, the thin film transistor provided with the source electrode and the drain electrode is completed. The thin film transistor in this embodiment is a so-called bottom gate thin film transistor in which a gate electrode is provided below a semiconductor film. More specifically, it is a so-called channel etch type in which the semiconductor film is slightly etched. A substrate provided with a plurality of such thin film transistors is referred to as a TFT substrate.
また本実施の形態で示した薄膜トランジスタは、インクジェット法により導電膜を形成する前に、プラズマ処理を行うことを特徴とする。インクジェット法によりゲート電極、ソース電極及びドレイン電極を形成する前にプラズマ処理を行っているが、少なくとも1つのインクジェット工程の前にプラズマ処理を行えばよい。そのため、本実施の形態で示した以外のインクジェット工程の前であればいつプラズマ処理を行ってもよい。 The thin film transistor described in this embodiment is characterized in that plasma treatment is performed before a conductive film is formed by an inkjet method. Although the plasma treatment is performed before forming the gate electrode, the source electrode, and the drain electrode by an inkjet method, the plasma treatment may be performed before at least one inkjet process. Therefore, plasma treatment may be performed at any time before the ink jet process other than that shown in this embodiment mode.
以上のように、インクジェット工程前のプラズマ処理により、微細化されたゲート電極や、ソース電極及びドレイン電極を有する薄膜トランジスタを得ることができる。 As described above, a thin film transistor including a miniaturized gate electrode, a source electrode, and a drain electrode can be obtained by plasma treatment before an inkjet process.
またインクジェット法により配線やマスク等を形成すると、材料の利用効率が向上し、コストの削減、廃液処理量の削減が可能となる。特にインクジェット法によりマスクを形成すると、フォトリソグラフィー工程と比較して工程の簡略化を行うことができる。その結果、設備投資コストの削減、コストの削減、製造時間を短縮することができる。 In addition, when a wiring, a mask, or the like is formed by the ink jet method, the material utilization efficiency is improved, and the cost can be reduced and the amount of waste liquid can be reduced. In particular, when a mask is formed by an inkjet method, the process can be simplified as compared with a photolithography process. As a result, it is possible to reduce capital investment cost, cost reduction, and manufacturing time.
(実施の形態2)
本実施の形態では、実施の形態1と異なる構造の薄膜トランジスタの作製方法を説明する。実施の形態1と異なる構造は、半導体膜上に保護膜を形成する点である。そのため、その他の作製方法については実施の形態1を参照すればよく、詳細な説明を省略する。
(Embodiment 2)
In this embodiment, a method for manufacturing a thin film transistor having a structure different from that in Embodiment 1 will be described. A structure different from that in Embodiment Mode 1 is that a protective film is formed over the semiconductor film. Therefore, Embodiment 1 may be referred to for other manufacturing methods, and detailed description thereof is omitted.
図2(A)に示すように、絶縁表面を有する基板100上に下地膜101を形成する。そして下地膜101に対してプラズマ処理を行う。このプラズマ処理を行う結果、アルコールや油等の液体に対して濡れ性の低い撥液性となるように表面改質が行われる。
As shown in FIG. 2A, a
図2(B)に示すように、下地膜上にゲート電極103を形成し、ゲート電極を覆ってゲート絶縁膜104を形成し、ゲート絶縁膜上に半導体膜105を形成する。プラズマ処理を行う結果、インクジェット法により形成されたゲート電極を微細化することができる。その後、ドットの溶媒を除去する必要があるとき、焼成したり、乾燥させるため加熱処理を施す。その後、半導体膜上に保護膜を形成する。保護膜は、酸化珪素や、窒化珪素、窒化酸化珪素などの絶縁膜をインクジェット法、プラズマCVD法、スパッタリング法等により形成する。また半導体膜、及び保護膜、さらにゲート絶縁膜を連続形成するとよい。同一チャンバー内で、原料ガスの供給を変化させることにより、大気開放せずに連続形成することができる。
As shown in FIG. 2B, a
またインクジェット法により保護膜を形成すると、材料の利用効率が向上し、コストの削減、廃液処理量の削減が可能となるからである。そしてインクジェット法により保護膜を形成すると、フォトリソグラフィー工程の簡略化を行うことができる。その結果、フォトマスクが不要となり、設備投資コストの削減、コストの削減を達成することができる。さらにフォトリソグラフィー工程が不要となるため、製造時間を短縮することができるからである。このとき、保護膜の被形成面に対してプラズマ処理を行ってもよい。その結果、インクジェット法により形成された保護膜を微細化することができる。本実施の形態では、インクジェット法を用いてポリイミド又はポリビニルアルコール等を滴下して保護膜110を形成する。
Further, when the protective film is formed by the ink jet method, the material utilization efficiency is improved, and the cost and the amount of waste liquid can be reduced. When a protective film is formed by an ink jet method, the photolithography process can be simplified. As a result, a photomask becomes unnecessary, and it is possible to achieve a reduction in capital investment cost and a reduction in cost. In addition, since a photolithography process is not required, manufacturing time can be shortened. At this time, plasma treatment may be performed on the surface on which the protective film is formed. As a result, the protective film formed by the inkjet method can be miniaturized. In this embodiment mode, the
また保護膜を所望の形状にパターニングする必要があるとき、マスクを用いてパターニングする。このとき、ゲート電極をマスクとして基板裏面から露光すれば自己整合的に保護膜をエッチングすることができる。もちろんフォトリソグラフィー法やインクジェット法によりマスクを形成してもよい。インクジェット法によりマスクを形成する場合、マスクの被形成面に対してプラズマ処理を行ってもよい。その結果、インクジェット法により形成されたマスクを微細化することができる。 When it is necessary to pattern the protective film into a desired shape, patterning is performed using a mask. At this time, the protective film can be etched in a self-aligned manner by exposing from the back surface of the substrate using the gate electrode as a mask. Of course, the mask may be formed by a photolithography method or an inkjet method. When the mask is formed by an inkjet method, plasma treatment may be performed on a surface on which the mask is formed. As a result, the mask formed by the inkjet method can be miniaturized.
図2(C)に示すように、一導電型を有する半導体膜を形成する。本実施の形態では、プラズマCVD法を用いてN型を有する半導体膜106を形成する。
As shown in FIG. 2C, a semiconductor film having one conductivity type is formed. In this embodiment, the N-
図2(D)に示すように、N型を有する半導体膜、及び半導体膜を所望の形状にパターニングする。この場合、図示しないが所望箇所にマスクを形成し、マスクを用いてエッチングすればよい。マスクは、材料の利用効率が向上し、コストの削減、廃液処理量の削減が可能となるためインクジェット法を用いて形成すると好ましいが、フォトリソグラフィー法により形成してもよい。特にインクジェット法によりマスクを形成すると、フォトリソグラフィー工程と比較して工程の簡略化を行うことができる。その結果、設備投資コストの削減、コストの削減、製造時間を短縮することができる。本実施の形態では、マスクとしてインクジェット法を用いてポリイミド又はポリビニルアルコール等を滴下する。このとき、マスクの被形成面に対してプラズマ処理を行ってもよい。その結果、インクジェット法により形成されたマスクを微細化することができる。 As shown in FIG. 2D, the N-type semiconductor film and the semiconductor film are patterned into a desired shape. In this case, although not shown, a mask may be formed at a desired location and etched using the mask. The mask is preferably formed by an ink jet method because it improves material utilization efficiency, reduces costs, and reduces the amount of waste liquid, but may be formed by a photolithography method. In particular, when a mask is formed by an inkjet method, the process can be simplified as compared with a photolithography process. As a result, it is possible to reduce capital investment cost, cost reduction, and manufacturing time. In this embodiment mode, polyimide or polyvinyl alcohol or the like is dropped using an inkjet method as a mask. At this time, plasma treatment may be performed on the formation surface of the mask. As a result, the mask formed by the inkjet method can be miniaturized.
エッチング後、マスクを除去するため、プラズマ処理を行う。なお、インクジェット法を用いて形成されるマスクは除去せずに絶縁膜として機能させてもよい。 After the etching, plasma treatment is performed to remove the mask. Note that a mask formed by an inkjet method may be functioned as an insulating film without being removed.
そして図2(A)と同様にソース電極及びドレイン電極の被形成面に対してプラズマ処理を行う。本実施の形態では、ソース電極及びドレイン電極の被形成面であるN型を有する半導体膜、及びゲート絶縁膜に対してプラズマ処理を行う。プラズマ処理は、ソース電極及びドレイン電極の被形成面に対して非接触で行うとよい。このプラズマ処理を行う結果、アルコールや油等の液体に対して濡れ性の低い撥液性となるように表面改質が行われる。 Then, as in FIG. 2A, plasma treatment is performed on the formation surfaces of the source electrode and the drain electrode. In this embodiment mode, plasma treatment is performed on an N-type semiconductor film, which is a surface where a source electrode and a drain electrode are formed, and a gate insulating film. The plasma treatment may be performed in a non-contact manner on the formation surfaces of the source electrode and the drain electrode. As a result of this plasma treatment, surface modification is performed so that the liquid repellency is low in wettability with respect to liquids such as alcohol and oil.
図2(E)に示すように、ソース電極及びドレイン電極108として機能する導電膜を形成する。本実施の形態では、インクジェット法により銀(Ag)が混入されたドットを用いて形成する。プラズマ処理を行う結果、インクジェット法により形成されたソース電極及びドレイン電極を微細化することができる。その後、ドットの溶媒を除去する必要があるとき、焼成したり、乾燥させるため加熱処理を施す。
As shown in FIG. 2E, a conductive film functioning as the source and drain
以上のように、ソース電極及びドレイン電極まで設けられた薄膜トランジスタが完成する。本実施の形態の薄膜トランジスタは、半導体膜より下方にゲート電極が設けられる、所謂ボトムゲート型の薄膜トランジスタである。より詳細には、半導体膜がエッチングされない、所謂チャネル保護型である。このような薄膜トランジスタが複数設けられた基板をTFT基板と表記する。 As described above, the thin film transistor provided with the source electrode and the drain electrode is completed. The thin film transistor in this embodiment is a so-called bottom gate thin film transistor in which a gate electrode is provided below a semiconductor film. More specifically, it is a so-called channel protection type in which the semiconductor film is not etched. A substrate provided with a plurality of such thin film transistors is referred to as a TFT substrate.
またこのようにして形成される薄膜トランジスタは、インクジェット法により導電膜を形成する前に、プラズマ処理を行うことを特徴とする。本実施の形態では、インクジェット法によりゲート電極、及びソース電極及びドレイン電極を形成する前にプラズマ処理を行っているが、少なくとも1つのインクジェット工程前においてプラズマ処理を行えばよい。そのため、本実施の形態で示した以外であっても、インクジェット工程の前であればいつにプラズマ処理を行ってもよい。 The thin film transistor thus formed is characterized in that plasma treatment is performed before the conductive film is formed by an inkjet method. In this embodiment mode, plasma treatment is performed before the gate electrode, the source electrode, and the drain electrode are formed by an inkjet method. However, plasma treatment may be performed before at least one inkjet step. Therefore, plasma treatment may be performed at any time before the ink jet process, other than those described in this embodiment mode.
以上のように、インクジェット工程前のプラズマ処理により、微細化されたゲート電極や、ソース電極及びドレイン電極を有する薄膜トランジスタを得ることができる。 As described above, a thin film transistor including a miniaturized gate electrode, a source electrode, and a drain electrode can be obtained by plasma treatment before an inkjet process.
またインクジェット法により配線やマスク等を形成すると、材料の利用効率が向上し、コストの削減、廃液処理量の削減が可能となる。特にインクジェット法によりマスクを形成すると、フォトリソグラフィー工程と比較して工程の簡略化を行うことができる。その結果、設備投資コストの削減、コストの削減、製造時間を短縮することができる。 In addition, when a wiring, a mask, or the like is formed by the ink jet method, the material utilization efficiency is improved, and the cost can be reduced and the amount of waste liquid can be reduced. In particular, when a mask is formed by an inkjet method, the process can be simplified as compared with a photolithography process. As a result, it is possible to reduce capital investment cost, cost reduction, and manufacturing time.
(実施の形態3)
本実施の形態では、実施の形態1及び2に示す構造と異なり、半導体膜より上方にゲート電極が設けられる、所謂トップゲート型の薄膜トランジスタである。そのため、その他の作製方法については実施の形態1及び2を参照すればよく、詳細な説明は省略する。
(Embodiment 3)
Unlike the structures shown in
図3(A)に示すように、絶縁表面を有する基板100上に下地膜101を形成する。その後、ソース電極及びドレイン電極108となる導電膜、一導電型を有する半導体膜を順に形成する。本実施の形態では、一導電型を有する半導体膜にN型を有する半導体膜106を用いる。ソース電極及びドレイン電極となる導電膜、N型を有する半導体膜を形成後、マスクを用いて所望の形状にパターニングする。図示しないが、マスクはインクジェット法又はフォトリソグラフィー法により形成することができる。インクジェット法によりマスクを形成すると、材料の利用効率が向上し、コストの削減、廃液処理量の削減が可能となるからである。特にインクジェット法によりマスクを形成すると、フォトリソグラフィー工程と比較して工程の簡略化を行うことができる。その結果、設備投資コストの削減、コストの削減、製造時間を短縮することができる。インクジェット法によりマスクを形成する場合、マスクの被形成面に対してプラズマ処理を行ってもよい。その結果、インクジェット法により形成されたマスクを微細化することができるからである。本実施の形態ではマスクとしてインクジェット法を用いてポリイミド又はポリビニルアルコール等を滴下する。その後、必要に応じて加熱を行い焼成し、ドライエッチング法を用いてパターニングする。
As shown in FIG. 3A, a
パターニング後、マスクを除去するため、プラズマ処理を行う。なお、インクジェット法を用いて形成されるマスクは除去せずに絶縁膜として機能させてもよい。 After the patterning, plasma treatment is performed to remove the mask. Note that a mask formed by an inkjet method may be functioned as an insulating film without being removed.
図3(B)に示すように、半導体膜105を、N型を有する半導体膜を覆うように形成する。半導体膜105上にマスク112を形成する。マスク112は、インクジェット法又はフォトリソグラフィー法により形成することができる。本実施の形態ではマスクとしてインクジェット法を用いてポリイミド又はポリビニルアルコール等を滴下する。必要に応じて、インクジェット法により形成されたマスクに対して加熱を行い、焼成する。なおこのとき、半導体膜105に対してプラズマ処理を行ってもよい。その結果、インクジェット法により形成されたマスクを微細化することができる。
As shown in FIG. 3B, the
その後、マスクを用いて半導体膜105を所望の形状にパターニングする。このとき同時に、N型を有する半導体膜をパターニングすることもできる。すなわち、半導体膜105とN型を有する半導体膜106とが同一ガスに対して同様のエッチレートを有する場合、同時にパターニングされてしまう。
Thereafter, the
パターニング後、マスク112を除去するため、プラズマ処理を行う。なお、インクジェット法を用いて形成されるマスクは除去せずに絶縁膜として機能させてもよい。
After the patterning, plasma treatment is performed to remove the
図3(C)に示すように、半導体膜105を覆うようにゲート絶縁膜104として機能する絶縁膜を形成する。ゲート絶縁膜は少なくとも半導体膜と、後に形成されるゲート電極との間に形成されていればよい。そしてゲート絶縁膜104に対してプラズマ処理を行う。このプラズマ処理を行う結果、アルコールや油等の液体に対して濡れ性の低い撥液性となるように表面改質が行われる。
As shown in FIG. 3C, an insulating film functioning as the
図3(D)に示すように、ゲート絶縁膜を介して半導体膜上にゲート電極103として機能する導電膜を形成する。本実施の形態では、テトラデカンの溶媒中に銀(Ag)の導電体が分散しているドットを滴下する。プラズマ処理を行う結果、インクジェット法により形成されたゲート電極を微細化することができる。その後、ドットの溶媒を除去する必要があるとき、焼成したり、乾燥させるため加熱処理を施す。
As shown in FIG. 3D, a conductive film functioning as the
このようにゲート電極まで形成され、半導体素子として機能する薄膜トランジスタが完成する。このような薄膜トランジスタが複数設けられた基板をTFT基板と表記する。 Thus, a thin film transistor that is formed up to the gate electrode and functions as a semiconductor element is completed. A substrate provided with a plurality of such thin film transistors is referred to as a TFT substrate.
図3(E)に示すように、少なくともゲート電極を覆って保護膜113を形成すると好ましい。保護膜は積層構造又は単層構造を有することができる。保護膜として、プラズマCVD法により酸化珪素、窒化珪素又は窒化酸化珪素等の絶縁体を形成することができる。なおインクジェット法により絶縁膜の材料が混入されたドットを吐出して保護膜を形成してもよい。本実施の形態のように、銀(Ag)をゲート電極として用いる場合、ゲート電極を覆う保護膜には窒化珪素膜を用いると好ましい。酸素を有する保護膜を用いると、銀(Ag)と反応し、酸化銀が形成されゲート電極表面が荒れる恐れがあるからである。
As shown in FIG. 3E, a
本実施の形態の薄膜トランジスタは、半導体膜より上方にゲート電極が設けられる、所謂トップゲート型の薄膜トランジスタである。 The thin film transistor of this embodiment is a so-called top gate thin film transistor in which a gate electrode is provided above a semiconductor film.
本実施の形態のように形成される薄膜トランジスタは、インクジェット法により導電膜を形成する前に、プラズマ処理を行うことを特徴とする。本実施の形態では、インクジェット法によりゲート電極を形成する前にプラズマ処理を行っているが、少なくとも1つのインクジェット工程前においてプラズマ処理を行えばよい。そのため、本実施の形態で示した以外であっても、インクジェット工程の前であればいつにプラズマ処理を行ってもよい。 A thin film transistor formed as in this embodiment mode is characterized in that plasma treatment is performed before a conductive film is formed by an inkjet method. In this embodiment mode, plasma treatment is performed before the gate electrode is formed by an inkjet method. However, plasma treatment may be performed before at least one inkjet step. Therefore, plasma treatment may be performed at any time before the ink jet process, other than those described in this embodiment mode.
以上のように、インクジェット工程前のプラズマ処理により、微細化されたゲート電極を有する薄膜トランジスタを得ることができる。 As described above, a thin film transistor having a miniaturized gate electrode can be obtained by plasma treatment before an inkjet process.
またインクジェット法により配線やマスク等を形成すると、材料の利用効率が向上し、コストの削減、廃液処理量の削減が可能となる。特にインクジェット法によりマスクを形成すると、フォトリソグラフィー工程と比較して工程の簡略化を行うことができる。その結果、設備投資コストの削減、コストの削減、製造時間を短縮することができる。 In addition, when a wiring, a mask, or the like is formed by the ink jet method, the material utilization efficiency is improved, and the cost can be reduced and the amount of waste liquid can be reduced. In particular, when a mask is formed by an inkjet method, the process can be simplified as compared with a photolithography process. As a result, it is possible to reduce capital investment cost, cost reduction, and manufacturing time.
(実施の形態4)
本実施の形態では、実施の形態3と異なる構造の薄膜トランジスタの作製方法を説明する。実施の形態3と異なる構造は、ソース電極及びドレイン電極をインクジェット法により形成する点である。そのため、その他の作製方法については実施の形態3等を参照すればよく、詳細な説明は省略する。
(Embodiment 4)
In this embodiment, a method for manufacturing a thin film transistor having a structure different from that in Embodiment 3 will be described. A structure different from that in Embodiment 3 is that a source electrode and a drain electrode are formed by an inkjet method. Therefore, for other manufacturing methods, Embodiment Mode 3 and the like may be referred to, and detailed description thereof is omitted.
図4(A)に示すように、絶縁表面を有する基板100上に下地膜101を形成する。そして下地膜101に対してプラズマ処理を行う。このプラズマ処理を行う結果、アルコールや油等の液体に対して濡れ性の低い撥液性となるように表面改質が行われる。
As shown in FIG. 4A, a
図4(B)に示すように、インクジェット法によりソース電極及びドレイン電極を形成する。本実施の形態では、テトラデカンの溶媒中に銀(Ag)の導電体が分散しているドットを滴下する。プラズマ処理を行う結果、インクジェット法により形成されたソース電極及びドレイン電極を微細化することができる。その後、ドットの溶媒を除去する必要があるとき、焼成したり、乾燥させるため加熱処理を施す。 As shown in FIG. 4B, a source electrode and a drain electrode are formed by an inkjet method. In this embodiment, a dot in which a silver (Ag) conductor is dispersed in a tetradecane solvent is dropped. As a result of performing the plasma treatment, the source electrode and the drain electrode formed by an inkjet method can be miniaturized. Then, when it is necessary to remove the solvent of a dot, it heat-processes in order to bake or to dry.
図4(C)に示すように、ソース電極及びドレイン電極を覆うように一導電型を有する半導体膜を形成する。本実施の形態では、一導電型を有する半導体膜としてN型を有する半導体膜106を用いる。またソース電極及びドレイン電極を覆うN型を有する半導体膜を短絡防止のためエッチングする。例えば、マスクを用いてドライエッチング法によりソース電極及びドレイン電極間のN型を有する半導体膜をエッチングする。
As shown in FIG. 4C, a semiconductor film having one conductivity type is formed so as to cover the source electrode and the drain electrode. In this embodiment mode, an N-
図4(D)に示すように、N型を有する半導体膜を覆って半導体膜105を形成する。次いで、マスクを用いて半導体膜105をパターニングする。このとき同時に、N型を有する半導体膜をパターニングされることがある。すなわち、半導体膜105とN型を有する半導体膜106とが同一ガスに対して同様のエッチレートを有する場合、同時にパターニングされてしまう。マスクは、インクジェット法又はフォトリソグラフィー法により形成することができる。図示しないが、本実施の形態ではマスクとしてインクジェット法を用いてポリイミド又はポリビニルアルコール等を滴下する。必要に応じて加熱を行い焼成し、ドライエッチング法を用いてパターニングすればよい。なおこのとき、半導体膜105に対してプラズマ処理を行ってもよい。その結果、インクジェット法により形成されたマスクを微細化することができる。
As illustrated in FIG. 4D, a
パターニング後、マスクを除去するため、プラズマ処理を行う。なお、インクジェット法を用いて形成されるマスクは除去せずに絶縁膜として機能させてもよい。 After the patterning, plasma treatment is performed to remove the mask. Note that a mask formed by an inkjet method may be functioned as an insulating film without being removed.
その後半導体膜を覆うようにゲート絶縁膜104として機能する絶縁膜を形成する。そしてゲート絶縁膜104に対してプラズマ処理を行う。このプラズマ処理を行う結果、アルコールや油等の液体に対して濡れ性の低い撥液性となるように表面改質が行われる。
After that, an insulating film functioning as the
図4(E)に示すように、ゲート絶縁膜を介して半導体膜上にゲート電極103として機能する導電膜を形成する。本実施の形態では、テトラデカンの溶媒中に銀(Ag)の導電体が分散しているドットを滴下する。プラズマ処理を行う結果、インクジェット法により形成されたゲート電極を微細化することができる。その後、ドットの溶媒を除去する必要があるとき、焼成したり、乾燥させるため加熱処理を施す。
As shown in FIG. 4E, a conductive film functioning as the
このようにゲート電極まで形成された半導体素子として機能する薄膜トランジスタが完成する。このような薄膜トランジスタが複数設けられた基板をTFT基板と表記する。 Thus, a thin film transistor functioning as a semiconductor element formed up to the gate electrode is completed. A substrate provided with a plurality of such thin film transistors is referred to as a TFT substrate.
次いで、少なくともゲート電極を覆って保護膜113を形成すると好ましい。保護膜は積層構造又は単層構造を有することができる。保護膜として、プラズマCVD法により酸化珪素、窒化珪素又は窒化酸化珪素等の絶縁体を形成することができる。なおインクジェット法により絶縁膜の材料が混入されたドットを吐出して保護膜を形成してもよい。本実施の形態のように、銀(Ag)をゲート電極として用いる場合、ゲート電極を覆う保護膜には窒化珪素膜を用いると好ましい。酸素を有する保護膜を用いると、銀(Ag)と反応し、酸化銀が形成されゲート電極表面が荒れる恐れがあるからである。
Next, it is preferable to form the
本実施の形態の薄膜トランジスタは、半導体膜より上方にゲート電極が設けられる、所謂トップゲート型の薄膜トランジスタである。 The thin film transistor of this embodiment is a so-called top gate thin film transistor in which a gate electrode is provided above a semiconductor film.
またこのようにして形成される薄膜トランジスタは、インクジェット法により導電膜を形成する前に、プラズマ処理を行うことを特徴とする。本実施の形態では、インクジェット法によりソース電極、ドレイン電極、及びゲート電極を形成する前にプラズマ処理を行っているが、少なくとも1つのインクジェット工程前においてプラズマ処理を行えばよい。そのため、本実施の形態で示した以外であってもインクジェット工程の前であればいつプラズマ処理を行ってもよい。 The thin film transistor thus formed is characterized in that plasma treatment is performed before the conductive film is formed by an inkjet method. In this embodiment mode, plasma treatment is performed before the source electrode, the drain electrode, and the gate electrode are formed by an inkjet method; however, plasma treatment may be performed before at least one inkjet step. Therefore, plasma treatment may be performed at any time before the inkjet process even if it is not shown in this embodiment mode.
以上のように、インクジェット工程前のプラズマ処理により、微細化されたソース電極、ドレイン電極、及びゲート電極を有する薄膜トランジスタを得ることができる。 As described above, a thin film transistor having a miniaturized source electrode, drain electrode, and gate electrode can be obtained by plasma treatment before an inkjet process.
またインクジェット法により配線やマスク等を形成すると、材料の利用効率が向上し、コストの削減、廃液処理量の削減が可能となる。特にインクジェット法によりマスクを形成すると、フォトリソグラフィー工程と比較して工程の簡略化を行うことができる。その結果、設備投資コストの削減、コストの削減、製造時間を短縮することができる。 In addition, when a wiring, a mask, or the like is formed by the ink jet method, the material utilization efficiency is improved, and the cost can be reduced and the amount of waste liquid can be reduced. In particular, when a mask is formed by an inkjet method, the process can be simplified as compared with a photolithography process. As a result, it is possible to reduce capital investment cost, cost reduction, and manufacturing time.
(実施の形態5)
本実施の形態では、結晶性半導体膜を用いた薄膜トランジスタを形成する場合について説明する。
(Embodiment 5)
In this embodiment, the case where a thin film transistor using a crystalline semiconductor film is formed is described.
図18(A)に示すように、絶縁表面を有する基板100上に下地膜101を形成する。下地膜101は積層構造を有してもよく、本実施の形態ではプラズマCVD法を用いて、第1の下地膜101aとして、プラズマCVD法を用い、原料ガスにSiH4、N2O、NH3、H2、圧力が0.3Torr(39.9Pa)、RFパワーが50W、RF周波数が60MHz、基板温度が400℃として形成する酸化窒化珪素膜を10〜200nm(好ましくは50〜200nm)、第2の下地膜101bとして、プラズマCVD法を用い、原料ガスにSiH4、N2O、圧力が0.3Torr(39.9Pa)、RFパワーが150W、RF周波数が60MHz、基板温度が400℃として形成する酸化窒化珪素膜を50〜200nm(好ましくは200〜150nm)の順に積層する。
As shown in FIG. 18A, a
下地膜101上に非晶質半導体膜を形成する。非晶質半導体膜の膜厚は25〜100nm(好ましくは30〜60nm)とする。また非晶質半導体は珪素だけではなくシリコンゲルマニウムも用いることができ、シリコンゲルマニウムを用いる場合、ゲルマニウムの濃度は0.01〜4.5atomic%程度であることが好ましい。本実施の形態では66nmの珪素を主成分とする半導体膜(非晶質珪素膜、アモルファスシリコンとも表記する)を用いる。
An amorphous semiconductor film is formed over the
次いで非晶質半導体膜を結晶化し、結晶性半導体膜を形成する。結晶化する手段は、非晶質半導体膜の結晶化を促進する金属元素を添加し、加熱する方法を用いることができる。金属元素としてはNi、Fe、Co、Pd、Pt、Cu、Au、Ag、In、Snから選ばれた一種又は複数種を用いることができる。金属元素を形成することにより、低温で結晶化できるため好ましい。但し、金属元素を除去する工程、所謂ゲッタリング工程が必要となる。 Next, the amorphous semiconductor film is crystallized to form a crystalline semiconductor film. As a means for crystallization, a method of heating by adding a metal element that promotes crystallization of an amorphous semiconductor film can be used. As the metal element, one or more selected from Ni, Fe, Co, Pd, Pt, Cu, Au, Ag, In, and Sn can be used. Forming a metal element is preferable because it can be crystallized at a low temperature. However, a step of removing the metal element, that is, a so-called gettering step is required.
また非晶質半導体膜に、レーザ光を照射すればよい。連続発振型のレーザ(CWレーザ)やパルス発振型のレーザ(パルスレーザ)を用いることができる。レーザとして、Arレーザ、Krレーザ、エキシマレーザ、YAGレーザ、Y2O3レーザ、YVO4レーザ、YLFレーザ、YalO3レーザ、ガラスレーザ、ルビーレーザ、アレキサンドライドレーザ、Ti:サファイヤレーザ、銅蒸気レーザ又は金蒸気レーザのうち一種又は複数種を用いることができる。 In addition, the amorphous semiconductor film may be irradiated with laser light. A continuous wave laser (CW laser) or a pulsed laser (pulse laser) can be used. Lasers include Ar laser, Kr laser, excimer laser, YAG laser, Y 2 O 3 laser, YVO 4 laser, YLF laser, YalO 3 laser, glass laser, ruby laser, alexandride laser, Ti: sapphire laser, copper vapor laser Alternatively, one or a plurality of gold vapor lasers can be used.
例えば、非晶質半導体膜上にスピンコーティング法やディップ法といった塗布法、又はインクジェット法によりNi溶液(水溶液や酢酸溶液を含む)を塗布する。このとき非晶質半導体膜の表面の濡れ性を改善し、非晶質半導体膜の表面全体に溶液を行き渡らせるため、酸素雰囲気中でのUV光の照射、熱酸化法、ヒドロキシラジカルを含むオゾン水又は過酸化水素による処理等により、酸化膜を1〜5nmに成膜することが望ましい。また、イオン注入法によりNiイオンを非晶質半導体膜中に注入したり、Niを含有する水蒸気雰囲気中で加熱したり、ターゲットをNi材料としてArプラズマでスパッタリングしてもよい。本実施の形態では、Ni酢酸塩10ppmを含有した水溶液をスピンコーティング法により塗布する。 For example, a Ni solution (including an aqueous solution and an acetic acid solution) is applied to the amorphous semiconductor film by a coating method such as a spin coating method or a dip method, or an inkjet method. At this time, in order to improve the wettability of the surface of the amorphous semiconductor film and spread the solution over the entire surface of the amorphous semiconductor film, irradiation with UV light in an oxygen atmosphere, thermal oxidation method, ozone containing hydroxy radicals It is desirable to form an oxide film with a thickness of 1 to 5 nm by treatment with water or hydrogen peroxide. Alternatively, Ni ions may be implanted into the amorphous semiconductor film by an ion implantation method, heated in a water vapor atmosphere containing Ni, or sputtered with Ar plasma using a target as a Ni material. In this embodiment, an aqueous solution containing 10 ppm of Ni acetate is applied by a spin coating method.
その後、非晶質半導体を500〜550℃で2〜20時間かけて熱処理を行い、非晶質半導体膜を結晶化し結晶性半導体膜を形成する。このとき加熱温度を徐々に変化させると好ましい。最初の低温加熱工程により、非晶質半導体膜の水素等が出てくるため、結晶化の際の膜荒れを低減する、いわゆる水素出しを行うことができるからである。また磁場をかけて、その磁気エネルギーと合わせて結晶化させてもよいし、高出力マイクロ波を使用しても構わない。本実施の形態では、縦型炉を用いて500℃で1時間熱処理後、550℃4時間で熱処理を行う。 Thereafter, the amorphous semiconductor is heat-treated at 500 to 550 ° C. for 2 to 20 hours to crystallize the amorphous semiconductor film and form a crystalline semiconductor film. At this time, it is preferable to gradually change the heating temperature. This is because hydrogen or the like of the amorphous semiconductor film comes out in the first low-temperature heating step, so that so-called hydrogen extraction can be performed to reduce film roughness during crystallization. Alternatively, a magnetic field may be applied to crystallize the magnetic energy and high-power microwaves may be used. In this embodiment, heat treatment is performed at 550 ° C. for 4 hours after heat treatment at 500 ° C. for 1 hour using a vertical furnace.
そして結晶性半導体膜をパターニングして、島状の半導体膜502を形成する。
Then, the crystalline semiconductor film is patterned to form an island-shaped
島状の半導体膜502を覆うようにゲート絶縁膜104として機能する絶縁膜を形成する。ゲート絶縁膜には、上述した絶縁膜を用いることができる。実施の形態では、ゲート絶縁膜にTiO2を用いる。
An insulating film functioning as the
図18(B)に示すように、ゲート電極の被形成面に対してプラズマ処理を行う。本実施の形態では、ゲート電極の被形成面であるゲート絶縁膜に対してプラズマ処理を行う。プラズマ処理は、ゲート電極の被形成面に対して非接触で行うとよい。このプラズマ処理を行う結果、水、アルコールや油等の液体に対して濡れ性の低い撥液性となるように表面改質が行われる。すなわち、プラズマ処理により撥液性領域が形成される。 As shown in FIG. 18B, plasma treatment is performed on the formation surface of the gate electrode. In this embodiment mode, plasma treatment is performed on a gate insulating film which is a formation surface of a gate electrode. The plasma treatment may be performed in a non-contact manner with respect to the formation surface of the gate electrode. As a result of this plasma treatment, surface modification is performed so that the liquid repellency is low in wettability with respect to liquids such as water, alcohol and oil. That is, a liquid repellent region is formed by plasma treatment.
図18(C)に示すように、インクジェット法を用いて、溶媒中に導電体が混入したドットを滴下して、ゲート電極103として機能する導電膜を形成する。本実施の形態では、テトラデカンの溶媒中に銀(Ag)の導電体が分散しているドットを滴下する。プラズマ照射領域にドットを滴下するため、インクジェット法により形成されたゲート電極を微細化することができる。
As shown in FIG. 18C, a dot in which a conductor is mixed in a solvent is dropped by an inkjet method, so that a conductive film functioning as the
その後、ドットの溶媒を除去する必要があるとき、焼成したり、乾燥させるため加熱処理を施す。具体的には、所定の温度、例えば、200℃〜300℃で加熱すればよく、好ましくは酸素を有する雰囲気で加熱処理を行う。このときゲート電極表面に凹凸が生じないように加熱温度を設定する。本実施の形態のように銀(Ag)を有するドットを用いる場合、酸素及び窒素を有する雰囲気で加熱処理を行うと、溶媒中に含まれる接着剤等の熱硬化性樹脂などの有機物が分解されるため、有機物を含まない銀(Ag)を得ることができる。その結果、ゲート電極表面の平坦性を高め、比抵抗値を低くすることができる。 Then, when it is necessary to remove the solvent of a dot, it heat-processes in order to bake or to dry. Specifically, heating may be performed at a predetermined temperature, for example, 200 ° C. to 300 ° C., and heat treatment is preferably performed in an atmosphere containing oxygen. At this time, the heating temperature is set so that the gate electrode surface is not uneven. When using a dot containing silver (Ag) as in this embodiment, if heat treatment is performed in an atmosphere containing oxygen and nitrogen, organic substances such as a thermosetting resin such as an adhesive contained in the solvent are decomposed. Therefore, silver (Ag) which does not contain organic substances can be obtained. As a result, the flatness of the gate electrode surface can be improved and the specific resistance value can be lowered.
またゲート電極は、銀(Ag)以外にタンタル、タングステン、チタン、モリブデン、アルミニウム、銅から選ばれた元素、または前記元素を主成分とする合金材料もしくは化合物材料から形成することもできる。また導電膜は、インクジェット法以外に、スパッタリング法、プラズマCVD法により形成することができる。スパッタリング法、プラズマCVD法により形成する導電膜として、リン等の不純物元素をドーピングした多結晶シリコン膜に代表される半導体膜や、AgPdCu合金を用いることができる。 In addition to silver (Ag), the gate electrode can be formed of an element selected from tantalum, tungsten, titanium, molybdenum, aluminum, and copper, or an alloy material or compound material containing the element as a main component. The conductive film can be formed by a sputtering method or a plasma CVD method in addition to the ink jet method. As a conductive film formed by a sputtering method or a plasma CVD method, a semiconductor film typified by a polycrystalline silicon film doped with an impurity element such as phosphorus, or an AgPdCu alloy can be used.
その後、ゲート電極103を用いて、自己整合的に不純物元素を添加する。例えば、Nチャネル型の薄膜トランジスタとなる半導体膜にはリン(P)を添加し、pチャネル型の薄膜トランジスタとなる半導体膜にはボロン(B)を添加する。
After that, an impurity element is added in a self-aligning manner using the
以上のように、不純物領域まで形成された薄膜トランジスタが完成する。本実施の形態の薄膜トランジスタは、結晶性半導体膜を有する結晶性薄膜トランジスタであり、半導体膜より上方にゲート電極が設けられる、所謂トップゲート型の薄膜トランジスタである。このような薄膜トランジスタが複数設けられた基板をTFT基板と表記する。 As described above, the thin film transistor formed up to the impurity region is completed. The thin film transistor of this embodiment is a crystalline thin film transistor including a crystalline semiconductor film, and is a so-called top gate thin film transistor in which a gate electrode is provided above the semiconductor film. A substrate provided with a plurality of such thin film transistors is referred to as a TFT substrate.
その後、図18(D)に示すように、ゲート電極103を覆って、窒素を有する絶縁膜507を形成する。本実施の形態において、絶縁膜507はインクジェット法により形成することもできる。その後、絶縁膜507を設けた状態で加熱することにより、半導体膜のダングリングボンドを低減することができる。
After that, as illustrated in FIG. 18D, an insulating
またこのようにして形成される薄膜トランジスタは、インクジェット法により導電膜を形成する前に、プラズマ処理を行うことを特徴とする。本実施の形態では、インクジェット法によりソース電極、ドレイン電極、及びゲート電極を形成する前にプラズマ処理を行っているが、少なくとも1つのインクジェット工程前においてプラズマ処理を行えばよい。そのため、本実施の形態で示した以外であってもインクジェット工程の前であればいつプラズマ処理を行ってもよい。 The thin film transistor thus formed is characterized in that plasma treatment is performed before the conductive film is formed by an inkjet method. In this embodiment mode, plasma treatment is performed before the source electrode, the drain electrode, and the gate electrode are formed by an inkjet method; however, plasma treatment may be performed before at least one inkjet step. Therefore, plasma treatment may be performed at any time before the inkjet process even if it is not shown in this embodiment mode.
以上のように、インクジェット工程前のプラズマ処理により、微細化されたソース電極、ドレイン電極、及びゲート電極を有する薄膜トランジスタを得ることができる。更に、ドットが多少ずれて吐出された場合であっても、親液性領域に配線を形成することができ、配線形成の正確な位置制御が可能となる。 As described above, a thin film transistor having a miniaturized source electrode, drain electrode, and gate electrode can be obtained by plasma treatment before an inkjet process. Furthermore, even when the dots are ejected with a slight shift, wiring can be formed in the lyophilic region, and accurate position control of wiring formation is possible.
またインクジェット法により配線やマスク等を形成すると、材料の利用効率が向上し、コストの削減、廃液処理量の削減が可能となる。特にインクジェット法によりマスクを形成すると、フォトリソグラフィー工程と比較して工程の簡略化を行うことができる。その結果、設備投資コストの削減、コストの削減、製造時間を短縮することができる。 In addition, when a wiring, a mask, or the like is formed by the ink jet method, the material utilization efficiency is improved, and the cost can be reduced and the amount of waste liquid can be reduced. In particular, when a mask is formed by an inkjet method, the process can be simplified as compared with a photolithography process. As a result, it is possible to reduce capital investment cost, cost reduction, and manufacturing time.
(実施の形態6)
本実施の形態では、プラズマ処理を行う装置について説明する。
(Embodiment 6)
In this embodiment, an apparatus for performing plasma treatment is described.
図15(A)に示すように、処理室401内に、電極403、電極表面を覆うようにに形成された誘電体404、電極に接続される電源402、プラズマ処理を行う面(被処理面)を有する基板406、基板を固定するためのステージ407、が設けられている。本実施の形態では誘電体としてテフロン(登録商標)を用いる。
As shown in FIG. 15A, an
なお本実施の形態において、誘電体は電極表面を覆うように形成されているが、誘電体は、少なくとも被処理物と電極との間に発生するプラズマに曝されるように設ければよい。例えば、誘電体を被処理物と電極との間に設ければよい。 Note that in this embodiment mode, the dielectric is formed so as to cover the electrode surface; however, the dielectric may be provided so as to be exposed to plasma generated at least between the object to be processed and the electrode. For example, a dielectric may be provided between the object to be processed and the electrode.
プラズマ処理を行う被処理面を有する基板をステージ配置し、電源からパルス電圧を印加する。すると、電極及び基板間にプラズマが生成される。そのプラズマのプラズマ密度は1×1010〜1×1014m-3である。このとき処理室内の圧力は数十Torr〜800Torr(106400Pa)、好ましくは700Torr(93100Pa)〜800Torr(大気圧又は大気圧近傍の圧力)で、パルス電圧を使って放電させる。本実施の形態では大気圧又は大気圧近傍の圧力で安定なプラズマを生成するため、パルス電圧を印加している。このプラズマ処理における、処理ガスは空気、酸素又は窒素を用いる。 A substrate having a surface to be processed for plasma processing is placed on a stage, and a pulse voltage is applied from a power source. Then, plasma is generated between the electrode and the substrate. The plasma density of the plasma is 1 × 10 10 to 1 × 10 14 m −3 . At this time, the pressure in the processing chamber is several tens Torr to 800 Torr (106400 Pa), preferably 700 Torr (93100 Pa) to 800 Torr (atmospheric pressure or pressure near atmospheric pressure), and discharge is performed using a pulse voltage. In this embodiment mode, a pulse voltage is applied in order to generate stable plasma at atmospheric pressure or a pressure near atmospheric pressure. Air, oxygen, or nitrogen is used as a processing gas in this plasma processing.
具体的には、印加する電圧を減衰振動波が間欠的に繰り返し生ずる減衰振動波形周期波として各減衰振動波のように共振させる。正負一対のパルスを繰り返し周波数で高圧トランスの一次側に供給し、高圧トランスの二次側から各減衰振動波に共振した減衰振動波形周期波を出力して一対の電極に印加する。このとき共振した各減衰振動波の電圧立ち上がり時間は5μs以下であると好ましい。また減衰振動波の繰り返し周期が10〜100kHzであると好ましい。またパルスは100〜10000pps(1秒当たり10000回)であると好ましい。 Specifically, the applied voltage is resonated like a damped vibration wave as a damped vibration waveform periodic wave in which the damped vibration wave is intermittently repeated. A pair of positive and negative pulses is supplied to the primary side of the high-voltage transformer at a repetition frequency, and a damped oscillation waveform periodic wave resonated with each damped oscillation wave is output from the secondary side of the high-voltage transformer and applied to the pair of electrodes. At this time, the voltage rise time of each damped oscillation wave resonated is preferably 5 μs or less. Moreover, it is preferable that the repetition period of the damped vibration wave is 10 to 100 kHz. The pulse is preferably 100 to 10,000 pps (10,000 times per second).
プラズマ処理を行う結果、導電膜の被形成面の表面が改質される。具体的には、電極表面にテフロン(登録商標)が付着しいている場合、導電膜の被形成面にCF2結合が形成される。具体的なプラズマ処理前後におけるCF2結合状態の変化は実施例で示す。その結果、被処理面は撥液性を示す。その後、配線等を形成すると、線幅が小さくなり微細化を達成することができる。 As a result of performing the plasma treatment, the surface of the conductive film is modified. Specifically, when Teflon (registered trademark) is attached to the electrode surface, a CF 2 bond is formed on the formation surface of the conductive film. Specific changes in the CF 2 bonding state before and after the plasma treatment are shown in the examples. As a result, the surface to be treated exhibits liquid repellency. After that, when a wiring or the like is formed, the line width is reduced and miniaturization can be achieved.
このように好ましくは大気圧又は大気圧近傍でプラズマ処理を行う場合、真空引きを行うことなく、簡便にプラズマ処理を行うことができる。その結果、薄膜トランジスタの作製時間を大幅に短縮することができる。もちろんプラズマ処理は真空中で行ってもよい。 Thus, preferably, when the plasma treatment is performed at or near atmospheric pressure, the plasma treatment can be easily performed without evacuation. As a result, the manufacturing time of the thin film transistor can be significantly shortened. Of course, the plasma treatment may be performed in a vacuum.
またプラズマ処理を行う処理室と、インクジェット工程を行う処理室とを、密接して設け、所謂マルチチャンバーを形成してもよい。特に、プラズマ処理とインクジェット工程とを真空中で行う場合、大気開放せずに被処理面を有する基板を搬送することができるため、マルチチャンバーとすると好適である。 In addition, a processing chamber for performing plasma treatment and a processing chamber for performing an ink jet process may be provided in close contact to form a so-called multi-chamber. In particular, when the plasma treatment and the inkjet process are performed in a vacuum, it is preferable to use a multi-chamber because a substrate having a surface to be processed can be transported without opening to the atmosphere.
また大気圧又は大気圧近傍でプラズマ処理を行うことができるため、図15(B)に示すように処理室内で行わなくともよい。 In addition, since plasma treatment can be performed at or near atmospheric pressure, the treatment may not be performed in the treatment chamber as illustrated in FIG.
図15(B)には、X軸用の一軸ロボット410、Y軸用の一軸ロボット411が設けられ、いずれか一方のロボット上にステージ407が設けられている。ステージ上には被処理面を有する基板406が配置されている。電極403は円柱状を有し、周りを誘電体404が覆っている。本実施の形態では誘電体としてテフロン(登録商標)を用いる。その他のプラズマ条件等は上述したとおりであるため説明を省略する。
In FIG. 15B, a single-
そしてプラズマ処理を行う場合、相対的に電極と基板とを移動させる。また基板が電極に対して大きい場合、矩形状に移動しながら相対的に電極と基板とを移動させればよい。また基板を回転させ、相対的に電極と基板とを移動させてもよい。このように移動させる場合、アライメントマーカ等を目印とし、CCDカメラ等を用いて位置制御するとよい。 When performing plasma treatment, the electrode and the substrate are relatively moved. When the substrate is larger than the electrode, the electrode and the substrate may be moved relatively while moving in a rectangular shape. Alternatively, the substrate may be rotated to relatively move the electrode and the substrate. When moving in this way, the position may be controlled using a CCD camera or the like using an alignment marker or the like as a mark.
このように大気中でプラズマ処理を行うため、真空引きを行うことなく、簡便にプラズマ処理を行うことができる。その結果、薄膜トランジスタの作製時間を大幅に短縮することができる。もちろんプラズマ処理は真空中で行うことができる。 Since the plasma treatment is performed in the air as described above, the plasma treatment can be easily performed without evacuation. As a result, the manufacturing time of the thin film transistor can be significantly shortened. Of course, the plasma treatment can be performed in a vacuum.
(実施の形態7)
本実施の形態では、撥液処理として、プラズマ処理ではなくフッ素を有する膜を形成する場合について説明する。そのため、その他の作製方法については上記実施の形態を参照すればよい。
(Embodiment 7)
In this embodiment, the case where a film containing fluorine is formed instead of plasma treatment as the liquid repellent treatment will be described. Therefore, the above embodiment mode may be referred to for other manufacturing methods.
図14(A)に示すように、絶縁表面を有する基板100上に下地膜101を形成する。その後、フッ素を有する膜、例えばテフロン(登録商標)膜128を形成する。テフロン(登録商標)膜は、単分子層レベルの厚さ、つまり膜厚が5nm以下で形成すればよい。テフロン(登録商標)膜はスパッタリング法、CVD法等により形成することができる。本実施の形態では、フッ素を有する膜としてテフロン(登録商標)膜を用いて説明するが、シランカップリング剤等をスピンコーティング法により形成してもよい。
As shown in FIG. 14A, a
シランカップリング剤は上記以外に、気相法や浸漬法により形成することができる。気相法の場合、アルミニウム等からなるトレイ上に基板をのせ、基板周辺にFAS材料を滴下する。その後、加熱する。例えばホットプレートを用いて100〜150℃で10分加熱する。このとき、ホットプレートにフタをしておくとよい。次いで基板を取り出し、アセトン洗浄、水洗を行い、乾燥させる。
また浸漬法の場合、FAS材料が入った容器に基板を5〜10分間漬ける。このとき、60℃程度に加熱を施してもよい。次いでアセトン洗浄、水洗を行う。その後基板を乾燥させる。乾燥により、単分子が配向する傾向にある。
このような方法により、シランカップリング剤を有する膜を形成すると、スピンコーティング法よりも均一な膜を形成することができる。
In addition to the above, the silane coupling agent can be formed by a vapor phase method or an immersion method. In the case of the vapor phase method, the substrate is placed on a tray made of aluminum or the like, and the FAS material is dropped around the substrate. Then, it heats. For example, it heats at 100-150 degreeC for 10 minutes using a hotplate. At this time, it is preferable to cover the hot plate. Next, the substrate is taken out, washed with acetone, washed with water, and dried.
In the case of the immersion method, the substrate is immersed in a container containing the FAS material for 5 to 10 minutes. At this time, you may heat at about 60 degreeC. Next, acetone washing and water washing are performed. Thereafter, the substrate is dried. By drying, the single molecules tend to be oriented.
When a film having a silane coupling agent is formed by such a method, a film that is more uniform than the spin coating method can be formed.
図14(B)に示すように、テフロン(登録商標)膜上にゲート電極103として機能する導電膜を形成する。ゲート電極は、インクジェット法を用いて、溶媒中に導電体が混入したドットを滴下して形成することができる。本実施の形態では、テトラデカンの溶媒中に銀(Ag)の導電体が分散しているドットを滴下する。テフロン(登録商標)膜を形成する結果、インクジェット法により形成されたゲート電極を微細化することができる。
As shown in FIG. 14B, a conductive film functioning as the
その後、ドットの溶媒を除去する必要があるとき、焼成したり、乾燥させるため加熱処理を施す。この加熱処理により、単分子層レベルの厚さに形成されるテフロン(登録商標)膜は、消去される。 Then, when it is necessary to remove the solvent of a dot, it heat-processes in order to bake or to dry. By this heat treatment, the Teflon (registered trademark) film formed to a thickness of a monomolecular layer is erased.
図14(C)に示すように、ゲート絶縁膜104、半導体膜105、N型を有する半導体膜106を順に形成し、所望の形状にパターニングする。その後、ソース電極及びドレイン電極108として機能する導電膜を形成する。ソース電極及びドレイン電極を形成する前にテフロン(登録商標)膜を形成してもよい。
As shown in FIG. 14C, a
本実施の形態では、実施の形態1に示すチャネルエッチ型の薄膜トランジスタを用いて説明したが、薄膜トランジスタの構成には限定されない。すなわち上記実施の形態のいずれに記載の薄膜トランジスタの作製方法において、撥液性を有するためにテフロン(登録商標)膜を形成してもよい。 In this embodiment mode, the channel-etched thin film transistor described in Embodiment Mode 1 is described; however, the structure of the thin film transistor is not limited. That is, in the method for manufacturing a thin film transistor described in any of the above embodiments, a Teflon (registered trademark) film may be formed in order to have liquid repellency.
以上のように、ソース電極及びドレイン電極まで設けられた薄膜トランジスタが完成する。このような薄膜トランジスタが複数設けられた基板をTFT基板と表記する。 As described above, the thin film transistor provided with the source electrode and the drain electrode is completed. A substrate provided with a plurality of such thin film transistors is referred to as a TFT substrate.
またこのようにして形成される薄膜トランジスタは、インクジェット法により導電膜を形成する前に、テフロン(登録商標)膜を形成することを特徴とする。本実施の形態では、インクジェット法によりゲート電極を形成する前にテフロン(登録商標)膜を形成しているが、少なくとも1つのインクジェット工程前においてテフロン(登録商標)膜を形成すればよい。そのため、本実施の形態で示した以外であっても、インクジェット工程の前であればいつテフロン(登録商標)膜形成を施してもよい。また、インクジェット法を用いる前に、テフロン(登録商標)膜を形成する工程以外に、上述したプラズマ処理を行ってもよい。 In addition, the thin film transistor thus formed is characterized in that a Teflon (registered trademark) film is formed before the conductive film is formed by an inkjet method. In this embodiment mode, the Teflon (registered trademark) film is formed before the gate electrode is formed by the inkjet method. However, the Teflon (registered trademark) film may be formed before at least one inkjet process. Therefore, a Teflon (registered trademark) film may be formed at any time before the ink jet process even if it is not shown in the present embodiment. In addition to the step of forming a Teflon (registered trademark) film, the above-described plasma treatment may be performed before using the inkjet method.
以上のように、インクジェット工程前のテフロン(登録商標)膜形成により、微細化されたゲート電極や、ソース電極及びドレイン電極を有する薄膜トランジスタを得ることができる。 As described above, a thin film transistor having a miniaturized gate electrode, a source electrode, and a drain electrode can be obtained by forming a Teflon (registered trademark) film before the inkjet process.
またインクジェット法により配線やマスク等を形成すると、材料の利用効率が向上し、コストの削減、廃液処理量の削減が可能となる。特にインクジェット法によりマスクを形成すると、フォトリソグラフィー工程と比較して工程の簡略化を行うことができる。その結果、設備投資コストの削減、コストの削減、製造時間を短縮することができる。 In addition, when a wiring, a mask, or the like is formed by the ink jet method, the material utilization efficiency is improved, and the cost can be reduced and the amount of waste liquid can be reduced. In particular, when a mask is formed by an inkjet method, the process can be simplified as compared with a photolithography process. As a result, it is possible to reduce capital investment cost, cost reduction, and manufacturing time.
(実施の形態8)
本実施の形態では、薄膜トランジスタを覆うように設けられる層間絶縁膜と、層間絶縁膜に設けられる開口部に形成される配線について説明する。
(Embodiment 8)
In this embodiment, an interlayer insulating film provided so as to cover the thin film transistor and a wiring formed in an opening provided in the interlayer insulating film are described.
図5(A)に示すように、上記実施の形態に基づき絶縁表面を有する基板100上に保護膜113を有する薄膜トランジスタ(TFT)120を形成する。本実施の形態は、実施の形態1に記載のTFTを用いて説明するが、上記実施の形態に記載のいずれのTFTを用いても構わない。
As shown in FIG. 5A, a thin film transistor (TFT) 120 including a
そしてTFT120を覆うように層間絶縁膜121を形成する。その結果、平坦性を高めることができる。層間絶縁膜には、無機材料(酸化シリコン、窒化シリコン、酸化窒化シリコンなど)、感光性又は非感光性の有機材料(ポリイミド、アクリル、ポリアミド、ポリイミドアミド、レジスト又はベンゾシクロブテン)、シロキサン、ポリシラザン、及びそれらの積層構造を用いることができる。シロキサンとは、珪素(Si)と酸素(O)との結合で骨格構造が構成され、置換基に少なくとも水素を含む、又は置換基にフッ素、アルキル基、又は芳香族炭化水素のうち少なくとも1種を有するポリマー材料、を出発原料として形成される。またポリシラザンとは、珪素(Si)と窒素(N)の結合を有するポリマー材料を含む液体材料を出発原料として形成される。また有機材料として、ポジ型感光性有機樹脂及びネガ型感光性有機樹脂のいずれを用いてもよい。
Then, an
更に平坦性を高める場合、層間絶縁膜に対して、CMP等の研磨を行ってもよい。 In order to further improve the flatness, polishing such as CMP may be performed on the interlayer insulating film.
図5(B)に示すように、層間絶縁膜121の所望の位置に所望の形状の開口部122を形成する。本実施の形態では、ソース電極又はドレイン電極上の層間絶縁膜に、側面がテーパを有する開口部を形成する場合を説明する。
As shown in FIG. 5B, an
まず、層間絶縁膜121上にマスクを形成し、マスクを用いてエッチングにより開口部を形成する。マスクはインクジェット法又はフォトリソグラフィー法により形成することができる。特にインクジェット法によりマスクを形成すると、フォトリソグラフィー工程と比較して工程の簡略化を行うことができる。その結果、設備投資コストの削減、コストの削減、製造時間を短縮することができる。このとき、層間絶縁膜121に対してプラズマ処理を行ってもよい。その結果、インクジェット法により形成されたマスクを微細化することができる。
First, a mask is formed over the
または、インクジェット法により、エッチャントを含むドットを滴下して、層間絶縁膜に開口部を形成してもよい。インクジェット法により開口部を形成すると、エッチャンの利用効率が向上し、コストの削減、廃液処理量の削減が可能となるからである。そしてインクジェット法により開口部を形成すると、フォトリソグラフィー工程の簡略化を行うことができる。 Alternatively, an opening may be formed in the interlayer insulating film by dropping dots containing an etchant by an inkjet method. This is because when the opening is formed by the ink jet method, the use efficiency of the etchant is improved, and the cost and the amount of waste liquid can be reduced. When the opening is formed by an inkjet method, the photolithography process can be simplified.
そして開口部が形成された層間絶縁膜121に対して、プラズマ処理を行う。このプラズマ処理を行う結果、アルコールや油等の液体に対して濡れ性の低い撥液性となるように、層間絶縁膜及び開口部内(開口部側面を含む)の表面改質が行われる。
Then, plasma treatment is performed on the
図5(C)に示すように、開口部に配線123を形成する。配線123は、スパッタリング法やインクジェット法により形成することができる。本実施の形態では、テトラデカンの溶媒中に銀(Ag)の導電体が分散しているドットを滴下して配線を形成する。このとき、層間絶縁膜の表面及び開口部内(開口部側面を含む)は撥液性となっている。その結果、インクジェット法により形成された配線を微細化することができる。その後、ドットの溶媒を除去する必要があるとき、焼成したり、乾燥させるため加熱処理を施す。
As shown in FIG. 5C, a
次いで図6を用いて、プラズマ処理を行うタイミングが異なり、プラズマ処理を行った後、開口部を形成する場合を説明する。その他の構成は図5と同様であるため、詳細な説明は省略する。 Next, with reference to FIG. 6, a case where the timing of performing the plasma treatment is different and the opening is formed after the plasma treatment will be described. Since other configurations are the same as those in FIG. 5, detailed description is omitted.
図6(A)に示すように、上記実施の形態に基づき絶縁表面を有する基板100上に保護膜113を有する薄膜トランジスタ120を形成する。
As shown in FIG. 6A, a
そして図5と同様に、TFT120を覆うように層間絶縁膜121を形成する。その結果、平坦性を高めることができる。
Then, similarly to FIG. 5, an
そして、最初に層間絶縁膜121に対して、プラズマ処理を行う。このプラズマ処理を行う結果、アルコールや油等の液体に対して濡れ性の低い撥液性となるように、層間絶縁膜の表面改質が行われる。
First, plasma treatment is performed on the
図6(B)に示すように、層間絶縁膜121に所望の形状及び位置に開口部122を形成する。
As shown in FIG. 6B, an
まず、層間絶縁膜121上にマスクを形成し、マスクを用いてエッチングにより開口部を形成する。マスクはインクジェット法又はフォトリソグラフィー法により形成することができる。そしてインクジェット法により開口部を形成すると、フォトリソグラフィー工程の簡略化を行うことができる。このとき、層間絶縁膜121に対してプラズマ処理を行っているため、インクジェット法により形成されたマスクを微細化することができる。
First, a mask is formed over the
また図20(A)に示すように、インクジェット法により、エッチャントを含むドットを滴下して、層間絶縁膜に開口部を形成してもよい。インクジェット法により開口部を形成すると、エッチャンの利用効率が向上し、コストの削減、廃液処理量の削減が可能となるからである。そしてインクジェット法により開口部を形成すると、フォトリソグラフィー工程の簡略化を行うことができる。 Alternatively, as shown in FIG. 20A, an opening may be formed in the interlayer insulating film by dropping dots containing an etchant by an inkjet method. This is because when the opening is formed by the ink jet method, the use efficiency of the etchant is improved, and the cost and the amount of waste liquid can be reduced. When the opening is formed by an inkjet method, the photolithography process can be simplified.
図6(C)に示すように、開口部に配線123を形成する。配線123は、スパッタリング法やインクジェット法により形成することができる。本実施の形態では、テトラデカンの溶媒中に銀(Ag)の導電体が分散しているドットを滴下する。
As shown in FIG. 6C, a
このとき、層間絶縁膜121の表面は撥液性となっており、開口部内(開口部側面を含む)はプラズマ処理が施されていないため、表面よりも撥液性が低くなっている。すわなち、配線材料を有するドットは層間絶縁膜の表面において撥液性を示し、開口部内(開口部側面を含む)では層間絶縁膜の表面より親液性を示す。その結果、図5で示した状態よりも、配線材料を有するドットは開口部内に侵入しやすい状況になっている。更に、インクジェット法により層間絶縁膜の表面に形成された配線を微細化することができる。このように撥液性と親液性を制御することは、インクジェット法により配線を形成する場合に好適である。
At this time, the surface of the
その後、ドットの溶媒を除去する必要があるとき、焼成したり、乾燥させるため加熱処理を施す。 Then, when it is necessary to remove the solvent of a dot, it heat-processes in order to bake or to dry.
また図21(A)に示すように、インクジェット法により、層間絶縁膜の材料と、配線の材料とを滴下することにより配線123を形成してもよい。この場合図21(B)に示すように、平坦性を向上させるため、CMP等により層間絶縁膜や配線の表面を研磨するとよい。
In addition, as illustrated in FIG. 21A, the
このようにして形成される薄膜トランジスタは、インクジェット法により層間絶縁膜上に配線を形成する前に、プラズマ処理を行うことを特徴とする。本実施の形態では、開口部形成後又は前に、プラズマ処理を行っているが、開口部形成前後にプラズマ処理を行ってもよい。 The thin film transistor thus formed is characterized in that plasma treatment is performed before a wiring is formed over the interlayer insulating film by an inkjet method. In this embodiment mode, plasma treatment is performed after or before the opening is formed. However, plasma treatment may be performed before and after the opening is formed.
また層間絶縁膜に対してプラズマ処理を行うことにより、開口部に形成される配線及びその他の配線(例えば、信号線)をインクジェット法により形成する場合、微細化することができる。 Further, by performing plasma treatment on the interlayer insulating film, the wiring formed in the opening and other wirings (for example, signal lines) can be miniaturized when formed by an inkjet method.
以上のように、インクジェット工程前のプラズマ処理により、微細化された層間絶縁膜上に形成された配線を有する薄膜トランジスタを得ることができる。 As described above, a thin film transistor having a wiring formed over a miniaturized interlayer insulating film can be obtained by plasma treatment before the ink jet process.
(実施の形態9)
本実施の形態では、画素電極の形成方法について説明する。
(Embodiment 9)
In this embodiment mode, a method for forming a pixel electrode will be described.
図7(A)に示すように、上記実施の形態に基づき絶縁表面を有する基板100上に保護膜113を有する薄膜トランジスタ120を形成する。本実施の形態は、実施の形態1に記載のTFTを用いて説明するが、上記実施の形態に記載のいずれのTFTを用いても構わない。また、ソース電極及びドレイン電極と接続するように、該電極の下方に画素電極125を形成する場合を説明する。
As shown in FIG. 7A, a
まず、ゲート絶縁膜形成後、半導体膜及びN型を有する半導体膜をパターニングし、ソース電極又はドレイン電極を形成する領域に画素電極を形成する。画素電極は、スパッタリング法やインクジェット法により形成することができる。画素電極は透光性又は非透光性を有する材料から形成する。例えば、透光性を有する場合、ITO等を用いることができ、非透光性を有する場合、金属膜を用いることができる。具体的な画素電極の材料として、ITO、酸化インジウムに2〜20%の酸化亜鉛(ZnO)を混合したIZO、酸化インジウムに2〜20%の酸化珪素(SiO2)を混合したITSO、有機インジウム、有機スズ、窒化チタン(TiN)等を用いることもできる。 First, after forming the gate insulating film, the semiconductor film and the N-type semiconductor film are patterned to form a pixel electrode in a region where a source electrode or a drain electrode is to be formed. The pixel electrode can be formed by a sputtering method or an inkjet method. The pixel electrode is formed from a light-transmitting or non-light-transmitting material. For example, ITO or the like can be used when it has translucency, and a metal film can be used when it has non-translucency. As specific pixel electrode materials, ITO, IZO in which 2 to 20% zinc oxide (ZnO) is mixed in indium oxide, ITSO in which 2 to 20% silicon oxide (SiO 2 ) is mixed in indium oxide, organic indium Organic tin, titanium nitride (TiN), or the like can also be used.
特に、インクジェット法により画素電極を形成する場合、画素電極の被形成面である、ゲート絶縁膜に対してプラズマ処理を行ってもよい。このプラズマ処理を行う結果、アルコールや油等の液体に対して濡れ性の低い撥液性となるように表面改質が行われる。 In particular, when a pixel electrode is formed by an inkjet method, plasma treatment may be performed on a gate insulating film which is a surface where the pixel electrode is formed. As a result of this plasma treatment, surface modification is performed so that the liquid repellency is low in wettability with respect to liquids such as alcohol and oil.
図7(A)では、画素電極としてインクジェット法を用いてITOの導電体が分散しているドットを滴下する。プラズマ処理行う結果、インクジェット法により形成された画素電極を微細化することができる。その後、ドットの溶媒を除去する必要があるとき、焼成したり、乾燥させるため加熱処理を施す。 In FIG. 7A, a dot in which an ITO conductor is dispersed is dropped using an inkjet method as a pixel electrode. As a result of performing the plasma treatment, the pixel electrode formed by the inkjet method can be miniaturized. Then, when it is necessary to remove the solvent of a dot, it heat-processes in order to bake or to dry.
図7(B)には、図7(A)と異なり、ソース電極又はドレイン電極の上に画素電極を形成する場合を説明する。画素電極は、上記と同様にスパッタリング法やインクジェット法により形成することができる。特に、インクジェット法により画素電極を形成する場合、画素電極の被形成面である、ソース電極、ドレイン電極、及びにゲート絶縁膜に対してプラズマ処理を行ってもよい。このプラズマ処理を行う結果、アルコールや油等の液体に対して濡れ性の低い撥液性となるように表面改質が行われる。 FIG. 7B illustrates a case where a pixel electrode is formed over a source electrode or a drain electrode, unlike FIG. 7A. The pixel electrode can be formed by a sputtering method or an inkjet method in the same manner as described above. In particular, when a pixel electrode is formed by an inkjet method, plasma treatment may be performed on the source electrode, the drain electrode, and the gate insulating film, which are surfaces on which the pixel electrode is formed. As a result of this plasma treatment, surface modification is performed so that the liquid repellency is low in wettability with respect to liquids such as alcohol and oil.
図7(B)では、画素電極としてインクジェット法を用いてITOの導電体が分散しているドットを滴下する。プラズマ処理を行う結果、インクジェット法により形成された画素電極を微細化することができる。その後、ドットの溶媒を除去する必要があるとき、焼成したり、乾燥させるため加熱処理を施す。 In FIG. 7B, a dot in which an ITO conductor is dispersed is dropped using an inkjet method as a pixel electrode. As a result of performing the plasma treatment, the pixel electrode formed by the inkjet method can be miniaturized. Then, when it is necessary to remove the solvent of a dot, it heat-processes in order to bake or to dry.
図7(C)には、図7(A)(B)と異なり、層間絶縁膜121を形成して平坦化した後に、配線123を形成し、配線123と画素電極とを接続する。画素電極は、上記と同様にスパッタリング法やインクジェット法により形成することができる。特に、インクジェット法により画素電極を形成する場合、配線123を形成後、画素電極の被形成面である、層間絶縁膜に対してプラズマ処理を行ってもよい。このプラズマ処理を行う結果、アルコールや油等の液体に対して濡れ性の低い撥液性となるように表面改質が行われる。
In FIG. 7C, unlike FIGS. 7A and 7B, the
図7(C)では、画素電極としてITSOを用いる。ITSOは、インクジェット法を用いてITOの導電体と珪素が分散しているドットを滴下して形成することができる。または、珪素を有するITOのターゲットを用いたスパッタリング法により形成することができる。このとき、層間絶縁膜121としてシロキサンを用いるとよい。さらにシロキサンの層間絶縁膜上に窒素を有する絶縁膜126、例えば窒化珪素、又は酸化窒化珪素を形成するとよい。このような構成を有する発光素子を形成すると、発光輝度や寿命を向上することができる。また層間絶縁膜121にアクリルやポリイミドを用いる場合、窒素を有する絶縁膜126は省略することができる。このような構成を有する場合、液晶素子を形成するとよい。
In FIG. 7C, ITSO is used as the pixel electrode. ITSO can be formed by dropping an ITO conductive material and silicon dispersed dots using an inkjet method. Alternatively, it can be formed by a sputtering method using an ITO target containing silicon. At this time, siloxane is preferably used for the
インクジェット法により画素電極を形成する場合、プラズマ処理を行う結果、画素電極を微細化することができる。その後、ドットの溶媒を除去する必要があるとき、焼成したり、乾燥させるため加熱処理を施す。 When the pixel electrode is formed by an inkjet method, the pixel electrode can be miniaturized as a result of performing plasma treatment. Then, when it is necessary to remove the solvent of a dot, it heat-processes in order to bake or to dry.
このように、インクジェット法により画素電極を形成する場合、好ましくは画素電極の被形成面に対してプラズマ処理を行うことを特徴とする。 As described above, when a pixel electrode is formed by an inkjet method, it is preferable that plasma treatment is performed on a surface on which the pixel electrode is formed.
以上のように、インクジェット工程前のプラズマ処理により、微細化された画素電極を有する薄膜トランジスタを得ることができる。 As described above, a thin film transistor having a miniaturized pixel electrode can be obtained by plasma treatment before an ink jet process.
画素電極まで設けられた状態のTFT基板をモジュール用TFT基板と表記する。 The TFT substrate provided with up to the pixel electrode is referred to as a module TFT substrate.
(実施の形態10)
本実施の形態では、上記実施の形態で示した薄膜トランジスタを有する液晶モジュールを有する表示装置(液晶表示装置)について説明する。
(Embodiment 10)
In this embodiment, a display device (liquid crystal display device) including a liquid crystal module including the thin film transistor described in the above embodiment is described.
図8には、上記実施で示したようなTFT基板に形成された薄膜トランジスタ120と、画素電極125とを有する液晶表示装置の断面を示す。画素電極125に透光性を有する導電膜(例えば、ITOやITSO)を用いると透過型液晶表示装置となり、非透光性、つまり反射性の高い導電膜(例えアルミニウム)を用いると反射型液晶表示装置を形成することができる。本実施の形態のように液晶表示装置に用いられるモジュール用TFT基板を、液晶モジュール用TFT基板と表記する。
FIG. 8 shows a cross section of a liquid crystal display device having the
薄膜トランジスタ120、保護膜113、画素電極125を覆うように、配向膜131を形成する。
An
対向基板135には、カラーフィルター134、対向電極133、配向膜131を順に形成する。カラーフィルター、対向電極、又は配向膜はインクジェット法により形成することができる。図示していないが、ブラックマトリクスを形成してもよく、ブラックマトリクスもインクジェット法により形成することができる。
A
その後、基板100と対向基板135とを、シール材を用いて張り合わせ、その間に液晶を注入して液晶層136を形成し、液晶モジュールを形成する。液晶の注入を行う場合、真空状態となる処理室が必要となる。
After that, the
なお液晶は、滴下して形成してもよく、液晶を滴下する手段にインクジェット法を用いてもよい。特に大型基板の場合、滴下して液晶を形成すると好ましい。液晶注入法を用いると、大型基板になるにつれ処理室が拡大し、基板の重量が重くなり、困難をきたすためである。 Note that the liquid crystal may be formed by dropping, or an inkjet method may be used as a means for dropping the liquid crystal. Particularly in the case of a large substrate, it is preferable to form liquid crystals by dropping. This is because when the liquid crystal injection method is used, the processing chamber is enlarged as the substrate becomes large, and the weight of the substrate increases, resulting in difficulty.
液晶を滴下する場合、まず一方の基板の周囲へシール材を形成する。一方の基板と記載するのは、基板100及び対向基板135のいずれにシール材を形成してもよいからである。このとき、シール材の始点と終点が一致した、閉じられた領域にシール材を形成する。その後、一滴又は複数滴の液晶を滴下する。大型基板の場合、複数箇所に、複数滴の液晶を滴下する。そして真空状態とし、他方の基板と張り合わせる。真空状態とすると、不要な空気を取り除くことができ、空気に起因するシール材の破損や膨張を防止することができるからである。
When liquid crystal is dropped, a sealing material is first formed around one substrate. The reason why one substrate is described is that a sealant may be formed on either the
次いで、仮止めを行うためにシール材が形成された領域の2点以上を固化し、接着させる。シール材に紫外線硬化樹脂を用いる場合、シール材が形成された領域の2点以上に紫外線を照射すればよい。その後、処理室から基板を取り出し、本止めを行うため、シール材全体を固化し、接着させる。このとき、薄膜トランジスタや液晶に紫外線が照射されないように遮光材を配置するとよい。 Next, at least two points in the region where the sealing material is formed are solidified and bonded to perform temporary fixing. In the case where an ultraviolet curable resin is used for the sealing material, it is only necessary to irradiate ultraviolet rays to two or more points in the region where the sealing material is formed. Thereafter, the substrate is taken out from the processing chamber and the entire sealing material is solidified and bonded in order to perform the final fixing. At this time, a light shielding material is preferably arranged so that the thin film transistor and the liquid crystal are not irradiated with ultraviolet rays.
また、基板間のギャップを保持するため、シール材以外に、柱状又は球状のスペーサを用いるとよい。 Further, in order to maintain a gap between the substrates, a columnar or spherical spacer may be used in addition to the sealant.
このようにして液晶モジュールが完成する。 In this way, the liquid crystal module is completed.
その後、異方性導電膜を用いてFPC(フレキシブルプリントサーキット:Flexible Printed Circuit)を接着して外部端子と、信号線駆動回路又は走査線駆動回路とを接続すればよい。また信号線駆動回路又は走査線駆動回路を外部回路として形成してもよい。 After that, an external terminal and a signal line driver circuit or a scanning line driver circuit may be connected by bonding an FPC (Flexible Printed Circuit) using an anisotropic conductive film. Further, the signal line driver circuit or the scan line driver circuit may be formed as an external circuit.
このように、微細な配線を有する薄膜トランジスタを具備し、外部端子が接続された液晶表示装置を形成することができる。 In this manner, a liquid crystal display device including a thin film transistor having a fine wiring and connected to an external terminal can be formed.
本実施の形態において、薄膜トランジスタは層間絶縁膜を形成しないため非常に薄い液晶表示装置を形成することができる。 In this embodiment mode, since the thin film transistor does not form an interlayer insulating film, a very thin liquid crystal display device can be formed.
また本実施の形態において、上記実施の形態に示すように、層間絶縁膜を形成して平坦性を高めてもよい。平坦性を高めると、配向膜を均一に形成することができ、液晶層へ均一に電圧を印加することができるため好ましい。 In this embodiment mode, as shown in the above embodiment mode, an interlayer insulating film may be formed to improve flatness. Increasing the flatness is preferable because an alignment film can be formed uniformly and a voltage can be uniformly applied to the liquid crystal layer.
層間絶縁膜には、無機材料(酸化シリコン、窒化シリコン、酸化窒化シリコンなど)、感光性又は非感光性の有機材料(ポリイミド、アクリル、ポリアミド、ポリイミドアミド、レジスト又はベンゾシクロブテン)、シロキサン、ポリシラザン、及びそれらの積層構造を用いることができる。有機材料として、ポジ型感光性有機樹脂又はネガ型感光性有機樹脂を用いることができる。 For the interlayer insulating film, inorganic materials (silicon oxide, silicon nitride, silicon oxynitride, etc.), photosensitive or non-photosensitive organic materials (polyimide, acrylic, polyamide, polyimide amide, resist or benzocyclobutene), siloxane, polysilazane , And their stacked structures can be used. As the organic material, a positive photosensitive organic resin or a negative photosensitive organic resin can be used.
(実施の形態11)
本実施の形態では、上記実施の形態で示した薄膜トランジスタを有する発光モジュールを有する表示装置(発光装置)について説明する。
(Embodiment 11)
In this embodiment, a display device (light-emitting device) including a light-emitting module including the thin film transistor described in the above embodiment is described.
図10には、上記実施で示したようなTFT基板に形成された薄膜トランジスタ120と、画素電極125とを有する発光装置の断面を示す。
FIG. 10 shows a cross section of a light emitting device having the
上記実施の形態に示したように画素電極125を有する薄膜トランジスタ120を形成する。なお画素電極125は、発光素子の第1の電極として機能する。
As shown in the above embodiment mode, the
その後、土手又は隔壁として機能する絶縁膜143を第1の電極上に形成する。絶縁膜には、無機材料(酸化シリコン、窒化シリコン、酸化窒化シリコンなど)、感光性又は非感光性の有機材料(ポリイミド、アクリル、ポリアミド、ポリイミドアミド、レジスト又はベンゾシクロブテン)、シロキサン、ポリシラザン、及びそれらの積層構造を用いることができる。有機材料として、ポジ型感光性有機樹脂又はネガ型感光性有機樹脂を用いることができる。例えば、有機材料としてポジ型の感光性アクリルを用いた場合、露光処理により感光性有機樹脂をエッチングすると上端部に曲率を有する開口部を形成することができる。そのため、後に形成する電界発光層等の段切れを防止することができる。この状態のTFT基板を発光モジュール用TFT基板と表記する。
After that, an insulating
第1の電極上に設けられた絶縁膜143の開口部に、電界発光層141を形成する。電界発光層を形成する前にプラズマ処理を施し、表面改質を行ってもよい。本実施の形態では、絶縁膜143の開口部に対してプラズマ処理を行い、インクジェット法により高分子材料を有する電界発光層を形成する。
An
その後、電界発光層141及び絶縁膜143を覆うように発光素子の第2の電極142を形成する。
After that, the
なお電界発光層が形成する分子励起子の種類としては一重項励起状態と三重項励起状態が可能である。基底状態は通常一重項状態であり、一重項励起状態からの発光は蛍光と呼ばれる。また、三重項励起状態からの発光は燐光と呼ばれる。電界発光層からの発光とは、どちらの励起状態が寄与する場合も含まれる。更には、蛍光と燐光を組み合わせて用いてもよく、各RGBの発光特性(発光輝度や寿命等)により蛍光及び燐光のいずれかを選択することができる。 Note that the type of molecular excitons formed by the electroluminescent layer can be a singlet excited state or a triplet excited state. The ground state is usually a singlet state, and light emission from the singlet excited state is called fluorescence. In addition, light emission from the triplet excited state is called phosphorescence. The light emission from the electroluminescent layer includes the case where either excited state contributes. Furthermore, fluorescence and phosphorescence may be used in combination, and either fluorescence or phosphorescence can be selected depending on the emission characteristics of each RGB (emission luminance, lifetime, etc.).
電界発光層141は、画素電極125に相当する第1の電極側から順に、HIL(ホール注入層)、HTL(ホール輸送層)、EML(発光層)、ETL(電子輸送層)、EIL(電子注入層)の順に積層されている。なお電界発光層は、積層構造以外に単層構造、又は混合構造をとることができる。
The
また、電界発光層141として、赤色(R)、緑色(G)、青色(B)の発光を示す材料を、それぞれ蒸着マスクを用いた蒸着法等によって選択的に形成する。赤色(R)、緑色(G)、青色(B)の発光を示す材料はインクジェット法により形成することもでき、この場合マスクを用いずとも、RGBの塗り分けを行うことができるため好ましい。
In addition, as the
具体的には、HILとしてCuPcやPEDOT、HTLとしてα−NPD、ETLとしてBCPやAlq3、EILとしてBCP:LiやCaF2をそれぞれ用いる。また例えばEMLは、R、G、Bのそれぞれの発光色に対応したドーパント(Rの場合DCM等、Gの場合DMQD等)をドープしたAlq3を用いればよい。 Specifically, CuPc or PEDOT is used as HIL, α-NPD is used as HTL, BCP or Alq 3 is used as ETL, and BCP: Li or CaF 2 is used as EIL. Further, for example, EML may be Alq 3 doped with a dopant corresponding to each emission color of R, G, and B (DCM in the case of R, DMQD in the case of G).
なお、電界発光層は上記材料に限定されない。例えば、CuPcやPEDOTの代わりに酸化モリブデン(MoOx:x=2〜3)等の酸化物とα−NPDやルブレンを共蒸着して形成し、ホール注入性を向上させることもできる。また電界発光層の材料は、有機材料(低分子又は高分子を含む)、又は有機材料と無機材料の複合材料として用いることができる。 Note that the electroluminescent layer is not limited to the above materials. For example, instead of CuPc or PEDOT, an oxide such as molybdenum oxide (MoOx: x = 2 to 3) and α-NPD or rubrene can be co-evaporated to improve the hole injection property. The material of the electroluminescent layer can be used as an organic material (including a low molecule or a polymer), or a composite material of an organic material and an inorganic material.
さらに各RGBの電界発光層を形成する場合、カラーフィルターを用いて、高精細な表示を行うこともできる。カラーフィルターにより、各RGBの発光スペクトルにおいてブロードなピークを鋭くなるように補正できるからである。 Furthermore, when each RGB electroluminescent layer is formed, high-definition display can be performed using a color filter. This is because the color filter can correct a broad peak to be sharp in the emission spectrum of each RGB.
以上、各RGBの発光を示す材料を形成する場合を説明したが、単色の発光を示す材料を形成し、カラーフィルターや色変換層を組み合わせることによりフルカラー表示を行うことができる。例えば、白色又は橙色の発光を示す電界発光層を形成する場合、カラーフィルター、又はカラーフィルターと色変換層とを組み合わせたものを別途設けることによってフルカラー表示ができる。カラーフィルターや色変換層は、例えば第2の基板(封止基板)に形成し、基板へ張り合わせればよい。単色の発光を示す材料、カラーフィルター、及び色変換層のいずれもインクジェット法により形成することができる。 As described above, the case where a material that emits light of each RGB is formed has been described. However, full color display can be performed by forming a material that emits light of a single color and combining a color filter and a color conversion layer. For example, when an electroluminescent layer that emits white or orange light is formed, full color display can be performed by separately providing a color filter or a combination of a color filter and a color conversion layer. The color filter and the color conversion layer may be formed on, for example, a second substrate (sealing substrate) and attached to the substrate. Any of a material exhibiting monochromatic light emission, a color filter, and a color conversion layer can be formed by an inkjet method.
もちろん単色発光の表示を行ってもよい。例えば、単色発光を用いてエリアカラータイプの表示装置を形成してもよい。エリアカラータイプは、パッシブマトリクス型の表示部が適しており、主に文字や記号を表示することができる。 Of course, monochromatic light emission may be displayed. For example, an area color type display device may be formed using monochromatic light emission. As the area color type, a passive matrix type display unit is suitable, and characters and symbols can be mainly displayed.
また第1の電極125及び第2の電極142は仕事関数を考慮して材料を選択する必要がある。そして第1の電極及び第2の電極は、画素構成によりいずれも陽極、又は陰極となりうる。本実施の形態では、駆動用TFTの極性がNチャネル型であるため、第1の電極を陰極、第2の電極を陽極とすると好ましい。また駆動用TFTの極性がpチャネル型である場合、第1の電極を陽極、第2の電極を陰極とするとよい。
In addition, it is necessary to select materials for the
以下に、陽極及び陰極に用いる電極材料について説明する。 Below, the electrode material used for an anode and a cathode is demonstrated.
陽極として用いる電極材料としては、仕事関数の大きい(仕事関数4.0eV以上)金属、合金、電気伝導性化合物、及びこれらの混合物などを用いることが好ましい。具体例な材料としては、ITO、酸化インジウムに2〜20%の酸化亜鉛(ZnO)を混合したIZO、酸化インジウムに2〜20%の酸化珪素(SiO2)を混合したITSO、金、白金、ニッケル、タングステン、クロム、モリブデン、鉄、コバルト、銅、パラジウム、又は金属材料の窒化物(例えば、窒化チタン等)を用いることができる。 As an electrode material used as the anode, it is preferable to use a metal, an alloy, an electrically conductive compound, a mixture thereof, or the like having a high work function (work function of 4.0 eV or more). Specific examples include ITO, IZO in which 2 to 20% zinc oxide (ZnO) is mixed in indium oxide, ITSO in which 2 to 20% silicon oxide (SiO 2 ) is mixed in indium oxide, gold, platinum, Nickel, tungsten, chromium, molybdenum, iron, cobalt, copper, palladium, or a nitride of a metal material (eg, titanium nitride) can be used.
一方、陰極として用いる電極材料としては、仕事関数の小さい(仕事関数3.8eV以下)金属、合金、電気伝導性化合物、及びこれらの混合物などを用いることが好ましい。具体的な材料としては、元素周期律の1族又は2族に属する元素、すなわちリチウムやセシウム等のアルカリ金属、及びマグネシウム、カルシウム、ストロンチウム等のアルカリ土類金属、及びこれらを含む合金(Mg:Ag、Al:Li)や化合物(LiF、CsF、CaF2)の他、希土類金属を含む遷移金属を用いて形成することができる。
On the other hand, as an electrode material used as a cathode, it is preferable to use a metal, an alloy, an electrically conductive compound, a mixture thereof, or the like having a low work function (work function of 3.8 eV or less). Specific examples of the material include elements belonging to Group 1 or
また、本実施の形態において第2の電極を透光性とする必要がある場合、これら金属、又はこれら金属を含む合金を非常に薄く形成し、ITO、IZO、ITSO又はその他の金属(合金を含む)との積層により形成することができる。 Further, in the present embodiment, when the second electrode needs to be light-transmitting, these metals or an alloy containing these metals are formed very thin, and ITO, IZO, ITSO, or other metals (alloys are used). Including).
これら第1の電極及び第2の電極は蒸着法、スパッタリング法、又はインクジェット法等により形成することができる。 The first electrode and the second electrode can be formed by an evaporation method, a sputtering method, an inkjet method, or the like.
特に第2の電極としてスパッタリング法による導電膜、ITO若しくはITSO、又はそれらの積層体を形成する場合、スパッタリング時、電界発光層にダメージが入る恐れがある。スパッタリングによるダメージを低減するため、酸化モリブデン(MoOx:x=2〜3)等の酸化物が電界発光層の最上面に形成されると好ましい。そのため、HIL等として機能する酸化モリブデン(MoOx:x=2〜3)等の酸化物を電界発光層の最上面に形成し、第1の電極側から順に、EIL(電子注入層)、ETL(電子輸送層)、EML(発光層)、HTL(ホール輸送層)、HIL(ホール注入層)、第2の電極の順に積層するとよい。このとき第1の電極は陰極として機能し、第2の電極は陽極として機能する。 In particular, when a conductive film by sputtering, ITO or ITSO, or a laminate thereof is formed as the second electrode, the electroluminescent layer may be damaged during sputtering. In order to reduce damage due to sputtering, an oxide such as molybdenum oxide (MoOx: x = 2 to 3) is preferably formed on the uppermost surface of the electroluminescent layer. Therefore, an oxide such as molybdenum oxide (MoOx: x = 2 to 3) functioning as HIL or the like is formed on the uppermost surface of the electroluminescent layer, and sequentially from the first electrode side, EIL (electron injection layer), ETL ( The electron transport layer), the EML (light emitting layer), the HTL (hole transport layer), the HIL (hole injection layer), and the second electrode may be stacked in this order. At this time, the first electrode functions as a cathode, and the second electrode functions as an anode.
特に本実施の形態では、駆動用TFTの極性がNチャネル型であるため、電子の移動方向を考慮すると、第1の電極を陰極、EIL(電子注入層)、ETL(電子輸送層)、EML(発光層)、HTL(ホール輸送層)、HIL(ホール注入層)、第2の電極を陽極とすると好ましい。 In particular, in this embodiment, since the polarity of the driving TFT is an N-channel type, considering the electron moving direction, the first electrode is a cathode, EIL (electron injection layer), ETL (electron transport layer), EML. The (light emitting layer), HTL (hole transport layer), HIL (hole injection layer), and the second electrode are preferably anodes.
その後、窒素を含むパッシベーション膜又はDLC(Diamond Like Carbon)等をスパッタリング法やCVD法により形成するとよい。その結果、水分や酸素の侵入を防止することができる。また第1の電極、第2の電極、その他の電極により、表示手段の側面を覆って酸素や水分の侵入を防ぐこともできる。次いで、封止基板を張り合わせる。封止基板により形成される空間には、窒素を封入したり、乾燥剤を配置してもよい。また透光性を有し、吸水性の高い樹脂を充填してもよい。封止構造は、下記実施の形態で詳細に説明する。 After that, a passivation film containing nitrogen, DLC (Diamond Like Carbon), or the like may be formed by a sputtering method or a CVD method. As a result, moisture and oxygen can be prevented from entering. In addition, the first electrode, the second electrode, and other electrodes can cover the side surface of the display means to prevent oxygen and moisture from entering. Next, the sealing substrate is attached. In the space formed by the sealing substrate, nitrogen may be sealed or a desiccant may be disposed. Further, a resin having translucency and high water absorption may be filled. The sealing structure will be described in detail in the following embodiment.
このようにして発光モジュールが完成する。 In this way, the light emitting module is completed.
発光モジュールにおいて、第1の電極及び第2の電極が透光性を有するように形成すると、信号線から入力されるビデオ信号に応じた輝度で電界発光層から光が両矢印方向145、146に出射する。また第1の電極が透光性を有し、第2の電極が非透光性を有するように形成すると、矢印方向146のみに射出する。また第1の電極が非透光性を有し、第2の電極が透光性を有するように形成すると、矢印方向145のみに射出する。このとき、光の出射方向とならない側に設けられた非透光性の電極に、反射性の高い導電膜を用いることにより光を有効利用することができる。
In the light-emitting module, when the first electrode and the second electrode are formed so as to have a light-transmitting property, light from the electroluminescent layer has a luminance corresponding to the video signal input from the signal line in the
本実施の形態において、透光性を有する導電膜を得るためには、非透光性を有する導電膜を、透光性を有するように薄く形成し、その上に透光性を有する導電膜を積層してもよい。 In this embodiment, in order to obtain a light-transmitting conductive film, a light-transmitting conductive film is thinly formed to have a light-transmitting property, and the light-transmitting conductive film is formed thereover. May be laminated.
その後、異方性導電膜を用いてFPCを接着して外部端子と、信号線駆動回路又は走査線駆動回路とを接続すればよい。また信号線駆動回路又は走査線駆動回路を外部回路として形成してもよい。 After that, an FPC may be bonded using an anisotropic conductive film to connect the external terminal and the signal line driver circuit or the scan line driver circuit. Further, the signal line driver circuit or the scan line driver circuit may be formed as an external circuit.
このように、微細な配線を有する薄膜トランジスタを具備し、外部端子が接続された発光装置を形成することができる。 As described above, a light-emitting device including a thin film transistor having a fine wiring and connected to an external terminal can be formed.
本実施の形態において、薄膜トランジスタは層間絶縁膜を形成しないため非常に薄い発光装置を形成することができる。 In this embodiment mode, since the thin film transistor does not form an interlayer insulating film, a very thin light-emitting device can be formed.
また本実施の形態において、上記実施の形態に示すように層間絶縁膜を形成して平坦性を高めてもよい。平坦性を高めると、電界発光層へ均一に電圧を印加することができるため好ましい。 In this embodiment mode, as shown in the above embodiment mode, an interlayer insulating film may be formed to improve flatness. Increasing the flatness is preferable because a voltage can be uniformly applied to the electroluminescent layer.
層間絶縁膜には、無機材料(酸化シリコン、窒化シリコン、酸化窒化シリコンなど)、感光性又は非感光性の有機材料(ポリイミド、アクリル、ポリアミド、ポリイミドアミド、レジスト又はベンゾシクロブテン)、シロキサン、ポリシラザン、及びそれらの積層構造を用いることができる。有機材料として、ポジ型感光性有機樹脂又はネガ型感光性有機樹脂を用いることができる。 For the interlayer insulating film, inorganic materials (silicon oxide, silicon nitride, silicon oxynitride, etc.), photosensitive or non-photosensitive organic materials (polyimide, acrylic, polyamide, polyimide amide, resist or benzocyclobutene), siloxane, polysilazane , And their stacked structures can be used. As the organic material, a positive photosensitive organic resin or a negative photosensitive organic resin can be used.
図9(A)には、発光装置の画素部の等価回路図を例示する。一画素は、スイッチング用のTFT(スイッチ用TFT)800、駆動用のTFT(駆動用TFT)801、電流制御用のTFT(電流制御用TFT)802を有し、これらTFTはNチャネル型を有する。スイッチング用TFT800の一方の電極及びゲート電極は、それぞれ信号線803及び走査線805に接続されている。電流制御用TFT802の一方の電極は第1の電源線804に接続され、ゲート電極はスイッチング用TFTの他方の電極に接続されている。
FIG. 9A illustrates an equivalent circuit diagram of a pixel portion of a light-emitting device. One pixel includes a switching TFT (switching TFT) 800, a driving TFT (driving TFT) 801, and a current control TFT (current control TFT) 802. These TFTs have an N-channel type. . One electrode and a gate electrode of the switching
容量素子808は、電流制御用TFTのゲート・ソース間の電圧を保持するように設ければよい。本実施の形態において、例えば第1の電源線の電位を低電位とし、発光素子を高電位とすると、電流制御用TFTはNチャネル型を有するため、ソース電極と第1の電源線とが接続する。そのため、容量素子は電流制御用TFTのゲート電極と、ソース電極、つまり第1の電源線との間に設けることができる。なお、スイッチング用TFT、駆動用TFT、又は電流制御用TFTのゲート容量が大きく、各TFTからのリーク電流が許容範囲である場合、容量素子808は設ける必要はない。
The
駆動用TFT801の一方の電極は、電流制御用TFTの他方の電極に接続され、ゲート電極は第2の電源線806に接続されている。第2の電源線806は、固定電位を有する。そのため、駆動用TFTのゲート電位を固定電位とすることができ、寄生容量や配線容量によってゲート・ソース間の電圧Vgsが変化しないように動作させることができる。
One electrode of the driving
そして駆動用TFTの他方の電極に発光素子807が接続されている。本実施の形態において、例えば第1の電源線の電位を低電位とし、発光素子を高電位とすると、駆動用TFTのドレイン電極に発光素子の陰極が接続される。そのため、陰極、電界発光層、陽極の順に積層すると好ましい。このとき、第2の電極形成時のスパッタリングによるダメージを低減するため、酸化モリブデン(MoOx:x=2〜3)等の酸化物が電界発光層の最上面に形成されるとよい。そのため、HIL等として機能する酸化モリブデン(MoOx:x=2〜3)等の酸化物を電界発光層の最上面に形成するとさらに好ましい。このように、非晶質半導体膜を有するTFTであって、Nチャネル型を有する場合、TFTのドレイン電極と陰極とを接続し、EIL、ETL、EML、HTL、HIL、陽極の順に積層すると好適である。
A
以下に、このような画素回路の動作について説明する。 The operation of such a pixel circuit will be described below.
走査線805が選択されるとき、スイッチング用TFTがオンとなると、容量素子808に電荷が蓄積されはじめる。容量素子808の電荷は、電流制御用TFTのゲート・ソース間電圧と等しくなるまで蓄積される。等しくなると、電流制御用TFTがオンとなり、直列に接続された駆動用TFTがオンとなる。このとき、駆動用TFTのゲート電位が固定電位となっているため、発光素子へ寄生容量や配線容量によらない一定のゲート・ソース間電圧Vgsを印加する、つまり一定のゲート・ソース間電圧Vgs分の電流を供給することができる。
When the
このように、発光素子は電流駆動型の素子であるため、画素内のTFTの特性バラツキ、特にVthバラツキが少ない場合アナログ駆動を用いることが好適である。本実施の形態のように、非晶質半導体膜を有するTFTは、特性バラツキが低いため、アナログ駆動を用いることができる。一方デジタル駆動でも、駆動用TFTを飽和領域(|Vgs−Vth|<|Vds|を満たす領域)で動作させることで、一定の電流を発光素子に供給することができる。 As described above, since the light-emitting element is a current-driven element, it is preferable to use analog driving when there is little variation in TFT characteristics in the pixel, particularly Vth variation. As in this embodiment mode, a TFT having an amorphous semiconductor film has low characteristic variation, and thus analog driving can be used. On the other hand, even in digital driving, a constant current can be supplied to the light emitting element by operating the driving TFT in a saturation region (region satisfying | Vgs−Vth | <| Vds |).
図9(B)には、上記等価回路を有する画素部の上面図の一例を示す。 FIG. 9B illustrates an example of a top view of a pixel portion having the above equivalent circuit.
まず、下地膜上にインクジェット法又はスパッタリング法により、各TFTのゲート電極、走査線、及び第2の電源線を同一導電膜から形成する。インクジェット法によりゲート電極等を形成する場合、ゲート電極等の被形成面である下地膜に対してプラズマ処理を行う。このプラズマ処理を行う結果、アルコールや油等の液体に対して濡れ性の低い撥液性となるように表面改質が行われる。その結果、インクジェット法により形成されたゲート電極、走査線及び第2の電源線を微細化することができる。 First, a gate electrode, a scanning line, and a second power supply line of each TFT are formed from the same conductive film on the base film by an inkjet method or a sputtering method. In the case where a gate electrode or the like is formed by an inkjet method, plasma treatment is performed on a base film that is a formation surface of the gate electrode or the like. As a result of this plasma treatment, surface modification is performed so that the liquid repellency is low in wettability with respect to liquids such as alcohol and oil. As a result, the gate electrode, the scanning line, and the second power supply line formed by the ink jet method can be miniaturized.
図示しないが、その後ゲート絶縁膜を形成する。 Although not shown, a gate insulating film is formed thereafter.
ゲート絶縁膜上に発光素子807の第1の電極810を形成する。第1の電極810は、インクジェット法又はスパッタリング法等により形成することができる。インクジェット法により第1の電極を形成する場合、第1の電極の被形成面であるゲート絶縁膜に対してプラズマ処理を行う。このプラズマ処理を行う結果、アルコールや油等の液体に対して濡れ性の低い撥液性となるように表面改質が行われる。その結果、インクジェット法により形成された第1の電極を微細化することができる。
A
次いで、半導体膜を形成する。本実施の形態ではプラズマCVD法により全面に半導体膜を形成し、マスクを用いて所望の形状の半導体膜となるようにパターニングする。半導体膜上に、N型を有する半導体膜を形成してもよく、半導体膜及びN型を有する半導体膜を連続形成することができる。 Next, a semiconductor film is formed. In this embodiment mode, a semiconductor film is formed over the entire surface by a plasma CVD method, and is patterned using a mask so that the semiconductor film has a desired shape. An N-type semiconductor film may be formed over the semiconductor film, and the semiconductor film and the N-type semiconductor film can be continuously formed.
その後、スパッタリング法又はCVD法により形成された導電膜をパターニングして、ソース配線及、ドレイン配線、信号線、及び第1の電源線を形成する。パターニングするためのマスクは、インクジェット法又はフォトリソグラフィー法により形成することができる。 Thereafter, the conductive film formed by a sputtering method or a CVD method is patterned to form a source wiring, a drain wiring, a signal line, and a first power supply line. The mask for patterning can be formed by an inkjet method or a photolithography method.
またソース電極、ドレイン電極、信号線及び第1の電源線は、インクジェット法、により形成することができる。インクジェット法によりソース電極、ドレイン電極、信号線及び第1の電源線を形成する場合、ソース電極、ドレイン電極、信号線及び第1の電源線の被形成面に対してプラズマ処理を行う。このプラズマ処理を行う結果、アルコールや油等の液体に対して濡れ性の低い撥液性となるように表面改質が行われる。その結果、インクジェット法により形成されたソース電極、ドレイン電極、信号線及び第1の電源線を微細化することができる。 In addition, the source electrode, the drain electrode, the signal line, and the first power supply line can be formed by an inkjet method. In the case where the source electrode, the drain electrode, the signal line, and the first power supply line are formed by an inkjet method, plasma treatment is performed on formation surfaces of the source electrode, the drain electrode, the signal line, and the first power supply line. As a result of this plasma treatment, surface modification is performed so that the liquid repellency is low in wettability with respect to liquids such as alcohol and oil. As a result, the source electrode, the drain electrode, the signal line, and the first power supply line that are formed by an inkjet method can be miniaturized.
本実施の形態において、容量素子808は、ゲート絶縁膜を介して設けられたゲート配線、及びソース・ドレイン配線により形成されている。
In this embodiment mode, the
本実施の形態において、駆動用TFTは非晶質半導体膜を有するため、駆動用TFTのチャネル幅(W)が広くなるように設計するとよい。 In this embodiment mode, since the driving TFT includes an amorphous semiconductor film, the driving TFT may be designed to have a wide channel width (W).
このようにして、発光装置の画素部を形成することができる。 In this manner, a pixel portion of the light emitting device can be formed.
なお図9(B)のC−C’の断面図は、図10に記載の断面図に相当する。 Note that a cross-sectional view taken along C-C ′ in FIG. 9B corresponds to the cross-sectional view illustrated in FIG. 10.
このようなアクティブマトリクス型の発光装置は、画素密度が増えた場合、各画素にTFTが設けられているため低電圧駆動でき、有利であると考えられている。 Such an active matrix light-emitting device is considered to be advantageous because it can be driven at a low voltage because a TFT is provided in each pixel when the pixel density is increased.
本実施の形態では、一画素に各TFTが設けられるアクティブマトリクス型の発光装置について説明したが、一列毎にTFTが設けられるパッシブマトリクス型の発光装置を形成することもできる。パッシブマトリクス型の発光装置は、各画素にTFTが設けられていないため、高開口率となる。発光が電界発光層の両側へ射出する発光装置の場合、パッシブマトリクス型の表示装置を用いると透過率を高めることができる。 In this embodiment mode, an active matrix light-emitting device in which each pixel is provided with each TFT has been described; however, a passive matrix light-emitting device in which a TFT is provided for each column can also be formed. A passive matrix light-emitting device has a high aperture ratio because a TFT is not provided for each pixel. In the case of a light-emitting device in which light emission is emitted to both sides of an electroluminescent layer, the transmittance can be increased by using a passive matrix display device.
(実施の形態12)
本実施の形態では、外部端子が接続された発光装置や液晶表示装置等の表示装置の形態を説明する。
(Embodiment 12)
In this embodiment mode, a mode of a display device such as a light-emitting device or a liquid crystal display device to which an external terminal is connected will be described.
図11には、コントロール回路601a及び電源回路602が実装された表示装置の外観図を示す。基板600上には、発光素子又は液晶素子が各画素に設けられた画素部603が設けられている。画素部603が有する薄膜トランジスタは、上記実施の形態のように微細化された配線等を有するように形成することができる。画素部603が有する画素を選択する走査線駆動回路604aと、選択された画素にビデオ信号を供給する信号線駆動回路605aとはICチップにより実装されている。実装するICの長辺、短辺の長さやその個数は、本実施の形態に限定されない。また、走査線駆動回路や信号線駆動回路は、画素部と一体形成してもよい。
FIG. 11 shows an external view of a display device on which the
プリント基板607にはコントロール回路601a、電源回路602、映像信号処理回路609a、ビデオRAM610a、オーディオ用回路611aが設けられている。電源回路602、から出力された電源電圧、また、コントロール回路601a、映像信号処理回路609a、ビデオRAM610a、オーディオ用回路611aからの各種信号はFPC606を介して走査線駆動回路604a、信号線駆動回路605aに供給され、さらに画素部603へ供給される。
The printed
またプリント基板607の電源電圧及び各種信号は、複数の入力端子が配置されたインターフェース(I/F)部608を介して供給される。映像信号処理回路609aは、インターフェース(I/F)部608から信号が入力される。さらに映像信号処理回路609aはビデオRAM610aと相互に信号のやりとりを行う。
The power supply voltage and various signals of the printed
本実施の形態ではプリント基板607がFPC606を用いて実装されているが、必ずしもこの構成に限定されない。COG(Chip on Glass)方式を用い、コントロール回路601a、電源回路602を直接基板上に実装させるようにしてもよい。また信号線駆動回路や走査線駆動回路等のICチップの実装方法は、本実施の形態に限定されず、基板上に形成されたICチップをワイヤボンディング法により、画素部の配線と接続してもよい。
In this embodiment mode, the printed
また、プリント基板607において、引きまわしの配線間に形成される容量や配線自体が有する抵抗等によって、電源電圧や信号にノイズがのったり、信号の立ち上がりが鈍ったりすることがある。そこで、プリント基板607にコンデンサ、バッファ等の各種素子を設けて、電源電圧や信号にノイズがのったり、信号の立ち上がりが鈍ったりするのを防ぐようにしてもよい。
Further, in the printed
以上のように、微細化された配線等を有する薄膜トランジスタを具備する表示装置を形成することができる。 As described above, a display device including a thin film transistor having a miniaturized wiring or the like can be formed.
図19には図11と異なる表示装置の形態を示す。図19は、実施の形態5で示すような結晶性半導体膜を有する薄膜トランジスタを用いてモジュールを形成する。そのため、駆動回路部や周辺回路部に形成される素子を基板上に一体形成することができる。 FIG. 19 shows a form of a display device different from FIG. In FIG. 19, a module is formed using a thin film transistor having a crystalline semiconductor film as described in Embodiment Mode 5. Therefore, elements formed in the drive circuit portion and the peripheral circuit portion can be integrally formed on the substrate.
図19(A)に示すように、基板600上に、画素部603、走査線駆動回路604b、信号線駆動回路605b、コントロール回路601b、オーディオ用回路611b、映像信号処理回路609b、ビデオRAM610bが設けられている。その結果、プリント基板に形成される素子を少なくすることができる。
As shown in FIG. 19A, a
図19(B)には、基板600上に形成された各回路のブロック図を示す。なお、画素部603に液晶素子が形成される場合の回路について説明する。パネル上には、画素部603が設けられ、階調表示を行うための階調電源617を有する。また画素部603の周囲には、走査線駆動回路604aと、信号線駆動回路605aとが設けられている。
FIG. 19B shows a block diagram of each circuit formed over the
コントロール回路601bは、CPU616、CPU用インターフェース(I/F)623、CPUが使用するスタック・変数用SRAMとして機能するWRAM624、プログラムと画像データが格納されているマスクROMとして機能するPROM615、PROMとWRAMのアドレス・データバスのインターフェース及びWRAM用アドレスの一部をデコードしてオーディオ用回路を制御する信号を作製する機能を有するメモリーコントローラ625、を有している。
The
オーディオ用回路611bは、音声データが格納されているマスクROMとして機能するオーディオROM619、オーディオ用回路のクロック信号を作製したり、カウンタを使ってオーディオROMのアドレスを作製する機能を有するオーディオコントローラ621、デジタル音声データからアナログ波形を作製したり、アナログ波形を増幅する機能を有するアンプ618を有する。
The
映像信号処理回路609bは、画像データの色情報を格納するSRAMとして機能するCRAM622を有する。
The video
さらに、画像キャラクタの座標情報や画像一行分のキャラクタ情報を格納するSRAM626が設けられている。 Further, an SRAM 626 for storing the coordinate information of the image character and the character information for one line of the image is provided.
これら機能を有する各回路は、プリント基板607に設けられた電源回路602からの電源が、FPC606を介して供給される。
Each circuit having these functions is supplied with power from the
このように結晶性半導体膜を用いて薄膜トランジスタを作製する場合、ガラス基板に一体形成でき、表示装置の小型化、及び軽量化を達成することができる。また、FPCとの接続点を削減することができるため、表示装置の生産性を高めることができる。 In the case where a thin film transistor is manufactured using a crystalline semiconductor film in this manner, the thin film transistor can be integrally formed with a glass substrate, and the display device can be reduced in size and weight. In addition, since the number of connection points with the FPC can be reduced, the productivity of the display device can be increased.
以上のように、微細化された配線等を有する薄膜トランジスタを具備する表示装置を形成することができる。 As described above, a display device including a thin film transistor having a miniaturized wiring or the like can be formed.
(実施の形態13)
本実施の形態では、上記実施の形態で示した発光装置を封止した状態を説明する。
(Embodiment 13)
In this embodiment, a state where the light-emitting device described in the above embodiment is sealed is described.
図12(A)は、封止された発光装置の断面図であって、図11のD−D’に相当する断面図を示す。画素部903は、基板(便宜上第1の基板と表記する)911上に、下地膜912を介して、Nチャネル型を有する駆動用TFT914が設けられている。駆動用TFTは、上記実施の形態のように微細化された配線等を有するように形成することができる。駆動用TFTが有するソース電極又はドレイン電極として機能する配線に陽極915が接続されている。陽極上には電界発光層916、陰極917の順に形成されている。
FIG. 12A is a cross-sectional view of the sealed light-emitting device, and shows a cross-sectional view corresponding to D-D ′ in FIG. 11. In the
さらに陰極を覆って保護膜918が設けられている。保護膜は、スパッタ法(DC方式やRF方式)により得られる窒化珪素または窒化酸化珪素を主成分とする絶縁膜、水素を含むDLC膜、または窒化炭素膜を有するように形成されている。また保護膜は、上記膜の単層構造又は積層構造を有することができる。例えば保護膜として、水分や酸素の侵入を防ぐための硬度の高い膜を形成する場合、応力を緩和するための膜、例えば窒化炭素膜を設けた後に硬度の高い膜を設けることができる。保護膜により、水分や酸素等による電界発光層の劣化を防止することができる。
Further, a
陰極及び保護膜は、第1の接続領域920まで設けられている。接続領域920において陰極は、接続配線919と接続している。
The cathode and the protective film are provided up to the
封止領域923では、シール材921を介して、第1の基板911と対向基板(便宜上第2の基板と表記する)922とが張り合わせられている。対向基板には、乾燥剤を設けてもよい。乾燥剤により、水分や酸素の侵入を防止することができる。また更に、対向基板にカラーフィルターを形成してもよい。カラーフィルターにより、各RGBの発光スペクトルにおいてブロードなピークを鋭くなるように補正できるからである。シール材は、熱硬化樹脂又は紫外線硬化樹脂からなり、圧力を加えながら加熱したり、紫外線を照射して第1の基板と第2の基板とを接着、固定させる。例えば、シール材としてエポキシ系樹脂を用いることができる。シール材には、スペーサが混入されており、第1の基板と第2の基板の間隔、いわゆるギャップを保持している。スペーサとしては、球状又は柱状の形状を有しているものが使用され、本実施の形態では、円柱状のスペーサを使用し、円の直径がギャップとなる。
In the sealing
第2の接続領域926では、接続配線919がICチップ927により形成される信号線駆動回路と異方性導電膜924を介して接続している。なおICチップは、FPC906上に設けられている。また加圧や加熱により異方性導電膜を接着するときに、フィルム基板のフレキシブル性や加熱による軟化のため、クラックが生じないように注意する。例えば、接着領域に硬性の高い基板を補助として配置したりすればよい。このようにして接続されたICチップから、ビデオ信号やクロック信号を受け取る。
In the
第2の基板922で封止すると、保護膜918との間に空間が形成される。空間には、不活性ガス、例えば窒素ガスを充填したり、吸水性の高い材料を形成して、さらに水分や酸素の侵入の防止を高めることができる。また透光性を有し、吸水性の高い樹脂を形成してもよい。透光性を有する樹脂により、発光素子からの光が第2の基板側へ出射される場合であっても、透過率を低減することなく形成することができる。
When sealed with the
図12(B)には、図12(A)と異なり、第2の基板を用いず封止する場合を示す。その他の構成は同様であるため、説明を省略する。 FIG. 12B shows a case of sealing without using the second substrate, unlike FIG. 12A. Since other configurations are the same, description thereof is omitted.
図12(B)には、保護膜918を覆って、第2の保護膜930が設けられている。第2の保護膜として、エポキシ樹脂、ウレタン樹脂、又はシリコーン樹脂等の有機材料を用いることができる。また第2の保護膜は、インクジェット法によりポリマー材料を滴下して形成してもよい。本実施の形態では、ディスペンサを用いてエポキシ樹脂を吐出し、乾燥させる。
In FIG. 12B, a second
水分や酸素等による電界発光層の劣化が問題とならない場合は、保護膜918を設けなくともよい。さらに第2の保護膜上に、第2の基板を設けて封止してもよい。
In the case where deterioration of the electroluminescent layer due to moisture, oxygen, or the like is not a problem, the
このように第2の基板を用いず封止すると、表示装置の軽量化、小型化、薄膜化を向上させることができる。 When sealing is performed without using the second substrate in this manner, the weight, size, and thickness of the display device can be improved.
また本実施の形態においてコントラストを高めるため、偏光板又は円偏光板を設けてもよい。例えば、表示面の一面又は両面に偏光板、若しくは円偏光板を設けることができる。 In this embodiment mode, a polarizing plate or a circular polarizing plate may be provided to increase contrast. For example, a polarizing plate or a circularly polarizing plate can be provided on one surface or both surfaces of the display surface.
(実施の形態14)
上記実施の形態で示した表示装置を用いた電子機器として、ビデオカメラ、デジタルカメラ、ゴーグル型ディスプレイ(ヘッドマウントディスプレイ)、ナビゲーションシステム、音響再生装置(カーオーディオ、オーディオコンポ等)、ノート型パーソナルコンピュータ、ゲーム機器、携帯情報端末(モバイルコンピュータ、携帯電話、携帯型ゲーム機又は電子書籍等)、記録媒体を備えた画像再生装置(具体的にはDigital Versatile Disc(DVD)等の記録媒体を再生し、その画像を表示しうるディスプレイを備えた装置)などが挙げられる。特に、大型画面を有する大型テレビ等に上記実施の形態で示したインクジェット法を用いることが望ましい。それら電子機器の具体例を図13に示す。
(Embodiment 14)
As electronic devices using the display device described in the above embodiment, a video camera, a digital camera, a goggle type display (head mounted display), a navigation system, a sound reproducing device (car audio, audio component, etc.), a notebook type personal computer A game machine, a portable information terminal (mobile computer, mobile phone, portable game machine, electronic book, etc.), and an image playback device (specifically, Digital Versatile Disc (DVD)) provided with a recording medium. And a device provided with a display capable of displaying the image). In particular, it is desirable to use the ink jet method described in the above embodiment mode for a large television having a large screen. Specific examples of these electronic devices are shown in FIGS.
図13(A)は大型の表示装置であり、筐体2001、支持台2002、表示部2003、スピーカー部2004、ビデオ入力端子2005等を含む。表示部2003は、画素部及び駆動回路部を有するモジュールが設けられている。画素部は、発光素子又は液晶素子を有し、上記実施の形態で示したインクジェット法より形成されたTFTを有する。なお、表示装置は、パーソナルコンピュータ用、TV放送受信用、広告表示用などの全ての情報表示用表示装置が含まれる。
FIG. 13A illustrates a large display device including a
図13(B)は携帯端末のうちの携帯電話機であり、本体2101、筐体2102、表示部2103、音声入力部2104、音声出力部2105、操作キー2106、アンテナ2107等を含む。表示部2103は、画素部及び駆動回路部を有するモジュールが設けられている。画素部は、発光素子又は液晶素子を有し、上記実施の形態で示したインクジェット法より形成されたTFTを有する。またさらに表示部2103を多面取りにより形成することにより、携帯電話機のコストを低減することができる。
FIG. 13B illustrates a mobile phone among mobile terminals, which includes a main body 2101, a housing 2102, a display portion 2103, a sound input portion 2104, a sound output portion 2105, operation keys 2106, an
図13(C)はシート型の携帯電話機であり、本体2301、表示部2303、音声入力部2304、音声出力部2305、スイッチ2306、外部接続ポート2307等を含む。外部接続ポート2307を介して、別途用意したイヤホン2308を接続することができる。表示部2303には、センサを備えたタッチパネル式の表示画面が用いられており、表示部2303に表示されたタッチパネル式操作キー2309に触れることで、一連の操作を行うことができる。表示部2303は、画素部及び駆動回路部を有するモジュールが設けられている。画素部は、発光素子又は液晶素子を有し、上記実施の形態で示したインクジェット法より形成されたTFTを有する。またさらに表示部2303を多面取りにより形成することにより、シート型の携帯電話機のコストを低減することができる。
FIG. 13C shows a sheet type mobile phone, which includes a main body 2301, a display portion 2303, an audio input portion 2304, an audio output portion 2305, a switch 2306, an external connection port 2307, and the like. A separately
以上の様に、本発明の適用範囲は極めて広く、あらゆる分野の電子機器に用いることが可能である。また本実施例の電子機器は、上記実施の形態に示したいずれの構成を用いることができる。 As described above, the applicable range of the present invention is so wide that it can be used for electronic devices in various fields. In addition, any of the structures described in the above embodiments can be used for the electronic device of this example.
(実施の形態15)
本発明において、プラズマ処理の処理ガスに不活性ガスを用いることができる。不活性ガスは、ヘリウム(He)、ネオン(Ne)、アルゴン(Ar)、クリプトン(Kr)、キセノン(Xe)等の希ガスを用いることができる。またその他の条件、例えば圧力等は、上記実施の形態と同様である。
(Embodiment 15)
In the present invention, an inert gas can be used as a processing gas for plasma processing. As the inert gas, a rare gas such as helium (He), neon (Ne), argon (Ar), krypton (Kr), or xenon (Xe) can be used. Other conditions, such as pressure, are the same as in the above embodiment.
(実施例1)
本実施例では、非晶質珪素膜、ガラス、及びアクリルに対してプラズマ処理を30sec間行った表面の結合状態を、XPS(X線光電子分光法)を用いて調べた結果を示す。
(Example 1)
In this example, the result of examining the bonding state of a surface obtained by performing plasma treatment for 30 seconds on an amorphous silicon film, glass, and acrylic using XPS (X-ray photoelectron spectroscopy) is shown.
図16(A)はガラスに対するプラズマ処理前、(B)はガラスに対するプラズマ処理後の結果を示す。CF2結合のエネルギーバンドは290eV付近にピークを有するC5で示しており、図16(A)ではCF2結合ピークの面積比率は、3.18%である。また図16(B)をみると、CF2結合ピークの面積比率は、14.6%となり、プラズマ処理を30sec間行うとCF2結合ピークの面積比率は増加している。CF2結合の強度を比べると、図16(A)では4.89%であり、図16(B)では32.86%であった。 FIG. 16A shows the result before the plasma treatment for the glass, and FIG. 16B shows the result after the plasma treatment for the glass. The energy band of the CF 2 bond is indicated by C5 having a peak near 290 eV. In FIG. 16A, the area ratio of the CF 2 bond peak is 3.18%. In FIG. 16B, the area ratio of the CF 2 bond peak is 14.6%, and the area ratio of the CF 2 bond peak increases when the plasma treatment is performed for 30 seconds. Comparing the strength of the CF 2 bond, it was 4.89% in FIG. 16A and 32.86% in FIG.
図17(A)はアクリルに対するプラズマ処理前、(B)はアクリルに対するプラズマ処理後の結果を示す。図17(A)ではCF2結合ピークの面積比率は、0.92%である。また図17(B)をみると、CF2結合ピークの面積比率は、65.83%となり、プラズマ処理を30sec間行っただけで、急激にCF2結合の強度は増加している。CF2結合の強度を比べると、図17(A)では1.88%であり、図17(B)では100%であった。 FIG. 17A shows the result before the plasma treatment for acrylic, and FIG. 17B shows the result after the plasma treatment for acrylic. In FIG. 17A, the area ratio of the CF 2 bond peak is 0.92%. In FIG. 17B, the area ratio of the CF 2 bond peak is 65.83%, and the strength of the CF 2 bond increases rapidly only by performing the plasma treatment for 30 seconds. Comparing the strength of the CF 2 bond, it was 1.88% in FIG. 17A and 100% in FIG.
以上のように、CF2結合に起因するピークは、プラズマ処理を行うにつれて増加する傾向にある。従って、プラズマ処理によりCF2結合が増加し、撥液性を示すようになったと考えられる。また、フッ素(F)はプラズマ処理装置の電極を覆うテフロン(登録商標)に起因すると考えられる。以上より、微細化したい導電膜等の被形成面に、CF2結合を形成すればよいことがわかる。 As described above, the peak due to the CF 2 bond tends to increase as the plasma treatment is performed. Therefore, it is considered that the CF 2 bond is increased by the plasma treatment and the liquid repellency is exhibited. Further, it is considered that fluorine (F) is caused by Teflon (registered trademark) covering the electrodes of the plasma processing apparatus. From the above, it can be seen that a CF 2 bond may be formed on a formation surface of a conductive film or the like to be miniaturized.
Claims (27)
処理ガスに空気、酸素又は窒素を用い、大気圧又は大気圧近傍の圧力で、前記プラズマ処理を行うことを特徴とする配線の作製方法。 In claim 2,
A method for manufacturing a wiring, wherein air, oxygen, or nitrogen is used as a processing gas, and the plasma treatment is performed at atmospheric pressure or a pressure near atmospheric pressure.
前記プラズマ処理を行って前記配線の被形成面にCF2結合を形成することにより、前記被形成面を撥液性とすることを特徴とする配線の作製方法。 In claim 2 or 3,
A method for manufacturing a wiring, wherein the plasma treatment is performed to form a CF 2 bond on a surface on which the wiring is formed, whereby the surface to be formed is made liquid repellent.
フッ素を有する膜としてテフロン又はシランカップリング剤を有する膜を形成し、前記配線材料が混入された組成物を滴下することにより配線を形成することを特徴とする配線の作製方法。 In claim 5,
A method for manufacturing a wiring, comprising forming a film containing Teflon or a silane coupling agent as a film containing fluorine, and dropping the composition mixed with the wiring material.
インクジェット法を用いて前記組成物を滴下することを特徴とする配線の作製方法。 In any one of Claims 1 thru | or 6,
A method for manufacturing a wiring, wherein the composition is dropped using an inkjet method.
ことを特徴とする薄膜トランジスタの作製方法。 A method for manufacturing a thin film transistor, wherein a conductive film is formed by dropping a composition in which a conductive material is mixed, and a composition in which the conductive material is mixed is dropped.
前記被形成面を撥液性とする手段はプラズマ処理であることを特徴とする薄膜トランジスタの作製方法。 In claim 8,
A method for manufacturing a thin film transistor, characterized in that the means for making the surface to be formed liquid-repellent is plasma treatment.
前記プラズマ処理を行って前記被形成面にCF2結合を形成することにより、前記被形成面を撥液性とすることを特徴とする薄膜トランジスタの作製方法。 In claim 9,
A method for manufacturing a thin film transistor, wherein the plasma treatment is performed to form CF 2 bonds on the surface to be formed, whereby the surface to be formed is made liquid-repellent.
前記被形成面上にフッ素を有する膜を形成することにより、前記被形成面を撥液性とすることを特徴とする薄膜トランジスタの作製方法。 In claim 8,
A method for manufacturing a thin film transistor, wherein a film having fluorine is formed over the surface to be formed so that the surface to be formed has liquid repellency.
フッ素を有する膜としてテフロン又はシランカップリング剤を有する膜を形成することにより、前記被形成面を撥液性とすることを特徴とする薄膜トランジスタの作製方法。 In claim 8 or 11,
A method for manufacturing a thin film transistor, wherein a film having Teflon or a silane coupling agent is formed as a film having fluorine to make the surface to be formed liquid-repellent.
前記ゲート電極の材料が混入された組成物を滴下することにより、前記ゲート電極の被形成面の前記撥液性の領域にゲート電極を形成し、
ソース電極及びドレイン電極の被形成面にプラズマ処理を行って撥液性とし、
前記ソース電極及びドレイン電極の材料が混入された組成物を滴下することにより、ソース電極及びドレイン電極の被形成面の前記撥液性の領域にソース電極及びドレイン電極を形成する
ことを特徴とする薄膜トランジスタの作製方法。 Plasma treatment is performed on the formation surface of the gate electrode to make it liquid repellent,
By dropping a composition mixed with the material of the gate electrode, a gate electrode is formed in the liquid repellent region of the formation surface of the gate electrode,
Plasma treatment is performed on the formation surface of the source electrode and the drain electrode to make it liquid repellent,
The source electrode and the drain electrode are formed in the liquid-repellent region of the formation surface of the source electrode and the drain electrode by dropping a composition mixed with the material of the source electrode and the drain electrode. A method for manufacturing a thin film transistor.
ゲート電極材料が混入された組成物を滴下することにより、前記基板の前記撥液性の領域にゲート電極を形成し、
前記ゲート電極を覆ってゲート絶縁膜を形成し、
前記ゲート電極上に半導体膜を形成し、
前記半導体膜上に一導電型を有する半導体膜を形成し、
前記一導電型を有する半導体膜及び前記ゲート絶縁膜にプラズマ処理を行って撥液性とし、
ソース電極及びドレイン電極の材料が混入された組成物を滴下することにより、前記一導電型を有する半導体膜及び前記ゲート絶縁膜の前記撥液性の領域に、ソース電極及びドレイン電極を形成する
ことを特徴とする薄膜トランジスタの作製方法。 Plasma treatment is performed on the substrate to make it liquid repellent,
A gate electrode is formed in the liquid-repellent region of the substrate by dropping a composition mixed with a gate electrode material,
Forming a gate insulating film covering the gate electrode;
Forming a semiconductor film on the gate electrode;
Forming a semiconductor film having one conductivity type on the semiconductor film;
The semiconductor film having the one conductivity type and the gate insulating film are subjected to plasma treatment to be liquid repellent,
Forming a source electrode and a drain electrode in the liquid-repellent region of the semiconductor film having one conductivity type and the gate insulating film by dropping a composition mixed with a material of the source electrode and the drain electrode; A manufacturing method of a thin film transistor characterized by the above.
前記ソース電極及びドレイン電極上に半導体膜を形成し、
前記半導体膜上方のゲート電極の被形成面にプラズマ処理を行って撥液性とし、
前記ゲート電極材料が混入された組成物を滴下することにより、前記ゲート電極の被形成面の前記撥液性の領域に、ゲート電極を形成する
ことを特徴とする薄膜トランジスタの作製方法。 Forming a source electrode and a drain electrode;
Forming a semiconductor film on the source and drain electrodes;
Plasma treatment is performed on the formation surface of the gate electrode above the semiconductor film to make it liquid repellent,
A method for manufacturing a thin film transistor, wherein a gate electrode is formed in the liquid-repellent region of a formation surface of the gate electrode by dropping a composition mixed with the gate electrode material.
前記ソース電極及びドレイン電極上に半導体膜を形成し、
前記半導体膜表面にプラズマ処理を行って撥液性とし、
マスク材料が混入された組成物を滴下することにより、前記半導体膜の前記撥液性の領域に、マスクを形成し、
前記マスクを用いて半導体膜をパターニングし、
前記半導体膜を覆ってゲート絶縁膜を形成し、
前記ゲート絶縁膜にプラズマ処理を行って撥液性とし、
ゲート電極材料が混入された組成物を滴下することにより、前記ゲート絶縁膜の前記撥液性の領域に、ゲート電極を形成する
ことを特徴とする薄膜トランジスタの作製方法。 A source electrode and a drain electrode are formed on the base film,
Forming a semiconductor film on the source and drain electrodes;
Plasma treatment is performed on the semiconductor film surface to make it liquid repellent,
By dropping a composition mixed with a mask material, a mask is formed in the liquid-repellent region of the semiconductor film,
Patterning the semiconductor film using the mask;
Forming a gate insulating film covering the semiconductor film;
Plasma treatment is performed on the gate insulating film to make it liquid repellent,
A method for manufacturing a thin film transistor, wherein a gate electrode is formed in the liquid-repellent region of the gate insulating film by dropping a composition mixed with a gate electrode material.
ソース電極及びドレイン電極の材料が混入された組成物を滴下することにより前記下地膜の前記撥液性の領域に、ソース電極及びドレイン電極を形成し、
前記ソース電極及びドレイン電極上に半導体膜を形成し、
前記半導体膜にプラズマ処理を行って撥液性とし、
マスク材料が混入された組成物を滴下することにより、前記半導体膜の前記撥液性の領域に、マスクを形成し、
前記マスクを用いて半導体膜をパターニングし、
前記半導体膜を覆ってゲート絶縁膜を形成し、
前記ゲート絶縁膜にプラズマ処理を行って撥液性とし、
ゲート電極材料が混入された組成物を滴下することにより、前記ゲート絶縁膜の前記撥液性の領域にゲート電極を形成する
ことを特徴とする薄膜トランジスタの作製方法。 Plasma treatment is applied to the base film to make it liquid repellent,
A source electrode and a drain electrode are formed in the liquid-repellent region of the base film by dropping a composition mixed with a material for the source electrode and the drain electrode,
Forming a semiconductor film on the source and drain electrodes;
Plasma treatment is performed on the semiconductor film to make it liquid repellent,
By dropping a composition mixed with a mask material, a mask is formed in the liquid-repellent region of the semiconductor film,
Patterning the semiconductor film using the mask;
Forming a gate insulating film covering the semiconductor film;
Plasma treatment is performed on the gate insulating film to make it liquid repellent,
A method for manufacturing a thin film transistor, wherein a gate electrode is formed in the liquid-repellent region of the gate insulating film by dropping a composition mixed with a gate electrode material.
ゲート電極材料が混入された組成物を滴下することにより、前記テフロン膜上にゲート電極を形成し、
前記ゲート電極を焼成するために加熱処理を行い、前記加熱処理により前記テフロンは除去される
ことを特徴とする薄膜トランジスタの作製方法。 Forming a Teflon film,
By dropping a composition mixed with a gate electrode material, a gate electrode is formed on the Teflon film,
A method for manufacturing a thin film transistor, wherein a heat treatment is performed to fire the gate electrode, and the Teflon is removed by the heat treatment.
ゲート電極材料が混入された組成物を滴下することにより、前記第1のテフロン膜上にゲート電極を形成し、
前記ゲート電極を焼成するために加熱処理を行い、前記加熱処理により前記第1のテフロン膜は除去され、
前記ゲート電極を覆ってゲート絶縁膜を形成し、
前記ゲート電極上に半導体膜を形成し、
前記半導体膜上に一導電型を有する半導体膜を形成し、
前記一導電型を有する半導体膜及び前記ゲート絶縁膜上に第2のテフロン膜を形成し、
ソース電極及びドレイン電極の材料が混入された組成物を滴下することにより、前記一導電型を有する半導体膜及び前記ゲート絶縁膜上に、ソース電極及びドレイン電極を形成し、
前記ソース電極及びドレイン電極を焼成するために加熱処理を行い、前記加熱処理により前記第2のテフロン膜は除去される
ことを特徴とする薄膜トランジスタの作製方法。 Forming a first Teflon film;
A gate electrode is formed on the first Teflon film by dropping a composition mixed with a gate electrode material,
Heat treatment is performed to fire the gate electrode, and the first Teflon film is removed by the heat treatment,
Forming a gate insulating film covering the gate electrode;
Forming a semiconductor film on the gate electrode;
Forming a semiconductor film having one conductivity type on the semiconductor film;
Forming a second Teflon film on the semiconductor film having one conductivity type and the gate insulating film;
A source electrode and a drain electrode are formed on the semiconductor film having one conductivity type and the gate insulating film by dropping a composition mixed with a material for the source electrode and the drain electrode.
A method for manufacturing a thin film transistor, wherein a heat treatment is performed to fire the source electrode and the drain electrode, and the second Teflon film is removed by the heat treatment.
前記薄膜トランジスタ上に層間絶縁膜を形成し、
前記層間絶縁膜に開口部を形成し、
前記開口部が形成された層間絶縁膜にプラズマ処理を行って、前記開口部及び前記層間絶縁膜の表面を撥液性とし、
配線材料が混入された組成物を滴下することにより、前記開口部を介して前記薄膜トランジスタのソース電極又はドレイン電極と接続する配線を形成する
ことを特徴とする薄膜トランジスタの作製方法。 In any one of Claims 8 thru | or 19.
Forming an interlayer insulating film on the thin film transistor;
Forming an opening in the interlayer insulating film;
Plasma treatment is performed on the interlayer insulating film in which the opening is formed to make the surface of the opening and the interlayer insulating film liquid repellent,
A method for manufacturing a thin film transistor, wherein a wiring connected to a source electrode or a drain electrode of the thin film transistor through the opening is formed by dropping a composition mixed with a wiring material.
前記薄膜トランジスタ上に層間絶縁膜を形成し、
前記層間絶縁膜にプラズマ処理を行って、前記層間絶縁膜の表面を撥液性とし、
前記層間絶縁膜に開口部を形成し、
配線材料が混入された組成物を滴下することにより、前記開口部を介して前記薄膜トランジスタのソース電極又はドレイン電極と接続する配線を形成する薄膜トランジスタの作製方法であって、
前記開口部は前記層間絶縁膜の表面より撥液性が低いことを特徴とする薄膜トランジスタの作製方法。 In any one of Claims 8 thru | or 19.
Forming an interlayer insulating film on the thin film transistor;
Plasma treatment is performed on the interlayer insulating film to make the surface of the interlayer insulating film liquid repellent,
Forming an opening in the interlayer insulating film;
A method for manufacturing a thin film transistor, in which a wiring connected to a source electrode or a drain electrode of the thin film transistor is formed through the opening by dropping a composition mixed with a wiring material,
The method for manufacturing a thin film transistor, wherein the opening has lower liquid repellency than the surface of the interlayer insulating film.
インクジェット法を用いて前記組成物を滴下することを特徴とする配線の作製方法。 A method according to any one of claims 8 to 21.
A method for manufacturing a wiring, wherein the composition is dropped using an inkjet method.
前記電極へ電圧を印加するための電源と、を有するプラズマ処理装置を用いて、
前記電極と対向する位置に被処理物を配置し、
前記電源へパルス状の電圧を印加することによりプラズマを発生させ、前記被処理物の表面にCF2結合を形成し、
配線材料が混入された組成物を滴下することにより、前記CF2結合が形成された面に、配線を形成する
ことを特徴とする液滴吐出方法。 An electrode provided with a dielectric;
Using a plasma processing apparatus having a power source for applying a voltage to the electrode,
An object to be processed is disposed at a position facing the electrode,
Plasma is generated by applying a pulsed voltage to the power source, and a CF 2 bond is formed on the surface of the object to be processed.
A droplet discharge method comprising: forming a wiring on a surface on which the CF 2 bond is formed by dropping a composition mixed with a wiring material.
前記電極へ電圧を印加するための電源と、を有するプラズマ処理装置を用いて、
大気圧又は大気圧近傍において、前記電極と対向する位置に被処理物を配置し、
前記電源へパルス状の電圧を印加することによりプラズマを発生させ、前記被処理物の表面にCF2結合を形成し、
配線材料が混入された組成物を滴下することにより、前記CF2結合が形成された面に、配線を形成する
ことを特徴とする液滴吐出方法。 An electrode provided with a dielectric;
Using a plasma processing apparatus having a power source for applying a voltage to the electrode,
Arranging the object to be processed at a position facing the electrode at or near atmospheric pressure,
Plasma is generated by applying a pulsed voltage to the power source, and a CF 2 bond is formed on the surface of the object to be processed.
A droplet discharge method comprising: forming a wiring on a surface on which the CF 2 bond is formed by dropping a composition mixed with a wiring material.
前記電極へ電圧を印加するための電源と、を有するプラズマ処理装置を用いて、
大気圧又は大気圧近傍において、前記電極と対向する位置に被処理物を配置し、
前記電源へパルス状の電圧を印加することによりプラズマ密度が1×1010〜1×1014m-3となるプラズマを発生させ、前記被処理物の表面にCF2結合を形成し、
配線材料が混入された組成物を滴下することにより、前記CF2結合が形成された面に、配線を形成する
ことを特徴とする液滴吐出方法。 An electrode provided with a dielectric;
Using a plasma processing apparatus having a power source for applying a voltage to the electrode,
Arranging the object to be processed at a position facing the electrode at or near atmospheric pressure,
By applying a pulsed voltage to the power source, plasma having a plasma density of 1 × 10 10 to 1 × 10 14 m −3 is generated, and CF 2 bonds are formed on the surface of the object to be processed.
A droplet discharge method comprising: forming a wiring on a surface on which the CF 2 bond is formed by dropping a composition mixed with a wiring material.
前記誘電体はテフロンからなることを特徴とする液滴吐出方法。 Any one of claims 23 to 25,
A method of discharging a droplet, wherein the dielectric is made of Teflon.
インクジェット法を用いて前記組成物を滴下することを特徴とする液滴吐出方法。
A device according to any one of claims 23 to 26.
A droplet discharge method, wherein the composition is dropped using an inkjet method.