JP2005111740A - Dry lacquer tone pencil - Google Patents

Dry lacquer tone pencil Download PDF

Info

Publication number
JP2005111740A
JP2005111740A JP2003346600A JP2003346600A JP2005111740A JP 2005111740 A JP2005111740 A JP 2005111740A JP 2003346600 A JP2003346600 A JP 2003346600A JP 2003346600 A JP2003346600 A JP 2003346600A JP 2005111740 A JP2005111740 A JP 2005111740A
Authority
JP
Japan
Prior art keywords
pencil
coating film
paint
polymer particles
dry
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
JP2003346600A
Other languages
Japanese (ja)
Inventor
Shuichi Nakano
修市 中野
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nakano KK
Original Assignee
Nakano KK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nakano KK filed Critical Nakano KK
Priority to JP2003346600A priority Critical patent/JP2005111740A/en
Publication of JP2005111740A publication Critical patent/JP2005111740A/en
Withdrawn legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide a pencil, on the surface of which a finely uneven coating film is formed, which has a dry lacquer tone external appearance and effects such as anti-skid, excellent gripping feeling, marbelizing of coating surface, anti-scratching of coating surface (protective film) or the like. <P>SOLUTION: This dry lacquer tone pencil has a coating film, which is formed by coating polymeric particle-containing paint so as to form finely uneven coating film on its surfaces. As a result, as the polymeric particle, an amidic polymeric particle and/or acrylic polymeric particle can be used suitably. In this case, the polymeric particle passing through the sieve of 50-500 mesh can be used suitably. <P>COPYRIGHT: (C)2005,JPO&NCIPI

Description

この発明は、乾漆調外観を有する鉛筆に関するものである。更に詳しくは、表面に微細な凹凸塗膜を有する乾漆調の外観をもつ鉛筆に関するものである。   The present invention relates to a pencil having a dry lacquer-like appearance. More specifically, the present invention relates to a pencil having a dry lacquer-like appearance having a fine uneven coating film on the surface.

漆を、例えば、ガラス上に薄く塗布し、漆を乾燥させた後、漆の塗膜を剥離し、粉砕し、粉砕した乾燥漆の塗膜を再び漆に混入し塗布する乾漆の技術が知られている。乾漆において、突起の高さを揃えた、微細で、かつ均一な凹凸塗膜が形成され、滑り止め、塗膜面の多彩化、塗膜面の傷防止(保護膜)等の効果をもたらすものである。   For example, the technology of dry lacquer is known in which lacquer is applied thinly on glass and dried, and then the lacquer coating film is peeled off, crushed, and the dried lacquer coating film is mixed and applied to the lacquer again. It has been. In dry lacquer, a fine and uniform concavo-convex coating with the same height of protrusions is formed, providing effects such as anti-slip, diversification of coating surface, and prevention of scratches (protection film) on coating surface It is.

このような乾漆の効果を奏する塗膜を鉛筆に形成せしめようとするのが本発明の目的である。鉛筆にある種の特徴ある塗膜を形成することは従来から知られているが、突起を有し、微細な凹凸塗膜であって、滑り止め、塗膜面の多彩化、塗膜面の傷防止(保護膜)等の効果をもたらす塗膜を鉛筆に形成したものは知られていない。   It is an object of the present invention to try to form a coating film having such a dry lacquer effect on a pencil. It has been conventionally known to form a coating film with a certain characteristic on a pencil, but it has protrusions and is a fine uneven coating film that prevents slippage, diversifies the coating surface, There is no known one that forms a coating film on a pencil that provides effects such as scratch prevention (protective film).

即ち、柱体に色の異なる漆を多層に塗布して塗膜を形成せしめた漆塗り鉛筆が実開平2−126892号公報に記載され、鉛筆の端部に紫外線硬化塗料をもって形成された丸味を持った塗膜を形成した鉛筆が特開平5−8588号公報に記載され、木材製の鉛筆軸の表面を水性塗料で仕上げる鉛筆軸の水性塗料仕上げ方法が特開平9−193589号公報に記載され、また、巻紙の条片を剥いでいくに従い、剥がれた条片の内側に施された絵柄や文字が現れる紙巻き鉛筆が特開2002−17441号公報に記載されている。しかしながら、ポリマー粒子を含む塗料を塗布して塗膜を形成せしめた鉛筆については、未だ知られていない。   That is, a lacquered pencil in which lacquers of different colors are applied in multiple layers to a pillar to form a coating film is described in Japanese Utility Model Laid-Open No. 2-126892, and the roundness formed with an ultraviolet curable paint at the end of the pencil is described. A pencil on which a coated film is formed is described in JP-A-5-8588, and a pencil shaft aqueous paint finishing method for finishing the surface of a wood pencil shaft with an aqueous paint is described in JP-A-9-193589. Also, Japanese Patent Application Laid-Open No. 2002-17441 discloses a paper-wound pencil in which patterns and characters appearing on the inner side of the peeled strip as the strip of the rolled paper is peeled off. However, a pencil that has been coated with a coating containing polymer particles to form a coating film is not yet known.

特開2002−17441号公報Japanese Patent Laid-Open No. 2002-17441 特開平9−193589号公報JP-A-9-193589 特開平5−8588号公報Japanese Patent Laid-Open No. 5-8588 実開平2−126892号公報Japanese Utility Model Publication No. 1-212692

本発明は、乾燥した漆の塗膜を粉砕したものを使用することなく、鉛筆の表面に微細な凹凸塗膜を形成せしめた、乾漆調の外観を有する鉛筆を提供しようとするものである。即ち、突起を有し、微細な凹凸塗膜であって、滑り止め、塗膜面の多彩化、塗膜面の傷防止(保護膜)等の効果をもたらす塗膜を形成した乾漆調の鉛筆を提供しようとするものである。   The present invention intends to provide a pencil having a dry lacquer-like appearance in which a fine uneven coating film is formed on the surface of a pencil without using a crushed dry lacquer coating film. In other words, a dry lacquer-like pencil that has protrusions and is a fine uneven coating film that has effects such as anti-slip, diversification of the coating surface, and prevention of scratches on the coating surface (protective film). Is to provide.

本発明の要旨は、表面に微細な凹凸塗膜を有することを特徴とする乾漆調鉛筆である。より具体的には、ポリマー粒子を含む塗料を塗布して形成せしめた表面に微細な凹凸塗膜を有する乾漆調鉛筆である。ポリマー粒子としては、アミド系ポリマー粒子及び/又はアクリル系ポリマー粒子を好適に使用することができる。また、ポリマー粒子は50〜500メッシュ通過粒子が好ましい。   The gist of the present invention is a dry lacquered pencil characterized by having a fine uneven coating film on the surface. More specifically, it is a dry lacquer-like pencil having a fine uneven coating film on the surface formed by applying a coating containing polymer particles. As the polymer particles, amide polymer particles and / or acrylic polymer particles can be suitably used. The polymer particles are preferably 50-500 mesh passing particles.

塗料としては、エポキシ系塗料、ウレタン系塗料、アクリル系塗料から選択される少なくとも1種が好適に使用できる。そして、ポリマー粒子の量は塗料の量100重量部に対して10〜30重量部であることが好ましい。また、塗膜は引き抜き塗装方法により形成することができる。表面に微細な凹凸塗膜を有する乾漆調の鉛筆は、通常の形状を有するものであってもよいし、その一端が先細になった形状のものでもよい。   As the paint, at least one selected from an epoxy paint, a urethane paint, and an acrylic paint can be suitably used. The amount of the polymer particles is preferably 10 to 30 parts by weight with respect to 100 parts by weight of the paint. Further, the coating film can be formed by a drawing coating method. The dry lacquer-like pencil having a fine uneven coating film on the surface may have a normal shape, or may have a shape in which one end is tapered.

本発明は、乾燥した漆の塗膜を粉砕したものを漆に混合して塗布して形成せしめた乾漆膜の外観、所謂乾漆調外観を有する鉛筆を提供することを可能にする効果がある。即ち、突起を有し、微細な凹凸塗膜を有し、滑り止め、持ったときにすぐれた感触、塗膜面の多彩化、塗膜面の傷防止(保護膜)等の効果をもたらす。特に、鉛筆の表面に凹凸があるので、手に持ったときに滑りにくいという特徴があるとともにすぐれた感触を楽しむことができる。   INDUSTRIAL APPLICABILITY The present invention has an effect that it is possible to provide a pencil having a so-called dry lacquer-like appearance, which is an appearance of a dry lacquer film formed by mixing and applying a pulverized dry lacquer coating film. That is, it has protrusions, a fine uneven coating film, anti-slip, excellent feel when held, diversification of the coating film surface, scratch prevention (protective film) of the coating film surface, and the like. In particular, since the surface of the pencil has irregularities, it has a feature that it is difficult to slip when it is held in the hand, and an excellent feel can be enjoyed.

以下本発明を実施形態に基づいて説明する。まず、溶剤に溶解した塗料にポリマー粒子を混合する。この際使用する塗料は、市販のものでよい。なかでも、エポキシ系塗料、ポリウレタン系塗料、アクリル系塗料が好適使用することができる。塗料は、芳香族系溶剤やケトン系溶剤に樹脂を溶解したものである。この際の樹脂の量は、概ね20〜85重量%である。このように樹脂を溶解した塗料にポリマー粒子を混合する。混合するポリマー粒子の量は、塗料100重量部に対して10〜30重量部である。   Hereinafter, the present invention will be described based on embodiments. First, polymer particles are mixed in a paint dissolved in a solvent. The paint used at this time may be a commercially available one. Among these, epoxy paints, polyurethane paints, and acrylic paints can be preferably used. The paint is obtained by dissolving a resin in an aromatic solvent or a ketone solvent. The amount of resin at this time is approximately 20 to 85% by weight. The polymer particles are mixed with the paint in which the resin is dissolved in this way. The amount of polymer particles to be mixed is 10 to 30 parts by weight with respect to 100 parts by weight of the paint.

ポリマー粒子は、任意に選択されたポリマー粒子を使用することができる。なかでも、ポリアミド系ポリマー、アクリル系ポリマー粒子が好適に使用できる。ポリマー粒子は、乳化重合、懸濁重合、沈殿重合等の手法で重合したポリマー粉末を適宜篩い分けすることによって得ることができるし、また、重合したポリマーを溶剤に溶解後、再沈させることによっても得ることができる。ポリマー粒子は、50〜500メッシュ通過粒子であることが好ましい。更に好ましくは、80〜200メッシュ通過粒子である。それは、ポリマー粒子の粒子径が大きいと(メッシュが小さい)突起が大きくなり鉛筆を手に持ったときの感触が悪くなり、また、ポリマー粒子の粒子径が小さいと(メッシュが大きい)突起が小さくなり滑り止め、塗膜面の多彩化、塗膜面の傷防止(保護膜)、手に持ったときの感触等の効果が小さくなるからである。   As the polymer particles, arbitrarily selected polymer particles can be used. Of these, polyamide polymer and acrylic polymer particles can be preferably used. The polymer particles can be obtained by appropriately sieving polymer powder polymerized by techniques such as emulsion polymerization, suspension polymerization, precipitation polymerization, etc., and by re-precipitation after dissolving the polymerized polymer in a solvent. Can also be obtained. The polymer particles are preferably 50-500 mesh passing particles. More preferably, it is 80-200 mesh passing particle. That is, if the particle size of the polymer particles is large (the mesh is small), the protrusion becomes large and the feel when holding a pencil is worsened. If the particle size of the polymer particle is small (the mesh is large), the protrusion is small. This is because the effects of anti-slip, diversification of the paint film surface, prevention of scratches on the paint film surface (protective film), and feel when held in the hand are reduced.

ポリマー粒子を混合した塗料を鉛筆に塗布して、突起を有し、微細な凹凸塗膜を形成せしめる。該ポリマー粒子を混合した塗料を鉛筆に塗布するに際しては、引き抜き塗装の手法を適用する。引き抜き塗装の原理を示したのが図1である。ポリマー粒子を含む塗料3の中を鉛筆1を通過させ、ゴム板2からなる小孔4から鉛筆1を引き抜くのである。引き抜いた後、鉛筆1の表面には塗膜6が形成される。引き抜き速度が大きいと塗膜の厚みは薄くなり、引き抜き速度が小さいと塗膜の厚みは厚くなる。   A paint in which polymer particles are mixed is applied to a pencil to form a fine uneven film having protrusions. When applying the paint mixed with the polymer particles to the pencil, a drawing paint technique is applied. FIG. 1 shows the principle of drawing paint. The pencil 1 is passed through the paint 3 containing polymer particles, and the pencil 1 is pulled out from the small hole 4 made of the rubber plate 2. After drawing, a coating film 6 is formed on the surface of the pencil 1. When the drawing speed is high, the thickness of the coating film becomes thin, and when the drawing speed is low, the thickness of the coating film becomes thick.

引き抜き塗装には、複数の鉛筆を連続して塗装する方法と鉛筆1本ずつを塗装する方法がある。前者においては、図2に示したように、ポリマー粒子を含む塗料3を入れた容器5にその両端に鉛筆1が入る入り口と鉛筆が出る出口にゴム板2、2’からなる小孔4、4’が設けられている。複数の鉛筆1、1’、1’’は、連続して塗小孔4’から料容器内に挿入され、小孔4から引き抜かれる。引き抜かれた鉛筆1の表面には、塗膜6、6’が形成される。   There are two methods of drawing painting: a method of painting a plurality of pencils continuously and a method of painting one pencil at a time. In the former, as shown in FIG. 2, a small hole 4 made of rubber plates 2 and 2 'is provided at the entrance where the pencil 1 enters the container 5 containing the paint 3 containing polymer particles and at the exit where the pencil exits. 4 'is provided. The plurality of pencils 1, 1 ′, 1 ″ are continuously inserted into the material container from the small coating holes 4 ′ and pulled out from the small holes 4. Coating films 6 and 6 ′ are formed on the surface of the drawn pencil 1.

後者の方法では、ポリマー粒子を含む塗料3を入れた容器5の一端にゴム板2からなる小孔4が設けられている。図3に示したように、小孔4から鉛筆1を挿入し、その後引き抜くのである。引き抜いた後には、鉛筆の表面に塗膜が形成されている。この場合、鉛筆1を小孔に挿入するために、鉛筆1の挿入側の先は先細としておくのがよい。   In the latter method, a small hole 4 made of a rubber plate 2 is provided at one end of a container 5 containing a paint 3 containing polymer particles. As shown in FIG. 3, the pencil 1 is inserted from the small hole 4 and then pulled out. After drawing, a coating film is formed on the surface of the pencil. In this case, in order to insert the pencil 1 into the small hole, the tip of the insertion side of the pencil 1 is preferably tapered.

塗装された鉛筆の断面を示したのが図5である。通常の鉛筆においては、塗膜には凹凸を有しない平らなものとなっている。この状態を模式的に図4に示した。鉛筆1の表面には平らな塗膜が形成されている。塗膜は、下塗13、中塗12及び上塗11からなっている。勿論、これは例示的に示したもので、塗装膜が一膜の場合もあれば二膜の場合もある。これに対して、本発明の鉛筆1の表面にはポリマー粒子9に基づく凹凸が形成されている。塗膜は、下塗7、中塗8及び上塗10からなっているが、これに限定されるものではない。   FIG. 5 shows a cross-section of the painted pencil. In a normal pencil, the coating film is flat without unevenness. This state is schematically shown in FIG. A flat coating film is formed on the surface of the pencil 1. The coating film is composed of a base coat 13, an intermediate coat 12 and a top coat 11. Of course, this is shown by way of example, and there may be a case where the coating film is a single film or a case where there are two films. On the other hand, the unevenness | corrugation based on the polymer particle 9 is formed in the surface of the pencil 1 of this invention. Although the coating film consists of the undercoat 7, the intermediate coat 8, and the top coat 10, it is not limited to this.

本発明を更に具体的な例に基づき説明する。エポキシ系塗料の70重量%のキシレン溶液100重量部にアクリル系ポリマーの200メッシュ通過粒子20重量部を混合した。図2に示すように、このポリマー粒子を含む塗料3を容器5に入れ、連続的に鉛筆1を小孔4’から挿入し、小孔4から引き抜き鉛筆1を塗装した。塗装した鉛筆は、70℃の温度で1時間15分熱処理した。この熱処理温度は、一般的には65ないし80℃であり、処理時間は1時間ないし105時間程度である。熱処理により、鉛筆の表面に堅牢な凹凸のある塗膜が形成される。鉛筆の表面は凹凸のある塗膜で被覆されるので、手で持ったときに、滑りにくい、持った感触がよい等の特徴がある。その他、塗膜面の多彩化が可能であり、塗膜面の傷防止(保護膜)等の効果ももたらす。下塗や中塗の過程で、種々の図柄や文字、更には色調の異なる図柄や文字を描いておき、ポリマー粒子を含む透明な塗料で上塗りして仕上げることも可能である。   The present invention will be further described based on specific examples. 20 parts by weight of 200-mesh particles of acrylic polymer were mixed with 100 parts by weight of a 70% by weight xylene solution of an epoxy paint. As shown in FIG. 2, the paint 3 containing the polymer particles was put in a container 5, and the pencil 1 was continuously inserted from the small hole 4 ′, and the pencil 1 was drawn out from the small hole 4 and painted. The painted pencil was heat-treated at a temperature of 70 ° C. for 1 hour and 15 minutes. The heat treatment temperature is generally 65 to 80 ° C., and the treatment time is about 1 to 105 hours. By the heat treatment, a solid uneven film is formed on the surface of the pencil. Since the surface of the pencil is coated with an uneven coating film, it has features such as being hard to slip and having a good feel when held by hand. In addition, the coating surface can be diversified, and effects such as prevention of scratches on the coating surface (protective film) can be brought about. In the process of undercoating and intermediate coating, it is possible to draw various designs and characters, and also designs and characters with different color tones, and finish them by overcoating with a transparent paint containing polymer particles.

本発明は、表面に微細な凹凸塗膜を有することを特徴とする乾漆調鉛筆であり、より具体的には、ポリマー粒子を含む塗料を塗布して形成せしめた表面に微細な凹凸塗膜を有する乾漆調鉛筆である。表面に微細な凹凸塗膜を有するので、乾漆調の外観を有し、手に持ったとき滑り止め、すぐれた感触をもたらし、更に、塗膜面の多彩化、塗膜面の傷防止(保護膜)等の効果をもたらす。鉛筆を製造する者にとっては鉛筆の多彩化、実用上のみならずデザイン的にも多様化を促し、使用する者の両者にとっては使い勝手の良さとともに楽しめる鉛筆が提供されるという特徴をもたらす。   The present invention is a dry lacquer-like pencil characterized by having a fine concavo-convex coating on the surface, and more specifically, a fine concavo-convex coating on the surface formed by applying a paint containing polymer particles. It is a dry lacquer-like pencil. Since it has a fine uneven film on the surface, it has a dry lacquer-like appearance, and when it is held in your hand, it provides a non-slip feel and a good feel. Effect). For those who manufacture pencils, the diversification of pencils is promoted not only for practical use but also for design. For both users, the pencils that can be enjoyed with ease of use are provided.

引き抜き塗装の原理を示す図である。It is a figure which shows the principle of drawing-out painting. 連続引き抜き塗装の原理を示す図である。It is a figure which shows the principle of continuous drawing. 単独引き抜き塗装の原理を示す図である。It is a figure which shows the principle of independent drawing. 通常の塗装断面を示す図である。It is a figure which shows a normal coating cross section. 凹凸を有する本発明の塗装断面を示す図である。It is a figure which shows the coating cross section of this invention which has an unevenness | corrugation.

符号の説明Explanation of symbols

1、1’、1’’ 鉛筆
2、2’ ゴム板
3 塗料
4、4’ 小孔
5 容器
6 塗膜
7、13 下塗
8、12 中塗
9 ポリマー粒子
10、11 上塗
15 芯





1, 1 ', 1''pencil
2, 2 'rubber plate
3 Paint
4, 4 'small hole
5 containers
6 Coating film
7, 13 Undercoat
8, 12 Middle coat
9 Polymer particles
10, 11 Top coat
15 cores





Claims (8)

表面に微細な凹凸塗膜を有することを特徴とする乾漆調鉛筆。   A dry lacquered pencil characterized by having a fine uneven coating film on the surface. ポリマー粒子を含む塗料を塗布して形成せしめた塗膜を有することを特徴とする請求項1に記載の乾漆調鉛筆。   The dry lacquer-like pencil according to claim 1, which has a coating film formed by applying a paint containing polymer particles. 前記ポリマー粒子がアミド系ポリマー粒子及び/又はアクリル系ポリマー粒子であることを特徴とする請求項2に記載の乾漆調鉛筆。   The dry lacquer-like pencil according to claim 2, wherein the polymer particles are amide polymer particles and / or acrylic polymer particles. 前記塗料がエポキシ系塗料、ウレタン系塗料、アクリル系塗料から選択される少なくとも1種であることを特徴とする請求項2又は請求項3に記載の乾漆調鉛筆。   The dry lacquered pencil according to claim 2 or 3, wherein the paint is at least one selected from an epoxy paint, a urethane paint, and an acrylic paint. 前記ポリマー粒子が50〜500メッシュ通過粒子であることを特徴とする請求項2から請求項4のいずれかに記載の乾漆調鉛筆。   The dry lacquered pencil according to any one of claims 2 to 4, wherein the polymer particles are 50-500 mesh passing particles. 前記ポリマー粒子の量が塗料の量100重量部に対して10〜30重量部であることを特徴とする請求項2から請求項5のいずれかに記載の乾漆調鉛筆。   The dry lacquered pencil according to any one of claims 2 to 5, wherein the amount of the polymer particles is 10 to 30 parts by weight with respect to 100 parts by weight of the paint. 前記塗膜が引き抜き塗装方法により形成されたことを特徴とする請求項2から請求項7のいずれかに記載の乾漆調鉛筆。   The dry lacquer-like pencil according to any one of claims 2 to 7, wherein the coating film is formed by a drawing coating method. 鉛筆の一端を先細にして引き抜き塗装方法により塗膜を形成したたことを特徴とする請求項7に記載の乾漆調鉛筆。
The dry lacquer-like pencil according to claim 7, wherein one end of the pencil is tapered and a coating film is formed by a drawing method.
JP2003346600A 2003-10-06 2003-10-06 Dry lacquer tone pencil Withdrawn JP2005111740A (en)