JP2005104824A - Optical glass with low refractive index - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide an SiO<SB>2</SB>-R<SB>2</SB>O-RO-based optical glass used for various optical members such as an interchangeable lens and the like having such optical constants as a refractive index (nd) of 1.49-1.54 and an Abbe's number (νd) of 55-65. <P>SOLUTION: The optical glass comprises by mass% >65-75% SiO<SB>2</SB>, 15-25% R<SB>2</SB>O (wherein, R is Li, Na, K and Cs; but Li<SB>2</SB>O is 0.1-5.0%; Na<SB>2</SB>O is 1.0-10.0%; K<SB>2</SB>O is 5.0-20.0%; Cs<SB>2</SB>O is 0-5.0%), 0.5-10% R'O (wherein, R' is Mg, Ca, Sr and Ba; but MgO, CaO, SrO and BaO are 0-10% respectively), furthermore, 0-6.0% B<SB>2</SB>O<SB>3</SB>, 0-<1.0% Al<SB>2</SB>O<SB>3</SB>, 0-<3.0% ZnO, 0-<2.0% TiO<SB>2</SB>, 0-2.0% ZrO<SB>2</SB>, 0-3.0% WO<SB>3</SB>, 0-2.0% Sb<SB>2</SB>O<SB>3</SB>and 0-2% F in fluorides by which a part or all of one or more kinds of above oxides are displaced. <P>COPYRIGHT: (C)2005,JPO&NCIPI

Description

The present invention relates to SiO ₂ —R ₂ used for various optical members such as an interchangeable lens having a refractive index (nd) of 1.49 to 1.54 and an Abbe number (νd) of 55 to 65. The present invention relates to an O-RO optical glass. More specifically, ion exchange (for the purpose of refractive index distribution formation and chemical strengthening) and glass surface modification (except for glass coating treatment with a functional film such as an antireflection film) are not performed. The present invention relates to an optical glass used for an optical member.

In recent years, from the viewpoint of global environmental conservation, there is an increasing tendency to exclude environmental pollutants from products. In the optical glass field, it was manufactured using components with high environmental loads such as PbO and As ₂ O _{3 in the} old days, but it has been gradually replaced with optical glasses that do not contain these environmental pollutants. However, some optical glasses still contain an environmental pollutant component, and further environmental load reduction is desired.

As an SiO ₂ —R ₂ O—RO optical glass having an optical constant in the range of refractive index (nd) of 1.49 to 1.54 and Abbe number (νd) of 55 to 65, JP-A-3-183638 is disclosed. And optical glass mainly for the purpose of sealing stainless steel such as JP-A-4-224132, optical glass without solarization such as JP-A-8-34633, and lead-free crown glass disclosed in JP-A-10-167753. ing.

Glasses containing a relatively large amount of Al ₂ O ₃ as disclosed in JP-A-3-183638 and JP-A-4-224132 are excellent in chemical durability but poor in defoaming properties, and are glass at high temperatures. Dissolution is necessary, which is undesirable due to concerns about an increase in energy consumption and deterioration in production efficiency. Further, if the chemical durability is excessively pursued, there is a concern that the workability such as polishing is deteriorated and the manufacturing cost is increased.

In addition, JP-A-8-34633 discloses an optical glass containing SnO and SnO ₂ components as essential components for preventing solarization. However, SnO and SnO ₂ components are used as a platinum member and an alloy of a melting apparatus during glass melting. It often becomes a problem to have a great adverse effect on the melting equipment, such as causing glass leakage.

The lead-free crown glass disclosed in JP-A-10-167753 does not contain PbO or As ₂ O ₃ components, but contains a ZnO component. The ZnO component elutes into the water (as Zn ions) through grinding / polishing waste (sludge) containing moisture generated in the glass grinding / polishing process, so draining without proper treatment will cause water pollution, so be careful with wastewater treatment. Cost. From the viewpoint of environmental protection and reduction of manufacturing costs, optical glass containing as little environmental pollutants as possible is required.

Furthermore, Japanese Patent Laid-Open No. 9-255253 describes lead-free crown flint glass that does not contain PbO or As ₂ O ₃ components. However, in order to increase the content of TiO ₂ and Nb ₂ O ₅ , a desired νd is set. It is difficult to realize.

JP-A-48-85613 describes a glass for glasses which does not contain PbO and As ₂ O ₃ components, but this requires chemical strengthening and contains a relatively large amount of Al ₂ O _3. Glass is excellent in chemical durability but requires glass melting at a high temperature, which is undesirable because of an increase in energy consumption and deterioration in production efficiency. Further, if the chemical durability is excessively pursued, there is a concern that the workability such as polishing is deteriorated and the manufacturing cost is increased.

Further, in hot working such as reheat press, pressing to a desired shape by lower temperature heating leads to saving of energy usage, so that the environmental load can be reduced as the glass softening temperature is lower. In general, a glass containing a large amount of SiO ₂ has a high softening temperature, and thus must be reheat-pressed at a high temperature.
JP-A-3-183638 JP-A-4-224132 JP-A-8-34633 Japanese Patent Laid-Open No. 10-167753 JP-A-9-255253 JP-A-48-85613

An object of the present invention is to provide an SiO ₂ —R ₂ O—RO based optical glass having an optical constant in the range of refractive index (nd) of 1.49 to 1.54 and Abbe number (νd) of 55 to 65, The purpose is to provide an environmental load with low manufacturing costs.

The present inventor has conducted extensive studies to achieve the above-mentioned goal, and as a result, in the SiO ₂ —R ₂ O—RO optical glass having a specific composition, an environmental pollutant such as PbO or As ₂ O _3. The present inventors have found that a desired optical constant can be realized without using a glass, and a desired optical glass can be supplied at a low production cost through a glass raw material, a glass melting step and a processing step.

The first configuration of the present invention has an optical constant in the range of refractive index (nd) 1.49 to 1.54, Abbe number (νd) 55 to 65,
SiO ₂ > 65 to 75%
R ₂ O (R is one or more selected from the group consisting of Li, Na, K and Cs)
15-25%
_As, Li 2 O 0.1 ~ 5.0%
Na ₂ O 1.0 ~ 10.0%
K ₂ O 5.0 ~ 20.0%, and Cs ₂ O 0 ~ 5.0%
And R′O (R ′ is one or more selected from the group consisting of Mg, Ca, Sr and Ba)
0.5 to 10%
MgO 0 to 10% and / or CaO 0 to 10% and / or SrO 0 to 10% and / or BaO 0 to 10%
_{Further, B 2 O 3 0 ~ 6.0} %
Al ₂ O ₃ 0 to <1.0% and / or ZnO 0 to <3.0% and / or TiO ₂ 0 to <2.0% and / or ZrO ₂ 0 to 2.0% and / or WO ₃ Each of 0 to 3.0% and / or Sb ₂ O ₃ 0 to 2.0% and a total amount of 0 to 2% of F in the fluoride in which part or all of one or more of the above oxides are substituted Glass containing components.

The second configuration of the present invention has an optical constant in the range of refractive index (nd) 1.50 to 1.53 and Abbe number (νd) 57 to 62, and is SiO ₂ 67 to 72% in mass%.
B ₂ O ₃ 0 to 6.0%
Al ₂ O ₃ 0 to <1.0% and / or R ₂ O (R is one or more selected from the group consisting of Li, Na, K and Cs)
20-25%
Li ₂ O 0.1-5.0%
Na ₂ O 1.0 ~ 10.0%
K ₂ O 10.0 ~ 20.0%, and Cs ₂ O 0 ~ 5.0%
R′O (R ′ is one or more selected from the group consisting of Mg, Ca, Sr and Ba)
0.5-5.0%
MgO 0 to 5.0% and / or CaO 0 to 5.0% and / or SrO 0 to 5.0% and / or BaO 0 to 5.0%
_{Further, B 2 O 3 0 ~ 6.0} %
Al ₂ O ₃₀ to <1.0% and / or TiO ₂ 0 to <2.0% and / or ZrO ₂ 0 to 2.0% and / or WO ₃ 0 to 3.0% and / or Sb ₂ O ₃ 0 ~ 2.0%
It is the glass containing each component of.

A third configuration of the present invention, ZnO, a glass according to the configuration 1 or 2 containing no PbO and _As 2 _{O 3.}

  As described above, according to the present invention, an optical glass having an optical constant in the range of refractive index (nd) of 1.49 to 1.54 and Abbe number (νd) of 55 to 65 is reduced in environmental load, And it was able to produce at a low manufacturing cost. Further, since the glass of the present invention has a low glass transition point (Tg), it can be reheat-pressed at a relatively low temperature, and can be used as a lens or the like without requiring grinding or polishing after press molding. It is also suitable as a precision press for glass that can be used as an optical element, that is, glass for so-called mold press.

As described above, the reason for limiting the composition range of each component is as follows. Hereinafter, each component is expressed in mass%.
SiO ₂ is an indispensable component as a glass-forming oxide, but if it is 65% or less, the chemical durability is insufficient and it is difficult to obtain a desired optical constant. On the other hand, if it exceeds 75%, the melting property of the glass deteriorates and a great amount of energy is consumed for melting the glass. Therefore, the content of SiO ₂ is preferably more than 65%, more preferably 66% or more, most preferably 67% as the lower limit, preferably 75%, more preferably 73%, most preferably 72%. Is contained as the upper limit.

B ₂ O ₃ has the effect of improving the meltability and stability of the glass, so it can be added as necessary. However, if it is contained in an amount of more than 6.0%, only the chemical durability is deteriorated and the glass is colored. Instead, it causes milky whiteness (phase separation and devitrification) due to reheating. Accordingly, the upper limit is preferably 6.0%, more preferably 5.8%, and most preferably 5.7%.

Al ₂ O ₃ has an effect of improving the chemical durability of the glass when contained in a trace amount, but excessive addition requires melting at a high temperature, so it is preferably less than 1.0%, and more preferably Is 0.8% or less, and most preferably contains 0.6% as an upper limit.

Li ₂ O is an essential component in the present invention because it has the effect of improving the meltability of the glass with a small amount of addition and lowering the softening temperature of the glass, and can reduce the production cost at the time of glass melting and reheat press processing. It is. If it is less than 0.1%, the effect is not sufficiently obtained, and if it exceeds 5%, the desired optical constant cannot be obtained, and the chemical durability is remarkably deteriorated.
Therefore, it is preferably 0.1%, more preferably 0.2%, most preferably 0.4% as the lower limit, preferably 5%, more preferably 4.5%, most preferably 4%. The

Na ₂ O is an essential component because it is effective in improving the meltability of the glass and adjusting the optical constant. However, if it is less than 1.0%, the effect is not sufficient. There is a tendency to significantly reduce durability. Therefore, it is preferably 1.0%, more preferably 1.5%, most preferably 2% as the lower limit, preferably 10%, more preferably 9.5%, most preferably 9%.

K ₂ O is an essential component because it has the same effect as Na ₂ O. However, if it is less than 5%, the effect is not sufficient, and if it exceeds 20%, devitrification resistance is deteriorated and chemical durability is poor. It causes deterioration. Therefore, in order to lower the viscosity at the time of glass melting, particularly while maintaining a desired optical constant, the lower limit is preferably 5%, more preferably 10%, and most preferably more than 12%, preferably 20%. More preferably, the upper limit is 19%, and most preferably 18%.

The Cs ₂ O component can be arbitrarily added because the same effect as the above-mentioned alkali metal oxide can be obtained. However, since the raw material price is relatively high, Preferably, the upper limit is 5%, more preferably 4%, and most preferably 3%.

By coexisting a plurality of alkali metal oxides, an effect of improving chemical durability due to the mixed alkali effect is obtained. Therefore, the total amount of the alkali metal oxides R ₂ O is preferably 15%, more preferably 20 %, Most preferably 21% is the lower limit, preferably 25%, more preferably 24.5%, and most preferably 24%. If the total amount of R ₂ O is less than 15%, the effect of improving the meltability of the alkali metal oxide cannot be obtained sufficiently, and glass melting at a high temperature is required, leading to an increase in energy consumption and a decrease in productivity. It is. On the other hand, if it exceeds 25%, the content of the SiO ₂ component is relatively lowered, so that the chemical durability of the glass is remarkably deteriorated.

Each alkaline earth metal oxide (R′O) component of MgO, CaO, SrO, and BaO can adjust optical constants (refractive index (nd) and Abbe number (νd)), so each component has 10%. Any upper limit can be added. In order to realize a glass with nd = 1.50 to 1.53, it is more preferable that each component is arbitrarily added with an upper limit of 5%. In addition, R'O component has the effect of suppressing migration / diffusion of alkali metal ions in the glass by adding an appropriate amount to the SiO ₂ -R ₂ O glass, thereby improving the chemical durability of the glass. Therefore, the total amount of R′O component must be 0.5% or more. However, when the total content of R′O components is 10% or more, the refractive index (nd) becomes too large, and a desired optical constant cannot be obtained. Therefore, the total amount of R′O is preferably 0.5%, more preferably 0.8%, most preferably 1%, and preferably 10%, more preferably 7%, most preferably 5%. The upper limit.

  The ZnO component has an effect of lowering the glass viscosity at the time of melting, improves the meltability of the glass, and also has an effect of lowering the softening temperature of the glass, so that less than 3.0% can be arbitrarily contained. Addition beyond that is not preferable because the desired optical constant cannot be realized. In order to dispel the concern that the ZnO component will elute into the waste water and cause water pollution, the upper limit is more preferably 2%, and most preferably it is not contained at all except unavoidable contamination.

Since the TiO ₂ component is useful for preventing solarization and adjusting the optical constant, it can optionally be added in an amount of less than 2.0%. Addition beyond that is not preferable because a desired optical constant cannot be realized. Therefore, in the present invention, it is preferably contained in an upper limit of less than 2.0%, more preferably 1.9%, and most preferably 1.8%.

The ZrO ₂ component can be arbitrarily added up to 2.0% because of the effect of adjusting the optical constant and improving the chemical durability. Is not preferable because it deteriorates. Therefore, in the present invention, it is preferably contained at an upper limit of 2.0%, more preferably 1.5%, and most preferably 1%.

Since the WO ₃ component can adjust the optical constant while improving the meltability of the glass, it can be arbitrarily added up to 3.0%, but if it is added more, the coloring of the glass becomes remarkable. Therefore, it is not preferable. Accordingly, in the present invention, the upper limit of the content is preferably 3.0%, more preferably 2.5%, and most preferably 2%.

As known as a defoaming component, the Sb ₂ O ₃ component is effective for clarifying and defoaming glass, so it can be added up to 2.0%. Further addition is not necessary because it does not contribute to fining and defoaming effects. Therefore, in the present invention, it is preferably contained at an upper limit of 2.0%, more preferably 1.5%, and most preferably 1%.

  Since the F component can reduce the viscosity of the glass and has a defoaming effect, the total of fluorides in which a part or all of one or more oxides of the above metal elements are substituted as F. Up to 2% can be added. However, when the F component is added, the F component volatilizes during the melting of the glass and may contaminate the atmosphere. Therefore, in this invention, Preferably it is 2.0%, More preferably, it is 1%, Most preferably, it does not contain at all.

Furthermore, in the present invention, lead and / or PbO and As ₂ O ₃ are preferably 0.01%, more preferably 0.005% as the upper limit, and most preferably, except for unavoidable contamination, do not contain at all. Is preferred.

SnO ₂ and SnO are preferably 0.01%, more preferably 0.005%, and most preferably none.

Each transition metal component such as V, Cr, Mn, Fe, Co, Ni, Cu, Ag, and Mo, excluding Ti, is colored even when contained in a small amount by combining them individually or in combination. In order to cause absorption at the wavelength of the optical glass, it is preferable that the optical glass using the wavelength in the visible region does not substantially contain. In addition, since each rare earth component except La and Gd may be colored alone or in combination, it tends to cause absorption at a specific wavelength in the visible range. In the optical glass to be used, it is preferable not to contain substantially.
Furthermore, each component of Pb, Th, Cd, Tl, As, Os, Te, Be, Se, Bi has tended to be refrained from being used as a harmful chemical material in recent years. In addition, since measures for environmental measures are required up to the disposal after commercialization, it is preferable that they are not substantially included when importance is placed on the environmental impact.

Next, examples of the present invention will be described.
Table 1 shows the compositions and preferred examples (Nos. 1 to 10) for obtaining optical glass having a refractive index (nd) of 1.49 to 1.54 and an Abbe number (νd) of 55 to 65. The refractive index (nd), Abbe number (νd) of the obtained glass, wavelength (T80%) at which 80% external transmittance of 10 mm thick glass is obtained, and the result (B) of the defoaming test in glass melting are shown.

  Table 2 shows those of comparative examples (A to C) of known optical glasses. Here, Comparative Examples A and B show Examples 1 and 3 of the above-mentioned JP-A-10-167753, and Comparative Example C shows Example 6 of the above-mentioned JP-A-4-224132.

  All the numerical values in the table represent the mass% of each component with respect to the total glass mass.

Details of the defoaming test in glass melting are described. 300 g of glass raw material prepared to have a predetermined composition was put into a platinum crucible and put into an electric furnace at 1400 ° C. to be vitrified. After putting it in, after 1 hour, it was taken out of the furnace and the glass was stirred with a platinum rod. After that, the temperature was kept again in an electric furnace at 1400 ° C. for 2 hours, and then the temperature was lowered to 1300 ° C. and kept for 1 hour. A glass sample obtained by pouring into a mold and slowly cooling was polished face-to-face with a thickness of 10 mm, and the number of bubbles contained in the glass was observed. According to glass observation, less than 20 bubbles per cm ³ unit volume were indicated as “〇”, 20 or more and less than 50 as “Δ”, and 50 or more bubbles as “×”.

  The glasses of the examples of the present invention described in Table 1 were all mixed with a predetermined ratio using ordinary optical glass materials such as oxides, carbonates, nitrates, fluorine compounds and hydroxides, and then platinum. Put into a crucible, etc., melt for 3 to 4 hours at a temperature of 1300 to 1450 ° C. according to the difficulty of melting the glass composition, homogenize with stirring, lower to an appropriate temperature, and then cast into a mold etc. Was obtained.

As shown in Table 1, in the preferred embodiments of the present invention, all of the preferred embodiments of the present invention achieve a desired optical constant without containing environmental pollutants typified by PbO and As ₂ O ₃ , and remove during melting. It is clear that the foamability is excellent. On the other hand, in the comparative examples shown in Table 2, in Comparative Examples A and B, the score of the defoaming test is Δ, and there is a concern about an increase in energy consumption during glass melting. In addition, a ZnO component is compared in the glass. Because it is contained at a high concentration, care must be taken in wastewater treatment at processing waste and processing equipment. Comparative Example C has a high glass viscosity at the time of melting, is inferior in defoaming property, needs to be melted at a higher temperature, and seems to cause an increase in energy consumption.

Although the present invention has been described in detail for the purpose of illustration, this embodiment is only for the purpose of illustration, and many modifications can be made by those skilled in the art without departing from the spirit and scope of the present invention. Will be understood.

Claims (3)

It has an optical constant in the range of refractive index (nd) 1.49 to 1.54, Abbe number (νd) 55 to 65,
SiO ₂ > 65 to 75%
R ₂ O (R is one or more selected from the group consisting of Li, Na, K and Cs)
15-25%
_As, Li 2 O 0.1 ~ 5.0%
Na ₂ O 1.0 ~ 10.0%
K ₂ O 5.0 ~ 20.0%, and Cs ₂ O 0 ~ 5.0%
And R′O (R ′ is one or more selected from the group consisting of Mg, Ca, Sr and Ba)
0.5 to 10%
MgO 0 to 10% and / or CaO 0 to 10% and / or SrO 0 to 10% and / or BaO 0 to 10%
_{Further, B 2 O 3 0 ~ 6.0} %
Al ₂ O ₃ 0 to <1.0% and / or ZnO 0 to <3.0% and / or TiO ₂ 0 to <2.0% and / or ZrO ₂ 0 to 2.0% and / or WO ₃ Each of 0 to 3.0% and / or Sb ₂ O ₃ 0 to 2.0% and a total amount of 0 to 2% of F in the fluoride in which one or more of the above oxides are partially or fully substituted Glass containing ingredients. It has an optical constant in the range of refractive index (nd) 1.50 to 1.53 and Abbe number (νd) 57 to 62, and is SiO ₂ 67 to 72% by mass.
B ₂ O ₃ 0 to 6.0%
Al ₂ O ₃ 0 to <1.0% and / or R ₂ O (R is one or more selected from the group consisting of Li, Na, K and Cs)
20-25%
Li ₂ O 0.1-5.0%
Na ₂ O 1.0 ~ 10.0%
K ₂ O 10.0 ~ 20.0%, and Cs ₂ O 0 ~ 5.0%
R′O (R ′ is one or more selected from the group consisting of Mg, Ca, Sr and Ba)
0.5-5.0%
MgO 0 to 5.0% and / or CaO 0 to 5.0% and / or SrO 0 to 5.0% and / or BaO 0 to 5.0%
_{Further, B 2 O 3 0 ~ 6.0} %
Al ₂ O ₃₀ to <1.0% and / or TiO ₂ 0 to <2.0% and / or ZrO ₂ 0 to 2.0% and / or WO ₃ 0 to 3.0% and / or Sb ₂ O ₃ 0 ~ 2.0%
Glass containing each component. ZnO, glass according to claim 1 or 2 containing no PbO and _As 2 _{O 3.}