JP2005047104A - Inner surface-lined steel pipe and its manufacturing method - Google Patents
Inner surface-lined steel pipe and its manufacturing method Download PDFInfo
- Publication number
- JP2005047104A JP2005047104A JP2003205011A JP2003205011A JP2005047104A JP 2005047104 A JP2005047104 A JP 2005047104A JP 2003205011 A JP2003205011 A JP 2003205011A JP 2003205011 A JP2003205011 A JP 2003205011A JP 2005047104 A JP2005047104 A JP 2005047104A
- Authority
- JP
- Japan
- Prior art keywords
- steel pipe
- mass
- resin
- parts
- lining
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】
【発明の属する技術分野】
本発明は、給水、給湯、空調、排水等の配管等に使用される、内側に水が流れる内面樹脂ライニング鋼管に関し、特に、効率的な方法で製造され、かつ、長期性能の優れた内面樹脂ライニング鋼管およびその製造方法に関するものである。
【0002】
【従来の技術】
従来、給水、給湯、排水等に使われる配管は、耐食性等の改善のために、ポリエチレン樹脂粉体等を化成処理、プライマー処理等の表面処理が施された鋼管の内面に加熱した状態で粉体塗装することで内面ライニング層を形成するといった方法が用いられているが、この粉体塗装法は、生産効率の面で優れるものではなく、また、防食性能の低下につながるピンホール等が発生しやすい、また厚膜化が困難であるなどの問題があった。
【0003】
また、形状復元性を有することが知られている塩ビ樹脂を用い、形状復元性を付与した、鋼管の内径より小さなパイプを作製、鋼管内で加熱復元させることにより拡径し、鋼管内面に貼り付ける方法が知られており、この方法は非常に生産性も高く、塩ビ樹脂の価格も安価であるため、従来より給水用内面樹脂ライニング鋼管の主流になっている。しかし塩化ビニル樹脂は、耐衝撃性、特に低温での耐衝撃性が低く、給水・給湯管として寒冷地で使用する際、及び施工時の屋外放置の際などにライニング層にダメージを受ける場合があるなどの問題があり、さらに、近年は、塩化ビニル樹脂の廃却の際の有害物の発生、塩化ビニル樹脂処理ルートにのせるための鋼管と塩化ビニル樹脂の分離など処理の負荷が大きく、環境負荷の大きい材料との認識のもとに、その使用は制限されてきている。
【0004】
また、架橋ポリエチレン管に形状復元性を付与し、鋼管内で加熱復元することにより拡径しライニングする方法も知られているが、架橋剤からの溶出成分があるため水道水の衛生性を確保できないなどの問題があった(例えば、特許文献1参照)。
【0005】
また、上記問題のないものとして、ポリエチレン管に形状復元性を付与し鋼管の内面ライニングをする方法も開示されているが(例えば、特許文献2参照)、本発明者らの検討によれば、給水、給湯用として長期耐久性の点で信頼性の劣るものであった。
【0006】
また、防食性能の高いものとして、ガス管などに用いられる外面被覆鋼管のための外面被覆材料として様々なものが知られているが、いずれも本目的には充分な性能を有さない。例えば、フッ素樹脂(例えば、特許文献3参照)、ポリエーテルエーテルケトン樹脂(例えば、特許文献4参照)が知られているが、これらはいずれも樹脂価格が高く、さらに効率の低い粉体塗装や高温での焼付け工程が必要などかなり使用に制限が加わるものである。また、ポリフェニレンスルフィド樹脂(例えば、特許文献5参照)、及びナイロンなどポリアミド樹脂(例えば、特許文献6参照)などは給水用、特に給湯用の内面ライニング鋼管とした場合、性能に問題がある。
【0007】
【特許文献1】
特開2001−9912号公報(第2〜3頁)
【0008】
【特許文献2】
特開2002−257265号公報(第2〜4頁、図1)
【0009】
【特許文献3】
特開平8−300554号公報(第2〜3頁)
【0010】
【特許文献4】
特開平4−50585号公報(第2〜3頁)
【0011】
【特許文献5】
特開平7−329240号公報(第2〜5頁、表1、図1〜図4)
【0012】
【特許文献6】
特開平8−294994号公報(第2〜4頁、図1)
【0013】
【発明が解決しようとする課題】
給水、給湯用に使用される配管の内面ライニング層に求められる性能は、通常の被覆材料に求められる性能とは全く異なり、耐塩素水性、耐冷熱水サイクル性、耐ウォーターハンマー性、溶出性、低温衝撃性などが求められる。
【0014】
例えば、耐塩素水性が低いと水道水中に添加されている塩素により内面ライニング層が劣化し、剥離やツマリなどの原因となる。また、耐冷熱水サイクル性が低いと、水とお湯の切替や、常温に冷えている配管内にお湯が流れ込む回数が長年使用で多くなった時点で、内面ライニング層が変形したり、クラックが入ったりする結果、水と直接触れた鋼管内面部分が錆びて赤水が蛇口より供給されることになってしまう。
【0015】
耐ウォーターハンマー性が低いと、蛇口を止めた瞬間に管内に生じる負圧により、ライニング層の剥離、ツマリなどが起きる。また、通常、過マンガン酸カリウム消費量で定量される溶出性が高いと、水道水中に溶け出す有機物の量が多いことを意味し、衛生性に悪い。
【0016】
また、低温衝撃性が悪いと、寒冷地での施工、及び使用において、内面ライニング層がダメージを受けツマリ、赤水発生などの原因となる。
【0017】
さらに、内面ライニングは、鋼板の被覆や、鋼管の外面被覆に比べ行いにくく、効率的な内面ライニング方法に適用可能な事も重要である。
【0018】
上述したように従来はこれら全てを満足する手段はなく、それらを解決できる手法が望まれていた。
【0019】
本発明は上記の課題を解決するためになされたものであって、給水、給湯、空調、排水等に用いられる配管において、耐塩素水性、耐冷熱水サイクル性、耐ウォーターハンマー性、溶出性、低温衝撃性に優れた内面ライニング鋼管及びその製造方法を提供することを目的とする。
【0020】
【課題を解決するための手段】
本発明者らは、給水・給湯等に用いられる配管の内面ライニングに要求される上記諸特性に関して鋭意研究した結果、以下の方法により上記課題を解決でき、給水、給湯用として充分な性能を有する内面樹脂ライニング鋼管を提供できることが判明した。
【0021】
本発明に係る内面ライニング鋼管は、鋼管の内面にライニング層を有する内面ライニング鋼管において、前記ライニング層は、ポリスチレン系樹脂と、スチレン系エラストマー及びゴム成分のうちの少なくとも一方の添加材と、非スチレン系エラストマーとを含有し、前記ポリスチレン系樹脂100質量部に対して、前記スチレン系エラストマー及びゴム成分のうちの少なくとも一方の添加剤の含有量は合計で3質量部以上30質量部以下、前記非スチレン系エラストマーの含有量は1質量部以上30質量部以下、且つ前記スチレン系エラストマー及びゴム成分のうちの少なくとも一方の添加剤の合計含有量と前記非スチレン系エラストマーの含有量の和は50重量部以下である樹脂組成物からなることを特徴とする。
【0022】
ゴム及びスチレン系エラストマー成分が3質量部未満だと耐衝撃性が低下し、30質量部超だと耐冷熱水サイクル性及び耐ウォーターハンマー性が不十分になる。
【0023】
非スチレン系エラストマーの含有量は、ポリスチレン系樹脂100質量部に対して1質量部以上30質量部以下とすることが必要であり、1質量部以上10質量部以下とすることがより好ましい。
【0024】
理由は定かではないが、非スチレン系エラストマーがポリスチレン系樹脂100質量部に対して1質量部より少なくなっても30質量部より多くなっても、実使用環境をシミュレートした冷熱水サイクル特性が不十分になることが判明している。さらにライニング特性を向上させるには、非スチレン系エラストマーの含有量を10質量部以下に抑える。
【0025】
ゴム及びスチレン系エラストマー成分の合計含有量と、非スチレン系エラストマーの含有量の総和は50質量部以下とすることが必要である。ゴム及びスチレン系エラストマー成分の合計含有量と、非スチレン系エラストマーの含有量の総和が50質量部を超えると、耐冷熱水サイクル性及び耐ウォーターハンマー性が不十分になる。
【0026】
さらに、ライニング層は、前記ポリスチレン系樹脂100質量部に対して、(i)100質量部以下のポリスチレングラフト共重合体、(ii)5質量部以下の酸化チタン、からなる群より選択される1又は2以上の添加材を含有することが好ましい。
【0027】
ポリスチレングラフト共重合体を添加すると、樹脂組成物からなるライニング層の低温衝撃特性が向上する。しかし、100質量部を超えて添加すると、耐冷熱水サイクル性及びウォーターハンマー特性が不充分なものになる。
【0028】
酸化チタンを添加すると、耐塩素水性が向上する。しかし、5質量部を超えて添加すると、耐冷熱水サイクル性が不充分なものになる。
【0029】
本発明に係る内面ライニング鋼管の製造方法は、ポリスチレン系樹脂と、スチレン系エラストマー及びゴム成分のうちの少なくとも一方の添加材と、非スチレン系エラストマーとを含有し、前記ポリスチレン系樹脂100質量部に対して、前記スチレン系エラストマー及びゴム成分のうちの少なくとも一方の添加剤の含有量は合計で3質量部以上30質量部以下、前記非スチレン系エラストマーの含有量は1質量部以上30質量部以下、且つ前記スチレン系エラストマー及びゴム成分のうちの少なくとも一方の添加剤の合計含有量と前記非スチレン系エラストマーの含有量の和は50重量部以下である樹脂管を加熱下で縮径させ、鋼管内に挿入し、再度加熱して拡径させ、該樹脂管を鋼管の内面にライニングすることを特徴とする。
【0030】
さらに、ライニング層と鋼管との間に接着層を設けるようにしてもよい。この場合、前記樹脂管は外面に接着層を形成した樹脂管を用いてもよい。接着層として、無水マレイン酸変性ポリスチレン又はホットメルト系接着剤を用いることが望ましく、接着層を設けることにより樹脂管を鋼管の内面に強固に接着することができる。
【0031】
(作用)
本発明の樹脂組成によれば、給水、給湯用配管の内面ライニング層に求められる耐塩素水性、耐冷熱水ヒートサイクル性、耐ウォーターハンマー性、溶出性、低温衝撃性などを充分に満足する結果、長期間の使用によってもライニング層の変形やクラック発生などに起因する赤水が発生しなくなる。
【0032】
さらに、本発明の樹脂組成物は形状復元性に優れているため、ライニング鋼管の製造方法として、管状に成形した樹脂組成物を加熱下で縮径させて形状復元性を付与し、これを鋼管内に挿入して再度加熱することにより、樹脂管が膨張して拡径し、鋼管の内面にライニングすることができる。
【0033】
【発明の実施の形態】
図1は、本発明の実施の形態に係る内面ライニング鋼管の一部を模式的に示す拡大断面図である。図1は鋼管内面とライニング層との間に接着層を有する例で、1は内面ライニング鋼管、2は鋼管、3は接着層、4はライニング層(樹脂組成物)である。
【0034】
以下に本発明の種々の好ましい実施の形態について説明する。
【0035】
(鋼管)
本発明で用いられる鋼管は、鋼管外面にブラスト処理、酸洗処理、化成処理、メッキ処理、プライマー処理もしくはプラスチックライニングを行なっても良い。また、鋼管内面には、ブラスト処理、酸洗処理、化成処理、メッキ処理などをしてもよく、さらにその内側に通常行なわれているような熱硬化性エポキシ樹脂、熱硬化性ウレタン樹脂、熱硬化性フェノール樹脂、フェノキシ樹脂、ポリエステル樹脂によるプライマー処理をしても良く、後述するように必要に応じてそれらとライニング層との間に接着層を介在させても良い。鋼管の大きさは外径が10〜2000mm程度、通常20〜170mm程度のものを、長さは3〜10m程度、通常4〜6m程度、肉厚は2.0〜5.3mm程度のものを用いる。
【0036】
(ポリスチレン系樹脂)
ライニング層に用いられるポリスチレン系樹脂は、既知の汎用樹脂であり、最も代表的なスチレンをはじめとして下記一般式に示したようなビニル芳香族化合物もしくはその誘導体の繰り返し単位を有する単独重合体または共重合体である。
【0037】
【化1】
【0038】
上記の式中、Rは水素、またはアルキル基等を、R’はアルキル基、ビニル基、ハロゲン、またはアミノ基等を、そしてmは0または1〜5の整数を表す。
【0039】
代表例としては、ポリスチレン、ポリα−メチルスチレン等があり、さらにこれらの共重合体を用いてもよい。また、ポリスチレンやポリα−メチルスチレンには立体異性体であるアタクチック型、シンジオタクチック型、アイソタクチック型があるが、それらを適宜使うことができる。例えば通常のアタクチックポリスチレンの他にもシンジオタクチックポリスチレン、アイソタクチックポリスチレンを用いることができ、さらに適宜これらの混合物を用いることができる。また、このような芳香族ビニル化合物と非芳香族化合物との共重合体であっても良い。代表例としては、スチレン−アクリロニトリル共重合体、スチレン−無水マレイン酸共重合体、スチレン−メチルメタクリレート共重合体等が挙げられる。
【0040】
(ゴム・スチレン系エラストマー)
スチレン系エラストマー成分としては公知の熱可塑性のスチレン系エラストマーでよく、スチレンとブタジエン、イソプレンなどのジエン成分とを共重合したもの、もしくはそれらの水添物等であれば良い。また、ゴム成分としては、公知のゴムであれば何でもよい。具体例としては例えば、スチレン系、ブタジエン系、イソプレン系、アクリル系、もしくはエチレンプロピレン系ゴムや、それらの水添物等を挙げることができる。
【0041】
また、ゴムもしくはエラストマー成分を有するポリスチレンとして、HIPS(ハイインパクトポリスチレン)と称されるような耐衝撃性を改善したポリスチレンを用いてもよい。
【0042】
本発明の樹脂組成物は、前記エラストマー成分のグループ及び前記ゴム成分のグループのうちから選ばれるエラストマー成分及び/又はゴム成分の1種又は2種以上を含有する。
【0043】
(非スチレン系エラストマー)
非スチレン系エラストマーとは、スチレン成分を含まない熱可塑性エラストマーであり、ポリテトラメチレングリコールのような脂肪族ポリエーテルとポリブチレンテレフタレートのような芳香族ポリエステルとが結合したようなポリエステル系エラストマーや、ポリアミド6、66、11、12等の結晶性ポリアミドとポリオキシエチレン、ポリオキシプロピレン、ポリテトラメチレングリコール等のポリエーテルとが結合したようなポリアミド系エラストマーや、エチレン、プロピレン等の非スチレン系オレフィンをモノマーとした樹脂からなる熱可塑性ポリオレフィン系エラストマーや、イソシアネートとポリテトラメチレングリコールなどのポリエーテルもしくはポリエステルを共重合したウレタン系エラストマーを使用できる。また、これら樹脂を必要に応じて2種以上混ぜ合わせたブレンド樹脂でもよく、これらに性能を損なわない範囲で可塑材、着色剤、顔料、充填材、難燃剤、酸化防止剤、紫外線吸収材、帯電材、滑剤、粘着付与剤等の添加剤を加えることができる。
【0044】
(組成比)
これら樹脂組成物において、ポリスチレン系樹脂100質量部に対して非スチレン系エラストマーを1〜30質量部、より好ましくは1〜10質量部とし、かつ、ポリスチレン系樹脂100質量部に対して合計で3〜30質量部のゴム及び/もしくはスチレン系エラストマーを含有することが必要である。また、前記非スチレン系エラストマーの含有量と前記スチレン系エラストマーとゴム成分の合計含有量の総和は50重量部以下とすることが必要である。
【0045】
理由は定かではないが、非スチレン系エラストマーが1質量部より少なくなっても30質量部より多くなっても、実使用環境をシミュレートした冷熱水サイクル特性が不十分になる。ポリスチレン系樹脂100質量部に対してゴムおよびスチレン系エラストマー成分の合計含有量が3質量部未満だと耐衝撃性が低下し、30質量部超だと実使用環境をシミュレートした耐冷熱水サイクル性能と耐ウォーターハンマー性とが悪くなる。また、前記非スチレン系エラストマーの含有量と前記スチレン系エラストマーとゴム成分の合計含有量の総和が50重量部を超えても耐冷熱水サイクル性能と耐ウォーターハンマー性とが悪くなる。さらにライニング特性を向上させるには、非スチレン系エラストマーの含有量を10質量部以下に抑えることが好ましい。
【0046】
前記樹脂組成物からなるライニング層を鋼管内面に有する内面ライニング鋼管は、耐塩素水性、耐冷熱水サイクル性、耐ウォーターハンマー性、溶出性、低温衝撃性に優れる。また、該内面ライニング鋼管は、樹脂組成物の加熱復元性を利用した効率的方法で製造することができる。
【0047】
(ポリスチレングラフト共重合体)
本発明の樹脂組成物には、また、低温衝撃特性を向上させるためにポリスチレングラフト共重合体を添加しても良い。
【0048】
ポリスチレングラフト共重合体は、オレフィン系化合物の単独もしくは共重合体に、ポリスチレン重合体がグラフトされた重合体であり、オレフィン系化合物の単独もしくは共重合体の具体例としては、ポリエチレン、エチレンエチルアクリレート共重合体、エチレン酢酸ビニル共重合体、エチレングリシジルメタクリレート共重合体、エチレンエチルアクリレート無水マレイン酸共重合体が挙げられ、特にこれら共重合体中のエステル系モノマー含有率が10〜25質量%、無水マレイン酸モノマー含有率が10質量%以下のものが望ましい。また、ポリスチレン重合体には性能を損なわない範囲で若干の共重合モノマーが混在しても良い。ポリスチレングラフト共重合体は、1種を添加してもよく、2種以上添加してもよい。
【0049】
これら、ゴム、もしくはスチレン系エラストマー成分は、ポリスチレン系樹脂100質量部に対して、30質量部以下とすることが好ましい。また、ポリスチレングラフト共重合体の添加は、ポリスチレン系樹脂100質量部に対して、100質量部以下とすることが好ましい。それらを超えて過剰に添加すると耐冷熱水サイクル性能とウォーターハンマー特性が不充分なものになる。さらに50質量部以下とすることで樹脂管のライニング特性が向上する。
【0050】
(酸化チタン)
本発明の樹脂組成物には、また、耐塩素水性を向上させるために酸化チタンを添加しても良い。
【0051】
酸化チタンは、公知のものでよくルチル型でもアナターゼ型でもよく、粒径も特に制限されるものではないが、樹脂組成物中への均一分散などを考慮すると30μm以下の粒径が好ましい。添加量は、ポリスチレン系樹脂100質量部に対し、0.1質量部以上5質量部以下にすることが好ましい。5重量部を超えると冷熱水サイクル特性が不十分なものになる。
【0052】
(樹脂組成物の混合)
これら樹脂組成物の混合は、従来より樹脂混練の方法として公知の一般的方法を用いて行うことができ、高温下でニーダーや押出し機により混練することにより可能であり、特に、ゴムやエラストマー成分は場合によりポリスチレン樹脂重合時に添加、もしくはポリスチレン重合と同時に重合しても良い。
【0053】
また、着色等の目的で、アゾ系、フタロシアニン系、アンスラキノン系、インジゴ系、チタニア系、ベンガラ系、カーボンブラック、炭酸カルシウム、硫酸バリウム、タルク、シリカ、クレー等の顔料、およびそれらを複合した顔料を添加しても良い。
【0054】
また、上記樹脂組成物には本発明の性能を損なわない範囲で、上記樹脂組成物を主成分として他の樹脂を混ぜ合わせても良く、必要に応じて酸化防止剤、紫外線吸収剤、耐光安定化剤、難燃剤、充填剤、滑剤、帯電防止剤、粘着付与剤等の添加剤を加えることができる。
【0055】
(接着層)
また、鋼管1とライニング層4の間に接着層3を設けること(図1参照)により、ライニング層4と鋼管2との密着力が向上し、配管施工工事現場での作業性向上や、使用時の信頼性確保になる。そのような接着層の材料としては、無水マレイン酸変性ポリスチレンや、ホットメルト接着剤を用いることができる。ホットメルト接着剤としては、例えば、エチレン−無水マレイン酸共重合樹脂、エチレン−無水マレイン酸−アクリル酸エステル共重合体、エチレン−メタクリル酸共重合体、エチレン−アクリル酸共重合体、エチレン−アクリル酸エステル共重合樹脂、エチレン−メタクリル酸エステル共重合樹脂、アイオノマー樹脂、もしくはエチレン−酢酸ビニル共重合体等の1種又は2種以上をベースとしたポリオレフィン系ホットメルト接着剤、もしくは、ポリエステル系ホットメルト接着剤、ポリアミド系ホットメルト接着剤、ポリウレタン系ホットメルト接着剤などが挙げられるがこれらに限定されるものではない。
【0056】
また、上記接着剤には本発明の性能をそこなわない範囲で、上記接着剤同士もしくは他の樹脂を混ぜ合わせても良く、必要に応じて酸化防止剤、紫外線吸収剤、耐光安定化剤、可塑材、難燃剤、顔料、着色剤、充填剤、滑剤、帯電防止剤、粘着付与剤等の添加剤を加えることができる。
【0057】
(内面ライニング鋼管の製造方法)
ライニング方法としては、上記樹脂組成物を公知の方法で混練混合した後、破砕、粉状にしたものを、加熱した鋼管内面に吹付ける粉体塗装法、もしくは粉体流動槽の中に加熱した鋼管を浸漬する流動浸漬法などが適用可能である。
【0058】
また、本発明の樹脂組成物は形状復元性を有するため生産効率のよい方法として形状復元法にも適用可能である。ここで、形状復元性とは、樹脂管を加熱下で縮径させた後冷却したものを再度加熱すると、その樹脂組成物が本来有する線膨張係数以上の割合で拡径する特性である。また、形状復元法とは、ライニングしようとする鋼管の内径よりも大きな外径を有する樹脂管を加熱下で鋼管内径より小さい径まで縮径させ、冷却して得られた樹脂管を鋼管内に挿入し、再度加熱して拡径させ、該樹脂管を鋼管の内面にライニングする方法である。
【0059】
具体的には、まず、本発明の樹脂組成物を通常の方法で金型よりパイプ状に押出しし、サイジングダイ、水冷シャワー等を用いて樹脂を固化温度以下まで冷却しながら外径を固定して、鋼管内径よりも大きな外径を有する樹脂管にする。その後、形状復元性を付与するために、該樹脂管を、赤外線加熱炉、マイクロ波加熱炉、高周波加熱炉、熱風炉等を利用して該樹脂組成物のガラス転移温度以上まで昇温しながら、もしくはガラス転移温度以上の温度域で、鋼管内径よりも小さな外径になるまで縮径し、冷却することで形状復元性を付与することが好ましい。
【0060】
この縮径は、2台の引取機の間に、加熱炉と冷却槽を配置させたラインを採用し、2台の引取機の速度差を利用して管の長手方向に延伸して縮径する方法、もしくは出側の径が鋼管内径より細いテーパーのついた金型内を通過させて縮径する方法、もしくはロール等で径方向に絞り込み縮径する等の方法が適用できる。また、これらの工程において形状を安定させるため、パイプの内側にエアを送り込むなどの方法でパイプ内側を加圧したり、金型への成形物の追随を良くするためパイプの外側を減圧にし金型に吸い付けるようにするなどの方法を適用することも可能である。
【0061】
また、樹脂組成物を金型よりパイプ状に押出しする際に、樹脂温度がガラス転移温度以上になる様にし、それを冷却しながら上記方法で縮径を行っても良い。
【0062】
縮径後の樹脂管のサイズは、ライニングしようとする管のサイズ、作業性、経済性等を考慮して、通常、外径12〜158mm、肉厚0.4〜4.5mmになるようにするが、特にこれに制限されるものではない。
【0063】
また、樹脂組成物のガラス転移温度は示差走査熱量分析等、通常行われる方法で得ることができる。
【0064】
縮径するときの樹脂管温度は、ガラス転移温度より低いとネッキングなどが発生し安定的に縮径が行えなくなり、さらに形状復元するときも不均一なものになりきれいに鋼管内面をライニングできなくなる。
【0065】
ライニング層と鋼管の間に接着層を設けるときは、加熱した鋼管の内側に、無水マレイン酸変性ポリスチレン又はホットメルト系接着剤(以下、無水マレイン酸変性ポリスチレン又はホットメルト系接着剤を、接着剤等という。)の粉体を吹き込んで鋼管内面に融着させてもよいし、樹脂管の外面に接着剤等を被覆して接着層を形成してもよい。樹脂管の外面に接着剤等を被覆する時は、形状復元性を付与する前もしくは後にクロスヘッド丸ダイやTダイで接着剤等を樹脂管表面に被覆する方法、もしくはあらかじめフィルム状に成形した接着剤等を樹脂管の表面に巻きつける方法、もしくは多層金型でライニング層となる樹脂と接着剤等を共押出しする方法などが適用できる。通常接着層の厚みは0.05〜0.8mmであるが特にこれに限定されるものではない。
【0066】
このようにして作製したライニング用樹脂管を鋼管内に挿入し、高周波加熱炉、熱風炉等で加熱し、好ましくは樹脂管を該樹脂組成物の[ガラス転移温度−10℃]より高い温度、さらに好ましくはガラス転移温度以上の温度に加熱することにより、樹脂管が膨張して鋼管内面にライニングされる。
【0067】
この形状復元プロセスでは、単に加熱するだけではなく、該樹脂管の内部に圧縮空気などを吹込むことにより加熱膨張をさらに促進させる方法や、該樹脂管の両端部を密封することにより温度上昇に伴う該樹脂管内の空気の体積増加により加熱膨張をさらに促進させる方法もある。
【0068】
樹脂管の加熱温度を前記のようにするのは、加熱時の樹脂管温度が[ガラス転移温度−10℃]より低い場合に、樹脂管の拡径が不足して鋼管とライニング層との間に隙間が存在する部分が発生してしまう可能性のあることが判明し、ガラス転移温度以上に加熱することにより安定的に樹脂管を拡径することができるという知見を得たことに基づく。
【0069】
また、鋼管と樹脂管の間の空気を抜けやすくするために、管中央部より両端部へ、もしくは一方の管端より他端へ、加熱していくのが好ましい。さらに、鋼管端部付近は、熱が樹脂管へと伝わりにくいので、ライニング後に熱処理を行なってもかまわない。該樹脂管が鋼管内面に密着した後は、冷却し、鋼管端部よりはみ出している樹脂管部分を切断することにより内面樹脂ライニング鋼管を得ることができる。
【0070】
【実施例】
以下に、本発明の内面樹脂ライニング鋼管について、樹脂管を形状復元法で鋼管内面にラインニングして製造した場合を実施例に基いて説明するが、本発明は以下の実施例のみに限定されるものではない。
【0071】
(実施例1〜29、比較例1〜11、13、15〜21)
あらかじめ、各種原料を、単軸もしくは2軸押出し機、もしくはニーダーなどで混練し、表1〜6に示した組成の樹脂ペレットを得た。但し、数値部は質量比を示す。なお、表1〜6中のポリスチレングラフトエチレンエチルアクリレート共重合体、ポリスチレングラフトエチレン酢酸ビニル共重合体において、ポリスチレン重合体がグラフトされた共重合体の組成は下記に示すとおりである。
1)エチレンエチルアクリレート共重合体:エチルアクリレート含有量20質量%
2)エチレン酢酸ビニル共重合体:酢酸ビニル含有量15質量%
【0072】
【表1】
【0073】
【表2】
【0074】
【表3】
【0075】
【表4】
【0076】
【表5】
【0077】
【表6】
【0078】
ライニング用樹脂管は、概略、押出し機、金型、冷却槽、引取り機、加熱炉、冷却槽、引取り機、パイプ切断機の順に並んだ成形ラインにおいて、連続的に製造した。
【0079】
先ず、表1〜6に示す組成の樹脂を所定温度で丸ダイスより外径29.0〜30.0mmのパイプ形状に押出した直後に、パイプ表面が40℃以下になるまで冷却し、次にパイプ外面が表1〜6に示した温度に到達するように加熱炉で加熱しながら、加熱炉の前後に配した2台の引取り機の速度差でパイプの外径が25.8mmになるようにパイプを延伸縮径し、冷却水槽にて冷却し、外径が25.8mm、肉厚が0.8〜1.2mmのライニング用樹脂管を作製した。
【0080】
作製した樹脂管を長さ4m50cmにし、酸洗処理した呼び径25Aの鋼管(内径27.6mmφ、外径34mmφ×4m)の内にさし込み、その後、樹脂管が表1〜6に示した温度になるように高周波加熱装置により鋼管を加熱し、樹脂管を加熱膨張させ鋼管内面にライニングした。さらに、鋼管端部よりはみ出した樹脂部分を切断しライニング鋼管を得た。
【0081】
(比較例12)
実施例1と同様の方法で作製したが、表6記載の樹脂2種を、2層の厚み比が内層:外層=7:3になるように、外径30.0mmのパイプ形状に共押出しし、それを冷却後、パイプ外面が105℃に到達するように加熱炉で加熱しながら、加熱炉の前後に配した2台の引取り機の速度差でパイプの外径が26.0mmになるようにパイプを延伸縮径し、冷却水槽にて冷却し、外径が26.0mm、肉厚約1.4mmのライニング用樹脂管を作製した。
【0082】
作製した樹脂管を長さ4m50cmにし、酸洗処理した呼び径25Aの鋼管(内径27.6mmφ、外径34mmφ×4m)の内にさし込み、その後、樹脂管が105℃になるように、高周波加熱装置により鋼管を加熱し(この時の鋼管の温度は128℃であった)、樹脂管を加熱膨張させ鋼管内面にライニングした。さらに、鋼管端部よりはみ出した樹脂部分を切断しライニング鋼管を得た。
【0083】
(比較例14)
実施例1と同様の方法で作製したが、表6記載の樹脂を、外径30.0mmのパイプ形状に押出しし、それを冷却して樹脂パイプを得た。樹脂パイプを80℃の温水槽に24hr浸漬し架橋処理を行った。処理後の樹脂パイプのJIS K6769によるゲル分率は32%であった。このパイプをパイプ外面が140℃に到達するように加熱炉で加熱しながら、加熱炉の前後に配した2台の引取り機の速度差でパイプの外径が26.0mmになるように延伸縮径し、冷却水槽にて冷却し、外径が26.0mm、肉厚約1.4mmのライニング用樹脂管を作製した。
【0084】
作製した樹脂管を長さ4m50cmにし、酸洗処理した呼び径25Aの鋼管(内径27.6mmφ、外径34mmφ×4m)の内にさし込み、その後、樹脂管が140℃になるように、高周波加熱装置により鋼管を加熱し(この時の鋼管の温度は170℃であった)、樹脂管を加熱膨張させ鋼管内面にライニングした。さらに、鋼管端部よりはみ出した樹脂部分を切断しライニング鋼管を得た。
【0085】
評価は、縮径特性、ライニング特性、冷熱水サイクル特性、低温衝撃特性、溶出性、ウォーターハンマー特性、耐塩素水性について行った。ライニング特性の評価が×のものは、冷熱水サイクル特性のみ評価し、低温衝撃特性、溶出性、ウォーターハンマー特性、耐塩素水性の評価を行わなかった。
【0086】
<縮径特性>
延伸縮径時に、樹脂管がちぎれたり、極度に変形し断面形状がつぶれてしまうなど、縮径が良好にできなかったものを縮径特性「×」、縮径後のパイプ外径を10cmピッチで10点測定し、バラツキが目標外径の±5%未満であったものを「○」、パイプの縮径は良好にできたもののバラツキが目標外径の±5%以上であったものを「△」とした。
【0087】
<ライニング特性>
ライニング後、ライニング鋼管を10cmピッチで10ヶ所切断、断面観察し、ライニング層が鋼管内面より0.5mm以上離れている部分が1ヵ所でもあった場合ライニング特性「△」、目視ではライニング層と鋼管との間にスキマが認められなかったもの及びスキマが0.5mm未満であった場合「○」、またライニング前の樹脂管外径に対しほとんど変化が見られなかった部分があった場合「×」とした。
【0088】
<冷熱水サイクル特性>
ライニング鋼管を50cm長さに切断し、内面に85℃の熱水を10分、室温水を10分流すというサイクルを10000回行い、その後のライニング層の変化を観察、ライニング層が収縮、膨張、剥離などの変形もしくは内表面にクラックが発生し、赤水が発生したものを「×」、赤水が発生しなかったものを「○」、ライニング層に変形もしくはクラック発生などの変化のなかったものを「◎」とした。
【0089】
<低温衝撃特性>
先端がR20mmの半球になっており重さが6.3kgの錘を、水平に固定したライニング鋼管の真中外表面に−8℃で、高さ0.8mより落として鋼管が露出しなかったものを「◎」、高さ0.8mでは鋼管内面が露出したものの高さ0.5mより落としたときには鋼管が露出しなかったものを「○」、高さ0.5mでも鋼管が露出したものを「×」とした。
【0090】
<溶出性>
水道水へのライニング材料からの溶出性を過マンガン酸カリウム消費量にて評価した。方法はJIS K6769に準じ、消費量が2mg/L以下を「○」、それより大きい時を「×」、とした。
【0091】
<ウォーターハンマー特性>
JWWA(水道協会)規格に準じ、ウォーターハンマー特性を評価した。ライニング鋼管内面に流す水の流速を2.64m/secとし、バルブ開閉時の圧力が1.9kgf/cm2以上になる状態で、300回バルブ開閉を行い、その後のライニング層が変形していたものを「×」、変形していなかったものを「○」とした。
【0092】
<耐塩素水性>
JIS K6762の方法にて樹脂組成物の耐塩素水性を評価した。1000時間経過後もライニング層に水泡発生のなかったものを「◎◎」、1000時間経過後水泡発生があったがJISと同じ168時間経過後には水泡発生がなかったものを「○」、それ以下で水泡発生など異常の見られたものを「×」とした。
【0093】
上記評価結果を表7および8に示した。
【0094】
【表7】
【0095】
【表8】
【0096】
縮径特性およびライニング特性については、実施例9、10、23、27および比較例5〜9、19、20が△もしくは×評価であったのを除いて、その他の実施例、比較例ではすべて○評価であった。
【0097】
冷熱水サイクル特性については、すべての実施例1〜29で○評価以上であったのに対して、比較例1〜21はすべて×評価であった。
【0098】
比較例19、20は、樹脂管を形状復元法によって鋼管内面にライニングする際に、縮径時および拡径時の温度条件が好ましい温度範囲を外れるため、縮径特性が△評価、又はライニング特性が×評価であり、これらは内面ライニング層の性状が悪くなり、冷熱水サイクル特性が劣る。
【0099】
低温衝撃特性については、実施例1〜20、26〜29で○評価、実施例21〜25で◎評価であったのに対して、比較例3、13、18では×評価であった。
【0100】
溶出性については、すべての実施例1〜29で○評価であったのに対して、比較例14では×評価であった。
【0101】
ウォーターハンマー特性については、すべての実施例1〜29で○評価であったのに対して、比較例5〜9、11、12では×評価であった。
【0102】
耐塩素水性については、実施例26で特に優れた◎◎評価結果が得られ、他の実施例で○評価であったのに対して、比較例13では×評価であった。
【0103】
以上の結果より、本発明による内面ライニング鋼管は冷熱水サイクル性能をはじめ給水、給湯用の管として十分な性能を有していることが確認された。
【0104】
(実施例30〜47)
また、実施例1と同様の方法で、表9に示した条件でライニング用樹脂管を作製した後、その外表面に、表9に示した接着剤をクロスヘッドダイスより溶融押出しし厚み0.1mmになるように被覆した、被覆後直後に冷却し、接着層つきのライニング用樹脂管を作成した。
【0105】
作製した樹脂管を長さ4m50cmにし、酸洗処理した呼び径25Aの鋼管(内径27.6mmφ、外径34mmφ×4m)の内にさし込み、その後、表9に示した条件で鋼管内面にライニングした。さらに、鋼管端部よりはみ出した樹脂部分を切断しライニング鋼管を得た。
【0106】
評価は、ライニング鋼管を2cm長さに切断し、外側の鋼管部分をおさえ、内側のライニング樹脂層のみを軸方向に押していったときの、押し抜き剪断接着力を測定し、100N/cm2以上の場合「○」、100N/cm2未満の場合「△」とした。評価結果を表9に記載した。
【0107】
【表9】
【0108】
接着剤を用いない実施例30、36、42では初期接着力がいずれも100N/cm2を下回る結果となった。
【0109】
これにより無水マレイン酸変性ポリスチレン、もしくはホットメルト接着剤からなる接着層を設けることで、鋼管とライニング層の密着力を向上できることが確認された。
【0110】
【発明の効果】
本発明の内面樹脂ライニング鋼管は、耐塩素水性、耐冷熱水サイクル性、耐ウォーターハンマー性、溶出性、低温衝撃性に優れ、ライニング層と鋼管との接着力も高く、さらに加熱復元性を利用した効率的方法で製造できる。
【0111】
本発明の内面ライニング鋼管は、給水管、給湯管、空調もしくは排水等に用いられる配管に必要な充分な性能を有しており、これらの用途への使用に適する。
【図面の簡単な説明】
【図1】本発明の内面ライニング鋼管の一部を模式的に示す拡大断面図である。
【符号の説明】
1…内面ライニング鋼管
2…鋼管
3…接着層
4…ライニング層(樹脂組成物)[0001]
BACKGROUND OF THE INVENTION
TECHNICAL FIELD The present invention relates to an inner surface resin-lined steel pipe used for piping for water supply, hot water supply, air conditioning, drainage, etc., and more particularly to an inner surface resin-lined steel pipe in which water flows inside. The present invention relates to a lining steel pipe and a manufacturing method thereof.
[0002]
[Prior art]
Conventionally, pipes used for water supply, hot water supply, drainage, etc. are powdered in a state where the inner surface of a steel pipe that has been subjected to a surface treatment such as chemical conversion treatment or primer treatment for improving the corrosion resistance or the like. Although a method of forming an inner lining layer by body coating is used, this powder coating method is not excellent in terms of production efficiency, and pinholes etc. that lead to deterioration in anticorrosion performance occur There is a problem that it is easy to form and it is difficult to increase the film thickness.
[0003]
In addition, using a PVC resin known to have shape resilience, a pipe smaller than the inner diameter of the steel pipe, which has been given shape resilience, is produced, heated to be restored in the steel pipe, and then expanded on the inner surface of the steel pipe. Since this method is very productive and the price of the vinyl chloride resin is low, it has been the mainstream of inner surface resin-lined steel pipes for water supply. However, vinyl chloride resin has low impact resistance, especially impact resistance at low temperatures, and the lining layer may be damaged when used in cold districts as water and hot water pipes or when left outdoors during construction. In addition, in recent years, the burden of processing such as generation of harmful substances at the time of disposal of vinyl chloride resin, separation of steel pipe and vinyl chloride resin for placing on vinyl chloride resin processing route, Its use has been limited based on the recognition that it has a high environmental impact.
[0004]
Also known is a method of expanding the diameter and lining by imparting shape restoration to the crosslinked polyethylene pipe and heat restoring it in the steel pipe, but there is an elution component from the crosslinking agent to ensure the hygiene of tap water. There was a problem that it was not possible (see Patent Document 1, for example).
[0005]
Further, as a method without the above problem, a method for imparting a shape restoring property to a polyethylene pipe and lining an inner surface of a steel pipe is also disclosed (for example, refer to Patent Document 2). It was inferior in reliability in terms of long-term durability for water supply and hot water supply.
[0006]
Moreover, as a thing with high anti-corrosion performance, although various things are known as an outer surface coating material for the outer surface covering steel pipe used for a gas pipe etc., all do not have sufficient performance for this purpose. For example, fluororesins (see, for example, Patent Document 3) and polyether ether ketone resins (see, for example, Patent Document 4) are known, but these are both expensive and less efficient powder coatings. Use is considerably limited, such as the need for a baking process at high temperatures. In addition, polyphenylene sulfide resin (for example, see Patent Document 5) and polyamide resin such as nylon (for example, see Patent Document 6) have problems in performance when used as an inner lining steel pipe for water supply, particularly for hot water supply.
[0007]
[Patent Document 1]
JP 2001-9912 A (
[0008]
[Patent Document 2]
JP 2002-257265 A (
[0009]
[Patent Document 3]
JP-A-8-300554 (
[0010]
[Patent Document 4]
JP-A-4-50585 (
[0011]
[Patent Document 5]
Japanese Patent Laid-Open No. 7-329240 (
[0012]
[Patent Document 6]
JP-A-8-294994 (
[0013]
[Problems to be solved by the invention]
The performance required for the inner lining layer of pipes used for water supply and hot water supply is completely different from the performance required for ordinary coating materials, and is resistant to chlorine water, cold and hot water cycle, water hammer, elution, Low temperature impact properties are required.
[0014]
For example, if the chlorine water resistance is low, the inner lining layer is deteriorated by chlorine added to tap water, which causes peeling or tsumari. Also, if the resistance to cold and hot water cycle is low, the inner lining layer may be deformed or cracked when the number of switching between water and hot water and the number of times hot water flows into piping that is cooled to room temperature increases over many years. As a result, the inner surface portion of the steel pipe that is in direct contact with water rusts and red water is supplied from the faucet.
[0015]
If the water hammer resistance is low, the negative pressure generated in the pipe at the moment when the faucet is stopped may cause the lining layer to peel off or to become thickened. Moreover, if the elution property quantified by the amount of potassium permanganate consumed is high, it means that the amount of organic matter dissolved in the tap water is large, and the hygiene is poor.
[0016]
In addition, when the low temperature impact property is poor, the inner lining layer is damaged during construction and use in a cold region, which causes tsumari and red water.
[0017]
Furthermore, it is also important that the inner lining is applicable to an efficient inner lining method because it is difficult to perform compared with the coating of a steel plate or the outer coating of a steel pipe.
[0018]
As described above, conventionally, there is no means that satisfies all of these, and a method that can solve them has been desired.
[0019]
The present invention was made to solve the above problems, and in piping used for water supply, hot water supply, air conditioning, drainage, etc., chlorine water resistance, cold and hot water cycle resistance, water hammer resistance, elution, An object is to provide an internally lined steel pipe excellent in low-temperature impact resistance and a method for producing the same.
[0020]
[Means for Solving the Problems]
As a result of earnest research on the above-mentioned characteristics required for the inner surface lining of pipes used for water supply and hot water supply, etc., the present inventors can solve the above problems by the following method and have sufficient performance for water supply and hot water supply. It has been found that an internal resin-lined steel pipe can be provided.
[0021]
An inner surface lining steel pipe according to the present invention is an inner surface lining steel pipe having a lining layer on the inner surface of the steel pipe, wherein the lining layer includes a polystyrene resin, an additive material of at least one of a styrene elastomer and a rubber component, and non-styrene. A total amount of the additive of at least one of the styrene elastomer and the rubber component is 3 parts by mass to 30 parts by mass with respect to 100 parts by mass of the polystyrene resin. The content of the styrene elastomer is 1 part by mass or more and 30 parts by mass or less, and the sum of the total content of at least one additive of the styrene elastomer and the rubber component and the content of the non-styrene elastomer is 50% by weight. It consists of the resin composition which is below the part.
[0022]
When the rubber and styrene elastomer component is less than 3 parts by mass, the impact resistance is lowered, and when it exceeds 30 parts by mass, the cold / hot water cycle resistance and the water hammer resistance are insufficient.
[0023]
The content of the non-styrene elastomer is required to be 1 part by mass or more and 30 parts by mass or less with respect to 100 parts by mass of the polystyrene resin, and more preferably 1 part by mass or more and 10 parts by mass or less.
[0024]
Although the reason is not clear, even if the non-styrene elastomer is less than 1 part by mass or more than 30 parts by mass with respect to 100 parts by mass of the polystyrene resin, the hot and cold water cycle characteristics simulating the actual use environment can be obtained. It turns out to be insufficient. In order to further improve the lining characteristics, the content of the non-styrene elastomer is suppressed to 10 parts by mass or less.
[0025]
The total content of the rubber and the styrene elastomer component and the total content of the non-styrene elastomer needs to be 50 parts by mass or less. When the total content of the rubber and the styrene elastomer component and the total content of the non-styrene elastomer exceeds 50 parts by mass, the cold / hot water cycle resistance and the water hammer resistance become insufficient.
[0026]
Further, the lining layer is selected from the group consisting of (i) 100 parts by mass or less of polystyrene graft copolymer and (ii) 5 parts by mass or less of titanium oxide with respect to 100 parts by mass of the polystyrene-based resin. Or it is preferable to contain two or more additives.
[0027]
When the polystyrene graft copolymer is added, the low-temperature impact characteristics of the lining layer made of the resin composition are improved. However, if it is added in excess of 100 parts by mass, the cold / hot water cycle resistance and water hammer characteristics become insufficient.
[0028]
When titanium oxide is added, the chlorine water resistance is improved. However, if it is added in an amount exceeding 5 parts by mass, the resistance to cold and hot water cycle becomes insufficient.
[0029]
The method for manufacturing an inner surface lining steel pipe according to the present invention comprises a polystyrene resin, an additive material of at least one of a styrene elastomer and a rubber component, and a non-styrene elastomer, and 100 parts by mass of the polystyrene resin. On the other hand, the total content of at least one of the styrene elastomer and the rubber component is 3 parts by mass or more and 30 parts by mass or less, and the content of the non-styrene elastomer is 1 part by mass or more and 30 parts by mass or less. And the sum of the content of at least one of the styrene-based elastomer and the rubber component and the content of the non-styrene-based elastomer is 50 parts by weight or less, the diameter of the resin tube is reduced by heating, and the steel tube The resin tube is inserted into the tube and heated again to expand the diameter, and the resin tube is lined on the inner surface of the steel tube.
[0030]
Furthermore, an adhesive layer may be provided between the lining layer and the steel pipe. In this case, the resin tube may be a resin tube having an adhesive layer formed on the outer surface. As the adhesive layer, it is desirable to use a maleic anhydride-modified polystyrene or a hot melt adhesive. By providing the adhesive layer, the resin pipe can be firmly adhered to the inner surface of the steel pipe.
[0031]
(Function)
According to the resin composition of the present invention, the results of sufficiently satisfying chlorine water resistance, cold / hot water heat cycle resistance, water hammer resistance, dissolution property, low temperature impact resistance and the like required for the inner lining layer of water supply and hot water supply pipes Even when used for a long time, red water due to deformation or cracking of the lining layer does not occur.
[0032]
Furthermore, since the resin composition of the present invention is excellent in shape restoration property, as a method for producing a lining steel pipe, the resin composition molded into a tubular shape is reduced in diameter by heating to give shape restoration property. By inserting and heating again, the resin pipe expands and expands in diameter, and can be lined on the inner surface of the steel pipe.
[0033]
DETAILED DESCRIPTION OF THE INVENTION
FIG. 1 is an enlarged cross-sectional view schematically showing a part of an inner lining steel pipe according to an embodiment of the present invention. FIG. 1 shows an example in which an adhesive layer is provided between an inner surface of a steel pipe and a lining layer, wherein 1 is an inner surface lining steel pipe, 2 is a steel pipe, 3 is an adhesive layer, and 4 is a lining layer (resin composition).
[0034]
Various preferred embodiments of the present invention will be described below.
[0035]
(Steel pipe)
The steel pipe used in the present invention may be subjected to blasting, pickling, chemical conversion, plating, primer treatment, or plastic lining on the outer surface of the steel pipe. Also, the inner surface of the steel pipe may be subjected to blasting, pickling, chemical conversion, plating, etc., and thermosetting epoxy resins, thermosetting urethane resins, heat Primer treatment with a curable phenol resin, phenoxy resin, or polyester resin may be performed, and an adhesive layer may be interposed between them and the lining layer as necessary, as will be described later. The steel pipe has an outer diameter of about 10 to 2000 mm, usually about 20 to 170 mm, a length of about 3 to 10 m, usually about 4 to 6 m, and a wall thickness of about 2.0 to 5.3 mm. Use.
[0036]
(Polystyrene resin)
The polystyrene resin used for the lining layer is a known general-purpose resin, and is a homopolymer or copolymer having repeating units of vinyl aromatic compounds or derivatives thereof as shown in the following general formula including most typical styrene. It is a polymer.
[0037]
[Chemical 1]
[0038]
In the above formula, R represents hydrogen or an alkyl group, R ′ represents an alkyl group, a vinyl group, a halogen, or an amino group, and m represents 0 or an integer of 1 to 5.
[0039]
Typical examples include polystyrene, poly α-methylstyrene and the like, and these copolymers may be used. Polystyrene and poly α-methylstyrene include stereotactic atactic, syndiotactic and isotactic types, which can be used as appropriate. For example, in addition to normal atactic polystyrene, syndiotactic polystyrene and isotactic polystyrene can be used, and a mixture thereof can be used as appropriate. Moreover, the copolymer of such an aromatic vinyl compound and a non-aromatic compound may be sufficient. Representative examples include styrene-acrylonitrile copolymers, styrene-maleic anhydride copolymers, styrene-methyl methacrylate copolymers, and the like.
[0040]
(Rubber / styrene elastomer)
The styrene-based elastomer component may be a known thermoplastic styrene-based elastomer, which may be a copolymer of styrene and a diene component such as butadiene or isoprene, or a hydrogenated product thereof. As the rubber component, any known rubber may be used. Specific examples include styrene-based, butadiene-based, isoprene-based, acrylic-based, or ethylene-propylene-based rubbers, hydrogenated products thereof, and the like.
[0041]
Further, as the polystyrene having a rubber or elastomer component, polystyrene having improved impact resistance such as HIPS (high impact polystyrene) may be used.
[0042]
The resin composition of the present invention contains one or more elastomer components and / or rubber components selected from the group of elastomer components and the group of rubber components.
[0043]
(Non-styrene elastomer)
The non-styrene elastomer is a thermoplastic elastomer that does not contain a styrene component, and a polyester elastomer in which an aliphatic polyether such as polytetramethylene glycol and an aromatic polyester such as polybutylene terephthalate are combined, Polyamide elastomers in which crystalline polyamides such as polyamides 6, 66, 11, and 12 are bonded to polyethers such as polyoxyethylene, polyoxypropylene, and polytetramethylene glycol, and non-styrene olefins such as ethylene and propylene It is possible to use a thermoplastic polyolefin elastomer comprising a resin having a monomer as a monomer, and a urethane elastomer obtained by copolymerizing an isocyanate and a polyether or polyester such as polytetramethylene glycol. In addition, a blend resin in which two or more kinds of these resins are mixed as necessary may be used, and plastics, colorants, pigments, fillers, flame retardants, antioxidants, ultraviolet absorbers, and the like as long as the performance is not impaired. Additives such as charging materials, lubricants, and tackifiers can be added.
[0044]
(Composition ratio)
In these resin compositions, the non-styrene elastomer is 1 to 30 parts by mass, more preferably 1 to 10 parts by mass with respect to 100 parts by mass of the polystyrene resin, and 3 in total with respect to 100 parts by mass of the polystyrene resin. It is necessary to contain -30 parts by mass of rubber and / or styrene elastomer. The total content of the non-styrene elastomer and the total content of the styrene elastomer and the rubber component needs to be 50 parts by weight or less.
[0045]
Although the reason is not clear, even if the amount of non-styrene elastomer is less than 1 part by mass or more than 30 parts by mass, the cold / hot water cycle characteristics that simulate the actual use environment are insufficient. When the total content of rubber and styrene elastomer component is less than 3 parts by mass with respect to 100 parts by mass of polystyrene resin, the impact resistance is lowered, and when it exceeds 30 parts by mass, a cold / hot water cycle that simulates the actual use environment Performance and water hammer resistance deteriorates. Further, even if the total content of the non-styrene elastomer and the total content of the styrene elastomer and the rubber component exceeds 50 parts by weight, the cold / hot water cycle performance and the water hammer resistance are deteriorated. In order to further improve the lining characteristics, the content of the non-styrene elastomer is preferably suppressed to 10 parts by mass or less.
[0046]
The inner surface lining steel pipe having the lining layer made of the resin composition on the inner surface of the steel pipe is excellent in chlorine water resistance, cold / hot water cycle resistance, water hammer resistance, dissolution property, and low temperature impact resistance. Moreover, this inner surface lining steel pipe can be manufactured by the efficient method using the heat restoring property of the resin composition.
[0047]
(Polystyrene graft copolymer)
In addition, a polystyrene graft copolymer may be added to the resin composition of the present invention in order to improve low temperature impact characteristics.
[0048]
The polystyrene graft copolymer is a polymer in which a polystyrene polymer is grafted to an olefin compound alone or a copolymer. Specific examples of the olefin compound alone or copolymer include polyethylene, ethylene ethyl acrylate. A copolymer, an ethylene vinyl acetate copolymer, an ethylene glycidyl methacrylate copolymer, an ethylene ethyl acrylate maleic anhydride copolymer, and in particular, the ester-based monomer content in these copolymers is 10 to 25% by mass, A maleic anhydride monomer content of 10% by mass or less is desirable. In addition, some copolymerization monomers may be mixed in the polystyrene polymer as long as the performance is not impaired. One type of polystyrene graft copolymer may be added, or two or more types may be added.
[0049]
These rubber or styrene elastomer components are preferably 30 parts by mass or less with respect to 100 parts by mass of the polystyrene resin. Moreover, it is preferable that addition of a polystyrene graft copolymer shall be 100 mass parts or less with respect to 100 mass parts of polystyrene resins. If it is added excessively beyond these, the cold / hot water cycle performance and water hammer characteristics will be insufficient. Furthermore, the lining characteristic of a resin pipe improves by setting it as 50 mass parts or less.
[0050]
(Titanium oxide)
In addition, titanium oxide may be added to the resin composition of the present invention in order to improve chlorine water resistance.
[0051]
The titanium oxide may be a known one and may be a rutile type or anatase type, and the particle size is not particularly limited, but a particle size of 30 μm or less is preferable in consideration of uniform dispersion in the resin composition. The addition amount is preferably 0.1 parts by mass or more and 5 parts by mass or less with respect to 100 parts by mass of the polystyrene-based resin. If it exceeds 5 parts by weight, the cold / hot water cycle characteristics become insufficient.
[0052]
(Mixing of resin composition)
The mixing of these resin compositions can be carried out by using a known general method as a resin kneading method, and can be carried out by kneading with a kneader or an extruder at a high temperature, particularly rubber and elastomer components. In some cases, it may be added at the time of polymerization of polystyrene resin, or may be polymerized simultaneously with polystyrene polymerization.
[0053]
In addition, pigments such as azo, phthalocyanine, anthraquinone, indigo, titania, bengara, carbon black, calcium carbonate, barium sulfate, talc, silica, clay, and the like are combined for coloring and other purposes. A pigment may be added.
[0054]
In addition, the resin composition may be mixed with other resins based on the resin composition as long as it does not impair the performance of the present invention. If necessary, an antioxidant, an ultraviolet absorber, and a light resistant stability Additives such as an agent, a flame retardant, a filler, a lubricant, an antistatic agent, and a tackifier can be added.
[0055]
(Adhesive layer)
Further, by providing the
[0056]
In addition, the adhesive may be mixed with other adhesives or other resins as long as the performance of the present invention is not impaired, and an antioxidant, an ultraviolet absorber, a light stabilizer, Additives such as plasticizers, flame retardants, pigments, colorants, fillers, lubricants, antistatic agents and tackifiers can be added.
[0057]
(Manufacturing method of inner lining steel pipe)
As a lining method, the above resin composition is kneaded and mixed by a known method, and then crushed and powdered, and then heated in a powder coating method in which the inner surface of a heated steel pipe is sprayed or in a powder flow tank A fluid dipping method for dipping a steel pipe is applicable.
[0058]
In addition, since the resin composition of the present invention has a shape restoring property, it can be applied to a shape restoring method as a method with high production efficiency. Here, the shape restoring property is a characteristic that, when the resin tube is reduced in diameter after being heated and then cooled again, the resin composition is expanded at a rate equal to or higher than the linear expansion coefficient inherent in the resin composition. The shape restoration method is a method in which a resin pipe having an outer diameter larger than the inner diameter of the steel pipe to be lined is reduced to a diameter smaller than the inner diameter of the steel pipe under heating, and the resin pipe obtained by cooling is put into the steel pipe. In this method, the resin tube is inserted, expanded again by heating, and the resin tube is lined on the inner surface of the steel tube.
[0059]
Specifically, first, the resin composition of the present invention is extruded into a pipe shape from a mold by a normal method, and the outer diameter is fixed while cooling the resin to below the solidification temperature using a sizing die, a water-cooled shower or the like. Thus, the resin pipe has an outer diameter larger than the inner diameter of the steel pipe. Thereafter, in order to impart shape restoring properties, the resin tube is heated up to a glass transition temperature or higher of the resin composition using an infrared heating furnace, a microwave heating furnace, a high-frequency heating furnace, a hot air furnace, or the like. Alternatively, it is preferable to reduce the diameter until the outer diameter is smaller than the inner diameter of the steel pipe in a temperature range equal to or higher than the glass transition temperature, and to cool the structure, thereby providing shape restoration properties.
[0060]
This reduced diameter employs a line in which a heating furnace and a cooling bath are arranged between two take-up machines, and draws in the longitudinal direction of the pipe by utilizing the speed difference between the two take-up machines. A method of reducing the diameter by passing through a die having a taper whose outlet side diameter is smaller than the inner diameter of the steel pipe, or a method of reducing the diameter in the radial direction with a roll or the like can be applied. Also, in order to stabilize the shape in these processes, the inside of the pipe is pressurized by a method such as sending air into the inside of the pipe, or the outside of the pipe is decompressed to improve the follow-up of the molded product to the mold. It is also possible to apply a method such as sucking on the.
[0061]
In addition, when the resin composition is extruded from the mold into a pipe shape, the resin temperature may be equal to or higher than the glass transition temperature, and the diameter may be reduced by the above method while cooling the resin composition.
[0062]
The size of the resin pipe after the diameter reduction is usually set to an outer diameter of 12 to 158 mm and a wall thickness of 0.4 to 4.5 mm in consideration of the size of the pipe to be lined, workability, economy, and the like. However, it is not particularly limited to this.
[0063]
Further, the glass transition temperature of the resin composition can be obtained by a commonly performed method such as differential scanning calorimetry.
[0064]
When the diameter of the resin tube is reduced below the glass transition temperature, necking or the like occurs, and the diameter cannot be stably reduced. Further, when the shape is restored, it becomes non-uniform and the inner surface of the steel tube cannot be lined cleanly.
[0065]
When an adhesive layer is provided between the lining layer and the steel pipe, a maleic anhydride-modified polystyrene or a hot-melt adhesive (hereinafter referred to as maleic anhydride-modified polystyrene or a hot-melt adhesive) Etc.) may be blown and fused to the inner surface of the steel pipe, or an adhesive layer may be formed by coating the outer surface of the resin pipe with an adhesive or the like. When coating the outer surface of the resin tube with an adhesive or the like, a method of coating the surface of the resin tube with a crosshead round die or a T-die before or after imparting shape restoring properties, or a film shape in advance A method of winding an adhesive or the like around the surface of a resin tube, or a method of co-extruding a resin that becomes a lining layer with a multilayer mold and an adhesive or the like can be applied. Usually, the thickness of the adhesive layer is 0.05 to 0.8 mm, but is not particularly limited thereto.
[0066]
The resin tube for lining produced in this way is inserted into a steel tube and heated in a high-frequency heating furnace, a hot air furnace or the like, preferably the resin tube is at a temperature higher than the [glass transition temperature −10 ° C.] of the resin composition, More preferably, by heating to a temperature equal to or higher than the glass transition temperature, the resin tube expands and is lined to the inner surface of the steel tube.
[0067]
In this shape restoration process, not only heating, but also a method of further promoting heating expansion by blowing compressed air or the like into the inside of the resin tube, or a temperature rise by sealing both ends of the resin tube. There is also a method of further promoting heating expansion by increasing the volume of air in the resin tube.
[0068]
The heating temperature of the resin tube is set as described above when the resin tube temperature at the time of heating is lower than [glass transition temperature−10 ° C.], the resin tube is insufficiently expanded in diameter and between the steel tube and the lining layer. It is based on the knowledge that the resin tube can be stably expanded by heating to a temperature higher than the glass transition temperature.
[0069]
Further, in order to facilitate the escape of air between the steel pipe and the resin pipe, it is preferable to heat from the center of the pipe to both ends or from one pipe end to the other end. Furthermore, since heat is hardly transmitted to the resin pipe near the end of the steel pipe, heat treatment may be performed after lining. After the resin pipe is in close contact with the inner surface of the steel pipe, it is cooled and an inner resin lining steel pipe can be obtained by cutting the resin pipe portion protruding from the end of the steel pipe.
[0070]
【Example】
Hereinafter, the inner surface resin-lined steel pipe of the present invention will be described based on examples in which the resin pipe is lined and manufactured on the inner surface of the steel pipe by the shape restoration method. However, the present invention is limited only to the following examples. It is not something.
[0071]
(Examples 1 to 29, Comparative Examples 1 to 11, 13, 15 to 21)
Various raw materials were kneaded in advance with a single or twin screw extruder or a kneader to obtain resin pellets having the compositions shown in Tables 1-6. However, a numerical part shows mass ratio. In addition, in the polystyrene graft ethylene ethyl acrylate copolymer and the polystyrene graft ethylene vinyl acetate copolymer in Tables 1 to 6, the composition of the copolymer grafted with the polystyrene polymer is as shown below.
1) Ethylene ethyl acrylate copolymer: Ethyl acrylate content 20% by mass
2) Ethylene vinyl acetate copolymer: 15% by mass of vinyl acetate
[0072]
[Table 1]
[0073]
[Table 2]
[0074]
[Table 3]
[0075]
[Table 4]
[0076]
[Table 5]
[0077]
[Table 6]
[0078]
The resin pipe for lining was continuously manufactured in a molding line generally arranged in the order of an extruder, a mold, a cooling tank, a take-up machine, a heating furnace, a cooling tank, a take-up machine, and a pipe cutting machine.
[0079]
First, immediately after extruding a resin having the composition shown in Tables 1 to 6 into a pipe shape having an outer diameter of 29.0 to 30.0 mm from a round die at a predetermined temperature, the pipe surface is cooled to 40 ° C. or lower, and then While heating in the heating furnace so that the pipe outer surface reaches the temperature shown in Tables 1 to 6, the outer diameter of the pipe becomes 25.8 mm due to the speed difference between the two take-up machines arranged before and after the heating furnace. Thus, the pipe was expanded and contracted in diameter, cooled in a cooling water tank, and a lining resin tube having an outer diameter of 25.8 mm and a wall thickness of 0.8 to 1.2 mm was produced.
[0080]
The prepared resin tube was 4 m and 50 cm in length, and was inserted into a pickled pipe having a nominal diameter of 25A (inner diameter: 27.6 mmφ, outer diameter: 34 mmφ × 4 m). Thereafter, the resin tubes are shown in Tables 1-6. The steel pipe was heated with a high-frequency heating device so as to reach a temperature, and the resin pipe was heated and expanded to line the inner surface of the steel pipe. Further, the resin portion protruding from the end of the steel pipe was cut to obtain a lining steel pipe.
[0081]
(Comparative Example 12)
Although produced by the same method as in Example 1, two types of resins listed in Table 6 were coextruded into a pipe shape having an outer diameter of 30.0 mm so that the thickness ratio of the two layers was inner layer: outer layer = 7: 3. Then, after cooling it, while heating in the heating furnace so that the outer surface of the pipe reaches 105 ° C., the outer diameter of the pipe becomes 26.0 mm due to the difference in speed between the two take-up machines placed before and after the heating furnace. The pipe was expanded and contracted in diameter, and cooled in a cooling water tank to produce a lining resin tube having an outer diameter of 26.0 mm and a wall thickness of about 1.4 mm.
[0082]
The produced resin tube is 4 m 50 cm in length and is inserted into a pickled steel pipe having a nominal diameter of 25A (inner diameter 27.6 mmφ, outer diameter 34 mmφ × 4 m), and then the resin tube is at 105 ° C. The steel pipe was heated with a high-frequency heating device (the temperature of the steel pipe at this time was 128 ° C.), and the resin pipe was heated and expanded to line the inner surface of the steel pipe. Further, the resin portion protruding from the end of the steel pipe was cut to obtain a lining steel pipe.
[0083]
(Comparative Example 14)
Although produced by the same method as in Example 1, the resins listed in Table 6 were extruded into a pipe shape having an outer diameter of 30.0 mm and cooled to obtain a resin pipe. The resin pipe was immersed in a hot water bath at 80 ° C. for 24 hours for crosslinking treatment. The gel fraction of the resin pipe after the treatment according to JIS K6769 was 32%. While this pipe is heated in a heating furnace so that the outer surface of the pipe reaches 140 ° C., the outer diameter of the pipe is extended to 26.0 mm due to the speed difference between the two take-up machines placed before and after the heating furnace. The resin pipe for lining having an outer diameter of 26.0 mm and a wall thickness of about 1.4 mm was prepared by expanding and contracting and cooling in a cooling water tank.
[0084]
The prepared resin tube is 4 m 50 cm in length, and is inserted into a pickled steel tube (nominal diameter 27.6 mmφ, outer diameter 34 mmφ × 4 m) having a nominal diameter of 25A, and then the resin tube is 140 ° C. The steel pipe was heated by a high-frequency heating device (the temperature of the steel pipe at this time was 170 ° C.), and the resin pipe was heated and expanded to line the inner surface of the steel pipe. Further, the resin portion protruding from the end of the steel pipe was cut to obtain a lining steel pipe.
[0085]
The evaluation was made on the diameter-reducing characteristics, the lining characteristics, the cold / hot water cycle characteristics, the low-temperature impact characteristics, the dissolution properties, the water hammer characteristics, and the chlorine water resistance. When the lining characteristics were evaluated as x, only the cold / hot water cycle characteristics were evaluated, and the low-temperature impact characteristics, elution characteristics, water hammer characteristics, and chlorine water resistance were not evaluated.
[0086]
<Reduction characteristics>
When the diameter of the expanded tube is reduced, the resin tube is torn, or the cross-sectional shape is severely deformed and the cross-sectional shape is crushed. Measured at 10 points, “○” indicates that the variation was less than ± 5% of the target outer diameter, while the pipe diameter was good, but the variation was ± 5% or more of the target outer diameter “△”.
[0087]
<Lining characteristics>
After lining, cut the lining steel pipe at 10 cm pitch at 10 locations, observe the cross section, and if the lining layer is at least 0.5 mm away from the inner surface of the steel pipe, the lining characteristic is “△”. Visually, the lining layer and the steel pipe When there was no gap between the gap and the gap was less than 0.5 mm, “◯”, and when there was a portion where there was almost no change with respect to the outer diameter of the resin tube before lining “×” "
[0088]
<Cooling water cycle characteristics>
A lining steel pipe is cut to a length of 50 cm, a cycle of flowing 85 ° C. hot water for 10 minutes and room temperature water for 10 minutes is performed 10,000 times, and then the change of the lining layer is observed, the lining layer contracts and expands, Deformation such as peeling or cracks on the inner surface, red water is generated “X”, red water is not generated “○”, the lining layer is not changed such as deformation or crack generation “◎”.
[0089]
<Low temperature impact characteristics>
The tip is a hemisphere with a radius of R20mm and a weight of 6.3kg is placed on the center outer surface of a horizontally fixed lining steel pipe at -8 ° C at a height of less than 0.8m and the steel pipe is not exposed. "◎", the steel pipe inner surface exposed at a height of 0.8m, but the steel pipe was not exposed when dropped from a height of 0.5m, "○", the steel pipe exposed even at a height of 0.5m It was set as “x”.
[0090]
<Elution properties>
The elution from the lining material into tap water was evaluated by the consumption of potassium permanganate. The method conformed to JIS K6769, and the consumption was 2 mg / L or less as “◯”, and when the consumption was larger than that, “×”.
[0091]
<Water hammer characteristics>
Water hammer characteristics were evaluated according to JWWA (Waterworks Association) standards. The flow rate of water flowing on the inner surface of the lining steel pipe was 2.64 m / sec, and the valve was opened and closed 300 times with the pressure at the time of opening and closing the valve being 1.9 kgf / cm 2 or more, and the subsequent lining layer was deformed. The thing which was not deform | transformed was set as "(circle)".
[0092]
<Chlorine resistant water>
The chlorine water resistance of the resin composition was evaluated by the method of JIS K6762. “◎◎” indicates that no bubbles were generated in the lining layer after 1000 hours, “○” indicates that bubbles were generated after 1000 hours, but no bubbles were generated after 168 hours. In the following, an abnormality such as the generation of water bubbles was indicated as “x”.
[0093]
The evaluation results are shown in Tables 7 and 8.
[0094]
[Table 7]
[0095]
[Table 8]
[0096]
Regarding the diameter-reducing characteristics and the lining characteristics, except for Examples 9, 10, 23 and 27 and Comparative Examples 5 to 9, 19 and 20, which were evaluated as Δ or ×, all other Examples and Comparative Examples ○ It was evaluation.
[0097]
Regarding the hot and cold water cycle characteristics, all Examples 1 to 29 were evaluated as “good” or better, while Comparative Examples 1 to 21 were all evaluated as “x”.
[0098]
In Comparative Examples 19 and 20, when the resin pipe is lined on the inner surface of the steel pipe by the shape restoration method, the temperature condition at the time of diameter reduction and the diameter expansion time is outside the preferable temperature range. Is evaluated as x, and these properties deteriorate the properties of the inner surface lining layer and the cold / hot water cycle characteristics.
[0099]
The low temperature impact characteristics were evaluated as ○ in Examples 1 to 20 and 26 to 29, and evaluated as 実 施 in Examples 21 to 25, whereas in Comparative Examples 3, 13, and 18, the evaluation was x.
[0100]
The dissolution property was evaluated as “Good” in all Examples 1 to 29, whereas “Comparative Example 14” was evaluated as x.
[0101]
The water hammer characteristics were evaluated as “Good” in all Examples 1 to 29, while “Poor” was evaluated in Comparative Examples 5 to 9, 11, and 12.
[0102]
With respect to the chlorine-resistant aqueous solution, a particularly excellent evaluation result was obtained in Example 26. In other examples, the evaluation was good, whereas in Comparative Example 13, the evaluation was x.
[0103]
From the above results, it was confirmed that the internally lined steel pipe according to the present invention has sufficient performance as a pipe for water supply and hot water supply as well as cold / hot water cycle performance.
[0104]
(Examples 30 to 47)
Further, after producing a lining resin tube under the conditions shown in Table 9 in the same manner as in Example 1, the adhesive shown in Table 9 was melt-extruded from a crosshead die on the outer surface of the resin tube. The resin tube for lining with an adhesive layer was prepared by coating to 1 mm and cooling immediately after coating.
[0105]
The produced resin pipe is 4 m and 50 cm in length, and is inserted into a pickled steel pipe having a nominal diameter of 25 A (inner diameter: 27.6 mmφ, outer diameter: 34 mmφ × 4 m). Thereafter, the inner surface of the steel pipe is subjected to the conditions shown in Table 9 below. Lining. Further, the resin portion protruding from the end of the steel pipe was cut to obtain a lining steel pipe.
[0106]
Evaluation was made by measuring the punching shear adhesive force when cutting the lining steel pipe into 2 cm length, holding the outer steel pipe part, and pushing only the inner lining resin layer in the axial direction, 100 N / cm 2 or more In the case of ◯, “◯”, and in the case of less than 100 N / cm 2 , “△”. The evaluation results are shown in Table 9.
[0107]
[Table 9]
[0108]
In Examples 30, 36 and 42 in which no adhesive was used, the initial adhesive force was less than 100 N / cm 2 .
[0109]
Thus, it was confirmed that the adhesion between the steel pipe and the lining layer can be improved by providing an adhesive layer made of maleic anhydride-modified polystyrene or a hot-melt adhesive.
[0110]
【The invention's effect】
The inner surface resin-lined steel pipe of the present invention is excellent in chlorine water resistance, cold / hot water cycle resistance, water hammer resistance, elution property, and low temperature impact resistance, and has high adhesion between the lining layer and the steel pipe, and further utilizes heat resilience. Can be manufactured in an efficient manner.
[0111]
The inner lining steel pipe of the present invention has sufficient performance necessary for piping used for water supply pipes, hot water supply pipes, air conditioning or drainage, and is suitable for use in these applications.
[Brief description of the drawings]
FIG. 1 is an enlarged sectional view schematically showing a part of an inner lining steel pipe of the present invention.
[Explanation of symbols]
DESCRIPTION OF SYMBOLS 1 ... Inner
Claims (10)