JP2005003841A - Heat developable photosensitive material - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a heat developable photosensitive material improved in image color tone and image preservability. <P>SOLUTION: The heat developable photosensitive material contains a photosensitive silver halide, a non-photosensitive organic silver salt, a reducing agent, a binder and a coupler which colors upon heat development on the same surface of a support, wherein a silver iodide content of the photosensitive silver halide is ≥40 mol% and a dye produced by the coupler is capable of forming a hydrogen bond in a molecule. <P>COPYRIGHT: (C)2005,JPO&NCIPI

Description

【００１５】
〔式（Ｉａ）、または（Ｉｂ）において、Ｒ_１１〜Ｒ_１５は水素原子またはベンゼン環に置換し得る置換基を表し、Ｘはアリール基、ヘテロ環基または活性メチン基を表わし、Ｒ_１１〜Ｒ_１５、およびＸの少なくとも１つが少なくとも１つの水素結合性の置換基を有する。〕
＜５＞ 前記式（Ｉａ）、または（Ｉｂ）において、Ｒ_１２が２級または３級のアルキル基であることを特徴とする＜４＞に記載の熱現像感光材料。
＜６＞ 前記式（Ｉａ）、または（Ｉｂ）で表される発色剤が、下記式（ＩＩａ）、または（ＩＩｂ）で表されることを特徴とする＜４＞または＜５＞に記載の熱現像感光材料。
【００１６】
【化４】

【００１７】
〔式（ＩＩａ）、または（ＩＩｂ）において、Ｒ_２１〜Ｒ_２７は、水素原子またはベンゼン環に置換し得る置換基を表す。Ｙ_２１、Ｙ_２２は、水素原子またはベンゼン環に置換し得る置換基を表し、少なくともその一方はヒドロキシ基またはアミノ基であり、Ｒ_２１〜Ｒ_２７、Ｙ_２１、およびＹ_２２の少なくとも１つが少なくとも１つの水素結合性の置換基を有する。〕
＜７＞ 前記式（ＩＩａ）、または（ＩＩｂ）において、Ｒ_２２は２級または３級のアルキル基であり、Ｒ_２５またはＲ_２６の少なくとも一方が水素結合性の置換基であることを特徴とする＜６＞に記載の熱現像感光材料。
＜８＞ 前記発色剤より生成する色素が、分子内で水素結合することにより５〜７員の環を形成し得ることを特徴とする＜１＞〜＜７＞のいずれかに記載の熱現像感光材料。
＜９＞ 前記感光性ハロゲン化銀のヨウ化銀含有率が８０モル％以上であることを特徴とする＜１＞〜＜８＞のいずれかに記載の熱現像感光材料。
＜１０＞ 前記感光性ハロゲン化銀のヨウ化銀含有率が９０モル％以上であることを特徴とする＜１＞〜＜９＞のいずれかに記載の熱現像感光材料。
＜１１＞ 現像促進剤を含有することを特徴とする＜１＞〜＜１０＞のいずれかに記載の熱現像感光材料。
＜１２＞ レーザー光により走査露光されることを特徴とする＜１＞〜＜１１＞のいずれかに記載の熱現像感光材料。
＜１３＞ 前記レーザー光が半導体レーザーであることを特徴とする＜１２＞に記載の熱現像感光材料。
＜１４＞ 前記半導体レーザーが青色半導体レーザーであることを特徴とする＜１３＞に記載の熱現像感光材料。
＜１５＞ 熱現像時間が１０秒以内で熱現像されることを特徴とする＜１＞〜＜１４＞のいずれかに記載の熱現像感光材料。
【００１８】
【発明の実施の形態】
以下に本発明を詳細に説明する。
（熱現像によって発色し得る発色剤の説明）
本発明の熱現像によって発色し得る発色剤とは、熱現像を施した時、露光されていない非画像部では実質的に色素を形成せず、現像銀が形成された画像部で色素を形成する化合物を言う。この化合物は単独で発色する化合物でもよく、２種以上の化合物のカップリング反応、脱離反応、およびその他の反応により色素を形成するものであってもよい。
【００１９】
熱現像において生成する銀画像は、多くの場合、ニュートラルな色よりマゼンタ成分が多いので、本発明の発色剤により形成される色素はイエローまたはシアン領域に吸収を持つことが好ましい。生成色素の波長領域で言うと、３５０ｎｍ〜５００ｎｍのイエロー領域または、６００ｎｍ〜７００ｎｍのシアン領域に吸収の７０％以上がある化合物が好ましい。特に３５０ｎｍ〜５００ｎｍ領域に７０％以上がある化合物が好ましく、３８０ｎｍ〜４６０ｎｍの領域に７０％以上の吸収がある化合物がより好ましい。
【００２０】
発色の効率の向上、すなわち、より少量の発色剤の添加量で有効に発色することは、素材の使用量が削減できるので感材のコストの観点から好ましく、この見地では単独で発色する化合物がより好ましい。
【００２１】
本発明の発色剤から生成する色素は、分子内で水素結合を形成し得ることが特徴である。水素結合とは、水素原子が２個の陰性な原子の間にあって、２価のように見える結合のことを言う。好ましい水素結合の例としては、Ｏ−Ｈ・・・Ｏ、Ｎ−Ｈ・・・Ｏ、Ｏ−Ｈ・・・Ｎ、Ｎ−Ｈ・・・Ｎ、Ｎ−Ｈ・・・Ｃｌ、Ｎ−Ｈ・・・Ｆ、Ｏ−Ｈ・・・Ｃｌ等が挙げられる。
【００２２】
上記のＯ−Ｈとは例えば、１級、２級、３級のアルコール類、フェノール類、エノール類、Ｎ−ヒドロキシカルバモイル類、カルボン酸類、Ｎ−ヒドロキシウレイド類、ヒドロキシアミノ類、−ＮＨＣＯ−基の互変異性体である−Ｎ＝Ｃ（ＯＨ）−基等に含まれるものが挙げられる。
【００２３】
上記のＮ−Ｈとは例えば、１級または２級のアミノ類、カルバモイル類、アシルアミノ類、スルホンアミド基、スルファモイル類、ウレイド基、カルバメート類、セミカルバジド類、ヒドラジノ類、イミド類、ヒドロキシアミノ類等に含まれるものが挙げられる。
【００２４】
上記のＯとは例えば、ヘテロ環類、アシル類、アルコキシカルボニル類、カルバモイル類、カルボン酸類、オキサリル類、アルコール類、フェノール類、エーテル類、アシルアミノ類、ウレイド類、ニトロ基等に含まれるものが挙げられる。
【００２５】
上記のＮとは例えば、含窒素ヘテロ環類、Ｎ−ヒドロキシカルバモイル類、シアノ基、アミノ基、（アルキル，アリール，またはヘテロ環）アミノ類、イミド類、ヒドラジノ基、ヒドロキシアミノ基、イミノ基等に含まれるものが挙げられる。
【００２６】
該水素結合は、水素結合を形成することにより、好ましくは５〜７員環を形成する場合であり、より好ましくは５または６員環を形成する場合である。
【００２７】
本発明において好ましい発色剤は、下記式（Ｉａ）、または（Ｉｂ）で表される化合物である。
【００２８】
【化５】

【００２９】
式（Ｉａ）、または（Ｉｂ）において、Ｒ_１１〜Ｒ_１５は水素原子またはベンゼン環に置換し得る置換基を表わし、Ｒ_１１〜Ｒ_１５、およびＸの少なくとも１つが少なくとも１つの水素結合性の置換基を有する。
【００３０】
Ｒ_１１〜Ｒ_１５は水素原子またはベンゼン環に置換し得る置換基を表す。ここで言うベンゼン環に置換し得る置換基とは、例えばハロゲン原子（フッ素原子、クロル原子、臭素原子、または沃素原子）、アルキル基（直鎖、分岐、環状のアルキル基で、ビシクロアルキル基、活性メチン基を含む）、アルケニル基、アルキニル基、アリール基、ヘテロ環基（置換する位置は問わない）、アシル基、アルコキシカルボニル基、アリールオキシカルボニル基、ヘテロ環オキシカルボニル基、カルバモイル基、Ｎ−ヒドロキシカルバモイル基、Ｎ−アシルカルバモイル基、Ｎ−スルホニルカルバモイル基、Ｎ−カルバモイルカルバモイル基、チオカルバモイル基、Ｎ−スルファモイルカルバモイル基、カルバゾイル基、カルボキシ基またはその塩、オキサリル基、オキサモイル基、シアノ基、カルボンイミドイル基（Ｃａｒｂｏｎｉｍｉｄｏｙｌ基）、ホルミル基、ヒドロキシ基、アルコキシ基（エチレンオキシ基もしくはプロピレンオキシ基単位を繰り返し含む基を含む）、アリールオキシ基、ヘテロ環オキシ基、アシルオキシ基、（アルコキシもしくはアリールオキシ）カルボニルオキシ基、カルバモイルオキシ基、スルホニルオキシ基、アミノ基、（アルキル，アリール，またはヘテロ環）アミノ基、アシルアミノ基、スルホンアミド基、ウレイド基、チオウレイド基、Ｎ−ヒドロキシウレイド基、イミド基、（アルコキシもしくはアリールオキシ）カルボニルアミノ基、スルファモイルアミノ基、セミカルバジド基、チオセミカルバジド基、ヒドラジノ基、アンモニオ基、オキサモイルアミノ基、Ｎ−（アルキルもしくはアリール）スルホニルウレイド基、Ｎ−アシルウレイド基、Ｎ−アシルスルファモイルアミノ基、ヒドロキシアミノ基、ニトロ基、４級化された窒素原子を含むヘテロ環基（例えばピリジニオ基、イミダゾリオ基、キノリニオ基、イソキノリニオ基）、イソシアノ基、イミノ基、メルカプト基、（アルキル，アリール，またはヘテロ環）チオ基、（アルキル，アリール，またはヘテロ環）ジチオ基、（アルキルまたはアリール）スルホニル基、（アルキルまたはアリール）スルフィニル基、スルホ基またはその塩、スルファモイル基、Ｎ−アシルスルファモイル基、Ｎ−スルホニルスルファモイル基またはその塩、ホスフィノ基、ホスフィニル基、ホスフィニルオキシ基、ホスフィニルアミノ基、シリル基等が挙げられる。なおここで活性メチン基とは２つの電子求引性基で置換されたメチン基を意味し、ここに電子求引性基とはアシル基、アルコシキカルボニル基、アリールオキシカルボニル基、カルバモイル基、アルキルスルホニル基、アリールスルホニル基、スルファモイル基、トリフルオロメチル基、シアノ基、ニトロ基、カルボンイミドイル基（Ｃａｒｂｏｎｉｍｉｄｏｙｌ基）を意味する。ここで２つの電子求引性基は互いに結合して環状構造をとっていてもよい。また塩とは、アルカリ金属、アルカリ土類金属、重金属などの陽イオンや、アンモニウムイオン、ホスホニウムイオンなどの有機の陽イオンを意味する。これら置換基は、これら置換基でさらに置換されていてもよい。
【００３１】
式（Ｉａ）、または（Ｉｂ）において、Ｒ_１２は好ましくはアルキル基であり、さらに好ましくは２級または３級のアルキル基であり、特に好ましくは３級のアルキル基である。
式（Ｉａ）、または（Ｉｂ）において、Ｒ_１１、Ｒ_１３〜Ｒ_１５は、水素原子またはアルキル基、アリール基が好ましく、さらに好ましいものは水素原子またはアルキル基である。
【００３２】
式（Ｉａ）、または（Ｉｂ）において、Ｘは炭素数６〜３０、好ましくは６〜２０の置換もしくは無置換のアリール基、炭素数１〜３０、好ましくは１〜２０の置換もしくは無置換の、芳香族もしくは非芳香族の、飽和もしくは不飽和のヘテロ環基、活性メチン基（活性メチン基とは２つの電子求引性基で置換されたメチン基を意味し、ここに電子求引性基とはハメットの置換基定数σｐ値が正の値を示す基、例えばアシル基、アルコシキカルボニル基、アリールオキシカルボニル基、カルバモイル基、アルキルスルホニル基、アリールスルホニル基、スルファモイル基、トリフルオロメチル基、シアノ基、ニトロ基、カルボンイミドイル基（Ｃａｒｂｏｎｉｍｉｄｏｙｌ基）等である。ここで２つの電子求引性基は互いに結合して環状構造をとっていてもよい。）を表す。
【００３３】
式（Ｉａ）、または（Ｉｂ）において、Ｘは二つ以上の置換基を有していることが好ましく、該置換基とは前述のＲ_１１〜Ｒ_１５で説明した置換基と同義である。ここでこれらの置換基は生成した色素の構造において、水素ドナーと水素アクセプターとなり、互いに水素結合を形成するものが好ましい。このような置換基として好ましい基は、ハロゲン原子（フッ素原子、クロル原子、臭素原子、または沃素原子）、アシル基、アルコキシまたはアリールオキシカルボニル基、カルバモイル基、カルボキシ基またはその塩、オキサリル基、オキサモイル基、ホルミル基、ヒドロキシ基、アシルオキシ基、アミノ基、（アルキル，アリール，またはヘテロ環）アミノ基、アシルアミノ基、スルホンアミド基、ウレイド基、イミド基、（アルコキシもしくはアリールオキシ）カルボニルアミノ基、ニトロ基、イミノ基、スルファモイル基等が挙げられる。
【００３４】
式（Ｉａ）、または（Ｉｂ）において、Ｘは置換アリール基、置換芳香族ヘテロ環基、活性メチン基が好ましく、特に置換アリール基が好ましい。
【００３５】
本発明の発色剤の構造は、下記式（ＩＩａ）、または（ＩＩｂ）で表されるものがより好ましい。
【００３６】
【化６】

【００３７】
式（ＩＩａ）、または（ＩＩｂ）において、Ｒ_２１〜Ｒ_２７は、水素原子またはベンゼン環に置換し得る置換基をあり、Ｙ_２１、およびＹ_２２は、水素原子またはベンゼン環に置換し得る置換基を表し、少なくともその一方はヒドロキシ基またはアミノ基であり、Ｒ_２１〜Ｒ_２７、Ｙ_２１、およびＹ_２２の少なくとも１つが少なくとも１つの水素結合性の置換基を有する。〕ここでいう置換基とは前述の式（Ｉａ）、または（Ｉｂ）のＲ_１１〜Ｒ_１５で表される置換基と同義である。
【００３８】
Ｒ_２２の好ましい範囲は前述した式（Ｉａ）、または（Ｉｂ）のＲ_１２の好ましい範囲と同じであり、２級または３級のアルキル基が好ましい。
【００３９】
Ｒ_２５またはＲ_２６の少なくとも一方が水素結合性の置換基であることが好ましい。この水素結合性置換基は、色素の構造によって水素ドナーまたは水素アクセプターとなる。この場合の好ましい置換基は例えばハロゲン原子（フッ素原子、クロル原子、臭素原子、または沃素原子）、アシル基、アルコキシまたはアリールオキシカルボニル基、カルバモイル基、カルボキシ基またはその塩、オキサリル基、オキサモイル基、ホルミル基、ヒドロキシ基、アシルオキシ基、アミノ基、（アルキル，アリール，またはヘテロ環）アミノ基、アシルアミノ基、スルホンアミド基、ウレイド基、イミド基、（アルコキシもしくはアリールオキシ）カルボニルアミノ基、ニトロ基、イミノ基、スルファモイル基等が挙げられる。
【００４０】
Ｙ_２１、Ｙ_２２は、水素原子またはベンゼン環に置換し得る置換基を表し、少なくとも一方はヒドロキシ基または（無置換、アルキル、アリールまたはヘテロ環）アミノ基であり、より好ましくはヒドロキシ基である。
【００４１】
式（Ｉａ）、または（Ｉｂ）、あるいは式（ＩＩａ）、または（ＩＩｂ）で表される発色剤から生成する色素の構造を下記に示す。下記色素構造においてＹ_２１またはＹ_２２がヒドロキシ基のときのようにケト−エノール互変異性体が存在する場合、該互変異性体のいずれか一方において分子内水素結合が形成可能であればよい。
【００４２】
【化７】

【００４３】
本発明の発色剤には、ハロゲン化銀に対して吸着し得る吸着性の基が組み込まれていてもよい。かかる吸着基としては、アルキルチオ基、アリールチオ基、チオ尿素基、チオアミド基、メルカプト複素環基、トリアゾール基などの米国特許第４，３８５，１０８号、同４，４５９，３４７号、特開昭５９−１９５２３３号、同５９−２００２３１号、同５９−２０１０４５号、同５９−２０１０４６号、同５９−２０１０４７号、同５９−２０１０４８号、同５９−２０１０４９号、特開昭６１−１７０７３３号、同６１−２７０７４４号、同６２−９４８号、同６３−２３４２４４号、同６３−２３４２４５号、同６３−２３４２４６号に記載された基があげられる。またこれらハロゲン化銀への吸着基は、プレカーサー化されていてもよい。その様なプレカーサーとしては、特開平２ー２８５３４４号に記載された基が挙げられる。
【００４４】
本発明の発色剤には、その中にカプラー等の不動性写真用添加剤において常用されているバラスト基またはポリマーが組み込まれているものでもよい。バラスト基は８以上の炭素数を有する、写真性に対して比較的不活性な基であり、例えばアルキル基、アラルキル基、アルコキシ基、フェニル基、アルキルフェニル基、フェノキシ基、アルキルフェノキシ基などの中から選ぶことができる。またポリマーとしては、例えば特開平１−１００５３０号に記載のものが挙げられる。
【００４５】
本発明の発色剤の分子量は、好ましくは２００〜１００００であり、さらに好ましくは３００〜２０００であり、特に好ましくは４００〜１０００である。
【００４６】
以下に本発明の好ましい化合物の具体例を挙げるが、本発明はこれらの化合物に限定されるものではない。
【００４７】
【化８】

【００４８】
【化９】

【００４９】
【化１０】

【００５０】
【化１１】

【００５１】
【化１２】

【００５２】
本発明の発色剤は溶液形態、乳化分散形態、固体微粒子分散物形態など、いかなる方法で塗布液に含有せしめ、感光材料に含有させてもよい。よく知られている乳化分散法としては、ジブチルフタレート、トリクレジルフォスフェート、グリセリルトリアセテートあるいはジエチルフタレートなどのオイル、酢酸エチルやシクロヘキサノンなどの補助溶媒を用いて溶解し、機械的に乳化分散物を作製する方法が挙げられる。
【００５３】
また、固体微粒子分散法としては、発色剤の粉末を水等の適当な溶媒中にボールミル、コロイドミル、振動ボールミル、サンドミル、ジェットミル、ローラーミルあるいは超音波によって分散し、固体分散物を作成する方法が挙げられる。尚、その際に保護コロイド（例えば、ポリビニルアルコール）、界面活性剤（例えばトリイソプロピルナフタレンスルホン酸ナトリウム（３つのイソプロピル基の置換位置が異なるものの混合物）などのアニオン性界面活性剤）を用いてもよい。上記ミル類では分散媒体としてジルコニア等のビーズが使われるのが普通であり、これらのビーズから溶出するＺｒ等が分散物中に混入することがある。分散条件にもよるが通常は１ｐｐｍ〜１０００ｐｐｍの範囲である。感材中のＺｒの含有量が銀１ｇ当たり０．５ｍｇ以下であれば実用上差し支えない。水分散物には防腐剤（例えばベンゾイソチアゾリノンナトリウム塩）を含有させることが好ましい。
特に好ましいのは、発色剤の固体粒子分散法であり、平均粒子サイズ０．０１μｍ〜１０μｍ、好ましくは０．０５μｍ〜５μｍ、より好ましくは０．１μｍ〜２μｍの微粒子して添加するのが好ましい。本願においては他の固体分散物もこの範囲の粒子サイズに分散して用いるのが好ましい。
【００５４】
本発明において発色剤の添加量は、０．１ｍｇ／ｍ^２〜３ｇ／ｍ^２の範囲が好ましく、より好ましくは１ｍｇ／ｍ^２〜１ｇ／ｍ^２、特に好ましくは２ｍｇ／ｍ^２〜０．５ｇ／ｍ^２である。
【００５５】
（非感光性有機銀塩の説明）
１）組成
本発明に用いることのできる有機銀塩は、光に対して比較的安定であるが、露光された感光性ハロゲン化銀及び還元剤の存在下で、８０℃或いはそれ以上に加熱された場合に銀イオン供給体として機能し、銀画像を形成せしめる銀塩である。有機銀塩は還元剤により還元されうる銀イオンを供給できる任意の有機物質であってよい。このような非感光性の有機銀塩については、特開平１０−６２８９９号の段落番号００４８〜００４９、欧州特許公開第０８０３７６４Ａ１号の第１８ページ第２４行〜第１９ページ第３７行、欧州特許公開第０９６２８１２Ａ１号、特開平１１−３４９５９１号、特開２０００−７６８３号、同２０００−７２７１１号等に記載されている。有機酸の銀塩、特に（炭素数が１０〜３０、好ましくは１５〜２８の）長鎖脂肪族カルボン酸の銀塩が好ましい。脂肪酸銀塩の好ましい例としては、リグノセリン酸銀、ベヘン酸銀、アラキジン酸銀、ステアリン酸銀、オレイン酸銀、ラウリン酸銀、カプロン酸銀、ミリスチン酸銀、パルミチン酸銀、エルカ酸銀およびこれらの混合物などを含む。本発明においては、これら脂肪酸銀の中でも、ベヘン酸銀含有率が好ましくは５０モル％以上１００モル％以下、より好ましくは８５モル％以上１００モル％以下、さらに好ましくは９５モル％以上１００モル％以下の脂肪酸銀を用いることが好ましい。更に、エルカ酸銀含有率が２モル％以下、より好ましくは１モル％以下、更に好ましくは０．１モル％以下の脂肪酸銀を用いることが好ましい。
【００５６】
また、ステアリン酸銀含有率が１モル％以下であることが好ましい。前記ステアリン酸銀含有率を１モル％以下とすることにより、Ｄｍｉｎが低く、高感度で画像保存性に優れた有機酸の銀塩が得られる。前記ステアリン酸銀含有率としては、０．５モル％以下が好ましく、実質的に含まないことが特に好ましい。
【００５７】
さらに、有機酸の銀塩としてアラキジン酸銀を含む場合は、アラキジン酸銀含有率が６モル％以下であることが、低いＤｍｉｎを得ること及び画像保存性の優れた有機酸の銀塩を得る点で好ましく、３モル％以下であることが更に好ましい。
【００５８】
２）形状
本発明に用いることができる有機銀塩の形状としては特に制限はなく、針状、棒状、平板状、りん片状いずれでもよい。
本発明においてはりん片状の有機銀塩が好ましい。また、長軸と単軸の長さの比が５以下の短針状、直方体、立方体またはジャガイモ状の不定形粒子も好ましく用いられる。これらの有機銀粒子は長軸と単軸の長さの比が５を越える長針状粒子に比べて熱現像時のカブリが少ないという特徴を有している。特に、長軸と単軸の比が３以下の粒子は塗布膜の機械的安定性が向上し好ましい。本明細書において、りん片状の有機銀塩とは、次のようにして定義する。有機酸銀塩を電子顕微鏡で観察し、有機酸銀塩粒子の形状を直方体と近似し、この直方体の辺を一番短かい方からａ、ｂ、ｃとした（ｃはｂと同じであってもよい。）とき、短い方の数値ａ、ｂで計算し、次のようにしてｘを求める。
ｘ＝ｂ／ａ
【００５９】
このようにして２００個程度の粒子についてｘを求め、その平均値ｘ（平均）としたとき、ｘ（平均）≧１．５の関係を満たすものをりん片状とする。好ましくは３０≧ｘ（平均）≧１．５、より好ましくは１５≧ｘ（平均）≧１．５である。因みに針状とは１≦ｘ（平均）＜１．５である。
【００６０】
りん片状粒子において、ａはｂとｃを辺とする面を主平面とした平板状粒子の厚さとみることができる。ａの平均は０．０１μ 以上０．３μｍ 以下が好ましく０．１μｍ 以上０．２３μｍ 以下がより好ましい。ｃ／ｂの平均は１以上９以下であることが好ましく、より好ましくは１以上６以下、さらに好ましくは１以上４以下、最も好ましくは１以上３以下である。
【００６１】
前記球相当直径を０．０５μｍ以上１μｍ以下とすることにより、感光材料中で凝集を起こしにくく、画像保存性が良好となる。前記球相当直径としては、０．１μｍ以上１μｍ以下が好ましい。本発明において、球相当直径の測定方法は、電子顕微鏡を用いて直接サンプルを撮影し、その後、ネガを画像処理することによって求められる。
前記リン片状粒子において、粒子の球相当直径／ａをアスペクト比と定義する。リン片状粒子のアスペクト比としては、感光材料中で凝集を起こしにくく、画像保存性が良好となる観点から、１．１以上３０以下であることが好ましく、１．１以上１５以下がより好ましい。
【００６２】
有機銀塩の粒子サイズ分布は単分散であることが好ましい。単分散とは短軸、長軸それぞれの長さの標準偏差を短軸、長軸それぞれで割った値の１００分率が好ましくは１００％以下、より好ましくは８０％以下、更に好ましくは５０％以下である。有機銀塩の形状の測定方法としては有機銀塩分散物の透過型電子顕微鏡像より求めることができる。単分散性を測定する別の方法として、有機銀塩の体積加重平均直径の標準偏差を求める方法があり、体積加重平均直径で割った値の百分率（変動係数）が好ましくは１００％以下、より好ましくは８０％以下、更に好ましくは５０％以下である。測定方法としては例えば液中に分散した有機銀塩にレーザー光を照射し、その散乱光のゆらぎの時間変化に対する自己相関関数を求めることにより得られた粒子サイズ（体積加重平均直径）から求めることができる。
【００６３】
３）調製
本発明に用いられる有機酸銀の製造及びその分散法は、公知の方法等を適用することができる。例えば上記の特開平１０−６２８９９号、欧州特許公開第０８０３７６３Ａ１、欧州特許公開第０９６２８１２Ａ１号、特開平１１−３４９５９１号、特開２０００−７６８３号、同２０００−７２７１１号、同２００１−１６３８８９号、同２００１−１６３８９０号、同２００１−１６３８２７号、同２００１−３３９０７号、同２００１−１８８３１３号、同２００１−８３６５２号、同２００２−６４４２、同２００２−４９１１７号、同２００２−３１８７０号、同２００２−１０７８６８号等を参考にすることができる。
【００６４】
なお、有機銀塩の分散時に、感光性銀塩を共存させると、カブリが上昇し、感度が著しく低下するため、分散時には感光性銀塩を実質的に含まないことがより好ましい。本発明では、分散される水分散液中での感光性銀塩量は、その液中の有機酸銀塩１ｍｏｌに対し１ｍｏｌ％以下であることが好ましく、より好ましくは０．１ｍｏｌ％以下であり、さらに好ましいのは積極的な感光性銀塩の添加を行わないものである。
【００６５】
本発明において有機銀塩水分散液と感光性銀塩水分散液を混合して感光材料を製造することが可能であるが、有機銀塩と感光性銀塩の混合比率は目的に応じて選べるが、有機銀塩に対する感光性銀塩の割合は１モル％〜３０モル％の範囲が好ましく、更に２モル％〜２０モル％、特に３モル％〜１５モル％の範囲が好ましい。混合する際に２種以上の有機銀塩水分散液と２種以上の感光性銀塩水分散液を混合することは、写真特性の調節のために好ましく用いられる方法である。
【００６６】
４）添加量
本発明の有機銀塩は所望の量で使用できるが、ハロゲン化銀も含めた全塗布銀量として０．１ ｇ／ｍ^２〜５．０ｇ／ｍ^２が好ましく、より好ましくは０．５ ｇ／ｍ^２〜３．０ｇ／ｍ^２、さらに好ましくは０．８ ｇ／ｍ^２〜１．９ｇ／ｍ^２である。特に、画像保存性を向上させるためには、全塗布銀量が１．７ｇ／ｍ^２以下、より好ましくは１．５ｇ／ｍ^２以下であることが好ましい。本発明の好ましい還元剤を使用すれば、このような低銀量においても十分な画像濃度をが可能である。
【００６７】
（還元剤の説明）
本発明の熱現像感光材料には有機銀塩のための還元剤である熱現像剤を含むことが好ましい。有機銀塩のための還元剤は、銀イオンを金属銀に還元する任意の物質（好ましくは有機物質）であってよい。このような還元剤の例は、特開平１１−６５０２１号の段落番号００４３〜００４５や、欧州特許公開第０８０３７６４Ａ１号の第７ページ第３４行〜第１８ページ第１２行に記載されている。
【００６８】
本発明において、還元剤としてはフェノール性水酸基のオルト位に置換基を有するいわゆるヒンダードフェノール系還元剤あるいはビスフェノール系還元剤が好ましく、下記一般式（Ｒ）で表される化合物がより好ましい。
【００６９】
一般式（Ｒ）
【化１３】

【００７０】
（一般式（Ｒ）において、Ｒ^１１およびＲ^１１’は各々独立に炭素数１〜２０のアルキル基を表す。Ｒ^１２およびＲ^１２’は各々独立に水素原子またはベンゼン環に置換可能な置換基を表す。Ｌは−Ｓ−基または−ＣＨＲ^１３−基を表す。Ｒ^１３は水素原子または炭素数１〜２０のアルキル基を表す。Ｘ^１およびＸ^１’は各々独立に水素原子またはベンゼン環に置換可能な基を表す。）
【００７１】
一般式（Ｒ）について詳細に説明する。
１）Ｒ^１１およびＲ^１１’
Ｒ^１１およびＲ^１１’は各々独立に置換または無置換の炭素数１〜２０のアルキル基であり、アルキル基の置換基は特に限定されることはないが、好ましくは、アリール基、ヒドロキシ基、アルコキシ基、アリールオキシ基、アルキルチオ基、アリールチオ基、アシルアミノ基、スルホンアミド基、スルホニル基、ホスホリル基、アシル基、カルバモイル基、エステル基、ウレイド基、ウレタン基、ハロゲン原子等があげられる。
【００７２】
２）Ｒ^１２およびＲ^１２’、Ｘ^１およびＸ^１’
Ｒ^１２およびＲ^１２’は各々独立に水素原子またはベンゼン環に置換可能な置換基であり、Ｘ^１およびＸ^１’も各々独立に水素原子またはベンゼン環に置換可能な基を表す。それぞれベンゼン環に置換可能な基としては、好ましくはアルキル基、アリール基、ハロゲン原子、アルコキシ基、アシルアミノ基があげられる。
【００７３】
３）Ｌ
Ｌは−Ｓ−基または−ＣＨＲ^１３−基を表す。Ｒ^１３は水素原子または炭素数１〜２０のアルキル基を表し、アルキル基は置換基を有していてもよい。Ｒ^１３の無置換のアルキル基の具体例はメチル基、エチル基、プロピル基、ブチル基、ヘプチル基、ウンデシル基、イソプロピル基、１−エチルペンチル基、２，４，４−トリメチルペンチル基、シクロヘキシル基、２，４−ジメチル−３−シクロヘキセニル基、２，４−ジメチル−３−シクロヘキセニル基などがあげられる。アルキル基の置換基の例はＲ^１１の置換基と同様で、ハロゲン原子、アルコキシ基、アルキルチオ基、アリールオキシ基、アリールチオ基、アシルアミノ基、スルホンアミド基、スルホニル基、ホスホリル基、オキシカルボニル基、カルバモイル基、スルファモイル基などがあげられる。
【００７４】
４）好ましい置換基
Ｒ^１１およびＲ^１１’として好ましくは炭素数１〜１５の１級、２級または３級のアルキル基であり、具体的にはメチル基、イソプロピル基、ｔ−ブチル基、ｔ−アミル基、ｔ−オクチル基、シクロヘキシル基、シクロペンチル基、１−メチルシクロヘキシル基、１−メチルシクロプロピル基などがあげられる。Ｒ^１１およびＲ^１１’としてより好ましくは炭素数１〜４のアルキル基で、その中でもメチル基、ｔ−ブチル基、ｔ−アミル基、１−メチルシクロヘキシル基が更に好ましく、メチル基、ｔ−ブチル基が最も好ましい。
【００７５】
Ｒ^１２およびＲ^１２’として好ましくは炭素数１〜２０のアルキル基であり、具体的にはメチル基、エチル基、プロピル基、ブチル基、イソプロピル基、ｔ−ブチル基、ｔ−アミル基、シクロヘキシル基、１−メチルシクロヘキシル基、ベンジル基、メトキシメチル基、メトキシエチル基などがあげられる。より好ましくはメチル基、エチル基、プロピル基、イソプロピル基、ｔ−ブチル基であり、特に好ましくはメチル基、エチル基である。
Ｘ^１およびＸ^１’は、好ましくは水素原子、ハロゲン原子、アルキル基で、より好ましくは水素原子である。
【００７６】
Ｌは好ましくは−ＣＨＲ^１３−基である。
Ｒ^１３として好ましくは水素原子または炭素数１〜１５のアルキル基であり、該アルキル基としては鎖状のアルキル基の他、環状のアルキル基も好ましく用いられる。また、これらのアルキル基の中にＣ＝Ｃ結合を有しているものも好ましく用いることができる。アルキル基としては例えばメチル基、エチル基、プロピル基、イソプロピル基、２，４，４−トリメチルペンチル基、シクロヘキシル基、２，４−ジメチル−３−シクロヘキセニル基、３，５−ジメチル−３−シクロヘキセニル基等が好ましい。Ｒ^１３として特に好ましいのは水素原子、メチル基、エチル基、プロピル基、イソプロピル基、２，４−ジメチル−３−シクロヘキセニル基である。
【００７７】
Ｒ^１１、Ｒ^１１’が３級のアルキル基でＲ^１２、Ｒ^１２’がメチル基の場合、Ｒ^１３は炭素数１〜８の１級または２級のアルキル基（メチル基、エチル基、プロピル基、イソプロピル基、２，４−ジメチル−３−シクロヘキセニル基等）が好ましい。
Ｒ^１１、Ｒ^１１’が３級のアルキル基でＲ^１２、Ｒ^１２’がメチル基以外のアルキル基の場合、Ｒ^１３は水素原子が好ましい。
Ｒ^１１、Ｒ^１１’が３級のアルキル基でない場合、Ｒ^１３は水素原子または２級のアルキル基であることが好ましく、２級のアルキル基であることが特に好ましい。Ｒ^１３の２級アルキル基として好ましい基はイソプロピル基、２，４−ジメチル−３−シクロヘキセニル基である。
上記還元剤はＲ^１１、Ｒ^１１’、Ｒ^１２、Ｒ^１２’およびＲ^１３の組み合わせにより、熱現像性、現像銀色調などが異なる。２種以上の還元剤を組み合わせることでこれらを調整することができるため、目的によっては２種以上を組み合わせて使用することが好ましい。
【００７８】
以下に本発明の一般式（Ｒ）で表される化合物をはじめとする本発明の還元剤の具体例を示すが、本発明はこれらに限定されるものではない。
【００７９】
【化１４】

【００８０】
【化１５】

【００８１】
上記以外の本発明の好ましい還元剤の例は特開２００１−１８８３１４号、同２００１−２０９１４５号、同２００１−３５０２３５号、同２００２−１５６７２７号、ＥＰ１２７８１０１Ａ２号に記載された化合物である。
【００８２】
本発明において還元剤の添加量は０．１ｇ／ｍ^２〜３．０ｇ／ｍ^２であることが好ましく、より好ましくは０．２ｇ／ｍ^２〜１．５ｇ／ｍ^２で、さらに好ましくは０．３ｇ／ｍ^２〜１．０ｇ／ｍ^２である。画像形成層を有する面の銀１モルに対しては５モル％〜５０モル％含まれることが好ましく、より好ましくは８モル％〜３０モル％であり、１０モル％〜２０モル％で含まれることがさらに好ましい。還元剤は画像形成層に含有させることが好ましい。
【００８３】
還元剤は溶液形態、乳化分散形態、固体微粒子分散物形態など、いかなる方法で塗布液に含有せしめ、感光材料に含有させてもよい。
よく知られている乳化分散法としては、ジブチルフタレート、トリクレジルフォスフェート、グリセリルトリアセテートあるいはジエチルフタレートなどのオイル、酢酸エチルやシクロヘキサノンなどの補助溶媒を用いて溶解し、機械的に乳化分散物を作製する方法が挙げられる。
【００８４】
また、固体微粒子分散法としては、還元剤の粉末を水等の適当な溶媒中にボールミル、コロイドミル、振動ボールミル、サンドミル、ジェットミル、ローラーミルあるいは超音波によって分散し、固体分散物を作成する方法が挙げられる。尚、その際に保護コロイド（例えば、ポリビニルアルコール）、界面活性剤（例えばトリイソプロピルナフタレンスルホン酸ナトリウム（３つのイソプロピル基の置換位置が異なるものの混合物）などのアニオン性界面活性剤）を用いてもよい。上記ミル類では分散媒体としてジルコニア等のビーズが使われるのが普通であり、これらのビーズから溶出するＺｒ等が分散物中に混入することがある。分散条件にもよるが通常は１ｐｐｍ〜１０００ｐｐｍの範囲である。感材中のＺｒの含有量が銀１ｇ当たり０．５ｍｇ以下であれば実用上差し支えない。
【００８５】
水分散物には防腐剤（例えばベンゾイソチアゾリノンナトリウム塩）を含有させることが好ましい。
【００８６】
特に好ましいのは、還元剤の固体粒子分散法であり、平均粒子サイズ０．０１μｍ〜１０μｍ、好ましくは０．０５μｍ〜５μｍ、より好ましくは０．１μｍ〜２μｍの微粒子して添加するのが好ましい。本願においては他の固体分散物もこの範囲の粒子サイズに分散して用いるのが好ましい。
【００８７】
（感光性ハロゲン化銀）
１）ハロゲン組成
本発明に用いられる感光性ハロゲン化銀は、ヨウ化銀含有率が４０モル％以上、１００モル％以下と高い組成のものであることが重要である。残りは特に制限はなく、塩化銀、臭化銀またはチオシアン酸銀や燐酸銀などの有機銀塩から選ぶことができるが、特に臭化銀、塩化銀であることが好ましい。この様なヨウ化銀含有率が高い組成のハロゲン化銀を用いることによって、現像処理後の画像保存性、特に光照射によるカブリの増加が著しく小さい好ましい熱現像感光材料が設計できる。
【００８８】
さらに、ヨウ化銀含有率が８０モル％以上１００モル％以下であると好ましく、特に９０モル％以上１００モル％以下であることが処理後の光照射に対する画像保存性の観点では極めて好ましい。
【００８９】
粒子内におけるハロゲン組成の分布は均一であってもよく、ハロゲン組成がステップ状に変化したものでもよく、或いは連続的に変化したものでもよい。また、コア／シェル構造を有するハロゲン化銀粒子も好ましく用いることができる。構造として好ましいものは２〜５重構造であり、より好ましくは２〜４重構造のコア／シェル粒子を用いることができる。コア部のヨウ化銀含有率が高いコア高ヨウ化銀構造、またはシェル部のヨウ化銀含有率が高いシェル高ヨウ化銀構造も好ましく用いることができる。また、粒子の表面にエピタキシャル部分とした塩化銀や臭化銀を局在させる技術も好ましく用いることができる。
【００９０】
２）粒子サイズ
本発明に用いる高ヨウ化銀のハロゲン化銀については、粒子サイズは特に重要である。ハロゲン化銀のサイズが大きいと、必要な最高濃度を達成するために必要なハロゲン化銀の塗布量が増加する。本発明者は、本発明で好ましく用いられるヨウ化銀含有率の高い組成のハロゲン化銀は、その塗布量が多いと現像が著しく抑制され低感化するとともに現像の時間に対する濃度安定性が悪化し好ましくなく、そのため一定以上の粒子サイズでは所定の現像時間で最高濃度が得られないことを見出した。一方、その添加量を制限すればヨウ化銀ながら十分な現像性を有することを発見した。
【００９１】
この様に高ヨウ化銀を用いた場合、十分な最高光学濃度を達成するためには、ハロゲン化銀粒子のサイズは従来の臭化銀や低ヨウド含量のヨウ臭化銀に比べて十分に小さいことが必要である。好ましいハロゲン化銀の粒子サイズは５ｎｍ以上７０ｎｍ以下であり、さらに５ｎｍ以上５５ｎｍ以下であることが好ましい。特に好ましくは１０ｎｍ以上４５ｎｍ以下である。ここでいう粒子サイズとは、電子顕微鏡により観察した投影面積と同面積の円像に換算したときの直径の平均をいう。
【００９２】
３）塗布量
この様なハロゲン化銀粒子の塗布量は、後述する非感光性有機銀塩の銀１モルに対して０．５モル％以上１５モル％以下、好ましくは０．５モル％以上１２モル％以下、１０モル％以下であることがさらに好ましい。１モル％以上９モル％以下であることがより好ましく、特に好ましくは１モル％以上７モル％以下である。本発明者の見出したヨウ化銀含有率の高い組成のハロゲン化銀による著しい現像抑制を押さえるためには、この添加量の選択は極めて重要である。
【００９３】
４）粒子形成方法
感光性ハロゲン化銀の形成方法は当業界ではよく知られており、例えば、リサーチディスクロージャー１９７８年６月の第１７０２９号、および米国特許第３，７００，４５８号に記載されている方法を用いることができるが、具体的にはゼラチンあるいは他のポリマー溶液中に銀供給化合物及びハロゲン供給化合物を添加することにより感光性ハロゲン化銀を調製し、その後で有機銀塩と混合する方法を用いる。また、特開平１１−１１９３７４号公報の段落番号０２１７〜０２２４に記載されている方法、特開平１１−３５２６２７号、特願２０００−４２３３６号記載の方法も好ましい。
【００９４】
５）粒子形状
本発明におけるハロゲン化銀粒子の形状としては、立方体、八面体、十二面体、十四面体、平板状粒子、球状粒子、棒状粒子、ジャガイモ状粒子等を挙げることができるが、本発明においては特に十二面体、十四面体が好ましい。ここでいう十二面体粒子とは、（００１）、｛１（−１）０｝、｛１０１｝面を有する粒子で、十四面体粒子とは、（００１）、｛１００｝、｛１０１｝面を有する粒子である。ここで｛１００｝は、（１００）面と等価な面指数を持つ結晶面群を表す。
【００９５】
本発明の沃化銀は任意のβ相およびγ相含有率を取ることができる。上記のβ相とは六方晶系のウルツァイト構造を有する高沃化銀構造を指し、γ相とは立方晶系のジンクブレンド構造を有する高沃化銀構造を指す。
【００９６】
ここでいう平均γ相比率とは、Ｃ．Ｒ． Ｂｅｒｒｙ （ベリー）により提案された手法を用いて決定されるものである。この手法は、粉末Ｘ線回折法での沃化銀β相（１００）、（１０１）、（００２）とγ相（１１１）によるピーク比を元にして決定するもので、詳細については例えば、Ｐｈｙｓｉｃａｌ Ｒｅｖｉｅｗ， Ｖｏｌｕｍｅ １６１， Ｎｕｍｂｅｒ ３， Ｐａｇｅ ８４８−８５１， １９６７年を参考にすることができる。
【００９７】
沃化銀の平板粒子の形成方法に関しては、特開昭５９−１１９３５０、特開昭５９−１１９３４４に記載の方法が好ましく用いられる。１２面体、１４面体、８面体に関しては、特願２００２−０８１０２０、同２００２−８７９５５、同２００２−９１７５６を参考にして調製することができる。
【００９８】
本発明のヨウ化銀含有率の高い組成のハロゲン化銀は複雑な形態を取り得るが、好ましい形態は例えば、Ｒ．Ｌ．ＪＥＮＫＩＮＳ ｅｔａｌ． Ｊ ｏｆ Ｐｈｏｔ． Ｓｃｉ． Ｖｏｌ．２８ （１９８０）のｐ１６４−Ｆｉｇ１に示されているような接合粒子が挙げられる。同Ｆｉｇ．１に示されているような平板状粒子も好ましく用いられる。ハロゲン化銀粒子のコーナーが丸まった粒子も好ましく用いることができる。感光性ハロゲン化銀粒子の外表面の面指数（ミラー指数）については特に制限はないが、分光増感色素が吸着した場合の分光増感効率が高い［１００］面の占める割合が高いことが好ましい。その割合としては５０％以上が好ましく、６５％以上がより好ましく、８０％以上が更に好ましい。ミラー指数［１００］面の比率は増感色素の吸着における［１１１］面と［１００］面との吸着依存性を利用したＴ．Ｔａｎｉ；Ｊ．Ｉｍａｇｉｎｇ Ｓｃｉ．，２９、１６５（１９８５年）に記載の方法により求めることができる。
【００９９】
６）重金属
本発明の感光性ハロゲン化銀粒子は、周期律表（第１〜１８族までを示す）の第８族〜第１０族の金属または金属錯体を含有することができる。周期律表の第８族〜第１０族の金属または金属錯体の中心金属として好ましくは、ロジウム、ルテニウム、イリジウムである。これら金属錯体は１種類でもよいし、同種金属及び異種金属の錯体を２種以上併用してもよい。好ましい含有率は銀１モルに対し１×１０^−９モルから１×１０^−３モルの範囲が好ましい。これらの重金属や金属錯体及びそれらの添加法については特開平７−２２５４４９号、特開平１１−６５０２１号段落番号００１８〜００２４、特開平１１−１１９３７４号段落番号０２２７〜０２４０に記載されている。
【０１００】
本発明においては、六シアノ金属錯体を粒子最表面に存在させたハロゲン化銀粒子が好ましい。六シアノ金属錯体としては、［Ｆｅ（ＣＮ）_６］^４−、［Ｆｅ（ＣＮ）_６］^３−、［Ｒｕ（ＣＮ）_６］^４−、［Ｏｓ（ＣＮ）_６］^４−、［Ｃｏ（ＣＮ）_６］^３−、［Ｒｈ（ＣＮ）_６］^３−、［Ｉｒ （ＣＮ）_６］^３−、［Ｃｒ（ＣＮ）_６］^３−、［Ｒｅ（ＣＮ）_６］^３−などが挙げられる。本発明においては六シアノＦｅ錯体が好ましい。
【０１０１】
六シアノ金属錯体は、水溶液中でイオンの形で存在するので対陽イオンは重要ではないが、水と混和しやすく、ハロゲン化銀乳剤の沈澱操作に適合しているナトリウムイオン、カリウムイオン、ルビジウムイオン、セシウムイオンおよびリチウムイオン等のアルカリ金属イオン、アンモニウムイオン、アルキルアンモニウムイオン（例えばテトラメチルアンモニウムイオン、テトラエチルアンモニウムイオン、テトラプロピルアンモニウムイオン、テトラ（ｎ−ブチル）アンモニウムイオン）を用いることが好ましい。
【０１０２】
六シアノ金属錯体は、水の他に水と混和しうる適当な有機溶媒（例えば、アルコール類、エーテル類、グリコール類、ケトン類、エステル類、アミド類等）との混合溶媒やゼラチンと混和して添加することができる。
【０１０３】
六シアノ金属錯体の添加量は、銀１モル当たり１×１０^−５モル以上１×１０^−２モル以下が好ましく、より好ましくは１×１０^−４モル以上１×１０^−３モル以下である。
【０１０４】
六シアノ金属錯体をハロゲン化銀粒子最表面に存在させるには、六シアノ金属錯体を、粒子形成に使用する硝酸銀水溶液を添加終了した後、硫黄増感、セレン増感およびテルル増感のカルコゲン増感や金増感等の貴金属増感を行う化学増感工程の前までの仕込工程終了前、水洗工程中、分散工程中、または化学増感工程前に直接添加する。ハロゲン化銀微粒子を成長させないためには、粒子形成後速やかに六シアノ金属錯体を添加することが好ましく、仕込工程終了前に添加することが好ましい。
【０１０５】
尚、六シアノ金属錯体の添加は、粒子形成をするために添加する硝酸銀の総量の９６質量％を添加した後から開始してもよく、９８質量％添加した後から開始するのがより好ましく、９９質量％添加した後が特に好ましい。
これら六シアノ金属錯体を粒子形成の完了する直前の硝酸銀水溶液を添加した後に添加すると、ハロゲン化銀粒子最表面に吸着することができ、そのほとんどが粒子表面の銀イオンと難溶性の塩を形成する。この六シアノ鉄（ＩＩ）の銀塩は、ＡｇＩよりも難溶性の塩であるため、微粒子による再溶解を防ぐことができ、粒子サイズが小さいハロゲン化銀微粒子を製造することが可能となった。
【０１０６】
さらに本発明に用いられるハロゲン化銀粒子に含有することのできる金属原子（例えば［Ｆｅ（ＣＮ）_６］^４−）、ハロゲン化銀乳剤の脱塩法や化学増感法については特開平１１−８４５７４号段落番号００４６〜００５０、特開平１１−６５０２１号段落番号００２５〜００３１、特開平１１−１１９３７４号段落番号０２４２〜０２５０に記載されている。
【０１０７】
７）ゼラチン
本発明に用いる感光性ハロゲン化銀乳剤に含有されるゼラチンとしては、種々のゼラチンが使用することができる。感光性ハロゲン化銀乳剤の有機銀塩含有塗布液中での分散状態を良好に維持するために、分子量は、５００〜６０，０００の低分子量ゼラチンを使用することが好ましい。これらの低分子量ゼラチンは粒子形成時あるいは脱塩処理後の分散時に使用してもよいが、脱塩処理後の分散時に使用することが好ましい。
【０１０８】
８）化学増感
本発明に用いられる感光性ハロゲン化銀は、未化学増感でもよいが、カルコゲン増感法、金増感法、還元増感法の少なくとも１つの方法で化学増感されるのが好ましい。カルコゲン増感法としては、硫黄増感法、セレン増感法およびテルル増感法が挙げられる。
【０１０９】
硫黄増感においては、不安定硫黄化合物を用い、Ｐ．Ｇｒａｆｋｉｄｅｓ著、Ｃｈｉｍｉｅ ｅｔ Ｐｈｙｓｉｑｕｅ Ｐｈｏｔｏｇｒａｐｈｉｑｕｅ（Ｐａｕｌ Ｍｏｍｔｅｌ社刊、１９８７年、第５版）、Ｒｅｓｅａｒｃｈ Ｄｉｓｃｌｏｓｕｒｅ誌３０７巻３０７１０５号などに記載されている不安定硫黄化合物を用いる事が出来る。
【０１１０】
具体的には、チオ硫酸塩（例えばハイポ）、チオ尿素類（例えば、ジフェニルチオ尿素、トリエチルチオ尿素、ＮーエチルーＮ´ー（４ーメチルー２ーチアゾリル）チオ尿素、カルボキシメチルトリメチルチオ尿素）、チオアミド類（例えば、チオアセトアミド）、ローダニン類（例えば、ジエチルローダニン、５ーベンジリデン−Ｎ−エチルローダニン）、フォスフィンスルフィド類（例えば、トリメチルフォスフィンスルフィド）、チオヒダントイン類、４ーオキソーオキサゾリジンー２ーチオン類、ジスルフィド類またはポリスルフィド類（例えば、ジモルフォリンジスルフィド、シスチン、レンチオニン）、ポリチオン酸塩、元素状硫黄などの公知の硫黄化合物および活性ゼラチンなども用いることができる。特にチオ硫酸塩、チオ尿素類とローダニン類が好ましい。
【０１１１】
セレン増感においては、不安定セレン化合物を用い、特公昭４３ー１３４８９号、同４４ー１５７４８号、特開平４ー２５８３２号、同４ー１０９３４０号、同４ー２７１３４１号、同５ー４０３２４号、同５ー１１３８５号、特願平４ー２０２４１５号、同４ー３３０４９５号、同４ー３３３０３０号、同５ー４２０３号、同５ー４２０４号、同５ー１０６９７７号、同５ー２３６５３８号、同５ー２４１６４２号、同５ー２８６９１６号などに記載されているセレン化合物を用いる事が出来る。
【０１１２】
具体的には、コロイド状金属セレン、セレノ尿素類（例えば、Ｎ，Ｎージメチルセレノ尿素、トリフルオルメチルカルボニルートリメチルセレノ尿素、アセチルートリメチルセレノ尿素）、セレノアミド類（例えば、セレノアミド，Ｎ，Ｎージエチルフェニルセレノアミド）、フォスフィンセレニド類（例えば、トリフェニルフォスフィンセレニド、ペンタフルオロフェニルートリフェニルフォスフィンセレニド）、セレノフォスフェート類（例えば、トリーｐ−トリルセレノフォスフェート、トリ−ｎ−ブチルセレノフォスフェート）、セレノケトン類（例えば、セレノベンゾフェノン）、イソセレノシアネート類、セレノカルボン酸類、セレノエステル類、ジアシルセレニド類などを用いればよい。またさらに、特公昭４６ー４５５３号、同５２ー３４４９２号などに記載の非不安定セレン化合物、例えば亜セレン酸、セレノシアン酸塩、セレナゾール類、セレニド類なども用いる事が出来る。特に、フォスフィンセレニド類、セレノ尿素類とセレノシアン酸塩が好ましい。
【０１１３】
テルル増感においては、不安定テルル化合物を用い、特開平４ー２２４５９５号、同４ー２７１３４１号、同４ー３３３０４３号、同５ー３０３１５７号、同６−２７５７３号、同６−１７５２５８号、同６−１８０４７８号、同６−２０８１８６号、同６−２０８１８４号、同６−３１７８６７号、同７−１４０５７９号、同７−３０１８７９号、同７−３０１８８０号などに記載されている不安定テルル化合物を用いる事が出来る。
【０１１４】
具体的には、フォスフィンテルリド類（例えば、ブチルージイソプロピルフォスフィンテルリド、トリブチルフォスフィンテルリド、トリブトキシフォスフィンテルリド、エトキシージフェニルフォスフィンテルリド）、ジアシル（ジ）テルリド類（例えば、ビス（ジフェニルカルバモイル）ジテルリド、ビス（Ｎ−フェニルーＮ−メチルカルバモイル）ジテルリド、ビス（Ｎ−フェニルーＮーメチルカルバモイル）テルリド、ビス（Ｎ−フェニルーＮーベンジルカルバモイル）テルリド、ビス（エトキシカルボニル）テルリド）、テルロ尿素類（例えば、Ｎ，Ｎ´ージメチルエチレンテルロ尿素、Ｎ，Ｎ´ージフェニルエチレンテルロ尿素）テルロアミド類、テルロエステル類などを用いれば良い。特に、ジアシル（ジ）テルリド類とフォスフィンテルリド類が好ましく、特に特開平１１−６５０２１号段落番号００３０に記載の文献に記載の化合物、特開平５−３１３２８４号中の一般式（ＩＩ），（ＩＩＩ），（ＩＶ）で示される化合物がより好ましい。
【０１１５】
特に本発明のカルコゲン増感においてはセレン増感とテルル増感が好ましく、特にテルル増感が好ましい。
【０１１６】
金増感においては、Ｐ．Ｇｒａｆｋｉｄｅｓ著、Ｃｈｉｍｉｅ ｅｔ Ｐｈｙｓｉｑｕｅ Ｐｈｏｔｏｇｒａｐｈｉｑｕｅ（Ｐａｕｌ Ｍｏｍｔｅｌ社刊、１９８７年、第５版）、Ｒｅｓｅａｒｃｈ Ｄｉｓｃｌｏｓｕｒｅ誌３０７巻３０７１０５号に記載されている金増感剤を用いることができる。具体的には、塩化金酸、カリウムクロロオーレート、カリウムオーリチオシアネート、硫化金、金セレニドなどでありこれらにくわえて、米国特許第２６４２３６１号、同５０４９４８４号、同５０４９４８５号、同５１６９７５１号、同５２５２４５５号、ベルギー特許第６９１８５７などに記載の金化合物も用いることが出来る。またＰ．Ｇｒａｆｋｉｄｅｓ著、Ｃｈｉｍｉｅ ｅｔ Ｐｈｙｓｉｑｕｅ Ｐｈｏｔｏｇｒａｐｈｉｑｕｅ（Ｐａｕｌ Ｍｏｍｔｅｌ社刊、１９８７年、第５版）、Ｒｅｓｅａｒｃｈ Ｄｉｓｃｌｏｓｕｒｅ誌３０７巻３０７１０５号に記載されている金以外の、白金、パラジュウム、イリジュウムなどの貴金属塩を用いる事も出来る。
【０１１７】
金増感は単独で用いることもできるが、前記のカルコゲン増感と組み合わせて用いることが好ましい。具体的には金硫黄増感、金セレン増感、金テルル増感、金硫黄セレン増感、金硫黄テルル増感、金セレンテルル増感、金硫黄セレンテルル増感である。
【０１１８】
本発明においては、化学増感は粒子形成後で塗布前であればいかなる時期でも可能であり、脱塩後、（１）分光増感前、（２）分光増感と同時、（３）分光増感後、（４）塗布直前等があり得る。
【０１１９】
本発明で用いられるカルコゲン増感剤の使用量は、使用するハロゲン化銀粒子、化学熟成条件等によって変わるが、ハロゲン化銀１モル当たり１０^−８モル〜１０^−１モル、好ましくは１０^−７モル〜１０^−２モル程度を用いる。
同様に、本発明で用いられる金増感剤の添加量は種々の条件により異なるが、目安としてはハロゲン化銀１モル当たり１０^−７モル〜１０^−２モル、より好ましくは１０^−６モル〜５×１０^−３モルである。この乳剤を化学増感する環境条件としてはいかなる条件でも選択可能ではあるが、ｐＡｇとしては８以下、好ましくは７．０以下より６．５以下、とくに６．０以下、およびｐＡｇが１．５以上、好ましくは２．０以上、特に好ましくは２．５以上の条件であり、ｐＨとしては３〜１０、好ましくは４〜９、温度としては２０℃〜９５℃、好ましくは２５℃〜８０℃程度である。
【０１２０】
本発明においてカルコゲン増感や金増感に加えて、さらに還元増感も併用することができる。とくにカルコゲン増感と併用するのが好ましい。
還元増感法の具体的な化合物としてはアスコルビン酸、二酸化チオ尿素、ジメチルアミンボランが好ましく、その他に塩化第一スズ、アミノイミノメタンスルフィン酸、ヒドラジン誘導体、ボラン化合物、シラン化合物、ポリアミン化合物等を用いることが好ましい。還元増感剤の添加は、結晶成長から塗布直前の調製工程までの感光乳剤製造工程のどの過程でもよい。また、乳剤のｐＨを８以上またはｐＡｇを４以下に保持して熟成することにより還元増感することも好ましく、粒子形成中に銀イオンのシングルアディション部分を導入することにより還元増感することも好ましい。
還元増感剤の添加量としては、同様に種々の条件により異なるが、目安としてはハロゲン化銀１モル当たり１０^−７モル〜１０^−１モル、より好ましくは１０^−６モル〜５×１０^−２モルである。
【０１２１】
本発明で用いるハロゲン化銀乳剤には、欧州特許公開第２９３，９１７号公報に示される方法により、チオスルフォン酸化合物を添加してもよい。
本発明における感光性ハロゲン化銀粒子は、金増感、カルコゲン増感、の少なくとも１つの方法で化学増感されていることが高感度の熱現像感光材料を設計する点から好ましい。
【０１２２】
９）１電子酸化されて生成する１電子酸化体が１電子もしくはそれ以上の電子を放出し得る化合物
本発明における熱現像感光材料は、１電子酸化されて生成する１電子酸化体が１電子もしくはそれ以上の電子を放出し得る化合物を含有することが好ましい。該化合物は、単独、あるいは前記の種々の化学増感剤と併用して用いられ、ハロゲン化銀の感度増加をもたらすことができる。
【０１２３】
本発明の熱現像感光材料に含有される１電子酸化されて生成する１電子酸化体が１電子もしくはそれ以上の電子を放出し得る化合物とは以下のタイプ１〜５から選ばれる化合物である。
【０１２４】
（タイプ１）
１電子酸化されて生成する１電子酸化体が、引き続く結合開裂反応を伴って、さらに２電子以上の電子を放出し得る化合物。
（タイプ２）
１電子酸化されて生成する１電子酸化体が、引き続く結合開裂反応を伴って、さらにもう１電子を放出し得る化合物で、かつ同じ分子内にハロゲン化銀への吸着性基を２つ以上有する化合物。
（タイプ３）
１電子酸化されて生成する１電子酸化体が、引き続く結合形成過程を経た後に、さらに１電子もしくはそれ以上の電子を放出し得る化合物。
（タイプ４）
１電子酸化されて生成する１電子酸化体が、引き続く分子内の環開裂反応を経た後に、さらに１電子もしくはそれ以上の電子を放出し得る化合物。
（タイプ５）
Ｘ−Ｙで表される化合物においてＸは還元性基を、Ｙは脱離基を表し、Ｘで表される還元性基が１電子酸化されて生成する１電子酸化体が、引き続くＸ−Ｙ結合の開裂反応を伴ってＹを脱離してＸラジカルを生成し、そこからさらにもう１電子を放出し得る化合物。
【０１２５】
上記タイプ１およびタイプ３〜５の化合物のうち好ましいものは、「分子内にハロゲン化銀への吸着性基を有する化合物」であるか、または「分子内に、分光増感色素の部分構造を有する化合物」である。より好ましくは「分子内にハロゲン化銀への吸着性基を有する化合物」である。タイプ１〜４の化合物はより好ましくは「２つ以上のメルカプト基で置換された含窒素ヘテロ環基を吸着性基として有する化合物」である。
【０１２６】
タイプ１〜５の化合物について詳細に説明する。
タイプ１の化合物において「結合開裂反応」とは具体的に炭素−炭素、炭素−ケイ素、炭素−水素、炭素−ホウ素、炭素−スズ、炭素−ゲルマニウムの各元素間の結合の開裂を意味し、炭素−水素結合の開裂がさらにこれらに付随してもよい。タイプ１の化合物は１電子酸化されて１電子酸化体となった後に、初めて結合開裂反応を伴って、さらに２電子以上（好ましくは３電子以上）の電子を放出し得る化合物である。
【０１２７】
タイプ１の化合物のうち好ましい化合物は一般式（Ａ）、一般式（Ｂ）、一般式（１）、一般式（２）または一般式（３）で表される。
【０１２８】
一般式（Ａ）
【化１６】

【０１２９】
一般式（Ｂ）
【化１７】

【０１３０】
一般式（Ａ）においてＲＥＤ_１１は１電子酸化され得る還元性基を表し、Ｌ_１１は脱離基を表す。Ｒ_１１２は水素原子または置換基を表す。Ｒ_１１１は炭素原子（Ｃ）およびＲＥＤ_１１と共に、５員もしくは６員の芳香族環（芳香族ヘテロ環を含む）のテトラヒドロ体、ヘキサヒドロ体、もしくはオクタヒドロ体に相当する環状構造を形成し得る非金属原子団を表す。
【０１３１】
一般式（Ｂ）においてＲＥＤ_１２は１電子酸化され得る還元性基を表し、Ｌ_１２は脱離基を表す。Ｒ_１２１およびＲ_１２２は、それぞれ水素原子または置換基を表す。ＥＤ_１２は電子供与性基を表す。一般式（Ｂ）においてＲ_１２１とＲＥＤ_１２、Ｒ_１２１とＲ_１２２、またはＥＤ_１２とＲＥＤ_１２とは、互いに結合して環状構造を形成していてもよい。
【０１３２】
これら一般式（Ａ）または一般式（Ｂ）で表される化合物は、ＲＥＤ_１１またはＲＥＤ_１２で表される還元性基が１電子酸化された後、自発的にＬ_１１またはＬ_１２を結合開裂反応により離脱することで、これに伴いさらに電子を２つ以上、好ましくは３つ以上放出し得る化合物である。
【０１３３】
一般式（１）、一般式（２）、一般式（３）
【化１８】

【０１３４】
一般式（１）においてＺ_１は窒素原子およびベンゼン環の２つの炭素原子と共に６員環を形成し得る原子団を表し、Ｒ_１、Ｒ_２、Ｒ_Ｎ１はそれぞれ水素原子または置換基を表し、Ｘ_１はベンゼン環に置換可能な置換基を表し、ｍ_１は０〜３の整数を表し、Ｌ_１は脱離基を表す。一般式（２）においてＥＤ_２１は電子供与性基を表し、Ｒ_１１、Ｒ_１２、Ｒ_Ｎ２１、Ｒ_１３、Ｒ_１４はそれぞれ水素原子または置換基を表し、Ｘ_２１はベンゼン環に置換可能な置換基を表し、ｍ_２１は０〜３の整数を表し、Ｌ_２１は脱離基を表す。Ｒ_Ｎ２１、Ｒ_１３、Ｒ_１４、Ｘ_２１およびＥＤ_２１は、互いに結合して環状構造を形成していてもよい。一般式（３）においてＲ_３２、Ｒ_３３、Ｒ_３１、Ｒ_Ｎ３１、Ｒ_ａ、Ｒ_ｂはそれぞれ水素原子または置換基を表し、Ｌ_３１は脱離基を表す。但しＲ_Ｎ３１がアリール基以外の基を表す時、Ｒ_ａおよびＲ_ｂは互いに結合して芳香族環を形成する。
【０１３５】
これら化合物は１電子酸化された後、自発的にＬ_１、Ｌ_２１、またはＬ_３１を結合開裂反応により離脱することで、これに伴いさらに電子を２つ以上、好ましくは３つ以上放出し得る化合物である。
【０１３６】
以下、先ず一般式（Ａ）で表される化合物について詳しく説明する。
一般式（Ａ）においてＲＥＤ_１１で表される１電子酸化され得る還元性基は、後述するＲ_１１１と結合して特定の環形成をし得る基であり、具体的には次の１価基から環形成をするのに適切な箇所の水素原子１個を除いた２価基が挙げられる。例えば、アルキルアミノ基、アリールアミノ基（アニリノ基、ナフチルアミノ基等）、ヘテロ環アミノ基（ベンズチアゾリルアミノ基、ピロリルアミノ基等）、アルキルチオ基、アリールチオ基（フェニルチオ基等）、ヘテロ環チオ基、アルコキシ基、アリールオキシ基（フェノキシ基等）、ヘテロ環オキシ基、アリール基（フェニル基、ナフチル基、アントラニル基等）、芳香族または非芳香族のヘテロ環基（５員〜７員の、単環もしくは縮合環の、窒素原子、硫黄原子、酸素原子、セレン原子のうち少なくとも１つのヘテロ原子を含むヘテロ環で、その具体例としては、例えばテトラヒドロキノリン環、テトラヒドロイソキノリン環、テトラヒドロキノキサリン環、テトラヒドロキナゾリン環、インドリン環、インドール環、インダゾール環、カルバゾール環、フェノキサジン環、フェノチアジン環、ベンゾチアゾリン環、ピロール環、イミダゾール環、チアゾリン環、ピペリジン環、ピロリジン環、モルホリン環、ベンゾイミダゾール環、ベンゾイミダゾリン環、ベンゾオキサゾリン環、メチレンジオキシフェニル環等が挙げられる）である（以後、便宜上ＲＥＤ_１１は１価基名として記述する）。ＲＥＤ_１１は置換基を有していてもよい。
【０１３７】
本発明において置換基とは、特に説明がない限り、以下の基から選ばれる置換基を意味する。ハロゲン原子、アルキル基（アラルキル基、シクロアルキル基、活性メチン基等を含む）、アルケニル基、アルキニル基、アリール基、ヘテロ環基（置換する位置は問わない）、４級化された窒素原子を含むヘテロ環基（例えばピリジニオ基、イミダゾリオ基、キノリニオ基、イソキノリニオ基）、アシル基、アルコキシカルボニル基、アリールオキシカルボニル基、カルバモイル基、カルボキシ基またはその塩、スルホニルカルバモイル基、アシルカルバモイル基、スルファモイルカルバモイル基、カルバゾイル基、オキサリル基、オキサモイル基、シアノ基、カルボンイミドイル基、チオカルバモイル基、ヒドロキシ基、アルコキシ基（エチレンオキシ基もしくはプロピレンオキシ基単位を繰り返し含む基を含む）、アリールオキシ基、ヘテロ環オキシ基、アシルオキシ基、（アルコキシもしくはアリールオキシ）カルボニルオキシ基、カルバモイルオキシ基、スルホニルオキシ基、アミノ基、（アルキル、アリール、またはヘテロ環）アミノ基、アシルアミノ基、スルホンアミド基、ウレイド基、チオウレイド基、イミド基、（アルコキシもしくはアリールオキシ）カルボニルアミノ基、スルファモイルアミノ基、セミカルバジド基、チオセミカルバジド基、ヒドラジノ基、アンモニオ基、オキサモイルアミノ基、（アルキルもしくはアリール）スルホニルウレイド基、アシルウレイド基、アシルスルファモイルアミノ基、ニトロ基、メルカプト基、（アルキル、アリール、またはヘテロ環）チオ基、（アルキルまたはアリール）スルホニル基、（アルキルまたはアリール）スルフィニル基、スルホ基またはその塩、スルファモイル基、アシルスルファモイル基、スルホニルスルファモイル基またはその塩、リン酸アミドもしくはリン酸エステル構造を含む基、等が挙げられる。これら置換基は、これら置換基でさらに置換されていてもよい。
【０１３８】
ＲＥＤ_１１として好ましくは、アルキルアミノ基、アリールアミノ基、ヘテロ環アミノ基、アリール基、芳香族または非芳香族のヘテロ環基であり、さらに好ましくはアリールアミノ基（特にアニリノ基）、アリール基（特にフェニル基）である。これらが置換基を有する時、置換基として好ましくはハロゲン原子、アルキル基、アルコキシ基、カルバモイル基、スルファモイル基、アシルアミノ基、スルホンアミド基である。
但しＲＥＤ_１１がアリール基を表す時、アリール基は少なくとも１つの「電子供与性基」を有していることが好ましい。ここに「電子供与性基」とは、ヒドロキシ基、アルコキシ基、メルカプト基、スルホンアミド基、アシルアミノ基、アルキルアミノ基、アリールアミノ基、ヘテロ環アミノ基、活性メチン基、窒素原子を環内に少なくとも１つ含む５員の、単環もしくは縮合環の、電子過剰な芳香族ヘテロ環基（例えばインドリル基、ピロリル基、イミダゾリル基、ベンズイミダゾリル基、チアゾリル基、ベンズチアゾリル基、インダゾリル基など）、窒素原子で置換する非芳香族含窒素ヘテロ環基（ピロリジニル基、インドリニル基、ピペリジニル基、ピペラジニル基、モルホリノ基などで環状のアミノ基とも呼べる基）である。ここで活性メチン基とは２つの「電子求引性基」で置換されたメチン基を意味し、ここに「電子求引性基」とはアシル基、アルコシキカルボニル基、アリールオキシカルボニル基、カルバモイル基、アルキルスルホニル基、アリールスルホニル基、スルファモイル基、トリフルオロメチル基、シアノ基、ニトロ基、カルボンイミドイル基を意味する。ここで２つの電子求引性基は互いに結合して環状構造をとっていてもよい。
【０１３９】
一般式（Ａ）においてＬ_１１は、具体的にはカルボキシ基もしくはその塩、シリル基、水素原子、トリアリールホウ素アニオン、トリアルキルスタニル基、トリアルキルゲルミル基、または−ＣＲ_Ｃ１Ｒ_Ｃ２Ｒ_Ｃ３基を表す。ここにシリル基とは具体的にトリアルキルシリル基、アリールジアルキルシリル基、トリアリールシリル基などを表し、任意の置換基を有していてもよい。
【０１４０】
Ｌ_１１がカルボキシ基の塩を表すとき、塩を形成するカウンターイオンとしてはアルカリ金属イオン、アルカリ土類金属イオン、重金属イオン、アンモニウムイオン、ホスホニウムイオンなどが挙げられ、好ましくはアルカリ金属イオンまたはアンモニウムイオンであり、アルカリ金属イオン（特にＬｉ^＋、Ｎａ^＋、Ｋ^＋イオン）が最も好ましい。
【０１４１】
Ｌ_１１が−ＣＲ_Ｃ１Ｒ_Ｃ２Ｒ_Ｃ３基を表す時、ここにＲ_Ｃ１、Ｒ_Ｃ２、Ｒ_Ｃ３はそれぞれ独立に、水素原子、アルキル基、アリール基、ヘテロ環基、アルキルチオ基、アリールチオ基、アルキルアミノ基、アリールアミノ基、ヘテロ環アミノ基、アルコキシ基、アリールオキシ基、ヒドロキシ基を表し、これらが互いに結合して環状構造を形成していてもよく、さらに任意の置換基を有していてもよい。但し、Ｒ_Ｃ１、Ｒ_Ｃ２、Ｒ_Ｃ３のうち１つが水素原子もしくはアルキル基を表す時、残る２つが水素原子もしくはアルキル基を表すことはない。Ｒ_Ｃ１、Ｒ_Ｃ２、Ｒ_Ｃ３として好ましくは、それぞれ独立に、アルキル基、アリール基（特にフェニル基）、アルキルチオ基、アリールチオ基、アルキルアミノ基、アリールアミノ基、ヘテロ環基、アルコキシ基、ヒドロキシ基で、具体的にその例を挙げると、フェニル基、ｐ−ジメチルアミノフェニル基、ｐ−メトキシフェニル基、２，４−ジメトキシフェニル基、ｐ−ヒドロキシフェニル基、メチルチオ基、フェニルチオ基、フェノキシ基、メトキシ基、エトキシ基、ジメチルアミノ基、Ｎ−メチルアニリノ基、ジフェニルアミノ基、モルホリノ基、チオモルホリノ基、ヒドロキシ基などが挙げられる。またこれらが互いに結合して環状構造を形成する場合の例としては１，３−ジチオラン−２−イル基、１，３−ジチアン−２−イル基、Ｎ−メチル−１，３−チアゾリジン−２−イル基、Ｎ−ベンジル−ベンゾチアゾリジン−２−イル基などが挙げられる。
−ＣＲ_Ｃ１Ｒ_Ｃ２Ｒ_Ｃ３基が、Ｒ_Ｃ１、Ｒ_Ｃ２、Ｒ_Ｃ３についてそれぞれ上述した範囲内で選択された結果として、一般式（Ａ）からＬ_１１を除いた残基と同じ基を表す場合もまた好ましい。
【０１４２】
一般式（Ａ）においてＬ_１１は、好ましくはカルボキシ基またはその塩、および水素原子である。より好ましくはカルボキシ基またはその塩である。
【０１４３】
Ｌ_１１が水素原子を表す時、一般式（Ａ）で表される化合物は、分子内に内在する塩基部位を有していることが好ましい。この塩基部位の作用により、一般式（Ａ）で表される化合物が酸化された後、Ｌ_１１で表される水素原子が脱プロトン化されて、ここからさらに電子が放出されるのである。
【０１４４】
ここに塩基とは、具体的に約１〜約１０のｐＫａを示す酸の共役塩基である。例えば含窒素ヘテロ環類（ピリジン類、イミダゾール類、ベンゾイミダゾール類、チアゾール類など）、アニリン類、トリアルキルアミン類、アミノ基、炭素酸類（活性メチレンアニオンなど）、チオ酢酸アニオン、カルボキシレート（−ＣＯＯ⁻）、サルフェート（−ＳＯ_３ ⁻）、またはアミンオキシド（＞Ｎ^＋（Ｏ⁻）−）などが挙げられる。好ましくは約１〜約８のｐＫａを示す酸の共役塩基であり、カルボキシレート、サルフェート、またはアミンオキシドがより好ましく、カルボキシレートが特に好ましい。これらの塩基がアニオンを有する時、対カチオンを有していてもよく、その例としてはアルカリ金属イオン、アルカリ土類金属イオン、重金属イオン、アンモニウムイオン、ホスホニウムイオンなどが挙げられる。これら塩基は、任意の位置で一般式（Ａ）で表される化合物に連結される。これら塩基部位が結合する位置としては、一般式（Ａ）のＲＥＤ_１１、Ｒ_１１１、Ｒ_１１２の何れでもよく、またこれらの基の置換基に連結していてもよい。
【０１４５】
一般式（Ａ）においてＲ_１１２は水素原子または炭素原子に置換可能な置換基を表す。但しＲ_１１２がＬ_１１と同じ基を表すことはない。
Ｒ_１１２は好ましくは水素原子、アルキル基、アリール基（フェニル基など）、アルコキシ基（メトキシ基、エトキシ基、ベンジルオキシ基など）、ヒドロキシ基、アルキルチオ基（メチルチオ基、ブチルチオ基など）、アミノ基、アルキルアミノ基、アリールアミノ基、ヘテロ環アミノ基であり、より好ましくは水素原子、アルキル基、アルコキシ基、ヒドロキシ基、フェニル基、アルキルアミノ基である。
【０１４６】
一般式（Ａ）においてＲ_１１１が形成する環状構造とは、５員もしくは６員の芳香族環（芳香族ヘテロ環を含む）のテトラヒドロ体、ヘキサヒドロ体もしくはオクタヒドロ体に相当する環構造で、ここにヒドロ体とは、芳香族環（芳香族ヘテロ環を含む）に内在する炭素−炭素２重結合（または炭素−窒素２重結合）が部分的に水素化された環構造を意味し、テトラヒドロ体とは２つの、ヘキサヒドロ体とは３つの、オクタヒドロ体とは４つの、炭素−炭素２重結合（または炭素−窒素２重結合）が水素化された構造を意味する。水素化されることで芳香族環は、部分的に水素化された非芳香族の環構造となる。
【０１４７】
具体的には、ピロリジン環、イミダゾリジン環、チアゾリジン環、ピラゾリジン環およびオキサゾリジン環、ピペリジン環、テトラヒドロピリジン環、テトラヒドロピリミジン環、ピペラジン環、テトラリン環、テトラヒドロキノリン環、テトラヒドロイソキノリン環、テトラヒドロキナゾリン環、およびテトラヒドロキノキサリン環、テトラヒドロカルバゾール環、オクタヒドロフェナントリジン環等が挙げられる。これらの環構造は任意の置換基を有していてもよい。
【０１４８】
Ｒ_１１１が形成する環状構造としてさらに好ましくは、ピロリジン環、イミダゾリジン環、ピペリジン環、テトラヒドロピリジン環、テトラヒドロピリミジン環、ピペラジン環、テトラヒドロキノリン環、テトラヒドロイソキノリン環、テトラヒドロキナゾリン環、テトラヒドロキノキサリン環、テトラヒドロカルバゾール環であり、特に好ましくは、ピロリジン環、ピペリジン環、ピペラジン環、テトラヒドロピリジン環、テトラヒドロキノリン環、テトラヒドロイソキノリン環、テトラヒドロキナゾリン環、テトラヒドロキノキサリン環であり、最も好ましくはピロリジン環、ピペリジン環、テトラヒドロピリジン環、テトラヒドロキノリン環、テトラヒドロイソキノリン環である。
【０１４９】
一般式（Ｂ）においてＲＥＤ_１２、Ｌ_１２は、それぞれ一般式（Ａ）のＲＥＤ_１１、Ｌ_１１に同義の基であり、その好ましい範囲もまた同じである。但し、ＲＥＤ_１２は下記の環状構造を形成する場合以外は１価基であり、具体的にはＲＥＤ_１１で記載した１価基名の基が挙げられる。Ｒ_１２１およびＲ_１２２は一般式（Ａ）のＲ_１１２に同義の基であり、その好ましい範囲もまた同じである。ＥＤ_１２は電子供与性基を表す。Ｒ_１２１とＲＥＤ_１２、Ｒ_１２１とＲ_１２２、またはＥＤ_１２とＲＥＤ_１２とは、互いに結合して環状構造を形成していてもよい。
【０１５０】
一般式（Ｂ）においてＥＤ_１２で表される電子供与性基とは、ＲＥＤ_１１がアリール基を表すときの置換基として説明した電子供与性基と同じものである。ＥＤ_１２として好ましくはヒドロキシ基、アルコキシ基、メルカプト基、スルホンアミド基、アルキルアミノ基、アリールアミノ基、活性メチン基、窒素原子を環内に少なくとも１つ含む５員の、単環もしくは縮合環の、電子過剰な芳香族ヘテロ環基、窒素原子で置換する非芳香族含窒素ヘテロ環基、およびこれら電子供与性基で置換されたフェニル基であり、さらにヒドロキシ基、メルカプト基、スルホンアミド基、アルキルアミノ基、アリールアミノ基、活性メチン基、窒素原子で置換する非芳香族含窒素ヘテロ環基、およびこれら電子供与性基で置換されたフェニル基（例えばｐ−ヒドロキシフェニル基、ｐ−ジアルキルアミノフェニル基、ｏ，ｐ−ジアルコキシフェニル基等）がより好ましい。
【０１５１】
一般式（Ｂ）においてＲ_１２１とＲＥＤ_１２、Ｒ_１２２とＲ_１２１、またはＥＤ_１２とＲＥＤ_１２とは、互いに結合して環状構造を形成していてもよい。ここで形成される環状構造とは、非芳香族の炭素環もしくはヘテロ環であって、５員〜７員環の単環または縮合環で、置換もしくは無置換の環状構造である。Ｒ_１２１とＲＥＤ_１２とが環構造を形成するとき、その具体例としては、一般式（Ａ）においてＲ_１１１が形成する環状構造の例として挙げたものに加えて、ピロリン環、イミダゾリン環、チアゾリン環、ピラゾリン環、オキサゾリン環、インダン環、モルホリン環、インドリン環、テトラヒドロ−１，４−オキサジン環、２，３−ジヒドロベンゾ−１，４−オキサジン環、テトラヒドロ−１，４−チアジン環、２，３−ジヒドロベンゾ−１，４−チアジン環、２，３−ジヒドロベンゾフラン環、２，３−ジヒドロベンゾチオフェン環等が挙げられる。ＥＤ_１２とＲＥＤ_１２とが環構造を形成するとき、ＥＤ_１２は好ましくはアミノ基、アルキルアミノ基、アリールアミノ基を表し、形成される環構造の具体例としては、テトラヒドロピラジン環、ピペラジン環、テトラヒドロキノキサリン環、テトラヒドロイソキノリン環などが挙げられる。Ｒ_１２２とＲ_１２１とが環構造を形成するとき、その具体例としてはシクロヘキサン環、シクロペンタン環などが挙げられる。
【０１５２】
次に一般式（１）〜（３）について説明する。
一般式（１）〜（３）においてＲ_１、Ｒ_２、Ｒ_１１、Ｒ_１２、Ｒ_３１は、一般式（Ａ）のＲ_１１２と同義の基であり、その好ましい範囲もまた同じである。Ｌ_１、Ｌ_２１、Ｌ_３１は、一般式（Ａ）のＬ_１１について説明した中で具体例として挙げた基と同じ脱離基を表し、その好ましい範囲もまた同じである。Ｘ_１、Ｘ_２１で表される置換基としては、一般式（Ａ）のＲＥＤ_１１が置換基を有する時の置換基の例と同じであり、好ましい範囲も同じである。ｍ_１、ｍ_２１は好ましくは０〜２の整数であり、より好ましくは０または１である。
【０１５３】
Ｒ_Ｎ１、Ｒ_Ｎ２１、Ｒ_Ｎ３１が置換基を表す時、置換基としてはアルキル基、アリール基、ヘテロ環基が好ましく、これらはさらに任意の置換基を有していてもよい。Ｒ_Ｎ１、Ｒ_Ｎ２１、Ｒ_Ｎ３１は水素原子、アルキル基またはアリール基が好ましく、水素原子またはアルキル基がより好ましい。
【０１５４】
Ｒ_１３、Ｒ_１４、Ｒ_３３、Ｒ_ａ、Ｒ_ｂが置換基を表す時、置換基として好ましくは、アルキル基、アリール基、アシル基、アルコキシカルボニル基、カルバモイル基、シアノ基、アルコキシ基、アシルアミノ基、スルホンアミド基、ウレイド基、チオウレイド基、アルキルチオ基、アリールチオ基、アルキルスルホニル基、アリールスルホニル基、スルファモイル基などである。
【０１５５】
一般式（１）においてＺ_１が形成する６員環は、一般式（１）のベンゼン環と縮合した非芳香族のヘテロ環であり、具体的には縮合するベンゼン環も含めた環構造としてテトラヒドロキノリン環、テトラヒドロキノキサリン環、テトラヒドロキナゾリン環であり、好ましくはテトラヒドロキノリン環、テトラヒドロキノキサリン環である。これらは置換基を有していてもよい。
【０１５６】
一般式（２）においてＥＤ_２１は、一般式（Ｂ）のＥＤ_１２と同義の基であり、その好ましい範囲もまた同じである。
【０１５７】
一般式（２）においてＲ_Ｎ２１、Ｒ_１３、Ｒ_１４、Ｘ_２１およびＥＤ_２１のいずれか２つは、互いに結合して環状構造を形成していてもよい。ここでＲ_Ｎ２１とＸ_２１が結合して形成される環状構造とは、好ましくはベンゼン環と縮合した５員〜７員の非芳香族の炭素環もしくはヘテロ環であって、その具体例としては、テトラヒドロキノリン環、テトラヒドロキノキサリン環、インドリン環、２，３−ジヒドロ−５，６−ベンゾ−１，４−チアジン環などが挙げられる。好ましくはテトラヒドロキノリン環、テトラヒドロキノキサリン環、インドリン環である。
【０１５８】
一般式（３）においてＲ_Ｎ３１がアリール基以外の基を表す時、Ｒ_ａおよびＲ_ｂは互いに結合して芳香族環を形成する。ここに芳香族環とはアリール基（例えばフェニル基、ナフチル基）および芳香族ヘテロ環基（例えばピリジン環基、ピロール環基、キノリン環基、インドール環基など）であり、アリール基が好ましい。該芳香族環基は任意の置換基を有していてもよい。
一般式（３）においてＲ_ａおよびＲ_ｂは、互いに結合して芳香族環（特にフェニル基）を形成する場合が好ましい。
【０１５９】
一般式（３）においてＲ_３２は好ましくは水素原子、アルキル基、アリール基、ヒドロキシ基、アルコキシ基、メルカプト基、アミノ基などであり、ここにＲ_３２がヒドロキシ基を表す時、同時にＲ_３３が「電子求引性基」を表す場合も好ましい例の１つである。ここに「電子求引性基」とは、先に説明したものと同じであり、アシル基、アルコシキカルボニル基、カルバモイル基、シアノ基が好ましい。
【０１６０】
次にタイプ２の化合物について説明する。
タイプ２の化合物において「結合開裂反応」とは炭素−炭素、炭素−ケイ素、炭素−水素、炭素−ホウ素、炭素−スズ、炭素−ゲルマニウムの各元素間の結合の開裂を意味し、炭素−水素結合の開裂がこれに付随してもよい。
【０１６１】
タイプ２の化合物は分子内にハロゲン化銀への吸着性基を２つ以上（好ましくは２〜６つ、より好ましくは２〜４つ）有する化合物である。より好ましくは２つ以上のメルカプト基で置換された含窒素ヘテロ環基を吸着性基として有する化合物である。吸着性基の数は、好ましくは２〜６、さらに好ましくは２〜４が良い。吸着性基については後述する。
【０１６２】
タイプ２の化合物のうち好ましい化合物は一般式（Ｃ）で表される。
【０１６３】
一般式（Ｃ）
【化１９】

【０１６４】
ここに一般式（Ｃ）で表される化合物は、ＲＥＤ_２で表される還元性基が１電子酸化された後、自発的にＬ_２を結合開裂反応により離脱することで、これに伴いさらに電子を１つ放出し得る化合物である。
【０１６５】
一般式（Ｃ）においてＲＥＤ_２は一般式（Ｂ）のＲＥＤ_１２と同義の基を表し、その好ましい範囲も同じである。Ｌ_２は一般式（Ａ）のＬ_１１について説明したのと同義の基を表し、その好ましい範囲も同じである。なおＬ_２がシリル基を表す時、該化合物は分子内に、２つ以上のメルカプト基で置換された含窒素ヘテロ環基を吸着性基として有する化合物である。Ｒ_２１、Ｒ_２２は水素原子または置換基を表し、これらは一般式（Ａ）のＲ_１１２と同義の基であり、その好ましい範囲も同じである。ＲＥＤ_２とＲ_２１とは互いに結合して環構造を形成していてもよい。
【０１６６】
ここで形成される環構造とは、５員〜７員の、単環もしくは縮合環の、非芳香族の炭素環またはヘテロ環であり、置換基を有していてもよい。但し該環構造が、芳香族環または芳香族ヘテロ環のテトラヒドロ体、ヘキサヒドロ体もしくはオクタヒドロ体に相当する環構造であることはない。環構造として好ましくは、芳香族環または芳香族ヘテロ環のジヒドロ体に相当する環構造で、その具体例としては、例えば２−ピロリン環、２−イミダゾリン環、２−チアゾリン環、１，２−ジヒドロピリジン環、１，４−ジヒドロピリジン環、インドリン環、ベンゾイミダゾリン環、ベンゾチアゾリン環、ベンゾオキサゾリン環、２，３−ジヒドロベンゾチオフェン環、２，３−ジヒドロベンゾフラン環、ベンゾ−α−ピラン環、１，２−ジヒドロキノリン環、１，２−ジヒドロキナゾリン環、１，２−ジヒドロキノキサリン環などが挙げられ、好ましくは２−イミダゾリン環、２−チアゾリン環、インドリン環、ベンゾイミダゾリン環、ベンゾチアゾリン環、ベンゾオキサゾリン環、１，２−ジヒドロピリジン環、１，２−ジヒドロキノリン環、１，２−ジヒドロキナゾリン環、１，２−ジヒドロキノキサリン環などであり、インドリン環、ベンゾイミダゾリン環、ベンゾチアゾリン環、１，２−ジヒドロキノリン環がより好ましく、インドリン環が特に好ましい。
【０１６７】
次にタイプ３の化合物について説明する。
タイプ３の化合物において「結合形成過程」とは炭素−炭素、炭素−窒素、炭素−硫黄、炭素−酸素などの原子間結合の形成を意味する。
【０１６８】
タイプ３の化合物は好ましくは、１電子酸化されて生成する１電子酸化体が、引き続いて分子内に共存する反応性基部位（炭素−炭素２重結合部位、炭素−炭素３重結合部位、芳香族基部位、またはベンゾ縮環の非芳香族ヘテロ環基部位）と反応して結合を形成した後に、さらに１電子もしくはそれ以上の電子を放出し得ることを特徴とする化合物である。
【０１６９】
さらに詳細に述べるとタイプ３の化合物は、１電子酸化されて生成するその１電子酸化体（カチオンラジカル種、またはそこからプロトンの脱離により生成する中性のラジカル種）が、同じ分子内に共存する上記反応性基と反応し、結合を形成して、分子内に新たに環構造を有するラジカル種を生成する。そしてこのラジカル種から、直接もしくはプロトンの脱離を伴って、２電子目の電子が放出される特徴を有している。
【０１７０】
そしてさらにタイプ３の化合物の中には、そうして生成した２電子酸化体がその後、ある場合には加水分解反応を受けた後に、またある場合には直接プロトンの移動を伴なう互変異性化反応を起して、そこからさらに１電子以上、通常２電子以上の電子を放出する場合がある。あるいはまたこうした互変異性化反応を経由せずに直接２電子酸化体から、さらに１電子以上、通常２電子以上の電子を放出する能力を有しているものも含まれる。
【０１７１】
タイプ３の化合物は好ましくは、一般式（Ｄ）で表される。
【０１７２】
一般式（Ｄ）
【化２０】

【０１７３】
一般式（Ｄ）においてＲＥＤ_３は１電子酸化され得る還元性基を表し、Ｙ_３はＲＥＤ_３が１電子酸化された後に反応する反応性基部位を表し、具体的には炭素−炭素２重結合部位、炭素−炭素３重結合部位、芳香族基部位、またはベンゾ縮環の非芳香族ヘテロ環基部位を含む有機基を表す。Ｌ_３はＲＥＤ_３とＹ_３とを連結する連結基を表す。
【０１７４】
ＲＥＤ_３は一般式（Ｂ）のＲＥＤ_１２と同義の基を表し、好ましくはアリールアミノ基、ヘテロ環アミノ基、アリールオキシ基、アリールチオ基、アリール基、芳香族または非芳香族のヘテロ環基（特に含窒素ヘテロ環基が好ましい）であり、さらに好ましくはアリールアミノ基、ヘテロ環アミノ基、アリール基、芳香族または非芳香族のヘテロ環基であり、このうちヘテロ環基に関しては、テトラヒドロキノリン環基、テトラヒドロキノキサリン環基、テトラヒドロキナゾリン環基、インドリン環基、インドール環基、カルバゾール環基、フェノキサジン環基、フェノチアジン環基、ベンゾチアゾリン環基、ピロール環基、イミダゾール環基、チアゾール環基、ベンゾイミダゾール環基、ベンゾイミダゾリン環基、ベンゾチアゾリン環基、３，４−メチレンジオキシフェニル−１−イル基などが好ましい。
ＲＥＤ_３として特に好ましくはアリールアミノ基（特にアニリノ基）、アリール基（特にフェニル基）、芳香族または非芳香族のヘテロ環基である。
【０１７５】
ここでＲＥＤ_３がアリール基を表す時、アリール基は少なくとも１つの「電子供与性基」を有していることが好ましい。「電子供与性基」は先に説明したものと同じである。
【０１７６】
ＲＥＤ_３がアリール基を表す時、そのアリール基の置換基としてより好ましくはアルキルアミノ基、ヒドロキシ基、アルコキシ基、メルカプト基、スルホンアミド基、活性メチン基、窒素原子で置換する非芳香族含窒素ヘテロ環基であり、さらに好ましくはアルキルアミノ基、ヒドロキシ基、活性メチン基、窒素原子で置換する非芳香族含窒素ヘテロ環基であり、最も好ましくはアルキルアミノ基、窒素原子で置換する非芳香族含窒素ヘテロ環基である。
【０１７７】
Ｙ_３で表される炭素−炭素２重結合部位を含む有機基（例えばビニル基）が置換基を有するとき、その置換基として好ましくは、アルキル基、フェニル基、アシル基、シアノ基、アルコキシカルボニル基、カルバモイル基、電子供与基などであり、ここに電子供与性基として好ましくは、アルコキシ基、ヒドロキシ基（シリル基で保護されていてもよく、例えばトリメチルシリルオキシ基、ｔ−ブチルジメチルシリルオキシ基、トリフェニルシリルオキシ基、トリエチルシリルオキシ基、フェニルジメチルシリルオキシ基などが挙げられる）、アミノ基、アルキルアミノ基、アリールアミノ基、スルホンアミド基、活性メチン基、メルカプト基、アルキルチオ基、およびこれら電子供与性基を置換基に有するフェニル基である。
【０１７８】
なおここで炭素−炭素２重結合部位を含む有機基が置換基としてヒドロキシ基を有する時、Ｙ_３は右記部分構造：＞Ｃ_１＝Ｃ_２（−ＯＨ）−を含むことになるが、これは互変異性化して右記部分構造：＞Ｃ_１Ｈ−Ｃ_２（＝Ｏ）−となっていても良い。さらにこの場合に、該Ｃ_１炭素に置換する置換基が電子求引性基である場合もまた好ましく、この場合Ｙ_３は「活性メチレン基」または「活性メチン基」の部分構造を有することになる。このような活性メチレン基または活性メチン基の部分構造を与え得る電子求引性基とは、上述の「活性メチン基」の説明の中で説明したものと同じである。
【０１７９】
Ｙ_３で表される炭素−炭素３重結合部位を含む有機基（例えばエチニル基）が置換基を有するとき、その置換基としてはアルキル基、フェニル基、アルコキシカルボニル基、カルバモイル基、電子供与基などが好ましい。
【０１８０】
Ｙ_３が芳香族基部位を含む有機基を表す時、芳香族基として好ましくは電子供与性基を置換基として有するアリール基（特にフェニル基が好ましい）またはインドール環基で、ここに電子供与性基として好ましくは、ヒドロキシ基（シリル基で保護ざれていてもよい）、アルコキシ基、アミノ基、アルキルアミノ基、活性メチン基、スルホンアミド基、メルカプト基である。
【０１８１】
Ｙ_３がベンゾ縮環の非芳香族ヘテロ環基部位を含む有機基を表す時、ベンゾ縮環の非芳香族ヘテロ環基として好ましくはアニリン構造を部分構造として内在するもので、例えば、インドリン環基、１，２，３，４−テトラヒドロキノリン環基、１，２，３，４−テトラヒドロキノキサリン環基、４−キノロン環基などが挙げられる。
【０１８２】
Ｙ_３で表される反応性基としてより好ましくは、炭素−炭素２重結合部位、芳香族基部位、またはベンゾ縮環の非芳香族ヘテロ環基を含む有機基である。さらに好ましくは、炭素−炭素２重結合部位、電子供与性基を置換基として有するフェニル基、インドール環基、アニリン構造を部分構造として内在するベンゾ縮環の非芳香族ヘテロ環基である。ここに炭素−炭素２重結合部位は少なくとも１つの電子供与性基を置換基として有することがより好ましい。
【０１８３】
Ｙ_３で表される反応性基が、これまでに説明した範囲から選択された結果として、ＲＥＤ_３で表される還元性基と同じ部分構造を有する場合もまた、一般式（Ｄ）で表される化合物の好ましい例である。
【０１８４】
Ｌ_３は、ＲＥＤ_３とＹ_３とを連結する連結基を表し、具体的には単結合、アルキレン基、アリーレン基、ヘテロ環基、−Ｏ−、−Ｓ−、−ＮＲ_Ｎ−、−Ｃ（＝Ｏ）−、−ＳＯ_２−、−ＳＯ−、−Ｐ（＝Ｏ）−の各基の単独、またはこれらの基の組み合わせからなる基を表す。ここにＲ_Ｎは水素原子、アルキル基、アリール基、ヘテロ環基を表す。Ｌ_３で表される連結基は任意の置換基を有していてもよい。Ｌ_３で表される連結基は、ＲＥＤ_３およびＹ_３で表される基の任意の位置で、それぞれの任意の１個の水素原子と置換する形で、連結され得る。
Ｌ_３の好ましい例としては、単結合、アルキレン基（特にメチレン基、エチレン基、プロピレン基）、アリーレン基（特にフェニレン基）、−Ｃ（＝Ｏ）−基、−Ｏ−基、−ＮＨ−基、−Ｎ（アルキル基）−基、およびこれらの基の組み合わせからなる２価の連結基が挙げられる。
【０１８５】
Ｌ_３で表される基は、ＲＥＤ_３が酸化されて生成するカチオンラジカル種（Ｘ^＋・）、またはそこからプロトンの脱離を伴って生成するラジカル種（Ｘ・）と、Ｙ_３で表される反応性基とが反応して結合形成する際、これに関わる原子団が、Ｌ_３を含めて３〜７員の環状構造を形成しうることが好ましい。この為にはラジカル種（Ｘ^＋・またはＸ・）、Ｙで表される反応性基、およびＬが、３〜７個の原子団で連結されていることが好ましい。
【０１８６】
次にタイプ４の化合物について説明する。
タイプ４の化合物は還元性基の置換した環構造を有する化合物であり、該還元性基が１電子酸化された後、環構造の開裂反応を伴ってさらに１電子もしくはそれ以上の電子を放出しうる化合物である。ここで言う環構造の開裂反応とは、下記で表される形式のものを意味する。
【０１８７】
【化２１】

【０１８８】
式中、化合物ａはタイプ４の化合物を表す。化合物ａ中、Ｄは還元性基を表し、Ｘ、Ｙは環構造中の１電子酸化後に開裂する結合を形成している原子を表す。まず化合物ａが１電子酸化されて １電子酸化体ｂを生成する。ここからＤ−Ｘの単結合が２重結合になると同時にＸ−Ｙの結合が切断され開環体ｃが生成する。あるいはまた１電子酸化体ｂからプロトンの脱離を伴ってラジカル中間体ｄが生成し、ここから同様に開環体ｅを生成する経路をとる場合もある。このように生成した開環体ｃまたはｅから、引き続きさらに１つ以上の電子が放出される点に本発明の化合物の特徴がある。
【０１８９】
タイプ４の化合物が有する環構造とは、３〜７員環の炭素環またはヘテロ環であり、単環もしくは縮環の、飽和もしくは不飽和の非芳香族の環を表す。好ましくは飽和の環構造であり、より好ましくは３員環あるいは４員環である。好ましい環構造としてはシクロプロパン環、シクロブタン環、オキシラン環、オキセタン環、アジリジン環、アゼチジン環、エピスルフィド環、チエタン環が挙げられる。より好ましくはシクロプロパン環、シクロブタン環、オキシラン環、オキセタン環、アゼチジン環であり、特に好ましくはシクロプロパン環、シクロブタン環、アゼチジン環である。環構造は任意の置換基を有していても良い。
【０１９０】
タイプ４の化合物は好ましくは一般式（Ｅ）または（Ｆ）で表される。
【０１９１】
一般式（Ｅ）
【化２２】

【０１９２】
一般式（Ｆ）
【化２３】

【０１９３】
一般式（Ｅ）および一般式（Ｆ）においてＲＥＤ_４１およびＲＥＤ_４２は、それぞれ一般式（Ｂ）のＲＥＤ_１２と同義の基を表し、その好ましい範囲もまた同じである。Ｒ_４０〜Ｒ_４４およびＲ_４５〜Ｒ_４９は、それぞれ水素原子または置換基を表す。一般式（Ｆ）においてＺ_４２は、−ＣＲ_４２０Ｒ_４２１−、−ＮＲ_４２３−、または−Ｏ−を表す。ここにＲ_４２０、Ｒ_４２１は、それぞれ水素原子または置換基を表し、Ｒ_４２３は水素原子、アルキル基、アリール基またはヘテロ環基を表す。
【０１９４】
一般式（Ｅ）および一般式（Ｆ）においてＲ_４０およびＲ_４５は、好ましくは水素原子、アルキル基、アリール基、ヘテロ環基を表し、水素原子、アルキル基、アリール基がより好ましい。Ｒ_４１〜Ｒ_４４およびＲ_４６〜Ｒ_４９として好ましくは水素原子、アルキル基、アルケニル基、アリール基、ヘテロ環基、アリールチオ基、アルキルチオ基、アシルアミノ基、スルホンアミド基であり、より好ましくは水素原子、アルキル基、アリール基、ヘテロ環基である。
【０１９５】
Ｒ_４１〜Ｒ_４４は、これらのうち少なくとも１つがドナー性基である場合と、Ｒ_４１とＲ_４２、あるいはＲ_４３とＲ_４４がともに電子求引性基である場合が好ましい。より好ましくはＲ_４１〜Ｒ_４４の少なくとも１つがドナー性基である場合である。さらに好ましくはＲ_４１〜Ｒ_４４の少なくとも１つがドナー性基であり且つ、Ｒ_４１〜Ｒ_４４の中でドナー性基でない基が水素原子またはアルキル基である場合である。
【０１９６】
ここで言うドナー性基とは、「電子供与性基」、または少なくとも１つの「電子供与性基」で置換されたアリール基である。ドナー性基として好ましくはアルキルアミノ基、アリールアミノ基、ヘテロ環アミノ基、窒素原子を環内に少なくとも１つ含む５員の、単環もしくは縮合環の、電子過剰な芳香族ヘテロ環基、窒素原子で置換する非芳香族含窒素ヘテロ環基、少なくとも１つの電子供与性基で置換されたフェニル基が用いられる。より好ましくはアルキルアミノ基、アリールアミノ基、窒素原子を環内に少なくとも１つ含む５員の、単環もしくは縮合環の、電子過剰な芳香族ヘテロ環基（インドール環、ピロール環、カルバゾール環など）、電子供与性基で置換されたフェニル基（３つ以上のアルコキシ基で置換されたフェニル基、ヒドロキシ基またはアルキルアミノ基またはアリールアミノ基で置換されたフェニル基など）が用いられる。 特に好ましくはアリールアミノ基、窒素原子を環内に少なくとも１つ含む５員の、単環もしくは縮合環の、電子過剰な芳香族ヘテロ環基（特に３−インドリル基）、電子供与性基で置換されたフェニル基（特にトリアルコキシフェニル基、アルキルアミノ基またはアリールアミノ基で置換されたフェニル基）が用いられる。
【０１９７】
Ｚ_４２として好ましくは−ＣＲ_４２０Ｒ_４２１−または−ＮＲ_４２３−であり、より好ましくは−ＮＲ_４２３−である。Ｒ_４２０、Ｒ_４２１は好ましくは、水素原子、アルキル基、アリール基、ヘテロ環基、アシルアミノ基、スルホンアミノ基であり、より好ましくは水素原子、アルキル基、アリール基、ヘテロ環基である。Ｒ_４２３は好ましくは水素原子、アルキル基、アリール基、芳香族ヘテロ環基を表し、より好ましくは水素原子、アルキル基、アリール基である。
【０１９８】
Ｒ_４０〜Ｒ_４９およびＲ_４２０、Ｒ_４２１、Ｒ_４２３の各基が置換基である場合にはそれぞれ総炭素数が４０以下のものが好ましく、より好ましくは総炭素数３０以下で、特に好ましくは総炭素数１５以下である。またこれらの置換基は互いに結合して、あるいは分子中の他の部位（ＲＥＤ_４１、ＲＥＤ_４２あるいはＺ_４２）と結合して環を形成していても良い。
【０１９９】
本発明のタイプ１〜４の化合物においてハロゲン化銀への吸着性基とは、ハロゲン化銀に直接吸着する基、またはハロゲン化銀への吸着を促進する基であり、具体的には、メルカプト基（またはその塩）、チオン基（−Ｃ（＝Ｓ）−）、窒素原子、硫黄原子、セレン原子およびテルル原子から選ばれる少なくとも１つの原子を含むヘテロ環基、スルフィド基、カチオン性基、またはエチニル基である。但し、本発明のタイプ２の化合物においては、吸着性基としてスルフィド基は含まれない。
【０２００】
吸着性基としてメルカプト基（またはその塩）とは、メルカプト基（またはその塩）そのものを意味すると同時に、より好ましくは、少なくとも１つのメルカプト基（またはその塩）の置換したヘテロ環基またはアリール基またはアルキル基を表す。ここにヘテロ環基は、５員〜７員の、単環もしくは縮合環の、芳香族または非芳香族のヘテロ環基で、例えばイミダゾール環基、チアゾール環基、オキサゾール環基、ベンズイミダゾール環基、ベンズチアゾール環基、ベンズオキサゾール環基、トリアゾール環基、チアジアゾール環基、オキサジアゾール環基、テトラゾール環基、プリン環基、ピリジン環基、キノリン環基、イソキノリン環基、ピリミジン環基、トリアジン環基等が挙げられる。また４級化された窒素原子を含むヘテロ環基でもよく、この場合、置換したメルカプト基が解離してメソイオンとなっていてもよく、この様なヘテロ環基の例としてはイミダゾリウム環基、ピラゾリウム環基、チアゾリウム環基、トリアゾリウム環基、テトラゾリウム環基、チアジアゾリウム環基、ピリジニウム環基、ピリミジニウム環基、トリアジニウム環基などが挙げられ、中でもトリアゾリウム環基（例えば１，２，４−トリアゾリウム−３−チオレート環基）が好ましい。アリール基としてはフェニル基またはナフチル基が挙げられる。アルキル基としては炭素数１〜３０の直鎖または分岐または環状のアルキル基が挙げられる。メルカプト基が塩を形成するとき、対イオンとしてはアルカリ金属、アルカリ土類金属、重金属などのカチオン（Ｌｉ^＋、Ｎａ^＋、Ｋ^＋、Ｍｇ^２＋、Ａｇ^＋、Ｚｎ^２＋等）、アンモニウムイオン、４級化された窒素原子を含むヘテロ環基、ホスホニウムイオンなどが挙げられる。
【０２０１】
吸着性基としてのメルカプト基はさらにまた、互変異性化してチオン基となっていてもよく、具体的にはチオアミド基（ここでは−Ｃ（＝Ｓ）−ＮＨ−基）、および該チオアミド基の部分構造を含む基、すなわち、鎖状もしくは環状のチオアミド基、チオウレイド基、チオウレタン基、またはジチオカルバミン酸エステル基などが挙げられる。ここで環状の例としてはチアゾリジン−２−チオン基、オキサゾリジン−２−チオン基、２−チオヒダントイン基、ローダニン基、イソローダニン基、チオバルビツール酸基、２−チオキソ−オキサゾリジン−４−オン基などが挙げられる。
【０２０２】
吸着性基としてチオン基とは、上述のメルカプト基が互変異性化してチオン基となった場合を含め、メルカプト基に互変異性化できない（チオン基のα位に水素原子を持たない）、鎖状もしくは環状のチオアミド基、チオウレイド基、チオウレタン基、またはジチオカルバミン酸エステル基も含まれる。
【０２０３】
吸着性基として窒素原子、硫黄原子、セレン原子およびテルル原子から選ばれる少なくとも１つの原子を含むヘテロ環基とは、イミノ銀（＞ＮＡｇ）を形成しうる−ＮＨ−基をヘテロ環の部分構造として有する含窒素ヘテロ環基、または配位結合で銀イオンに配位し得る、”−Ｓ−”基または”−Ｓｅ−”基または”−Ｔｅ−”基または”＝Ｎ−”基をヘテロ環の部分構造として有するヘテロ環基で、前者の例としてはベンゾトリアゾール基、トリアゾール基、インダゾール基、ピラゾール基、テトラゾール基、ベンズイミダゾール基、イミダゾール基、プリン基などが、後者の例としてはチオフェン基、チアゾール基、オキサゾール基、ベンゾチアゾール基、ベンゾオキサゾール基、チアジアゾール基、オキサジアゾール基、トリアジン基、セレノアゾール基、ベンズセレノアゾール基、テルルアゾール基、ベンズテルルアゾール基などが挙げられる。好ましくは前者である。
【０２０４】
吸着性基としてスルフィド基とは、”−Ｓ−”の部分構造を有する基すべてが挙げられるが、好ましくはアルキル（またはアルキレン）−Ｓ−アルキル（またはアルキレン）、アリール（またはアリーレン）−Ｓ−アルキル（またはアルキレン）、アリール（またはアリーレン）−Ｓ−アリール（またはアリーレン）の部分構造を有する基である。さらにこれらのスルフィド基は、環状構造を形成していてもよく、また−Ｓ−Ｓ−基となっていてもよい。環状構造を形成する場合の具体例としてはチオラン環、１，３−ジチオラン環または１，２−ジチオラン環、チアン環、ジチアン環、テトラヒドロ−１，４−チアジン環（チオモルホリン環）などを含む基が挙げられる。スルフィド基として特に好ましくはアルキル（またはアルキレン）−Ｓ−アルキル（またはアルキレン）の部分構造を有する基である。
【０２０５】
吸着性基としてカチオン性基とは、４級化された窒素原子を含む基を意味し、具体的にはアンモニオ基または４級化された窒素原子を含む含窒素ヘテロ環基を含む基である。但し、該カチオン性基が色素構造を形成する原子団（例えばシアニン発色団）の一部となることはない。ここにアンモニオ基とは、トリアルキルアンモニオ基、ジアルキルアリールアンモニオ基、アルキルジアリールアンモニオ基などで、例えばベンジルジメチルアンモニオ基、トリヘキシルアンモニオ基、フェニルジエチルアンモニオ基などが挙げられる。４級化された窒素原子を含む含窒素ヘテロ環基とは、例えばピリジニオ基、キノリニオ基、イソキノリニオ基、イミダゾリオ基などが挙げられる。好ましくはピリジニオ基およびイミダゾリオ基であり、特に好ましくはピリジニオ基である。これら４級化された窒素原子を含む含窒素ヘテロ環基は任意の置換基を有していてもよいが、ピリジニオ基およびイミダゾリオ基の場合、置換基として好ましくはアルキル基、アリール基、アシルアミノ基、クロル原子、アルコキシカルボニル基、カルバモイル基などが挙げられ、ピリジニオ基の場合、置換基として特に好ましくはフェニル基である。
【０２０６】
吸着性基としてエチニル基とは、−Ｃ≡ＣＨ基を意味し、水素原子は置換されていてもよい。
上記の吸着性基は任意の置換基を有していてもよい。
【０２０７】
なお吸着性基の具体例としては、さらに特開平１１−９５３５５号の明細書４〜７頁に記載されているものが挙げられる。
【０２０８】
本発明において吸着性基として好ましいものは、メルカプト置換含窒素ヘテロ環基（例えば２−メルカプトチアジアゾール基、３−メルカプト−１，２，４−トリアゾール基、５−メルカプトテトラゾール基、２−メルカプト−１，３，４−オキサジアゾール基、２−メルカプトベンズオキサゾール基、２−メルカプトベンズチアゾール基、１，５−ジメチル−１，２，４−トリアゾリウム−３−チオレート基など）、またはイミノ銀（＞ＮＡｇ）を形成しうる−ＮＨ−基をヘテロ環の部分構造として有する含窒素ヘテロ環基（例えば、ベンゾトリアゾール基、ベンズイミダゾール基、インダゾール基など）である。特に好ましくは、５−メルカプトテトラゾール基、３−メルカプト−１，２，４−トリアゾール基、およびベンゾトリアゾール基であり、最も好ましいのは、３−メルカプト−１，２，４−トリアゾール基、および５−メルカプトテトラゾール基である。
【０２０９】
本発明の化合物のうち、分子内に２つ以上のメルカプト基を部分構造として有する化合物もまた特に好ましい化合物である。ここにメルカプト基（−ＳＨ）は、互変異性化できる場合にはチオン基となっていてもよい。この様な化合物の例としては、以上述べてきたメルカプト基もしくはチオン基を部分構造として有する吸着性基（例えば環形成チオアミド基、アルキルメルカプト基、アリールメルカプト基、ヘテロ環メルカプト基など）を分子内に２つ以上有する化合物であってもよいし、また吸着性基の中で、２つ以上のメルカプト基またはチオン基を部分構造として有する吸着性基（例えばジメルカプト置換含窒素ヘテロ環基）を、１つ以上有していてもよい。
【０２１０】
２つ以上のメルカプト基を部分構造として有する吸着性基（ジメルカプト置換含窒素ヘテロ環基など）の例としては、２，４−ジメルカプトピリミジン基、２，４−ジメルカプトトリアジン基、３，５−ジメルカプト−１，２，４−トリアゾール基、２，５−ジメルカプト−１，３−チアゾール基、２，５−ジメルカプト−１，３−オキサゾール基、２，７−ジメルカプト−５−メチル−ｓ−トリアゾロ（１，５−Ａ）−ピリミジン、２，６，８−トリメルカプトプリン、６，８−ジメルカプトプリン、３，５，７−トリメルカプト−ｓ−トリアゾロトリアジン、４，６−ジメルカプトピラゾロピリミジン、２，５−ジメルカプトイミダゾールなどが挙げられ、２，４−ジメルカプトピリミジン基、２，４−ジメルカプトトリアジン基、３，５−ジメルカプト−１，２，４−トリアゾール基が特に好ましい。
【０２１１】
吸着性基は一般式（Ａ）〜（Ｆ）および一般式（１）〜（３）のどこに置換されていてもよいが、一般式（Ａ）〜（Ｄ）においてはＲＥＤ_１１、ＲＥＤ_１２、ＲＥＤ_２、ＲＥＤ_３に、一般式（Ｅ）、（Ｆ）においてはＲＥＤ_４１、Ｒ_４１、ＲＥＤ_４２、Ｒ_４６〜Ｒ_４８に、一般式（１）〜（３）においてはＲ_１、Ｒ_２、Ｒ_１１、Ｒ_１２、Ｒ_３１、Ｌ_１、Ｌ_２１、Ｌ_３１を除く任意の位置に置換されていることが好ましく、さらに一般式（Ａ）〜（Ｆ）全てでＲＥＤ_１１〜ＲＥＤ_４２に置換されていることがより好ましい。
【０２１２】
分光増感色素の部分構造とは分光増感色素の発色団を含む基であり、分光増感色素化合物から任意の水素原子または置換基を除いた残基である。分光増感色素の部分構造は一般式（Ａ）〜（Ｆ）および一般式（１）〜（３）のどこに置換されていてもよいが、一般式（Ａ）〜（Ｄ）においてはＲＥＤ_１１、ＲＥＤ_１２、ＲＥＤ_２、ＲＥＤ_３に、一般式（Ｅ）、（Ｆ）においてはＲＥＤ_４１、Ｒ_４１、ＲＥＤ_４２、Ｒ_４６〜Ｒ_４８に、一般式（１）〜（３）においてはＲ_１、Ｒ_２、Ｒ_１１、Ｒ_１２、Ｒ_３１、Ｌ_１、Ｌ_２１、Ｌ_３１を除く任意の位置に置換されていることが好ましく、さらに一般式（Ａ）〜（Ｆ）全てでＲＥＤ_１１〜ＲＥＤ_４２に置換されていることがより好ましい。
【０２１３】
好ましい分光増感色素は、典型的にカラー増感技法で用いられる分光増感色素であり、例えばシアニン色素類、複合シアニン色素類、メロシアニン色素類、複合メロシアニン色素類、同極のシアニン色素類、スチリル色素類、ヘミシアニン色素類を含む。代表的な分光増感色素は、リサーチディスクロージャー、アイテム３６５４４、１９９４年９月に開示されている。前記リサーチディスクロージャー、もしくはＦ．Ｍ．ＨａｍｅｒのＴｈｅ Ｃｙａｎｉｎｅ ｄｙｅｓ ａｎｄ Ｒｅｌａｔｅｄ Ｃｏｍｐｏｕｎｄｓ （Ｉｎｔｅｒｓｃｉｅｎｃｅ Ｐｕｂｌｉｓｈｅｒｓ， Ｎｅｗ ｙｐｒｋ， １９６４）に記載される手順によって当業者は、これらの色素を合成することができる。さらに特開平１１−９５３５５号（米国特許６，０５４，２６０号）の明細書７〜１４頁に記載された色素類が全てそのまま当てはまる。
【０２１４】
本発明のタイプ１〜４の化合物は、その総炭素数が１０〜６０の範囲のものが好ましい。より好ましくは１５〜５０、さらに好ましくは１８〜４０であり、特に好ましくは１８〜３０である。
【０２１５】
本発明のタイプ１〜４の化合物は、これを用いたハロゲン化銀写真感光材料が露光されることを引き金に１電子酸化され、引き続く反応の後、さらに１電子、あるいはタイプによっては２電子以上の電子が放出され、酸化されるが、その１電子目の酸化電位は、約１．４Ｖ以下が好ましく、さらには１．０Ｖ以下が好ましい。この酸化電位は好ましくは０Ｖより高く、より好ましくは０．３Ｖより高い。従って酸化電位は好ましくは約０〜約１．４Ｖ、より好ましくは約０．３〜約１．０Ｖの範囲である。
【０２１６】
ここに酸化電位はサイクリックボルタンメトリーの技法で測定でき、具体的には試料をアセトニトリル：水（０．１Ｍの過塩素酸リチウムを含む）＝８０％：２０％（容量％）の溶液に溶解し、１０分間窒素ガスを通気した後、ガラス状のカーボンディスクを動作電極に用い、プラチナ線を対電極に用い、そしてカロメル電極（ＳＣＥ）を参照電極に用いて、２５℃で、０．１Ｖ／秒の電位走査速度で測定したものである。サイクリックボルタンメトリー波のピーク電位の時に酸化電位対ＳＣＥをとる。
【０２１７】
本発明のタイプ１〜４の化合物が１電子酸化され、引き続く反応の後、さらに１電子を放出する化合物である場合には、この後段の酸化電位は好ましくは−０．５Ｖ〜−２Ｖであり、より好ましくは−０．７Ｖ〜−２Ｖであり、さらに好ましくは−０．９Ｖ〜−１．６Ｖである。
【０２１８】
本発明のタイプ１〜４の化合物が１電子酸化され、引き続く反応の後、さらに２電子以上の電子を放出し、酸化される化合物である場合には、この後段の酸化電位については特に制限はない。２電子目の酸化電位と３電子目以降の酸化電位が明確に区別できない点で、これらを実際に正確に測定し区別することは困難な場合が多いためである。
【０２１９】
次にタイプ５の化合物について説明する。
タイプ５の化合物はＸ−Ｙで表され、ここにＸは還元性基を、Ｙは脱離基を表し、Ｘで表される還元性基が１電子酸化されて生成する１電子酸化体が、引き続くＸ−Ｙ結合の開裂反応を伴ってＹを脱離してＸラジカルを生成し、そこからさらにもう１電子を放出し得る化合物である。この様なタイプ５の化合物が酸化された時の反応は、以下の式で表すことができる。
【０２２０】
【化２４】

【０２２１】
タイプ５の化合物は好ましくはその酸化電位が０〜１．４Ｖであり、より好ましくは０．３Ｖ〜１．０Ｖである。また上記反応式において生成するラジカルＸ・の酸化電位は−０．７Ｖ〜−２．０Ｖであることが好ましく、−０．９Ｖ〜−１．６Ｖがより好ましい。
【０２２２】
タイプ５の化合物は、好ましくは一般式（Ｇ）で表される。
【０２２３】
一般式（Ｇ）
【化２５】

【０２２４】
一般式（Ｇ）においてＲＥＤ_０は還元性基を表し、Ｌ_０は脱離基を表し、Ｒ_０およびＲ_００は水素原子または置換基を表す。ＲＥＤ_０ とＲ_０、およびＲ_０とＲ_００とは互いに結合して環構造を形成していてもよい。ＲＥＤ_０は一般式（Ｃ）のＲＥＤ_２と同義の基を表し、その好ましい範囲も同じである。Ｒ_０およびＲ_００は一般式（Ｃ）のＲ_２１およびＲ_２２と同義の基であり、その好ましい範囲も同じである。但しＲ_０およびＲ_００が、水素原子を除いて、Ｌ_０と同義の基を表すことはない。ＲＥＤ_０とＲ_０とは互いに結合して環構造を形成していてもよく、ここに環構造の例としては、一般式（Ｃ）のＲＥＤ_２とＲ_２１が連結して環構造を形成する場合と同じ例が挙げられ、その好ましい範囲も同じである。Ｒ_０とＲ_００とが互いに結合して形成される環構造の例としては、シクロペンタン環やテトラヒドロフラン環などが挙げられる。一般式（Ｇ）においてＬ_０は、一般式（Ｃ）のＬ_２と同義の基であり、その好ましい範囲も同じである。
【０２２５】
一般式（Ｇ）で表される化合物は分子内にハロゲン化銀への吸着性基、もしくは分光増感色素の部分構造を有していることが好ましいが、Ｌ_０がシリル基以外の基を表す時、分子内に吸着性基を同時に２つ以上有することはない。但しここで吸着性基としてのスルフィド基は、Ｌ_０に依らず、これを２つ以上有していてもよい。
【０２２６】
一般式（Ｇ）で表される化合物が有するハロゲン化銀への吸着性基としては、本発明のタイプ１〜４の化合物が有していてもよい吸着性基と同じものがその例として挙げられるが、さらに加えて、特開平１１−９５３５５号の明細書４〜７頁に「ハロゲン化銀吸着基」として記載されているもの全てが挙げられ、好ましい範囲も同じである。
一般式（Ｇ）で表される化合物が有していてもよい分光増感色素の部分構造とは、本発明のタイプ１〜４の化合物が有していてもよい分光増感色素の部分構造と同じであるが、同時に特開平１１−９５３５５号の明細書７〜１４頁に「光吸収性基」として記載されているもの全てが挙げられ、好ましい範囲も同じである。
【０２２７】
以下に本発明のタイプ１〜５の化合物の具体例を列挙するが、本発明はこれらに限定されるものではない。
【０２２８】
【化２６】

【０２２９】
【化２７】

【０２３０】
【化２８】

【０２３１】
【化２９】

【０２３２】
本発明のタイプ１〜４の化合物は、それぞれ特願２００２−１９２３７３号、特願２００２−１８８５３７号、特願２００２−１８８５３６号、特願２００１−２７２１３７号、特願２００２−１９２３７４号において、詳細に説明した化合物と同じものである。これら特許出願明細書に記載した具体的化合物例もまた、本発明のタイプ１〜４の化合物の具体例として挙げることができる。また本発明のタイプ１〜４の化合物の合成例も、これら特許に記載したものと同じである。
【０２３３】
本発明のタイプ５の化合物の具体例としては、さらに特開平９−２１１７６９号（２８〜３２頁の表Ｅおよび表Ｆに記載の化合物ＰＭＴ−１〜Ｓ−３７）、特開平９−２１１７７４号、特開平１１−９５３５５号（化合物ＩＮＶ１〜３６）、特表２００１−５００９９６号（化合物１〜７４、８０〜８７、９２〜１２２）、米国特許５，７４７，２３５号、米国特許５，７４７，２３６号、欧州特許７８６６９２Ａ１号（化合物ＩＮＶ１〜３５）、欧州特許８９３７３２Ａ１号、米国特許６，０５４，２６０号、米国特許５，９９４，０５１号などの特許に記載の「１光子２電子増感剤」または「脱プロトン化電子供与増感剤」と称される化合物の例が、そのまま挙げられる。
【０２３４】
本発明のタイプ１〜５の化合物は感光性ハロゲン化銀乳剤調製時、熱現像感光材料製造工程中のいかなる場合にも使用しても良い。例えば感光性ハロゲン化銀粒子形成時、脱塩工程、化学増感時、塗布前などである。またこれらの工程中の複数回に分けて添加することも出来る。添加位置として好ましくは、感光性ハロゲン化銀粒子形成終了時から脱塩工程の前、化学増感時（化学増感開始直前から終了直後）、塗布前であり、より好ましくは化学増感時から非感光性有機銀塩と混合される前までである。
【０２３５】
本発明のタイプ１〜５の化合物は水、メタノール、エタノールなどの水可溶性溶媒またはこれらの混合溶媒に溶解して添加することが好ましい。水に溶解する場合、ｐＨを高くまたは低くした方が溶解度が上がる化合物については、ｐＨを高くまたは低くして溶解し、これを添加しても良い。
【０２３６】
本発明のタイプ１〜５の化合物は感光性ハロゲン化銀と非感光性有機銀塩を含有するＩ画像形成層中に使用するのが好ましいが、感光性ハロゲン化銀と非感光性有機銀塩を含有するＩ画像形成層と共に保護層や中間層に添加しておき、塗布時に拡散させてもよい。本発明の化合物の添加時期は増感色素の前後を問わず、それぞれ好ましくはハロゲン化銀１モル当り、１×１０^−９モル〜５×１０^−１モル、更に好ましくは１×１０^−８モル〜５×１０^−２モルの割合でハロゲン化銀Ｉ画像形成層に含有する。
【０２３７】
１０）吸着基と還元基を有する吸着性レドックス化合物
本発明においては、分子内に銀への吸着基と還元基を有する吸着性レドックス化合物を含有させることが好ましい。本吸着性レドックス化合物は下記式（Ｉ）で表される化合物であることが好ましい。
【０２３８】
式（Ｉ） Ａ−（Ｗ）ｎ−Ｂ
［式（Ｉ）中、Ａはハロゲン化銀に吸着可能な基（以後、吸着基と呼ぶ）を表し、Ｗは２価の連結基を表し、ｎは０または１を表し、Ｂは還元基を表す。］
【０２３９】
式（Ｉ）中、Ａで表される吸着基とはハロゲン化銀に直接吸着する基、またはハロゲン化銀への吸着を促進する基であり、具体的には、メルカプト基（またはその塩）、チオン基（−Ｃ（＝Ｓ）−）、窒素原子、硫黄原子、セレン原子およびテルル原子から選ばれる少なくとも１つの原子を含むヘテロ環基、スルフィド基、ジスルフィド基、カチオン性基、またはエチニル基等が挙げられる。
【０２４０】
吸着基としてメルカプト基（またはその塩）とは、メルカプト基（またはその塩）そのものを意味すると同時に、より好ましくは、少なくとも１つのメルカプト基（またはその塩）の置換したヘテロ環基またはアリール基またはアルキル基を表す。ここにヘテロ環基とは、少なくとも５員〜７員の、単環もしくは縮合環の、芳香族または非芳香族のヘテロ環基、例えばイミダゾール環基、チアゾール環基、オキサゾール環基、ベンゾイミダゾール環基、ベンゾチアゾール環基、ベンゾオキサゾール環基、トリアゾール環基、チアジアゾール環基、オキサジアゾール環基、テトラゾール環基、プリン環基、ピリジン環基、キノリン環基、イソキノリン環基、ピリミジン環基、トリアジン環基等が挙げられる。また４級化された窒素原子を含むヘテロ環基でもよく、この場合、置換したメルカプト基が解離してメソイオンとなっていても良い。メルカプト基が塩を形成するとき、対イオンとしてはアルカリ金属、アルカリ土類金属、重金属などのカチオン（Ｌｉ^＋、Ｎａ^＋、Ｋ^＋、Ｍｇ^２＋、Ａｇ^＋、Ｚｎ^２＋等）、アンモニウムイオン、４級化された窒素原子を含むヘテロ環基、ホスホニウムイオンなどが挙げられる。
【０２４１】
吸着基としてのメルカプト基はさらにまた、互変異性化してチオン基となっていても良い。
【０２４２】
吸着基としてチオン基とは、鎖状もしくは環状のチオアミド基、チオウレイド基、チオウレタン基、またはジチオカルバミン酸エステル基も含まれる。
【０２４３】
吸着基として窒素原子、硫黄原子、セレン原子およびテルル原子から選ばれる少なくとも１つの原子を含むヘテロ環基とは、イミノ銀（＞ＮＡｇ）を形成しうる−ＮＨ−基をヘテロ環の部分構造として有する含窒素ヘテロ環基、または配位結合で銀イオンに配位し得る、”−Ｓ−”基または”−Ｓｅ−”基または”−Ｔｅ−”基または”＝Ｎ−”基をヘテロ環の部分構造として有するヘテロ環基で、前者の例としてはベンゾトリアゾール基、トリアゾール基、インダゾール基、ピラゾール基、テトラゾール基、ベンゾイミダゾール基、イミダゾール基、プリン基などが、後者の例としてはチオフェン基、チアゾール基、オキサゾール基、ベンゾチオフェン基、ベンゾチアゾール基、ベンゾオキサゾール基、チアジアゾール基、オキサジアゾール基、トリアジン基、セレノアゾール基、ベンゾセレノアゾール基、テルルアゾール基、ベンゾテルルアゾール基などが挙げられる。
【０２４４】
吸着基としてスルフィド基またはジスルフィド基とは、”−Ｓ−”または”−Ｓ−Ｓ−”の部分構造を有する基すべてが挙げられる。
【０２４５】
吸着基としてカチオン性基とは、４級化された窒素原子を含む基を意味し、具体的にはアンモニオ基または４級化された窒素原子を含む含窒素ヘテロ環基を含む基である。４級化された窒素原子を含む含窒素ヘテロ環基とは、例えばピリジニオ基、キノリニオ基、イソキノリニオ基、イミダゾリオ基などが挙げられる。吸着基としてエチニル基とは、−Ｃ≡ＣＨ基を意味し、該水素原子は置換されていてもよい。
【０２４６】
上記の吸着基は任意の置換基を有していてもよい。
【０２４７】
さらに吸着基の具体例としては、さらに特開平１１−９５３５５号の明細書ｐ４〜ｐ７に記載されているものが挙げられる。
【０２４８】
式（Ｉ）中、Ａで表される吸着基として好ましいものは、メルカプト置換ヘテロ環基（例えば２−メルカプトチアジアゾール基、２−メルカプト−５−アミノチアジアゾール基、３−メルカプト−１，２，４−トリアゾール基、５−メルカプトテトラゾール基、２−メルカプト−１，３，４−オキサジアゾール基、２−メルカプトベンズイミダゾール基、１，５−ジメチル−１，２，４−トリアゾリウム−３−チオレート基、２，４−ジメルカプトピリミジン基、２，４−ジメルカプトトリアジン基、３，５−ジメルカプト−１，２，４−トリアゾール基、２，５−ジメルカプト−１，３−チアゾール基など）、またはイミノ銀（＞ＮＡｇ）を形成しうる−ＮＨ−基をヘテロ環の部分構造として有する含窒素ヘテロ環基（例えばベンゾトリアゾール基、ベンズイミダゾール基、インダゾール基など）であり、さらに好ましい吸着基は２−メルカプトベンズイミダゾール基、３，５−ジメルカプト−１，２，４−トリアゾール基である。
【０２４９】
式（Ｉ）中、Ｗは２価の連結基を表す。該連結基は写真性に悪影響を与えないものであればどのようなものでも構わない。例えば炭素原子、水素原子、酸素原子、窒素原子、硫黄原子から構成される２価の連結基が利用できる。具体的には炭素数１〜２０のアルキレン基（例えばメチレン基、エチレン基、トリメチレン基、テトラメチレン基、ヘキサメチレン基等）、炭素数２〜２０のアルケニレン基、炭素数２〜２０のアルキニレン基、炭素数６〜２０のアリーレン基（例えばフェニレン基、ナフチレン基等）、−ＣＯ−、−ＳＯ_２−、−Ｏ−、−Ｓ−、−ＮＲ_１−、これらの連結基の組み合わせ等があげられる。ここでＲ_１は水素原子、アルキル基、ヘテロ環基、アリール基を表わす。
Ｗで表される連結基は任意の置換基を有していてもよい。
【０２５０】
式（Ｉ）中、Ｂで表される還元基とは銀イオンを還元可能な基を表し、例えばホルミル基、アミノ基、アセチレン基やプロパルギル基などの３重結合基、メルカプト基、ヒドロキシルアミン類、ヒドロキサム酸類、ヒドロキシウレア類、ヒドロキシウレタン類、ヒドロキシセミカルバジド類、レダクトン類（レダクトン誘導体を含む）、アニリン類、フェノール類（クロマン−６−オール類、２，３−ジヒドロベンゾフラン−５−オール類、アミノフェノール類、スルホンアミドフェノール類、およびハイドロキノン類、カテコール類、レゾルシノール類、ベンゼントリオール類、ビスフェノール類のようなポリフェノール類を含む）、アシルヒドラジン類、カルバモイルヒドラジン類、３−ピラゾリドン類等から水素原子を１つ除去した残基が挙げられる。もちろん、これらは任意の置換基を有していても良い。
【０２５１】
式（Ｉ）中、Ｂで表される還元基はその酸化電位を、藤嶋昭著「電気化学測定法」（１５０−２０８頁、技報堂出版）や日本化学会編著「実験化学講座」第４版（９巻２８２−３４４頁、丸善）に記載の測定法を用いて測定することができる。例えば回転ディスクボルタンメトリーの技法で、具体的には試料をメタノール：ｐＨ６．５ ブリトン−ロビンソン緩衝液（Ｂｒｉｔｔｏｎ−Ｒｏｂｉｎｓｏｎ ｂｕｆｆｅｒ）＝１０％：９０％（容量％）の溶液に溶解し、１０分間窒素ガスを通気した後、グラッシーカーボン製の回転ディスク電極（ＲＤＥ）を作用電極に用い、白金線を対極に用い、飽和カロメル電極を参照電極に用いて、２５℃、１０００回転／分、２０ｍＶ／秒のスイープ速度で測定できる。得られたボルタモグラムから半波電位（Ｅ１／２）を求めることができる。
【０２５２】
本発明のＢで表される還元基は上記測定法で測定した場合、その酸化電位が約−０．３Ｖ〜約１．０Ｖの範囲にあることが好ましい。より好ましくは約−０．１Ｖ〜約０．８Ｖの範囲であり、特に好ましくは約０〜約０．７Ｖの範囲である。
【０２５３】
式（Ｉ）中、Ｂで表される還元基は好ましくはヒドロキシルアミン類、ヒドロキサム酸類、ヒドロキシウレア類、ヒドロキシセミカルバジド類、レダクトン類、フェノール類、アシルヒドラジン類、カルバモイルヒドラジン類、３−ピラゾリドン類から水素原子を１つ除去した残基である。
【０２５４】
以下にＢで表される還元基の具体例を例示するが、本発明はこれらに限定されるものではない。ここで＊印は式（Ｉ）において、ＡまたはＷと結合する位置を示す。
【０２５５】
【化３０】

【０２５６】
本発明の式（Ｉ）の化合物は、その中にカプラー等の不動性写真用添加剤において常用されているバラスト基またはポリマー鎖が組み込まれているものでもよい。またポリマーとしては、例えば特開平１−１００５３０号に記載のものが挙げられる。
【０２５７】
本発明の式（Ｉ）の化合物はビス体、トリス体であっても良い。本発明の式（Ｉ）の化合物の分子量は好ましくは１００〜１００００の間であり、より好ましくは１２０〜１０００の間であり、特に好ましくは１５０〜５００の間である。
【０２５８】
以下に本発明の式（Ｉ）の化合物を例示するが、本発明はこれらに限定されるものではない。
【０２５９】
【化３１】

【０２６０】
【化３２】

【０２６１】
【化３３】

【０２６２】
【化３４】

【０２６３】
【化３５】

【０２６４】
【化３６】

【０２６５】
【化３７】

【０２６６】
【化３８】

【０２６７】
本発明の化合物は公知の方法にならって容易に合成することが出来る。
本発明の式（Ｉ）の化合物は、一種類の化合物を単独で用いてもよいが、同時に２種以上の化合物を用いることも好ましい。２種類以上の化合物を用いる場合、それらは同一層に添加しても、別層に添加してもよく、またそれぞれ添加方法が異なっていてもよい。
【０２６８】
本発明の式（Ｉ）の化合物は、感光性ハロゲン化銀乳剤を含有する層に添加されることが好ましく、乳剤調製時に添加することがより好ましい。乳剤調製時に添加する場合、その工程中のいかなる場合に添加することも可能であり、その例を挙げると、ハロゲン化銀の粒子形成工程、脱塩工程の開始前、脱塩工程、化学熟成の開始前、化学熟成の工程、完成乳剤調製前の工程などを挙げることができる。またこれらの工程中の複数回にわけて添加することもできる。
本発明の式（Ｉ）の化合物は、画像形成層に使用するのが好ましいが、画像形成層とともに隣接する保護層や中間層に添加しておき、塗布時に拡散させてもよい。
【０２６９】
好ましい添加量は、上述した添加法や添加する化合物種に大きく依存するが、一般には感光性ハロゲン化銀１モル当たり、１×１０^−６モル〜１モル、好ましくは１×１０^−５モル〜５×１０^−１モルさらに好ましくは１×１０^−４モル〜１×１０^−１モルである。
【０２７０】
本発明の式（Ｉ）の化合物は、水、メタノール、エタノールなどの水可溶性溶媒またはこれらの混合溶媒に溶解して添加することができる。この際、酸または塩基によってｐＨを適当に調整してもよく、また界面活性剤を共存させてもよい。さらに乳化分散物として高沸点有機溶媒に溶解させて添加することもできる。また、固体分散物として添加することもできる。
【０２７１】
１１）増感色素
本発明に適用できる増感色素としてはハロゲン化銀粒子に吸着した際、所望の波長領域でハロゲン化銀粒子を分光増感できるもので、露光光源の分光特性に適した分光感度を有する増感色素を有利に選択することができる。本発明の熱現像感光材料は特に６００ｎｍ以上９００ｎｍ以下、または３００ｎｍ以上５００ｎｍ以下に分光感度ピークを持つように分光増感されていることが好ましい。増感色素及び添加法については、特開平１１−６５０２１号の段落番号０１０３〜０１０９、特開平１０−１８６５７２号一般式（ＩＩ）で表される化合物、特開平１１−１１９３７４号の一般式（Ｉ） で表される色素及び段落番号０１０６、米国特許第５，５１０，２３６号、同第３，８７１，８８７号実施例５に記載の色素、特開平２−９６１３１号、特開昭５９−４８７５３号に開示されている色素、欧州特許公開第０８０３７６４Ａ１号の第１９ページ第３８行〜第２０ページ第３５行、特願２０００−８６８６５号、特願２０００−１０２５６０号、特願２０００−２０５３９９号等に記載されている。これらの増感色素は単独で用いてもよく、２種以上組合せて用いてもよい。
【０２７２】
本発明における増感色素の添加量は、感度やカブリの性能に合わせて所望の量にすることができるが、感光性層のハロゲン化銀１モル当たり１０^−６〜１モルが好ましく、さらに好ましくは１０^−４〜１０^−１モルである。
【０２７３】
本発明は分光増感効率を向上させるため、強色増感剤を用いることができる。本発明に用いる強色増感剤としては、欧州特許公開第５８７，３３８号、米国特許第３，８７７，９４３号、同第４，８７３，１８４号、特開平５−３４１４３２号、同１１−１０９５４７号、同１０−１１１５４３号等に記載の化合物が挙げられる。
【０２７４】
１２）ハロゲン化銀の併用
本発明に用いられる熱現像感光材料中の感光性ハロゲン化銀乳剤は、一種だけでもよいし、二種以上（例えば、平均粒子サイズの異なるもの、ハロゲン組成の異なるもの、晶癖の異なるもの、化学増感の条件の異なるもの）併用してもよい。感度の異なる感光性ハロゲン化銀を複数種用いることで階調を調節することができる。これらに関する技術としては特開昭５７−１１９３４１号、同５３−１０６１２５号、同４７−３９２９号、同４８−５５７３０号、同４６−５１８７号、同５０−７３６２７号、同５７−１５０８４１号などが挙げられる。感度差としてはそれぞれの乳剤で０．２ｌｏｇＥ以上の差を持たせることが好ましい。
【０２７５】
１３）ハロゲン化銀と有機銀塩の混合
本発明の感光性ハロゲン化銀の粒子は、非感光性有機銀塩の存在しないところで形成され、化学増感されることが特に好ましい。有機銀塩に対してハロゲン化剤を添加することによってハロゲン化銀を形成する方法では十分な感度が達成できない場合があるからである。
ハロゲン化銀と有機銀塩を混合する方法としては、別々に調製した感光性ハロゲン化銀と有機銀塩を高速撹拌機やボールミル、サンドミル、コロイドミル、振動ミル、ホモジナイザー等で混合する方法や、あるいは有機銀塩の調製中のいずれかのタイミングで調製終了した感光性ハロゲン化銀を混合して有機銀塩を調製する方法等があげられる。いずれの方法でも本発明の効果を好ましく得ることができる。
【０２７６】
１４）ハロゲン化銀の塗布液への混合
本発明のハロゲン化銀の画像形成層塗布液中への好ましい添加時期は、塗布する１８０分前から直前、好ましくは６０分前から１０秒前であるが、混合方法及び混合条件については本発明の効果が十分に現れる限りにおいては特に制限はない。具体的な混合方法としては添加流量とコーターへの送液量から計算した平均滞留時間を所望の時間となるようにしたタンクでの混合する方法やＮ．Ｈａｒｎｂｙ、Ｍ．Ｆ．Ｅｄｗａｒｄｓ、Ａ．Ｗ．Ｎｉｅｎｏｗ著、高橋幸司訳”液体混合技術”（日刊工業新聞社刊、１９８９年）の第８章等に記載されているスタチックミキサーなどを使用する方法がある。
【０２７７】
（現像促進剤の説明）
本発明の熱現像感光材料では、現像促進剤として特開２０００−２６７２２２号明細書や特開２０００−３３０２３４号明細書等に記載の一般式（Ａ）で表されるスルホンアミドフェノール系の化合物、特開平２００１−９２０７５記載の一般式（ＩＩ）で表されるヒンダードフェノール系の化合物、特開平１０−６２８９５号明細書や特開平１１−１５１１６号明細書等に記載の一般式（Ｉ）、特開２００２−１５６７２７号の一般式（Ｄ）や特願２００１−０７４２７８号明細書に記載の一般式（１）で表されるヒドラジン系の化合物、特開２００１−２６４９２９号明細書に記載されている一般式（２）で表されるフェノール系またはナフトール系の化合物が好ましく用いられる。これらの現像促進剤は還元剤に対して０．１モル％〜２０モル％の範囲で使用され、好ましくは０．５モル％〜１０モル％の範囲で、より好ましくは１モル％〜５モル％の範囲である。感材への導入方法は還元剤同様の方法があげられるが、特に固体分散物または乳化分散物として添加することが好ましい。乳化分散物として添加する場合、常温で固体である高沸点溶剤と低沸点の補助溶剤を使用して分散した乳化分散物として添加するか、もしくは高沸点溶剤を使用しない所謂オイルレス乳化分散物として添加することが好ましい。
本発明においては上記現像促進剤の中でも、特開２００２−１５６７２７号明細書に記載の一般式（Ｄ）で表されるヒドラジン系の化合物および特開２００１−２６４９２９号明細書に記載されている一般式（２）で表されるフェノール系またはナフトール系の化合物がより好ましい。
【０２７８】
本発明の特に好ましい現像促進剤は下記一般式（Ａ−１）および（Ａ−２）で表される化合物である。
一般式（Ａ−１）
Ｑ_１−ＮＨＮＨ−Ｑ_２
（式中、Ｑ_１は炭素原子で−ＮＨＮＨ−Ｑ_２と結合する芳香族基、またはヘテロ環基を表し、Ｑ_２はカルバモイル基、アシル基、アルコキシカルボニル基、アリールオキシカルボニル基、スルホニル基、またはスルファモイル基を表す。）
【０２７９】
一般式（Ａ−１）において、Ｑ_１で表される芳香族基またはヘテロ環基としては５〜７員の不飽和環が好ましい。好ましい例としては、ベンゼン環、ピリジン環、ピラジン環、ピリミジン環、ピリダジン環、１，２，４−トリアジン環、１，３，５−トリアジン環、ピロール環、イミダゾール環、ピラゾール環、１，２，３−トリアゾール環、１，２，４−トリアゾール環、テトラゾール環、１，３，４−チアジアゾール環、１，２，４−チアジアゾール環、１，２，５−チアジアゾール環、１，３，４−オキサジアゾール環、１，２，４−オキサジアゾール環、１，２，５−オキサジアゾール環、チアゾール環、オキサゾール環、イソチアゾール環、イソオキサゾール環、チオフェン環などが好ましく、さらにこれらの環が互いに縮合した縮合環も好ましい。
【０２８０】
これらの環は置換基を有していてもよく、２個以上の置換基を有する場合には、それらの置換基は同一であっても異なっていてもよい。置換基の例としては、ハロゲン原子、アルキル基、アリール基、カルボンアミド基、アルキルスルホンアミド基、アリールスルホンアミド基、アルコキシ基、アリールオキシ基、アルキルチオ基、アリールチオ基、カルバモイル基、スルファモイル基、シアノ基、アルキルスルホニル基、アリールスルホニル基、アルコキシカルボニル基、アリールオキシカルボニル基、およびアシル基を挙げることができる。これらの置換基が置換可能な基である場合、さらに置換基を有してもよく、好ましい置換基の例としては、ハロゲン原子、アルキル基、アリール基、カルボンアミド基、アルキルスルホンアミド基、アリールスルホンアミド基、アルコキシ基、アリールオキシ基、アルキルチオ基、アリールチオ基、アシル基、アルコキシカルボニル基、アリールオキシカルボニル基、カルバモイル基、シアノ基、スルファモイル基、アルキルスルホニル基、アリールスルホニル基、およびアシルオキシ基を挙げることができる。
【０２８１】
Ｑ_２で表されるカルバモイル基は、好ましくは炭素数１〜５０、より好ましくは炭素数６〜４０のカルバモイル基であり、例えば、無置換カルバモイル、メチルカルバモイル、Ｎ−エチルカルバモイル、Ｎ−プロピルカルバモイル、Ｎ−ｓｅｃ−ブチルカルバモイル、Ｎ−オクチルカルバモイル、Ｎ−シクロヘキシルカルバモイル、Ｎ−ｔｅｒｔ−ブチルカルバモイル、Ｎ−ドデシルカルバモイル、Ｎ−（３−ドデシルオキシプロピル）カルバモイル、Ｎ−オクタデシルカルバモイル、Ｎ−｛３−（２，４−ｔｅｒｔ−ペンチルフェノキシ）プロピル｝カルバモイル、Ｎ−（２−ヘキシルデシル）カルバモイル、Ｎ−フェニルカルバモイル、Ｎ−（４−ドデシルオキシフェニル）カルバモイル、Ｎ−（２−クロロ−５−ドデシルオキシカルボニルフェニル）カルバモイル、Ｎ−ナフチルカルバモイル、Ｎ−３−ピリジルカルバモイル、Ｎ−ベンジルカルバモイルが挙げられる。
【０２８２】
Ｑ_２で表されるアシル基は、好ましくは炭素数１〜５０、より好ましくは炭素数６〜４０のアシル基であり、例えば、ホルミル、アセチル、２−メチルプロパノイル、シクロヘキシルカルボニル、オクタノイル、２−ヘキシルデカノイル、ドデカノイル、クロロアセチル、トリフルオロアセチル、ベンゾイル、４−ドデシルオキシベンゾイル、２−ヒドロキシメチルベンゾイルが挙げられる。Ｑ２で表されるアルコキシカルボニル基は、好ましくは炭素数２〜５０、より好ましくは炭素数６〜４０のアルコキシカルボニル基であり、例えば、メトキシカルボニル、エトキシカルボニル、イソブチルオキシカルボニル、シクロヘキシルオキシカルボニル、ドデシルオキシカルボニル、ベンジルオキシカルボニルが挙げられる。
【０２８３】
Ｑ_２で表されるアリールオキシカルボニル基は、好ましくは炭素数７〜５０、より好ましくは炭素数７〜４０のアリールオキシカルボニル基で、例えば、フェノキシカルボニル、４−オクチルオキシフェノキシカルボニル、２−ヒドロキシメチルフェノキシカルボニル、４−ドデシルオキシフェノキシカルボニルが挙げられる。Ｑ２で表されるスルホニル基は、好ましくは炭素数１〜５０、より好ましくは炭素数６〜４０のスルホニル基で、例えば、メチルスルホニル、ブチルスルホニル、オクチルスルホニル、２−ヘキサデシルスルホニル、３−ドデシルオキシプロピルスルホニル、２−オクチルオキシ−５−ｔｅｒｔ−オクチルフェニルスルホニル、４−ドデシルオキシフェニルスルホニルが挙げられる。
【０２８４】
Ｑ_２で表されるスルファモイル基は、好ましくは炭素数０〜５０、より好ましくは炭素数６〜４０のスルファモイル基で、例えば、無置換スルファモイル、Ｎ−エチルスルファモイル基、Ｎ−（２−エチルヘキシル）スルファモイル、Ｎ−デシルスルファモイル、Ｎ−ヘキサデシルスルファモイル、Ｎ−｛３−（２−エチルヘキシルオキシ）プロピル｝スルファモイル、Ｎ−（２−クロロ−５−ドデシルオキシカルボニルフェニル）スルファモイル、Ｎ−（２−テトラデシルオキシフェニル）スルファモイルが挙げられる。Ｑ_２で表される基は、さらに、置換可能な位置に前記のＱ_１で表される５〜７員の不飽和環の置換基の例として挙げた基を有していてもよく、２個以上の置換基を有する場合には、それ等の置換基は同一であっても異なっていてもよい。
【０２８５】
次に、式（Ａ−１）で表される化合物の好ましい範囲について述べる。Ｑ_１としては５〜６員の不飽和環が好ましく、ベンゼン環、ピリミジン環、１，２，３−トリアゾール環、１，２，４−トリアゾール環、テトラゾール環、１，３，４−チアジアゾール環、１，２，４−チアジアゾール環、１，３，４−オキサジアゾール環、１，２，４−オキサジアゾール環、チアゾール環、オキサゾール環、イソチアゾール環、イソオキサゾール環、およびこれらの環がベンゼン環もしくは不飽和ヘテロ環と縮合した環が更に好ましい。また、Ｑ_２はカルバモイル基が好ましく、特に窒素原子上に水素原子を有するカルバモイル基が好ましい。
【０２８６】
一般式（Ａ−２）
【化３９】

【０２８７】
一般式（Ａ−２）においてＲ_１はアルキル基、アシル基、アシルアミノ基、スルホンアミド基、アルコキシカルボニル基、カルバモイル基を表す。Ｒ_２は水素原子、ハロゲン原子、アルキル基、アルコキシ基、アリールオキシ基、アルキルチオ基、アリールチオ基、アシルオキシ基、炭酸エステル基を表す。Ｒ_３、Ｒ_４はそれぞれ一般式（Ａ−１）の置換基例で挙げたベンゼン環に置換可能な基を表す。Ｒ_３とＲ_４は互いに連結して縮合環を形成してもよい。
【０２８８】
Ｒ_１は好ましくは炭素数１〜２０のアルキル基（例えばメチル基、エチル基、イソプロピル基、ブチル基、ｔｅｒｔ−オクチル基、シクロヘキシル基など）、アシルアミノ基（例えばアセチルアミノ基、ベンゾイルアミノ基、メチルウレイド基、４−シアノフェニルウレイド基など）、カルバモイル基（ｎ−ブチルカルバモイル基、Ｎ，Ｎ−ジエチルカルバモイル基、フェニルカルバモイル基、２−クロロフェニルカルバモイル基、２，４−ジクロロフェニルカルバモイル基など）でアシルアミノ基（ウレイド基、ウレタン基を含む）がより好ましい。Ｒ２は好ましくはハロゲン原子（より好ましくは塩素原子、臭素原子）、アルコキシ基（例えばメトキシ基、ブトキシ基、ｎ−ヘキシルオキシ基、ｎ−デシルオキシ基、シクロヘキシルオキシ基、ベンジルオキシ基など）、アリールオキシ基（フェノキシ基、ナフトキシ基など）である。
【０２８９】
Ｒ_３は好ましくは水素原子、ハロゲン原子、炭素数１〜２０のアルキル基であり、ハロゲン原子がもっとも好ましい。Ｒ_４は水素原子、アルキル基、アシルアミノ基が好ましく、アルキル基またはアシルアミノ基がより好ましい。これらの好ましい置換基の例はＲ_１と同様である。Ｒ_４がアシルアミノ基である場合Ｒ_４はＲ_３と連結してカルボスチリル環を形成することも好ましい。
【０２９０】
一般式（Ａ−２）においてＲ_３とＲ_４が互いに連結して縮合環を形成する場合、縮合環としてはナフタレン環が特に好ましい。ナフタレン環には一般式（Ａ−１）で挙げた置換基例と同じ置換基が結合していてもよい。一般式（Ａ−２）がナフトール系の化合物であるとき、Ｒ_１はカルバモイル基であることが好ましい。その中でもベンゾイル基であることが特に好ましい。Ｒ_２はアルコキシ基、アリールオキシ基であることが好ましく、アルコキシ基であることが特に好ましい。
【０２９１】
以下、本発明の現像促進剤の好ましい具体例を挙げる。本発明はこれらに限定されるものではない。
【０２９２】
【化４０】

【０２９３】
（水素結合性化合物の説明）
本発明における還元剤が芳香族性の水酸基（−ＯＨ）またはアミノ基（−ＮＨＲ、Ｒは水素原子またはアルキル基）を有する場合、特に前述のビスフェノール類の場合には、これらの基と水素結合を形成することが可能な基を有する非還元性の化合物を併用することが好ましい。
水酸基またはアミノ基と水素結合を形成する基としては、ホスホリル基、スルホキシド基、スルホニル基、カルボニル基、アミド基、エステル基、ウレタン基、ウレイド基、３級アミノ基、含窒素芳香族基などが挙げられる。その中でも好ましいのはホスホリル基、スルホキシド基、アミド基（但し、＞Ｎ−Ｈ基を持たず、＞Ｎ−Ｒａ（ＲａはＨ以外の置換基）のようにブロックされている。）、ウレタン基（但し、＞Ｎ−Ｈ基を持たず、＞Ｎ−Ｒａ（ＲａはＨ以外の置換基）のようにブロックされている。）、ウレイド基（但し、＞Ｎ−Ｈ基を持たず、＞Ｎ−Ｒａ（ＲａはＨ以外の置換基）のようにブロックされている。）を有する化合物である。
本発明で、特に好ましい水素結合性の化合物は下記一般式（Ｄ）で表される化合物である。
【０２９４】
一般式（Ｄ）
【化４１】

【０２９５】
一般式（Ｄ）においてＲ^２１ないしＲ^２３は各々独立にアルキル基、アリール基、アルコキシ基、アリールオキシ基、アミノ基またはヘテロ環基を表し、これらの基は無置換であっても置換基を有していてもよい。
Ｒ^２１ないしＲ^２３が置換基を有する場合の置換基としてはハロゲン原子、アルキル基、アリール基、アルコキシ基、アミノ基、アシル基、アシルアミノ基、アルキルチオ基、アリールチオ基、スルホンアミド基、アシルオキシ基、オキシカルボニル基、カルバモイル基、スルファモイル基、スルホニル基、ホスホリル基などがあげられ、置換基として好ましいのはアルキル基またはアリール基でたとえばメチル基、エチル基、イソプロピル基、ｔ−ブチル基、ｔ−オクチル基、フェニル基、４−アルコキシフェニル基、４−アシルオキシフェニル基などがあげられる。
【０２９６】
Ｒ^２１ないしＲ^２３のアルキル基としては具体的にはメチル基、エチル基、ブチル基、オクチル基、ドデシル基、イソプロピル基、ｔ−ブチル基、ｔ−アミル基、ｔ−オクチル基、シクロヘキシル基、１−メチルシクロヘキシル基、ベンジル基、フェネチル基、２−フェノキシプロピル基などがあげられる。
アリール基としてはフェニル基、クレジル基、キシリル基、ナフチル基、４−ｔ−ブチルフェニル基、４−ｔ−オクチルフェニル基、４−アニシジル基、３，５−ジクロロフェニル基などが挙げられる。
【０２９７】
アルコキシ基としてはメトキシ基、エトキシ基、ブトキシ基、オクチルオキシ基、２−エチルヘキシルオキシ基、３，５，５−トリメチルヘキシルオキシ基、ドデシルオキシ基、シクロヘキシルオキシ基、４−メチルシクロヘキシルオキシ基、ベンジルオキシ基等が挙げられる。
アリールオキシ基としてはフェノキシ基、クレジルオキシ基、イソプロピルフェノキシ基、４−ｔ−ブチルフェノキシ基、ナフトキシ基、ビフェニルオキシ基等が挙げられる。
アミノ基としてはジメチルアミノ基、ジエチルアミノ基、ジブチルアミノ基、ジオクチルアミノ基、Ｎ−メチル−Ｎ−ヘキシルアミノ基、ジシクロヘキシルアミノ基、ジフェニルアミノ基、Ｎ−メチル−Ｎ−フェニルアミノ基等が挙げられる。
【０２９８】
Ｒ^２１ないしＲ^２３としてはアルキル基、アリール基、アルコキシ基、アリールオキシ基が好ましい。本発明の効果の点ではＲ^２１ないしＲ^２３のうち少なくとも一つ以上がアルキル基またはアリール基であることが好ましく、二つ以上がアルキル基またはアリール基であることがより好ましい。また、安価に入手する事ができるという点ではＲ^２１ないしＲ^２３が同一の基である場合が好ましい。
【０２９９】
以下に本発明における一般式（Ｄ）の化合物をはじめとする水素結合性化合物の具体例を示すが、本発明はこれらに限定されるものではない。
【０３００】
【化４２】

【０３０１】
水素結合性化合物の具体例は上述の他に欧州特許１０９６３１０号明細書、特開２００２−１５６７２７号、特願２００１−１２４７９６号に記載のものがあげられる。
本発明の一般式（Ｄ）の化合物は、還元剤と同様に溶液形態、乳化分散形態、固体分散微粒子分散物形態で塗布液に含有せしめ、感光材料中で使用することができるが、固体分散物として使用することが好ましい。本発明の化合物は、溶液状態でフェノール性水酸基、アミノ基を有する化合物と水素結合性の錯体を形成しており、還元剤と本発明の一般式（Ｄ）の化合物との組み合わせによっては錯体として結晶状態で単離することができる。
【０３０２】
このようにして単離した結晶粉体を固体分散微粒子分散物として使用することは安定した性能を得る上で特に好ましい。また、還元剤と本発明の一般式（Ｄ）の化合物を粉体で混合し、適当な分散剤を使って、サンドグラインダーミル等で分散時に錯形成させる方法も好ましく用いることができる。
本発明の一般式（Ｄ）の化合物は還元剤に対して、１モル％〜２００モル％の範囲で使用することが好ましく、より好ましくは１０モル％〜１５０モル％の範囲で、さらに好ましくは２０モル％〜１００モル％の範囲である。
【０３０３】
（バインダーの説明）
本発明の有機銀塩含有層のバインダーはいかなるポリマーを使用してもよく、好適なバインダーは透明又は半透明で、一般に無色であり、天然樹脂やポリマー及びコポリマー、合成樹脂やポリマー及びコポリマー、その他フィルムを形成する媒体、例えば、ゼラチン類、ゴム類、ポリ（ビニルアルコール）類、ヒドロキシエチルセルロース類、セルロースアセテート類、セルロースアセテートブチレート類、ポリ（ビニルピロリドン）類、カゼイン、デンプン、ポリ（アクリル酸）類、ポリ（メチルメタクリル酸）類、ポリ（塩化ビニル）類、ポリ（メタクリル酸）類、スチレン−無水マレイン酸共重合体類、スチレン−アクリロニトリル共重合体類、スチレン−ブタジエン共重合体類、ポリ（ビニルアセタール）類（例えば、ポリ（ビニルホルマール）及びポリ（ビニルブチラール））、ポリ（エステル）類、ポリ（ウレタン）類、フェノキシ樹脂、ポリ（塩化ビニリデン）類、ポリ（エポキシド）類、ポリ（カーボネート）類、ポリ（酢酸ビニル）類、ポリ（オレフィン）類、セルロースエステル類、ポリ（アミド）類がある。バインダーは水又は有機溶媒またはエマルションから被覆形成してもよい。
【０３０４】
本発明では、有機銀塩を含有する層に併用できるバインダーのガラス転移温度は０℃以上８０℃以下である（以下、高Ｔｇバインダーということあり）ことが好ましく、１０℃〜７０℃であることがより好ましく、１５℃以上６０℃以下であることが更に好ましい。
【０３０５】
なお、本明細書においてＴｇは下記の式で計算した。
１／Ｔｇ＝Σ（Ｘｉ／Ｔｇｉ）
ここでは、ポリマーはｉ＝１からｎまでのｎ個のモノマー成分が共重合しているとする。Ｘｉはｉ番目のモノマーの重量分率（ΣＸｉ＝１）、 Ｔｇｉはｉ番目のモノマーの単独重合体のガラス転移温度（絶対温度）である。ただしΣはｉ＝１からｎまでの和をとる。尚、各モノマーの単独重合体ガラス転移温度の値（Ｔｇｉ）はＰｏｌｙｍｅｒ Ｈａｎｄｂｏｏｋ（３ｒｄ Ｅｄｉｔｉｏｎ）（Ｊ．Ｂｒａｎｄｒｕｐ， Ｅ．Ｈ．Ｉｍｍｅｒｇｕｔ著（Ｗｉｌｅｙ−Ｉｎｔｅｒｓｃｉｅｎｃｅ、１９８９））の値を採用した。
【０３０６】
バインダーは必要に応じて２種以上を併用しても良い。また、ガラス転移温度が２０℃以上のものとガラス転移温度が２０℃未満のものを組み合わせて用いてもよい。Ｔｇの異なるポリマーを２種以上ブレンドして使用する場合には、その重量平均Ｔｇが上記の範囲にはいることが好ましい。
【０３０７】
本発明においては、有機銀塩含有層が溶媒の３０質量％以上が水である塗布液を用いて塗布、乾燥して被膜を形成させることが好ましい。
本発明においては、有機銀塩含有層が溶媒の３０質量％以上が水である塗布液を用いて塗布し、乾燥して形成される場合に、さらに有機銀塩含有層のバインダーが水系溶媒（水溶媒）に可溶または分散可能である場合に、特に２５℃６０％ＲＨでの平衡含水率が２質量％以下のポリマーのラテックスからなる場合に性能が向上する。最も好ましい形態は、イオン伝導度が２．５ｍＳ／ｃｍ以下になるように調製されたものであり、このような調製法としてポリマー合成後分離機能膜を用いて精製処理する方法が挙げられる。
【０３０８】
ここでいう前記ポリマーが可溶または分散可能である水系溶媒とは、水または水に７０質量％以下の水混和性の有機溶媒を混合したものである。水混和性の有機溶媒としては、例えば、メチルアルコール、エチルアルコール、プロピルアルコール等のアルコール系、メチルセロソルブ、エチルセロソルブ、ブチルセロソルブ等のセロソルブ系、酢酸エチル、ジメチルホルムアミドなどを挙げることができる。
【０３０９】
なお、ポリマーが熱力学的に溶解しておらず、いわゆる分散状態で存在している系の場合にも、ここでは水系溶媒という言葉を使用する。
【０３１０】
また「２５℃６０％ＲＨにおける平衡含水率」とは、２５℃６０％ＲＨの雰囲気下で調湿平衡にあるポリマーの重量Ｗ１と２５℃で絶乾状態にあるポリマーの重量Ｗ０を用いて以下のように表すことができる。
２５℃６０％ＲＨにおける平衡含水率＝［（Ｗ１−Ｗ０）／Ｗ０］×１００（質量％）
【０３１１】
含水率の定義と測定法については、例えば高分子工学講座１４、高分子材料試験法（高分子学会編、地人書館）を参考にすることができる。
【０３１２】
本発明のバインダーポリマーの２５℃６０％ＲＨにおける平衡含水率は２質量％以下であることが好ましいが、より好ましくは０．０１質量％以上１．５質量％以下、さらに好ましくは０．０２質量％以上１質量％以下が望ましい。
【０３１３】
本発明においては水系溶媒に分散可能なポリマーが特に好ましい。分散状態の例としては、水不溶な疎水性ポリマーの微粒子が分散しているラテックスやポリマー分子が分子状態またはミセルを形成して分散しているものなどいずれでもよいが、ラテックス分散した粒子がより好ましい。分散粒子の平均粒径は１〜５００００ｎｍ、好ましくは５〜１０００ｎｍの範囲で、より好ましくは１０〜５００ｎｍの範囲、さらに好ましくは５０〜２００ｎｍの範囲である。分散粒子の粒径分布に関しては特に制限は無く、広い粒径分布を持つものでも単分散の粒径分布を持つものでもよい。単分散の粒径分布を持つものを２種以上混合して使用することも塗布液の物性を制御する上で好ましい使用法である。
【０３１４】
本発明において水系溶媒に分散可能なポリマーの好ましい態様としては、アクリル系ポリマー、ポリ（エステル）類、ゴム類（例えばＳＢＲ樹脂）、ポリ（ウレタン）類、ポリ（塩化ビニル）類、ポリ（酢酸ビニル）類、ポリ（塩化ビニリデン）類、ポリ（オレフィン）類等の疎水性ポリマーを好ましく用いることができる。これらポリマーとしては直鎖のポリマーでも枝分かれしたポリマーでもまた架橋されたポリマーでもよいし、単一のモノマーが重合したいわゆるホモポリマーでもよいし、２種類以上のモノマーが重合したコポリマーでもよい。コポリマーの場合はランダムコポリマーでも、ブロックコポリマーでもよい。これらポリマーの分子量は数平均分子量で５０００〜１００００００、好ましくは１００００〜２０００００がよい。分子量が小さすぎるものはＩ画像形成層の力学強度が不十分であり、大きすぎるものは成膜性が悪く好ましくない。また、架橋性のポリマーラッテクスは特に好ましく使用される。
【０３１５】
―ラテックスの具体例―
好ましいポリマーラテックスの具体例としては以下のものを挙げることができる。以下では原料モノマーを用いて表し、括弧内の数値は質量％、分子量は数平均分子量である。多官能モノマーを使用した場合は架橋構造を作るため分子量の概念が適用できないので架橋性と記載し、分子量の記載を省略した。Ｔｇはガラス転移温度を表す。
【０３１６】
Ｐ−１；−ＭＭＡ（７０）−ＥＡ（２７）−ＭＡＡ（３）−のラテックス（分子量３７０００、Ｔｇ６１℃）
Ｐ−２；−ＭＭＡ（７０）−２ＥＨＡ（２０）−Ｓｔ（５）−ＡＡ（５）−のラテックス（分子量４００００、Ｔｇ５９℃）
Ｐ−３；−Ｓｔ（５０）−Ｂｕ（４７）−ＭＡＡ（３）−のラテックス（架橋性、Ｔｇ−１７℃） Ｐ−４；−Ｓｔ（６８）−Ｂｕ（２９）−ＡＡ（３）−のラテックス（架橋性、Ｔｇ１７℃）Ｐ−５；−Ｓｔ（７１）−Ｂｕ（２６）−ＡＡ（３）−のラテックス（架橋性，Ｔｇ２４℃）Ｐ−６；−Ｓｔ（７０）−Ｂｕ（２７）−ＩＡ（３）−のラテックス（架橋性）
Ｐ−７；−Ｓｔ（７５）−Ｂｕ（２４）−ＡＡ（１）−のラテックス（架橋性、Ｔｇ２９℃）Ｐ−８；−Ｓｔ（６０）−Ｂｕ（３５）−ＤＶＢ（３）−ＭＡＡ（２）−のラテックス（架橋性） Ｐ−９；−Ｓｔ（７０）−Ｂｕ（２５）−ＤＶＢ（２）−ＡＡ（３）−のラテックス（架橋性）Ｐ−１０；−ＶＣ（５０）−ＭＭＡ（２０）−ＥＡ（２０）−ＡＮ（５）−ＡＡ（５）−のラテックス（分子量８００００）Ｐ−１１；−ＶＤＣ（８５）−ＭＭＡ（５）−ＥＡ（５）−ＭＡＡ（５）−のラテックス（分子量６７０００）Ｐ−１２；−Ｅｔ（９０）−ＭＡＡ（１０）−のラテックス（分子量１２０００）
Ｐ−１３；−Ｓｔ（７０）−２ＥＨＡ（２７）−ＡＡ（３）のラテックス（分子量１３００００、Ｔｇ４３℃）Ｐ−１４；−ＭＭＡ（６３）−ＥＡ（３５）− ＡＡ（２）のラテックス（分子量３３０００、Ｔｇ４７℃）
Ｐ−１５；−Ｓｔ（７０．５）−Ｂｕ（２６．５）−ＡＡ（３）−のラテックス（架橋性，Ｔｇ２３℃）
Ｐ−１６；−Ｓｔ（６９．５）−Ｂｕ（２７．５）−ＡＡ（３）−のラテックス（架橋性，Ｔｇ２０．５℃）
【０３１７】
上記構造の略号は以下のモノマーを表す。ＭＭＡ；メチルメタクリレート，ＥＡ ；エチルアクリレート、ＭＡＡ；メタクリル酸，２ＥＨＡ；２−エチルヘキシルアクリレート，Ｓｔ；スチレン，Ｂｕ；ブタジエン，ＡＡ；アクリル酸，ＤＶＢ；ジビニルベンゼン，ＶＣ；塩化ビニル，ＡＮ；アクリロニトリル，ＶＤＣ；塩化ビニリデン，Ｅｔ；エチレン，ＩＡ；イタコン酸。
【０３１８】
以上に記載したポリマーラテックスは市販もされていて、以下のようなポリマーが利用できる。アクリル系ポリマーの例としては、セビアンＡ−４６３５，４７１８，４６０１（以上ダイセル化学工業（株）製）、Ｎｉｐｏｌ Ｌｘ８１１、８１４、８２１、８２０、８５７（以上日本ゼオン（株）製）など、ポリ（エステル）類の例としては、ＦＩＮＥＴＥＸ ＥＳ６５０、６１１、６７５、８５０（以上大日本インキ化学（株）製）、ＷＤ−ｓｉｚｅ、ＷＭＳ（以上イーストマンケミカル製）など、ポリ（ウレタン）類の例としては、ＨＹＤＲＡＮ ＡＰ１０、２０、３０、４０（以上大日本インキ化学（株）製）など、ゴム類の例としては、ＬＡＣＳＴＡＲ ７３１０Ｋ、３３０７Ｂ、４７００Ｈ、７１３２Ｃ（以 上大日本インキ化学（株）製）、Ｎｉｐｏｌ Ｌｘ４１６、４１０、４３８Ｃ、２５０７（以上日本ゼオン（株）製）など、ポリ（塩化ビニル）類の例としては、Ｇ３５１、Ｇ５７６（以上日本ゼオン（株）製）など、ポリ（塩化ビニリデン）類の例としては、Ｌ５０２、Ｌ５１３（以上旭化成工業（株）製）など、ポリ（オレフィン）類の例としては、ケミパールＳ１２０、ＳＡ１００（以上三井石油化学（株）製）などを挙げることができる。
【０３１９】
これらのポリマーラテックスは単独で用いてもよいし、必要に応じて２種以上ブレンドしてもよい。
【０３２０】
―好ましいラテックス−
本発明に用いられるポリマーラテックスとしては、特に、スチレン−ブタジエン共重合体のラテックスが好ましい。スチレン−ブタジエン共重合体におけるスチレンのモノマー単位とブタジエンのモノマー単位との重量比は４０：６０〜９５：５であることが好ましい。また、スチレンのモノマー単位とブタジエンのモノマー単位との共重合体に占める割合は６０質量％〜９９質量％であることが好ましい。また、本発明のポリマーラッテクスはアクリル酸またはメタクリル酸をスチレンとブタジエンの和に対して１質量％〜６質量％含有することが好ましく、より好ましくは２質量％〜５質量％含有する。本発明のポリマーラテックスはアクリル酸を含有することが好ましい。好ましい分子量の範囲は前記と同様である。
【０３２１】
本発明に用いることが好ましいスチレン−ブタジエン酸共重合体のラテックスとしては、前記のＰ−３〜Ｐ−８，１５、市販品であるＬＡＣＳＴＡＲ−３３０７Ｂ、７１３２Ｃ、Ｎｉｐｏｌ Ｌｘ４１６等が挙げられる。
【０３２２】
本発明の感光材料の有機銀塩含有層には必要に応じてゼラチン、ポリビニルアルコール、メチルセルロース、ヒドロキシプロピルセルロース、カルボキシメチルセルロースなどの親水性ポリマーを添加してもよい。これらの親水性ポリマーの添加量は有機銀塩含有層の全バインダーの３０質量％以下、より好ましくは２０質量％以下が好ましい。
【０３２３】
本発明の有機銀塩含有層（即ち、画像形成層）は、ポリマーラテックスを用いて形成されたものが好ましい。有機銀塩含有層のバインダーの量は、全バインダー／有機銀塩の重量比が１／１０〜１０／１、より好ましくは１／３〜５／１の範囲、さらに好ましくは１／１〜３／１の範囲である。
【０３２４】
また、このような有機銀塩含有層は、通常、感光性銀塩である感光性ハロゲン化銀が含有された感光性層（Ｉ画像形成層）でもあり、このような場合の、全バインダー／ハロゲン化銀の重量比は４００〜５、より好ましくは２００〜１０の範囲である。
【０３２５】
本発明の画像形成層の全バインダー量は好ましくは０．２ ｇ／ｍ^２〜３０ｇ／ｍ^２、より好ましくは１ ｇ／ｍ^２〜１５ｇ／ｍ^２、さらに好ましくは２ ｇ／ｍ^２〜１０ｇ／ｍ^２の範囲である。本発明の画像形成層には架橋のための架橋剤、塗布性改良のための界面活性剤などを添加してもよい。
【０３２６】
（好ましい塗布液の溶媒）
本発明において感光材料の有機銀塩含有層塗布液の溶媒（ここでは簡単のため、溶媒と分散媒をあわせて溶媒と表す。）は、水を３０質量％以上含む水系溶媒が好ましい。水以外の成分としてはメチルアルコール、エチルアルコール、イソプロピルアルコール、メチルセロソルブ、エチルセロソルブ、ジメチルホルムアミド、酢酸エチルなど任意の水混和性有機溶媒を用いてよい。塗布液の溶媒の水含有率は５０質量％以上、より好ましくは７０質量％以上が好ましい。好ましい溶媒組成の例を挙げると、水の他、水／メチルアルコール＝９０／１０、水／メチルアルコール＝７０／３０、水／メチルアルコール／ジメチルホルムアミド＝８０／１５／５、水／メチルアルコール／エチルセロソルブ＝８５／１０／５、水／メチルアルコール／イソプロピルアルコール＝８５／１０／５などがある（数値は質量％）。
【０３２７】
（かぶり防止剤）
１）有機ポリハロゲン化合物
以下、本発明で用いることができる好ましい有機ポリハロゲン化合物について具体的に説明する。本発明の好ましいポリハロゲン化合物は下記一般式（Ｈ）で表される化合物である。
【０３２８】
一般式（Ｈ）
Ｑ−（Ｙ）ｎ−Ｃ（Ｚ_１）（Ｚ_２）Ｘ
【０３２９】
一般式（Ｈ）において、Ｑはアルキル基、アリール基またはヘテロ環基を表し、Ｙは２価の連結基を表し、ｎは０〜１を表し、Ｚ_１およびＺ_２はハロゲン原子を表し、Ｘは水素原子または電子求引性基を表す。
一般式（Ｈ）においてＱは好ましくは炭素数１〜６のアルキル基、炭素数６〜１２のアリール基または窒素原子を少なくとも一つ含むヘテロ環基（ピリジン、キノリン基等）である。
【０３３０】
一般式（Ｈ）において、Ｑがアリール基である場合、Ｑは好ましくはハメットの置換基定数σｐが正の値をとる電子求引性基で置換されたフェニル基を表す。ハメットの置換基定数に関しては、Ｊｏｕｒｎａｌ ｏｆ Ｍｅｄｉｃｉｎａｌ Ｃｈｅｍｉｓｔｒｙ，１９７３，Ｖｏｌ．１６，Ｎｏ．１１，１２０７−１２１６ 等を参考にすることができる。このような電子求引性基としては、例えばハロゲン原子、電子求引性基で置換されたアルキル基、電子求引性基で置換されたアリール基、ヘテロ環基、アルキルまたはアリールスルホニル基、アシル基、アルコキシカルボニル基、カルバモイル基、スルファモイル基等があげられる。電子求引性基として特に好ましいのは、ハロゲン原子、カルバモイル基、アリールスルホニル基であり、特にカルバモイル基が好ましい。
【０３３１】
Ｘは好ましくは電子求引性基である。好ましい電子求引性基は、ハロゲン原子、脂肪族・アリールもしくは複素環スルホニル基、脂肪族・アリールもしくは複素環アシル基、脂肪族・アリールもしくは複素環オキシカルボニル基、カルバモイル基、スルファモイル基であり、さらに好ましくはハロゲン原子、カルバモイル基であり、特に好ましくは臭素原子である。
Ｚ_１およびＺ_２は好ましくは臭素原子、ヨウ素原子であり、更に好ましくは臭素原子である。
【０３３２】
Ｙは好ましくは−Ｃ（＝Ｏ）−、−ＳＯ −、−ＳＯ_２−、−Ｃ（＝Ｏ）Ｎ（Ｒ）−、−ＳＯ_２Ｎ（Ｒ）−を表し、より好ましくは−Ｃ（＝Ｏ）−、−ＳＯ_２−、−Ｃ（＝Ｏ）Ｎ（Ｒ）−であり、特に好ましくは−ＳＯ_２−、−Ｃ（＝Ｏ）Ｎ（Ｒ）−である。ここでいうＲとは水素原子、アリール基またはアルキル基を表し、より好ましくは水素原子またはアルキル基であり、特に好ましくは水素原子である。
ｎは、０または１を表し、好ましくは１である。
【０３３３】
一般式（Ｈ）において、Ｑがアルキル基の場合、好ましいＹは−Ｃ（＝Ｏ）Ｎ（Ｒ）−であり、Ｑがアリール基またはヘテロ環基の場合、好ましいＹは−ＳＯ_２−である。
一般式（Ｈ）において、該化合物から水素原子を取り去った残基が互いに結合した形態（一般にビス型、トリス型、テトラキス型と呼ぶ）も好ましく用いることが出来る。
一般式（Ｈ）において、解離性基（例えばＣＯＯＨ基またはその塩、ＳＯ_３Ｈ基またはその塩、ＰＯ_３Ｈ基またはその塩等）、４級窒素カチオンを含む基（例えばアンモニウム基、ピリジニウム基等）、ポリエチレンオキシ基、水酸基等を置換基に有するものも好ましい形態である。
【０３３４】
以下に本発明の一般式（Ｈ）の化合物の具体例を示す。
【０３３５】
【化４３】

【０３３６】
【化４４】

【０３３７】
上記以外の本発明に用いることが出来るポリハロゲン化合物としては、ＵＳ３８７４９４６号、ＵＳ４７５６９９９号、ＵＳ５３４０７１２号、ＵＳ５３６９０００号、ＵＳ５４６４７３７号、ＵＳ６５０６５４８号、特開昭５０−１３７１２６号、同５０−８９０２０号、同５０−１１９６２４号、同５９−５７２３４号、特開平７−２７８１号、同７−５６２１号、同９−１６０１６４号、同９−２４４１７７号、同９−２４４１７８号、同９−１６０１６７号、同９−３１９０２２号、同９−２５８３６７号、同９−２６５１５０号、同９−３１９０２２号、同１０−１９７９８８号、同１０−１９７９８９号、同１１−２４２３０４号、特開２０００−２９６３、特開２０００−１１２０７０、特開２０００−２８４４１０、特開２０００−２８４４１２、特開２００１−３３９１１、特開２００１−３１６４４、特開２００１−３１２０２７号、特開２００３−５０４４１号明細書の中で当該発明の例示化合物として挙げられている化合物が好ましく用いられるが、特に特開平７−２７８１号、特開２００１−３３９１１、特開２００１−３１２０２７号に具体的に例示されている化合物が好ましい。
【０３３８】
本発明の一般式（Ｈ）で表される化合物は画像形成層の非感光性銀塩１モルあたり、１０^−４モル〜１モルの範囲で使用することが好ましく、より好ましくは１０^−３モル〜０．５モルの範囲で、さらに好ましくは１×１０^−２モル〜０．２モルの範囲で使用することが好ましい。
本発明において、カブリ防止剤を感光材料に含有せしめる方法としては、前記還元剤の含有方法に記載の方法が挙げられ、有機ポリハロゲン化合物についても固体微粒子分散物で添加することが好ましい。
【０３３９】
２）その他のかぶり防止剤
その他のカブリ防止剤としては特開平１１−６５０２１号段落番号０１１３の水銀（ＩＩ）塩、同号段落番号０１１４の安息香酸類、特開２０００−２０６６４２号のサリチル酸誘導体、特開２０００−２２１６３４号の式（Ｓ）で表されるホルマリンスカベンジャー化合物、特開平１１−３５２６２４号の請求項９に係るトリアジン化合物、特開平６−１１７９１号の一般式（ＩＩＩ）で表される化合物、４−ヒドロキシ−６−メチル−１，３，３ａ，７−テトラザインデン等が挙げられる。
【０３４０】
本発明における熱現像感光材料はカブリ防止を目的としてアゾリウム塩を含有しても良い。アゾリウム塩としては、特開昭５９−１９３４４７号記載の一般式（ＸＩ）で表される化合物、特公昭５５−１２５８１号記載の化合物、特開昭６０−１５３０３９号記載の一般式（ＩＩ）で表される化合物が挙げられる。アゾリウム塩は感光材料のいかなる部位に添加しても良いが、添加層としては感光性層を有する面の層に添加することが好ましく、有機銀塩含有層に添加することがさらに好ましい。アゾリウム塩の添加時期としては塗布液調製のいかなる工程で行っても良く、有機銀塩含有層に加する場合は有機銀塩調製時から塗布液調製時のいかなる工程でも良いが有機銀塩調製後から塗布直前が好ましい。アゾリウム塩の添加法としては粉末、溶液、微粒子分散物などいかなる方法で行っても良い。また、増感色素、還元剤、色調剤など他の添加物と混合した溶液として添加しても良い。本発明においてアゾリウム塩の添加量としてはいかなる量でも良いが、銀１モル当たり１×１０^−６モル以上２モル以下が好ましく、１×１０^−３モル以上０．５モル以下がさらに好ましい。
【０３４１】
（その他の添加剤）
１）メルカプト、ジスルフィド、およびチオン類
本発明には現像を抑制あるいは促進させ現像を制御するため、分光増感効率を向上させるため、現像前後の保存性を向上させるためなどにメルカプト化合物、ジスルフィド化合物、チオン化合物を含有させることができ、特開平１０−６２８９９号の段落番号００６７〜００６９、特開平１０−１８６５７２号の一般式（Ｉ）で表される化合物及びその具体例として段落番号００３３〜００５２、欧州特許公開第０８０３７６４Ａ１号の第２０ページ第３６〜５６行に記載されている。その中でも特開平９−２９７３６７号、特開平９−３０４８７５号、特開２００１−１００３５８号、特願２００１−１０４２１３号、特願２００１−１０４２１４等に記載されているメルカプト置換複素芳香族化合物が好ましい。
【０３４２】
２）色調剤
本発明の熱現像感光材料では色調剤の添加が好ましく、色調剤については、特開平１０−６２８９９号の段落番号００５４〜００５５、欧州特許公開第０８０３７６４Ａ１号の第２１ページ第２３〜４８行、特開２０００−３５６３１７号や特開２０００−１８７２９８号に記載されており、特に、フタラジノン類（フタラジノン、フタラジノン誘導体もしくは金属塩；例えば４−（１−ナフチル）フタラジノン、６−クロロフタラジノン、５，７−ジメトキシフタラジノンおよび２，３−ジヒドロ−１，４−フタラジンジオン）；フタラジノン類とフタル酸類（例えば、フタル酸、４−メチルフタル酸、４−ニトロフタル酸、フタル酸二アンモニウム、フタル酸ナトリウム、フタル酸カリウムおよびテトラクロロ無水フタル酸）との組合せ；フタラジン類（フタラジン、フタラジン誘導体もしくは金属塩；例えば４−（１−ナフチル）フタラジン、６−イソプロピルフタラジン、６−ｔ−ブチルフラタジン、６−クロロフタラジン、５，７−ジメトキシフタラジンおよび２，３−ジヒドロフタラジン）；フタラジン類とフタル酸類との組合せが好ましく、特にフタラジン類とフタル酸類の組合せが好ましい。そのなかでも特に好ましい組み合わせは６−イソプロピルフタラジンとフタル酸または４メチルフタル酸との組み合わせである。
【０３４３】
３）可塑剤、潤滑剤
本発明の感光性層に用いることのできる可塑剤および潤滑剤については特開平１１−６５０２１号段落番号０１１７に記載されている。滑り剤については特開平１１−８４５７３号段落番号００６１〜００６４や特願平１１−１０６８８１号段落番号００４９〜００６２記載されている。
【０３４４】
４）染料、顔料
本発明の感光性層には色調改良、レーザー露光時の干渉縞発生防止、イラジエーション防止の観点から各種染料や顔料（例えばＣ．Ｉ．Ｐｉｇｍｅｎｔ Ｂｌｕｅ ６０、Ｃ．Ｉ．Ｐｉｇｍｅｎｔ Ｂｌｕｅ ６４、Ｃ．Ｉ．Ｐｉｇｍｅｎｔ Ｂｌｕｅ １５：６）を用いることができる。これらについてはＷＯ９８／３６３２２号、特開平１０−２６８４６５号、同１１−３３８０９８号等に詳細に記載されている。
【０３４５】
５）超硬調化剤
印刷製版用途に適した超硬調画像形成のためには、画像形成層に超硬調化剤を添加することが好ましい。超硬調化剤やその添加方法及び添加量については、特開平１１−６５０２１号号公報段落番号０１１８、特開平１１−２２３８９８号公報段落番号０１３６〜０１９３、特願平１１−８７２９７号明細書の式（Ｈ）、式（１）〜（３）、式（Ａ）、（Ｂ）の化合物、特願平１１−９１６５２号明細書記載の一般式（ＩＩＩ）〜（Ｖ）の化合物（具体的化合物：化２１〜化２４）、硬調化促進剤については特開平１１−６５０２１号公報段落番号０１０２、特開平１１−２２３８９８号公報段落番号０１９４〜０１９５に記載されている。
【０３４６】
蟻酸や蟻酸塩を強いかぶらせ物質として用いるには、感光性ハロゲン化銀を含有する画像形成層を有する側に銀１モル当たり５ミリモル以下、さらには１ミリモル以下で含有させることが好ましい。
本発明の熱現像感光材料で超硬調化剤を用いる場合には五酸化二リンが水和してできる酸またはその塩を併用して用いることが好ましい。五酸化二リンが水和してできる酸またはその塩としては、メタリン酸（塩）、ピロリン酸（塩）、オルトリン酸（塩）、三リン酸（塩）、四リン酸（塩）、ヘキサメタリン酸（塩）などを挙げることができる。特に好ましく用いられる五酸化二リンが水和してできる酸またはその塩としては、オルトリン酸（塩）、ヘキサメタリン酸（塩）を挙げることができる。具体的な塩としてはオルトリン酸ナトリウム、オルトリン酸二水素ナトリウム、ヘキサメタリン酸ナトリウム、ヘキサメタリン酸アンモニウムなどが挙げられる。
五酸化二リンが水和してできる酸またはその塩の使用量（感光材料１ｍ^２あたりの塗布量）は感度やカブリなどの性能に合わせて所望の量でよいが、０．１ｍｇ／ｍ^２〜５００ｍｇ／ｍ^２が好ましく、０．５ｍｇ／ｍ^２〜１００ｍｇ／ｍ^２がより好ましい。
【０３４７】
（塗布液の調製および塗布）
本発明の画像形成層塗布液の調製温度は３０℃以上６５℃以下がよく、さらに好ましい温度は３５℃以上６０℃未満、より好ましい温度は３５℃以上５５℃以下である。また、ポリマーラテックス添加直後の画像形成層塗布液の温度が３０℃以上６５℃以下で維持されることが好ましい。
【０３４８】
（層構成および構成成分）
本発明の画像形成層は、支持体上に一またはそれ以上の層で構成される。一層で構成する場合は有機銀塩、感光性ハロゲン化銀、還元剤およびバインダーよりなり、必要により色調剤、被覆助剤および他の補助剤などの所望による追加の材料を含む。二層以上で構成する場合は、第１画像形成層（通常は支持体に隣接した層）中に有機銀塩および感光性ハロゲン化銀を含み、第２画像形成層または両層中にいくつかの他の成分を含まなければならない。多色感光性熱現像写真材料の構成は、各色についてこれらの二層の組合せを含んでよく、また、米国特許第４，７０８，９２８号に記載されているように単一層内に全ての成分を含んでいてもよい。多染料多色感光性熱現像写真材料の場合、各Ｉ画像形成層は、一般に、米国特許第４，４６０，６８１号に記載されているように、各感光性層の間に官能性もしくは非官能性のバリアー層を使用することにより、互いに区別されて保持される。
【０３４９】
本発明の熱現像感光材料は、画像形成層に加えて非感光性層を有することができる。非感光性層は、その配置から（ａ）画像形成層の上（支持体よりも遠い側）に設けられる表面保護層、（ｂ）複数の画像形成層の間や画像形成層と保護層の間に設けられる中間層、（ｃ）画像形成層と支持体との間に設けられる下塗り層、（ｄ）画像形成層の反対側に設けられるバック層に分類できる。
【０３５０】
また、光学フィルターとして作用する層を設けることができるが、（ａ）または（ｂ）の層として設けられる。アンチハレーション層は、（ｃ）または（ｄ）の層として感光材料に設けられる。
【０３５１】
１）表面保護層
本発明における熱現像感光材料は画像形成層の付着防止などの目的で表面保護層を設けることができる。表面保護層は単層でもよいし、複数層であってもよい。
表面保護層については、特開平１１−６５０２１号段落番号０１１９〜０１２０、特開２０００−１７１９３６号に記載されている。
本発明の表面保護層のバインダーとしてはゼラチンが好ましいがポリビニルアルコール（ＰＶＡ）を用いる若しくは併用することも好ましい。ゼラチンとしてはイナートゼラチン（例えば新田ゼラチン７５０）、フタル化ゼラチン（例えば新田ゼラチン８０１）など使用することができる。ＰＶＡとしては、特開２０００−１７１９３６号の段落番号０００９〜００２０に記載のものがあげられ、完全けん化物のＰＶＡ−１０５、部分けん化物のＰＶＡ−２０５，ＰＶＡ−３３５、変性ポリビニルアルコールのＭＰ−２０３（以上、クラレ（株）製の商品名）などが好ましく挙げられる。保護層（１層当たり）のポリビニルアルコール塗布量（支持体１ｍ^２当たり）としては０．３ ｇ／ｍ^２〜４．０ｇ／ｍ^２が好ましく、０．３ ｇ／ｍ^２〜２．０ｇ／ｍ^２がより好ましい。
【０３５２】
表面保護層（１層当たり）の全バインダー（水溶性ポリマー及びラテックスポリマーを含む）塗布量（支持体１ｍ^２当たり）としては０．３ ｇ／ｍ^２〜５．０ｇ／ｍ^２が好ましく、０．３ ｇ／ｍ^２〜２．０ｇ／ｍ^２がより好ましい。
【０３５３】
２）アンチハレーション層
本発明の熱現像感光材料においては、アンチハレーション層を感光性層に対して光源から遠い側に設けることができる。
【０３５４】
アンチハレーション層については特開平１１−６５０２１号段落番号０１２３〜０１２４、特開平１１−２２３８９８号、同９−２３０５３１号、同１０−３６６９５号、同１０−１０４７７９号、同１１−２３１４５７号、同１１−３５２６２５号、同１１−３５２６２６号等に記載されている。
アンチハレーション層には、露光波長に吸収を有するアンチハレーション染料を含有する。露光波長が赤外域にある場合には赤外線吸収染料を用いればよく、その場合には可視域に吸収を有しない染料が好ましい。
可視域に吸収を有する染料を用いてハレーション防止を行う場合には、画像形成後には染料の色が実質的に残らないようにすることが好ましく、熱現像の熱により消色する手段を用いることが好ましく、特に非感光性層に熱消色染料と塩基プレカーサーとを添加してアンチハレーション層として機能させることが好ましい。これらの技術については特開平１１−２３１４５７号等に記載されている。
【０３５５】
消色染料の添加量は、染料の用途により決定する。一般には、目的とする波長で測定したときの光学濃度（吸光度）が０．１を越える量で使用する。光学濃度は、０．１５〜２であることが好ましく０．２〜１であることがより好ましい。このような光学濃度を得るための染料の使用量は、一般に０．００１ｇ／ｍ^２〜１ｇ／ｍ^２程度である。
【０３５６】
なお、このように染料を消色すると、熱現像後の光学濃度を０．１以下に低下させることができる。二種類以上の消色染料を、熱消色型記録材料や熱現像感光材料において併用してもよい。同様に、二種類以上の塩基プレカーサーを併用してもよい。
このような消色染料と塩基プレカーサーを用いる熱消色においては、特開平１１−３５２６２６号に記載のような塩基プレカーサーと混合すると融点を３℃（ｄｅｇ）以上降下させる物質（例えば、ジフェニルスルホン、４−クロロフェニル（フェニル）スルホン）、２−ナフチルベンゾエート等を併用することが熱消色性等の点で好ましい。
【０３５７】
３）バック層
本発明に適用することのできるバック層については特開平１１−６５０２１号段落番号０１２８〜０１３０に記載されている。
【０３５８】
本発明においては、銀色調、画像の経時変化を改良する目的で３００〜４５０ｎｍに吸収極大を有する着色剤を添加することができる。このような着色剤は、特開昭６２−２１０４５８号、同６３−１０４０４６号、同６３−１０３２３５号、同６３−２０８８４６号、同６３−３０６４３６号、同６３−３１４５３５号、特開平０１−６１７４５号、特開平２００１−１００３６３などに記載されている。このような着色剤は、通常、０．１ｍｇ／ｍ^２〜１ｇ／ｍ^２の範囲で添加され、添加する層としては感光性層の反対側に設けられるバック層が好ましい。
また、ベース色調を調整するために５８０〜６８０ｎｍに吸収ピークを有する染料を使用することが好ましい。この目的の染料としては短波長側の吸収強度が小さい特開平４−３５９９６７、同４−３５９９６８記載のアゾメチン系の油溶性染料、特願２００２−９６７９７号記載のフタロシアニン系の水溶性染料が好ましい。この目的の染料はいずれの層に添加してもよいが、乳剤面側の非感光層またはバック面側に添加することがより好ましい。
【０３５９】
本発明における熱現像感光材料は、支持体の一方の側に少なくとも１層のハロゲン化銀乳剤を含む感光性層を有し、他方の側にバック層を有する、いわゆる片面感光材料であることが好ましい。
【０３６０】
４）マット剤
本発明において、搬送性改良のためにマット剤を添加することが好ましく、マット剤については、特開平１１−６５０２１号段落番号０１２６〜０１２７に記載されている。マット剤は感光材料１ｍ^２当たりの塗布量で示した場合、好ましくは１ ｍｇ／ｍ^２〜４００ｍｇ／ｍ^２、より好ましくは５ ｍｇ／ｍ^２〜３００ｍｇ／ｍ^２である。
【０３６１】
本発明においてマット剤の形状は定型、不定形のいずれでもよいが好ましくは定型で、球形が好ましく用いられる。平均粒径は０．５μｍ〜１０μｍであることが好ましく、より好ましくは１．０μｍ〜８．０μｍ、さらに好ましくは２．０μｍ〜６．０μｍの範囲である。また、サイズ分布の変動係数としては５０％以下であることが好ましく、より好ましくは４０％以下、さらに好ましくは、３０％以下である。ここで変動係数とは（粒径の標準偏差）／（粒径の平均値）×１００で表される値である。また、変動係数が小さいマット剤で平均粒径の比が３より大きいものを２種併用することも好ましい。
【０３６２】
また、乳剤面のマット度は星屑故障が生じなければいかようでも良いが、ベック平滑度が３０秒以上２０００秒以下が好ましく、特に４０秒以上１５００秒以下が好ましい。ベック平滑度は、日本工業規格（ＪＩＳ）Ｐ８１１９「紙および板紙のベック試験器による平滑度試験方法」およびＴＡＰＰＩ標準法Ｔ４７９により容易に求めることができる。
【０３６３】
本発明においてバック層のマット度としてはベック平滑度が１２００秒以下１０秒以上が好ましく、８００秒以下２０秒以上が好ましく、さらに好ましくは５００秒以下４０秒以上である。
【０３６４】
本発明において、マット剤は感光材料の最外表面層もしくは最外表面層として機能する層、あるいは外表面に近い層に含有されるのが好ましく、またいわゆる保護層として作用する層に含有されることが好ましい。
【０３６５】
５）ポリマーラテックス
特に寸法変化が問題となる印刷用途に本発明の熱現像感光材料を用いる場合には、表面保護層やバック層にポリマーラテックスを用いることが好ましい。このようなポリマーラテックスについては「合成樹脂エマルジョン（奥田平、稲垣寛編集、高分子刊行会発行（１９７８））」、「合成ラテックスの応用（杉村孝明、片岡靖男、鈴木聡一、笠原啓司編集、高分子刊行会発行（１９９３））」、「合成ラテックスの化学（室井宗一著、高分子刊行会発行（１９７０））」などにも記載され、具体的にはメチルメタクリレート（３３．５質量％）／エチルアクリレート（５０質量％）／メタクリル酸（１６．５質量％）コポリマーのラテックス、メチルメタクリレート（４７．５質量％）／ブタジエン（４７．５質量％）／イタコン酸（５質量％）コポリマーのラテックス、エチルアクリレート／メタクリル酸のコポリマーのラテックス、メチルメタクリレート（５８．９質量％）／２−エチルヘキシルアクリレート（２５．４質量％）／スチレン（８．６質量％）／２−ヒドロキシエチルメタクリレート（５．１質量％）／アクリル酸（２．０質量％）コポリマーのラテックス、メチルメタクリレート（６４．０質量％）／スチレン（９．０質量％） ／ブチルアクリレート（２０．０質量％）／２−ヒドロキシエチルメタクリレート（５．０質量％）／アクリル酸（２．０質量％）コポリマーのラテックスなどが挙げられる。
【０３６６】
さらに、表面保護層用のバインダーとして、特願平１１−６８７２号明細書のポリマーラテックスの組み合わせ、特開２０００−２６７２２６号明細書の段落番号００２１〜００２５に記載の技術、特願平１１−６８７２号明細書の段落番号００２７〜００２８に記載の技術、特開２０００−１９６７８号明細書の段落番号００２３〜００４１に記載の技術を適用してもよい。表面保護層のポリマーラテックスの比率は全バインダーの１０質量％以上９０質量％以下が好ましく、特に２０質量％以上８０質量％以下が好ましい。
【０３６７】
６）膜面ｐＨ
本発明の熱現像感光材料は、熱現像処理前の膜面ｐＨが７．０以下であることが好ましく、さらに好ましくは６．６以下である。その下限には特に制限はないが、３程度である。最も好ましいｐＨ範囲は４〜６．２の範囲である。膜面ｐＨの調節はフタル酸誘導体などの有機酸や硫酸などの不揮発性の酸、アンモニアなどの揮発性の塩基を用いることが、膜面ｐＨを低減させるという観点から好ましい。特にアンモニアは揮発しやすく、塗布する工程や熱現像される前に除去できることから低膜面ｐＨを達成する上で好ましい。
また、水酸化ナトリウムや水酸化カリウム、水酸化リチウム等の不揮発性の塩基とアンモニアを併用することも好ましく用いられる。なお、膜面ｐＨの測定方法は、特開２０００−２８４３９９号明細書の段落番号０１２３に記載されている。
【０３６８】
７）硬膜剤
本発明の感光性層、保護層、バック層など各層には硬膜剤を用いても良い。硬膜剤の例としてはＴ．Ｈ．Ｊａｍｅｓ著”ＴＨＥ ＴＨＥＯＲＹ ＯＦ ＴＨＥ ＰＨＯＴＯＧＲＡＰＨＩＣ ＰＲＯＣＥＳＳ ＦＯＵＲＴＨ ＥＤＩＴＩＯＮ”（Ｍａｃｍｉｌｌａｎ Ｐｕｂｌｉｓｈｉｎｇ Ｃｏ．， Ｉｎｃ．刊、１９７７年刊）７７頁から８７頁に記載の各方法があり、クロムみょうばん、２，４−ジクロロ−６−ヒドロキシ−ｓ−トリアジンナトリウム塩、Ｎ，Ｎ−エチレンビス（ビニルスルホンアセトアミド）、Ｎ，Ｎ−プロピレンビス（ビニルスルホンアセトアミド）の他、同書７８頁など記載の多価金属イオン、米国特許４，２８１，０６０号、特開平６−２０８１９３号などのポリイソシアネート類、米国特許４，７９１，０４２号などのエポキシ化合物類、特開昭６２−８９０４８号などのビニルスルホン系化合物類が好ましく用いられる。
【０３６９】
硬膜剤は溶液として添加され、この溶液の保護層塗布液中への添加時期は、塗布する１８０分前から直前、好ましくは６０分前から１０秒前であるが、混合方法及び混合条件については本発明の効果が十分に現れる限りにおいては特に制限はない。具体的な混合方法としては添加流量とコーターへの送液量から計算した平均滞留時間を所望の時間となるようにしたタンクでの混合する方法やＮ．Ｈａｒｎｂｙ、Ｍ．Ｆ．Ｅｄｗａｒｄｓ、Ａ．Ｗ．Ｎｉｅｎｏｗ著、高橋幸司訳”液体混合技術”（日刊工業新聞社刊、１９８９年）の第８章等に記載されているスタチックミキサーなどを使用する方法がある。
【０３７０】
８）界面活性剤
本発明に適用できる界面活性剤については特開平１１−６５０２１号段落番号０１３２、溶剤については同号段落番号０１３３、支持体については同号段落番号０１３４、帯電防止又は導電層については同号段落番号０１３５、カラー画像を得る方法については同号段落番号０１３６に、滑り剤については特開平１１−８４５７３号段落番号００６１〜００６４や特願平１１−１０６８８１号段落番号００４９〜００６２記載されている。
【０３７１】
本発明においてはフッ素系の界面活性剤を使用することが好ましい。フッ素系界面活性剤の具体例は特開平１０−１９７９８５号、特開２０００−１９６８０号、特開２０００−２１４５５４号等に記載された化合物があげられる。また、特開平９−２８１６３６号記載の高分子フッ素系界面活性剤も好ましく用いられる。本発明の熱現像感光材料においては特開２００２−８２４１１号、特願２００１−２４２３５７号および特願２００１−２６４１１０号記載のフッ素系界面活性剤の使用が好ましい。特に特願２００１−２４２３５７号および特願２００１−２６４１１０号記載のフッ素系界面活性剤は水系の塗布液で塗布製造を行う場合、帯電調整能力、塗布面状の安定性、スベリ性の点で好ましく、特願２００１−２６４１１０号記載のフッ素系界面活性剤は帯電調整能力が高く使用量が少なくてすむという点で最も好ましい。
【０３７２】
本発明においてフッ素系界面活性剤は乳剤面、バック面のいずれにも使用することができ、両方の面に使用することが好ましい。また、前述の金属酸化物を含む導電層と組み合わせて使用することが特に好ましい。この場合には導電層を有する面のフッ素系界面活性剤の使用量を低減もしくは除去しても十分な性能が得られる。
フッ素系界面活性剤の好ましい使用量は乳剤面、バック面それぞれに０．１ｍｇ／ｍ^２〜１００ｍｇ／ｍ^２の範囲で、より好ましくは０．３ｍｇ／ｍ^２〜３０ｍｇ／ｍ^２の範囲、さらに好ましくは１ｍｇ／ｍ^２〜１０ｍｇ／ｍ^２の範囲である。特に特願２００１−２６４１１０号記載のフッ素系界面活性剤は効果が大きく、０．０１ ｍｇ／ｍ^２〜１０ｍｇ／ｍ^２の範囲が好ましく、０．１ ｍｇ／ｍ^２〜５ｍｇ／ｍ^２の範囲がより好ましい。
【０３７３】
９）帯電防止剤
本発明においては金属酸化物あるいは導電性ポリマーを含む導電層を有することが好ましい。帯電防止層は下塗り層、バック層表面保護層などと兼ねてもよく、また別途設けてもよい。帯電防止層の導電性材料は金属酸化物中に酸素欠陥、異種金属原子を導入して導電性を高めた金属酸化物が好ましく用いられる。金属酸化物の例としてはＺｎＯ、ＴｉＯ_２、ＳｎＯ_２が好ましく、ＺｎＯに対してはＡｌ、Ｉｎの添加、ＳｎＯ_２に対してはＳｂ、Ｎｂ、Ｐ、ハロゲン元素等の添加、ＴｉＯ_２に対してはＮｂ、Ｔａ等の添加が好ましい。特にＳｂを添加したＳｎＯ_２が好ましい。異種原子の添加量は０．０１〜３０ｍｏｌ％の範囲が好ましく、０．１から１０ｍｏｌ％の範囲がより好ましい。金属酸化物の形状は球状、針状、板状いずれでもよいが、導電性付与の効果の点で長軸／単軸比が２．０以上、好ましくは３．０〜５０の針状粒子がよい。金属酸化物の使用量は好ましくは１ｍｇ／ｍ^２〜１０００ｍｇ／ｍ^２の範囲で、より好ましくは１０ｍｇ／ｍ^２〜５００ｍｇ／ｍ^２の範囲、さらに好ましくは２０ｍｇ／ｍ^２〜２００ｍｇ／ｍ^２の範囲である。
【０３７４】
本発明の帯電防止層は乳剤面側、バック面側のいずれに設置してもよいが、支持体とバック層との間に設置することが好ましい。本発明の帯電防止層の具体例は特開平１１−６５０２１号段落番号０１３５、特開昭５６−１４３４３０号、同５６−１４３４３１号、同５８−６２６４６号、同５６−１２０５１９号、特開平１１−８４５７３号の段落番号００４０〜００５１、米国特許第５，５７５，９５７号、特開平１１−２２３８９８号の段落番号００７８〜００８４に記載されている。
【０３７５】
１０）支持体
透明支持体は二軸延伸時にフィルム中に残存する内部歪みを緩和させ、熱現像処理中に発生する熱収縮歪みをなくすために、１３０〜１８５℃の温度範囲で熱処理を施したポリエステル、特にポリエチレンテレフタレートが好ましく用いられる。医療用の熱現像感光材料の場合、透明支持体は青色染料（例えば、特開平８−２４０８７７号実施例記載の染料−１）で着色されていてもよいし、無着色でもよい。支持体には、特開平１１−８４５７４号の水溶性ポリエステル、同１０−１８６５６５号のスチレンブタジエン共重合体、特開２０００−３９６８４号や特願平１１−１０６８８１号段落番号００６３〜００８０の塩化ビニリデン共重合体などの下塗り技術を適用することが好ましい。支持体にＩ画像形成層もしくはバック層を塗布するときの、支持体の含水率は０．５質量％以下であることが好ましい。
【０３７６】
１１）その他の添加剤
熱現像感光材料には、さらに、酸化防止剤、安定化剤、可塑剤、紫外線吸収剤あるいは被覆助剤を添加してもよい。各種の添加剤は、感光性層あるいは非感光性層のいずれかに添加する。それらについてＷＯ９８／３６３２２号、ＥＰ８０３７６４Ａ１号、特開平１０−１８６５６７号、同１０−１８５６８号等を参考にすることができる。
【０３７７】
１２）塗布方式
本発明における熱現像感光材料はいかなる方法で塗布されても良い。具体的には、エクストルージョンコーティング、スライドコーティング、カーテンコーティング、浸漬コーティング、ナイフコーティング、フローコーティング、または米国特許第２，６８１，２９４号に記載の種類のホッパーを用いる押出コーティングを 含む種々のコーティング操作が用いられ、Ｓｔｅｐｈｅｎ Ｆ． Ｋｉｓｔｌｅｒ、Ｐｅｔｅｒｔ Ｍ． Ｓｃｈｗｅｉｚｅｒ著”ＬＩＱＵＩＤ ＦＩＬＭ ＣＯＡＴＩＮＧ”（ＣＨＡＰＭＡＮ ＆ ＨＡＬＬ社刊、１９９７年）３９９頁から５３６頁記載のエクストルージョンコーティング、またはスライドコーティング好ましく用いられ、特に好ましくはスライドコーティングが用いられる。スライドコーティングに使用されるスライドコーターの形状の例は同書４２７頁のＦｉｇｕｒｅ １１ｂ．１に ある。また、所望により同書３９９頁から５３６頁記載の方法、米国特許第２，７６１，７９１ 号および英国特許第８３７，０９５号に記載の方法により２層またはそれ以上の層を同時に被覆することができる。本発明において特に好ましい塗布方法は特開２００１−１９４７４８号、同２００２−１５３８０８号、同２００２−１５３８０３号、同２００２−１８２３３３号に記載された方法である。
【０３７８】
本発明における有機銀塩含有層塗布液は、いわゆるチキソトロピー流体であることが好ましい。この技術については特開平１１−５２５０９号を参考にすることができる。本発明における有機銀塩含有層塗布液は剪断速度０．１Ｓ^−１における粘度は４００ｍＰａ・ｓ以上１００，０００ ｍＰａ・ｓ以下が好ましく、さらに好ましくは５００ｍＰａ・ｓ以上２０，０００ ｍＰａ・ｓ以下である。また、剪断速度１０００Ｓ^−１においては１ｍＰａ・ｓ以上２００ ｍＰａ・ｓ以下が好ましく、さらに好ましくは５ｍＰａ・ｓ以上８０ ｍＰａ・ｓ以下である。
【０３７９】
本発明の塗布液を調合する場合において２種の液を混合する際は公知のインライン混合機、インプラント混合機が好ましく用いられる。本発明の好ましいインライン混合機は特開２００２−８５９４８号に、インプラント混合機は特開２００２−９０９４０号に記載されている。
本発明における塗布液は塗布面状を良好に保つため脱泡処理をすることが好ましい。本発明の好ましい脱泡処理方法については特開２００２−６６４３１号に記載された方法である。
【０３８０】
本発明の塗布液を塗布する際には支持体の耐電による塵、ほこり等の付着を防止するために除電を行うことが好ましい。本発明において好ましい除電方法の例は特開２００２−１４３７４７に記載されている。
本発明においては非セット性の画像形成層塗布液を乾燥するため乾燥風、乾燥温度を精密にコントロールすることが重要である。本発明の好ましい乾燥方法は特開２００１−１９４７４９号、同２００２−１３９８１４号に詳しく記載されている。
【０３８１】
本発明の熱現像感光材料は成膜性を向上させるために塗布、乾燥直後に加熱処理をすることが好ましい。加熱処理の温度は膜面温度で６０℃〜１００℃の範囲が好ましく、加熱時間は１秒〜６０秒の範囲が好ましい。より好ましい範囲は膜面温度が７０℃〜９０℃、加熱時間が２秒〜１０秒の範囲である。本発明の好ましい加熱処理の方法は特開２００２−１０７８７２号に記載されている。
【０３８２】
また、本発明の熱現像感光材料を安定して連続製造するためには特開２００２−１５６７２８号、同２００２−１８２３３３号に記載の製造方法が好ましく用いられる。
熱現像感光材料は、モノシート型（受像材料のような他のシートを使用せずに、熱現像感光材料上に画像を形成できる型）であることが好ましい。
【０３８３】
１３）包装材料
本発明の感光材料は生保存時の写真性能の変動を押えるため、もしくはカール、巻癖などを改良するために、酸素透過率および／または水分透過率の低い包装材料で包装することが好ましい。酸素透過率は２５℃で５０ｍｌ／ａｔｍ・ｍ^２・ｄａｙ以下であることが好ましく、より好ましくは１０ｍｌ／ａｔｍ・ｍ^２・ｄａｙ以下、さらに好ましくは１．０ｍｌ／ａｔｍ・ｍ^２・ｄａｙ以下である。水分透過率は１０ｇ／ａｔｍ・ｍ^２・ｄａｙ以下であることが好ましく、より好ましくは５ｇ／ａｔｍ・ｍ^２・ｄａｙ以下、さらに好ましくは１ｇ／ａｔｍ・ｍ^２・ｄａｙ以下である。
該酸素透過率および／または水分透過率の低い包装材料の具体例としては、たとえば特開平８−２５４７９３号。特開２０００−２０６６５３号明細書に記載されている包装材料である。
【０３８４】
１４）その他の利用できる技術
本発明の熱現像感光材料に用いることのできる技術としては、ＥＰ８０３７６４Ａ１号、ＥＰ８８３０２２Ａ１号、ＷＯ９８／３６３２２号、特開昭５６−６２６４８号、同５８−６２６４４号、特開平９−４３７６６、同９−２８１６３７、同９−２９７３６７号、同９−３０４８６９号、同９−３１１４０５号、同９−３２９８６５号、同１０−１０６６９号、同１０−６２８９９号、同１０−６９０２３号、同１０−１８６５６８号、同１０−９０８２３号、同１０−１７１０６３号、同１０−１８６５６５号、同１０−１８６５６７号、同１０−１８６５６９号〜同１０−１８６５７２号、同１０−１９７９７４号、同１０−１９７９８２号、同１０−１９７９８３号、同１０−１９７９８５号〜同１０−１９７９８７号、同１０−２０７００１号、同１０−２０７００４号、同１０−２２１８０７号、同１０−２８２６０１号、同１０−２８８８２３号、同１０−２８８８２４号、同１０−３０７３６５号、同１０−３１２０３８号、同１０−３３９９３４号、同１１−７１００号、同１１−１５１０５号、同１１−２４２００号、同１１−２４２０１号、同１１−３０８３２号、同１１−８４５７４号、同１１−６５０２１号、同１１−１０９５４７号、同１１−１２５８８０号、同１１−１２９６２９号、同１１−１３３５３６号〜同１１−１３３５３９号、同１１−１３３５４２号、同１１−１３３５４３号、同１１−２２３８９８号、同１１−３５２６２７号、同１１−３０５３７７号、同１１−３０５３７８号、同１１−３０５３８４号、同１１−３０５３８０号、同１１−３１６４３５号、同１１−３２７０７６号、同１１−３３８０９６号、同１１−３３８０９８号、同１１−３３８０９９号、同１１−３４３４２０号、特開２０００−１８７２９８号、同２０００−１０２２９号、同２０００−４７３４５号、同２０００−２０６６４２号、同２０００−９８５３０号、同２０００−９８５３１号、同２０００−１１２０５９号、同２０００−１１２０６０号、同２０００−１１２１０４号、同２０００−１１２０６４号、同２０００−１７１９３６号も挙げられる。
【０３８５】
多色カラー熱現像感光材料の場合、各Ｉ画像形成層は、一般に、米国特許第４，４６０，６８１号に記載されているように、各感光性層の間に官能性もしくは非官能性のバリアー層を使用することにより、互いに区別されて保持される。
多色カラー熱現像感光材料の場合の構成は、各色についてこれらの二層の組合せを含んでよく、また、米国特許第４，７０８，９２８号に記載されているように単一層内に全ての成分を含んでいてもよい。
【０３８６】
（画像形成方法）
１）露光
本発明の感光材料はいかなる方法で露光されても良いが、露光光源としてレーザー光が好ましい。本発明のようにヨウ化銀含有率の高いハロゲン化銀乳剤は、従来はその感度が低くて問題であった。しかし、レーザー光のような高照度で書き込むことで低感度の問題も解消され、しかもより少ないエネルギーで画像記録できることがわかった。このような強い光で短時間に書き込むことによって目標の感度を達成することができる。
【０３８７】
特に最高濃度（Ｄｍａｘ）を出すような露光量を与える場合、感光材料表面の好ましい光量は０．１Ｗ／ｍｍ^２〜１００Ｗ／ｍｍ^２である。より好ましくは０．５Ｗ／ｍｍ^２〜５０Ｗ／ｍｍ^２であり、最も好ましくは１Ｗ／ｍｍ^２〜５０Ｗ／ｍｍ^２である。
【０３８８】
本発明によるレーザー光としては、ガスレーザー（Ａｒ^＋，Ｈｅ−Ｎｅ，Ｈｅ−Ｃｄ）、ＹＡＧレーザー、色素レーザー、半導体レーザーなどが好ましい。また、半導体レーザーと第２高調波発生素子などを用いることもできる。好ましく用いられるレーザーは、熱現像感光材料の分光増感色素などの光吸収ピーク波長に対応して決まるが、赤〜赤外発光のＨｅ−Ｎｅレーザー、赤色半導体レーザー、あるいは青〜緑発光のＡｒ^＋，Ｈｅ−Ｎｅ，Ｈｅ−Ｃｄレーザー、青色半導体レーザーである。 近年、特に、ＳＨＧ（Ｓｅｃｏｎｄ Ｈａｒｍｏｎｉｃ Ｇｅｎｅｒａｔｏｒ）素子と半導体レーザーを一体化したモジュールや青色半導体レーザーが開発されてきて、短波長領域のレーザー出力装置がクローズアップされてきた。青色半導体レーザーは、高精細の画像記録が可能であること、記録密度の増大、かつ長寿命で安定した出力が得られることから、今後需要が拡大していくことが期待されている。レーザー光のピーク波長は、青色の３００ｎｍ〜５００ｎｍ、好ましくは３５０ｎｍ〜４３０ｎｍ、より好ましくは３８０ｎｍ〜４２０ｎｍ、赤〜近赤外の６００ｎｍ〜９００ｎｍ、好ましくは６２０ｎｍ〜８５０ｎｍ、より好ましくは６４０ｎｍ〜８３０ｎｍである。
【０３８９】
レーザー光は、高周波重畳などの方法によって縦マルチに発振していることも好ましく用いられる。
【０３９０】
２）熱現像
本発明の熱現像感光材料はいかなる方法で現像されても良いが、通常イメージワイズに露光した熱現像感光材料を昇温して現像される。好ましい現像温度としては８０℃〜２５０℃であり、さらに好ましくは１００℃〜１４０℃である。
現像時間としては１秒〜３０秒が好ましく、２秒〜２０秒がさらに好ましく、３秒〜１０秒が特に好ましい。
【０３９１】
熱現像の方式としてはプレートヒーター方式が好ましい。プレートヒーター方式による熱現像方式とは特開平１１−１３３５７２号に記載の方法が好ましく、潜像を形成した熱現像感光材料を熱現像部にて加熱手段に接触させることにより可視像を得る熱現像装置であって、前記加熱手段がプレートヒータからなり、かつ前記プレートヒータの一方の面に沿って複数個の押えローラが対向配設され、前記押えローラと前記プレートヒータとの間に前記熱現像感光材料を通過させて熱現像を行うことを特徴とする熱現像装置である。プレートヒータを２〜６段に分けて先端部については１℃〜１０℃程度温度を下げることが好ましい。
【０３９２】
このような方法は特開昭５４−３００３２号にも記載されており、熱現像感光材料に含有している水分や有機溶媒を系外に除外させることができ、また、急激に熱現像感光材料が加熱されることでの熱現像感光材料の支持体形状の変化を押さえることもできる。
【０３９３】
３）システム
露光部および熱現像部を備えた医療用レーザーイメージャーとして富士メディカルドライイメージャー−ＦＭ−ＤＰＬやＤＲＹＰＩＸ７０００を挙げることができる。該システムは、Ｆｕｊｉ Ｍｅｄｉｃａｌ Ｒｅｖｉｅｗ Ｎｏ．８，ｐａｇｅ３９〜５５に記載されており、それらの技術を利用することができる。また、ＤＩＣＯＭ規格に適合したネットワークシステムとして富士フィルムメディカル（株）が提案した「ＡＤ ｎｅｔｗｏｒｋ」の中のレーザーイメージャー用の熱現像感光材料としても適用することができる。
【０３９４】
（本発明の用途）
本発明の高ヨウ化銀写真乳剤を用いた熱現像感光材料は、銀画像による黒白画像を形成し、医療診断用の熱現像感光材料、工業写真用熱現像感光材料、印刷用熱現像感光材料、ＣＯＭ用の熱現像感光材料として使用されることが好ましい。
【０３９５】
【実施例】
以下、本発明を実施例によって具体的に説明するが、本発明はこれらに限定されるものではない。
実施例１
【０３９６】
１．ＰＥＴ支持体の作製
１）製膜
テレフタル酸とエチレングリコ−ルを用い、常法に従い固有粘度ＩＶ＝０．６６（フェノ−ル／テトラクロルエタン＝６／４（質量比）中２５℃で測定）のＰＥＴを得た。これをペレット化した後１３０℃で４時間乾燥し、３００℃で溶融後Ｔ型ダイから押し出して急冷し、熱固定後の膜厚が１７５μｍになるような厚みの未延伸フィルムを作成した。
【０３９７】
これを、周速の異なるロ−ルを用い３．３倍に縦延伸、ついでテンタ−で４．５倍に横延伸を実施した。この時の温度はそれぞれ、１１０℃、１３０℃であった。この後、２４０℃で２０秒間熱固定後これと同じ温度で横方向に４％緩和した。この後テンタ−のチャック部をスリットした後、両端にナ−ル加工を行い、４ｋｇ／ｃｍ^２で巻き取り、厚み１７５μｍのロ−ルを得た。
【０３９８】
２）表面放電コロナ処理
ピラー社製ソリッドステートコロナ放電処理機６ＫＶＡモデルを用い、支持体の両面を室温下において２０ｍ／分で処理した。この時の電流、電圧の読み取り値から、支持体には０．３７５ｋＶ・Ａ・分／ｍ^２の処理がなされていることがわかった。この時の処理周波数は９．６ｋＨｚ、電極と誘電体ロ−ルのギャップクリアランスは１．６ｍｍであった。
【０３９９】
３）下塗り
（下塗層塗布液の作成）

【０４００】

【０４０１】

【０４０２】
（下塗り）
上記厚さ１７５μｍの２軸延伸ポリエチレンテレフタレート支持体の両面それぞれに、上記コロナ放電処理を施した後、片面（感光性層面）に上記下塗り塗布液処方▲１▼をワイヤーバーでウエット塗布量が６．６ｍｌ／ｍ^２（片面当たり）になるように塗布して１８０ ℃で５分間乾燥し、ついでこの裏面（バック面）に上記下塗り塗布液処方▲２▼をワイヤーバーでウエット塗布量が５．７ｍｌ／ｍ^２になるように塗布して１８０ ℃で５分間乾燥し、更に裏面（バック面）に上記下塗り塗布液処方▲３▼をワイヤーバーでウエット塗布量が７．７ｍｌ／ｍ^２になるように塗布して１８０ ℃で６分間乾燥して下塗り支持体を作製した。
【０４０３】
２．バック層
１）塗布液の調製
【０４０４】
（ハレーション防止層塗布液の調製）
４０℃に保温した水に石灰処理ゼラチン３２．７ｇ、単分散ポリメチルメタクリレート微粒子（平均粒子サイズ８μｍ、粒径標準偏差０．４μｍ）０．７７ｇ、ベンゾイソチアゾリノン０．０８ｇ、ポリスチレンスルホン酸ナトリウム０．３ｇ、青色染料化合物−１を０．０６ｇ、紫外光吸収剤−１を１．５ｇ、アクリル酸／エチルアクリレート共重合ラテックス（共重合比５／９５）５．０ｇ、Ｎ，Ｎ−エチレンビス（ビニルスルホンアセトアミド）１．７ｇを混合し、１ｍｏｌ／ｌの水酸化ナトリウムでｐＨを６．０に調整し、水にて全体を８１８ｍｌとし、ハレーション防止層塗布液を調製した。
【０４０５】
（バック面保護層塗布液の調製）
４０℃に保温した水に石灰処理ゼラチン６６．５ｇ、流動パラフィン乳化物を流動パラフィンとして５．４ｇ、ベンゾイソチアゾリノン０．１０ｇ、スルホコハク酸ジ（２−エチルヘキシル）ナトリウム０．５ｇ、ポリスチレンスルホン酸ナトリウム０．２７ｇ、フッ素系界面活性剤（Ｆ−１）２質量％水溶液を１３．６ｍＬ、アクリル酸／エチルアクリレート共重合体（共重合重量比５／９５）１０．０ｇを混合し、１ｍｏｌ／ｌの水酸化ナトリウムでｐＨを６．０に調整し、水で１０００ｍｌとしてバック面保護層塗布液とした。
【０４０６】
２）バック層の塗布
上記下塗り支持体のバック面側に、ハレーション防止層塗布液をゼラチン塗布量が１．７０ｇ／ｍ^２となるように、またバック面保護層塗布液をゼラチン塗布量が０．７９ｇ／ｍ^２となるように同時重層塗布し、乾燥し、バック層を作成した。
【０４０７】
３．画像形成層、中間層、および表面保護層
３−１．塗布用材料の準備
１）ハロゲン化銀乳剤の調製
（ハロゲン化銀乳剤−１の調製）
蒸留水１４２０ｍｌに１質量％ヨウ化カリウム溶液４．３ｍｌを加え、さらに０．５ｍｏｌ／Ｌ濃度の硫酸を３．５ｍｌ、フタル化ゼラチン３６．７ｇを添加した液をステンレス製反応壺中で攪拌しながら、４２℃に液温を保ち、硝酸銀２２．２２ｇに蒸留水を加え１９５．６ｍｌに希釈した溶液Ａとヨウ化カリウム２１．８ｇを蒸留水にて容量２１８ｍｌに希釈した溶液Ｂを一定流量で９分間かけて全量添加した。その後、３．５質量％の過酸化水素水溶液を１０ｍｌ添加し、さらにベンゾイミダゾールの１０質量％水溶液を１０．８ｍｌ添加した。
【０４０８】
さらに、硝酸銀５１．８６ｇに蒸留水を加えて３１７．５ｍｌに希釈した溶液Ｃとヨウ化カリウム６０ｇを蒸留水にて容量６００ｍｌに希釈した溶液Ｄを、溶液Ｃは一定流量で１２０分間かけて全量添加し、溶液ＤはｐＡｇを８．１に維持しながらコントロールドダブルジェット法で添加した。銀１モル当たり１×１０^−４モルになるよう六塩化イリジウム（ＩＩＩ）酸カリウム塩を溶液Ｃおよび溶液Ｄを添加しはじめてから１０分後に全量添加した。また、溶液Ｃの添加終了の５秒後に六シアン化鉄（ＩＩ）カリウム水溶液を銀１モル当たり３×１０^−４モル全量添加した。０．５ｍｏｌ／Ｌ濃度の硫酸を用いてｐＨを３．８に調整し、攪拌を止め、沈降／脱塩／水洗工程をおこなった。１ｍｏｌ／Ｌ濃度の水酸化ナトリウムを用いてｐＨ５．９に調整し、ｐＡｇ８．０のハロゲン化銀分散物を作成した。
【０４０９】
上記ハロゲン化銀分散物を攪拌しながら３８℃に維持して、０．３４質量％の１、２−ベンゾイソチアゾリン−３−オンのメタノール溶液を５ｍｌ加え、４７℃に昇温した。昇温の２０分後にベンゼンチオスルフォン酸ナトリウムをメタノール溶液で銀１モルに対して７．６×１０^−５モル加え、さらに５分後にテルル増感剤Ｂをメタノール溶液で銀１モル当たり２．９×１０^−４モル加えて９１分間熟成した。
Ｎ、Ｎ’−ジヒドロキシ−Ｎ”、Ｎ”−ジエチルメラミンの０．８質量％メタノール溶液１．３ｍｌを加え、さらに４分後に、５−メチル−２−メルカプトベンゾイミダゾールをメタノール溶液で銀１モル当たり４．８×１０^−３モル及び１−フェニル−２−ヘプチル−５−メルカプト−１、３、４−トリアゾールをメタノール溶液で銀１モルに対して５．４×１０^−３モル添加して、ハロゲン化銀乳剤−１を作製した。
【０４１０】
調製できたハロゲン化銀乳剤中の粒子は、平均球相当径０．０４０μｍ、球相当径の変動係数１８％の純ヨウ化銀粒子であった。また（００１）、｛１００｝、｛１０１｝面を有する１４面体粒子であり、Ｘ線粉末回折分析を用いて測定するとそのγ相の比率は３０％であった。粒子サイズ等は、電子顕微鏡を用い１０００個の粒子の平均から求めた。
【０４１１】
（ハロゲン化銀乳剤２の調製）
反応溶液の温度を６５℃に変更し、２，２‘−（エチレンジチオ）ジエタノールの５質量％メタノール溶液５ｍｌを溶液ＡとＢの添加後に添加したこと、ｐＡｇを１０．５に維持しながら溶液Ｄをコントロールドダブルジェット法で添加したこと、および化学増感時にテルル増感剤の添加３分後に臭化金酸を銀１モル当たり５×１０^−４モルとチオシアン酸カリウムを銀１モルあたり２×１０^−３モルを添加したこと以外は乳剤１と同様にしてハロゲン化銀乳剤２を作成した。
【０４１２】
調製できたハロゲン化銀乳剤中の粒子は、投影面積の平均円相当径０．１６４μｍ、粒子厚み０．０３２μｍ、平均アスペクト比が５、平均球相当径０．１１μｍ、球相当径の変動係数２３％の純ヨウ化銀平板状粒子であった。Ｘ線粉末回折分析を用いて測定するとそのγ相の比率は８０％であった。粒子サイズ等は、電子顕微鏡を用い１０００個の粒子の平均から求めた。
【０４１３】
（ハロゲン化銀乳剤３の調製）
反応溶液の温度を２７℃に変更したこと、ｐＡｇを１０．２に維持しながら溶液Ｄをコントロールドダブルジェット法で添加したこと以外はハロゲン化銀乳剤１と全く同様にしてハロゲン化銀乳剤３を作成した。
【０４１４】
調製できたハロゲン化銀乳剤中の粒子は、平均球相当径０．０２２μｍ、球相当径の変動係数１７％の純ヨウ化銀粒子であった。また（００１）、｛１（−１）０｝、｛１０１｝面を有する１２面体粒子であり、Ｘ線粉末回折分析を用いて測定するとほぼβ相からなる沃化銀であった。粒子サイズ等は、電子顕微鏡を用い１０００個の粒子の平均から求めた。
【０４１５】
（塗布液用混合乳剤Ａの調製）
ハロゲン化銀乳剤−１とハロゲン化銀乳剤−２とハロゲン化銀乳剤−３を銀モル比として５：２：３になる量を溶解し、ベンゾチアゾリウムヨーダイドを１質量％水溶液にて銀１モル当たり７×１０^−３モル添加した。さらに塗布液用混合乳剤１ｋｇあたりハロゲン化銀の含有量が銀として３８．２ｇとなるように加水した。
【０４１６】
さらに「１電子酸化されて生成する１電子酸化体が１電子もしくはそれ以上の電子を放出し得る化合物」として、化合物２と２０と２６をそれぞれハロゲン化銀の銀１モル当たり２×１０^−３モルになる量を添加した。
【０４１７】
また吸着基と還元基を有する化合物として、化合物（１２）と（２７）と（３６）をそれぞれハロゲン化銀１モルあたり８×１０^−３モルになる量を添加した。
【０４１８】
２）脂肪酸銀分散物の調製
＜再結晶ベヘン酸の調製＞
ヘンケル社製ベヘン酸（製品名Ｅｄｅｎｏｒ Ｃ２２−８５Ｒ）１００ｋｇを、１２００ｋｇのイソプロピルアルコールにまぜ、５０℃で溶解し、１０μｍのフィルターで濾過した後、３０℃まで、冷却し、再結晶を行った。再結晶をする際の、冷却スピードは、３℃／時間にコントロールした。得られた結晶を遠心濾過し、１００ｋｇのイソプルピルアルコールでかけ洗いを実施した後、乾燥を行った。得られた結晶をエステル化してＧＣ−ＦＩＤ測定をしたところ、ベヘン酸含有率は９６モル％、それ以外にリグノセリン酸が２モル％、アラキジン酸が２モル％、エルカ酸０．００１モル％含まれていた。
【０４１９】
＜脂肪酸銀分散物の調製＞
再結晶ベヘン酸８８ｋｇ、蒸留水４２２Ｌ、５ｍｏｌ／Ｌ濃度のＮａＯＨ水溶液４９．２Ｌ、ｔ−ブチルアルコール１２０Ｌを混合し、７５℃にて１時間攪拌し反応させ、ベヘン酸ナトリウム溶液Ｂを得た。別に、硝酸銀４０．４ｋｇの水溶液２０６．２Ｌ（ｐＨ４．０）を用意し、１０℃にて保温した。６３５Ｌの蒸留水と３０Ｌのｔ−ブチルアルコールを入れた反応容器を３０℃に保温し、十分に撹拌しながら先のベヘン酸ナトリウム溶液の全量と硝酸銀水溶液の全量を流量一定でそれぞれ９３分１５秒と９０分かけて添加した。このとき、硝酸銀水溶液添加開始後１１分間は硝酸銀水溶液のみが添加されるようにし、そのあとベヘン酸ナトリウム溶液を添加開始し、硝酸銀水溶液の添加終了後１４分１５秒間はベヘン酸ナトリウム溶液のみが添加されるようにした。このとき、反応容器内の温度は３０℃とし、液温度が一定になるように外温コントロールした。また、ベヘン酸ナトリウム溶液の添加系の配管は、２重管の外側に温水を循環させる事により保温し、添加ノズル先端の出口の液温度が７５℃になるよう調製した。また、硝酸銀水溶液の添加系の配管は、２重管の外側に冷水を循環させることにより保温した。ベヘン酸ナトリウム溶液の添加位置と硝酸銀水溶液の添加位置は撹拌軸を中心として対称的な配置とし、また反応液に接触しないような高さに調製した。
【０４２０】
ベヘン酸ナトリウム溶液を添加終了後、そのままの温度で２０分間撹拌放置し、３０分かけて３５℃に昇温し、その後２１０分熟成を行った。熟成終了後直ちに、遠心濾過で固形分を濾別し、固形分を濾過水の伝導度が３０μＳ／ｃｍになるまで水洗した。こうして脂肪酸銀塩を得た。得られた固形分は、乾燥させないでウエットケーキとして保管した。
【０４２１】
得られたベヘン酸銀粒子の形態を電子顕微鏡撮影により評価したところ、平均値でａ＝０．２１μｍ、ｂ＝０．４μｍ、ｃ＝０．４μｍ、平均アスペクト比２．１、球相当径の変動係数１１％の結晶であった。（ａ，ｂ，ｃは本文の規定）
【０４２２】
乾燥固形分２６０ｋｇ相当のウエットケーキに対し、ポリビニルアルコール（商品名：ＰＶＡ−２１７）１９．３ｋｇおよび水を添加し、全体量を１０００ｋｇとしてからディゾルバー羽根でスラリー化し、更にパイプラインミキサー（みづほ工業製：ＰＭ−１０型）で予備分散した。
【０４２３】
次に予備分散済みの原液を分散機（商品名：マイクロフルイダイザーＭ−６１０、マイクロフルイデックス・インターナショナル・コーポレーション製、Ｚ型インタラクションチャンバー使用）の圧力を１１５０ｋｇ／ｃｍ^２に調節して、三回処理し、ベヘン酸銀分散物を得た。冷却操作は蛇管式熱交換器をインタラクションチャンバーの前後に各々装着し、冷媒の温度を調節することで１８℃の分散温度に設定した。
【０４２４】
３）還元剤分散物の調製
（還元剤−１分散物の調製）
還元剤―１（２，２’−メチレンビス−（４−エチル−６−ｔｅｒｔ−ブチルフェノール））１０ｋｇと変性ポリビニルアルコール（クラレ（株）製、ポバールＭＰ２０３）の１０質量％水溶液１６ｋｇに、水１０ｋｇを添加して、良く混合してスラリーとした。このスラリーをダイアフラムポンプで送液し、平均直径０．５ｍｍのジルコニアビーズを充填した横型サンドミル（ＵＶＭ−２：アイメックス（株）製）にて３時間分散したのち、ベンゾイソチアゾリノンナトリウム塩０．２ｇと水を加えて還元剤の濃度が２５質量％になるように調製した。この分散液を６０℃で５時間加熱処理し、還元剤―１分散物を得た。こうして得た還元剤分散物に含まれる還元剤粒子はメジアン径０．４０μｍ、最大粒子径１．４μｍ以下であった。得られた還元剤分散物は孔径３．０μｍのポリプロピレン製フィルターにてろ過を行い、ゴミ等の異物を除去して収納した。
（還元剤−２分散物の調製）
還元剤―２（６，６’−ジ−ｔ−ブチル−４，４’−ジメチル−２，２’−ブチリデンジフェノール）１０ｋｇと変性ポリビニルアルコール（クラレ（株）製、ポバールＭＰ２０３）の１０質量％水溶液１６ｋｇに、水１０ｋｇを添加して、良く混合してスラリーとした。このスラリーをダイアフラムポンプで送液し、平均直径０．５ｍｍのジルコニアビーズを充填した横型サンドミル（ＵＶＭ−２：アイメックス（株）製）にて３時間３０分分散したのち、ベンゾイソチアゾリノンナトリウム塩０．２ｇと水を加えて還元剤の濃度が２５質量％になるように調製した。この分散液を４０℃で１時間加熱した後、引き続いてさらに８０℃で１時間加熱処理し、還元剤―２分散物を得た。こうして得た還元剤分散物に含まれる還元剤粒子はメジアン径０．５０μｍ、最大粒子径１．６μｍ以下であった。得られた還元剤分散物は孔径３．０μｍのポリプロピレン製フィルターにてろ過を行い、ゴミ等の異物を除去して収納した。
【０４２５】
（その他の還元剤分散物の調製）
その他の還元剤の固体分散物についても還元剤−２と同様の方法により分散した。
【０４２６】
４）水素結合性化合物−１分散物の調製
水素結合性化合物−１（トリ（４−ｔ−ブチルフェニル）ホスフィンオキシド）１０ｋｇと変性ポリビニルアルコール（クラレ（株）製、ポバールＭＰ２０３）の１０質量％水溶液１６ｋｇに、水１０ｋｇを添加して、良く混合してスラリーとした。このスラリーをダイアフラムポンプで送液し、平均直径０．５ｍｍのジルコニアビーズを充填した横型サンドミル（ＵＶＭ−２：アイメックス（株）製）にて４時間分散したのち、ベンゾイソチアゾリノンナトリウム塩０．２ｇと水を加えて水素結合性化合物の濃度が２５質量％になるように調製した。この分散液を４０℃で１時間加熱した後、引き続いてさらに８０℃で１時間加温し、水素結合性化合物―１分散物を得た。こうして得た水素結合性化合物分散物に含まれる水素結合性化合物粒子はメジアン径０．４５μｍ、最大粒子径１．３μｍ以下であった。得られた水素結合性化合物分散物は孔径３．０μｍのポリプロピレン製フィルターにてろ過を行い、ゴミ等の異物を除去して収納した。
【０４２７】
５）現像促進剤分散物の調製
（現像促進剤−１分散物の調製）
現像促進剤−１を１０ｋｇと変性ポリビニルアルコール（クラレ（株）製、ポバールＭＰ２０３）の１０質量％水溶液２０ｋｇに、水１０ｋｇを添加して、良く混合してスラリーとした。このスラリーをダイアフラムポンプで送液し、平均直径０．５ｍｍのジルコニアビーズを充填した横型サンドミル（ＵＶＭ−２：アイメックス（株）製）にて３時間３０分分散したのち、ベンゾイソチアゾリノンナトリウム塩０．２ｇと水を加えて現像促進剤の濃度が２０質量％になるように調製し、現像促進剤−１分散物を得た。こうして得た現像促進剤分散物に含まれる現像促進剤粒子はメジアン径０．４８μｍ、最大粒子径１．４μｍ以下であった。得られた現像促進剤分散物は孔径３．０μｍのポリプロピレン製フィルターにてろ過を行い、ゴミ等の異物を除去して収納した。
【０４２８】
（現像促進剤−２およびその他の現像促進剤の分散物調製）
現像促進剤−２およびその他の現像促進剤の固体分散物についても現像促進剤−１と同様の方法により分散した。
【０４２９】
６）ポリハロゲン化合物分散物の調製
（有機ポリハロゲン化合物−１分散物）
有機ポリハロゲン化合物―１（トリブロモメタンスルホニルベンゼン）１０ｋｇと変性ポリビニルアルコール（クラレ（株）製ポバールＭＰ２０３）の２０質量％水溶液１０ｋｇと、トリイソプロピルナフタレンスルホン酸ナトリウムの２０質量％水溶液０．４ｋｇと、水１４ｋｇを添加して、良く混合してスラリーとした。このスラリーをダイアフラムポンプで送液し、平均直径０．５ｍｍのジルコニアビーズを充填した横型サンドミル（ＵＶＭ−２：アイメックス（株）製）にて５時間分散したのち、ベンゾイソチアゾリノンナトリウム塩０．２ｇと水を加えて有機ポリハロゲン化合物の濃度が３０質量％になるように調製し、有機ポリハロゲン化合物―１分散物を得た。こうして得たポリハロゲン化合物分散物に含まれる有機ポリハロゲン化合物粒子はメジアン径０．４１μｍ、最大粒子径２．０μｍ以下であった。得られた有機ポリハロゲン化合物分散物は孔径１０．０μｍのポリプロピレン製フィルターにてろ過を行い、ゴミ等の異物を除去して収納した。
【０４３０】
（有機ポリハロゲン化合物−２分散物）
有機ポリハロゲン化合物―２（Ｎ−ブチル−３−トリブロモメタンスルホニルベンゾアミド）１０ｋｇと変性ポリビニルアルコール（クラレ（株）製ポバールＭＰ２０３）の１０質量％水溶液２０ｋｇと、トリイソプロピルナフタレンスルホン酸ナトリウムの２０質量％水溶液０．４ｋｇを添加して、良く混合してスラリーとした。このスラリーをダイアフラムポンプで送液し、平均直径０．５ｍｍのジルコニアビーズを充填した横型サンドミル（ＵＶＭ−２：アイメックス（株）製）にて５時間分散したのち、ベンゾイソチアゾリノンナトリウム塩０．２ｇと水を加えて有機ポリハロゲン化合物の濃度が３０質量％になるように調製した。この分散液を４０℃で５時間加温し、有機ポリハロゲン化合物―２分散物を得た。こうして得たポリハロゲン化合物分散物に含まれる有機ポリハロゲン化合物粒子はメジアン径０．４０μｍ、最大粒子径１．３μｍ以下であった。得られた有機ポリハロゲン化合物分散物は孔径３．０μｍのポリプロピレン製フィルターにてろ過を行い、ゴミ等の異物を除去して収納した。
【０４３１】
７）フタラジン化合物−１溶液の調
８ｋｇのクラレ（株）製変性ポリビニルアルコールＭＰ２０３を水１７４．５７ｋｇに溶解し、次いでトリイソプロピルナフタレンスルホン酸ナトリウムの２０質量％水溶液３．１５ｋｇとフタラジン化合物―１（６−イソプロピルフタラジン）の７０質量％水溶液１４．２８ｋｇを添加し、フタラジン化合物―１の５質量％溶液を調製した。
【０４３２】
８）メルカプト化合物の調製
（メルカプト化合物−１水溶液の調製）
メルカプト化合物―１（１−（３−スルホフェニル）−５−メルカプトテトラゾールナトリウム塩）７ｇを水９９３ｇに溶解し、０．７質量％の水溶液とした。
【０４３３】
（メルカプト化合物−２水溶液の調製）
メルカプト化合物―２（１−（３−メチルウレイドフェニル）−５−メルカプトテトラゾール）２０ｇを水９８０ｇに溶解し、２．０質量％の水溶液とした。
【０４３４】
９）顔料−１分散物の調製
Ｃ．Ｉ．Ｐｉｇｍｅｎｔ Ｂｌｕｅ ６０を６４ｇと花王（株）製デモールＮを６．４ｇに水２５０ｇを添加し良く混合してスラリーとした。平均直径０．５ｍｍのジルコニアビーズ８００ｇを用意してスラリーと一緒にベッセルに入れ、分散機（１／４Ｇサンドグラインダーミル：アイメックス（株）製）にて２５時間分散し、水を加えて顔料の濃度が５質量％になるように調製して顔料−１分散物を得た。こうして得た顔料分散物に含まれる顔料粒子は平均粒径０．２１μｍであった。
【０４３５】
１０）ＳＢＲラテックス液の調製
ＳＢＲラテックスは以下により調整した。
ガスモノマー反応装置（耐圧硝子工業（株）製ＴＡＳ−２Ｊ型）の重合釜に、蒸留水２８７ｇ、界面活性剤（パイオニンＡ−４３−Ｓ（竹本油脂（株）製）：固形分４８．５質量％）７．７３ｇ、１ｍｏｌ／リットルＮａＯＨ１４．０６ｍｌ、エチレンジアミン４酢酸４ナトリウム塩０．１５ｇ、スチレン２５５ｇ、アクリル酸１１．２５ｇ、ｔｅｒｔ−ドデシルメルカプタン３．０ｇを入れ、反応容器を密閉し撹拌速度２００ｒｐｍで撹拌した。真空ポンプで脱気し窒素ガス置換を数回繰返した後に、１，３−ブタジエン１０８．７５ｇを圧入して内温６０℃まで昇温した。ここに過硫酸アンモニウム１．８７５ｇを水５０ｍｌに溶解した液を添加し、そのまま５時間撹拌した。さらに９０℃に昇温して３時間撹拌し、反応終了後内温が室温になるまで下げた後、１ｍｏｌ／リットルのＮａＯＨとＮＨ_４ＯＨを用いてＮａ^＋イオン：ＮＨ_４ ^＋イオン＝１：５．３（モル比）になるように添加処理し、ｐＨ８．４に調整した。その後、孔径１．０μｍのポリプロピレン製フィルターにてろ過を行い、ゴミ等の異物を除去して収納し、ＳＢＲラテックスを７７４．７ｇ得た。イオンクロマトグラフィーによりハロゲンイオンを測定したところ、塩化物イオン濃度３ｐｐｍであった。高速液体クロマトグラフィーによりキレート剤の濃度を測定した結果、１４５ｐｐｍであった。
【０４３６】
上記ラテックスは平均粒径９０ｎｍ、Ｔｇ＝１７℃、固形分濃度４４質量％、２５℃６０％ＲＨにおける平衡含水率０．６質量％、イオン伝導度４．８０ｍＳ／ｃｍ（イオン伝導度の測定は東亜電波工業（株）製伝導度計ＣＭ−３０Ｓ使用し、ラテックス原液（４４質量％）を２５℃にて測定）、ｐＨ８．４であった。
【０４３７】
１１）本発明の発色剤、および比較化合物の分散物の調製
本発明の発色剤（Ｄ−１）を１ｋｇと変性ポリビニルアルコール（クラレ（株）製、ポバールＭＰ２０３）の１０質量％水溶液２ｋｇに、水１ｋｇを添加して、良く混合してスラリーとした。このスラリーをダイアフラムポンプで送液し、平均直径０．５ｍｍのジルコニアビーズを充填した横型サンドミル（ＵＶＭ−２：アイメックス（株）製）にて４５分間分散したのち、ベンゾイソチアゾリノンナトリウム塩０．０２ｇと水を加えて本発明の発色剤（Ｄ−１）の濃度が２０質量％になるように調製し、本発明の発色剤（Ｄ−１）分散物を得た。こうして得た本発明の発色剤（Ｄ−１）分散物に含まれる本発明の発色剤（Ｄ−１）粒子はメジアン径０．４５μｍ、最大粒子径１．４μｍ以下であった。得られた現像促進剤分散物は孔径３．０μｍのポリプロピレン製フィルターにてろ過を行い、ゴミ等の異物を除去して収納した。その他の本発明の発色剤と比較発色剤Ｃ−１も同様に分散し、１５質量％の分散物を得た。それぞれの粒子のメジアン径が０．４５μｍになるように分散時間を調整して分散物を得た。
その他の本発明の発色剤および比較化合物についても同様に分散物を調製した。
【０４３８】
３−２．塗布液の調製
１）画像形成層塗布液の調製
上記で得た脂肪酸銀分散物１０００ｇ、水２７６ｍｌに顔料−１分散物、有機ポリハロゲン化合物−１分散物、有機ポリハロゲン化合物−２分散物、フタラジン化合物―１溶液、ＳＢＲラテックス（Ｔｇ：１７℃）液、還元剤分散物（量と種類は表１に記載）、水素結合性化合物−１分散物、現像促進剤−１分散物、現像促進剤−２分散物、メルカプト化合物−１水溶液、メルカプト化合物−２水溶液、本発明の発色剤または比較化合物Ｃ−１（量と種類は表１に記載）を順次添加し、塗布直前にハロゲン化銀混合乳剤Ａを添加して良く混合したＩ画像形成層塗布液をそのままコーティングダイへ送液した。
【０４３９】
上記画像形成層塗布液の粘度は東京計器のＢ型粘度計で測定して、４０℃（Ｎｏ．１ローター、６０ｒｐｍ）で２５［ｍＰａ・ｓ］であった。
レオメトリックスファーイースト株式会社製ＲＦＳフルードスペクトロメーターを使用した２５℃での塗布液の粘度は剪断速度が０．１、１、１０、１００、１０００［１／秒］ においてそれぞれ２４２、６５、４８、２６、２０［ｍＰａ・ｓ］であった。
【０４４０】
塗布液中のジルコニウム量は銀１ｇあたり０．５２ｍｇであった。
【０４４１】
２）中間層塗布液の調製
ポリビニルアルコールＰＶＡ−２０５（クラレ（株）製）１０００ｇ、顔料−１分散物２７２ｇ、メチルメタクリレート／スチレン／ブチルアクリレート／ヒドロキシエチルメタクリレート／アクリル酸共重合体（共重合重量比６４／９／２０／５／２）ラテックス１９質量％液４２００ｍｌにエアロゾールＯＴ（アメリカンサイアナミド社製）の５質量％水溶液を２７ｍｌ、フタル酸二アンモニウム塩の２０質量％水溶液を１３５ｍｌ、総量１００００ｇになるように水を加え、ｐＨが７．５になるようにＮａＯＨで調整して中間層塗布液とし、９．１ｍｌ／ｍ^２になるようにコーティングダイへ送液した。
塗布液の粘度はＢ型粘度計４０℃（Ｎｏ．１ローター、６０ｒｐｍ）で５８［ｍＰａ・ｓ］であった。
【０４４２】
３）表面保護層第１層塗布液の調製
イナートゼラチン６４ｇを水に溶解し、メチルメタクリレート／スチレン／ブチルアクリレート／ヒドロキシエチルメタクリレート／アクリル酸共重合体（共重合重量比６４／９／２０／５／２）ラテックス１９．０質量％液１１２ｇ、フタル酸の１５質量％メタノール溶液を３０ｍｌ、４−メチルフタル酸の１０質量％水溶液２３ｍｌ、０．５ｍｏｌ／Ｌ濃度の硫酸を２８ｍｌ、エアロゾールＯＴ（アメリカンサイアナミド社製）の５質量％水溶液を５ｍｌ、フェノキシエタノール０．５ｇ、ベンゾイソチアゾリノン０．１ｇを加え、総量７５０ｇになるように水を加えて塗布液とし、４質量％のクロムみょうばん２６ｍｌを塗布直前にスタチックミキサーで混合したものを１８．６ｍｌ／ｍ^２になるようにコーティングダイへ送液した。
塗布液の粘度はＢ型粘度計４０℃（Ｎｏ．１ローター、６０ｒｐｍ）で２０［ｍＰａ・ｓ］であった。
【０４４３】
４）表面保護層第２層塗布液の調製
イナートゼラチン８０ｇを水に溶解し、メチルメタクリレート／スチレン／ブチルアクリレート／ヒドロキシエチルメタクリレート／アクリル酸共重合体（共重合重量比６４／９／２０／５／２）ラテックス２７．５質量％液１０２ｇ、フッ素系界面活性剤（Ｆ−１）の２質量％溶液を５．４ｍｌ、フッ素系界面活性剤（Ｆ−２）の２質量％水溶液を５．４ｍｌ、エアロゾールＯＴ（アメリカンサイアナミド社製）の５質量％溶液を２３ｍｌ、ポリメチルメタクリレート微粒子（平均粒径０．７μｍ）４ｇ、ポリメチルメタクリレート微粒子（平均粒径４．５μｍ）２１ｇ、４−メチルフタル酸１．６ｇ、フタル酸４．８ｇ、０．５ｍｏｌ／Ｌ濃度の硫酸４４ｍｌ、ベンゾイソチアゾリノン１０ｍｇに総量６５０ｇとなるよう水を添加して、４質量％のクロムみょうばんと０．６７質量％のフタル酸を含有する水溶液４４５ｍｌを塗布直前にスタチックミキサーで混合したものを表面保護層第２層塗布液とし、８．３ｍｌ／ｍ^２になるようにコーティングダイへ送液した。
塗布液の粘度はＢ型粘度計４０℃（Ｎｏ．１ローター，６０ｒｐｍ）で１９［ｍＰａ・ｓ］であった。
【０４４４】
３−３．塗布試料の作製
１）熱現像感光材料の作製
バック面と反対の面に下塗り面から画像形成層、中間層、表面保護層第１層、表面保護層第２層の順番でスライドビード塗布方式にて同時重層塗布し、熱現像感光材料の試料を作成した。このとき、画像形成層と中間層は３１℃に、表面保護層第１層は３６℃に、表面保護層第２層は３７℃に温度調整した。
【０４４５】
画像形成層の各化合物の塗布量（ｇ／ｍ^２）は以下の通りである。
脂肪酸銀 ５．２７
顔料（Ｃ．Ｉ．Ｐｉｇｍｅｎｔ Ｂｌｕｅ ６０） ０．０３６
ポリハロゲン化合物−１ ０．０９
ポリハロゲン化合物−２ ０．１４
フタラジン化合物−１ ０．１８
ＳＢＲラテックス ９．４３
還元剤 （量と種類は表１に記載）
水素結合性化合物−１ ０．２８
現像促進剤−１ ０．０２５
現像促進剤−２ ０．０２０
メルカプト化合物−１ ０．００２
メルカプト化合物−２ ０．００６
発色剤（本発明の化合物または比較化合物） （量と種類は表１に記載）
ハロゲン化銀（Ａｇとして） ０．０４６
【０４４６】
塗布乾燥条件は以下のとおりである。
支持体は塗布前にイオン風にて除電し、塗布はスピード１６０ｍ／ｍｉｎで行った。塗布乾燥条件は各試料に対して以下の範囲で調整し、もっとも安定した面状が得られる条件に設定した。
コーティングダイ先端と支持体との間隙を０．１０〜０．３０ｍｍ。
減圧室の圧力を大気圧に対して１９６〜８８２Ｐａ低く設定。
引き続くチリングゾーンにて、乾球温度１０〜２０℃の風にて塗布液を冷却。
無接触型搬送して、つるまき式無接触型乾燥装置にて、乾球温度２３〜４５℃、湿球温度１５〜２１℃の乾燥風で乾燥。
乾燥後、２５℃で湿度４０〜６０％ＲＨで調湿。
引き続き、膜面を７０〜９０℃になるように加熱し、加熱後、膜面を２５℃まで冷却した。
【０４４７】
作製された熱現像感光材料のマット度はベック平滑度で画像形成層面側が５５０秒、バック面が１３０秒であった。また、画像形成層面側の膜面のｐＨを測定したところ６．０であった。
【０４４８】
以下に本発明の実施例で用いた化合物の化学構造を示す。
【０４４９】
【化４５】

【０４５０】
【化４６】

【０４５１】
【化４７】

【０４５２】
【化４８】

【０４５３】
【化４９】

【０４５４】
【化５０】

【０４５５】
（写真性能の評価）
得られた試料は半切サイズに切断し、２５℃５０％ＲＨの環境下で以下の包装材料に包装し、２週間常温下で保管した後、以下の評価を行った。
（包装材料）
ＰＥＴ １０μｍ／ＰＥ １２μｍ／アルミ箔９μｍ／Ｎｙ １５μｍ／カーボン３質量％を含むポリエチレン５０μｍ；
酸素透過率：０．０２ｍｌ／ａｔｍ・ｍ^２・２５℃・ｄａｙ、
水分透過率：０．１０ｇ／ａｔｍ・ｍ^２・２５℃・ｄａｙ。
【０４５６】
試料は富士メディカルドライレーザーイメージャーＤＲＹＰＩＸ７０００の露光部に半導体レーザー光源として日亜化学工業のＮＬＨＶ３０００Ｅ半導体レーザーを実装し、ビーム径を１００μｍに絞った。レーザー光の感光材料面での照度を０および１ｍＷ／ｍｍ^２〜１０００ｍＷ／ｍｍ^２の間で変化させて１０^−６秒で露光を行った。レーザー光の発振波長は４０５ｎｍであった。熱現像は３枚のパネルヒーターを１０７℃−１２１℃−１２１℃に設定し、搬送速度を速めて合計８秒になるように現像した。
【０４５７】
３）写真性能の評価
＜色相角ｈａｂの評価＞
色相角は濃度１．０においてＪＩＳ Ｚ８７２９規格に規定されたａ^＊ｂ^＊座標から得られる角度で、医療用感材としては１８０°から２７０°の範囲が好ましく、
２１０°から２６０°の範囲がより好ましい。特に好ましくは２４５°から２５５°の範囲である。
【０４５８】
＜暗熱画像保存性の評価＞
強制的環境条件下での画像色調の変化を調べた。熱現像したサンプルを暗所で４０℃、４０％ＲＨの環境に５日間保存して、濃度１．０の画像についてその前後での色調変化を観察するために、経時前後の濃度１．０における色相角ｈａｂを測定し，経時前との角度差（△色相角）で表し、その差が小さいほうが、色調変化が小さく好ましい性能である。
【０４５９】
＜プリントアウト性の色調評価＞
プリントアウト性を強制的評価条件下で評価した。
評価条件は、熱現像したサンプルをシャーカステン（２５℃６０％ＲＨ環境で照度７０００ルクス）に５日間かけて、濃度１．０の画像についてその前後での色調変化を観察するために、経時前後の濃度１．０における色相角ｈａｂを測定し，経時前との角度差（△色相角）で表し、その差が小さいほうが、色調変化が小さく好ましい性能である
【０４６０】
【表１】

【０４６１】
得られた結果を表１に示した。
本発明の発色剤を用いることで、暗所、光照射時（シャーカステン経時）共に△色相角が小さくなり、色調変化が小さくなった。
特に熱現像感光材料−１０〜１２が好ましい結果を与えた。
【０４６２】
実施例２
実施例１の試料Ｎｏ．１０においてて、現像促進剤―１および現像促進剤―２の代わりに、表２に示すように現像促進剤を変更して試料―２０〜２４を作成した。
これらの促進剤は現像促進剤―１と同様の方法で分散物を調製し添加した。
【０４６３】
【表２】

【０４６４】
実施例１と同様に評価した結果を表２に示した。
表２の結果から明らかなように、現像促進剤の種類を変更しても、暗所、光照射時（シャーカステン経時）の色調変化がない優れた熱現像感光材料を得ることができた。
特に熱現像感光材料−２０，２３，２４が好ましい結果を与えた。
【０４６５】
実施例３
実施例１で用いた試料１〜４において、還元剤―１の代わりに一般式Ｒで表される化合物Ｒ−１７、ポリハロゲン化合物―１の代わりに一般式（Ｈ）で表される化合物Ｈ−１７を用いて、その他は実施例１と同様にして試料を作成した。実施例１と同様に評価した結果、実施例１と同様に本発明の効果が得られた。
【０４６６】
【発明の効果】
本発明によれば、画像色調および画像保存性が改良された熱現像感光材料が提供される。[0001]
BACKGROUND OF THE INVENTION
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a photothermographic material having improved image tone and image storability, and more particularly to a photothermographic material having a small increase in fog and a small change in color tone when exposed to light such as Schaukasten for a long time. Is.
[0002]
[Prior art]
In recent years, in the medical field, reduction of waste processing liquid has been strongly desired from the viewpoint of environmental protection and space saving. Therefore, photosensitive thermal development for medical diagnosis and photographic technology that can be efficiently exposed by a laser image setter or laser imager and can form a clear black image with high resolution and sharpness. There is a need for technology relating to photographic materials. These photosensitive heat-developable photographic materials eliminate the use of solution processing chemicals and can provide customers with a heat-development processing system that is simpler and does not impair the environment.
[0003]
Although there is a similar requirement in the field of general image forming materials, medical images are required to have high image quality with excellent sharpness and graininess because they are required to be finely drawn, and are cooled from the viewpoint of ease of diagnosis. There is a feature that a black tone image is preferred. At present, various hard copy systems using pigments and dyes such as inkjet printers and electrophotography are distributed as general image forming systems. However, there is no satisfactory output system for medical images.
[0004]
On the other hand, thermal image forming systems using organic silver salts are known (see, for example, Patent Documents 1 and 2 and Non-Patent Document 1). In particular, the photothermographic material generally contains a catalytically active amount of a photocatalyst (eg, silver halide), a reducing agent, a reducible silver salt (eg, an organic silver salt), and a color tone that controls the color tone of silver if necessary. And a photosensitive layer dispersed in a binder matrix. The photothermographic material is heated to a high temperature (for example, 80 ° C. or higher) after image exposure, and is blackened by an oxidation-reduction reaction between silver halide or a reducible silver salt (functioning as an oxidizing agent) and a reducing agent. Form a silver image. The oxidation-reduction reaction is promoted by the catalytic action of the latent image of silver halide generated by exposure. Therefore, a black silver image is formed in the exposure area. Fuji Medical Dry Imager FM-DPL is disclosed as a medical image forming system using a photothermographic material disclosed in many documents including Patent Documents 3 and 4.
[0005]
In manufacturing a thermal image forming system using an organic silver salt, there are a method of manufacturing by solvent coating and a method of manufacturing by coating and drying a coating liquid containing polymer fine particles as a water dispersion as a main binder. Since the latter method does not require a process such as solvent recovery, the manufacturing equipment is simple and it is advantageous for mass production.
[0006]
In any of the manufacturing methods, the biggest problem of the photothermographic material is that the fog is increased by the reactive compound remaining in the photosensitive material after development, or the image color tone is changed and the image is deteriorated. Was that. In order to solve this problem, diligent studies have been conducted, and improvements in thermal developers (see, for example, Patent Documents 5, 6, and 7) and image stabilizers (see, for example, Patent Document 8). Development has been done.
[0007]
It is known to use silver iodide as the photosensitive silver halide (see, for example, Patent Documents 11 and 12).
[0008]
In particular, in medical image recording materials, the problem of image color tone is an extremely important quality because it affects the diagnostic ability, and is a major improvement problem required for photothermographic materials.
[0009]
Many efforts have been made to control the silver tone of a photothermographic material image to a preferred color tone. For example, with respect to a silver carrier that greatly affects the silver color tone, development of a preferable silver carrier (see, for example, Patent Document 9), development of a color tone adjusting agent as a method for controlling the color tone (for example, see Patent Document 10), and other methods. Development of color tone adjustment technology (for example, see Patent Documents 13 to 16) has been performed.
[0010]
However, even with the above-described technology, a sufficiently satisfactory one has not been obtained from the viewpoint of achieving both image color tone and image storability. In particular, in the means for improving the color tone by forming a dye, the light and heat fastness of the dye are not sufficiently strong, so that there is a problem that the color tone changes due to fading over time.
[0011]
[Patent Document 1]
U.S. Pat. No. 3,152,904
[Patent Document 2]
U.S. Pat. No. 3,457,075
[Patent Document 3]
US Patent 2,910,377
[Patent Document 4]
Japanese Patent Publication No.43-4924
[Patent Document 5]
JP 2001-188314 A
[Patent Document 6]
JP 2002-365758 A
[Patent Document 7]
JP 2001-209145 A
[Patent Document 8]
JP 2001-281793 A
[Patent Document 9]
JP-A-9-149249, etc.
[Patent Document 10]
JP 2002-169249 A
[Patent Document 11]
US-6143488
[Patent Document 12]
EP092295
[Patent Document 13]
JP 2000-241927 A
[Patent Document 14]
JP 2001-330923 A
[Patent Document 15]
JP 2001-330925 A
[Patent Document 16]
JP 2002-49123 A
[Non-Patent Document 1]
D. H. “Thermally Processed Silver Systems” by Kolsterboer (Imaging Processes and Materials), 8th edition, Sturge (Australia) (Walworth, A. Shepp, Chapter 9, 279, 1989)
[0012]
[Problems to be solved by the invention]
SUMMARY OF THE INVENTION Accordingly, an object of the present invention is to provide a photothermographic material which forms an image having a preferable color tone and at the same time has a small increase in fog and a change in image color tone with respect to long-term storage in a light place and a dark place.
[0013]
[Means for Solving the Problems]
The object of the present invention has been achieved by the following photothermographic materials.
<1> A photothermographic material comprising photosensitive silver halide, a non-photosensitive organic silver salt, a reducing agent, a binder, and a color former that develops color by heat development on the same surface of a support, A photothermographic material, wherein the silver iodide content of the light-sensitive silver halide is 80 mol% or more, and the dye produced by the color former can form a hydrogen bond in the molecule.
<2> The photothermographic material according to <1>, wherein the dye produced by the color former has a maximum absorption in a wavelength region of 350 nm to 500 nm or 600 nm to 700 nm.
<3> The photothermographic material according to <1> or <2>, wherein the dye produced by the color former has a maximum absorption in a wavelength region of 350 nm to 500 nm.
<4> The photothermographic material according to any one of <1> to <3>, wherein the color former is a compound represented by the following formula (Ia) or (Ib).
[0014]
[Chemical Formula 3]

[0015]
[In the formula (Ia) or (Ib), R₁₁~ R₁₅Represents a hydrogen atom or a substituent which can be substituted on the benzene ring, X represents an aryl group, a heterocyclic group or an active methine group;₁₁~ R₁₅And at least one of X has at least one hydrogen-bonding substituent. ]
<5> In the formula (Ia) or (Ib), R₁₂The photothermographic material according to <4>, wherein is a secondary or tertiary alkyl group.
<6> The color former represented by the formula (Ia) or (Ib) is represented by the following formula (IIa) or (IIb), according to <4> or <5> Photothermographic material.
[0016]
[Formula 4]

[0017]
[In the formula (IIa) or (IIb), R₂₁~ R₂₇Represents a hydrogen atom or a substituent that can be substituted on the benzene ring. Y₂₁, Y₂₂Represents a hydrogen atom or a substituent that can be substituted on the benzene ring, at least one of which is a hydroxy group or an amino group, and R₂₁~ R₂₇, Y₂₁And Y₂₂At least one of has at least one hydrogen-bonding substituent. ]
<7> In the formula (IIa) or (IIb), R₂₂Is a secondary or tertiary alkyl group and R₂₅Or R₂₆The photothermographic material according to <6>, wherein at least one of the above is a hydrogen bonding substituent.
<8> The thermal development according to any one of <1> to <7>, wherein the dye produced from the color former can form a 5- to 7-membered ring by hydrogen bonding in the molecule. Photosensitive material.
<9> The photothermographic material according to any one of <1> to <8>, wherein the photosensitive silver halide has a silver iodide content of 80 mol% or more.
<10> The photothermographic material according to any one of <1> to <9>, wherein the photosensitive silver halide has a silver iodide content of 90 mol% or more.
<11> The photothermographic material according to any one of <1> to <10>, which contains a development accelerator.
<12> The photothermographic material according to any one of <1> to <11>, which is subjected to scanning exposure with a laser beam.
<13> The photothermographic material according to <12>, wherein the laser beam is a semiconductor laser.
<14> The photothermographic material according to <13>, wherein the semiconductor laser is a blue semiconductor laser.
<15> The photothermographic material according to any one of <1> to <14>, wherein the photothermographic material is heat-developed within 10 seconds.
[0018]
DETAILED DESCRIPTION OF THE INVENTION
The present invention is described in detail below.
(Description of color former that can develop color by heat development)
The color former that can develop color by heat development of the present invention means that when heat development is performed, a dye is not substantially formed in the non-exposed non-image area, and a dye is formed in the image area where developed silver is formed. Refers to the compound. This compound may be a compound that develops color alone, or may form a dye by a coupling reaction, elimination reaction, or other reaction of two or more compounds.
[0019]
In many cases, a silver image produced by heat development has a magenta component more than a neutral color. Therefore, it is preferable that the dye formed by the color former of the present invention has absorption in the yellow or cyan region. In terms of the wavelength range of the generated dye, a compound having 70% or more of absorption in a yellow region of 350 nm to 500 nm or a cyan region of 600 nm to 700 nm is preferable. In particular, a compound having 70% or more in the 350 nm to 500 nm region is preferable, and a compound having 70% or more absorption in the 380 nm to 460 nm region is more preferable.
[0020]
Improving the efficiency of color development, that is, effective color development with the addition of a smaller amount of color former is preferable from the viewpoint of the cost of the light-sensitive material because the amount of material used can be reduced. More preferred.
[0021]
The dye produced from the color former of the present invention is characterized in that it can form hydrogen bonds in the molecule. A hydrogen bond refers to a bond in which a hydrogen atom is between two negative atoms and appears to be divalent. Examples of preferred hydrogen bonds include OH ... O, NH ... O, OH ... N, NH ... N, NH ... Cl, N-. H ... F, OH ... Cl, etc. are mentioned.
[0022]
Examples of the O—H include, for example, primary, secondary, tertiary alcohols, phenols, enols, N-hydroxycarbamoyls, carboxylic acids, N-hydroxyureidos, hydroxyaminos, —NHCO— groups. And those contained in the —N═C (OH) — group which is a tautomer.
[0023]
The above NH is, for example, primary or secondary aminos, carbamoyls, acylaminos, sulfonamide groups, sulfamoyls, ureido groups, carbamates, semicarbazides, hydrazinos, imides, hydroxyaminos, etc. Are included.
[0024]
Examples of the above O include those contained in heterocycles, acyls, alkoxycarbonyls, carbamoyls, carboxylic acids, oxalyls, alcohols, phenols, ethers, acylaminos, ureidos, nitro groups and the like. Can be mentioned.
[0025]
Examples of N include nitrogen-containing heterocycles, N-hydroxycarbamoyls, cyano groups, amino groups, (alkyl, aryl, or heterocyclic) aminos, imides, hydrazino groups, hydroxyamino groups, imino groups, and the like. Are included.
[0026]
The hydrogen bond is preferably a case where a 5- to 7-membered ring is formed by forming a hydrogen bond, and more preferably a 5- or 6-membered ring is formed.
[0027]
Preferred color formers in the present invention are compounds represented by the following formula (Ia) or (Ib).
[0028]
[Chemical formula 5]

[0029]
In the formula (Ia) or (Ib), R₁₁~ R₁₅Represents a substituent which can be substituted on a hydrogen atom or a benzene ring, and R₁₁~ R₁₅And at least one of X has at least one hydrogen-bonding substituent.
[0030]
R₁₁~ R₁₅Represents a hydrogen atom or a substituent that can be substituted on the benzene ring. Examples of the substituent that can be substituted on the benzene ring mentioned here include a halogen atom (a fluorine atom, a chloro atom, a bromine atom, or an iodine atom), an alkyl group (a linear, branched, or cyclic alkyl group, a bicycloalkyl group, Active methine group), alkenyl group, alkynyl group, aryl group, heterocyclic group (regardless of the position of substitution), acyl group, alkoxycarbonyl group, aryloxycarbonyl group, heterocyclic oxycarbonyl group, carbamoyl group, N -Hydroxycarbamoyl group, N-acylcarbamoyl group, N-sulfonylcarbamoyl group, N-carbamoylcarbamoyl group, thiocarbamoyl group, N-sulfamoylcarbamoyl group, carbazoyl group, carboxy group or a salt thereof, oxalyl group, oxamoyl group, Cyano group, Carboximidoyl group (Ca bonymidyl group), formyl group, hydroxy group, alkoxy group (including groups containing repeating ethyleneoxy group or propyleneoxy group units), aryloxy group, heterocyclic oxy group, acyloxy group, (alkoxy or aryloxy) carbonyloxy group , Carbamoyloxy group, sulfonyloxy group, amino group, (alkyl, aryl, or heterocyclic) amino group, acylamino group, sulfonamide group, ureido group, thioureido group, N-hydroxyureido group, imide group, (alkoxy or aryl) Oxy) carbonylamino group, sulfamoylamino group, semicarbazide group, thiosemicarbazide group, hydrazino group, ammonio group, oxamoylamino group, N- (alkyl or aryl) sulfonylureido , N-acylureido group, N-acylsulfamoylamino group, hydroxyamino group, nitro group, quaternized heterocyclic group containing nitrogen atom (for example, pyridinio group, imidazolio group, quinolinio group, isoquinolinio group), isocyano Group, imino group, mercapto group, (alkyl, aryl, or heterocyclic) thio group, (alkyl, aryl, or heterocyclic) dithio group, (alkyl or aryl) sulfonyl group, (alkyl or aryl) sulfinyl group, sulfo group Or a salt thereof, a sulfamoyl group, an N-acylsulfamoyl group, an N-sulfonylsulfamoyl group or a salt thereof, a phosphino group, a phosphinyl group, a phosphinyloxy group, a phosphinylamino group, a silyl group, and the like. . Here, the active methine group means a methine group substituted with two electron-withdrawing groups, and the electron-withdrawing group here means an acyl group, an alkoxycarbonyl group, an aryloxycarbonyl group, a carbamoyl group, An alkylsulfonyl group, an arylsulfonyl group, a sulfamoyl group, a trifluoromethyl group, a cyano group, a nitro group, or a carbonimidoyl group (Carbonimidoyl group) is meant. Here, the two electron withdrawing groups may be bonded to each other to form a cyclic structure. The salt means a cation such as alkali metal, alkaline earth metal or heavy metal, or an organic cation such as ammonium ion or phosphonium ion. These substituents may be further substituted with these substituents.
[0031]
In the formula (Ia) or (Ib), R₁₂Is preferably an alkyl group, more preferably a secondary or tertiary alkyl group, and particularly preferably a tertiary alkyl group.
In the formula (Ia) or (Ib), R₁₁, R₁₃~ R₁₅Is preferably a hydrogen atom, an alkyl group or an aryl group, more preferably a hydrogen atom or an alkyl group.
[0032]
In the formula (Ia) or (Ib), X is a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, preferably 6 to 20 carbon atoms, and a substituted or unsubstituted carbon group having 1 to 30 carbon atoms, preferably 1 to 20 carbon atoms. , Aromatic or non-aromatic, saturated or unsaturated heterocyclic group, active methine group (active methine group means a methine group substituted with two electron-withdrawing groups, Group is a group having a positive Hammett substituent constant σp value, for example, an acyl group, alkoxycarbonyl group, aryloxycarbonyl group, carbamoyl group, alkylsulfonyl group, arylsulfonyl group, sulfamoyl group, trifluoromethyl group , A cyano group, a nitro group, a carbonimidoyl group, etc. Here, two electron withdrawing groups are bonded to each other to form a cyclic structure. May take.) Represents the.
[0033]
In the formula (Ia) or (Ib), X preferably has two or more substituents, and the substituent is the aforementioned R₁₁~ R₁₅It is synonymous with the substituent demonstrated by. Here, it is preferable that these substituents form a hydrogen bond and form a hydrogen bond with each other in the structure of the produced dye. Preferred examples of such a substituent include a halogen atom (fluorine atom, chloro atom, bromine atom, or iodine atom), acyl group, alkoxy or aryloxycarbonyl group, carbamoyl group, carboxy group or salt thereof, oxalyl group, oxamoyl group Group, formyl group, hydroxy group, acyloxy group, amino group, (alkyl, aryl, or heterocyclic) amino group, acylamino group, sulfonamide group, ureido group, imide group, (alkoxy or aryloxy) carbonylamino group, nitro Group, imino group, sulfamoyl group and the like.
[0034]
In the formula (Ia) or (Ib), X is preferably a substituted aryl group, a substituted aromatic heterocyclic group or an active methine group, particularly preferably a substituted aryl group.
[0035]
The structure of the color former of the present invention is more preferably one represented by the following formula (IIa) or (IIb).
[0036]
[Chemical 6]

[0037]
In the formula (IIa) or (IIb), R₂₁~ R₂₇Has a substituent which can be substituted on a hydrogen atom or a benzene ring, and Y₂₁And Y₂₂Represents a hydrogen atom or a substituent that can be substituted on the benzene ring, at least one of which is a hydroxy group or an amino group, and R₂₁~ R₂₇, Y₂₁And Y₂₂At least one of has at least one hydrogen-bonding substituent. The substituent here is R in the above formula (Ia) or (Ib).₁₁~ R₁₅It is synonymous with the substituent represented by these.
[0038]
R₂₂Is preferably R in the formula (Ia) or (Ib).₁₂The secondary range or the tertiary alkyl group is preferable.
[0039]
R₂₅Or R₂₆It is preferable that at least one of these is a hydrogen bonding substituent. This hydrogen bonding substituent becomes a hydrogen donor or a hydrogen acceptor depending on the structure of the dye. Preferred substituents in this case are, for example, a halogen atom (fluorine atom, chloro atom, bromine atom, or iodine atom), acyl group, alkoxy or aryloxycarbonyl group, carbamoyl group, carboxy group or a salt thereof, oxalyl group, oxamoyl group, Formyl group, hydroxy group, acyloxy group, amino group, (alkyl, aryl, or heterocyclic) amino group, acylamino group, sulfonamide group, ureido group, imide group, (alkoxy or aryloxy) carbonylamino group, nitro group, Examples include imino group and sulfamoyl group.
[0040]
Y₂₁, Y₂₂Represents a hydrogen atom or a substituent that can be substituted on the benzene ring, at least one of which is a hydroxy group or an (unsubstituted, alkyl, aryl, or heterocyclic) amino group, more preferably a hydroxy group.
[0041]
The structure of the dye produced from the color former represented by the formula (Ia) or (Ib) or the formula (IIa) or (IIb) is shown below. Y in the following dye structure₂₁Or Y₂₂When a keto-enol tautomer exists as in the case where is a hydroxy group, it is sufficient that an intramolecular hydrogen bond can be formed in any one of the tautomers.
[0042]
[Chemical 7]

[0043]
The color former of the present invention may incorporate an adsorptive group that can adsorb to silver halide. Examples of such adsorbing groups include alkylthio groups, arylthio groups, thiourea groups, thioamide groups, mercaptoheterocyclic groups, triazole groups and the like, U.S. Pat. Nos. 4,385,108, 4,459,347, -195233, 59-200231, 59-201045, 59-201046, 59-201047, 59-201048, 59-201049, JP-A-61-170733, 61 -270744, 62-948, 63-234244, 63-234245, 63-234246, and the like. Further, these adsorbing groups to silver halide may be made into a precursor. Examples of such a precursor include groups described in JP-A-2-285344.
[0044]
The color former of the present invention may be incorporated with a ballast group or polymer commonly used in an immobile photographic additive such as a coupler. A ballast group is a group having a carbon number of 8 or more and relatively inert to photographic properties, such as an alkyl group, an aralkyl group, an alkoxy group, a phenyl group, an alkylphenyl group, a phenoxy group, and an alkylphenoxy group. You can choose from the inside. Examples of the polymer include those described in JP-A-1-100530.
[0045]
The molecular weight of the color former of the present invention is preferably 200 to 10000, more preferably 300 to 2000, and particularly preferably 400 to 1000.
[0046]
Although the specific example of the preferable compound of this invention is given to the following, this invention is not limited to these compounds.
[0047]
[Chemical 8]

[0048]
[Chemical 9]

[0049]
[Chemical Formula 10]

[0050]
Embedded image

[0051]
Embedded image

[0052]
The color former of the present invention may be contained in the coating solution by any method such as a solution form, an emulsified dispersion form, or a solid fine particle dispersion form, and may be contained in the photosensitive material. Well-known emulsification dispersion methods include dissolving oil using an oil such as dibutyl phthalate, tricresyl phosphate, glyceryl triacetate or diethyl phthalate, or an auxiliary solvent such as ethyl acetate or cyclohexanone, and mechanically emulsifying the dispersion. The method of producing is mentioned.
[0053]
Further, as the solid fine particle dispersion method, the color former powder is dispersed in an appropriate solvent such as water by a ball mill, a colloid mill, a vibration ball mill, a sand mill, a jet mill, a roller mill or an ultrasonic wave to create a solid dispersion. A method is mentioned. In this case, a protective colloid (for example, polyvinyl alcohol) or a surfactant (for example, an anionic surfactant such as sodium triisopropylnaphthalenesulfonate (a mixture of three isopropyl groups having different substitution positions)) may be used. Good. In the mills, beads such as zirconia are usually used as a dispersion medium, and Zr and the like eluted from these beads may be mixed in the dispersion. Although it depends on the dispersion conditions, it is usually in the range of 1 ppm to 1000 ppm. If the Zr content in the light-sensitive material is 0.5 mg or less per 1 g of silver, there is no practical problem. The aqueous dispersion preferably contains a preservative (for example, benzoisothiazolinone sodium salt).
Particularly preferred is a solid particle dispersion method of a color former, which is preferably added as fine particles having an average particle size of 0.01 μm to 10 μm, preferably 0.05 μm to 5 μm, more preferably 0.1 μm to 2 μm. In the present application, it is preferable to use other solid dispersions dispersed in a particle size within this range.
[0054]
In the present invention, the addition amount of the color former is 0.1 mg / m.²~ 3g / m²Is preferable, more preferably 1 mg / m²~ 1g / m², Particularly preferably 2 mg / m²~ 0.5g / m²It is.
[0055]
(Description of non-photosensitive organic silver salt)
1) Composition
Organic silver salts that can be used in the present invention are relatively stable to light, but when heated to 80 ° C. or higher in the presence of exposed photosensitive silver halide and reducing agent. It is a silver salt that functions as a silver ion supplier and forms a silver image. The organic silver salt may be any organic substance that can supply silver ions that can be reduced by a reducing agent. Regarding such non-photosensitive organic silver salt, paragraph numbers 0048 to 0049 of JP-A-10-62899, page 18 line 24 to page 19 line 37 of European Patent Publication No. 0803764A1, European Patent Publication. No. 0968212A1, JP-A-11-349591, JP-A-2000-7683, JP-A-2000-72711, and the like. Silver salts of organic acids, particularly silver salts of long-chain aliphatic carboxylic acids (having 10 to 30, preferably 15 to 28 carbon atoms) are preferred. Preferable examples of the fatty acid silver salt include silver lignocerate, silver behenate, silver arachidate, silver stearate, silver oleate, silver laurate, silver caproate, silver myristate, silver palmitate, silver erucate and the like. Including a mixture of In the present invention, among these fatty acid silvers, the silver behenate content is preferably 50 mol% to 100 mol%, more preferably 85 mol% to 100 mol%, still more preferably 95 mol% to 100 mol%. The following fatty acid silver is preferably used. Furthermore, it is preferable to use fatty acid silver having a silver erucate content of 2 mol% or less, more preferably 1 mol% or less, and still more preferably 0.1 mol% or less.
[0056]
Moreover, it is preferable that silver stearate content rate is 1 mol% or less. By setting the silver stearate content to 1 mol% or less, a silver salt of an organic acid having a low Dmin, high sensitivity and excellent image storage stability can be obtained. As said silver stearate content rate, 0.5 mol% or less is preferable and it is especially preferable not to contain substantially.
[0057]
Furthermore, when silver arachidate is included as the silver salt of the organic acid, the silver arachidate content is 6 mol% or less to obtain a low Dmin and an organic acid silver salt excellent in image storability. It is preferable at a point and it is still more preferable that it is 3 mol% or less.
[0058]
2) Shape
The shape of the organic silver salt that can be used in the present invention is not particularly limited, and may be any of a needle shape, a rod shape, a flat plate shape, and a flake shape.
In the present invention, scaly organic silver salts are preferred. In addition, short needle-like, rectangular parallelepiped, cubic or potato-like amorphous particles having a major axis / uniaxial length ratio of 5 or less are also preferably used. These organic silver particles have a feature that there is less fog at the time of thermal development than long needle-like particles having a major axis / uniaxial length ratio exceeding 5. In particular, particles having a major axis / uniaxial ratio of 3 or less are preferable because the mechanical stability of the coating film is improved. In the present specification, the scaly organic silver salt is defined as follows. The organic acid silver salt was observed with an electron microscope, the shape of the organic acid silver salt particle was approximated to a rectangular parallelepiped, and the sides of the rectangular parallelepiped were designated a, b, and c from the shortest side (c was the same as b). Then, the shorter numerical values a and b are calculated, and x is obtained as follows.
x = b / a
[0059]
In this way, x is obtained for about 200 particles, and when the average value x (average) is obtained, particles satisfying the relationship of x (average) ≧ 1.5 are defined as flakes. Preferably, 30 ≧ x (average) ≧ 1.5, more preferably 15 ≧ x (average) ≧ 1.5. Incidentally, the needle shape is 1 ≦ x (average) <1.5.
[0060]
In the flake shaped particle, a can be regarded as a thickness of a tabular particle having a main plane with b and c as sides. The average of a is preferably 0.01 μm or more and 0.3 μm or less, and more preferably 0.1 μm or more and 0.23 μm or less. The average c / b is preferably 1 or more and 9 or less, more preferably 1 or more and 6 or less, still more preferably 1 or more and 4 or less, and most preferably 1 or more and 3 or less.
[0061]
By setting the equivalent sphere diameter to 0.05 μm or more and 1 μm or less, aggregation is hardly caused in the photosensitive material, and image storability is improved. The sphere equivalent diameter is preferably 0.1 μm or more and 1 μm or less. In the present invention, the method for measuring the equivalent sphere diameter is obtained by directly photographing a sample using an electron microscope and then image-processing the negative.
In the flake shaped particles, the spherical equivalent diameter / a of the particles is defined as the aspect ratio. The aspect ratio of the flake shaped particles is preferably 1.1 or more and 30 or less, more preferably 1.1 or more and 15 or less, from the viewpoint of preventing aggregation in the photosensitive material and improving the image storage stability. .
[0062]
The particle size distribution of the organic silver salt is preferably monodispersed. Monodispersion is preferably 100% or less, more preferably 80% or less, and even more preferably 50% of the value obtained by dividing the standard deviation of the lengths of the short and long axes by the short and long axes. It is as follows. The method for measuring the shape of the organic silver salt can be determined from a transmission electron microscope image of the organic silver salt dispersion. As another method for measuring monodispersity, there is a method for obtaining the standard deviation of the volume weighted average diameter of the organic silver salt, and the percentage (variation coefficient) of the value divided by the volume weighted average diameter is preferably 100% or less, more Preferably it is 80% or less, More preferably, it is 50% or less. As a measuring method, for example, it is obtained from the particle size (volume weighted average diameter) obtained by irradiating an organic silver salt dispersed in a liquid with laser light and obtaining an autocorrelation function with respect to the temporal change of the fluctuation of the scattered light. Can do.
[0063]
3) Preparation
Known methods and the like can be applied to the production and dispersion method of the organic acid silver used in the present invention. For example, the above-mentioned JP-A-10-62899, European Patent Publication No. 0803763A1, European Patent Publication No. 0968212A1, JP-A-11-349591, JP-A-2000-7683, JP-A-2000-72711, JP-A-2001-163889, 2001-163890, 2001-163828, 2001-33907, 2001-188313, 2001-83651, 2002-6442, 2002-49117, 2002-31870, 2002-107868 You can refer to the issue.
[0064]
In addition, when the photosensitive silver salt is allowed to coexist at the time of dispersion of the organic silver salt, the fog is increased and the sensitivity is remarkably lowered. Therefore, it is more preferable that the photosensitive silver salt is not substantially contained at the time of dispersion. In the present invention, the amount of the photosensitive silver salt in the aqueous dispersion to be dispersed is preferably 1 mol% or less, more preferably 0.1 mol% or less with respect to 1 mol of the organic acid silver salt in the liquid. Further, it is more preferable that no positive photosensitive silver salt is added.
[0065]
In the present invention, it is possible to produce a photosensitive material by mixing an organic silver salt aqueous dispersion and a photosensitive silver salt aqueous dispersion, but the mixing ratio of the organic silver salt and the photosensitive silver salt can be selected according to the purpose. The ratio of the photosensitive silver salt to the organic silver salt is preferably in the range of 1 mol% to 30 mol%, more preferably in the range of 2 mol% to 20 mol%, particularly 3 mol% to 15 mol%. Mixing two or more organic silver salt aqueous dispersions and two or more photosensitive silver salt aqueous dispersions when mixing is a method preferably used for adjusting photographic characteristics.
[0066]
4) Amount added
The organic silver salt of the present invention can be used in a desired amount, but the total coated silver amount including silver halide is 0.1 g / m.²~ 5.0 g / m²Is more preferable, and more preferably 0.5 g / m²~ 3.0 g / m²More preferably 0.8 g / m²~ 1.9g / m²It is. In particular, in order to improve image storability, the total coated silver amount is 1.7 g / m.²Or less, more preferably 1.5 g / m²The following is preferable. If the preferred reducing agent of the present invention is used, a sufficient image density can be obtained even with such a low silver amount.
[0067]
(Description of reducing agent)
The photothermographic material of the present invention preferably contains a heat developer which is a reducing agent for the organic silver salt. The reducing agent for the organic silver salt may be any substance (preferably an organic substance) that reduces silver ions to metallic silver. Examples of such reducing agents are described in JP-A No. 11-65021, paragraphs 0043 to 0045, and European Patent Publication No. 0803764A1, page 7, line 34 to page 18, line 12.
[0068]
In the present invention, the reducing agent is preferably a so-called hindered phenol-based reducing agent or bisphenol-based reducing agent having a substituent at the ortho position of the phenolic hydroxyl group, and more preferably a compound represented by the following general formula (R).
[0069]
Formula (R)
Embedded image

[0070]
(In the general formula (R), R¹¹And R¹¹Each independently represents an alkyl group having 1 to 20 carbon atoms. R¹²And R¹²Each independently represents a hydrogen atom or a substituent that can be substituted on the benzene ring. L is a -S- group or -CHR.¹³-Represents a group. R¹³Represents a hydrogen atom or an alkyl group having 1 to 20 carbon atoms. X¹And X¹Each independently represents a hydrogen atom or a group capable of substituting for a benzene ring. )
[0071]
The general formula (R) will be described in detail.
1) R¹¹And R¹¹’
R¹¹And R¹¹Each independently represents a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms, and the substituent of the alkyl group is not particularly limited, but is preferably an aryl group, a hydroxy group, an alkoxy group, an aryloxy group. Group, alkylthio group, arylthio group, acylamino group, sulfonamido group, sulfonyl group, phosphoryl group, acyl group, carbamoyl group, ester group, ureido group, urethane group, halogen atom and the like.
[0072]
2) R¹²And R¹²', X¹And X¹’
R¹²And R¹²Each independently represents a hydrogen atom or a substituent capable of substituting for a benzene ring;¹And X¹'Also independently represents a hydrogen atom or a group capable of substituting for a benzene ring. Preferred examples of each group that can be substituted on the benzene ring include an alkyl group, an aryl group, a halogen atom, an alkoxy group, and an acylamino group.
[0073]
3) L
L is a -S- group or -CHR.¹³-Represents a group. R¹³Represents a hydrogen atom or an alkyl group having 1 to 20 carbon atoms, and the alkyl group may have a substituent. R¹³Specific examples of the unsubstituted alkyl group are methyl group, ethyl group, propyl group, butyl group, heptyl group, undecyl group, isopropyl group, 1-ethylpentyl group, 2,4,4-trimethylpentyl group, cyclohexyl group, Examples include 2,4-dimethyl-3-cyclohexenyl group and 2,4-dimethyl-3-cyclohexenyl group. Examples of substituents for alkyl groups are R¹¹In the same manner as the above substituent, a halogen atom, alkoxy group, alkylthio group, aryloxy group, arylthio group, acylamino group, sulfonamido group, sulfonyl group, phosphoryl group, oxycarbonyl group, carbamoyl group, sulfamoyl group and the like can be mentioned.
[0074]
4) Preferred substituents
R¹¹And R¹¹'Is preferably a primary, secondary or tertiary alkyl group having 1 to 15 carbon atoms, specifically, a methyl group, an isopropyl group, a t-butyl group, a t-amyl group, a t-octyl group or a cyclohexyl group. Group, cyclopentyl group, 1-methylcyclohexyl group, 1-methylcyclopropyl group and the like. R¹¹And R¹¹'Is more preferably an alkyl group having 1 to 4 carbon atoms, and among them, a methyl group, a t-butyl group, a t-amyl group and a 1-methylcyclohexyl group are more preferable, and a methyl group and a t-butyl group are most preferable.
[0075]
R¹²And R¹²'Is preferably an alkyl group having 1 to 20 carbon atoms, specifically, methyl group, ethyl group, propyl group, butyl group, isopropyl group, t-butyl group, t-amyl group, cyclohexyl group, 1-methyl group. Examples include cyclohexyl group, benzyl group, methoxymethyl group, methoxyethyl group and the like. More preferred are methyl group, ethyl group, propyl group, isopropyl group and t-butyl group, and particularly preferred are methyl group and ethyl group.
X¹And X¹'Is preferably a hydrogen atom, a halogen atom or an alkyl group, more preferably a hydrogen atom.
[0076]
L is preferably -CHR¹³-Group.
R¹³Is preferably a hydrogen atom or an alkyl group having 1 to 15 carbon atoms. As the alkyl group, in addition to a chain alkyl group, a cyclic alkyl group is also preferably used. Moreover, what has a C = C bond in these alkyl groups can also be used preferably. Examples of the alkyl group include methyl group, ethyl group, propyl group, isopropyl group, 2,4,4-trimethylpentyl group, cyclohexyl group, 2,4-dimethyl-3-cyclohexenyl group, 3,5-dimethyl-3- A cyclohexenyl group and the like are preferable. R¹³Particularly preferred are a hydrogen atom, a methyl group, an ethyl group, a propyl group, an isopropyl group, and a 2,4-dimethyl-3-cyclohexenyl group.
[0077]
R¹¹, R¹¹′ Is a tertiary alkyl group and R¹², R¹²When ′ is a methyl group, R¹³Is preferably a primary or secondary alkyl group having 1 to 8 carbon atoms (methyl group, ethyl group, propyl group, isopropyl group, 2,4-dimethyl-3-cyclohexenyl group, etc.).
R¹¹, R¹¹′ Is a tertiary alkyl group and R¹², R¹²When ′ is an alkyl group other than a methyl group, R¹³Is preferably a hydrogen atom.
R¹¹, R¹¹When ′ is not a tertiary alkyl group, R¹³Is preferably a hydrogen atom or a secondary alkyl group, more preferably a secondary alkyl group. R¹³Preferred groups as the secondary alkyl group are isopropyl group and 2,4-dimethyl-3-cyclohexenyl group.
The reducing agent is R¹¹, R¹¹', R¹², R¹²'And R¹³Depending on the combination, the heat developability, developed silver color tone and the like are different. Since these can be adjusted by combining two or more reducing agents, it is preferable to use a combination of two or more depending on the purpose.
[0078]
Although the specific example of the reducing agent of this invention including the compound represented by general formula (R) of this invention below is shown, this invention is not limited to these.
[0079]
Embedded image

[0080]
Embedded image

[0081]
Examples of preferable reducing agents of the present invention other than the above are compounds described in JP-A Nos. 2001-188314, 2001-209145, 2001-350235, 2002-156727, and EP1278101A2.
[0082]
In the present invention, the reducing agent is added in an amount of 0.1 g / m.²~ 3.0 g / m²And more preferably 0.2 g / m²~ 1.5g / m²And more preferably 0.3 g / m²~ 1.0 g / m²It is. It is preferably contained in an amount of 5 mol% to 50 mol%, more preferably 8 mol% to 30 mol%, and more preferably 10 mol% to 20 mol%, based on 1 mol of silver on the surface having the image forming layer. More preferably. The reducing agent is preferably contained in the image forming layer.
[0083]
The reducing agent may be contained in the coating solution by any method such as a solution form, an emulsified dispersion form, or a solid fine particle dispersion form, and may be contained in the photosensitive material.
Well-known emulsification dispersion methods include dissolving oil using an oil such as dibutyl phthalate, tricresyl phosphate, glyceryl triacetate or diethyl phthalate, or an auxiliary solvent such as ethyl acetate or cyclohexanone, and mechanically emulsifying the dispersion. The method of producing is mentioned.
[0084]
Further, as the solid fine particle dispersion method, a reducing agent powder is dispersed in an appropriate solvent such as water by a ball mill, a colloid mill, a vibrating ball mill, a sand mill, a jet mill, a roller mill, or an ultrasonic wave to create a solid dispersion. A method is mentioned. In this case, a protective colloid (for example, polyvinyl alcohol) or a surfactant (for example, an anionic surfactant such as sodium triisopropylnaphthalenesulfonate (a mixture of three isopropyl groups having different substitution positions)) may be used. Good. In the mills, beads such as zirconia are usually used as a dispersion medium, and Zr and the like eluted from these beads may be mixed in the dispersion. Although it depends on the dispersion conditions, it is usually in the range of 1 ppm to 1000 ppm. If the Zr content in the light-sensitive material is 0.5 mg or less per 1 g of silver, there is no practical problem.
[0085]
The aqueous dispersion preferably contains a preservative (for example, benzoisothiazolinone sodium salt).
[0086]
Particularly preferred is a solid particle dispersion method of a reducing agent, and it is preferable to add fine particles having an average particle size of 0.01 μm to 10 μm, preferably 0.05 μm to 5 μm, more preferably 0.1 μm to 2 μm. In the present application, it is preferable to use other solid dispersions dispersed in a particle size within this range.
[0087]
(Photosensitive silver halide)
1) Halogen composition
It is important that the photosensitive silver halide used in the present invention has a high silver iodide content of 40 mol% or more and 100 mol% or less. The rest is not particularly limited and can be selected from silver chloride, silver bromide, or organic silver salts such as silver thiocyanate and silver phosphate. Silver bromide and silver chloride are particularly preferred. By using such a silver halide having a high silver iodide content, it is possible to design a preferable photothermographic material in which image storage stability after development processing, in particular, an increase in fog due to light irradiation is remarkably small.
[0088]
Further, the silver iodide content is preferably 80 mol% or more and 100 mol% or less, and particularly preferably 90 mol% or more and 100 mol% or less from the viewpoint of image storage stability against light irradiation after processing.
[0089]
The distribution of the halogen composition in the grains may be uniform, the halogen composition may be changed stepwise, or may be continuously changed. Further, silver halide grains having a core / shell structure can also be preferably used. A preferable structure is a 2- to 5-fold structure, more preferably 2- to 4-fold core / shell particles. A core high silver iodide structure having a high silver iodide content in the core part or a shell high silver iodide structure having a high silver iodide content in the shell part can also be preferably used. Further, a technique of localizing silver chloride or silver bromide as an epitaxial portion on the surface of the grain can be preferably used.
[0090]
2) Particle size
The grain size is particularly important for high silver iodide silver halides used in the present invention. Larger silver halide sizes increase the amount of silver halide coating required to achieve the required maximum density. The present inventor found that the silver halide composition having a high silver iodide content preferably used in the present invention, when the coating amount is large, the development is remarkably suppressed and the sensitivity is lowered, and the density stability with respect to the development time deteriorates. It has been found that the maximum density cannot be obtained in a predetermined development time when the particle size is not less than a certain value. On the other hand, it has been found that if the amount added is limited, the silver iodide has sufficient developability.
[0091]
In this way, when using high silver iodide, the size of the silver halide grains is sufficiently larger than that of conventional silver bromide and silver iodide containing low iodine to achieve a sufficient maximum optical density. It needs to be small. The preferred silver halide grain size is 5 nm or more and 70 nm or less, and more preferably 5 nm or more and 55 nm or less. Especially preferably, it is 10 nm or more and 45 nm or less. The term “particle size” as used herein means an average diameter when converted into a circular image having the same area as the projected area observed with an electron microscope.
[0092]
3) Application amount
The coating amount of such silver halide grains is 0.5 mol% or more and 15 mol% or less, preferably 0.5 mol% or more and 12 mol% or less with respect to 1 mol of silver of the non-photosensitive organic silver salt described later. More preferably, it is 10 mol% or less. It is more preferably 1 mol% or more and 9 mol% or less, and particularly preferably 1 mol% or more and 7 mol% or less. In order to suppress remarkable development suppression by the silver halide having a high silver iodide content found by the present inventor, the selection of the addition amount is extremely important.
[0093]
4) Particle formation method
Methods for forming photosensitive silver halide are well known in the art, for example using the methods described in Research Disclosure No. 17029 of June 1978 and US Pat. No. 3,700,458. Specifically, there is used a method in which a photosensitive silver halide is prepared by adding a silver supply compound and a halogen supply compound to gelatin or another polymer solution, and then mixed with an organic silver salt. Further, the method described in paragraph Nos. 0217 to 0224 of JP-A No. 11-119374, and the method described in JP-A No. 11-352627 and Japanese Patent Application No. 2000-42336 are also preferable.
[0094]
5) Particle shape
Examples of the shape of the silver halide grains in the present invention include cubes, octahedrons, dodecahedrons, tetrahedrons, tabular grains, spherical grains, rod-shaped grains, potato-like grains, etc. Is particularly preferably a dodecahedron or a tetrahedron. The dodecahedron particles referred to here are particles having (001), {1 (-1) 0}, {101} faces, and the tetradecahedral particles are (001), {100}, {101. } A particle having a face. Here, {100} represents a crystal plane group having a plane index equivalent to the (100) plane.
[0095]
The silver iodide of the present invention can have any β phase and γ phase content. The β phase refers to a high silver iodide structure having a hexagonal wurtzite structure, and the γ phase refers to a high silver iodide structure having a cubic zinc blend structure.
[0096]
The average γ phase ratio here is C.I. R. It is determined using the method proposed by Berry. This method is determined based on the peak ratio of the silver iodide β phase (100), (101), (002) and the γ phase (111) in the powder X-ray diffraction method. Reference can be made to Physical Review, Volume 161, Number 3, Page 848-851, 1967.
[0097]
Regarding the method for forming tabular grains of silver iodide, the methods described in JP-A-59-119350 and JP-A-59-119344 are preferably used. The dodecahedron, the tetrahedron, and the octahedron can be prepared with reference to Japanese Patent Application Nos. 2002-081020, 2002-87955, and 2002-91756.
[0098]
The silver halide having a high silver iodide content composition of the present invention can take a complicated form. L. JENKINS et al. J of Photo. Sci. Vol. 28 (1980) p164-Fig1. FIG. Tabular grains as shown in Fig. 1 are also preferably used. Grains with rounded corners of silver halide grains can also be preferably used. The surface index (Miller index) of the outer surface of the photosensitive silver halide grain is not particularly limited, but the ratio of the [100] plane having high spectral sensitization efficiency when the spectral sensitizing dye is adsorbed is high. preferable. The ratio is preferably 50% or more, more preferably 65% or more, and still more preferably 80% or more. The ratio of the Miller index [100] plane is a T.K. based on the adsorption dependency of [111] plane and [100] plane in the adsorption of sensitizing dye. Tani; Imaging Sci. 29, 165 (1985).
[0099]
6) Heavy metal
The photosensitive silver halide grain of the present invention can contain a metal or metal complex of Group 8 to Group 10 of the Periodic Table (showing Groups 1 to 18). As the central metal of the group 8 to group 10 metal or metal complex of the periodic table, rhodium, ruthenium and iridium are preferable. One kind of these metal complexes may be used, or two or more kinds of complexes of the same metal and different metals may be used in combination. The preferred content is 1 x 10 per mole of silver.^-9From mole to 1 × 10^-3A molar range is preferred. These heavy metals and metal complexes and methods for adding them are described in JP-A-7-225449, JP-A-11-65021, paragraphs 0018 to 0024, and JP-A-11-119374, paragraphs 0227 to 0240.
[0100]
In the present invention, silver halide grains in which a hexacyano metal complex is present on the outermost surface of the grains are preferred. As the hexacyano metal complex, [Fe (CN)₆]^4-, [Fe (CN)₆]^3-, [Ru (CN)₆]^4-, [Os (CN)₆]^4-, [Co (CN)₆]^3-, [Rh (CN)₆]^3-, [Ir (CN)₆]^3-, [Cr (CN)₆]^3-, [Re (CN)₆]^3-Etc. In the present invention, a hexacyano Fe complex is preferred.
[0101]
The hexacyano metal complex is present in the form of ions in aqueous solution, so the counter cation is not important, but it is easy to mix with water and is suitable for precipitation of silver halide emulsions. Sodium ion, potassium ion, rubidium It is preferable to use alkali metal ions such as ions, cesium ions, and lithium ions, ammonium ions, and alkylammonium ions (for example, tetramethylammonium ions, tetraethylammonium ions, tetrapropylammonium ions, tetra (n-butyl) ammonium ions).
[0102]
In addition to water, the hexacyano metal complex is miscible with a mixed solvent or gelatin with an appropriate organic solvent miscible with water (for example, alcohols, ethers, glycols, ketones, esters, amides, etc.). Can be added.
[0103]
The amount of hexacyano metal complex added is 1 × 10 5 per mole of silver.^-51 x 10 moles or more^-2Or less, more preferably 1 × 10^-41 x 10 moles or more^-3It is below the mole.
[0104]
In order for the hexacyano metal complex to be present on the outermost surface of the silver halide grain, the chalcogen sensitization of sulfur sensitization, selenium sensitization and tellurium sensitization is completed after the addition of the aqueous silver nitrate solution used for grain formation. It is added directly before the completion of the preparation step before the chemical sensitization step for performing noble metal sensitization such as sensitization and gold sensitization, during the washing step, during the dispersion step, or before the chemical sensitization step. In order to prevent the silver halide fine grains from growing, it is preferable to add the hexacyano metal complex immediately after the grain formation, and it is preferable to add it before the completion of the preparation step.
[0105]
The addition of the hexacyano metal complex may be started after adding 96% by mass of the total amount of silver nitrate to be added to form grains, more preferably starting after adding 98% by mass, The addition of 99% by mass is particularly preferable.
When these hexacyanometal complexes are added after the addition of the aqueous silver nitrate solution just before the completion of grain formation, they can be adsorbed on the outermost surface of the silver halide grains, and most of them form slightly soluble salts with silver ions on the grain surface. To do. This silver salt of hexacyanoiron (II) is a less soluble salt than AgI, so that re-dissolution by fine particles can be prevented and silver halide fine particles having a small particle size can be produced. .
[0106]
Further, metal atoms that can be contained in the silver halide grains used in the present invention (for example, [Fe (CN)₆]^4-), Desalting methods and chemical sensitization methods for silver halide emulsions, paragraph numbers 0046 to 0050 of JP-A No. 11-84574, paragraph numbers of paragraph Nos. 0025 to 0031 of JP-A No. 11-65021, and paragraph number 0242 of JP-A No. 11-119374. ~ 0250.
[0107]
7) Gelatin
Various gelatins can be used as the gelatin contained in the photosensitive silver halide emulsion used in the present invention. In order to maintain a good dispersion state of the photosensitive silver halide emulsion in the organic silver salt-containing coating solution, it is preferable to use low molecular weight gelatin having a molecular weight of 500 to 60,000. These low molecular weight gelatins may be used at the time of particle formation or dispersion after desalting, but are preferably used at the time of dispersion after desalting.
[0108]
8) Chemical sensitization
The photosensitive silver halide used in the present invention may be non-chemically sensitized, but is preferably chemically sensitized by at least one of a chalcogen sensitizing method, a gold sensitizing method, and a reduction sensitizing method. Examples of the chalcogen sensitizing method include a sulfur sensitizing method, a selenium sensitizing method, and a tellurium sensitizing method.
[0109]
In sulfur sensitization, unstable sulfur compounds are used. The unstable sulfur compounds described in Grafkides, Chimie et Physique Photographic (published by Paul Momtel, 1987, 5th edition), Research Disclosure 307, 307105, and the like can be used.
[0110]
Specifically, thiosulfate (for example, hypo), thioureas (for example, diphenylthiourea, triethylthiourea, N-ethyl-N ′-(4-methyl-2-thiazolyl) thiourea, carboxymethyltrimethylthiourea), thioamides (Eg, thioacetamide), rhodanines (eg, diethyl rhodanine, 5-benzylidene-N-ethyl rhodanine), phosphine sulfides (eg, trimethylphosphine sulfide), thiohydantoins, 4-oxo-oxazolidin-2 Known sulfur compounds such as -thiones, disulfides or polysulfides (for example, dimorpholine disulfide, cystine, lenthionine), polythionates, elemental sulfur, and active gelatin can also be used. Particularly preferred are thiosulfates, thioureas and rhodanines.
[0111]
In selenium sensitization, unstable selenium compounds are used, and Japanese Patent Publication Nos. 43-13489, 44-15748, JP-A-4-25832, JP-A-4-109340, JP-A-4-271341, and JP-A-5-40324. No. 5-11385, Japanese Patent Application No. Hei 4-202415, No. 4-330495, No. 4-333030, No. 5-4203, No. 5-4204, No. 5-106977, No. 5-236538. Selenium compounds described in JP-A-5-241642 and JP-A-5-286916 can be used.
[0112]
Specifically, colloidal metal selenium, selenoureas (eg, N, N-dimethylselenourea, trifluoromethylcarbonyl-trimethylselenourea, acetyl-trimethylselenourea), selenoamides (eg, selenoamide, N, N-diethyl) Phenylselenoamide), phosphine selenides (eg, triphenylphosphine selenide, pentafluorophenyl-triphenylphosphine selenide), selenophosphates (eg, tri-p-tolylselenophosphate, tri-n) -Butylselenophosphate), selenoketones (for example, selenobenzophenone), isoselenocyanates, selenocarboxylic acids, selenoesters, diacyl selenides and the like may be used. Furthermore, non-labile selenium compounds described in JP-B Nos. 46-4553 and 52-34492, such as selenite, selenocyanate, selenazoles, and selenides can also be used. In particular, phosphine selenides, selenoureas and selenocyanates are preferred.
[0113]
In tellurium sensitization, an unstable tellurium compound is used, and JP-A-4-224595, JP-A-4-271341, JP-A-4-3333043, JP-A-5-303157, JP-A-6-27573, JP-A-6-175258, The unstable tellurium described in JP-A-6-180478, JP-A-6-208186, JP-A-6-208184, JP-A-6-317867, JP-A-7-140579, JP-A-7-301879, JP-A-7-301880, etc. A compound can be used.
[0114]
Specifically, phosphine tellurides (for example, butyl-diisopropylphosphine telluride, tributylphosphine telluride, tributoxyphosphine telluride, ethoxydiphenylphosphine telluride), diacyl (di) tellurides ( For example, bis (diphenylcarbamoyl) ditelluride, bis (N-phenyl-N-methylcarbamoyl) ditelluride, bis (N-phenyl-N-methylcarbamoyl) telluride, bis (N-phenyl-N-benzylcarbamoyl) telluride, bis (ethoxycarbonyl) Telluride), telluroureas (for example, N, N′-dimethylethylenetellurourea, N, N′-diphenylethylenetellurourea) telluramides, telluroesters and the like may be used. In particular, diacyl (di) tellurides and phosphine tellurides are preferable. Particularly, compounds described in literatures described in paragraph No. 0030 of JP-A-11-65021, general formula (II) in JP-A-5-313284, Compounds represented by (III) and (IV) are more preferred.
[0115]
Particularly, in the chalcogen sensitization of the present invention, selenium sensitization and tellurium sensitization are preferable, and tellurium sensitization is particularly preferable.
[0116]
In gold sensitization, P.I. Gold sensitizers described by Grafkides, Chimie et Physique Photographic (published by Paul Momtel, 1987, 5th edition), Research Disclosure 307, No. 307105 can be used. Specifically, chloroauric acid, potassium chloroaurate, potassium aurithiocyanate, gold sulfide, gold selenide and the like, in addition to these, U.S. Pat. Nos. 2,642,361, 5,049,484, 5,049,485, 5,169,751, Gold compounds described in 5252455, Belgian Patent No. 691857 and the like can also be used. P. Other than gold, such as platinum, palladium, iridium, etc., other than gold described in Grafkides, Chimie et Physique Photographic (published by Paul Momtel, 1987, 5th edition), Research Disclosure 307, 307105 I can do it.
[0117]
Although gold sensitization can be used alone, it is preferably used in combination with the chalcogen sensitization described above. Specifically, gold sulfur sensitization, gold selenium sensitization, gold tellurium sensitization, gold sulfur selenium sensitization, gold sulfur tellurium sensitization, gold selenium tellurium sensitization, and gold sulfur selenium tellurium sensitization.
[0118]
In the present invention, chemical sensitization can be performed at any time after particle formation and before coating. After desalting, (1) before spectral sensitization, (2) simultaneously with spectral sensitization, (3) spectral After sensitization, there may be (4) immediately before application.
[0119]
The amount of chalcogen sensitizer used in the present invention varies depending on the silver halide grains used, chemical ripening conditions, etc., but is 10 per mole of silver halide.^-8Mol-10^-1Moles, preferably 10^-7Mol-10^-2Use moles.
Similarly, the amount of the gold sensitizer used in the present invention varies depending on various conditions, but as a guideline, it is 10 per silver halide.^-7Mol-10^-2Mole, more preferably 10^-6Mol ~ 5x10^-3Is a mole. The environmental conditions for chemically sensitizing this emulsion can be selected under any conditions, but the pAg is 8 or less, preferably 7.0 or less to 6.5 or less, particularly 6.0 or less, and the pAg is 1.5 or less. Above, preferably 2.0 or more, particularly preferably 2.5 or more, pH is 3 to 10, preferably 4 to 9, temperature is 20 ° C. to 95 ° C., preferably 25 ° C. to 80 ° C. Degree.
[0120]
In the present invention, reduction sensitization can be used in combination with chalcogen sensitization or gold sensitization. In particular, it is preferably used in combination with chalcogen sensitization.
As specific compounds for the reduction sensitization, ascorbic acid, thiourea dioxide, and dimethylamine borane are preferable. In addition, stannous chloride, aminoiminomethanesulfinic acid, hydrazine derivatives, borane compounds, silane compounds, polyamine compounds, etc. It is preferable to use it. The reduction sensitizer may be added at any stage in the photosensitive emulsion production process from crystal growth to the preparation process immediately before coating. Further, reduction sensitization is also preferable by ripening while maintaining the pH of the emulsion at 8 or more or pAg at 4 or less, and reduction sensitization by introducing a single addition portion of silver ions during grain formation. Is also preferable.
The amount of reduction sensitizer added varies depending on various conditions, but as a guideline it is 10 per silver halide.^-7Mol-10^-1Mole, more preferably 10^-6Mol ~ 5x10^-2Is a mole.
[0121]
A thiosulfonic acid compound may be added to the silver halide emulsion used in the present invention by the method shown in European Patent Publication No. 293,917.
The photosensitive silver halide grains in the invention are preferably chemically sensitized by at least one of gold sensitization and chalcogen sensitization from the viewpoint of designing a high-sensitivity photothermographic material.
[0122]
9) One-electron oxidant produced by one-electron oxidation can emit one electron or more.
In the photothermographic material of the invention, it is preferable that the one-electron oxidant produced by one-electron oxidation contains a compound capable of emitting one electron or more. The compound can be used alone or in combination with the above-described various chemical sensitizers, and can increase the sensitivity of silver halide.
[0123]
The one-electron oxidant produced by one-electron oxidation contained in the photothermographic material of the present invention is a compound selected from the following types 1 to 5 that can emit one or more electrons.
[0124]
(Type 1)
A compound in which a one-electron oxidant produced by one-electron oxidation can further emit two or more electrons with a subsequent bond cleavage reaction.
(Type 2)
The one-electron oxidant produced by one-electron oxidation is a compound capable of releasing another electron with subsequent bond cleavage reaction, and has two or more adsorptive groups to silver halide in the same molecule. Compound.
(Type 3)
A compound capable of emitting one or more electrons after a one-electron oxidant produced by one-electron oxidation undergoes a subsequent bond formation process.
(Type 4)
A compound capable of emitting one or more electrons after a one-electron oxidant produced by one-electron oxidation undergoes a subsequent intramolecular ring-cleaving reaction.
(Type 5)
In the compound represented by XY, X represents a reducing group, Y represents a leaving group, and a one-electron oxidant formed by one-electron oxidation of the reducing group represented by X is followed by XY A compound capable of releasing Y by releasing Y with a bond cleavage reaction and releasing another electron therefrom.
[0125]
Preferred among the compounds of types 1 and 3 to 5 above are “compounds having an adsorptive group to silver halide in the molecule” or “partial structure of spectral sensitizing dye in the molecule”. Compound ". More preferred is a “compound having an adsorptive group to silver halide in the molecule”. The compounds of types 1 to 4 are more preferably “compounds having a nitrogen-containing heterocyclic group substituted with two or more mercapto groups as an adsorptive group”.
[0126]
The compounds of types 1 to 5 will be described in detail.
In the type 1 compound, “bond cleavage reaction” specifically means cleavage of bonds between carbon-carbon, carbon-silicon, carbon-hydrogen, carbon-boron, carbon-tin, and carbon-germanium elements, These may be further accompanied by carbon-hydrogen bond cleavage. A type 1 compound is a compound capable of emitting two or more (preferably three or more) electrons for the first time after a one-electron oxidation to form a one-electron oxidant, followed by a bond cleavage reaction.
[0127]
Among the compounds of type 1, preferred compounds are represented by general formula (A), general formula (B), general formula (1), general formula (2), or general formula (3).
[0128]
Formula (A)
Embedded image

[0129]
General formula (B)
Embedded image

[0130]
In general formula (A), RED₁₁Represents a reducing group which can be oxidized by one electron, and L₁₁Represents a leaving group. R₁₁₂Represents a hydrogen atom or a substituent. R₁₁₁Is carbon atom (C) and RED₁₁And a nonmetallic atomic group capable of forming a cyclic structure corresponding to a tetrahydro form, hexahydro form, or octahydro form of a 5-membered or 6-membered aromatic ring (including an aromatic heterocycle).
[0131]
In the general formula (B), RED₁₂Represents a reducing group which can be oxidized by one electron, and L₁₂Represents a leaving group. R₁₂₁And R₁₂₂Each represents a hydrogen atom or a substituent. ED₁₂Represents an electron donating group. R in the general formula (B)₁₂₁And RED₁₂, R₁₂₁And R₁₂₂Or ED₁₂And RED₁₂And may be bonded to each other to form a cyclic structure.
[0132]
These compounds represented by general formula (A) or general formula (B) are represented by RED.₁₁Or RED₁₂After the reducing group represented by₁₁Or L₁₂Is a compound that can release two or more electrons, preferably three or more electrons, by releasing them by bond cleavage reaction.
[0133]
General formula (1), general formula (2), general formula (3)
Embedded image

[0134]
In general formula (1), Z₁Represents an atomic group capable of forming a 6-membered ring with a nitrogen atom and two carbon atoms of a benzene ring, and R₁, R₂, R_N1Each represents a hydrogen atom or a substituent, and X₁Represents a substitutable substituent on the benzene ring, m₁Represents an integer of 0 to 3, L₁Represents a leaving group. ED in general formula (2)₂₁Represents an electron donating group, R₁₁, R₁₂, R_N21, R₁₃, R₁₄Each represents a hydrogen atom or a substituent, and X₂₁Represents a substitutable substituent on the benzene ring, m₂₁Represents an integer of 0 to 3, L₂₁Represents a leaving group. R_N21, R₁₃, R₁₄, X₂₁And ED₂₁May be bonded to each other to form a cyclic structure. In the general formula (3), R₃₂, R₃₃, R₃₁, R_N31, R_a, R_bEach represents a hydrogen atom or a substituent, and L₃₁Represents a leaving group. However, R_N31When represents a group other than an aryl group, R_aAnd R_bCombine with each other to form an aromatic ring.
[0135]
After these compounds are oxidized by one electron,₁, L₂₁Or L₃₁Is a compound that can release two or more electrons, preferably three or more electrons, by releasing them by bond cleavage reaction.
[0136]
Hereinafter, the compound represented by the general formula (A) will be described in detail first.
In general formula (A), RED₁₁A reducing group that can be oxidized by one electron is represented by R described later.₁₁₁And a divalent group obtained by removing one hydrogen atom at a suitable site for ring formation from the following monovalent group. For example, alkylamino group, arylamino group (anilino group, naphthylamino group, etc.), heterocyclic amino group (benzthiazolylamino group, pyrrolylamino group, etc.), alkylthio group, arylthio group (phenylthio group, etc.), heterocyclic thio Group, alkoxy group, aryloxy group (phenoxy group etc.), heterocyclic oxy group, aryl group (phenyl group, naphthyl group, anthranyl group etc.), aromatic or non-aromatic heterocyclic group (5-membered to 7-membered) A monocyclic or condensed heterocyclic ring containing at least one heteroatom among nitrogen atom, sulfur atom, oxygen atom and selenium atom. Specific examples thereof include, for example, a tetrahydroquinoline ring, a tetrahydroisoquinoline ring, and a tetrahydroquinoxaline ring. , Tetrahydroquinazoline ring, indoline ring, indole ring, indazo Ring, carbazole ring, phenoxazine ring, phenothiazine ring, benzothiazoline ring, pyrrole ring, imidazole ring, thiazoline ring, piperidine ring, pyrrolidine ring, morpholine ring, benzimidazole ring, benzimidazoline ring, benzoxazoline ring, methylenedioxyphenyl Ring, etc.) (hereinafter referred to as RED for convenience)₁₁Is described as a monovalent radical name). RED₁₁May have a substituent.
[0137]
In the present invention, the substituent means a substituent selected from the following groups unless otherwise specified. Halogen atoms, alkyl groups (including aralkyl groups, cycloalkyl groups, active methine groups, etc.), alkenyl groups, alkynyl groups, aryl groups, heterocyclic groups (regardless of the position of substitution), quaternized nitrogen atoms Heterocyclic groups (eg pyridinio group, imidazolio group, quinolinio group, isoquinolinio group), acyl group, alkoxycarbonyl group, aryloxycarbonyl group, carbamoyl group, carboxy group or salt thereof, sulfonylcarbamoyl group, acylcarbamoyl group, sulfa Moylcarbamoyl group, carbazoyl group, oxalyl group, oxamoyl group, cyano group, carbonimidoyl group, thiocarbamoyl group, hydroxy group, alkoxy group (including groups containing ethyleneoxy group or propyleneoxy group units repeatedly), aryloxy group , Telocyclic oxy group, acyloxy group, (alkoxy or aryloxy) carbonyloxy group, carbamoyloxy group, sulfonyloxy group, amino group, (alkyl, aryl, or heterocyclic) amino group, acylamino group, sulfonamide group, ureido group Thioureido group, imide group, (alkoxy or aryloxy) carbonylamino group, sulfamoylamino group, semicarbazide group, thiosemicarbazide group, hydrazino group, ammonio group, oxamoylamino group, (alkyl or aryl) sulfonylureido group, Acylureido group, acylsulfamoylamino group, nitro group, mercapto group, (alkyl, aryl, or heterocyclic) thio group, (alkyl or aryl) sulfonyl group, (alkyl or aryl) Rufiniru group, a sulfo group or a salt thereof, sulfamoyl group, sulfonylsulfamoyl group or a salt thereof, phosphoric acid amide or a group containing a phosphoric acid ester structure and so forth. These substituents may be further substituted with these substituents.
[0138]
RED₁₁Are preferably alkylamino group, arylamino group, heterocyclic amino group, aryl group, aromatic or non-aromatic heterocyclic group, more preferably arylamino group (especially anilino group), aryl group (especially phenyl). Group). When these have a substituent, the substituent is preferably a halogen atom, an alkyl group, an alkoxy group, a carbamoyl group, a sulfamoyl group, an acylamino group, or a sulfonamide group.
However, RED₁₁When represents an aryl group, the aryl group preferably has at least one “electron-donating group”. Here, the “electron donating group” means a hydroxy group, an alkoxy group, a mercapto group, a sulfonamide group, an acylamino group, an alkylamino group, an arylamino group, a heterocyclic amino group, an active methine group, and a nitrogen atom in the ring. 5-membered, monocyclic or condensed, electron-rich aromatic heterocyclic group (for example, indolyl group, pyrrolyl group, imidazolyl group, benzimidazolyl group, thiazolyl group, benzthiazolyl group, indazolyl group) containing at least one, nitrogen A non-aromatic nitrogen-containing heterocyclic group (a group that can also be called a cyclic amino group such as a pyrrolidinyl group, an indolinyl group, a piperidinyl group, a piperazinyl group, or a morpholino group) substituted with an atom. Here, the active methine group means a methine group substituted by two “electron-withdrawing groups”, and the “electron-withdrawing group” means an acyl group, an alkoxycarbonyl group, an aryloxycarbonyl group, It means a carbamoyl group, an alkylsulfonyl group, an arylsulfonyl group, a sulfamoyl group, a trifluoromethyl group, a cyano group, a nitro group, or a carbonimidoyl group. Here, the two electron withdrawing groups may be bonded to each other to form a cyclic structure.
[0139]
In general formula (A), L₁₁Is specifically a carboxy group or a salt thereof, a silyl group, a hydrogen atom, a triarylboron anion, a trialkylstannyl group, a trialkylgermyl group, or -CR_C1R_C2R_C3Represents a group. Here, the silyl group specifically represents a trialkylsilyl group, an aryldialkylsilyl group, a triarylsilyl group, or the like, and may have an arbitrary substituent.
[0140]
L₁₁When represents a salt of a carboxy group, examples of counter ions that form salts include alkali metal ions, alkaline earth metal ions, heavy metal ions, ammonium ions, phosphonium ions, and the like, preferably alkali metal ions or ammonium ions. , Alkali metal ions (especially Li⁺, Na⁺, K⁺Ion) is most preferred.
[0141]
L₁₁-CR_C1R_C2R_C3When representing a group, here R_C1, R_C2, R_C3Each independently represents a hydrogen atom, an alkyl group, an aryl group, a heterocyclic group, an alkylthio group, an arylthio group, an alkylamino group, an arylamino group, a heterocyclic amino group, an alkoxy group, an aryloxy group, or a hydroxy group. May be bonded to each other to form a cyclic structure, and may further have an arbitrary substituent. However, R_C1, R_C2, R_C3When one of them represents a hydrogen atom or an alkyl group, the remaining two do not represent a hydrogen atom or an alkyl group. R_C1, R_C2, R_C3Preferably, each independently represents an alkyl group, an aryl group (particularly a phenyl group), an alkylthio group, an arylthio group, an alkylamino group, an arylamino group, a heterocyclic group, an alkoxy group, or a hydroxy group. For example, phenyl group, p-dimethylaminophenyl group, p-methoxyphenyl group, 2,4-dimethoxyphenyl group, p-hydroxyphenyl group, methylthio group, phenylthio group, phenoxy group, methoxy group, ethoxy group, dimethylamino Group, N-methylanilino group, diphenylamino group, morpholino group, thiomorpholino group, hydroxy group and the like. Examples of the case where they are bonded to each other to form a cyclic structure include 1,3-dithiolan-2-yl group, 1,3-dithian-2-yl group, N-methyl-1,3-thiazolidine-2 -Yl group, N-benzyl-benzothiazolidin-2-yl group and the like.
-CR_C1R_C2R_C3The group is R_C1, R_C2, R_C3As a result of each selected within the above-mentioned range, the general formula (A) to L₁₁It is also preferred if it represents the same group as the residue excluding.
[0142]
In general formula (A), L₁₁Is preferably a carboxy group or a salt thereof, and a hydrogen atom. More preferably, it is a carboxy group or a salt thereof.
[0143]
L₁₁When represents a hydrogen atom, the compound represented by the general formula (A) preferably has a base moiety inherent in the molecule. After the compound represented by the general formula (A) is oxidized by the action of this base moiety,₁₁Is deprotonated, and further electrons are emitted therefrom.
[0144]
Here, the base is specifically a conjugate base of an acid having a pKa of about 1 to about 10. For example, nitrogen-containing heterocycles (pyridines, imidazoles, benzimidazoles, thiazoles, etc.), anilines, trialkylamines, amino groups, carbon acids (active methylene anions, etc.), thioacetic acid anions, carboxylates (- COO⁻), Sulfate (-SO₃ ⁻), Or amine oxide (> N⁺(O⁻)-) And the like. Preferably, it is a conjugate base of an acid having a pKa of about 1 to about 8, more preferably carboxylate, sulfate, or amine oxide, and particularly preferably carboxylate. When these bases have anions, they may have counter cations, examples of which include alkali metal ions, alkaline earth metal ions, heavy metal ions, ammonium ions, phosphonium ions and the like. These bases are linked to the compound represented by the general formula (A) at an arbitrary position. The position at which these base sites are bonded includes RED of the general formula (A).₁₁, R₁₁₁, R₁₁₂Any of these may be sufficient, and you may connect with the substituent of these groups.
[0145]
R in the general formula (A)₁₁₂Represents a substituent substitutable on a hydrogen atom or a carbon atom. However, R₁₁₂Is L₁₁And does not represent the same group.
R₁₁₂Is preferably a hydrogen atom, an alkyl group, an aryl group (such as a phenyl group), an alkoxy group (such as a methoxy group, an ethoxy group, and a benzyloxy group), a hydroxy group, an alkylthio group (such as a methylthio group and a butylthio group), an amino group, and an alkyl group An amino group, an arylamino group and a heterocyclic amino group, more preferably a hydrogen atom, an alkyl group, an alkoxy group, a hydroxy group, a phenyl group and an alkylamino group.
[0146]
R in the general formula (A)₁₁₁Is a ring structure corresponding to a tetrahydro, hexahydro or octahydro form of a 5-membered or 6-membered aromatic ring (including aromatic heterocycle), where the hydro form is an aromatic A ring structure in which a carbon-carbon double bond (or carbon-nitrogen double bond) in a ring (including an aromatic heterocycle) is partially hydrogenated means a tetrahydro form, and two tetrahydro forms are hexahydro forms The three and octahydro forms mean a structure in which four carbon-carbon double bonds (or carbon-nitrogen double bonds) are hydrogenated. By being hydrogenated, the aromatic ring becomes a partially hydrogenated non-aromatic ring structure.
[0147]
Specifically, pyrrolidine ring, imidazolidine ring, thiazolidine ring, pyrazolidine ring and oxazolidine ring, piperidine ring, tetrahydropyridine ring, tetrahydropyrimidine ring, piperazine ring, tetralin ring, tetrahydroquinoline ring, tetrahydroisoquinoline ring, tetrahydroquinazoline ring, And tetrahydroquinoxaline ring, tetrahydrocarbazole ring, octahydrophenanthridine ring and the like. These ring structures may have an arbitrary substituent.
[0148]
R₁₁₁More preferably, the cyclic structure formed by pyrrolidine ring, imidazolidine ring, piperidine ring, tetrahydropyridine ring, tetrahydropyrimidine ring, piperazine ring, tetrahydroquinoline ring, tetrahydroisoquinoline ring, tetrahydroquinazoline ring, tetrahydroquinoxaline ring, tetrahydrocarbazole ring Particularly preferred are pyrrolidine ring, piperidine ring, piperazine ring, tetrahydropyridine ring, tetrahydroquinoline ring, tetrahydroisoquinoline ring, tetrahydroquinazoline ring, tetrahydroquinoxaline ring, most preferably pyrrolidine ring, piperidine ring, tetrahydropyridine ring. , Tetrahydroquinoline ring and tetrahydroisoquinoline ring.
[0149]
In the general formula (B), RED₁₂, L₁₂Are respectively RED of the general formula (A)₁₁, L₁₁The preferred range is also the same. However, RED₁₂Is a monovalent group except when it forms the following cyclic structure, specifically RED.₁₁And monovalent group names described in the above. R₁₂₁And R₁₂₂Is R in the general formula (A)₁₁₂The preferred range is also the same. ED₁₂Represents an electron donating group. R₁₂₁And RED₁₂, R₁₂₁And R₁₂₂Or ED₁₂And RED₁₂And may be bonded to each other to form a cyclic structure.
[0150]
ED in general formula (B)₁₂The electron donating group represented by RED₁₁Is the same as the electron-donating group described as the substituent for when A represents an aryl group. ED₁₂Preferably a hydroxy group, an alkoxy group, a mercapto group, a sulfonamide group, an alkylamino group, an arylamino group, an active methine group, a 5-membered monocyclic or condensed ring electron containing at least one nitrogen atom in the ring An excess aromatic heterocyclic group, a non-aromatic nitrogen-containing heterocyclic group substituted with a nitrogen atom, and a phenyl group substituted with these electron donating groups, and further a hydroxy group, a mercapto group, a sulfonamide group, an alkylamino group Group, arylamino group, active methine group, non-aromatic nitrogen-containing heterocyclic group substituted with nitrogen atom, and phenyl group substituted with these electron donating groups (for example, p-hydroxyphenyl group, p-dialkylaminophenyl group) , O, p-dialkoxyphenyl group, etc.) are more preferable.
[0151]
R in the general formula (B)₁₂₁And RED₁₂, R₁₂₂And R₁₂₁Or ED₁₂And RED₁₂And may be bonded to each other to form a cyclic structure. The cyclic structure formed here is a non-aromatic carbocyclic or heterocyclic ring, which is a 5-membered to 7-membered monocyclic or condensed ring, and is a substituted or unsubstituted cyclic structure. R₁₂₁And RED₁₂When and form a ring structure, specific examples thereof include R in general formula (A).₁₁₁In addition to those listed as examples of the cyclic structure formed by pyrrole, imidazoline, thiazoline, pyrazoline, oxazoline, indane, morpholine, indoline, tetrahydro-1,4-oxazine, 2, 3-dihydrobenzo-1,4-oxazine ring, tetrahydro-1,4-thiazine ring, 2,3-dihydrobenzo-1,4-thiazine ring, 2,3-dihydrobenzofuran ring, 2,3-dihydrobenzothiophene A ring etc. are mentioned. ED₁₂And RED₁₂And form a ring structure, ED₁₂Preferably represents an amino group, an alkylamino group, or an arylamino group, and specific examples of the ring structure formed include a tetrahydropyrazine ring, a piperazine ring, a tetrahydroquinoxaline ring, and a tetrahydroisoquinoline ring. R₁₂₂And R₁₂₁When and form a ring structure, specific examples thereof include a cyclohexane ring and a cyclopentane ring.
[0152]
Next, general formulas (1) to (3) will be described.
In the general formulas (1) to (3), R₁, R₂, R₁₁, R₁₂, R₃₁Is R in the general formula (A)₁₁₂The preferred range is also the same. L₁, L₂₁, L₃₁Is L in the general formula (A)₁₁Represents the same leaving group as the specific examples given in the description, and preferred ranges thereof are also the same. X₁, X₂₁As the substituent represented by the formula (A),₁₁Is the same as the example of the substituent when has a substituent, and the preferred range is also the same. m₁, M₂₁Is preferably an integer of 0 to 2, more preferably 0 or 1.
[0153]
R_N1, R_N21, R_N31When represents a substituent, the substituent is preferably an alkyl group, an aryl group, or a heterocyclic group, and these may further have an arbitrary substituent. R_N1, R_N21, R_N31Is preferably a hydrogen atom, an alkyl group or an aryl group, more preferably a hydrogen atom or an alkyl group.
[0154]
R₁₃, R₁₄, R₃₃, R_a, R_bWhen represents a substituent, the substituent is preferably an alkyl group, aryl group, acyl group, alkoxycarbonyl group, carbamoyl group, cyano group, alkoxy group, acylamino group, sulfonamide group, ureido group, thioureido group, alkylthio group. An arylthio group, an alkylsulfonyl group, an arylsulfonyl group, a sulfamoyl group, and the like.
[0155]
In general formula (1), Z₁The 6-membered ring formed by is a non-aromatic heterocycle condensed with the benzene ring of the general formula (1). Specifically, a tetrahydroquinoline ring, a tetrahydroquinoxaline ring as a ring structure including the condensed benzene ring, A tetrahydroquinazoline ring, preferably a tetrahydroquinoline ring or a tetrahydroquinoxaline ring. These may have a substituent.
[0156]
ED in general formula (2)₂₁Is the ED of the general formula (B)₁₂The preferred range is also the same.
[0157]
In the general formula (2), R_N21, R₁₃, R₁₄, X₂₁And ED₂₁Any two of these may combine with each other to form a cyclic structure. Where R_N21And X₂₁The cyclic structure formed by bonding is preferably a 5- to 7-membered non-aromatic carbocyclic or heterocyclic ring condensed with a benzene ring. Specific examples thereof include a tetrahydroquinoline ring and a tetrahydroquinoxaline. A ring, an indoline ring, a 2,3-dihydro-5,6-benzo-1,4-thiazine ring, and the like. Preferred are a tetrahydroquinoline ring, a tetrahydroquinoxaline ring and an indoline ring.
[0158]
In the general formula (3), R_N31When represents a group other than an aryl group, R_aAnd R_bCombine with each other to form an aromatic ring. Here, the aromatic ring is an aryl group (for example, a phenyl group or a naphthyl group) and an aromatic heterocyclic group (for example, a pyridine ring group, a pyrrole ring group, a quinoline ring group, or an indole ring group), and an aryl group is preferable. The aromatic ring group may have an arbitrary substituent.
In the general formula (3), R_aAnd R_bAre preferably bonded to each other to form an aromatic ring (particularly a phenyl group).
[0159]
In the general formula (3), R₃₂Is preferably a hydrogen atom, an alkyl group, an aryl group, a hydroxy group, an alkoxy group, a mercapto group, an amino group, etc., where R₃₂When R represents a hydroxy group,₃₃The case where represents an “electron-withdrawing group” is also a preferred example. Here, the “electron withdrawing group” is the same as described above, and an acyl group, an alkoxycarbonyl group, a carbamoyl group, and a cyano group are preferable.
[0160]
Next, the type 2 compound will be described.
In the type 2 compound, “bond cleavage reaction” means carbon-carbon, carbon-silicon, carbon-hydrogen, carbon-boron, carbon-tin, carbon-germanium bond cleavage, and carbon-hydrogen. This may be accompanied by cleavage of the bond.
[0161]
The type 2 compound is a compound having two or more (preferably 2 to 6, more preferably 2 to 4) adsorptive groups to silver halide in the molecule. More preferred is a compound having a nitrogen-containing heterocyclic group substituted with two or more mercapto groups as an adsorptive group. The number of adsorptive groups is preferably 2-6, more preferably 2-4. The adsorptive group will be described later.
[0162]
A preferable compound among the compounds of type 2 is represented by the general formula (C).
[0163]
General formula (C)
Embedded image

[0164]
The compound represented by the general formula (C) is RED₂After the reducing group represented by₂It is a compound that can release one more electron with this by leaving the group by bond cleavage reaction.
[0165]
In the general formula (C), RED₂Is the RED of the general formula (B)₁₂Represents the same group, and the preferred range is also the same. L₂Is L in the general formula (A)₁₁Represents the same group as described above, and its preferred range is also the same. L₂When represents a silyl group, the compound is a compound having, as an adsorptive group, a nitrogen-containing heterocyclic group substituted with two or more mercapto groups in the molecule. R₂₁, R₂₂Represents a hydrogen atom or a substituent, and these are R in the general formula (A)₁₁₂The preferred range is also the same. RED₂And R₂₁And may be bonded to each other to form a ring structure.
[0166]
The ring structure formed here is a 5-membered to 7-membered monocyclic or condensed, non-aromatic carbocycle or heterocycle, which may have a substituent. However, the ring structure is not a ring structure corresponding to a tetrahydro, hexahydro or octahydro form of an aromatic ring or an aromatic heterocycle. The ring structure is preferably a ring structure corresponding to a dihydro form of an aromatic ring or an aromatic heterocycle, and specific examples thereof include, for example, a 2-pyrroline ring, a 2-imidazoline ring, a 2-thiazoline ring, 1,2- Dihydropyridine ring, 1,4-dihydropyridine ring, indoline ring, benzimidazoline ring, benzothiazoline ring, benzoxazoline ring, 2,3-dihydrobenzothiophene ring, 2,3-dihydrobenzofuran ring, benzo-α-pyran ring, 1 , 2-dihydroquinoline ring, 1,2-dihydroquinazoline ring, 1,2-dihydroquinoxaline ring and the like, preferably 2-imidazoline ring, 2-thiazoline ring, indoline ring, benzoimidazoline ring, benzothiazoline ring, Benzoxazoline ring, 1,2-dihydropyridine ring, 1,2-dihydroquino Down ring, 1,2-dihydro-quinazoline ring, and the like 1,2-dihydro-quinoxaline ring, indoline ring, benzimidazoline ring, a benzothiazoline ring, 1,2-dihydroquinoline ring is more preferable, indoline ring is particularly preferred.
[0167]
Next, the compound of type 3 will be described.
In the type 3 compound, “bond formation process” means formation of an interatomic bond such as carbon-carbon, carbon-nitrogen, carbon-sulfur, carbon-oxygen and the like.
[0168]
The compound of type 3 is preferably a reactive group site (carbon-carbon double bond site, carbon-carbon triple bond site, fragrance) in which a one-electron oxidant formed by one-electron oxidation coexists in the molecule. And a non-aromatic heterocyclic group part of a benzo-condensed ring) to form a bond and then emit one electron or more electrons.
[0169]
More specifically, a type 3 compound has a one-electron oxidant formed by one-electron oxidation (a cation radical species or a neutral radical species produced by elimination of a proton therefrom) in the same molecule. It reacts with the coexisting reactive group, forms a bond, and generates a radical species having a new ring structure in the molecule. This radical species has a feature that electrons of the second electron are emitted directly or with elimination of protons.
[0170]
And in some Type 3 compounds, the two-electron oxidant so produced is then subjected to a hydrolysis reaction in some cases, and in some cases tautomerization with direct proton transfer. There is a case in which one or more electrons, usually two or more electrons are emitted from the oxidization reaction. Alternatively, those having the ability to emit one or more electrons, usually two or more electrons, directly from a two-electron oxidant without going through such a tautomerization reaction are also included.
[0171]
The compound of type 3 is preferably represented by the general formula (D).
[0172]
Formula (D)
Embedded image

[0173]
In general formula (D), RED₃Represents a reducing group which can be oxidized by one electron, Y₃Is RED₃Represents a reactive group site that reacts after one-electron oxidation, specifically a carbon-carbon double bond site, a carbon-carbon triple bond site, an aromatic group site, or a non-aromatic heterocycle of a benzo-fused ring An organic group containing a ring group site is represented. L₃Is RED₃And Y₃Represents a linking group for linking.
[0174]
RED₃Is the RED of the general formula (B)₁₂And is preferably an arylamino group, a heterocyclic amino group, an aryloxy group, an arylthio group, an aryl group, an aromatic or non-aromatic heterocyclic group (particularly a nitrogen-containing heterocyclic group is preferred). And more preferably an arylamino group, a heterocyclic amino group, an aryl group, an aromatic or non-aromatic heterocyclic group, and among these heterocyclic groups, a tetrahydroquinoline ring group, a tetrahydroquinoxaline ring group, a tetrahydroquinazoline ring Group, indoline ring group, indole ring group, carbazole ring group, phenoxazine ring group, phenothiazine ring group, benzothiazoline ring group, pyrrole ring group, imidazole ring group, thiazole ring group, benzimidazole ring group, benzimidazoline ring group, Benzothiazoline ring group, 3,4-methylenedioxyphenyl- - etc. yl group.
RED₃Particularly preferred are an arylamino group (particularly anilino group), an aryl group (particularly a phenyl group), and an aromatic or non-aromatic heterocyclic group.
[0175]
Where RED₃When represents an aryl group, the aryl group preferably has at least one “electron-donating group”. The “electron donating group” is the same as described above.
[0176]
RED₃When represents an aryl group, the substituent of the aryl group is more preferably an alkylamino group, a hydroxy group, an alkoxy group, a mercapto group, a sulfonamide group, an active methine group, a non-aromatic nitrogen-containing heterocycle substituted with a nitrogen atom More preferably an alkylamino group, a hydroxy group, an active methine group, and a non-aromatic nitrogen-containing heterocyclic group substituted with a nitrogen atom, and most preferably an alkylamino group and a non-aromatic group substituted with a nitrogen atom. Nitrogen heterocyclic group.
[0177]
Y₃When the organic group containing a carbon-carbon double bond site represented by (for example, vinyl group) has a substituent, the substituent is preferably an alkyl group, a phenyl group, an acyl group, a cyano group, an alkoxycarbonyl group, A carbamoyl group, an electron donating group, and the like. As the electron donating group, an alkoxy group, a hydroxy group (which may be protected with a silyl group, such as a trimethylsilyloxy group, a t-butyldimethylsilyloxy group, Phenylsilyloxy group, triethylsilyloxy group, phenyldimethylsilyloxy group, etc.), amino group, alkylamino group, arylamino group, sulfonamide group, active methine group, mercapto group, alkylthio group, and these electron donors It is a phenyl group having a functional group as a substituent.
[0178]
Here, when the organic group containing a carbon-carbon double bond site has a hydroxy group as a substituent, Y₃Is the partial structure on the right:> C₁= C₂(—OH) — is included, but this is tautomerized and the partial structure shown on the right:> C₁HC₂It may be (= O)-. In this case, the C₁It is also preferred that the substituent substituted for carbon is an electron withdrawing group, in which case Y₃Has a partial structure of “active methylene group” or “active methine group”. The electron withdrawing group that can give such a partial structure of the active methylene group or active methine group is the same as that described in the description of the above-mentioned “active methine group”.
[0179]
Y₃When the organic group containing a carbon-carbon triple bond site represented by (for example, ethynyl group) has a substituent, examples of the substituent include an alkyl group, a phenyl group, an alkoxycarbonyl group, a carbamoyl group, and an electron donating group. preferable.
[0180]
Y₃Represents an organic group containing an aromatic group, an aromatic group is preferably an aryl group having an electron donating group as a substituent (particularly a phenyl group is preferred) or an indole ring group, where the electron donating group is Preferred are a hydroxy group (which may be protected with a silyl group), an alkoxy group, an amino group, an alkylamino group, an active methine group, a sulfonamide group and a mercapto group.
[0181]
Y₃Represents an organic group containing a non-aromatic heterocyclic group portion of a benzo-fused ring, preferably a benzo-fused non-aromatic heterocyclic group that preferably has an aniline structure as a partial structure, for example, an indoline ring group, 1,2,3,4-tetrahydroquinoline ring group, 1,2,3,4-tetrahydroquinoxaline ring group, 4-quinolone ring group and the like can be mentioned.
[0182]
Y₃More preferred as the reactive group represented by is an organic group containing a carbon-carbon double bond site, an aromatic group site, or a benzo-fused non-aromatic heterocyclic group. More preferred are a carbon-carbon double bond site, a phenyl group having an electron donating group as a substituent, an indole ring group, and a benzo-fused non-aromatic heterocyclic group having an aniline structure as a partial structure. Here, the carbon-carbon double bond site preferably has at least one electron donating group as a substituent.
[0183]
Y₃As a result of the selection of the reactive group represented by₃The case where it has the same partial structure as the reducing group represented by general formula (D) is also a preferred example of the compound represented by general formula (D).
[0184]
L₃RED₃And Y₃And specifically represents a single bond, an alkylene group, an arylene group, a heterocyclic group, -O-, -S-, -NR._N-, -C (= O)-, -SO₂The group which consists of individual group of-, -SO-, -P (= O)-, or a combination of these groups is represented. R here_NRepresents a hydrogen atom, an alkyl group, an aryl group, or a heterocyclic group. L₃The linking group represented by may have an arbitrary substituent. L₃The linking group represented by RED₃And Y₃In any position of the group represented by the formula (1), each of the hydrogen atoms may be linked to replace any one hydrogen atom.
L₃Preferred examples of are: a single bond, an alkylene group (particularly a methylene group, an ethylene group, a propylene group), an arylene group (particularly a phenylene group), a —C (═O) — group, an —O— group, an —NH— group, -N (alkyl group)-group and the bivalent coupling group which consists of a combination of these groups are mentioned.
[0185]
L₃The group represented by₃Cation radical species (X⁺.), Or a radical species (X.) generated from the proton withdrawn therefrom, and Y₃When the reactive group represented by the above reacts to form a bond, the atomic group involved in this reaction is L₃It is preferable that a 3-7 membered cyclic structure including can be formed. For this purpose, radical species (X⁺-Or X-), the reactive group represented by Y, and L are preferably connected by 3 to 7 atomic groups.
[0186]
Next, the type 4 compound will be described.
A compound of type 4 is a compound having a ring structure substituted with a reducing group, and after the reducing group is oxidized by one electron, one or more electrons are emitted along with the ring structure cleavage reaction. Compound. The ring structure cleavage reaction referred to here means one having the following form.
[0187]
Embedded image

[0188]
In the formula, compound a represents a type 4 compound. In compound a, D represents a reducing group, and X and Y represent atoms forming a bond that is cleaved after one-electron oxidation in the ring structure. First, the compound a is one-electron oxidized to produce a one-electron oxidant b. From this, the single bond of XX becomes a double bond, and at the same time, the bond of XY is cleaved to produce a ring-opened product c. Alternatively, a radical intermediate d may be generated from the one-electron oxidant b with proton desorption, and a ring-opening body e may be similarly generated therefrom. The compound of the present invention is characterized in that one or more electrons are subsequently released from the ring-opened product c or e thus produced.
[0189]
The ring structure possessed by the type 4 compound is a 3- to 7-membered carbocyclic or heterocyclic ring, and represents a monocyclic or condensed, saturated or unsaturated non-aromatic ring. A saturated ring structure is preferable, and a 3-membered ring or 4-membered ring is more preferable. Preferred examples of the ring structure include a cyclopropane ring, a cyclobutane ring, an oxirane ring, an oxetane ring, an aziridine ring, an azetidine ring, an episulfide ring, and a thietane ring. More preferred are a cyclopropane ring, a cyclobutane ring, an oxirane ring, an oxetane ring and an azetidine ring, and particularly preferred are a cyclopropane ring, a cyclobutane ring and an azetidine ring. The ring structure may have an arbitrary substituent.
[0190]
The compound of type 4 is preferably represented by the general formula (E) or (F).
[0191]
General formula (E)
Embedded image

[0192]
Formula (F)
Embedded image

[0193]
RED in general formula (E) and general formula (F)₄₁And RED₄₂Are respectively RED of the general formula (B)₁₂Represents a group having the same meaning, and the preferred range thereof is also the same. R₄₀~ R₄₄And R₄₅~ R₄₉Each represents a hydrogen atom or a substituent. In general formula (F), Z₄₂Is -CR₄₂₀R₄₂₁-, -NR₄₂₃-Represents-or -O-. R here₄₂₀, R₄₂₁Each represents a hydrogen atom or a substituent, and R₄₂₃Represents a hydrogen atom, an alkyl group, an aryl group or a heterocyclic group.
[0194]
R in general formula (E) and general formula (F)₄₀And R₄₅Preferably represents a hydrogen atom, an alkyl group, an aryl group or a heterocyclic group, more preferably a hydrogen atom, an alkyl group or an aryl group. R₄₁~ R₄₄And R₄₆~ R₄₉And preferably a hydrogen atom, an alkyl group, an alkenyl group, an aryl group, a heterocyclic group, an arylthio group, an alkylthio group, an acylamino group, or a sulfonamide group, more preferably a hydrogen atom, an alkyl group, an aryl group, or a heterocyclic group. is there.
[0195]
R₄₁~ R₄₄In which at least one of these is a donor group and R₄₁And R₄₂Or R₄₃And R₄₄Are preferably electron withdrawing groups. More preferably R₄₁~ R₄₄This is a case where at least one of the above is a donor group. More preferably R₄₁~ R₄₄At least one of them is a donor group and R₄₁~ R₄₄In this case, the group that is not a donor group is a hydrogen atom or an alkyl group.
[0196]
The donor group mentioned here is an “electron-donating group” or an aryl group substituted with at least one “electron-donating group”. The donor group is preferably an alkylamino group, an arylamino group, a heterocyclic amino group, a 5-membered monocyclic or condensed ring electron-rich aromatic heterocyclic group containing at least one nitrogen atom in the ring, nitrogen A non-aromatic nitrogen-containing heterocyclic group substituted with an atom or a phenyl group substituted with at least one electron-donating group is used. More preferably, an alkylamino group, an arylamino group, a 5-membered monocyclic or condensed ring-excessive aromatic heterocyclic group containing at least one nitrogen atom in the ring (indole ring, pyrrole ring, carbazole ring, etc.) ), A phenyl group substituted with an electron donating group (such as a phenyl group substituted with three or more alkoxy groups, a phenyl group substituted with a hydroxy group, an alkylamino group, or an arylamino group). Particularly preferably an arylamino group, a 5-membered monocyclic or condensed ring-containing electron-rich aromatic heterocyclic group (especially a 3-indolyl group) or an electron-donating group containing at least one nitrogen atom in the ring. Used phenyl groups (particularly phenyl groups substituted by trialkoxyphenyl groups, alkylamino groups or arylamino groups).
[0197]
Z₄₂Preferably as -CR₄₂₀R₄₂₁-Or -NR₄₂₃-, More preferably -NR₄₂₃-. R₄₂₀, R₄₂₁Is preferably a hydrogen atom, an alkyl group, an aryl group, a heterocyclic group, an acylamino group, or a sulfoneamino group, more preferably a hydrogen atom, an alkyl group, an aryl group, or a heterocyclic group. R₄₂₃Preferably represents a hydrogen atom, an alkyl group, an aryl group or an aromatic heterocyclic group, more preferably a hydrogen atom, an alkyl group or an aryl group.
[0198]
R₄₀~ R₄₉And R₄₂₀, R₄₂₁, R₄₂₃When each of these groups is a substituent, the total number of carbon atoms is preferably 40 or less, more preferably 30 or less, and particularly preferably 15 or less. These substituents may be bonded to each other or other sites in the molecule (RED₄₁, RED₄₂Or Z₄₂) To form a ring.
[0199]
In the compounds of types 1 to 4 of the present invention, the adsorptive group to silver halide is a group that directly adsorbs to silver halide or a group that promotes adsorption to silver halide. Specifically, mercapto A heterocyclic group containing at least one atom selected from a group (or a salt thereof), a thione group (-C (= S)-), a nitrogen atom, a sulfur atom, a selenium atom and a tellurium atom, a sulfide group, a cationic group, Or an ethynyl group. However, the type 2 compound of the present invention does not contain a sulfide group as an adsorptive group.
[0200]
The mercapto group (or salt thereof) as the adsorptive group means the mercapto group (or salt thereof) itself, and more preferably a heterocyclic group or aryl group substituted with at least one mercapto group (or salt thereof). Or represents an alkyl group. Here, the heterocyclic group is a 5-membered to 7-membered monocyclic or condensed aromatic or non-aromatic heterocyclic group such as an imidazole ring group, a thiazole ring group, an oxazole ring group, or a benzimidazole ring group. , Benzthiazole ring group, benzoxazole ring group, triazole ring group, thiadiazole ring group, oxadiazole ring group, tetrazole ring group, purine ring group, pyridine ring group, quinoline ring group, isoquinoline ring group, pyrimidine ring group, triazine A cyclic group etc. are mentioned. Further, it may be a heterocyclic group containing a quaternized nitrogen atom. In this case, the substituted mercapto group may be dissociated into a meso ion. Examples of such a heterocyclic group include an imidazolium ring group, Examples include a pyrazolium ring group, a thiazolium ring group, a triazolium ring group, a tetrazolium ring group, a thiadiazolium ring group, a pyridinium ring group, a pyrimidinium ring group, and a triazinium ring group. Among them, a triazolium ring group (for example, 1,2,4- Triazolium-3-thiolate ring group) is preferable. Examples of the aryl group include a phenyl group and a naphthyl group. Examples of the alkyl group include linear, branched or cyclic alkyl groups having 1 to 30 carbon atoms. When the mercapto group forms a salt, the counter ion is a cation such as an alkali metal, alkaline earth metal, or heavy metal (Li⁺, Na⁺, K⁺, Mg²⁺, Ag⁺, Zn²⁺And the like, ammonium ions, quaternized heterocyclic groups containing nitrogen atoms, phosphonium ions, and the like.
[0201]
Further, the mercapto group as the adsorptive group may be tautomerized into a thione group, specifically, a thioamide group (here, —C (═S) —NH— group) and the thioamide group. A group having a partial structure of, ie, a chain or cyclic thioamide group, a thioureido group, a thiourethane group, or a dithiocarbamate group. Examples of cyclic groups include thiazolidine-2-thione group, oxazolidine-2-thione group, 2-thiohydantoin group, rhodanine group, isorhodanine group, thiobarbituric acid group, 2-thioxo-oxazolidine-4-one group Is mentioned.
[0202]
The thione group as an adsorptive group cannot be tautomerized to a mercapto group (including a hydrogen atom at the α-position of the thione group), including the case where the mercapto group described above is tautomerized into a thione group. A chain or cyclic thioamide group, thioureido group, thiourethane group, or dithiocarbamate group is also included.
[0203]
A heterocyclic group containing at least one atom selected from a nitrogen atom, a sulfur atom, a selenium atom and a tellurium atom as the adsorptive group is a -NH- group capable of forming imino silver (> NAg) and a partial structure of the heterocyclic ring A nitrogen-containing heterocyclic group, or a “—S—” group, a “—Se—” group, a “—Te—” group, or a “═N—” group that can coordinate to a silver ion via a coordination bond. A heterocyclic group having a ring partial structure. Examples of the former include benzotriazole group, triazole group, indazole group, pyrazole group, tetrazole group, benzimidazole group, imidazole group, and purine group, and examples of the latter include thiophene. Group, thiazole group, oxazole group, benzothiazole group, benzoxazole group, thiadiazole group, oxadiazole group, triazine group Seleno azole group, benzimidazole seleno azole group, tellurium azole group, such as benz tellurium azole group. The former is preferred.
[0204]
The sulfide group as the adsorptive group includes all groups having a partial structure of “—S—”, preferably alkyl (or alkylene) -S-alkyl (or alkylene), aryl (or arylene) -S—. A group having a partial structure of alkyl (or alkylene), aryl (or arylene) -S-aryl (or arylene). Furthermore, these sulfide groups may form a cyclic structure or may be an -S-S- group. Specific examples in the case of forming a cyclic structure include a thiolane ring, a 1,3-dithiolane ring or a 1,2-dithiolane ring, a thiane ring, a dithiane ring, a tetrahydro-1,4-thiazine ring (thiomorpholine ring) and the like. Groups. Particularly preferred as the sulfide group is a group having a partial structure of alkyl (or alkylene) -S-alkyl (or alkylene).
[0205]
The cationic group as the adsorptive group means a group containing a quaternized nitrogen atom, specifically, an ammonio group or a group containing a nitrogen-containing heterocyclic group containing a quaternized nitrogen atom. . However, the cationic group does not become a part of an atomic group forming a dye structure (for example, a cyanine chromophore). Here, the ammonio group is a trialkylammonio group, a dialkylarylammonio group, an alkyldiarylammonio group or the like, and examples thereof include a benzyldimethylammonio group, a trihexylammonio group, and a phenyldiethylammonio group. Examples of the nitrogen-containing heterocyclic group containing a quaternized nitrogen atom include a pyridinio group, a quinolinio group, an isoquinolinio group, an imidazolio group, and the like. A pyridinio group and an imidazolio group are preferable, and a pyridinio group is particularly preferable. These nitrogen-containing heterocyclic groups containing a quaternized nitrogen atom may have an arbitrary substituent, but in the case of a pyridinio group and an imidazolio group, the substituent is preferably an alkyl group, an aryl group, an acylamino group , A chloro atom, an alkoxycarbonyl group, a carbamoyl group, and the like. In the case of a pyridinio group, a phenyl group is particularly preferable as a substituent.
[0206]
An ethynyl group as an adsorptive group means a —C≡CH group, and a hydrogen atom may be substituted.
The above adsorptive group may have an arbitrary substituent.
[0207]
Specific examples of the adsorptive group further include those described in pages 4 to 7 of JP-A No. 11-95355.
[0208]
Preferred as the adsorptive group in the present invention is a mercapto-substituted nitrogen-containing heterocyclic group (for example, 2-mercaptothiadiazole group, 3-mercapto-1,2,4-triazole group, 5-mercaptotetrazole group, 2-mercapto-1). , 3,4-oxadiazole group, 2-mercaptobenzoxazole group, 2-mercaptobenzthiazole group, 1,5-dimethyl-1,2,4-triazolium-3-thiolate group), or imino silver (> A nitrogen-containing heterocyclic group (for example, a benzotriazole group, a benzimidazole group, an indazole group, etc.) having a —NH— group that can form NAg) as a partial structure of the heterocyclic ring. Particularly preferred are 5-mercaptotetrazole group, 3-mercapto-1,2,4-triazole group, and benzotriazole group, most preferred are 3-mercapto-1,2,4-triazole group, and 5 -Mercaptotetrazole group.
[0209]
Of the compounds of the present invention, compounds having two or more mercapto groups as partial structures in the molecule are also particularly preferred compounds. Here, the mercapto group (—SH) may be a thione group if it can be tautomerized. Examples of such compounds include the above-described adsorptive groups having a mercapto group or thione group as a partial structure (for example, a ring-forming thioamide group, an alkyl mercapto group, an aryl mercapto group, a heterocyclic mercapto group, etc.) Or a compound having two or more mercapto groups or thione groups as a partial structure (for example, a dimercapto-substituted nitrogen-containing heterocyclic group), You may have one or more.
[0210]
Examples of the adsorptive group having two or more mercapto groups as a partial structure (such as a dimercapto-substituted nitrogen-containing heterocyclic group) include 2,4-dimercaptopyrimidine group, 2,4-dimercaptotriazine group, 3,5 -Dimercapto-1,2,4-triazole group, 2,5-dimercapto-1,3-thiazole group, 2,5-dimercapto-1,3-oxazole group, 2,7-dimercapto-5-methyl-s- Triazolo (1,5-A) -pyrimidine, 2,6,8-trimercaptopurine, 6,8-dimercaptopurine, 3,5,7-trimercapto-s-triazolotriazine, 4,6-dimercapto And pyrazolopyrimidine, 2,5-dimercaptoimidazole, and the like. 2,4-dimercaptopyrimidine group, 2,4-dimercaptotriazine group, 3, - dimercapto-1,2,4-triazole group are particularly preferred.
[0211]
The adsorptive group may be substituted anywhere in the general formulas (A) to (F) and the general formulas (1) to (3), but in the general formulas (A) to (D), RED₁₁, RED₁₂, RED₂, RED₃In the general formulas (E) and (F), RED₄₁, R₄₁, RED₄₂, R₄₆~ R₄₈In the general formulas (1) to (3), R₁, R₂, R₁₁, R₁₂, R₃₁, L₁, L₂₁, L₃₁It is preferably substituted at any position except for RED, and RED in all of the general formulas (A) to (F)₁₁~ RED₄₂More preferably, it is substituted.
[0212]
The partial structure of the spectral sensitizing dye is a group containing a chromophore of the spectral sensitizing dye, and is a residue obtained by removing any hydrogen atom or substituent from the spectral sensitizing dye compound. The partial structure of the spectral sensitizing dye may be substituted anywhere in the general formulas (A) to (F) and the general formulas (1) to (3), but in the general formulas (A) to (D), RED₁₁, RED₁₂, RED₂, RED₃In the general formulas (E) and (F), RED₄₁, R₄₁, RED₄₂, R₄₆~ R₄₈In the general formulas (1) to (3), R₁, R₂, R₁₁, R₁₂, R₃₁, L₁, L₂₁, L₃₁It is preferably substituted at any position except for RED, and RED in all of the general formulas (A) to (F)₁₁~ RED₄₂More preferably, it is substituted.
[0213]
Preferred spectral sensitizing dyes are spectral sensitizing dyes typically used in color sensitization techniques such as cyanine dyes, complex cyanine dyes, merocyanine dyes, complex merocyanine dyes, homopolar cyanine dyes, Includes styryl dyes and hemicyanine dyes. Exemplary spectral sensitizing dyes are disclosed in Research Disclosure, Item 36544, September 1994. Research Disclosure or F.I. M.M. One of ordinary skill in the art can synthesize these dyes by the procedure described in Hammer's The Cyanines and Related Compounds (Interscience Publishers, New yprk, 1964). Further, all the dyes described in JP-A-11-95355 (US Pat. No. 6,054,260), pages 7 to 14 are applied as they are.
[0214]
The compounds of types 1 to 4 of the present invention preferably have a total carbon number of 10 to 60. More preferably, it is 15-50, More preferably, it is 18-40, Most preferably, it is 18-30.
[0215]
The compounds of types 1 to 4 of the present invention are subjected to 1-electron oxidation triggered by exposure of the silver halide photographic light-sensitive material using the compound, and after the subsequent reaction, further 1 electron, or 2 electrons or more depending on the type. Electrons are emitted and oxidized, and the oxidation potential of the first electron is preferably about 1.4 V or less, and more preferably 1.0 V or less. This oxidation potential is preferably higher than 0V, more preferably higher than 0.3V. Accordingly, the oxidation potential is preferably in the range of about 0 to about 1.4V, more preferably about 0.3 to about 1.0V.
[0216]
Here, the oxidation potential can be measured by a cyclic voltammetry technique. Specifically, a sample is dissolved in a solution of acetonitrile: water (including 0.1 M lithium perchlorate) = 80%: 20% (volume%). After bubbling nitrogen gas for 10 minutes, a glassy carbon disk was used as the working electrode, a platinum wire was used as the counter electrode, and a calomel electrode (SCE) was used as the reference electrode at 25 ° C. and 0.1 V / Measured at a potential scanning speed of seconds. The oxidation potential versus SCE is taken at the peak potential of the cyclic voltammetry wave.
[0217]
In the case where the compounds of types 1 to 4 of the present invention are one-electron oxidized and further emit one electron after the subsequent reaction, the subsequent oxidation potential is preferably −0.5 V to −2 V. More preferably, it is -0.7V--2V, More preferably, it is -0.9V--1.6V.
[0218]
In the case where the compound of types 1 to 4 of the present invention is a compound that is oxidized by one electron and emits two or more electrons after the subsequent reaction and is oxidized, there is no particular limitation on the oxidation potential of this latter stage. Absent. This is because the oxidation potential of the second electron and the oxidation potential of the third and subsequent electrons cannot be clearly distinguished, and it is often difficult to accurately measure and distinguish these actually.
[0219]
Next, the compound of type 5 will be described.
A compound of type 5 is represented by XY, where X represents a reducing group, Y represents a leaving group, and a one-electron oxidant produced by one-electron oxidation of the reducing group represented by X is This is a compound capable of releasing X by further elimination of Y with subsequent XY bond cleavage reaction to generate an X radical, from which another electron is emitted. The reaction when such a type 5 compound is oxidized can be represented by the following formula.
[0220]
Embedded image

[0221]
The compound of type 5 preferably has an oxidation potential of 0 to 1.4V, more preferably 0.3V to 1.0V. The oxidation potential of the radical X · generated in the above reaction formula is preferably −0.7 V to −2.0 V, more preferably −0.9 V to −1.6 V.
[0222]
The compound of type 5 is preferably represented by the general formula (G).
[0223]
General formula (G)
Embedded image

[0224]
In general formula (G), RED₀Represents a reducing group, L₀Represents a leaving group, R₀And R₀₀Represents a hydrogen atom or a substituent. RED₀  And R₀And R₀And R₀₀And may be bonded to each other to form a ring structure. RED₀Is RED of general formula (C)₂Represents the same group, and the preferred range is also the same. R₀And R₀₀Is R in the general formula (C)₂₁And R₂₂The preferred range is also the same. However, R₀And R₀₀Except for the hydrogen atom, L₀Does not represent the same group as RED₀And R₀May be bonded to each other to form a ring structure, and examples of the ring structure include RED of the general formula (C).₂And R₂₁Examples are the same as in the case of linking to form a ring structure, and the preferred range is also the same. R₀And R₀₀Examples of the ring structure formed by bonding to each other include a cyclopentane ring and a tetrahydrofuran ring. In general formula (G), L₀Is L in the general formula (C)₂The preferred range is also the same.
[0225]
The compound represented by the general formula (G) preferably has an adsorbing group for silver halide or a partial structure of a spectral sensitizing dye in the molecule.₀When represents a group other than a silyl group, it does not have two or more adsorptive groups in the molecule at the same time. However, the sulfide group as the adsorptive group here is L₀You may have two or more regardless of this.
[0226]
Examples of the adsorptive group to the silver halide of the compound represented by the general formula (G) include the same adsorptive groups that the compounds of types 1 to 4 of the present invention may have. In addition, all those described as “silver halide adsorbing groups” on pages 4 to 7 of JP-A No. 11-95355 can be mentioned, and preferred ranges are also the same.
The partial structure of the spectral sensitizing dye that the compound represented by the general formula (G) may have is the partial structure of the spectral sensitizing dye that the compounds of types 1 to 4 of the present invention may have. However, at the same time, all those described as “light-absorbing groups” on pages 7 to 14 of JP-A No. 11-95355 can be mentioned, and preferred ranges are also the same.
[0227]
Specific examples of the compounds of types 1 to 5 of the present invention are listed below, but the present invention is not limited thereto.
[0228]
Embedded image

[0229]
Embedded image

[0230]
Embedded image

[0231]
Embedded image

[0232]
The compounds of types 1 to 4 of the present invention are described in detail in Japanese Patent Application No. 2002-192373, Japanese Patent Application No. 2002-188537, Japanese Patent Application No. 2002-188536, Japanese Patent Application No. 2001-272137, and Japanese Patent Application No. 2002-192374, respectively. Same as described compound. Specific compound examples described in these patent application specifications can also be given as specific examples of the compounds of types 1 to 4 of the present invention. The synthesis examples of the compounds of types 1 to 4 of the present invention are also the same as those described in these patents.
[0233]
Specific examples of the compound of type 5 of the present invention are further described in JP-A-9-211769 (compounds PMT-1 to S-37 described in Table E and Table F on pages 28-32), JP-A-9-21774. JP-A-11-95355 (compounds INV1-36), JP-T-2001-99696 (compounds 1-74, 80-87, 92-122), US Pat. No. 5,747,235, US Pat. No. 5,747, No. 236, European Patent No. 786692A1 (compounds INV1 to 35), European Patent No. 893732A1, US Pat. No. 6,054,260, US Pat. No. 5,994,051, etc. Examples of compounds referred to as “deprotonated electron donating sensitizers” are mentioned as they are.
[0234]
The compounds of types 1 to 5 of the present invention may be used at any time during the process of producing a photothermographic material when preparing a photosensitive silver halide emulsion. For example, at the time of photosensitive silver halide grain formation, desalting step, chemical sensitization, before coating. Moreover, it can also add in several steps in these processes. The addition position is preferably from the end of formation of the photosensitive silver halide grains to before the desalting step, at the time of chemical sensitization (immediately after the start of chemical sensitization to immediately after completion), and before coating, more preferably from the time of chemical sensitization Until before mixing with the non-photosensitive organic silver salt.
[0235]
The compounds of types 1 to 5 of the present invention are preferably added after being dissolved in water, a water-soluble solvent such as methanol or ethanol, or a mixed solvent thereof. When the compound is dissolved in water, the compound having higher solubility when the pH is increased or decreased may be dissolved at a higher or lower pH and added.
[0236]
The compounds of types 1 to 5 of the present invention are preferably used in an I image-forming layer containing photosensitive silver halide and non-photosensitive organic silver salt, but photosensitive silver halide and non-photosensitive organic silver salt It may be added to the protective layer and the intermediate layer together with the I image forming layer containing, and diffused during coating. The timing of addition of the compound of the present invention is preferably before or after the sensitizing dye, and preferably 1 × 10 5 per mole of silver halide.^-9Mol ~ 5x10^-1Mole, more preferably 1 × 10^-8Mol ~ 5x10^-2It is contained in the silver halide I image forming layer in a molar ratio.
[0237]
10) adsorptive redox compounds having adsorbing groups and reducing groups
In the present invention, it is preferable to contain an adsorptive redox compound having an adsorbing group for silver and a reducing group in the molecule. The adsorptive redox compound is preferably a compound represented by the following formula (I).
[0238]
Formula (I) A- (W) n-B
[In Formula (I), A represents a group capable of being adsorbed to silver halide (hereinafter referred to as an adsorbing group), W represents a divalent linking group, n represents 0 or 1, and B represents a reducing group. Represents. ]
[0239]
In formula (I), the adsorptive group represented by A is a group that directly adsorbs to silver halide or a group that promotes adsorption to silver halide. Specifically, a mercapto group (or a salt thereof) , A thione group (—C (═S) —), a heterocyclic group, a sulfide group, a disulfide group, a cationic group, or an ethynyl group containing at least one atom selected from a nitrogen atom, a sulfur atom, a selenium atom, and a tellurium atom Etc.
[0240]
The mercapto group (or salt thereof) as the adsorptive group means the mercapto group (or salt thereof) itself, and more preferably, a heterocyclic group or aryl group substituted with at least one mercapto group (or salt thereof) or Represents an alkyl group. Here, the heterocyclic group is at least a 5- to 7-membered monocyclic or condensed aromatic or non-aromatic heterocyclic group such as an imidazole ring group, a thiazole ring group, an oxazole ring group, or a benzimidazole ring. Group, benzothiazole ring group, benzoxazole ring group, triazole ring group, thiadiazole ring group, oxadiazole ring group, tetrazole ring group, purine ring group, pyridine ring group, quinoline ring group, isoquinoline ring group, pyrimidine ring group, And triazine ring group. Further, it may be a heterocyclic group containing a quaternized nitrogen atom. In this case, the substituted mercapto group may be dissociated to form a meso ion. When the mercapto group forms a salt, the counter ion is a cation such as an alkali metal, alkaline earth metal, or heavy metal (Li⁺, Na⁺, K⁺, Mg²⁺, Ag⁺, Zn²⁺And the like, ammonium ions, quaternized heterocyclic groups containing nitrogen atoms, phosphonium ions, and the like.
[0241]
Further, the mercapto group as the adsorptive group may be tautomerized into a thione group.
[0242]
The thione group as the adsorptive group also includes a chain or cyclic thioamide group, thioureido group, thiourethane group, or dithiocarbamate group.
[0243]
A heterocyclic group containing at least one atom selected from a nitrogen atom, a sulfur atom, a selenium atom and a tellurium atom as an adsorptive group is a -NH- group capable of forming imino silver (> NAg) as a partial structure of the heterocyclic ring. A nitrogen-containing heterocyclic group having a heterocyclic ring, or a "-S-" group, a "-Se-" group, a "-Te-" group or a "= N-" group capable of coordinating to a silver ion by a coordination bond A heterocyclic group having a partial structure of benzotriazole group, triazole group, indazole group, pyrazole group, tetrazole group, benzimidazole group, imidazole group, purine group, etc. , Thiazole group, oxazole group, benzothiophene group, benzothiazole group, benzoxazole group, thiadiazole group, oxadiazo Group, a triazine group, seleno azole group, benzoselenazole group, tellurium azole group, such as benzo tellurium azole group.
[0244]
Examples of the sulfide group or disulfide group as the adsorbing group include all groups having a partial structure of “—S—” or “—S—S—”.
[0245]
The cationic group as the adsorptive group means a group containing a quaternized nitrogen atom, specifically, an ammonio group or a group containing a nitrogen-containing heterocyclic group containing a quaternized nitrogen atom. Examples of the nitrogen-containing heterocyclic group containing a quaternized nitrogen atom include a pyridinio group, a quinolinio group, an isoquinolinio group, an imidazolio group, and the like. An ethynyl group as an adsorptive group means a —C≡CH group, and the hydrogen atom may be substituted.
[0246]
The adsorbing group may have an arbitrary substituent.
[0247]
Further, specific examples of the adsorbing group include those described in the specifications p4 to p7 of JP-A No. 11-95355.
[0248]
In the formula (I), preferred as the adsorptive group represented by A is a mercapto-substituted heterocyclic group (for example, 2-mercaptothiadiazole group, 2-mercapto-5-aminothiadiazole group, 3-mercapto-1,2,4). -Triazole group, 5-mercaptotetrazole group, 2-mercapto-1,3,4-oxadiazole group, 2-mercaptobenzimidazole group, 1,5-dimethyl-1,2,4-triazolium-3-thiolate group 2,4-dimercaptopyrimidine group, 2,4-dimercaptotriazine group, 3,5-dimercapto-1,2,4-triazole group, 2,5-dimercapto-1,3-thiazole group), or Nitrogen-containing heterocyclic groups having —NH— groups that can form imino silver (> NAg) as a heterocyclic partial structure (for example, benzotria) Lumpur group, benzimidazole group, an indazole group), more preferable as an adsorptive group is a 2-mercaptobenzimidazole group, a 3,5-dimercapto-1,2,4-triazole group.
[0249]
In formula (I), W represents a divalent linking group. Any linking group may be used as long as it does not adversely affect photographic properties. For example, a divalent linking group composed of a carbon atom, a hydrogen atom, an oxygen atom, a nitrogen atom, or a sulfur atom can be used. Specifically, an alkylene group having 1 to 20 carbon atoms (for example, a methylene group, an ethylene group, a trimethylene group, a tetramethylene group, a hexamethylene group, etc.), an alkenylene group having 2 to 20 carbon atoms, and an alkynylene group having 2 to 20 carbon atoms. An arylene group having 6 to 20 carbon atoms (for example, a phenylene group, a naphthylene group, etc.), -CO-, -SO₂-, -O-, -S-, -NR₁-, The combination of these coupling groups, etc. are mention | raise | lifted. Where R₁Represents a hydrogen atom, an alkyl group, a heterocyclic group, or an aryl group.
The linking group represented by W may have an arbitrary substituent.
[0250]
In formula (I), the reducing group represented by B represents a group capable of reducing silver ions. For example, a triple bond group such as formyl group, amino group, acetylene group or propargyl group, mercapto group, hydroxylamines. Hydroxamic acids, hydroxyureas, hydroxyurethanes, hydroxysemicarbazides, reductones (including reductone derivatives), anilines, phenols (chroman-6-ols, 2,3-dihydrobenzofuran-5-ols, Aminophenols, sulfonamidophenols, and hydroquinones, catechols, resorcinols, benzenetriols, polyphenols such as bisphenols), acylhydrazines, carbamoylhydrazines, 3-pyrazolidones, etc. The residue after removing one And the like. Of course, these may have an arbitrary substituent.
[0251]
In the formula (I), the reducing group represented by B shows its oxidation potential by Akira Fujishima “Electrochemical measurement method” (pages 150-208, published by Gihodo) or “The Experimental Chemistry Course” edited by the Chemical Society of Japan, 4th edition ( 9 pages 282-344, Maruzen). For example, by a rotating disk voltammetry technique, specifically, a sample is dissolved in a solution of methanol: pH 6.5 Briton-Robinson buffer = 10%: 90% (volume%), and nitrogen gas is used for 10 minutes. , A glassy carbon rotating disk electrode (RDE) is used as a working electrode, a platinum wire is used as a counter electrode, a saturated calomel electrode is used as a reference electrode, 25 ° C., 1000 rev / min, 20 mV / sec. Can be measured at sweep speed. A half-wave potential (E1 / 2) can be obtained from the obtained voltammogram.
[0252]
The reducing group represented by B of the present invention preferably has an oxidation potential in the range of about -0.3 V to about 1.0 V when measured by the above-described measurement method. More preferably, it is in the range of about -0.1V to about 0.8V, and particularly preferably in the range of about 0 to about 0.7V.
[0253]
In the formula (I), the reducing group represented by B is preferably selected from hydroxylamines, hydroxamic acids, hydroxyureas, hydroxysemicarbazides, reductones, phenols, acylhydrazines, carbamoylhydrazines, and 3-pyrazolidones. A residue obtained by removing one hydrogen atom.
[0254]
Specific examples of the reducing group represented by B are illustrated below, but the present invention is not limited thereto. Here, * indicates a position where A or W is bonded in Formula (I).
[0255]
Embedded image

[0256]
The compound of the formula (I) of the present invention may be one in which a ballast group or a polymer chain commonly used in an immobile photographic additive such as a coupler is incorporated. Examples of the polymer include those described in JP-A-1-100530.
[0257]
The compound of the formula (I) of the present invention may be a bis form or a tris form. The molecular weight of the compound of formula (I) of the present invention is preferably between 100 and 10,000, more preferably between 120 and 1000, particularly preferably between 150 and 500.
[0258]
Examples of the compound of formula (I) of the present invention are shown below, but the present invention is not limited thereto.
[0259]
Embedded image

[0260]
Embedded image

[0261]
Embedded image

[0262]
Embedded image

[0263]
Embedded image

[0264]
Embedded image

[0265]
Embedded image

[0266]
Embedded image

[0267]
The compounds of the present invention can be easily synthesized according to known methods.
As the compound of the formula (I) of the present invention, one kind of compound may be used alone, but it is also preferred to use two or more kinds of compounds at the same time. When two or more kinds of compounds are used, they may be added in the same layer or in different layers, and the addition method may be different.
[0268]
The compound of formula (I) of the present invention is preferably added to a layer containing a photosensitive silver halide emulsion, and more preferably added during preparation of the emulsion. When added at the time of emulsion preparation, it can be added at any time during the process. For example, silver halide grain formation process, before the start of desalting process, desalting process, chemical ripening Examples include a step before starting, a chemical ripening step, and a step before preparing a finished emulsion. Moreover, it can also be added in several steps in these processes.
The compound of the formula (I) of the present invention is preferably used in an image forming layer, but may be added to an adjacent protective layer or intermediate layer together with the image forming layer and diffused during coating.
[0269]
The preferred addition amount largely depends on the above-mentioned addition method and the kind of compound to be added, but generally 1 × 10 5 per mole of photosensitive silver halide.^-6Mol to 1 mol, preferably 1 × 10^-5Mol ~ 5x10^-1Mole more preferably 1 × 10^-4Mol ~ 1 × 10^-1Is a mole.
[0270]
The compound of the formula (I) of the present invention can be added after being dissolved in water, a water-soluble solvent such as methanol or ethanol, or a mixed solvent thereof. At this time, the pH may be appropriately adjusted with an acid or a base, and a surfactant may be allowed to coexist. Furthermore, it can also be dissolved in a high boiling point organic solvent and added as an emulsified dispersion. It can also be added as a solid dispersion.
[0271]
11) Sensitizing dye
As a sensitizing dye that can be applied to the present invention, it can spectrally sensitize silver halide grains in a desired wavelength region when adsorbed on silver halide grains, and has a spectral sensitivity suitable for the spectral characteristics of the exposure light source. The dye can be advantageously selected. The photothermographic material of the present invention is preferably spectrally sensitized so as to have a spectral sensitivity peak at 600 nm to 900 nm, or 300 nm to 500 nm. Regarding the sensitizing dye and the addition method, paragraphs 0103 to 0109 of JP-A-11-65021, compounds represented by the general formula (II) of JP-A-10-186572, and general formulas (I) of JP-A-11-119374 ) And dyes described in paragraph No. 0106, U.S. Pat. Nos. 5,510,236 and 3,871,887, Example 5, JP-A-2-96131, JP-A-59-48753 Dyes disclosed in Japanese Patent Application No. 0803764A1, page 19, line 38 to page 20, line 35, Japanese Patent Application No. 2000-86865, Japanese Patent Application No. 2000-102560, Japanese Patent Application No. 2000-205399, etc. It is described in. These sensitizing dyes may be used alone or in combination of two or more.
[0272]
The addition amount of the sensitizing dye in the present invention can be set to a desired amount in accordance with the sensitivity and the fogging performance, but is 10 per mol of silver halide in the photosensitive layer.^-6~ 1 mol is preferred, more preferably 10^-4-10^-1Is a mole.
[0273]
In the present invention, a supersensitizer can be used to improve spectral sensitization efficiency. As the supersensitizer used in the present invention, European Patent Publication No. 587,338, US Pat. Nos. 3,877,943, 4,873,184, JP-A-5-341432, 11- 109547, 10-111543, etc. are mentioned.
[0274]
12) Combined use of silver halide
The photosensitive silver halide emulsion in the photothermographic material used in the present invention may be one kind or two or more kinds (for example, those having different average grain sizes, those having different halogen compositions, those having different crystal habits, Those having different chemical sensitization conditions) may be used in combination. The gradation can be adjusted by using a plurality of types of photosensitive silver halides having different sensitivities. Examples of these technologies include JP-A-57-119341, 53-106125, 47-3929, 48-55730, 46-5187, 50-73627, 57-150841 and the like. Can be mentioned. The sensitivity difference is preferably 0.2 log E or more for each emulsion.
[0275]
13) Mixing of silver halide and organic silver salt
The photosensitive silver halide grains of the present invention are particularly preferably formed and chemically sensitized in the absence of a non-photosensitive organic silver salt. This is because sufficient sensitivity may not be achieved by the method of forming silver halide by adding a halogenating agent to the organic silver salt.
As a method of mixing silver halide and organic silver salt, a method of mixing separately prepared photosensitive silver halide and organic silver salt with a high speed stirrer, ball mill, sand mill, colloid mill, vibration mill, homogenizer, etc. Alternatively, there may be mentioned a method of preparing an organic silver salt by mixing photosensitive silver halide which has been prepared at any timing during the preparation of the organic silver salt. In any method, the effects of the present invention can be preferably obtained.
[0276]
14) Mixing silver halide into coating solution
The preferred addition timing of the silver halide of the present invention to the image forming layer coating solution is from 180 minutes before coating to immediately before, preferably from 60 minutes to 10 seconds before coating. There is no particular limitation as long as the effect is sufficiently exhibited. Specific mixing methods include mixing in a tank in which the average residence time calculated from the addition flow rate and the amount of liquid fed to the coater is a desired time, and N.I. Harnby, M.M. F. Edwards, A.D. W. There is a method using a static mixer described in Chapter 8 of Nienow's Koji Takahashi "Liquid Mixing Technology" (published by Nikkan Kogyo Shimbun, 1989).
[0277]
(Description of development accelerator)
In the photothermographic material of the present invention, a sulfonamide phenol compound represented by the general formula (A) described in JP-A-2000-267222, JP-A-2000-330234, or the like as a development accelerator, Hindered phenol compounds represented by general formula (II) described in JP-A-2001-92075, general formula (I) described in JP-A-10-62895, JP-A-11-15116, and the like, A hydrazine-based compound represented by the general formula (D) of JP-A No. 2002-156727 or the general formula (1) described in Japanese Patent Application No. 2001-074278, and described in the specification of JP-A No. 2001-264929 A phenolic or naphtholic compound represented by the general formula (2) is preferably used. These development accelerators are used in the range of 0.1 mol% to 20 mol% with respect to the reducing agent, preferably in the range of 0.5 mol% to 10 mol%, more preferably 1 mol% to 5 mol. % Range. The introduction method to the light-sensitive material includes the same method as the reducing agent, but it is particularly preferable to add as a solid dispersion or an emulsified dispersion. When added as an emulsified dispersion, it is added as an emulsified dispersion dispersed using a high-boiling solvent and a low-boiling auxiliary solvent that are solid at room temperature, or as a so-called oilless emulsified dispersion that does not use a high-boiling solvent. It is preferable to add.
In the present invention, among the development accelerators described above, hydrazine compounds represented by the general formula (D) described in JP-A No. 2002-156727 and those described in JP-A No. 2001-264929 A phenol-based or naphthol-based compound represented by the formula (2) is more preferable.
[0278]
Particularly preferred development accelerators of the present invention are compounds represented by the following general formulas (A-1) and (A-2).
Formula (A-1)
Q₁-NHNH-Q₂
(Where Q₁Is a carbon atom -NHNH-Q₂Represents an aromatic group or a heterocyclic group bonded to₂Represents a carbamoyl group, an acyl group, an alkoxycarbonyl group, an aryloxycarbonyl group, a sulfonyl group, or a sulfamoyl group. )
[0279]
In general formula (A-1), Q₁The aromatic group or heterocyclic group represented by is preferably a 5- to 7-membered unsaturated ring. Preferred examples include benzene ring, pyridine ring, pyrazine ring, pyrimidine ring, pyridazine ring, 1,2,4-triazine ring, 1,3,5-triazine ring, pyrrole ring, imidazole ring, pyrazole ring, 1,2 , 3-triazole ring, 1,2,4-triazole ring, tetrazole ring, 1,3,4-thiadiazole ring, 1,2,4-thiadiazole ring, 1,2,5-thiadiazole ring, 1,3,4 -Oxadiazole ring, 1,2,4-oxadiazole ring, 1,2,5-oxadiazole ring, thiazole ring, oxazole ring, isothiazole ring, isoxazole ring, thiophene ring, etc. are preferable, and these Also preferred are fused rings in which the rings are fused together.
[0280]
These rings may have a substituent, and when they have two or more substituents, these substituents may be the same or different. Examples of substituents include halogen atoms, alkyl groups, aryl groups, carbonamido groups, alkylsulfonamido groups, arylsulfonamido groups, alkoxy groups, aryloxy groups, alkylthio groups, arylthio groups, carbamoyl groups, sulfamoyl groups, cyano Groups, alkylsulfonyl groups, arylsulfonyl groups, alkoxycarbonyl groups, aryloxycarbonyl groups, and acyl groups. When these substituents are substitutable groups, they may further have substituents. Examples of preferred substituents include halogen atoms, alkyl groups, aryl groups, carbonamido groups, alkylsulfonamido groups, aryls. Sulfonamide group, alkoxy group, aryloxy group, alkylthio group, arylthio group, acyl group, alkoxycarbonyl group, aryloxycarbonyl group, carbamoyl group, cyano group, sulfamoyl group, alkylsulfonyl group, arylsulfonyl group, and acyloxy group Can be mentioned.
[0281]
Q₂Is preferably a carbamoyl group having 1 to 50 carbon atoms, more preferably 6 to 40 carbon atoms, such as unsubstituted carbamoyl, methylcarbamoyl, N-ethylcarbamoyl, N-propylcarbamoyl, N -Sec-butylcarbamoyl, N-octylcarbamoyl, N-cyclohexylcarbamoyl, N-tert-butylcarbamoyl, N-dodecylcarbamoyl, N- (3-dodecyloxypropyl) carbamoyl, N-octadecylcarbamoyl, N- {3- ( 2,4-tert-pentylphenoxy) propyl} carbamoyl, N- (2-hexyldecyl) carbamoyl, N-phenylcarbamoyl, N- (4-dodecyloxyphenyl) carbamoyl, N- (2-chloro-5-dodecyloxy) Carbonyl Eniru) carbamoyl, N- naphthylcarbamoyl, N-3- pyridylcarbamoyl include N- benzylcarbamoyl.
[0282]
Q₂Is preferably an acyl group having 1 to 50 carbon atoms, more preferably 6 to 40 carbon atoms. For example, formyl, acetyl, 2-methylpropanoyl, cyclohexylcarbonyl, octanoyl, 2-hexyl. Examples include decanoyl, dodecanoyl, chloroacetyl, trifluoroacetyl, benzoyl, 4-dodecyloxybenzoyl, and 2-hydroxymethylbenzoyl. The alkoxycarbonyl group represented by Q2 is preferably an alkoxycarbonyl group having 2 to 50 carbon atoms, more preferably 6 to 40 carbon atoms, such as methoxycarbonyl, ethoxycarbonyl, isobutyloxycarbonyl, cyclohexyloxycarbonyl, dodecyl. Examples include oxycarbonyl and benzyloxycarbonyl.
[0283]
Q₂Is preferably an aryloxycarbonyl group having 7 to 50 carbon atoms, more preferably 7 to 40 carbon atoms, such as phenoxycarbonyl, 4-octyloxyphenoxycarbonyl, 2-hydroxymethylphenoxy. Examples include carbonyl and 4-dodecyloxyphenoxycarbonyl. The sulfonyl group represented by Q2 is preferably a sulfonyl group having 1 to 50 carbon atoms, more preferably 6 to 40 carbon atoms, such as methylsulfonyl, butylsulfonyl, octylsulfonyl, 2-hexadecylsulfonyl, 3-dodecyl. Examples include oxypropylsulfonyl, 2-octyloxy-5-tert-octylphenylsulfonyl, and 4-dodecyloxyphenylsulfonyl.
[0284]
Q₂Is preferably a sulfamoyl group having 0 to 50 carbon atoms, more preferably 6 to 40 carbon atoms, such as an unsubstituted sulfamoyl group, an N-ethylsulfamoyl group, or N- (2-ethylhexyl). Sulfamoyl, N-decylsulfamoyl, N-hexadecylsulfamoyl, N- {3- (2-ethylhexyloxy) propyl} sulfamoyl, N- (2-chloro-5-dodecyloxycarbonylphenyl) sulfamoyl, N- (2-tetradecyloxyphenyl) sulfamoyl. Q₂In the group represented by₁May have the groups mentioned as examples of the substituents of the 5- to 7-membered unsaturated ring represented by the formula (1), and when they have two or more substituents, these substituents are the same. Or different.
[0285]
Next, a preferable range of the compound represented by formula (A-1) is described. Q₁Is preferably a 5- to 6-membered unsaturated ring, such as a benzene ring, pyrimidine ring, 1,2,3-triazole ring, 1,2,4-triazole ring, tetrazole ring, 1,3,4-thiadiazole ring, 1 , 2,4-thiadiazole ring, 1,3,4-oxadiazole ring, 1,2,4-oxadiazole ring, thiazole ring, oxazole ring, isothiazole ring, isoxazole ring, and these rings are benzene More preferred is a ring fused to a ring or an unsaturated heterocycle. Q₂Is preferably a carbamoyl group, particularly preferably a carbamoyl group having a hydrogen atom on a nitrogen atom.
[0286]
Formula (A-2)
Embedded image

[0287]
In the general formula (A-2), R₁Represents an alkyl group, an acyl group, an acylamino group, a sulfonamide group, an alkoxycarbonyl group, or a carbamoyl group. R₂Represents a hydrogen atom, a halogen atom, an alkyl group, an alkoxy group, an aryloxy group, an alkylthio group, an arylthio group, an acyloxy group, or a carbonate group. R₃, R₄Each represents a group capable of substituting for the benzene ring mentioned in the example of the substituent of formula (A-1). R₃And R₄May be linked together to form a condensed ring.
[0288]
R₁Is preferably an alkyl group having 1 to 20 carbon atoms (for example, methyl group, ethyl group, isopropyl group, butyl group, tert-octyl group, cyclohexyl group, etc.), acylamino group (for example, acetylamino group, benzoylamino group, methylureido group). , 4-cyanophenylureido group, etc.), carbamoyl group (n-butylcarbamoyl group, N, N-diethylcarbamoyl group, phenylcarbamoyl group, 2-chlorophenylcarbamoyl group, 2,4-dichlorophenylcarbamoyl group, etc.) and acylamino group ( More preferred are ureido groups and urethane groups). R2 is preferably a halogen atom (more preferably a chlorine atom or a bromine atom), an alkoxy group (for example, methoxy group, butoxy group, n-hexyloxy group, n-decyloxy group, cyclohexyloxy group, benzyloxy group, etc.), aryloxy A group (phenoxy group, naphthoxy group, etc.).
[0289]
R₃Is preferably a hydrogen atom, a halogen atom, or an alkyl group having 1 to 20 carbon atoms, and most preferably a halogen atom. R₄Is preferably a hydrogen atom, an alkyl group or an acylamino group, more preferably an alkyl group or an acylamino group. Examples of these preferred substituents are R₁It is the same. R₄R is an acylamino group₄Is R₃It is also preferred to form a carbostyryl ring by linking with.
[0290]
In the general formula (A-2), R₃And R₄Are connected to each other to form a condensed ring, the naphthalene ring is particularly preferable as the condensed ring. The same substituent as the example of a substituent quoted by general formula (A-1) may couple | bond with the naphthalene ring. When general formula (A-2) is a naphtholic compound, R₁Is preferably a carbamoyl group. Of these, a benzoyl group is particularly preferable. R₂Is preferably an alkoxy group or an aryloxy group, particularly preferably an alkoxy group.
[0291]
Hereinafter, preferred specific examples of the development accelerator of the present invention will be given. The present invention is not limited to these.
[0292]
Embedded image

[0293]
(Description of hydrogen bonding compounds)
When the reducing agent in the present invention has an aromatic hydroxyl group (—OH) or an amino group (—NHR, R is a hydrogen atom or an alkyl group), particularly in the case of the aforementioned bisphenols, these groups and hydrogen bonds It is preferable to use together a non-reducing compound having a group capable of forming.
Examples of the group that forms a hydrogen bond with a hydroxyl group or an amino group include a phosphoryl group, a sulfoxide group, a sulfonyl group, a carbonyl group, an amide group, an ester group, a urethane group, a ureido group, a tertiary amino group, and a nitrogen-containing aromatic group. Can be mentioned. Among them, preferred are a phosphoryl group, a sulfoxide group, an amide group (however, it has no> N—H group and is blocked like> N—Ra (Ra is a substituent other than H)), a urethane group. (However, it has no> N—H group and is blocked like> N—Ra (Ra is a substituent other than H)), a ureido group (however, it has no> N—H group,> N-Ra (Ra is a substituent other than H).)
In the present invention, a particularly preferred hydrogen bonding compound is a compound represented by the following general formula (D).
[0294]
Formula (D)
Embedded image

[0295]
R in general formula (D)²¹Or R²³Each independently represents an alkyl group, an aryl group, an alkoxy group, an aryloxy group, an amino group or a heterocyclic group, and these groups may be unsubstituted or may have a substituent.
R²¹Or R²³In the case where has a substituent, the substituent is a halogen atom, alkyl group, aryl group, alkoxy group, amino group, acyl group, acylamino group, alkylthio group, arylthio group, sulfonamido group, acyloxy group, oxycarbonyl group, carbamoyl Group, sulfamoyl group, sulfonyl group, phosphoryl group and the like. Preferred as substituents are alkyl groups or aryl groups such as methyl group, ethyl group, isopropyl group, t-butyl group, t-octyl group, phenyl group, 4-alkoxyphenyl group, 4-acyloxyphenyl group and the like can be mentioned.
[0296]
R²¹Or R²³Specific examples of the alkyl group include methyl group, ethyl group, butyl group, octyl group, dodecyl group, isopropyl group, t-butyl group, t-amyl group, t-octyl group, cyclohexyl group, and 1-methylcyclohexyl group. Benzyl group, phenethyl group, 2-phenoxypropyl group, and the like.
Examples of the aryl group include phenyl group, cresyl group, xylyl group, naphthyl group, 4-t-butylphenyl group, 4-t-octylphenyl group, 4-anisidyl group, and 3,5-dichlorophenyl group.
[0297]
Alkoxy groups include methoxy, ethoxy, butoxy, octyloxy, 2-ethylhexyloxy, 3,5,5-trimethylhexyloxy, dodecyloxy, cyclohexyloxy, 4-methylcyclohexyloxy, benzyl An oxy group etc. are mentioned.
Examples of the aryloxy group include a phenoxy group, a cresyloxy group, an isopropylphenoxy group, a 4-t-butylphenoxy group, a naphthoxy group, and a biphenyloxy group.
Examples of the amino group include a dimethylamino group, a diethylamino group, a dibutylamino group, a dioctylamino group, an N-methyl-N-hexylamino group, a dicyclohexylamino group, a diphenylamino group, and an N-methyl-N-phenylamino group. .
[0298]
R²¹Or R²³Are preferably an alkyl group, an aryl group, an alkoxy group, or an aryloxy group. In terms of the effect of the present invention, R²¹Or R²³Of these, at least one is preferably an alkyl group or an aryl group, and more preferably two or more are an alkyl group or an aryl group. In addition, R can be obtained at low cost.²¹Or R²³Are preferably the same group.
[0299]
Specific examples of the hydrogen bonding compound including the compound of the general formula (D) in the present invention are shown below, but the present invention is not limited thereto.
[0300]
Embedded image

[0301]
Specific examples of the hydrogen bonding compound include those described in European Patent No. 1096310, Japanese Patent Application Laid-Open No. 2002-156727, and Japanese Patent Application No. 2001-12496 in addition to the above.
The compound of the general formula (D) of the present invention can be used in a light-sensitive material by being incorporated in a coating solution in the form of a solution, an emulsified dispersion, or a solid dispersion fine particle dispersion in the same manner as the reducing agent. It is preferable to use it as a product. The compound of the present invention forms a hydrogen-bonding complex with a compound having a phenolic hydroxyl group or an amino group in a solution state, and depending on the combination of the reducing agent and the compound of the general formula (D) of the present invention, It can be isolated in the crystalline state.
[0302]
The use of the crystal powder isolated in this way as a solid dispersed fine particle dispersion is particularly preferable for obtaining stable performance. Further, a method in which the reducing agent and the compound of the general formula (D) of the present invention are mixed as a powder and complexed at the time of dispersion with a sand grinder mill or the like using an appropriate dispersant can be preferably used.
The compound of the general formula (D) of the present invention is preferably used in the range of 1 mol% to 200 mol%, more preferably in the range of 10 mol% to 150 mol%, still more preferably relative to the reducing agent. It is in the range of 20 mol% to 100 mol%.
[0303]
(Description of binder)
Any polymer may be used as the binder of the organic silver salt-containing layer of the present invention, and suitable binders are transparent or translucent and generally colorless, and include natural resins, polymers and copolymers, synthetic resins, polymers and copolymers, etc. Film-forming media such as gelatins, rubbers, poly (vinyl alcohol) s, hydroxyethyl celluloses, cellulose acetates, cellulose acetate butyrates, poly (vinyl pyrrolidone) s, casein, starch, poly (acrylic acid) ), Poly (methyl methacrylic acid), poly (vinyl chloride), poly (methacrylic acid), styrene-maleic anhydride copolymers, styrene-acrylonitrile copolymers, styrene-butadiene copolymers , Poly (vinyl acetal) s (eg, poly (vinyl Lumar) and poly (vinyl butyral)), poly (esters), poly (urethane) s, phenoxy resins, poly (vinylidene chloride) s, poly (epoxides), poly (carbonates), poly (vinyl acetate) s , Poly (olefin) s, cellulose esters, and poly (amides). The binder may be coated from water or an organic solvent or emulsion.
[0304]
In the present invention, the glass transition temperature of the binder that can be used in combination with the layer containing the organic silver salt is preferably 0 ° C. or higher and 80 ° C. or lower (hereinafter sometimes referred to as a high Tg binder), and preferably 10 ° C. to 70 ° C. Is more preferable, and it is still more preferable that it is 15 degreeC or more and 60 degrees C or less.
[0305]
In this specification, Tg was calculated by the following formula.
1 / Tg = Σ (Xi / Tgi)
Here, it is assumed that n monomer components from i = 1 to n are copolymerized in the polymer. Xi is the weight fraction of the i-th monomer (ΣXi = 1), and Tgi is the glass transition temperature (absolute temperature) of the homopolymer of the i-th monomer. However, Σ is the sum from i = 1 to n. The homopolymer glass transition temperature (Tgi) of each monomer was the value of Polymer Handbook (3rd Edition) (by J. Brandrup, EH Immergut (Wiley-Interscience, 1989)).
[0306]
Two or more binders may be used in combination as required. Further, a glass transition temperature of 20 ° C. or higher and a glass transition temperature of less than 20 ° C. may be used in combination. When two or more kinds of polymers having different Tg are blended, the weight average Tg is preferably within the above range.
[0307]
In the present invention, the organic silver salt-containing layer is preferably applied and dried using a coating solution in which 30% by mass or more of the solvent is water to form a film.
In the present invention, when the organic silver salt-containing layer is formed using a coating solution in which 30% by mass or more of the solvent is water and dried, the binder of the organic silver salt-containing layer is further added to an aqueous solvent ( When it is soluble or dispersible in an aqueous solvent), the performance is improved particularly when it is made of a latex of a polymer having an equilibrium water content of 2% by mass or less at 25 ° C. and 60% RH. The most preferable form is one prepared so that the ionic conductivity is 2.5 mS / cm or less, and as such a preparation method, there is a method of performing purification treatment using a separation functional membrane after polymer synthesis.
[0308]
The aqueous solvent in which the polymer is soluble or dispersible here is a mixture of water or water with 70% by mass or less of a water-miscible organic solvent. Examples of the water-miscible organic solvent include alcohols such as methyl alcohol, ethyl alcohol, and propyl alcohol, cellosolvs such as methyl cellosolve, ethyl cellosolve, and butyl cellosolve, ethyl acetate, and dimethylformamide.
[0309]
In the case of a system in which the polymer is not dissolved thermodynamically and exists in a so-called dispersed state, the term aqueous solvent is used here.
[0310]
The “equilibrium moisture content at 25 ° C. and 60% RH” is the following using the weight W1 of the polymer in the humidity-controlled equilibrium under the atmosphere of 25 ° C. and 60% RH and the weight W0 of the polymer in the absolutely dry state at 25 ° C. It can be expressed as
Equilibrium water content at 25 ° C. and 60% RH = [(W1-W0) / W0] × 100 (mass%)
[0311]
For the definition and measurement method of moisture content, for example, Polymer Engineering Course 14, Polymer Material Testing Method (Edited by Society of Polymer Sciences, Jinshokan) can be referred to.
[0312]
The equilibrium moisture content at 25 ° C. and 60% RH of the binder polymer of the present invention is preferably 2% by mass or less, more preferably 0.01% by mass or more and 1.5% by mass or less, and further preferably 0.02% by mass. % To 1% by mass is desirable.
[0313]
In the present invention, a polymer dispersible in an aqueous solvent is particularly preferred. Examples of the dispersed state may be either latex in which fine particles of a water-insoluble hydrophobic polymer are dispersed or polymer molecules dispersed in a molecular state or a micelle form. preferable. The average particle diameter of the dispersed particles is 1 to 50000 nm, preferably 5 to 1000 nm, more preferably 10 to 500 nm, and still more preferably 50 to 200 nm. The particle size distribution of the dispersed particles is not particularly limited, and may have a wide particle size distribution or a monodispersed particle size distribution. Mixing two or more types having a monodispersed particle size distribution is also a preferable method for controlling the physical properties of the coating solution.
[0314]
In the present invention, preferred embodiments of the polymer that can be dispersed in an aqueous solvent include acrylic polymers, poly (esters), rubbers (eg, SBR resin), poly (urethanes), poly (vinyl chloride) s, poly (acetic acid). Hydrophobic polymers such as vinyl), poly (vinylidene chloride) and poly (olefin) can be preferably used. These polymers may be linear polymers, branched polymers, crosslinked polymers, so-called homopolymers obtained by polymerizing a single monomer, or copolymers obtained by polymerizing two or more types of monomers. In the case of a copolymer, it may be a random copolymer or a block copolymer. These polymers have a number average molecular weight of 5,000 to 1,000,000, preferably 10,000 to 200,000. When the molecular weight is too small, the mechanical strength of the I image forming layer is insufficient, and when the molecular weight is too large, the film formability is poor, which is not preferable. A crosslinkable polymer latex is particularly preferably used.
[0315]
―Specific examples of latex―
Specific examples of preferable polymer latex include the following. Below, it represents using a raw material monomer, the numerical value in a parenthesis is the mass%, and molecular weight is a number average molecular weight. When a polyfunctional monomer was used, the concept of molecular weight was not applicable because a crosslinked structure was formed, so it was described as crosslinkability, and the description of molecular weight was omitted. Tg represents the glass transition temperature.
[0316]
Latex of P-1; -MMA (70) -EA (27) -MAA (3)-(molecular weight 37000, Tg 61 ° C.)
Latex of P-2; -MMA (70) -2EHA (20) -St (5) -AA (5)-(molecular weight 40000, Tg 59 ° C.)
P-3; Latex of -St (50) -Bu (47) -MAA (3)-(crosslinkability, Tg-17 ° C) P-4; -St (68) -Bu (29) -AA (3) -Latex (crosslinkable, Tg17 ° C) P-5; -St (71) -Bu (26) -AA (3) -Latex (crosslinkable, Tg24 ° C) P-6; -St (70) -Bu (27) -IA (3) -latex (crosslinkable)
P-7; Latex of -St (75) -Bu (24) -AA (1)-(crosslinkable, Tg 29 ° C) P-8; -St (60) -Bu (35) -DVB (3) -MAA (2) -latex (crosslinkable) P-9; -St (70) -Bu (25) -DVB (2) -AA (3) -latex (crosslinkable) P-10; -VC (50) -MMA (20)-EA (20)-AN (5)-AA (5)-latex (molecular weight 80000) P-11;-VDC (85)-MMA (5)-EA (5)-MAA (5 ) -Latex (molecular weight 67000) P-12; -Et (90) -MAA (10) -latex (molecular weight 12000)
P-13; Latex of St (70) -2EHA (27) -AA (3) (molecular weight 130000, Tg43 ° C.) P-14; Latex of MMA (63) -EA (35) -AA (2) ( (Molecular weight 33000, Tg 47 ° C)
Latex of P-15; -St (70.5) -Bu (26.5) -AA (3)-(crosslinkability, Tg 23 ° C.)
Latex of P-16; -St (69.5) -Bu (27.5) -AA (3)-(crosslinkability, Tg 20.5 ° C)
[0317]
The abbreviations for the above structures represent the following monomers. MMA; methyl methacrylate, EA; ethyl acrylate, MAA; methacrylic acid, 2EHA; 2-ethylhexyl acrylate, St; styrene, Bu; butadiene, AA; acrylic acid, DVB; divinylbenzene, VC; vinyl chloride, AN; Vinylidene chloride, Et; ethylene, IA; itaconic acid.
[0318]
The polymer latex described above is also commercially available, and the following polymers can be used. Examples of the acrylic polymer include Sebian A-4635, 4718, 4601 (manufactured by Daicel Chemical Industries, Ltd.), Nipol Lx811, 814, 821, 820, 857 (manufactured by Nippon Zeon Co., Ltd.), poly ( Examples of esters) include, for example, poly (urethanes) such as FINETEX ES650, 611, 675, 850 (above made by Dainippon Ink Chemical Co., Ltd.), WD-size, WMS (more made by Eastman Chemical). Examples of rubbers such as HYDRAN AP10, 20, 30, 40 (above made by Dainippon Ink Chemical Co., Ltd.) include LACSTAR 7310K, 3307B, 4700H, 7132C (made by Dainippon Ink Chemical Co., Ltd.) , Nipol Lx416, 410, 438C, 2507 (all manufactured by Nippon Zeon Co., Ltd.) However, examples of poly (vinyl chloride) include G351 and G576 (manufactured by Nippon Zeon Co., Ltd.), and examples of poly (vinylidene chloride) include L502 and L513 (manufactured by Asahi Kasei Kogyo Co., Ltd.). Examples of poly (olefin) s include Chemipearl S120, SA100 (manufactured by Mitsui Petrochemical Co., Ltd.).
[0319]
These polymer latexes may be used alone or in combination of two or more as required.
[0320]
-Preferred latex-
As the polymer latex used in the present invention, a styrene-butadiene copolymer latex is particularly preferable. The weight ratio of the styrene monomer unit to the butadiene monomer unit in the styrene-butadiene copolymer is preferably 40:60 to 95: 5. The proportion of the styrene monomer unit and the butadiene monomer unit in the copolymer is preferably 60% by mass to 99% by mass. Moreover, it is preferable that the polymer latex of this invention contains acrylic acid or methacrylic acid 1 mass%-6 mass% with respect to the sum of styrene and butadiene, More preferably, 2 mass%-5 mass% are contained. The polymer latex of the present invention preferably contains acrylic acid. The preferred molecular weight range is the same as described above.
[0321]
Examples of latexes of styrene-butadiene acid copolymer that are preferably used in the present invention include the above-mentioned P-3 to P-8,15, commercially available products LACSTAR-3307B, 7132C, Nipol Lx416, and the like.
[0322]
If necessary, a hydrophilic polymer such as gelatin, polyvinyl alcohol, methylcellulose, hydroxypropylcellulose, carboxymethylcellulose may be added to the organic silver salt-containing layer of the light-sensitive material of the present invention. The amount of these hydrophilic polymers added is preferably 30% by mass or less, more preferably 20% by mass or less, based on the total binder of the organic silver salt-containing layer.
[0323]
The organic silver salt-containing layer (that is, the image forming layer) of the present invention is preferably formed using a polymer latex. The amount of binder in the organic silver salt-containing layer is such that the weight ratio of total binder / organic silver salt is 1/10 to 10/1, more preferably 1/3 to 5/1, and still more preferably 1/1 to 3/1. / 1 range.
[0324]
Such an organic silver salt-containing layer is usually a photosensitive layer (I image forming layer) containing a photosensitive silver halide which is a photosensitive silver salt. The weight ratio of silver halide is in the range of 400-5, more preferably 200-10.
[0325]
The total binder amount of the image forming layer of the present invention is preferably 0.2 g / m.²~ 30g / m², More preferably 1 g / m²~ 15g / m²More preferably 2 g / m²-10g / m²Range. The image forming layer of the present invention may contain a crosslinking agent for crosslinking, a surfactant for improving coating properties, and the like.
[0326]
(Preferable solvent for coating solution)
In the present invention, the solvent of the organic silver salt-containing layer coating solution of the light-sensitive material (here, for simplicity, the solvent and the dispersion medium are collectively referred to as a solvent) is preferably an aqueous solvent containing 30% by mass or more of water. As a component other than water, any water-miscible organic solvent such as methyl alcohol, ethyl alcohol, isopropyl alcohol, methyl cellosolve, ethyl cellosolve, dimethylformamide, and ethyl acetate may be used. The water content of the solvent of the coating solution is preferably 50% by mass or more, more preferably 70% by mass or more. Examples of preferred solvent compositions include water, water / methyl alcohol = 90/10, water / methyl alcohol = 70/30, water / methyl alcohol / dimethylformamide = 80/15/5, water / methyl alcohol / Ethyl cellosolve = 85/10/5, water / methyl alcohol / isopropyl alcohol = 85/10/5, etc. (numerical values are mass%).
[0327]
(Anti-fogging agent)
1) Organic polyhalogen compounds
Hereinafter, preferred organic polyhalogen compounds that can be used in the present invention will be specifically described. A preferred polyhalogen compound of the present invention is a compound represented by the following general formula (H).
[0328]
General formula (H)
Q- (Y) n-C (Z₁) (Z₂) X
[0329]
In General Formula (H), Q represents an alkyl group, an aryl group, or a heterocyclic group, Y represents a divalent linking group, n represents 0 to 1, Z₁And Z₂Represents a halogen atom, and X represents a hydrogen atom or an electron withdrawing group.
In general formula (H), Q is preferably an alkyl group having 1 to 6 carbon atoms, an aryl group having 6 to 12 carbon atoms, or a heterocyclic group containing at least one nitrogen atom (pyridine, quinoline group, etc.).
[0330]
In the general formula (H), when Q is an aryl group, Q preferably represents a phenyl group substituted with an electron-attracting group having a positive Hammett's substituent constant σp. For Hammett's substituent constants, see Journal of Medicinal Chemistry, 1973, Vol. 16, no. 11, 1207-1216 etc. can be referred to. Examples of such an electron withdrawing group include a halogen atom, an alkyl group substituted with an electron withdrawing group, an aryl group substituted with an electron withdrawing group, a heterocyclic group, an alkyl or arylsulfonyl group, acyl Group, alkoxycarbonyl group, carbamoyl group, sulfamoyl group and the like. Particularly preferred as the electron withdrawing group are a halogen atom, a carbamoyl group, and an arylsulfonyl group, and a carbamoyl group is particularly preferred.
[0331]
X is preferably an electron withdrawing group. Preferred electron withdrawing groups are halogen atoms, aliphatic / aryl or heterocyclic sulfonyl groups, aliphatic / aryl or heterocyclic acyl groups, aliphatic / aryl or heterocyclic oxycarbonyl groups, carbamoyl groups, sulfamoyl groups, More preferred are a halogen atom and a carbamoyl group, and particularly preferred is a bromine atom.
Z₁And Z₂Is preferably a bromine atom or an iodine atom, more preferably a bromine atom.
[0332]
Y is preferably —C (═O) —, —SO 2 —, —SO₂-, -C (= O) N (R)-, -SO₂N (R)-, more preferably -C (= O)-, -SO₂-, -C (= O) N (R)-, particularly preferably -SO.₂-, -C (= O) N (R)-. R here represents a hydrogen atom, an aryl group or an alkyl group, more preferably a hydrogen atom or an alkyl group, and particularly preferably a hydrogen atom.
n represents 0 or 1, and is preferably 1.
[0333]
In general formula (H), when Q is an alkyl group, preferred Y is —C (═O) N (R) —, and when Q is an aryl group or heterocyclic group, preferred Y is —SO.₂-.
In the general formula (H), a form in which residues obtained by removing a hydrogen atom from the compound are bonded to each other (generally referred to as a bis type, a tris type, or a tetrakis type) can also be preferably used.
In general formula (H), a dissociable group (for example, a COOH group or a salt thereof, SO₃H group or a salt thereof, PO₃A group having a group containing a quaternary nitrogen cation (for example, an ammonium group, a pyridinium group, etc.), a polyethyleneoxy group, a hydroxyl group or the like as a substituent is also a preferable form.
[0334]
Specific examples of the compound of the general formula (H) of the present invention are shown below.
[0335]
Embedded image

[0336]
Embedded image

[0337]
Polyhalogen compounds that can be used in the present invention other than those described above include US Pat. No. 3,874,946, US Pat. No. 4,756,999, US Pat. No. 5,340,712, US Pat. No. 5,369,000, US Pat. No. 5,464,537, US Pat. No. 6,506,548, JP-A Nos. 50-137126, 50-89020, and 50. 119624, 59-57234, JP-A-7-2781, 7-5621, 9-160164, 9-244177, 9-244178, 9-160167, 9- 319022, 9-258367, 9-265150, 9-319022, 10-197988, 10-197989, 11-242304, JP-A 2000-2963, JP-A 2000-112070 , JP2000-284410, JP2 The compounds listed as exemplary compounds of the invention in 00-284212, JP-A-2001-33911, JP-A-2001-31644, JP-A-2001-312027, and JP-A-2003-50441 are preferably used. In particular, compounds specifically exemplified in JP-A-7-2781, JP-A-2001-33911, and JP-A-2001-312027 are preferred.
[0338]
The compound represented by the general formula (H) of the present invention is 10 per mole of the non-photosensitive silver salt of the image forming layer.^-4It is preferably used in the range of 1 mol to 1 mol, more preferably 10^-3In the range of mol to 0.5 mol, more preferably 1 × 10^-2It is preferable to use in the range of mol to 0.2 mol.
In the present invention, the antifoggant is contained in the light-sensitive material by the method described in the method for containing a reducing agent, and the organic polyhalogen compound is also preferably added as a solid fine particle dispersion.
[0339]
2) Other antifogging agents
Examples of other antifoggants include mercury (II) salts described in JP-A No. 11-65021, paragraph number 0113, benzoic acids described in paragraph No. 0114, salicylic acid derivatives disclosed in JP-A No. 2000-206642, and formulas described in JP-A No. 2000-221634. A formalin scavenger compound represented by (S), a triazine compound according to claim 9 of JP-A-11-352624, a compound represented by formula (III) of JP-A-6-11791, 4-hydroxy-6-6 Examples include methyl-1,3,3a, 7-tetrazaindene.
[0340]
The photothermographic material in the invention may contain an azolium salt for the purpose of fog prevention. Examples of the azolium salt include compounds represented by general formula (XI) described in JP-A-59-193447, compounds described in JP-B-55-12581, and general formula (II) described in JP-A-60-153039. And the compounds represented. The azolium salt may be added to any part of the photosensitive material, but the addition layer is preferably added to the layer having the photosensitive layer, and more preferably to the organic silver salt-containing layer. The azolium salt may be added at any step in the coating solution preparation. When added to the organic silver salt-containing layer, any step from the preparation of the organic silver salt to the coating solution preparation may be performed. To immediately before coating. The azolium salt may be added by any method such as powder, solution, fine particle dispersion. Moreover, you may add as a solution mixed with other additives, such as a sensitizing dye, a reducing agent, and a color toning agent. In the present invention, any amount of the azolium salt may be added, but 1 × 10 10 per silver mole.^-6Preferred is 1 to 10 moles.^-3More preferably, it is at least 0.5 moles.
[0341]
(Other additives)
1) Mercapto, disulfide, and thiones
In the present invention, a mercapto compound, a disulfide compound, and a thione compound can be contained in order to suppress or promote development to control development, to improve spectral sensitization efficiency, and to improve storage stability before and after development. JP-A-10-62899, paragraphs 0067 to 0069, JP-A-10-186572, the compound represented by the general formula (I) and specific examples thereof include paragraphs 0033 to 0052, EP 080376A1, No. 20 pages, lines 36-56. Of these, mercapto-substituted heteroaromatic compounds described in JP-A-9-297367, JP-A-9-304875, JP-A-2001-100388, JP-A-2001-104213, JP-A-2001-104214, and the like are preferable.
[0342]
2) Color preparation
In the photothermographic material of the present invention, it is preferable to add a color toning agent. For the color toning agent, paragraph numbers 0054 to 0055 of JP-A-10-62899, page 21, lines 23 to 48 of European Patent Publication No. 0803764A1, No. 2000-356317 and JP-A-2000-187298. In particular, phthalazinones (phthalazinone, phthalazinone derivatives or metal salts; for example, 4- (1-naphthyl) phthalazinone, 6-chlorophthalazinone, 5,7 -Dimethoxyphthalazinone and 2,3-dihydro-1,4-phthalazinedione); phthalazinones and phthalic acids (eg phthalic acid, 4-methylphthalic acid, 4-nitrophthalic acid, diammonium phthalate, sodium phthalate) , Potassium phthalate and tetrachlorophthalic anhydride) Phthalazines (phthalazine, phthalazine derivatives or metal salts; for example 4- (1-naphthyl) phthalazine, 6-isopropylphthalazine, 6-t-butylphthalazine, 6-chlorophthalazine, 5,7-dimethoxyphthalazine and 2 , 3-dihydrophthalazine); a combination of phthalazines and phthalic acids is preferred, and a combination of phthalazines and phthalic acids is particularly preferred. Of these, a particularly preferred combination is a combination of 6-isopropylphthalazine and phthalic acid or 4-methylphthalic acid.
[0343]
3) Plasticizer, lubricant
The plasticizer and lubricant that can be used in the photosensitive layer of the present invention are described in paragraph No. 0117 of JP-A No. 11-65021. The slip agent is described in JP-A No. 11-84573, paragraph numbers 0061 to 0064 and Japanese Patent Application No. 11-106881, paragraph numbers 0049 to 0062.
[0344]
4) Dyes and pigments
In the photosensitive layer of the present invention, various dyes and pigments (for example, CI Pigment Blue 60, CI Pigment Blue 64, C.I. Pigment Blue 64, C.I. I. Pigment Blue 15: 6) can be used. These are described in detail in WO98 / 36322, JP-A-10-268465, JP-A-11-338098 and the like.
[0345]
5) Ultra-high contrast agent
In order to form an ultrahigh contrast image suitable for printing plate making applications, it is preferable to add an ultrahigh contrast agent to the image forming layer. As for the ultra-high contrast agent and its addition method and addition amount, the formulas of JP-A No. 11-65021, paragraph No. 0118, JP-A No. 11-223898, paragraph Nos. 0136 to 0193, and Japanese Patent Application No. 11-87297 are disclosed. (H), compounds of formulas (1) to (3), compounds of formulas (A) and (B), compounds of general formulas (III) to (V) described in Japanese Patent Application No. 11-91652 (specific compounds) : Chemical Formula 21 to Chemical Formula 24), and the high contrast accelerator are described in paragraph No. 0102 of JP-A No. 11-65021 and paragraph Nos. 0194 to 0195 of JP-A No. 11-223898.
[0346]
In order to use formic acid or formate as a strong fogging substance, it is preferable to contain 5 mmol or less, more preferably 1 mmol or less, per mol of silver on the side having the image forming layer containing photosensitive silver halide.
When the ultrahigh contrast agent is used in the photothermographic material of the present invention, it is preferable to use an acid formed by hydrating diphosphorus pentoxide or a salt thereof in combination. Acids or salts thereof formed by hydration of diphosphorus pentoxide include metaphosphoric acid (salt), pyrophosphoric acid (salt), orthophosphoric acid (salt), triphosphoric acid (salt), tetraphosphoric acid (salt), hexametalin An acid (salt) etc. can be mentioned. Examples of the acid or salt thereof formed by hydrating diphosphorus pentoxide particularly preferably include orthophosphoric acid (salt) and hexametaphosphoric acid (salt). Specific examples of the salt include sodium orthophosphate, sodium dihydrogen orthophosphate, sodium hexametaphosphate, ammonium hexametaphosphate and the like.
Amount of acid or salt thereof formed by hydration of diphosphorus pentoxide (1m photosensitive material)²The coating amount per unit) may be a desired amount according to the performance such as sensitivity and fog, but 0.1 mg / m²~ 500mg / m²Is preferred, 0.5 mg / m²~ 100mg / m²Is more preferable.
[0347]
(Preparation and application of coating solution)
The preparation temperature of the image forming layer coating solution of the present invention is preferably 30 ° C. or more and 65 ° C. or less, more preferably 35 ° C. or more and less than 60 ° C., and more preferably 35 ° C. or more and 55 ° C. or less. Moreover, it is preferable that the temperature of the image forming layer coating liquid immediately after the addition of the polymer latex is maintained at 30 ° C. or higher and 65 ° C. or lower.
[0348]
(Layer structure and components)
The image forming layer of the present invention is composed of one or more layers on a support. In the case of a single layer, it consists of an organic silver salt, a photosensitive silver halide, a reducing agent and a binder, and optionally contains additional materials such as toning agents, coating aids and other auxiliary agents. In the case of two or more layers, an organic silver salt and a light-sensitive silver halide are contained in the first image forming layer (usually a layer adjacent to the support), and some in the second image forming layer or both layers. Must contain other ingredients. The construction of a multicolor photosensitive photothermographic material may include a combination of these two layers for each color and all components in a single layer as described in US Pat. No. 4,708,928. May be included. In the case of multi-dye multicolor photosensitive photothermographic materials, each I image-forming layer is generally functional or non-functional between each photosensitive layer as described in US Pat. No. 4,460,681. By using a functional barrier layer, they are kept separate from each other.
[0349]
The photothermographic material of the present invention can have a non-photosensitive layer in addition to the image forming layer. The non-photosensitive layer includes (a) a surface protective layer provided on the image forming layer (on the side farther than the support), (b) between the plurality of image forming layers and between the image forming layer and the protective layer. It can be classified into an intermediate layer provided therebetween, (c) an undercoat layer provided between the image forming layer and the support, and (d) a back layer provided on the opposite side of the image forming layer.
[0350]
In addition, although a layer acting as an optical filter can be provided, it is provided as the layer (a) or (b). The antihalation layer is provided on the photosensitive material as the layer (c) or (d).
[0351]
1) Surface protective layer
In the photothermographic material of the invention, a surface protective layer can be provided for the purpose of preventing adhesion of the image forming layer. The surface protective layer may be a single layer or a plurality of layers.
The surface protective layer is described in JP-A No. 11-65021, paragraph numbers 0119 to 0120 and JP-A No. 2000-171936.
As the binder for the surface protective layer of the present invention, gelatin is preferable, but it is also preferable to use polyvinyl alcohol (PVA) or a combination thereof. As gelatin, inert gelatin (for example, Nitta gelatin 750), phthalated gelatin (for example, Nitta gelatin 801), and the like can be used. Examples of PVA include those described in paragraph Nos. 0009 to 0020 of JP-A No. 2000-171936. Completely saponified PVA-105, partially saponified PVA-205, PVA-335, and modified polyvinyl alcohol MP- Preferred is 203 (trade name, manufactured by Kuraray Co., Ltd.). Polyvinyl alcohol coating amount of protective layer (per layer) (support 1m²Per unit) is 0.3 g / m²~ 4.0 g / m²Is preferably 0.3 g / m²~ 2.0 g / m²Is more preferable.
[0352]
Total binder (including water-soluble polymer and latex polymer) coating amount of surface protective layer (per layer) (support 1m)²Per unit) is 0.3 g / m²~ 5.0 g / m²Is preferably 0.3 g / m²~ 2.0 g / m²Is more preferable.
[0353]
2) Antihalation layer
In the photothermographic material of the present invention, the antihalation layer can be provided on the side far from the light source with respect to the photosensitive layer.
[0354]
As for the antihalation layer, paragraph numbers 0123 to 0124 of JP-A No. 11-65021, JP-A Nos. 11-223898, 9-230531, 10-36695, 10-104779, 11-231457, 11 -352625, 11-352626 and the like.
The antihalation layer contains an antihalation dye having absorption at the exposure wavelength. When the exposure wavelength is in the infrared region, an infrared absorbing dye may be used, and in that case, a dye having no absorption in the visible region is preferable.
When antihalation is performed using a dye having absorption in the visible range, it is preferable that substantially no dye color remains after image formation, and a means for decoloring by the heat of heat development is used. In particular, it is preferable to add a thermally decolorable dye and a base precursor to the non-photosensitive layer to function as an antihalation layer. These techniques are described in JP-A-11-231457 and the like.
[0355]
The amount of decoloring dye added is determined by the use of the dye. In general, the optical density (absorbance) measured at the target wavelength is used in an amount exceeding 0.1. The optical density is preferably 0.15 to 2, and more preferably 0.2 to 1. The amount of dye used to obtain such an optical density is generally 0.001 g / m.²~ 1g / m²Degree.
[0356]
When the dye is decolored in this way, the optical density after heat development can be reduced to 0.1 or less. Two or more kinds of decoloring dyes may be used in combination in a heat decoloring type recording material or a photothermographic material. Similarly, two or more kinds of base precursors may be used in combination.
In the thermal decoloration using such decoloring dye and base precursor, a substance (for example, diphenylsulfone, which lowers the melting point by 3 ° C. (deg) or more when mixed with a base precursor as described in JP-A No. 11-352626). 4-Chlorophenyl (phenyl) sulfone), 2-naphthyl benzoate and the like are preferably used in view of thermal decoloring properties.
[0357]
3) Back layer
The back layer applicable to the present invention is described in paragraph Nos. 0128 to 0130 of JP-A No. 11-65021.
[0358]
In the present invention, a colorant having an absorption maximum at 300 to 450 nm can be added for the purpose of improving the silver color tone and the temporal change of the image. Such colorants are disclosed in JP-A-62-210458, JP-A-63-104046, JP-A-63-103235, JP-A-63-208846, JP-A-63-306436, JP-A-63-141435, and JP-A-01-61745. No. 1, Japanese Patent Laid-Open No. 2001-100363, and the like. Such colorants are typically 0.1 mg / m²~ 1g / m²The back layer provided on the opposite side of the photosensitive layer is preferable as the layer to be added in the range of.
In order to adjust the base color tone, it is preferable to use a dye having an absorption peak at 580 to 680 nm. As the dye for this purpose, azomethine-based oil-soluble dyes described in JP-A-4-359967 and JP-A-4-359968 having a small absorption intensity on the short wavelength side, and phthalocyanine-based water-soluble dyes described in Japanese Patent Application No. 2002-96797 are preferable. The dye for this purpose may be added to any layer, but is more preferably added to the non-photosensitive layer on the emulsion surface side or the back surface side.
[0359]
The photothermographic material in the invention is a so-called single-sided photosensitive material having a photosensitive layer containing at least one silver halide emulsion on one side of a support and a back layer on the other side. preferable.
[0360]
4) Matting agent
In the present invention, it is preferable to add a matting agent for improving transportability, and the matting agent is described in paragraph Nos. 0126 to 0127 of JP-A No. 11-65021. Matting agent is photosensitive material 1m²When expressed as a coating amount per unit, preferably 1 mg / m²~ 400mg / m², More preferably 5 mg / m²~ 300mg / m²It is.
[0361]
In the present invention, the shape of the matting agent may be either a regular shape or an irregular shape, but is preferably a regular shape, and a spherical shape is preferably used. The average particle size is preferably 0.5 μm to 10 μm, more preferably 1.0 μm to 8.0 μm, and still more preferably 2.0 μm to 6.0 μm. The variation coefficient of the size distribution is preferably 50% or less, more preferably 40% or less, and still more preferably 30% or less. Here, the coefficient of variation is a value represented by (standard deviation of particle size) / (average value of particle size) × 100. It is also preferable to use two types of matting agents having a small variation coefficient and having an average particle size ratio larger than 3.
[0362]
The emulsion surface may have any matte degree as long as no stardust failure occurs, but the Beck smoothness is preferably 30 seconds or more and 2000 seconds or less, and particularly preferably 40 seconds or more and 1500 seconds or less. The Beck smoothness can be easily obtained by Japanese Industrial Standard (JIS) P8119 “Smoothness test method using Beck tester for paper and paperboard” and TAPPI standard method T479.
[0363]
In the present invention, the matte degree of the back layer is preferably a Beck smoothness of 1200 seconds or less and 10 seconds or more, preferably 800 seconds or less and 20 seconds or more, and more preferably 500 seconds or less and 40 seconds or more.
[0364]
In the present invention, the matting agent is preferably contained in the outermost surface layer of the photosensitive material, the layer functioning as the outermost surface layer, or a layer close to the outer surface, and is contained in a layer acting as a so-called protective layer. It is preferable.
[0365]
5) Polymer latex
In particular, when the photothermographic material of the present invention is used for printing applications in which dimensional change is a problem, it is preferable to use a polymer latex for the surface protective layer or the back layer. For such polymer latex, “Synthetic resin emulsion (Hiraku Okuda, Hiroshi Inagaki, published by Kobunshi Publishing (1978))”, “Application of synthetic latex (Takaaki Sugimura, Ikuo Kataoka, Junichi Suzuki, Keiji Kasahara, Takashi "Molecular Publications (1993))" and "Synthetic Latex Chemistry (Muroichi Muroi, published by High Polymers Publication (1970))", specifically, methyl methacrylate (33.5% by mass) / Ethyl acrylate (50 wt%) / Methacrylic acid (16.5 wt%) copolymer latex, Methyl methacrylate (47.5 wt%) / Butadiene (47.5 wt%) / Itaconic acid (5 wt%) copolymer Latex, latex of ethyl acrylate / methacrylic acid copolymer, methyl methacrylate (58.9% by mass) / 2-ethyl A latex of xyl acrylate (25.4% by weight) / styrene (8.6% by weight) / 2-hydroxyethyl methacrylate (5.1% by weight) / acrylic acid (2.0% by weight) copolymer, methyl methacrylate (64. 0 mass%) / styrene (9.0 mass%) / butyl acrylate (20.0 mass%) / 2-hydroxyethyl methacrylate (5.0 mass%) / acrylic acid (2.0 mass%) copolymer latex, etc. Is mentioned.
[0366]
Furthermore, as a binder for the surface protective layer, a combination of polymer latex described in Japanese Patent Application No. 11-6872, the technique described in Paragraph Nos. 0021 to 0025 of Japanese Patent Application Laid-Open No. 2000-267226, and Japanese Patent Application No. 11-6872. The technology described in paragraph numbers 0027 to 0028 of the specification and the technology described in paragraph numbers 0023 to 0041 of JP 2000-19678 may be applied. The ratio of the polymer latex in the surface protective layer is preferably 10% by mass or more and 90% by mass or less, and particularly preferably 20% by mass or more and 80% by mass or less of the total binder.
[0367]
6) Membrane pH
The photothermographic material of the present invention preferably has a film surface pH of 7.0 or less, more preferably 6.6 or less before heat development. The lower limit is not particularly limited, but is about 3. The most preferred pH range is in the range of 4 to 6.2. For the adjustment of the film surface pH, it is preferable to use an organic acid such as a phthalic acid derivative, a non-volatile acid such as sulfuric acid, and a volatile base such as ammonia from the viewpoint of reducing the film surface pH. In particular, ammonia is volatile and is preferable for achieving a low film surface pH because it can be removed before the coating process or thermal development.
In addition, it is also preferable to use ammonia in combination with a nonvolatile base such as sodium hydroxide, potassium hydroxide, or lithium hydroxide. A method for measuring the film surface pH is described in paragraph No. 0123 of JP-A No. 2000-284399.
[0368]
7) Hardener
A hardener may be used in each layer such as the photosensitive layer, protective layer, and back layer of the present invention. Examples of hardeners include T.W. H. There are various methods described in "THE THEORY OF THE PHOTOGRAPHIC PROCESS FOURTH EDITION" by James (published by Macmillan Publishing Co., Inc., published in 1977), pages 77 to 87. Chrome Alum, 2,4-Dichloro 6-hydroxy -S-triazine sodium salt, N, N-ethylenebis (vinylsulfoneacetamide), N, N-propylenebis (vinylsulfoneacetamide), polyvalent metal ions described on page 78 of the same, U.S. Pat. No. 4,281, Polyisocyanates such as 060 and JP-A-6-208193, epoxy compounds such as US Pat. No. 4,791,042, and vinylsulfone compounds such as JP-A-62-289048 are preferably used. .
[0369]
The hardening agent is added as a solution, and the addition time of this solution into the protective layer coating solution is from 180 minutes before to immediately before application, preferably from 60 minutes to 10 seconds before application. As long as the effects of the present invention are sufficiently exhibited, there is no particular limitation. Specific mixing methods include mixing in a tank in which the average residence time calculated from the addition flow rate and the amount of liquid fed to the coater is a desired time, and N.I. Harnby, M.M. F. Edwards, A.D. W. There is a method using a static mixer described in Chapter 8 of Nienow's Koji Takahashi "Liquid Mixing Technology" (published by Nikkan Kogyo Shimbun, 1989).
[0370]
8) Surfactant
JP-A No. 11-65021 paragraph No. 0132 for surfactants applicable to the present invention, paragraph No. 0133 for solvents, paragraph No. 0134 for supports, paragraph No. for antistatic or conductive layers No. 0136 for the method of obtaining a color image, and paragraph Nos. 0061 to 0064 of JP-A No. 11-84573 and paragraph Nos. 0049 to 0062 of Japanese Patent Application No. 11-106881 for the slip agent.
[0371]
In the present invention, it is preferable to use a fluorosurfactant. Specific examples of the fluorosurfactant include compounds described in JP-A Nos. 10-197985, 2000-19680, 2000-214554 and the like. Further, a polymeric fluorine-based surfactant described in JP-A-9-281636 is also preferably used. In the photothermographic material of the present invention, it is preferable to use a fluorosurfactant described in JP-A No. 2002-82411, Japanese Patent Application Nos. 2001-242357 and 2001-264110. In particular, the fluorosurfactants described in Japanese Patent Application Nos. 2001-242357 and 2001-264110 are preferable in terms of charge adjustment ability, stability of the coated surface, and smoothness when coating and manufacturing with an aqueous coating solution. The fluorine-containing surfactant described in Japanese Patent Application No. 2001-264110 is most preferable in that it has a high charge adjustment capability and requires a small amount of use.
[0372]
In the present invention, the fluorosurfactant can be used on either the emulsion surface or the back surface, and is preferably used on both surfaces. Further, it is particularly preferable to use in combination with a conductive layer containing the above-described metal oxide. In this case, sufficient performance can be obtained even if the amount of the fluorosurfactant used on the surface having the conductive layer is reduced or removed.
The preferred amount of the fluorosurfactant is 0.1 mg / m for each of the emulsion surface and the back surface.²~ 100mg / m²In the range, more preferably 0.3 mg / m²~ 30mg / m²Range, more preferably 1 mg / m²-10 mg / m²Range. In particular, the fluorosurfactant described in Japanese Patent Application No. 2001-264110 has a large effect and is 0.01 mg / m.²-10 mg / m²A range of 0.1 mg / m²~ 5mg / m²The range of is more preferable.
[0373]
9) Antistatic agent
In the present invention, it is preferable to have a conductive layer containing a metal oxide or a conductive polymer. The antistatic layer may serve as an undercoat layer, a back layer surface protective layer, or the like, or may be provided separately. As the conductive material for the antistatic layer, a metal oxide in which conductivity is improved by introducing oxygen defects or different metal atoms into the metal oxide is preferably used. Examples of metal oxides are ZnO, TiO₂, SnO₂And for ZnO, addition of Al and In, SnO₂For Sb, Nb, P, halogen elements, etc., TiO₂In contrast, addition of Nb, Ta or the like is preferable. Especially SnO with Sb added₂Is preferred. The amount of different atoms added is preferably in the range of 0.01 to 30 mol%, more preferably in the range of 0.1 to 10 mol%. The shape of the metal oxide may be spherical, needle-like, or plate-like, but the long axis / uniaxial ratio is 2.0 or more, preferably 3.0 to 50 in terms of the effect of imparting conductivity. Good. The amount of metal oxide used is preferably 1 mg / m²~ 1000mg / m²In the range, more preferably 10 mg / m²~ 500mg / m²Range, more preferably 20 mg / m²~ 200mg / m²Range.
[0374]
The antistatic layer of the present invention may be disposed on either the emulsion surface side or the back surface side, but is preferably disposed between the support and the back layer. Specific examples of the antistatic layer of the present invention include paragraph No. 0135 of JP-A No. 11-65021, JP-A Nos. 56-143430, 56-143431, 58-62646, No. 56-120519, JP-A No. 11-120. No. 84573, paragraph numbers 0040 to 0051, US Pat. No. 5,575,957, and JP-A No. 11-223898, paragraph numbers 0078 to 0084.
[0375]
10) Support
The transparent support is a polyester, particularly polyethylene, which has been heat-treated in a temperature range of 130 to 185 ° C. in order to relieve internal strain remaining in the film during biaxial stretching and to eliminate thermal shrinkage strain generated during heat development. Terephthalate is preferably used. In the case of a photothermographic material for medical use, the transparent support may be colored with a blue dye (for example, dye-1 described in Examples of JP-A-8-240877) or may be uncolored. Examples of the support include water-soluble polyesters disclosed in JP-A-11-84574, styrene-butadiene copolymers described in JP-A-10-186565, and vinylidene chloride described in JP-A-2000-39684 and Japanese Patent Application No. 11-106881, paragraph numbers 0063 to 0080. It is preferable to apply an undercoating technique such as a copolymer. When the I image forming layer or the back layer is applied to the support, the water content of the support is preferably 0.5% by mass or less.
[0376]
11) Other additives
An antioxidant, a stabilizer, a plasticizer, an ultraviolet absorber, or a coating aid may be further added to the photothermographic material. Various additives are added to either the photosensitive layer or the non-photosensitive layer. With respect to these, WO 98/36322, EP 803764A1, JP-A-10-186567, 10-18568 and the like can be referred to.
[0377]
12) Application method
The photothermographic material in the invention may be applied by any method. Specifically, various coating operations including extrusion coating, slide coating, curtain coating, dip coating, knife coating, flow coating, or extrusion coating using a hopper of the type described in US Pat. No. 2,681,294. And Stephen F. Kistler, Peter M. et al. Extrusion coating or slide coating described in pages 399 to 536 of “LIQUID FILM COATING” (CHAPMAN & HALL, 1997) by Schweizer is preferably used, and slide coating is particularly preferably used. An example of the shape of a slide coater used for slide coating is shown in FIG. 11b. 1 If desired, two or more layers can be simultaneously coated by the method described on pages 399 to 536 of the same document, the method described in US Pat. No. 2,761,791 and British Patent No. 837,095. . In the present invention, particularly preferred coating methods are those described in JP-A Nos. 2001-194748, 2002-153808, 2002-153803, and 2002-182333.
[0378]
The organic silver salt-containing layer coating solution in the present invention is preferably a so-called thixotropic fluid. Regarding this technique, JP-A-11-52509 can be referred to. The organic silver salt-containing layer coating solution in the present invention has a shear rate of 0.1 S.^-1The viscosity in is preferably 400 mPa · s or more and 100,000 mPa · s or less, and more preferably 500 mPa · s or more and 20,000 mPa · s or less. Also, shear rate 1000S^-1Is preferably from 1 mPa · s to 200 mPa · s, more preferably from 5 mPa · s to 80 mPa · s.
[0379]
In the case of preparing the coating liquid of the present invention, a known in-line mixer or implant mixer is preferably used when mixing two kinds of liquids. A preferred in-line mixer of the present invention is described in JP-A No. 2002-85948, and an implant mixer is described in JP-A No. 2002-90940.
The coating solution in the present invention is preferably subjected to defoaming treatment in order to keep the coated surface state good. A preferable defoaming treatment method of the present invention is the method described in JP-A No. 2002-66431.
[0380]
When applying the coating solution of the present invention, it is preferable to perform static elimination in order to prevent adhesion of dust, dust, and the like due to electric resistance of the support. An example of a preferable static elimination method in the present invention is described in JP-A No. 2002-143747.
In the present invention, it is important to precisely control the drying air and the drying temperature in order to dry the non-setting image forming layer coating solution. The preferred drying method of the present invention is described in detail in JP-A Nos. 2001-194749 and 2002-139814.
[0381]
The photothermographic material of the present invention is preferably subjected to a heat treatment immediately after coating and drying in order to improve film formability. The temperature of the heat treatment is preferably in the range of 60 ° C. to 100 ° C. as the film surface temperature, and the heating time is preferably in the range of 1 second to 60 seconds. A more preferable range is a film surface temperature of 70 ° C. to 90 ° C. and a heating time of 2 seconds to 10 seconds. A preferable heat treatment method of the present invention is described in JP-A No. 2002-107872.
[0382]
In order to stably and continuously produce the photothermographic material of the present invention, the production methods described in JP-A Nos. 2002-156728 and 2002-182333 are preferably used.
The photothermographic material is preferably a mono-sheet type (a type capable of forming an image on the photothermographic material without using another sheet such as an image receiving material).
[0383]
13) Packaging materials
The light-sensitive material of the present invention is preferably packaged with a packaging material having a low oxygen permeability and / or moisture permeability in order to suppress fluctuations in photographic performance during raw storage or to improve curling, curling, etc. Oxygen permeability is 50ml / atm · m at 25 ° C²· Day or less is preferable, more preferably 10 ml / atm · m²-Day or less, more preferably 1.0 ml / atm.m²-Day or less. Moisture permeability is 10 g / atm · m²· Day or less, more preferably 5 g / atm · m²· Day or less, more preferably 1 g / atm · m²-Day or less.
Specific examples of the packaging material having low oxygen permeability and / or moisture permeability are disclosed in, for example, JP-A-8-254793. This is a packaging material described in JP-A-2000-206653.
[0384]
14) Other available technologies
Techniques that can be used for the photothermographic material of the present invention include EP80364A1, EP883022A1, WO98 / 36322, JP56-62648, 58-62644, JP9-43766, and 9-. 281637, 9-297367, 9-304869, 9-311405, 9-329865, 10-10669, 10-62899, 10-69023, 10-186568, 10-90823, 10-171106, 10-186565, 10-186567, 10-186567 to 10-186572, 10-197974, 10-197982, 10 -197983, 10-197985 to 10-197987, 10- 07001, 10-207004, 10-221807, 10-282601, 10-288823, 10-288824, 10-307365, 10-312038, 10-339934 11-7100, 11-15105, 11-24200, 11-24201, 11-30201, 11-30832, 11-84574, 11-65021, 11-109547, 11-125880, 11-129629, 11-133536 to 11-133539, 11-133542, 11-133543, 11-223898, 11-352627, 11- 305377, 11-305378, 11-305384, 11-30538 11-316435, 11-327076, 11-338096, 11-338098, 11-338099, 11-343420, JP 2000-187298, 2000-10229 2000-47345, 2000-206642, 2000-98530, 2000-98531, 2000-112059, 2000-112060, 2000-112104, 2000-112604, No. 2000-171936 is also mentioned.
[0385]
In the case of multicolor color photothermographic materials, each I image forming layer is generally a functional or non-functional layer between each photosensitive layer as described in US Pat. No. 4,460,681. By using barrier layers, they are kept distinct from each other.
The construction in the case of a multicolor color photothermographic material may include a combination of these two layers for each color and all within a single layer as described in US Pat. No. 4,708,928. Ingredients may be included.
[0386]
(Image forming method)
1) Exposure
The light-sensitive material of the present invention may be exposed by any method, but laser light is preferred as the exposure light source. A silver halide emulsion having a high silver iodide content as in the present invention has been problematic because of its low sensitivity. However, it has been found that writing with high illuminance such as laser light eliminates the problem of low sensitivity and enables image recording with less energy. The target sensitivity can be achieved by writing with such strong light in a short time.
[0387]
In particular, when an exposure amount giving the maximum density (Dmax) is given, the preferable light amount on the surface of the photosensitive material is 0.1 W / mm.²~ 100W / mm²It is. More preferably 0.5 W / mm²~ 50W / mm²And most preferably 1 W / mm²~ 50W / mm²It is.
[0388]
As the laser light according to the present invention, a gas laser (Ar⁺, He—Ne, He—Cd), YAG laser, dye laser, semiconductor laser and the like are preferable. A semiconductor laser and a second harmonic generation element can also be used. The laser preferably used is determined according to the light absorption peak wavelength of the photosensitizing material such as a spectral sensitizing dye, but it is a red to infrared emitting He-Ne laser, a red semiconductor laser, or a blue to green emitting Ar.⁺, He—Ne, He—Cd laser, blue semiconductor laser. In recent years, in particular, a module in which an SHG (Second Harmonic Generator) element and a semiconductor laser are integrated and a blue semiconductor laser have been developed, and a laser output device in a short wavelength region has been closed up. The blue semiconductor laser is expected to increase in demand in the future because high-definition image recording is possible, the recording density is increased, and a stable output is obtained with a long lifetime. The peak wavelength of the laser light is 300 nm to 500 nm of blue, preferably 350 nm to 430 nm, more preferably 380 nm to 420 nm, 600 nm to 900 nm of red to near infrared, preferably 620 nm to 850 nm, more preferably 640 nm to 830 nm. .
[0389]
It is also preferable that the laser light is oscillated in a vertical multi by a method such as high frequency superposition.
[0390]
2) Thermal development
The photothermographic material of the present invention may be developed by any method, but is usually developed by raising the temperature of the photothermographic material exposed imagewise. The preferred development temperature is 80 ° C to 250 ° C, more preferably 100 ° C to 140 ° C.
The development time is preferably 1 to 30 seconds, more preferably 2 to 20 seconds, and particularly preferably 3 to 10 seconds.
[0390]
A plate heater method is preferred as the heat development method. The heat development method using the plate heater method is preferably a method described in JP-A-11-133572. The heat development photosensitive material on which a latent image is formed is brought into contact with a heating means in a heat development part, and heat for obtaining a visible image. In the developing device, the heating unit includes a plate heater, and a plurality of press rollers are disposed to face each other along one surface of the plate heater, and the heat is interposed between the press roller and the plate heater. A thermal development apparatus that performs thermal development by passing a development photosensitive material. It is preferable to divide the plate heater into 2 to 6 stages and lower the temperature of the tip portion by about 1 ° C. to 10 ° C.
[0392]
Such a method is also described in JP-A-54-30032, which can exclude moisture and organic solvents contained in the photothermographic material out of the system, and rapidly develop the photothermographic material. It is also possible to suppress changes in the shape of the support of the photothermographic material due to heating of the photothermographic material.
[0393]
3) System
Fuji Medical Dry Imager-FM-DPL and DRYPIX7000 can be given as medical laser imagers having an exposure unit and a heat development unit. The system is Fuji Medical Review No. 8, pages 39 to 55, and these techniques can be used. Further, it can also be applied as a photothermographic material for a laser imager in “AD network” proposed by Fuji Film Medical Co., Ltd. as a network system conforming to the DICOM standard.
[0394]
(Use of the present invention)
The photothermographic material using the high silver iodide photographic emulsion of the present invention forms a black-and-white image with a silver image, and is a photothermographic material for medical diagnosis, a photothermographic material for industrial photography, and a photothermographic material for printing. It is preferably used as a photothermographic material for COM.
[0395]
【Example】
EXAMPLES The present invention will be specifically described below with reference to examples, but the present invention is not limited to these examples.
Example 1
[0396]
1. Preparation of PET support
1) Film formation
Using terephthalic acid and ethylene glycol, PET having an intrinsic viscosity of IV = 0.66 (measured at 25 ° C. in phenol / tetrachloroethane = 6/4 (mass ratio)) was obtained according to a conventional method. This was pelletized, dried at 130 ° C. for 4 hours, melted at 300 ° C., extruded from a T-die and quenched, and an unstretched film having a thickness of 175 μm after heat setting was prepared.
[0397]
This was longitudinally stretched 3.3 times using rolls with different peripheral speeds, and then stretched 4.5 times with a tenter. The temperatures at this time were 110 ° C. and 130 ° C., respectively. Thereafter, the film was heat-fixed at 240 ° C. for 20 seconds and relaxed by 4% in the lateral direction at the same temperature. After slitting the chuck part of the tenter, knurling is performed on both ends and 4 kg / cm.²And a roll having a thickness of 175 μm was obtained.
[0398]
2) Surface discharge corona treatment
Using a solid state corona discharge treatment machine 6KVA model manufactured by Pillar, both surfaces of the support were treated at room temperature at 20 m / min. From the current and voltage readings at this time, the support is 0.375 kV · A · min / m.²It was found that the process was done. The treatment frequency at this time was 9.6 kHz, and the gap clearance between the electrode and the dielectric roll was 1.6 mm.
[0399]
3) Undercoat
(Preparation of undercoat layer coating solution)

[0400]

[0401]

[0402]
(undercoat)
After both surfaces of the biaxially stretched polyethylene terephthalate support having a thickness of 175 μm are subjected to the corona discharge treatment, the undercoat coating solution formulation {circle around (1)} is applied to one surface (photosensitive layer surface) with a wire bar. .6ml / m²(Per side) and dried at 180 ° C. for 5 minutes, and then the undercoat coating solution formulation (2) is applied to the back surface (back surface) with a wire bar at a wet coating amount of 5.7 ml / m.²And then dried at 180 ° C. for 5 minutes, and further, the undercoat coating solution formulation (3) is applied to the back surface (back surface) with a wire bar at a wet coating amount of 7.7 ml / m.²And then dried at 180 ° C. for 6 minutes to prepare an undercoat support.
[0403]
2. Back layer
1) Preparation of coating solution
[0404]
(Preparation of antihalation layer coating solution)
32.7 g of lime-processed gelatin in water kept at 40 ° C., monodisperse polymethyl methacrylate fine particles (average particle size 8 μm, particle size standard deviation 0.4 μm) 0.77 g, benzoisothiazolinone 0.08 g, sodium polystyrene sulfonate 0.3 g, 0.06 g of blue dye compound-1, 1.5 g of ultraviolet light absorber-1, 5.0 g of acrylic acid / ethyl acrylate copolymer latex (copolymerization ratio 5/95), N, N-ethylene Bis (vinylsulfone acetamide) 1.7 g was mixed, pH was adjusted to 6.0 with 1 mol / l sodium hydroxide, and the whole was made up to 818 ml with water to prepare an antihalation layer coating solution.
[0405]
(Preparation of back surface protective layer coating solution)
66.5 g of lime-processed gelatin in water kept at 40 ° C., 5.4 g of liquid paraffin emulsion as liquid paraffin, 0.10 g of benzoisothiazolinone, 0.5 g of sodium di (2-ethylhexyl) sulfosuccinate, polystyrene sulfonic acid 0.27 g of sodium, 13.6 mL of a 2% by mass aqueous solution of a fluorosurfactant (F-1), and 10.0 g of acrylic acid / ethyl acrylate copolymer (copolymerization weight ratio 5/95) were mixed to obtain 1 mol / The pH was adjusted to 6.0 with 1 sodium hydroxide, and the solution was made up to 1000 ml with water to obtain a back surface protective layer coating solution.
[0406]
2) Application of back layer
The coating amount of the antihalation layer coating solution on the back surface side of the undercoat support is 1.70 g / m.²In addition, the coating amount of the back surface protective layer was 0.79 g / m for the gelatin coating amount.²Then, a simultaneous multilayer coating was applied and dried to form a back layer.
[0407]
3. Image forming layer, intermediate layer, and surface protective layer
3-1. Preparation of coating materials
1) Preparation of silver halide emulsion
(Preparation of silver halide emulsion-1)
To a solution of 1420 ml of distilled water was added 4.3 ml of a 1% by weight potassium iodide solution, and a solution containing 3.5 ml of 0.5 mol / L sulfuric acid and 36.7 g of phthalated gelatin was stirred in a stainless steel reaction vessel. While maintaining the liquid temperature at 42 ° C., a solution A in which distilled water was diluted to 22.56 g of silver nitrate and diluted to 195.6 ml and solution B in which 21.8 g of potassium iodide was diluted with distilled water to a volume of 218 ml were added at a constant flow rate. The whole amount was added over 9 minutes. Thereafter, 10 ml of a 3.5% by mass aqueous hydrogen peroxide solution was added, and 10.8 ml of a 10% by mass aqueous solution of benzimidazole was further added.
[0408]
Further, Solution C obtained by diluting 51.86 g of silver nitrate to 317.5 ml and diluting Solution I obtained by diluting 60 g of potassium iodide to a volume of 600 ml with distilled water was completely added over 120 minutes at a constant flow rate. Solution D was added by the controlled double jet method while maintaining pAg at 8.1. 1 x 10 per mole of silver^-4The total amount of potassium hexachloroiridate (III) was added 10 minutes after the start of the addition of Solution C and Solution D so as to have a molar ratio. In addition, 5 seconds after completion of the addition of the solution C, an aqueous solution of potassium iron (II) hexacyanide was added at 3 × 10 5 per mol of silver.^-4The whole molar amount was added. The pH was adjusted to 3.8 using 0.5 mol / L sulfuric acid, stirring was stopped, and a precipitation / desalting / water washing step was performed. The pH was adjusted to 5.9 with 1 mol / L sodium hydroxide to prepare a silver halide dispersion having a pAg of 8.0.
[0409]
While maintaining the silver halide dispersion at 38 ° C. with stirring, 5 ml of a 0.34 mass% 1,2-benzisothiazolin-3-one methanol solution was added, and the temperature was raised to 47 ° C. After 20 minutes of temperature increase, sodium benzenethiosulfonate was added to a methanol solution with 7.6 × 10 6 per mol of silver.^-55 minutes later, tellurium sensitizer B was added in methanol solution to give 2.9 × 10 6 per mole of silver.^-4Mole was added and aged for 91 minutes.
Add 1.3 ml of a 0.8 mass% methanol solution of N, N′-dihydroxy-N ″, N ″ -diethylmelamine, and after 4 minutes, add 1 mol of 5-methyl-2-mercaptobenzimidazole with a methanol solution. 4.8 × 10 per^-3Mole and 1-phenyl-2-heptyl-5-mercapto-1,3,4-triazole in methanol solution at 5.4 × 10 5 per mole of silver^-3A silver halide emulsion-1 was prepared by adding a molar amount.
[0410]
The grains in the silver halide emulsion thus prepared were pure silver iodide grains having an average sphere equivalent diameter of 0.040 μm and a sphere equivalent diameter variation coefficient of 18%. Moreover, it is a tetrahedral particle | grain which has (001), {100}, {101} face, The ratio of the (gamma) phase was 30% when measured using the X-ray powder diffraction analysis. The particle size and the like were determined from an average of 1000 particles using an electron microscope.
[0411]
(Preparation of silver halide emulsion 2)
The temperature of the reaction solution was changed to 65 ° C., 5 ml of a 5 mass% methanol solution of 2,2 ′-(ethylenedithio) diethanol was added after the addition of solutions A and B, and the solution was maintained while maintaining pAg at 10.5. D was added by the controlled double jet method, and 3 minutes after addition of tellurium sensitizer during chemical sensitization, bromoauric acid was added at 5 × 10 5 per mole of silver.^-4Moles and potassium thiocyanate 2 x 10 per mole of silver^-3A silver halide emulsion 2 was prepared in the same manner as Emulsion 1 except that mol was added.
[0412]
Grains in the prepared silver halide emulsion have an average equivalent circle diameter of projected area of 0.164 μm, a grain thickness of 0.032 μm, an average aspect ratio of 5, an average sphere equivalent diameter of 0.11 μm, and a coefficient of variation of the equivalent sphere diameter of 23. % Pure silver iodide tabular grains. When measured using X-ray powder diffraction analysis, the proportion of the γ phase was 80%. The particle size and the like were determined from an average of 1000 particles using an electron microscope.
[0413]
(Preparation of silver halide emulsion 3)
Silver halide emulsion 3 in exactly the same manner as silver halide emulsion 1 except that the temperature of the reaction solution was changed to 27 ° C. and solution D was added by the controlled double jet method while maintaining pAg at 10.2. It was created.
[0414]
The grains in the prepared silver halide emulsion were pure silver iodide grains having an average sphere equivalent diameter of 0.022 μm and a sphere equivalent diameter variation coefficient of 17%. Further, they were dodecahedron grains having (001), {1 (-1) 0}, and {101} planes, and were silver iodide substantially consisting of a β phase as measured by X-ray powder diffraction analysis. The particle size and the like were determined from an average of 1000 particles using an electron microscope.
[0415]
(Preparation of mixed emulsion A for coating solution)
Silver halide emulsion-1, silver halide emulsion-2, and silver halide emulsion-3 were dissolved in an amount of 5: 2: 3 as a silver molar ratio, and benzothiazolium iodide was dissolved in a 1% by mass aqueous solution. 7 x 10 per mole of silver^-3Mole was added. Further, water was added so that the content of silver halide per 1 kg of the mixed emulsion for coating solution was 38.2 g as silver.
[0416]
Further, as “a compound in which a one-electron oxidant produced by one-electron oxidation can emit one electron or more”, compounds 2 and 20 and 26 are each 2 × 10 2 per mole of silver halide silver.^-3Molar amounts were added.
[0417]
Further, as compounds having an adsorbing group and a reducing group, the compounds (12), (27) and (36) are each 8 × 10 6 per mole of silver halide.^-3Molar amounts were added.
[0418]
2) Preparation of fatty acid silver dispersion
<Preparation of recrystallized behenic acid>
100 kg of behenic acid (product name Edenor C22-85R) manufactured by Henkel was mixed in 1200 kg of isopropyl alcohol, dissolved at 50 ° C., filtered through a 10 μm filter, cooled to 30 ° C., and recrystallized. The cooling speed during recrystallization was controlled at 3 ° C./hour. The obtained crystals were centrifugally filtered, washed with 100 kg of isopropyl alcohol, and then dried. When the obtained crystals were esterified and subjected to GC-FID measurement, the behenic acid content was 96 mol%, and in addition, lignoceric acid was 2 mol%, arachidic acid was 2 mol%, and erucic acid was 0.001 mol%. It was.
[0419]
<Preparation of fatty acid silver dispersion>
Recrystallized behenic acid 88 kg, distilled water 422 L, 5 mol / L NaOH aqueous solution 49.2 L and t-butyl alcohol 120 L were mixed and stirred at 75 ° C. for 1 hour to react to obtain sodium behenate solution B. Separately, 206.2 L (pH 4.0) of an aqueous solution containing 40.4 kg of silver nitrate was prepared and kept warm at 10 ° C. A reaction vessel containing 635 L of distilled water and 30 L of t-butyl alcohol was kept at 30 ° C., and with sufficient agitation, the total amount of the previous sodium behenate solution and the total amount of silver nitrate aqueous solution were kept at a constant flow rate of 93 minutes and 15 seconds, respectively. And added over 90 minutes. At this time, only the silver nitrate aqueous solution is added for 11 minutes after the start of the addition of the aqueous silver nitrate solution, and then the addition of the sodium behenate solution is started. After the addition of the aqueous silver nitrate solution, only the sodium behenate solution is added for 14 minutes and 15 seconds. It was made to be. At this time, the temperature in the reaction vessel was 30 ° C., and the external temperature was controlled so that the liquid temperature was constant. The pipe of the addition system for the sodium behenate solution was kept warm by circulating hot water outside the double pipe so that the liquid temperature at the outlet at the tip of the addition nozzle was 75 ° C. Moreover, the piping of the addition system of the silver nitrate aqueous solution was kept warm by circulating cold water outside the double pipe. The addition position of the sodium behenate solution and the addition position of the aqueous silver nitrate solution were arranged symmetrically around the stirring axis, and were adjusted so as not to contact the reaction solution.
[0420]
After completion of the addition of the sodium behenate solution, the mixture was left stirring for 20 minutes at the same temperature, heated to 35 ° C. over 30 minutes, and then aged for 210 minutes. Immediately after completion of aging, the solid content was separated by centrifugal filtration, and the solid content was washed with water until the conductivity of filtered water reached 30 μS / cm. Thus, a fatty acid silver salt was obtained. The obtained solid content was stored as a wet cake without drying.
[0421]
When the morphology of the obtained silver behenate particles was evaluated by electron microscope photography, the average values were a = 0.21 μm, b = 0.4 μm, c = 0.4 μm, average aspect ratio 2.1, and equivalent sphere diameter. The crystal had a coefficient of variation of 11%. (A, b, and c are the text provisions)
[0422]
19.3 kg of polyvinyl alcohol (trade name: PVA-217) and water are added to a wet cake corresponding to a dry solid content of 260 kg, and the whole amount is made 1000 kg, and then slurried with a dissolver blade, and further a pipeline mixer (manufactured by Mizuho Kogyo Co., Ltd.). : PM-10 type).
[0423]
Next, the pre-dispersed stock solution is subjected to a pressure of 1150 kg / cm of a disperser (trade name: Microfluidizer M-610, manufactured by Microfluidics International Corporation, using a Z-type interaction chamber).²And was treated three times to obtain a silver behenate dispersion. The cooling operation was carried out by installing a serpentine heat exchanger before and after the interaction chamber, and adjusting the temperature of the refrigerant to a dispersion temperature of 18 ° C.
[0424]
3) Preparation of reducing agent dispersion
(Preparation of reducing agent-1 dispersion)
10 kg of water was added to 10 kg of a reducing agent-1 (2,2′-methylenebis- (4-ethyl-6-tert-butylphenol)) 10 kg and a 10% by weight aqueous solution of modified polyvinyl alcohol (Kuraray Co., Ltd., Poval MP203). Add and mix well to make a slurry. This slurry was fed with a diaphragm pump, dispersed for 3 hours in a horizontal sand mill (UVM-2: manufactured by Imex Co., Ltd.) filled with zirconia beads having an average diameter of 0.5 mm, and then benzoisothiazolinone sodium salt 0. 2 g and water were added to prepare a reducing agent concentration of 25% by mass. This dispersion was heat-treated at 60 ° C. for 5 hours to obtain a reducing agent-1 dispersion. The reducing agent particles contained in the reducing agent dispersion thus obtained had a median diameter of 0.40 μm and a maximum particle diameter of 1.4 μm or less. The obtained reducing agent dispersion was filtered through a polypropylene filter having a pore size of 3.0 μm to remove foreign substances such as dust and stored.
(Preparation of reducing agent-2 dispersion)
10 mass of reducing agent-2 (6,6′-di-t-butyl-4,4′-dimethyl-2,2′-butylidenediphenol) and modified polyvinyl alcohol (Kuraray Co., Ltd., Poval MP203) 10 kg of water was added to 16 kg of% aqueous solution and mixed well to obtain a slurry. This slurry was fed with a diaphragm pump and dispersed for 3 hours 30 minutes in a horizontal sand mill (UVM-2: manufactured by Imex Co., Ltd.) filled with zirconia beads having an average diameter of 0.5 mm, and then benzoisothiazolinone sodium salt 0.2 g and water were added to prepare a reducing agent concentration of 25% by mass. This dispersion was heated at 40 ° C. for 1 hour, and then further heated at 80 ° C. for 1 hour to obtain a reducing agent-2 dispersion. The reducing agent particles contained in the reducing agent dispersion thus obtained had a median diameter of 0.50 μm and a maximum particle diameter of 1.6 μm or less. The obtained reducing agent dispersion was filtered through a polypropylene filter having a pore size of 3.0 μm to remove foreign substances such as dust and stored.
[0425]
(Preparation of other reducing agent dispersions)
Other solid dispersions of the reducing agent were also dispersed by the same method as that for the reducing agent-2.
[0426]
4) Preparation of hydrogen bonding compound-1 dispersion
Add 10 kg of water to 10 kg of 10% aqueous solution of hydrogen bonding compound-1 (tri (4-t-butylphenyl) phosphine oxide) and modified polyvinyl alcohol (Kuraray Co., Ltd., Poval MP203). Mix to make a slurry. This slurry was fed with a diaphragm pump and dispersed for 4 hours in a horizontal sand mill (UVM-2: manufactured by Imex Co., Ltd.) filled with zirconia beads having an average diameter of 0.5 mm. 2 g and water were added to prepare a hydrogen bonding compound concentration of 25% by mass. This dispersion was heated at 40 ° C. for 1 hour and then further heated at 80 ° C. for 1 hour to obtain a hydrogen bonding compound-1 dispersion. The hydrogen bonding compound particles contained in the hydrogen bonding compound dispersion thus obtained had a median diameter of 0.45 μm and a maximum particle diameter of 1.3 μm or less. The obtained hydrogen bonding compound dispersion was filtered through a polypropylene filter having a pore size of 3.0 μm to remove foreign substances such as dust and stored.
[0427]
5) Preparation of development accelerator dispersion
(Preparation of Development Accelerator-1 Dispersion)
10 kg of development accelerator-1 and 20 kg of 10% by weight aqueous solution of modified polyvinyl alcohol (Kuraray Co., Ltd., Poval MP203) were added to 10 kg of water and mixed well to obtain a slurry. This slurry was fed with a diaphragm pump and dispersed for 3 hours 30 minutes in a horizontal sand mill (UVM-2: manufactured by Imex Co., Ltd.) filled with zirconia beads having an average diameter of 0.5 mm, and then benzoisothiazolinone sodium salt 0.2 g and water were added to adjust the concentration of the development accelerator to 20% by mass to obtain a development accelerator-1 dispersion. The development accelerator particles contained in the development accelerator dispersion thus obtained had a median diameter of 0.48 μm and a maximum particle diameter of 1.4 μm or less. The obtained development accelerator dispersion was filtered through a polypropylene filter having a pore size of 3.0 μm to remove foreign substances such as dust and stored.
[0428]
(Preparation of dispersion of development accelerator-2 and other development accelerators)
The solid dispersions of development accelerator-2 and other development accelerators were also dispersed by the same method as development accelerator-1.
[0429]
6) Preparation of polyhalogen compound dispersion
(Organic polyhalogen compound-1 dispersion)
10 kg of organic polyhalogen compound-1 (tribromomethanesulfonylbenzene), 10 kg of 20% by weight aqueous solution of modified polyvinyl alcohol (Poval MP203 manufactured by Kuraray Co., Ltd.), 0.4 kg of 20% by weight aqueous solution of sodium triisopropylnaphthalenesulfonate, Then, 14 kg of water was added and mixed well to obtain a slurry. This slurry was fed with a diaphragm pump and dispersed for 5 hours in a horizontal sand mill (UVM-2: manufactured by Imex Co., Ltd.) filled with zirconia beads having an average diameter of 0.5 mm. 2 g and water were added to prepare an organic polyhalogen compound concentration of 30% by mass to obtain an organic polyhalogen compound-1 dispersion. The organic polyhalogen compound particles contained in the polyhalogen compound dispersion thus obtained had a median diameter of 0.41 μm and a maximum particle diameter of 2.0 μm or less. The obtained organic polyhalogen compound dispersion was filtered through a polypropylene filter having a pore size of 10.0 μm to remove foreign substances such as dust and stored.
[0430]
(Organic polyhalogen compound-2 dispersion)
10 kg of an organic polyhalogen compound-2 (N-butyl-3-tribromomethanesulfonylbenzoamide), 20 kg of a 10% by mass aqueous solution of modified polyvinyl alcohol (Poval MP203 manufactured by Kuraray Co., Ltd.), and 20 of sodium triisopropylnaphthalenesulfonate 0.4 kg of a mass% aqueous solution was added and mixed well to obtain a slurry. This slurry was fed with a diaphragm pump and dispersed for 5 hours in a horizontal sand mill (UVM-2: manufactured by Imex Co., Ltd.) filled with zirconia beads having an average diameter of 0.5 mm. 2 g and water were added to prepare an organic polyhalogen compound concentration of 30% by mass. This dispersion was heated at 40 ° C. for 5 hours to obtain an organic polyhalogen compound-2 dispersion. The organic polyhalogen compound particles contained in the polyhalogen compound dispersion thus obtained had a median diameter of 0.40 μm and a maximum particle diameter of 1.3 μm or less. The obtained organic polyhalogen compound dispersion was filtered through a polypropylene filter having a pore size of 3.0 μm to remove foreign substances such as dust and stored.
[0431]
7) Preparation of phthalazine compound-1 solution
8 kg of modified polyvinyl alcohol MP203 manufactured by Kuraray Co., Ltd. was dissolved in 174.57 kg of water, and then 3.15 kg of a 20 mass% aqueous solution of sodium triisopropylnaphthalenesulfonate and 70 mass of phthalazine compound-1 (6-isopropylphthalazine). 14.28 kg of a% aqueous solution was added to prepare a 5% by mass solution of phthalazine compound-1.
[0432]
8) Preparation of mercapto compound
(Preparation of mercapto compound-1 aqueous solution)
7 g of mercapto compound-1 (1- (3-sulfophenyl) -5-mercaptotetrazole sodium salt) was dissolved in 993 g of water to obtain a 0.7% by mass aqueous solution.
[0433]
(Preparation of mercapto compound-2 aqueous solution)
20 g of mercapto compound-2 (1- (3-methylureidophenyl) -5-mercaptotetrazole) was dissolved in 980 g of water to obtain a 2.0 mass% aqueous solution.
[0434]
9) Preparation of pigment-1 dispersion
C. I. Pigment Blue 60 (64 g) and Kao Corp. Demol N (6.4 g) were added to 250 g of water and mixed well to obtain a slurry. Prepare 800 g of zirconia beads having an average diameter of 0.5 mm, put them in a vessel together with the slurry, and disperse with a disperser (1/4 G sand grinder mill: manufactured by IMEX Co., Ltd.) for 25 hours. A pigment-1 dispersion was obtained by adjusting the concentration to 5% by mass. The pigment particles contained in the pigment dispersion thus obtained had an average particle size of 0.21 μm.
[0435]
10) Preparation of SBR latex solution
The SBR latex was prepared as follows.
In a polymerization kettle of a gas monomer reactor (TAS-2J type manufactured by Pressure Glass Industrial Co., Ltd.), 287 g of distilled water and a surfactant (Pionin A-43-S (manufactured by Takemoto Yushi Co., Ltd.)): solid content 48.5 (Mass%) 7.73 g, 1 mol / liter NaOH 14.06 ml, ethylenediaminetetraacetic acid tetrasodium salt 0.15 g, styrene 255 g, acrylic acid 11.25 g, tert-dodecyl mercaptan 3.0 g were put, the reaction vessel was sealed and the stirring speed was Stir at 200 rpm. After degassing with a vacuum pump and repeating nitrogen gas replacement several times, 108.75 g of 1,3-butadiene was injected to raise the internal temperature to 60 ° C. A solution obtained by dissolving 1.875 g of ammonium persulfate in 50 ml of water was added thereto, and the mixture was stirred as it was for 5 hours. The mixture was further heated to 90 ° C. and stirred for 3 hours. After the reaction was completed, the internal temperature was lowered to room temperature, and then 1 mol / liter NaOH and NH.₄Na with OH⁺Ion: NH₄ ⁺The addition treatment was performed so that the ion was 1: 5.3 (molar ratio), and the pH was adjusted to 8.4. Thereafter, the mixture was filtered through a polypropylene filter having a pore size of 1.0 μm to remove foreign substances such as dust and stored, and 774.7 g of SBR latex was obtained. When the halogen ions were measured by ion chromatography, the chloride ion concentration was 3 ppm. As a result of measuring the concentration of the chelating agent by high performance liquid chromatography, it was 145 ppm.
[0436]
The latex has an average particle size of 90 nm, Tg = 17 ° C., solid content concentration of 44 mass%, equilibrium moisture content at 25 ° C. and 60% RH, 0.6 mass%, ion conductivity of 4.80 mS / cm (measurement of ion conductivity is A conductivity meter CM-30S manufactured by Toa Denpa Kogyo Co., Ltd. was used, and the latex stock solution (44% by mass measured at 25 ° C.) was pH 8.4.
[0437]
11) Preparation of color former of the present invention and dispersion of comparative compound
1 kg of the color former (D-1) of the present invention and 2 kg of a 10% by weight aqueous solution of modified polyvinyl alcohol (Kuraray Co., Ltd., Poval MP203) were added to 1 kg of water and mixed well to obtain a slurry. This slurry was fed with a diaphragm pump and dispersed for 45 minutes in a horizontal sand mill (UVM-2: manufactured by Imex Co., Ltd.) filled with zirconia beads having an average diameter of 0.5 mm. 02 g and water were added so that the concentration of the color former (D-1) of the present invention was 20% by mass to obtain a color former (D-1) dispersion of the present invention. The color former (D-1) particles of the present invention contained in the color former (D-1) dispersion of the present invention thus obtained had a median diameter of 0.45 μm and a maximum particle diameter of 1.4 μm or less. The obtained development accelerator dispersion was filtered through a polypropylene filter having a pore size of 3.0 μm to remove foreign substances such as dust and stored. Other color formers of the present invention and comparative color former C-1 were also dispersed in the same manner to obtain a 15% by mass dispersion. A dispersion was obtained by adjusting the dispersion time so that the median diameter of each particle was 0.45 μm.
Dispersions were similarly prepared for other color formers and comparative compounds of the present invention.
[0438]
3-2. Preparation of coating solution
1) Preparation of image forming layer coating solution
1000 g of the fatty acid silver dispersion obtained above, 276 ml of water, pigment-1 dispersion, organic polyhalogen compound-1 dispersion, organic polyhalogen compound-2 dispersion, phthalazine compound-1 solution, SBR latex (Tg: 17 ° C. ) Liquid, reducing agent dispersion (amount and type are listed in Table 1), hydrogen bonding compound-1 dispersion, development accelerator-1 dispersion, development accelerator-2 dispersion, mercapto compound-1 aqueous solution, mercapto Compound I aqueous solution, the color former of the present invention, or comparative compound C-1 (amount and type are listed in Table 1) were added in order, and silver halide mixed emulsion A was added immediately before coating and mixed well. The layer coating solution was fed directly to the coating die.
[0439]
The viscosity of the image forming layer coating solution was 25 [mPa · s] at 40 ° C. (No. 1 rotor, 60 rpm) as measured with a B-type viscometer of Tokyo Keiki.
The viscosity of the coating solution at 25 ° C. using an RFS fluid spectrometer manufactured by Rheometrics Far East Co., Ltd. is 242, 65, 48 at shear rates of 0.1, 1, 10, 100, and 1000 [1 / second], respectively. 26 and 20 [mPa · s].
[0440]
The amount of zirconium in the coating solution was 0.52 mg per 1 g of silver.
[0441]
2) Preparation of intermediate layer coating solution
Polyvinyl alcohol PVA-205 (manufactured by Kuraray Co., Ltd.) 1000 g, pigment-1 dispersion 272 g, methyl methacrylate / styrene / butyl acrylate / hydroxyethyl methacrylate / acrylic acid copolymer (copolymer weight ratio 64/9/20/5 / 2) 27200 ml of an aerosol OT (manufactured by American Cyanamid Co.) was added to 4200 ml of a latex 19 mass% solution, 135 ml of a 20 mass% aqueous solution of diammonium phthalate, and water was added to a total amount of 10000 g. In addition, an intermediate layer coating solution was prepared by adjusting with NaOH so that the pH was 7.5, and 9.1 ml / m²Then, the solution was fed to the coating die.
The viscosity of the coating solution was 58 [mPa · s] at a B-type viscometer of 40 ° C. (No. 1 rotor, 60 rpm).
[0442]
3) Preparation of surface protective layer first layer coating solution
Inert gelatin (64 g) is dissolved in water, and methyl methacrylate / styrene / butyl acrylate / hydroxyethyl methacrylate / acrylic acid copolymer (copolymerization weight ratio 64/9/20/5/2) 19.0% by weight of latex 112 g, 30 ml of 15% by weight methanol solution of phthalic acid, 23 ml of 10% by weight aqueous solution of 4-methylphthalic acid, 28 ml of sulfuric acid having a concentration of 0.5 mol / L, and 5% by weight aqueous solution of Aerosol OT (American Cyanamid Co., Ltd.) Add 5 ml, 0.5 g phenoxyethanol, 0.1 g benzoisothiazolinone, add water to make a total amount of 750 g, and use 26 ml of 4% by weight chromium alum mixed with a static mixer just before coating. 18.6 ml / m²Then, the solution was fed to the coating die.
The viscosity of the coating solution was 20 [mPa · s] at a B-type viscometer of 40 ° C. (No. 1 rotor, 60 rpm).
[0443]
4) Preparation of surface protective layer second layer coating solution
Inert gelatin (80 g) is dissolved in water, and methyl methacrylate / styrene / butyl acrylate / hydroxyethyl methacrylate / acrylic acid copolymer (copolymerization weight ratio 64/9/20/5/2) 27.5% by weight of latex 102 g, 5.4 ml of a 2% by weight solution of a fluorosurfactant (F-1), 5.4 ml of a 2% by weight aqueous solution of a fluorosurfactant (F-2), Aerosol OT (American Cyanamid Co., Ltd.) ) 23 ml, 4 g of polymethyl methacrylate fine particles (average particle size 0.7 μm), 21 g of polymethyl methacrylate fine particles (average particle size 4.5 μm), 1.6 g of 4-methylphthalic acid, 4.8 g of phthalic acid Water was added to 44 ml of 0.5 mol / L sulfuric acid and 10 mg of benzoisothiazolinone to a total amount of 650 g. A solution prepared by mixing 445 ml of an aqueous solution containing a mass% chromium alum and 0.67 mass% phthalic acid with a static mixer immediately before coating is used as the surface protective layer second layer coating solution, 8.3 ml / m.²Then, the solution was fed to the coating die.
The viscosity of the coating solution was 19 [mPa · s] at a B-type viscometer of 40 ° C. (No. 1 rotor, 60 rpm).
[0444]
3-3. Preparation of coated sample
1) Preparation of photothermographic material
A photothermographic material sample was applied simultaneously on the surface opposite to the back surface by the slide bead coating method in the order of the image forming layer, intermediate layer, surface protective layer first layer, and surface protective layer second layer from the undercoat surface. It was created. At this time, the image forming layer and the intermediate layer were adjusted to 31 ° C., the first surface protective layer was adjusted to 36 ° C., and the second surface protective layer was adjusted to 37 ° C.
[0445]
Coating amount of each compound in the image forming layer (g / m²) Is as follows.
Fatty acid silver 5.27
Pigment (C.I. Pigment Blue 60) 0.036
Polyhalogen compound-1 0.09
Polyhalogen compound-2 0.14
Phthalazine Compound-1 0.18
SBR latex 9.43
Reducing agent (Amount and type are listed in Table 1)
Hydrogen bonding compound-1 0.28
Development accelerator-1 0.025
Development accelerator-2 0.020
Mercapto Compound-1 0.002
Mercapto compound-2 0.006
Color former (compound of the present invention or comparative compound) (Amounts and types are listed in Table 1)
Silver halide (as Ag) 0.046
[0446]
The coating and drying conditions are as follows.
The support was neutralized with ion wind before coating, and coating was performed at a speed of 160 m / min. The coating and drying conditions were adjusted within the following ranges for each sample, and were set to conditions that would provide the most stable surface shape.
The gap between the coating die tip and the support is 0.10 to 0.30 mm.
The pressure in the decompression chamber is set to 196 to 882 Pa lower than the atmospheric pressure.
In the subsequent chilling zone, the coating solution is cooled with air at a dry bulb temperature of 10 to 20 ° C.
It is transported in a non-contact manner, and dried with a dry air having a dry bulb temperature of 23 to 45 ° C. and a wet bulb temperature of 15 to 21 ° C. in a helical contactless dryer.
After drying, the humidity is adjusted at 25 ° C. and humidity of 40-60% RH.
Subsequently, the film surface was heated to 70 to 90 ° C., and after the heating, the film surface was cooled to 25 ° C.
[0447]
The photothermographic material thus prepared had a Beck smoothness of 550 seconds on the image forming layer surface side and 130 seconds on the back surface. Further, the pH of the film surface on the image forming layer surface side was measured and found to be 6.0.
[0448]
The chemical structures of the compounds used in the examples of the present invention are shown below.
[0449]
Embedded image

[0450]
Embedded image

[0451]
Embedded image

[0452]
Embedded image

[0453]
Embedded image

[0454]
Embedded image

[0455]
(Evaluation of photographic performance)
The obtained sample was cut into half-cut sizes, packaged in the following packaging materials in an environment of 25 ° C. and 50% RH, stored at room temperature for 2 weeks, and then evaluated as follows.
(Packaging material)
PET 10 μm / PE 12 μm / aluminum foil 9 μm / Ny 15 μm / polyethylene 50 μm containing 3% by mass of carbon;
Oxygen permeability: 0.02 ml / atm · m²・ 25 ℃ ・ day,
Moisture permeability: 0.10 g / atm · m²-25 degreeCday.
[0456]
As a sample, an NLHV3000E semiconductor laser manufactured by Nichia Corporation was mounted as a semiconductor laser light source on the exposure part of Fuji Medical Dry Laser Imager DRYPIX7000, and the beam diameter was reduced to 100 μm. The illuminance on the photosensitive material surface of the laser beam is 0 and 1 mW / mm²~ 1000mW / mm²Vary between 10^-6Exposure was performed in seconds. The oscillation wavelength of the laser beam was 405 nm. In the heat development, three panel heaters were set at 107 ° C.-121 ° C.-121 ° C., and the development was carried out so that the conveyance speed was increased to a total of 8 seconds.
[0457]
3) Evaluation of photographic performance
<Evaluation of hue angle hab>
The hue angle is a defined in JIS Z8729 standard at a density of 1.0.^*b^*In the angle obtained from the coordinates, the medical sensitive material is preferably in the range of 180 ° to 270 °,
A range of 210 ° to 260 ° is more preferable. Particularly preferred is a range of 245 ° to 255 °.
[0458]
<Evaluation of dark thermal image storage stability>
The change of image tone under forced environmental conditions was investigated. In order to store the heat-developed sample in an environment of 40 ° C. and 40% RH in the dark for 5 days, and observe the color tone change before and after the image of density 1.0, the density at 1.0 before and after aging was observed. The hue angle hab is measured and expressed as an angle difference (Δ hue angle) from before the lapse of time, and the smaller the difference, the smaller the hue change and the better performance.
[0459]
<Evaluation of print-out color tone>
The printout property was evaluated under forced evaluation conditions.
The evaluation condition was that the heat-developed sample was subjected to Schaukasten (illuminance 7000 lux in a 25 ° C. 60% RH environment) for 5 days, and the change in color tone before and after aging was observed for an image with a density of 1.0. The hue angle hab at a density of 1.0 is measured and expressed as an angle difference (Δ hue angle) from before aging, and the smaller the difference, the smaller the color change and the better performance.
[0460]
[Table 1]

[0461]
The obtained results are shown in Table 1.
By using the color former of the present invention, the Δ hue angle became small and the change in color tone became small both in the dark and at the time of irradiation with light (Shakasten aging).
In particular, the photothermographic materials -10 to 12 gave preferable results.
[0462]
Example 2
Sample No. 1 of Example 1 10, Samples 20 to 24 were prepared by changing the development accelerator as shown in Table 2 instead of the development accelerator-1 and the development accelerator-2.
These accelerators were added by preparing dispersions in the same manner as development accelerator-1.
[0463]
[Table 2]

[0464]
The results of evaluation in the same manner as in Example 1 are shown in Table 2.
As is apparent from the results in Table 2, even when the type of the development accelerator was changed, an excellent photothermographic material having no change in color tone in a dark place and when irradiated with light (timed by Shakasten) could be obtained.
In particular, the photothermographic materials-20, 23 and 24 gave preferable results.
[0465]
Example 3
In samples 1 to 4 used in Example 1, compound R-17 represented by general formula R instead of reducing agent-1 and compound H represented by general formula (H) instead of polyhalogen compound-1 A sample was prepared in the same manner as in Example 1 except that -17 was used. As a result of evaluation in the same manner as in Example 1, the effect of the present invention was obtained as in Example 1.
[0466]
【The invention's effect】
According to the present invention, a photothermographic material having improved image color tone and image storage stability is provided.

Claims (15)

A photothermographic material comprising a photosensitive silver halide, a non-photosensitive organic silver salt, a reducing agent, a binder, and a color former that develops color by thermal development on the same surface of the support, the photosensitive halogenated A photothermographic material, wherein the silver iodide content of silver is 40 mol% or more, and the dye produced by the color former can form hydrogen bonds in the molecule. 2. The photothermographic material according to claim 1, wherein the dye produced by the color former has a maximum absorption in a wavelength region of 350 nm to 500 nm or 600 nm to 700 nm. 3. The photothermographic material according to claim 1, wherein the dye produced by the color former has a maximum absorption in a wavelength region of 350 nm to 500 nm. 4. The photothermographic material according to claim 1, wherein the color former is a compound represented by the following formula (Ia) or (Ib).

In [Formula (Ia), or _{(Ib), R} 11 ~R ₁₅ represents a substituent group which substitutes a hydrogen atom or a benzene ring, X represents an aryl group, a heterocyclic group or an active methine _{group, R 11} ~ At least one of R ₁₅ and X has at least one hydrogen bonding substituent. ] 5. The photothermographic material according to claim 4, wherein, in the formula (Ia) or (Ib), R ₁₂ is a secondary or tertiary alkyl group. 6. The photothermographic material according to claim 4, wherein the color former represented by the formula (Ia) or (Ib) is represented by the following formula (IIa) or (IIb): material.

[In Formula (IIa) or (IIb), R _{21 to} R ₂₇ represent a hydrogen atom or a substituent that can be substituted on the benzene ring. Y ₂₁ and Y ₂₂ represent a hydrogen atom or a substituent that can be substituted on the benzene ring, at least one of which is a hydroxy group or an amino group, and at least one of R _{21 to} R ₂₇ , Y ₂₁ , and Y ₂₂ is at least It has one hydrogen bonding substituent. ] In the formula (IIa) or (IIb), R ₂₂ is a secondary or tertiary alkyl group, and at least one of R ₂₅ or R ₂₆ is a hydrogen-bonding substituent. 6. The photothermographic material according to 6. 8. The photothermographic material according to claim 1, wherein the dye produced from the color former can form a 5- to 7-membered ring by hydrogen bonding in the molecule. 9. The photothermographic material according to claim 1, wherein a silver iodide content of the photosensitive silver halide is 80 mol% or more. The photothermographic material according to claim 1, wherein the silver iodide content of the photosensitive silver halide is 90 mol% or more. The photothermographic material according to claim 1, further comprising a development accelerator. The photothermographic material according to claim 1, wherein the photothermographic material is subjected to scanning exposure with a laser beam. 13. The photothermographic material according to claim 12, wherein the laser beam is a semiconductor laser. 14. The photothermographic material according to claim 13, wherein the semiconductor laser is a blue semiconductor laser. The photothermographic material according to claim 1, wherein the photothermographic material is heat-developed within a time of 10 seconds.