JP2004285286A

JP2004285286A - Polyamide composition

Info

Publication number: JP2004285286A
Application number: JP2003081925A
Authority: JP
Inventors: Kozo Tamura; 興造田村; Kiyobumi Kadowaki; 清文門脇
Original assignee: Kuraray Co Ltd
Current assignee: Kuraray Co Ltd
Priority date: 2003-03-25
Filing date: 2003-03-25
Publication date: 2004-10-14
Anticipated expiration: 2023-03-25
Also published as: JP4180413B2

Abstract

<P>PROBLEM TO BE SOLVED: To provide a polyamide composition which can meet such a requirement as to shorten a cycle of injection molding, to improve dynamic properties or heat aging resistance, etc. <P>SOLUTION: The polyamide composition comprises a dicarboxylic acid unit containing 50-100 mol% terephthalic acid unit and a diamine unit containing 50-100 mol% aliphatic alkylene diamine unit of 6-18C, and at least one sort of hydroxide of 0.01-0.2 mol selected from the group consisting of sodium hydroxide, potassium hydroxide and barium hydroxide is combined with 1 kg polyamide whose intrinsic viscosity[η] measured at 30°C in a concentrated sulfuric acid is 0.4-3.0 dL/g. <P>COPYRIGHT: (C)2005,JPO&NCIPI

Description

【０００１】
【発明の属する技術分野】
本発明は、特定のジカルボン酸単位とジアミン単位からなるポリアミドに特定の金属水酸化物を配合したポリアミド組成物に関する。
【０００２】
【従来の技術】
従来からナイロン６、ナイロン６６などに代表される結晶性ポリアミドはその優れた特性と溶融成形の容易さから汎用のエンジニアリングプラスチックとして広く用いられているが、一方では耐熱性不足、吸水による寸法安定性の不良などの問題点も指摘されている。特に近年の表面実装技術（ＳＭＴ）の発展に伴うリフローハンダ耐熱性を必要とする電気・電子分野、あるいは年々耐熱性への要求が高まる自動車のエンジンルーム部品などにおいては、従来のポリアミドでの使用が困難となってきており、より耐熱性、寸法安定性、機械特性、物理化学特性に優れたポリアミドへの要求が高まっている。
【０００３】
このような世の中の要求に対し、テレフタル酸と１，６−ヘキサンジアミンを主成分とするＰＡ６Ｔ系ポリアミド等の半芳香族ポリアミドなどが種々提案され、一部は実用化されている。また、耐熱性、低吸水性および耐クリープ性においてさらに優れた性能を有する、テレフタル酸と１，９−ノナンジアミンおよび／または２−メチル−１，８−オクタンジアミンをジアミン単位とするＰＡ９Ｔ系ポリアミドも提案されている。
しかしながら、用途によっては射出成形のサイクル短縮、さらなる力学特性の向上、さらなる耐熱老化性の向上が要求される場合がある。
【０００４】
ＰＡ９Ｔ系ポリアミドに関しては、特開平７−２２８７６８号公報（特許文献１）に、銅化合物、ハロゲン化アルカリ金属塩および有機系安定剤を配合してなる耐熱老化性ポリアミド組成物が、また、特開２０００−１９８９２２号公報（特許文献２）に、銅化合物、ハロゲン化アルカリ金属塩および結晶核剤を配合してなる、耐熱性、溶融安定性などに優れたポリアミド組成物が記載されている。
【０００５】
【特許文献１】
特開平７−２２８７６８号公報
【特許文献２】
特開２０００−１９８９２２号公報
【０００６】
【発明が解決しようとする課題】
しかして本発明は、半芳香族ポリアミドに対する、射出成形のサイクル短縮、さらなる力学特性の向上、さらなる耐熱老化性の向上といった要求に応えることのできるポリアミド組成物を新たに提供することにある。
【０００７】
【課題を解決するための手段】
本発明者らは、上記の課題を解決するために鋭意研究した結果、半芳香族ポリアミドに対して水酸化ナトリウム、水酸化カリウム、水酸化バリウムからなる群より選ばれる少なくとも１種の水酸化物を特定量配合することにより、半芳香族ポリアミドが有する耐熱性、低吸水性、耐薬品性などを損なうことなく、結晶化速度、力学特性および熱安定性を向上させることができることを見出して本発明を完成するに至った。
【０００８】
すなわち、本発明は、テレフタル酸単位を５０〜１００モル％含有するジカルボン酸単位と、炭素数６〜１８の脂肪族アルキレンジアミン単位を５０〜１００モル％含有するジアミン単位とからなり、濃硫酸中３０℃で測定した極限粘度［η］が０．４〜３．０ｄｌ／ｇであるポリアミド１ｋｇに対し、水酸化ナトリウム、水酸化カリウム、水酸化バリウムからなる群より選ばれる少なくとも１種の水酸化物０．０１〜０．２モルを配合してなるポリアミド組成物を提供する。
【０００９】
なお、特開昭５５−７８０５３号公報には、水酸化バリウムなどの周期律表第ＩＩＡ族金属の化合物を含有し、γ型結晶混在率が０．３〜０．７である、剛性が改良されたナイロン６が記載されている。しかし、同公報には、剛性以外の特性向上に関する記述はないし、ナイロン６以外の他種ポリアミドについては言及されていない。
また、特開２００３−４１１１７号公報には、ＰＡ９Ｔ系ポリアミドにアミド基１個当たりの炭素数が７〜１２である脂肪族ポリアミドを配合してなる、低温での金型冷却が可能なポリアミド組成物が記載されており、さらに水酸化マグネシウム、水酸化アルミニウム、水酸化カルシウム、水酸化バリウム等の金属水酸化物を配合できることが記載されている。しかし、この金属水酸化物は、ＰＡ９Ｔ系ポリアミドと脂肪族ポリアミドとのアミド交換反応を促進する効果のある酸を捕捉することを目的としており、本発明とは全く異なる技術思想の下で使用されるものである。
【００１０】
【発明の実施の形態】
本発明に用いられるポリアミドを構成するジカルボン酸単位は、テレフタル酸単位を５０〜１００モル％含有していることが必要であり、６０〜１００モル％含有していることが好ましく、７５〜１００モル％含有していることがより好ましく、９０〜１００モル％含有していることがさらに好ましい。ジカルボン酸単位におけるテレフタル酸単位の含有量が５０モル％未満の場合には、ポリアミド組成物から得られる成形品の耐熱性、力学特性が低下する。
【００１１】
上記のジカルボン酸単位は、５０モル％以下であれば、テレフタル酸単位以外の他のジカルボン酸単位を含有していてもよい。かかる他のジカルボン酸単位としては、例えば、マロン酸、ジメチルマロン酸、コハク酸、グルタル酸、アジピン酸、２−メチルアジピン酸、トリメチルアジピン酸、ピメリン酸、２，２−ジメチルグルタル酸、３，３−ジエチルコハク酸、アゼライン酸、セバシン酸、スベリン酸、ドデカン二酸等の脂肪族カルボン酸；１，３−シクロペンタンジカルボン酸、１，４−シクロヘキサンジカルボン酸等の脂環式ジカルボン酸；イソフタル酸、２，６−ナフタレンジカルボン酸、２，７−ナフタレンジカルボン酸、１，４−ナフタレンジカルボン酸、１，４−フェニレンジオキシジ酢酸、１，３−フェニレンジオキシジ酢酸、ジフェン酸、４，４’−オキシジ安息香酸、ジフェニルメタン−４，４’−ジカルボン酸、ジフェニルスルホン−４，４’−ジカルボン酸、４，４’−ビフェニルジカルボン酸等の芳香族ジカルボン酸から誘導される単位を挙げることができ、これらのうちの１種または２種以上を使用することができる。ジカルボン酸単位におけるこれらの他のジカルボン酸単位の含有率は、４０モル％以下であることが好ましく、２５モル％以下であることがより好ましく、１０モル％以下であることがさらに好ましい。また、トリメリット酸、トリメシン酸、ピロメリット酸などの多価カルボン酸から誘導される単位を、溶融成形が可能な範囲内で含有していてもよい。
【００１２】
本発明に用いられるポリアミドを構成するジアミン単位は、炭素数６〜１８の脂肪族アルキレンジアミン単位を５０〜１００モル％含有していることが必要であり、６０〜１００モル％含有していることが好ましく、７５〜１００モル％含有していることがより好ましく、９０〜１００モル％含有していることがさらに好ましい。炭素数６〜１８の脂肪族アルキレンジアミン単位を上記の割合で含有するポリアミドを使用すると、耐熱性、低吸水性、耐薬品性に優れた成形品が得られる。
【００１３】
炭素数６〜１８の脂肪族アルキレンジアミン単位としては、例えば、１，６−ヘキサンジアミン、１，７−ヘプタンジアミン、１，８−オクタンジアミン、１，９−ノナンジアミン、１，１０−デカンジアミン、１，１１−ウンデカンジアミン、１，１２−ドデカンジアミン等の直鎖状脂肪族アルキレンジアミン；１−ブチル−１，２−エタンジアミン、１，１−ジメチル−１，４−ブタンジアミン、１−エチル−１，４−ブタンジアミン、１，２−ジメチル−１，４−ブタンジアミン、１，３−ジメチル−１，４−ブタンジアミン、１，４−ジメチル−１，４−ブタンジアミン、２，３−ジメチル−１，４−ブタンジアミン、２−メチル−１，５−ペンタンジアミン、３−メチル−１，５−ペンタンジアミン、２，５−ジメチル−１，６−ヘキサンジアミン、２，４−ジメチル−１，６−ヘキサンジアミン、３，３−ジメチル−１，６−ヘキサンジアミン、２，２−ジメチル−１，６−ヘキサンジアミン、２，２，４−トリメチル−１，６−ヘキサンジアミン、２，４，４−トリメチル−１，６−ヘキサンジアミン、２，４−ジエチル−１，６−ヘキサンジアミン、２，２−ジメチル−１，７−ヘプタンジアミン、２，３−ジメチル−１，７−ヘプタンジアミン、２，４−ジメチル−１，７−ヘプタンジアミン、２，５−ジメチル−１，７−ヘプタンジアミン、２−メチル−１，８−オクタンジアミン、３−メチル−１，８−オクタンジアミン、４−メチル−１，８−オクタンジアミン、１，３−ジメチル−１，８−オクタンジアミン、１，４−ジメチル−１，８−オクタンジアミン、２，４−ジメチル−１，８−オクタンジアミン、３，４−ジメチル−１，８−オクタンジアミン、４，５−ジメチル−１，８−オクタンジアミン、２，２−ジメチル−１，８−オクタンジアミン、３，３−ジメチル−１，８−オクタンジアミン、４，４−ジメチル−１，８−オクタンジアミン、５−メチル−１，９−ノナンジアミン等の分岐鎖状脂肪族アルキレンジアミンなどから誘導される単位を挙げることができ、これらのうち１種または２種以上を使用することができる。
【００１４】
上記の脂肪族アルキレンジアミン単位の中でも、１，６−ヘキサンジアミン、１，８−オクタンジアミン、２−メチル−１，８−オクタンジアミン、１，９−ノナンジアミン、１，１０−デカンジアミン、１，１１−ウンデカンジアミン、１，１２−ドデカンジアミンから誘導される単位が好ましく、１，９−ノナンジアミン単位および／または２−メチル−１，８−オクタンジアミン単位がより好ましい。１，９−ノナンンジアミン単位と２−メチル−１，８−オクタンジアミン単位を併用する場合には、１，９−ノナンンジアミン単位：２−メチル−１，８−オクタンジアミン単位のモル比は、９９：１〜１：９９であることが好ましく、９５：５〜４０：６０であることがより好ましく、９０：１０〜６０：４０であることがさらに好ましい。
【００１５】
上記のジアミン単位は、５０モル％以下であれば、炭素数６〜１８の脂肪族アルキレンジアミン単位以外の他のジアミン単位を含有していてもよい。該他のジアミン単位としては、例えば、エチレンジアミン、プロパンジアミン、１，４−ブタンジアミン等の脂肪族ジアミン；シクロヘキサンジアミン、メチルシクロヘキサンジアミン、イソホロンジアミン、ノルボルナンジメチルアミン、トリシクロデカンジメチルアミン等の脂環式ジアミン；ｐ−フェニレンジアミン、ｍ−フェニレンジアミン、ｐ−キシリレンジアミン、ｍ−キシリレンジアミン、４，４’−ジアミノジフェニルメタン、４，４’−ジアミノジフェニルスルホン、４，４’−ジアミノジフェニルエーテル等の芳香族ジアミンなどから誘導される単位を挙げることができ、これらのうち１種または２種以上を使用することができる。これらの他のジアミン単位の含有率は、４０モル％以下であることが好ましく、２５モル％以下であることがより好ましく、１０モル％以下であることがさらに好ましい。
【００１６】
また、本発明で使用するポリアミドにはアミノカルボン酸単位を含ませることもできる。該アミノカルボン酸単位としては、例えば、カプロラクタム、ラウリルラクタム等のラクタム；１−アミノラウリン酸、１−アミノドデシル酸等のアミノカルボン酸などから誘導される単位を挙げることができる。アミノカルボン酸単位の含有率は、ポリアミドの全ジカルボン酸単位に基づいて４０モル％以下であることが好ましく、２０モル％以下であることがより好ましい。
【００１７】
本発明で使用するポリアミドは、その分子鎖の末端基の１０％以上が末端封止剤により封止されていることが好ましい。分子鎖の末端基が末端封止剤により封止されている割合（末端封止率）は、４０％以上であることがより好ましく、６０％以上であることがさらに好ましく、７０％以上であることが特に好ましい。末端封止率が１０％以上のポリアミドを使用すると、耐熱老化性などの物性がより優れたポリアミド組成物が得られる。
【００１８】
ポリアミドの末端封止率は、ポリアミドに存在しているカルボキシル基末端、アミノ基末端および末端封止剤によって封止された末端基の数をそれぞれ測定し、下記の式（１）に従って求めることができる。各末端基の数は、^１Ｈ−ＮＭＲにより、各末端基に対応する特性シグナルの積分値より求めるのが精度、簡便さの点で好ましい。
【００１９】
末端封止率（％）＝［（Ａ−Ｂ）／Ａ］×１００（１）
［式中、Ａは分子鎖の末端基の総数（これは通常、ポリアミド分子の数の２倍に等しい）を表し、Ｂは封止されずに残ったカルボキシル基末端およびアミノ基末端の合計数を表す。］
【００２０】
末端封止剤としては、ポリアミド末端のアミノ基またはカルボキシル基との反応性を有する単官能性の化合物であれば特に制限はないが、反応性および封止末端の安定性などの点から、モノカルボン酸またはモノアミンが好ましく、取扱いの容易さなどの点から、モノカルボン酸がより好ましい。その他、酸無水物、モノイソシアネート、モノ酸ハロゲン化物、モノエステル類、モノアルコール類などを末端封止剤として使用することもできる。
【００２１】
末端封止剤として使用されるモノカルボン酸としては、アミノ基との反応性を有するものであれば特に制限はなく、例えば、酢酸、プロピオン酸、酪酸、吉草酸、カプロン酸、カプリル酸、ラウリン酸、トリデカン酸、ミリスチン酸、パルミチン酸、ステアリン酸、ピバリン酸、イソ酪酸等の脂肪族モノカルボン酸；シクロヘキサンカルボン酸等の脂環式モノカルボン酸；安息香酸、トルイル酸、α−ナフタレンカルボン酸、β−ナフタレンカルボン酸、メチルナフタレンカルボン酸、フェニル酢酸等の芳香族モノカルボン酸；これらの任意の混合物などを挙げることができる。これらの中でも、反応性、封止末端の安定性、価格などの点から、酢酸、プロピオン酸、酪酸、吉草酸、カプロン酸、カプリル酸、ラウリン酸、トリデカン酸、ミリスチン酸、パルミチン酸、ステアリン酸、安息香酸が好ましい。
【００２２】
末端封止剤として使用されるモノアミンとしては、カルボキシル基との反応性を有するものであれば特に制限はなく、例えば、メチルアミン、エチルアミン、プロピルアミン、ブチルアミン、ヘキシルアミン、オクチルアミン、デシルアミン、ステアリルアミン、ジメチルアミン、ジエチルアミン、ジプロピルアミン、ジブチルアミン等の脂肪族モノアミン；シクロヘキシルアミン、ジシクロヘキシルアミン等の脂環式モノアミン；アニリン、トルイジン、ジフェニルアミン、ナフチルアミン等の芳香族モノアミン；これらの任意の混合物などを挙げることができる。これらの中でも、反応性、沸点、封止末端の安定性、価格などの点から、ブチルアミン、ヘキシルアミン、オクチルアミン、デシルアミン、ステアリルアミン、シクロヘキシルアミン、アニリンが好ましい。
【００２３】
本発明で使用するポリアミドは、結晶性ポリアミドを製造する方法として知られている任意の方法を用いて製造することができる。例えば、酸クロライドとジアミンを原料とする界面重合法、ジカルボン酸とジアミンを原料とする溶融重合法、固相重合法、溶融押出重合法などの方法により製造することができる。
【００２４】
ポリアミドを製造するに際して、前記の末端封止剤の他に、例えば触媒としてリン酸、亜リン酸、次亜リン酸またはその塩またはそのエステル、具体的にはカリウム、ナトリウム、マグネシウム、バナジウム、カルシウム、亜鉛、コバルト、マンガン、錫、タングステン、ゲルマニウム、チタン、アンチモンなどの金属塩やアンモニウム塩、エチルエステル、イソプロピルエステル、ブチルエステル、ヘキシルエステル、イソデシルエステル、オクタデシルエステル、デシルエステル、フェニルエステルなどを添加することができる。
【００２５】
本発明で使用するポリアミドは、濃硫酸中３０℃で測定した極限粘度［η］が、０．４〜３．０ｄｌ／ｇの範囲内であることが必要である。極限粘度が０．４ｄｌ／ｇ未満のポリアミドを使用すると、得られるポリアミド組成物から得られる成形品の力学物性が低下し、３．０ｄｌ／ｇより大きいポリアミドを使用すると、ポリアミド組成物の成形性が低下する。本発明で使用するポリアミドは、濃硫酸中３０℃で測定した極限粘度［η］が、１．０〜２．０ｄｌ／ｇの範囲内であることが好ましい。
【００２６】
また、本発明のポリアミド組成物は、水酸化ナトリウム、水酸化カリウム、水酸化バリウムからなる群より選ばれる少なくとも１種の水酸化物を上記したポリアミド１ｋｇに対して０．０１〜０．２モルの割合で含有する。
上記した水酸化物の含有量が上記した範囲より少ないと、得られるポリアミド組成物は、結晶化速度、力学特性および耐熱老化性の向上効果に乏しい。また、水酸化物の含有量が上記し
た範囲を超えると、得られるポリアミド組成物は、滞留安定性、靭性が損なわれる。
水酸化物の含有量は上記したポリアミド１ｋｇに対して０．０２〜０．１モルの範囲内であることが好ましい。
【００２７】
本発明のポリアミド組成物の製造方法は特に制限されず、ポリアミドおよび水酸化ナトリウム、水酸化カリウム、水酸化バリウムからなる群より選ばれる少なくとも１種の水酸化物を均一に混合させ得る方法であればいずれでもよく、具体的にはポリアミド重合時の任意の段階で上記した水酸化物を添加する方法、または重合完了後のポリアミドに上記した水酸化物を添加する方法などが挙げられる。何れの場合も、上記した水酸化物を固体状で添加してもよいし、水溶液などの溶液として添加してもよい。
【００２８】
本発明のポリアミド組成物には、必要に応じてガラス繊維、炭素繊維、ホウ素繊維、アラミド繊維、液晶ポリエステル繊維などの繊維状充填剤；チタン酸カリウムウィスカ、ゾノトライトウィスカ、ワラストナイトウィスカ、ホウ酸アルミニウムウィスカ、酸化亜鉛ウィスカ、酸化チタンウィスカ、炭化ケイ素ウィスカ、窒化ケイ素ウィスカなどの針状充填材；ガラスフレーク、シリカ、シリカアルミナ、アルミナ、タルク、マイカ、カオリン、クレー、モンモリロナイト、グラファイト、炭酸カルシウム、二酸化チタン、二硫化モリブデン、ポリテトラフルオロエチレンなどの粉末状充填材；各種潤滑油などの添加剤を配合してもよい。これらの充填材や添加剤をポリアミド組成物に対して２〜２００重量部の割合で配合すると、力学特性および成形性のバランスがより優れたポリアミド組成物が得られる。
【００２９】
さらに、本発明のポリアミド組成物には、必要に応じて、さらに従来から公知の銅系安定剤、ヒンダードフェノール系酸化防止剤、ヒンダードアミン系酸化防止剤、リン系酸化防止剤、チオ系酸化防止剤、着色剤、紫外線吸収剤、光安定剤、帯電防止剤、滑剤、結晶核剤あるいはＰＡ６１２、ＰＡ１２等の脂肪族ポリアミド、ポリエチレン、ポリプロピレン、ＥＰＤＭ等のポリオレフィン、ＰＰＳ（ポリフェニレンサルファイド）、ＰＰＥ（ポリフェニレンエーテル）、ＬＣＰ（液晶ポリマー）等の他種ポリマーなども含有させることができる。また、本発明のポリアミド組成物には、必要に応じて、従来から公知の難燃剤や難燃助剤を配合してもよい。
【００３０】
本発明のポリアミド組成物を、目的とする成形品の種類、用途、形状などに応じて、射出成形、押出成形、プレス成形、ブロー成形、カレンダー成形、流延成形などの一般に熱可塑性樹脂組成物に用いられる成形方法によって成形することにより、成形品を製造することができる。また上記したものを組み合わせた成形方法を採用することもできる。さらに、本発明のポリアミド組成物と他のポリマーとを複合成形することもできる。
【００３１】
本発明のポリアミド組成物はその優れた特性を活かして、コネクタ、スイッチ、リレー、プリント配線板等の電子部品；ランプリフレクタ等の反射鏡、ギヤおよびカム等のような摺動部品；エアインテークマニホールドなどの自動車部品；流し台などの水回り部品；種々の装飾部品；あるいは、フィルム、シート、繊維など種々の用途に用いることができる。
【００３２】
【実施例】
以下、本発明を実施例により具体的に説明するが、本発明はこれらの実施例により何ら限定されるものではない。
なお、以下の実施例および比較例においては、極限粘度、半結晶化時間（結晶化速度）、曲げ弾性率、耐衝撃強度、耐熱老化性および滞留安定性は以下の方法により測定した。
【００３３】
極限粘度［η］：
濃硫酸中、３０℃にて、０．０５、０．１、０．２、０．４ｇ／ｄｌの各濃度の試料溶液のインヘレント粘度（η_ｉｎｈ）を以下のようにして測定し、これを濃度０に外挿した値を極限粘度［η］とした。
η_ｉｎｈ＝［ｌｎ（ｔ_１／ｔ_０）］／ｃ
〔式中、ｔ_０は溶媒の流下時間（秒）を表し、ｔ_１は試料溶液の流下時間（秒）を表し、ｃは試料溶液の濃度（ｇ／ｄｌ）を表す。〕
【００３４】
半結晶化時間：
示差走査型熱量計〔メトラー社製、「ＤＳＣ３０」〕を使用し、３３０℃で２分間保持した後、８０℃／分の速度で２８０℃まで降温し、次いで２８０℃で保持したときの半結晶化時間を測定した。なお、測定は、窒素流通下（速度：１００ｃｃ／分）で行った。
【００３５】
曲げ弾性率：
縦１２７ｍｍ×横１４ｍｍ×厚さ３ｍｍの試験片を射出成形にて作製し、ＡＳＴＭＤ７９０に従って、曲げ弾性率を測定した。
【００３６】
耐衝撃強度：
縦６４ｍｍ×横１２．７ｍｍ×厚さ３．２ｍｍの試験片を射出成形にて作製し、ＪＩＳＫ７１１０に準じて、アイゾット衝撃試験機（株式会社東洋精機製作所製）を使用して、ノッチ付きアイゾット衝撃値を測定した。
【００３７】
耐熱老化性：
ＪＩＳ１号ダンベル型試験片を射出成形にて作成し、１５０℃の熱風乾燥機中に１週間放置（熱処理）した。オートグラフ（株式会社島津製作所製）を使用して引張降伏強さを測定し、熱処理前の試験片の引張降伏強さに対する保持率を求めた。
【００３８】
滞留安定性：
キャピラリーレオメーター（株式会社安田精機製作所製、「ＭＯＤＥＬ８０５２」）を使用し、シリンダー温度３５０℃、キャピラリーダイの直径１ｍｍ、キャピラリーダイの長さ１０ｍｍ、剪断速度６０８ｓ^−１の条件で溶融粘度を測定した。３５０℃で３０分間滞留させたときの溶融粘度（ＭＶ_３０）の、３５０℃で５分滞留させたときの溶融粘度（ＭＶ_５）に対する比を測定した。
【００３９】
また、以下の実施例および比較例で使用したポリアミドは、以下のものである。
〔ポリアミドＡ〕
特許第３２４２７８１号公報の実施例２に記載された方法に準じて調製した、テレフタル酸単位と、１，９−ノナンジアミン単位および２−メチル−１，８−オクタンジアミン単位〔１，９−ノナンジアミン単位：２−メチル−１，８−オクタンジアミン単位＝８０：２０（モル比）〕とからなり、融点が３０１℃、極限粘度［η］が１．２１ｄｌ／ｇ、末端封止率が８０％（末端封止剤：安息香酸）であるポリアミド。
【００４０】
〔ポリアミドＢ〕
特許第３２４２７８１号公報の比較例３に記載された方法に準じて調製した、テレフタル酸単位およびイソフタル酸単位〔テレフタル酸単位：イソフタル酸単位＝７０：３０（モル比）〕とヘキサメチレンジアミン単位とからなり、融点が３１１℃、極限粘度［η］が１．０２ｄｌ／ｇであるポリアミド。末端封止率が４５％（末端封止剤：安息香酸）であるポリアミド。
【００４１】
実施例１〜５よび比較例１〜３
ポリアミドＡまたはポリアミドＢに下記の表１に示す化合物を下記の表１に示す割合で添加し、１２０℃で一晩真空乾燥した後、ベント付二軸押出機（スクリュー径：３０ｍｍ、Ｌ／Ｄ＝２８）に供給してシリンダー温度３３０℃、ベントの減圧度８ＫＰａ（６０ｔｏｒｒ）の条件下に溶融混練して押出し、冷却、切断してポリアミド組成物のペレットを製造した。得られたポリアミド組成物を用いて半結晶化時間、曲げ弾性率、耐衝撃強度、耐熱老化性、滞留安定性を測定した。結果を下記の表１に示す。
なお、水酸化バリウムは固体状のもの（キシダ化学株式会社製、特級試薬）を、水酸化ナトリウムは０．５規定の水溶液（キシダ化学株式会社製）を、水酸化カリウムは０．５規定の水溶液（キシダ化学株式会社製）を、水酸化マグネシウムは固体状のもの（キシダ化学株式会社製）を、それぞれ使用し、配合した。
【００４２】
【表１】

【００４３】
【発明の効果】
本発明によれば、射出成形のサイクル短縮、力学特性の向上、耐熱老化性の向上といった要求に応えることのできるポリアミド組成物が新たに提供される。[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention relates to a polyamide composition obtained by blending a specific metal hydroxide with a polyamide comprising a specific dicarboxylic acid unit and a diamine unit.
[0002]
[Prior art]
Conventionally, crystalline polyamides such as nylon 6 and nylon 66 have been widely used as general-purpose engineering plastics because of their excellent properties and ease of melt molding, but on the other hand, lack of heat resistance and dimensional stability due to water absorption. Problems such as poor quality have been pointed out. In particular, in the electrical and electronic fields that require reflow soldering heat resistance accompanying the development of surface mount technology (SMT) in recent years, or in engine room parts of automobiles where the demand for heat resistance is increasing year by year, use of conventional polyamides And the demand for a polyamide having more excellent heat resistance, dimensional stability, mechanical properties, and physicochemical properties is increasing.
[0003]
In response to such a demand in the world, various semi-aromatic polyamides such as PA6T-based polyamide containing terephthalic acid and 1,6-hexanediamine as main components have been proposed, and some of them have been put to practical use. PA9T-based polyamides having terephthalic acid and 1,9-nonanediamine and / or 2-methyl-1,8-octanediamine as diamine units, which have more excellent heat resistance, low water absorption and creep resistance, are also available. Proposed.
However, depending on the application, the injection molding cycle may be shortened, the mechanical properties may be further improved, and the heat aging resistance may be further improved.
[0004]
With respect to PA9T-based polyamides, JP-A-7-228768 (Patent Document 1) discloses a heat-aging polyamide composition comprising a copper compound, an alkali metal halide, and an organic stabilizer. JP-A-2000-198922 (Patent Document 2) describes a polyamide composition comprising a copper compound, an alkali metal halide, and a crystal nucleating agent and having excellent heat resistance, melt stability, and the like.
[0005]
[Patent Document 1]
JP-A-7-228768 [Patent Document 2]
JP 2000-198922 A
[Problems to be solved by the invention]
Accordingly, an object of the present invention is to provide a new polyamide composition capable of meeting the requirements for a semi-aromatic polyamide such as a shorter injection molding cycle, a further improvement in mechanical properties, and a further improvement in heat aging resistance.
[0007]
[Means for Solving the Problems]
The present inventors have conducted intensive studies to solve the above-mentioned problems, and as a result, at least one hydroxide selected from the group consisting of sodium hydroxide, potassium hydroxide, and barium hydroxide with respect to the semi-aromatic polyamide. It has been found that the crystallization rate, mechanical properties, and thermal stability can be improved without impairing the heat resistance, low water absorption, chemical resistance, etc. of the semi-aromatic polyamide by adding a specific amount of The invention has been completed.
[0008]
That is, the present invention comprises a dicarboxylic acid unit containing 50 to 100 mol% of a terephthalic acid unit and a diamine unit containing 50 to 100 mol% of an aliphatic alkylenediamine unit having 6 to 18 carbon atoms. For 1 kg of polyamide having an intrinsic viscosity [η] of 0.4 to 3.0 dl / g measured at 30 ° C., at least one kind of hydroxide selected from the group consisting of sodium hydroxide, potassium hydroxide, and barium hydroxide. The present invention provides a polyamide composition containing 0.01 to 0.2 mol of a product.
[0009]
Japanese Patent Application Laid-Open No. 55-78053 discloses that a compound of a metal of Group IIA of the periodic table such as barium hydroxide is contained, the γ-type crystal mixture ratio is 0.3 to 0.7, and the rigidity is improved. Nylon 6 is described. However, the publication does not describe improvement in properties other than rigidity, and does not mention other polyamides other than nylon 6.
Japanese Patent Application Laid-Open No. 2003-41117 discloses a polyamide composition comprising a PA9T-based polyamide and an aliphatic polyamide having 7 to 12 carbon atoms per amide group, which can be cooled at a low temperature. And that a metal hydroxide such as magnesium hydroxide, aluminum hydroxide, calcium hydroxide, barium hydroxide and the like can be blended. However, the purpose of this metal hydroxide is to capture an acid that has the effect of promoting the transamidation reaction between the PA9T-based polyamide and the aliphatic polyamide, and is used under a technical idea completely different from the present invention. Things.
[0010]
BEST MODE FOR CARRYING OUT THE INVENTION
It is necessary that the dicarboxylic acid unit constituting the polyamide used in the present invention contains 50 to 100 mol% of the terephthalic acid unit, preferably 60 to 100 mol%, and 75 to 100 mol%. %, More preferably 90 to 100 mol%. When the content of the terephthalic acid unit in the dicarboxylic acid unit is less than 50 mol%, heat resistance and mechanical properties of a molded article obtained from the polyamide composition are reduced.
[0011]
The above dicarboxylic acid unit may contain another dicarboxylic acid unit other than the terephthalic acid unit as long as it is 50 mol% or less. Examples of such other dicarboxylic acid units include, for example, malonic acid, dimethylmalonic acid, succinic acid, glutaric acid, adipic acid, 2-methyladipic acid, trimethyladipic acid, pimelic acid, 2,2-dimethylglutaric acid, 3,3 Aliphatic carboxylic acids such as 3-diethylsuccinic acid, azelaic acid, sebacic acid, suberic acid, dodecane diacid; alicyclic dicarboxylic acids such as 1,3-cyclopentanedicarboxylic acid and 1,4-cyclohexanedicarboxylic acid; isophthalic acid Acid, 2,6-naphthalenedicarboxylic acid, 2,7-naphthalenedicarboxylic acid, 1,4-naphthalenedicarboxylic acid, 1,4-phenylenedioxydiacetic acid, 1,3-phenylenedioxydiacetic acid, diphenic acid, 4 , 4'-oxydibenzoic acid, diphenylmethane-4,4'-dicarboxylic acid, diphenylsulfone-4,4 ' Dicarboxylic acid, there may be mentioned units derived from aromatic dicarboxylic acids such as 4,4'-biphenyl dicarboxylic acid, can be used one or two or more of them. The content of these other dicarboxylic acid units in the dicarboxylic acid unit is preferably at most 40 mol%, more preferably at most 25 mol%, even more preferably at most 10 mol%. Further, a unit derived from a polycarboxylic acid such as trimellitic acid, trimesic acid, and pyromellitic acid may be contained within a range in which melt molding is possible.
[0012]
It is necessary that the diamine unit constituting the polyamide used in the present invention contains 50 to 100 mol% of an aliphatic alkylenediamine unit having 6 to 18 carbon atoms, and contains 60 to 100 mol%. Is preferably contained in an amount of 75 to 100 mol%, and more preferably 90 to 100 mol%. When a polyamide containing an aliphatic alkylenediamine unit having 6 to 18 carbon atoms in the above ratio is used, a molded article excellent in heat resistance, low water absorption and chemical resistance can be obtained.
[0013]
Examples of the aliphatic alkylenediamine unit having 6 to 18 carbon atoms include 1,6-hexanediamine, 1,7-heptanediamine, 1,8-octanediamine, 1,9-nonanediamine, 1,10-decanediamine, Linear aliphatic alkylenediamines such as 1,11-undecanediamine and 1,12-dodecanediamine; 1-butyl-1,2-ethanediamine, 1,1-dimethyl-1,4-butanediamine, 1-ethyl -1,4-butanediamine, 1,2-dimethyl-1,4-butanediamine, 1,3-dimethyl-1,4-butanediamine, 1,4-dimethyl-1,4-butanediamine, 2,3 -Dimethyl-1,4-butanediamine, 2-methyl-1,5-pentanediamine, 3-methyl-1,5-pentanediamine, 2,5-dimethyl-1,6- Xanediamine, 2,4-dimethyl-1,6-hexanediamine, 3,3-dimethyl-1,6-hexanediamine, 2,2-dimethyl-1,6-hexanediamine, 2,2,4-trimethyl- 1,6-hexanediamine, 2,4,4-trimethyl-1,6-hexanediamine, 2,4-diethyl-1,6-hexanediamine, 2,2-dimethyl-1,7-heptanediamine, 2, 3-dimethyl-1,7-heptanediamine, 2,4-dimethyl-1,7-heptanediamine, 2,5-dimethyl-1,7-heptanediamine, 2-methyl-1,8-octanediamine, 3- Methyl-1,8-octanediamine, 4-methyl-1,8-octanediamine, 1,3-dimethyl-1,8-octanediamine, 1,4-dimethyl-1,8-octanedia 2,4-dimethyl-1,8-octanediamine, 3,4-dimethyl-1,8-octanediamine, 4,5-dimethyl-1,8-octanediamine, 2,2-dimethyl-1,8 -Branched aliphatic alkylenediamines such as octanediamine, 3,3-dimethyl-1,8-octanediamine, 4,4-dimethyl-1,8-octanediamine, and 5-methyl-1,9-nonanediamine; Derived units can be mentioned, and one or more of these can be used.
[0014]
Among the above aliphatic alkylenediamine units, 1,6-hexanediamine, 1,8-octanediamine, 2-methyl-1,8-octanediamine, 1,9-nonanediamine, 1,10-decanediamine, Units derived from 11-undecanediamine and 1,12-dodecanediamine are preferred, and 1,9-nonanediamine units and / or 2-methyl-1,8-octanediamine units are more preferred. When 1,9-nonanediamine unit and 2-methyl-1,8-octanediamine unit are used together, the molar ratio of 1,9-nonanediamine unit: 2-methyl-1,8-octanediamine unit is used. Is preferably from 99: 1 to 1:99, more preferably from 95: 5 to 40:60, even more preferably from 90:10 to 60:40.
[0015]
The above diamine unit may contain other diamine units other than the aliphatic alkylenediamine unit having 6 to 18 carbon atoms as long as it is 50 mol% or less. Examples of the other diamine unit include aliphatic diamines such as ethylenediamine, propanediamine, and 1,4-butanediamine; and alicyclic rings such as cyclohexanediamine, methylcyclohexanediamine, isophoronediamine, norbornanedimethylamine, and tricyclodecanedimethylamine. Formula diamine; p-phenylenediamine, m-phenylenediamine, p-xylylenediamine, m-xylylenediamine, 4,4'-diaminodiphenylmethane, 4,4'-diaminodiphenylsulfone, 4,4'-diaminodiphenylether and the like And a unit derived from an aromatic diamine, and one or more of these units can be used. The content of these other diamine units is preferably at most 40 mol%, more preferably at most 25 mol%, even more preferably at most 10 mol%.
[0016]
In addition, the polyamide used in the present invention may contain an aminocarboxylic acid unit. Examples of the aminocarboxylic acid unit include units derived from lactams such as caprolactam and lauryl lactam; and aminocarboxylic acids such as 1-aminolauric acid and 1-aminododecylic acid. The aminocarboxylic acid unit content is preferably at most 40 mol%, more preferably at most 20 mol%, based on the total dicarboxylic acid units of the polyamide.
[0017]
In the polyamide used in the present invention, it is preferable that 10% or more of the terminal groups of the molecular chain are blocked by a terminal blocking agent. The rate at which the terminal groups of the molecular chains are blocked by the terminal blocking agent (terminal blocking ratio) is more preferably 40% or more, further preferably 60% or more, and more preferably 70% or more. Is particularly preferred. When a polyamide having a terminal blocking rate of 10% or more is used, a polyamide composition having more excellent physical properties such as heat aging resistance can be obtained.
[0018]
The end capping rate of the polyamide can be determined according to the following formula (1) by measuring the number of carboxyl group ends, amino group ends and the number of end groups sealed by the end capping agent, respectively, present in the polyamide. it can. The number of each terminal group is preferably obtained from the integrated value of the characteristic signal corresponding to each terminal group by ¹ H-NMR in terms of accuracy and simplicity.
[0019]
Terminal blocking rate (%) = [(AB) / A] × 100 (1)
[Wherein A represents the total number of terminal groups in the molecular chain (this is usually equal to twice the number of polyamide molecules), and B represents the total number of carboxyl and amino groups remaining unsealed. Represents ]
[0020]
The terminal blocking agent is not particularly limited as long as it is a monofunctional compound having reactivity with an amino group or a carboxyl group at a polyamide terminal. Carboxylic acids or monoamines are preferred, and monocarboxylic acids are more preferred from the viewpoint of easy handling. In addition, acid anhydrides, monoisocyanates, monoacid halides, monoesters, monoalcohols, and the like can also be used as terminal blocking agents.
[0021]
The monocarboxylic acid used as the terminal blocking agent is not particularly limited as long as it has reactivity with an amino group, and for example, acetic acid, propionic acid, butyric acid, valeric acid, caproic acid, caprylic acid, lauric acid Aliphatic monocarboxylic acids such as acid, tridecanoic acid, myristic acid, palmitic acid, stearic acid, pivalic acid, and isobutyric acid; alicyclic monocarboxylic acids such as cyclohexanecarboxylic acid; benzoic acid, toluic acid, α-naphthalenecarboxylic acid And aromatic monocarboxylic acids such as β-naphthalenecarboxylic acid, methylnaphthalenecarboxylic acid, and phenylacetic acid; and arbitrary mixtures thereof. Among them, acetic acid, propionic acid, butyric acid, valeric acid, caproic acid, caprylic acid, lauric acid, tridecanoic acid, myristic acid, palmitic acid, stearic acid, from the viewpoints of reactivity, sealed terminal stability, and price. Benzoic acid is preferred.
[0022]
The monoamine used as the terminal blocking agent is not particularly limited as long as it has reactivity with a carboxyl group. For example, methylamine, ethylamine, propylamine, butylamine, hexylamine, octylamine, decylamine, stearyl Aliphatic monoamines such as amine, dimethylamine, diethylamine, dipropylamine and dibutylamine; alicyclic monoamines such as cyclohexylamine and dicyclohexylamine; aromatic monoamines such as aniline, toluidine, diphenylamine and naphthylamine; arbitrary mixtures of these; Can be mentioned. Among them, butylamine, hexylamine, octylamine, decylamine, stearylamine, cyclohexylamine, and aniline are preferred from the viewpoints of reactivity, boiling point, stability of a sealed end, and price.
[0023]
The polyamide used in the present invention can be produced by any method known as a method for producing a crystalline polyamide. For example, it can be produced by an interfacial polymerization method using acid chloride and diamine as raw materials, a melt polymerization method using dicarboxylic acid and diamine as raw materials, a solid phase polymerization method, a melt extrusion polymerization method, and the like.
[0024]
In the production of polyamide, in addition to the terminal blocking agent, for example, as a catalyst, phosphoric acid, phosphorous acid, hypophosphorous acid or a salt or ester thereof, specifically potassium, sodium, magnesium, vanadium, calcium Metal salts such as zinc, cobalt, manganese, tin, tungsten, germanium, titanium, antimony and ammonium salts, ethyl ester, isopropyl ester, butyl ester, hexyl ester, isodecyl ester, octadecyl ester, decyl ester, phenyl ester, etc. Can be added.
[0025]
The polyamide used in the present invention needs to have an intrinsic viscosity [η] measured in concentrated sulfuric acid at 30 ° C. within the range of 0.4 to 3.0 dl / g. When a polyamide having an intrinsic viscosity of less than 0.4 dl / g is used, the mechanical properties of a molded product obtained from the obtained polyamide composition are reduced. When a polyamide having a limiting viscosity of more than 3.0 dl / g is used, the moldability of the polyamide composition is reduced. Decreases. The polyamide used in the present invention preferably has an intrinsic viscosity [η] measured at 30 ° C. in concentrated sulfuric acid in the range of 1.0 to 2.0 dl / g.
[0026]
Further, the polyamide composition of the present invention contains 0.01 to 0.2 mol of at least one hydroxide selected from the group consisting of sodium hydroxide, potassium hydroxide, and barium hydroxide based on 1 kg of the polyamide. In the proportion of
When the content of the above-mentioned hydroxide is less than the above-mentioned range, the obtained polyamide composition is poor in the effect of improving the crystallization speed, mechanical properties and heat aging resistance. When the content of the hydroxide exceeds the above-mentioned range, the obtained polyamide composition has impaired retention stability and toughness.
The content of the hydroxide is preferably in the range of 0.02 to 0.1 mol per 1 kg of the polyamide.
[0027]
The method for producing the polyamide composition of the present invention is not particularly limited as long as the polyamide and at least one hydroxide selected from the group consisting of sodium hydroxide, potassium hydroxide and barium hydroxide can be uniformly mixed. Any method may be used, and specific examples include a method of adding the above-mentioned hydroxide at an arbitrary stage during the polymerization of polyamide, and a method of adding the above-mentioned hydroxide to the polyamide after the completion of polymerization. In any case, the above-mentioned hydroxide may be added in a solid state, or may be added as a solution such as an aqueous solution.
[0028]
The polyamide composition of the present invention may contain, if necessary, fibrous fillers such as glass fiber, carbon fiber, boron fiber, aramid fiber, and liquid crystal polyester fiber; potassium titanate whisker, zonotolite whisker, wollastonite whisker, boric acid. Acicular fillers such as aluminum whisker, zinc oxide whisker, titanium oxide whisker, silicon carbide whisker, silicon nitride whisker; glass flake, silica, silica alumina, alumina, talc, mica, kaolin, clay, montmorillonite, graphite, calcium carbonate, Powdered fillers such as titanium dioxide, molybdenum disulfide, and polytetrafluoroethylene; and additives such as various lubricating oils may be added. When these fillers and additives are blended at a ratio of 2 to 200 parts by weight with respect to the polyamide composition, a polyamide composition having a better balance between mechanical properties and moldability can be obtained.
[0029]
Furthermore, the polyamide composition of the present invention may further contain, if necessary, a conventionally known copper-based stabilizer, a hindered phenol-based antioxidant, a hindered amine-based antioxidant, a phosphorus-based antioxidant, and a thio-based antioxidant. Agents, coloring agents, ultraviolet absorbers, light stabilizers, antistatic agents, lubricants, crystal nucleating agents or aliphatic polyamides such as PA612 and PA12, polyolefins such as polyethylene, polypropylene, EPDM, PPS (polyphenylene sulfide), PPE (polyphenylene) Ether), LCP (liquid crystal polymer), and other polymers. Further, the polyamide composition of the present invention may contain a conventionally known flame retardant or flame retardant auxiliary, if necessary.
[0030]
The polyamide composition of the present invention is generally a thermoplastic resin composition such as injection molding, extrusion molding, press molding, blow molding, calender molding, cast molding, etc., depending on the type, use, shape, etc. of the intended molded article. A molded article can be manufactured by molding using the molding method used in the above. Also, a molding method combining the above-described ones can be adopted. Further, the polyamide composition of the present invention and another polymer can be formed into a composite.
[0031]
The polyamide composition of the present invention takes advantage of its excellent properties to make use of electronic components such as connectors, switches, relays, and printed wiring boards; sliding components such as reflectors such as lamp reflectors, gears and cams; and air intake manifolds. It can be used for various applications such as automobile parts; water-drainage parts such as sinks; various decorative parts; and films, sheets, and fibers.
[0032]
【Example】
Hereinafter, the present invention will be described specifically with reference to examples, but the present invention is not limited to these examples.
In the following Examples and Comparative Examples, intrinsic viscosity, half-crystallization time (crystallization rate), flexural modulus, impact strength, heat aging resistance and retention stability were measured by the following methods.
[0033]
Intrinsic viscosity [η] :
Inherent viscosity (η _inh ) of each of the sample solutions having concentrations of 0.05, 0.1, 0.2, and 0.4 g / dl was measured in concentrated sulfuric acid at 30 ° C. as follows. The value extrapolated to the concentration 0 was defined as the intrinsic viscosity [η].
η _inh = [ln (t ₁ / t ₀ )] / c
[In the formula, t ₀ represents the flow time (second) of the solvent, t ₁ represents the flow time (second) of the sample solution, and c represents the concentration (g / dl) of the sample solution. ]
[0034]
Semi-crystallization time :
Using a differential scanning calorimeter (“DSC30” manufactured by Mettler Co., Ltd.), the temperature was kept at 330 ° C. for 2 minutes, then the temperature was lowered to 280 ° C. at a rate of 80 ° C./min, and then the semi-crystal when held at 280 ° C. The activation time was measured. The measurement was performed under a nitrogen flow (speed: 100 cc / min).
[0035]
Flexural modulus :
A test piece having a length of 127 mm, a width of 14 mm and a thickness of 3 mm was prepared by injection molding, and the flexural modulus was measured according to ASTM D790.
[0036]
Impact strength :
A test piece having a length of 64 mm, a width of 12.7 mm, and a thickness of 3.2 mm was prepared by injection molding, and a notched Izod using an Izod impact tester (manufactured by Toyo Seiki Seisaku-sho, Ltd.) according to JIS K7110. The impact value was measured.
[0037]
Heat aging resistance :
A JIS No. 1 dumbbell-shaped test piece was prepared by injection molding, and left in a hot-air dryer at 150 ° C. for one week (heat treatment). The tensile yield strength was measured using an autograph (manufactured by Shimadzu Corporation), and the retention of the test piece before the heat treatment with respect to the tensile yield strength was determined.
[0038]
Retention stability :
Using a capillary rheometer (“MODEL8052” manufactured by Yasuda Seiki Seisaku-Sho, Ltd.), the melt viscosity was measured under the conditions of a cylinder temperature of 350 ° C., a capillary die diameter of 1 mm, a capillary die length of 10 mm, and a shearing speed of 608 s ⁻¹ . . The ratio of the melt viscosity (MV ₃₀ ) at 30 ° C. for 30 minutes to the melt viscosity (MV ₅ ) at 350 ° C. for 5 minutes was measured.
[0039]
The polyamide used in the following Examples and Comparative Examples is as follows.
[Polyamide A]
A terephthalic acid unit, a 1,9-nonanediamine unit and a 2-methyl-1,8-octanediamine unit [1,9-nonanediamine unit] prepared according to the method described in Example 2 of Japanese Patent No. 3242781. : 2-methyl-1,8-octanediamine unit = 80: 20 (molar ratio)], the melting point is 301 ° C., the intrinsic viscosity [η] is 1.21 dl / g, and the terminal blocking ratio is 80% ( Polyamide which is a terminal blocking agent: benzoic acid).
[0040]
[Polyamide B]
A terephthalic acid unit and an isophthalic acid unit (terephthalic acid unit: isophthalic acid unit = 70: 30 (molar ratio)) and a hexamethylenediamine unit prepared according to the method described in Comparative Example 3 of Japanese Patent No. 3242781. A polyamide having a melting point of 311 ° C. and an intrinsic viscosity [η] of 1.02 dl / g. A polyamide having a terminal blocking ratio of 45% (terminal blocking agent: benzoic acid).
[0041]
Examples 1 to 5 and Comparative Examples 1 to 3
Compounds shown in Table 1 below were added to polyamide A or polyamide B at the ratios shown in Table 1 below, and dried in vacuum at 120 ° C. overnight, followed by vented twin-screw extruder (screw diameter: 30 mm, L / D = 28), melt-kneaded under the conditions of a cylinder temperature of 330 ° C. and a degree of vent pressure reduction of 8 KPa (60 torr), extruded, cooled, and cut to produce polyamide composition pellets. Using the obtained polyamide composition, the half-crystallization time, flexural modulus, impact strength, heat aging resistance, and retention stability were measured. The results are shown in Table 1 below.
Barium hydroxide was a solid (Kisida Chemical Co., Ltd., special grade reagent), sodium hydroxide was a 0.5 N aqueous solution (Kishida Chemical Co., Ltd.), and potassium hydroxide was 0.5 N. An aqueous solution (manufactured by Kishida Chemical Co., Ltd.) and a solid magnesium hydroxide (manufactured by Kishida Chemical Co., Ltd.) were used and compounded.
[0042]
[Table 1]

[0043]
【The invention's effect】
ADVANTAGE OF THE INVENTION According to this invention, the polyamide composition which can respond to requirements, such as shortening of the cycle of injection molding, improvement of mechanical characteristics, and improvement of heat aging resistance, is newly provided.

Claims

A limit composed of a dicarboxylic acid unit containing 50 to 100 mol% of a terephthalic acid unit and a diamine unit containing 50 to 100 mol% of an aliphatic alkylenediamine unit having 6 to 18 carbon atoms, and measured at 30 ° C in concentrated sulfuric acid. For 1 kg of polyamide having a viscosity [η] of 0.4 to 3.0 dl / g, at least one kind of hydroxide selected from the group consisting of sodium hydroxide, potassium hydroxide, and barium hydroxide is used. .2 mol of a polyamide composition.

The polyamide composition according to claim 1, wherein the aliphatic alkylenediamine unit is a 1,9-nonanediamine unit and / or a 2-methyl-1,8-octanediamine unit.

A molded article comprising the polyamide composition according to claim 1.