JP2004211010A - Gel composition - Google Patents
Gel composition Download PDFInfo
- Publication number
- JP2004211010A JP2004211010A JP2003001649A JP2003001649A JP2004211010A JP 2004211010 A JP2004211010 A JP 2004211010A JP 2003001649 A JP2003001649 A JP 2003001649A JP 2003001649 A JP2003001649 A JP 2003001649A JP 2004211010 A JP2004211010 A JP 2004211010A
- Authority
- JP
- Japan
- Prior art keywords
- synthetic
- gel composition
- mpc
- clay mineral
- formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】
【発明の属する技術分野】
本発明は新規なゲル組成物、さらに詳しくは前記式(1)で示される、平均分子量2,000〜5,000,000の2−メタクリロイルオキシエチルホスホリルコリンの単独重合体及び2−メタクリロイルオキシエチルホスホリルコリンとブチルメタクリレートとの共重合体を1種又は2種以上、合成粘土鉱物と水を含むことにより、低濃度で著しく粘性が高くなるゲル組成物に関するものである。
【0002】
【従来の技術】
2−メタクリロイルオキシエチルホスホリルコリン(以下MPCと略す)等のリン脂質類似構造を持ち、かつ重合性官能性基を有する単量体は重合反応性に優れ、単独重合では生体親和性を有する親水性重合体を生成する。近年、MPC等の単独重合体や共重合体が、抗血栓性、抗タンパク付着性、生体親和性等の機能を示すことが明らかとなっており、各種医用医療材料、コンタクトレンズ、眼内レンズ、化粧品保湿剤等への用途が展開されつつある。またMPCは各種コモノマーとの共重合も容易なため、適度な疎水ユニットを導入したり、様々な機能をもたせることができることが知られている(特許文献1〜3)。
【0003】
【特許文献1】
特公昭60−21599号公報
【特許文献2】
特開平3−39309号公報
【特許文献3】
特開平10−45626号公報
【0004】
最近、皮膚刺激性、毒性のない安全な合成の重合体である、MPCの単独重合体又はMPCの単量体とブチルメタクリレート(以下BMAと略す)の単量体との共重合体が、極めて高い親水性を有し、この共重合体が皮膚になんら悪影響を及ぼすことなく角質層のバリアー能を低下させ、薬効成分の経皮吸収性を向上させる効果を有すること、及びこれらを含む皮膚外用基剤が、経皮吸収用外用製剤用の基剤として優れた特性を有することを見いだしている(特許文献3)。
【0005】しかし、MPCの単独重合体又はMPCの単量体とBMAの単量体との共重合体は水に溶解した際に低濃度領域において粘性が低いため、製剤において剤型の制限がある。高濃度になると液粘性は高くなるが流動性を有する。また、配合濃度が高くなると使用性が悪く、製品コストも高くなる。
【0006】
一方、合成粘土鉱物を水に分散させた場合、例えば(1)べとつきがなく、滑らかでさわやかな感触、(2)皮膚表面でのびがよく、フィルムを形成して接着する、(3)含水性を高める、(4)エマルションやサスペンジョンの安定化、(5)ローションやシャンプーのクレンジング性能の向上、(6)油分を含んだローションのべとつきの解消、(7)水や石ケンによる洗い落とし性の向上などの性質が付与されていることが知られている(非特許文献1)。すなわち、合成粘土鉱物を水に分散させることにより、液性が変化するとともに、その使用後の質感、仕上がり感を向上することができる。
【0007】
【非特許文献1】
粘土ハンドブック 第2版 日本粘土学会編 技報堂出版 1987年
【0008】
しかし、合成粘土鉱物のゲル組成物はチキソトロピー性があり、わずかな力でも加わると系の粘性が下がる。それゆえ、ゲル組成物の粘性強度を高くするには配合濃度を高くする必要があり、配合濃度を高くすると使用性が悪くなる。
【0009】
【発明が解決しようとする課題】
本発明は、このような従来のMPCの単独重合体又はMPCの単量体とBMAの単量体との共重合体がもつ欠点、さらに合成粘土鉱物がもつ欠点を克服し、MPCの単独重合体又はMPCの単量体とBMAの単量体との共重合体を1種又は2種以上、合成粘土鉱物と水を配合し、低濃度で著しく粘性が高くなるゲル組成物を提供することを目的となされたものである。
【0010】
【課題を解決するための手段】
本発明者らはこのような事情に鑑み、鋭意研究を重ねた結果、本発明を完成した。すなわち、本発明は前記式(1)で示される、平均分子量2,000〜5,000,000のMPCの単独重合体及びMPCとBMAとの共重合体を1種又は2種以上、合成粘土鉱物と水を配合し、好ましくは前記式(1)で示される、平均分子量2,000〜5,000,000のMPCの単独重合体及びMPCとBMAとの共重合体を1種又は2種以上と合成粘土鉱物を重量比で1/1〜100/1の範囲で組み合わせ、さらに好ましくは前記式(1)で示される、平均分子量2,000〜5,000,000のMPCの単独重合体及びMPCとBMAとの共重合体を1種又は2種以上を0.01〜10wt%と合成粘土鉱物を0.0001〜10wt%をそれぞれの範囲内で配合し、低濃度で著しく粘性が高くなるゲル組成物を提供するものである。
【0011】
前記式(1)で示される、平均分子量2,000〜5,000,000のMPCの単独重合体及びMPCとBMAとの共重合体と合成スチブンサイトとの重量比で100/1の組成比を超えるとゲル組成物を得ることができない。また、前記式(1)で示される、1/1未満では平均分子量2,000〜5,000,000のMPCの単独重合体及びMPCとBMAとの共重合体と合成粘土鉱物との凝集が起き、安定なゲル組成物を得ることが困難になる。増粘効果および分散安定性の面から、好ましい配合重量比は1/1〜100/1の範囲である。
【0012】
本発明における前記式(1)で示される、平均分子量2,000〜5,000,000のMPCの単独重合体及びMPCとBMAとの共重合体が0.01%未満の配合ではゲル組成物の増粘液を形成しない。また、10wt%を越えると重合体の粘性が高くなり、透明分散性が悪くなり且つ経時安定性が悪くなる場合がある。特に、ゲル組成物の使用時にはしっとり感とは逆にべとつき感を感じたりする。増粘効果、分散安定性及び使用時のべとつき感を防止する面から、好ましい配合量は0.01〜10wt%の範囲である。
【0013】
本発明における合成粘土鉱物が0.0001%未満の配合ではゲル組成物の増粘液を形成しない場合がある。また、10wt%を越えると粘性が高くなり過ぎ、透明分散性が悪くなり且つ経時安定性が悪くなる場合がある。特に、ゲル組成物の使用時にはさっぱり感とは逆にざらつき感を感じたりする。増粘効果、分散安定性及び使用時のざらつき感を防止する面から、好ましい配合量は0.0001〜10wt%の範囲である。
【0014】
本発明の下記式(3)で示される重合体(以下、重合体1と略す)の単位の含有割合は、1〜100モル%であり、特に5〜100モル%が好ましい。重合体1中の(a)単位と(b)単位との重合形態は特に限定されず、ランダム、ブロック、グラフト等の形態をとることができる。
【0015】
【化3】
【0016】
重合体1の数平均分子量は、製造する際の重合温度、重合開始剤使用量、重合度調整剤の使用等によって様々なものとなるが、2,000〜5,000,000、好ましくは5,000〜1,000,000の範囲内である。数平均分子量が2000より小さいと真皮中に重合体が浸透する可能性があり、また、数平均分子量が5,000,000以上であると重合体の粘性が高くなりすぎて、取り扱いが困難となる。
【0017】
本発明に用いられる合成粘土鉱物は、スメクタイトに属する合成スチブンサイト、合成ヘクトライト、合成モンモリロナイト、合成サポナイト及び合成パイロフィライトなどがあげられる。
【0018】
さらに、本発明によれば、前記合成粘土鉱物が、合成スチブンサイトである請求項4の記載のゲル組成物が提供される。
【0019】
さらに、本発明に用いられる好適な合成スチブンサイトはスチブンサイト型フィロケイ酸マグネシウムナトリウムから成り、その組成は前記(2)式
式中、xとyはx+y<3という条件下で、
xは2以上の数であり、
yは0ないし0.1の数であり、
zは0より大で1.0までの数である、
で表される化学組成を有する。
【0020】
本発明に用いられる合成スチブンサイトは、スメクタイトに属するケイ酸マグネシウム水和物という観点からは合成ヘクトライトや合成サポナイトと軌を一にしている。しかしながら、本発明に用いられる合成スチブンサイトでは層内のアルカリ金属部分がナトリウムであるのに対して、ヘクトライトでは層内のアルカリ金属部分がリチウムであること、及び層内のマグネシウムとリチウムとの合計原子数(x+y)が3であるのに対して、本発明に用いられる合成スチブンサイトでは層内のマグネシウムとナトリウムとの合計原子数(x+y)が3よりも小さいことにおいて相違することが認められる。また、合成サポナイトにおいても層内にアルミニウムがあること、及び層内のマグネシウムとアルミニウムとの合計原子数(x+y)が3であることからも本発明に用いられる合成スチブンサイトとは異なることが認められる。本発明に用いられる合成スチブンサイトは不純金属成分を含まない形で得られ、一般にハンター白色度が80%以上、90%以上の白色粉末である。
【0021】
本発明のゲル組成物は、他の成分を配合することができる。他の成分としては、特に限定されないが、一般的に医薬品、医薬部外品、化粧品等に配合される任意の成分を配合することができる。かかる成分としては多価アルコール、油分、ワックス、酸、アルカリ、界面活性剤、粉末、顔料、染料、防腐剤、酸化防止剤、紫外線吸収剤、キレート剤、水溶性高分子、アルコール、溶媒ならびに香料等を挙げることができる。
【0022】
特に、軟膏剤、クリーム剤の基剤として本発明のゲル組成物を調製する際には、例えば脂肪油、ラノリン、ワセリン、パラフィン、グリコール類、高級脂肪酸、アルカリ、界面活性剤、高級アルコール等を配合することができ、さらに必要に応じて、安定化剤、防腐剤、乳化剤、懸濁化剤等を添加することができる。
【0023】
またパップ剤の基剤として本発明のゲル組成物を調製する際には、例えばゼラチン、アルギン酸ナトリウム、デンプン、カゼイン等の天然ポリマー、メチルセルロース、エチルセルロース、ヒドロキシエチルセルロース等のセルロース系、デキストラン、カルボキシメチルデンプン等のデンプン系、ポリビニルアルコール、ポリアクリル酸ナトリウム、ポリビニルピロリドン、ポリビニルエーテル等の合成ポリマー等を配合することができ、さらに必要に応じて、例えばグリセリン、プロピレングリコール等の保湿剤、亜鉛華等の無機充填剤、粘度調整剤、pH調整剤等を配合することができる。
【0024】
【発明の効果】
本発明の乳化型化粧料は、重合体1、合成粘土鉱物と水を配合し、好ましくは1種もしくは2種以上の重合体1と合成粘土鉱物を重量比で100/1〜1/1の範囲で組み合わせて配合することを特徴とするものである。
【0025】
【実施例】
次に実施例により本発明をさらに詳しく説明する。本発明はこれに限定されるものではない。実施例中の物性の測定と評価は以下の方法で行った。例中、%とあるのはすべて重量%である。
【0026】
粘度測定はB型粘度計を用いて測定した。
【0027】
経時安定性は、5℃、室温、40℃の3ヶ所で1ヶ月間の保存した状態のものについて、目視で判断し、離水、沈殿物など生じた場合のものを×、外観上、変化がなかったものについて〇、◎とした。
【0028】
使用性は、パネラー10名が使用し、「良い」とつけたものを「+1」とし、普通とつけたものを「0」とし、「悪い」とつけたものを「−1」として、合計点で0点を超えるものを○、5点以上を◎、0点以下を×とした。
【0029】
実施例1
重合体1 :分子量80,000のMPC単独重合体
合成粘土鉱物:合成サポナイト
【0030】
このMPC単独重合体と合成サポナイトから得られたゲル組成物の組成、粘性、経時安定性を表1に示す。
【0031】
【表1】
【0032】
実施例2
重合体1 :分子量1,000,000のMPCとBMAで、MPC:BMAのモル分率が80:20の共重合体
合成粘土鉱物:合成ヘクトライト
【0033】
MPC−BMA共重合体と合成ヘクトライトから得られたゲル組成物の組成、粘性、経時安定性を表2に示す。
【0034】
【表2】
【0035】
実施例3
重合体1 :分子量80,000のMPC単独重合体と分子量600,000のMPC:BMAのモル分率が90:10の共重合体で、重量比が1:1の混合物合成粘土鉱物:合成スチブンサイト
合成スチブンサイトの組成分析を行い、式(3)におけるx、y、zの値は下記の値であった。
x=2.809
y=0.047
z=0.430
【0036】
MPC単独重合体、MPC−BMA共重合体と合成スチブンサイトから得られたゲル組成物の組成、粘性、経時安定性を表3に示す。
【0037】
【表3】
[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention relates to a novel gel composition, more specifically, a homopolymer of 2-methacryloyloxyethyl phosphorylcholine represented by the formula (1) and having an average molecular weight of 2,000 to 5,000,000, and 2-methacryloyloxyethyl phosphorylcholine The present invention relates to a gel composition that contains one or more copolymers of butyl methacrylate and butyl methacrylate, a synthetic clay mineral and water, and has a very low viscosity at a low concentration.
[0002]
[Prior art]
Monomers having a phospholipid-like structure such as 2-methacryloyloxyethylphosphorylcholine (hereinafter abbreviated as MPC) and having a polymerizable functional group have excellent polymerization reactivity, and have homophilic hydrophilicity in homopolymerization. Generate coalescence. In recent years, it has been revealed that homopolymers and copolymers such as MPC exhibit functions such as antithrombotic properties, antiprotein adhesion properties, and biocompatibility, and various medical materials, contact lenses, and intraocular lenses Applications for cosmetic moisturizers and the like are being developed. Also, it is known that MPC can easily incorporate an appropriate hydrophobic unit and have various functions because it can be easily copolymerized with various comonomers (Patent Documents 1 to 3).
[0003]
[Patent Document 1]
JP-B-60-21599 [Patent Document 2]
JP-A-3-39309 [Patent Document 3]
JP-A-10-45626
Recently, a homopolymer of MPC or a copolymer of a monomer of MPC and a monomer of butyl methacrylate (hereinafter abbreviated as BMA), which is a safe synthetic polymer having no skin irritation and no toxicity, has been extremely Having high hydrophilicity, this copolymer has the effect of lowering the barrier function of the stratum corneum without any adverse effect on the skin, and has the effect of improving the percutaneous absorption of the active ingredient, and external use for skin containing these It has been found that a base has excellent properties as a base for an external preparation for transdermal absorption (Patent Document 3).
However, since the homopolymer of MPC or the copolymer of the MPC monomer and the BMA monomer has low viscosity in a low concentration range when dissolved in water, the dosage form is limited in the preparation. is there. The higher the concentration, the higher the liquid viscosity but the fluidity. In addition, if the compounding concentration is high, the usability is poor and the product cost is high.
[0006]
On the other hand, when the synthetic clay mineral is dispersed in water, for example, (1) it has no stickiness and has a smooth and refreshing feel, (2) it spreads well on the skin surface, and forms a film and adheres. (4) Stabilization of emulsions and suspensions, (5) Improvement of cleansing performance of lotions and shampoos, (6) Eliminating stickiness of lotions containing oil, (7) Improvement of washability with water and soap It is known that such properties are provided (Non-Patent Document 1). That is, by dispersing the synthetic clay mineral in water, the liquid property changes and the texture and finish after use can be improved.
[0007]
[Non-patent document 1]
Clay Handbook 2nd edition, edited by The Clay Society of Japan, Gihodo Publishing, 1987 [0008]
However, the gel composition of the synthetic clay mineral has a thixotropic property, and the viscosity of the system decreases when a slight force is applied. Therefore, in order to increase the viscosity strength of the gel composition, it is necessary to increase the compounding concentration.
[0009]
[Problems to be solved by the invention]
The present invention overcomes the drawbacks of the conventional MPC homopolymer or the copolymer of the MPC monomer and the BMA monomer, as well as the drawbacks of the synthetic clay mineral, and provides an MPC homopolymer. To provide a gel composition in which one or two or more copolymers of a monomer of MPC and MPC and a monomer of BMA, a synthetic clay mineral and water are blended, and the viscosity is significantly increased at a low concentration. It was made for the purpose.
[0010]
[Means for Solving the Problems]
In view of such circumstances, the present inventors have conducted intensive studies and, as a result, completed the present invention. That is, the present invention relates to a method of preparing one or more of MPC homopolymers and copolymers of MPC and BMA represented by the formula (1) having an average molecular weight of 2,000 to 5,000,000, A mineral and water are blended, and one or two types of a homopolymer of MPC and a copolymer of MPC and BMA each having an average molecular weight of 2,000 to 5,000,000, preferably represented by the above formula (1), are used. The above and a synthetic clay mineral are combined in a weight ratio of 1/1 to 100/1, and more preferably, a homopolymer of MPC having an average molecular weight of 2,000 to 5,000,000 represented by the above formula (1). One or two or more copolymers of MPC and BMA are blended in an amount of 0.01 to 10 wt% and a synthetic clay mineral in an amount of 0.0001 to 10 wt%. A gel composition comprising: It is intended.
[0011]
A composition ratio of 100/1 by weight of a homopolymer of MPC having an average molecular weight of 2,000 to 5,000,000, a copolymer of MPC and BMA, and a synthetic stevensite represented by the above formula (1). If it exceeds, a gel composition cannot be obtained. When the ratio is less than 1/1, the homopolymer of MPC having a mean molecular weight of 2,000 to 5,000,000, the copolymer of MPC and BMA, and the aggregation of the synthetic clay mineral are less than 1/1. And it becomes difficult to obtain a stable gel composition. From the viewpoint of the thickening effect and the dispersion stability, the preferred compounding weight ratio is in the range of 1/1 to 100/1.
[0012]
The gel composition according to the present invention, in which the homopolymer of MPC having an average molecular weight of 2,000 to 5,000,000 and the copolymer of MPC and BMA represented by the formula (1) are less than 0.01%, Does not form a thickener. On the other hand, if it exceeds 10% by weight, the viscosity of the polymer may be increased, the transparency and the dispersibility may be deteriorated, and the stability over time may be deteriorated. In particular, when the gel composition is used, a sticky feeling is felt contrary to a moist feeling. From the viewpoints of thickening effect, dispersion stability, and prevention of stickiness at the time of use, the preferable amount is 0.01 to 10% by weight.
[0013]
If the amount of the synthetic clay mineral in the present invention is less than 0.0001%, a thickening liquid of the gel composition may not be formed. On the other hand, if it exceeds 10% by weight, the viscosity may be too high, the transparency and the dispersibility may deteriorate, and the stability over time may deteriorate. In particular, when the gel composition is used, a rough feeling is felt contrary to a refreshing feeling. From the viewpoints of thickening effect, dispersion stability, and prevention of roughness during use, the preferred amount is in the range of 0.0001 to 10 wt%.
[0014]
The content ratio of the unit of the polymer of the present invention represented by the following formula (3) (hereinafter abbreviated as polymer 1) is from 1 to 100 mol%, particularly preferably from 5 to 100 mol%. The polymerization form of the unit (a) and the unit (b) in the polymer 1 is not particularly limited, and may be a form such as random, block, or graft.
[0015]
Embedded image
[0016]
The number average molecular weight of the polymer 1 varies depending on the polymerization temperature during production, the amount of polymerization initiator used, the use of a polymerization degree regulator, and the like, but is 2,000 to 5,000,000, preferably 5 2,000 to 1,000,000. If the number average molecular weight is less than 2,000, the polymer may penetrate into the dermis, and if the number average molecular weight is more than 5,000,000, the viscosity of the polymer becomes too high, making it difficult to handle. Become.
[0017]
Examples of the synthetic clay mineral used in the present invention include synthetic stevensite belonging to smectite, synthetic hectorite, synthetic montmorillonite, synthetic saponite, and synthetic pyrophyllite.
[0018]
Further, according to the present invention, there is provided the gel composition according to claim 4, wherein the synthetic clay mineral is synthetic stevensite.
[0019]
Further, a preferred synthetic stevensite used in the present invention comprises stevensite-type magnesium sodium phyllosilicate, and its composition is represented by the formula (2), wherein x and y are x + y <3.
x is a number greater than or equal to 2;
y is a number from 0 to 0.1,
z is a number greater than 0 and up to 1.0;
Has a chemical composition represented by
[0020]
The synthetic stevensite used in the present invention is in line with synthetic hectorite and synthetic saponite from the viewpoint of magnesium silicate hydrate belonging to smectite. However, in the synthetic stevensite used in the present invention, the alkali metal portion in the layer is sodium, whereas in hectorite, the alkali metal portion in the layer is lithium, and the total of magnesium and lithium in the layer is hectorite. While the number of atoms (x + y) is 3, it is recognized that the synthetic stevensite used in the present invention differs in that the total number of atoms (x + y) of magnesium and sodium in the layer is smaller than 3. It is also recognized that the synthetic saponite is different from the synthetic stevensite used in the present invention because aluminum exists in the layer and the total number of atoms (x + y) of magnesium and aluminum in the layer is three. . The synthetic stevensite used in the present invention is a white powder having a Hunter whiteness of 80% or more and 90% or more, which is obtained in a form containing no impurity metal component.
[0021]
The gel composition of the present invention can contain other components. The other components are not particularly limited, but may be any components generally used in pharmaceuticals, quasi-drugs, cosmetics, and the like. Such components include polyhydric alcohols, oils, waxes, acids, alkalis, surfactants, powders, pigments, dyes, preservatives, antioxidants, ultraviolet absorbers, chelating agents, water-soluble polymers, alcohols, solvents and fragrances. And the like.
[0022]
In particular, when preparing the gel composition of the present invention as a base for ointments and creams, for example, fatty oils, lanolin, petrolatum, paraffin, glycols, higher fatty acids, alkalis, surfactants, higher alcohols, etc. They can be blended, and if necessary, stabilizers, preservatives, emulsifiers, suspending agents and the like can be added.
[0023]
In preparing the gel composition of the present invention as a base for a poultice, for example, gelatin, sodium alginate, starch, natural polymers such as casein, methylcellulose, ethylcellulose, cellulosics such as hydroxyethylcellulose, dextran, carboxymethylstarch Such starch-based, polyvinyl alcohol, sodium polyacrylate, polyvinylpyrrolidone, synthetic polymers such as polyvinyl ether and the like can be blended, and further, if necessary, for example, humectants such as glycerin, propylene glycol, zinc white etc. An inorganic filler, a viscosity adjuster, a pH adjuster and the like can be blended.
[0024]
【The invention's effect】
The emulsified cosmetic of the present invention comprises a polymer 1, a synthetic clay mineral and water, and preferably contains one or more polymers 1 and a synthetic clay mineral in a weight ratio of 100/1 to 1/1. It is characterized by being combined in a range.
[0025]
【Example】
Next, the present invention will be described in more detail by way of examples. The present invention is not limited to this. Measurement and evaluation of physical properties in the examples were performed by the following methods. In the examples, all percentages are by weight.
[0026]
The viscosity was measured using a B-type viscometer.
[0027]
Stability over time was determined by visual inspection of the condition stored for 1 month at 3 locations of 5 ° C, room temperature, and 40 ° C. Those that did not exist were marked with 〇 and ◎.
[0028]
Usability was used by 10 panelists, and those with "good" were assigned as "+1", those with normal as "0", and those with "bad" as "-1". A point exceeding 0 points was rated as ○, 5 points or more as ◎, and 0 points or less as ×.
[0029]
Example 1
Polymer 1: MPC homopolymer having a molecular weight of 80,000 Synthetic clay mineral: Synthetic saponite
Table 1 shows the composition, viscosity and stability over time of the gel composition obtained from the MPC homopolymer and the synthetic saponite.
[0031]
[Table 1]
[0032]
Example 2
Polymer 1: a copolymer of MPC and BMA having a molecular weight of 1,000,000 and a molar fraction of MPC: BMA of 80:20 Synthetic clay mineral: Synthetic hectorite
Table 2 shows the composition, viscosity, and stability over time of the gel composition obtained from the MPC-BMA copolymer and the synthetic hectorite.
[0034]
[Table 2]
[0035]
Example 3
Polymer 1: a copolymer of MPC homopolymer having a molecular weight of 80,000 and a copolymer of MPC: BMA having a molecular weight of 600,000 having a mole fraction of 90:10, and a weight ratio of 1: 1 synthetic clay mineral: synthetic stevensite The composition of the synthesized stevensite was analyzed, and the values of x, y, and z in the formula (3) were as follows.
x = 2.809
y = 0.047
z = 0.430
[0036]
Table 3 shows the composition, viscosity, and stability over time of the gel composition obtained from the MPC homopolymer, the MPC-BMA copolymer, and the synthetic stevensite.
[0037]
[Table 3]
Claims (6)
式中、xとyはx+y<3という条件下で、
xは2以上の数であり、
yは0ないし0.1の数であり、
zは0より大で1.0までの数である、
で表される化学組成を有する合成スチブンサイトを配合することを特徴とする第1項ないし請求項2に記載のゲル組成物。
x is a number greater than or equal to 2;
y is a number from 0 to 0.1,
z is a number greater than 0 and up to 1.0;
The gel composition according to any one of claims 1 to 2, further comprising a synthetic stevensite having a chemical composition represented by the following formula: