JP2004184549A - Electrostatic charge image developing yellow developer, image forming method, and image forming apparatus - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide an electrostatic charge image developing yellow developer having aging stability of electrostatic chargeability and capable of forming an image of high image quality nearly free of image degradation, excellent in transparency and light resistance, and having high definition and high resolution. <P>SOLUTION: The electrostatic charge image developing yellow developer is obtained by mixing a toner comprising at least a binder resin and a yellow colorant represented by formula (I) with a carrier prepared by disposing a coating layer comprising at least a resin and particles on a surface of a magnetic core material, wherein the carrier has surface irregularities originating in particles comprised in the coating layer, and the toner is obtained by dissolving or dispersing a toner composition containing a modified polyester resin capable of reacting with a compound having an active hydrogen group as a binder resin in an organic solvent, dispersing the resulting solution or dispersion in an aqueous medium, reacting the resin with the compound having an active hydrogen group, and removing the solvent from the resulting dispersion. <P>COPYRIGHT: (C)2004,JPO&NCIPI

Description

（２）前記トナー中のイエロー着色剤の分散粒径が個数平均径で０．５μｍ以下であることを特徴とする前記（１）に記載の静電荷像現像用イエロー現像剤、
（３）前記着色剤として、結着樹脂及びイエロー着色剤を予め水と共に混練させた組成物を用いることを特徴とする前記（１）又は（２）に記載の静電荷像現像用イエロー現像剤、
（４）前記トナー粒子の体積平均粒径が４〜８μｍであり、体積平均粒径と個数平均粒径との比である（体積平均粒径／個数平均粒径）が１．２５以下であることを特徴とする前記（１）〜（３）のいずれかに記載の静電荷像現像用イエロー現像剤、
（５）前記トナー粒子の平均円径度が０．９０〜０．９９であることを特徴とする前記（１）〜（４）のいずれかに記載の静電荷像現像用イエロー現像剤、
（６）前記キャリア表面凹凸の平均高低差が０．１〜２．０μｍであることを特徴とする前記（１）〜（５）のいずれかに記載の静電荷像現像用イエロー現像剤、
（７）前記キャリアコート層に含まれる粒子の粒子径（Ｄ）と、該コート層樹脂の膜厚（ｈ）との比が、１＜［Ｄ／ｈ］＜１０、であることを特徴とする前記（１）〜（６）のいずれかに記載の静電荷像現像用イエロー現像剤、
（８）前記キャリアコート層に含まれる粒子の総含有量がコート層組成成分の２０〜９５重量％であることを特徴とする前記（１）〜（７）のいずれかに記載の静電荷像現像用イエロー現像剤、
（９）前記（１）〜（８）のいずれかに記載の静電荷像現像用イエロー現像剤を用いることを特徴とするカラー画像形成方法、
（１０）前記（１）〜（８）のいずれかに記載の静電荷像現像用イエロー現像剤を装填したことを特徴とするカラー画像形成装置、
が提供される。
【００１４】
【発明の実施の形態】
以下に、本発明について更に具体的に詳しく説明する。
本発明において、前期構造式（Ｉ）で示される顔料は、イソインドリノン顔料に属し、Ｃ．Ｉ．Ｐｉｇｍｅｎｔ Ｙｅｌｌｏｗ １８５に相当する。上記したイエロー着色剤は、高温高湿環境下において吸湿性の影響を受けづらく、トナー特性の変動を生じることを少なくでき、連続通紙させた場合であっても、耐久性において初期と変わらぬ画像を維持させることができる。これ自体、既に公知ではあるが、難分散性の顔料であり、そのために当該技術分野では用いられてこなかった。
【００１５】
前記構造式（１）で示される化合物をイエロー着色剤として含有する、本発明の現像剤を構成するイエロートナーは、フルカラー画像形成用イエロートナーとして好ましい分光特性を有し、また、高い彩度を得る事ができる。
また、フルカラー画像においては色の再現性が重要であるが、該構造式（１）で示される化合物を含有するイエロートナーは良好な色相を有し、その使用により、広い範囲の色を再現する事が可能である。
さらにトナー構成を、前記本発明のイエロートナーの様にする事によって、該構造式（１）で示される化合物を良好に分散させることができる為、ＯＨＰシート等にも適した光透過性の高いカラー画像を得る事ができる。
【００１６】
またトナー作成に使用できる結着樹脂としての活性水素基を有する化合物と反応可能な変性ポリエステル系樹脂としては、イソシアネート基を有するポリエステルプレポリマー（Ａ）が挙げられ、また、該活性水素基を有する化合物としては、アミン類（Ｂ）が挙げられる。
イソシアネート基を有するポリエステルプレポリマー（Ａ）としては、ポリオール（１）とポリカルボン酸（２）の重縮合物でかつ活性水素基を有するポリエステルをさらにポリイソシアネート（３）と反応させた物などが挙げられる。上記ポリエステルの有する活性水素基としては、水酸基（アルコール性水酸基およびフェノール性水酸基）、アミノ基、カルボキシル基、メルカプト基などが挙げられ、これらのうち好ましいものはアルコール性水酸基である。
【００１７】
ポリオール（１）としては、ジオール（１−１）および３価以上のポリオール（１−２）が挙げられ、（１−１）単独、または（１−１）と少量の（１−２）の混合物が好ましい。
ジオール（１−１）としては、アルキレングリコール（エチレングリコール、１，２−プロピレングリコール、１，３−プロピレングリコール、１，４−ブタンジオール、１，６−ヘキサンジオールなど）；アルキレンエーテルグリコール（ジエチレングリコール、トリエチレングリコール、ジプロピレングリコール、ポリエチレングリコール、ポリプロピレングリコール、ポリテトラメチレンエーテルグリコールなど）；脂環式ジオール（１，４−シクロヘキサンジメタノール、水素添加ビスフェノールＡなど）；ビスフェノール類（ビスフェノールＡ、ビスフェノールＦ、ビスフェノールＳなど）；上記脂環式ジオールのアルキレンオキサイド（エチレンオキサイド、プロピレンオキサイド、ブチレンオキサイドなど）付加物；上記ビスフェノール類のアルキレンオキサイド（エチレンオキサイド、プロピレンオキサイド、ブチレンオキサイドなど）付加物などが挙げられる。これらのうち好ましいものは、炭素数２〜１２のアルキレングリコールおよびビスフェノール類のアルキレンオキサイド付加物であり、特に好ましいものはビスフェノール類のアルキレンオキサイド付加物、およびこれと炭素数２〜１２のアルキレングリコールとの併用である。
【００１８】
３価以上のポリオール（１−２）としては、３〜８価またはそれ以上の多価脂肪族アルコール（グリセリン、トリメチロールエタン、トリメチロールプロパン、ペンタエリスリトール、ソルビトールなど）；３価以上のフェノール類（トリスフェノールＰＡ、フェノールノボラック、クレゾールノボラックなど）；上記３価以上のポリフェノール類のアルキレンオキサイド付加物などが挙げられる。
【００１９】
ポリカルボン酸（２）としては、ジカルボン酸（２−１）および３価以上のポリカルボン酸（２−２）が挙げられ、（２−１）単独、および（２−１）と少量の（２−２）の混合物が好ましい。
ジカルボン酸（２−１）としては、アルキレンジカルボン酸（コハク酸、アジピン酸、セバシン酸など）；アルケニレンジカルボン酸（マレイン酸、フマール酸など）；芳香族ジカルボン酸（フタル酸、イソフタル酸、テレフタル酸、ナフタレンジカルボン酸など）などが挙げられる。これらのうち好ましいものは、炭素数４〜２０のアルケニレンジカルボン酸および炭素数８〜２０の芳香族ジカルボン酸である。
【００２０】
３価以上のポリカルボン酸（２−２）としては、炭素数９〜２０の芳香族ポリカルボン酸（トリメリット酸、ピロメリット酸など）などが挙げられる。なお、ポリカルボン酸（２）としては、上述のものの酸無水物または低級アルキルエステル（メチルエステル、エチルエステル、イソプロピルエステルなど）を用いてポリオール（１）と反応させてもよい。
【００２１】
ポリオール（１）とポリカルボン酸（２）の比率は、水酸基［ＯＨ］とカルボキシル基［ＣＯＯＨ］の当量比［ＯＨ］／［ＣＯＯＨ］として、通常２／１〜１／１、好ましくは１．５／１〜１／１、さらに好ましくは１．３／１〜１．０２／１である。
【００２２】
ポリイソシアネート（３）としては、脂肪族ポリイソシアネート（テトラメチレンジイソシアネート、ヘキサメチレンジイソシアネート、２，６−ジイソシアナトメチルカプロエートなど）；脂環式ポリイソシアネート（イソホロンジイソシアネート、シクロヘキシルメタンジイソシアネートなど）；芳香族ジイソシアネート（トリレンジイソシアネート、ジフェニルメタンジイソシアネートなど）；芳香脂肪族ジイソシアネート（α，α，α′，α′−テトラメチルキシリレンジイソシアネートなど）；イソシアヌレート類；前記ポリイソシアネートをフェノール誘導体、オキシム、カプロラクタムなどでブロックしたもの；およびこれら２種以上の併用が挙げられる。
【００２３】
ポリイソシアネート（３）の比率は、イソシアネート基［ＮＣＯ］と、水酸基を有するポリエステルの水酸基［ＯＨ］の当量比［ＮＣＯ］／［ＯＨ］として、通常５／１〜１／１、好ましくは４／１〜１．２／１、さらに好ましくは２．５／１〜１．５／１である。［ＮＣＯ］／［ＯＨ］が５を超えると低温定着性が悪化する。［ＮＣＯ］のモル比が１未満では、変性ポリエステル中のウレア含量が低くなり、耐ホットオフセット性が悪化する。
【００２４】
末端にイソシアネート基を有するプレポリマー（Ａ）中のポリイソシアネート（３）構成成分の含有量は、通常０．５〜４０重量％、好ましくは１〜３０重量％、さらに好ましくは２〜２０重量％である。０．５重量％未満では、耐ホットオフセット性が悪化するとともに、耐熱保存性と低温定着性の両立の面で不利になる。また、４０重量％を超えると低温定着性が悪化する。
【００２５】
イソシアネート基を有するプレポリマー（Ａ）中の１分子当たりに含有するイソシアネート基は、通常１個以上、好ましくは、平均１．５〜３個、さらに好ましくは、平均１．８〜２．５個である。１分子当たり１個未満では、ウレア変性ポリエステルの分子量が低くなり、耐ホットオフセット性が悪化する。
【００２６】
アミン類（Ｂ）としては、ジアミン（Ｂ１）、３価以上のポリアミン（Ｂ２）、アミノアルコール（Ｂ３）、アミノメルカプタン（Ｂ４）、アミノ酸（Ｂ５）、およびＢ１〜Ｂ５のアミノ基をブロックしたもの（Ｂ６）などが挙げられる。ジアミン（Ｂ１）としては、芳香族ジアミン（フェニレンジアミン、ジエチルトルエンジアミン、４，４′−ジアミノジフェニルメタンなど）；脂環式ジアミン（４，４′−ジアミノ−３，３′−ジメチルジシクロヘキシルメタン、ジアミンシクロヘキサン、イソホロンジアミンなど）；および脂肪族ジアミン（エチレンジアミン、テトラメチレンジアミン、ヘキサメチレンジアミンなど）などが挙げられる。
【００２７】
３価以上のポリアミン（Ｂ２）としては、ジエチレントリアミン、トリエチレンテトラミンなどが挙げられる。アミノアルコール（Ｂ３）としては、エタノールアミン、ヒドロキシエチルアニリンなどが挙げられる。アミノメルカプタン（Ｂ４）としては、アミノエチルメルカプタン、アミノプロピルメルカプタンなどが挙げられる。アミノ酸（Ｂ５）としては、アミノプロピオン酸、アミノカプロン酸などが挙げられる。Ｂ１〜Ｂ５のアミノ基をブロックしたもの（Ｂ６）としては、前記Ｂ１〜Ｂ５のアミン類とケトン類（アセトン、メチルエチルケトン、メチルイソブチルケトンなど）から得られるケチミン化合物、オキサゾリン化合物などが挙げられる。これらアミン類（Ｂ）のうち好ましいものは、Ｂ１およびＢ１と少量のＢ２の混合物である。
【００２８】
さらに、必要により伸長停止剤を用いてウレア変性ポリエステルの分子量を調整することができる。伸長停止剤としては、モノアミン（ジエチルアミン、ジブチルアミン、ブチルアミン、ラウリルアミンなど）、およびそれらをブロックしたもの（ケチミン化合物）などが挙げられる。
【００２９】
アミン類（Ｂ）の比率は、イソシアネート基を有するプレポリマー（Ａ）中のイソシアネート基［ＮＣＯ］と、アミン類（Ｂ）中のアミノ基［ＮＨｘ］の当量比［ＮＣＯ］／［ＮＨｘ］として、通常１／２〜２／１、好ましくは１．５／１〜１／１．５、さらに好ましくは１．２／１〜１／１．２である。［ＮＣＯ］／［ＮＨｘ］が２を超えたり１／２未満では、ウレア変性ポリエステル（ｉ）の分子量が低くなり、耐ホットオフセット性が悪化する。
【００３０】
本発明においては、ウレア結合で変性されたポリエステル（ｉ）中に、ウレア結合と共にウレタン結合を含有していてもよい。ウレア結合含有量とウレタン結合含有量のモル比は、通常１００／０〜１０／９０であり、好ましくは８０／２０〜２０／８０、さらに好ましくは、６０／４０〜３０／７０である。ウレア結合のモル比が１０％未満では、耐ホットオフセット性が悪化する。
【００３１】
これらの反応により、本発明のトナーに用いられる変性ポリエステル、好ましくはウレア変性ポリエステル（ｉ）が作成できる。これらウレア変性ポリエステル（ｉ）は、ワンショット法、プレポリマー法により製造される。ウレア変性ポリエステル（ｉ）の重量平均分子量は、通常１万以上、好ましくは２万〜１０００万、さらに好ましくは３万〜１００万である。１万未満では耐ホットオフセット性が悪化する。ウレア変性ポリエステルの数平均分子量は、後述の変性されていないポリエステル（ii）を用いる場合は特に限定されるものではなく、前記重量平均分子量とするのに得やすい数平均分子量でよい。（ｉ）単独の場合は、数平均分子量は、通常２００００以下、好ましくは１０００〜１００００、さらに好ましくは２０００〜８０００である。２００００を超えると低温定着性およびフルカラー装置に用いた場合の光沢性が悪化する。
【００３２】
また、本発明においては、前記ウレア結合で変性されたポリエステル（ｉ）単独使用だけでなく、この（ｉ）と共に、変性されていないポリエステル（ii）を結着樹脂成分として含有させることもできる。（ii）を併用することで、低温定着性およびフルカラー装置に用いた場合の光沢性が向上し、単独使用より好ましい。（ii）としては、前記（ｉ）のポリエステル成分と同様なポリオール（１）とポリカルボン酸（２）との重縮合物などが挙げられ、好ましいものも（ｉ）と同様である。また、（ii）は無変性のポリエステルだけでなく、ウレア結合以外の化学結合で変性されているものでもよく、例えばウレタン結合で変性されていてもよい。（ｉ）と（ii）は少なくとも一部が相溶していることが低温定着性、耐ホットオフセット性の面で好ましい。従って、（ｉ）のポリエステル成分と（ii）は類似の組成が好ましい。（ii）を含有させる場合の（ｉ）と（ii）の重量比は、通常５／９５〜８０／２０、好ましくは５／９５〜３０／７０、さらに好ましくは５／９５〜２５／７５、特に好ましくは７／９３〜２０／８０である。（ｉ）の重量比が５％未満では、耐ホットオフセット性が悪化するとともに、耐熱保存性と低温定着性の両立の面で不利になる。
【００３３】
（ii）のピーク分子量は、通常１０００〜３００００、好ましくは１５００〜１００００、さらに好ましくは２０００〜８０００である。１０００未満では耐熱保存性が悪化し、１００００を超えると低温定着性が悪化する。（ii）の水酸基価は５以上であることが好ましく、さらに好ましくは１０〜１２０、特に好ましくは２０〜８０である。５未満では耐熱保存性と低温定着性の両立の面で不利になる。（ii）の酸価は通常１〜３０、好ましくは５〜２０である。酸価を持たせることで負帯電性となりやすい傾向がある。
【００３４】
本発明において、結着樹脂のガラス転移点（Ｔｇ）は通常５０〜７０℃、好ましくは５５〜６５℃である。５０℃未満ではトナーの高温保管時のブロッキングが悪化し、７０℃を超えると低温定着性が不十分となる。ウレア変性ポリエステル樹脂の共存により、本発明の乾式トナーにおいては、公知のポリエステル系トナーと比較して、ガラス転移点が低くても耐熱保存性が良好な傾向を示す。
【００３５】
結着樹脂の貯蔵弾性率としては、測定周波数２０Ｈｚにおいて１００００ｄｙｎｅ／ｃｍ^２となる温度（ＴＧ’）が、通常１００℃以上、好ましくは１１０〜２００℃である。１００℃未満では耐ホットオフセット性が悪化する。結着樹脂の粘性としては、測定周波数２０Ｈｚにおいて１０００ポイズとなる温度（Ｔη）が、通常１８０℃以下、好ましくは９０〜１６０℃である。１８０℃を超えると低温定着性が悪化する。すなわち、低温定着性と耐ホットオフセット性の両立の観点から、ＴＧ’はＴηより高いことが好ましい。言い換えるとＴＧ’とＴηの差（ＴＧ’−Ｔη）は０℃以上が好ましい。さらに好ましくは１０℃以上であり、特に好ましくは２０℃以上である。差の上限は特に限定されない。また、耐熱保存性と低温定着性の両立の観点から、ＴηとＴｇの差は０〜１００℃が好ましい。さらに好ましくは１０〜９０℃であり、特に好ましくは２０〜８０℃である。
【００３６】
結着樹脂は以下の方法などで製造することができる。
ポリオール（１）とポリカルボン酸（２）を、テトラブトキシチタネート、ジブチルチンオキサイドなど公知のエステル化触媒の存在下、１５０〜２８０℃に加熱し、必要により減圧としながら生成する水を留去して、水酸基を有するポリエステルを得る。次いで４０〜１４０℃にて、これにポリイソシアネート（３）を反応させ、イソシアネート基を有するプレポリマー（Ａ）を得る。さらに（Ａ）にアミン類（Ｂ）を０〜１４０℃にて反応させ、ウレア結合で変性されたポリエステルを得る。（３）を反応させる際および（Ａ）と（Ｂ）を反応させる際には、必要により溶剤を用いることもできる。使用可能な溶剤としては、芳香族溶剤（トルエン、キシレンなど）；ケトン類（アセトン、メチルエチルケトン、メチルイソブチルケトンなど）；エステル類（酢酸エチルなど）；アミド類（ジメチルホルムアミド、ジメチルアセトアミドなど）およびエーテル類（テトラヒドロフランなど）などのイソシアネート（３）に対して不活性なものが挙げられる。ウレア結合で変性されていないポリエステル（ii）を併用する場合は、水酸基を有するポリエステルと同様な方法で（ii）を製造し、これを前記（ｉ）の反応完了後の溶液に溶解し、混合する。
【００３７】
また、本発明の現像剤に用いるトナーは概ね以下の方法で製造することができるが勿論これらに限定されることはない。
本発明に用いる水系媒体としては、水単独でもよいが、水と混和可能な溶剤を併用することもできる。混和可能な溶剤としては、アルコール（メタノール、イソプロパノール、エチレングリコールなど）、ジメチルホルムアミド、テトラヒドロフラン、セルソルブ類（メチルセルソルブなど）、低級ケトン類（アセトン、メチルエチルケトンなど）などが挙げられる。
【００３８】
トナー粒子は、水系媒体中でイソシアネート基を有するプレポリマー（Ａ）からなる分散体を、（Ｂ）と反応させて形成しても良いし、あらかじめ製造したウレア変性ポリエステル（ｉ）を用いても良い。水系媒体中でウレア変性ポリエステル（ｉ）やプレポリマー（Ａ）からなる分散体を安定して形成させる方法としては、水系媒体中にウレア変性ポリエステル（ｉ）やプレポリマー（Ａ）からなるトナー原料の組成物を加えて、せん断力により分散させる方法などが挙げられる。プレポリマー（Ａ）と他のトナー組成物（以下トナー原料と呼ぶ）である着色剤、着色剤マスターバッチ、離型剤、帯電制御剤、未変性ポリエステル樹脂などは、水系媒体中で分散体を形成させる際に混合してもよいが、あらかじめトナー原料を混合した後、水系媒体中にその混合物を加えて分散させたほうがより好ましい。また、本発明においては、着色剤、離型剤、帯電制御剤などの他のトナー原料は、必ずしも、水系媒体中で粒子を形成させる時に混合しておく必要はなく、粒子を形成せしめた後、添加してもよい。たとえば、着色剤を含まない粒子を形成させた後、公知の染着の方法で着色剤を添加することもできる。
【００３９】
分散の方法としては特に限定されるものではないが、低速せん断式、高速せん断式、摩擦式、高圧ジェット式、超音波などの公知の設備が適用できる。分散体の粒径を２〜２０μｍにするために高速せん断式が好ましい。高速せん断式分散機を使用した場合、回転数は特に限定はないが、通常１０００〜３００００ｒｐｍ、好ましくは５０００〜２００００ｒｐｍである。分散時間は特に限定はないが、バッチ方式の場合は、通常０．１〜５分である。分散時の温度としては、通常０〜１５０℃（加圧下）、好ましくは４０〜９８℃である。高温な方が、ウレア変性ポリエステル（ｉ）やプレポリマー（Ａ）からなる分散体の粘度が低く、分散が容易な点で好ましい。
【００４０】
ウレア変性ポリエステル（ｉ）やプレポリマー（Ａ）を含むトナー組成物１００重量部に対する水系媒体の使用量は、通常５０〜２０００重量部、好ましくは１００〜１０００重量部である。５０重量部未満ではトナー組成物の分散状態が悪く、所定の粒径のトナー粒子が得られない。２０００重量部を超えると経済的でない。また、必要に応じて、分散剤を用いることもできる。分散剤を用いたほうが、粒度分布がシャープになるとともに分散が安定である点で好ましい。
【００４１】
プレポリマー（Ａ）からウレア変性ポリエステル（ｉ）を合成する工程は水系媒体中でトナー組成物を分散する前にアミン類（Ｂ）を加えて反応させても良いし、水系媒体中に分散した後にアミン類（Ｂ）を加えて粒子界面から反応を起こしても良い。この場合製造されるトナー表面に優先的にウレア変性ポリエステルが生成し、粒子内部で濃度勾配を設けることもできる。
【００４２】
トナー組成物が分散された油性相を水が含まれる液体に乳化、分散するための分散剤としてアルキルベンゼンスルホン酸塩、α−オレフィンスルホン酸塩、リン酸エステルなどの陰イオン界面活性剤、アルキルアミン塩、アミノアルコール脂肪酸誘導体、ポリアミン脂肪酸誘導体、イミダゾリンなどのアミン塩型や、アルキルトリメチルアンモニム塩、ジアルキルジメチルアンモニウム塩、アルキルジメチルベンジルアンモニウム塩、ピリジニウム塩、アルキルイソキノリニウム塩、塩化ベンゼトニウムなどの四級アンモニウム塩型の陽イオン界面活性剤、脂肪酸アミド誘導体、多価アルコール誘導体などの非イオン界面活性剤、例えばアラニン、ドデシルジ（アミノエチル）グリシン、ジ（オクチルアミノエチル）グリシンやＮ−アルキル−Ｎ，Ｎ−ジメチルアンモニウムべタインなどの両性界面活性剤が挙げられる。
【００４３】
またフルオロアルキル基を有する界面活性剤を用いることにより、非常に少量でその効果をあげることができる。好ましく用いられるフルオロアルキル基を有するアニオン性界面活性剤としては、炭素数２〜１０のフルオロアルキルカルボン酸及びその金属塩、パーフルオロオクタンスルホニルグルタミン酸ジナトリウム、３−［オメガ−フルオロアルキル（Ｃ６〜Ｃ１１）オキシ］−１−アルキル（Ｃ３〜Ｃ４）スルホン酸ナトリウム、３−［オメガ−フルオロアルカノイル（Ｃ６〜Ｃ８）−Ｎ−エチルアミノ］−１−プロパンスルホン酸ナトリウム、フルオロアルキル（Ｃ１１〜Ｃ２０）カルボン酸及び金属塩、パーフルオロアルキルカルボン酸（Ｃ７〜Ｃ１３）及びその金属塩、パーフルオロアルキル（Ｃ４〜Ｃ１２）スルホン酸及びその金属塩、パーフルオロオクタンスルホン酸ジエタノールアミド、Ｎ−プロピル−Ｎ−（２ヒドロキシエチル）パーフルオロオクタンスルホンアミド、パーフルオロアルキル（Ｃ６〜Ｃ１０）スルホンアミドプロピルトリメチルアンモニウム塩、パーフルオロアルキル（Ｃ６〜Ｃ１０）−Ｎ−エチルスルホニルグリシン塩、モノパーフルオロアルキル（Ｃ６〜Ｃ１６）エチルリン酸エステルなどが挙げられる。
【００４４】
商品名としては、サーフロンＳ−１１１、Ｓ−１１２、Ｓ−１１３（旭硝子社製）、フロラードＦＣ−９３、ＦＣ−９５、ＦＣ−９８、ＦＣ−ｌ２９（住友３Ｍ社製）、ユニダインＤＳ−１０１、ＤＳ−ｌ０２、（ダイキン工業社製）、メガファックＦ−ｌｌ０、Ｆ−ｌ２０、Ｆ−１１３、Ｆ−１９１、Ｆ−８１２、Ｆ−８３３（大日本インキ社製）、エクトップＥＦ−１０２、ｌ０３、１０４、１０５、１１２、１２３Ａ、１２３Ｂ、３０６Ａ、５０１、２０１、２０４、（トーケムプロダクツ社製）、フタージェントＦ−１００、Ｆ１５０（ネオス社製）などが挙げられる。
また、カチオン界面活性剤としては、フルオロアルキル基を有する脂肪族一級、二級もしくは二級アミン酸、パーフルオロアルキル（Ｃ６−Ｃ１０）スルホンアミドプロピルトリメチルアンモニウム塩などの脂肪族４級アンモニウム塩、ベンザルコニウム塩、塩化ベンゼトニウム、ピリジニウム塩、イミダゾリニウム塩、商品名としてはサーフロンＳ−ｌ２１（旭硝子社製）、フロラードＦＣ−１３５（住友３Ｍ社製）、ユニダインＤＳ−２０２（ダイキンエ業社製）、メガファックＦ−１５０、Ｆ−８２４（大日本インキ社製）、エクトップＥＦ−ｌ３２（トーケムプロダクツ社製）、フタージェントＦ−３００（ネオス社製）などが挙げられる。
【００４５】
また水に難溶の無機化合物分散剤としてリン酸三カルシウム、炭酸カルシウム、酸化チタン、コロイダルシリカ、ヒドロキシアパタイトなども用いる事が出来る。
【００４６】
また高分子系保護コロイドにより分散液滴を安定化させても良い。例えばアクリル酸、メタクリル酸、α−シアノアクリル酸、α−シアノメタクリル酸、イタコン酸、クロトン酸、フマール酸、マレイン酸または無水マレイン酸などの酸類、あるいは水酸基を含有する（メタ）アクリル系単量体、例えばアクリル酸β−ヒドロキシエチル、メタクリル酸β−ヒドロキシエチル、アクリル酸β−ヒドロキシプロビル、メタクリル酸β−ヒドロキシプロピル、アクリル酸γ−ヒドロキシプロピル、メタクリル酸γ−ヒドロキシプロピル、アクリル酸３−クロロ−２−ヒドロキシプロビル、メタクリル酸３−クロロ−２−ヒドロキシプロピル、ジエチレングリコールモノアクリル酸エステル、ジエチレングリコールモノメタクリル酸エステル、グリセリンモノアクリル酸エステル、グリセリンモノメタクリル酸エステル、Ｎ−メチロールアクリルアミド、Ｎ−メチロールメタクリルアミドなど、ビニルアルコールまたはビニルアルコールとのエーテル類、例えばビニルメチルエーテル、ビニルエチルエーテル、ビニルプロピルエーテルなど、またはビニルアルコールとカルボキシル基を含有する化合物のエステル類、例えば酢酸ビニル、プロピオン酸ビニル、酪酸ビニルなど、アクリルアミド、メタクリルアミド、ジアセトンアクリルアミドあるいはこれらのメチロール化合物、アクリル酸クロライド、メタクリル酸クロライドなどの酸クロライド類、ビニルビリジン、ビニルピロリドン、ビニルイミダゾール、エチレンイミンなどの窒素原子、またはその複素環を有するものなどのホモポリマーまたは共重合体、ポリオキシエチレン、ポリオキシプロピレン、ポリオキシエチレンアルキルアミン、ポリオキシプロピレンアルキルアミン、ポリオキシエチレンアルキルアミド、ポリオキシプロピレンアルキルアミド、ポリオキシエチレンノニルフェニルエーテル、ポリオキシエチレンラウリルフェニルエーテル、ポリオキシエチレンステアリルフェニルエステル、ポリオキシエチレンノニルフェニルエステルなどのポリオキシエチレン系、メチルセルロース、ヒドロキシエチルセルロース、ヒドロキシプロピルセルロースなどのセルロース類などが使用できる。
【００４７】
なお、分散安定剤としてリン酸カルシウム塩などの酸、アルカリに溶解可能な物を用いた場合は、塩酸等の酸により、リン酸カルシウム塩を溶解した後、水洗するなどの方法によって、微粒子からリン酸カルシウム塩を除去する。その他酵素による分解などの操作によっても除去できる。
【００４８】
分散剤を使用した場合には、該分散剤がトナー粒子表面に残存したままとすることもできるが、伸長および／または架橋反応後、洗浄除去するほうがトナーの帯電面から好ましい。
【００４９】
さらに、トナー組成物の粘度を低くするために、ウレア変性ポリエステル（ｉ）やプレポリマー（Ａ）が可溶の溶剤を使用することもできる。溶剤を用いたほうが粒度分布がシャープになる点で好ましい。該溶剤は沸点が１００℃未満の揮発性であることが除去が容易である点から好ましい。該溶剤としては、例えば、トルエン、キシレン、ベンゼン、四塩化炭素、塩化メチレン、１，２−ジクロロエタン、１，１，２−トリクロロエタン、トリクロロエチレン、クロロホルム、モノクロロベンゼン、ジクロロエチリデン、酢酸メチル、酢酸エチル、メチルエチルケトン、メチルイソブチルケトンなどを単独あるいは２種以上組合せて用いることができる。特に、トルエン、キシレン等の芳香族系溶媒および塩化メチレン、１，２−ジクロロエタン、クロロホルム、四塩化炭素等のハロゲン化炭化水素が好ましい。プレポリマー（Ａ）１００重量部に対する溶剤の使用量は、通常０〜３００重量部、好ましくは０〜１００重量部、さらに好ましくは２５〜７０重量部である。溶剤を使用した場合は、伸長および／または架橋反応後、常圧または減圧下にて加温し除去する。
【００５０】
伸長および／または架橋反応時間は、プレポリマー（Ａ）の有するイソシアネート基構造とアミン類（Ｂ）の組み合わせによる反応性により選択されるが、通常１０分〜４０時間、好ましくは２〜２４時間である。反応温度は、通常０〜１５０℃、好ましくは４０〜９８℃である。また、必要に応じて公知の触媒を使用することができる。具体的にはジブチルチンラウレート、ジオクチルチンラウレートなどが挙げられる。
【００５１】
得られた乳化分散体から有機溶媒を除去するためには、系全体を徐々に昇温し、液滴中の有機溶媒を完全に蒸発除去する方法を採用することができる。あるいはまた、乳化分散体を乾燥雰囲気中に噴霧して、液滴中の非水溶性有機溶媒を完全に除去してトナー微粒子を形成し、合せて水系分散剤を蒸発除去することも可能である。乳化分散体が噴霧される乾燥雰囲気としては、空気、窒素、炭酸ガス、燃焼ガス等を加熱した気体、特に使用される最高沸点溶媒の沸点以上の温度に加熱された各種気流が一般に用いられる。スプレイドライアー、ベルトドライアー、ロータリーキルンなどの短時間の処理で十分目的とする品質が得られる。
【００５２】
乳化分散時の粒度分布が広く、その粒度分布を保って洗浄、乾燥処理が行われた場合、所望の粒度分布に分級して粒度分布を整えることができる。
分級操作は液中でサイクロン、デカンター、遠心分離等により、微粒子部分を取り除くことができる。もちろん乾燥後に粉体として取得した後に分級操作を行っても良いが、液体中で行うことが効率の面で好ましい。得られた不要の微粒子、または粗粒子は再び混練工程に戻して粒子の形成に用いることができる。その際微粒子、または粗粒子はウェットの状態でも構わない。
用いた分散剤は得られた分散液からできるだけ取り除くことが好ましいが、先に述べた分級操作と同時に行うのが好ましい。
【００５３】
得られた乾燥後のトナーの粉体と離型剤微粒子、帯電制御性微粒子、流動化剤微粒子、着色剤微粒子などの異種粒子とともに混合したり、混合粉体に機械的衝撃力を与えることによって表面で固定化、融合化させ、得られる複合体粒子の表面からの異種粒子の脱離を防止することができる。
具体的手段としては、高速で回転する羽根によって混合物に衝撃力を加える方法、高速気流中に混合物を投入し、加速させ、粒子同士または複合化した粒子を適当な衝突板に衝突させる方法などがある。装置としては、オングミル（ホソカワミクロン社製）、Ｉ式ミル（日本ニューマチック社製）を改造して、粉砕エアー圧力を下げた装置、ハイブリダイゼイションシステム（奈良機械製作所社製）、クリプトロンシステム（川崎重工業社製）、自動乳鉢などがあげられる。
【００５４】
また、本発明で用いられるトナー中の前記構造式（１）で表される化合物の個数平均径は０．５μｍ以下であることが望ましく、好ましくは０．４μｍ以下、より好ましくは０．３μｍ以下が望ましい。
トナー中の該化合物の個数平均径が０．５μｍより大きいときには、顔料の分散性が充分なレベルには到らず、これでは特定の樹脂と、特定の粒径を有する着色剤を用いても目的とする透明性は得られない。
０．１μｍより小さい微小粒径の着色剤は、可視光の半波長より十分小さいため、光の反射、吸収特性に悪影響を及ぼさないと考えられる。よって、０．１μｍ未満の着色剤の粒子は良好な色再現性と、定着画像を有するＯＨＰシートの透明性に貢献する。一方、０．５μｍより大きな粒径の着色剤が多く存在していると、入射光の透過が阻害されたり、散乱されたりして、ＯＨＰシートの投影画像の明るさ及び彩かさが低下する傾向がある。
さらに、０．５μｍより大きな粒径の着色剤が多く存在していると、イエロートナー粒子表面からイエロー着色剤が脱離し、カブリ、ドラム汚染、クリーニング不良といった種々の問題を引き起こしやすいため、好ましくない。特に、０．７μｍより大きな粒径の着色剤は、全着色剤の１０個数％以下である事が好ましく、５個数％以下である事がより好ましい。
【００５５】
また、着色剤を結着樹脂の一部もしくは全部と共に、予め湿潤液を加えた上で混練しておく事により、初期的に結着樹脂と着色剤が十分に付着した状態となって、その後のトナー製造工程でのトナー粒子中における着色剤分散がより効果的に行なわれ、着色剤の分散粒径が小さくなり、一層良好な透明性を得る事ができる。
【００５６】
予めの混錬に用いる結着樹脂としては、変性、未変性ポリエステル樹脂の他にポリスチレン、ポリｐ−クロロスチレン、ポリビニルトルエンなどのスチレン及びその置換体の重合体；スチレン−ｐ−クロロスチレン共重合体、スチレン−プロピレン共重合体、スチレン−ビニルトルエン共重合体、スチレン−ビニルナフタリン共重合体、スチレン−アクリル酸メチル共重合体、スチレン−アクリル酸エチル共重合体、スチレン−アクリル酸ブチル共重合体、スチレン−アクリル酸オクチル共重合体、スチレン−メタクリル酸メチル共重合体、スチレン−メタクリル酸エチル共重合体、スチレン−メタクリル酸ブチル共重合体、スチレン−α−クロルメタクリル酸メチル共重合体、スチレン−アクリロニトリル共重合体、スチレン−ビニルメチルケトン共重合体、スチレン−ブタジエン共重合体、スチレン−イソプレン共重合体、スチレン−アクリロニトリル−インデン共重合体、スチレン−マレイン酸共重合体、スチレン−マレイン酸エステル共重合体などのスチレン系共重合体；ポリメチルメタクリレート、ポリブチルメタクリレート、ポリ塩化ビニル、ポリ酢酸ビニル、ポリエチレン、ポリプロピレン、ポリエステル、エポキシ樹脂、エポキシポリオール樹脂、ポリウレタン、ポリアミド、ポリビニルブチラール、ポリアクリル酸樹脂、ロジン、変性ロジン、テルペン樹脂、脂肪族叉は脂環族炭化水素樹脂、芳香族系石油樹脂、塩素化パラフィン、パラフィンワックスなどの一般適な熱可塑性を持つ樹脂が挙げられ、単独あるいは混合して使用できるが、これらに限定されるものではない。
【００５７】
前記の結着樹脂と着色剤の混合物を予め湿潤液と共に混練する具体的な方法としては、例えば、結着樹脂、着色剤及び湿潤液を、ヘンシェルミキサー等のブレンダーにて混合した後、得られた混合物を二本ロール、三本ロール等の混練機により、結着樹脂の溶融温度よりも低い温度で混練して、サンプルを得る。
【００５８】
また、湿潤液としては、結着樹脂の溶解性や、着色剤との塗れ性を考慮しながら、一般的なものを使用できるが、特に、アセトン、トルエン、ブタノン等の有機溶剤や水が、着色剤の分散性の面から好ましい。
中でも、水の使用は、環境への配慮及び、後のトナー製造工程におけるイエロー着色剤の分散安定性維持の点から、一層好ましい。
この製法によると、得られるカラートナーに含有される着色剤粒子の粒径が小さくなるばかりでなく、該粒子の分散状態の均一性が高くなるため、ＯＨＰによる投影像の色の再現性がより一層良くなる。
【００５９】
本発明において、現像剤を構成するトナーの体積平均粒径（Ｄｖ）としては４〜８μｍである事が好ましく、個数平均粒径（Ｄｎ）との比（Ｄｖ／Ｄｎ）は１．２５以下が好ましく、特に１．１０〜１．２５である事が好ましい。
該トナーの粒径を、この様にする事により、耐熱保存性、低温定着性、耐ホットオフセット性のいずれにも優れ、とりわけフルカラー複写機などに用いた場合に画像の光沢性に優れ、更に二成分現像剤においては、長期にわたるトナーの収支が行われても、現像剤中のトナー粒子径の変動が少なくなり、現像装置における長期の攪拌においても、良好で安定した現像性が得られる。
【００６０】
一般的には、トナーの粒子径は小さければ小さい程、高解像で高画質の画像を得る為に有利であると言われているが、逆に転写性やクリーニング性に対しては不利になりがちである。また、トナー体積平均径が本発明の前記範囲よりも小さい場合、二成分現像剤の現像装置における長期攪拌において、キャリアの表面にトナーが融着し、キャリアの帯電能力を低下させやすくなる。
逆に、トナーの体積平均径が本発明の前記範囲よりも大きい場合には、高解像で高画質の画像を得ることが難しくなると共に、現像剤中のトナーの収支が行われた場合にトナーの粒子径の変動が大きくなる場合が多い。また、体積平均粒子径／個数平均粒子径が１．２５よりも大きい場合も同様であることが明らかとなった。
【００６１】
また、該トナーは特定の形状とその分布を有する事が好ましく、中でも平均円形度が０．９０未満で、球形からあまりに離れた不定形のトナーの存在は、満足した転写性やチリのない高画質画像の獲得に対して悪影響を与えがちである。
なお形状の計測方法としては粒子を含む懸濁液を平板上の撮像部検知帯に通過させ、ＣＣＤカメラで光学的に粒子画像を検知し、解析する光学的検知帯の手法が適当である。この手法で得られる投影面積の等しい相当円の周囲長を実在粒子の周囲長で除した値である平均円形度が０．９０〜０．９９のトナーが適正な濃度の再現性のある高精細な画像を形成するのに有効である事が判明した。より好ましくは、平均円形度が０．９４〜０．９８５で、円形度が０．９４未満の粒子が１０個数％以下である。
【００６２】
また、転写残トナーを除去するためにブレードクリーニング等を採用しているシステムにおいては、平均円形度が０．９６以上の場合、感光体上および転写ベルトなどのクリーニング不良が発生し、画像上の汚れを引き起こす事があるため、この様なシステムの場合には、平均円形度は０．９６未満である事が好ましい。
例えば、画像面積率の低い現像・転写では転写残トナーが少なく、クリーニング不良が問題となることはないが、写真画像など画像面積率の高いもの、さらには、給紙不良等で未転写の画像形成したトナーが感光体上に転写残トナーとして発生することがあり、蓄積すると画像の地汚れを発生してしまう事がある。また、感光体を接触帯電させる帯電ローラ等を用いたシステムでは、これらを汚染してしまい、本来の帯電能力を発揮できなくなってしまう事がある。
【００６３】
この他、本発明の構成をとる限り、トナー中に結着樹脂や着色剤とともにワックスに代表される離型剤を含有させることもできる。
離型剤としては公知のものが使用でき、例えばポリオレフィンワッックス（ポリエチレンワックス、ポリプロピレンワックスなど）；長鎖炭化水素（パラフィンワッックス、サゾールワックスなど）；カルボニル基含有ワックスなどが挙げられる。
これらのうち好ましいものは、カルボニル基含有ワックスである。カルボニル基含有ワックスとしては、ポリアルカン酸エステル（カルナバワックス、モンタンワックス、トリメチロールプロパントリベヘネート、ペンタエリスリトールテトラベヘネート、ペンタエリスリトールジアセテートジベヘネート、グリセリントリベヘネート、１，１８−オクタデカンジオールジステアレートなど）；ポリアルカノールエステル（トリメリット酸トリステアリル、ジステアリルマレエートなど）；ポリアルカン酸アミド（エチレンジアミンジベヘニルアミドなど）；ポリアルキルアミド（トリメリット酸トリステアリルアミドなど）；およびジアルキルケトン（ジステアリルケトンなど）などが挙げられる。
これらカルボニル基含有ワックスのうち好ましいものは、ポリアルカン酸エステルである。
【００６４】
これら離型剤の融点は、通常４０〜１６０℃であり、好ましくは５０〜１２０℃、さらに好ましくは６０〜９０℃である。融点が４０℃未満のワックスは耐熱保存性に悪影響を与え、１６０℃を超えるワックスは低温での定着時にコールドオフセットを起こしやすい。また、ワックスの溶融粘度は、融点より２０℃高い温度での測定値として、５〜１０００ｃｐｓが好ましく、さらに好ましくは１０〜１００ｃｐｓである。１０００ｃｐｓを超えるワックスは、耐ホットオフセット性、低温定着性への向上効果に乏しい。
トナー中のワックスの含有量は通常０〜４０重量％であり、好ましくは３〜３０重量％である。
【００６５】
また、トナー帯電量及びその立ち上がりを早くするために、トナー中に、必要に応じて帯電制御剤を含有してもよい。ここで、帯電制御剤として有色材料を用いると色の変化が起こるため、無色、白色に近い材料が好ましい。
帯電制御剤としては公知のものが全て使用でき、例えば、トリフェニルメタン系染料、モリブデン酸キレート顔料、ローダミン系染料、アルコキシ系アミン、４級アンモニウム塩（フッ素変性４級アンモニウム塩を含む）、アルキルアミド、燐の単体または化合物、タングステンの単体または化合物、フッ素系活性剤、サリチル酸金属塩、及びサリチル酸誘導体の金属塩等である。具体的には第四級アンモニウム塩のボントロンＰ−５１、オキシナフトエ酸系金属錯体のＥ−８２、サリチル酸系金属錯体のＥ−８４、フェノール系縮合物のＥ−８９（以上、オリエント化学工業社製）、第四級アンモニウム塩モリブデン錯体のＴＰ−３０２、ＴＰ−４１５（以上、保土谷化学工業社製）、第四級アンモニウム塩のコピーチャージＰＳＹ ＶＰ２０３８、トリフェニルメタン誘導体のコピーブルーＰＲ、第四級アンモニウム塩のコピーチャージ ＮＥＧ ＶＰ２０３６、コピーチャージ ＮＸ ＶＰ４３４（以上、ヘキスト社製）、ＬＲＡ−９０１、ホウ素錯体であるＬＲ−１４７（日本カーリット社製）、キナクリドン、アゾ系顔料、その他スルホン酸基、カルボキシル基、四級アンモニウム塩等の官能基を有する高分子系の化合物が挙げられる。
【００６６】
本発明において帯電制御剤の使用量は、バインダー樹脂の種類、必要に応じて使用される添加剤の有無、分散方法を含めたトナー製造方法によって決定されるもので、一義的に限定されるものではないが、好ましくはバインダー樹脂１００重量部に対して、０．１〜１０重量部の範囲で用いられる。好ましくは、０．２〜５重量部の範囲がよい。１０重量部を越える場合にはトナーの帯電性が大きすぎ、主帯電制御剤の効果を減退させ、現像ローラとの静電的吸引力が増大し、現像剤の流動性低下や、画像濃度の低下を招く。これらの帯電制御剤はマスターバッチ、樹脂とともに溶融混練した後溶解分散させる事もできるし、有機溶剤に直接溶解、分散する際に加えても良いし、トナー表面にトナー粒子作成後固定化させてもよい。
【００６７】
また、トナー製造過程で水系媒体中にトナー組成物を分散させるに際して、主に分散安定化のための樹脂微粒子を添加してもよい。
使用される樹脂微粒子は、水性分散体を形成しうる樹脂であればいかなる樹脂も使用でき、熱可塑性樹脂でも熱硬化性樹脂でもよいが、例えばビニル系樹脂、ポリウレタン樹脂、エポキシ樹脂、ポリエステル樹脂、ポリアミド樹脂、ポリイミド樹脂、ケイ素系樹脂、フェノール樹脂、メラミン樹脂、ユリア樹脂、アニリン樹脂、アイオノマー樹脂、ポリカーボネート樹脂等が挙げられる。樹脂微粒子としては、上記の樹脂を２種以上併用しても差し支えない。このうち好ましいのは、微細球状樹脂粒子の水性分散体が得られやすい点から、ビニル系樹脂、ポリウレタン樹脂、エポキシ樹脂、ポリエステル樹脂及びそれらの併用が好ましい。
【００６８】
ビニル系樹脂としては、ビニル系モノマーを単独重合また共重合したポリマーで、例えば、スチレン−（メタ）アクリル酸エステル樹脂、スチレン−ブタジエン共重合体、（メタ）アクリル酸−アクリル酸エステル重合体、スチレン−アクリロニトリル共重合体、スチレン−無水マレイン酸共重合体、スチレン−（メタ）アクリル酸共重合体等が挙げられるがこれらに限定されるものではない。
【００６９】
更に、トナー粒子の流動性や現像性、帯電性を補助するための外添剤としては、無機微粒子を好ましく用いることができる。
この無機微粒子の一次粒子径は、５ｍμ〜２μｍであることが好ましく、特に５ｍμ〜５００ｍμであることが好ましい。また、ＢＥＴ法による比表面積は、２０〜５００ｍ^２／ｇであることが好ましい。この無機微粒子の使用割合は、トナーの０．０１〜５重量％であることが好ましく、特に０．０１〜２．０重量％であることが好ましい。
【００７０】
無機微粒子の具体例としては、例えばシリカ、アルミナ、酸化チタン、チタン酸バリウム、チタン酸マグネシウム、チタン酸カルシウム、チタン酸ストロンチウム、酸化亜鉛、酸化スズ、ケイ砂、クレー、雲母、ケイ灰石、ケイソウ土、酸化クロム、酸化セリウム、ベンガラ、三酸化アンチモン、酸化マグネシウム、酸化ジルコニウム、硫酸バリウム、炭酸バリウム、炭酸カルシウム、炭化ケイ素、窒化ケイ素などを挙げることができる。
【００７１】
この他高分子系微粒子たとえばソープフリー乳化重合や懸濁重合、分散重合によって得られるポリスチレン、メタクリル酸エステルやアクリル酸エステル共重合体やシリコーン、ベンゾグアナミン、ナイロンなどの重縮合系、熱硬化性樹脂による重合体粒子が挙げられる。
【００７２】
このような流動化剤は表面処理を行って、疎水性を上げ、高湿度下においても流動特性や帯電特性の悪化を防止することができる。例えばシランカップリング剤、シリル化剤、フッ化アルキル基を有するシランカップリング剤、有機チタネート系カップリング剤、アルミニウム系のカップリング剤、シリコーンオイル、変性シリコーンオイルなどが好ましい表面処理剤として挙げられる。
【００７３】
また、感光体や一次転写媒体に残存する転写後の現像剤を除去するためのクリーニング性向上剤を用いてもよく、該クリーニング性向上剤としては、例えばステアリン酸亜鉛、ステアリン酸カルシウム、ステアリン酸など脂肪酸金属塩、例えばポリメチルメタクリレート微粒子、ポリスチレン微粒子などのソープフリー乳化重合などによって製造された、ポリマー微粒子などを挙げることかできる。ポリマー微粒子は比較的粒度分布が狭く、体積平均粒径が０．０１〜１μｍのものが好ましい。
【００７４】
一方、本発明の現像剤に用いるキャリアは、磁性コア材表面に少なくとも樹脂及び粒子を含むコート層を設け、かつ、キャリア表面にコート層に含まれる粒子に由来する凹凸を有するキャリアである。該キャリアは、上述のトナーと共に用いた場合、画像品質及びその安定性に対する改善が顕著である事がわかった。
【００７５】
一般的に、画像品質はトナー帯電量や現像剤抵抗の変動によって左右され、キャリア表面の磨耗やトナー成分のキャリア表面への固着により、経時変動する事が一般的に知られている。
特に、本発明の現像剤に用いるトナーに含まれるイエロー着色剤は、キャリア表面への極少量のトナー固着によっても、キャリアの帯電性能を大きく劣化させ、トナー固着量が増加すると、トナーへの電荷付与が全く出来なくなる事がある。
そのため、キャリア表面は、トナー固着が増加しない様、リフレッシュする必要があるが、コート層を削って、表面リフレッシュを行いながらの使用は、おのずとキャリア耐久性、特に抵抗変動や流動性変動の面で限界がある。
そこで本発明の如く、キャリア構成として、その表面にコート層に含まれる粒子に由来する凹凸を形成することによって、キャリア表面に固着したトナー組成物のみを除去し、コート層を磨耗させる事無くキャリア表面をリフレッシュさせる事ができる。
【００７６】
また、凹凸形状を実質的にコート層のみによって制御できるため、磁性コア材に制限を加えずに選択して用いる事ができる。
また、該キャリア表面凹凸の平均高低差は、０．１〜２．０μｍである事が好ましく、０．２〜１．４μｍである事がより好ましい。
これより大きな高低差では、凹部にトナー組成成分が固着してしまい、キャリア帯電性能を劣化させたり、凸部を形成するキャリア表面粒子が脱離してしまう事がある。
また、逆に高低差が小さい場合には、十分なトナー固着物の掻き取り効果が得られず、キャリア表面全面にわたって、トナー組成成分の固着が発生する事がある。
【００７７】
更に、粒子径（Ｄ）と該コート層樹脂膜厚（ｈ）との比が、１＜［Ｄ／ｈ］＜１０、となるような粒子をキャリア被覆膜に含有することで、その効果は顕著である。これは、１＜［Ｄ／ｈ］＜１０であることで、被覆膜に比べ粒子の方が凸となるので、現像剤を摩擦帯電させるための攪拌により、トナーとの摩擦あるいはキャリア同士の摩擦で、結着樹脂への強い衝撃を伴う接触を緩和することができる。
これにより、キャリア表面へのトナー組成成分のスペントは、いっそう確実に防止され、結着樹脂の膜削れも抑制することが可能となる。［Ｄ／ｈ］が１以下の場合、粒子は結着樹脂中に埋もれてしまうため、効果が著しく低下し好ましくない。
［Ｄ／ｈ］が１０以上の場合、粒子と結着樹脂との接触面積が少ないため充分な拘束力が得られず、該粒子が容易に脱離してしまうため好ましくない。
【００７８】
また、該粒子は絶縁性無機粒子を、好ましく用いる事ができる。該絶縁性無機粒子としては、特に限定されるものではなく、酸化アルミニウム、酸化ケイ素、炭酸カルシウム、タルク、クレイ、石英ガラス、アルミノシリケートガラス、雲母片、酸化ジルコニウム、ムライト、サイアロン、ステアタイト、フォルステライト、コーディエライト、酸化ベリリウム、窒化ケイ素といった公知の絶縁物の粉末粒子を使用する事ができるが、これらに限定されるものではない。中でも、絶縁性無機粒子中に、少なくとも酸化アルミニウムや酸化ケイ素に代表される、アルミニウム元素および／またはケイ素元素成分を構成単位として含む事により、コート層からの粒子の脱離を更に抑止する事ができ、初期のキャリア表面状態の経時変動をより確実に抑止することができるため、より好ましい。
【００７９】
また、キャリア表面に粒子に由来する凹凸を確実に形成するためには、粒子の含有量が、コート膜組成成分の２０〜９５重量％である事が好ましい。粒子含有量がコート層組成成分の２０重量％未満である場合には、該キャリア表面に凹凸構造を形成できたとしても、その構造がなだらかになりがちであるため、キャリア表面状態の変動が大きくなり過ぎ、本発明の効果を十分に発揮できない場合がある。一方、粒子含有量が、コート層組成成分の９５重量％を越えるような場合には、凹凸構造が脆くなる事があり、初期の凹凸構造を長期間にわたって維持できず、同様に本発明の効果を維持できない場合がある。粒子含有量は、５５〜８０重量％である事が更に好ましい。
【００８０】
該キャリアのコート層を形成するための樹脂としても、本発明の規定を逸脱しない限り、特に制限なく使用する事ができ、ポリオレフィン（例えばポリエチレン、ポリプロピレン等）やその変性品、スチレン、アクリル樹脂、アクリロニトリル、ビニルアセテート、ビニルアルコール、塩化ビニル、ビニルカルバゾール、ビニルエーテル等を含む架橋性共重合物；オルガノシロキサン結合からなるシリコーン樹脂またはその変性品（例えばアルキッド樹脂、ポリエステル樹脂、エポキシ樹脂、ポリウレタン等による変性品）；ポリアミド；ポリエステル；ポリウレタン；ポリカーボネート；ユリア樹脂；メラミン樹脂；ベンゾグアナミン樹脂；エポキシ樹脂；ポリイミド樹脂や、これらの誘導体等が挙げられる。
【００８１】
中でも、上述の様な絶縁性無機粒子を確実にキャリアコート層中に固定化し、摩擦による無機粒子の脱離をより良く抑止するためには、コート層の樹脂が、少なくともアクリル部分を構成単位として含む事が好ましい。これにより、上記の無機粒子の、摩擦による脱離を、極めて効果的に抑制でき、長期にわたってキャリア表面の凹凸構造を維持し得るものである。更に、該アクリル樹脂はガラス転移温度（Ｔｇ）が２０〜１００℃である事が好ましく、２５〜８０℃である事がより好ましい。樹脂のＴｇをこの範囲とする事により、コート層樹脂は適度な弾性を持ち、現像剤の摩擦帯電時にキャリアが受ける衝撃を軽減させると考えられ、コート層の破損が抑止される。
【００８２】
また、コート層樹脂を、アクリル樹脂とアミノ樹脂の架橋物とする事により、適度な弾性を維持したまま、アクリル樹脂単独使用の場合発生しがちな、樹脂同士の融着、いわゆるブロッキングを、防止する事ができるため、より一層好ましい。
アミノ樹脂としては、従来知られているアミノ樹脂を用いる事ができるが、中でも、グアナミン樹脂、メラミン樹脂を用いる事で、キャリアの帯電付与能力をも向上させる事ができるため、より好ましく用いられる。また、適度にキャリアの帯電付与能力を制御する必要がある場合には、グアナミン樹脂および／またはメラミン樹脂と、他のアミノ樹脂を併用しても差し支えない。
【００８３】
また更に、上述のコート層樹脂が、シリコーン部分を構成単位として含む事により、キャリア表面の表面エネルギー自体を低くする事ができ、トナースペントの発生自体を抑制する事ができるため、単一のキャリア特性自体をより長期にわたって維持することができる。
該シリコーン部分の構成単位としては、メチルトリシロキサン単位、ジメチルジシロキサン単位、トリメチルシロキサン単位の少なくとも一種を含む事が好ましく、該シリコーン部分は、他のコート層樹脂と化学的に結合していても良く、ブレンド状態であっても良く、または、多層状になっていても良い。また、多層状である場合には、シリコーン部分は少なくとも最表層に位置させる事が好ましい。
【００８４】
ブレンドや多層状の構成とする場合には、シリコーン樹脂および／またはその変性体を使用する事が好ましく、例えば、従来から知られているいずれのシリコーン樹脂のうち、三次元網目構造を取り得る熱硬化型シリコーン樹脂を使用でき、下記一般式（２）で示されるオルガノシロキサン結合のみからなるストレートシリコーンおよびアルキド、ポリエステル、エポキシ、ウレタンなどで変性したシリコーン樹脂が挙げられる。
【化３】

（上記式中、Ｒ１は水素原子、炭素原子数１〜４のアルキル基またはフェニル基、Ｒ２およびＲ３は水素基、炭素原子数１〜４のアルコキシ基、フェニル基、フェノキシ基、炭素原子数２〜４のアリケニル基、炭素原子数２〜４のアルケニルオキシ基、ヒドロキシ基、カルボキシル基、エチレンオキシド基、グリシジル基または下記一般式（３）で示される基である。
【化４】

上記式中Ｒ４、Ｒ５はヒドロキシ基、カルボキシル基、炭素原子数１〜４のアルキル基、炭素原子数１〜４のアルコキシ基、炭素原子数２〜４のアルケニル基、炭素原子数２〜４のアルケニルオキシ基、フェニル基、フェノキシ基、ｋ、ｌ、ｍ、ｎ、ｏ、ｐは１以上の整数を示す。）
上記各置換基は未置換のもののほか、例えばヒドロキシ基、カルボキシル基、アルキル基、フェニル基、ハロゲン原子のような置換基を有してもよい。
【００８５】
また、該コート層には、上述の絶縁性無機粒子に代表される、表面凹凸を形作る粒子の個数平均径より小さな個数平均径を持つ導電性または半導性粒子を含む事が好ましく、この様な導電性または半導性粒子をコート層中に含有させる事により、表面凹凸形状を形成する機能とキャリアの抵抗を制御する機能とを、独立して制御する事が容易となる。
【００８６】
これら、導電性または半導性粒子としては、従来公知の物で良く、導電性粒子の例としては、鉄、金、銅等の金属；フェライト、マグネタイト等の酸化鉄；酸化ビスマス、酸化モリブデン等の酸化物；ヨウ化銀、βアルミナ等のイオン導電体；カーボンブラック等の顔料が挙げられ、半導性粒子の例としては、チタン酸バリウム、チタン酸ストロンチウム、チタン酸ランタン酸鉛等に代表される複酸化物や、酸化チタン、酸化亜鉛、酸化スズの酸素欠陥形成物（フレンケル型半導体）、不純物型欠陥形成物（ショトキー型半導体）が挙げられる。
この中でも特にカーボンブラックの一つであるファーネスブラックやアセチレンブラックを用いることにより、少量の低抵抗微粉末の添加で効果的に導電性の調整が可能であり、好ましく用いられる。
これらの低抵抗微粉末は、キャリア表面凹凸を形成するための粒子より小さくする必要があるが、およそ個数平均径で０．０１〜１μｍ程度のものが好ましく、コート層樹脂１００重量部に対して２〜３０重量部添加されることが好ましい。
【００８７】
また、現像剤重量中のトナー重量は、２〜１２重量％である事が好ましく、２．５〜１０重量％である事が更に好ましい。
【００８８】
本発明に用いるキャリアとしては、他の材料を限定するものではなく、従来公知のものが使用でき、例えば、キャリア粒子のコア材に使用できる無機／金属の磁性粒子の例としては、鉄、コバルト、ニッケル等の金属；マグネタイト、ヘマタイト、フェライトなどの合金や化合物等が挙げられるが、これらに限定されるものではない。これら磁性粒子は、単結晶／アモルファスの粒子、単独／複合の焼結体、単独／複合の粒子を樹脂等の高分子中に分散させた粒子等の、いずれのコア材形態で使用しても良い。また、磁性粒子を高分子中に分散させた粒子で、キャリア粒子の磁気特性と磁性粒子の分散性を両立させるには、これらの磁性粒子は０．５〜１０μｍ程度の大きさの粒子を含む事が好ましい。
【００８９】
磁性粉末を分散した樹脂粒子を用いる場合の、キャリア粒子のコア材粒子を形成する樹脂としては、例えばポリエチレン、ポリプロピレン、塩素化ポリエチレン、クロロスルホン化ポリエチレン等のポリオレフィン系樹脂；ポリスチレン、アクリル系樹脂（例えばポリメチルメタクリレート）、ポリアクリロニトリル、ポリビニルアセテート、ポリビニルアルコール、ポリビニルブチラール、ポリ塩化ビニル、ポリビニルカルバゾール、ポリビニルエーテル、ポリビニルケトン等のポリビニル及びポリビニリデン系樹脂；塩化ビニル−酢酸ビニル共重合体；ポリテトラフルオロエチレン、ポリ弗化ビニル、ポリ弗化ビニリデン、ポリクロロトリフルオロエチレン等の弗素樹脂；ポリアミド；ポリエステル；ポリウレタン；ポリカーボネート等が挙げられるが、これらに限定されるものではない。
【００９０】
磁性体分散タイプのコア材粒子には、これらの密着性を向上させたり、抵抗制御材の分散性を向上させる目的でシランカップリング剤、チタンカップリング剤等のカップリング剤を助剤として添加しても良い。
【００９１】
これらのコア材は、２０〜２００μｍ程度の粒径である事が、より好ましい。
【００９２】
コート層の形成法としては、従来公知の方法が使用でき、コア材粒子の表面にコート層形成液を噴霧法、浸漬法等の手段で塗布すればよい。また、コート層の厚さは０．０１〜２０μｍが好ましく、０．３〜１０μｍ程度であれば更に好ましい。
更に、この様にしてコート層を形成したキャリア粒子を加熱することによりコート層の重合反応を促進させることが好ましい。
これらのキャリア粒子の加熱保持は、コート層形成後これに引き続きコート装置内で行っても良く、また、コート層形成後、通常の電気炉や焼成キルン等、別の加熱手段によって行っても良い。
また、加熱保持温度は、使用するコート層材料により異なるため、一概に決められるものではないが、１２０〜３５０℃程度の温度が好ましく用いられる。この時、加熱保持温度は、コート層樹脂の分解温度以下の温度が好ましく用いられ、２００℃程度までの上限温度である事がより好ましい。
また加熱保持時間としては、５〜１２０分間程度である事が好ましい。
【００９３】
【実施例】
以下実施例により本発明を更に説明するが、本発明はこれに限定されるものではない。
また、部は重量部を示す。
【００９４】
実施例１
（結着樹脂合成例１）
冷却管、攪拌機および窒素導入管の付いた反応槽中に、ビスフェノールＡエチレンオキサイド２モル付加物７２４部、イソフタル酸２７６部およびジブチルチンオキサイド２部を入れ、常圧下２３０℃で８時間反応させ、さらに１０〜１５ｍｍＨｇの減圧で５時間反応させた後、１６０℃まで冷却して、これに３２部の無水フタル酸を加えて２時間反応させた。
次いで、８０℃まで冷却し、酢酸エチル中にてイソホロンジイソシアネート１８８部と２時間反応を行いイソシアネート含有プレポリマー（Ｐ１）を得た。
次いでプレポリマー（Ｐ１）２６７部とイソホロンジアミン１４部を５０℃で２時間反応させ、重量平均分子量６４０００のウレア変性ポリエステル（Ｕ１）を得た。
上記と同様にビスフェノールＡエチレンオキサイド２モル付加物７２４部、テレフタル酸２７６部を常圧下、２３０℃で８時間重縮合させ、次いで１０〜１５ｍｍＨｇの減圧で５時間反応させて、ピーク分子量５０００の変性されていないポリエステル（Ｅ１）を得た。
ウレア変性ポリエステル（Ｕ１）２００部と変性されていないポリエステル（Ｅ１）８００部を酢酸エチル／ＭＥＫ（１／１）混合溶剤２０００部に溶解、混合し、結着樹脂（Ｂ１）の酢酸エチル／ＭＥＫ溶液を得た。
一部減圧乾燥し、結着樹脂（Ｂ１）を単離した。Ｔｇは６２℃であった。
【００９５】

上記組成物を、温度計、攪拌器、コンデンサー及び窒素ガス導入管を備えた容量１Ｌの４つ口丸底フラスコ内に入れ、このフラスコをマントルヒーターにセットし、窒素ガス導入管より窒素ガスを導入してフラスコ内を不活性雰囲気下に保った状態で昇温し、次いで０．０５ｇのジブチルスズオキシドを加えて温度を２００℃に保って反応させポリエステルＡを得た。
このポリエステルＡのピーク分子量は４２００であり、ガラス転移点は５９．４℃であった。
【００９６】

上記原材料をヘンシェルミキサーにて混合し、顔料凝集体中に水が染み込んだ混合物を得た。これをロ−ル表面温度１３０℃に設定した２本ロールにより４５分間混練を行ない、パルベライザーで１ｍｍφの大きさに粉砕し、 マスターバッチ（Ｍ１）を得た。
【００９７】
（トナー製造例１）
ビーカー内に前記の結着樹脂（Ｂ１）の酢酸エチル／ＭＥＫ溶液２４０部、ペンタエリスリトールテトラベヘネート（融点８１℃、溶融粘度２５ｃｐｓ）２０部、マスターバッチ（Ｍ１）８部を入れ、６０℃にてＴＫ式ホモミキサーで１２０００ｒｐｍで攪拌し、均一に溶解、分散させ、トナー材料液を用意した。
ビーカー内にイオン交換水７０６部、ハイドロキシアパタイト１０％懸濁液（日本化学工業（株）製スーパタイト１０）２９４部、ドデシルベンゼンスルホン酸ナトリウム０．２部を入れ均一に溶解した。
ついで６０℃に昇温し、ＴＫ式ホモミキサーで１２０００ｒｐｍに攪拌しながら、上記トナー材料溶液を投入し１０分間攪拌した。
ついでこの混合液を攪拌棒および温度計付のコルベンに移し、９８℃まで昇温して溶剤を除去し、濾別、洗浄、乾燥した後、風力分級し、トナー粒子を得た。ついで、このトナー粒子１００部に疎水性シリカ０．５部と、疎水化酸化チタン０．５部をヘンシェルミキサーにて混合して、トナー（Ｔ１）を得た。
【００９８】
このトナー（Ｔ１）の超薄切片を作成し、透過型電子顕微鏡（日立社製Ｈ−９０００Ｈ）を用いて、トナーの断面写真（倍率×１００，０００）を撮影し、写真から、ランダム選択した１００点の着色剤部分の分散径から平均値を求めた。ここで、１粒子の分散径は最長径と最短径の平均とし、また、凝集状態にあるものは凝集体自身を１粒子とした。
着色剤の平均分散粒径は、０．３９μｍであった。また、０．７μｍ以上の分散粒径を持つ着色剤は、４．４個数％であった。
次にトナー（Ｔ１）の粒径を、コールターエレクトロニクス社製の粒度測定器「コールターカウンターＴＡ２」を用い、アパーチャー径１００μｍで測定したところ、体積平均粒径（Ｄｖ）＝６．３μｍ、個数平均粒径（Ｄｎ）＝５．０μｍで、Ｄｖ／Ｄｎは１．２６であった。
引き続き、トナー（Ｔ１）の円形度を、フロー式粒子像分析装置ＦＰＩＡ−１０００（東亜医用電子株式会社製）により平均円形度として計測した。測定は、前記装置に、予め不純固形物を除去した水１００〜１５０ｍｌ中に分散剤として界面活性剤（アルキルベンゼンスフォン酸塩）を０．１〜０．５ｍｌ加え、更に測定試料を０．１〜０．５ｇ程度加え、超音波分散器で約１〜３分間分散処理を行ない、分散液濃度を３０００〜１万個／μｌに調整した測定液をセットして行った。
得られたトナー（Ｔ１）の平均円形度は０．９５であった。
【００９９】

上記処方をホモミキサーで３０分間分散してコート層形成用の塗工液を調整した。
これを重量平均粒径５０μｍの球形フェライト粒子５０００部の表面へ流動床型スプレーコート装置によりコート後、１５０℃／１時間加熱してキャリア（Ｃ１）を得た。
キャリア（Ｃ１）の表面を、走査型電子顕微鏡で２０００倍に拡大し観察したところ、表面にアルミナ由来の凹凸が形成され、レーザー顕微鏡を用いて非接触で測定したキャリア表面凹凸の平均高低差は、０．４μｍであった。
また、キャリア断面を透過型電子顕微鏡にて観察し、キャリア表面を覆う被覆膜の膜厚の平均値をもって膜厚とした。キャリア（Ｃ１）の膜厚は、０．１６μｍであった。
【０１００】
次に、キャリア（Ｃ１）９３０部とトナー（Ｔ１）７０部を、ターブラ−ミキサーにて２分間混合し、二成分現像剤を得た。
【０１０１】
実施例２
（トナー製造例２）
着色剤をＣ．Ｉ．Ｐｉｇｍｅｎｔ Ｙｅｌｌｏｗ １８５の生顔料４部に変える以外は実施例１と同様にして、トナー粒子を得た。
ついで、トナー粒子１００部に疎水性シリカ０．５部と、疎水化酸化チタン０．５部をヘンシェルミキサーにて混合して、トナー（Ｔ２）を得た。
このトナー（Ｔ２）の体積平均粒径（Ｄｖ）は６．０μｍ、個数平均粒径（Ｄｎ）は５．０μｍで、Ｄｖ／Ｄｎは１．２０であった。
また、この着色剤平均分散粒径は０．６２μｍで、０．７μｍ以上の分散粒径を持つ着色剤は８．７個数％であった。
トナー（Ｔ２）を用いた以外は、実施例１と同様にし、二成分現像剤を得た。
【０１０２】
実施例３
（トナー製造例３）
実施例１で得られたＴＫ式ホモミキサー分散後のトナー組成物２１０部を酢酸エチル５７６部で希釈した。希釈した分散体２１０部を同様に処理して乳化後粒子化した。
その後は実施例１と同様にしてトナー粒子を得た。
ついで、トナー粒子１００部に疎水性シリカ０．５部と、疎水化酸化チタン０．５部をヘンシェルミキサーにて混合して、トナー（Ｔ３）を得た。
このトナー（Ｔ３）の体積平均粒径（Ｄｖ）は３．８μｍ、個数平均粒径（Ｄｎ）は３．２μｍで、Ｄｖ／Ｄｎは１．１９であった。
また、この着色剤平均分散粒径は０．３３μｍで、０．７μｍ以上の分散粒径を持つ着色剤は３．６個数％であった。
トナー（Ｔ３）を用いた以外は、実施例１と同様にして、二成分現像剤を得た。
【０１０３】
実施例４
（トナー製造例４）
実施例１における結着樹脂（Ｂ１）を酢酸エチル／ＭＥＫ（１／１）混合溶剤に溶解、混合する際に、混合溶剤量を１２００部とし、トナー製造時にこの溶液２４０部を用いた以外は、実施例１と同様にしてトナー粒子を得た。
ついで、トナー粒子１００部に疎水性シリカ０．５部と、疎水化酸化チタン０．５部をヘンシェルミキサーにて混合して、本発明のトナー（Ｔ４）を得た。
このトナー（Ｔ４）の体積平均粒径（Ｄｖ）は８．５μｍ、個数平均粒径（Ｄｎ）は７．１μｍで、Ｄｖ／Ｄｎは１．２０であった。
また、この着色剤平均分散粒径は０．５１μｍで、０．７μｍ以上の分散粒径を持つ着色剤は４．９個数％であった。
トナー（Ｔ４）を用いた以外は、実施例１と同様にして、二成分現像剤を得た。
【０１０４】
実施例５
（トナー製造例５）
溶解温度及び分散温度を５０℃に変える以外は実施例１と同様にしてトナー粒子を得た。
ついで、トナー粒子１００部に疎水性シリカ０．５部と、疎水化酸化チタン０．５部をヘンシェルミキサーにて混合して、本発明のトナー（Ｔ５）を得た。
このトナー（Ｔ５）の体積平均粒径（Ｄｖ）は５．６μｍ、個数平均粒径（Ｄｎ）は４．７μｍで、Ｄｖ／Ｄｎは１．１９であった。
また、この着色剤平均分散粒径は０．４１μｍで、０．７μｍ以上の分散粒径を持つ着色剤は３．５個数％であった。
トナー（Ｔ５）を用いた以外は、実施例１と同様にして、二成分現像剤を得た。
【０１０５】
実施例６〜１０

上記処方をホモミキサーで３０分間分散してコート層形成用の塗工液を調整した。
これを重量平均粒径５０μｍの球形フェライト粒子５０００部の表面へ流動床型スプレーコート装置によりコート後、１５０℃／１時間加熱してキャリア（Ｃ２）を得た。
キャリア（Ｃ２）表面凹凸の平均高低差は、０．２μｍであった。
また、キャリア（Ｃ２）の膜厚は、０．１２μｍであった。
ついで、キャリア（Ｃ２）と実施例１〜５のトナー（Ｔ１）〜トナー（Ｔ５）と各々組合せて、本発明（実施例６〜１０）のイエロー二成分現像剤を作成した。
【０１０６】
比較例１

上記原材料をヘンシェルミキサーにて混合し、顔料凝集体中に水が染み込んだ混合物を得た。これをロ−ル表面温度１３０℃に設定した２本ロールにより４５分間混練を行ない、パルベライザーで１ｍｍφの大きさに粉砕し、マスターバッチ（Ｍ２）を得た。
【０１０７】
（トナー製造例６）
着色剤をマスターバッチ（Ｍ２）８部に変える以外は実施例１と同様にしトナー粒子を得た。
ついで、トナー粒子１００部に疎水性シリカ０．５部と、疎水化酸化チタン０．５部をヘンシェルミキサーにて混合して、比較トナー（Ｔ６）を得た。
このトナー（Ｔ６）の体積平均粒径（Ｄｖ）は６．５μｍ、個数平均粒径（Ｄｎ）は５．４μｍで、Ｄｖ／Ｄｎは１．２０であった。
また、この着色剤平均分散粒径は０．５μｍで、０．７μｍ以上の分散粒径を持つ着色剤は４．５個数％であった。
トナー（Ｔ６）を用いた以外は、実施例１と同様にして、二成分現像剤を得た。
【０１０８】
比較例２

以上の処方で２軸エクストルーダーを用いて１００℃で混練し、粉砕、分級し、トナー粒子を得た。
ついで、トナー粒子１００部に疎水性シリカ０．５部と、疎水化酸化チタン０．５部をヘンシェルミキサーにて混合して、比較トナー（Ｔ７）を得た。
このトナー（Ｔ７）の体積平均粒径（Ｄｖ）は８．７μｍ、個数平均粒径（Ｄｎ）は６．７μｍで、Ｄｖ／Ｄｎは１．３０であった。
また、この顔料系着色剤平均分散粒径は０．６２μｍで、０．７μｍ以上の個数％は５．８％であった。
トナー（Ｔ７）を用いた以外は、実施例１と同様にして、二成分現像剤を得た。
【０１０９】
比較例３

上記処方をホモミキサーで３０分間分散してコート層形成用の塗工液を調整した。
これを重量平均粒径５０μｍの球形フェライト粒子５０００部の表面へ流動床型スプレーコート装置によりコート後、１５０℃／１時間加熱してキャリア（Ｃ３）を得た。
キャリア（Ｃ３）表面凹凸の平均高低差は、０．０６μｍであったが、これは、コア材の凹凸によるものであった。
また、キャリア（Ｃ３）の膜厚は、０．１１μｍであった。
キャリア（Ｃ３）を用いた以外は、実施例１と同様にして、二成分現像剤を得た。
【０１１０】
［物性測定及び評価方法］
各実施例及び比較例で得られたトナー、キャリアについてそれらの物性を表１及び表２に示す。
また各実施例及び比較例で得られた二成分現像剤を使用して、Ｒｉｃｏｈ製ＩＰＳＩＯ ｃｏｌｏｒ８０００改造機を用い、Ａ４版、画像面積率５％原稿２０万枚の連続画像出図試験を行い、画質評価、現像剤の帯電量評価を行った。
画像評価としては、ベタ画像部の光沢度、ヘイズ度、耐光性、画像濃度、地肌カブリを、以下の方法で行った。また、同時に、その他の不具合の発生有無を観察した。評価結果を表３及び表４に示す。
【０１１１】
（光沢度）
上記単色画像サンプルにおいて、定着ベルト表面温度が１６０℃ の時のサンプルの光沢度を、日本電色工業株式会社製のグロスメーターにより、入射角度６０°により計測した。この光沢度は、値の高い程、光沢感が出る。フルカラーのコピー画像としては、適度な光沢が好まれ、１０〜３０％程度が好ましい。光沢度の評価は、初期画像のみ行った。
【０１１２】
（ヘイズ度）
上記評価機にて、イエロー単色画像サンプルを、転写紙としてリコー製のＯＨＰシート（ タイプＰＰＣ−ＤＸ）を用い、定着温度が１６０℃ でのサンプルのヘイズ度を、スガ試験機株式会社製の直読ヘイズ度コンピューター ＨＧＭ−２ＤＰ型により測定した。ヘイズ度の評価は、初期画像のみ行った。
このヘイズ度は、曇り度とも言われ、トナーの透明性を示す尺度として測定され、値の低いほど透明性が高く、ＯＨＰシートを用いた場合の発色性が良好なものとなる。また、良好な発色性を示すヘイズ度の値は、３０％以下が好ましく、特に２０％以下である場合が好ましい。
【０１１３】
（耐光性）
イエロー単色ベタ画像を作成し、フェードメーターにて、キセノンランプを用い、１００時間光照射した後の退色具合を目視にて評価した。耐光性の評価は、初期画像のみ行った。
耐光性ランク
◎：極めて優れる
○：実用上問題無し
△：許容レベル
×：使用不可
（△以上がＯＫ）
【０１１４】
（画像濃度）
ベタ画像出力後、画像濃度をＸ−Ｒｉｔｅ（Ｘ−Ｒｉｔｅ社製）により測定した。評価値としては、ベタ画像内の独立した５点を測定し、その平均値を使用した。
【０１１５】
（地肌カブリ）
転写紙上地肌部のトナー汚れ度合を目視にて評価した。
地肌カブリランク
◎：極めて優れる
○：実用上問題無し
△：許容レベル
×：使用不可
（△以上がＯＫ）
【０１１６】
（帯電量）
トナー帯電量の測定は、エレクトロメーター（６１０Ｃ；ケスレー社製）を用い、気流によりトナーとキャリアを分離しつつ帯電電荷量を測定する、いわゆるブローオフ法によって行った。
帯電量は、一旦、現像剤中のトナーを気流により除去してキャリアのみを取り出し、あらためて、現像剤に用いているものと同じトナーを、トナー濃度７重量％となるように仕込み、５分間攪拌後、得られた帯電量測定用現像剤をブローオフ測定した。
【０１１７】
これらの評価の結果、初期、２０万枚後共に良好な画像品質が得られ、本発明の静電荷像現像用イエロー現像剤が、画像品質、寿命の両面で有用であることが判った。
【０１１８】
【表１】

【０１１９】
【表２】

【０１２０】
【表３】

【０１２１】
【表４】

【０１２２】
【発明の効果】
本発明によれば、実施例および比較例の対比から明らかなように、帯電量が経時的に安定し、画像劣化の極めて少ない、安定した画像を得るに必要な特性を有すると同時に、透明性が高く、耐光性に優れた、高精細・高解像度の高品質画像を得るのに有効な静電荷像現像用イエロー現像剤を提供することができる。
また本発明によれば、上記静電荷像現像用イエロー現像剤を用いる画像形成方法、及び該トナーを装填した画像形成装置を提供することが出来る。[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention relates to a yellow developer for developing an electrostatic image, which visualizes an electrostatic image formed on the surface of a photoreceptor in electrophotography and electrostatic recording, and a color image forming method using the same, and a method for mounting the same. To a color image forming apparatus.
[0002]
[Prior art]
In an electrophotographic apparatus or an electrostatic recording apparatus, a toner is attached to an electrostatic latent image formed on a photoconductor, transferred to a transfer material, and then fixed on the transfer material by heat to form a toner image. are doing. In addition, full-color image formation generally reproduces colors using four color toners of black, yellow, magenta, and cyan. A toner image is formed by developing each color and superimposing each toner layer on a transfer material. Are heated and fixed at the same time to obtain a full-color image.
However, from the point of view of users who are generally accustomed to printing, images in full-color copiers are not yet at a satisfactory level, and there is a demand for higher definition that satisfies high definition and high resolution close to photography and printing. It is known to use a toner having a small particle size and a narrow particle size distribution to improve the image quality of an image.
[0003]
Conventional pulverized toner is manufactured by melting and mixing a colorant, a charge control agent, an anti-offset agent and the like in a thermoplastic resin, uniformly dispersing the resultant, and pulverizing and classifying the obtained composition to produce a toner. In such a toner manufacturing method, a high-range particle size distribution is easily formed, and in order to obtain a copied image having good resolution and gradation, for example, a fine powder having a particle size of 5 μm or less and a fine powder having a particle size of 20 μm or more are used. There is a disadvantage that the coarse powder must be removed by classification, and the yield is very low. In particular, in the case of a color toner, it is difficult to uniformly disperse a colorant, a charge control agent, and the like in a thermoplastic resin by a pulverization method. Non-uniform dispersion of the compounding agent adversely affects toner fluidity, developability, durability, image quality, and the like.
[0004]
In recent years, in order to overcome the problems in these pulverization methods, a method for producing a toner by a polymerization method has been proposed and implemented. A technique for producing a toner for developing an electrostatic latent image by a polymerization method is known. For example, toner particles are obtained by a suspension polymerization method.
According to the polymerization method, the conventional pulverizing step and kneading step can be omitted, which greatly contributes to cost reduction, such as energy saving, shortening of production time, improvement of process yield, and further, when the toner particles are reduced in particle size. At the same time, it is easy to make the particle size distribution sharper than the pulverization method, and the contribution to high image quality is large. Therefore, the polymerization method is a promising method.
[0005]
Further, in order to improve the image quality of a full-color image in an electrophotography as high as printing, it is necessary that each toner has a wide color reproducibility. To achieve the above object without any problem, it is necessary to highly disperse a colorant having excellent transparency, light resistance and heat resistance in a binder resin.
Conventionally known colorants for yellow toner have many problems. For example, dye-based colorants generally have excellent transparency, but are inferior in light resistance and have a problem in image storage stability.
Further, although pigments are superior in light resistance as compared with dyes, they still have a problem in light resistance as compared with, for example, copper phthalocyanine pigments used for cyan toner.
Further, even a yellow pigment excellent in light resistance and heat resistance has an excessively high concealing property, resulting in extremely low transparency, and is not suitable for full color use.
[0006]
Japanese Patent Publication No. 2-37949 discloses a disazo compound excellent in light resistance and a method for producing the same. This is a group of compounds represented by Pigment Yellow 180, and is one of the azo pigments that not only excel in light resistance and heat resistance, but also meet recent safety requirements.
Pigment Yellow 180 is described in JP-A-6-230607, JP-A-6-266163, and JP-A-8-262799. However, the toner using the pigment has poor coloring power. In addition, transparency is not always good, but because of the above characteristics, it is widely used as a pigment for pulverized toner. However, Pigment Yellow 180 has relatively high water penetration, and in a method of dispersing an oil layer in water such as suspension polymerization, it may be used after segregation on the particle surface or reaggregation in the particle. Is difficult.
[0007]
Therefore, as a yellow pigment capable of suppressing the above-described surface segregation and re-aggregation, the present inventors have previously proposed a toner using a yellow pigment having the structure of Pigment Yellow 154, whereby a toner having good characteristics is obtained. (Japanese Patent Application No. 2002-237954).
However, when these toners are used in a two-component developer, a stable charge amount for a long period of time may not be obtained depending on the combination with the carrier used.
[0008]
On the other hand, regarding the surface structure of the carrier for stabilizing the charge amount and improving the durability, prevention of filming of the toner component on the carrier surface, formation of a uniform surface of the carrier, prevention of surface oxidation, prevention of deterioration in moisture sensitivity, development agent Coating with a suitable resin material for the purpose of extending the life of the photoreceptor, preventing the carrier from adhering to the photoreceptor surface, protecting the photoreceptor from scratches or abrasion, controlling the charging polarity or adjusting the charging amount, etc. Thus, a hard and high-strength coating layer is provided. For example, a coating layer coated with a specific resin material (JP-A-58-108548) and various additives are added to the coating layer. (JP-A-54-155048, JP-A-57-40267, JP-A-58-108548, JP-A-58-108549, JP-A-59-16) 968, Japanese Patent Publication No. 1-19584, Japanese Patent Publication No. 3-628, Japanese Patent Application Laid-Open No. 6-202381, and Patent Documents 1 to 6). Japanese Patent Application Laid-Open No. Hei 5-273789 and Japanese Patent Application Laid-Open No. Hei 9-160304 disclose using a coating film containing conductive particles larger than the coating film thickness. JP-A-8-6307 describes that a benzoguanamine-n-butyl alcohol-formaldehyde copolymer is used as a main component in a carrier coating material. Japanese Patent No. 2868324 discloses that a melamine resin and an acrylic resin are used. It describes that a crosslinked product is used as a carrier coating material.
[0009]
However, these proposals still have insufficient durability and insufficient suppression of adhesion of the toner composition to the carrier surface.
[0010]
Therefore, regarding durability, there are problems such as spent on the carrier surface of the toner, the resulting instability of the charge amount, and the reduction of the coating layer due to the film scraping of the coating resin and the resulting reduction in resistance. However, the quality of the copied image deteriorates as the number of copies increases, which is a problem.
Further, regarding the improvement of durability, it is necessary to further improve the functions in consideration of the recent global environment.
[0011]
[Patent Document 1]
JP-A-54-155048
[Patent Document 2]
JP-A-57-40267
[Patent Document 3]
JP-A-58-108548
[Patent Document 4]
JP-A-58-108549
[Patent Document 5]
JP-A-59-166968
[Patent Document 6]
Japanese Patent Publication No. 1-19584
[0012]
[Problems to be solved by the invention]
SUMMARY OF THE INVENTION An object of the present invention is to provide a yellow developer for electrostatic charge development which has good coloring properties and excellent charge stability over a long period of time.
It is another object of the present invention to provide a color image forming method using the yellow developer for developing an electrostatic image and excellent image quality, and a color image forming apparatus loaded with the developer.
[0013]
[Means for Solving the Problems]
According to the present invention,
(1) A yellow developer for electrostatic image development, which is obtained by mixing a toner containing at least a binder resin and a yellow colorant, and a carrier provided with a coating layer containing at least a resin and particles on the surface of a magnetic core material, The carrier is a carrier having irregularities derived from particles contained in a coat layer on a carrier surface, and the toner is a binder resin comprising a modified polyester resin capable of reacting with a compound having an active hydrogen group in an organic solvent. Is obtained by dissolving or dispersing the toner component containing as a component, dispersing the dissolved or dispersed product in an aqueous medium to react with a compound having an active hydrogen group, and removing the solvent from the obtained dispersion. A yellow developer for electrostatic image development, wherein the yellow developer is a compound represented by the following structural formula (I):
Embedded image

(2) The yellow developer for electrostatic charge image development according to (1), wherein the dispersed particle size of the yellow colorant in the toner is 0.5 μm or less in number average diameter.
(3) The yellow developer for electrostatic charge image development according to the above (1) or (2), wherein a composition obtained by previously kneading a binder resin and a yellow colorant with water is used as the colorant. ,
(4) The volume average particle size of the toner particles is 4 to 8 μm, and the ratio of the volume average particle size to the number average particle size (volume average particle size / number average particle size) is 1.25 or less. The yellow developer for developing an electrostatic image according to any one of the above (1) to (3),
(5) The yellow developer according to any one of (1) to (4), wherein the toner particles have an average circularity of 0.90 to 0.99.
(6) The yellow developer for developing an electrostatic image according to any of (1) to (5), wherein the average height difference of the carrier surface irregularities is 0.1 to 2.0 μm.
(7) The ratio of the particle size (D) of the particles contained in the carrier coat layer to the film thickness (h) of the coat layer resin is 1 <[D / h] <10. The yellow developer for developing an electrostatic image according to any one of the above (1) to (6),
(8) The electrostatic charge image according to any one of (1) to (7), wherein the total content of the particles contained in the carrier coat layer is 20 to 95% by weight of the composition of the coat layer. Yellow developer for development,
(9) A color image forming method using the yellow developer for electrostatic image development according to any one of (1) to (8) above,
(10) A color image forming apparatus, wherein the yellow developer for developing an electrostatic image according to any one of (1) to (8) is loaded.
Is provided.
[0014]
BEST MODE FOR CARRYING OUT THE INVENTION
Hereinafter, the present invention will be described more specifically.
In the present invention, the pigment represented by Structural Formula (I) belongs to isoindolinone pigment, and C.I. I. Pigment Yellow 185. The above-mentioned yellow colorant is hardly affected by hygroscopicity in a high-temperature and high-humidity environment, can reduce fluctuations in toner characteristics, and has the same durability as the initial state even when continuous paper is passed. Images can be maintained. As such, it is a well-known, but hardly dispersible pigment, and has therefore not been used in the art.
[0015]
The yellow toner constituting the developer of the present invention, which contains the compound represented by the structural formula (1) as a yellow colorant, has preferable spectral characteristics as a yellow toner for forming a full-color image, and has high chroma. You can get.
In a full-color image, color reproducibility is important. However, a yellow toner containing the compound represented by the structural formula (1) has a good hue, and reproduces a wide range of colors by using the toner. Things are possible.
Further, the compound represented by the structural formula (1) can be satisfactorily dispersed by making the toner composition like the above-mentioned yellow toner of the present invention, so that it has high light transmittance suitable for OHP sheets and the like. A color image can be obtained.
[0016]
Examples of the modified polyester resin capable of reacting with a compound having an active hydrogen group as a binder resin that can be used for preparing a toner include a polyester prepolymer (A) having an isocyanate group. Examples of the compound include amines (B).
Examples of the polyester prepolymer (A) having an isocyanate group include a polycondensate of a polyol (1) and a polycarboxylic acid (2), which is obtained by further reacting a polyester having an active hydrogen group with a polyisocyanate (3). No. Examples of the active hydrogen group contained in the polyester include a hydroxyl group (alcoholic hydroxyl group and phenolic hydroxyl group), an amino group, a carboxyl group, a mercapto group, and the like. Of these, an alcoholic hydroxyl group is preferable.
[0017]
Examples of the polyol (1) include a diol (1-1) and a polyol having a valence of 3 or more (1-2), and (1-1) alone or a mixture of (1-1) and a small amount of (1-2). Mixtures are preferred.
Examples of the diol (1-1) include alkylene glycols (such as ethylene glycol, 1,2-propylene glycol, 1,3-propylene glycol, 1,4-butanediol, and 1,6-hexanediol); and alkylene ether glycols (diethylene glycol). , Triethylene glycol, dipropylene glycol, polyethylene glycol, polypropylene glycol, polytetramethylene ether glycol, etc.); alicyclic diols (1,4-cyclohexane dimethanol, hydrogenated bisphenol A, etc.); bisphenols (bisphenol A, bisphenol F, bisphenol S, etc.); alkylene oxide (ethylene oxide, propylene oxide, butylene oxide, etc.) adduct of the above alicyclic diol; Alkylene oxide phenol compound (ethylene oxide, propylene oxide, butylene oxide, etc.), etc. adducts. Of these, preferred are alkylene glycols having 2 to 12 carbon atoms and alkylene oxide adducts of bisphenols, and particularly preferred are alkylene oxide adducts of bisphenols, and alkylene glycols having 2 to 12 carbon atoms. Is a combination of
[0018]
Trihydric or higher polyols (1-2) include trihydric or higher polyhydric aliphatic alcohols (glycerin, trimethylolethane, trimethylolpropane, pentaerythritol, sorbitol, etc.); trihydric or higher phenols (Such as trisphenol PA, phenol novolak, and cresol novolak); and the above-mentioned trivalent or higher polyphenols alkylene oxide adducts.
[0019]
Examples of the polycarboxylic acid (2) include a dicarboxylic acid (2-1) and a trivalent or higher polycarboxylic acid (2-2), and (2-1) alone or (2-1) and a small amount of ( The mixture of 2-2) is preferred.
Examples of the dicarboxylic acid (2-1) include alkylenedicarboxylic acids (succinic acid, adipic acid, sebacic acid, etc.); alkenylene dicarboxylic acids (maleic acid, fumaric acid, etc.); aromatic dicarboxylic acids (phthalic acid, isophthalic acid, terephthalic acid). , Naphthalenedicarboxylic acid, etc.). Of these, preferred are alkenylene dicarboxylic acids having 4 to 20 carbon atoms and aromatic dicarboxylic acids having 8 to 20 carbon atoms.
[0020]
Examples of the trivalent or higher polycarboxylic acid (2-2) include aromatic polycarboxylic acids having 9 to 20 carbon atoms (such as trimellitic acid and pyromellitic acid). The polycarboxylic acid (2) may be reacted with the polyol (1) using the above-mentioned acid anhydride or lower alkyl ester (eg, methyl ester, ethyl ester, isopropyl ester).
[0021]
The ratio of the polyol (1) to the polycarboxylic acid (2) is usually 2/1 to 1/1, preferably 1, as the equivalent ratio [OH] / [COOH] of the hydroxyl group [OH] and the carboxyl group [COOH]. It is from 5/1 to 1/1, more preferably from 1.3 / 1 to 1.02 / 1.
[0022]
Examples of the polyisocyanate (3) include aliphatic polyisocyanates (such as tetramethylene diisocyanate, hexamethylene diisocyanate, and 2,6-diisocyanatomethylcaproate); alicyclic polyisocyanates (such as isophorone diisocyanate and cyclohexylmethane diisocyanate); Aromatic diisocyanates (such as tolylene diisocyanate and diphenylmethane diisocyanate); araliphatic diisocyanates (such as α, α, α ′, α′-tetramethylxylylene diisocyanate); isocyanurates; And a combination of two or more of these.
[0023]
The ratio of the polyisocyanate (3) is usually 5/1 to 1/1, preferably 4/1, as the equivalent ratio [NCO] / [OH] of the isocyanate group [NCO] and the hydroxyl group [OH] of the hydroxyl group-containing polyester. The ratio is 1 to 1.2 / 1, more preferably 2.5 / 1 to 1.5 / 1. If [NCO] / [OH] exceeds 5, the low-temperature fixability deteriorates. If the molar ratio of [NCO] is less than 1, the urea content in the modified polyester becomes low, and the hot offset resistance deteriorates.
[0024]
The content of the polyisocyanate (3) component in the prepolymer (A) having an isocyanate group at the terminal is usually 0.5 to 40% by weight, preferably 1 to 30% by weight, and more preferably 2 to 20% by weight. It is. If the content is less than 0.5% by weight, the hot offset resistance is deteriorated and the heat storage stability and the low-temperature fixability are both disadvantageous. On the other hand, if it exceeds 40% by weight, the low-temperature fixability deteriorates.
[0025]
The isocyanate group contained in one molecule in the prepolymer (A) having an isocyanate group is usually at least 1, preferably 1.5 to 3 on average, and more preferably 1.8 to 2.5 on average. It is. If the number is less than one per molecule, the molecular weight of the urea-modified polyester becomes low, and the hot offset resistance deteriorates.
[0026]
Examples of the amines (B) include diamines (B1), trivalent or higher valent polyamines (B2), amino alcohols (B3), aminomercaptans (B4), amino acids (B5), and those obtained by blocking amino groups of B1 to B5. (B6) and the like. Examples of the diamine (B1) include aromatic diamines (phenylenediamine, diethyltoluenediamine, 4,4'-diaminodiphenylmethane, etc.); alicyclic diamines (4,4'-diamino-3,3'-dimethyldicyclohexylmethane, diamine Cyclohexane, isophoronediamine, etc.); and aliphatic diamines (ethylenediamine, tetramethylenediamine, hexamethylenediamine, etc.).
[0027]
Examples of the trivalent or higher polyamine (B2) include diethylenetriamine and triethylenetetramine. Examples of the amino alcohol (B3) include ethanolamine and hydroxyethylaniline. Examples of the aminomercaptan (B4) include aminoethylmercaptan and aminopropylmercaptan. Examples of the amino acid (B5) include aminopropionic acid and aminocaproic acid. Examples of the product obtained by blocking the amino group of B1 to B5 (B6) include ketimine compounds and oxazoline compounds obtained from the amines and ketones (such as acetone, methyl ethyl ketone, and methyl isobutyl ketone) of B1 to B5. Preferred of these amines (B) are B1 and a mixture of B1 and a small amount of B2.
[0028]
Furthermore, if necessary, the molecular weight of the urea-modified polyester can be adjusted by using an elongation terminator. Examples of the elongation terminator include monoamines (diethylamine, dibutylamine, butylamine, laurylamine and the like), and those obtained by blocking them (ketimine compounds).
[0029]
The ratio of the amines (B) is defined as the equivalent ratio [NCO] / [NHx] of the isocyanate groups [NCO] in the prepolymer (A) having isocyanate groups and the amino groups [NHx] in the amines (B). , Usually 1/2 to 2/1, preferably 1.5 / 1 to 1 / 1.5, and more preferably 1.2 / 1 to 1 / 1.2. When [NCO] / [NHx] is more than 2 or less than 1/2, the molecular weight of the urea-modified polyester (i) becomes low, and the hot offset resistance deteriorates.
[0030]
In the present invention, the polyester (i) modified with a urea bond may contain a urethane bond together with a urea bond. The molar ratio of the urea bond content to the urethane bond content is usually from 100/0 to 10/90, preferably from 80/20 to 20/80, and more preferably from 60/40 to 30/70. When the molar ratio of the urea bond is less than 10%, the hot offset resistance deteriorates.
[0031]
By these reactions, a modified polyester, preferably a urea-modified polyester (i) used in the toner of the present invention can be prepared. These urea-modified polyesters (i) are produced by a one-shot method or a prepolymer method. The weight average molecular weight of the urea-modified polyester (i) is usually 10,000 or more, preferably 20,000 to 10,000,000, and more preferably 30,000 to 1,000,000. If it is less than 10,000, the hot offset resistance deteriorates. The number-average molecular weight of the urea-modified polyester is not particularly limited when unmodified polyester (ii) described later is used, and may be a number-average molecular weight that is easily obtained to obtain the weight-average molecular weight. (I) When used alone, the number average molecular weight is usually 20,000 or less, preferably 1,000 to 10,000, and more preferably 2,000 to 8,000. If it exceeds 20,000, the low-temperature fixability and the gloss when used in a full-color device deteriorate.
[0032]
Further, in the present invention, not only the polyester (i) modified with the urea bond alone but also the unmodified polyester (ii) can be contained as a binder resin component together with this (i). The combined use of (ii) improves low-temperature fixability and glossiness when used in a full-color device, and is more preferable than use alone. Examples of (ii) include the same polycondensates of polyol (1) and polycarboxylic acid (2) as in the polyester component (i), and preferred ones are also the same as (i). Further, (ii) may be not only an unmodified polyester but also a polyester modified with a chemical bond other than a urea bond, for example, a modified urethane bond. It is preferable that (i) and (ii) are at least partially compatible with each other in view of low-temperature fixability and hot offset resistance. Therefore, the polyester component (i) and (ii) preferably have similar compositions. When (ii) is contained, the weight ratio of (i) to (ii) is usually 5/95 to 80/20, preferably 5/95 to 30/70, more preferably 5/95 to 25/75, Particularly preferably, it is 7/93 to 20/80. When the weight ratio of (i) is less than 5%, the hot offset resistance deteriorates, and the heat resistance storage stability and the low-temperature fixability are disadvantageous.
[0033]
The peak molecular weight of (ii) is generally from 1,000 to 30,000, preferably from 1500 to 10,000, and more preferably from 2,000 to 8,000. If it is less than 1,000, the heat-resistant preservability deteriorates, and if it exceeds 10,000, the low-temperature fixability deteriorates. The hydroxyl value of (ii) is preferably 5 or more, more preferably 10 to 120, and particularly preferably 20 to 80. If it is less than 5, it is disadvantageous in terms of compatibility between heat-resistant storage stability and low-temperature fixability. The acid value of (ii) is usually 1 to 30, preferably 5 to 20. By having an acid value, it tends to be negatively chargeable.
[0034]
In the present invention, the glass transition point (Tg) of the binder resin is usually 50 to 70 ° C, preferably 55 to 65 ° C. If the temperature is lower than 50 ° C., the blocking of the toner during high-temperature storage deteriorates, and if the temperature exceeds 70 ° C., the low-temperature fixability becomes insufficient. Due to the coexistence of a urea-modified polyester resin, the dry toner of the present invention tends to have good heat-resistant storage stability even at a low glass transition point, as compared with known polyester-based toners.
[0035]
The storage elastic modulus of the binder resin was 10,000 dyne / cm at a measurement frequency of 20 Hz. ² Is usually 100 ° C. or higher, preferably 110 to 200 ° C. If the temperature is lower than 100 ° C., the hot offset resistance deteriorates. As for the viscosity of the binder resin, the temperature (Tη) at which the poisoning becomes 1000 poise at a measurement frequency of 20 Hz is usually 180 ° C. or less, preferably 90 to 160 ° C. If it exceeds 180 ° C., the low-temperature fixability deteriorates. That is, TG ′ is preferably higher than Tη from the viewpoint of achieving both low-temperature fixability and hot offset resistance. In other words, the difference between TG ′ and Tη (TG′−Tη) is preferably 0 ° C. or more. It is more preferably at least 10 ° C, particularly preferably at least 20 ° C. The upper limit of the difference is not particularly limited. The difference between Tη and Tg is preferably from 0 to 100 ° C. from the viewpoint of achieving both heat-resistant storage stability and low-temperature fixability. The temperature is more preferably from 10 to 90 ° C, particularly preferably from 20 to 80 ° C.
[0036]
The binder resin can be manufactured by the following method or the like.
The polyol (1) and the polycarboxylic acid (2) are heated to 150 to 280 ° C. in the presence of a known esterification catalyst such as tetrabutoxytitanate or dibutyltin oxide, and the generated water is distilled off under reduced pressure if necessary. Thus, a polyester having a hydroxyl group is obtained. Next, the polyisocyanate (3) is reacted therewith at 40 to 140 ° C. to obtain a prepolymer (A) having an isocyanate group. Further, (A) is reacted with an amine (B) at 0 to 140 ° C. to obtain a polyester modified with a urea bond. When reacting (3) and when reacting (A) and (B), a solvent can be used if necessary. Solvents that can be used include aromatic solvents (toluene, xylene, etc.); ketones (acetone, methyl ethyl ketone, methyl isobutyl ketone, etc.); esters (ethyl acetate, etc.); amides (dimethyl formamide, dimethyl acetamide, etc.) and ethers And the like (e.g., tetrahydrofuran) which are inert to isocyanate (3). When a polyester (ii) not modified with a urea bond is used in combination, (ii) is produced in the same manner as the polyester having a hydroxyl group, and this is dissolved in the solution after the completion of the reaction (i) and mixed. I do.
[0037]
In addition, the toner used for the developer of the present invention can be generally manufactured by the following method, but is not limited thereto.
As the aqueous medium used in the present invention, water alone may be used, or a solvent miscible with water may be used in combination. Examples of miscible solvents include alcohols (eg, methanol, isopropanol, ethylene glycol), dimethylformamide, tetrahydrofuran, cellosolves (eg, methylcellosolve), lower ketones (eg, acetone, methylethylketone), and the like.
[0038]
The toner particles may be formed by reacting a dispersion composed of a prepolymer (A) having an isocyanate group in an aqueous medium with (B) or using a urea-modified polyester (i) produced in advance. good. As a method for stably forming a dispersion composed of the urea-modified polyester (i) or the prepolymer (A) in an aqueous medium, a toner raw material comprising the urea-modified polyester (i) or the prepolymer (A) in an aqueous medium is used. And dispersing the composition by a shearing force. The prepolymer (A) and another toner composition (hereinafter, referred to as toner raw material) such as a colorant, a colorant masterbatch, a release agent, a charge control agent, and an unmodified polyester resin are dispersed in an aqueous medium. The toner may be mixed at the time of formation, but it is more preferable to mix the toner raw materials in advance and then add and disperse the mixture in an aqueous medium. Further, in the present invention, other toner raw materials such as a colorant, a release agent, and a charge control agent do not necessarily need to be mixed when forming particles in an aqueous medium, and after forming the particles. May be added. For example, after forming particles containing no coloring agent, a coloring agent can be added by a known dyeing method.
[0039]
The dispersing method is not particularly limited, but known equipment such as a low-speed shearing type, a high-speed shearing type, a friction type, a high-pressure jet type, and an ultrasonic wave can be applied. In order to make the particle size of the dispersion 2 to 20 μm, a high-speed shearing type is preferred. When a high-speed shearing disperser is used, the number of rotations is not particularly limited, but is generally 1,000 to 30,000 rpm, preferably 5,000 to 20,000 rpm. The dispersion time is not particularly limited, but is usually 0.1 to 5 minutes in the case of a batch system. The temperature at the time of dispersion is usually 0 to 150 ° C (under pressure), preferably 40 to 98 ° C. Higher temperatures are preferred because the dispersion of the urea-modified polyester (i) or the prepolymer (A) has a lower viscosity and is easier to disperse.
[0040]
The amount of the aqueous medium to be used per 100 parts by weight of the toner composition containing the urea-modified polyester (i) and the prepolymer (A) is usually 50 to 2,000 parts by weight, preferably 100 to 1,000 parts by weight. If the amount is less than 50 parts by weight, the dispersion state of the toner composition is poor, and toner particles having a predetermined particle size cannot be obtained. If it exceeds 2000 parts by weight, it is not economical. In addition, a dispersant can be used if necessary. The use of a dispersant is preferred because the particle size distribution becomes sharp and the dispersion is stable.
[0041]
In the step of synthesizing the urea-modified polyester (i) from the prepolymer (A), the amine composition (B) may be added before the toner composition is dispersed in the aqueous medium and reacted, or the urea-modified polyester (i) may be dispersed in the aqueous medium. The amine (B) may be added later to cause a reaction from the particle interface. In this case, urea-modified polyester is preferentially generated on the surface of the toner to be produced, and a concentration gradient can be provided inside the particles.
[0042]
As a dispersant for emulsifying and dispersing the oil phase in which the toner composition is dispersed in a liquid containing water, an anionic surfactant such as an alkylbenzene sulfonate, an α-olefin sulfonate, or a phosphate, an alkylamine Salts, amino alcohol fatty acid derivatives, polyamine fatty acid derivatives, amine salt forms such as imidazoline, and alkyltrimethylammonium salts, dialkyldimethylammonium salts, alkyldimethylbenzylammonium salts, pyridinium salts, alkylisoquinolinium salts, benzethonium chloride, etc. Nonionic surfactants such as quaternary ammonium salt type cationic surfactants, fatty acid amide derivatives and polyhydric alcohol derivatives, for example, alanine, dodecyldi (aminoethyl) glycine, di (octylaminoethyl) glycine and N-alkyl N, amphoteric surfactants such as N- dimethyl ammonium betaine and the like.
[0043]
By using a surfactant having a fluoroalkyl group, the effect can be improved with a very small amount. Preferred examples of the anionic surfactant having a fluoroalkyl group include a fluoroalkyl carboxylic acid having 2 to 10 carbon atoms and a metal salt thereof, disodium perfluorooctanesulfonylglutamate, and 3- [omega-fluoroalkyl (C6 to C11). ) Sodium] oxy] -1-alkyl (C3-C4) sulfonate, Sodium 3- [omega-fluoroalkanoyl (C6-C8) -N-ethylamino] -1-propanesulfonate, Fluoroalkyl (C11-C20) carboxy Acid and metal salt, perfluoroalkylcarboxylic acid (C7-C13) and its metal salt, perfluoroalkyl (C4-C12) sulfonic acid and its metal salt, perfluorooctanesulfonic acid diethanolamide, N-propyl-N- ( 2-hydroxyethyl) -Fluorooctanesulfonamide, perfluoroalkyl (C6-C10) sulfonamidopropyltrimethylammonium salt, perfluoroalkyl (C6-C10) -N-ethylsulfonylglycine salt, monoperfluoroalkyl (C6-C16) ethyl phosphate, etc. Is mentioned.
[0044]
As trade names, Surflon S-111, S-112, S-113 (manufactured by Asahi Glass Co., Ltd.), Florard FC-93, FC-95, FC-98, FC-129 (manufactured by Sumitomo 3M), Unidyne DS-101 , DS-102, (manufactured by Daikin Industries, Ltd.), Megafac F-110, F-120, F-113, F-191, F-812, F-833 (manufactured by Dainippon Ink and Chemicals), Ektop EF-102 , 103, 104, 105, 112, 123A, 123B, 306A, 501, 201, 204, (manufactured by Tochem Products), Futagent F-100, F150 (manufactured by Neos), and the like.
Examples of the cationic surfactant include an aliphatic primary, secondary or secondary amine having a fluoroalkyl group, an aliphatic quaternary ammonium salt such as a perfluoroalkyl (C6-C10) sulfonamidopropyltrimethylammonium salt, and benza. Ruconium salt, benzethonium chloride, pyridinium salt, imidazolinium salt, trade names are Surflon S-121 (manufactured by Asahi Glass Co., Ltd.), Florard FC-135 (manufactured by Sumitomo 3M), Unidine DS-202 (manufactured by Daikin Industries, Ltd.) , Megafac F-150, F-824 (manufactured by Dainippon Ink and Chemicals), Ectop EF-132 (manufactured by Tochem Products), Futagent F-300 (manufactured by Neos) and the like.
[0045]
Further, tricalcium phosphate, calcium carbonate, titanium oxide, colloidal silica, hydroxyapatite, and the like can be used as the inorganic compound dispersant that is hardly soluble in water.
[0046]
Further, the dispersed droplets may be stabilized by a polymer-based protective colloid. For example, an acid such as acrylic acid, methacrylic acid, α-cyanoacrylic acid, α-cyanomethacrylic acid, itaconic acid, crotonic acid, fumaric acid, maleic acid or maleic anhydride, or a (meth) acrylic monomer containing a hydroxyl group Such as β-hydroxyethyl acrylate, β-hydroxyethyl methacrylate, β-hydroxypropyl acrylate, β-hydroxypropyl methacrylate, γ-hydroxypropyl acrylate, γ-hydroxypropyl methacrylate, 3-acrylic acid Chloro-2-hydroxypropyl, 3-chloro-2-hydroxypropyl methacrylate, diethylene glycol monoacrylate, diethylene glycol monomethacrylate, glycerin monoacrylate, glycerin monomethacrylate, N-methylol acrylamide, N-methylol methacrylamide, such as vinyl alcohol or ethers with vinyl alcohol, such as vinyl methyl ether, vinyl ethyl ether, vinyl propyl ether, or esters of vinyl alcohol and compounds containing a carboxyl group, For example, vinyl acetate, vinyl propionate, vinyl butyrate, etc., acrylamide, methacrylamide, diacetone acrylamide or methylol compounds thereof, acid chlorides such as acrylic acid chloride, methacrylic acid chloride, vinyl pyridine, vinyl pyrrolidone, vinyl imidazole, ethylene imine Homopolymers or copolymers such as those having a nitrogen atom or a heterocycle thereof, polyoxyethylene, polyoxypropylene, Lioxyethylene alkylamine, polyoxypropylene alkylamine, polyoxyethylene alkylamide, polyoxypropylene alkylamide, polyoxyethylene nonyl phenyl ether, polyoxyethylene lauryl phenyl ether, polyoxyethylene stearyl phenyl ester, polyoxyethylene nonyl phenyl Polyoxyethylenes such as esters and celluloses such as methylcellulose, hydroxyethylcellulose and hydroxypropylcellulose can be used.
[0047]
In addition, when an acid such as calcium phosphate salt or an alkali-soluble substance is used as the dispersion stabilizer, the calcium phosphate salt is removed from the fine particles by a method such as dissolving the calcium phosphate salt with an acid such as hydrochloric acid and washing with water. I do. In addition, it can be removed by an operation such as decomposition with an enzyme.
[0048]
When a dispersant is used, the dispersant can be left on the surface of the toner particles, but it is preferable to remove the dispersant by washing after the elongation and / or cross-linking reaction from the charged surface of the toner.
[0049]
Further, in order to lower the viscosity of the toner composition, a solvent in which the urea-modified polyester (i) or the prepolymer (A) is soluble can be used. The use of a solvent is preferred in that the particle size distribution becomes sharp. It is preferable that the solvent is volatile having a boiling point of less than 100 ° C. from the viewpoint of easy removal. Examples of the solvent include toluene, xylene, benzene, carbon tetrachloride, methylene chloride, 1,2-dichloroethane, 1,1,2-trichloroethane, trichloroethylene, chloroform, monochlorobenzene, dichloroethylidene, methyl acetate, ethyl acetate, Methyl ethyl ketone, methyl isobutyl ketone and the like can be used alone or in combination of two or more. In particular, aromatic solvents such as toluene and xylene and halogenated hydrocarbons such as methylene chloride, 1,2-dichloroethane, chloroform and carbon tetrachloride are preferred. The amount of the solvent to be used relative to 100 parts by weight of the prepolymer (A) is usually 0 to 300 parts by weight, preferably 0 to 100 parts by weight, more preferably 25 to 70 parts by weight. When a solvent is used, it is removed by heating under normal pressure or reduced pressure after the elongation and / or crosslinking reaction.
[0050]
The elongation and / or crosslinking reaction time is selected depending on the reactivity of the isocyanate group structure of the prepolymer (A) and the combination of the amines (B), and is usually 10 minutes to 40 hours, preferably 2 to 24 hours. is there. The reaction temperature is generally 0-150 ° C, preferably 40-98 ° C. In addition, a known catalyst can be used as needed. Specific examples include dibutyltin laurate and dioctyltin laurate.
[0051]
In order to remove the organic solvent from the obtained emulsified dispersion, a method of gradually raising the temperature of the entire system and completely evaporating and removing the organic solvent in the droplets can be adopted. Alternatively, it is also possible to spray the emulsified dispersion in a dry atmosphere, completely remove the water-insoluble organic solvent in the droplets to form toner fine particles, and collectively evaporate and remove the aqueous dispersant. . As a drying atmosphere in which the emulsified dispersion is sprayed, a gas obtained by heating air, nitrogen, carbon dioxide, combustion gas, or the like, particularly various air streams heated to a temperature equal to or higher than the boiling point of the highest boiling solvent used is generally used. Satisfactory target quality can be obtained by short-time treatment such as spray dryer, belt dryer and rotary kiln.
[0052]
The particle size distribution at the time of emulsification dispersion is wide, and when washing and drying are performed while maintaining the particle size distribution, the particle size distribution can be adjusted by classifying into a desired particle size distribution.
In the classification operation, the fine particle portion can be removed in the liquid by cyclone, decanter, centrifugation, or the like. Of course, the classification operation may be performed after obtaining the powder after drying, but it is preferable to perform the classification operation in a liquid in terms of efficiency. The obtained unnecessary fine particles or coarse particles can be returned to the kneading step again and used for forming particles. At this time, the fine particles or coarse particles may be in a wet state.
The dispersant used is preferably removed from the obtained dispersion as much as possible, but is preferably carried out simultaneously with the classification operation described above.
[0053]
By mixing the resulting dried toner powder with different kinds of particles such as release agent fine particles, charge control fine particles, fluidizing agent fine particles, and colorant fine particles, or by applying a mechanical impact force to the mixed powder. Immobilization and fusion at the surface can prevent the dissociation of foreign particles from the surface of the resulting composite particles.
As specific means, there are a method of applying an impact force to the mixture by a blade rotating at a high speed, a method of throwing the mixture into a high-speed air flow, accelerating, and colliding particles or composite particles with an appropriate collision plate. is there. As the equipment, Angmill (manufactured by Hosokawa Micron), I-type mill (manufactured by Nippon Pneumatic) was modified to reduce the pulverizing air pressure, hybridization system (manufactured by Nara Machinery Co., Ltd.), Kryptron system (Manufactured by Kawasaki Heavy Industries, Ltd.) and automatic mortars.
[0054]
The number average diameter of the compound represented by the structural formula (1) in the toner used in the present invention is desirably 0.5 μm or less, preferably 0.4 μm or less, more preferably 0.3 μm or less. Is desirable.
When the number average particle size of the compound in the toner is larger than 0.5 μm, the dispersibility of the pigment does not reach a sufficient level. In this case, even if a specific resin and a colorant having a specific particle size are used, The desired transparency cannot be obtained.
Since the colorant having a fine particle diameter smaller than 0.1 μm is sufficiently smaller than the half wavelength of visible light, it is considered that the colorant does not adversely affect the light reflection and absorption characteristics. Therefore, particles of the coloring agent having a size of less than 0.1 μm contribute to good color reproducibility and transparency of the OHP sheet having a fixed image. On the other hand, if there are many colorants having a particle size larger than 0.5 μm, the transmission of incident light is hindered or scattered, and the brightness and color of the projected image on the OHP sheet tend to decrease. There is.
Further, if a large amount of a coloring agent having a particle size larger than 0.5 μm is present, the yellow coloring agent is detached from the surface of the yellow toner particles, and various problems such as fog, drum contamination, and poor cleaning are likely to occur. . In particular, the colorant having a particle size larger than 0.7 μm is preferably 10% by number or less of all the colorants, and more preferably 5% by number or less.
[0055]
In addition, by adding a wetting liquid in advance and kneading the colorant together with part or all of the binder resin and kneading, the binder resin and the colorant are initially in a state of being sufficiently attached, and thereafter, In the toner production process, the dispersion of the colorant in the toner particles is performed more effectively, the dispersion particle size of the colorant is reduced, and better transparency can be obtained.
[0056]
Examples of the binder resin used in advance kneading include modified and unmodified polyester resins, and polymers of styrene such as polystyrene, poly-p-chlorostyrene, and polyvinyltoluene, and their substituted polymers; styrene-p-chlorostyrene copolymer. Copolymer, styrene-propylene copolymer, styrene-vinyltoluene copolymer, styrene-vinylnaphthalene copolymer, styrene-methyl acrylate copolymer, styrene-ethyl acrylate copolymer, styrene-butyl acrylate copolymer Coalesce, styrene-octyl acrylate copolymer, styrene-methyl methacrylate copolymer, styrene-ethyl methacrylate copolymer, styrene-butyl methacrylate copolymer, styrene-α-chloromethyl methacrylate copolymer, Styrene-acrylonitrile copolymer, styrene-vinyl methyl Styrene copolymers such as ketone copolymers, styrene-butadiene copolymers, styrene-isoprene copolymers, styrene-acrylonitrile-indene copolymers, styrene-maleic acid copolymers, and styrene-maleic acid ester copolymers Coalescing; polymethyl methacrylate, polybutyl methacrylate, polyvinyl chloride, polyvinyl acetate, polyethylene, polypropylene, polyester, epoxy resin, epoxy polyol resin, polyurethane, polyamide, polyvinyl butyral, polyacrylic resin, rosin, modified rosin, terpene resin , Aliphatic or alicyclic hydrocarbon resins, aromatic petroleum resins, chlorinated paraffins, paraffin waxes, and other resins having a generally suitable thermoplasticity. These resins can be used alone or in combination, but are not limited to these. What is done is not.
[0057]
As a specific method of kneading the mixture of the binder resin and the colorant together with the wetting liquid in advance, for example, the binder resin, the coloring agent and the wetting liquid are mixed in a blender such as a Henschel mixer, and then obtained. The resulting mixture is kneaded with a kneader such as a two-roll or three-roll mill at a temperature lower than the melting temperature of the binder resin to obtain a sample.
[0058]
In addition, as the wetting liquid, a general one can be used in consideration of the solubility of the binder resin and the wettability with the colorant.In particular, acetone, toluene, and organic solvents such as butanone and water are used. It is preferable from the viewpoint of dispersibility of the colorant.
Among them, the use of water is more preferable in consideration of the environment and maintenance of the dispersion stability of the yellow colorant in the subsequent toner manufacturing process.
According to this manufacturing method, not only the particle size of the colorant particles contained in the obtained color toner becomes small, but also the uniformity of the dispersed state of the particles becomes high, so that the reproducibility of the color of the projected image by the OHP is improved. It gets better.
[0059]
In the present invention, the volume average particle diameter (Dv) of the toner constituting the developer is preferably 4 to 8 μm, and the ratio (Dv / Dn) to the number average particle diameter (Dn) is 1.25 or less. Preferably, it is particularly preferably 1.10 to 1.25.
By setting the particle diameter of the toner in this way, the toner has excellent heat storage stability, low-temperature fixability, and hot offset resistance, and particularly has excellent image gloss when used in a full-color copying machine. In the two-component developer, even when the balance of the toner is performed for a long time, the fluctuation of the toner particle diameter in the developer is reduced, and good and stable developability can be obtained even when the developing device is stirred for a long time.
[0060]
In general, it is said that the smaller the particle size of the toner, the more advantageous it is to obtain a high-resolution and high-quality image, but it is disadvantageous to the transferability and the cleaning property. It tends to be. Further, when the toner volume average diameter is smaller than the above range of the present invention, the toner is fused to the surface of the carrier during long-term stirring in the developing device of the two-component developer, and the charging ability of the carrier is easily reduced.
Conversely, when the volume average diameter of the toner is larger than the above range of the present invention, it becomes difficult to obtain a high-resolution and high-quality image, and when the balance of the toner in the developer is performed. In many cases, the fluctuation of the particle diameter of the toner becomes large. It was also found that the same applies when the volume average particle diameter / number average particle diameter is larger than 1.25.
[0061]
It is preferable that the toner has a specific shape and its distribution. Above all, the presence of an irregular toner having an average circularity of less than 0.90 and being too far from a sphere indicates high transferability without satisfactory transferability and high dust freeness. It tends to have an adverse effect on obtaining a quality image.
As a method of measuring the shape, a method of an optical detection band in which a suspension containing particles is passed through a detection band on an imaging unit on a flat plate, and a particle image is optically detected and analyzed by a CCD camera. A toner having an average circularity of 0.90 to 0.99, which is a value obtained by dividing the perimeter of an equivalent circle having the same projected area obtained by this method by the perimeter of the actual particles, has high density and reproducibility with an appropriate density. It was found to be effective for forming a perfect image. More preferably, particles having an average circularity of 0.94 to 0.985 and a circularity of less than 0.94 are 10% by number or less.
[0062]
In a system that employs blade cleaning or the like to remove transfer residual toner, when the average circularity is 0.96 or more, poor cleaning of the photoreceptor and the transfer belt occurs, and the In such a system, the average circularity is preferably less than 0.96, as it can cause contamination.
For example, in development / transfer with a low image area ratio, there is little transfer residual toner, and there is no problem of poor cleaning. However, images with a high image area ratio such as photographic images, and untransferred images due to poor paper feed etc. The formed toner may be generated as a transfer residual toner on the photoconductor, and when accumulated, the image may be stained. Further, in a system using a charging roller or the like for charging the photoconductor in contact, these may be contaminated, and the original charging ability may not be exhibited.
[0063]
In addition, as long as the configuration of the present invention is adopted, a release agent represented by wax can be contained in the toner together with the binder resin and the colorant.
Known release agents can be used, and examples thereof include polyolefin waxes (eg, polyethylene wax and polypropylene wax); long-chain hydrocarbons (eg, paraffin wax, sasol wax); and carbonyl group-containing waxes. .
Preferred among these are carbonyl group-containing waxes. Examples of the carbonyl group-containing wax include polyalkanoic acid esters (carnauba wax, montan wax, trimethylolpropane tribehenate, pentaerythritol tetrabehenate, pentaerythritol diacetate dibehenate, glycerin tribehenate, 1,18 Polyalkanol esters (such as tristearyl trimellitate and distearyl maleate); polyalkanoic acid amides (such as ethylenediamine dibehenylamide); and polyalkylamides (such as trimellitic acid tristearyl amide). And dialkyl ketones (such as distearyl ketone).
Preferred among these carbonyl group-containing waxes are polyalkanoic esters.
[0064]
The melting point of these release agents is usually 40 to 160 ° C, preferably 50 to 120 ° C, and more preferably 60 to 90 ° C. A wax having a melting point of less than 40 ° C. has an adverse effect on heat-resistant storage stability, and a wax having a melting point of more than 160 ° C. tends to cause cold offset at the time of fixing at a low temperature. The melt viscosity of the wax is preferably 5 to 1000 cps, more preferably 10 to 100 cps, as a value measured at a temperature 20 ° C. higher than the melting point. Waxes exceeding 1000 cps have poor improvement effects on hot offset resistance and low-temperature fixability.
The content of the wax in the toner is usually 0 to 40% by weight, preferably 3 to 30% by weight.
[0065]
Further, in order to accelerate the charge amount of the toner and its rise, a charge control agent may be contained in the toner as needed. Here, when a colored material is used as the charge controlling agent, a color change occurs. Therefore, a colorless and nearly white material is preferable.
As the charge control agent, any known charge control agents can be used, and examples thereof include triphenylmethane dyes, molybdic acid chelate pigments, rhodamine dyes, alkoxy amines, quaternary ammonium salts (including fluorine-modified quaternary ammonium salts), and alkyl. An amide, a simple substance or compound of phosphorus, a simple substance or compound of tungsten, a fluorine-based activator, a metal salt of salicylic acid, and a metal salt of a salicylic acid derivative. Specifically, bontron P-51 of a quaternary ammonium salt, E-82 of an oxynaphthoic acid-based metal complex, E-84 of a salicylic acid-based metal complex, and E-89 of a phenol-based condensate (these are Orient Chemical Industries, Ltd.) TP-302, TP-415 of quaternary ammonium salt molybdenum complex (both manufactured by Hodogaya Chemical Industry Co., Ltd.), Copy Charge PSY VP2038 of quaternary ammonium salt, Copy Blue PR of triphenylmethane derivative, Copy Charge of Quaternary Ammonium Salt NEG VP2036, Copy Charge NX VP434 (above, manufactured by Hoechst), LRA-901, LR-147 which is a boron complex (manufactured by Nippon Carlit Co.), quinacridone, azo pigment, and other sulfonic acid groups Of polymer system having functional groups such as carboxylic acid, carboxyl group and quaternary ammonium salt Thing, and the like.
[0066]
In the present invention, the amount of the charge control agent used is determined by the type of the binder resin, the presence or absence of additives used as necessary, and the toner production method including the dispersion method, and is uniquely limited. However, it is preferably used in the range of 0.1 to 10 parts by weight based on 100 parts by weight of the binder resin. Preferably, the range is 0.2 to 5 parts by weight. If the amount exceeds 10 parts by weight, the chargeability of the toner is too large, the effect of the main charge control agent is reduced, the electrostatic attraction with the developing roller increases, the fluidity of the developer decreases, and the image density decreases. Causes a decline. These charge control agents can be dissolved and dispersed after being melt-kneaded with the masterbatch and the resin, or may be directly dissolved and dispersed in an organic solvent, or may be added after toner particles are formed and fixed on the toner surface. Is also good.
[0067]
Further, when dispersing the toner composition in an aqueous medium during the toner production process, resin fine particles mainly for stabilizing dispersion may be added.
The resin fine particles used can be any resin as long as it is a resin capable of forming an aqueous dispersion, and may be a thermoplastic resin or a thermosetting resin, for example, a vinyl resin, a polyurethane resin, an epoxy resin, a polyester resin, Examples thereof include a polyamide resin, a polyimide resin, a silicon-based resin, a phenol resin, a melamine resin, a urea resin, an aniline resin, an ionomer resin, and a polycarbonate resin. As the resin fine particles, two or more of the above resins may be used in combination. Of these, vinyl resins, polyurethane resins, epoxy resins, polyester resins, and combinations thereof are preferable because an aqueous dispersion of fine spherical resin particles is easily obtained.
[0068]
The vinyl resin is a polymer obtained by homopolymerizing or copolymerizing a vinyl monomer, for example, a styrene- (meth) acrylate resin, a styrene-butadiene copolymer, a (meth) acrylic acid-acrylate polymer, Examples include, but are not limited to, styrene-acrylonitrile copolymer, styrene-maleic anhydride copolymer, styrene- (meth) acrylic acid copolymer, and the like.
[0069]
Further, inorganic fine particles can be preferably used as an external additive for assisting the fluidity, developability and chargeability of the toner particles.
The primary particle size of the inorganic fine particles is preferably from 5 μm to 2 μm, and particularly preferably from 5 μm to 500 μm. The specific surface area by the BET method is 20 to 500 m. ² / G. The use ratio of the inorganic fine particles is preferably from 0.01 to 5% by weight of the toner, and particularly preferably from 0.01 to 2.0% by weight.
[0070]
Specific examples of the inorganic fine particles include, for example, silica, alumina, titanium oxide, barium titanate, magnesium titanate, calcium titanate, strontium titanate, zinc oxide, tin oxide, silica sand, clay, mica, wollastonite, and diatomaceous Examples include earth, chromium oxide, cerium oxide, red iron oxide, antimony trioxide, magnesium oxide, zirconium oxide, barium sulfate, barium carbonate, calcium carbonate, silicon carbide, and silicon nitride.
[0071]
In addition, polymer-based fine particles such as polystyrene obtained by soap-free emulsion polymerization, suspension polymerization, and dispersion polymerization, polycondensation systems such as silicone, benzoguanamine, and nylon, and methacrylic acid ester and acrylic acid ester copolymers, and thermosetting resins Polymer particles.
[0072]
Such a fluidizing agent can be subjected to a surface treatment to increase hydrophobicity and prevent deterioration of fluidity and charging properties even under high humidity. For example, silane coupling agents, silylating agents, silane coupling agents having a fluorinated alkyl group, organic titanate-based coupling agents, aluminum-based coupling agents, silicone oil, modified silicone oil, and the like are preferable surface treatment agents. .
[0073]
Further, a cleaning property improver for removing the developer after transfer remaining on the photoreceptor or the primary transfer medium may be used. Examples of the cleaning property improver include zinc stearate, calcium stearate, and stearic acid. Fatty acid metal salts, for example, polymer fine particles produced by soap-free emulsion polymerization of polymethyl methacrylate fine particles, polystyrene fine particles and the like can be mentioned. The polymer fine particles preferably have a relatively narrow particle size distribution and a volume average particle size of 0.01 to 1 μm.
[0074]
On the other hand, the carrier used in the developer of the present invention is a carrier provided with a coat layer containing at least a resin and particles on the surface of a magnetic core material and having irregularities derived from particles contained in the coat layer on the carrier surface. When the carrier was used together with the above-mentioned toner, it was found that the improvement in image quality and stability was remarkable.
[0075]
In general, it is generally known that the image quality is affected by variations in toner charge amount and developer resistance, and fluctuates with time due to abrasion of the carrier surface and adhesion of toner components to the carrier surface.
In particular, the yellow colorant contained in the toner used in the developer of the present invention significantly deteriorates the charging performance of the carrier even when a very small amount of toner is fixed to the carrier surface, and increases the amount of toner fixed. It may not be possible to give at all.
For this reason, the carrier surface needs to be refreshed so that toner adhesion does not increase.However, use while shaving the coat layer and performing surface refreshing naturally requires carrier durability, especially in terms of resistance fluctuation and fluidity fluctuation. There is a limit.
Therefore, as in the present invention, as the carrier structure, by forming irregularities derived from the particles contained in the coat layer on the surface, only the toner composition fixed on the carrier surface is removed, and the carrier layer is not worn away without abrasion of the coat layer. The surface can be refreshed.
[0076]
Further, since the uneven shape can be controlled substantially only by the coat layer, the magnetic core material can be selectively used without any limitation.
Further, the average height difference of the carrier surface irregularities is preferably 0.1 to 2.0 μm, more preferably 0.2 to 1.4 μm.
If the height difference is larger than this, the toner composition component is fixed to the concave portions, and the carrier charging performance may be deteriorated, or the carrier surface particles forming the convex portions may be detached.
On the other hand, when the height difference is small, a sufficient effect of scraping off the toner-fixed matter cannot be obtained, and the toner component may be fixed on the entire surface of the carrier.
[0077]
Further, by containing particles in the carrier coating film such that the ratio of the particle diameter (D) to the coating layer resin film thickness (h) is 1 <[D / h] <10, the effect is improved. Is remarkable. This is because when 1 <[D / h] <10, the particles are more convex than the coating film. Therefore, the friction with the toner or the carrier between the carriers is caused by stirring for frictionally charging the developer. Friction can reduce contact with a strong impact on the binder resin.
As a result, the spent of the toner composition component on the carrier surface is more reliably prevented, and the film of the binder resin can be prevented from being scraped. When [D / h] is 1 or less, the particles are buried in the binder resin, and the effect is remarkably reduced, which is not preferable.
When [D / h] is 10 or more, a sufficient contact force cannot be obtained due to a small contact area between the particles and the binder resin, and the particles are easily detached, which is not preferable.
[0078]
Further, as the particles, insulating inorganic particles can be preferably used. The insulating inorganic particles are not particularly limited, and include aluminum oxide, silicon oxide, calcium carbonate, talc, clay, quartz glass, aluminosilicate glass, mica flakes, zirconium oxide, mullite, sialon, steatite, and phorite. Known insulator powder particles such as stellite, cordierite, beryllium oxide, and silicon nitride can be used, but are not limited thereto. Above all, by including at least an aluminum element and / or a silicon element component represented by aluminum oxide or silicon oxide as a constituent unit in the insulating inorganic particles, desorption of the particles from the coat layer can be further suppressed. This is more preferable because the change with time of the initial carrier surface state can be more reliably suppressed.
[0079]
In order to surely form irregularities derived from particles on the surface of the carrier, the content of the particles is preferably 20 to 95% by weight of the coating film composition component. When the particle content is less than 20% by weight of the composition component of the coating layer, even if a concavo-convex structure can be formed on the carrier surface, the structure tends to be smooth, so that the carrier surface state greatly varies. In some cases, the effect of the present invention cannot be sufficiently exhibited. On the other hand, if the particle content exceeds 95% by weight of the composition of the coating layer, the uneven structure may become brittle, and the initial uneven structure cannot be maintained for a long period of time. May not be maintained. More preferably, the particle content is 55 to 80% by weight.
[0080]
The resin for forming the coat layer of the carrier can also be used without any particular limitation as long as it does not deviate from the provisions of the present invention. Polyolefin (eg, polyethylene, polypropylene, etc.) and its modified products, styrene, acrylic resin, Crosslinkable copolymers containing acrylonitrile, vinyl acetate, vinyl alcohol, vinyl chloride, vinyl carbazole, vinyl ether, etc .; silicone resins comprising organosiloxane bonds or modified products thereof (for example, modified with alkyd resins, polyester resins, epoxy resins, polyurethanes, etc.) Polyamide; Polyester; Polyurethane; Polycarbonate; Urea resin; Melamine resin; Benzoguanamine resin; Epoxy resin; Polyimide resin and derivatives thereof.
[0081]
Above all, in order to reliably fix the insulating inorganic particles as described above in the carrier coat layer and to better suppress the detachment of the inorganic particles due to friction, the resin of the coat layer has at least an acrylic portion as a constituent unit. It is preferred to include. Thereby, the detachment of the inorganic particles due to friction can be suppressed very effectively, and the uneven structure of the carrier surface can be maintained for a long period of time. Further, the acrylic resin preferably has a glass transition temperature (Tg) of 20 to 100 ° C, more preferably 25 to 80 ° C. By setting the Tg of the resin within this range, it is considered that the coat layer resin has an appropriate elasticity, and it is considered that the impact applied to the carrier during the frictional charging of the developer is reduced, thereby preventing the damage of the coat layer.
[0082]
In addition, by using a cross-linked resin of an acrylic resin and an amino resin as the coat layer resin, it is possible to prevent the fusion between resins, so-called blocking, which tends to occur when using an acrylic resin alone while maintaining appropriate elasticity. It is even more preferable because it can be performed.
As the amino resin, a conventionally known amino resin can be used. Among them, a guanamine resin or a melamine resin is more preferably used because the charge imparting ability of the carrier can be improved. If it is necessary to appropriately control the charge-imparting ability of the carrier, a guanamine resin and / or a melamine resin may be used in combination with another amino resin.
[0083]
Furthermore, since the above-mentioned coat layer resin contains a silicone portion as a constituent unit, the surface energy itself of the carrier surface can be reduced, and the generation of toner spent can be suppressed. The properties themselves can be maintained for a longer period.
The constituent unit of the silicone portion preferably contains at least one of a methyltrisiloxane unit, a dimethyldisiloxane unit, and a trimethylsiloxane unit, and the silicone portion may be chemically bonded to another coat layer resin. Good, it may be in a blended state, or may be in a multilayer form. In the case of a multilayer structure, the silicone portion is preferably located at least on the outermost layer.
[0084]
In the case of a blend or a multilayer structure, it is preferable to use a silicone resin and / or a modified product thereof. For example, among any conventionally known silicone resins, a heat-sensitive resin having a three-dimensional network structure can be used. A curable silicone resin can be used, and examples thereof include a straight silicone having only an organosiloxane bond represented by the following general formula (2) and a silicone resin modified with alkyd, polyester, epoxy, urethane, or the like.
Embedded image

(In the above formula, R1 is a hydrogen atom, an alkyl group having 1 to 4 carbon atoms or a phenyl group, R2 and R3 are a hydrogen group, an alkoxy group having 1 to 4 carbon atoms, a phenyl group, a phenoxy group, a 2 carbon atom. Or an alkenyloxy group having 2 to 4 carbon atoms, a hydroxy group, a carboxyl group, an ethylene oxide group, a glycidyl group, or a group represented by the following general formula (3).
Embedded image

In the above formula, R4 and R5 are a hydroxy group, a carboxyl group, an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, an alkenyl group having 2 to 4 carbon atoms, and an alkyl group having 2 to 4 carbon atoms. An alkenyloxy group, a phenyl group, a phenoxy group, k, l, m, n, o, and p represent an integer of 1 or more. )
Each of the above substituents may have a substituent such as a hydroxy group, a carboxyl group, an alkyl group, a phenyl group, or a halogen atom, in addition to the unsubstituted one.
[0085]
Further, the coating layer preferably contains conductive or semiconductive particles having a number average diameter smaller than the number average diameter of the particles forming the surface irregularities, such as the insulating inorganic particles described above. By including such conductive or semiconductive particles in the coating layer, it becomes easy to independently control the function of forming the surface unevenness and the function of controlling the resistance of the carrier.
[0086]
Conventionally known conductive or semiconductive particles may be used. Examples of the conductive particles include metals such as iron, gold and copper; iron oxides such as ferrite and magnetite; bismuth oxide, molybdenum oxide and the like. Oxides; ionic conductors such as silver iodide and β-alumina; and pigments such as carbon black. Examples of semiconductive particles include barium titanate, strontium titanate, and lead lanthanum titanate. Or a defect formed by oxygen (a Frenkel semiconductor) or an impurity formed by a titanium oxide, zinc oxide or tin oxide (a Schottky semiconductor).
Of these, furnace black or acetylene black, which is one of the carbon blacks, is particularly preferably used because the conductivity can be effectively adjusted by adding a small amount of low-resistance fine powder.
These low-resistance fine powders need to be smaller than the particles for forming the carrier surface irregularities, but preferably have a number average diameter of about 0.01 to 1 μm, and are based on 100 parts by weight of the coating layer resin. It is preferable to add 2 to 30 parts by weight.
[0087]
Further, the weight of the toner in the weight of the developer is preferably from 2 to 12% by weight, and more preferably from 2.5 to 10% by weight.
[0088]
The carrier used in the present invention is not limited to other materials, and conventionally known carriers can be used. Examples of the inorganic / metal magnetic particles that can be used for the core material of the carrier particles include iron and cobalt. , Nickel and the like; alloys and compounds such as magnetite, hematite, ferrite and the like, but are not limited thereto. These magnetic particles may be used in any core material form such as single crystal / amorphous particles, single / composite sintered bodies, and particles obtained by dispersing single / composite particles in a polymer such as a resin. good. In addition, in order to achieve both the magnetic properties of the carrier particles and the dispersibility of the magnetic particles, the magnetic particles include particles having a size of about 0.5 to 10 μm. Things are preferred.
[0089]
In the case of using resin particles in which magnetic powder is dispersed, examples of the resin forming the core material particles of the carrier particles include polyolefin resins such as polyethylene, polypropylene, chlorinated polyethylene, and chlorosulfonated polyethylene; polystyrene, acrylic resins ( For example, polymethyl methacrylate), polyacrylonitrile, polyvinyl acetate, polyvinyl alcohol, polyvinyl butyral, polyvinyl chloride, polyvinyl carbazole, polyvinyl ether, polyvinyl ketone, and other polyvinyl and polyvinylidene resins; vinyl chloride-vinyl acetate copolymer; polytetra Fluororesins such as fluoroethylene, polyvinyl fluoride, polyvinylidene fluoride and polychlorotrifluoroethylene; polyamides; polyesters; polyurethanes; Including but not limited to.
[0090]
Coupling agents such as silane coupling agents and titanium coupling agents are added to the magnetic material-dispersed core material particles as auxiliaries for the purpose of improving their adhesion and improving the dispersibility of the resistance control material. You may.
[0091]
More preferably, these core materials have a particle size of about 20 to 200 μm.
[0092]
As a method for forming the coat layer, a conventionally known method can be used, and a coat layer forming liquid may be applied to the surface of the core material particles by a method such as a spraying method and a dipping method. Further, the thickness of the coat layer is preferably 0.01 to 20 μm, and more preferably about 0.3 to 10 μm.
Further, it is preferable to accelerate the polymerization reaction of the coat layer by heating the carrier particles on which the coat layer is formed as described above.
The heating and holding of these carrier particles may be performed in the coating apparatus after forming the coat layer, or may be performed by another heating means such as a normal electric furnace or a firing kiln after forming the coat layer. .
Further, since the heating and holding temperature varies depending on the coating layer material to be used, it is not absolutely determined, but a temperature of about 120 to 350 ° C. is preferably used. At this time, the heating and holding temperature is preferably a temperature equal to or lower than the decomposition temperature of the coat layer resin, and more preferably the upper limit temperature up to about 200 ° C.
Further, the heating and holding time is preferably about 5 to 120 minutes.
[0093]
【Example】
Hereinafter, the present invention will be further described with reference to examples, but the present invention is not limited thereto.
Parts represent parts by weight.
[0094]
Example 1
(Binder resin synthesis example 1)
In a reaction vessel equipped with a cooling pipe, a stirrer and a nitrogen introduction pipe, 724 parts of bisphenol A ethylene oxide 2 mol adduct, 276 parts of isophthalic acid and 2 parts of dibutyltin oxide were put, and reacted at 230 ° C. under normal pressure for 8 hours. After further reacting at a reduced pressure of 10 to 15 mmHg for 5 hours, the mixture was cooled to 160 ° C., and 32 parts of phthalic anhydride was added thereto and reacted for 2 hours.
Next, the mixture was cooled to 80 ° C. and reacted with 188 parts of isophorone diisocyanate in ethyl acetate for 2 hours to obtain an isocyanate-containing prepolymer (P1).
Next, 267 parts of the prepolymer (P1) and 14 parts of isophoronediamine were reacted at 50 ° C. for 2 hours to obtain a urea-modified polyester (U1) having a weight average molecular weight of 64000.
In the same manner as above, 724 parts of bisphenol A ethylene oxide 2 mol adduct and 276 parts of terephthalic acid are polycondensed at 230 ° C. for 8 hours under normal pressure, and then reacted at a reduced pressure of 10 to 15 mmHg for 5 hours to modify the peak molecular weight to 5,000. Untreated polyester (E1) was obtained.
200 parts of urea-modified polyester (U1) and 800 parts of unmodified polyester (E1) are dissolved and mixed in 2,000 parts of a mixed solvent of ethyl acetate / MEK (1/1), and ethyl acetate / MEK of the binder resin (B1) is mixed. A solution was obtained.
A part of the resin was dried under reduced pressure to isolate the binder resin (B1). Tg was 62 ° C.
[0095]

The above composition was placed in a 1 L four-necked round bottom flask equipped with a thermometer, a stirrer, a condenser, and a nitrogen gas inlet tube. The flask was set on a mantle heater, and nitrogen gas was supplied from the nitrogen gas inlet tube. After the introduction, the temperature was raised while keeping the inside of the flask under an inert atmosphere, and then 0.05 g of dibutyltin oxide was added to carry out the reaction while maintaining the temperature at 200 ° C. to obtain a polyester A.
The peak molecular weight of this polyester A was 4,200, and the glass transition point was 59.4 ° C.
[0096]

The above raw materials were mixed with a Henschel mixer to obtain a mixture in which water was permeated into the pigment aggregate. This was kneaded for 45 minutes with two rolls set at a roll surface temperature of 130 ° C., and pulverized with a pulverizer to a size of 1 mmφ to obtain a master batch (M1).
[0097]
(Toner Production Example 1)
In a beaker, 240 parts of the above ethyl acetate / MEK solution of the binder resin (B1), 20 parts of pentaerythritol tetrabehenate (melting point: 81 ° C., melt viscosity: 25 cps), and 8 parts of a master batch (M1) are placed at 60 ° C. The mixture was stirred with a TK homomixer at 12,000 rpm to uniformly dissolve and disperse, thereby preparing a toner material liquid.
In a beaker, 706 parts of ion-exchanged water, 294 parts of a 10% suspension of hydroxyapatite (Supatite 10 manufactured by Nippon Chemical Industry Co., Ltd.) and 0.2 part of sodium dodecylbenzenesulfonate were put and uniformly dissolved.
Then, the temperature was raised to 60 ° C., and the above-mentioned toner material solution was charged and stirred for 10 minutes while stirring at 12,000 rpm with a TK homomixer.
Then, the mixture was transferred to a kolben equipped with a stir bar and a thermometer, heated to 98 ° C. to remove the solvent, separated by filtration, washed, dried, and then subjected to air classification to obtain toner particles. Then, 0.5 part of hydrophobic silica and 0.5 part of hydrophobic titanium oxide were mixed with 100 parts of the toner particles using a Henschel mixer to obtain a toner (T1).
[0098]
An ultra-thin section of the toner (T1) was prepared, and a cross-sectional photograph (magnification × 100,000) of the toner was taken using a transmission electron microscope (H-9000H manufactured by Hitachi, Ltd.), and randomly selected from the photograph. The average value was determined from the dispersion diameters of 100 colorant portions. Here, the dispersion diameter of one particle was the average of the longest diameter and the shortest diameter, and in the case of an aggregated state, the aggregate itself was regarded as one particle.
The average dispersion particle size of the colorant was 0.39 μm. The colorant having a dispersed particle size of 0.7 μm or more was 4.4% by number.
Next, the particle diameter of the toner (T1) was measured with an aperture diameter of 100 μm using a particle size analyzer “Coulter Counter TA2” manufactured by Coulter Electronics Co., Ltd., and the volume average particle diameter (Dv) = 6.3 μm and the number average particle diameter The diameter (Dn) was 5.0 μm, and Dv / Dn was 1.26.
Subsequently, the circularity of the toner (T1) was measured as an average circularity by a flow-type particle image analyzer FPIA-1000 (manufactured by Toa Medical Electronics Co., Ltd.). The measurement was performed by adding 0.1 to 0.5 ml of a surfactant (alkylbenzenesulfonate) as a dispersant to 100 to 150 ml of water from which impure solids had been removed in advance, and further adding 0.1 ml of a measurement sample to the apparatus. Approximately 0.5 g was added, and a dispersion treatment was performed for about 1 to 3 minutes with an ultrasonic disperser, and a measurement liquid whose dispersion liquid concentration was adjusted to 3000 to 10,000 particles / μl was set.
The average circularity of the obtained toner (T1) was 0.95.
[0099]

The above formulation was dispersed with a homomixer for 30 minutes to prepare a coating solution for forming a coat layer.
This was coated on the surface of 5000 parts of spherical ferrite particles having a weight average particle size of 50 μm by a fluidized bed spray coater, and then heated at 150 ° C. for 1 hour to obtain a carrier (C1).
When the surface of the carrier (C1) was observed at a magnification of 2000 times with a scanning electron microscope, irregularities derived from alumina were formed on the surface, and the average height difference of the carrier surface irregularities measured without contact using a laser microscope was , 0.4 μm.
The cross section of the carrier was observed with a transmission electron microscope, and the average value of the film thickness of the coating film covering the carrier surface was defined as the film thickness. The thickness of the carrier (C1) was 0.16 μm.
[0100]
Next, 930 parts of the carrier (C1) and 70 parts of the toner (T1) were mixed for 2 minutes using a Turbula mixer to obtain a two-component developer.
[0101]
Example 2
(Toner Production Example 2)
The coloring agent is C.I. I. Pigment Yellow 185 was used in the same manner as in Example 1 except that the raw pigment was changed to 4 parts.
Then, 0.5 part of hydrophobic silica and 0.5 part of hydrophobic titanium oxide were mixed with 100 parts of the toner particles using a Henschel mixer to obtain a toner (T2).
The volume average particle diameter (Dv) of the toner (T2) was 6.0 μm, the number average particle diameter (Dn) was 5.0 μm, and Dv / Dn was 1.20.
The average dispersed particle size of the colorant was 0.62 μm, and the colorant having a dispersed particle size of 0.7 μm or more was 8.7% by number.
A two-component developer was obtained in the same manner as in Example 1 except that the toner (T2) was used.
[0102]
Example 3
(Toner Production Example 3)
210 parts of the TK homomixer-dispersed toner composition obtained in Example 1 was diluted with 576 parts of ethyl acetate. 210 parts of the diluted dispersion was treated in the same manner to form particles after emulsification.
After that, toner particles were obtained in the same manner as in Example 1.
Then, 0.5 part of hydrophobic silica and 0.5 part of hydrophobic titanium oxide were mixed with 100 parts of the toner particles using a Henschel mixer to obtain a toner (T3).
The volume average particle diameter (Dv) of the toner (T3) was 3.8 μm, the number average particle diameter (Dn) was 3.2 μm, and Dv / Dn was 1.19.
The average dispersed particle size of the colorant was 0.33 μm, and 3.6% by number of colorants had a dispersed particle size of 0.7 μm or more.
A two-component developer was obtained in the same manner as in Example 1 except that the toner (T3) was used.
[0103]
Example 4
(Toner Production Example 4)
When the binder resin (B1) in Example 1 was dissolved and mixed in a mixed solvent of ethyl acetate / MEK (1/1), the amount of the mixed solvent was changed to 1200 parts, and 240 parts of this solution was used in producing the toner. In the same manner as in Example 1, toner particles were obtained.
Then, 0.5 parts of hydrophobic silica and 0.5 parts of hydrophobic titanium oxide were mixed with 100 parts of the toner particles using a Henschel mixer to obtain a toner (T4) of the present invention.
The volume average particle diameter (Dv) of the toner (T4) was 8.5 μm, the number average particle diameter (Dn) was 7.1 μm, and Dv / Dn was 1.20.
The average dispersed particle size of the colorant was 0.51 μm, and the number of the colorants having a dispersed particle size of 0.7 μm or more was 4.9% by number.
A two-component developer was obtained in the same manner as in Example 1 except that the toner (T4) was used.
[0104]
Example 5
(Toner Production Example 5)
Toner particles were obtained in the same manner as in Example 1, except that the melting temperature and the dispersion temperature were changed to 50 ° C.
Then, 0.5 part of hydrophobic silica and 0.5 part of hydrophobic titanium oxide were mixed with 100 parts of the toner particles using a Henschel mixer to obtain a toner (T5) of the present invention.
The volume average particle diameter (Dv) of the toner (T5) was 5.6 μm, the number average particle diameter (Dn) was 4.7 μm, and Dv / Dn was 1.19.
The average dispersed particle diameter of the colorant was 0.41 μm, and 3.5% by number of colorants had a dispersed particle diameter of 0.7 μm or more.
A two-component developer was obtained in the same manner as in Example 1 except that the toner (T5) was used.
[0105]
Examples 6 to 10

The above formulation was dispersed with a homomixer for 30 minutes to prepare a coating solution for forming a coat layer.
This was coated on the surface of 5000 parts of spherical ferrite particles having a weight average particle diameter of 50 μm by a fluidized bed spray coater, and then heated at 150 ° C. for 1 hour to obtain a carrier (C2).
The average height difference between the surface irregularities of the carrier (C2) was 0.2 μm.
The thickness of the carrier (C2) was 0.12 μm.
Subsequently, the carrier (C2) and each of the toners (T1) to (T5) of Examples 1 to 5 were combined to prepare a yellow two-component developer of the present invention (Examples 6 to 10).
[0106]
Comparative Example 1

The above raw materials were mixed with a Henschel mixer to obtain a mixture in which water was permeated into the pigment aggregate. This was kneaded for 45 minutes with two rolls set at a roll surface temperature of 130 ° C., and pulverized with a pulverizer to a size of 1 mmφ to obtain a master batch (M2).
[0107]
(Toner Production Example 6)
Toner particles were obtained in the same manner as in Example 1, except that the colorant was changed to 8 parts of the master batch (M2).
Then, 0.5 part of hydrophobic silica and 0.5 part of hydrophobic titanium oxide were mixed with 100 parts of the toner particles using a Henschel mixer to obtain a comparative toner (T6).
The volume average particle diameter (Dv) of the toner (T6) was 6.5 μm, the number average particle diameter (Dn) was 5.4 μm, and Dv / Dn was 1.20.
The average dispersed particle size of the colorant was 0.5 μm, and 4.5% by number of colorants having a dispersed particle size of 0.7 μm or more.
A two-component developer was obtained in the same manner as in Example 1 except that the toner (T6) was used.
[0108]
Comparative Example 2

The mixture was kneaded at 100 ° C. using a twin-screw extruder according to the above formulation, pulverized and classified to obtain toner particles.
Then, 0.5 part of hydrophobic silica and 0.5 part of hydrophobic titanium oxide were mixed with 100 parts of the toner particles using a Henschel mixer to obtain a comparative toner (T7).
The volume average particle diameter (Dv) of the toner (T7) was 8.7 μm, the number average particle diameter (Dn) was 6.7 μm, and Dv / Dn was 1.30.
The pigment-based colorant had an average dispersed particle size of 0.62 μm, and the number% of 0.7 μm or more was 5.8%.
A two-component developer was obtained in the same manner as in Example 1, except that the toner (T7) was used.
[0109]
Comparative Example 3

The above formulation was dispersed with a homomixer for 30 minutes to prepare a coating solution for forming a coat layer.
This was coated on the surface of 5000 parts of spherical ferrite particles having a weight average particle size of 50 μm by a fluidized bed spray coater, and then heated at 150 ° C. for 1 hour to obtain a carrier (C3).
The average height difference of the carrier (C3) surface unevenness was 0.06 μm, which was due to the unevenness of the core material.
The thickness of the carrier (C3) was 0.11 μm.
A two-component developer was obtained in the same manner as in Example 1 except that the carrier (C3) was used.
[0110]
[Physical property measurement and evaluation methods]
Tables 1 and 2 show the physical properties of the toner and carrier obtained in each of Examples and Comparative Examples.
Further, using the two-component developer obtained in each of the examples and comparative examples, a continuous image drawing test of 200,000 sheets of A4 size, 5% image area ratio original was performed by using a modified version of Ricoh IPSIO color8000, The image quality and the charge amount of the developer were evaluated.
As the image evaluation, the glossiness, haze, light resistance, image density, and background fog of the solid image portion were evaluated by the following methods. At the same time, the occurrence of other defects was observed. The evaluation results are shown in Tables 3 and 4.
[0111]
(Glossiness)
In the above monochrome image sample, the glossiness of the sample when the fixing belt surface temperature was 160 ° C. was measured by a gloss meter manufactured by Nippon Denshoku Industries Co., Ltd. at an incident angle of 60 °. The glossiness increases as the value increases. As a full-color copy image, moderate gloss is preferred, and about 10 to 30% is preferred. The evaluation of the glossiness was performed only on the initial image.
[0112]
(Haze degree)
Using the above evaluator, a yellow single-color image sample was used as a transfer paper using an RHP OHP sheet (type PPC-DX), and the haze of the sample at a fixing temperature of 160 ° C. was directly read by Suga Test Instruments Co., Ltd. The haze was measured using a computer HGM-2DP. The evaluation of the haze degree was performed only on the initial image.
The haze is also referred to as haze, and is measured as a measure of the transparency of the toner. The lower the value, the higher the transparency, and the better the color developability when using an OHP sheet. Further, the value of the haze degree that shows good color developability is preferably 30% or less, particularly preferably 20% or less.
[0113]
(Lightfastness)
A solid image of a single color of yellow was prepared, and the fading degree was visually evaluated with a fade meter using a xenon lamp for 100 hours with light irradiation. The light fastness was evaluated only for the initial image.
Lightfastness rank
◎: extremely excellent
○: No problem in practical use
△: allowable level
×: Cannot be used
(△ and above are OK)
[0114]
(Image density)
After outputting the solid image, the image density was measured by X-Rite (manufactured by X-Rite). As evaluation values, five independent points in a solid image were measured, and the average value was used.
[0115]
(Surface fog)
The degree of toner contamination on the background of the transfer paper was visually evaluated.
Ground fog rank
◎: extremely excellent
○: No problem in practical use
△: allowable level
×: Cannot be used
(△ and above are OK)
[0116]
(Charge amount)
The measurement of the toner charge amount was performed by a so-called blow-off method using an electrometer (610C; manufactured by Kesley) to measure the charge amount while separating the toner and the carrier by an air current.
As for the charge amount, the toner in the developer is once removed by an air current, and only the carrier is taken out. The same toner as that used for the developer is charged again so as to have a toner concentration of 7% by weight, and stirred for 5 minutes. Thereafter, the obtained developer for measuring the charge amount was subjected to blow-off measurement.
[0117]
As a result of these evaluations, good image quality was obtained both at the initial stage and after 200,000 copies, and it was found that the yellow developer for electrostatic image development of the present invention was useful in both image quality and life.
[0118]
[Table 1]

[0119]
[Table 2]

[0120]
[Table 3]

[0121]
[Table 4]

[0122]
【The invention's effect】
According to the present invention, as is clear from the comparison between the examples and the comparative examples, the charge amount is stable with time, image deterioration is extremely small, and the characteristics necessary for obtaining a stable image are obtained. It is possible to provide a yellow developer for developing an electrostatic image, which is effective for obtaining a high-definition, high-resolution, high-quality image having high light resistance and high light resistance.
Further, according to the present invention, it is possible to provide an image forming method using the yellow developer for developing an electrostatic image, and an image forming apparatus loaded with the toner.

Claims (10)

A yellow developer for developing an electrostatic image, which is obtained by mixing a toner having at least a binder resin and a yellow colorant, and a carrier having a coating layer containing at least a resin and particles on the surface of a magnetic core material, wherein the carrier is A carrier having a surface having irregularities derived from particles contained in a coat layer, wherein the toner contains, as a binder resin, a modified polyester resin capable of reacting with a compound having an active hydrogen group in an organic solvent. A toner obtained by dissolving or dispersing the composition, and then dispersing the dissolved or dispersed product in an aqueous medium to react with a compound having an active hydrogen group, and removing the solvent from the obtained dispersion. In addition, the yellow colorant is a compound represented by the following structural formula (1).

2. The yellow developer according to claim 1, wherein the dispersed particle diameter of the yellow colorant in the toner is 0.5 [mu] m or less in number average diameter. The yellow developer for electrostatic image development according to claim 1, wherein a composition obtained by previously kneading a binder resin and a yellow colorant with water is used as the colorant. The volume average particle diameter of the toner particles is 4 to 8 μm, and the ratio of the volume average particle diameter to the number average particle diameter (volume average particle diameter / number average particle diameter) is 1.25 or less. The yellow developer for developing an electrostatic image according to claim 1. The yellow developer according to any one of claims 1 to 4, wherein the toner particles have an average circularity of 0.90 to 0.99. The yellow developer according to any one of claims 1 to 5, wherein an average height difference of the carrier surface irregularities is 0.1 to 2.0 µm. The ratio of the particle diameter (D) of the particles contained in the carrier coat layer to the film thickness (h) of the coat layer resin is 1 <[D / h] <10. 7. The yellow developer for developing an electrostatic image according to any one of 1 to 6. The yellow developer according to any one of claims 1 to 7, wherein the total content of the particles contained in the carrier coat layer is 20 to 95% by weight of the composition of the coat layer. A color image forming method, comprising using the yellow developer for developing an electrostatic charge image according to claim 1. A color image forming apparatus comprising the yellow developer for developing an electrostatic image according to any one of claims 1 to 8.