JP2004141080A

JP2004141080A - Filter for use in aquarium fish basin

Info

Publication number: JP2004141080A
Application number: JP2002310650A
Authority: JP
Inventors: Yuko Yamamoto; 山本　優子
Original assignee: Kureha Ltd
Current assignee: Kureha Ltd
Priority date: 2002-10-25
Filing date: 2002-10-25
Publication date: 2004-05-20

Abstract

<P>PROBLEM TO BE SOLVED: To provide a filter for use in aquarium fish basins causing no death of aquarium fishes due to bubbling and/or water pollution effected by any auxiliary and sufficient in mechanical strength retention. <P>SOLUTION: The filter is obtained by laminating at least two fiber layers with each other, mutually interlacing the constituent fibers and integratedly bonding the layers together via a binder. The binder contains no water-soluble auxiliary, its content being 10-40 wt.%, on a solid basis, of the total basis weight of this filter. This filter, when installed in an aquarium fish basin, gives a temperature gradient in a coarse-to-dense fashion from the inlet to outlet side of water. <P>COPYRIGHT: (C)2004,JPO

Description

【０００１】
【発明の属する技術分野】
本発明は特に観賞魚用水槽に用いて好適な水槽用フィルターに関するものである。
【０００２】
【従来の技術】
観賞魚用水槽に用いる濾過装置としては、水槽内に砂利を敷き詰めた底面濾過方式や水槽内の水を循環させながら浄化する水中濾過方式等がある。
このうち、水中濾過方式においては従来よりフィルター材として厚さ５０ｍｍ程度の固綿や、更に該固綿の中に活性炭や他鉱石あるいはイオン交換繊維や活性炭素繊維などを使用したものが用いられているが、近時、繊維ウエブを利用したウールマットや５ｍｍ厚さの２層でプリーツ折りした不織布タイプのもの、あるいはスポンジなどが夫々、適宜形状に形成されて用いられている。
なかでも、不織布はフィルターとして広く一般に用いられており、ニードリングし、又はせずして構成繊維を互いにバインダーを用いて接着一体化することによって形成されている。
【０００３】
【発明が解決しようとする課題】
ところが、上記バインダーを用いて繊維層構成繊維を接着し、一体化したものは、バインダーに界面活性剤や乳化剤、触媒、更に発泡剤、安定剤、黄変防止剤などの助剤が含まれており、これを水中濾過に用いたとき、それら助剤の成分が水に溶けて浮遊することにより水に泡立ちが発生したり、水質が汚濁して折角の観賞魚が死亡するという事態が生じた。
またバインダーに代わり低融点繊維を溶融し、融着一体化すれば水質汚濁は一部避けられるとしても、苔，藻，微生物などの影響により低融点成分がなくなり、強力を保持することができないという問題があった。
【０００４】
本発明は上述の如き実情に対処し、特に水に溶ける助剤を使用しないバインダーの使用を見出すことにより、観賞魚用の水槽に利用したとき、水中に乳化剤等の溶出がなく、水質汚濁を防止せしめると共に、バインダー使用によりフィルターの強力を保持せしめて観賞魚用水槽に使用し循環水濾過に好適なフィルター材を提供することを目的とするものである。
【０００５】
【課題を解決するための手段】
即ち、上記目的に適合する本発明は、基本的に少なくとも２層の繊維層よりなり、構成繊維が互いに交絡され、バインダーにより接着一体化されていて、水槽中に設置されたとき、水槽内を循環する水の入口側から出口側に粗から密への密度勾配を有している観賞魚用水槽に用いるフィルターであって、該フィルターは総目付に対して１０〜４０重量％のバインダーを含み、かつ該バインダーには水に溶ける乳化剤等の助剤が使用されていないことを特徴とする。
【０００６】
ここで、繊維層を構成する繊維としては、ポリエステル繊維，ポリアクリル繊維，レーヨン繊維から選ばれた１種又は２種以上の使用が好ましく、また構成繊維間を接着するバインダーとしてはソープフリー乳化重合によって作られたアクリル酸エステル，ＳＢＲ，ＰＳ，ＮＢＲから選ばれた少なくとも１種が好適である。
なお、繊維層への上記バインダー付与手段としては表面処理，含浸処理又は噴霧処理が可能であり、適宜適用される。
【０００７】
【発明の実施の形態】
以下、更に本発明の具体的な実施の態様について説明する。
【０００８】
本発明は前述の如く観賞魚用の水槽に用いられるフィルターである。
フィルターは単層又は複数層の繊維ウエブ層をニードリングするか、又はせずして、構成繊維を互いに交絡すると共に、バインダーにより接着一体化することによって基本的構成が形成されている。
【０００９】
そして、上記フィルターは観賞魚用水槽内に配設したとき、水槽内を循環する水の入口側から出口側に繊維密度が粗から密への密度勾配を有しており、濾過性能の低下を阻止している。
ここで、上記フィルターを構成する繊維層に使用する繊維としては、ポリエステル繊維（ＰＥＴ），ポリアクリル繊維（ＰＡＮ）等の合成繊維やレーヨンなどであり、特に拘泥されないが、とりわけポリエステル繊維とレーヨン繊維との混綿は好ましく、就中、レーヨン繊維を少なくとも２０％含有した混綿は最も好適である。
【００１０】
レーヨン繊維は親水性繊維であるために、繊維層の積層後に交絡処理し、更にバインダーによる接着処理を行うに際し、親水性繊維であるレーヨン繊維の存在により、繊維間の接着を良好ならしめる。
殊に、ポリエステル繊維１００重量％では積層不織布の厚さ調整が困難であるのに対し、レーヨンの存在は厚さ調整が容易にできる利点を有すると共に、更に使用後のフィルターの洗浄にあたり、レーヨン繊維の存在により水分との関係で伸縮を起こし、その結果、捕集した塵埃を落とし易く、また乾燥後の形態をよくする効果もあることが知見されている。
【００１１】
なお、混合する合成繊維も上記ポリエステル繊維に限らず、ナイロン，ポリアクリル繊維，ポリオレフィン系繊維なども使用可能であり、適宜混合し得ることは云うまでもない。
しかし、低融点成分を含むサイドバイサイド又は芯鞘構造の複合繊維の使用は水槽内における苔，藻，微生物の影響により、低融点成分がなくなり、強力保持が難しくなるので好ましくない。
【００１２】
いずれにせよ、上記フィルターを構成する繊維は水槽内を汚濁又は泡立ちを発生させないことが重要であり、水中に浸出しない限り繊維に消臭，抗菌加工等を施すことも可能である。
そして、上記フィルターは、泡立ちが発生しないこと、汚濁しないことに加え、更に使用に際し強度の低下を来さず、強度を維持することが求められる。
そのため、用いるバインダーの種類や量を選定することも頗る重要なことである。
バインダーは水中での白濁，泡立ち防止のため、水中に溶出する成分を含んでいないことが条件であり、従って乳化剤や触媒等、あるいは発泡剤，安定剤，黄変防止剤，樹脂の界面活性剤等は水に溶ける成分を使用していないものに限られる。
【００１３】
かかるバインダーとしては、ソープフリー乳化重合によって作られたものが好ましく、該タイプのアクリル酸エステル，ＳＢＲ，ＰＳ，ＮＢＲなどが使用可能であり、水に溶ける乳化剤等を使用しないものが用いられる。なかでもソープフリー乳化重合によって作られたアクリル酸エステルは最も実用的である。
しかも、バインダーの使用は一方において強度を向上させる上に重要であり、総目付（繊維目付＋バインダー目付）に対し１０〜４０重量％の使用が最も有効である。
１０重量％以下ではフィルター強度を保持することが困難であり、４０重量％以上では強度綿では有効であるが、通水量が不足し、またコスト不利となるので、１０〜４０重量％の範囲が最も好適である。
【００１４】
かくして上記バインダーの使用により、使用時に泡立ちがないこと、強力低下がないこと、ある程度の通水量を有することの条件を満足し、効果的な観賞魚用水槽に用いるフィルターを得ることが出来る。
【００１５】
【実施例】
以下、更に本発明の実施例を掲げる。
【００１６】
実施例１
上層に６デニールのポリエステル繊維８０％と３デニールのポリエステル繊維２０％からなる目付１５０ｇ／ｍ^２の繊維層を配し、下層に２デニールのポリエステル繊維８０％と、３デニールのレーヨン繊維２０％とからなる目付５０ｇ／ｍ^２の繊維層を配して積層し、交絡の後、バインダーとしてソープフリー乳化重合によるアクリル酸エステルを用い、繊維層表面に固形分５０ｇ／ｍ^２（２０重量％）で付与し、総目付２５０ｇ／ｍ^２のフィルターを得た。
【００１７】
実施例２
上層に６デニールのポリエステル繊維８０％と３デニールのポリエステル繊維２０％からなる目付１５０ｇ／ｍ^２の繊維層を配し、下層に２デニールのポリエステル繊維８０％と、３デニールのレーヨン繊維２０％とからなる目付１００ｇ／ｍ^２の繊維層を配して積層し、交絡の後、バインダーとしてソープフリー乳化十微雨によるアクリル酸エステルを用い、繊維層表面に固形分６５ｇ／ｍ^２で付与すると共に、含浸により固形分１５ｇ／ｍ^２（合計２４．２重量％）付与して総目付３３０ｇ／ｍ^２のフィルターを得た。
【００１８】
実施例３
上層に６デニールのポリエステル繊維１００％からなる目付１００ｇ／ｍ^２の繊維層、中層に６デニールのポリエステル繊維７０％と２デニールのポリエステル繊維３０％からなる目付１００ｇ／ｍ^２の繊維層を配し、下層に２デニールのポリエステル繊維７５％と、３デニールのレーヨン繊維２５％とからなる目付５０ｇ／ｍ^２の繊維層を配して積層し、交絡の後、バインダーとしてソープフリー乳化重合によるアクリル酸エステルを用い、繊維層表面に固形分４５ｇ／ｍ^２で付与し、含浸により固形分５ｇ／ｍ^２（合計１６．７重量％）付与して総目付３００ｇ／ｍ^２のフィルターを得た。
【００１９】
一方、比較のため下記の各比較例により、比較フィルターを得た。
比較例１
実施例１と同じ繊維層構成を用いバインダーとしてソープフリー乳化重合によらないアクリル酸エステルを表面付与により固形分５０ｇ／ｍ^２（２０重量％）付与し、総目付２５０ｇ／ｍ^２の比較フィルターを得た。
【００２０】
比較例２
上層に６デニールのポリエステル繊維５０％と４デニールの低融点ポリエステル成分を含む複合ポリエステルポリエステル繊維５０％とからなる目付１５０ｇ／ｍ^２の繊維層を配し、下層に３デニールのポリエステル繊維５０％と、２デニールの低融点ポリエステル成分を含む複合ポリエステル繊維５０％とからなる目付１００ｇ／ｍ^２の繊維層を配して積層し、パインダーを用いることなく交絡のみで総目付２５０ｇ／ｍ^２のフィルターを得た。
【００２１】
比較例３
上層に６デニールのポリエステル繊維５０％と４デニールの低融点ポリエステル成分を含む複合ポリエステル繊維５０％とからなる目付１５０ｇ／ｍ^２の繊維層を配し、下層に３デニールのポリエステル繊維５０％と、２デニールの低融点ポリエステル成分を含む複合ポリエステル繊維５０％とからなる目付８０ｇ／ｍ^２の繊維層を配して積層し、交絡の後、バインダーとしてソープフリー乳化重合によるアクリル酸エステルを用い、噴霧方式により繊維層表面に固形分２０ｇ／ｍ^２（８重量％）を付与し、総目付２５０ｇ／ｍ^２のフィルターを得た。
【００２２】
以上の実施例及び比較例で得られた各フィルターについて、泡立ち性及び使用時の強力維持性を下記により観察，測定した。結果を圧力損失と共に表１に示す。
泡立ち性；１リットルのビーカーにフィルターを取り付けたエアー発生器を入れて、水道水を入れ、３０分エアーを発生させ、水面の泡立ち性，泡の種類，泡の消え方を観察する。
使用時の強力維持性；金魚がいる寸法の水槽中にフィルターを取り付けたエアー発生器を入れ、３ケ月間運転させ、使用前後の強力を測定する。
【００２３】
【表１】

【００２４】
上記表より本発明に係るフィルターは各比較例に比し発生した泡立ちが直ぐに消え、また強力維持及び圧力損失においても殆ど代わらないことが分かる。
【００２５】
【発明の効果】
本発明は以上のように、少なくとも２層の繊維層を、その構成繊維を互いに交絡し、バインダーにより接着一体化すると共に、水槽中に設置したとき、水槽内を循環する水の入口側から出口側に粗から密への密度勾配を有している観賞魚用水槽に用いるフィルターにおいて総目付に対して１０〜４０重量％のバインダーを付与すると共に、該バインダーを水に溶ける乳化剤等の助剤が使用されていないものとしたものであり、バインダーに水に溶ける助剤が含まれていないため、水槽中においても泡立ちの発生がなく、また、助剤の白濁成分が溶出することがないため、水槽内を汚濁することもなく、従って水質汚濁による観賞魚の死亡は回避され、観賞魚用水槽の循環水用フィルターとして顕著な効果を有している。しかも、本発明フィルターはバインダーが所定の割合、付与されていることから強度の低下を来すことがなく、充分、強度を保持でき、通水量も確保できる実効を有している。[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention particularly relates to an aquarium filter suitable for use in an aquarium fish tank.
[0002]
[Prior art]
As a filtering device used for an aquarium fish tank, there are a bottom filtration method in which gravel is spread in the water tank and an underwater filtration method in which water in the water tank is circulated for purification.
Among them, in the underwater filtration method, conventionally, as a filter material, a solid cotton having a thickness of about 50 mm, and further, those using activated carbon, other ores, ion exchange fibers, activated carbon fibers, or the like in the solid cotton have been used. Recently, a wool mat using a fiber web, a nonwoven fabric type pleated with two layers having a thickness of 5 mm, a sponge, and the like have been used in appropriate shapes.
Above all, a nonwoven fabric is widely and generally used as a filter, and is formed by bonding and integrating constituent fibers to each other with or without needling.
[0003]
[Problems to be solved by the invention]
However, the fiber layer constituting fibers are bonded and integrated using the binder, and the binder contains surfactants, emulsifiers, catalysts, and further auxiliary agents such as a foaming agent, a stabilizer, and an anti-yellowing agent. When this was used for underwater filtration, the components of these auxiliaries dissolved in water and floated, causing bubbling in the water, or polluting the water quality, causing the death of the ornamental fish with a sharp angle .
In addition, if the low-melting fiber is melted instead of the binder and fused and integrated, water pollution can be partially avoided, but the low-melting component disappears due to the influence of moss, algae, microorganisms, etc., and the strength cannot be maintained. There was a problem.
[0004]
The present invention addresses the circumstances as described above, and in particular, by finding use of a binder that does not use a water-soluble auxiliary agent, when used in an aquarium for aquarium fish, there is no elution of an emulsifier or the like in water, and water pollution is reduced. It is an object of the present invention to provide a filter material which can be used for ornamental fish tanks and which is suitable for circulating water filtration while preventing the filter and maintaining the strength of the filter by using a binder.
[0005]
[Means for Solving the Problems]
That is, the present invention that meets the above-mentioned object basically consists of at least two fiber layers, and the constituent fibers are entangled with each other, bonded and integrated with a binder, and when installed in a water tank, the inside of the water tank What is claimed is: 1. A filter for use in an ornamental fish tank having a density gradient from coarse to dense from the inlet side to the outlet side of circulating water, said filter comprising 10 to 40% by weight of a binder based on the total basis weight. The binder is characterized in that no auxiliary agent such as a water-soluble emulsifier is used in the binder.
[0006]
Here, as the fibers constituting the fiber layer, one or more selected from polyester fibers, polyacryl fibers and rayon fibers are preferably used, and soap-free emulsion polymerization is used as a binder for bonding the constituent fibers. At least one selected from the group consisting of acrylic esters, SBR, PS, and NBR prepared by the above method is suitable.
As a means for applying the binder to the fiber layer, a surface treatment, an impregnation treatment or a spray treatment is possible, and is appropriately applied.
[0007]
BEST MODE FOR CARRYING OUT THE INVENTION
Hereinafter, specific embodiments of the present invention will be further described.
[0008]
The present invention is a filter used in an aquarium for aquarium fish as described above.
The basic configuration of the filter is formed by entanglement of the constituent fibers with each other with or without needling a single layer or a plurality of fiber web layers, and by bonding and integrating with a binder.
[0009]
And, when the filter is arranged in the aquarium fish tank, the fiber density has a density gradient from coarse to dense from the inlet side to the outlet side of the water circulating in the tank, which reduces the filtering performance. It is blocking.
Here, the fibers used for the fiber layer constituting the filter are synthetic fibers such as polyester fiber (PET) and polyacryl fiber (PAN) and rayon, and are not particularly limited. Is preferable, and particularly, a cotton blend containing at least 20% of rayon fiber is most preferable.
[0010]
Since rayon fibers are hydrophilic fibers, they are entangled after lamination of the fiber layers, and furthermore, when bonding treatment with a binder is performed, the presence of the rayon fibers, which are hydrophilic fibers, improves the adhesion between the fibers.
In particular, it is difficult to adjust the thickness of the laminated nonwoven fabric with 100% by weight of the polyester fiber, whereas the presence of rayon has the advantage that the thickness can be easily adjusted. It has been found that due to the presence of water, expansion and contraction occurs in relation to moisture, and as a result, the collected dust is easy to drop and also has an effect of improving the form after drying.
[0011]
The synthetic fibers to be mixed are not limited to the above polyester fibers, but nylon, polyacrylic fibers, polyolefin fibers and the like can be used, and it goes without saying that they can be mixed appropriately.
However, the use of a side-by-side or core-sheath composite fiber containing a low-melting component is not preferable because the low-melting component disappears due to the influence of moss, algae, and microorganisms in the water tank, and it becomes difficult to maintain the strength.
[0012]
In any case, it is important that the fibers constituting the filter do not cause contamination or bubbling in the water tank, and the fibers can be subjected to deodorization, antibacterial treatment and the like as long as they do not leach into water.
The filter is required to maintain its strength without causing a bubbling and not being polluted, and furthermore, at the time of use without lowering its strength.
Therefore, it is also very important to select the type and amount of the binder to be used.
In order to prevent clouding and bubbling in water, the binder must not contain components that elute in water. Therefore, emulsifiers, catalysts, etc., or foaming agents, stabilizers, yellowing inhibitors, resin surfactants Etc. are limited to those that do not use water-soluble components.
[0013]
As such a binder, a binder produced by soap-free emulsion polymerization is preferable, and acrylates, SBR, PS, NBR and the like of this type can be used, and a binder which does not use a water-soluble emulsifier or the like is used. Among them, acrylates made by soap-free emulsion polymerization are the most practical.
In addition, the use of a binder is important for improving the strength on the one hand, and the use of 10 to 40% by weight based on the total basis weight (fiber basis weight + binder basis weight) is most effective.
If it is less than 10% by weight, it is difficult to maintain the filter strength, and if it is more than 40% by weight, it is effective to use a strong cotton. However, the amount of water passing is insufficient and the cost is disadvantageous. Most preferred.
[0014]
Thus, the use of the binder satisfies the conditions of no foaming during use, no reduction in strength, and a certain amount of water flow, and it is possible to obtain an effective filter for an aquarium fish tank.
[0015]
【Example】
Hereinafter, examples of the present invention will be further described.
[0016]
Example 1
A fiber layer having a basis weight of 150 g / m ² composed of 80% of 6-denier polyester fiber and 20% of 3-denier polyester fiber is provided in the upper layer, and 80% of 2-denier polyester fiber and 20% of 3-denier rayon fiber are provided in the lower layer. A fiber layer having a basis weight of 50 g / m ² is arranged and laminated, and after entanglement, an acrylic ester by soap-free emulsion polymerization is used as a binder, and a solid content of 50 g / m ² (20% by weight) is applied to the fiber layer surface. This gave a filter having a total basis weight of 250 g / m ² .
[0017]
Example 2
A fiber layer having a basis weight of 150 g / m ² composed of 80% of 6-denier polyester fiber and 20% of 3-denier polyester fiber is provided in the upper layer, and 80% of 2-denier polyester fiber and 20% of 3-denier rayon fiber are provided in the lower layer. A fiber layer having a basis weight of 100 g / m ² is disposed and laminated, and after entanglement, an acrylic acid ester by soap-free emulsification is used as a binder, and a solid content of 65 g / m ² is applied to the fiber layer surface. A solid content of 15 g / m ² (24.2% by weight in total) was applied by impregnation to obtain a filter having a total basis weight of 330 g / m ² .
[0018]
Example 3
Fiber layer having a basis weight of 100 g / ^{m 2} consisting of 100% 6 denier polyester fibers in the upper layer, arranged fiber layer having a basis weight of 100 g / ^{m 2} consisting of 70% polyester fibers and 30% 2 denier polyester fibers 6 deniers in the middle layer In the lower layer, a fibrous layer having a basis weight of 50 g / m ² composed of 75% of 2 denier polyester fiber and 25% of 3 denier rayon fiber is arranged and laminated. After confounding, acrylic acid by soap-free emulsion polymerization is used as a binder. Using an ester, a solid content of 45 g / m ² was applied to the fiber layer surface, and a solid content of 5 g / m ² (16.7% by weight in total) was applied by impregnation to obtain a filter having a total basis weight of 300 g / m ² .
[0019]
On the other hand, for comparison, comparative filters were obtained by the following comparative examples.
Comparative Example 1
A comparative filter having a solid content of 50 g / m ² (20% by weight) was applied to the surface by applying an acrylate ester not based on soap-free emulsion polymerization as a binder using the same fiber layer structure as in Example 1, and a total basis weight of 250 g / m ^2. Obtained.
[0020]
Comparative Example 2
Arranged fiber layer having a basis weight of 150 g / m ² consisting of 50% bicomponent polyester polyester fiber containing a low-melting polyester component 50% polyester fibers and 4 denier 6 denier upper, and 50% polyester fibers of the lower layer 3 denier A fiber layer having a basis weight of 100 g / m ² composed of 50% of a composite polyester fiber containing a 2-denier low-melting polyester component is arranged and laminated, and a filter having a total basis weight of 250 g / m ² is obtained only by confounding without using a binder. Obtained.
[0021]
Comparative Example 3
In the upper layer, a fiber layer having a basis weight of 150 g / m ² composed of 50% of 6-denier polyester fiber and 50% of 4-denier composite polyester fiber containing a low-melting polyester component is disposed, and in the lower layer, 50% of 3-denier polyester fiber, A fiber layer having a basis weight of 80 g / m ² composed of 50% of a composite polyester fiber containing a 2 denier low-melting polyester component is arranged and laminated. After entanglement, spraying is performed using an acrylic acid ester by soap-free emulsion polymerization as a binder. According to the method, a solid content of 20 g / m ² (8% by weight) was applied to the fiber layer surface to obtain a filter having a total basis weight of 250 g / m ² .
[0022]
For each of the filters obtained in the above Examples and Comparative Examples, the foaming property and the strength retention during use were observed and measured as follows. The results are shown in Table 1 together with the pressure loss.
Foaming property: Put an air generator equipped with a filter into a 1-liter beaker, fill with tap water, generate air for 30 minutes, and observe the foaming property of the water surface, the type of foam, and how the foam disappears.
Maintain strength during use: Put an air generator fitted with a filter into a water tank with the size of the goldfish, run for 3 months, and measure the strength before and after use.
[0023]
[Table 1]

[0024]
From the above table, it can be seen that the filter according to the present invention immediately disappears the generated foam as compared with each of the comparative examples, and hardly maintains the strength and the pressure loss.
[0025]
【The invention's effect】
As described above, the present invention provides at least two fiber layers in which the constituent fibers are entangled with each other, bonded and integrated with a binder, and when installed in a water tank, the water circulates in the water tank from the inlet side to the outlet side. In a filter for an aquarium fish tank having a density gradient from coarse to dense on the side, a binder of 10 to 40% by weight based on the total basis weight is provided and an auxiliary agent such as an emulsifier that dissolves the binder in water. Is not used, and since the binder does not contain water-soluble auxiliary agent, no bubbling occurs even in the water tank, and the cloudy component of the auxiliary agent is not eluted. It does not pollute the inside of the aquarium, so that the death of the ornamental fish due to water pollution is avoided, which has a remarkable effect as a filter for circulating water in the aquarium for aquarium fish. In addition, the filter of the present invention has an effect that the strength is sufficiently maintained without a decrease in strength because the binder is applied at a predetermined ratio, and the water flow rate can be secured.

Claims

Consisting of at least two fiber layers, the constituent fibers are entangled with each other and bonded and integrated with a binder, and when installed in a water tank, the water circulating in the water tank changes from coarse to dense from the inlet side to the outlet side. A filter for use in an aquarium for aquarium fish having a density gradient of 10 to 40% by weight based on the total weight of the filter, and the binder has an auxiliary agent such as a water-soluble emulsifier. A filter for use in an aquarium for aquarium fish, which is not used.

The filter for use in an aquarium fish tank according to claim 1, wherein the fibers constituting the fiber layer are one or more selected from polyester fibers, polyacryl fibers, and rayon fibers.

3. The filter used in an aquarium fish tank according to claim 1, wherein the binder for bonding the constituent fibers is at least one selected from acrylate, SBR, PS, and NBR produced by soap-free emulsion polymerization.

4. The filter for use in an aquarium fish tank according to claim 1, wherein the binder for the fiber layer is applied by surface treatment, impregnation treatment or spray treatment.