JP2004099911A - Color aggregate-containing coating material and colored aggregate-containing coating material - Google Patents
Color aggregate-containing coating material and colored aggregate-containing coating material Download PDFInfo
- Publication number
- JP2004099911A JP2004099911A JP2003418888A JP2003418888A JP2004099911A JP 2004099911 A JP2004099911 A JP 2004099911A JP 2003418888 A JP2003418888 A JP 2003418888A JP 2003418888 A JP2003418888 A JP 2003418888A JP 2004099911 A JP2004099911 A JP 2004099911A
- Authority
- JP
- Japan
- Prior art keywords
- coating material
- aggregate
- colored aggregate
- colored
- containing coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
この発明は、建築物に代表される構造物の外壁、内壁及び天井等の塗装面に仕上げを行うための塗装に使われる有色骨材含有塗材及び着色骨材含有塗材に関するものである。 (4) The present invention relates to a colored aggregate-containing coating material and a colored aggregate-containing coating material used for painting a finish such as an outer wall, an inner wall, and a ceiling of a structure represented by a building.
従来、合成樹脂と有色骨材とからなる有色骨材含有塗材は、その有色骨材含有塗材により形成される塗膜の多彩感などの質感から多く用いられることがある。また、この有色骨材含有塗材を１種又は２種以上を用いて、御影石、大理石又は砂岩などの石材に似た質感を表現する塗膜を得ることがある。
このように、有色骨材含有塗材は、高級感のある塗膜を得るために好ましく用いられることがある。
2. Description of the Related Art Conventionally, a colored aggregate-containing coating material composed of a synthetic resin and a colored aggregate is often used because of a texture such as a versatility of a coating film formed by the colored aggregate-containing coating material. In addition, a coating film expressing a texture similar to a stone material such as granite, marble or sandstone may be obtained by using one or two or more of the colored aggregate-containing coating materials.
As described above, the colored aggregate-containing coating material may be preferably used in order to obtain a high-grade coating film.
ところが、有色骨材含有塗材により形成される塗膜では、耐候性が劣ることがあるため、有色骨材含有塗材により形成される塗膜にさらに透明なクリアー塗料を塗布することがある。透明なクリアー塗料を塗布することにより、塗膜としての耐候性は向上する。しかし、この塗膜を得るためには、透明なクリアー塗料を塗布する工程が必要となるため、有色骨材含有塗材により形成される塗膜を得るためには、塗装期間が長くかかるなど塗装作業の効率が低下する問題が生じる。 However, since a coating film formed by the colored aggregate-containing coating material may have poor weather resistance, a clear transparent paint may be further applied to the coating film formed by the colored aggregate-containing coating material. By applying a transparent clear paint, the weather resistance as a coating film is improved. However, in order to obtain this coating film, a step of applying a transparent clear paint is required. There is a problem that the work efficiency is reduced.
この発明は、上記のような従来技術に存在する問題点に着目してなされたものである。その目的とするところは、容易に耐候性が優れた塗膜を形成することができる有色骨材含有塗材及び着色骨材含有塗材を提供することにある。 The present invention has been made by focusing on the problems existing in the prior art as described above. It is an object of the present invention to provide a colored aggregate-containing coating material and a colored aggregate-containing coating material that can easily form a coating film having excellent weather resistance.
上記の目的を達成するために、請求項１に記載の発明の有色骨材含有塗材は、有色骨材と合成樹脂とを主成分とする塗材において、ヒンダードアミンライトスタビライザー（以下「ＨＡＬＳ」とする。）を添加したものである。 In order to achieve the above object, the colored aggregate-containing coating material of the invention according to claim 1 is a coating material containing a colored aggregate and a synthetic resin as main components, and a hindered amine light stabilizer (hereinafter, referred to as “HALS”). ) Is added.
請求項２に記載の発明の有色骨材含有塗材は、請求項１に記載の発明において、前記有色骨材が寒水砂及び／又は着色骨材であるものである。 塗 The colored aggregate-containing coating material of the invention according to claim 2 is the coating material according to claim 1, wherein the colored aggregate is cold water sand and / or colored aggregate.
請求項３に記載の発明の着色骨材含有塗材は、有色骨材に塗料被覆層を有する着色骨材を含有する塗材において、その塗料被覆層にＨＡＬＳを含有したものである。 The colored aggregate-containing coating material of the invention according to claim 3 is a coating material containing a colored aggregate having a paint coating layer on a colored aggregate, wherein the paint coating layer contains HALS.
この発明は、以上のように構成されているため、次のような効果を奏する。
請求項１に記載の発明の有色骨材含有塗材によれば、容易に耐候性が優れた塗膜を形成することができる有色骨材含有塗材を得ることができる。
The present invention is configured as described above, and has the following effects.
According to the colored aggregate-containing coating material of the first aspect of the present invention, a colored aggregate-containing coating material capable of easily forming a coating film having excellent weather resistance can be obtained.
請求項２に記載の発明の有色骨材含有塗材によれば、請求項１に記載の発明の効果に加え、この発明の効果が、より顕著に現れるものである。
請求項３に記載の発明の着色骨材含有塗材によれば、容易に耐候性が優れた塗膜を形成することができる着色骨材含有塗材を得ることができる。
According to the colored aggregate-containing coating material of the invention described in claim 2, the effect of the present invention appears more remarkably in addition to the effect of the invention described in claim 1.
According to the colored aggregate-containing coating material of the third aspect of the present invention, a colored aggregate-containing coating material capable of easily forming a coating film having excellent weather resistance can be obtained.
以下、この発明の実施形態を詳細に説明する。
この発明の有色骨材含有塗材は、有色骨材と合成樹脂とを主成分とする塗材において、ＨＡＬＳを添加したものである。
Hereinafter, embodiments of the present invention will be described in detail.
The colored aggregate-containing coating material of the present invention is obtained by adding HALS to a coating material containing a colored aggregate and a synthetic resin as main components.
まず、有色骨材と合成樹脂とを主成分とする塗材とは、合成樹脂により有色骨材の粒子同士を結合させ塗膜を形成させるものである。
有色骨材とは、色を有する骨材のことであり、有色骨材含有塗材により形成される塗膜に多彩感などの高級感を与え、意匠感を向上させるものである。
前記有色骨材は、透明感の高い骨材から隠蔽力の高い骨材、光沢の有る骨材から光沢のない骨材等が挙げられる。全く無色で透明な骨材は、色を有しないため、有色骨材ではない。しかし、有色骨材含有塗材の色調に影響を与えない範囲で、無色で透明な骨材を加えることは、可能である。
First, a coating material containing a colored aggregate and a synthetic resin as main components is one in which particles of the colored aggregate are combined with each other by the synthetic resin to form a coating film.
The colored aggregate is an aggregate having a color, and gives a coating film formed by a colored aggregate-containing coating material a sense of quality such as versatility and improves a design feeling.
Examples of the colored aggregate include a highly transparent aggregate to an aggregate having high hiding power, a glossy aggregate to a dull aggregate, and the like. A completely colorless and transparent aggregate has no color and is not a colored aggregate. However, it is possible to add a colorless and transparent aggregate within a range that does not affect the color tone of the colored aggregate-containing coating material.
この有色骨材含有塗材に用いられる有色骨材は、有色のものであり、有色天然石を粉砕したものや陶磁器などを粉砕したセルベンなどがある。また、有色天然石や陶磁器を粉砕したものに人工的に着色を施したものや工業的に生産されたものなど着色骨材がある。
有色天然石の粉砕物には、花崗岩、蛇紋岩、黒曜石、蛍石、カナリヤ、白玉、寒水、小桜、漆雪、美濃霞、蛇紋等の大理石粉砕粒、珪砂、天然細砂利（金華、大磯、チェリーサンド）などが挙げられる。
さらに、シラスバルーン、パーライト、ガラスの粉砕物を発泡させたものなどの軽量骨材も挙げることができる。
The colored aggregate used in the colored aggregate-containing coating material is a colored one, such as a crushed colored natural stone or a cerven that is obtained by crushing a ceramic or the like. There are also colored aggregates such as artificially colored colored natural stones and crushed porcelain and artificially colored ones.
Pulverized colored natural stones include granite, serpentine, obsidian, fluorite, canary, shiratama, cold water, small cherry, lacquer snow, Mino Kasumi, serpentine, etc. Sand).
Furthermore, lightweight aggregates such as shirasu balloons, perlite, and foamed crushed glass can also be used.
有色骨材含有塗材に用いられる有色骨材の粒子径は、３７〜２０００μｍの範囲のものが好ましく、４５〜１０００μｍの範囲のものがさらに好ましい。３７μｍより細かい骨材の場合、有色骨材含有塗材より得られる塗膜の多彩感が少なく意匠性に欠けることがあり、塗材の安定性、塗布作業の作業性などが劣る場合がある。また、２０００μｍより大きい骨材の場合、塗膜の仕上がり面が荒く、意匠的に好ましくない。
４５〜１０００μｍの範囲の有色骨材を用いた場合には、有色骨材含有塗材の貯蔵時の安定性が良く、形成された塗膜の意匠性がより好ましくバランスの取れたものである。
The particle size of the colored aggregate used for the colored aggregate-containing coating material is preferably in the range of 37 to 2000 μm, more preferably in the range of 45 to 1000 μm. In the case of an aggregate finer than 37 μm, the coating film obtained from the colored aggregate-containing coating material may have little versatility and lack designability, and the stability of the coating material and the workability of the coating operation may be poor. In the case of an aggregate larger than 2000 μm, the finished surface of the coating film is rough, which is not preferable in design.
When a colored aggregate in the range of 45 to 1000 μm is used, the stability of the colored aggregate-containing coating material during storage is good, and the design of the formed coating film is more preferably balanced.
合成樹脂としては、アクリル樹脂、スチレン樹脂、ウレタン樹脂、シリコーン樹脂、フッ素樹脂、エポキシ樹脂、メラミン樹脂、アルキッド樹脂、塩化ビニル樹脂、酢酸ビニル樹脂、ポリエステル樹脂などの樹脂を単独又は共重合したもの、これら樹脂を有機溶媒に溶解させたもの、エマルションとして水に分散させたもの又は弱溶剤に分散させたものが用いられる。 As a synthetic resin, acrylic resin, styrene resin, urethane resin, silicone resin, fluororesin, epoxy resin, melamine resin, alkyd resin, vinyl chloride resin, vinyl acetate resin, those obtained by homopolymerizing or copolymerizing resins, Those obtained by dissolving these resins in an organic solvent, those dispersed in water as an emulsion, or those dispersed in a weak solvent are used.
この合成樹脂は、硬化及び乾燥後に透明のフィルムを形成するものであれば良い。乾燥し造膜した後に透明となる合成樹脂は、有色骨材含有塗材における結合材であり、また、被塗布面と有色骨材含有塗材とを接着させるものである。また、骨材の色調、風合いを生かし、意匠感を高めるために乾燥し造膜した後に透明となるものであることが必要である。この有色骨材含有塗材の使いやすさ、製造の容易さ、入手の容易さにより合成樹脂エマルションが好ましく用いられる。 合成 The synthetic resin may be any resin that forms a transparent film after curing and drying. The synthetic resin which becomes transparent after being dried and formed into a film is a binder in the colored aggregate-containing coating material, and also bonds the coated surface to the colored aggregate-containing coating material. Further, it is necessary that the material be transparent after being dried and formed into a film in order to utilize the color tone and texture of the aggregate and enhance the design feeling. Synthetic resin emulsions are preferably used because of the ease of use, ease of production, and availability of the colored aggregate-containing coating material.
合成樹脂エマルションは、乳化重合のような通常の重合技術で製造できる一般的なもので良い。例えば、アクリル樹脂、スチレン樹脂、ウレタン樹脂、シリコーン樹脂、フッ素樹脂、エポキシ樹脂、酢酸ビニル樹脂などの樹脂より製造された合成樹脂エマルションなどがある。 The synthetic resin emulsion may be a general one that can be produced by a usual polymerization technique such as emulsion polymerization. For example, there is a synthetic resin emulsion manufactured from a resin such as an acrylic resin, a styrene resin, a urethane resin, a silicone resin, a fluorine resin, an epoxy resin, and a vinyl acetate resin.
有色骨材含有塗材としての適性や物性、入手の容易性などからアクリル樹脂、スチレン樹脂より製造されたアクリル系合成樹脂エマルションやアクリルスチレン系合成樹脂エマルションが好ましく用いられる。また、より一層耐候性を向上させるためには、ウレタン樹脂、シリコーン樹脂、フッ素樹脂より製造される、ウレタン系合成樹脂エマルション、シリコーン系合成樹脂エマルション、フッ素系合成樹脂エマルション、アクリルシリコーン系合成樹脂エマルションなどを用いることがある。 ア ク リ ル Acrylic synthetic resin emulsions and acrylic styrene synthetic resin emulsions made from acrylic resins and styrene resins are preferably used from the viewpoint of suitability, physical properties, availability and the like as colored aggregate-containing coating materials. Further, in order to further improve the weather resistance, a urethane-based synthetic resin emulsion, a silicone-based synthetic resin emulsion, a fluorine-based synthetic resin emulsion, an acrylic silicone-based synthetic resin emulsion manufactured from a urethane resin, a silicone resin, and a fluororesin. Etc. may be used.
前記合成樹脂エマルションは、乾燥性の良いものが好ましい。乾燥性が劣るものであると、有色骨材含有塗材を塗布した後に降雨があった場合、その塗布された有色骨材含有塗材が未硬化又は未乾燥である場合、流れてしまうことがある。
また、合成樹脂のガラス転移温度は、好ましくは−２０〜５０℃の範囲であり、−２０℃より低い場合には、有色骨材含有塗材により形成される塗膜に汚れやすくなることがあり、５０℃より高い場合には、塗膜が割れやすくなる場合があり、有色骨材含有塗材の用途に応じて、適したガラス転移温度の合成樹脂を選択することができる。
The synthetic resin emulsion preferably has good drying properties. If the drying properties are poor, if there is rainfall after applying the colored aggregate-containing coating material, if the applied colored aggregate-containing coating material is uncured or undried, it may run off is there.
Further, the glass transition temperature of the synthetic resin is preferably in the range of -20 to 50 ° C. When the glass transition temperature is lower than -20 ° C, the coating film formed by the colored aggregate-containing coating material may be easily stained. If the temperature is higher than 50 ° C., the coating film may be easily broken, and a synthetic resin having a suitable glass transition temperature can be selected according to the use of the colored aggregate-containing coating material.
合成樹脂の固形分は、有色骨材含有塗材の固形分中に５〜５０重量％の範囲が好ましい。５重量％より少ない場合には、塗膜の耐候性が低下し、脆くなることがある。また、５０重量％より多い場合は、汚れやすくなる場合がある。
さらに、有色骨材含有塗材のその他の成分として、ハロゲン系、リン系、三酸化アンチモン系化合物などの難燃剤、消泡剤、分散剤、湿潤剤などとして用いられる界面活性剤、造膜助剤、防凍剤などとして用いられる高沸点溶剤、粘度、粘性調整のための増粘剤、防腐剤、防藻剤、防黴剤等のように一般に塗料に配合されている成分を用いることができる。
The solid content of the synthetic resin is preferably in the range of 5 to 50% by weight based on the solid content of the colored aggregate-containing coating material. If the amount is less than 5% by weight, the weather resistance of the coating film may be reduced and the coating film may be brittle. On the other hand, if it is more than 50% by weight, it may be easily stained.
Further, as other components of the colored aggregate-containing coating material, a surfactant used as a flame retardant such as a halogen-based, phosphorus-based or antimony trioxide-based compound, a defoaming agent, a dispersant, a wetting agent, and a film-forming aid. Ingredients commonly used in paints, such as high-boiling solvents used as agents, antifreezing agents, thickeners for adjusting viscosity and viscosity, preservatives, antialgal agents, antifungal agents, etc. can be used. .
また、必要に応じ、着色顔料、酸化チタンなどの白色顔料などの着色成分を添加することができる。 着色 If necessary, a coloring component such as a coloring pigment or a white pigment such as titanium oxide can be added.
この発明に用いられるＨＡＬＳは、有色骨材含有塗材により形成される塗膜に耐候性を向上させるためのものである。この塗膜の耐候性の向上は、塗膜中の合成樹脂の劣化に影響を与える遊離ラジカルを捕捉、過酸化物の分解、消光などによるものである。 Ｈ The HALS used in the present invention is for improving the weather resistance of the coating film formed by the colored aggregate-containing coating material. This improvement in the weather resistance of the coating film is due to trapping of free radicals that affect the deterioration of the synthetic resin in the coating film, decomposition of peroxide, quenching, and the like.
前記ＨＡＬＳは、（化１）に示されるテトラメチルペピリジンを有するものが好ましく用いられる。
テトラメチルペピリジンの数が１のものには、１−［２−〔３−（３，５−ジ−ｔ−ブチル−４−ヒドロキシフェニル）プロピオニルオキシ〕エチル］−４−〔３−（３，５−ジ−ｔ−ブチル−４−ヒドロキシフェニル）プロピオニルオキシ〕−２，２，６，６−テトラメチルピペリジン、４−ベンゾイルオキシ−２，２，６，６−テトラメチルペピリジン、Ｎ−メチル−３−ドデシル−１−（２，２，６，６−ペンタメチル−４−ピペリジル）ピロリジン−２，５−ジオンなどがある。 When the number of tetramethylpepyridines is 1, 1- [2- [3- (3,5-di-t-butyl-4-hydroxyphenyl) propionyloxy] ethyl] -4- [3- (3 , 5-Di-t-butyl-4-hydroxyphenyl) propionyloxy] -2,2,6,6-tetramethylpiperidine, 4-benzoyloxy-2,2,6,6-tetramethylpepyridine, N- Methyl-3-dodecyl-1- (2,2,6,6-pentamethyl-4-piperidyl) pyrrolidine-2,5-dione and the like.
テトラメチルペピリジンの数が２のものには、８−アセチル−３−ドデシル−７，７，９，９−テトラメチル−１，３，８−トリアザスピロ［４．５］デカン−２，４−ジオン、ビス（２，２，６，６−テトラメチル−４−ピペリジル）セバケート、ビス（１，２，２，６，６−ペンタメチル−４−ピペリジル）セバケートなどがある。 When the number of tetramethylpepyridines is 2, 8-acetyl-3-dodecyl-7,7,9,9-tetramethyl-1,3,8-triazaspiro [4.5] decane-2,4- Dione, bis (2,2,6,6-tetramethyl-4-piperidyl) sebacate, bis (1,2,2,6,6-pentamethyl-4-piperidyl) sebacate and the like.
テトラメチルペピリジンの数が４のものには、テトラキス（１，２，２，６，６−ペンタメチル−４−ピペリジル）１，２，３，４−ブタンテトラカルボキシラート、１，２，２，６，６−ペンタメチル−４−ピペリジル／トリデシル１，２，３，４ブタンテトラカルボキシラートなどを挙げることができる。
また、前記ＨＡＬＳの平均分子量は、２００〜１０００の範囲のものが好ましく用いられる。
When the number of tetramethylpepyridines is 4, tetrakis (1,2,2,6,6-pentamethyl-4-piperidyl) 1,2,3,4-butanetetracarboxylate, 1,2,2 6,6-pentamethyl-4-piperidyl / tridecyl 1,2,3,4-butanetetracarboxylate and the like can be mentioned.
The average molecular weight of the HALS is preferably in the range of 200 to 1,000.
平均分子量が２００より小さいものは、有色骨材含有塗材により形成された塗膜から流出することがあり、ＨＡＬＳによる耐候性の向上が少なくなることがある。
平均分子量が１０００より大きいものは、有色骨材含有塗材の貯蔵安定性を損なうことがあり、また、形成された塗膜の色調が希望した色調と違うものになることがある。
Those having an average molecular weight of less than 200 may flow out of the coating film formed by the colored aggregate-containing coating material, and the improvement of the weather resistance by HALS may be reduced.
When the average molecular weight is more than 1000, the storage stability of the colored aggregate-containing coating material may be impaired, and the color tone of the formed coating film may be different from the desired color tone.
前記ＨＡＬＳの粒子径は、０．１μｍ〜１０μｍの範囲のものが好ましい。０．１μｍより小さい場合は、ＨＡＬＳの入手が困難なことがある。また、１０μｍより大きい場合には、塗膜の意匠に影響を与えることがある。 Ｈ The particle size of the HALS is preferably in the range of 0.1 μm to 10 μm. If it is smaller than 0.1 μm, it may be difficult to obtain HALS. When it is larger than 10 μm, the design of the coating film may be affected.
また、前記ＨＡＬＳの添加量は、塗材固形分１００重量部中に、０．０１重量部〜１．０重量部の割合の範囲が好ましい。０．０１重量部より少ない場合には、有色骨材含有塗材により形成された塗膜の耐候性の向上を期待することができない場合がある。１．０重量部より多い場合には、１．０重量部添加したものと大差がないことがある。
より好ましくは、０．０５重量部〜０．５重量部の割合の範囲である。この範囲である場合には、十分な塗膜の耐候性を期待できるものである。
The amount of the HALS to be added is preferably in the range of 0.01 to 1.0 part by weight based on 100 parts by weight of the solid content of the coating material. If the amount is less than 0.01 part by weight, it may not be possible to expect an improvement in the weather resistance of the coating film formed by the colored aggregate-containing coating material. When the amount is more than 1.0 part by weight, there is a case where there is not much difference from the case where 1.0 part by weight is added.
More preferably, the ratio is in the range of 0.05 part by weight to 0.5 part by weight. When it is in this range, sufficient weather resistance of the coating film can be expected.
塗材へのＨＡＬＳの添加時期としては、塗材の製造時に添加する又は塗材を使用する直前に添加する場合がある。また、その添加方法は、塗材中に均一に混ぜ合わせることができれば、どのような方法でも問題はない。一般的には、攪拌機により混合する方法を用いる場合が多い。
さらに、ＨＡＬＳは、合成樹脂の中で好ましく用いられる合成樹脂エマルションと容易に混ざり合うものが良い。
HALS may be added to the coating material at the time of production of the coating material or immediately before using the coating material. In addition, any method can be used as long as it can be uniformly mixed in the coating material. Generally, a method of mixing with a stirrer is often used.
Further, it is preferable that HALS be easily mixed with a synthetic resin emulsion which is preferably used among synthetic resins.
また、紫外線吸収剤（以下、「ＵＶＡ」と言う。）との併用により、より塗膜の耐候性を増すことがある。ＨＡＬＳは、塗膜の劣化を起こす有害な光を吸収するものではないため、有害な紫外線を吸収し、無害な熱又は運動エネルギーに変換するＵＶＡを併用することにより、塗膜の耐候性がより増すものである。さらに、酸化防止剤を添加することにより、より一層の耐候性を得ることができる。 Also, the combined use with an ultraviolet absorber (hereinafter referred to as “UVA”) may further increase the weather resistance of the coating film. Since HALS does not absorb harmful light that causes deterioration of the coating film, the UVA that absorbs harmful ultraviolet light and converts it to harmless heat or kinetic energy is used in combination to improve the weather resistance of the coating film. It will increase. Further, by adding an antioxidant, further weather resistance can be obtained.
ＵＶＡには、ベンゾトリアゾール系、ベンゾフェノン系、サリシレート系、シアノアクリレート系、オギザニリド系の紫外線吸収剤が挙げられる。これらの中の紫外線吸収剤の中では、ベンゾトリアゾール系、ベンゾフェノン系の紫外線吸収剤が、熱及び光に安定であるため好ましく用いられる。さらに、ベンゾトリアゾール系紫外線吸収剤は、ＨＡＬＳとの相乗効果が大きいためより好ましく用いられる。 UVA includes benzotriazole-based, benzophenone-based, salicylate-based, cyanoacrylate-based, and agizanide-based ultraviolet absorbers. Among these ultraviolet absorbers, benzotriazole-based and benzophenone-based ultraviolet absorbers are preferably used because they are stable to heat and light. Furthermore, benzotriazole-based ultraviolet absorbers are more preferably used because they have a large synergistic effect with HALS.
ベンゾトリアゾール系紫外線吸収剤には、２−（２’−ヒドロキシ−５’−メチルフェニル）ベンゾトリアゾール、２−［２’−ヒドロキシ−３’，５’−ビス（α，α−ジメチルベンジル）フェニル］ベンゾトリアゾール、２−（２’−ヒドロキシ−３’，５−ジ−ｔ−ブチル−フェニル）−ベンゾトリアゾールなどがある。 Benzotriazole ultraviolet absorbers include 2- (2'-hydroxy-5'-methylphenyl) benzotriazole and 2- [2'-hydroxy-3 ', 5'-bis (α, α-dimethylbenzyl) phenyl Benzotriazole, 2- (2'-hydroxy-3 ', 5-di-t-butyl-phenyl) -benzotriazole and the like.
ベンゾフェノン系紫外線吸収剤には、２，４−ジヒドロキシ ベンゾフェノン、２−ヒドロキシ−４−メトキシ ベンゾトリアゾール、２−ヒドロキシ−４−メトキシ ベンゾトリアゾール−５−スルフォニック アシドなどが挙げられる。 {Benzophenone-based UV absorbers include 2,4-dihydroxy} benzophenone, 2-hydroxy-4-methoxy} benzotriazole, 2-hydroxy-4-methoxy {benzotriazole-5-sulfonic} acid, and the like.
また、酸化防止剤との併用により、より塗膜の耐候性を増すことがある。酸化防止剤は、塗膜の熱酸化劣化を防止することができる。
酸化防止剤には、リン系、フェノール系、イオウ系の酸化防止剤を挙げることができる。しかし、イオウ系酸化防止剤は、ＨＡＬＳの効果を低下することがあるため、ほとんど用いることがなく、リン系、フェノール系の酸化防止剤が好ましく用いられる。また、リン系酸化防止剤は、ＨＡＬＳとの相乗効果が大きいためより好ましく用いられる。
In addition, when used in combination with an antioxidant, the weather resistance of the coating film may be further increased. The antioxidant can prevent thermal oxidation deterioration of the coating film.
Antioxidants include phosphorus-based, phenol-based, and sulfur-based antioxidants. However, sulfur-based antioxidants are rarely used because they may reduce the effect of HALS, and phosphorus-based and phenol-based antioxidants are preferably used. Further, phosphorus-based antioxidants are more preferably used because they have a large synergistic effect with HALS.
リン系酸化防止剤には、トリスノニルフェニルホスファイト、トリス（２，４−ジ−ｔ−ブチルフェニル）ホスファイト、ジステアリルペンタエリスリトールジホスファイトなどが挙げられる。
さらに、ＵＶＡと酸化防止剤を併用することも可能である。
Examples of the phosphorus-based antioxidant include trisnonylphenyl phosphite, tris (2,4-di-t-butylphenyl) phosphite, distearylpentaerythritol diphosphite, and the like.
Further, UVA and an antioxidant can be used in combination.
前記有色骨材のうち寒水砂及び／又は着色骨材の場合に、この発明の効果が、顕著に現れる場合がある。
寒水砂とは、炭酸カルシウムを主成分とする、大理石の１種であり、寒水石を粉砕して粒度調整したものである。この寒水砂の外観は、白色粒子であるが、透明感のある骨材のため、それを用いた有色骨材含有塗材より得られた塗膜の意匠感が向上するため好ましく用いられる。
In the case of the cold aggregate and / or the colored aggregate among the colored aggregates, the effect of the present invention may be remarkably exhibited.
Cold water sand is a kind of marble containing calcium carbonate as a main component, and is obtained by grinding cold water stone to adjust the particle size. Although the appearance of the cold water sand is white particles, it is preferably used because the aggregate has a transparent feeling and the design feeling of the coating film obtained from the colored aggregate-containing coating material using the same is improved.
前記寒水砂を着色骨材含有塗料に含有することにより、その塗料から形成される塗膜に透明感を与えることができ、より一層意匠感を向上させることができる。また、塗料との混和性に優れ、入手が容易である。
しかし、寒水砂が透明感のある白色粒子であるため、その寒水砂を含有した塗料により形成された塗膜は、太陽光などの紫外線が塗膜内部まで届き、塗膜全体の劣化を促進することがある。そのため、多くの場合には、寒水砂を含有した塗料により形成された塗膜には、透明なクリアー塗料を塗布するものであったが、前記ＨＡＬＳを塗料中に添加することにより、塗膜全体の劣化の速度を遅くすることができる。
By including the cold water sand in the colored aggregate-containing paint, it is possible to give a transparent feeling to the coating film formed from the paint, and it is possible to further improve the design feeling. In addition, it has excellent miscibility with paints and is easily available.
However, since cold water sand is a transparent white particle, the coating film formed by the paint containing the cold water sand reaches the inside of the coating film with ultraviolet rays such as sunlight and promotes the deterioration of the entire coating film. Sometimes. Therefore, in many cases, a transparent clear paint is applied to a paint film formed of paint containing cold water sand. However, by adding HALS into the paint, the entire paint film is formed. Can be slowed down.
着色骨材は、骨材に着色を施したものであり、骨材の色が安定し、それにより、塗膜の色調も安定することになる。骨材の着色方法の多くは、骨材表面に塗料、顔料、釉薬などの着色成分により着色する方法である。また、ガラスビーズ、プラスチックビーズなどは骨材の内部から着色することも可能である。 The colored aggregate is obtained by coloring the aggregate, so that the color of the aggregate is stabilized, and the color tone of the coating film is also stabilized. Many of the methods for coloring aggregates involve coloring the surface of the aggregates with coloring components such as paints, pigments and glazes. Glass beads, plastic beads, and the like can be colored from the inside of the aggregate.
骨材表面に塗料、顔料、釉薬などにより着色する着色骨材に用いられる骨材は、大理石、御影石などの有色天然石の粉砕物、珪砂、寒水砂、陶磁器砕粒、ガラスビーズ、プラスチックビーズ、軽量骨材などが用いられる。
内部から着色することで得られる着色骨材は、骨材の製造過程において、内部から着色されたもののことであり、ガラスを略球状にしたガラスビーズや、アクリル樹脂などの合成樹脂を略球状にしたプラスチックビーズなどがある。
Aggregates used for coloring aggregates whose surfaces are colored with paints, pigments, glazes, etc. are crushed colored natural stones such as marble and granite, silica sand, cold water sand, ceramic granules, glass beads, plastic beads, and lightweight bones. Materials are used.
Colored aggregate obtained by coloring from the inside is the one that is colored from the inside during the manufacturing process of the aggregate. There are plastic beads and the like.
着色骨材は、着色骨材以外の有色天然石を粉砕したものに比べ、人工的に着色を施したものや工業的に生産されたものは、色調の他に粒子径も安定している場合も多く、塗料の塗布作業が安定的であり、塗料の安定においても優れているものである。特に、人工的に着色した珪砂や寒水砂、陶磁器砕粒は、入手が容易であり、合成樹脂との混和性に優れているため、より好ましく用いられる。 Colored aggregates, compared to those obtained by crushing colored natural stones other than colored aggregates, those that are artificially colored or those that are industrially produced, even if the particle size is stable in addition to color tone In many cases, the coating operation of the paint is stable, and the paint is excellent in stability. In particular, artificially colored quartz sand, cold water sand, and granulated porcelain are more preferably used because they are easily available and have excellent miscibility with synthetic resins.
しかし、着色骨材が骨材表面に塗料、釉薬などにより着色したものであるため、その着色骨材の着色成分が太陽光などの紫外線により、変色又は退色することがある。そのため、多くの場合には、着色骨材を含有した塗料により形成された塗膜には、透明なクリアー塗料を塗布するものであったが、前記ＨＡＬＳを塗料中に添加することにより、着色成分の変色又は退色の速度を遅くすることができる。 However, since the colored aggregate is obtained by coloring the surface of the aggregate with paint, glaze, or the like, the coloring component of the colored aggregate may be discolored or faded by ultraviolet rays such as sunlight. Therefore, in many cases, a transparent clear paint is applied to a coating film formed by a paint containing a colored aggregate. However, by adding the HALS to the paint, a coloring component is obtained. Can be slowed down.
珪砂は、ニ酸化けい素を主成分とするものであり、川砂、海砂に代表される天然状態で粒状のものと、珪石を粉砕して粒度調整したものがある。寒水砂は、炭酸カルシウムを主成分とするものであり、寒水石を粉砕して粒度調整したものである。陶磁器砕粒は、陶磁器を粉砕して得られるものであり、粒度を調製されて用いられる。これら骨材を適宜選択して使用することができる。
前記のように、有色骨材と合成樹脂とを主成分とする塗材において、ＨＡＬＳを添加することにより、容易に耐候性が優れた塗膜を形成することができる有色骨材含有塗材を得ることができる。
Silica sand is mainly composed of silicon dioxide, and is classified into particles in a natural state typified by river sand and sea sand, and particles whose particle size is adjusted by crushing silica stone. Cold water sand is mainly composed of calcium carbonate, and is obtained by grinding cold water stone to adjust the particle size. Ceramic crushed granules are obtained by crushing ceramics, and are used after adjusting the particle size. These aggregates can be appropriately selected and used.
As described above, in a coating material containing a colored aggregate and a synthetic resin as main components, by adding HALS, a colored aggregate-containing coating material that can easily form a coating film having excellent weather resistance can be obtained. Obtainable.
また、前記のような構成以外にも有色骨材に塗料被覆層を有する着色骨材を含有する塗材において、その塗料被覆層にＨＡＬＳを含有したものである。つまり、有色骨材に着色骨材を用いた場合には、その着色骨材を被覆する塗料にＨＡＬＳを含有させ、そのＨＡＬＳを含有させた塗料により、塗料被覆層を形成させた着色骨材を着色骨材含有塗材に用いることにより、容易に耐候性が優れた塗膜を形成することができる着色骨材含有塗材を得ることができる。 塗 In addition to the above-described configuration, in a coating material containing a colored aggregate having a paint coating layer on a colored aggregate, HALS is contained in the paint coating layer. That is, when a colored aggregate is used as the colored aggregate, HALS is contained in the coating material for coating the colored aggregate, and the colored aggregate having a paint coating layer formed by the HALS-containing coating material is used. By using it as a colored aggregate-containing coating material, a colored aggregate-containing coating material capable of easily forming a coating film having excellent weather resistance can be obtained.
着色骨材は、前述したように、骨材に着色を施したものであり、その骨材の着色方法の多くは、骨材表面に塗料、釉薬などにより着色する方法であが、その着色成分が塗料であることにより、ＨＡＬＳを含有させ、それにより塗料被覆層を形成させることができる。 As described above, the colored aggregate is obtained by coloring the aggregate, and most of the methods of coloring the aggregate are methods of coloring the surface of the aggregate with a paint, glaze, or the like. Is a paint, so that HALS can be contained, whereby a paint coating layer can be formed.
塗料としては、アクリル樹脂系、シリコーン樹脂系、ウレタン樹脂系、シリコーンアクリル樹脂系等の水系塗料、溶剤系塗料又は無溶剤系塗料が用いられ、必要とされる色調に着色顔料などの成分により着色されたものを用いる。この塗料は、着色骨材の用途や性能に応じて適宜選択することができるが、着色骨材の製造が容易なため、水系塗料又は溶剤系塗料が好ましく用いられる。 Water-based paints such as acrylic resin-based, silicone resin-based, urethane resin-based, and silicone acrylic resin-based paints, solvent-based paints, and solvent-free paints are used as paints. Use what was done. This paint can be appropriately selected depending on the use and performance of the colored aggregate, but a water-based paint or a solvent-based paint is preferably used because the colored aggregate is easily manufactured.
着色顔料としては、無機、有機系顔料及びその両方を用いられる。着色顔料は、チタン白、カーボンブラック、オキサイドイエロー、弁柄、シアニンブルー、又はシアニングリーンなど塗料に通常用いられるものを使用することができる。それらは、耐候性のよいものが好ましい。 Inorganic and organic pigments and both are used as coloring pigments. As the coloring pigment, those usually used for paints such as titanium white, carbon black, oxide yellow, red iron oxide, cyanine blue, and cyanine green can be used. Those having good weather resistance are preferable.
また、この塗料には、その他の添加剤として、低沸点アルコール、高沸点溶剤、界面活性剤、増粘剤、ｐＨ調整剤、防腐剤等のような一般に塗料製造に配合されている成分を使用することができる。高沸点溶剤は造膜助剤、防凍剤として用いられ、界面活性剤は消泡剤、分散剤、湿潤剤などとして用いられる。増粘剤は、粘度及び粘性調整のために用いられる。 In addition, other additives commonly used in paint production, such as low-boiling alcohols, high-boiling solvents, surfactants, thickeners, pH adjusters, and preservatives, are used in this coating. can do. High-boiling solvents are used as film-forming auxiliaries and antifreezing agents, and surfactants are used as defoamers, dispersants, wetting agents and the like. Thickeners are used for viscosity and viscosity control.
前記のような構成の塗料にＨＡＬＳを添加し、その塗料により骨材に塗料被覆層を形成させ、着色骨材を得るものである。
このＨＡＬＳは、前述したものを用いることができる。また、その添加量は、塗料中の合成樹脂成分１００重量部に対して、０．１重量部〜３．０重量部の範囲が好ましい。０．１重量部より少ない場合には、その着色骨材を含有した有色骨材含有塗材により形成された塗膜の耐候性の向上を期待することができない場合がある。３．０重量部より多い場合には、３．０重量部添加したものと大差がないことがある。
HALS is added to the paint having the above-described structure, and a paint coating layer is formed on the aggregate with the paint to obtain a colored aggregate.
As the HALS, those described above can be used. Further, the addition amount is preferably in the range of 0.1 part by weight to 3.0 parts by weight based on 100 parts by weight of the synthetic resin component in the paint. If the amount is less than 0.1 part by weight, it may not be possible to expect an improvement in the weather resistance of a coating film formed by the colored aggregate-containing coating material containing the colored aggregate. When the amount is more than 3.0 parts by weight, there is a case where there is not much difference from the case where 3.0 parts by weight is added.
次に、塗料を用いて骨材に塗料被覆層を形成させる。この形成方法は、特に限定されるものではない。例えば、骨材を容器に入れ、ミキサー等により攪拌を行いながら前記塗料をスプレー等により骨材全体に均一になるよう噴霧し、塗料により骨材を被覆する。
塗料が骨材全体に均一になった状態にした後、振動乾燥機を用い、振動を与えながら、熱風等を用い、塗料を被覆した骨材を乾燥させる。そして、塗料被覆層を有する着色骨材を得ることができる。
Next, a paint coating layer is formed on the aggregate using a paint. This forming method is not particularly limited. For example, the aggregate is put into a container, and the above-mentioned paint is sprayed by a spray or the like so as to be uniform over the entire aggregate while stirring with a mixer or the like, and the aggregate is coated with the paint.
After the paint is made uniform throughout the aggregate, the paint-coated aggregate is dried using hot air or the like while applying vibrations using a vibration dryer. Then, a colored aggregate having a paint coating layer can be obtained.
このようにして得られた着色骨材を着色骨材含有塗材として用いる場合などは、篩等により粒度調整を行うことがある。
着色骨材含有塗材にＨＡＬＳを含有した被覆層を有する着色骨材を用いた場合には、塗材の固形分中でのその着色骨材含有率は、２０〜８０重量％が好ましい範囲である。２０重量％より少ない場合には、ＨＡＬＳによる耐候性向上の効果が少なくなる。８０重量％より大きい場合には、ＨＡＬＳによる効果の向上は少なくなるが、その効果は十分である。５０〜８０重量％がさらに好ましい範囲である。
When the colored aggregate thus obtained is used as a colored aggregate-containing coating material, the particle size may be adjusted by a sieve or the like.
When a colored aggregate having a coating layer containing HALS is used as the colored aggregate-containing coating material, the content of the colored aggregate in the solid content of the coating material is preferably in a range of 20 to 80% by weight. is there. When the amount is less than 20% by weight, the effect of improving the weather resistance by HALS is reduced. When the content is more than 80% by weight, the effect of HALS is less improved, but the effect is sufficient. 50 to 80% by weight is a more preferable range.
この着色骨材含有塗材は、着色骨材以外の骨材を含有することができる。この骨材は、前述した有色骨材を用いることができる。またその有色骨材は、着色骨材と同じ粒子径の範囲のものを用いることが好ましい。このことにより、着色骨材含有塗材の粘度などの安定性に優れ、塗布作業の行い易いものとなる。
このようにして構成されるＨＡＬＳを含有した被覆層を有する着色骨材は、着色骨材含有塗材として用いることができる。
The colored aggregate-containing coating material can contain aggregates other than the colored aggregate. As the aggregate, the above-described colored aggregate can be used. The colored aggregate preferably has the same particle diameter as the colored aggregate. Thereby, the coloring aggregate-containing coating material has excellent stability such as viscosity, and can be easily applied.
The colored aggregate having the HALS-containing coating layer thus configured can be used as a colored aggregate-containing coating material.
次に、前記のように構成された有色骨材含有塗材及び着色骨材含有塗材の塗布方法について説明する。
この有色骨材含有塗材又は着色骨材含有塗材は、刷毛、ローラー、スプレー、鏝、へらなどの通常の塗布方法により塗布することができ、スプレーにより塗装した場合には、複数色の有色骨材含有塗材及び／又は着色骨材含有塗材を用いて、多色スプレーにより塗布することができる。多色スプレーにより塗布し、形成された塗膜は、より多彩感のあるものを形成することができる。その塗布方法は、必要に応じて適宜選択し、特に限定されるものではない。
Next, a method of applying the colored aggregate-containing coating material and the colored aggregate-containing coating material configured as described above will be described.
This colored aggregate-containing coating material or colored aggregate-containing coating material can be applied by a normal application method such as a brush, a roller, a spray, a trowel, and a spatula. Using an aggregate-containing coating material and / or a colored aggregate-containing coating material, it can be applied by a multicolor spray. The coating film formed by application with a multicolor spray can form a more colorful film. The application method is appropriately selected as needed, and is not particularly limited.
また、この有色骨材含有塗材又は着色骨材含有塗材を不織布などの可撓性のある基材に、前記のような手段により塗装を行ったシート状の表装材として用いることもできる。このシート状表装材は、この発明の有色骨材含有塗材又は着色骨材含有塗材と適用する部位と同じ部位に接着材を用いて、貼り付けるものである。
さらに、可撓性のない基材に有色骨材含有塗材を塗装したものを用いて建築物の外壁、内壁及び天井等に用いることもできる。
Further, the colored aggregate-containing coating material or the colored aggregate-containing coating material may be used as a sheet-like surface covering material obtained by coating a flexible base material such as a nonwoven fabric by the above-described means. The sheet-like covering material is attached to the same portion as the portion to which the colored aggregate-containing coating material or the colored aggregate-containing coating material of the present invention is applied by using an adhesive.
Furthermore, a non-flexible base material coated with a colored aggregate-containing coating material can be used for an outer wall, an inner wall, a ceiling, and the like of a building.
以上のように、この実施形態によれば次のような効果が発揮される。
・ 有色骨材と合成樹脂とを主成分とする塗材において、ＨＡＬＳを添加したものであることにより、容易に耐候性が優れた塗膜を形成することができる有色骨材含有塗材を得ることができる。
As described above, according to this embodiment, the following effects are exhibited.
A coating material containing a colored aggregate and a synthetic resin as main components to which HALS is added, thereby obtaining a coating material containing a colored aggregate that can easily form a coating film having excellent weather resistance. be able to.
・ 前記有色骨材が寒水砂及び／又は着色骨材であるものであることにより、この発明の効果が、より顕著に現れるものである。
・ 有色骨材に塗料被覆層を有する着色骨材を含有する塗材において、その塗料被覆層にＨＡＬＳを含有したものであることにより、容易に耐候性が優れた塗膜を形成することができる有色骨材含有塗材を得ることができる。
-The effect of this invention appears more remarkably by the said colored aggregate being cold water sand and / or colored aggregate.
In a coating material containing a colored aggregate having a paint coating layer on a colored aggregate, a coating film having excellent weather resistance can be easily formed because the paint coating layer contains HALS. A colored aggregate-containing coating material can be obtained.
・ 有色骨材含有塗材に用いられる有色骨材の粒子径は、３７〜２０００μｍの範囲のものであることにより、有色骨材含有塗材より得られる塗膜の多彩感が少なく意匠性のある塗材であり、その塗材の安定性、塗布作業の作業性などが良いものである。 ・ The particle size of the colored aggregate used in the colored aggregate-containing coating material is in the range of 37 to 2000 μm, so that the coating film obtained from the colored aggregate-containing coating material has less versatility and has designability. It is a coating material having good stability of the coating material, workability of the coating operation, and the like.
・ 前記合成樹脂がとしては、硬化及び乾燥後に透明のフィルムを形成するものであることにより、有色骨材の色調、風合いを生かし、意匠感を高めるものである。
・ 前記ＨＡＬＳの粒子径が０．１μｍ〜１０μｍの範囲のものであることにより、入手が容易で、塗膜の意匠に影響を与えないものである。
-The synthetic resin forms a transparent film after curing and drying, thereby making use of the color tone and texture of the colored aggregate to enhance the design.
-HALS having a particle size in the range of 0.1 μm to 10 μm makes it easy to obtain and does not affect the design of the coating film.
・ 前記ＨＡＬＳの添加量が塗材固形分１００重量部中に、０．０１重量部〜１．０重量部の範囲であることにより、有色骨材含有塗材により形成された塗膜の耐候性の向上を期待することができるものである。
・ さらに、ＵＶＡ及び／又は酸化防止剤を添加することにより、より塗膜の耐候性を増すことがあるものである。
When the amount of the HALS added is in the range of 0.01 to 1.0 part by weight based on 100 parts by weight of the solid content of the coating material, the weather resistance of the coating film formed from the coating material containing the colored aggregate is adjusted. Can be expected to improve.
Further, the weather resistance of the coating film may be further increased by adding UVA and / or an antioxidant.
・ 着色骨材の塗料被覆層を形成させるための塗料中の合成樹脂成分１００重量部に対して、ＨＡＬＳを０．１重量部〜３．０重量部の範囲で添加したことにより、その着色骨材を含有した有色骨材含有塗材により形成された塗膜の耐候性の向上させることができる。 ・ HALS was added in an amount of 0.1 to 3.0 parts by weight to 100 parts by weight of the synthetic resin component in the paint for forming the paint coating layer of the colored aggregate, whereby the colored bone was The weather resistance of the coating film formed by the colored aggregate-containing coating material containing the material can be improved.
・ 着色骨材含有塗材にＨＡＬＳを含有した被覆層を有する着色骨材を塗材の固形分中でのその着色骨材含有率は、２０〜８０重量％であることにより、ＨＡＬＳによる効果があるものである。 ・ The effect of HALS is obtained by the fact that the content of the colored aggregate in the solid content of the colored aggregate having a coating layer containing HALS in the colored aggregate-containing coating material is 20 to 80% by weight. There is something.
乾燥し造膜した後に透明となる合成樹脂としては、アクリル系合成樹脂エマルションでガラス転移温度が１０℃、固形分が４５％のものを用いた。 (4) An acrylic synthetic resin emulsion having a glass transition temperature of 10 ° C. and a solid content of 45% was used as a synthetic resin which becomes transparent after drying and forming a film.
有色骨材は、寒水砂、珪砂に着色を施した赤色のものを用いた。寒水砂は、平均粒子径が５５μｍのものと５００μｍのものの２種類を用いた。着色骨材には、目開きが３００μｍと８５０μｍの篩を用い、３００μｍ以上８５０μｍ未満の粒子径の範囲に納まるものを用いた。着色に用いられた着色成分は、アクリル系合成樹脂エマルションを主成分としたエナメル塗料を用いた。
その他の成分として、造膜助剤、消泡剤、分散剤、湿潤剤、増粘剤を用いた。下記に塗材配合例を示す。
The colored aggregate used was cold water sand or silica sand colored in red. Two types of cold water sand having an average particle diameter of 55 μm and 500 μm were used. As the colored aggregate, sieves having openings of 300 μm and 850 μm were used, and those having a particle diameter in a range of 300 μm or more and less than 850 μm were used. As a coloring component used for coloring, an enamel paint containing an acrylic synthetic resin emulsion as a main component was used.
As other components, a film forming aid, an antifoaming agent, a dispersant, a wetting agent, and a thickener were used. The following shows examples of coating material formulations.
塗材配合例
アクリル系合成樹脂エマルション ２５０．０（ｇ）
寒水砂 ５００．０（ｇ）
着色骨材 ５００．０（ｇ）
造膜助剤 ３０．０（ｇ）
消泡剤 ２．０（ｇ）
分散剤 １．０（ｇ）
湿潤剤 ０．５（ｇ）
増粘剤 １．０（ｇ）
配合水 １５．５（ｇ）
合 計 １３００．０（ｇ）
Coating material composition example Acrylic synthetic resin emulsion 250.0 (g)
Cold water sand 500.0 (g)
Colored aggregate 500.0 (g)
Film-forming aid 30.0 (g)
Defoamer 2.0 (g)
Dispersant 1.0 (g)
0.5 (g) wetting agent
Thickener 1.0 (g)
Formulation water 15.5 (g)
Total 1300.0 (g)
実施例１として、塗材配合例の配合にＨＡＬＳを添加し、その添加された有色骨材含有塗材をスプレーにより、厚みが３ｍｍ程度になるようにスレート板に塗布し、試験体を得た。
有色骨材含有塗材に添加したＨＡＬＳは、テトラメチルペピリジンの数が４の１，２，２，６，６−ペンタメチル−４−ピペリジル／トリデシル１，２，３，４ブタンテトラカルボキシラートを用いた。このＨＡＬＳの平均分子量は、約９００であり、平均粒子径が０．５μｍのものである。
その添加量は、塗材固形分１００重量部中に、１．０重量部添加した。
As Example 1, HALS was added to the formulation of the coating material formulation, and the added colored aggregate-containing coating material was applied to a slate plate by spraying so as to have a thickness of about 3 mm to obtain a test body. .
HALS added to the colored aggregate-containing coating material is 1,2,2,6,6-pentamethyl-4-piperidyl / tridecyl 1,2,3,4 butanetetracarboxylate having 4 tetramethylpepyridines. Using. The HALS has an average molecular weight of about 900 and an average particle size of 0.5 μm.
The amount added was 1.0 part by weight based on 100 parts by weight of the solid content of the coating material.
実施例２として、塗材配合例の配合に用いられる着色骨材の被覆に用いられるエナメル塗料にＨＡＬＳを添加したものを用いた。その塗材により実施例１と同様な試験体を作成した。用いられたＨＡＬＳは、実施例１で用いられたものと同じものである。
また、その添加量は、塗料中の合成樹脂成分１００重量部に対して、ＨＡＬＳを２．０重量部添加した。
In Example 2, a material obtained by adding HALS to an enamel paint used for coating a colored aggregate used in the formulation of the coating material formulation was used. A test specimen similar to that of Example 1 was prepared from the coating material. The HALS used is the same as that used in Example 1.
The amount of HALS was 2.0 parts by weight based on 100 parts by weight of the synthetic resin component in the coating material.
比較例１として、塗材配合例の塗材をスプレーにより、厚みが３ｍｍ程度になるようにスレート板に塗布した。また、比較例２として、塗材配合例の塗材をスプレーにより、厚みが３ｍｍ程度になるようにスレート板に塗布した後に、シリコーン系の溶剤クリアーを塗布した。 As Comparative Example 1, the coating material of the coating material formulation was applied to a slate plate by spraying so as to have a thickness of about 3 mm. As Comparative Example 2, the coating material of the coating material formulation was applied to a slate plate by spraying so as to have a thickness of about 3 mm, and then a silicone-based solvent clear was applied.
実施例１、実施例２、比較例１及び比較例２の試験体を１年間の暴露試験を行った。暴露試験は、３階建ての建物の屋上に設置した南面３０°条件の暴露台に試験体を置いて行った。暴露台を設置している建物の屋上は、冬至、夏至においても太陽光を遮る障害物ない場所であった。 (4) The test specimens of Example 1, Example 2, Comparative Example 1 and Comparative Example 2 were subjected to a one-year exposure test. The exposure test was performed by placing the test specimen on an exposure table on a south-facing 30 ° condition installed on the roof of a three-story building. The roof of the building where the exposure table was installed was a place where there was no obstruction to block sunlight even in the winter solstice and summer solstice.
実施例１、実施例２及び比較例２の試験体の暴露試験をした後の劣化の程度は、どの試験体も大差がないものであり、ほとんど劣化状態のない健全な塗膜であった。しかし、比較例１の試験体は、塗膜の退色が激しかった。
比較例２は、塗材を塗布した後にシリコーン系の溶剤クリアーを塗布しているため劣化がほとんど無いものであったことが言える。また、実施例１は塗材中にＨＡＬＳを添加したことにより、実施例２では、着色骨材の被覆層にＨＡＬＳを含有させたことにより、劣化がほとんど無いものであった。
The degree of deterioration of the test pieces of Example 1, Example 2 and Comparative Example 2 after the exposure test was not significantly different in any of the test pieces, and was a sound coating film with almost no deterioration state. However, the test piece of Comparative Example 1 suffered severe color fading of the coating film.
In Comparative Example 2, it can be said that there was almost no deterioration because the silicone-based solvent clear was applied after the coating material was applied. In addition, in Example 1, HALS was added to the coating material, and in Example 2, HALS was contained in the coating layer of the colored aggregate, so that there was almost no deterioration.
次に、前記実施形態から把握できる技術的思想について以下に記載する。
・ 前記合成樹脂が硬化及び乾燥後に透明のフィルムを形成するものであることを特徴とする請求項１に記載の有色骨材含有塗料。
このことにより、有色骨材の色調、風合いを生かし、意匠感を高めるものである。
Next, technical ideas that can be grasped from the embodiment will be described below.
The colored aggregate-containing paint according to claim 1, wherein the synthetic resin forms a transparent film after curing and drying.
This enhances the design feeling by utilizing the color tone and texture of the colored aggregate.
・ 前記ＨＡＬＳの粒子径が０．１μｍ〜１０μｍの範囲のものであることを特徴とする請求項１に記載の有色骨材含有塗料。
このことにより、入手が容易で、塗膜の意匠に影響を与えないものである。
The colored aggregate-containing paint according to claim 1, wherein the particle size of the HALS is in a range of 0.1 µm to 10 µm.
This makes it easy to obtain and does not affect the design of the coating film.
・ 前記ＨＡＬＳの添加量が塗材１００重量部に対して、０．０１重量部〜１．０重量部の範囲であることを特徴とする請求項１に記載の有色骨材含有塗料。
このことにより、有色骨材含有塗材により形成された塗膜の耐候性の向上を期待することができるものである。
The colored aggregate-containing paint according to claim 1, wherein the amount of the HALS added is in the range of 0.01 to 1.0 part by weight based on 100 parts by weight of the coating material.
This can be expected to improve the weather resistance of the coating film formed by the colored aggregate-containing coating material.
・ さらに、ＵＶＡ及び／又は酸化防止剤を添加することを特徴とする請求項１に記載の有色骨材含有塗料。
このことにより、より塗膜の耐候性を増すものである。
The colored aggregate-containing paint according to claim 1, further comprising a UVA and / or an antioxidant.
Thereby, the weather resistance of the coating film is further increased.
・ 着色骨材含有塗材にＨＡＬＳを含有した被覆層を有する着色骨材を塗材の固形分中でのその着色骨材含有率は、２０〜８０重量％であることを特徴とする請求項３に記載の着色骨材含有塗料。
このことにより、ＨＡＬＳによる効果があるものである。
The colored aggregate having a coating layer containing HALS in the colored aggregate-containing coating material, wherein the content of the colored aggregate in the solid content of the coating material is 20 to 80% by weight. 4. The colored aggregate-containing paint according to 3.
This has the effect of HALS.
Claims (3)
What is claimed is: 1. A coating material containing a colored aggregate comprising a colored aggregate having a coating layer on a colored aggregate, wherein the coating layer comprises a hindered amine light stabilizer (HALS).