JP2004091875A - Germanium alloy-silica composite, thin film using the same, laminated body, accessory and coating material - Google Patents
Germanium alloy-silica composite, thin film using the same, laminated body, accessory and coating material Download PDFInfo
- Publication number
- JP2004091875A JP2004091875A JP2002256185A JP2002256185A JP2004091875A JP 2004091875 A JP2004091875 A JP 2004091875A JP 2002256185 A JP2002256185 A JP 2002256185A JP 2002256185 A JP2002256185 A JP 2002256185A JP 2004091875 A JP2004091875 A JP 2004091875A
- Authority
- JP
- Japan
- Prior art keywords
- germanium
- alloy
- germanium alloy
- thin film
- silica
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】
【発明の属する技術分野】
本発明は、ゲルマニウム合金−シリカ複合体、ゲルマニウム合金−シリカ複合体薄膜、積層体、装身具及びコーティング剤に関する。
【０００２】
【従来の技術】
ゲルマニウム−インジウム合金は、遠赤外線を発して健康増進効果や治療効果を発揮することが知られており、銀との合金は上記効果を奏する装身具用の合金として適用可能であることが知られている（特許３０２５２４５号公報）。
【０００３】
【発明が解決しようとする課題】
しかし、装身具を構成する基材は、真珠等金属以外の材質からなるものも多く、かかる材料にゲルマニウム−インジウム合金を混成させたり、高い堅牢性を備えた被覆を形成させて、健康増進や治療効果を発揮する装身具を作成することは非常に困難である。
【０００４】
一方、装身具の基材には金、プラチナ、ステンレス等の金属が多く用いられており、かかる金属にゲルマニウム−インジウム合金を添加して合金を得ることが可能であるが、上記効果は主に表面付近に存在するゲルマニウム−インジウム合金に起因するものであるため、充分な効果を得るためには高価なゲルマニウム−インジウム合金を多く添加する必要がある。また、表面にゲルマニウム−インジウム合金を析出させる方法には困難性が伴う。
【０００５】
そこで、本発明の目的は、金属、セラミック、樹脂、天然素材を始めとする種々の基材に容易に薄膜を形成可能なゲルマニウム−インジウム合金を含む材料であって、遠赤外線に基づく健康増進効果や治療効果を発揮し得る材料を提供することにある。本発明の目的はまた、かかる材料を用いた薄膜、かかる薄膜を備える積層体及び装身具、並びに、かかる薄膜を形成するためのコーティング剤を提供することにある。
【０００６】
【課題を解決するための手段】
上記目的を達成するために、本発明は、ゲルマニウム合金とシリカとを含むゲルマニウム合金−シリカ複合体であって、前記ゲルマニウム合金は、ゲルマニウムと、該ゲルマニウムに対して重量比で２〜２０％のインジウムと、を含むゲルマニウム合金であり、前記ゲルマニウム合金は、粒子形状をなして前記シリカ中で分散していることを特徴とするゲルマニウム合金−シリカ複合体を提供する。
【０００７】
上記組成のゲルマニウム−インジウム合金は、遠赤外線に基づく健康増進効果や治療効果を奏し得る合金であり、かかる合金が種々の基材に対する密着性に優れたシリカ中に分散されていることから、本発明のゲルマニウム合金−シリカ複合体は、金属、セラミック、樹脂、天然素材を始めとする種々の基材に容易に薄膜を形成可能であり、形成された薄膜は健康増進効果や治療効果を発揮する。
【０００８】
ゲルマニウムの重量比は、ゲルマニウム合金−シリカ複合体の全重量を基準として、０．０００１〜９０重量％であることが好ましく、ゲルマニウム合金の粒子の平均粒径が５０μｍ以下であることが好ましい。
【０００９】
ゲルマニウム又はゲルマニウム合金が、上記要件を具備する場合には、高い健康増進効果や治療効果が得られるばかりでなく、薄膜の透明性が優れているために、例えば、金の表面に薄膜を形成させた場合に金の光沢を保つことも可能になる。
【００１０】
本発明はまた、上記本発明のゲルマニウム合金−シリカ複合体からなることを特徴とするゲルマニウム合金−シリカ複合体薄膜を提供する。ここで、ゲルマニウム合金の粒子の面密度が１％以下であることが好ましい。かかる薄膜は、高い健康増進効果や治療効果を発揮し、高い透明性に基づいて薄膜を形成する基材の外観を損ねることがない。また、本発明にかかる薄膜は、堅牢性に優れることから高い耐久性を発揮する。
【００１１】
本発明は更に、基材と、該基材上に形成された、上記ゲルマニウム合金−シリカ複合体薄膜と、を備えることを特徴とする積層体を提供する。ここで、基材は、少なくとも、ゲルマニウム合金−シリカ複合体薄膜が形成された面が、金からなることが好ましい。かかる基材としては金、金鍍金がなされた金属等が挙げられる。
【００１２】
本発明はまた、身体に装用した状態で皮膚に接触する外表面に、上記ゲルマニウム合金−シリカ複合体薄膜を備えることを特徴とする装身具を提供する。かかる装身具は身体に装用するものであることから、高い健康増進効果や治療効果を得ることができる。また、薄膜の透明性に基づいて美麗性にも優れる。
【００１３】
本発明は更に、ゲルマニウムと該ゲルマニウムに対して重量比で２〜２０％のインジウムとを含むゲルマニウム合金の微粒子と、シリカ前駆体と、を含むことを特徴とするコーティング剤を提供する。ここで、シリカ前駆体は、ポリシラザンであることが好ましい。
【００１４】
かかるコーティング剤は、ゲルマニウム合金がシリカ前駆体に分散、混合されたものであるために、種々の基材にゲルマニウム合金−シリカ複合体薄膜を形成することができる。シリカ前駆体がポリシラザンである場合は、室温付近でもシリカ膜を形成できることから、加熱に弱い樹脂や天然素材等にも、ゲルマニウム合金−シリカ複合体薄膜を形成することができる。
【００１５】
【発明の実施の形態】
（ゲルマニウム合金−シリカ複合体）
ゲルマニウム合金−シリカ複合体は、ゲルマニウムと、該ゲルマニウムに対して重量比で２〜２０％のインジウムと、を含むゲルマニウム合金（ゲルマニウム−インジウム合金）を有している。
【００１６】
ゲルマニウムはそれ自体遠赤外効果を有しており、肩凝り等を治療・治癒する健康増進、治療効果を発揮する。ゲルマニウムの遠赤外効果は、ゲルマニウム合金−シリカ複合体中でゲルマニウムの微結晶が形成されているときに、特に効果的に発揮される。この理由は、ゲルマニウムの微結晶は微小ながらも結晶であることから、半導体的な性質を持つためである。したがって、ゲルマニウムの量はゲルマニウムが微結晶を形成し得る量であることが好ましい。
【００１７】
ゲルマニウムの遠赤外効果は、Ｎ型あるいは真性の半導体のときに比べて、Ｐ型のときに著しく顕著に発揮されるが、インジウムはＩＩＩ族元素であって半導体に添加されるとアクセプターとなり、Ｐ型をもたらす。したがって、本発明のようにゲルマニウム−インジウム合金を用いることで、遠赤外効果が増強される。そして、かかる観点からはゲルマニウムに対するインジウムの重量比を１３％未満とすることが好ましい。なお、ゲルマニウム−インジウム合金等のゲルマニウム合金又はゲルマニウムの健康増進、治療効果については、特許３０２５２４５号を参照することができる。
【００１８】
また、ゲルマニウム合金−シリカ複合体の全重量を基準としたゲルマニウムの重量比は、その下限が０．００１重量％であることが好ましく、０．０１重量％であることがより好ましく、０．１重量％であることが更に好ましく、１重量％であることが特に好ましい。一方上限は、８０重量％であることが好ましく、７０重量％であることがより好ましく、６０重量％であることが更に好ましく、５０重量％であることが特に好ましい。
【００１９】
ゲルマニウム−インジウム合金の平均粒径は、その下限が０．０１μｍであることが好ましく、０．１μｍであることがより好ましい。一方上限は３０μｍであることが好ましく、１０μｍであることがより好ましく、５μｍであることが更に好ましい。特に好適な平均粒径は０．１〜５μｍ（更には０．１〜０．５μｍ）である。なお、ゲルマニウム−インジウム合金はシリカ中で二次粒子を形成する場合があるが、上記平均粒径は一次粒子の平均粒径を意味する。また、ゲルマニウム−インジウム合金はシリカ中で二次粒子を形成せずに、一次粒子として分散されていることが好ましい。
【００２０】
（ゲルマニウム合金−シリカ複合体薄膜）
ゲルマニウム合金−シリカ複合体薄膜は、充分な膜強度を得る観点から、ゲルマニウム−インジウム合金の粒子の平均粒径以上の膜厚を有していることが好ましい。好適な膜厚は、０．１〜５μｍ（更には０．１〜１μｍ）である。
【００２１】
ゲルマニウム合金−シリカ複合体薄膜におけるゲルマニウム−インジウム合金の粒子の面密度は、ゲルマニウム−インジウム合金の粒子の平均粒径に基づいて決定することができる。すなわち、ゲルマニウム合金−シリカ複合体薄膜は基材上に皮膜として形成される場合があり、かかる場合においては基材表面の材質や光沢を損なわないような透明性が要求されるため、かかる観点からゲルマニウム−インジウム合金の粒子の面密度が選択される。例えば、ゲルマニウム−インジウム合金の粒子の平均粒径が５０μｍである場合は、面密度を１０％以上にすると茶褐色の着色が生じる。したがって、ゲルマニウム−インジウム合金の粒子の平均粒径を５０μｍ以下とし面密度を１％以下とすることが好ましい。
【００２２】
（積層体）
本発明にかかる積層体は、基材上に上記ゲルマニウム合金−シリカ複合体薄膜を備えるものであり、膜厚の好適な範囲は上述のとおりであり、薄膜中におけるゲルマニウム−インジウム合金の粒子の面密度の好適な範囲も上記と同様である。基材としては、ガラス、金属、樹脂、フィルム材料、木材、石材等が挙げられるが、装身具として適用が容易な金属又は樹脂が好ましく、金又は金鍍金された金属若しくは樹脂が好ましい。
【００２３】
（装身具）
本発明の装身具は、身体に装用した状態で皮膚に接触する外表面に、上述したゲルマニウム合金−シリカ複合体薄膜（好適条件も上記と同様）を備えたものであるために、装身具として求められる以下の６要件が満たされる。
１）身に付ける装飾具としての充分な輝きと光沢を持っている。
２）適度の硬度と延性、展性を備えている。
３）耐酸化性、その他の耐腐食性に優れている。
４）身に付けて用いるのに安全な素材である。
５）いたずらに高価な材料を必要としない。
６）遠赤外効果つまり肩凝りを治療・治癒する等の健康増進、治療効果が十分に発揮される。
【００２４】
上記１）はゲルマニウム合金−シリカ複合体薄膜の透明性に起因して得られ、上記２）はゲルマニウム合金−シリカ複合体薄膜の強靭さに基づくものである。また、上記３）、４）及び５）はゲルマニウム合金−シリカ複合体におけるシリカの化学的安定性に由来している。特に４）に関して、薄膜を形成させる基材を金としたときに顕著な効果が得られる。すなわち、金は時としてアレルギー反応を引き起こすが、金の表面をシリカで覆うことによりアレルギーを防止できる。
【００２５】
上記６）は、ゲルマニウム合金−シリカ複合体薄膜が含有するゲルマニウム−インジウム合金の粒子に起因するものである。本発明の装身具においては、ゲルマニウム合金−シリカ複合体が薄膜として形成されているために、シリカを遠赤外線が充分に通過し、健康増進及び治療効果が減じることはない。
【００２６】
（コーティング剤）
本発明のコーティング剤は、上述したゲルマニウム−インジウム合金の微粒子と、シリカ前駆体と、を含んでいる。なお、シリカ前駆体とは、物理的、化学的変化によりシリカを生じる化合物をいう。
【００２７】
コーティング剤は、塗布の容易性の観点から室温で流動性を有することが好ましく、流動性の向上のために溶剤を含有していてもよい。また、シリカ前駆体から効果的にシリカが形成するように触媒を含んでいてもよい。
【００２８】
また、ゲルマニウム−インジウム合金の健康増進及び治療効果を発揮させるために、平均粒径は、その下限が０．０１μｍであることが好ましく、０．１μｍであることがより好ましい。一方上限は３０μｍであることが好ましく、１０μｍであることがより好ましく、５μｍであることが更に好ましい。特に好適な平均粒径は０．１〜５μｍ（好ましくは０．１〜１μｍ、更には０．１〜０．５μｍ）である。
【００２９】
コーティング剤におけるゲルマニウム−インジウム合金の微粒子の重量比は、ゲルマニウム合金−シリカ複合体が形成された場合に、その重量を基準としてゲルマニウムの重量比が０．０００１〜９０重量％（好ましくは０．００１〜８０重量％、より好ましくは０．０１〜７０重量％、更には０．１〜６０重量％、特には１〜５０重量％）となるような重量比であることが好ましい。
【００３０】
シリカ前駆体としては、テトラメトキシシランやテトラエトキシシラン等のアルコキシシランやポリシラザンが挙げられるが、低温（室温等）でシリカ形成が可能であることからポリシラザンが好ましい。また、シリカ前駆体としてポリシラザンを用いる場合には、低温硬化用の触媒を併用することが好ましい。
【００３１】
本発明のコーティング剤を基材に塗布して、シリカ前駆体をシリカへと変化させることによりシリカ中にゲルマニウム−インジウム合金の微粒子が分散したゲルマニウム合金−シリカ複合体の薄膜が形成される。
【００３２】
かかる薄膜は、スピンコート、ロールコート、スプレー塗布等の公知の塗布方法を用いて本発明のコーティング剤を塗布した後に、必要により溶剤等の揮発成分を除去して、シリカ前駆体の反応条件に合わせた条件に塗布物を晒すことにより得ることができる。例えば、シリカ前駆体がアルコキシシランである場合は加熱により加水分解及び縮合を効果的に進行させることができ、ポリシラザンの場合は、触媒の存在下で水蒸気を使用することができる。なお、ポリシラザンを用いた場合は室温でもシリカを形成させることができるために、加熱に弱い材料を基材とする場合に特に有効である。
【００３３】
【実施例】
以下、本発明の好適な実施例についてさらに詳細に説明するが、本発明はこれらの実施例に限定されるものではない。
【００３４】
ネックレスの表面に本発明のゲルマニウム合金−シリカ複合体薄膜等を形成させる実験を行った。図１は薄膜を形成させたネックレスを示す図であり、表面の顕微鏡観察は図１のＡで示されるネックレスの平坦部を使用した。
【００３５】
先ず、シリカ前駆体であるポリシラザンのみを図１に示すのと同様の形状の金ネックレスに塗布して、ポリシラザンをシリカに変化させた。図２は、得られたシリカ薄膜のレーザ顕微鏡写真である。次に、シリカ薄膜上に、ゲルマニウムと該ゲルマニウムに対して重量比で２〜２０％のインジウムとを含むゲルマニウム合金（本実施例において「ＧｅＩｎ合金」）と記載する。）粉末を単に降りかけたものを作製し、その表面を観察した。
【００３６】
図３はかかる表面のレーザ顕微鏡写真であり、同図に示すように種々のサイズのＧｅＩｎ合金粒子が観察された。図４は、図３と同一表面のレーザ顕微鏡写真であり、Ａ、Ｂ、Ｃ及びＤの矢印で指し示した粒子はＧｅＩｎ合金粒子である。図４中の破線で囲まれた曲線は表面の凹凸を示すものであるが、矢印で指し示した粒子はいずれも０．６９μｍの厚さを有していた。この結果から、Ａ、Ｂ、Ｃ及びＤの矢印で指し示した粒子は、ＧｅＩｎ合金粒子が平面状に固まって生じた二次粒子であることが分かった。
【００３７】
次いで、ＧｅＩｎ合金粒子をポリシラザンに添加してコーティング剤を作製し、図１に示すのと同様の形状の真鍮に金鍍金したネックレスに塗布して、１００℃で１時間加熱してポリシラザンをシリカに変化させ、ネックレスの表面にゲルマニウム合金−シリカ複合体薄膜を形成させた。図５は薄膜が形成されていない真鍮に金鍍金したネックレスの表面のレーザ顕微鏡写真であり、図６は上述のようにしてゲルマニウム合金−シリカ複合体薄膜が形成されたネックレス表面のレーザ顕微鏡写真である。図６においては、１〜２μｍ径のＧｅＩｎ合金粒子が観察され下地の金色は損なわれなかった。なお、ＧｅＩｎ合金粒子は２０μｍ平方あたり３〜４個存在していた。
【００３８】
図７は、図６のネックレスにおいてゲルマニウム合金−シリカ複合体薄膜が形成されていない領域を含む箇所のレーザ顕微鏡写真である。図８は、図７と同一表面のレーザ顕微鏡写真であり、ゲルマニウム合金−シリカ複合体薄膜が形成されていない領域を利用してシリカの膜厚を測定したものである。図８によれば、ゲルマニウム合金−シリカ複合体薄膜におけるシリカの膜厚は１μｍであった。
【００３９】
図９は、図６における場合よりもＧｅＩｎ合金粒子の数を増加させて、真鍮に金鍍金したネックレスに形成したゲルマニウム合金−シリカ複合体薄膜のレーザ顕微鏡写真である。図９の左上にはＧｅＩｎ合金粒子が密集した領域が存在しており、かかる部分の色は灰色を帯びていた。図１０は、図９と同一表面のレーザ顕微鏡写真であり、同図によればゲルマニウム合金−シリカ複合体薄膜におけるシリカの膜厚は０．８９μｍであった。
【００４０】
【発明の効果】
以上説明したように、本発明によれば、金属、セラミック、樹脂、天然素材を始めとする種々の基材に容易に薄膜を形成可能なゲルマニウム−インジウム合金を含む材料であって、遠赤外線に基づく健康増進効果や治療効果を発揮し得る材料が提供される。また、かかる材料を用いた薄膜、かかる薄膜を備える積層体及び装身具、並びに、かかる薄膜を形成するためのコーティング剤が提供される。
【図面の簡単な説明】
【図１】ゲルマニウム合金−シリカ複合体薄膜等を形成させたネックレスを示す図である。
【図２】金ネックレスに形成されたシリカ薄膜のレーザ顕微鏡写真である。
【図３】図２の表面にゲルマニウム合金粉末を降りかけた表面のレーザ顕微鏡写真である。
【図４】図３と同一表面のレーザ顕微鏡写真である。
【図５】薄膜が形成されていない、真鍮に金鍍金したネックレスの表面のレーザ顕微鏡写真である。
【図６】ゲルマニウム合金−シリカ複合体薄膜が形成されたネックレス表面のレーザ顕微鏡写真である。
【図７】図６のネックレスにおいてゲルマニウム合金−シリカ複合体薄膜が形成されていない領域を含む箇所のレーザ顕微鏡写真である。
【図８】図７と同一表面のレーザ顕微鏡写真である。
【図９】図６における場合よりもＧｅＩｎ合金粒子の数を増加させて、真鍮に金鍍金したネックレスに形成したゲルマニウム合金−シリカ複合体薄膜のレーザ顕微鏡写真である。
【図１０】図９と同一表面のレーザ顕微鏡写真である。[0001]
BACKGROUND OF THE INVENTION
The present invention relates to a germanium alloy-silica composite, a germanium alloy-silica composite thin film, a laminate, a jewelry, and a coating agent.
[0002]
[Prior art]
Germanium-indium alloys are known to emit far-infrared rays and exhibit health promotion effects and therapeutic effects, and alloys with silver are known to be applicable as alloys for jewelry that exhibit the above effects. (Japanese Patent No. 3025245).
[0003]
[Problems to be solved by the invention]
However, many of the base materials that make up jewelry are made of materials other than metals such as pearls, and such materials are mixed with germanium-indium alloys or coated with high robustness to promote health and treatment. It is very difficult to create an accessory that can be effective.
[0004]
On the other hand, metals such as gold, platinum, and stainless steel are often used for the base material of jewelry, and it is possible to obtain an alloy by adding a germanium-indium alloy to such a metal. Since it is caused by the germanium-indium alloy existing in the vicinity, it is necessary to add a large amount of expensive germanium-indium alloy in order to obtain a sufficient effect. Also, the method of depositing a germanium-indium alloy on the surface involves difficulty.
[0005]
Therefore, an object of the present invention is a material containing a germanium-indium alloy capable of easily forming a thin film on various base materials including metals, ceramics, resins, and natural materials, and has a health promotion effect based on far infrared rays. It is to provide a material capable of exerting a therapeutic effect. Another object of the present invention is to provide a thin film using such a material, a laminate and an accessory comprising the thin film, and a coating agent for forming the thin film.
[0006]
[Means for Solving the Problems]
To achieve the above object, the present invention provides a germanium alloy-silica composite containing a germanium alloy and silica, the germanium alloy having a weight ratio of 2 to 20% with respect to germanium and the germanium. A germanium alloy containing indium, wherein the germanium alloy has a particle shape and is dispersed in the silica to provide a germanium alloy-silica composite.
[0007]
The germanium-indium alloy having the above composition is an alloy that can exert a health promoting effect and a therapeutic effect based on far-infrared rays, and such an alloy is dispersed in silica having excellent adhesion to various substrates. The germanium alloy-silica composite of the invention can easily form a thin film on various base materials including metals, ceramics, resins and natural materials, and the formed thin film exhibits a health promotion effect and a therapeutic effect. .
[0008]
The weight ratio of germanium is preferably 0.0001 to 90% by weight based on the total weight of the germanium alloy-silica composite, and the average particle diameter of the germanium alloy particles is preferably 50 μm or less.
[0009]
When germanium or a germanium alloy has the above requirements, not only a high health promotion effect and a therapeutic effect can be obtained, but also the thin film has excellent transparency. In this case, it is possible to keep the gloss of gold.
[0010]
The present invention also provides a germanium alloy-silica composite thin film comprising the germanium alloy-silica composite of the present invention. Here, the surface density of the germanium alloy particles is preferably 1% or less. Such a thin film exhibits a high health promoting effect and a therapeutic effect, and does not impair the appearance of the substrate on which the thin film is formed based on high transparency. Moreover, since the thin film concerning this invention is excellent in robustness, it exhibits high durability.
[0011]
The present invention further provides a laminate comprising a base material and the germanium alloy-silica composite thin film formed on the base material. Here, it is preferable that at least the surface on which the germanium alloy-silica composite thin film is formed is made of gold. Examples of such a base material include gold and metal plated with gold.
[0012]
The present invention also provides a clothing accessory comprising the germanium alloy-silica composite thin film on the outer surface that comes into contact with the skin while worn on the body. Since such an accessory is worn on the body, a high health promotion effect and a therapeutic effect can be obtained. Moreover, it is excellent also in beauty based on the transparency of a thin film.
[0013]
The present invention further provides a coating agent comprising germanium alloy fine particles containing germanium and 2 to 20% by weight of indium with respect to the germanium, and a silica precursor. Here, the silica precursor is preferably polysilazane.
[0014]
Since such a coating agent is a germanium alloy dispersed and mixed in a silica precursor, a germanium alloy-silica composite thin film can be formed on various substrates. When the silica precursor is polysilazane, the silica film can be formed even near room temperature. Therefore, the germanium alloy-silica composite thin film can be formed also on a resin or natural material that is vulnerable to heating.
[0015]
DETAILED DESCRIPTION OF THE INVENTION
(Germanium alloy-silica composite)
The germanium alloy-silica composite has a germanium alloy (germanium-indium alloy) containing germanium and 2 to 20% by weight of indium with respect to the germanium.
[0016]
Germanium itself has a far-infrared effect, and exerts a health promotion and therapeutic effect for treating and healing stiff shoulders. The far-infrared effect of germanium is particularly effective when germanium microcrystals are formed in the germanium alloy-silica composite. This is because germanium microcrystals are semi-crystalline but have semiconducting properties. Therefore, the amount of germanium is preferably such that germanium can form microcrystals.
[0017]
The far-infrared effect of germanium is remarkably exerted in the P-type as compared with the N-type or intrinsic semiconductor, but indium is a group III element and becomes an acceptor when added to the semiconductor. This results in P type. Therefore, the far-infrared effect is enhanced by using a germanium-indium alloy as in the present invention. From this viewpoint, it is preferable that the weight ratio of indium to germanium is less than 13%. For the health promotion and therapeutic effect of germanium alloys such as germanium-indium alloy or germanium, Japanese Patent No. 3025245 can be referred to.
[0018]
The lower limit of the weight ratio of germanium based on the total weight of the germanium alloy-silica composite is preferably 0.001% by weight, more preferably 0.01% by weight, More preferably, it is more preferably 1% by weight. On the other hand, the upper limit is preferably 80% by weight, more preferably 70% by weight, still more preferably 60% by weight, and particularly preferably 50% by weight.
[0019]
The lower limit of the average particle diameter of the germanium-indium alloy is preferably 0.01 μm, and more preferably 0.1 μm. On the other hand, the upper limit is preferably 30 μm, more preferably 10 μm, still more preferably 5 μm. A particularly preferable average particle diameter is 0.1 to 5 μm (further, 0.1 to 0.5 μm). In addition, although a germanium-indium alloy may form a secondary particle in a silica, the said average particle diameter means the average particle diameter of a primary particle. The germanium-indium alloy is preferably dispersed as primary particles without forming secondary particles in silica.
[0020]
(Germanium alloy-silica composite thin film)
The germanium alloy-silica composite thin film preferably has a film thickness equal to or larger than the average particle diameter of germanium-indium alloy particles from the viewpoint of obtaining sufficient film strength. A suitable film thickness is 0.1-5 micrometers (further 0.1-1 micrometers).
[0021]
The surface density of the germanium-indium alloy particles in the germanium alloy-silica composite thin film can be determined based on the average particle diameter of the germanium-indium alloy particles. That is, the germanium alloy-silica composite thin film may be formed as a film on the substrate, and in such a case, transparency is required so as not to impair the material and gloss of the substrate surface. The areal density of the germanium-indium alloy particles is selected. For example, when the average particle diameter of germanium-indium alloy particles is 50 μm, brown coloration occurs when the surface density is 10% or more. Therefore, it is preferable that the average particle diameter of the germanium-indium alloy particles is 50 μm or less and the surface density is 1% or less.
[0022]
(Laminate)
The laminate according to the present invention comprises the above-described germanium alloy-silica composite thin film on a substrate, and the preferred range of the film thickness is as described above, and the surface of the germanium-indium alloy particles in the thin film The preferred range of density is the same as above. Examples of the base material include glass, metal, resin, film material, wood, stone, and the like, but metal or resin that can be easily applied as a jewelry is preferable, and gold or gold-plated metal or resin is preferable.
[0023]
(Jewelry)
The accessory of the present invention is required as an accessory because it is provided with the above-described germanium alloy-silica composite thin film (preferable conditions are the same as those described above) on the outer surface that comes into contact with the skin while worn on the body. The following 6 requirements are satisfied.
1) It has sufficient brightness and luster as decorations to be worn.
2) It has moderate hardness, ductility and malleability.
3) Excellent oxidation resistance and other corrosion resistance.
4) It is a safe material to wear and use.
5) Unnecessarily expensive materials are not required.
6) The far-infrared effect, that is, the promotion of health such as treatment and healing of stiff shoulders, and the therapeutic effect are fully exhibited.
[0024]
The above 1) is obtained due to the transparency of the germanium alloy-silica composite thin film, and the above 2) is based on the toughness of the germanium alloy-silica composite thin film. The above 3), 4) and 5) are derived from the chemical stability of silica in the germanium alloy-silica composite. Regarding 4) in particular, a remarkable effect is obtained when the base material on which the thin film is formed is gold. That is, gold sometimes causes an allergic reaction, but allergy can be prevented by covering the gold surface with silica.
[0025]
The above 6) is caused by the germanium-indium alloy particles contained in the germanium alloy-silica composite thin film. In the jewelry of the present invention, since the germanium alloy-silica composite is formed as a thin film, far-infrared rays sufficiently pass through silica, and health promotion and therapeutic effects are not reduced.
[0026]
(Coating agent)
The coating agent of the present invention contains the above-described germanium-indium alloy fine particles and a silica precursor. In addition, a silica precursor means the compound which produces a silica by a physical and chemical change.
[0027]
The coating agent preferably has fluidity at room temperature from the viewpoint of ease of application, and may contain a solvent for improving fluidity. Further, a catalyst may be included so that silica is effectively formed from the silica precursor.
[0028]
Moreover, in order to exhibit the health promotion and therapeutic effect of germanium-indium alloy, the lower limit of the average particle diameter is preferably 0.01 μm, and more preferably 0.1 μm. On the other hand, the upper limit is preferably 30 μm, more preferably 10 μm, still more preferably 5 μm. A particularly preferable average particle diameter is 0.1 to 5 μm (preferably 0.1 to 1 μm, and further 0.1 to 0.5 μm).
[0029]
When the germanium alloy-silica composite is formed, the weight ratio of the germanium-indium alloy fine particles in the coating agent is 0.0001 to 90% by weight (preferably 0.001) based on the weight. The weight ratio is preferably 80 to 80% by weight, more preferably 0.01 to 70% by weight, further 0.1 to 60% by weight, and particularly 1 to 50% by weight.
[0030]
Examples of the silica precursor include alkoxysilanes such as tetramethoxysilane and tetraethoxysilane, and polysilazanes. Polysilazanes are preferred because silica can be formed at a low temperature (such as room temperature). When polysilazane is used as the silica precursor, it is preferable to use a low-temperature curing catalyst in combination.
[0031]
By applying the coating agent of the present invention to a substrate and changing the silica precursor to silica, a germanium alloy-silica composite thin film in which fine particles of germanium-indium alloy are dispersed in silica is formed.
[0032]
Such a thin film is coated with the coating agent of the present invention using a known coating method such as spin coating, roll coating, spray coating, and the like, and then, if necessary, volatile components such as a solvent are removed to obtain reaction conditions for the silica precursor. It can be obtained by exposing the coating to the combined conditions. For example, when the silica precursor is an alkoxysilane, hydrolysis and condensation can be effectively advanced by heating. In the case of polysilazane, water vapor can be used in the presence of a catalyst. Note that when polysilazane is used, silica can be formed even at room temperature, which is particularly effective when a material vulnerable to heating is used as a base material.
[0033]
【Example】
EXAMPLES Hereinafter, although the preferable Example of this invention is described in detail, this invention is not limited to these Examples.
[0034]
An experiment was conducted in which the germanium alloy-silica composite thin film of the present invention was formed on the surface of the necklace. FIG. 1 is a view showing a necklace on which a thin film is formed, and the flat portion of the necklace shown by A in FIG.
[0035]
First, only the polysilazane which is a silica precursor was applied to a gold necklace having the same shape as shown in FIG. 1, and the polysilazane was changed to silica. FIG. 2 is a laser micrograph of the obtained silica thin film. Next, a germanium alloy (“GeIn alloy” in this embodiment) containing germanium and indium having a weight ratio of 2 to 20% with respect to the germanium is described on the silica thin film. ) A powder was simply dropped and the surface was observed.
[0036]
FIG. 3 is a laser micrograph of such a surface, and GeIn alloy particles of various sizes were observed as shown in FIG. FIG. 4 is a laser micrograph of the same surface as FIG. 3, and the particles indicated by arrows A, B, C, and D are GeIn alloy particles. The curve surrounded by the broken line in FIG. 4 indicates surface irregularities, but all of the particles pointed by the arrows had a thickness of 0.69 μm. From this result, it was found that the particles indicated by the arrows A, B, C, and D are secondary particles formed by solidifying GeIn alloy particles in a planar shape.
[0037]
Next, GeIn alloy particles are added to polysilazane to produce a coating agent, which is applied to a brass-plated necklace similar to that shown in FIG. 1 and heated at 100 ° C. for 1 hour to convert polysilazane to silica. As a result, a germanium alloy-silica composite thin film was formed on the surface of the necklace. FIG. 5 is a laser micrograph of the surface of the necklace plated with brass on which no thin film is formed, and FIG. 6 is a laser micrograph of the necklace surface on which the germanium alloy-silica composite thin film is formed as described above. is there. In FIG. 6, GeIn alloy particles having a diameter of 1 to 2 μm were observed, and the underlying gold color was not impaired. In addition, 3 to 4 GeIn alloy particles existed per 20 μm square.
[0038]
FIG. 7 is a laser micrograph of a portion including a region where the germanium alloy-silica composite thin film is not formed in the necklace of FIG. FIG. 8 is a laser micrograph of the same surface as in FIG. 7, and the silica film thickness is measured using a region where the germanium alloy-silica composite thin film is not formed. According to FIG. 8, the film thickness of silica in the germanium alloy-silica composite thin film was 1 μm.
[0039]
FIG. 9 is a laser micrograph of a germanium alloy-silica composite thin film formed on a brass-plated necklace with a larger number of GeIn alloy particles than in FIG. In the upper left of FIG. 9, there is a region where GeIn alloy particles are dense, and the color of such a portion is tinged with gray. FIG. 10 is a laser micrograph of the same surface as in FIG. 9, and according to the figure, the film thickness of silica in the germanium alloy-silica composite thin film was 0.89 μm.
[0040]
【The invention's effect】
As described above, according to the present invention, a material containing a germanium-indium alloy that can easily form a thin film on various base materials including metals, ceramics, resins, and natural materials, The material which can exhibit the health promotion effect based on this and a therapeutic effect is provided. Moreover, the thin film using such a material, the laminated body and jewelry provided with this thin film, and the coating agent for forming this thin film are provided.
[Brief description of the drawings]
FIG. 1 is a view showing a necklace on which a germanium alloy-silica composite thin film or the like is formed.
FIG. 2 is a laser micrograph of a silica thin film formed on a gold necklace.
FIG. 3 is a laser micrograph of the surface of the surface of FIG. 2 on which germanium alloy powder is applied.
4 is a laser micrograph of the same surface as FIG. 3. FIG.
FIG. 5 is a laser micrograph of the surface of a necklace made of gold-plated brass with no thin film formed thereon.
FIG. 6 is a laser micrograph of the surface of a necklace on which a germanium alloy-silica composite thin film is formed.
7 is a laser micrograph of a portion including a region where a germanium alloy-silica composite thin film is not formed in the necklace of FIG.
8 is a laser micrograph of the same surface as FIG. 7. FIG.
9 is a laser micrograph of a germanium alloy-silica composite thin film formed on a brass-plated necklace with an increased number of GeIn alloy particles than in the case of FIG.
10 is a laser micrograph of the same surface as FIG. 9. FIG.
Claims (10)
前記ゲルマニウム合金は、ゲルマニウムと、該ゲルマニウムに対して重量比で２〜２０％のインジウムと、を含むゲルマニウム合金であり、
前記ゲルマニウム合金は、粒子形状をなして前記シリカ中で分散していることを特徴とするゲルマニウム合金−シリカ複合体。A germanium alloy-silica composite containing a germanium alloy and silica,
The germanium alloy is a germanium alloy containing germanium and 2 to 20% by weight of indium with respect to the germanium,
The germanium alloy-silica composite, wherein the germanium alloy has a particle shape and is dispersed in the silica.