JP2003280528A - Label for synthetic resin bottle - Google Patents
Label for synthetic resin bottleInfo
- Publication number
- JP2003280528A JP2003280528A JP2002084763A JP2002084763A JP2003280528A JP 2003280528 A JP2003280528 A JP 2003280528A JP 2002084763 A JP2002084763 A JP 2002084763A JP 2002084763 A JP2002084763 A JP 2002084763A JP 2003280528 A JP2003280528 A JP 2003280528A
- Authority
- JP
- Japan
- Prior art keywords
- label
- synthetic resin
- adhesive
- bottle
- resin bottle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、清涼飲料水、乳飲
料、ビール、ワイン、栄養ドリンク、調味料、化粧品な
どに使用される合成樹脂ボトルの表面に付けるラベル、
及び、その使用方法に関するものである。詳しくは、使
用後、手で簡単に剥がすことのできる易剥離性を有する
ため、リサイクル性に適した合成樹脂ボトル用のラベ
ル、及び、その使用方法に関するものである。TECHNICAL FIELD The present invention relates to a label attached to the surface of a synthetic resin bottle used for soft drinks, milk drinks, beer, wine, nutritional drinks, seasonings, cosmetics, etc.
And the use thereof. More specifically, the present invention relates to a label for a synthetic resin bottle suitable for recycling because it has easy peelability that can be easily peeled off by hand after use, and a method of using the label.
【０００２】[0002]
【従来技術】従来、清涼飲料水、乳・乳飲料、ビール、
ワイン、調味料、化粧品などに使用されるガラスびんや
合成樹脂ボトル用のラベルは、印刷した紙製のラベル本
体裏面に、接着層として、水性の糊剤、カゼイングルー
などのコールドグルー、粘着剤、ディレードタック接着
剤、ホットメルト接着剤等の感熱接着剤などを全面又は
部分的にコーティングを施し、胴部分に巻きつけられて
貼るものが知られている。一方、最近、環境問題や資源
のリサイクル化などの面から、ＰＥＴボトル等の容器を
回収して再利用することが考えられてきており、容器リ
サイクルを円滑に行うための動きが近年活発化してい
る。また、リサイクル法の制定に伴い、ＰＥＴボトルリ
サイクル推進協議会によるリサイクル法「第二種指定Ｐ
ＥＴボトルの自主設計ガイドライン」によれば、１．５
％アルカリ濃度の洗浄液中に８５〜９０℃で１５分間浸
漬処理したときにラベルが剥離し、接着剤がボトルに残
らないものであることを要求している。更に、８５度の
熱水で１５分間浸漬処理したときにラベルが剥離し、接
着剤がボトルに残らないものであることが望ましいとし
ている。このため、リサイクル工場等でラベルと容器を
分別する際、上記の方法によるか、若しくは、一般家庭
でボトルを回収して捨てる際に、何も処理を施さず、ラ
ベルが剥離し、接着剤やラベルの残留物がボトルに残ら
ないものであることが求められてきている。BACKGROUND OF THE INVENTION Conventionally, soft drinks, milk / milk drinks, beer,
Labels for glass bottles and synthetic resin bottles used for wine, seasonings, cosmetics, etc., have a water-based glue, cold glue such as casein glue, and an adhesive as an adhesive layer on the back side of the printed paper label body. It is known that a heat-sensitive adhesive such as a delayed tack adhesive or a hot melt adhesive is coated on the entire surface or a part of the adhesive, and the adhesive is wound around the body portion and attached. On the other hand, recently, from the aspects of environmental problems and recycling of resources, it has been considered to collect and reuse containers such as PET bottles, and movements for smooth container recycling have recently become active. There is. In addition, with the enactment of the Recycling Law, the PET Bottle Recycling Promotion Council's Recycling Law “Type II Designated P
According to "ET Bottle Voluntary Design Guidelines", 1.5
It requires that the label peels off and the adhesive does not remain in the bottle when immersed in a cleaning solution having a concentration of% alkali at 85 to 90 ° C. for 15 minutes. Further, it is desirable that the label is peeled off and the adhesive does not remain on the bottle when the immersion treatment is performed with hot water of 85 degrees for 15 minutes. Therefore, when separating the label and the container at a recycling plant, or by the above method, or when collecting and discarding the bottle in a general household, the label is peeled off without applying any treatment. It is required that the label residue does not remain on the bottle.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、従来の
紙製ラベルでは、水に弱く、冷蔵庫で清涼飲料水等の入
ったボトルを保存する際、ラベルに露が付着したり、露
店等で販売する際に水に浸漬して冷却したりすると、水
がラベルに付着することにより、ラベルが剥がれるとい
う問題がある。このため、合成樹脂製のラベルがラベル
にしわが寄ったり、ラベルが脱落することなく、しっか
り容器に付設されるために望ましい。しかしながら、合
成樹脂製ラベルに使用される接着剤として、一般的に使
用されているホットメルト接着剤は、プラスチックボト
ルなどの容器の再利用又は回収再生によるプラスチック
材料として再利用する際、樹脂を溶融してフィルム面に
塗布するために、ラベル接着後に容器外面とラベルとの
接着強度が強く、ラベルとボトルを分別することが困難
であるという問題がある。更に、ラベル剥離後もラベル
や接着剤の一部が容器側に残り、更に、容器に残った接
着剤を除去するために熱水処理や、アルカリ処理を施し
ても、ラベルや接着剤を全て取り除くことが困難である
という問題がある。他の接着剤として、コールドグルー
は、ラインでの塗工量および粘度コントロールにオペレ
ーターの熟練が要求され、また、糊のはみ出しや皺、浮
きなどが出やすく、ラベリングの精度およびラベリング
後の外観にも問題が発生しやすい。タックラベルに使用
される粘着剤は、経済面で不利であり、また、剥離紙
（セパレーター）を使用しなければならないため、昨今
の環境問題の一つである廃棄の問題がある。合成樹脂フ
ィルムのラベルとして、裏面全体に有機溶剤、または、
有機溶剤を溶剤とする接着剤を塗布する技術が、特開平
５−１５０７２４号公報にあるが、乾燥時間がかかるた
め、生産性が悪いという問題がある。また、ラベルと容
器を接着していないため、製品を輸送したり、商品を陳
列する際、内容物による内圧変化による容器の伸縮に伴
い、しわが寄ったり、ラベルの位置ずれ、更には、ラベ
ルの脱落を生じるという問題がある。更に、熱収縮性を
有する合成樹脂製フィルムを基材とする合成樹脂ラベル
として、特開平１１−１７４９６２号公報があるが、熱
収縮性フィルムは、通常のフィルムより材料費が非常に
高いという問題がある。However, conventional paper labels are weak against water, and when storing bottles containing soft drinks, etc. in the refrigerator, dew adheres to the labels or is sold at stalls and the like. At this time, if it is immersed in water and cooled, water adheres to the label, causing a problem of peeling the label. Therefore, it is desirable that the label made of synthetic resin is securely attached to the container without the label wrinkling or falling off. However, hot-melt adhesives, which are commonly used as adhesives for synthetic resin labels, melt the resin when reused as a plastic material by reuse or recovery of containers such as plastic bottles. Since it is applied to the film surface, the adhesive strength between the outer surface of the container and the label is strong after the label is bonded, and it is difficult to separate the label and the bottle. Furthermore, even after the label is peeled off, part of the label or adhesive remains on the container side, and even if hot water treatment or alkali treatment is performed to remove the adhesive remaining in the container, all the label and adhesive remain There is a problem that it is difficult to remove. As another adhesive, cold glue requires operator's skill to control the coating amount and viscosity on the line, and it is easy for adhesive squeeze out, wrinkles, and floats to occur, which improves the labeling accuracy and appearance after labeling. Is also prone to problems. The pressure-sensitive adhesive used for tack labels is economically disadvantageous, and since release paper (separator) must be used, there is a problem of disposal, which is one of the recent environmental problems. As a label of synthetic resin film, organic solvent on the entire back surface, or
A technique of applying an adhesive using an organic solvent as a solvent is disclosed in Japanese Patent Laid-Open No. 5-150724, but it takes a long time for drying, and thus there is a problem that productivity is poor. In addition, since the label and the container are not adhered, when the product is transported or the product is displayed, the container expands or contracts due to the change in internal pressure due to the contents, and wrinkles or misalignment of the label occur. There is a problem that the dropout occurs. Further, as a synthetic resin label having a heat-shrinkable synthetic resin film as a base material, there is JP-A No. 11-174962, but the problem that the heat-shrinkable film has a much higher material cost than an ordinary film. There is.
【０００４】[0004]
【課題を解決するための手段】そこで本発明者らは、上
記の課題を解決するために、鋭意研究の結果、合成樹脂
フィルムを基材とし、感熱接着剤層を設ける合成樹脂ボ
トル用ラベルにより、容器が廃棄されるまでの間、しわ
が寄ったり外れたりすることなくしっかり容器に付設さ
れ、且つ、容器の廃棄時にラベルを容易に剥し取ること
ができる容器リサイクルに優れた合成樹脂ボトル用ラベ
ルを見出したものである。本発明は、少なくとも、感熱
接着剤層を有し、一軸、若しくは、二軸に延伸した合成
樹脂フィルムからなるラベルであって、且つ、該感熱接
着剤層が、熱可塑性樹脂成分と、粘着付与剤と、固形可
塑剤を主成分とするディレードタック型感熱接着剤であ
ることを特徴とする合成樹脂ボトル用ラベルにかかるも
のである。上記において、前記の合成樹脂ボトルとラベ
ルとの剥離強度、及び、該ラベルの両端部を重ね合わさ
れたラベルの端部同士の剥離強度が、１〜２０Ｎ／１５
ｍｍであることを特徴とする合成樹脂ボトル用ラベルを
提供することができる。また、水中に一日浸漬後の前記
の合成樹脂ボトルとラベルの接着強度、及び、該ラベル
の両端部を重ね合わされたラベルの端部同士の接着強度
が、１〜２０Ｎ／１５ｍｍであることを特徴とする合成
樹脂ボトル用ラベルを提供することができる。また、前
記の合成樹脂ボトルとラベルとの剥離面において、該合
成樹脂ボトル側の剥離面における接着剤の残留量が、１
３００ｐｐｍ以下であることを特徴とする合成樹脂ボト
ル用ラベルを提供することができる。８５度の熱水で、
１５分間浸漬後の該合成樹脂ボトル側のラベル剥離面に
おける接着剤の残留量が、１３００ｐｐｍ以下であるこ
とを特徴とする合成樹脂ボトル用ラベルを提供すること
ができる。また、アルカリ濃度１．５％の水溶液中に８
５〜９０度で、１５分間浸漬後の該合成樹脂ボトル側の
ラベル剥離面における接着剤の残留量が、１３００ｐｐ
ｍ以下であることを特徴とする合成樹脂ボトル用ラベル
を提供することができる。また、前記の合成樹脂フィル
ムからなる基材が、ポリプロピレン樹脂フィルム、ある
いは、ポリエステル系樹脂フィルムであることを特徴と
する合成樹脂ボトル用ラベルを提供することができる。
また、前記の被着体となる合成樹脂ボトルが、ポリエス
テル系樹脂、あるいは、ポリプロピレン樹脂からなるこ
とを特徴とする合成樹脂ボトル用ラベルを提供すること
ができる。In order to solve the above-mentioned problems, the inventors of the present invention have conducted earnest research and as a result, by using a label for a synthetic resin bottle provided with a heat-sensitive adhesive layer using a synthetic resin film as a base material. Labels for synthetic resin bottles that are firmly attached to the container without wrinkling or coming off until the container is discarded, and that the label can be easily peeled off when the container is discarded, which is excellent for container recycling Is found. The present invention is a label having at least a heat-sensitive adhesive layer and comprising a uniaxially or biaxially stretched synthetic resin film, and the heat-sensitive adhesive layer is a thermoplastic resin component and tackifier. The present invention relates to a label for a synthetic resin bottle, which is a delayed tack type heat-sensitive adhesive containing a solidifying agent and a solid plasticizer as a main component. In the above, the peel strength between the synthetic resin bottle and the label, and the peel strength between the end portions of the label in which both end portions of the label are overlapped are 1 to 20 N / 15.
It is possible to provide a label for synthetic resin bottles, which is characterized by having a size of mm. In addition, the adhesive strength between the synthetic resin bottle and the label after immersion in water for one day, and the adhesive strength between the ends of the label in which both ends of the label are overlapped are 1 to 20 N / 15 mm. A characteristic label for a synthetic resin bottle can be provided. Further, in the peeling surface between the synthetic resin bottle and the label, the residual amount of the adhesive on the peeling surface on the synthetic resin bottle side is 1
It is possible to provide a label for a synthetic resin bottle, which is characterized by being 300 ppm or less. With hot water of 85 degrees,
It is possible to provide a label for a synthetic resin bottle characterized in that the residual amount of the adhesive on the label peeling surface on the synthetic resin bottle side after 15 minutes of immersion is 1300 ppm or less. In addition, 8 in an aqueous solution with an alkali concentration of 1.5%
The residual amount of the adhesive on the label peeling surface of the synthetic resin bottle side after immersion for 15 minutes at 5 to 90 degrees is 1300 pp.
It is possible to provide a label for a synthetic resin bottle, which is characterized by being m or less. Further, it is possible to provide a label for a synthetic resin bottle, wherein the base material made of the synthetic resin film is a polypropylene resin film or a polyester resin film.
Further, it is possible to provide a label for a synthetic resin bottle, wherein the synthetic resin bottle as the adherend is made of a polyester resin or a polypropylene resin.
【０００５】[0005]
【発明の実施の形態】以下に本発明の実施の形態を説明
する。図１は、本発明の合成樹脂ボトル用ラベル１０の
一実施例を示す断面図である。図１に示すように、本発
明の合成樹脂ボトル用ラベルは、合成樹脂フィルムから
なる基材１の裏面に必要に応じて印刷インキ層２を設
け、更に、接着剤層３を設け、合成樹脂フィルム（基材
１）／印刷インキ層２／接着剤層３の層構成からなる。BEST MODE FOR CARRYING OUT THE INVENTION Embodiments of the present invention will be described below. FIG. 1 is a sectional view showing an embodiment of a label 10 for synthetic resin bottles of the present invention. As shown in FIG. 1, a label for a synthetic resin bottle according to the present invention is provided with a printing ink layer 2 on the back surface of a base material 1 made of a synthetic resin film, if necessary, and further with an adhesive layer 3 to provide a synthetic resin. It has a layer structure of film (base material 1) / printing ink layer 2 / adhesive layer 3.
【０００６】図２は、本発明の別態様の合成樹脂ボトル
用ラベル１０の一例を示す断面図である。図２に示すよ
うに、本発明の合成樹脂ボトル用ラベル１０は、合成樹
脂フィルムからなる基材１の裏面に必要に応じて、印刷
インキ層２を設け、必要に応じて、アンカーコート層４
を介して、接着剤層３を設け、合成樹脂フィルム（基材
１）／印刷インキ層２／アンカーコート層４／接着剤層
３の層構成からなる。FIG. 2 is a sectional view showing an example of a synthetic resin bottle label 10 according to another embodiment of the present invention. As shown in FIG. 2, the label 10 for a synthetic resin bottle of the present invention is provided with a printing ink layer 2 on the back surface of a base material 1 made of a synthetic resin film, if necessary, and an anchor coat layer 4 if necessary.
The adhesive layer 3 is provided via the above, and has a layer structure of synthetic resin film (base material 1) / printing ink layer 2 / anchor coat layer 4 / adhesive layer 3.
【０００７】図３は、本発明の一実施例を示すラベル付
合成樹脂ボトルを示す正面図である。図３に示すよう
に、本発明のラベル１０と容器５とを接着層３を介して
接着部を形成し、ラベルの端部上面とラベルの別の端部
との重なり部分に接着層３を介して別の接着部を形成し
てラベル付き容器３からなるものである。FIG. 3 is a front view showing a labeled synthetic resin bottle showing an embodiment of the present invention. As shown in FIG. 3, an adhesive portion is formed between the label 10 and the container 5 of the present invention via the adhesive layer 3, and the adhesive layer 3 is provided at the overlapping portion between the upper surface of the end portion of the label and another end portion of the label. Another adhesive part is formed through the container 3 with a label.
【０００８】本発明において、本発明に係る合成樹脂ボ
トル用ラベル１０を構成する合成樹脂フィルムからなる
基材層１としては、一軸、若しくは、二軸に延伸した合
成樹脂フィルムからなる基材で、且つ、耐熱性を有すれ
ば、いずれのものでも使用することができる。例えば、
ポリエチレンテレフタレートフィルム等のポリエステル
フィルム、ポリスチレンフィルム、ポリプロピレンフィ
ルム、６ナイロンフィルム、６，６ナイロンフィルム等
のポリアミドフィルム、低密度ポリエチレンフィルム、
中密度ポリエチレンフィルム、高密度ポリエチレンフィ
ルム、低密度直鎖状ポリエチレンフィルム等のポリエチ
レンフィルム、環状ポリオレフィンフィルム、ポリスチ
レンフィルム、エチレン−プロピレン共重合体、エチレ
ン−酢酸ビニル共重合体、アイオノマー樹脂、エチレン
−アクリル酸共重合体、エチレン−アクリル酸メチル共
重合体等の樹脂から製膜されたポリオレフィン系フィル
ム、塩素化ポリエチレン，塩素化ポリプロピレンなどの
樹脂から製膜された変性ポリオレフィンフィルム、塩化
ビニル−酢酸ビニル共重合体の樹脂から製膜されたフィ
ルム、アクリル系樹脂フィルム等が使用できる。また、
これらのフィルムをラミネートして、２層以上の積層フ
ィルムとして、使用してもよい。フィルムの厚さとして
は、１０〜１００μｍ程度に形成されるものが好まし
い。この中でも、特に耐熱性に優れた延伸ポリプロピレ
ンフィルム（以下「ＯＰＰフィルム」ともいう。）、二
軸延伸ポリエチレンテレフタレートフィルム（以下「Ｐ
ＥＴフィルム」ともいう。）が、好ましく使用できる。In the present invention, the base material layer 1 made of a synthetic resin film constituting the label 10 for a synthetic resin bottle according to the present invention is a base material made of a uniaxially or biaxially stretched synthetic resin film, Any material can be used as long as it has heat resistance. For example,
Polyester film such as polyethylene terephthalate film, polystyrene film, polypropylene film, 6 nylon film, polyamide film such as 6,6 nylon film, low density polyethylene film,
Polyethylene film such as medium density polyethylene film, high density polyethylene film, low density linear polyethylene film, cyclic polyolefin film, polystyrene film, ethylene-propylene copolymer, ethylene-vinyl acetate copolymer, ionomer resin, ethylene-acrylic Polyolefin film formed from resin such as acid copolymer, ethylene-methyl acrylate copolymer, modified polyolefin film formed from resin such as chlorinated polyethylene and chlorinated polypropylene, vinyl chloride-vinyl acetate copolymer A film formed from a polymer resin, an acrylic resin film, or the like can be used. Also,
These films may be laminated and used as a laminated film having two or more layers. The thickness of the film is preferably about 10 to 100 μm. Among them, a stretched polypropylene film (hereinafter also referred to as “OPP film”) having particularly excellent heat resistance and a biaxially stretched polyethylene terephthalate film (hereinafter referred to as “P”).
Also called "ET film". ) Can be preferably used.
【０００９】本発明において、本発明に係る合成樹脂ボ
トル用ラベル１０を構成する印刷層２としては、合成樹
脂フィルムからなる基材層１の全面に、または、部分的
に、グラビア印刷、フレキソ印刷、オフセット印刷等の
公知の印刷技術を用いて図形、文字、記号等の絵柄を形
成したものである。好ましくは、耐熱性に富むインキ
で、グラビアインキで印刷することが望ましい。ボトル
に貼着した状態における基材１の内外のどちら側に形成
してもよいが、この実施形態では基材１の内側に形成し
てある。なお、基材１の外側に印刷層２を形成する場合
には、形成した印刷層２を保護するために、透明ニス等
によって形成されるオーバーコート層を設けておくのが
望ましい。印刷層２に使用されるインキとしては、合成
樹脂フィルムからなる基材層１と接着性があり、必要な
耐性を有している一般的に用いられているインキが使用
できる。印刷層２の厚みは、例えば１〜８μｍ、好まし
くは２〜５μｍ程度である。In the present invention, as the printing layer 2 constituting the synthetic resin bottle label 10 according to the present invention, gravure printing or flexographic printing is performed on the entire surface of the base material layer 1 made of a synthetic resin film or partially. , A pattern such as a figure, a character, or a symbol is formed by using a known printing technique such as offset printing. It is preferable to print with a gravure ink, which is an ink having high heat resistance. It may be formed on either the inside or outside of the base material 1 when it is attached to a bottle, but in this embodiment it is formed on the inside of the base material 1. When the printed layer 2 is formed on the outer side of the substrate 1, it is desirable to provide an overcoat layer formed of a transparent varnish or the like in order to protect the formed printed layer 2. As the ink used for the printing layer 2, a generally used ink that has adhesiveness to the base material layer 1 made of a synthetic resin film and has necessary resistance can be used. The thickness of the printing layer 2 is, for example, 1 to 8 μm, preferably 2 to 5 μm.
【００１０】本発明において、本発明にかかる合成樹脂
ボトル用ラベル１０を構成する接着剤層３としては、感
熱接着剤を使用できる。感熱接着剤には、常温で固体の
もの（ホットメルト接着剤）と、液状のもの（ディレー
ドタック接着剤）とがある。ホットメルト接着剤は、塗
布時に高温にして溶融させる必要がある上、高粘度であ
る。これに対し、ディレードタック接着剤は、塗布時に
高温にする必要はなく、また、低粘度である。本発明に
かかるディレードタック型感熱接着剤としては、熱可塑
性樹脂成分からなるベースポリマーと、粘着付与剤と、
結晶性の固体可塑剤から形成るものが、好適に用いられ
る。而して、本発明にかかるディレードタック型感熱接
着剤は、常温で粘着性がなく、６０℃以上に加熱すると
粘着性を生じ、この粘着性が冷却後も１日〜数年間持続
するものである。また、該接着剤はアルカリ水溶液に接
触すると溶解され接着力が低下する性質を有するもので
ある。In the present invention, a heat-sensitive adhesive can be used as the adhesive layer 3 constituting the label 10 for a synthetic resin bottle according to the present invention. There are two types of heat-sensitive adhesives which are solid at room temperature (hot-melt adhesive) and liquid (delayed tack adhesive). The hot melt adhesive has a high viscosity in addition to being required to be heated at a high temperature during application. On the other hand, the delayed tack adhesive does not require high temperature at the time of application and has low viscosity. The delayed tack type heat-sensitive adhesive according to the present invention, a base polymer comprising a thermoplastic resin component, a tackifier,
Those formed of a crystalline solid plasticizer are preferably used. Thus, the delayed tack type heat-sensitive adhesive according to the present invention is not tacky at room temperature and becomes tacky when heated to 60 ° C. or higher, and this tackiness is maintained for one day to several years even after cooling. is there. Further, the adhesive has the property of being dissolved when it comes into contact with an alkaline aqueous solution to reduce the adhesive strength.
【００１１】本発明にかかる感熱接着剤の熱可塑性樹脂
としては、粘着剤のベースとなるものであり、可塑剤と
の相溶性があり、これにより使用時の凝集力が得られ
る。また、アルカリ可溶性の樹脂であり、これによりラ
ベルを剥がす際、アルカリ処理により、容易に剥がすこ
ともできる。例えば、アクリル酸メチル、アクリル酸エ
チル、アクリル酸−イソプロピレン、アクリル酸イソブ
チル、アクリル酸ｎ−ブチル、アクリル酸アミル、アク
リル酸ヘキシル、アクリル酸２−エチルヘキシル等のア
クリル酸エステル、メタクリル酸エステル類と、アクリ
ル酸、マイレン酸等の不飽和カルボン酸よりなる共重合
樹脂等のアクリル酸エステル共重合体、スチレン−アク
リル酸エステル、スチレン−ブタジエン等が挙げられ
る。この中でも、自己架橋型アクリル酸エステル共重合
体は、加熱時に耐水性が向上する性質を有するため、本
発明の感熱接着ラベルに適している。The thermoplastic resin of the heat-sensitive adhesive according to the present invention serves as a base of a pressure-sensitive adhesive and is compatible with the plasticizer, whereby a cohesive force during use can be obtained. Further, since it is an alkali-soluble resin, when the label is peeled off, it can be easily peeled off by an alkali treatment. For example, acrylic acid esters and methacrylic acid esters such as methyl acrylate, ethyl acrylate, acrylic acid-isopropylene, isobutyl acrylate, n-butyl acrylate, amyl acrylate, hexyl acrylate, and 2-ethylhexyl acrylate. Acrylic acid, maleic acid, and other unsaturated carboxylic acid copolymer resins, such as acrylic acid ester copolymers, styrene-acrylic acid esters, and styrene-butadiene. Among these, the self-crosslinking acrylic acid ester copolymer is suitable for the heat-sensitive adhesive label of the present invention because it has a property of improving water resistance when heated.
【００１２】本発明にかかる感熱接着剤の固形可塑剤と
しては、融点以下では樹脂に可塑性を与えず、結晶状態
であり、加熱により溶融して樹脂中に相溶して樹脂を膨
潤あるいは軟化させるので、常温では非粘着性のブロッ
キング防止剤となり、加熱により粘着性となる機能を有
する。例えば、フタル酸ジフェニル、フタル酸ジヘキシ
ル、フタル酸ジシクロヘキシル、フタル酸ジヒドロアビ
エチル、イソフタル酸ジメチル、安息香酸スクロ−ス、
ジ安息香酸エチレングリコ−ル、トリ安息香酸トリメチ
ロ−ルエタン、トリ安息香酸グリセリド、テトラ安息香
酸ペンタエリトリット、八酢酸スクロ−ス、クエン酸ト
リシクロヘキシル、Ｎ−シクロヘキシル−ｐ−トルエン
スルホンアミド等が挙げられる。而して、融点が５０〜
１００℃程度のものが好ましく使用できる。融点が５０
℃以下の場合、ラベルの保管時に接着剤を活性化する恐
れがあり、使用前の保管や運搬がシビアになり、好まし
くない。融点が１００℃以上の場合、ラベルの接着層を
活性化するための効率が悪くなり、好ましくない。The solid plasticizer of the heat-sensitive adhesive according to the present invention does not impart plasticity to the resin at a melting point or lower, is in a crystalline state, and is melted by heating to be compatible with the resin to swell or soften the resin. Therefore, it functions as a non-adhesive anti-blocking agent at room temperature and has a function of becoming tacky by heating. For example, diphenyl phthalate, dihexyl phthalate, dicyclohexyl phthalate, dihydroabietyl phthalate, dimethyl isophthalate, sucrose benzoate,
Examples include ethylene glycol dibenzoate, trimethylolethane tribenzoate, glyceride tribenzoate, pentaerythritol tetrabenzoate, sucrose octaacetate, tricyclohexyl citrate, N-cyclohexyl-p-toluenesulfonamide and the like. To be Thus, the melting point is 50-
The thing of about 100 degreeC can be used preferably. Melting point 50
If the temperature is lower than 0 ° C, the adhesive may be activated during storage of the label, and storage and transportation before use become severe, which is not preferable. If the melting point is 100 ° C. or higher, the efficiency for activating the adhesive layer of the label becomes poor, which is not preferable.
【００１３】本発明にかかる感熱接着剤の粘着付与剤と
しては、粘着剤の粘着性能を向上させる作用がある。例
えばテルペン樹脂、脂肪族系石油樹脂、芳香族系石油樹
脂、クマロン−インデン樹脂、スチレン系樹脂、フェノ
−ル樹脂、テルペン−フェノ−ル樹脂、ロジン誘導体
（ロジン、重合ロジン、水添ロジンおよびそれらのグリ
セリン、ペンタエリスリト−ル等とのエステル、樹脂酸
ダイマ−等）が挙げられる。The tackifier of the heat-sensitive adhesive according to the present invention has the function of improving the tackiness of the tackifier. For example, terpene resin, aliphatic petroleum resin, aromatic petroleum resin, coumarone-indene resin, styrene resin, phenol resin, terpene-phenol resin, rosin derivative (rosin, polymerized rosin, hydrogenated rosin and those Glycerin, an ester with pentaerythritol, etc., a resin acid dimer, etc.).
【００１４】上記固形可塑剤、熱可塑性樹脂および粘着
性付与剤は、熱可塑性樹脂の粒子（固体粒子または液
滴）が水中に乳化分散されているエマルション、また
は、熱可塑性樹脂が有機溶剤に溶解または分散して、単
独あるいは２種類以上の混合物で使用することができ
る。また、必要に応じて分散剤や消泡剤、増粘剤等を使
用することもできる。The solid plasticizer, the thermoplastic resin and the tackifier are emulsions in which particles of the thermoplastic resin (solid particles or droplets) are emulsified and dispersed in water, or the thermoplastic resin is dissolved in an organic solvent. Alternatively, they may be dispersed and used alone or as a mixture of two or more kinds. Further, if necessary, a dispersant, a defoaming agent, a thickener, etc. can be used.
【００１５】本発明において、本発明に係る合成樹脂ボ
トル用ラベル１０を構成する、層間の接着力を向上させ
るためのアンカーコート層４としては、例えば、ポリオ
レフィン系、有機チタネート系、ポリエチレンイミン
系、ポリブタジエン系、イソシアネート系、ポリエステ
ル系、アクリル系などの非硬化型または、硬化型のアン
カーコート剤が挙げられる。前記のアンカーコート層４
は、グラビアコート法、ロールコート法、リバースロー
ルコート法のコーティング方法により形成できる。な
お、アンカーコート層４は必要に応じて設ければよい。In the present invention, the anchor coat layer 4 for improving the adhesive force between the layers, which constitutes the label 10 for a synthetic resin bottle according to the present invention, is, for example, a polyolefin type, an organic titanate type, a polyethyleneimine type, Examples include non-curable or curable anchor coating agents such as polybutadiene-based, isocyanate-based, polyester-based, and acrylic-based. The anchor coat layer 4
Can be formed by a coating method such as a gravure coating method, a roll coating method, or a reverse roll coating method. The anchor coat layer 4 may be provided if necessary.
【００１６】上述のような熱可塑性樹脂成分からなるベ
ースポリマーと、粘着付与剤と、固形可塑剤とを溶媒に
分散させてなるディレードタック型感熱接着剤は、エマ
ルジョンの状態でグラビアコート法、ロールコート法、
リバースロールコート法、リップコート法、ナイフコー
ト法等のような通常の感熱接着剤を塗布するための手段
を用いて、基材１の印刷層２を形成している方の面の全
面にまたは部分的に塗布して接着剤層３を形成させ、例
えば、４０〜６０℃の温度で乾燥することにより、合成
樹脂ボトル用ラベルが得られる。The delayed tack type heat-sensitive adhesive prepared by dispersing the above-mentioned base polymer comprising a thermoplastic resin component, a tackifier and a solid plasticizer in a solvent is used as a gravure coat method or roll in an emulsion state. Coat method,
Using an ordinary means for applying a heat-sensitive adhesive such as a reverse roll coating method, a lip coating method, a knife coating method, etc., the entire surface of the surface of the substrate 1 on which the printing layer 2 is formed or A label for a synthetic resin bottle is obtained by partially applying the adhesive to form the adhesive layer 3 and drying at a temperature of 40 to 60 ° C., for example.
【００１７】ディレードタック型感熱接着剤の塗布量
は、５〜２５ｇ／ｍ2 程度が好ましくは、８〜１５ｇ／
ｍ2 程度がより好ましい。塗布量が５ｇ／ｍ2以下の場
合、充分な接着強度が得られないため、好ましくない。
塗布量が２５ｇ／ｍ2以上の場合、充分な接着強度が得
られるが、乾燥速度が遅くなるため、生産性が悪く、ま
た、ラベルをボトルから剥がして分別する際、ラベルを
剥がしにくく、ボトルの糊残りを生じやすいため、好ま
しくない。また、該接着剤を重ねて塗布する場合もあ
り、生産性が下がるため、好ましくない。The coating amount of the delayed tack type heat-sensitive adhesive is preferably about 5 to 25 g / m 2 , preferably 8 to 15 g / m 2.
About m 2 is more preferable. When the coating amount is 5 g / m 2 or less, sufficient adhesive strength cannot be obtained, which is not preferable.
When the coating amount is 25 g / m 2 or more, sufficient adhesive strength can be obtained, but the drying speed becomes slow, resulting in poor productivity, and when the label is peeled from the bottle and separated, it is difficult to remove the label. It is not preferable because the adhesive residue is likely to occur. Further, the adhesive may be applied in layers, which lowers the productivity and is not preferable.
【００１８】ディレードタック型接着剤層は、接着層に
粘着性が生じている間に合成樹脂ラベルの全面、また
は、部分的（一個所のみ、若しくは、散点状や、線状、
格子状に形成してもよい。）にコーティングすることが
できる。図３のように、部分的にコーティングする場
合、それぞれ必要な接着強度を得るために、第一接着部
と、第二接着部の塗り幅としては、３〜２５ｍｍである
ことが好ましい。The delayed tack type adhesive layer is formed on the entire surface of the synthetic resin label or while the adhesive layer is tacky or partially (only at one place or in a dotted or linear shape).
It may be formed in a lattice shape. ) Can be coated. As shown in FIG. 3, in the case of partial coating, the coating width of the first adhesive portion and the second adhesive portion is preferably 3 to 25 mm in order to obtain the required adhesive strength.
【００１９】ラベルの被着体となる合成樹脂ボトルとし
ては、ポリエチレンテレフタレート等のポリエステル樹
脂、ポリプロピレン樹脂、ポリエチレン樹脂等のポリオ
レフィン樹脂等が挙げられる。Examples of synthetic resin bottles to which the labels are adhered include polyester resins such as polyethylene terephthalate, polypropylene resins, polyolefin resins such as polyethylene resins and the like.
【００２０】このようにして作製した本発明にかかるラ
ベルを合成樹脂ボトルに貼付する場合は、一般的に使用
されているラベリングマシンを用いて、先ずラベルを加
熱しディレードタック接着剤からなる接着層を活性化さ
せる。次に、合成樹脂ボトル全体を熱風や、水蒸気、及
び、水蒸気が結露した湯気により加熱するスチームや、
高周波シール、赤外線等の輻射熱を作用させて加熱しな
がらラベルを押圧して合成樹脂ボトルに貼り付けること
ができる。あるいは、合成樹脂ボトルに貼付られたラベ
ルを熱板等により押圧してもよい。また、ラベルを加熱
する工程は、ラベルをボトルに装着する前の工程、ある
いは、ラベルをボトルに装着する工程のうち、適宜の段
階で施すことができる。この結果、ラベルの接着層をた
とえば９０〜１００℃程度にヒーターからの熱風で再加
熱して活性化させた状態で合成樹脂ボトルにラベルが密
着され、ラベル貼付合成樹脂ボトルが得られる。When a label according to the present invention thus produced is attached to a synthetic resin bottle, an adhesive layer made of a delayed tack adhesive is prepared by first heating the label using a generally used labeling machine. Activate. Next, hot air, steam, and steam that heats the entire synthetic resin bottle with steam from which water vapor has condensed,
The label can be pressed and attached to the synthetic resin bottle while being heated by applying radiant heat such as a high frequency seal or infrared rays. Alternatively, the label attached to the synthetic resin bottle may be pressed by a hot plate or the like. The step of heating the label can be performed at an appropriate stage of the step before the label is attached to the bottle or the step of attaching the label to the bottle. As a result, the label is brought into close contact with the synthetic resin bottle in a state where the adhesive layer of the label is reheated to, for example, about 90 to 100 ° C. by hot air from a heater to be activated, and a label-attached synthetic resin bottle is obtained.
【００２１】本発明にかかるラベル貼付合成樹脂ボトル
の側面に位置する部分には、開封用ミシン目が上端部か
ら下端部まで刻設されてもよい。また、ラベル開封用の
摘み片（切離開始部）を起点として、２条の縦ミシン目
を設けてもよく、該ミシン目によりラベルを容易に破断
することが可能である。なお、該ミシン目は、２条に限
らず、１条、あるいは、３条以上の複数条を設けること
も可能である。なお、ミシン目は、例えば、レーザー光
を用いて包材の厚さ方向に所定深さまで切り込みをいれ
て形成させる方法周囲に切断部と非切断部とが繰り返し
形成された円板状の刃物を押し当てて形成させる方法等
により施すことができる。また、該ミシン目は、ラベル
を製造する工程で、適宜の段階で施すことができる。[0021] A perforation for opening may be engraved from the upper end portion to the lower end portion on the side surface of the label-attached synthetic resin bottle according to the present invention. Further, two vertical perforations may be provided starting from the tab for opening the label (separation start portion), and the label can be easily broken by the perforations. The perforations are not limited to two, and one or a plurality of three or more can be provided. The perforation is, for example, a method of forming a cut to a predetermined depth in the thickness direction of the packaging material by using a laser beam to form a disc-shaped blade in which a cut portion and a non-cut portion are repeatedly formed around the circumference. It can be applied by a method of pressing and forming. Further, the perforations can be provided at an appropriate stage in the process of manufacturing the label.
【００２２】上記のラベル貼付合成樹脂ボトルの内容物
としては、ビール、ワイン、ビタミン飲料、乳・乳飲
料、ジュ−ス、炭酸飲料、水、お茶等の飲料水、あるい
は、油脂、調味料、医薬品、化粧品、洗剤、その他種々
の液状食品が挙げられる。The contents of the above-mentioned labeled synthetic resin bottles include beer, wine, vitamin drinks, milk / milk drinks, juice, carbonated drinks, water, drinking water such as tea, oils and fats, seasonings, Examples include pharmaceuticals, cosmetics, detergents, and various liquid foods.
【００２３】また、上記のようにして製造した本発明に
かかるラベルは、粘着持続性に優れたものである。前記
の合成樹脂ボトル用ラベルを貼付け３ヶ月後も、ラベル
貼着直後の初期接着強度を１００％とすると、８０％以
上の接着強度を維持することが可能なラベルを得ること
ができる。Further, the label according to the present invention produced as described above is excellent in stickiness persistence. Even after 3 months from the application of the label for a synthetic resin bottle, assuming that the initial adhesive strength immediately after the application of the label is 100%, a label capable of maintaining an adhesive strength of 80% or more can be obtained.
【００２４】また、上記のようにして製造した本発明に
かかるラベルは、耐水性に優れたものである。前記の合
成樹脂ボトル用ラベルを水中に一日浸漬後、水から取り
出し、合成樹脂ボトルからラベルの接着強度、及び、該
ラベルの両端部を重ね合わされたラベルの端部同士の接
着強度が、１〜２０Ｎ／１５ｍｍである合成樹脂ボトル
用ラベルであることが好ましい。接着強度が、１Ｎ／１
５ｍｍ以下の場合、冷蔵庫に保存したり、露店や、クー
ラーボックス等で水に入れて冷やす際、しわが寄った
り、ラベルの位置ずれ、更には、ラベルの脱落を生じる
ことがあり、好ましくない。接着強度が、２０Ｎ／１５
ｍｍ以上の場合、合成樹脂ボトルからラベルを剥がす
際、容易に手で剥がすことができなくなり、好ましくな
い。Further, the label according to the present invention produced as described above has excellent water resistance. The above-mentioned label for a synthetic resin bottle was immersed in water for one day, then taken out from the water, and the adhesive strength of the label from the synthetic resin bottle and the adhesive strength between the ends of the label in which both ends of the label were overlapped were 1. It is preferably a label for a synthetic resin bottle having a size of 20 N / 15 mm. Adhesive strength is 1N / 1
When the thickness is 5 mm or less, wrinkles may occur, the label may be misaligned, and the label may drop off when it is stored in a refrigerator or put in water in a stall or a cooler box to cool, which is not preferable. Adhesive strength is 20N / 15
When it is more than mm, it is not preferable because the label cannot be easily peeled by hand when peeling the label from the synthetic resin bottle.
【００２５】使用後に合成樹脂ボトルに貼付したラベル
を手で剥がす場合には、開封用ミシン目ミシン目により
ラベルを容易に破断することが可能である。合成樹脂ボ
トルの表面から容易に剥がすことができ、剥離後、ボト
ルにラベルや糊残りがなく、きれいな剥離面が得られ
る。When the label attached to the synthetic resin bottle is peeled off by hand after use, the label can be easily broken by the perforation for opening. It can be easily peeled from the surface of a synthetic resin bottle, and after peeling, there is no label or adhesive residue on the bottle, and a clean peeled surface is obtained.
【００２６】而して、前記の合成樹脂ボトルとラベルと
の剥離強度、及び、該ラベルの両端部を重ね合わされた
ラベルの端部同士の剥離強度としては、１〜２０Ｎ／１
５ｍｍであることが好ましい。具体的には、該ラベルの
両端部を重ね合わされたラベルの端部同士の剥離強度が
１〜２０Ｎ／１５ｍｍで、ラベルと合成樹脂ボトル間の
剥離強度が１〜１５Ｎ／１５ｍｍであることが望まし
い。合成樹脂ボトルとラベルとの剥離強度の方が、該ラ
ベルの両端部を重ね合わされたラベルの端部同士の剥離
強度より低い方が、ラベルの巻き付きが解除されて垂れ
下がってしまうことがなく、ラベルの接着剤がボトル側
に残留することなく、ラベルをボトルから剥がすことが
できるため、好ましいものである。Thus, the peel strength between the synthetic resin bottle and the label and the peel strength between the ends of the label in which both ends of the label are overlapped are 1 to 20 N / 1.
It is preferably 5 mm. Specifically, it is desirable that the peel strength between the ends of the label in which both ends of the label are overlapped is 1 to 20 N / 15 mm, and the peel strength between the label and the synthetic resin bottle is 1 to 15 N / 15 mm. . The peeling strength between the synthetic resin bottle and the label is lower than the peeling strength between the ends of the label in which both ends of the label are overlapped, and the label is not unrolled and hangs down. This is preferable because the label can be peeled off from the bottle without the adhesive of (2) remaining on the bottle side.
【００２７】使用後に合成樹脂ボトルに貼付したラベル
を剥がす他の処理方法として、８５度の水で、１５分間
浸漬する方法や、アルカリ濃度１．５％の水溶液中に８
５〜９０度で、１５分間浸漬する方法があり、処理後の
ボトル側の接着剤の残留量が、１３００ｐｐｍ以下にす
ることが好ましく、２０ｐｐｍ以下にすることが望まし
い。１３００ｐｐｍ以下にすることで、きれいな剥離面
が得られ、リサイクルに有用なボトルを得ることができ
る。Other treatment methods for removing the label attached to the synthetic resin bottle after use include dipping in water at 85 ° C for 15 minutes, or in an aqueous solution having an alkali concentration of 1.5%.
There is a method of dipping at 5 to 90 degrees for 15 minutes, and the residual amount of the adhesive on the bottle side after treatment is preferably 1300 ppm or less, and more preferably 20 ppm or less. By setting it to 1300 ppm or less, a clean peeled surface can be obtained, and a bottle useful for recycling can be obtained.
【００２８】以下に実施例をあげて本発明を説明する。
（実施例１）基材１として３８μｍのＰＥＴフィルム
（東洋紡製Ｅ５２００）を準備した。片面に所望の絵柄
のインキ層２を１色目にＨＵ単体ラベル白（ザ・インク
テック株式会社製）、２色目にＵＰＡＣ９８０白（ザ・
インクテック株式会社製）のインキを用いてグラビア印
刷法により施した。さらにその上に、熱可塑性樹脂とし
てエマルジョンタイプのアクリル樹脂、粘着付与剤とし
てロジン、テルペン樹脂を、固体可塑剤としてフタル酸
ジシクロヘキシルに不揮発成分６１％からなるディレー
トタック型接着剤である接着剤層３をグラビアコート法
にて、塗布幅２０ｍｍのボトル／ラベル間接着部、及
び、ラベル／ラベル間接着部に、それぞれ塗布量１０ｇ
／ｍ2、８ｇ／ｍ2で塗布し、接着剤層３を形成させ、こ
うして得られた積層フィルムを高さ１００ｍｍ、幅２４
０ｍｍにカットして、枚葉の実施例１の合成樹脂ボトル
用ラベルを得た。次に、ＰＥＴボトルの表面に実施例１
の合成樹脂ボトル用ラベルを、ラベリングマシンを用い
て、ボトル５の周囲に巻き付け、９５℃で５秒間加熱し
て粘着性を持たせたボトル／ラベル間接着部によってボ
トル５に接着し、加熱して粘着性を持たせたラベル／ラ
ベル間接着部によって、ラベル／ラベル間を接着するこ
とで、実施例１のラベル付合成樹脂ボトルを得た。The present invention will be described below with reference to examples. (Example 1) As a base material 1, a 38 µm PET film (E5200 manufactured by Toyobo) was prepared. The ink layer 2 with the desired pattern on one side is the HU simple label white for the first color (made by The Inktech Co., Ltd.) and the UPAC980 white (the
The ink was manufactured by Inktech Co., Ltd. and was applied by the gravure printing method. Further thereon, an emulsion type acrylic resin as a thermoplastic resin, a rosin and a terpene resin as a tackifier, and a dilate-tack type adhesive layer composed of dicyclohexyl phthalate and 61% of a non-volatile component as a solid plasticizer, an adhesive layer 3 Is applied to the bottle / label adhesive part and the label / label adhesive part each having a coating width of 20 mm by the gravure coating method.
/ M 2 , 8 g / m 2 to form an adhesive layer 3, and the laminated film thus obtained is 100 mm in height and 24 in width.
It was cut to 0 mm to obtain a single-wafer label for synthetic resin bottle of Example 1. Next, Example 1 was applied to the surface of the PET bottle.
Using the labeling machine, the label for the synthetic resin bottle of is wrapped around the bottle 5 and heated at 95 ° C. for 5 seconds to be adhered to the bottle 5 by the adhesive portion between the bottle and the label, and heated. The labeled synthetic resin bottle of Example 1 was obtained by adhering the labels / labels with each other by means of the label / label-bonding portion which has been made sticky.
【００２９】（実施例２）基材１として５０μｍのＯＰ
Ｐフィルム（東洋紡製 製品名：Ｐ２７６１）を準備し
た。基材１以外は、実施例１と同じ材料、方法を用いて
接着剤層を形成させ、実施例２の合成樹脂ボトル用ラベ
ルとした。このラベルを実施例１と同様にラベリングマ
シンを用いて、実施例１と同じ条件で貼付し、実施例２
のラベル付合成樹脂ボトルを得た。(Example 2) 50 μm OP as the base material 1
A P film (manufactured by Toyobo, product name: P2761) was prepared. An adhesive layer was formed using the same materials and methods as in Example 1 except for the base material 1 to obtain a synthetic resin bottle label in Example 2. This label was attached under the same conditions as in Example 1 using a labeling machine as in Example 1, and Example 2 was used.
A labeled synthetic resin bottle of was obtained.
【００３０】（比較例１）不揮発成分５７％からなるデ
ィレートタック型感熱接着剤を用い、塗布量５ｇ／ｍ2
にした以外は、実施例１と同じ材料、方法を用いて接着
剤層を形成させ、実施例１の合成樹脂ボトル用ラベルと
した。このラベルを実施例１と同様にラベリングマシン
を用いて、実施例１と同じ条件で貼付し、比較例１のラ
ベル付合成樹脂ボトルを得た。(Comparative Example 1) A dilate tack type heat-sensitive adhesive consisting of 57% of non-volatile components was used, and the coating amount was 5 g / m 2.
An adhesive layer was formed by using the same material and method as in Example 1 except that the label was used as the label for the synthetic resin bottle of Example 1. This label was attached under the same conditions as in Example 1 using a labeling machine as in Example 1 to obtain a labeled synthetic resin bottle of Comparative Example 1.
【００３１】（比較例２）不揮発成分６７％からなるデ
ィレートタック型感熱接着剤を用い、３回接着剤を塗布
し、塗布量１７ｇ／ｍ2にした以外は、実施例１と同じ
材料、方法を用いて接着剤層を形成させ、実施例１の合
成樹脂ボトル用ラベルとした。この感熱ラベルを実施例
１と同様にラベリングマシンを用いて、実施例１と同じ
条件で貼付し、比較例２のラベル付合成樹脂ボトルを得
た。(Comparative Example 2) The same material and method as in Example 1 except that a delate tack type heat-sensitive adhesive consisting of 67% of non-volatile components was used and the adhesive was applied three times to give a coating amount of 17 g / m 2. Was used to form an adhesive layer, and the label for the synthetic resin bottle of Example 1 was obtained. This heat-sensitive label was attached under the same conditions as in Example 1 by using a labeling machine as in Example 1 to obtain a labeled synthetic resin bottle of Comparative Example 2.
【００３２】このようにして作製した実施例１〜２、比
較例１〜２における合成樹脂ボトルへのラベルの剥離容
易性、保存安定性を評価するための接着強度、粘着持続
性、剥離性、耐水性、アルカリ処理適性の５項目を下記
する方法により評価した。その結果を表１に示す。The peelability of the label on the synthetic resin bottles of Examples 1 and 2 and Comparative Examples 1 and 2 thus prepared, the adhesive strength, stickiness persistence and peelability for evaluating the storage stability, Five items of water resistance and suitability for alkali treatment were evaluated by the following methods. The results are shown in Table 1.
【００３３】（実験１：接着強度）接着強度は、実施例
１〜２、比較例１〜２ラベル（印刷面、印刷なし面）を
合成樹脂ボトル（二軸延伸ポリエチレンテレフタレート
樹脂、二軸延伸ポリプロピレン樹脂）のフラット面に貼
り付け、室温で１週間エージングを行った。次に試験片
を長さ１０ｍｍ、幅１５ｍｍに切出し、これを引張試験
機（オリエンテック社製）を用いて、ＪＩＳ Ｋ６８４
８に準じて、１８０度剥離により３００ｍｍ／分の引張
速度で測定し、以下の基準で評価した。なお、表１中に
は、１５ｍｍ当たりの接着強度（単位：ｇ／１５ｍｍ）
を記載した。
○：接着強度が１〜１５Ｎ／１５ｍｍであってラベルと
合成樹脂ボトルを充分接着しているが、手で容易に剥離
できる。
×：接着強度が１Ｎ／１５ｍｍ未満では、他のラベル付
ボトルに接触した場合、容易にラベルの位置ずれが生じ
る。
また、１５Ｎ／１５ｍｍ以上では、剥離するのに強い力
が必要になり、また、ボトル側の剥離面にラベルや接着
剤の一部が残る。(Experiment 1: Adhesive strength) As for the adhesive strength, the labels (printed surface and non-printed surface) of Examples 1 and 2 and Comparative Examples 1 and 2 were made of synthetic resin bottles (biaxially oriented polyethylene terephthalate resin, biaxially oriented polypropylene). It was attached to the flat surface of (resin) and aged at room temperature for 1 week. Next, a test piece was cut into a length of 10 mm and a width of 15 mm, and this was cut using a tensile tester (manufactured by Orientec Co.) to JIS K684.
According to No. 8, it was measured by peeling 180 degrees at a tensile speed of 300 mm / min, and evaluated according to the following criteria. In Table 1, the adhesive strength per 15 mm (unit: g / 15 mm)
Was described. ◯: The adhesive strength is 1 to 15 N / 15 mm and the label and the synthetic resin bottle are sufficiently adhered, but they can be easily peeled off by hand. X: When the adhesive strength is less than 1 N / 15 mm, the label is easily displaced when it comes into contact with another labeled bottle. Further, if it is 15 N / 15 mm or more, a strong force is required for peeling, and a part of the label or the adhesive remains on the peeling surface on the bottle side.
【００３４】（実験２：粘着持続性）粘着持続性は、ラ
ベル（印刷面あり、印刷面なし）を合成樹脂ボトル（二
軸延伸ポリエチレンテレフタレートフィルム、二軸延伸
ポリプロピレンフィルム）に貼り付け、室温に３ヶ月間
保存後、ＪＩＳ Ｋ６８４８に準じて１８０度剥離によ
り３００ｍｍ／分の引張速度で測定し、以下の基準で評
価した。
○：接着強度が１Ｎ／１５ｍｍ以上あって、接着ラベル
と合成樹脂ボトルを充分接着しているが、手で容易に剥
離できる。
×：接着強度が１Ｎ／１５ｍｍ未満で、自然剥離しやす
い。
または、１５Ｎ／１５ｍｍ以上では剥離するのに強い力
が必要になり、ラベルが破けて合成樹脂ボトルに残る。(Experiment 2: Adhesion Persistence) Adhesion persistence was measured by sticking a label (with or without printing surface) to a synthetic resin bottle (biaxially stretched polyethylene terephthalate film, biaxially stretched polypropylene film) at room temperature. After storage for 3 months, it was measured by peeling at 180 degrees at a tensile speed of 300 mm / min according to JIS K6848, and evaluated according to the following criteria. ◯: The adhesive strength is 1 N / 15 mm or more, and the adhesive label and the synthetic resin bottle are sufficiently adhered, but they can be easily peeled off by hand. X: Adhesive strength of less than 1 N / 15 mm and easy spontaneous peeling. Alternatively, if it is 15 N / 15 mm or more, a strong force is required for peeling, and the label breaks and remains on the synthetic resin bottle.
【００３５】（実験３：剥離性）剥離性は、ラベルの隅
から爪で引掛けてラベルを合成樹脂ボトルから剥離し、
合成樹脂ボトルの表面に糊（または、ラベル）の残り具
合を目視で評価した。
○ ：糊（または、ラベル）残りがない。
× ：糊（または、ラベル）残りがボトルに付着してい
る。(Experiment 3: Peelability) Peelability was measured by hooking the corner of the label with a nail and peeling the label from the synthetic resin bottle.
The degree of remaining paste (or label) on the surface of the synthetic resin bottle was visually evaluated. ○: There is no adhesive (or label) residue. X: The adhesive (or label) residue is attached to the bottle.
【００３６】（実験４：耐水性）剥離性は、水温が５°
Ｃの水道水に１日浸漬後、ラベル（印刷面あり、印刷面
なし）を合成樹脂ボトル（二軸延伸ポリエチレンテレフ
タレート樹脂、二軸延伸ポリプロピレン樹脂）のフラッ
ト面に貼り付け、試験片を長さ１０ｍｍ、幅１５ｍｍに
切出し、これを引張試験機（オリエンテック社製）を用
いて、ＪＩＳ Ｋ６８４８に準じて、１８０度剥離によ
り３００ｍｍ／分の引張速度で測定し、以下の基準で評
価した。
○：接着強度が１Ｎ／１５ｍｍ以上あって、接着ラベル
と合成樹脂ボトルを充分接着しているが、手で容易に剥
離できる。
×：接着強度が１Ｎ／１５ｍｍ未満で、自然剥離しやす
い。
または、１５Ｎ／１５ｍｍ以上では剥離するのに強い力
が必要になり、ラベルが破けて合成樹脂ボトルに残る。(Experiment 4: Water resistance) Peelability was measured at a water temperature of 5 °.
After soaking in tap water of C for 1 day, a label (with or without printing surface) was attached to the flat surface of a synthetic resin bottle (biaxially stretched polyethylene terephthalate resin, biaxially stretched polypropylene resin), and the length of the test piece It was cut into 10 mm and 15 mm in width, and this was measured by a tensile tester (manufactured by Orientec Co., Ltd.) according to JIS K6848 by 180 degree peeling at a tensile speed of 300 mm / min, and evaluated according to the following criteria. ◯: The adhesive strength is 1 N / 15 mm or more, and the adhesive label and the synthetic resin bottle are sufficiently adhered, but they can be easily peeled off by hand. X: Adhesive strength of less than 1 N / 15 mm and easy spontaneous peeling. Alternatively, if it is 15 N / 15 mm or more, a strong force is required for peeling, and the label breaks and remains on the synthetic resin bottle.
【００３７】（実験５：アルカリ処理適性）アルカリ処
理適性は、ラベルを貼り付けた合成樹脂ボトルの試験片
を長さ８ｍｍ、幅８ｍｍに切出し、これを８５〜９０
℃，１．５％濃度の水酸化ナトリウム水溶液に１５分浸
漬後、ラベルの隅から爪で引掛けてラベルを合成樹脂ボ
トルから剥離し、合成樹脂ボトルの表面に糊（または、
ラベル）の残り具合を目視で評価した。
○ ：糊（または、ラベル）残りがない。
× ：糊（または、ラベル）残りがボトルに付着してい
る。(Experiment 5: Alkali treatment suitability) Alkali treatment suitability was determined by cutting a test piece of a label-attached synthetic resin bottle into a length of 8 mm and a width of 8 mm.
After immersing in a 1.5% concentration sodium hydroxide aqueous solution for 15 minutes at the temperature, hook the nail from the corner of the label to peel the label from the synthetic resin bottle, and glue (or,
The remaining condition of the label) was visually evaluated. ○: There is no adhesive (or label) residue. X: The adhesive (or label) residue is attached to the bottle.
【００３８】[0038]
【表１】 [Table 1]
【００３９】表１に示した実験１〜５の結果から明らか
なように、本発明の合成樹脂ボトル用ラベルは、接着強
度、粘着持続性、耐水性を保持しつつ、剥離性に優れた
ラベルが得られ、ラベルを剥がしたボトル表面に糊残り
がない。比較例１の合成樹脂ボトル用ラベルは、接着強
度がなく、ラベルが合成樹脂ボトルから脱落するものが
あり、問題があった。比較例２の合成樹脂ボトル用ラベ
ルは、接着強度、粘着持続性、耐水性について問題ない
が、ラベルをボトルから剥がす際に、容易に剥がすこと
ができず、ラベルを剥がしたボトル表面に糊残りや、ラ
ベルの残りがあり、問題があった。As is clear from the results of Experiments 1 to 5 shown in Table 1, the label for synthetic resin bottles of the present invention is a label excellent in peelability while maintaining adhesive strength, stickiness durability and water resistance. There is no adhesive residue on the surface of the bottle after peeling off the label. The label for the synthetic resin bottle of Comparative Example 1 had a problem in that there was no adhesive strength and the label fell off from the synthetic resin bottle. The label for the synthetic resin bottle of Comparative Example 2 has no problem with adhesive strength, stickiness persistence, and water resistance, but when the label is peeled from the bottle, it cannot be easily peeled off, and the adhesive remains on the bottle surface after peeling the label. There was a problem with the rest of the label.
【００４０】[0040]
【発明の効果】本発明により、合成樹脂からなるラベル
を合成樹脂ボトルに貼り付ける合成樹脂ボトル用ラベル
は、接着強度、粘着持続性、耐水性、熱水処理適性、ア
ルカリ処理適性とも実用特性を満足しながら、容易に手
で剥がすことができるラベルで、更に、ボトルに糊残り
がなく、ＰＥＴボトル等の合成樹脂ボトルの容器リサイ
クルを円滑に行うことができ、非常に有用なものであ
る。EFFECTS OF THE INVENTION According to the present invention, a label for a synthetic resin bottle in which a label made of a synthetic resin is attached to a synthetic resin bottle has practical properties in terms of adhesive strength, stickiness persistence, water resistance, hot water treatment suitability, and alkali treatment suitability. While satisfying, it is a label that can be easily peeled off by hand. Furthermore, there is no adhesive residue on the bottle, and it is possible to smoothly recycle a synthetic resin bottle such as a PET bottle, which is very useful.
【図１】本発明の合成樹脂ボトル用ラベル１０の一実施
例を示す断面図である。FIG. 1 is a sectional view showing an embodiment of a label 10 for a synthetic resin bottle of the present invention.
【図２】本発明の別態様の合成樹脂ボトル用ラベル１０
の一例を示す断面図である。FIG. 2 is a label 10 for a synthetic resin bottle according to another embodiment of the present invention.
It is sectional drawing which shows an example.
【図３】本発明の一実施例を示すラベル付合成樹脂ボト
ルを示す正面図である。FIG. 3 is a front view showing a labeled synthetic resin bottle showing an embodiment of the present invention.
１ 基材（合成樹脂フィルム） ２ 印刷層 ３ 接着層 ４ アンカーコート層 ５ 容器（合成樹脂ボトル） １０ 合成樹脂ボトル用ラベル 1 Base material (synthetic resin film) 2 printing layers 3 adhesive layer 4 Anchor coat layer 5 containers (synthetic resin bottles) 10 Labels for synthetic resin bottles
───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 3E086 AB01 AC06 AC12 AC15 AD30 BA04 BA15 BA33 BB52 BB62 BB71 BB90 CA11 CA12 CA13 CA23 CA28 CA35 ─────────────────────────────────────────────────── ─── Continued front page F-term (reference) 3E086 AB01 AC06 AC12 AC15 AD30 BA04 BA15 BA33 BB52 BB62 BB71 BB90 CA11 CA12 CA13 CA23 CA28 CA35
Claims (8)
軸、若しくは、二軸に延伸した合成樹脂フィルムからな
るラベルであって、且つ、該感熱接着剤層が、熱可塑性
樹脂成分と、粘着付与剤と、固形可塑剤を主成分とする
ディレードタック型感熱接着剤であることを特徴とする
合成樹脂ボトル用ラベル。1. A label comprising a uniaxially or biaxially stretched synthetic resin film having at least a heat sensitive adhesive layer, wherein the heat sensitive adhesive layer comprises a thermoplastic resin component and an adhesive. A label for a synthetic resin bottle, which is a delayed tack type heat-sensitive adhesive containing a solid plasticizer as a main component.
強度、及び、該ラベルの両端部を重ね合わされたラベル
の端部同士の剥離強度が、１〜２０Ｎ／１５ｍｍである
ことを特徴とする請求項１記載の合成樹脂ボトル用ラベ
ル。2. The peel strength between the synthetic resin bottle and the label and the peel strength between the end portions of the label in which both end portions of the label are overlapped are 1 to 20 N / 15 mm. The label for synthetic resin bottles according to claim 1.
ルとラベルの接着強度、及び、該ラベルの両端部を重ね
合わされたラベルの端部同士の接着強度が、１〜２０Ｎ
／１５ｍｍであることを特徴とする請求項１〜２のいず
れかに記載の合成樹脂ボトル用ラベル。3. The adhesive strength between the synthetic resin bottle and the label after immersion in water for one day, and the adhesive strength between the end portions of the label in which both end portions of the label are overlapped are 1 to 20 N.
/ 15 mm, The label for synthetic resin bottles according to any one of claims 1 to 2.
面において、該合成樹脂ボトル側の剥離面における接着
剤の残留量が、１３００ｐｐｍ以下であることを特徴と
する請求項１〜３のいずれかに記載の合成樹脂ボトル用
ラベル。4. The peeling surface between the synthetic resin bottle and the label, wherein the residual amount of the adhesive on the peeling surface on the synthetic resin bottle side is 1300 ppm or less. A label for synthetic resin bottles according to Crab.
成樹脂ボトル側のラベル剥離面における接着剤の残留量
が、１３００ｐｐｍ以下であることを特徴とする請求項
１〜３のいずれかに記載の合成樹脂ボトル用ラベル。5. The residual amount of the adhesive on the label peeling surface of the synthetic resin bottle side after immersion for 15 minutes in hot water of 85 ° C. is 1300 ppm or less. A label for synthetic resin bottles according to Crab.
〜９０度で、１５分間浸漬後の該合成樹脂ボトル側のラ
ベル剥離面における接着剤の残留量が、１３００ｐｐｍ
以下であることを特徴とする請求項１〜３のいずれかに
記載の合成樹脂ボトル用ラベル。6. 85 in an aqueous solution having an alkali concentration of 1.5%
The residual amount of the adhesive on the label peeling surface of the synthetic resin bottle side after immersion for 15 minutes at 1 to 90 degrees is 1300 ppm.
The label for a synthetic resin bottle according to any one of claims 1 to 3, wherein:
が、ポリプロピレン樹脂フィルム、あるいは、ポリエス
テル系樹脂フィルムであることを特徴とする請求項１〜
６のいずれかに記載の合成樹脂ボトル用ラベル。7. The substrate comprising the synthetic resin film is a polypropylene resin film or a polyester resin film.
The label for synthetic resin bottles according to any one of 6 above.
ポリエステル系樹脂、あるいは、ポリプロピレン樹脂か
らなることを特徴とする請求項１〜７のいずれかに記載
の合成樹脂ボトル用ラベル。8. A synthetic resin bottle as the adherend,
The label for synthetic resin bottles according to any one of claims 1 to 7, wherein the label is made of polyester resin or polypropylene resin.