JP2003278095A - Cast-coated paper and method for producing the same - Google Patents
Cast-coated paper and method for producing the sameInfo
- Publication number
- JP2003278095A JP2003278095A JP2002118550A JP2002118550A JP2003278095A JP 2003278095 A JP2003278095 A JP 2003278095A JP 2002118550 A JP2002118550 A JP 2002118550A JP 2002118550 A JP2002118550 A JP 2002118550A JP 2003278095 A JP2003278095 A JP 2003278095A
- Authority
- JP
- Japan
- Prior art keywords
- paper
- cast
- coated
- unbleached kraft
- coated paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、包装用紙、包装用
紙袋、包装用カートン、ノートおよび書籍の表紙、ファ
イル、カタログ、印刷用紙などとして使用されるキャス
トコート紙に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cast coated paper used as a wrapping paper, a wrapping paper bag, a wrapping carton, a notebook and a book cover, a file, a catalog, a printing paper and the like.
【0002】[0002]
【従来の技術】キャストコート紙は、コート紙に属し最
も高級な印刷用紙で、高平滑かつ強光沢の表面を有して
いる。その製造方法には、ウエットキャスト法、ゲル化
キャスト法、リウエットキャスト法などが知られてい
る。その製造方法に関して、本願出願人も出願をし、特
許第2987528号、同第3013059号、同第3
013061号として登録されている。2. Description of the Related Art Cast coated paper is the highest grade printing paper belonging to coated paper and has a highly smooth and strong glossy surface. As the manufacturing method, a wet casting method, a gelling casting method, a rewetting casting method and the like are known. Regarding the manufacturing method, the applicant of the present application has filed an application, and the patent Nos. 2987528, 3013059, and 3
It is registered as No. 013061.
【0003】[0003]
【発明が解決しようとする課題】キャストコート紙は、
コート紙を含む印刷紙の中で最も高級な印刷紙に属し、
従って使用する原紙も晒木材パルプを原料として抄造し
た紙を使用するのが通例である。[Problems to be Solved by the Invention] Cast coated paper is
Belonging to the most exclusive printing paper among the printing paper including coated paper,
Therefore, as the base paper to be used, it is customary to use paper made from bleached wood pulp as a raw material.
【0004】ここで、キャストコート紙の原紙に未晒ク
ラフトパルプを原料として抄造した包装用のクラフト紙
を用い、従来使用してきた塗料でリウエットキャスト法
によりキャストコート紙を試験的に製造を試みたとこ
ろ、白色度が20〜30%低下することが分かった。[0004] Here, a kraft paper for packaging made from unbleached kraft pulp as a raw material is used as a base paper for the cast-coated paper, and an attempt is made to experimentally produce the cast-coated paper by the rewet casting method with a coating material that has been conventionally used. As a result, it was found that the whiteness was reduced by 20 to 30%.
【0005】本願発明は、従来使用されることの無かっ
た未晒木材パルプ、とくに未晒クラフトパルプを原料と
して抄造した紙を原紙として用い、従来品のキャストコ
ート紙と比べ、遜色のないキャストコート紙を製造しよ
うとするものであり、更には、未晒クラフトパルプ紙の
特徴を活かした従来なかった新しいキャストコート紙を
提供しようとするものである。The present invention uses unbleached wood pulp, which has never been used before, in particular, paper made from unbleached kraft pulp as a raw material, and has a cast cast that is comparable to conventional cast-coated paper. The present invention is intended to manufacture paper, and further to provide a new cast-coated paper which has not been heretofore utilized by utilizing the characteristics of unbleached kraft pulp paper.
【0006】[0006]
【課題を解決するための手段】上記の問題点を解決する
ために、本願発明は、従来白色度が低くキャストコート
紙の原紙として使用されたことのなかった未晒クラフト
パルプを用い抄造した未晒クラフトパルプ紙を原紙とし
て用いる場合、キャストコート紙の原紙として要求され
る特性値の通気性を損なうことのないように、軽量塗工
をした未晒クラフトパルプ紙を原紙を用いることによ
り、使用する原紙の白色度低下を補うことができ、従来
のキャスト紙製造工程を殆ど変えることなく製造できる
ことが分かり、解決せるものである。In order to solve the above-mentioned problems, the present invention has not been made into paper by using unbleached kraft pulp which has never been used as a base paper for cast coated paper because of its low whiteness. When using bleached kraft pulp paper as the base paper, use light-coated unbleached kraft pulp paper as the base paper so as not to impair the air permeability of the characteristic value required as the base paper for cast coated paper. It can be understood that the decrease in whiteness of the base paper can be compensated for, and that it can be manufactured with almost no change in the conventional cast paper manufacturing process.
【0007】また、従来のキャストコート用塗料におい
て、透明化剤を添加することにより、使用する未晒クラ
フトパルプ紙の原紙としての色調を活かした新しいキャ
ストコート紙が得られることが分かり目的を達成せるも
のである。Further, it was found that by adding a clarifying agent to a conventional cast coating material, a new cast coated paper utilizing the color tone of the unbleached kraft pulp paper to be used can be obtained. It is something that can be made.
【0008】[0008]
【発明の実施の形態】本発明は、針葉樹未晒クラフトパ
ルプ,広葉樹未晒クラフトパルプを原料として抄造した
未晒クラフト紙を原紙として用い、キャストコート紙を
製造せるもの(2)である。BEST MODE FOR CARRYING OUT THE INVENTION The present invention is a product (2) for producing cast-coated paper by using unbleached kraft paper made from unleafed softwood kraft pulp and hardwood unbleached kraft pulp as a raw paper.
【0009】未晒クラフト紙の抄造時又は抄造後、カオ
リンと重質炭酸カルシュウムを顔料とした塗料を5〜1
0g/m2,ガーレー透気度(JIS P8117によ
る)が500秒以下,吸水性がコッブサイズ度(JIS
P8140 60秒測定による)が10〜50g/m
2となるよう塗被した軽量塗工の未晒クラフト紙を原紙
として用いると、従来同様の塗料により従来品に白色
度、表面光沢ともに遜色のないキャストコート紙を製造
することができる。At the time of papermaking of unbleached kraft paper or after papermaking, 5 to 1 paints containing kaolin and heavy calcium carbonate as pigments are used.
0 g / m 2 , Gurley air permeability (according to JIS P8117) is 500 seconds or less, water absorption is Cobb size degree (JIS
P8140 60 seconds measurement) is 10-50 g / m
When a light-weight unbleached kraft paper coated so as to have a weight of 2 is used as a base paper, it is possible to produce a cast-coated paper which has a whiteness and surface gloss comparable to those of the conventional product by using the same coating material as the conventional one.
【0010】軽量塗工せずに抄造した未晒クラフト紙を
原紙として用い、従来のキャストコート用塗料にアクリ
ル系共重合体ラテックスを加え塗布することにより、未
晒クラフト紙の色調を活かした新しいキャストコート紙
が得られる。なお、アクリル系の他、スチレン、ウレタ
ン、ポリエステル、アミノ系樹脂、ワックス系樹脂、ポ
リプロピレングリコールなどの塗料層の透明性を増す樹
脂を使用できる。Using unbleached kraft paper that has not been light-weight coated as a base paper and adding an acrylic copolymer latex to a conventional cast coat paint to apply it, a new color tone of unbleached kraft paper is utilized. A cast coated paper is obtained. In addition to acrylic resins, resins such as styrene, urethane, polyester, amino resins, wax resins and polypropylene glycol which increase the transparency of the paint layer can be used.
【0011】また、塗料に使用する顔料配合を減少させ
塗料層の透明性を増すようにすると良いが、印刷適正を
考慮し、使用する顔料を屈折率の小さい炭酸カルシュウ
ム,カオリン,珪藻土,ゼオライト(沸石)などを配合
するなど、顔料の特性を活かした変更が好ましい。It is preferable to reduce the amount of pigment used in the paint to increase the transparency of the paint layer, but in consideration of printability, the pigment to be used is calcium carbonate having a small refractive index, kaolin, diatomaceous earth, zeolite ( It is preferable to make changes that take advantage of the characteristics of the pigment, such as blending with (zeolite).
【0012】[0012]
【実施例】本発明を実施例に従って説明する。
実施例 1
使用した原紙の未晒クラフト紙は、坪量100g/
m2,針葉樹未晒クラフトパルプ5%,広葉樹未晒クラ
フトパルプ95%で抄造し、抄紙機のコーターで下記配
合の塗料を約7g/m2塗被した。
塗料組成
顔料 カオリン 30部
重質炭酸カルシュウム 70部
分散剤 ポリアクリル酸ソーダ 0.5部
消泡剤 トリブチルホスフェート 0.1部
バインダー SBRラテックス 25部
澱粉 5部
注.1.実施例に示す部及び%は、重量部、重量%で示した。(以下、同
じ。)
2.顔料100部に対し、分散剤及び消泡剤の補助剤とバインダーを
加え塗料とした。
得られた軽量塗工した未晒クラフト紙は、白色度(JI
S P8123 ハンター白色度による)45%,ガー
レ透気度500秒であった。この軽量塗工紙を原紙とし
て用い、下記塗料を塗被量約20g/m2となるように
塗布し乾燥の後、再湿潤液を塗布し、キャスト加工し
た。
塗料組成
顔料 カオリン 68.5部
軽質炭酸カルシュウム 30.0部
サチン白 1.5部
分散剤 ポリアクリル酸ソーダ 0.5部
消泡剤 トリブチルホスフェート 0.5部
離型剤 ステアリン酸カルシウム 1.5部
バインダー SBRラテックス 15.0部
カゼイン 10.0部
注.塗料の固形分濃度は40%になるよう調節した。
キャスト加工条件
湿潤液 硫酸亜鉛 3.0%
加工速度 60 m/分
線圧 150 kg/cm
ドライヤー 温度 60 ℃
塗工層水分 15.2%
得られたキャストコート紙は、光沢度(JIS P81
42 投光角度75°による)87%,白色度(JIS
P8123による)83%,平滑度(J.TAPPI
No5−2 王研式スムスターによる)3000秒
で、引裂度,耐折強さなどが、従来品の晒クラフト紙よ
りも強く、良好であった。EXAMPLES The present invention will be described according to examples. Example 1 The unbleached kraft paper used as the base paper had a basis weight of 100 g /
m 2, softwood unbleached kraft pulp 5%, and papermaking with 95% hardwood unbleached kraft pulp, a coating having the following composition was about 7 g / m 2 coated with a coater in the paper machine. Coating composition Pigment Kaolin 30 parts Heavy calcium carbonate 70 parts Dispersant Sodium polyacrylate 0.5 parts Defoamer tributyl phosphate 0.1 parts Binder SBR latex 25 parts Starch 5 parts Note. 1. Parts and% shown in the examples are parts by weight and% by weight. (The same applies below.) 2. A dispersant and an antifoaming agent and a binder were added to 100 parts of the pigment to prepare a paint. The resulting lightweight coated unbleached kraft paper has a whiteness (JI
S P8123 (depending on Hunter whiteness) 45%, Gurley air permeability 500 seconds. Using this light-weight coated paper as a base paper, the following coating material was applied at a coating amount of about 20 g / m 2 , dried, and then rewetting liquid was applied, followed by casting. Paint composition Pigment Kaolin 68.5 parts Light calcium carbonate 30.0 parts Satin white 1.5 parts Dispersant sodium polyacrylate 0.5 parts Defoamer tributyl phosphate 0.5 parts Release agent Calcium stearate 1.5 parts Binder SBR latex 15.0 parts Casein 10.0 parts Note. The solid content concentration of the paint was adjusted to 40%. Casting conditions Wetting liquid Zinc sulfate 3.0% Processing speed 60 m / min Linear pressure 150 kg / cm Dryer temperature 60 ° C Moisture of coating layer 15.2% The cast coated paper obtained has glossiness (JIS P81
42 Emission angle 75 °) 87%, whiteness (JIS
P8123) 83%, smoothness (J. TAPPI
No. 5-2, according to Oken type Sumster), the tear strength, folding endurance, etc. were stronger and better than the conventional bleached kraft paper at 3000 seconds.
【0013】実施例 2
実施例1の原紙抄造時に、軽量塗工せずに未晒クラフト
紙を抄造し原紙とした。また、実施例1のキャストコー
ト用塗料に、アクリル樹脂系共重合体ラテックスを10
部加え、固型分濃度約50%とし、20g/m2となる
ように塗布し、加工条件は変えずにキャスト加工を行な
った。得られたキャストコート紙は、光沢度(JIS
P8142による)90%,白色度(JIS P812
3による)53%,平滑度(J.TAPPI No5−
2による)5000秒で、未晒クラフト紙の色相が現れ
た特徴のあるキャストコート紙である。Example 2 An unbleached kraft paper was made into a base paper without light coating at the time of making the base paper of Example 1. Further, 10 parts of acrylic resin-based copolymer latex was added to the cast coating composition of Example 1.
Parts were added, the solid content concentration was set to about 50%, coating was performed so as to be 20 g / m 2, and cast processing was performed without changing the processing conditions. The resulting cast coated paper has a gloss (JIS
90%, whiteness (according to P8142) (JIS P812
53%, smoothness (J. TAPPI No5-
It is a characteristic cast-coated paper in which the hue of unbleached kraft paper appears in 5000 seconds (according to No. 2).
【0014】[0014]
【発明の効果】本発明は、以上説明したように実施さ
れ、以下に記載されるような効果を奏する。The present invention is implemented as described above and has the following effects.
【0015】従来、原紙として使用されることのなかっ
た未晒クラフト紙を、キャストコート紙の原紙として使
用することにより、晒パルプを原紙とした場合に比べ、
紙の強度は20〜30%強くなり、包装用紙としての適
性が良い製品を提供できる。By using unbleached kraft paper, which has never been used as a base paper, as a base paper for cast coated paper, compared to the case where bleached pulp is used as a base paper,
The strength of the paper is increased by 20 to 30%, and a product having good suitability as a packaging paper can be provided.
【0016】未晒クラフト紙を用いることにより、新し
いキャストコート紙を提供でき、更には塗料に樹脂系透
明化剤を配合することにより、強光沢のキャストコート
紙としての性質を損なうことなく、印刷適正、耐水性良
好な新製品を提供できる。By using unbleached kraft paper, a new cast-coated paper can be provided, and by adding a resin-based clarifying agent to the paint, printing can be performed without impairing the properties as cast coating paper with high gloss. Providing appropriate new products with good water resistance.
【0018】未晒クラフト紙を原紙としたキャストコー
ト紙は、使用後焼却するもダイオキシンの発生なく、環
境面を考慮した紙である。The cast coated paper using unbleached kraft paper as a base paper does not generate dioxin even if it is incinerated after use, and is an environmentally friendly paper.
Claims (3)
未晒クラフトパルプを原料として抄造した未晒クラフト
紙を原紙として製造したキャストコート紙。1. A cast-coated paper produced by using unbleached kraft paper made from unbleached kraft pulp of hardwood and unbleached kraft pulp of hardwood as raw materials.
ャストコート塗被面に塗料を顔料として約7g/m2塗
被した軽量塗工の未晒クラフト紙を原紙として用いるこ
とを特徴とするキャストコート紙の製造方法。2. A lightweight coated unbleached kraft paper coated with about 7 g / m 2 of a paint as a pigment on the cast coat coated surface during or after the unbleached kraft paper is used as a base paper. A method for producing cast-coated paper.
ート紙において、顔料と接着剤を主成分としたキャスト
コート用塗料に透明化剤としてアクリル系共重合体ラテ
ックスなどを配合したことを特徴とするキャストコート
紙の製造方法。3. A cast-coated paper using unbleached kraft paper as a base paper, characterized in that an acrylic copolymer latex or the like is blended as a clarifying agent in a cast-coating paint containing a pigment and an adhesive as main components. A method for producing cast-coated paper.