JP2003276137A - Multilayered film - Google Patents
Multilayered filmInfo
- Publication number
- JP2003276137A JP2003276137A JP2002036380A JP2002036380A JP2003276137A JP 2003276137 A JP2003276137 A JP 2003276137A JP 2002036380 A JP2002036380 A JP 2002036380A JP 2002036380 A JP2002036380 A JP 2002036380A JP 2003276137 A JP2003276137 A JP 2003276137A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- film
- nylon
- oxygen barrier
- outer layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は深絞り成形されたフ
ィルムに中身を充填し、蓋材によりシールされる食品等
包装分野において、透明性に優れ、レトルト処理が可能
な多層フィルムに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a multi-layer film which is excellent in transparency and can be retort processed in the field of packaging such as foods in which a deep-drawn film is filled with contents and sealed with a lid material. .
【０００２】[0002]
【従来の技術】食品や医薬品等の深絞り包装分野におい
て使用される包材には低温での成形加工性、内容物を識
別するための透明性、外部の衝撃から保護する耐ピンホ
ール性等の性能が必要であり、内容物によってはボイル
やレトルト処理が可能であることも必要である。ボイル
やレトルト処理は食品の変質や腐敗の原因となる微生物
を死滅、除去するために行われたり、食品の調理作業と
して行われたりする。しかしながら殺菌が不十分であっ
たり、保管が適切でない状態では製品が変色したり、腐
敗する場合がある。そのため包装材には酸素の透過を防
止する酸素バリア性が要求されている。2. Description of the Related Art Packaging materials used in the field of deep-drawing packaging such as foods and pharmaceuticals have low moldability at low temperature, transparency for identifying contents, and pinhole resistance for protection from external impact. Performance is required, and it is also necessary that boil and retort treatment are possible depending on the contents. Boil or retort treatment is performed to kill or remove microorganisms that cause deterioration or spoilage of food, or as a food cooking operation. However, if sterilization is inadequate, or if it is not properly stored, the product may become discolored or spoil. Therefore, the packaging material is required to have an oxygen barrier property for preventing the permeation of oxygen.
【０００３】酸素バリア性において、従来から用いられ
ている技術として多層フィルムの一層にエチレンビニル
アルコール共重合体を使用する方法がとられており、耐
熱水性の点から中間層として用いられ、外層には水蒸気
バリア性に優れるポリエチレンやポリプロピレンがエチ
レンビニルアルコール共重合体の殺菌時の吸湿による酸
素バリア性低下を防止するために用いられている。しか
しながらポリエチレンやポリプロピレンの比率を高くす
ると包材の透明性が低下し、商品の見栄えを損ねる問題
があり、比率を低くすると殺菌時の水蒸気バリア性が不
十分でエチレンビニルアルコール共重合体の酸素バリア
性が低下し、殺菌後の酸素バリア性の回復に長い時間が
かかる問題がある。また、包材に印刷が施されているこ
とも商品価値を高めるために必要な性能であり、一般に
は印刷したフィルムが外層にラミネートされるが、殺菌
処理がある場合は前述同様、殺菌時にチレンビニルアル
コール共重合体の酸素バリア性が低下し、殺菌後の酸素
バリア性の回復に長い時間がかかる問題がある。Regarding the oxygen barrier property, as a conventionally used technique, a method of using an ethylene vinyl alcohol copolymer for one layer of a multi-layer film has been adopted. From the viewpoint of hot water resistance, it is used as an intermediate layer and an outer layer. Polyethylene and polypropylene, which have excellent water vapor barrier properties, are used to prevent a decrease in oxygen barrier properties due to moisture absorption during sterilization of ethylene vinyl alcohol copolymers. However, if the ratio of polyethylene or polypropylene is increased, the transparency of the packaging material will decrease and the appearance of the product will be impaired.If the ratio is decreased, the water vapor barrier property during sterilization will be insufficient and the oxygen barrier of ethylene vinyl alcohol copolymer will be reduced. However, there is a problem in that it takes a long time to recover the oxygen barrier property after sterilization. In addition, the fact that the packaging material is printed is also a performance necessary for increasing the commercial value, and generally, the printed film is laminated on the outer layer, but if there is a sterilization treatment, it is the same as the above when it is sterilized during sterilization There is a problem that the oxygen barrier property of the vinyl alcohol copolymer is lowered and it takes a long time to recover the oxygen barrier property after sterilization.
【０００４】[0004]
【発明が解決しようとする課題】本発明の目的はレトル
ト等の加熱処理が可能な包装材として、内容物の保存性
に優れ、商品価値を高める印刷を有する多層フィルムを
提供することにある。SUMMARY OF THE INVENTION It is an object of the present invention to provide a multi-layer film having a print that enhances the commercial value as a packaging material that can be heat-treated, such as a retort, because the content has excellent storability.
【０００５】[0005]
【課題を解決するための手段】本発明は外層、中間層、
及びシール層からなる多層フィルムであり、外層がナイ
ロンからなり、中間層がエチレンビニルアルコール共重
合体からなり、シール層が印刷されたオレフィンフィル
ムからなり、好ましくは、外層、及び中間層が共押し出
し法により製膜され、シール層がラミネートされる多層
フィルムである。The present invention comprises an outer layer, an intermediate layer,
And a multilayer film comprising a seal layer, the outer layer comprising nylon, the intermediate layer comprising an ethylene vinyl alcohol copolymer, the seal layer comprising a printed olefin film, preferably the outer layer and the intermediate layer coextrusion It is a multi-layer film formed by a method and laminated with a seal layer.
【０００６】[0006]
【発明の実施の形態】本発明の外層にはナイロンが用い
られ、中間層のエチレンビニルアルコール共重合体（Ｅ
ＶＯＨ）の熱水からの保護、及び、酸素バリア性の回復
のために設けられる。熱水からの保護とはＥＶＯＨが熱
水に溶け出し、酸素バリア性の低下だけでなく、フィル
ム表面が荒れた状態になり白濁することをナイロンの耐
熱性により防止することである。また、酸素バリア性の
回復とは吸湿により一旦低下したＥＶＯＨの酸素バリア
性がナイロンの水蒸気透過性により乾燥し、酸素バリア
性が回復することである。ナイロン樹脂としては６ナイ
ロン、６−６ナイロン、６−１０ナイロン、６−１２ナ
イロン、１２ナイロンまたはこれらの共重合体や混合物
があるが、耐熱水性、耐ピンホール性能、加工性の点か
ら６ナイロン樹脂が望ましい。BEST MODE FOR CARRYING OUT THE INVENTION Nylon is used for the outer layer of the present invention, and an ethylene vinyl alcohol copolymer (E
It is provided to protect (VOH) from hot water and to recover the oxygen barrier property. The protection from hot water is to prevent EVOH from dissolving in hot water and reducing the oxygen barrier property, and also to prevent the film surface from becoming rough and clouding due to the heat resistance of nylon. The recovery of the oxygen barrier property means that the oxygen barrier property of EVOH once reduced by moisture absorption is dried by the water vapor permeability of nylon and the oxygen barrier property is recovered. Nylon resins include 6 nylon, 6-6 nylon, 6-10 nylon, 6-12 nylon, 12 nylon or copolymers or mixtures thereof, but in view of hot water resistance, pinhole resistance and processability, 6 Nylon resin is preferred.
【０００７】中間層にはＥＶＯＨが用いられ、内容物の
保護、保全のために設けられ、保護、保全機能として
は、具体的には酸素バリア性の付与を指す。酸素バリア
性を付与するにはＥＶＯＨやポリ塩化ビニリデン等の樹
脂を用いることができるが、酸素バリア性能の点からＥ
ＶＯＨが望ましい。EVOH is used for the intermediate layer and is provided for the purpose of protecting and preserving the contents. The protective and preserving function specifically refers to imparting an oxygen barrier property. Resins such as EVOH and polyvinylidene chloride can be used to impart oxygen barrier properties. However, from the viewpoint of oxygen barrier performance, E
VOH is preferred.
【０００８】シール層は印刷されたオレフィンフィルム
からなり意匠性とシール性のために設けられる。シール
層にはポリプロピレン、ポリエチレンやポリエチレンの
変性物等を用いることができるが、耐レトルト性の点か
らポリプロピレンが望ましい。意匠性を付与する印刷は
インクの剥がれの防止から印刷されたフィルムをラミネ
ート法により多層フィルムの内部に施すが、外層にラミ
ネートすると前述の理由により酸素バリア性の回復が妨
げられ、内層であるシール層としてラミネートすること
で酸素バリア性の回復についても満たすことが出来る。The seal layer is made of a printed olefin film and is provided for design and sealability. Although polypropylene, polyethylene, or a modified product of polyethylene can be used for the seal layer, polypropylene is preferable from the viewpoint of retort resistance. Printing that gives design is applied to the inside of the multilayer film by a laminating method to prevent the ink from peeling, but when laminated on the outer layer, recovery of the oxygen barrier property is hindered for the above-mentioned reason, and the seal of the inner layer is applied. By laminating as a layer, the recovery of the oxygen barrier property can also be satisfied.
【０００９】[0009]
【実施例】下記に示す原料を使用して多層マルチマニホ
ールド共押出しダイスで多層フィルムを作製し、下記に
示すフィルムとドライラミネートした。得られたフィル
ムを包装材として、連続深絞り包装機（大森機械工業製
ＦＶ６３００）で１００ｇの惣菜を真空パックしたサン
プルを作成し、１２０℃３０分間のレトルト処理後の外
観と、酸素バリア性を評価した。Example A multilayer film was prepared by using the following raw materials and a multi-layer multi-manifold coextrusion die, and was dry-laminated with the film shown below. Using the obtained film as a packaging material, a continuous deep-draw packaging machine (FV6300 manufactured by Omori Machinery Co., Ltd.) was used to vacuum-pack 100 g of prepared foods, and the appearance and oxygen barrier property after retort treatment at 120 ° C. for 30 minutes were prepared. evaluated.
【００１０】共押出しでの使用原料は次のとおりであ
る。
ＮＹ ：６ナイロン（宇部興産製UBEナイロン1024B）
ＥＶＯＨ：エチレン−ビニルアルコール共重合体（日本
合成化学製ソアノールRB1404）
ラミネートでの使用フィルムは次のとおりである。
ＰＰ ：印刷されたポリプロピレン（５０μm）
ＰＥ ：印刷されたポリエチレン（５０μm）
層構成及び厚みは下記の表１のとおりである。The raw materials used in coextrusion are as follows. NY: 6 nylon (UBE nylon 1024B manufactured by Ube Industries) EVOH: ethylene-vinyl alcohol copolymer (Soarnol RB1404 manufactured by Nippon Synthetic Chemical Industry) The films used in the laminate are as follows. PP: Printed polypropylene (50 μm) PE: Printed polyethylene (50 μm) The layer structure and thickness are shown in Table 1 below.
【００１１】評価は下記の方法で行った。
（１）外観…レトルト処理後の状態を観察した。
○：良好、×：白化、破袋発生
（２）酸素バリア性…レトルト処理1日後の酸素ガス透
過率を測定した。
酸素ガス透過率：１ml/m2・24hr・atm（25℃65％ＲＨ）
以下であれば良好評価結果は下記の表１のとおりであ
る。The evaluation was performed by the following method. (1) Appearance: The state after the retort treatment was observed. ◯: Good, ×: Whitening, bag breakage occurred (2) Oxygen barrier property: The oxygen gas permeability was measured 1 day after the retort treatment. Oxygen gas permeability: 1 ml / m 2 · 24 hr · atm (25 ° C 65% RH)
The results of good evaluation are as shown in Table 1 below.
【００１２】[0012]
【表１】 [Table 1]
【００１３】[0013]
【発明の効果】本発明による包装体はレトルト等の加熱
処理が可能な包装材として、内容物の保存性に優れ、印
刷を有するため商品価値の高い製品を提供することが出
来る。EFFECTS OF THE INVENTION The package according to the present invention can be provided as a packaging material that can be heat-treated, such as a retort, because it has excellent storability of contents and has printing, and thus has high commercial value.
Claims (2)
層フィルムであり、外層がナイロンからなり、中間層が
エチレンビニルアルコール共重合体からなり、シール層
が印刷されたオレフィンフィルムからなることを特徴と
する多層フィルム。1. A multilayer film comprising an outer layer, an intermediate layer and a seal layer, wherein the outer layer comprises nylon, the intermediate layer comprises an ethylene vinyl alcohol copolymer and the seal layer comprises a printed olefin film. Characteristic multilayer film.
製膜され、シール層がラミネートされることを特徴とす
る請求項１記載の多層フィルム。2. The multilayer film according to claim 1, wherein the outer layer and the intermediate layer are formed into a film by a co-extrusion method, and the seal layer is laminated.