JP2003184060A - Float cover - Google Patents
Float coverInfo
- Publication number
- JP2003184060A JP2003184060A JP2001389515A JP2001389515A JP2003184060A JP 2003184060 A JP2003184060 A JP 2003184060A JP 2001389515 A JP2001389515 A JP 2001389515A JP 2001389515 A JP2001389515 A JP 2001389515A JP 2003184060 A JP2003184060 A JP 2003184060A
- Authority
- JP
- Japan
- Prior art keywords
- float cover
- float
- polyester
- cover
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、海洋工事用の汚濁
防止膜等を浮かせるためのフロートを内包するのに用い
る、フロートカバーに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a float cover used for containing a float for floating a pollution prevention film for marine construction.
【０００２】[0002]
【従来の技術】海洋工事等で汚濁防止膜を使用する際に
は、水中で浮かせるためにフロートが用いられるが、こ
のフロートとしては、浮力に優れ、腐蝕がなく、価格も
安い等の理由から発泡スチロールが従来から主に使用さ
れている。この発泡スチロール製のフロートを用いる際
には、風波の衝撃等による崩壊と散逸を防ぐ等の目的か
ら、フロートカバーに内包して用いるのが通常である。2. Description of the Related Art A float is used to float in water when using a pollution control film in marine construction, etc., but this float is excellent in buoyancy, does not corrode, and is cheap in price. Styrofoam has been mainly used conventionally. When the float made of styrofoam is used, it is usually contained in a float cover for the purpose of preventing collapse and dissipation due to impact of wind waves.
【０００３】そのようなフロートカバーの材料として
は、ポリエステル繊維等を用いた織布に塩化ビニル系樹
脂を被覆加工したものが主に用いられており、かかる樹
脂被覆加工に際しては、船舶等が視認しやすいように、
黄・橙系色に着色した樹脂が用いられてきた。ここで、
当該被覆加工するための樹脂に塩化ビニル系樹脂が用い
られる理由としては、加工性が優れており、種々の加工
方法が採用でき、また任意の柔軟性に調整できること、
顔料による発色性の良好なことが挙げられる。As a material for such a float cover, a woven cloth made of polyester fiber or the like is mainly used, which is coated with a vinyl chloride resin. When such resin coating is carried out, a vessel or the like is visually recognized. To make it easier
Yellow-orange colored resins have been used. here,
The reason why the vinyl chloride resin is used as the resin for the coating process is that it has excellent processability, various processing methods can be adopted, and that it can be adjusted to any flexibility.
The good coloring property by the pigment is mentioned.
【０００４】[0004]
【発明が解決しょうとする課題】上記の如く、塩化ビニ
ル系樹脂を被覆加工した織布を用いたフロートカバー
は、多くの長所を有しているが、樹脂加工のために重量
が重くなりがちであった。また、近年の環境汚染問題を
考慮すれば、使用後に廃棄物として処理する場合にこれ
を焼却すると、塩化ビニル系樹脂を含んでいるためにダ
イオキシンの発生が懸念され、処理が困難になるという
問題もあった。As described above, the float cover using the woven cloth coated with vinyl chloride resin has many advantages, but tends to be heavy due to the resin processing. Met. Also, considering the recent environmental pollution problem, if this is incinerated when it is treated as a waste after use, it is feared that dioxins will be generated because it contains vinyl chloride resin, which makes the treatment difficult. There was also.
【０００５】本発明は、このような現状を鑑みて行われ
たもので、軽量で作業性に優れ、かつ塩化ビニル樹脂系
を含んでいないために焼却してもダイオキシンの発生す
る心配のないフロートカバーを提供することを課題とす
るものである。The present invention has been made in view of the above circumstances, and it is lightweight and has excellent workability, and since it does not contain a vinyl chloride resin system, it does not generate dioxin even when incinerated. The challenge is to provide a cover.
【０００６】[0006]
【課題を解決する手段】本発明は、上記課題を達成する
ものであり、固有粘度が0.85以上のポリエステル樹脂か
らなり、顔料を含有するポリエステル原着糸を用いて製
編織され、引張強力が２KN／３cm以上である布帛を用い
てなることを特徴とするフロ−トカバーを要旨とするも
のである。Means for Solving the Problems The present invention is to achieve the above-mentioned object and is made of a polyester resin having an intrinsic viscosity of 0.85 or more, and is knitted and woven using a polyester-dyed yarn containing a pigment, and the tensile strength is 2 KN. The gist of the present invention is a float cover, which is characterized by using a cloth having a length of / 3 cm or more.
【０００７】[0007]
【発明の実施の形態】以下、本発明について詳細に説明
する。本発明のフロートカバーは、ポリエステル原着糸
で製編織された布帛を用いてなるものである。ポリエス
テル原着糸を構成するポリエステル樹脂としては、ポリ
エチレンテレフタレートを主体としたものが好ましく用
いられ、少量の共重合成分や耐熱剤その他の添加剤が含
まれていてもよい。BEST MODE FOR CARRYING OUT THE INVENTION The present invention will be described in detail below. The float cover of the present invention is made of a fabric woven and knitted with polyester primary yarn. Polyester terephthalate is preferably used as the polyester resin forming the polyester spun yarn, and a small amount of a copolymerization component, a heat-resistant agent and other additives may be included.
【０００８】ポリエステル樹脂の固有粘度としては、
０．８５以上であることが必要であり、０．６７〜１．
２０が好ましい。ここで、固有粘度とは、フェノールと
テトラクロロエタンとを質量比１：１で混合したものを
測定用溶媒として、温度２０℃で測定した値をいう。固
有粘度が０．８５未満の場合、フロートカバー、特に汚
濁防止膜用フロートのフロートカバーの構成素材として
必要な強度をポリエステル原着糸に具備させるには延伸
倍率を極めて大きくしなければならなくなるため、原着
糸製造時の操業性が悪くなり、得られる原着糸の品位も
悪くなるので好ましくない。The intrinsic viscosity of the polyester resin is
It is necessary to be 0.85 or more, and 0.67 to 1.
20 is preferable. Here, the intrinsic viscosity means a value measured at a temperature of 20 ° C. using a mixture of phenol and tetrachloroethane at a mass ratio of 1: 1 as a measurement solvent. If the intrinsic viscosity is less than 0.85, the draw ratio must be extremely increased in order to provide the polyester spun yarn with the strength required as a constituent material of the float cover, especially the float cover of the antifouling film. However, the operability during the production of the spun-dyed yarn is deteriorated and the quality of the obtained spun-dyed yarn is also deteriorated, which is not preferable.
【０００９】また、ポリエステル原着糸には顔料が含有
されていることが必要である。顔料を含まず染料のみで
着色された原着糸では、耐候性に劣る。原着糸の色相と
して、船舶等から視認しやすいように黄色、橙色系が好
ましいことから、顔料としては、黄色系顔料もしくは橙
色系顔料が好ましい。黄色系顔料としては、アンスラキ
ン系黄及びペリノン系赤を主体とする着色顔料が好まし
く、また、橙色系顔料としては、アンスラキノン系黄・
ペリノン系赤及びアンスラキノン系茶を主体とする着色
顔料が好ましい。原着糸に上記の顔料を含有させる方法
としては、原着糸製造工程でチップに顔料を添加しても
よく、顔料のマスターチップを使用してもよい。Further, the polyester-dyed yarn must contain a pigment. The weathering resistance is inferior when the dyed yarn is dyed without a pigment. The hue of the spun yarn is preferably yellow or orange so that it can be easily seen from a ship or the like. Therefore, the pigment is preferably a yellow pigment or an orange pigment. The yellow pigment is preferably a color pigment mainly composed of anthraquin yellow and perinone red, and the orange pigment is anthraquinone yellow.
Coloring pigments based on perinone red and anthraquinone tea are preferred. As a method of incorporating the above-mentioned pigment into the spun-dyed yarn, the pigment may be added to the chip in the process of producing the spun-dyed yarn, or a pigment master chip may be used.
【００１０】上記のポリエステル原着糸で製編織された
布帛（以下、ポリエステル原着布帛）の組織構造として
は、特に限定されるものではなく、織物組織でも編物組
織でもよいが、強度を確保しやすい点から、平織、綾
織、朱子織又はこれらの組織を変化させた織物組織が好
ましい。There is no particular limitation on the structure structure of the above-mentioned cloth woven or knitted with the polyester original yarn (hereinafter referred to as polyester original cloth), and it may be a woven structure or a knit structure, but the strength is ensured. A plain weave, a twill weave, a satin weave, or a woven fabric structure obtained by changing these fabrics is preferable from the standpoint of ease.
【００１１】ポリエステル原着布帛にはフロートカバー
に適した強度が備わっている必要があることから、ポリ
エステル原着布帛の引張り強力としては、２kN／３cm以
上であることが必要であり、２kN／３cm〜１０kN／３cm
が好ましい。通常、フロートカバーは汚濁防止膜等の被
フロート物に連結されて用いられるものであり、波動等
の影響で被フロート物に力がかかることにより、それと
連結しているフロートカバーが引張られ、フロートの浮
力の抵抗により布帛に強い力がかかる。このとき、上記
の引張強力が２kN／３cm未満では、フロートカバーが破
損するおそれがある。一方、引張り強度の上限について
は、強度面だけを見れば強いほど良いともいえるが、引
張り強力を必要以上に高くすることは、糸の繊度や製編
織密度を極端に高くすることにつながるので、重量が増
したり、コストアップを招いて好ましくない。この点か
ら、引張強力が１０kN／３cmを超えないことが好ましい
のである。なお、布帛の目付けとしては、１２００ｇ／
ｍ2以下が好ましい。Since the polyester original cloth should have strength suitable for the float cover, the tensile strength of the polyester original cloth should be 2 kN / 3 cm or more, and 2 kN / 3 cm. -10kN / 3cm
Is preferred. Usually, the float cover is used by being connected to a floated object such as a pollution prevention film.When the floated object is subjected to a force due to the influence of waves or the like, the float cover connected to the float cover is pulled and the float cover is pulled. The buoyancy resistance causes a strong force on the fabric. At this time, if the tensile strength is less than 2 kN / 3 cm, the float cover may be damaged. On the other hand, regarding the upper limit of the tensile strength, it can be said that the stronger the strength alone is, the better.However, increasing the tensile strength more than necessary leads to extremely high yarn fineness and weaving density. It is not preferable because the weight increases and the cost increases. From this point, it is preferable that the tensile strength does not exceed 10 kN / 3 cm. The fabric weight is 1200 g /
It is preferably m 2 or less.
【００１２】上記のポリエステル原着布帛を用いて、使
用時に筒状もしくは袋状となるように適宜縫製すること
により、本発明のフロートカバーとする。その形態及び
使用態様の例を図１及び図２に基づいて説明すれば、例
えば筒状のフロートを内包するために、好ましくは長手
方向に沿って開口する筒状を形成できるようなフロート
カバー１を、汚濁防止膜等の被フロート物に連結する。
そして、フロートカバーにフロート２を内包させて、開
口部を取り込みロープ７で縛り、使用に供する。フロー
トには、フロート同士を連結させるため、またフロート
カバー内での安定を図るため、中通しロープを通すこと
が好ましく行われる。The float cover of the present invention is obtained by appropriately sewing the above-mentioned polyester swatch cloth so as to have a tubular shape or a bag shape when used. An example of the form and the mode of use will be described with reference to FIGS. 1 and 2. For example, in order to include a cylindrical float, a float cover 1 which can preferably form a cylinder opening along the longitudinal direction. Is connected to an object to be floated such as a pollution prevention film.
Then, the float 2 is enclosed in the float cover, and the opening is taken in and tied with the rope 7 for use. In order to connect the floats to each other and to stabilize the float in the float cover, it is preferable to pass an intermediate rope through the float.
【００１３】本発明のフロートカバーの層構造として
は、上記のポリエステル原着布帛の層のみからなるもの
でもよく、他の布帛やシート状材料とからなる複層構造
のものでもよい。上記のポリエステル原着布帛は通水性
を有しているので、フロートカバーが上記のポリエステ
ル原着布帛の層のみからなる場合や、他の通水性を有す
る材料との複層構造である場合には、フロートカバー内
部に水が滞留せず外部と頻繁に入れ代わるため、フロー
トカバー内で水が腐るという事態が回避できる。The layer structure of the float cover of the present invention may be a layer structure composed only of the above-mentioned polyester original cloth, or may be a multilayer structure composed of other cloth or sheet material. Since the above polyester primary cloth has water permeability, when the float cover is composed of only the layer of the above polyester original cloth, or when it has a multi-layer structure with another material having water permeability, Since water does not stay inside the float cover and is frequently replaced with the outside, it is possible to avoid a situation in which water rots inside the float cover.
【００１４】[0014]
【実施例】次に、本発明を実施例により具体的に説明す
る。なお、実施例中に記載の特性は以下の方法で測定し
た。
（１）固有粘度
フェノールとテトラクロロエタンとを質量比１：１で混
合したものを測定用溶媒として、温度２０℃で測定し
た。
（２）糸条の引張り強度
島津製作所製オートグラフAG−100B型を用い、試料長
（チャック間距離）２５０ｍｍ、引張速度３００ｍｍ／
分で測定した。
（３）織物の引張強力
ＪＩＳ Ｌ １０９６に準拠して、島津製作所製オート
グラフAG−100B型を用い、試料幅３ｃｍ、試料長（チャ
ック間距離）２００ｍｍ、引張速度２００ｍｍ／分で測
定した。EXAMPLES Next, the present invention will be specifically described by way of examples. The properties described in the examples were measured by the following methods. (1) Intrinsic viscosity A mixture of phenol and tetrachloroethane at a mass ratio of 1: 1 was used as a measurement solvent, and the measurement was performed at a temperature of 20 ° C. (2) Tensile strength of yarn Using Autograph AG-100B manufactured by Shimadzu Corporation, sample length (distance between chucks) 250 mm, pulling speed 300 mm /
Measured in minutes. (3) Tensile Strength of Woven Fabric According to JIS L 1096, using an Autograph AG-100B type manufactured by Shimadzu Corporation, measurement was performed with a sample width of 3 cm, a sample length (distance between chucks) 200 mm, and a pulling speed of 200 mm / min.
【００１５】実施例１
固有粘度が1.11のポリエチレンテレフタレート（PET）
樹脂のチップと、同じPET樹脂にアンスラキノン系黄、
ペリノン系赤及びアンスラキノン系茶を主体とする橙色
系着色顔料を20質量％含有させたマスターチップとを、
PET樹脂チップ／マスターチップ＝97.5／2.5の質量比で
溶融混合したものを原料として、紡糸温度 295℃で、孔
数96の紡糸口金から紡出し、口金直下に配設した長さ 2
10ｍｍ、雰囲気温度 430℃の加熱筒を通した後、冷却風
を吹きつけて冷却した。冷却固化した糸条に、紡糸油剤
を繊維質量に対して0.7質量％付与した後、周速 350ｍ
／分の引取ローラで引き取り、引取ローラと供給ローラ
との間で 0.5％のストレッチを与えて糸条を安定化さ
せ、供給ローラと 230℃の加熱延伸ローラとの間で過熱
水蒸気を吹きつけながら 6.0倍に延伸し、延伸ローラと
同速度の 150℃の加熱ローラで引き取り、仕上げ油剤を
繊維質量に対して 0.7質量％付与して巻き取り、強度6.
5ｃN／dtex、伸度21%、1100dtex／96fの橙色の原着糸条
を得た。 この原着糸条３本をｓ方向に８０Ｔ／ｍで施
撚したものを経糸及び緯糸に使用して、レピア織機によ
り、織組織が２／２斜子織、織密度が経２５本／2.54c
m、緯２５本／2.54cm、織巾が２１０cmの織物を製織し
た。この織物の引張強力は、経方向が５．６kN／3cm、
緯方向が５．５kN／3cmであった。この織物を用いて筒
状のフロートカバーを作成し、図１に示すような汚濁防
止膜ユニット（２０ｍ／１スパン）のカーテン部に縫い
付けた。しかる後にフロートカバー内に発泡ポリスチレ
ン製の筒状フロートを内包させ、この汚濁防止膜ユニッ
トを海中に設置し、カーテンを海底から垂直に浮かせた
状態で２年間使用した。使用後のフロートカバーには破
れた所もなく、まだ十分に使用できる状態であった。ま
た、このものを焼却したが、有害ガスの発生は無かっ
た。Example 1 Polyethylene terephthalate (PET) having an intrinsic viscosity of 1.11.
Anthraquinone yellow on the same PET resin as the resin chip,
A master chip containing 20 mass% of an orange coloring pigment mainly composed of perinone red and anthraquinone tea,
PET resin chip / master chip = 97.5 / 2.5 melt-mixed as raw material, spinning temperature 295 ℃, spun from a spinneret with 96 holes, and a length of 2 just below the spinneret.
After passing through a heating cylinder of 10 mm and an atmospheric temperature of 430 ° C., cooling air was blown to cool it. The spinning speed was 350 m after the spinning oil was added to the cooled and solidified yarn in an amount of 0.7% by mass of the fiber mass.
/ Min take-up roller to give a 0.5% stretch between the take-up roller and the feed roller to stabilize the yarn, while blowing superheated steam between the feed roller and the heated drawing roller at 230 ° C. Stretching 6.0 times, take it up with a heating roller at the same speed as the stretching roller at 150 ° C, add 0.7% by mass of finishing oil to the fiber mass, and wind it up.
An orange dyed yarn of 5cN / dtex, 21% elongation and 1100dtex / 96f was obtained. The warp and weft yarns obtained by twisting three of these spun yarns at 80 T / m in the s direction were used by a rapier loom to have a weave design of 2/2 weave and a weave density of 25 warp / 2.54 c
A woven fabric having m, 25 wefts / 2.54 cm, and a cloth width of 210 cm was woven. The tensile strength of this fabric is 5.6kN / 3cm in the warp direction,
The weft direction was 5.5 kN / 3 cm. A tubular float cover was prepared using this woven fabric and sewn to the curtain portion of the pollution prevention membrane unit (20 m / 1 span) as shown in FIG. Thereafter, a tubular float made of expanded polystyrene was included in the float cover, the pollution prevention membrane unit was installed in the sea, and the curtain was used for two years in a state of being vertically floated from the seabed. After use, there was no tear on the float cover, and it was still in good condition. The product was incinerated, but no harmful gas was generated.
【００１６】[0016]
【発明の効果】本発明のフロートカバーは、ポリエステ
ル原着糸を使用しているので耐候性に優れ、顔料による
発色が良好で視認性に優れ、色落ちもない。また、樹脂
加工を施す必要がないので、軽量で作業性にも優れてお
り、樹脂被覆の剥がれによる品位や視認性の低下を心配
することもない。また、塩化ビニル系樹脂を含んでいな
いので、焼却処理をしてもダイオキシン等の有害物質を
発生しない。以上のように優れた特長を有し、強度的に
も優れた本発明のフロートカバーは、各種フロートのカ
バーとして使用でき、特に汚濁防止膜用に好適である。EFFECTS OF THE INVENTION The float cover of the present invention, which uses polyester-dyed yarn, has excellent weather resistance, good coloring due to pigments, excellent visibility, and no discoloration. Further, since it is not necessary to perform resin processing, it is lightweight and excellent in workability, and there is no fear of deterioration of quality and visibility due to peeling of the resin coating. In addition, since it does not contain vinyl chloride resin, it does not generate harmful substances such as dioxins even when incinerated. The float cover of the present invention having the above-mentioned excellent features and excellent strength can be used as a cover for various floats, and is particularly suitable for a pollution control film.
【図１】 本発明のフロートカバーを有する汚濁防止膜
ユニットの一例を示す概略側面図である。FIG. 1 is a schematic side view showing an example of a pollution prevention membrane unit having a float cover of the present invention.
【図２】 本発明のフロートカバーの使用例を示す断面
図である。FIG. 2 is a cross-sectional view showing an example of use of the float cover of the present invention.
１．フロートカバー ２．フロート ３．カーテン ４．補強ベルト ５．アンカー ６．中通しロープ ７．取り込みロープ 1. Float cover 2. float 3. curtain 4. Reinforced belt 5. anchor 6. Medium rope 7. Capture rope
───────────────────────────────────────────────────── フロントページの続き (72)発明者 岩田 賢三 大阪府大阪市中央区備後町三丁目４番９号 ユニチカ通商株式会社内 Ｆターム(参考） 2D025 AA03 ─────────────────────────────────────────────────── ─── Continued front page (72) Inventor Kenzo Iwata 3-4-9 Bingo-cho, Chuo-ku, Osaka-shi, Osaka Prefecture Unitika Trading Co., Ltd. F-term (reference) 2D025 AA03
Claims (3)
からなり、顔料を含有するポリエステル原着糸を用いて
製編織され、引張強力が２kN／３cm以上である布帛を用
いてなることを特徴とするフロ−トカバー。1. A fabric made of a polyester resin having an intrinsic viscosity of 0.85 or more, woven and knitted using a polyester-dyed yarn containing a pigment, and having a tensile strength of 2 kN / 3 cm or more. Float cover.
とを特徴とする請求項１に記載のフロートカバー。2. The float cover according to claim 1, wherein the cloth is not resin-coated.
を特徴とする請求項２又は３に記載のフロートカバー。3. The float cover according to claim 2, which is a float cover for a pollution control film.