JP2003183584A - Metallic gloss exhibiting coating and method for depicting pictorial pattern by using the same - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To picture a decorative pattern of fine particles which exhibit metallic gloss. <P>SOLUTION: A coating for the decorative pattern which has diamond powder of 10-15 μm as a major component is prepared. On the surface of a substrate such as a surface printed in a two-color reactive ink by screen printing on a darkly coated surface and a Japanese lacquer coated surface, the coating is attached at a density of 0.05-1.0 g/cm<SP>2</SP>. The pictorial having a reflected light of diamond fine particles can be produced on the surface of a pottery by coating the coating obtained by kneading 0.1-0.3 g diamond powder of 10-15 μm with 1.0 g glaze on the surface of an unglazed pottery material and effecting burning at 800-900°C. <P>COPYRIGHT: (C)2003,JPO

Description

Detailed Description of the Invention

[001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention mainly relates to a coating material used for a decorative picture pattern such as a makie and a method for drawing a special decorative picture pattern using this coating material.

[002]

BACKGROUND OF THE INVENTION Various painting patterns are applied to resin-painted and lacquered makeup boxes. Especially, gold powder, silver powder, colored powder, etc. are used for the lacquer work to be applied to these makeup boxes. Is represented.

[003]

[Problems to be Solved by the Invention] In these makies,
If you can draw a picture pattern of fine particles that have a golden luster and reflect like a galaxy nebula, you can achieve a beautiful three-dimensional picture pattern that has never been obtained before. You can significantly increase the artistic added value of your product. However, a means for drawing such a picture pattern has not been known so far. Those using glass bead powder have a dull hue and cannot obtain reflected light with high brightness, so it was not possible to depict the presence and texture of nebulae and plants that shine with a three-dimensional effect.

Therefore, the first object of the present invention is to provide a novel coating material for drawing a decorative picture pattern of fine particles having a clear golden luster.

A second object of the present invention is to provide a method of drawing a decorative pictorial pattern of fine particles having a sharp and three-dimensional golden luster by using the above coating material.

[0096]

[Means for Solving the Problems] The first object is to
It can be achieved by a decorative painting material based on 15 micron diamond powder.

In order to achieve the above-mentioned second object, the method for drawing a picture pattern of the present invention is such that screen printing is performed on a dark-colored coated surface with a two-color reactive ink, and the screen-printed surface is coated with 10-15.
0.05-1.0g of micron diamond powder
It is characterized in that it is applied in a layer thickness of / cm ² and exhibits a nebula-like pictorial pattern with reflected light of diamond fine particles on the coated surface.

In addition, the method for drawing a picture pattern of the present invention is to deposit diamond powder of 10 to 15 microns at a density of 0.05 to 1.0 g / cm ^{2 on} the undried coated surface of the main lacquer,
This can be achieved by displaying a nebula-like pictorial pattern on the lacquer-coated surface with reflected light of diamond fine particles.

Furthermore, the method for drawing a picture pattern of the present invention is the same as that of glaze 1
The coating material prepared by kneading 10 to 15 micron of diamond powder in a ratio of 0.1 to 0.3 g is applied to the surface of the unglazed ceramic material and fired at 800 to 900 ° C. Can be achieved by representing a reflected light-like picture pattern.

[0101]

BEST MODE FOR CARRYING OUT THE INVENTION The coating material of the present invention is mainly composed of diamond powder obtained by powder processing diamond into fine particles of 10 to 15 microns, preferably 13 microns. As the diamond powder of this coating material, the diamond powder used for polishing diamond can be used. Although diamond gemstone itself is a material for ornaments, diamond powder obtained by pulverizing diamond is a mere white powder, a material that does not have the concept of ornaments anymore, and is used exclusively as an abrasive. When the inventor of the present invention applies the above-mentioned diamond powder to a dark-colored surface at a specific density, fine diamond powder particles reflect light to give a three-dimensional effect, and are nebulous with a sharp and unique golden luster. It was discovered that a picture pattern should be represented, and it was established to use this as a material for decorative picture patterns such as makie.

By applying the above diamond powder to a dark color (dark black, navy blue, purple, red, etc.) surface of a cosmetic box or the like, a nebula-like pictorial pattern having golden-reflective gloss is formed on the surface of the cosmetic box. It

A specific example of drawing the above-mentioned picture pattern on the surface of the cosmetic case is shown below. The cosmetic box is made by spraying a dark urethane resin such as dark black, navy blue, purple, red, green, or gray with a spray gun on the surface of a base material made of MDF (glued wood made by finely crushing natural wood). Apply a sandpaper to make the surface uniform, and spray again with urethane resin.

Screen printing of the two-color reactive inks is performed on the surface of this cosmetic box. The screen-printed surface functions as an adhesive, and a diamond powder of 10 to 15 μm, preferably 13 μm is used on the screen-printed surface using a powder cylinder to obtain a density of 0.05 to 1.0 g / cm ² . ,
Preferably, it is sown and attached at a density of 0.2 g / cm ² . As a result, a nebula-like decorative pictorial pattern of fine particles having a diamond-gloss light-glossy gloss is drawn on the surface of the cosmetic box.

Instead of the above screen printing, the above decorative picture pattern can be drawn on the main lacquer coated surface. In this case, apply the main lacquer to the surface of the above-mentioned makeup box, etc., and apply 10 to 15 micron diamond powder at a density of 0.05 to 1.0 g / cm ² when the coated surface is undried, A nebula-like picture pattern with reflected light of diamond particles on the lacquered surface. Preferably, the dried main lacquer coated surface is polished. As a result, the reflected light of the diamond particles becomes even brighter.

The diamond powder, which is an aggregate of diamond fine particles, is a mere white powder to the naked eye. However, according to the present invention, as described above, the diamond luster of the reflected light of diamond is obtained by plating the dark surface with a predetermined density. It was possible to draw a nebula-like decorative picture pattern of fine particles with a tinge.

The sowing density of diamond powder is 0.0
5 to 1.0 g / cm ² (layer thickness 0.3 to 1.0 m
m) range is feasible and the density is 0.2 g / cm
² (0.5 mm in layer thickness) is most preferable. Density 0.
If it is less than 05 / cm ² , it becomes difficult to see, and if the density exceeds 1.0 / cm ² , the surface on which the diamond powder is adhered rises too much and it becomes difficult to finish the surface smoothly.

The above decorative pictorial pattern of the present invention can be printed on the surface of a ceramic such as a plate or a bowl. In this case, 10 to 15 micron (preferably 13 micron) diamond powder is added to 0.1 g per 1 g of glaze.
Knead at a rate of 0.3 g, preferably 0.2 g, apply this to the surface of the unglazed ceramics, and if necessary, further apply a laxative to 800-900 ° C., preferably 85
Bake at a temperature of 0 ° C. As a result, a pattern of fine particles tinged with diamond reflected light is drawn on the surface of the ceramic.

In this case, if the mixing ratio of the diamond powder to the glaze is less than 0.1 g with respect to 1.0 g of the glaze, the reaction is difficult to occur, and if it exceeds 0.3 g, excessive bubbles are generated. Is not preferable. further,
If the firing temperature is lower than 800 ° C., bubbles are generated and peeling easily occurs, and if it exceeds 900 ° C., the dye reaction is hindered, which is not preferable.

The above has described the method of extracting a decorative picture pattern using diamond powder itself. However, since a picture pattern such as a makie is composed of various patterns and shades, when actually drawing a makie, The method is used in combination with the lacquer work technique, which uses Aoki shell, gold leaf, and Akane leaf.

[0204]

[Effect] According to the present invention, since diamond powder is used to draw a picture pattern, a fantastic picture pattern of Kongo reflection gloss which has never been seen can be displayed. In particular, by applying the present invention to the lacquer technique and ceramics of boxes and vessels,
You can draw beautiful pictures that you have never seen before.

Since the diamond powder is a mere white powder and does not have the luster of diamond itself and is used only as an abrasive, the present invention expands the range of use of the diamond powder. A high-value-added picture pattern can be obtained.

─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. ⁷ identification code FI theme code (reference) C09D 7/12 C09D 7/12 (72) Inventor Mariko Ishida 4-18-21 Fyozawa, Setagaya-ku, Tokyo F Term (reference) 4D075 AC19 AC45 AC92 AE04 AE12 AE27 BB28Z BB93Z CB04 CB11 CB18 DA06 DA23 DB14 DB21 DC38 EA02 EB05 EB38 EB56 EC01 EC53 EC54 4J038 EA011 HA026 KA08 NA01

Claims (5)

[Claims] 1. A coating material having a decorative pattern mainly composed of diamond powder of 10 to 15 microns. 2. A method for drawing a decorative picture pattern having an embossed luster, which comprises depositing 10 to 15 micron diamond powder on the coated surface. 3. A dark-coated surface is screen-printed with a two-color reactive ink, and the screen-printed surface is coated with 0.05 to 1.0 g / cm of diamond powder of 10 to 15 microns.
^A method for drawing a decorative picture pattern, characterized in that it is applied at a density of ² and a nebula-like picture pattern that reflects the reflected light of diamond particles on the painted surface is displayed. 4. Diamond powder of 10 to 15 microns is applied to the undried coated surface of the main lacquer in an amount of 0.05 to 1.0 g / cm.
^A method of drawing a decorative picture pattern, characterized in that it is attached at a density of ² and a nebula-like picture pattern is shown on the surface of the lacquer coated with the reflected light of diamond particles. 5. A 10 g to 15 g diamond powder is added to 1.0 g of glaze. 1 to 0.3 g of a kneaded paint is applied to the surface of the unglazed ceramic material and fired at 800 to 900 ° C. to form a pattern on the surface of the ceramic which is tinged with reflected light of diamond fine particles. How to draw decorative picture patterns