JP2003049149A - Solid adhesive composition - Google Patents
Solid adhesive compositionInfo
- Publication number
- JP2003049149A JP2003049149A JP2001234920A JP2001234920A JP2003049149A JP 2003049149 A JP2003049149 A JP 2003049149A JP 2001234920 A JP2001234920 A JP 2001234920A JP 2001234920 A JP2001234920 A JP 2001234920A JP 2003049149 A JP2003049149 A JP 2003049149A
- Authority
- JP
- Japan
- Prior art keywords
- solid adhesive
- adhesive composition
- solid
- solvent
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、低い塗布荷重、す
なわち、軽い押しつけ力でも良好な塗布性能と接着力を
確保できると共に、充分な強度を有し、かつ、長期間、
固形接着剤組成物の塗布部を大気中に放置しても優れた
塗布性能を有する固形接着剤組成物に関する。TECHNICAL FIELD The present invention can secure good coating performance and adhesive strength even with a low coating load, that is, a light pressing force, has sufficient strength, and can be used for a long period of time.
The present invention relates to a solid adhesive composition having excellent coating performance even when the coated part of the solid adhesive composition is left in the atmosphere.
【０００２】[0002]
【従来の技術】一般に、固形接着剤組成物は、少なくと
も接着剤成分と、ゲル化剤と、溶剤とを含有してなるも
のであり、例えば、ステック型固形糊などに用いられて
いる。2. Description of the Related Art Generally, a solid adhesive composition contains at least an adhesive component, a gelling agent and a solvent, and is used, for example, as a stick type solid paste.
【０００３】しかしながら、従来の固形接着剤組成物
は、塗布時の崩れやつぶれ防止のため強度を増大せしめ
た結果、低い塗布荷重で充分な付着量が得られず、結果
として接着力が低下してしまうという課題があった。ま
た、固形接着剤組成物は通常蓋付きの容器に収容された
状態で使用に供されるものであるが、塗布部を蓋を外し
た、いわゆるキャップオフ状態にしておくと、固形接着
剤組成物中に含有される溶剤が蒸発して接着剤成分が乾
燥固化し、塗布しづらくなるなどの課題があった。However, conventional solid adhesive compositions have increased strength to prevent collapse and crushing during coating, and as a result, a sufficient amount of adhesion cannot be obtained with a low coating load, resulting in a decrease in adhesive strength. There was a problem that it would end up. Further, the solid adhesive composition is usually used in a state of being housed in a container with a lid, but when the coating part is removed in a so-called cap-off state, the solid adhesive composition is There is a problem that the solvent contained in the product is evaporated and the adhesive component is dried and solidified, making it difficult to apply.
【０００４】一方、特開昭５３−３８７３７号公報に
は、微結晶セルロース、無定形シリカ微粉末、水酸化ア
ルミニウム、炭酸カルシウム、炭酸マグネシウム、タル
クなどの有機又は無機の微粉末を固形接着剤中に分散せ
しめることにより、充填補強作用を生ぜしめ、とりわけ
脆弱性を改善してなる固形状接着剤の改質方法が知られ
ている。On the other hand, Japanese Patent Laid-Open No. 53-38737 discloses microcrystalline cellulose, amorphous silica fine powder, organic hydroxide or inorganic fine powder such as aluminum hydroxide, calcium carbonate, magnesium carbonate, talc in a solid adhesive. There is known a method for modifying a solid adhesive, which has a filling and reinforcing effect by improving the fragility of the solid adhesive by dispersing it in the solid adhesive.
【０００５】しかしながら、この公報に記載される改質
方法も従来のものと同様、強度が増す代わりに低い塗布
荷重で使用した場合には、充分な付着量が得られず、結
果として糊の基本性能である接着力が低下してしまうと
いう課題があるものである。また、上記公報中には、
「接着力が増す」との記述もあるが、これは高い塗布荷
重の場合についての記述であり、崩れにくくなったため
に塗布量過多とならず、初期の接着力が増したという意
味であり、本発明とは技術思想が相違するものである。
更に、上記公報には、いあわゆるキャップオフ状態にし
た場合の課題、すなわち、使用性、塗布性能の低下等に
ついても何等記載も示唆もされていないものである。However, like the conventional method, the modifying method described in this publication does not increase the strength but, when used at a low coating load, a sufficient amount of adhesion cannot be obtained, and as a result, the basic adhesive The problem is that the adhesive strength, which is the performance, is reduced. Further, in the above publication,
There is also a description that "adhesiveness increases", but this is a description for the case of a high coating load, and it means that the amount of coating was not excessive because it did not collapse easily, and the initial adhesive force increased, The technical idea is different from that of the present invention.
Further, the above publication does not describe or suggest any problems in the case of so-called cap-off state, that is, deterioration of usability, coating performance and the like.
【０００６】[0006]
【発明が解決しようとする課題】本発明は、上記従来技
術の課題等に鑑み、これを解消しようとするものであ
り、低い塗布荷重、すなわち、軽い押しつけ力でも良好
な塗布性能と接着力を確保できると共に、充分な強度を
有し、かつ、長期間、固形接着剤組成物の塗布部を大気
中に放置しても優れた塗布性能を有する固形接着剤組成
物を提供することを目的とする。SUMMARY OF THE INVENTION The present invention has been made in view of the above-mentioned problems of the prior art and is intended to solve the problems. A low coating load, that is, a light pressing force provides good coating performance and adhesive force. An object of the present invention is to provide a solid adhesive composition which can be secured and has sufficient strength, and which has excellent coating performance even when the coated portion of the solid adhesive composition is left in the air for a long period of time. To do.
【０００７】[0007]
【課題を解決するための手段】本発明者らは、上記従来
技術の課題等について鋭意検討を重ねた結果、固形接着
剤組成物中に特定成分を含有せしめることにより、上記
目的の固形接着剤組成物が得られることを見い出し、本
発明を完成するに至ったのである。すなわち、本発明の
固形接着剤組成物は、次の(1)〜(3)に存する。
(1) 少なくとも接着剤成分と、ゲル化剤と、溶剤とを含
有する固形接着剤組成物であって、該組成物中に球形状
の微粒子を含有し、かつ、常温で固体であり、かつ溶剤
に対する溶解度が常温で２０％以下となるワックス類か
ら選ばれる少なくとも１種を含有してなることを特徴と
する固形接着剤組成物。
(2) 少なくとも接着剤成分と、ゲル化剤と、溶剤とを含
有する固形接着剤組成物であって、該組成物中に球形状
の微粒子を含有し、かつ、少なくとも大気中及び／又は
固形接着剤組成物中の水分を取り込んで蒸発抑制膜を形
成する物質を含有してなることを特徴とする固形接着剤
組成物。
(3) 少なくとも接着剤成分と、ゲル化剤と、溶剤とを含
有する固形接着剤組成物であって、該組成物中に球形状
の微粒子を含有し、かつ、常温で固体であり、かつ溶剤
に対する溶解度が常温で２０％以下となるワックス類か
ら選ばれる少なくとも１種と、少なくとも大気中及び／
又は固形接着剤組成物中の水分を取り込んで蒸発抑制膜
を形成する物質とを含有してなることを特徴とする固形
接着剤組成物。
なお、本発明で規定する「球形状の微粒子」における
「球形状」とは、断面形状が円形状、楕円形状をいい、
微粒子の任意の断面の長軸と短軸との比が１．０±０．
２以内のものをいう。Means for Solving the Problems The inventors of the present invention have made extensive studies as to the problems of the above-mentioned prior art, and as a result, by incorporating a specific component in the solid adhesive composition, the solid adhesive of the above object can be obtained. The inventors have found that a composition can be obtained, and completed the present invention. That is, the solid adhesive composition of the present invention resides in the following (1) to (3). (1) A solid adhesive composition containing at least an adhesive component, a gelling agent, and a solvent, containing spherical fine particles in the composition, and solid at room temperature, and A solid adhesive composition comprising at least one wax selected from waxes having a solubility in a solvent of 20% or less at room temperature. (2) A solid adhesive composition containing at least an adhesive component, a gelling agent, and a solvent, wherein the composition contains spherical fine particles, and at least in air and / or solid A solid adhesive composition comprising a substance that takes in water from the adhesive composition to form an evaporation suppression film. (3) A solid adhesive composition containing at least an adhesive component, a gelling agent, and a solvent, containing spherical fine particles in the composition, and solid at room temperature, and At least one selected from waxes having a solubility in a solvent of 20% or less at room temperature and at least in the air and / or
Alternatively, a solid adhesive composition containing a substance that takes in water in the solid adhesive composition to form an evaporation suppression film. The "spherical shape" in the "spherical fine particles" defined in the present invention means that the cross-sectional shape is circular or elliptical,
The ratio of the major axis to the minor axis of any cross section of the fine particles is 1.0 ± 0.
It is within 2.
【０００８】[0008]
【発明の実施の形態】以下に、本発明の実施形態を詳し
く説明する。本発明の固形接着剤組成物は、少なくとも
接着剤成分と、ゲル化剤と、溶剤とを含有する固形接着
剤組成物であって、該組成物中に球形状の微粒子を含有
すると共に、下記〜のいずれかの成分を含有してな
ることを特徴とするものである。
常温で固体であり、かつ溶剤に対する溶解度が常温
で２０％以下となるワックス類から選ばれる少なくとも
１種を含有してなること。
少なくとも大気中及び／又は固形接着剤組成物中の
水分を取り込んで蒸発抑制膜を形成する物質を含有して
なること。
常温で固体であり、かつ溶剤に対する溶解度が常温
で２０％以下となるワックス類から選ばれる少なくとも
１種と、少なくとも大気中及び／又は固形接着剤組成物
中の水分を取り込んで蒸発抑制膜を形成する物質とを含
有してなること。BEST MODE FOR CARRYING OUT THE INVENTION Embodiments of the present invention will be described in detail below. The solid adhesive composition of the present invention is a solid adhesive composition containing at least an adhesive component, a gelling agent, and a solvent, and the spherical adhesive particles are contained in the composition. It is characterized by containing any one of the components (1) to (5). At least one wax selected from waxes which is solid at room temperature and has a solubility in a solvent of 20% or less at room temperature. It contains at least a substance that takes in water in the air and / or solid adhesive composition to form an evaporation suppression film. At least one selected from waxes that are solid at room temperature and have a solubility in a solvent of 20% or less at room temperature, and at least water in the air and / or solid adhesive composition are taken in to form an evaporation suppression film. It contains the substance that does.
【０００９】本発明に用いる接着剤成分としては、従来
より固形接着剤に用いられている接着剤成分を用いるこ
とができ、例えば、平均分子量１万〜３００万のポリビ
ニルピロリドン、ポリビニルアルコール、アクリル酸エ
ステル、メタクリル酸エステル、ポリ酢酸ビニル、ポリ
ビニルブチラール等の合成樹脂、メチルセルロース、エ
チルセルロース等のセルロース類、デンプン、ゼラチ
ン、コーンスターチ等の天然樹脂等が挙げられ、これら
は単独又は２種以上混合して使用することが可能であ
り、その含有量は、固形接着剤組成物全量に対して、５
〜５０重量％、好ましくは、１０〜４０重量％である。As the adhesive component used in the present invention, an adhesive component conventionally used for a solid adhesive can be used. For example, polyvinylpyrrolidone having an average molecular weight of 10,000 to 3,000,000, polyvinyl alcohol, acrylic acid. Examples include synthetic resins such as esters, methacrylic acid esters, polyvinyl acetate and polyvinyl butyral, celluloses such as methyl cellulose and ethyl cellulose, and natural resins such as starch, gelatin and corn starch. These may be used alone or in combination of two or more. It is possible that the content is 5 with respect to the total amount of the solid adhesive composition.
˜50% by weight, preferably 10-40% by weight.
【００１０】また、本発明に用いるゲル化剤としては、
従来より固形接着剤に用いられているゲル化剤を用いる
ことができ、例えば、ソルビット・ベンズアルデヒド縮
合物、キシリット・ベンズアルデヒド縮合物等のベンズ
アルデヒドと４〜６価の脂肪族多価アルコールとの縮合
により得られる縮合物、炭素数８〜３６の脂肪族カルボ
ン酸のアルカリ金属塩又はアンモニウム塩、Ｎ−ラウロ
イル−グルタミン酸−α，γ−ジ−ｎ−ブチルアミド、
デキストリン脂肪酸エステル、脂肪酸アマイド、有機ベ
ントナイト、アルミニウムシリケート、シリカ、ヒドロ
キシセルロース、ヒドロキシプロピルセルロース等のセ
ルロース誘導体等が挙げられ、これらは１種又は２種以
上混合して使用することができる。ゲル化剤の含有量
は、固形接着剤組成物全量に対して、０．１〜１５重量
％、好ましくは、１〜１０重量％である。Further, as the gelling agent used in the present invention,
Gelling agents conventionally used for solid adhesives can be used, for example, by condensation of benzaldehyde such as sorbit benzaldehyde condensate and xylit benzaldehyde condensate with a 4- to 6-valent aliphatic polyhydric alcohol. The resulting condensate, an alkali metal salt or an ammonium salt of an aliphatic carboxylic acid having 8 to 36 carbon atoms, N-lauroyl-glutamic acid-α, γ-di-n-butyramide,
Examples thereof include dextrin fatty acid ester, fatty acid amide, organic bentonite, aluminum silicate, silica, and cellulose derivatives such as hydroxycellulose and hydroxypropylcellulose. These can be used alone or in combination of two or more. The content of the gelling agent is 0.1 to 15% by weight, preferably 1 to 10% by weight, based on the total amount of the solid adhesive composition.
【００１１】本発明に用いる溶剤としては、従来より固
形接着剤に用いられている溶剤を用いることができ、例
えば、エチルアルコ−ル、プロピルアルコ−ル、イソプ
ロピルアルコ−ル等の低級アルコールや、トルエン、キ
シレン等の芳香炭化水素や、メチルエチルケトン、メチ
ルイソブチルケトン等の低級脂肪族ケトンや、酢酸エチ
ル、酢酸ブチル等の低級脂肪酸の低級アルコールエステ
ルや、ヘキサン、ヘプタン等の脂肪酸炭化水素や、シク
ロヘキサン、エチルシクロヘキサン等の脂環族炭化水素
やグリコールのアルキルアルコール、プロピレングリコ
ールモノメチルエーテル等のグリコールエーテル等が挙
げられ、これらは単独又は２種以上混合して使用するこ
とが可能であり、その含有量は、固形接着剤組成物全量
に対して、３０〜９０重量％、好ましくは、４０〜７０
重量％である。また、上記溶剤は水と溶剤の混合物であ
ってもよい。As the solvent used in the present invention, a solvent which has been conventionally used for a solid adhesive can be used. For example, a lower alcohol such as ethyl alcohol, propyl alcohol, isopropyl alcohol, or toluene. , Aromatic hydrocarbons such as xylene, lower aliphatic ketones such as methyl ethyl ketone and methyl isobutyl ketone, lower alcohol esters of lower fatty acids such as ethyl acetate and butyl acetate, fatty acid hydrocarbons such as hexane and heptane, cyclohexane and ethyl Examples thereof include alicyclic hydrocarbons such as cyclohexane, alkyl alcohols of glycols, glycol ethers such as propylene glycol monomethyl ether, and these can be used alone or in combination of two or more, and the content thereof is 30-based on the total amount of the solid adhesive composition 0% by weight, preferably, 40 to 70
% By weight. Further, the solvent may be a mixture of water and the solvent.
【００１２】本発明に用いる球形状の微粒子は、低い塗
布荷重（軽い押しつけ力）でも良好な塗布性能と接着力
を確保させると共に、充分な強度を発揮せしめるために
固形接着剤組成物中に含有せしめるものである。本発明
に用いる樹脂粒子は、球形状の微粒子であれば特に限定
されず、例えば球形状の樹脂微粒子、球形状の無機系微
粒子などが挙げられる。球形状の樹脂微粒子としては、
例えば、球形状となるベンゾグアナミン樹脂、メラミン
樹脂、ベンゾグアナミン・ホルムアルデヒド縮合物、メ
ラミン・ホルムアルデヒド縮合物、アクリル樹脂、アク
リルスチレン樹脂、ベンゾグアナミン・メラミン・ホル
ムアルデヒド縮合物、フェノール樹脂、ユリア樹脂、フ
ラン樹脂、キシレン樹脂などが挙げられる。また、球形
状の無機系微粒子としては、例えば、ガラスビーズ、ア
ルミナなどが挙げられる。これらの球形状の微粒子は、
単独（１種）で又は２種以上の混合物として用いること
ができる。好ましくは、接着性能及び塗布性能の更なる
向上の点から、ベンゾグアナミン・ホルムアルデヒド縮
合物、メラミン・ホルムアルデヒド縮合物、アクリルス
チレン樹脂が望ましい。具体的には、エポスターＭＳ
（ベンゾグアナミン・ホルムアルデヒド縮合物）、エポ
スターＳ１２（メラミン・ホルムアルデヒド縮合物）、
エポスターＭ３０（ベンゾグアナミン・メラミン・ホル
ムアルデヒド縮合物）〔以上、日本触媒社製〕が好適に
用いることができる。The spherical fine particles used in the present invention are contained in the solid adhesive composition in order to secure good coating performance and adhesive strength even under a low coating load (light pressing force) and to exert sufficient strength. It is the one to be confused. The resin particles used in the present invention are not particularly limited as long as they are spherical fine particles, and examples thereof include spherical resin fine particles and spherical inorganic fine particles. As the spherical resin particles,
For example, spherical benzoguanamine resin, melamine resin, benzoguanamine / formaldehyde condensate, melamine / formaldehyde condensate, acrylic resin, acrylic styrene resin, benzoguanamine / melamine / formaldehyde condensate, phenol resin, urea resin, furan resin, xylene resin And so on. Examples of spherical inorganic fine particles include glass beads and alumina. These spherical particles are
They can be used alone (1 type) or as a mixture of 2 or more types. Preferably, benzoguanamine / formaldehyde condensate, melamine / formaldehyde condensate, and acrylic styrene resin are desirable from the viewpoint of further improving the adhesive performance and coating performance. Specifically, Eposter MS
(Benzoguanamine-formaldehyde condensate), Eposter S12 (melamine-formaldehyde condensate),
Eposter M30 (benzoguanamine / melamine / formaldehyde condensate) [above, manufactured by Nippon Shokubai Co., Ltd.] can be preferably used.
【００１３】本発明に用いる球形状の微粒子は、好まし
くは、平均粒子径が０．３〜３０μｍ、更に好ましく
は、０．５〜２０μｍとなるものが望ましい。球形状の
微粒子の平均粒子径が０．３μｍ未満では、球形状によ
り特徴づけられる効果よりも、その他の電荷や表面積に
よる効果の方が影響を受けてしまい、本発明の効果を発
現することが低くなり、また、平均粒子径が３０μｍを
越えると、均一に塗布するのが困難となる傾向が高くな
り、好ましくない。更に、この球形状の微粒子の含有量
は、固形接着剤組成物全量に対して、０．１〜１５重量
％、好ましくは、０．５〜１０重量％とすることが望ま
しい。この球形状微粒子の含有量が、０．１重量％未満
では、微粒子の添加効果が充分得られず、また、１５重
量％を越える量では、接着性が低下し、好ましくない。The spherical fine particles used in the present invention preferably have an average particle size of 0.3 to 30 μm, more preferably 0.5 to 20 μm. When the average particle size of the spherical fine particles is less than 0.3 μm, the effects due to other charges and surface area are more affected than the effects characterized by the spherical shape, and the effects of the present invention can be exhibited. When the average particle size is more than 30 μm, it tends to be difficult to apply the solution uniformly, which is not preferable. Further, the content of the spherical fine particles is 0.1 to 15% by weight, preferably 0.5 to 10% by weight, based on the total amount of the solid adhesive composition. If the content of the spherical fine particles is less than 0.1% by weight, the effect of adding the fine particles cannot be sufficiently obtained, and if it exceeds 15% by weight, the adhesiveness is deteriorated, which is not preferable.
【００１４】本発明において、上記及びの形態に用
いるワックス類は、常温（２５℃、以下同様）で固体で
あり、かつ溶剤に対する溶解度が常温で２０％以下、好
ましくは、１０％以下、更に好ましくは、５％以下とな
るものであり、これらの下限値は０％を含むものである
が、好ましくは、０．１％以上、更に好ましくは、１％
以上であることが望ましい。この溶解度特性となるワッ
クス類としては、例えば、パラフィンワックス、オレフ
ィンワックス、マイクロクリスタリンワックス、ペトロ
ラクタム、動物ワックス、植物ワックス、鉱物ワック
ス、ポリエチレンワックス、フィッシャー・トロプシュ
ワックスなどのワックス類が挙げられ、これらは１種又
は２種以上混合して使用することができる。ワックス類
が常温で液体のもの、または、溶剤に対する溶解度が常
温で２０％を越えるものでは、溶解、拡散作用によって
溶剤中に溶出してしまい、長期間の保存により効果が低
下したり、固形接着剤を使用するにしたがって効果が無
くなり、本発明の効果を達成できるものではない。な
お、上記溶剤に対する溶解度が２０％以下とは、ワック
ス類が本発明に使用する溶剤に対して、その溶解度が常
温で２０％以下であることを意味するものである。上記
溶解度となるワックス類は、本発明の更なる効果を達成
するために、融点（ｍｐ）が３５〜７５℃であることが
望ましい。上記の形態におけるワックス類の含有量
は、固形接着剤全量に対して、０．１〜１５重量％、好
ましくは、１．０〜１０重量％である。ワックス類の含
有量が０．１重量％未満であると、本発明の効果を発揮
することができず、また、１５重量％を越えると、接着
性が低下し、凝集破壊が起こり、好ましくない。In the present invention, the waxes used in the above and above embodiments are solid at room temperature (25 ° C., the same below) and have a solubility in a solvent at room temperature of 20% or less, preferably 10% or less, and more preferably. Is 5% or less, and these lower limit values include 0%, but are preferably 0.1% or more, and more preferably 1%.
The above is desirable. Examples of the waxes having the solubility characteristics include waxes such as paraffin wax, olefin wax, microcrystalline wax, petrolactam, animal wax, vegetable wax, mineral wax, polyethylene wax, and Fischer-Tropsch wax. Can be used alone or in combination of two or more. If the waxes are liquid at room temperature, or if their solubility in the solvent exceeds 20% at room temperature, they will dissolve in the solvent due to the dissolution and diffusion action, and the effect will be reduced by long-term storage, or solid adhesion will occur. The effect disappears as the agent is used, and the effect of the present invention cannot be achieved. The solubility in the solvent of 20% or less means that the solubility of the waxes in the solvent used in the present invention is 20% or less at room temperature. The waxes having the above-mentioned solubility preferably have a melting point (mp) of 35 to 75 ° C in order to achieve the further effect of the present invention. The content of waxes in the above-mentioned form is 0.1 to 15% by weight, preferably 1.0 to 10% by weight, based on the total amount of the solid adhesive. If the content of the waxes is less than 0.1% by weight, the effect of the present invention cannot be exhibited, and if it exceeds 15% by weight, the adhesiveness decreases and cohesive failure occurs, which is not preferable. .
【００１５】上記及びの形態に用いる少なくとも大
気中及び／又は固形接着剤中の水分を取り込んで蒸発抑
制膜を形成する物質としては、例えば、ポリオキシエチ
レンステアリルリン酸エステルなどのアルキルリン酸エ
ステル、ポリオキシエチレンソルビタンモノステアレー
ト、ポリオキシエチレンソルビタントリステアレートな
どのポリオキシエチレンソルビタン脂肪酸エステル、ポ
リオキシエチレンソルビットヘキサステアレートなどの
ポリオキシエチレンソルビット脂肪酸エステル、ペンタ
エリスリトールモノステアレート、ペンタエリスリトー
ルジステアレートなどのペンタエリスリトール誘導体、
高級アルコール脂肪酸エステル、レシチン、ショ糖エス
テル、アスコルビン酸ステアレート、ソルビタン酸ステ
アレートなどから選択される１種又は２種以上の混合物
が挙げられる。好ましくは、膜の形成のしやすさ、膜形
成時間の速さ等の点から、常温で固体であり、かつ溶剤
に対する溶解度が１０％以下となるものが望ましい。上
記の形態における蒸発抑制膜を形成する物質の含有量
は、固形接着剤全量に対して、０．０１〜１０重量％、
好ましくは、０．０３〜５重量％である。この蒸発抑制
膜を形成する物質の含有量が０．０１重量％未満である
と、本発明の効果を発揮することができず、また、１０
重量％を越えると、 接着性が低下し、凝集破壊が起こ
り、好ましくない。Examples of the substance used in the above and above embodiments to take in water in at least the air and / or the solid adhesive to form the evaporation suppression film include, for example, alkyl phosphates such as polyoxyethylene stearyl phosphate, Polyoxyethylene sorbitan monostearate, polyoxyethylene sorbitan tristearate and other polyoxyethylene sorbitan fatty acid esters, polyoxyethylene sorbit hexastearate and other polyoxyethylene sorbit fatty acid esters, pentaerythritol monostearate, pentaerythritol disteare Pentaerythritol derivatives such as rate,
One or a mixture of two or more selected from higher alcohol fatty acid ester, lecithin, sucrose ester, ascorbic acid stearate, sorbitan acid stearate and the like can be mentioned. From the viewpoints of ease of film formation, speed of film formation time, etc., it is preferable that the substance be solid at room temperature and have a solubility in a solvent of 10% or less. The content of the substance forming the evaporation suppression film in the above-mentioned embodiment is 0.01 to 10% by weight based on the total amount of the solid adhesive,
It is preferably 0.03 to 5% by weight. If the content of the substance forming the evaporation suppressing film is less than 0.01% by weight, the effect of the present invention cannot be exhibited, and 10
If it exceeds the weight%, the adhesiveness is lowered and cohesive failure occurs, which is not preferable.
【００１６】上記の固形接着剤の形態では、固形接着
剤中に常温で固体であり、かつ溶剤に対する溶解度が常
温で２０％以下となるパラフィンワックス、オレフィン
ワックスのワックス類から選ばれる少なくとも１種と、
少なくとも大気中及び／又は固形接着剤中の水分を取り
込んで蒸発抑制膜を形成する物質との二成分を併用する
ことにより、上記及びの形態の別々に含有せしめた
場合に較べて、更に長時間、優れた塗布性能を有する固
形接着剤とすることができる。このの固形接着剤の形
態におけるワックス類（Ａ）と少なくとも大気中及び／
又は固形接着剤中の水分を取り込んで蒸発抑制膜を形成
する物質（Ｂ）の含有比〔（Ａ）／（Ｂ）〕は、重量比
で１／１〜１００／１、好ましくは、２／１〜５０／１
であり、かつ、これらの合計含有量が０．１〜１０重量
％、好ましくは、１〜５重量％とすることが望ましい。
なお、ワックス類（Ａ）と上記蒸発抑制膜を形成する物
質（Ｂ）の含有比〔（Ａ）／（Ｂ）〕が、重量比で１／
１〜１００／１又はこれらの合計含有量が０．１〜１０
重量％の範囲外となると、二成分併用の更なる効果は発
揮できないものとなる。In the form of the above solid adhesive, at least one selected from paraffin wax and olefin wax which are solid in the solid adhesive at room temperature and have a solubility in a solvent of 20% or less at room temperature. ,
By using at least two components in combination with a substance that takes in moisture in the air and / or solid adhesive to form an evaporation suppression film, compared to the case of separately containing the above and the above forms, a longer time is required. A solid adhesive having excellent coating performance can be obtained. With the wax (A) in the form of this solid adhesive, at least in the atmosphere and / or
Alternatively, the content ratio [(A) / (B)] of the substance (B) that takes in water in the solid adhesive to form the evaporation suppression film is 1/1 to 100/1, preferably 2 / 1-50 / 1
It is desirable that the total content of these is 0.1 to 10% by weight, and preferably 1 to 5% by weight.
The content ratio [(A) / (B)] of the waxes (A) and the substance (B) forming the evaporation suppression film is 1 / by weight.
1-100 / 1 or their total content is 0.1-10
If it is out of the range of the weight%, the further effect of the combined use of two components cannot be exhibited.
【００１７】更に、本発明では、固形接着剤組成物用添
加剤として、従来より固形接着剤に用いられている種々
の添加剤、例えば、水、着色剤、香料、防黴剤、滑剤、
可塑剤、湿潤剤（保湿剤）、増量剤、防腐剤などを含有
せしめることができる。更に発色性色素（紙等に当該固
形のりを塗布した時に塗布色が青、緑、赤色などであ
り、塗布後固形接着剤が乾燥した時には無色となる色
素）などを含有せしめることができる。Furthermore, in the present invention, various additives conventionally used in solid adhesives as additives for solid adhesive compositions, such as water, colorants, fragrances, antifungal agents, lubricants,
A plasticizer, a humectant (humectant), a bulking agent, a preservative and the like can be contained. Further, a color-forming dye (a dye whose coating color is blue, green, red or the like when the solid paste is applied to paper or the like, and which becomes colorless when the solid adhesive is dried after application) can be added.
【００１８】本発明に用いる固形接着剤組成物は、上述
の接着剤成分と、ゲル化剤と、溶剤と、上述の球形状の
微粒子と、上述の各種のワックス類及び／又は上述の各
種の蒸発抑制膜を形成する物質とを常法により撹拌混合
して放冷等し固形化することにより製造することができ
る。The solid adhesive composition used in the present invention comprises the above-mentioned adhesive component, the gelling agent, the solvent, the above-mentioned spherical fine particles, the above-mentioned various waxes and / or the above-mentioned various kinds of waxes. It can be produced by stirring and mixing with a substance forming an evaporation suppression film by a conventional method, allowing to cool and solidifying.
【００１９】本発明における上記構成となる固形接着剤
組成物は、例えば、図１（ａ）及び（ｂ）に示す、繰り
出し容器Ａに収容されて使用に供することができる。こ
の繰り出し容器Ａは、固形接着剤組成物Ｘを収容する容
器本体１０と、該容器本体１０の底部に設けられる回動
部２０と、該回動部２０に連結されると共に、容器本体
１０内に突設する外表面に螺合部３０ａを有する棒状の
螺合軸体３０と、上記容器本体１０内に遊嵌されると共
に、該螺合部３０ａを有する螺合軸体３０に螺合する固
形接着剤組成物Ｘを保持する保持体４０と、容器本体１
０の開口部１０ａを嵌合により施蓋するキャップ体５０
とを備えたものである。この繰り出し容器Ａでは、容器
本体１０の底部に取り付けられた回動部２０を回転する
ことにより、容器本体１０内の中央部に突設することと
なる螺合部３０ａを有する螺合軸体３０に螺合された固
形接着剤組成物Ｘを保持する保持体４０を上下にスライ
ドさせて固形接着剤組成物Ｘを出没自在に繰り出すこと
ができるものである。なお、この形態では、固形接着剤
組成物を収容する繰り出し容器Ａ及び固形接着剤組成物
Ｘを、共に横断面形状を四角形形状から構成したが、繰
り出し容器Ａ及び固形接着剤組成物Ｘの横断面形状を周
知の円形形状（斜視態様では円柱形状）や、三角形状、
五角形形状や六角形形状等の方形状に設計変更等して、
この各形状の固形接着剤組成物を出没自在に繰り出して
使用しても良いものである。また、容器本体１０及びキ
ャップ５０を視認性を有する透明体又は半透明体により
構成すれば、固形接着剤組成物の消費状態が容易に判る
こととなる。The solid adhesive composition having the above-mentioned constitution according to the present invention can be put into a feeding container A shown in FIGS. 1 (a) and 1 (b) for use. The delivery container A is connected to the container body 10 for containing the solid adhesive composition X, a rotating portion 20 provided at the bottom of the container body 10, the rotating portion 20, and the inside of the container body 10. A rod-shaped screwing shaft body 30 having a screwing portion 30a on the outer surface protruding from the container is loosely fitted in the container body 10 and is screwed to the screwing shaft body 30 having the screwing portion 30a. Holder 40 for holding the solid adhesive composition X, and the container body 1
A cap body 50 for covering the 0 opening 10a by fitting
It is equipped with and. In this feeding container A, a screw shaft body 30 having a screwing portion 30a that is projected at the center of the container body 10 by rotating the rotating portion 20 attached to the bottom of the container body 10. The holding body 40 holding the solid adhesive composition X screwed in the above can be slid up and down, and the solid adhesive composition X can be drawn out freely. In this embodiment, the feeding container A containing the solid adhesive composition and the solid adhesive composition X both have a quadrangular cross section, but the feeding container A and the solid adhesive composition X traverse. Well-known circular shape (cylindrical shape in perspective mode), triangular shape,
Change the design to a square shape such as pentagonal shape or hexagonal shape,
The solid adhesive composition of each shape may be drawn out and used freely. Further, if the container body 10 and the cap 50 are made of a transparent or translucent body having visibility, the consumption state of the solid adhesive composition can be easily understood.
【００２０】本発明の固形接着剤組成物では、上述の如
く、少なくとも接着剤成分と、ゲル化剤と、溶剤とを含
有し、かつ、該固形接着剤組成物中に、上述の球形状の
微粒子と、上記〜のいずれかの成分を含有せしめる
ことにより、低い塗布荷重、すなわち、軽い押しつけ力
でも良好な塗布性能と接着力を確保できると共に、充分
な強度を有し、かつ、長期間、固形接着剤組成物の塗布
部を大気中に放置しても優れた塗布性能を発揮せしめる
ことができるものとなる。すなわち、本発明では、球形
状の微粒子を固形接着剤組成物中に含有せしめることに
より、塗布を行った際、糊の摩耗とスベリとのバランス
が丁度よくなり、低い塗布荷重（軽い押しつけ力）でも
良好な塗布性能と接着力を確保することができると共
に、充分な強度及び優れた塗布性能を発揮せしめること
となる。As described above, the solid adhesive composition of the present invention contains at least an adhesive component, a gelling agent and a solvent, and the solid adhesive composition has the above-mentioned spherical shape. By containing fine particles and any of the above components, a low coating load, that is, good coating performance and adhesive strength can be secured even with a light pressing force, and with sufficient strength, and for a long period of time, Even if the coated part of the solid adhesive composition is left in the atmosphere, excellent coating performance can be exhibited. That is, in the present invention, by including the spherical fine particles in the solid adhesive composition, when the application is performed, the balance between the abrasion of the paste and the slip is just good, and the low application load (light pressing force) However, good coating performance and adhesive strength can be secured, and sufficient strength and excellent coating performance can be exhibited.
【００２１】更に、本発明では、長時間、大気中に固形
接着剤の塗布部（上面部）等を外気と接触していても、
すなわち、キャップオフ状態にしておいても、固形接着
剤組成物中に、上記〜のいずれかの成分が含有され
ることにより、優れた経時安定性と共に、優れた塗布性
能を発揮することとなる。この作用機構は、上記〜
の固形接着剤の形態によって、若干その機能が異なるも
のである。すなわち、上記における、少なくとも接着
剤成分と、ゲル化剤と、溶剤と上述の球形状の微粒子と
を含有すると共に、上記各種の溶解度特性となるワック
ス類を含有せしめた固形接着剤組成物を用いた場合で
は、該固形接着剤組成物の塗布部を万一キャップオフ状
態にしておいても、固形接着剤組成物中に含有したワッ
クス類が乾燥して塗布部に非常に脆い被膜（蒸発抑制
膜）が形成されることとなり、この被膜により固形接着
剤組成物中に含まれる揮発成分となる溶剤などの蒸発が
防止され、また、該被膜は塗布時の塗布圧によって破
れ、塗布が可能となるものであり、しかも、該被膜の形
成は上記塗布量により若干相違もあるが、固形接着剤組
成物中に含有されるワックス類が再度必要量だけ塗布部
にあるので、次に塗布部が大気中等にさらされたとき、
乾燥により塗布部表面に新たな被膜を形成し、この被膜
形成→塗布→被膜形成→塗布……は何回も繰り返し効果
を示すものである。これにより、塗布部の表面には蒸発
抑制膜が常時再生し、塗布時に破れる再生被膜が形成さ
れることとなるので、長時間、大気中に固形接着剤の塗
布部をキャップオフ状態にしておいても、塗布部表面は
乾燥固化し難くなり、優れた塗布性能を有することとな
る。Further, in the present invention, even if the application portion (top surface portion) of the solid adhesive is kept in contact with the outside air in the air for a long time,
That is, even in the cap-off state, the solid adhesive composition contains any one of the above components (1) to (3), thereby exhibiting excellent temporal stability and excellent coating performance. . This action mechanism is
The function is slightly different depending on the form of the solid adhesive. That is, in the above, a solid adhesive composition containing at least an adhesive component, a gelling agent, a solvent and the above-mentioned spherical fine particles and containing waxes having various solubility characteristics is used. In such a case, even if the coated portion of the solid adhesive composition is capped off, the waxes contained in the solid adhesive composition will dry and the coating portion will be very brittle (evaporation suppression). Since a film is formed, this film prevents evaporation of a solvent that is a volatile component contained in the solid adhesive composition, and the film is broken by the application pressure during application and can be applied. Moreover, the formation of the coating film may be slightly different depending on the coating amount, but since the waxes contained in the solid adhesive composition are present again in the required amount in the coating portion, In the atmosphere When it is, et al.,
A new coating is formed on the surface of the coated part by drying, and this coating formation->coating->coating-formation-> coating shows repeated effects many times. As a result, the evaporation suppression film is constantly regenerated on the surface of the application part, and a regenerated film that breaks during application is formed.Therefore, the application part of the solid adhesive is capped off in the air for a long time. Even so, the surface of the coated portion is less likely to dry and solidify, and the coating has excellent coating performance.
【００２２】上記における、少なくとも接着剤成分
と、ゲル化剤と、溶剤と上述の球形状の微粒子とを含有
すると共に、蒸発抑制膜を形成する物質を含有せしめた
固形接着剤組成物を用いた場合では、該固形接着剤組成
物の塗布部を万一キャップオフ状態にしておいても、固
形接着剤組成物中に含有した蒸発抑制膜を形成する物質
が大気中及び／又は固形接着剤組成物中の水分を取り込
むことにより、具体的には、固形接着剤組成物表面から
溶剤等が蒸発するが、蒸発に際し、熱が奪われ表面の温
度が下がると同時に大気中の水分及び／又は溶剤との親
和性の高い雰囲気中の水分が固形接着剤組成物に溶け込
み、表面付近の組成変化に伴い塗布部（表面）に非常に
脆い被膜〔液晶表面膜（蒸発抑制膜）が形成されること
となり、この被膜により固形接着剤組成物中に含まれる
揮発成分となる溶剤などの蒸発が防止され、また、該被
膜は塗布時の塗布圧によって破れ、塗布が可能となるも
のであり、しかも、該被膜の形成は上記塗布量により若
干相違もあるが、固形接着剤組成物中に含有される蒸発
抑制膜を形成する物質が再度必要量だけ塗布部にあるの
で、次に塗布部が大気中等にさらされたとき、上記と同
様に大気中及び／又は固形接着剤組成物中の水分を取り
込んで塗布部表面に新たな被膜を形成し、この被膜形成
→塗布→被膜形成→塗布……は何回も繰り返し効果を示
すものである。これにより、塗布部の表面には蒸発抑制
膜が常時再生し、塗布時に破れる再生被膜が形成される
こととなるので、長時間、大気中に固形接着剤組成物の
塗布部をキャップオフ状態にしておいても、塗布部表面
は乾燥固化し難くなり、優れた塗布性能を有することと
なる。なお、固形接着剤組成物中に水分を含有している
場合は、湿度が低い場合にも効果を示すものであるが、
多すぎると乾燥性の低下などの理由により接着性の低下
を引き起こすこととなる。A solid adhesive composition containing at least an adhesive component, a gelling agent, a solvent, and the above-mentioned spherical fine particles, and a substance forming an evaporation suppressing film is used. In this case, even if the application part of the solid adhesive composition is capped off, the substance contained in the solid adhesive composition which forms the evaporation suppressing film is in the air and / or the solid adhesive composition. By taking in the moisture in the substance, specifically, the solvent or the like is evaporated from the surface of the solid adhesive composition, but at the time of evaporation, heat is taken away and the temperature of the surface is lowered, and at the same time moisture and / or solvent in the atmosphere. Moisture in an atmosphere with a high affinity for is dissolved in the solid adhesive composition, and a very brittle film [liquid crystal surface film (evaporation suppression film) is formed on the applied part (surface) as the composition changes near the surface. And this coating Evaporation of a solvent which is a volatile component contained in the solid adhesive composition is prevented, and the coating is broken by the coating pressure at the time of coating and can be coated, and the coating is not formed. Although there is a slight difference depending on the coating amount, the amount of the substance forming the evaporation suppression film contained in the solid adhesive composition is again in the coating part in the required amount, so that the next time the coating part is exposed to the atmosphere, etc. In the same manner as above, the moisture in the air and / or the solid adhesive composition is taken in to form a new film on the surface of the applied part, and this film formation → application → film formation → application ... is repeated many times. Is shown. As a result, the evaporation suppression film is constantly regenerated on the surface of the application part, and a regenerated film that breaks during application is formed, so the application part of the solid adhesive composition is capped off in the air for a long time. Even in such a case, the surface of the coated portion is hard to dry and solidify, and the coating has excellent coating performance. When the solid adhesive composition contains water, it is effective even when the humidity is low,
If the amount is too large, the adhesiveness may be lowered due to a decrease in drying property.
【００２３】更に上記における、少なくとも接着剤成
分と、ゲル化剤と、溶剤と上述の球形状の微粒子とを含
有すると共に、上記特性の各種ワックス類及び上記各種
の蒸発抑制膜を形成する物質を含有せしめた固形接着剤
組成物を用いた場合では、該固形接着剤組成物の塗布部
を万一キャップオフ状態にしておいても、固形接着剤組
成物中に含有したワックス類が乾燥することにより、か
つ、蒸発抑制膜を形成する物質が大気中及び／又は固形
接着剤組成物中の水分を取り込むことにより、塗布部に
非常に脆い複合被膜（蒸発抑制複合膜）が形成されるこ
ととなる。この複合被膜の形成態様は、i)ワックス類単
独の膜は若干不完全であり、該膜には微細な孔があるも
のと考えられ、この微細な孔に蒸発抑制物質が孔を埋め
る（膜形成する）ことにより形成されるか、または、i
i)ワックス類と類似構造をもつ蒸発抑制物質の配合によ
り（該蒸発抑制物質が流動性降下作用を有する物質とし
て作用することにより）、膜の結晶構造が微細（緻密）
になることにより形成されるかによるものと推察され
る。この複合被膜により固形接着剤組成物中に含まれる
揮発成分となる溶剤などの蒸発が上記及びの形態の
固形接着剤組成物に較べて、更に防止され、また、該複
合被膜は塗布時の塗布圧によって破れ、塗布が可能とな
るものであり、しかも、該複合被膜の形成は上記塗布量
により若干相違もあるが、固形接着剤組成物中に含有さ
れるワックス類及び蒸発抑制膜を形成する物質が再度必
要量だけ塗布部にあるので、次に塗布部が大気中等にさ
らされたとき、塗布部表面に新たな複合被膜を形成し、
この複合被膜形成→塗布→複合被膜形成→塗布……は何
回も繰り返し効果を示すものである。これにより、塗布
部の表面には蒸発抑制膜が常時再生し、塗布時に破れる
再生被膜が形成されることとなるので、長時間、大気中
に固形接着剤組成物の塗布部をキャップオフ状態にして
おいても、塗布部表面は乾燥固化し難くなり、更に優れ
た塗布性能を有することとなる。Further, the above-mentioned substances containing at least an adhesive component, a gelling agent, a solvent and the above-mentioned spherical fine particles, and various waxes having the above-mentioned characteristics and various evaporation-preventing films are formed. When the solid adhesive composition contained is used, the waxes contained in the solid adhesive composition should be dried even if the coated portion of the solid adhesive composition is capped off. In addition, the substance forming the evaporation suppression film takes in water in the air and / or the solid adhesive composition to form a very brittle composite film (evaporation suppression composite film) in the coating part. Become. In the formation mode of this composite film, i) the film of waxes alone is slightly incomplete, and it is considered that the film has fine pores, and the evaporation suppressing substance fills the pores in these fine pores (film. Formed) or i
i) The crystal structure of the film is fine (dense) by blending an evaporation inhibitor having a similar structure to waxes (because the evaporation inhibitor acts as a substance having a fluidity lowering effect).
It is presumed that it depends on whether or not it is formed. This composite coating further prevents evaporation of a solvent or the like which is a volatile component contained in the solid adhesive composition, as compared with the solid adhesive compositions of the above-mentioned and forms, and the composite coating is applied at the time of application. It is torn by pressure and can be applied, and the formation of the composite coating film forms the waxes and the evaporation suppression film contained in the solid adhesive composition, although there are some differences depending on the coating amount. Since the required amount of the substance is again in the coating part, the next time the coating part is exposed to the atmosphere or the like, a new composite film is formed on the surface of the coating part,
This composite film formation → application → composite film formation → application ... shows the effect repeatedly. As a result, the evaporation suppression film is constantly regenerated on the surface of the application part, and a regenerated film that breaks during application is formed, so the application part of the solid adhesive composition is capped off in the air for a long time. Even in this case, the surface of the coated part is hard to be dried and solidified, and the coating performance is further excellent.
【００２４】このように構成される本発明の固形接着剤
組成物では、少なくとも接着剤成分と、ゲル化剤と、溶
剤とを含有する固形接着剤組成物であって、該組成物中
に球形状の微粒子を含有すると共に、上記〜のいず
れかの成分を含有することにより、上述の如く、低い塗
布荷重、すなわち、軽い押しつけ力でも良好な塗布性能
と接着力を確保できると共に、充分な強度を有し、か
つ、長期間、固形接着剤組成物の塗布部を大気中に放置
しても優れた塗布性能を実現するものとなる。The solid adhesive composition of the present invention thus constituted is a solid adhesive composition containing at least an adhesive component, a gelling agent, and a solvent, and the composition contains balls. In addition to containing fine particles in a shape, by containing any of the above components, as described above, a low coating load, that is, good pressing performance and adhesive strength can be secured even with a light pressing force, and sufficient strength can be obtained. In addition, even if the coated portion of the solid adhesive composition is left in the atmosphere for a long period of time, excellent coating performance can be realized.
【００２５】本発明の固形接着剤組成物は、上述のよう
に構成されるものであるが、上記実施形態に限定される
ものでなく、本発明の技術思想の範囲内で、種々変更等
して実施することができるものである。例えば、固形接
着剤組成物の用途としては、例えば、事務用固形接着
剤、靴下止め用固形接着剤等の用途に応じて前記接着剤
成分、ゲル化剤及び溶剤の種類、配合組成等を適宜変更
して使用することができる。The solid adhesive composition of the present invention is constructed as described above, but is not limited to the above-mentioned embodiment, and various modifications may be made within the scope of the technical idea of the present invention. Can be carried out. For example, as the application of the solid adhesive composition, for example, the adhesive component, the type of gelling agent and the solvent, the compounding composition, etc. are appropriately selected depending on the application of the solid adhesive for office work, the solid adhesive for socks, etc. Can be changed and used.
【００２６】[0026]
【実施例】次に、本発明を実施例及び比較例に基づき更
に詳細に説明するが、本発明は下記実施例に限定される
ものではない。EXAMPLES Next, the present invention will be described in more detail based on Examples and Comparative Examples, but the present invention is not limited to the following Examples.
【００２７】〔実施例１〜７及び比較例１〜５〕下記表
１に示す組成となる各成分を１２０℃で撹拌混合して固
形接着剤組成物を作製した。また、パラフィンワックス
の溶剤（プロピレングリコールモノメチルエーテル）に
対する溶解度は常温で１％以下となり、ヘキサグリセリ
ルトリステアレートは約２％以下となるものであった。
なお、実施例及び比較例で配合するグリセリンは、湿潤
剤としての機能及びＰＶＰの可塑剤としての機能を有す
る。得られた各固形接着剤組成物について、下記評価法
により、付着力、接着力、崩れ荷重及びキャップオフ性
について評価を行った。これらの結果を下記表１に示
す。[Examples 1 to 7 and Comparative Examples 1 to 5] Each component having the composition shown in Table 1 below was stirred and mixed at 120 ° C. to prepare a solid adhesive composition. Further, the solubility of paraffin wax in a solvent (propylene glycol monomethyl ether) was 1% or less at room temperature, and hexaglyceryl tristearate was about 2% or less.
The glycerin blended in Examples and Comparative Examples has a function as a wetting agent and a function as a plasticizer for PVP. With respect to each of the obtained solid adhesive compositions, the adhesive force, the adhesive force, the collapse load and the cap-off property were evaluated by the following evaluation methods. The results are shown in Table 1 below.
【００２８】〔付着力の評価法〕直径１５ｍｍ、高さ５
０ｍｍの円柱状に成形した固形接着剤（糊）を保持容器
で支持後、所定の試験紙に対し垂直荷重５００ｇｆにて
長さ１０ｃｍ塗布し、下記評価基準で付着力を評価し
た。
○：５ｇ／ｍ2以上の付着量。
△：２ｇ／ｍ2以上５ｇ／ｍ2未満の付着量。
×：２ｇ／ｍ2未満の付着量。[Evaluation Method of Adhesion] Diameter 15 mm, Height 5
After supporting a solid adhesive (glue) formed in a cylindrical shape of 0 mm with a holding container, a predetermined test paper was applied with a vertical load of 500 gf for a length of 10 cm, and the adhesive force was evaluated according to the following evaluation criteria. ◯: Adhesion amount of 5 g / m 2 or more. Δ: Adhesion amount of 2 g / m 2 or more and less than 5 g / m 2 . X: Adhesion amount less than 2 g / m 2 .
【００２９】〔付着力の評価法〕直径１５ｍｍ、高さ５
０ｍｍの円柱状に成形した固形接着剤（糊）を保持容器
で支持後、所定の試験紙に対し糊を塗布後、直ちに同じ
紙質の試験紙を載せ、荷重５００ｇｆのローラーで圧着
した。次いで、２５℃で１時間乾燥した後、接着せしめ
た紙の剥離状態を下記評価基準で評価した。
○：紙破壊。
△：一部紙破壊。
×：紙破壊せず。[Adhesive Evaluation Method] Diameter 15 mm, Height 5
After supporting a solid adhesive (glue) formed in a cylindrical shape of 0 mm in a holding container, the glue was applied to a predetermined test paper, immediately after which a test paper of the same paper quality was placed and pressure-bonded with a roller having a load of 500 gf. Then, after drying at 25 ° C. for 1 hour, the peeled state of the adhered paper was evaluated according to the following evaluation criteria. ○: Paper destruction. Δ: Some paper was destroyed. X: Paper is not destroyed.
【００３０】〔崩れ荷重の評価法〕直径１５ｍｍ、高さ
５０ｍｍの円柱状に成形した固形接着剤（糊）の上面を
直径３０ｍｍの平板にてゆっくりと押してゆき、糊が破
壊するに要した荷重を下記評価基準で評価した。
○：２ｋｇｆ／ｃｍ2以上。
△：１ｋｇｆ／ｃｍ2以上２ｋｇｆ／ｃｍ2未満。
×：１ｋｇｆ／ｃｍ2未満。[Evaluation Method of Collapse Load] The upper surface of a solid adhesive (glue) molded into a column shape having a diameter of 15 mm and a height of 50 mm is slowly pushed by a flat plate having a diameter of 30 mm, and the load required for the glue to break. Was evaluated according to the following evaluation criteria. ◯: 2 kgf / cm 2 or more. Δ: 1 kgf / cm 2 or more and less than 2 kgf / cm 2 . X: less than 1 kgf / cm 2 .
【００３１】〔キャップオフ性の評価法〕直径１５ｍ
ｍ、高さ５０ｍｍの円柱状に成形した固形接着剤（糊）
の表面を２５℃／湿度６５％環境下において表面が乾燥
して塗布できない状態になるまで要した時間を下記評価
基準により評価した。
評価基準：
◎：１２０時間以上。
○：２４時間以上１２０時間未満。
△：１時間以上２４時間未満。
×：１時間未満。[Evaluation Method of Cap-Off Property] Diameter 15 m
Solid adhesive (glue) molded into a cylinder with m and height of 50 mm
The time required for the surface to dry and become inapplicable under the environment of 25 ° C./humidity of 65% was evaluated according to the following evaluation criteria. Evaluation criteria: A: 120 hours or more. ◯: 24 hours or more and less than 120 hours. Δ: 1 hour or more and less than 24 hours. X: less than 1 hour
【００３２】[0032]
【表１】 [Table 1]
【００３３】上記表１の結果から明らかなように、本発
明範囲となる実施例１〜７の固形接着剤組成物は、本発
明範囲外となる比較例１〜５の固形接着剤組成物に較
べ、接着力、付着力、崩れ荷重及びキャップオフ性に優
れていることが判明した。As is clear from the results of Table 1 above, the solid adhesive compositions of Examples 1 to 7 which fall within the scope of the present invention are the solid adhesive compositions of Comparative Examples 1 to 5 which fall outside the scope of the present invention. By comparison, it was found that the adhesive strength, the adhesive strength, the collapse load, and the cap-off property were excellent.
【００３４】[0034]
【発明の効果】本発明によれば、低い塗布荷重でも良好
な塗布性能と接着力を確保できると共に、充分な強度を
有し、かつ、長期間、固形接着剤組成物の塗布部を大気
中に放置しても優れた塗布性能を有する固形接着剤組成
物が提供される。EFFECTS OF THE INVENTION According to the present invention, good coating performance and adhesive strength can be ensured even with a low coating load, and sufficient strength is maintained, and the coated portion of the solid adhesive composition is kept in the air for a long period of time. Provided is a solid adhesive composition which has excellent coating performance even when left standing.
【図１】（ａ）は、本発明の固形接着剤組成物の実施形
態の一例を示す斜視図であり、（ｂ）は（ａ）の縦断面
図である。FIG. 1A is a perspective view showing an example of an embodiment of a solid adhesive composition of the present invention, and FIG. 1B is a vertical sectional view of FIG.
Ａ 繰り出し容器 １０ 容器本体 ２０ 回動部 ３０ 螺合軸体 ４０ 保持体 ５０ キャップ A feeding container 10 container body 20 Rotating part 30 screw shaft 40 holder 50 cap
───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 4J040 BA182 DA022 DB061 DF001 EB021 EB081 EB111 EB131 EB141 HA136 HA346 HB02 HB03 HB08 HB15 HB18 HB31 JA06 JB09 KA03 KA16 KA23 LA06 PA30 PA33 ─────────────────────────────────────────────────── ─── Continued front page F-term (reference) 4J040 BA182 DA022 DB061 DF001 EB021 EB081 EB111 EB131 EB141 HA136 HA346 HB02 HB03 HB08 HB15 HB18 HB31 JA06 JB09 KA03 KA16 KA23 LA06 PA30 PA33
Claims (3)
溶剤とを含有する固形接着剤組成物であって、該組成物
中に球形状の微粒子を含有し、かつ、常温で固体であ
り、かつ溶剤に対する溶解度が常温で２０％以下となる
ワックス類から選ばれる少なくとも１種を含有してなる
ことを特徴とする固形接着剤組成物。1. At least an adhesive component, a gelling agent,
A solid adhesive composition containing a solvent, which comprises spherical fine particles in the composition, is solid at room temperature, and has a solubility in a solvent of 20% or less at room temperature A solid adhesive composition comprising at least one selected.
溶剤とを含有する固形接着剤組成物であって、該組成物
中に球形状の微粒子を含有し、かつ、少なくとも大気中
及び／又は固形接着剤組成物中の水分を取り込んで蒸発
抑制膜を形成する物質を含有してなることを特徴とする
固形接着剤組成物。2. An adhesive component, a gelling agent, and
A solid adhesive composition containing a solvent, which contains spherical fine particles in the composition, and takes in at least the water in the air and / or the solid adhesive composition to form an evaporation suppressing film. A solid adhesive composition comprising a substance to be formed.
溶剤とを含有する固形接着剤組成物であって、該組成物
中に球形状の微粒子を含有し、かつ、常温で固体であ
り、かつ溶剤に対する溶解度が常温で２０％以下となる
ワックス類から選ばれる少なくとも１種と、少なくとも
大気中及び／又は固形接着剤組成物中の水分を取り込ん
で蒸発抑制膜を形成する物質とを含有してなることを特
徴とする固形接着剤組成物。3. An adhesive component, a gelling agent, and
A solid adhesive composition containing a solvent, which comprises spherical fine particles in the composition, is solid at room temperature, and has a solubility in a solvent of 20% or less at room temperature A solid adhesive composition comprising at least one selected from the above and at least a substance that takes in water in the air and / or solid adhesive composition to form an evaporation suppression film.