JP2002219944A - Belt molding - Google Patents
Belt moldingInfo
- Publication number
- JP2002219944A JP2002219944A JP2001017059A JP2001017059A JP2002219944A JP 2002219944 A JP2002219944 A JP 2002219944A JP 2001017059 A JP2001017059 A JP 2001017059A JP 2001017059 A JP2001017059 A JP 2001017059A JP 2002219944 A JP2002219944 A JP 2002219944A
- Authority
- JP
- Japan
- Prior art keywords
- door glass
- lip
- belt molding
- fiber
- door
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、植毛が施された可
撓性のリップ部を有し、昇降するドアガラスに前記リッ
プ部が当接し、ドア内部へ雨水や埃が侵入するのを防止
するベルトモールに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention has a flexible lip portion with a flocking, and the lip portion contacts an ascending and descending door glass to prevent rainwater and dust from entering the inside of the door. Concerning the belt mall to do.
【０００２】[0002]
【従来の技術】図３は車両リヤドアの上半斜視図で、ベ
ルトモール１は、ドアフレーム３の前辺３１と後辺３２
の間の長さを有する長尺体である。このベルトモール１
を、ベルトラインに沿ったドアアウタパネル２の上縁に
図の矢印のように押し込み装着する。2. Description of the Related Art FIG. 3 is a top half perspective view of a vehicle rear door, in which a belt molding 1 includes a front side 31 and a rear side 32 of a door frame 3.
It is a long body having a length between. This belt molding 1
On the upper edge of the door outer panel 2 along the belt line as shown by the arrow in the figure.
【０００３】ベルトモール１は、その断面を示す図４に
示すように、硬質樹脂材と、軟質樹脂材とからなる押出
し成形品であり、硬質樹脂材でなる基部１１と、基部１
１の周囲に形成され、可撓性を有し、昇降するドアガラ
ス４に当接し、ドア内部へ雨水や埃が侵入するのを防止
するリップ部１３とから構成されている。As shown in FIG. 4 showing a cross section of the belt molding 1, the belt molding 1 is an extruded product made of a hard resin material and a soft resin material, and has a base 11 made of a hard resin material and a base 1 made of a hard resin material.
The lip 13 is formed around the periphery of the door 1 and has flexibility, abuts against the door glass 4 that moves up and down, and prevents rainwater and dust from entering the inside of the door.
【０００４】図４に示すベルトモール１のリップ部１３
は、上リップ１５と下リップ１７とからなっており、こ
れら上リップ１５，下リップ１７のドアガラス４との当
接部分には、植毛１６，１８が施されている。The lip 13 of the belt molding 1 shown in FIG.
Is composed of an upper lip 15 and a lower lip 17, and flocked portions 16 and 18 are applied to contact portions of the upper lip 15 and the lower lip 17 with the door glass 4.
【０００５】この植毛１６，１８は、通常長さ約０．８
ｍｍ，太さ３デニールの６−ナイロン繊維を静電植毛し
たものである。なお、１デニール（ｄｅｎｉｅｒ 繊度
ｄ）とは、長さ９，０００ｍの繊維の重量が１ｇある
時の繊維の太さをいい、次式で表される。[0005] The flocking 16, 18 usually has a length of about 0.8.
It is obtained by electrostatically planting 6-nylon fibers having a thickness of 3 mm and a thickness of 3 mm. In addition, 1 denier (denier fineness d) means the thickness of the fiber when the weight of the fiber having a length of 9,000 m is 1 g and is represented by the following formula.
【０００６】断面積１平方ｍｍの繊維＝（１０，０００
×繊維の比重×０．９）ｄ 上記構成の作動を説明する。ドアガラス４が下降する
と、リップ部１３の植毛１６，１８によりドアガラス４
に付着した水滴が拭き取られる。Fiber having a cross section of 1 square mm = (10,000)
X specific gravity of fiber x 0.9) d The operation of the above configuration will be described. When the door glass 4 descends, the flock 16 and 18 of the lip portion 13 cause the door glass 4 to move.
Water droplets adhering to are wiped off.
【０００７】[0007]
【発明が解決しようとする課題】しかし、上記構成のベ
ルトモール１には、以下のような問題点がある。 （１）植毛１６，１８の繊維は、吸水性のある６−ナイ
ロンであるので、繊維間に水滴を保持し、ドアガラス４
が上昇する際にその水滴がドアガラス４に再付着し、水
切り性が悪い。However, the belt molding 1 having the above structure has the following problems. (1) Since the fibers of the flocking 16 and 18 are 6-nylon having water absorbency, water droplets are held between the fibers and the door glass 4
When the water rises, the water droplets re-attach to the door glass 4 and the drainage property is poor.
【０００８】さらに、６−ナイロンであっても、ドアガ
ラス４に対する摺動抵抗が大きく、リップ部１３をドア
ガラス４に強く押し当てると、ドアガラス４が下降する
際に、リップ部１３が暴れ（スティックスリップ）、水
切り性が悪くなる。Further, even with 6-nylon, the sliding resistance against the door glass 4 is large, and if the lip portion 13 is strongly pressed against the door glass 4, the lip portion 13 ramps up when the door glass 4 descends. (Stick-slip), the drainage becomes worse.
【０００９】また、リップ部１３の暴れが発生しない程
度にリップ部１３をドアガラス４に押し当てようとする
と、押し当て力が足らず、やはり水切り性が悪くなる。 （２）リップ部１３の上リップ１５の先端が太いので、
図４に示すように、上リップ１５の先端上に大きな水滴
Ｗが溜まり、ドアガラス４が上昇する際に水滴Ｗがドア
ガラス４に付着し、水切り性が悪い。 （３）リップ部１３の下リップ１７の基部が太いので、
撓みにくく、ドアガラス４への接触面積が狭くなり、水
切り性が悪い。If the lip portion 13 is pressed against the door glass 4 to such an extent that the lip portion 13 does not run out, the pressing force is insufficient, and the drainage property also deteriorates. (2) Since the tip of the upper lip 15 of the lip portion 13 is thick,
As shown in FIG. 4, large water droplets W accumulate on the tip of the upper lip 15, and when the door glass 4 rises, the water droplets W adhere to the door glass 4, resulting in poor drainage. (3) Since the base of the lower lip 17 of the lip portion 13 is thick,
It is difficult to bend, the contact area with the door glass 4 becomes small, and the drainage property is poor.
【００１０】本発明は、上記問題点に鑑みてなされたも
ので、その課題は、水切り性が向上するベルトモールを
提供することにある。[0010] The present invention has been made in view of the above problems, and an object of the present invention is to provide a belt molding having improved drainage.
【００１１】[0011]
【課題を解決するための手段】上記課題を解決する請求
項１記載の発明は、植毛が施された可撓性のリップ部を
有し、昇降するドアガラスに前記リップ部が当接し、ド
ア内部へ雨水や埃が侵入するのを防止するベルトモール
であって、前記植毛の繊維の太さが１デニール以下、繊
維の長さが０．６ｍｍ以下であることを特徴とするベル
トモールである。According to a first aspect of the present invention, there is provided a door having a flexible lip portion provided with flocks, wherein the lip portion abuts on a door glass which moves up and down. A belt molding for preventing rainwater and dust from entering inside, wherein the thickness of the flocking fiber is 1 denier or less and the fiber length is 0.6 mm or less. .
【００１２】従来より短く、且つ、細い繊維の植毛を用
いることで、ドアガラスに対する摺動抵抗が小さくな
り、ドアガラス上昇時にリップ部が暴れることなく、リ
ップ部をドアガラスに強く押し当てることができ、水切
り性が向上する。[0012] By using a shorter and thinner fiber implantation than before, the sliding resistance against the door glass is reduced, and the lip can be strongly pressed against the door glass without the lip rising when the door glass rises. It is possible to improve drainage.
【００１３】請求項２記載の発明は、請求項１記載の発
明の前記植毛の繊維を疎水性で低摩擦の材質で被覆した
ことを特徴とするベルトモールである。繊維を疎水性の
材質で被覆したことにより、繊維間に水滴を保持しにく
くなり、ドアガラスが上昇する際にその水滴がドアガラ
スに再付着しにくくなり、水切り性が向上する。According to a second aspect of the present invention, there is provided a belt molding according to the first aspect, wherein the fiber of the flocking is coated with a hydrophobic and low-friction material. By coating the fibers with a hydrophobic material, it is difficult to hold water droplets between the fibers, and when the door glass rises, the water droplets are less likely to adhere to the door glass, thereby improving drainage.
【００１４】繊維を低摩擦の材質で被覆したことによ
り、ドアガラスが下降する際に、リップ部が暴れにくく
なり、水切り性が向上する。請求項３記載の発明は、請
求項２記載の発明の前記疎水性で低摩擦の材質は、ポリ
ピロールであることを特徴とするベルトモールである。By coating the fiber with a material having low friction, when the door glass descends, the lip portion is less likely to be violent and the drainage property is improved. A third aspect of the present invention is a belt molding according to the second aspect, wherein the hydrophobic and low-friction material is polypyrrole.
【００１５】本発明でのポリピロールとは、ピロールお
よびその誘導体をモノマーとして（即ち、少なくともモ
ノマーの一成分として）重合して得られるポリマーを意
味し、無置換ピロールまたは各種の置換ピロールのホモ
ポリマーの他、ピロールと３，５−置換ピロール（３，
５−ジメチルピロール等）、３，４−置換ピロール（４
−メチルピロール−３−カルボン酸メチル等）、Ｎ−置
換ピロール（Ｎ−メチルピロール等）もしくは３−置換
ピロール（３−メチルピロール、３−オクチルピロール
等）とをモノマーとして重合して作られたコポリマーも
包含される。無置換ピロールのポリマーであるポリピロ
ールは、繊維等の被処理材との接着強度、導電性の程
度、加工性の良否等の点から、特に好ましい材料であ
る。最も好ましいポリピロールは、ピロールのみをモノ
マーとして重合して得られるホモポリマーである。The polypyrrole in the present invention means a polymer obtained by polymerizing pyrrole and its derivative as a monomer (that is, at least as a component of the monomer), and is an unsubstituted pyrrole or a homopolymer of various substituted pyrroles. In addition, pyrrole and 3,5-substituted pyrrole (3,
5-dimethylpyrrole), 3,4-substituted pyrrole (4
-Methylpyrrole-3-carboxylate), N-substituted pyrrole (N-methylpyrrole, etc.) or 3-substituted pyrrole (3-methylpyrrole, 3-octylpyrrole, etc.) as a monomer. Copolymers are also included. Polypyrrole, which is a polymer of unsubstituted pyrrole, is a particularly preferable material from the viewpoint of adhesive strength to a material to be treated such as fiber, degree of conductivity, and good workability. The most preferred polypyrrole is a homopolymer obtained by polymerizing pyrrole alone as a monomer.
【００１６】請求項４記載の発明は、請求項１乃至３の
いずれかに記載の発明の前記リップ部を、上リップと下
リップとで構成し、前記上リップの先端を細く、前記下
リップの基部を中空としたことを特徴とするベルトモー
ルである。According to a fourth aspect of the present invention, the lip portion according to any one of the first to third aspects comprises an upper lip and a lower lip, and the tip of the upper lip is made thinner. Is a belt molding characterized by having a hollow base.
【００１７】前記上リップの先端を細くしたことによ
り、上リップの先端上に大きな水滴が溜まらず、ドアガ
ラスが上昇する際にドアガラスに付着する水の量が少な
くなり、水切り性が向上する。By making the tip of the upper lip thin, large water droplets do not accumulate on the tip of the upper lip, and the amount of water adhering to the door glass when the door glass rises is reduced, thereby improving drainage. .
【００１８】前記下リップの基部を中空としたことによ
り、下リップが撓みやすく、ドアガラスへの接触面積が
広くなり、水切り性が向上する。By making the base of the lower lip hollow, the lower lip is easily bent, the contact area with the door glass is widened, and the drainage property is improved.
【００１９】[0019]
【発明の実施の形態】次に図面を用いて本発明の実施の
形態例を説明する。図１は本発明の一実施の形態例のベ
ルトモールの断面図である。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Next, embodiments of the present invention will be described with reference to the drawings. FIG. 1 is a sectional view of a belt molding according to an embodiment of the present invention.
【００２０】図において、ベルトモール１００は、硬質
樹脂材と、軟質樹脂材とからなる押出し成形品であり、
硬質樹脂材でなる基部１１１と、基部１１１の周囲に形
成され、可撓性を有し、昇降するドアガラス１０４に当
接し、ドア内部へ雨水や埃が侵入するのを防止するリッ
プ部１１３とから構成されている。In the figure, a belt molding 100 is an extruded product made of a hard resin material and a soft resin material.
A base portion 111 made of a hard resin material; and a lip portion 113 formed around the base portion 111 and having flexibility, abutting against the ascending and descending door glass 104, and preventing rainwater and dust from entering the inside of the door. It is composed of
【００２１】リップ部１１３は、上リップ１１５と下リ
ップ１１７とからなっており、これら上リップ１１５，
下リップ１１７のドアガラス１４との当接部分には、植
毛１１６，１１８が施されている。The lip portion 113 is composed of an upper lip 115 and a lower lip 117.
Flocked portions 116 and 118 are applied to a contact portion of the lower lip 117 with the door glass 14.
【００２２】本実施の形態例の植毛１１６，１１８の繊
維は、６−ナイロンで、従来より短く、且つ、細い繊
維、すなわち、繊維の太さが１デニール以下、繊維の長
さが０．６ｍｍ以下のものを用いた。The fibers of the flocking 116 and 118 of this embodiment are 6-nylon and are shorter and thinner than the conventional fiber, that is, the fiber thickness is 1 denier or less and the fiber length is 0.6 mm. The following were used.
【００２３】さらに、繊維を疎水性で低摩擦の材質であ
るポリピロールで被覆した。また、リップ部１１３の上
リップ１１５の先端を細く、下リップ１１７の基部に中
空部１１７ａを形成した。Further, the fiber was covered with polypyrrole, which is a hydrophobic and low friction material. Further, the tip of the upper lip 115 of the lip portion 113 is made thin, and a hollow portion 117 a is formed at the base of the lower lip 117.
【００２４】上記構成の作動を説明する。ドアガラス１
０４が下降すると、リップ部１１３の植毛１１６，１１
８によりドアガラス１０４に付着した水滴が拭き取られ
る。The operation of the above configuration will be described. Door glass 1
When 04 descends, the flocking 116, 11 of the lip part 113
With 8, water droplets attached to the door glass 104 are wiped off.
【００２５】上記構成によれば、以下のような効果を得
ることができる。 （１）植毛１１６，１１８の繊維の形状として、従来よ
り短く、且つ、細い繊維を用いることで、ドアガラス１
０４に対する摺動抵抗が小さくなり、ドアガラス１０４
上昇時のリップ部１１３の上リップ１１５，下リップ１
１７が暴れることなく、上リップ１１５，下リップ１１
７をドアガラス１０４へ強く押し当てることができ、水
切り性が向上する。 （２）植毛１１６，１１８の繊維をポリピロールで被覆
した。According to the above configuration, the following effects can be obtained. (1) As a fiber shape of the flocking 116 and 118, a shorter and thinner fiber than the conventional one is used, so that the door glass 1
04, the sliding resistance with respect to the door glass 104 decreases.
Upper lip 115 and lower lip 1 of the lip portion 113 when ascending
The upper lip 115 and the lower lip 11
7 can be pressed strongly against the door glass 104, and the drainage property is improved. (2) The fibers of the flocks 116 and 118 were covered with polypyrrole.
【００２６】よって、繊維を疎水性の材質で被覆したこ
とにより、繊維間に水滴を保持しにくくなり、ドアガラ
スが上昇する際にその水滴がドアガラスに再付着にくく
なり、水切り性が向上する。Therefore, by coating the fibers with a hydrophobic material, it is difficult to retain water droplets between the fibers, and when the door glass rises, it is difficult for the water droplets to re-attach to the door glass, thereby improving drainage. .
【００２７】また、繊維を低摩擦の材質で被覆したこと
により、ドアガラスが下降する際に、リップ部が暴れに
くくなり、水切り性が向上する。 （３）上リップ１１５の先端を細くしたことにより、上
リップ１１５の先端上に大きな水滴が溜まらず、ドアガ
ラス１０４が上昇する際にドアガラス１０４に付着する
水の量が少なくなり、水切り性が向上する。In addition, since the fibers are coated with a material having low friction, the lip portion is less likely to be violent when the door glass descends, and the drainage property is improved. (3) By making the tip of the upper lip 115 thin, large water droplets do not collect on the tip of the upper lip 115, and the amount of water adhering to the door glass 104 when the door glass 104 rises is reduced, and the drainage property is improved. Is improved.
【００２８】また、下リップ１１７の基部に中空部１１
７ａを設けたことにより、下リップ１１７が撓みやす
く、ドアガラス１０４への接触面積が広くなり、水切り
性が向上する。The hollow portion 11 is formed at the base of the lower lip 117.
By providing 7a, the lower lip 117 is easily bent, the contact area with the door glass 104 is increased, and the drainage property is improved.
【００２９】[0029]
【実施例】本願発明者は、本発明の効果を確認するため
に、以下のような実験を行った。図１に示すような形状
のベルトモール１００での植毛１１６，１１８の６−ナ
イロン繊維の形状及びポリピロール被覆を変え、ドアガ
ラス１０４を上昇及び下降させた場合でのドアガラス１
０４に対する摺動抵抗を測定した。EXAMPLES The inventors of the present application conducted the following experiments in order to confirm the effects of the present invention. The door glass 1 in a case where the shape of the 6-nylon fiber of the flocking 116, 118 in the belt molding 100 having the shape shown in FIG.
04 was measured for sliding resistance.
【００３０】その結果を図２に示す。ここで、太さが３
デニール、長さが０．８ｍｍの繊維が、従来のベルトモ
ールの植毛の繊維である。FIG. 2 shows the results. Where the thickness is 3
Denier, a fiber having a length of 0.8 mm, is a fiber used for flocking in a conventional belt molding.
【００３１】そして、太さが１デニール、長さが０．６
ｍｍの繊維が、本願発明のベルトモールの植毛の繊維で
ある。植毛１１６，１１８の繊維の形状として、従来よ
り短く、且つ、細い繊維を用いることで、ドアガラス１
０４に対する摺動抵抗が低くなることを確認した。The thickness is 1 denier and the length is 0.6
The mm fiber is the fiber of the belt molding of the present invention. As the fiber shape of the flocking 116 and 118, a shorter and thinner fiber than the conventional one is used, so that the door glass 1
It was confirmed that the sliding resistance with respect to No. 04 was low.
【００３２】また、繊維をポリピロールで被覆すること
により、さらに、ドアガラス１０４に対する摺動抵抗が
低くなることが確認した。Further, it was confirmed that by coating the fiber with polypyrrole, the sliding resistance against the door glass 104 was further reduced.
【００３３】[0033]
【発明の効果】以上述べたように請求項１記載の発明に
よれば、従来より短く、且つ、細い繊維の植毛を用いる
ことで、ドアガラスに対する摺動抵抗が小さくなり、ド
アガラス上昇時にリップ部が暴れることなく、リップ部
をドアガラスに強く押し当てることができ、水切り性が
向上する。As described above, according to the first aspect of the present invention, the use of flocked fibers, which are shorter and thinner than the conventional one, reduces the sliding resistance against the door glass. The lip part can be pressed strongly against the door glass without the part being violated, and the drainage property is improved.
【００３４】請求項２及び３記載の発明によれば、繊維
を疎水性の材質で被覆したことにより、繊維間に水滴を
保持しにくくなり、ドアガラスが上昇する際にその水滴
がドアガラスに再付着にくくなり、水切り性が向上す
る。According to the second and third aspects of the present invention, since the fibers are coated with the hydrophobic material, it is difficult to retain water droplets between the fibers, and when the door glass rises, the water droplets are applied to the door glass. Reattachment becomes difficult, and drainage is improved.
【００３５】繊維を低摩擦の材質で被覆したことによ
り、ドアガラスが下降する際に、リップ部が暴れにくく
なり、水切り性が向上する。請求項４記載の発明によれ
ば、前記上リップの先端を細くしたことにより、上リッ
プの先端上に大きな水滴が溜まらず、ドアガラスが上昇
する際にドアガラスに付着する水の量が少なくなり、水
切り性が向上する。By coating the fiber with a material having low friction, the lip portion is less likely to be violent when the door glass descends, and the drainage property is improved. According to the invention as set forth in claim 4, since the tip of the upper lip is made thin, large water droplets do not collect on the tip of the upper lip, and the amount of water adhering to the door glass when the door glass rises is small. And the drainage property is improved.
【００３６】前記下リップの基部を中空としたことによ
り、下リップが撓みやすく、ドアガラスへの接触面積が
広くなり、水切り性が向上する。By making the base of the lower lip hollow, the lower lip is easily bent, the contact area with the door glass is increased, and the drainage property is improved.
【図１】本発明の一実施の形態例のベルトモールの断面
図である。FIG. 1 is a sectional view of a belt molding according to an embodiment of the present invention.
【図２】実施例での実験の結果を示す図である。FIG. 2 is a diagram showing the results of an experiment in an example.
【図３】車両リヤドアの上半斜視図である。FIG. 3 is an upper half perspective view of a vehicle rear door.
【図４】従来のベルトモールの断面図ある。FIG. 4 is a sectional view of a conventional belt molding.
１００ ベルトモール １０４ ドアガラス １１３ リップ部 １１５ 上リップ １１７ 下リップ １１６，１１８ 植毛 100 Belt molding 104 Door glass 113 Lip part 115 Upper lip 117 Lower lip 116, 118 Flocked
Claims (4)
し、昇降するドアガラスに前記リップ部が当接し、ドア
内部へ雨水や埃が侵入するのを防止するベルトモールで
あって、 前記植毛の繊維の太さが１デニール以下、繊維の長さが
０．６ｍｍ以下であることを特徴とするベルトモール。1. A belt molding having a flexible lip portion on which hair is implanted, wherein the lip portion contacts an ascending and descending door glass to prevent rainwater and dust from entering the inside of the door. A belt molding, wherein the thickness of the flocking fiber is 1 denier or less and the length of the fiber is 0.6 mm or less.
で被覆したことを特徴とする請求項１記載のベルトモー
ル。2. The belt molding according to claim 1, wherein the fibers of the flocking are coated with a hydrophobic and low-friction material.
ールであることを特徴とする請求項２記載のベルトモー
ル。3. The belt molding according to claim 2, wherein the hydrophobic and low-friction material is polypyrrole.
で構成し、 前記上リップの先端を細く、 前記下リップの基部を中空としたことを特徴とする請求
項１乃至３のいずれかに記載のベルトモール。4. The lip portion according to claim 1, wherein the lip portion comprises an upper lip and a lower lip, a tip of the upper lip is thin, and a base of the lower lip is hollow. The belt molding described in.