JP2002169319A - Double-sided printing sheet - Google Patents
Double-sided printing sheetInfo
- Publication number
- JP2002169319A JP2002169319A JP2000370029A JP2000370029A JP2002169319A JP 2002169319 A JP2002169319 A JP 2002169319A JP 2000370029 A JP2000370029 A JP 2000370029A JP 2000370029 A JP2000370029 A JP 2000370029A JP 2002169319 A JP2002169319 A JP 2002169319A
- Authority
- JP
- Japan
- Prior art keywords
- double
- adhesive
- sided printing
- printing sheet
- polyester film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、両面が、レーザー
プリンタ−、インクジエットプリンター、電子複写機等
の印刷機により印刷できるようにした粘着剤付きの両面
印刷シートに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a double-sided printing sheet with an adhesive which can be printed on both sides by a printing machine such as a laser printer, an ink jet printer or an electronic copier.
【0002】[0002]
【従来の技術】従来、剥離用シートの両面に剥離可能に
粘着剤層を設け、その上に、印刷用紙又は表面処理した
印刷用合成樹脂フイルムをそれぞれ粘着し粘着剤付きの
両面印刷シートを、前述した印刷機で印刷すると、下記
のような欠点が起こりやすい。 印刷機の紙詰まりが発生しやすい。その理由は、剥離
用シートが、一般的に厚地の比較的硬性シートが使用さ
れていること、小型の反転式印刷機が使用されたとき、
印刷機内部で2回トナ定着ローラを通過する両面印刷機
が使用されたときなど、印刷機の紙詰まりが特に起こり
やすい。 また、印刷された印刷シートに、変形、カール、印刷
ずれ、熱収縮等が発生しやすい。その理由は、印刷のた
め、熱ローラーを通過するので、剥離用シートの耐熱性
や剥離用シートと印刷用シートとの熱膨張率の相違や印
刷用シートの湿気の吸収の度合等により、印刷用シート
の変形、カール、印刷ずれ、熱収縮等が発生しやすい。
そこで本発明者は、剥離用シートを、耐熱性や断熱性が
高く、通常の剥離用シートより柔軟で、引張り強度も強
い発泡ポリエステルフイルムを使用して、上記問題点を
解決することに成功した。2. Description of the Related Art Conventionally, a pressure-sensitive adhesive layer is provided on both sides of a release sheet so as to be releasable, and a printing paper or a synthetic resin film for surface treatment is adhered thereon, and a double-sided printing sheet with an adhesive is provided. When printing is performed by the above-described printing machine, the following disadvantages are likely to occur. Paper jams in printing machines are likely to occur. The reason is that the release sheet is generally a relatively hard sheet of thick material, when a small reversing printing machine is used,
Paper jams in the printing press are particularly likely to occur, such as when a two-sided printing press that passes through the toner fixing roller twice inside the printing press is used. In addition, deformation, curl, print misalignment, heat shrinkage, and the like are likely to occur on the printed printing sheet. The reason for this is that the printing sheet passes through a heat roller, so the printing is performed due to the heat resistance of the release sheet, the difference in the coefficient of thermal expansion between the release sheet and the printing sheet, the degree of moisture absorption of the printing sheet, and the like. Deformation, curl, print misalignment, heat shrinkage, etc. of the sheet for printing are likely to occur.
Therefore, the present inventor has succeeded in solving the above-described problems by using a foamed polyester film having a high heat resistance and a high heat insulating property, being more flexible than a normal release sheet, and having a high tensile strength. .
【0003】[0003]
【発明が解決しようとする課題】すなわち、本発明は、
粘着剤付きの両面印刷シートを、紙詰まりさせることな
く、また、変形、カール、印刷ずれ、熱収縮等を発生さ
せることなく、印刷できるようにした両面印刷シートを
提供するものである。また、本発明は、従来より厚手の
粘着剤付きの両面印刷シートを使用できるようにした両
面印刷シートを提供するものである。That is, the present invention provides:
An object of the present invention is to provide a double-sided printing sheet capable of printing on a double-sided printing sheet with an adhesive without causing paper jam and without causing deformation, curl, printing misalignment, heat shrinkage and the like. Further, the present invention provides a double-sided printing sheet which can use a thicker double-sided printing sheet with an adhesive than before.
【0004】[0004]
【課題を解決するための手段】本発明両面印刷シート
は、上記課題を達成するため、図示するように、発泡ポ
リエステルフイルム10の表面11及び裏面12を、そ
れぞれ非粘着乃至離型処理して粘着剤20、20を塗布
し、その上に、紙又は表面処理をした印刷用合成樹脂フ
イルム30、30の裏面32、32をそれぞれ粘着した
ものである。本発明において、発泡ポリエステルフイル
ムは、厚み15ミクロン以上250ミクロン以下のもの
を使用することが好ましい。また、本発明において、発
泡ポリエステルフイルムの表面及び裏面の非粘着乃至離
型処理は、シリコンの塗布、微小凹凸面の形成、非粘着
性乃至離型性フイルムの積層により達成される。シリコ
ン塗布は公知であるので、詳細説明は省略する。発泡ポ
リエステルフイルムに対する微小凹凸面は、フイルム成
形時又はフイルム成形後のフイルム自体に対する微小凹
凸面の形成のほか、微小シリカ粒、微小ビーズ粒等のマ
ット剤のフイルムコーテイングによる微小凹凸面の形成
が含まれ、ポリエステルフイルム自体の離型性の物性と
相俟つて、粘着面に対する非粘着性乃至離型性が発揮で
きる場合がある。非粘着性乃至離型性フイルムは、ポリ
エステルフイルムのほか、ポリ弗化ビニルフイルム、ポ
リプロピレンフイルム、ナイロンフイルム等があり、こ
れらを熱融着、接着等により積層することにより、粘着
面に対する非粘着性乃至離型性が発揮出来る場合があ
る。なお、これらの非粘着性乃至離型性フイルムに微小
凹凸面加工したときは、更に粘着面に対する非粘着性乃
至離型性の効果が発揮される。印刷用合成樹脂フイルム
は、印刷するためのトナ定着、重送防止、走行性の向
上、静電気防止等のため、静電防止剤及びマット剤をコ
ーテイングすることが必要で、このことは公知であるの
で、詳細説明は省略する。なお、印刷用合成樹脂フイル
ムにポリエチレンテレフタレートフイルム、ポリエチレ
ンナフタレートフイルムを使用するときは、厚み25ミ
クロン乃至100ミクロンが好ましい。また、紙はレー
ザープリンター用、電子複写用、インクジエットプリン
ター用の公知のものが好ましい。In order to achieve the above object, the double-sided printing sheet of the present invention has a surface 11 and a rear surface 12 of a foamed polyester film 10 which are non-adhesive or release-treated, respectively, as shown in the drawing. Agents 20, 20 are applied, and the back surfaces 32, 32 of paper or surface-treated synthetic resin films 30, 30, which have been subjected to surface treatment, are adhered thereon. In the present invention, it is preferable to use a foamed polyester film having a thickness of 15 μm or more and 250 μm or less. In the present invention, the non-adhesive or release treatment of the front and back surfaces of the foamed polyester film is achieved by applying silicon, forming a fine uneven surface, and laminating the non-adhesive or release film. Since silicon coating is known, detailed description is omitted. The micro-textured surface for the foamed polyester film includes the formation of micro-textured surface on the film itself during or after film forming, and the formation of micro-textured surface by film coating of matting agent such as micro silica particles and micro bead particles. In addition, in some cases, non-adhesiveness to the adhesive surface or releasability can be exhibited in combination with the physical properties of the releasability of the polyester film itself. Non-adhesive or release films include, in addition to polyester films, polyvinyl fluoride films, polypropylene films, nylon films, and the like. In some cases, releasability can be exhibited. In addition, when the non-adhesive or release film is processed into a fine uneven surface, the non-adhesive or release effect on the adhesive surface is further exhibited. Synthetic resin films for printing require coating with an antistatic agent and a matting agent for toner fixing for printing, prevention of double feed, improvement of running properties, prevention of static electricity, etc., and this is known. Therefore, detailed description is omitted. When a polyethylene terephthalate film or a polyethylene naphthalate film is used as the synthetic resin film for printing, the thickness is preferably 25 microns to 100 microns. The paper is preferably a known paper for a laser printer, electronic copying, or an ink jet printer.
【0005】[0005]
【発明の実施の形態1】本発明の実施の形態1が図1に
示されている。本発明実施例の両面印刷シートは、発泡
ポリエステルフイルム10、粘着剤層20、20、静電
気防止剤及びシリカ微粒によるマット剤の表面処理した
印刷用合成樹脂フイルム30、30からなる。発泡ポリ
エステルフイルム10は、独立発泡のポリエチレンテレ
フタレートフイルムで、表面11及び裏面12の両面
が、シリカ微粒のマット剤の合成樹脂コーテイングがさ
れて微小凹凸面111、121を形成し、粘着剤層2
0、20に対し、剥離可能に粘着している。粘着剤層2
0は、印刷用合成樹脂フイルム30、30の裏面32に
粘着すると共に、発泡ポリエステルフイルム10の表面
11及び裏面12に剥離可能に粘着している。印刷用フ
イルムは、ポリエチレンテレフタレートフイルム製で、
表面31には、静電防止剤及びシリカ微粒によるマット
剤の表面コーテイング層311を形成し、裏面32は、
プライマー処理されて粘着剤層20を粘着している。従
つて、発明実施例の両面印刷シートを印刷に使用する
と、剥離シート10が、従来の剥離シートを使用した場
合に比べて、柔軟性、断熱性及び引張り強度があるの
で、紙詰まり、変形、カール、印刷ずれが発生しなかつ
た。また、従来の両面印刷シートの厚みは、200ミク
ロンが最大厚みであつたが、これよりも厚い約250ミ
クロン程度の両面印刷シートを印刷機に通過させること
ができた。また、本発明実施例の両面印刷シートは、そ
れぞれ厚みの異なる印刷用合成樹脂フイルムや、一方又
は両方の印刷用合成樹脂フイルムがミシン目、ハーフカ
ットなどの施されたものでも、前述した支障は何ら発生
しなかつた。First Embodiment FIG. 1 shows a first embodiment of the present invention. The double-sided printing sheet according to the embodiment of the present invention comprises a foamed polyester film 10, pressure-sensitive adhesive layers 20, 20, a synthetic resin film for printing 30, which has been subjected to a surface treatment of a matting agent with an antistatic agent and silica fine particles. The foamed polyester film 10 is a closed-cell foamed polyethylene terephthalate film. Both surfaces of the front surface 11 and the back surface 12 are coated with a synthetic resin coating of a silica fine matting agent to form minute uneven surfaces 111 and 121, and the adhesive layer 2 is formed.
0 and 20 are peelably adhered. Adhesive layer 2
Numeral 0 is adhered to the back surface 32 of the synthetic resin film for printing 30, 30 and is detachably adhered to the front surface 11 and the back surface 12 of the foamed polyester film 10. The printing film is made of polyethylene terephthalate film,
On the front surface 31, a surface coating layer 311 of a matting agent formed by an antistatic agent and silica fine particles is formed,
The pressure-sensitive adhesive layer 20 is adhered by the primer treatment. Therefore, when the double-sided printing sheet of the embodiment of the invention is used for printing, the release sheet 10 has more flexibility, heat insulation and tensile strength than the case where a conventional release sheet is used. No curl or print misalignment occurred. Further, the maximum thickness of the conventional double-sided printing sheet was 200 microns, but a thicker double-sided printing sheet of about 250 microns could be passed through the printing machine. Further, the double-sided printing sheet of the embodiment of the present invention, even if the synthetic resin film for printing having a different thickness, or one or both of the synthetic resin films for printing are provided with perforations, half cuts, etc. Nothing happened.
【0006】[0006]
【発明の実施の形態2】本発明の実施の形態2が図2に
示されている。本発明実施例の両面印刷シートは、両面
がシリコン処理された発泡ポリエステルフイルム10
B、粘着剤層20B、20B、印刷用紙30B、30B
からなる。シリコン処理を除いた発泡ポリエステルフイ
ルム10B、粘着剤層20Bは、発明の実施の形態1と
同じであるので、詳細説明は省略する。紙は、公知の印
刷用紙であり、詳細説明は省略する。本発明実施例の両
面印刷シートを印刷した場合は、室内の湿度が大きい場
合、熱の影響を受けて、従来は紙のカールによる紙詰ま
りが発生しやすかつたが、本発明実施例の場合、熱の影
響を受けにくく、カールによる紙詰まりは発生しなかつ
た。その他、変形、カール、印刷ずれ、熱収縮等も発明
の実施の形態1と同様に、何ら発生しなかつた。Second Embodiment A second embodiment of the present invention is shown in FIG. The double-sided printing sheet of the embodiment of the present invention is made of a foamed polyester film 10 of which both sides are siliconized.
B, adhesive layer 20B, 20B, printing paper 30B, 30B
Consists of Since the foamed polyester film 10B and the pressure-sensitive adhesive layer 20B excluding the silicon treatment are the same as those in the first embodiment of the invention, detailed description will be omitted. The paper is a known printing paper, and a detailed description is omitted. When the double-sided printing sheet of the embodiment of the present invention is printed, when the humidity in the room is large, under the influence of heat, paper jam due to the curl of the paper is liable to occur conventionally. The paper is hardly affected by heat and does not cause paper jam due to curling. In addition, no deformation, curl, print misalignment, heat shrinkage, etc. occurred at all as in the first embodiment of the invention.
【0007】[0007]
【発明の効果】以上のように、本発明両面印刷シート
は、紙詰まり、変形、カール、印刷ずれ、熱収縮等を発
生させることなく印刷することができ、また、従来より
厚地の両面印刷シートを印刷できることになつた。従つ
て、厚手のラベル用紙やはがき用紙等の印刷が効率よく
行うことができ、本発明の実用価値は大きい。As described above, the double-sided printing sheet of the present invention can be printed without causing paper jam, deformation, curl, printing misalignment, heat shrinkage and the like. Can be printed. Therefore, printing on thick label paper or postcard paper can be performed efficiently, and the practical value of the present invention is great.
【図1】本発明の実施の形態を示す部分拡大断面の説明
図である。FIG. 1 is an explanatory view of a partially enlarged cross section showing an embodiment of the present invention.
【図2】本発明の実施の形態を示す別の部分拡大断面の
説明図である。FIG. 2 is an explanatory view of another partially enlarged cross section showing the embodiment of the present invention.
10、10B 発泡ポリエステルフイルム 11、11B 発泡ポリエステルフイルムの表面 12、12B 発泡ポリエステルフイルムの裏面 20、20B 粘着剤層 30、30B 印刷用紙又は合成樹脂フイルム 32、32B 印刷用紙又は合成樹脂フイルムの裏面 10, 10B Foamed polyester film 11, 11B Surface of foamed polyester film 12, 12B Backside of foamed polyester film 20, 20B Adhesive layer 30, 30B Printing paper or synthetic resin film 32, 32B Backing of printing paper or synthetic resin film
フロントページの続き Fターム(参考) 2H086 BA01 BA15 BA19 BA24 BA31 4F100 AA20H AK01B AK01C AK01D AK01E AK41A AK42 AK52G BA03 BA05 BA06 BA10B BA10C BA13 CA17B CA17C CA22B CA22C CB05 CC00B CC00C DD07A DG10B DG10C DJ01A EH46 EJ01 EJ39 EJ65 GB90 HB31B HB31C JA03 JL01 JL04 JL13D JL13E JL14D JL14E Continued on the front page F term (reference) 2H086 BA01 BA15 BA19 BA24 BA31 4F100 AA20H AK01B AK01C AK01D AK01E AK41A AK42 AK52G BA03 BA05 BA06 BA10B BA10C BA13 CA17B CA17C CA22B CA22C CB05 CC01B01B01 EBJB CB01B01 CB01B01 CB01E JL04 JL13D JL13E JL14D JL14E
Claims (5)
面を、それぞれ非粘着乃至離型処理して粘着剤を塗布
し、その上に、紙又は表面処理をした印刷用合成樹脂フ
イルムの裏面をそれぞれ粘着したことを特徴とする両面
印刷シート。1. A front side and a back side of a foamed polyester film are respectively subjected to a non-adhesive or release treatment to apply an adhesive, and a back surface of a paper or a surface-treated synthetic resin film subjected to a surface treatment is adhered thereon. A double-sided printing sheet, characterized in that:
び裏面の非粘着乃至離型処理が、シリコン塗布による請
求項1記載の両面印刷シート。2. The double-sided printing sheet according to claim 1, wherein the non-adhesive or release treatment of the front and back surfaces of the foamed polyester film is performed by applying silicon.
び裏面の非粘着乃至離型処理が、前記発泡ポリエステル
フイルムの表面及び裏面の微小凹凸面の形成による請求
項1記載の両面印刷シート。3. The double-sided printing sheet according to claim 1, wherein the non-adhesive or release treatment of the front and back surfaces of the foamed polyester film is performed by forming fine irregularities on the front and back surfaces of the foamed polyester film.
び裏面の非粘着乃至離型処理が、前記発泡ポリエステル
フイルムの表面及び裏面に非粘着性乃至離型性合成樹脂
フイルムの積層による請求項1記載の両面印刷シート。4. The double-sided surface according to claim 1, wherein the non-adhesive or release treatment of the front and back surfaces of the expanded polyester film is performed by laminating a non-adhesive or release synthetic resin film on the front and back surfaces of the expanded polyester film. Print sheet.
ムが、静電防止剤及びマット剤を含む合成樹脂コーテイ
ングによる請求項1記載の両面印刷シート。5. The double-sided printing sheet according to claim 1, wherein the surface-treated synthetic resin film for printing is a synthetic resin coating containing an antistatic agent and a matting agent.