JP2002150843A - Conductive plastic sheet for carrier tape - Google Patents
Conductive plastic sheet for carrier tapeInfo
- Publication number
- JP2002150843A JP2002150843A JP2000340946A JP2000340946A JP2002150843A JP 2002150843 A JP2002150843 A JP 2002150843A JP 2000340946 A JP2000340946 A JP 2000340946A JP 2000340946 A JP2000340946 A JP 2000340946A JP 2002150843 A JP2002150843 A JP 2002150843A
- Authority
- JP
- Japan
- Prior art keywords
- plastic sheet
- carrier tape
- sheet according
- conductive paint
- carbon black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、キャリアテープ用
導電性プラスチックシートに関し、詳しくは、特に引張
強度が改良されたキャリアテープ用導電性プラスチック
シートに関する。The present invention relates to a conductive plastic sheet for a carrier tape, and more particularly to a conductive plastic sheet for a carrier tape having improved tensile strength.
【０００２】[0002]
【従来の技術】キャリアテープは、電子部品の自動供給
用部品収納テープであり、具体的には、真空成形（エン
ボス加工）によってプラスチックシートの表面の電子部
品収納用のポケットを形成したものである。そして、ポ
ケット内に電子部品を収納し、カバーテープで蓋をした
後、リールに巻き取り、ユースポイトに連続的に供給さ
れる。2. Description of the Related Art A carrier tape is a component storage tape for automatically supplying electronic components. Specifically, a carrier tape is formed on a surface of a plastic sheet by vacuum forming (embossing) to store electronic components. . Then, the electronic components are stored in a pocket, covered with a cover tape, wound up on a reel, and continuously supplied to a use point.
【０００３】キャリアテープ用導電性プラスチックシー
トはキャリアテープの基材として使用され、その導電性
は、帯電性に基づくゴミやホコリ等の異物の付着を防止
するために付与される。そして、従来より、溶剤系導電
性インクの塗工により導電性が付与されたキャリアテー
プ用導電性プラスチックシートが提案されている。しか
しながら、斯かるキャリアテープ用導電性プラスチック
シートの場合、溶剤によるプラスチックシートの溶融・
劣化のため、キャリアテープとした際の引張強度が低い
と言う問題がある。[0003] A conductive plastic sheet for a carrier tape is used as a base material of a carrier tape, and its conductivity is imparted to prevent adhesion of foreign substances such as dust and dust due to the charging property. Conventionally, a conductive plastic sheet for a carrier tape to which conductivity has been imparted by applying a solvent-based conductive ink has been proposed. However, in the case of such a conductive plastic sheet for a carrier tape, melting of the plastic sheet by a solvent
Due to the deterioration, there is a problem that the tensile strength of the carrier tape is low.
【０００４】[0004]
【発明が解決しようとする課題】本発明は、上記実情に
鑑みなされたものであり、その目的は、特に引張強度が
改良されたキャリアテープ用導電性プラスチックシート
を提供することにある。SUMMARY OF THE INVENTION The present invention has been made in view of the above circumstances, and an object of the present invention is to provide a conductive plastic sheet for a carrier tape having improved tensile strength.
【０００５】[0005]
【課題を解決するための手段】本発明者は、鋭意検討を
重ねた結果、特定の処方に従って特定の導電材料を使用
することにより、上記の目的を容易に達成し得るとの知
見を得、本発明の完成に至った。Means for Solving the Problems As a result of intensive studies, the present inventor has found that the above object can be easily achieved by using a specific conductive material according to a specific prescription. The present invention has been completed.
【０００６】すなわち、本発明の要旨は、熱可塑性樹脂
より成る基材シートの表面に水性導電性塗料が塗布され
且つ当該塗布面の表面固有抵抗値が１×１０4〜１×１
０10Ω／□の範囲であることを特徴とするキャリアテー
プ用導電性プラスチックシートに存する。That is, the gist of the present invention is that a water-based conductive paint is applied to the surface of a substrate sheet made of a thermoplastic resin and the surface specific resistance of the applied surface is 1 × 10 4 to 1 × 1.
The conductive plastic sheet for a carrier tape is characterized by having a range of 0 10 Ω / □.
【０００７】[0007]
【発明の実施の形態】以下、本発明を詳細に説明する。
本発明において、基材シートとして使用される熱可塑性
樹脂としては、ポリスチレン、ポリエチレン、ポリプロ
ピレン、ポリエステル、ポリアミド等が挙げられるが、
コストの点からスチレン系樹脂が好適に使用される。こ
こで、スチレン系樹脂は、ビニル芳香族化合物の単独重
合体、ビニル芳香族化合物およびこれとラジカル共重合
可能な単量体の１種または２種以上から成る共重合体を
指す。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the present invention will be described in detail.
In the present invention, examples of the thermoplastic resin used as the base sheet include polystyrene, polyethylene, polypropylene, polyester, and polyamide,
Styrene resins are preferably used in terms of cost. Here, the styrene-based resin refers to a homopolymer of a vinyl aromatic compound, a copolymer of one or more of a vinyl aromatic compound and a monomer capable of being radically copolymerized with the vinyl aromatic compound.
【０００８】上記の共重合可能な単量体としては、例え
ばα−メチルスチレン、ビニルトルエン、ビニルキシレ
ン、モノクロルスチレン、ジクロルスチレン、モノブロ
ムスチレン、ジブロムスチレン等のスチレン誘導体、メ
チルメタクリレート、エチルメタクリレート等のメタク
リル酸エステル、メチルアクリレート、ブチルアクリレ
ート等のアクリル酸エステル、アクリロニトリル、メタ
クリロニトリル等の不飽和ニトリル化合物、無水マレイ
ン酸、無水イタコン酸等の不飽和酸無水物、アクリル
酸、メタクリル酸等の不飽和酸等が挙げられる。Examples of the copolymerizable monomer include styrene derivatives such as α-methylstyrene, vinyltoluene, vinylxylene, monochlorostyrene, dichlorostyrene, monobromostyrene, dibromostyrene, methyl methacrylate, ethyl Methacrylates such as methacrylate, acrylates such as methyl acrylate and butyl acrylate, unsaturated nitrile compounds such as acrylonitrile and methacrylonitrile, unsaturated anhydrides such as maleic anhydride and itaconic anhydride, acrylic acid, methacrylic acid And the like.
【０００９】本発明において、好ましいスチレン系樹脂
は、ポリスチレン、スチレン−アクリロニトリル共重合
体、スチレン−メチルメタクリレート共重合体、スチレ
ン−α−メチルスチレン共重合体、スチレン−無水マレ
イン酸共重合体、スチレン−アクリル酸共重合体であ
る。In the present invention, preferred styrene resins are polystyrene, styrene-acrylonitrile copolymer, styrene-methyl methacrylate copolymer, styrene-α-methylstyrene copolymer, styrene-maleic anhydride copolymer, and styrene. -An acrylic acid copolymer.
【００１０】上記の基材シートの表面には水性導電性塗
料が塗布される。ここに、水性導電性塗料とは、親水性
溶媒に導電材料が分散された意味する。斯かる水性導電
性塗料には、通常、造膜助剤と水性接着剤（エマルジョ
ン系接着剤）が含有されている。An aqueous conductive paint is applied to the surface of the base sheet. Here, the aqueous conductive paint means that a conductive material is dispersed in a hydrophilic solvent. Such an aqueous conductive paint usually contains a film forming aid and an aqueous adhesive (emulsion adhesive).
【００１１】上記の親水性溶媒としては、水またはメタ
ノール、エタノール、プロパノール、ブタノール、ペン
タノール、ヘキサノール等の炭素数が通常６以下の低級
アルコールが挙げられる。水性導電性塗料の乾燥性の観
点から、低級アルコールが好適に使用される。Examples of the hydrophilic solvent include water and lower alcohols having usually 6 or less carbon atoms, such as methanol, ethanol, propanol, butanol, pentanol and hexanol. From the viewpoint of drying properties of the aqueous conductive paint, a lower alcohol is preferably used.
【００１２】上記の導電材料としては、各種の金属
（金、銀、銅、パラジウム、インジウム−錫、亜鉛、ア
ルミニウム等）、金属酸化物、カーボンブラックが挙げ
られる。これらの中ではカーボンブラックが好適に使用
される。Examples of the conductive material include various metals (such as gold, silver, copper, palladium, indium-tin, zinc, and aluminum), metal oxides, and carbon black. Among them, carbon black is preferably used.
【００１３】カーボンブラックの種類は、特に制限され
ないが、比表面積に対する全酸素量が０．１０ｍｇ／ｍ
2以下であるカーボンブラック又は比表面積に対する全
水素量が８×１０-3ｍｇ／ｍ2以下であるカーボンブラ
ックが好ましく、特に全酸素量および全水素量に関する
上記の条件を同時に満足するカーボンブラックが好まし
い。Although the type of carbon black is not particularly limited, the total oxygen content relative to the specific surface area is 0.10 mg / m 2.
Carbon black having a total surface area of not more than 2 or carbon black having a total hydrogen amount of not more than 8 × 10 −3 mg / m 2 based on the specific surface area is preferable. preferable.
【００１４】上記の比表面積は、ＢＥＴの式を使用した
窒素吸着法により求められる。すなわち、低温窒素吸着
装置（イタリヤ、カルロ・エルバ社製「ソウプトマチッ
ク１８００」）を使用し低温窒素吸着法によりカーボン
ブラックの窒素吸着量を測定し、これからＢＥＴの式を
使用し多点法により算出することが出来る。The specific surface area is determined by a nitrogen adsorption method using the BET equation. That is, the amount of nitrogen adsorbed on carbon black is measured by a low-temperature nitrogen adsorption method using a low-temperature nitrogen adsorption device (“Soptomatik 1800” manufactured by Carlo Elba, Italy), and the multipoint method is then used using the BET equation Can be calculated.
【００１５】上記の全酸素量および全水素量は、耐熱性
の試料管に一定量の乾燥カーボンブラックを採取し、１
０-2ｍｍＨｇまで減圧した後、９５０℃に加熱した電気
炉内に上記の試料管を入れ、３０分間で脱離する揮発分
の全量をタンクに捕集し、ガスクロマト分析に供するこ
とによって求めることが出来る。カーボンブラックは、
種々の官能基（−ＯＨ、＝ＣＯ、−ＣＯＯＨ等）を有
し、全酸素量および全水素量に関する上記の条件は、官
能基の種類と量によって異る。これらは、カーボンブラ
ックの酸化処理の条件（使用するオゾン、過酸化水素、
硝酸、ＮＯガス、ＮＯ2ガス、空気、ＳＯ3ガス、フッ素
ガス等の酸化剤の種類など）によって異る。The total oxygen content and total hydrogen content are determined by collecting a fixed amount of dry carbon black in a heat-resistant sample tube,
After reducing the pressure to 0 -2 mmHg, the above sample tube is placed in an electric furnace heated to 950 ° C., and the total amount of volatile components desorbed in 30 minutes is collected in a tank and determined by gas chromatographic analysis. I can do it. Carbon black is
It has various functional groups (—OH, ＣＯCO, —COOH, etc.), and the above conditions regarding the total oxygen amount and the total hydrogen amount differ depending on the types and amounts of the functional groups. These are the conditions of the oxidation treatment of carbon black (ozone used, hydrogen peroxide,
Nitric acid, NO gas, NO 2 gas, air, SO 3 gas, fluorine gas, etc.).
【００１６】比表面積に対する全酸素量が０．１０ｍｇ
／ｍ2以下または比表面積に対する全水素量が８×１０
-3ｍｇ／ｍ2以下であるカーボンブラックを使用した場
合は、カーボンブラックの適度な充填量により導電性を
始めとする強度などの物性に優れた導電性プラスチック
シートが得られる。The total oxygen content relative to the specific surface area is 0.10 mg
/ M 2 or less or the total hydrogen content relative to the specific surface area is 8 × 10
When carbon black having a content of -3 mg / m 2 or less is used, a conductive plastic sheet having excellent physical properties such as strength including conductivity can be obtained by an appropriate amount of carbon black.
【００１７】前記の造膜助剤として、特に限定されない
が、エチレングリコール誘導体および／またはジエチレ
ングリコール誘導体が好ましい。エチレングリコール誘
導体の具体例としては、エチルセロソルブ、ブチルセロ
ソルブ等のエチレングリコールモノアルキルエーテル等
が挙げられる。また、ジエチレングリコール誘導体の具
体例としては、エチルカルビトール、ブチルカルビトー
ル等のジエチレングリコールモノアルキルエーテル、ジ
エチレングリコールジエチルエーテル等のジエチレング
リコールジアルキルエーテル等が挙げられる。The film forming aid is not particularly limited, but is preferably an ethylene glycol derivative and / or a diethylene glycol derivative. Specific examples of the ethylene glycol derivative include ethylene glycol monoalkyl ethers such as ethyl cellosolve and butyl cellosolve. Specific examples of the diethylene glycol derivative include diethylene glycol monoalkyl ethers such as ethyl carbitol and butyl carbitol, and diethylene glycol dialkyl ethers such as diethylene glycol diethyl ether.
【００１８】前記のエマルジョン系接着剤としては、特
に限定されないが、熱可塑性樹脂がスチレン系樹脂の場
合はアクリルエマルジョン系接着剤が好ましい。アクリ
ルエマルジョン系接着剤の市販品としては、ジョンソン
ポリマー社製「ジョンクリル８４０」等が挙げられる。
これらの固形分濃度は通常４０〜５０重量％である。The emulsion adhesive is not particularly limited. However, when the thermoplastic resin is a styrene resin, an acrylic emulsion adhesive is preferred. Commercially available acrylic emulsion-based adhesives include "Johncryl 840" manufactured by Johnson Polymer.
These solid contents are usually 40 to 50% by weight.
【００１９】本発明においては、水性導電性塗料中にフ
ィラー、例えば、マイカ、珪酸カルシウム、ポリエチレ
ンワックス等を配合することが出来る。フイラーの配合
により、塗膜密度の向上、滑り性の調節の他、次の様な
効果が期待できる。すなわち、キャリアテープとして実
際の使用の際に電子部品収納用のポケットの側面の光沢
度が高すぎる場合に画像処理機が半導体不良品と誤認知
してしまうと問題があるが、フィラーの配合によりポケ
ットの側面の光沢度を調節して上記の問題を回避するこ
とが出来る。フィラーの配合量は、使用目的によっても
異るが、水性導電性塗料中の割合として、通常１〜５重
量％である。In the present invention, a filler such as mica, calcium silicate, polyethylene wax or the like can be blended in the aqueous conductive paint. By adding the filler, the following effects can be expected in addition to the improvement of the coating film density and the adjustment of the slipperiness. In other words, when the glossiness of the side of the pocket for storing electronic components is too high during actual use as a carrier tape, there is a problem that the image processing machine may erroneously recognize it as a semiconductor defective product. The above problem can be avoided by adjusting the glossiness of the side of the pocket. The amount of the filler varies depending on the purpose of use, but is usually 1 to 5% by weight as a proportion in the aqueous conductive paint.
【００２０】水性導電性塗料の調製は、ディゾルバー等
の攪拌機、ボールミル、ニーダー等の分散機を使用して
前記の必要な各成分を撹拌・分散処理することに行われ
る。この際、親水性溶媒１００重量部に対し、導電材料
は、通常１〜４０重量部、好ましくは１〜１５重量部、
造膜助剤は、通常１〜４０重量部、好ましくは１〜２０
重量部、エマルジョン系接着剤は、エマルジョンとし
て、通常１０〜７０重量部、好ましくは２０〜５０重量
部とされる。The preparation of the aqueous conductive paint is carried out by stirring and dispersing the above-mentioned necessary components using a disperser such as a dissolver or a disperser such as a ball mill or a kneader. In this case, based on 100 parts by weight of the hydrophilic solvent, the conductive material is usually 1 to 40 parts by weight, preferably 1 to 15 parts by weight,
The film-forming auxiliary is usually 1 to 40 parts by weight, preferably 1 to 20 parts by weight.
The weight of the emulsion adhesive is usually 10 to 70 parts by weight, preferably 20 to 50 parts by weight as an emulsion.
【００２１】基材シートの表面に対する水性導電性塗料
の塗布は、例えば、リバースロールコータ、グラビアコ
ーター、ロッドコーター、エアドクタコーター等の適宜
の塗布装置を使用して行われる。The application of the water-based conductive paint to the surface of the substrate sheet is performed using an appropriate coating device such as a reverse roll coater, a gravure coater, a rod coater, and an air doctor coater.
【００２２】本発明のキャリアテープ用導電性プラスチ
ックシートにおいて、塗布面の表面固有抵抗値は１×１
０4〜１×１０10Ω／□の範囲であることが重要であ
る。斯かる表面固有抵抗値を有することにより、本発明
のキャリアテープ用導電性プラスチックシートは、ゴミ
やホコリ等の異物の付着から保護される。塗布面の表面
固有抵抗値は好ましくは１×１０5〜１×１０7Ω／□の
範囲である。In the conductive plastic sheet for a carrier tape of the present invention, the surface specific resistance of the coated surface is 1 × 1.
0 It is important that a 4 ~1 × 10 10 Ω / □ range. By having such a surface specific resistance value, the conductive plastic sheet for a carrier tape of the present invention is protected from adhesion of foreign substances such as dust and dust. The surface specific resistance of the coated surface is preferably in the range of 1 × 10 5 to 1 × 10 7 Ω / □.
【００２３】本発明のキャリアテープ用導電性プラスチ
ックシートは上記の様に構成されて次の様な特徴を有す
る。すなわち、水性導電性塗料を使用するため、溶剤系
導電性インクを使用する場合に惹起されるプラスチック
シートの溶融・劣化がなく、また、水性導電性塗料を塗
布して使用するため、導電材料をプラスチックシートに
練り込む場合の様にプラスチックシート（マトリック
ス）中にボイドが発生することがない。その結果、キャ
リアテープ用導電性プラスチックシートは優れた引張強
度を発揮する。The conductive plastic sheet for a carrier tape of the present invention is constituted as described above and has the following features. In other words, since the water-based conductive paint is used, there is no melting and deterioration of the plastic sheet caused when using the solvent-based conductive ink, and since the water-based conductive paint is applied and used, the conductive material is used. Voids are not generated in a plastic sheet (matrix) as in the case of kneading into a plastic sheet. As a result, the conductive plastic sheet for a carrier tape exhibits excellent tensile strength.
【００２４】[0024]
【実施例】以下、本発明を実施例により更に詳細に説明
するが、本発明は、その要旨を超えない限り、以下の実
施例に限定されるものではない。なお、以下の諸例にお
いて「部」とあるのは「重量部」を表す。また、物性測
定方法は次の通りである。EXAMPLES Hereinafter, the present invention will be described in more detail with reference to examples, but the present invention is not limited to the following examples unless it exceeds the gist of the present invention. In the following examples, “parts” means “parts by weight”. The method for measuring physical properties is as follows.
【００２５】（１）表面固有抵抗は三菱化学社製「ハイ
レスターＩＰ」を使用して測定した。(1) The surface resistivity was measured using “Hirester IP” manufactured by Mitsubishi Chemical Corporation.
【００２６】（２）引張強度および伸びはＪＩＳ Ｋ６
８７２に準拠して測定した。(2) Tensile strength and elongation are JIS K6
872.
【００２７】実施例１ ＜水性導電性塗料の調製＞エタノール５５部、カーボン
ブラック（比表面積に対する全酸素量が０．０４ｍｇ／
ｍ2、比表面積に対する全水素量が６×１０-3ｍｇ／
ｍ2）５部、ブチルセロソルブ１０部、アクリルエマル
ジョン（ジョンソンポリマー社製「ジョンクリル８４
０」、スチレン−アクリル共重合体、固形分４３重量
％）３０部をボールミルで分散処理し、水性導電性塗料
を調製した。Example 1 <Preparation of aqueous conductive paint> 55 parts of ethanol, carbon black (total oxygen content relative to specific surface area was 0.04 mg /
m 2 , the total amount of hydrogen relative to the specific surface area is 6 × 10 −3 mg /
m 2 ) 5 parts, butyl cellosolve 10 parts, acrylic emulsion (John Krill 84 manufactured by Johnson Polymer Co., Ltd.)
0 ", styrene-acrylic copolymer, solid content 43% by weight) were dispersed in a ball mill to prepare an aqueous conductive paint.
【００２８】＜キャリアテープ用導電性プラスチックシ
ートの作成＞厚さ０．３ｍｍのポリスチレン系樹脂シー
ト（旭化成工業社製「ＳＤ−２２０」）に上記で得られ
た水性導電性塗料をグラビアコート法で塗布した後に乾
燥し、導電性プラスチックシートを得た。塗布条件は、
版深さ２０μｍ、印刷速度３０ｍ／分とした。得られた
導電性プラスチックシートは、表面固有抵抗１×１０ 5
Ω／□、引張強度４８０Ｎ／ｍｍ2、伸び６０％であっ
た。<Conductive plastic sheet for carrier tape
Preparation of sheet> 0.3mm thick polystyrene resin sheet
(“SD-220” manufactured by Asahi Kasei Corporation)
Water-based conductive paint is applied by the gravure coating method and then dried.
After drying, a conductive plastic sheet was obtained. The application conditions are
The plate depth was 20 μm and the printing speed was 30 m / min. Got
The conductive plastic sheet has a surface resistivity of 1 × 10 Five
Ω / □, tensile strength 480N / mmTwo, The growth is 60%
Was.
【００２９】比較例１ ＜水性導電性塗料の調製＞トルエン８２部、実施例１と
同様のカーボンブラック５部、ブチルセロソルブ１０
部、アクリル樹脂（ジョンソンポリマー社製「ジョンク
リル６１１」）１３部をボールミルで分散処理し、溶剤
系導電性塗料を調製した。Comparative Example 1 <Preparation of aqueous conductive paint> 82 parts of toluene, 5 parts of carbon black as in Example 1, butyl cellosolve 10
And a acrylic resin ("Johncryl 611" manufactured by Johnson Polymer Co., Ltd.) were dispersed in a ball mill to prepare a solvent-based conductive paint.
【００３０】＜キャリアテープ用導電性プラスチックシ
ートの作成＞実施例１と同様のポリスチレン系樹脂シー
トに上記で得られた溶剤系導電性塗料をグラビアコート
法で塗布した後に乾燥し、導電性プラスチックシートを
得た。塗布条件は、版深さ２０μｍ、印刷速度３０ｍ／
分とした。得られた導電性プラスチックシートは、表面
固有抵抗１×１０6Ω／□、引張強度３７０Ｎ／ｍｍ2、
伸び２５％であった。<Preparation of Conductive Plastic Sheet for Carrier Tape> The solvent-based conductive paint obtained above was applied to the same polystyrene resin sheet as in Example 1 by a gravure coating method, and then dried. I got The coating conditions were plate depth 20 μm, printing speed 30 m /
Minutes. The obtained conductive plastic sheet had a surface resistivity of 1 × 10 6 Ω / □, a tensile strength of 370 N / mm 2 ,
The elongation was 25%.
【００３１】比較例２ 実施例１と同様のポリスチレン系樹脂シートの溶融物７
０部に実施例１と同様のカーボンブラック３０部を練り
込んだ後に押し出し成形して厚さ０．３ｍｍの導電性プ
ラスチックシートを得た。得られた導電性プラスチック
シートは、表面固有抵抗１×１０6Ω／□、引張強度２
８０Ｎ／ｍｍ2、伸び３０％であった。Comparative Example 2 Melt 7 of polystyrene resin sheet similar to that in Example 1
30 parts of the same carbon black as in Example 1 was kneaded into 0 parts and extruded to obtain a conductive plastic sheet having a thickness of 0.3 mm. The obtained conductive plastic sheet had a surface resistivity of 1 × 10 6 Ω / □ and a tensile strength of 2
80 N / mm 2 and elongation 30%.
【００３２】[0032]
【発明の効果】以上説明した本発明によれば、特に引張
強度が改良されたキャリアテープ用導電性プラスチック
シートが提供され、本発明は半導体の製造分野に寄与す
るところが大きい。According to the present invention described above, a conductive plastic sheet for a carrier tape having particularly improved tensile strength is provided, and the present invention greatly contributes to the field of semiconductor production.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｃ０９Ｄ 5/02 Ｃ０９Ｄ 5/02 ５Ｇ３０７ 5/24 5/24 7/12 7/12 133/00 133/00 201/00 201/00 // Ｂ６５Ｄ 85/86 Ｃ０８Ｌ 25:06 Ｃ０８Ｌ 25:06 Ｂ６５Ｄ 85/38 Ｍ Ｆターム(参考） 3E096 AA06 BA08 CA15 DA14 EA02X FA07 FA20 GA01 4D075 CA22 DA06 DB36 DB37 DB42 DB43 DB48 DB53 DC21 EA06 EA13 EB22 EB37 EC07 EC30 4F006 AA15 AB24 AB72 BA07 CA08 DA04 4F100 AA37B AK01A AK12 AK12A AK12J AK25 AK25B AK25J AL01 BA02 CA21B CC00B EH46B GB41 JB16A JG01B JG04B JK02 YY00B 4J038 CG141 HA026 HA066 HA216 JA19 JA20 JA26 KA06 MA08 MA10 NA11 NA20 PC08 5G307 GA08 GC02 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) C09D 5/02 C09D 5/02 5G307 5/24 5/24 7/12 7/12 133/00 133/00 201/00 201/00 // B65D 85/86 C08L 25:06 C08L 25:06 B65D 85/38 MF term (reference) 3E096 AA06 BA08 CA15 DA14 EA02X FA07 FA20 GA01 4D075 CA22 DA06 DB36 DB37 DB42 DB43 DB48 DB53 DC21 EA06 EA13 EB22 EB37 EC07 EC30 4F006 AA15 AB24 AB72 BA07 CA08 DA04 4F100 AA37B AK01A AK12 AK12A AK12J AK25 AK25B AK25J AL01 BA02 CA21B CC00B EH46B GB41 JB16A JG01B JG04B JK0 YY08A JA608A2
Claims (8)
に水性導電性塗料が塗布され且つ当該塗布面の表面固有
抵抗値が１×１０4〜１×１０10Ω／□の範囲であるこ
とを特徴とするキャリアテープ用導電性プラスチックシ
ート。An aqueous conductive paint is applied to the surface of a base sheet made of a thermoplastic resin, and the surface specific resistance of the applied surface is in the range of 1 × 10 4 to 1 × 10 10 Ω / □. A conductive plastic sheet for a carrier tape, comprising:
求項１に記載のシート。2. The sheet according to claim 1, wherein the thermoplastic resin is a styrene resin.
ルコールである請求項１又は２に記載のシート。3. The sheet according to claim 1, wherein the solvent constituting the aqueous conductive paint is a lower alcohol.
ーボンブラックである請求項１〜３の何れかに記載のシ
ート。4. The sheet according to claim 1, wherein the conductive material constituting the water-based conductive paint is carbon black.
酸素量が０．１０ｍｇ／ｍ2以下である請求項１〜４の
何れかに記載のシート。5. The sheet according to claim 1, wherein the total oxygen content relative to the specific surface area of the carbon black is 0.10 mg / m 2 or less.
水素量が８×１０-3ｍｇ／ｍ2以下である請求項１〜５
の何れかに記載のシート。6. The total amount of hydrogen relative to the specific surface area of carbon black is 8 × 10 −3 mg / m 2 or less.
The sheet according to any one of the above.
ングリコール誘導体および／またはジエチレングリコー
ル誘導体を含有する請求項１〜６の何れかに記載のシー
ト。7. The sheet according to claim 1, wherein the aqueous conductive paint contains an ethylene glycol derivative and / or a diethylene glycol derivative as a film-forming aid.
水性導電性塗料が接着剤としてアクリルエマルジョンを
含有する請求項１〜７の何れかに記載のシート。8. The thermoplastic resin is a styrene resin,
The sheet according to any one of claims 1 to 7, wherein the aqueous conductive paint contains an acrylic emulsion as an adhesive.