JP2001351536A - Operation method for ion source - Google Patents
Operation method for ion sourceInfo
- Publication number
- JP2001351536A JP2001351536A JP2000173362A JP2000173362A JP2001351536A JP 2001351536 A JP2001351536 A JP 2001351536A JP 2000173362 A JP2000173362 A JP 2000173362A JP 2000173362 A JP2000173362 A JP 2000173362A JP 2001351536 A JP2001351536 A JP 2001351536A
- Authority
- JP
- Japan
- Prior art keywords
- ion beam
- flow rate
- amount
- vapor
- plasma generation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【発明の属する技術分野】この発明は、有機金属蒸気を
原料として当該有機金属蒸気を構成する金属のイオンビ
ームを引き出すイオン源の運転方法に関し、より具体的
には、当該イオン源を構成するプラズマ生成容器の組立
後または清掃後に最初にイオンビームを引き出す際に、
イオンビーム量が安定するまでの時間を短縮する手段に
関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method of operating an ion source for extracting an ion beam of a metal constituting an organometallic vapor from an organometallic vapor as a raw material, and more specifically to a plasma forming the ion source. When first extracting the ion beam after assembling or cleaning the production vessel,
The present invention relates to means for shortening the time until the ion beam amount is stabilized.
【0002】[0002]
【従来の技術】イオン源から金属のイオンビームを引き
出す場合、原料として有機金属蒸気を用いる場合があ
る。例えば、インジウムイオンビームを引き出す場合、
有機金属蒸気として、In(CH3)3 (トリメチルインジ
ウム)、In(C2H5)3 (トリエチルインジウム)等の
蒸気を用いる。2. Description of the Related Art When extracting a metal ion beam from an ion source, an organic metal vapor may be used as a raw material in some cases. For example, when extracting an indium ion beam,
As the organic metal vapor, a vapor such as In (CH 3 ) 3 (trimethylindium) or In (C 2 H 5 ) 3 (triethylindium) is used.
【0003】このような有機金属蒸気のイオン源(より
具体的にはそれを構成するプラズマ生成容器)への供給
量は、引き出される目的金属のイオンビーム量に大きな
影響を与える。そのために従来から、イオン源を運転す
るときは、有機金属蒸気を、目的量のイオンビームを引
き出すのに応じた一定の流量に正確に調節して供給する
ようにしている。[0003] The supply amount of such an organic metal vapor to an ion source (more specifically, a plasma generating container constituting the same) has a great influence on the amount of ion beam of a target metal to be extracted. Therefore, conventionally, when the ion source is operated, the organometallic vapor is supplied while being accurately adjusted to a constant flow rate in accordance with extracting a desired amount of the ion beam.
【0004】[0004]
【発明が解決しようとする課題】ところが、有機金属蒸
気を原料として用いる場合、イオン源を構成するプラズ
マ生成容器の組立後または清掃後に最初にイオンビーム
を引き出す際に、図5に示すように、目的金属(この例
ではインジウム)のイオンビーム量(即ちイオンビーム
電流)が安定するまでに長時間を要するという課題があ
る。However, when an organometallic vapor is used as a raw material, when an ion beam is first extracted after assembling or cleaning of a plasma generating container constituting an ion source, as shown in FIG. There is a problem that it takes a long time until the ion beam amount (that is, ion beam current) of the target metal (indium in this example) is stabilized.
【0005】この図5は、プラズマ生成容器内に供給す
るトリメチルインジウム蒸気の流量を一定にしてインジ
ウムイオンビームの引き出しを始めたときの例であり、
インジウムイオンビーム電流は、時間経過に従って徐々
に上昇して、引き出し開始から20分強程度でほぼ一定
になっており、その後は、トリメチルインジウム蒸気の
供給量やその他の運転パラメータが変化しない限り大き
な変動はない。通常は、このイオンビーム電流がほぼ一
定になった以降をイオン注入等の処理に用いるため、上
記例では、イオンビームの立ち上げに(即ちイオンビー
ムの引き出しを始めてからほぼ一定量に落ち着くまで
に)20分強程度という長時間を要している。FIG. 5 shows an example in which extraction of an indium ion beam is started while the flow rate of trimethylindium vapor supplied into the plasma generation vessel is kept constant.
The indium ion beam current gradually rises with the passage of time, and remains almost constant for a little over 20 minutes from the start of the extraction. After that, there is a large fluctuation unless the supply amount of trimethylindium vapor and other operating parameters change. There is no. Normally, since the ion beam current becomes substantially constant after the ion beam current is used for processing such as ion implantation, in the above-described example, the ion beam is started up (that is, from the time when the ion beam is extracted until the time when the ion beam reaches a substantially constant amount). ) It takes a long time of about 20 minutes or more.
【0006】なお、一度目的金属のイオンビームを引き
出した後に、即ちプラズマ生成容器の組立後または清掃
後の最初のイオンビーム引き出しでないときに、イオン
ビームを立ち上げるときは、上記ほどには長い時間を要
しないことが実験によって確かめられている。After the ion beam of the target metal is extracted once, that is, when the ion beam is not initially extracted after assembling or cleaning the plasma generating container, it is necessary to start the ion beam for a long time as described above. It has been confirmed by experiment that the need for the above is not required.
【0007】そこでこの発明は、有機金属蒸気を原料と
して当該有機金属蒸気を構成する金属のイオンビームを
引き出すイオン源において、プラズマ生成容器の組立後
または清掃後に最初にイオンビームを引き出す際に、イ
オンビーム量が安定するまでの時間を短縮することを主
たる目的とする。Accordingly, the present invention provides an ion source for extracting an ion beam of a metal constituting an organometallic vapor from an organometallic vapor as a raw material, wherein the ion beam is first extracted after assembling or cleaning of a plasma generating vessel. The main purpose is to shorten the time until the beam amount is stabilized.
【0008】[0008]
【課題を解決するための手段】この発明のイオン源の運
転方法は、プラズマ生成容器の組立後または清掃後に最
初にイオンビームを引き出す際に、前記有機金属蒸気を
一定流量でプラズマ生成容器内に供給しながら目的量の
イオンビームを引き出す工程の前に、前記有機金属蒸気
を前記一定流量よりも大きい流量でプラズマ生成容器内
に供給する工程を設けることを特徴としている。According to the method of operating the ion source of the present invention, when the ion beam is first extracted after assembling or cleaning the plasma generating container, the organometallic vapor is introduced into the plasma generating container at a constant flow rate. Before the step of extracting a target amount of ion beam while supplying, a step of supplying the organometallic vapor into the plasma generation vessel at a flow rate larger than the predetermined flow rate is provided.
【0009】上記運転方法によれば、イオンビーム量が
安定するまでの時間を短縮することができた。その理由
は次のように考えられる。According to the above operation method, the time required for the ion beam amount to stabilize can be shortened. The reason is considered as follows.
【0010】即ち、有機金属蒸気を原料とするイオン源
においては、プラズマ生成によって有機金属蒸気から析
出した金属のプラズマ生成容器内壁への付着と、プラズ
マ生成容器が高温に加熱されることに伴う当該金属の内
壁からの再蒸発とが繰り返されていて、この付着と再蒸
発の量が、引き出されるイオンビーム量に関与している
と考えられる。That is, in an ion source using an organometallic vapor as a raw material, the metal deposited from the organometallic vapor by plasma generation adheres to the inner wall of the plasma generation vessel, and the plasma generation vessel is heated to a high temperature. The re-evaporation of the metal from the inner wall is repeated, and the amount of the adhesion and the re-evaporation is considered to be related to the amount of the extracted ion beam.
【0011】組立後または清掃後で未だ目的金属のイオ
ンビームを引き出していない新しいプラズマ生成容器に
は、内壁に付着している金属が存在しないため、イオン
ビームの引き出し始め時はイオンビーム量は少なく、運
転を続けるに従って、プラズマ生成容器の内壁に付着し
ている金属の量が増えてそこからの金属の再蒸発量も増
えるので、徐々にイオンビーム量は増加して行く。やが
て、プラズマ生成容器の内壁に付着する金属の量とそこ
から再蒸発する金属の量とが平衡状態に達してイオンビ
ーム量が安定する。In a new plasma generation vessel from which the target metal ion beam has not yet been extracted after assembly or cleaning, there is no metal adhering to the inner wall, so the amount of the ion beam is small at the start of extraction of the ion beam. As the operation is continued, the amount of metal adhering to the inner wall of the plasma generation vessel increases, and the amount of re-evaporation of the metal therefrom also increases, so that the amount of ion beam gradually increases. Eventually, the amount of metal adhering to the inner wall of the plasma generation vessel and the amount of metal re-evaporating therefrom reach an equilibrium state, and the ion beam amount stabilizes.
【0012】その場合、従来のように有機金属蒸気の供
給量を、初めから、目的量のイオンビームを引き出すの
に応じた一定の流量にしていたのでは、プラズマ生成容
器の内壁に付着する金属の量とそこから再蒸発する金属
の量とが平衡状態に達するまでに長時間を要するので、
イオンビームが安定するまでに長時間を要する。In such a case, if the supply amount of the organometallic vapor is set to a constant flow rate in accordance with the extraction of a desired amount of ion beam from the beginning as in the prior art, the metal adhering to the inner wall of the plasma generation vessel is not obtained. It takes a long time to reach an equilibrium state between the amount of
It takes a long time for the ion beam to stabilize.
【0013】これに対して、この発明のように、有機金
属蒸気を一定流量で供給しながら目的量のイオンビーム
を引き出す工程の前に、有機金属蒸気を前記一定流量よ
りも大きい流量で供給する工程を設けることによって、
プラズマ生成容器の内壁に付着している金属の量を短時
間で多くすることができるので、プラズマ生成容器の内
壁に付着する金属の量とそこから再蒸発する金属の量と
が平衡状態に達するまでの時間を短縮することができ
る。その結果、イオンビーム量が安定するまでの時間を
短縮することができる。On the other hand, as in the present invention, before the step of extracting the desired amount of ion beam while supplying the organometallic vapor at a constant flow rate, the organometallic vapor is supplied at a flow rate larger than the constant flow rate. By providing a process,
Since the amount of metal adhering to the inner wall of the plasma generation container can be increased in a short time, the amount of metal adhering to the inner wall of the plasma generation container and the amount of metal re-evaporating therefrom reach an equilibrium state. The time until the time can be shortened. As a result, the time until the ion beam amount becomes stable can be reduced.
【0014】[0014]
【発明の実施の形態】図1は、イオン源の一例を示す概
略図である。このイオン源2は、原料として供給される
有機金属蒸気8を電離させてプラズマ18を生成するプ
ラズマ生成容器12と、このプラズマ18から電界の作
用で、有機金属蒸気8を構成する金属のイオンビームを
含むイオンビーム24を引き出す引出し電極22とを備
えている。プラズマ生成容器12内の一方側には熱電子
放出用のフィラメント14が設けられており、他方側に
は電子反射用の反射電極16が設けられている。プラズ
マ生成容器12内には外部から電子捕捉用の磁界20が
印加される。このような構造のイオン源2は、バーナス
型イオン源と呼ばれる。26はフィラメント電源、28
はアーク電源である。FIG. 1 is a schematic view showing an example of an ion source. The ion source 2 includes a plasma generation vessel 12 for ionizing an organic metal vapor 8 supplied as a raw material to generate a plasma 18, and an ion beam of a metal constituting the organic metal vapor 8 by the action of an electric field from the plasma 18. And an extraction electrode 22 for extracting an ion beam 24 including A filament 14 for emitting thermoelectrons is provided on one side of the plasma generation container 12, and a reflection electrode 16 for reflecting electrons is provided on the other side. A magnetic field 20 for capturing electrons is applied to the inside of the plasma generation container 12 from the outside. The ion source 2 having such a structure is called a Bernas-type ion source. 26 is a filament power supply, 28
Is an arc power supply.
【0015】プラズマ生成容器12へは、この例では、
有機金属を加熱する蒸発源4で発生させ、かつ流量調節
器6で所望の流量に調節された有機金属蒸気8が、蒸気
導入管10を経由して供給される。この有機金属蒸気8
は、例えば、前述したようなトリメチルインジウム、ト
リエチルインジウム等のインジウム系の有機金属蒸気で
ある。なお、プラズマ生成容器12へ供給する有機金属
蒸気8の流量調節は、前記のように流量調節器6で行っ
ても良いし、蒸発源4の温度調節で行っても良いし、両
者を併用しても良い。In this example, the plasma generation vessel 12 is
An organic metal vapor 8 generated by an evaporation source 4 for heating the organic metal and adjusted to a desired flow rate by a flow controller 6 is supplied via a vapor introduction pipe 10. This organic metal vapor 8
Is an indium-based organometallic vapor such as trimethylindium or triethylindium as described above. The flow rate of the organometallic vapor 8 supplied to the plasma generation vessel 12 may be adjusted by the flow rate controller 6 as described above, may be adjusted by adjusting the temperature of the evaporation source 4, or both may be used in combination. May be.
【0016】プラズマ生成容器12内には、プラズマ1
8の安定生成に必要なガス流量を確保する等の目的で、
有機金属蒸気8の導入に加えて、ガス導入管32からA
r 等の不活性ガスから成る補助ガス30を導入する場合
もある。The plasma 1 is stored in the plasma generation vessel 12.
For the purpose of securing gas flow necessary for stable generation of 8,
In addition to the introduction of the organometallic vapor 8, A
An auxiliary gas 30 made of an inert gas such as r may be introduced.
【0017】前記イオンビーム24中に含まれている目
的金属のイオンビームは、当該イオンビーム24を質量
分離すること等によって取り出すことができる。The ion beam of the target metal contained in the ion beam 24 can be extracted by separating the ion beam 24 by mass or the like.
【0018】前記のようなイオン源2において、プラズ
マ生成容器12内に有機金属蒸気8としてトリメチルイ
ンジウム蒸気を0.3ccmの流量で供給しながらイン
ジウムイオンビームを引き出す運転を行ったときの、ト
リメチルインジウム蒸気の供給を停止する前と後のイン
ジウムイオンビーム電流の変化の一例を図2に示す。こ
のとき、アーク電流(即ちアーク電源28の出力電流)
は一定にした。また、補助ガス30としてAr ガスを
0.5ccmの流量で導入し続けた。In the ion source 2 as described above, trimethylindium is extracted when an operation of extracting an indium ion beam is performed while supplying trimethylindium vapor as the organometallic vapor 8 into the plasma generation vessel 12 at a flow rate of 0.3 ccm. FIG. 2 shows an example of a change in the indium ion beam current before and after the supply of steam is stopped. At this time, the arc current (ie, the output current of the arc power supply 28)
Was kept constant. Ar gas was continuously introduced as the auxiliary gas 30 at a flow rate of 0.5 ccm.
【0019】運転開始から800分が経過した時点でト
リメチルインジウム蒸気の供給を停止したところ、その
後もインジウムイオンビームは減少しながらも発生し続
けており、トリメチルインジウム蒸気の供給停止後約1
00分経過した時点でも約50μA発生している。これ
によって、前述したように、それまでの運転でプラズマ
生成容器12の内壁にインジウムが付着しており、トリ
メチルインジウム蒸気の供給停止後は、この付着してい
たインジウムが再蒸発し、これがインジウムイオンビー
ムの発生に寄与していることが確かめられた。When the supply of the trimethylindium vapor was stopped 800 minutes after the start of the operation, the indium ion beam continued to be generated while decreasing, and about 1 after the supply of the trimethylindium vapor was stopped.
Even at the time when 00 minutes have passed, about 50 μA is generated. As a result, as described above, indium has adhered to the inner wall of the plasma generation vessel 12 in the operation up to that time, and after the supply of the trimethylindium vapor was stopped, the indium thus adhered re-evaporated, and this indium ion was removed. It was confirmed that it contributed to beam generation.
【0020】更に、前記のようなイオン源2において、
プラズマ生成容器12の清掃後に最初にイオンビームを
引き出す際に、プラズマ生成容器12へのトリメチルイ
ンジウム蒸気の供給流量を図3に示すパターンで変化さ
せた。Further, in the ion source 2 as described above,
When the ion beam was first extracted after cleaning the plasma generation container 12, the supply flow rate of trimethylindium vapor to the plasma generation container 12 was changed according to the pattern shown in FIG.
【0021】ここでは、目的量のインジウムイオンビー
ム電流を引き出すためのトリメチルインジウム蒸気の設
定流量(一定流量)をQ1 、最初からこの一定流量Q1
でイオンビームを立ち上げるとした場合にインジウムイ
オンビーム電流が安定するまでの時間をt2 としてい
る。図5の従来例ではこの時間t2 が20分強程度であ
る。Here, the set flow rate (constant flow rate) of trimethylindium vapor for extracting a target amount of indium ion beam current is Q 1 , and this constant flow rate Q 1 from the beginning.
The time until the indium ion beam current stabilizes when the ion beam is started at is set as t 2 . The time t 2 is about 20 minutes little in the conventional example of FIG.
【0022】そしてこの実施例では、第1工程として、
イオンビームの引き出し開始から時間t1 (=t2 /
2)の間、トリメチルインジウム蒸気の流量Q2 を2Q
1 とし、時間t1 経過後に、第2工程として、トリメチ
ルインジウム蒸気の流量を前記一定流量Q1 としてイオ
ンビームの引き出しを続けた。より具体的には、Q1 =
0.3ccm、Q2 =0.6ccm、t1 =10分とし
た。In this embodiment, as a first step,
Time t 1 (= t 2 /
During 2), the flow rate Q 2 of the trimethylindium vapor is reduced to 2Q
1, and after a time t 1 has elapsed, a second step was continued withdrawal of the ion beam flow of trimethylindium vapor as the constant flow rate Q 1. More specifically, Q 1 =
0.3 ccm, Q 2 = 0.6 ccm, and t 1 = 10 minutes.
【0023】その結果、図4に示すように、インジウム
イオンビーム量が安定するまでの時間を10分強程度に
短縮することができた。この図4と前記図5とは、トリ
メチルインジウム蒸気の流量を前記のように変化させる
こと以外は、同一の運転条件とした。このように、従来
例よりもイオンビームの立ち上げ時間を約半分に短縮す
ることができた。As a result, as shown in FIG. 4, the time required for the indium ion beam amount to stabilize can be reduced to just over 10 minutes. FIG. 4 and FIG. 5 have the same operating conditions except that the flow rate of trimethylindium vapor is changed as described above. As described above, the start-up time of the ion beam can be reduced to about half that of the conventional example.
【0024】これは、第1工程を設けて、初めに第2工
程よりも大きな流量でトリメチルインジウム蒸気を供給
することによって、前述したように、プラズマ生成容器
12の内壁に付着しているインジウムの量を短時間で多
くすることができ、それによって、プラズマ生成容器2
の内壁に付着するインジウムの量とそこから再蒸発する
インジウムの量とが平衡状態に達するまでの時間が短縮
され、その結果、インジウムイオンビーム量が安定する
までの時間が短縮されたものと考えられる。This is because, by providing the first step and supplying trimethylindium vapor at a larger flow rate than in the second step, the indium adhering to the inner wall of the plasma generation vessel 12 is reduced as described above. The amount can be increased in a short time, so that the plasma generation vessel 2
It is thought that the time until the amount of indium adhering to the inner wall of the surface and the amount of indium re-evaporating therefrom reached an equilibrium state was shortened, and as a result, the time until the amount of indium ion beam became stable was shortened. Can be
【0025】このような現象は、原料として有機金属蒸
気、特にトリメチルインジウムやトリエチルインジウム
等のインジウム系の有機金属蒸気を用いる場合に特有の
現象であると言うことができる。これは、プラズマ生成
時のプラズマ生成容器12の壁面温度は、通常は500
℃〜600℃程度に達するのに対して、インジウムの融
点はそれよりも低い約156℃であり(ちなみに沸点は
2080℃)、このような温度の関係によって、プラズ
マ生成によってトリメチルインジウム蒸気から析出した
インジウムが液状になってプラズマ生成容器12の内壁
に付着する現象と、付着した液体表面からインジウムが
再蒸発する現象とが同時に起こっており、両者が平衡状
態になるところでインジウムイオンビーム量が安定する
と考えられるからである。Such a phenomenon can be said to be a peculiar phenomenon when an organic metal vapor, particularly an indium-based organic metal vapor such as trimethylindium or triethylindium is used as a raw material. This is because the wall temperature of the plasma generation vessel 12 during plasma generation is usually 500
The melting point of indium is about 156 ° C., which is lower than that (about boiling point of 2080 ° C.), and such temperature relationship has caused precipitation from trimethylindium vapor by plasma generation. The phenomenon that indium becomes liquid and adheres to the inner wall of the plasma generation vessel 12 and the phenomenon that indium re-evaporates from the surface of the adhered liquid occur simultaneously, and when the indium ion beam amount becomes stable where both are in an equilibrium state, Because it is possible.
【0026】これに対して、BF3 (ボラン)やPH3
(ホスフィン)等の従来からよく使用されている原料ガ
スを用いる場合は、前記のような2段階工程でイオンビ
ームを立ち上げる方法を採用しても、イオンビーム量が
安定するまでの時間を短縮する効果は殆ど得られない。
その理由は次のように考えられる。On the other hand, BF 3 (borane) and PH 3
In the case of using a conventionally used source gas such as (phosphine), the time until the ion beam amount is stabilized is shortened even if the method of starting the ion beam in the two-step process as described above is adopted. Effect is hardly obtained.
The reason is considered as follows.
【0027】即ち、BF3 の場合は、プラズマ生成に伴
ってホウ素がプラズマ生成容器12の内壁に付着するこ
とになるが、ホウ素の融点は2080℃、昇華点は25
50℃であり、これらの温度の方がプラズマ生成容器1
2の前記温度よりも遙かに高いので、ホウ素は壁面に付
着したままで再蒸発は非常に少なく、従って壁面に付着
したホウ素のイオンビーム量への影響は非常に少ないか
らである。That is, in the case of BF 3 , boron adheres to the inner wall of the plasma generation vessel 12 as the plasma is generated, but the melting point of boron is 2080 ° C. and the sublimation point is 25.
50 ° C., and these temperatures are higher in the plasma generation vessel 1
Since the temperature is much higher than the above temperature of 2, the amount of re-evaporation is very small while boron remains on the wall surface, and therefore, the effect of boron on the wall surface on the ion beam amount is very small.
【0028】PH3 の場合は、プラズマ生成に伴ってリ
ンがプラズマ生成容器12の内壁に付着することになる
が、リンの融点は約44℃、沸点は約208℃であり、
これらの温度よりもプラズマ生成容器12の前記温度の
方が遙かに高いので、リンが壁面に付着してもすぐに再
蒸発して残存せず、従って壁面に付着したリンのイオン
ビーム量への影響は非常に少ないからである。In the case of PH 3 , phosphorus adheres to the inner wall of the plasma generation vessel 12 with the generation of plasma, but the melting point of phosphorus is about 44 ° C. and the boiling point is about 208 ° C.
Since the temperature of the plasma generation vessel 12 is much higher than these temperatures, even if phosphorus adheres to the wall surface, it is not immediately re-evaporated and remains, and thus the amount of phosphorus ion beam adhered to the wall surface is reduced. Is very small.
【0029】なお、前記第1工程の流量Q2 をより大き
くし(例えばQ2 =3Q1 )、かつ時間t1 をより短く
する(例えばt1 =t2 /3)ことによって、金属の壁
面への付着をより加速して、イオンビーム量が安定する
までの時間をより短縮することも可能である。[0029] Incidentally, the first step of the flow rate Q 2 is greater (for example Q 2 = 3Q 1), and by a shorter time t 1 (e.g. t 1 = t 2/3) , the wall surface of the metal It is also possible to further accelerate the adhesion to the substrate and to shorten the time until the ion beam amount is stabilized.
【0030】また、一度目的金属のイオンビームを引き
出した後は、即ちプラズマ生成容器12の組立後または
清掃後の最初のイオンビーム引き出しでないときは、先
の運転でプラズマ生成容器12の内壁に付着した金属が
存在しているので、敢えて前記のような2段階工程でイ
オンビームを立ち上げる必要はない。そのようにしなく
ても、プラズマ生成容器12の組立後または清掃後の最
初のイオンビーム引き出し時よりも短時間でイオンビー
ム量は安定する。After the ion beam of the target metal is extracted once, that is, when it is not the first ion beam extraction after assembling or cleaning the plasma generating container 12, the ion beam adheres to the inner wall of the plasma generating container 12 in the previous operation. Since the metal is present, there is no need to dare to start the ion beam in the two-step process as described above. Even without doing so, the ion beam amount is stabilized in a shorter time than when the first ion beam is extracted after assembling or cleaning the plasma generation container 12.
【0031】また、この発明は、プラズマ生成容器12
内におけるプラズマ18の生成手段は問わないので、バ
ーナス型イオン源以外のイオン源にも広く適用すること
ができる。例えば、棒状のフィラメントを用いるフリー
マン型イオン源、プラズマ閉じ込めに多極磁場(カスプ
磁場)を用いるバケット型イオン源、プラズマ生成に高
周波(マイクロ波を含む)を用いる高周波イオン源、プ
ラズマ生成にECR(電子サイクロトロン共鳴)を用い
るECR型イオン源等にも適用することができる。Further, according to the present invention, the plasma generating vessel 12
Since the means for generating the plasma 18 in the inside is not limited, the invention can be widely applied to ion sources other than the Bernas-type ion source. For example, a Freeman-type ion source using a rod-shaped filament, a bucket-type ion source using a multipolar magnetic field (cusp magnetic field) for confining plasma, a high-frequency ion source using high frequency (including microwave) for plasma generation, and an ECR ( The present invention can also be applied to an ECR ion source using electron cyclotron resonance).
【0032】[0032]
【発明の効果】以上のようにこの発明によれば、有機金
属蒸気を一定流量で供給しながら目的量のイオンビーム
を引き出す工程の前に、有機金属蒸気を前記一定流量よ
りも大きい流量で供給する工程を設けることによって、
プラズマ生成容器の内壁に付着している金属の量を短時
間で多くすることができるので、プラズマ生成容器の内
壁に付着する金属の量とそこから再蒸発する金属の量と
が平衡状態に達するまでの時間を短縮することができ
る。その結果、イオンビーム量が安定するまでの時間を
短縮することができる。即ち、イオンビームの立ち上げ
時間を短縮することができる。As described above, according to the present invention, the organic metal vapor is supplied at a flow rate larger than the predetermined flow rate before the step of extracting a desired amount of ion beam while supplying the organic metal vapor at a constant flow rate. By providing a process to
Since the amount of metal adhering to the inner wall of the plasma generation container can be increased in a short time, the amount of metal adhering to the inner wall of the plasma generation container and the amount of metal re-evaporating therefrom reach an equilibrium state. The time until the time can be shortened. As a result, the time until the ion beam amount becomes stable can be reduced. That is, the start-up time of the ion beam can be reduced.
【図1】イオン源の一例を示す概略図である。FIG. 1 is a schematic diagram illustrating an example of an ion source.
【図2】トリメチルインジウム蒸気の供給を停止する前
と後のインジウムイオンビーム電流の変化の一例を示す
図である。FIG. 2 is a diagram showing an example of a change in indium ion beam current before and after stopping supply of trimethylindium vapor.
【図3】トリメチルインジウム蒸気の供給流量を変化さ
せるパターンの一例を示す図である。FIG. 3 is a diagram showing an example of a pattern for changing a supply flow rate of trimethylindium vapor.
【図4】図3のパターンのときのインジウムイオンビー
ム電流の立ち上がり状況の一例を示す図である。FIG. 4 is a diagram showing an example of a rising state of an indium ion beam current in the case of the pattern of FIG. 3;
【図5】トリメチルインジウム蒸気の供給流量を一定と
したときのインジウムイオンビーム電流の立ち上がり状
況の一例を示す図である。FIG. 5 is a diagram illustrating an example of a rising state of an indium ion beam current when a supply flow rate of trimethylindium vapor is fixed.
2 イオン源 8 有機金属蒸気 12 プラズマ生成容器 18 プラズマ 24 イオンビーム 2 Ion source 8 Organometallic vapor 12 Plasma generation vessel 18 Plasma 24 Ion beam
Claims (1)
容器内でプラズマを生成して、当該有機金属蒸気を構成
する金属のイオンビームを引き出すイオン源において、
プラズマ生成容器の組立後または清掃後に最初にイオン
ビームを引き出す際に、前記有機金属蒸気を一定流量で
プラズマ生成容器内に供給しながら目的量のイオンビー
ムを引き出す工程の前に、前記有機金属蒸気を前記一定
流量よりも大きい流量でプラズマ生成容器内に供給する
工程を設けることを特徴とするイオン源の運転方法。1. An ion source for generating a plasma in a plasma generation vessel using an organometallic vapor as a raw material and extracting an ion beam of a metal constituting the organometallic vapor,
When extracting the ion beam for the first time after assembling or cleaning the plasma generating container, the organic metal vapor is supplied before the step of extracting the target amount of ion beam while supplying the organometallic vapor into the plasma generating container at a constant flow rate. Supplying a gas into the plasma generation vessel at a flow rate larger than the predetermined flow rate.