JP2001187869A - Semi-opacifying water-based paint composition - Google Patents
Semi-opacifying water-based paint compositionInfo
- Publication number
- JP2001187869A JP2001187869A JP37452999A JP37452999A JP2001187869A JP 2001187869 A JP2001187869 A JP 2001187869A JP 37452999 A JP37452999 A JP 37452999A JP 37452999 A JP37452999 A JP 37452999A JP 2001187869 A JP2001187869 A JP 2001187869A
- Authority
- JP
- Japan
- Prior art keywords
- semi
- coating composition
- weight
- water
- synthetic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】この発明は、建築物などの構
築物の外壁、内壁及び天井などの被塗布物の表面仕上げ
を行うための塗装に使われる半隠ぺい性水系塗料組成物
に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a semi-opaque water-based coating composition used for coating a surface of an object such as an outer wall, an inner wall and a ceiling of a building such as a building.
【０００２】[0002]
【従来の技術】従来の塗料としては、一般的に使われる
エナメル塗料があり、この塗料では、塗替えと表現され
るように被塗布物の色調を隠し、異なった色調に変える
ことなどの目的のために使われている。つまり、被塗布
物の透けがあってはならないため十分な隠ぺい力が必要
であることになる。2. Description of the Related Art As a conventional paint, there is an enamel paint which is generally used. The purpose of this paint is to hide the color tone of an object to be applied and to change the color tone to a different color as described as repainting. Used for That is, since the object to be coated must not be transparent, a sufficient hiding power is required.
【０００３】それとは逆にクリアー塗料がある。この塗
料の目的は、被塗布物の色調を積極的に見せるためであ
って、その目的とするところは被塗布物の保護である。
一般的に良く利用されるのは、石材調仕上げという仕上
げ方法であって、まず、石材調仕上げ材と呼ばれる塗料
を建築物などの構築物に塗布し、その後クリアー塗料を
塗布し、構築物の表面を仕上げる方法である。これは、
クリアー塗料が石材調仕上げ面の保護を目的とし、石材
調仕上げ材を積極的に表面に表したものである。このた
め、クリアー塗料に隠ぺい力があった場合、石材調仕上
げ面が隠されてしまい、構築物が石材調の仕上がりにな
らない。従って、クリアー塗料には隠ぺい力があってな
らないことになる。On the contrary, there is a clear paint. The purpose of the paint is to positively show the color tone of the object to be coated, and the purpose is to protect the object to be coated.
A commonly used finishing method is stone finish, in which a paint called stone finish is first applied to a building or other structure, and then a clear paint is applied to the surface of the structure. It is a method of finishing. this is,
The clear paint is intended to protect the stone-finished surface, and the stone-finished material is positively displayed on the surface. Therefore, if the clear paint has a hiding power, the stone-finished surface is hidden, and the structure does not have a stone-like finish. Therefore, the clear paint must not have hiding power.
【０００４】また、クリヤー塗料には、乾燥後の塗膜に
艶を持たせたものと艶を消したものがあり、その中間的
な半艶と呼ばれるものもある。艶を持たせたクリアー塗
料では、主にバインダーとなる樹脂と添加剤などより構
成されている。艶を消したクリアー塗料は、バインダー
となる樹脂と添加剤及び艶消し材といわれるフィラーな
どにより構成されている場合が多い。だが、このフィラ
ーは塗膜の艶を消すことを目的として添加されるもので
あり、塗膜が隠ぺい力を持たないよう、その添加量も微
量である。[0004] In addition, clear coatings include those in which the coating film after drying has a luster and those in which the luster has been de-lustered, and those which are called intermediate semi-gloss. A glossy clear paint is mainly composed of a resin serving as a binder and additives. The matte clear paint is often composed of a resin serving as a binder, an additive, and a filler called a matting material. However, this filler is added for the purpose of matting the coating film, and its addition amount is very small so that the coating film has no hiding power.
【０００５】[0005]
【発明が解決しようとする課題】ところが、エナメル塗
料は、十分な隠ぺい力が必要なため、塗膜の膜厚１５０
μｍでの隠ぺい率が０．８５〜１．００程度であり、被
塗布物の色調を隠してしまうに、十分な隠ぺい力であ
る。また、クリヤー塗料おいては、隠ぺい力を要求され
ないので、艶を持たせたクリアー塗料では膜厚１５０μ
ｍでの隠ぺい率が０．０１程度であり、フィラーを添加
し艶を消した艶消しクリアー塗料でも、０．０５程度に
なり、隠ぺい力がなく、被塗布物の色調を表すことが十
分可能である。However, since the enamel paint requires a sufficient hiding power, the enamel paint has a thickness of 150 μm.
The concealing ratio in μm is about 0.85 to 1.00, which is a sufficient concealing power to hide the color tone of the object to be coated. In addition, the clear paint does not require a hiding power, so the glossy clear paint has a thickness of 150 μm.
The hiding ratio in m is about 0.01, and even a matte clear paint with matte added fillers has a hiding power of about 0.05 with no hiding power. It is.
【０００６】このため、構築物などの仕上げ対象物の仕
上げを行う際に、被塗布物の色調を生かし、それらを今
までとは違った新しい意匠感や質感に仕上げることや、
被塗布物の質感を生かしながら、欠損部等の補修部分を
目立たなく仕上げることができなかった。即ち、打放し
仕上げにおいて、エナメル塗料では、塗料固有の均一色
により覆ったものとなり、コンクリートが用いられるこ
とを隠すものであり、また、クリアー塗料では、欠損の
状態が透けて見えるものであった。For this reason, when finishing an object to be finished such as a structure, the color tone of the object to be applied is utilized to finish them with a new design feeling and texture different from the conventional one.
Repaired portions such as defective portions could not be inconspicuously finished while making use of the texture of the object to be coated. That is, in the exposed finish, the enamel paint was covered with a uniform color unique to the paint, hiding that concrete was used, and the clear paint was such that the state of the defect was seen through.
【０００７】この発明は、上記のような従来技術に存在
する問題点に着目してなされたものである。その目的と
するところは、構築物などの仕上げ対象物の仕上げを行
う際に、被塗布物の色調を生かし、それらを今までとは
違った新しい意匠感や質感に仕上げることや、被塗布物
の質感を生かしながら、欠損部等の補修部分を目立たな
く仕上げることなどを目的とした半隠ぺい性水系塗料組
成物を提供することにある。The present invention has been made by focusing on the problems existing in the prior art as described above. Its purpose is to make use of the color tone of the object to be applied when finishing the object to be finished such as a building, to finish them with a new design feeling and texture different from before, and to finish the object to be applied. It is an object of the present invention to provide a semi-opaque water-based paint composition for the purpose of inconspicuously finishing a repaired portion such as a defective portion while utilizing a texture.
【０００８】[0008]
【課題を解決するための手段】上記の目的を達成するた
めに、請求項１に記載の発明の半隠ぺい性水系塗料組成
物は、合成樹脂エマルションと、フィラ−からなる水系
塗料組成物であって、被塗布物に塗布して得られる塗膜
の膜厚１５０μｍでの隠ぺい率が０．１０〜０．８０で
あることを特徴とするものである。In order to achieve the above object, the semi-opaque aqueous coating composition according to the first aspect of the present invention is an aqueous coating composition comprising a synthetic resin emulsion and a filler. The concealment ratio at a film thickness of 150 μm of a coating film obtained by applying the coating material on an object to be coated is 0.10 to 0.80.
【０００９】請求項２に記載の発明の半隠ぺい性水系塗
料組成物は、請求項１に記載の発明において、さらに無
機系結合剤を含有することを特徴とするものである。請
求項３に記載の発明のは、請求項２に記載の発明におい
て、無機系結合剤がセメントであることを特徴とするも
のである。The semi-opaque aqueous coating composition according to the second aspect of the present invention is characterized in that, in the first aspect, the composition further comprises an inorganic binder. According to a third aspect of the present invention, in the second aspect, the inorganic binder is cement.
【００１０】[0010]
【発明の実施の形態】以下、この発明の実施形態につい
て詳細に説明する。半隠ぺい性水系塗料組成物は、合成
樹脂エマルションと、フィラ−とからなる水系塗料組成
物であって、被塗布物に塗布して得られる塗膜の膜厚１
５０μｍでの隠ぺい率が０．１０〜０．８０のものであ
る。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, embodiments of the present invention will be described in detail. The semi-opaque water-based paint composition is a water-based paint composition comprising a synthetic resin emulsion and a filler.
The opacity at 50 μm is 0.10 to 0.80.
【００１１】まず、合成樹脂エマルションは、半隠ぺい
性水系塗料組成物の主成分であって、乳化重合のような
通常の重合技術で製造できる一般的なものでよい。例え
ば、アクリル樹脂、スチレン樹脂、ウレタン樹脂、シリ
コーン樹脂、フッ素樹脂、エポキシ樹脂などの樹脂より
製造された合成樹脂エマルションなどがあり、合成樹脂
エマルションが乾燥後に透明のフィルムを形成するもの
であればよい。First, the synthetic resin emulsion is a main component of the semi-opaque aqueous coating composition and may be a general one which can be produced by a usual polymerization technique such as emulsion polymerization. For example, there is a synthetic resin emulsion manufactured from a resin such as an acrylic resin, a styrene resin, a urethane resin, a silicone resin, a fluorine resin, and an epoxy resin, and the synthetic resin emulsion may be any as long as the synthetic resin emulsion forms a transparent film after drying. .
【００１２】塗料適性、塗膜の物性、入手の容易性など
からアクリル樹脂、スチレン樹脂より製造されたアクリ
ル系合成樹脂エマルションやアクリルスチレン系合成樹
脂エマルションが好ましく用いられる。この合成樹脂エ
マルションは、水系塗料組成物の用途、性能に応じて適
宜選択して使用される。[0012] An acrylic synthetic resin emulsion or an acrylic styrene synthetic resin emulsion produced from an acrylic resin or a styrene resin is preferably used in view of suitability for paint, physical properties of a coating film, and availability. This synthetic resin emulsion is appropriately selected and used according to the use and performance of the water-based coating composition.
【００１３】また、合成樹脂エマルションに使われる樹
脂のガラス転移温度は、好ましくは０〜７０℃の範囲で
あるが、水系塗料組成物の用途に応じて、適したガラス
転移温度の合成樹脂を選択することができる。The glass transition temperature of the resin used in the synthetic resin emulsion is preferably in the range of 0 to 70 ° C., but a suitable synthetic resin having a glass transition temperature is selected according to the application of the water-based coating composition. can do.
【００１４】なお、アクリル樹脂などの樹脂を有機溶剤
に溶解させたものを用いて、半隠ぺい性の塗料組成物を
得ることもできるが、この場合には、無機系結合材を配
合して用いることは不可能となる。A semi-opaque coating composition can be obtained by dissolving a resin such as an acrylic resin in an organic solvent. In this case, an inorganic binder is used in combination. It becomes impossible.
【００１５】フィラーは、半隠ぺい性水系塗料組成物を
被塗布物の表面、つまり被塗布面に塗布したとき、半隠
ぺい性を発現させるためのものである。このフィラー
は、酸化チタン、炭酸カルシウム、珪砂、クレー、カオ
リン、タルク、珪藻土、ベントナイト、ホワイトカーボ
ン、ガラスビーズ、プラスチックビーズ、水酸化アルミ
ニウムなどが挙げられる。[0015] The filler is for imparting a semi-opaque property when the semi-opaque aqueous coating composition is applied to the surface of the object, that is, the surface to be applied. Examples of the filler include titanium oxide, calcium carbonate, silica sand, clay, kaolin, talc, diatomaceous earth, bentonite, white carbon, glass beads, plastic beads, and aluminum hydroxide.
【００１６】このフィラーの平均粒子径は、１５０μｍ
以下のものであればよいが、半隠ぺい性水系塗料組成物
を被塗布面に塗布したときの仕上りから平均粒子径が５
〜１００μｍのものが好ましい。The average particle size of the filler is 150 μm
The following may be used, but the average particle diameter is 5 based on the finish when the semi-opaque aqueous coating composition is applied to the surface to be applied.
Those having a thickness of from 100 to 100 μm are preferred.
【００１７】水系塗料配合物の隠ぺい性から考えると、
炭酸カルシウム、プラスチックビーズ、ガラスビーズ、
珪藻土、ホワイトカーボンなどは、これ自体が光を透過
する性質があるため、好ましく用いられる。炭酸カルシ
ウムは、一般的に塗料組成物に体質顔料として混合され
るものであり、入手の容易さ、コスト面からよく用いら
れる。Considering the opacity of the water-based paint composition,
Calcium carbonate, plastic beads, glass beads,
Diatomaceous earth, white carbon and the like are preferably used because they themselves have the property of transmitting light. Calcium carbonate is generally mixed with a coating composition as an extender, and is often used in terms of availability and cost.
【００１８】また、プラスチックビーズは、アクリル樹
脂などから工業的につくられるものであるので、光を透
過する性質、粒子径、形状などを任意に変えることがで
きるため、より好ましく用いられる。[0018] Further, since plastic beads are produced industrially from acrylic resin and the like, the properties of transmitting light, the particle diameter, the shape, and the like can be arbitrarily changed, so that they are more preferably used.
【００１９】炭酸カルシウム、ガラスビーズ、プラスチ
ックビーズは、それ自体に着色を施して、使用すること
ができる。この場合、塗布面の仕上りが、着色されたフ
ィラーにより、多彩感のある今までとは違った新しい意
匠感や質感に仕上げることができる。Calcium carbonate, glass beads, and plastic beads can be used by coloring themselves. In this case, the finish of the application surface can be finished with a colorful new and different design and texture by the colored filler.
【００２０】フィラーの含有量は、水系塗料組成物の固
形分中に５〜７０重量％の範囲が好ましい。５重量％よ
り少ない場合には、隠ぺい性がなくなり、欠損部等の補
修部分を目立たなく仕上げることができない。７０重量
％を超える場合には、隠ぺい性を持つために、被塗布物
の質感を生かしながら仕上げることができない。The content of the filler is preferably in the range of 5 to 70% by weight based on the solid content of the aqueous coating composition. When the amount is less than 5% by weight, the concealing property is lost, and the repaired portion such as a defective portion cannot be inconspicuously finished. If it exceeds 70% by weight, it cannot be finished while taking advantage of the texture of the object to be coated, because it has concealing properties.
【００２１】無機系結合剤は、無機系の被塗布面に対す
る接着力向上や、塗膜の有機分の含有量を少なくするこ
とができるため、耐熱性及び難燃性を付与することがで
き、セメント、シリカゾル、リチウムシリケート、アル
ミナゾルなどが挙げられる。The inorganic binder can improve heat resistance and flame retardancy because the inorganic binder can improve the adhesive strength to the surface to be coated and can reduce the organic content of the coating film. Examples include cement, silica sol, lithium silicate, and alumina sol.
【００２２】セメントは、入手の容易さ、コスト面から
より好ましく用いられる。セメントは、水と反応して硬
化する鉱物質の粉末であり、ポルトランドセメント、白
色セメント、混合セメント及び特殊セメントなどに大別
することができ、ポルトランドセメントの中でも普通ポ
ルトランドセメント、早強ポルトランドセメント、超早
強ポルトランドセメント、中庸熱ポルトランドセメント
及び耐硫酸塩ポルトランドセメントがある。Cement is more preferably used in terms of availability and cost. Cement is a powder of a mineral substance that hardens by reacting with water, and can be roughly classified into Portland cement, white cement, mixed cement, special cement, and the like.In Portland cement, ordinary Portland cement, early-strength Portland cement, There are super-high strength Portland cement, moderate heat Portland cement and sulfate resistant Portland cement.
【００２３】混合セメントは、普通ポルトランドセメン
トに高炉スラグ、シリカ質混合材及びフライアッシュを
混合したセメントである。セメントを構成する水硬性化
合物は、けい酸三カルシウム、けい酸ニカルシウム、ア
ルミン酸三カルシウム、鉄アルミン酸四カルシウムがあ
り、この配合割合、添加されるせっこう量、微量成分及
び粉末の粒度によりセメントの種類が決まってくる。The mixed cement is cement obtained by mixing blast furnace slag, siliceous admixture and fly ash with ordinary Portland cement. Hydraulic compounds that constitute cement include tricalcium silicate, dicalcium silicate, tricalcium aluminate, and tetracalcium iron aluminate.The mixing ratio, the amount of gypsum to be added, the trace components and the particle size of the powder are as follows. The type of cement is decided.
【００２４】この発明では、任意の種類のセメントを用
いることができる。容易に入手できる普通ポルトランド
セメントが好ましく用いられ、また、塗料の調色性が必
要な場合には、白色セメントが好ましい。セメントを結
合材として添加した場合、セメント自体にも隠ぺい力が
あるのでフィラーの添加の量を少なくすることができ
る。In the present invention, any kind of cement can be used. A readily available ordinary Portland cement is preferably used, and a white cement is preferred when the toning of the paint is required. When cement is added as a binder, cement itself has a hiding power, so that the amount of filler added can be reduced.
【００２５】セメントの含有量は、水系塗料組成物の固
形分中に１０〜３５重量％の範囲が好ましい。１０重量
％より少ない場合には、無機系の被塗布面に対する接着
力向上や、塗膜の耐熱性及び難燃性を付与することがで
きない。また、３５重量％を超える場合には、隠ぺい性
を持つために、被塗布物の質感を生かしながら仕上げる
ことができない。The content of cement is preferably in the range of 10 to 35% by weight based on the solid content of the water-based coating composition. When the amount is less than 10% by weight, it is impossible to improve the adhesive strength to the surface to be coated with the inorganic material and to impart the heat resistance and flame retardancy of the coating film. On the other hand, if it exceeds 35% by weight, it cannot be finished while taking advantage of the texture of the object to be coated, because it has concealing properties.
【００２６】シリカゾルは、ニ酸化けい素（ＳｉＯ2）
を主成分としたもので、微量成分として酸化ナトリウム
などが含まれ、透明な液体である。リチウムシリケート
はニ酸化けい素（ＳｉＯ2）と酸化リチウム（Ｌｉ2Ｏ）
を主成分とするものであり、アルミナゾルはアルミナ
（Ａｌ2Ｏ3）を主成分とするものである。これら無機系
結合材は、乾燥後に透明になるものであればよく、合成
樹脂エマルションとの混和性がよいものが好ましく用い
られる。その添加量は、無機系の被塗布面に対する接着
力向上や、塗膜の耐熱性及び難燃性などの物性を得られ
る範囲まで添加することができ、水系塗料組成物の固形
分中に５〜３０重量％の範囲になる添加量が好ましい。The silica sol is made of silicon dioxide (SiO 2 )
Is a transparent liquid containing sodium oxide and the like as trace components. Lithium silicate is composed of silicon dioxide (SiO 2 ) and lithium oxide (Li 2 O)
And the alumina sol is mainly composed of alumina (Al 2 O 3 ). Any of these inorganic binders may be used as long as they become transparent after drying, and those having good miscibility with the synthetic resin emulsion are preferably used. The amount thereof can be added to the extent that physical properties such as heat resistance and flame retardancy of the coating film can be improved, and the solid content of the water-based coating composition is 5%. An addition amount in the range of ３０30% by weight is preferable.
【００２７】この発明の半隠ぺい性水系塗料組成物は、
上記以外のその他添加剤として、分散剤、湿潤剤などと
して用いられる界面活性剤や造膜助剤、防凍剤などとし
て用いられる高沸点溶剤、増粘剤、粘性調整剤、消泡
剤、ｐＨ調整剤、防腐剤、防黴剤、防藻剤等のような一
般に塗料に配合されている成分を使用することができ
る。The semi-opaque aqueous coating composition of the present invention comprises:
Other additives other than the above, such as surfactants used as dispersants and wetting agents, film-forming aids, high-boiling solvents used as antifreezing agents, thickeners, viscosity modifiers, defoamers, and pH adjustment Ingredients generally blended in paints, such as agents, preservatives, fungicides, anti-algal agents, etc., can be used.
【００２８】さらに、必要に応じて着色顔料として無
機、有機系顔料及びその両方を加えることが可能であ
り、それらは、耐候性のよいものがよく用いられる。以
上のように調製された半隠ぺい性水系塗料組成物は、被
塗布物の表面に塗布されることにより塗膜が形成され
る。この塗膜は、被塗布物の表面を一定の隠ぺい率で隠
ぺいする。Further, if necessary, inorganic and organic pigments and both of them can be added as coloring pigments, and those having good weather resistance are often used. The semi-opaque aqueous coating composition prepared as described above forms a coating film by being applied to the surface of an object to be applied. This coating film conceals the surface of the object to be coated at a certain concealment rate.
【００２９】そこで、隠ぺい率について説明する。ここ
でいう隠ぺい率とは、ＪＩＳ−Ｋ５５８２に規定された
測定方法に準じて測定されたものである。これは、ＪＩ
Ｓ−Ｋ５４００規定の白地及び黒地の隠ぺい率試験紙に
それぞれ１５０μｍの膜厚で塗膜を形成させ、標準状態
で４８時間乾燥させる。その後、ＪＩＳ−Ｋ５４００に
規定された、視感反射率を測定する。視感反射率は、Ｊ
ＩＳ−Ｚ８７２２に規定する装置を用い、塗膜の明るさ
を測定するものである。それにより下記の計算式で、隠
ぺい率を算出する。Therefore, the concealment ratio will be described. Here, the concealment ratio is measured according to a measurement method specified in JIS-K5582. This is JI
A coating film having a film thickness of 150 μm was formed on each of test papers having an opacity ratio of a white background and a black background specified by S-K5400, and dried under standard conditions for 48 hours. Thereafter, the luminous reflectance specified in JIS-K5400 is measured. Luminous reflectance is J
The brightness of the coating film is measured using an apparatus specified in IS-Z8722. Thereby, the concealment ratio is calculated by the following formula.
【００３０】隠ぺい率＝黒地での視感反射率／白地での
視感反射率この発明において、半隠ぺい性水系塗料組成
物の塗布厚が１５０μｍでの隠ぺい率を０．１０〜０．
８０の範囲としている。隠ぺい率が０．８０より大きい
場合には、被塗布物の色調を生かした仕上がりや質感を
生かしながら、欠損部等の補修部分を目立たなく仕上げ
ることができず、エナメル塗料と変わらない仕上げとな
ってしまう。これとは逆に、隠ぺい率が０．１０より小
さい場合には、被塗布物の色調を表してしまい、艶消し
クリヤーより、少しぼやけた仕上がりとなってしまい目
的を達成することができない。Opacity = luminous reflectance on a black background / luminous reflectance on a white background In the present invention, the opacity at a coating thickness of the semi-opaque aqueous coating composition of 150 μm is 0.10 to 0.1.
The range is 80. If the concealment ratio is greater than 0.80, the repaired parts such as defective parts cannot be finished inconspicuously while making use of the finish and texture utilizing the color tone of the object to be applied, and the finish is the same as enamel paint Would. Conversely, if the concealment ratio is smaller than 0.10, the color tone of the object to be coated is expressed, and the finish becomes slightly more blurred than the matte clear, and the object cannot be achieved.
【００３１】この隠ぺい率のより好ましい範囲として
は、０．１０〜０．６５であり、この場合には、被塗布
物の色調を生かし、それらを今までとは違った新しい意
匠感や質感に仕上げ、被塗布物の質感を生かしながら、
欠損部等の補修部分を目立たなく仕上げることができ
る。A more preferable range of the concealment ratio is 0.10 to 0.65. In this case, the color tone of the object to be coated is utilized to obtain a new design and texture different from the conventional ones. Finish, while taking advantage of the texture of the object
Repaired parts such as missing parts can be finished inconspicuously.
【００３２】また、被塗布物の色調が、水系塗料組成物
の色調と異なる場合においては、隠ぺい率を０．１０〜
０．２０の範囲に設定することにより、被塗布物の色調
と水系塗料組成物の色調が程よく合い、より一層今まで
とは違った新しい意匠感や質感に仕上げることができ
る。When the color tone of the object to be coated is different from the color tone of the water-based coating composition, the concealment ratio is 0.10 to 0.10.
By setting it in the range of 0.20, the color tone of the object to be coated and the color tone of the water-based coating composition moderately match, and it is possible to achieve a new design and texture different from before.
【００３３】被塗布物の色調が、水系塗料組成物の色調
と同系色の場合においては、０．２５〜０．６５の範囲
に設定することにより、欠損部等の補修部分をまったく
目立たないように仕上げることができる。When the color tone of the object to be coated is similar to the color tone of the water-based coating composition, by setting the range of 0.25 to 0.65, the repaired portion such as a defective portion can be made inconspicuous at all. Can be finished.
【００３４】また、半隠ぺい性水系塗料組成物を塗布し
得られた塗膜表面に、クリヤー塗料を塗布することによ
り、塗膜表面の耐候性を向上させ、汚れ防止を図るなど
塗膜表面の保護をすることができる。さらに、クリヤー
塗料の種類を変えることによって、塗膜表面に艶を与え
たり、逆に艶を消すことができる。Further, a clear paint is applied to the surface of the coating film obtained by applying the semi-opaque water-based coating composition to improve the weather resistance of the coating film surface and prevent stains, for example, to prevent contamination. Can provide protection. Further, by changing the type of the clear paint, it is possible to impart gloss to the surface of the coating film or to reverse the gloss.
【００３５】以上のように、この実施形態によれば次の
ような効果が発揮される。 ・ 合成樹脂エマルションと、フィラ−とからなる水系
塗料組成物であって、塗膜の膜厚１５０μｍでの隠ぺい
率が０．１０〜０．８０であることにより、被塗布物の
色調を生かし、それらを今までとは違った新しい意匠感
や質感に仕上げることができる。また、被塗布物の質感
を生かしながら、欠損部等の補修部分を目立たなく仕上
げることもできる。As described above, according to this embodiment, the following effects are exhibited. An aqueous coating composition comprising a synthetic resin emulsion and a filler, wherein the opacity at a film thickness of 150 μm is 0.10 to 0.80, making use of the color of the object to be coated, They can be finished with new designs and textures different from before. In addition, a repaired portion such as a defective portion can be finished inconspicuously while utilizing the texture of the object to be coated.
【００３６】・ フィラーの平均粒子径が５〜１００μ
ｍの範囲であることにより、被塗布面に塗布したときの
仕上りが、それらを今までとは違った新しい意匠感や質
感に仕上げることができる。また、被塗布物の質感を生
かしながら、欠損部等の補修部分を目立たなく仕上げる
こともできる。The average particle diameter of the filler is 5 to 100 μm
When it is within the range of m, the finish when applied to the surface to be applied can be finished with a new design feeling and texture different from the past. In addition, a repaired portion such as a defective portion can be finished inconspicuously while utilizing the texture of the object to be coated.
【００３７】・ フィラーに着色を施して、使用するこ
とにより、多彩感のある今までとは違った新しい意匠感
や質感に仕上げることができる。 ・ 被塗布物の色調が、水系塗料組成物の色調と異なる
場合においては、隠ぺい率を０．１０〜０．２０の範囲
に設定することにより、被塗布物の色調と水性塗料組成
物の色調が程よく合い、より一層今までとは違った新し
い意匠感や質感に仕上げにすることができる ・ 被塗布物の色調が、水系塗料組成物の色調と同系色
の場合においては、０．２５〜０．６５の範囲に設定す
ることにより、欠損部等の補修部分をまったく目立たな
いように仕上げることができる。By coloring and using the filler, it is possible to finish it with a variety of new designs and textures different from before. When the color tone of the object to be coated is different from the color tone of the water-based coating composition, the hiding ratio is set in the range of 0.10 to 0.20, so that the color tone of the object to be coated and the color tone of the aqueous coating composition are adjusted. Fits well and can be finished with a new design and texture different from before.-When the color tone of the object is similar to the color tone of the water-based paint composition, By setting the value in the range of 0.65, a repaired portion such as a defective portion can be finished so as not to be conspicuous at all.
【００３８】・ 無機系結合剤を添加することにより、
無機系の被塗布面に対する塗膜の接着力向上や、塗膜の
有機分の含有量を少なくすることができるため、塗膜の
耐熱性及び難燃性を付与することができる。By adding an inorganic binder,
Since the adhesion of the coating film to the inorganic coating surface can be improved and the organic content of the coating film can be reduced, the heat resistance and flame retardancy of the coating film can be imparted.
【００３９】・ 無機系結合剤がセメントであることに
より、合成樹脂エマルションの添加量が少なくなり、セ
メント自体に隠ぺい性があるため、フィラーの添加の量
も少なくすることができる。When the inorganic binder is cement, the amount of the synthetic resin emulsion added is reduced, and the cement itself has concealing properties, so that the amount of the filler added can be reduced.
【００４０】[0040]
【実施例】以下、前記実施形体を具体化した実施例につ
いて、詳細に説明する。合成樹脂エマルションは、アク
リル系合成樹脂エマルションを用い、固形分が４５重量
％である。フィラーとしては炭酸カルシウム、プラスチ
ックビーズを使用した。炭酸カルシウムは、平均粒子径
が５〜５０μｍで、無着色の白色ものであり、プラスチ
ックビーズは、アクリル樹脂系のもので、平均粒子径が
３０〜１００μｍのものである。色調は、白色、赤色及
び黒色のものを用いた。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, embodiments of the present invention will be described in detail. The synthetic resin emulsion uses an acrylic synthetic resin emulsion and has a solid content of 45% by weight. Calcium carbonate and plastic beads were used as fillers. Calcium carbonate has an average particle diameter of 5 to 50 μm and is uncolored white, and the plastic beads are of an acrylic resin type and have an average particle diameter of 30 to 100 μm. The color tone used was white, red and black.
【００４１】無機系結合材としては、コロイダルシリ
カ、普通ポルトランドセメントを用いた。その他の成分
としては、分散剤、湿潤剤、造膜助剤、増粘剤、粘性調
整剤、消泡剤を使用した。 実施例１ 合成樹脂エマルション ４０．０重量％ プラスチックビーズ（白色） １０．０重量％ 炭酸カルシウム ２５．０重量％ その他の成分 １０．０重量％ 水 １５．０重量％ 合計 １００．０重量％ 実施例２ 合成樹脂エマルション ４０．０重量％ プラスチックビーズ（赤色） １５．０重量％ 炭酸カルシウム ２５．０重量％ その他の成分 ８．０重量％ 水 １２．０重量％ 合計 １００．０重量％ 実施例３ 合成樹脂エマルション ３０．０重量％ コロイダルシリカ １０・０重量％ プラスチックビーズ（黒色） ５．０重量％ プラスチックビーズ（白色） １０．０重量％ 炭酸カルシウム ３０．０重量％ その他の成分 ６．０重量％ 水 ９．０重量％ 合計 １００．０重量％ 実施例４ 合成樹脂エマルション ８５．０重量％ 普通ポルトランドセメント ８．８重量％ 炭酸カルシウム ５．３重量％ その他の成分 ０．９重量％ 合計 １００．０重量％ 実施例５ 合成樹脂エマルション ８０．０重量％ 普通ポルトランドセメント １２．３重量％ 炭酸カルシウム ７．４重量％ その他の成分 ０．３重量％ 合計 １００．０重量％ 実施例６ 合成樹脂エマルション ６７．０重量％ 普通ポルトランドセメント ２０．５重量％ 炭酸カルシウム １２．３重量％ その他の成分 ０．２重量％ 合計 １００．０重量％ 比較例１ 一般市販品 エナメル塗料（白色） 比較例２ 一般市販品 クリヤー塗料 比較例３ 一般市販品 艶消しクリヤー塗料 実施例１〜実施例６の半隠ぺい性水系塗料組成物と比較
例１〜比較例３の塗料を白地及び黒地の隠ぺい率試験紙
にそれぞれ１５０μｍの膜厚で塗膜を形成させ、標準状
態で４８時間乾燥させる。その後、ＪＩＳ−Ｋ５４００
に規定された、視感反射率を測定する。視感反射率は、
ＪＩＳ−Ｚ８７２２に規定する装置を用い、塗膜の明る
さを測定し、隠ぺい率を求めた。As the inorganic binder, colloidal silica and ordinary Portland cement were used. As other components, a dispersant, a wetting agent, a film forming aid, a thickener, a viscosity modifier, and an antifoaming agent were used. Example 1 Synthetic resin emulsion 40.0% by weight Plastic beads (white) 10.0% by weight Calcium carbonate 25.0% by weight Other components 10.0% by weight Water 15.0% by weight Total 100.0% by weight 2 Synthetic resin emulsion 40.0% by weight Plastic beads (red) 15.0% by weight Calcium carbonate 25.0% by weight Other components 8.0% by weight Water 12.0% by weight Total 100.0% by weight Example 3 Synthesis Resin emulsion 30.0% by weight Colloidal silica 10.0% by weight Plastic beads (black) 5.0% by weight Plastic beads (white) 10.0% by weight Calcium carbonate 30.0% by weight Other components 6.0% by weight Water 9.0% by weight Total 100.0% by weight Example 4 Synthetic resin emulsion 85.0% by weight Ordinary Portland Cement 8.8% by weight Calcium carbonate 5.3% by weight Other components 0.9% by weight Total 100.0% by weight Example 5 Synthetic resin emulsion 80.0% by weight Ordinary Portland cement 12.3% by weight Calcium carbonate 7. 4% by weight Other components 0.3% by weight Total 100.0% by weight Example 6 Synthetic resin emulsion 67.0% by weight Ordinary Portland cement 20.5% by weight Calcium carbonate 12.3% by weight Other components 0.2% by weight % Total 100.0% by weight Comparative example 1 General commercial product Enamel paint (white) Comparative example 2 General commercial product Clear paint Comparative example 3 General commercial product Matte clear paint Semi-opaque aqueous paint composition of Examples 1 to 6 The coating material of Comparative Example 1 to Comparative Example 3 was formed on a white background and a black background opacity test paper with a film thickness of 150 μm, respectively. In a quasi-state to be dried for 48 hours. After that, JIS-K5400
The luminous reflectance, as defined in, is measured. The luminous reflectance is
Using an apparatus specified in JIS-Z8722, the brightness of the coating film was measured, and the obscuration ratio was determined.
【００４２】その結果を表１にまとめて示す。The results are summarized in Table 1.
【００４３】[0043]
【表１】 黒色である被塗布面に、実施例１〜実施例３の水性塗料
組成物と比較例１のエナメル塗料及び比較例４の半艶ク
リヤー塗料をそれぞれスプレーガンを用い、塗布厚み１
５０μｍ程度に塗装し、塗布面の仕上りを比較した。[Table 1] The water-based coating compositions of Examples 1 to 3, the enamel coating of Comparative Example 1, and the semi-gloss clear coating of Comparative Example 4 were each applied to a black coating surface by using a spray gun to give a coating thickness of 1
The coating was performed to a thickness of about 50 μm, and the finish of the coated surface was compared.
【００４４】表１より隠ぺい率が０．１０〜０．８０の
範囲の水系塗料組成物であることにより、実施例１で
は、被塗布面の黒色が透けているために、全体として灰
色の仕上がりとなり、実施例２では、茶系色となり、ま
た、実施例３においては、濃灰色になり、被塗布物の色
調を生かした仕上がりとなった。According to Table 1, the opaque ratio of the water-based coating composition is in the range of 0.10 to 0.80. Thus, in Example 2, the color became a brownish color, and in Example 3, the color became dark gray, and the finish took advantage of the color tone of the object to be coated.
【００４５】また、実施例１〜３半隠ぺい性水系塗料組
成物を塗布した塗布面を近くで観察したところ、プラス
チックビーズが細かい点にあることが確認でき、それは
今までの色調をいかしながら、違った意匠感や質感に仕
上げにすることができた。In addition, close observation of the coated surface on which the semi-opaque aqueous coating composition was applied in Examples 1 to 3 confirmed that the plastic beads were at fine points. I was able to finish it with a different design and texture.
【００４６】また、実施例３では、実施例１、実施例２
に比べ半隠ぺい性水系塗料組成物の固形分中の有機分を
低減することができた。そのことにより塗膜の耐熱性及
び難燃性を向上させることができた。In the third embodiment, the first and second embodiments are used.
As compared with the above, the organic component in the solid content of the semi-opaque aqueous coating composition could be reduced. As a result, the heat resistance and flame retardancy of the coating film could be improved.
【００４７】これに対して比較例１の塗料では、隠ぺい
率が０．９５であるため、被塗布面の黒色がまったく感
じられないぐらい、白色に仕上がり、塗布前と色調が違
うものに変わった。比較例３の塗料では、艶が消えた黒
色面に仕上がり、隠ぺい率が０．０４であるために塗布
前と色調の変化は感じられない。On the other hand, in the paint of Comparative Example 1, the opacity was 0.95, so that the surface to be coated was finished in white so that the black color was not felt at all, and the color tone was different from that before coating. . The paint of Comparative Example 3 was finished to a matte black surface and had an opacity of 0.04, so that no change in color tone was felt before and after application.
【００４８】次に、コンクリート面に対して、実施例４
〜実施例６までの水系塗料組成物と比較例１のエナメル
塗料、比較例２のクリヤー塗料及び比較例３の艶消しク
リヤー塗料をウールローラー（大塚刷毛製造株式会社製
無泡ローラー）を用い、塗布厚み１５０μｍ程度に塗
装した。このコンクリート面は、モルタルにより欠損部
分の補修が行われているために、補修部分が色違いとな
って残っている。Next, Example 4 was applied to the concrete surface.
The water-based coating composition of Example 6 to the enamel coating of Comparative Example 1, the clear coating of Comparative Example 2 and the matte clear coating of Comparative Example 3 were coated on a wool roller (foamless roller manufactured by Otsuka Brush Co., Ltd.). It was applied to a coating thickness of about 150 μm. Since the defective portion is repaired by mortar on the concrete surface, the repaired portion remains in a different color.
【００４９】実施例４〜実施例６では、どれもモルタル
により補修部分の跡がわからない仕上がりとなり、コン
クリート面独特な仕上がりを保っていた。これは、半隠
ぺい性水系塗料組成物の隠ぺい率が０．２５〜０．６５
の範囲であり、コンクリート面と補修部分との色差を小
さくすることができたため、補修部分が目立ちにくくな
ったのである。In all of Examples 4 to 6, the mortar resulted in a finish with no trace of the repaired part, and the finish unique to the concrete surface was maintained. This is because the semi-opaque aqueous coating composition has an opacity of 0.25 to 0.65.
The color difference between the concrete surface and the repaired portion could be reduced, and the repaired portion became less noticeable.
【００５０】これに対し、比較例１の塗料では、隠ぺい
率が０．９５のため、コンクリート面が白色に仕上が
り、コンクリート面独特な仕上がりを失ってしまった
が、コンクリート面と補修部分の違いを確認することが
できなかった。比較例２のクリヤー塗料では、隠ぺい率
が０．０１のため、モルタルにより補修部分がはっきり
と確認できた。また、コンクリート面が艶を有してしま
い、これもまた、コンクリート面独特な仕上がりを失っ
てしまった。また、比較例３の艶消しクリヤーにおいて
は、比較例２とは違って、コンクリート面に艶を持たす
ことはなく仕上がったが、補修部分を確認することがで
きた。これは、この艶消しクリヤーの隠ぺい率が０．０
４であり、コンクリート面と補修部分との色違いを隠す
ほどの色差を小さくすることができなかったためであ
る。On the other hand, in the paint of Comparative Example 1, since the opacity was 0.95, the concrete surface was finished in white and lost the unique finish of the concrete surface. I could not confirm. Since the clear coating of Comparative Example 2 had an opacity of 0.01, the repaired portion could be clearly confirmed by mortar. In addition, the concrete surface became glossy, which also lost the unique finish of the concrete surface. Also, in the matte clear of Comparative Example 3, unlike the Comparative Example 2, the concrete surface was finished without gloss, but the repaired portion could be confirmed. This is because the hiding ratio of this matte clear is 0.0
This is because the color difference could not be so small as to hide the color difference between the concrete surface and the repaired part.
【００５１】即ち、打放し仕上げにおいて、エナメル塗
料では、塗料固有の均一色により覆ったものとなり、コ
ンクリートが用いられることを隠すものであり、また、
クリアー塗料では、欠損の状態が透けて見えるものであ
った。That is, in the exposed finish, the enamel paint is covered with a uniform color unique to the paint, which hides the use of concrete.
With the clear paint, the state of the defect was seen through.
【００５２】次に、前記実施形態から把握できる技術的
思想について以下に記載する。 ・ 前記フィラーの平均粒子径が５〜１００μｍの範囲
であることを特徴とする請求項１〜請求項３のいずれか
に記載の半隠ぺい性水系塗料組成物。Next, the technical ideas that can be grasped from the above embodiment will be described below. The semi-opaque aqueous coating composition according to any one of claims 1 to 3, wherein the average particle diameter of the filler is in the range of 5 to 100 µm.
【００５３】このような半隠ぺい性水系塗料組成物によ
れば、被塗布物の表面を今までとは違った新しい意匠感
や質感に仕上げることができる。また、被塗布物の質感
を生かしながら、欠損部等の補修部分を目立たなく仕上
げることもできる。According to such a semi-opaque water-based coating composition, the surface of the object to be coated can be finished with a new design and texture different from before. In addition, a repaired portion such as a defective portion can be finished inconspicuously while utilizing the texture of the object to be coated.
【００５４】・ 前記フィラーは着色を施したものであ
るする請求項１〜請求項３のいずれかに記載の半隠ぺい
性水系塗料組成物。このような半隠ぺい性水系塗料組成
物によれば、多彩感のある今までとは違った新しい意匠
感や質感に仕上げにすることができる。The semi-opaque aqueous coating composition according to any one of claims 1 to 3, wherein the filler is colored. According to such a semi-opaque water-based coating composition, it is possible to give a variety of finishes to a new design and texture different from before.
【００５５】・ 被塗布物の色調と組成物の色調が異な
る場合において、隠ぺい率を０．１０〜０．２０にする
ことを特徴とする請求項１〜請求項３のいずれかに記載
の半隠ぺい性水系塗料組成物。The half-haze according to any one of claims 1 to 3, wherein the hiding ratio is set to 0.10 to 0.20 when the color tone of the object to be coated and the color tone of the composition are different. Hiding water-based coating composition.
【００５６】このようによれば、被塗布物の色調と水系
塗料組成物の色調が程よく合い、より一層今までとは違
った新しい意匠感や質感に仕上げにすることができる。 ・ 被塗布物の色調と組成物の色調が同系色の場合にお
いて、隠ぺい率を０．２５〜０．６５にすることを特徴
とする請求項１〜請求項３のいずれかに記載の半隠ぺい
性水系塗料組成物。According to the above, the color tone of the object to be coated and the color tone of the water-based coating composition moderately match, and it is possible to achieve a finish with a new design and texture different from before. The semi-opaque according to any one of claims 1 to 3, wherein the opacity is set to 0.25 to 0.65 when the color tone of the object to be coated and the color tone of the composition are similar colors. Water-based coating composition.
【００５７】このようによれば、欠損部等の補修部分を
まったく目立たないように仕上げることができる。 ・ 請求項１〜請求項３のいずれかに記載の半隠ぺい性
水系塗料組成物を被塗布物に塗布して得られた塗膜表面
に、クリヤー塗料を塗布することを特徴とした塗装方
法。According to this, it is possible to finish the repaired portion such as the defective portion so as not to be conspicuous at all. A coating method characterized by applying a clear coating to the surface of a coating film obtained by applying the semi-opaque aqueous coating composition according to any one of claims 1 to 3 to an object to be coated.
【００５８】この塗装方法によれば、意匠感や質感を保
ちつつ、塗膜表面の耐候性を向上させ、汚れ防止を図る
など塗膜表面の保護をすることができ、またクリヤー塗
料の種類を変えることによって、塗膜表面に艶を与えた
り、逆に艶を消すことができる。According to this coating method, it is possible to protect the coating film surface by improving the weather resistance of the coating film surface and preventing stains while maintaining the sense of design and texture, and the type of clear coating material can be improved. By changing it, it is possible to give gloss to the surface of the coating film or to reverse it.
【００５９】[0059]
【発明の効果】この発明は、以上のように構成されてい
るため、次のような効果を奏する。請求項１に記載の発
明の半隠ぺい性水系塗料組成物によれば、構築物などの
仕上げ対象物の仕上げを行う際に、被塗布物の色調を生
かし、それらを今までとは違った新しい意匠感や質感に
仕上げることや、被塗布物の質感を生かしながら、その
欠損部等の補修部分を目立たなく仕上げることができ
る。The present invention is configured as described above, and has the following effects. According to the semi-opaque water-based coating composition of the invention according to claim 1, when finishing an object such as a construction, the color tone of the object to be applied is utilized, and a new design different from the conventional one is used. It is possible to finish a repaired portion such as a defective portion while making it feel and texture and making use of the texture of the object to be coated.
【００６０】請求項２に記載の発明の半隠ぺい性水系塗
料組成物によれば、請求項１に記載の発明の効果に加
え、無機系の被塗布面に対する接着力向上や、塗膜の耐
熱性及び難燃性を付与することができる。According to the semi-opaque aqueous coating composition of the invention described in claim 2, in addition to the effects of the invention described in claim 1, it is possible to improve the adhesive strength to the surface to be coated with an inorganic material and to improve the heat resistance of the coating film. And flame retardancy.
【００６１】請求項３に記載の発明の半隠ぺい性水系塗
料組成物によれば、請求項２に記載の発明の効果に加
え、セメント自体にも隠ぺい力があるのでフィラー類の
添加の量も少なくすることができる。According to the semi-opaque aqueous coating composition of the third aspect of the present invention, in addition to the effect of the second aspect of the present invention, the cement itself has a concealing power. Can be reduced.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 有賀 秀仁 岐阜県各務原市松本町２丁目457番地 菊 水化学工業 株式会社内 Ｆターム(参考） 4J038 AA011 AA012 CC021 CC022 CC061 CC062 CD091 CD092 CG141 CG142 CJ031 CJ032 DB001 DB002 DG031 DG032 DL031 DL032 HA001 HA002 HA161 HA162 HA166 HA286 HA441 HA442 HA446 HA451 HA452 HA486 HA491 HA492 HA526 HA536 HA556 HA566 KA08 MA08 MA10 MA13 NA01 NA14 NA15 PA18 PB05 PB12 PC04 ────────────────────────────────────────────────── ─── Continuing on the front page (72) Inventor Hidehito Ariga 2-457 Matsumotocho, Kakamigahara-shi, Gifu Kikusui Chemicals Co., Ltd. F-term (reference) 4J038 AA011 AA012 CC021 CC022 CC061 CC062 CD091 CD092 CG141 CG142 CJ031 CJ032 DB001 DB002 DG031 DG032 DL031 DL032 HA001 HA002 HA161 HA162 HA166 HA286 HA441 HA442 HA446 HA451 HA452 HA486 HA491 HA492 HA526 HA536 HA556 HA566 KA08 MA08 MA10 MA13 NA01 NA14 NA15 PA18 PB05 PB12 PC04
Claims (3)
らなる水系塗料組成物であって、被塗布物に塗布して得
られる塗膜の膜厚１５０μｍでの隠ぺい率が０．１０〜
０．８０であることを特徴とする半隠ぺい性水系塗料組
成物。1. A water-based coating composition comprising a synthetic resin emulsion and a filler, wherein a coating film obtained by coating an object to be coated has an opacity of 0.10 to 150 μm in film thickness.
The semi-opaque water-based coating composition having a ratio of 0.80.
徴とする請求項１に記載の半隠ペい性水系塗料組成物。2. The semi-opaque aqueous coating composition according to claim 1, further comprising an inorganic binder.
を特徴とする請求項２に記載の半隠ぺい性水系塗料組成
物。3. The semi-opaque aqueous coating composition according to claim 2, wherein the inorganic binder is cement.