JP2001052328A - Maganetic recording medium and magnetic recording apparatus - Google Patents

Abstract

PROBLEM TO BE SOLVED: To prevent a lubricant from scattering because of high-speed rotation for a long time under high temperatures and high humidity by including two kinds of perfluoropolyether of different structures each having an average- number molecular weight in a specific range into a lubrication layer set continuously with a recording layer and a protecting layer on a nonmagnetic substrate. SOLUTION: The recording medium includes in a lubrication layer a perfluoropolyether: PFPT (I) expressed by a formula I and having an average- number molecular weight exceeding 5000 and not larger than 10000, and a perfluoropolyether: PFPT (II) expressed by a formula II and having an average- number molecular weight of 500-10000. In the formulae, (m) is an integer of 1-4 and (n) is an integer. The A in the formula II is an aromatic cycle with a hydrophilic group. The A is preferably a phenyl group with a hydrophilic group, particularly a group expressed by a formula III. A weight ratio is preferably set to be PFPT (I): PFPT (II)=1:20-20:1, and a film thickness of the lubrication layer is preferably set to be 0.1-10 nm. With no lubricant scattered, no stiction brought about when the medium is left for a long time after rotated at high speed.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a magnetic recording medium having a lubricating layer excellent in long-term stability, durability, and head suction resistance, and a magnetic recording apparatus using the magnetic recording medium.

[0002]

2. Description of the Related Art A disk-shaped magnetic recording medium (hereinafter, may be simply referred to as a "disk"), which is a typical example of a high-density magnetic recording medium used in the information industry and the like, usually has a magnetic recording layer. By forming a magnetic metal or its alloy layer on a non-magnetic substrate by plating, vapor deposition, sputtering or the like. Currently, generally used magnetic recording media have information recording / recording when the drive is stopped.
A reproducing head (hereinafter, sometimes simply referred to as a "head") comes into contact with the disk, and when driven, the head flies above the disk to record / reproduce information.
A start / stop (CSS) method is used.
In this method, since the head and the disk are slid at high speed during actual use, there is a problem that the disk is damaged by abrasion and the magnetic characteristics are deteriorated.

As a method of solving such a defect, a protective layer is provided on the magnetic layer of the disk, and a lubricating layer is further provided on the protective layer to reduce static / dynamic friction at the time of contact sliding as much as possible, thereby reducing wear. (CSS characteristics) has been improved. In this case, as the lubricating layer, generally,
A perfluoropolyether compound, which is a liquid lubricant, is used, and a lubricating layer is usually formed by applying the compound to the disk surface. As the perfluoropolyether compound, for example, (A-O-A'-O)
_x - (A, A 'is CF ₂ or C ₂ F ₄₎ (manufactured by Ausimont) skeleton, Demnum lubricant :-( CF ₂ CF ₂ CF ₂ O) _p
A skeleton (manufactured by Daikin Industries, Ltd.) or a crytox-based lubricant:-(CF ₂ CF (CF ₃ ) O) _q -a skeleton having a skeleton (manufactured by DuPont) or the like and having -OH or the like at a terminal. (Where x, p, and q in the formula represent integers of 1 or more). In addition, those in which an alkyl group containing a hetero atom, a fluorine-substituted alkyl group, or an aromatic group is further bonded as a terminal group to such a perfluoropolyether-based molecular skeleton are widely used. The bond with the layer surface is strengthened, and excellent durability is provided.

In recent years, the flying height of the head on the disk has been required to be lower in order to obtain a higher recording density. In order to avoid contact between the disk and the head during start-up, the disk surface must be as smooth as possible. Is required. However, if the disk surface is smoothed, a sticking phenomenon (stiction) is likely to occur between the head and the disk, so that the head may stick to the disk and become inoperable. In particular, when the drive is stopped for a long time under high humidity, this stiction is accelerated.

In order to avoid this phenomenon, it has been proposed to use one or more kinds of perfluoropolyethers having different terminal functional groups (JP-A-9-282624 and JP-A-10-149527).

[0006]

However, conventional lubricants have some effect in suppressing stiction, but under severe conditions such as contact sliding under high temperature and high humidity, the lubricating properties of conventional lubricants are low. Stiction and abrasion damage tended to occur due to the decrease, and the reliability was poor.

The present invention solves the above-mentioned conventional problems, and does not cause a problem of a decrease in lubricity even when the rotor is rotated at a high speed under a high temperature and a high humidity for a long period of time. It is an object of the present invention to provide a magnetic recording medium having no magnetic recording medium and a magnetic recording device using the magnetic recording medium.

[0008]

The magnetic recording medium of the present invention comprises a recording layer, a protective layer and a lubricating layer provided in this order on a non-magnetic substrate. I), having a number average molecular weight of 500 to 100
00 and the following general formula (I
And perfluoropolyether having a number average molecular weight of 500 to 10,000.

[0009]

Embedded image

[0010]

Embedded image

That is, the inventors of the present invention have conducted intensive studies to prevent a decrease in lubricity under high temperature and high humidity, and as a result, have a specific molecular weight as a lubricant and a specific terminal functional group. By using two types of perfluoropolyethers in combination, specifically, at the terminal, a perfluoropolyether having two or more hydroxyl groups at two or less carbon atoms from the terminal and an aromatic ring having a hydrophilic group at the terminal It has been found that the combined use of a perfluoropolyether having the following effects can suppress stiction when left for a long period after CSS under high temperature and high humidity, and completed the present invention.

In the general formula (II), A is preferably a phenyl group having a hydrophilic group, particularly preferably a group represented by the following structural formula (III).

[0013]

Embedded image

In the present invention, m in the general formula (I) and / or (II) is preferably 1 or 2, and the perfluoropolyether represented by the general formula (I) and the general formula (II) The mixing ratio (I) :( II) with the perfluoropolyether represented by is preferably 1:20 to 20: 1 by weight.

In the present invention, the thickness of the lubricating layer formed of such a lubricant is preferably 0.1 to 10 nm. Preferably, the protective layer is made of amorphous carbon.

The magnetic recording apparatus of the present invention has a disk-shaped magnetic recording medium of the present invention, a rotating means for rotating the magnetic recording medium, and a head for recording / reproducing information. The magnetic recording medium is characterized in that the number of revolutions of the magnetic recording medium during information recording / reproduction is 10,000 rpm or more, and even if information is recorded / reproduced by such high-speed rotation, the lubricating layer of the magnetic recording medium is stable for a long time. Good recording / reproduction can be performed because of its excellent properties, durability and head absorption resistance.

[0017]

Embodiments of the present invention will be described below in detail.

In the magnetic recording medium of the present invention, the lubricating layer has a number average molecular weight of 500 to 10 represented by the general formula (I).
000 perfluoropolyether (hereinafter referred to as “PFP
E (I) ". ) And a perfluoropolyether represented by the general formula (II) and having a number average molecular weight of 500 to 10,000 (hereinafter referred to as “PFPE (II)”).

When the number average molecular weight of PFPE (I) is less than 500, the lubricant is liable to be scattered under high-temperature and high-speed rotation, and the film thickness is remarkably reduced. In addition, the number average molecular weight is 10,000
If it exceeds 3, the lubricant may have a high viscosity and the durability may be deteriorated. Therefore, the number average molecular weight of PFPE (I) is 5
00 to 10000, preferably 2000 to 8000, more preferably 2500 to 6000.

The number average molecular weight of PFPE (II) is
500 to 10000, preferably 2000 to 8000, more preferably 2500 to 600 for the same reason as above.
Set to 0.

The aromatic ring of the terminal substituent A of PFPE (II) includes a benzene ring, a naphthalene ring, an anthracene ring and the like, and a benzene ring is particularly preferable.

The hydrophilic groups include -OH, -OR
(R represents an alkyl group having 1 to 3 carbon atoms.), -COO
H, preferably -OH, -OR, and a plurality of these may be bonded to the aromatic ring. Further, these hydrophilic groups may be bonded to each other to form a cyclic hydrophilic structure such as a cyclic ether.

As the terminal substituent A, the above-mentioned structural formula (II)
A condensed ring of the cyclic ether represented by I) and a benzene ring is preferred.

In the above general formulas (I) and (II), m is an integer of 1 to 4, especially when it is 1 or 2, the rigidity of the whole molecule is reduced and excellent lubricity is obtained. Is preferable.

The present invention is intended to obtain the effect of specifically suppressing the stiction during long-term standing after CSS under high temperature and high humidity by mixing and using two kinds of lubricants. If the mixing ratio of (I) is large, the durability may be deteriorated. Conversely, if the mixing ratio of PFPE (II) is large, the film thickness is significantly reduced under high-temperature high-speed rotation, so that PFPE (I) and PFPE The mixing ratio of (II) is PFPE (I): PFPE (II) = 1: 20 by weight.
The ratio is preferably 20: 1, particularly 1:10 to 10: 1, particularly preferably high in PFPE (II), more preferably 1:10 to 4: 1, and particularly preferably 1:10 to 2. : 1.

Such PFPE (I) and PFPE
The thickness of the lubricating layer formed in (II) is not particularly limited, but is generally 0.1 to 10 nm, preferably 0.1 to 10 nm.
It is 5 nm, more preferably 0.5 to 3 nm.

The lubricating layer is usually formed by forming a magnetic layer on a substrate, providing a protective layer thereon, and then immersing the substrate in a solution in which a lubricant is dissolved. It is formed by a method of applying a load to a tape or the like to apply a load to form a coating film, a method of attaching a tape while rotating a pad on a substrate, or a spraying method.

In this case, the concentration of the lubricant coating solution varies depending on the compound of the lubricant and the type of the solvent, but is usually 0.1 to 5 g / l as the concentration in the solution. The solvent is not particularly limited as long as it can dissolve the lubricant, but a fluorine-based solvent is generally used, for example, PF
5060, PF5080, HFE-7100, HFE-
7200 (manufactured by 3M), Vertrel-XF (Dup
on), AK225 (Asahi Glass), ZEOROR
A (manufactured by Zeon Corporation).

In order to increase the affinity between the lubricating layer and the protective layer, it is preferable to perform a heat treatment at about 40 to 200 ° C. after the application of the lubricant. The heat treatment is performed using radiant heat or hot air. In this case, as a heat source, a lamp heater using an infrared lamp, a halogen lamp, a resistance heater using a nichrome wire, a platinum wire, a tungsten wire, or a circular stove or a near-infrared ray such as an electric stove or a pipe heater, A radiating heat radiator can be used.

Next, the structure of the magnetic recording medium according to the present invention other than the lubricating layer will be described.

As the nonmagnetic substrate in the magnetic recording medium of the present invention, a substrate containing Al as a main component, for example, Al—Mg
Any non-magnetic substrate can be used as long as it is a non-magnetic substrate such as an Al alloy substrate such as an alloy, a normal soda glass, an aluminosilicate glass, an amorphous glass, a substrate made of silicon, titanium, ceramics, and various resins. . Among them, it is preferable to use a glass substrate such as an Al alloy substrate or crystallized glass. In the process of manufacturing a magnetic disk, it is usual that the substrate is first washed and dried.
In the present invention as well, from the viewpoint of ensuring the adhesion of each layer, it is desirable to perform washing and drying before the formation.

In manufacturing the magnetic recording medium of the present invention,
It is preferable to form a nonmagnetic metal coating layer such as NiP on the surface of the nonmagnetic substrate. As a method for forming the nonmagnetic metal coating layer, a method used for forming various thin films such as an electroless plating method, a sputtering method, a vacuum evaporation method, and a CVD (chemical film formation) method can be used. In the case of a substrate made of a conductive material, it is possible to use electrolytic plating. The thickness of the nonmagnetic metal coating layer may be 50 nm or more. However, considering the productivity of the magnetic recording medium and the like, the thickness is preferably 50 to 500 nm, particularly preferably 50 to 300 nm. The area where the non-magnetic metal coating layer is formed is desirably the entire area of the substrate surface, but may be only a part, for example, only the area to be textured.

Further, in the magnetic recording medium of the present invention,
It is preferable to apply concentric texturing to the surface of the disk-shaped substrate or the surface of the substrate on which the nonmagnetic metal coating layer is formed. Concentric texturing is, for example, mechanical texturing using free abrasive grains and texture tape, texturing using laser light, or the like, or by using both of them, by polishing in the circumferential direction, thereby polishing the substrate circumference. A state in which a large number of minute grooves are formed in the direction is referred to.

As the type of free abrasive grains for mechanical texturing, diamond abrasive grains, particularly those whose surfaces are graphitized, are most preferred. Alumina abrasive grains are widely used as abrasive grains for mechanical texturing, but diamond abrasive grains have extremely good performance, especially from the viewpoint of orienting the axis of easy magnetization along the texturing grooves. Demonstrate.

Regarding the surface roughness (Ra) of the substrate, it is effective for realizing high-density magnetic recording that the head flying height is as small as possible. Therefore, the Ra of the substrate surface is 2 nm or less, particularly 1 nm or less. Preferably, it is more preferably 0.5 nm or less. However,
Here, the determination of Ra assumes a case where measurement is performed using a stylus type surface roughness meter. At this time, the tip of the measuring needle has a radius of about 0.2 μm.

On the non-magnetic substrate on which the non-magnetic metal coating layer has been formed and the concentric texturing has been performed, if necessary, C
After sequentially forming a seed layer containing r as a main component and an underlayer having a B2 crystal structure such as NiAl, a Co alloy magnetic layer is formed. Further, a second underlayer containing Cr as a main component may be formed between the underlayer and the magnetic layer. The purpose is
The purpose is to control the orientation of the crystal plane of the underlayer having a B2 crystal structure formed on the seed layer, the second underlayer containing Cr as a main component, and eventually the Co alloy magnetic layer.

As a material for the seed layer containing Cr as a main component, in addition to pure Cr, V, Ti, Mo, Zr, Hf, Ta, W, G
e, Nb, Si, Cu, B and the like to which second and third elements are added, and Cr oxide are included. Above all, those having pure Cr or Cr and Ti, Mo, W, V, Ta, Si, Nb, Zr and Hf are preferable. The content of the second and third elements varies depending on the respective elements, but is generally in the range of 1 to 50 at%, preferably 5 to 30 at%, and more preferably 5 to 20 at%. .

The thickness of the seed layer containing Cr as a main component or the underlayer having a B2 crystal structure such as NiAl may be sufficient as long as it can express this anisotropy.
0 nm, preferably 0.3 to 30 nm, more preferably 0.5 to 10 nm. Substrate heating may or may not be performed during the formation of the seed layer mainly composed of Cr.

As the Co alloy magnetic layer, pure Co, CoNi, CoSm, CoCrTa, CoNiCr, C
Co, commonly used as a magnetic material such as oCrPt
An alloy magnetic material is used. These Co alloys are further added with N
Elements to which i, Cr, Pt, Ta, W, B or the like, or compounds such as SiO ₂ may be added. For example, CoCrPtT
a, CoCrPtB, CoNiPt, CoNiCrPt
B and the like. The thickness of the Co alloy magnetic layer is arbitrary, but is usually 5 to 50 nm, preferably 10 to 30 nm.

When a second underlayer mainly composed of Cr is provided between the underlayer having the B2 crystal structure and the Co alloy magnetic layer, the second underlayer mainly contains Cr. The same material as the seed layer as a component can be used, and the element composition of both may be the same or different. The thickness of the second underlayer can be arbitrarily set according to the desired characteristics of the magnetic recording medium, but is usually 1 to 100 nm, preferably 5 to 50 nm.

Further, the magnetic layer may have a laminated structure of two or more types, and an intermediate layer such as nonmagnetic CoCr may be provided between the magnetic layer and the second underlayer mainly composed of Cr. .

The film forming method for forming each layer of the magnetic recording medium is arbitrary. For example, physical vapor deposition methods such as direct current (magnetron) sputtering, high frequency (magnetron) sputtering, ECR sputtering, and vacuum deposition are used. No.

There are no particular restrictions on the conditions at the time of film formation, and the ultimate vacuum, substrate heating method and substrate temperature, sputtering gas pressure, bias voltage, etc. may be determined as appropriate by the film forming apparatus. For example, in the case of sputtering film formation, usually, the ultimate vacuum degree is 1 × 10 ⁻⁶ Torr or less, the substrate temperature is from room temperature to 400 ° C., and the sputtering gas pressure is 1 × 1.
0 ^{−3 to} 20 × 10 ⁻³ Torr, and the bias voltage is generally 0 to −500V. In forming the film, a nonmagnetic substrate is generally used to promote the segregation of Cr in the magnetic layer.
It is preferable to heat to about 0 to 350 ° C. Substrate heating may be performed before the formation of the underlayer, or when a transparent substrate having a low heat absorption is used, in order to increase the heat absorption, a seed layer containing Cr as a main component or a B2 crystal structure is used. Is formed, and then the substrate is heated.
An alloy magnetic layer or a second underlayer mainly composed of Cr may be formed.

On the magnetic layer thus formed,
An optional protective layer is formed. As the material of the protective layer, a carbon layer such as C, hydrogenated C, nitrogenated C, Almophas C, or SiC, or a commonly used protective layer material such as SiO ₂ , Zr ₂ O ₃ , or TiN can be used. The main material of the protective layer is preferably carbonaceous, and this carbonaceous film is usually formed by sputtering or CVD.

In the case of the sputtering method, carbon is used as a target, and in addition to a normal rare gas such as Ar or He as a sputtering gas, H ₂ , N ₂ , O ₂ ,
The film is formed while introducing a hydrocarbon, a nitrogen-containing hydrocarbon, a fluorine-containing hydrocarbon, or the like. The power source is not particularly limited, such as direct current, alternating current, high frequency, and pulse, but a direct current or high frequency power source is preferable. Alternatively, the film may be formed while applying a DC or high frequency bias voltage to the substrate.

On the other hand, in the CVD method, a compound containing carbon such as hydrocarbons such as methane, ethane, propane, ethylene, acetylene, benzene, and toluene, alcohols, nitrogen-containing hydrocarbons, and fluorine-containing hydrocarbons is used as a reaction gas. It is introduced into the chamber, and the source gas is decomposed by electric energy such as direct current, alternating current, high frequency, heat energy of the heating filament, thermionic energy emitted from the heating filament, energy of accelerated electrons, etc. to generate film-forming species. It is formed by guiding it to a substrate. The raw material gas may be a mixture of different types of monomers, or may be used as a mixture with an inert gas such as Ar or He or a reactive gas such as H ₂ , N ₂ or O ₂ . At the time of film formation, a bias voltage can be applied to the substrate. Conditions such as gas pressure, power supply voltage, bias voltage, film formation time and the like vary depending on the shape, size, etc. of the apparatus, and thus cannot be particularly limited.
All can be performed under known conditions.

The protective layer may be composed of two or more layers, and the method and conditions for forming each layer may be different.
The thickness of the protective layer is usually 150 ° or less, preferably 100 °.
Hereinafter, it is more preferably 50 ° or less, and the lower limit is usually 5 °.

The magnetic recording apparatus of the present invention includes a disk-shaped magnetic recording medium of the present invention, a rotating means for rotating the magnetic recording medium in the recording direction, a magnetic head comprising an information recording section and a reproducing section, and a magnetic head. Means for causing relative movement with respect to the disk, and recording and reproduction signal processing means for performing signal input to the magnetic head and reproduction of an output signal from the magnetic head; Is effectively suppressed, and high reliability can be exhibited.
In the case of 2,000 rpm or more, the flying height of the magnetic head is 0.01 μm or more and less than 0.05 μm.
A high device S / N can be obtained by improving output with high reliability.
A large-capacity magnetic recording device can be provided.

[0049]

Next, the present invention will be described more specifically with reference to examples and comparative examples, but the present invention is not limited to the following examples unless it exceeds the gist thereof.

In the following Examples and Comparative Examples, Fomblin Z-TE commercially available as PFPE (I) was used.
TRAOL (manufactured by Ausimont Co., Ltd.) (in the general formula (I), m is an integer of 1 to 2, n is an integer, and the number average molecular weight is 2600), and Fomblin AM2001 (manufactured by Ausimont) is commercially available as PFPE (II). (In the general formula (II), m is an integer of 1 to 2, n is an integer, A is the structural formula (III), and the number average molecular weight is 2400). As a perfluoropolyether for comparison, a commercially available Fomblin Z-DOL (manufactured by Ausimont) represented by the following general formula (IV) (the above-mentioned general formula (I
In V), m is an integer of 1 to 2, n is an integer, and the number average molecular weight is 4000).

[0051]

Embedded image

Examples 1 to 5, Comparative Examples 1 and 2 A 15 μm thick NiP layer was formed by electroless plating on both sides of a 3.5 inch diameter aluminum alloy disk substrate having an average surface roughness of 1 nm. Formed, then energy beam with a radius of 17mm to 19mm (CSS zone)
Was irradiated to form a projection having an average height of 19 nm. Thereafter, a chromium base layer (thickness: 20 nm) and a cobalt alloy magnetic layer (thickness: 20 nm) were formed by a sputtering method, and then a carbon film was formed to a thickness of 13 nm as a protective layer. On this carbon film, two kinds of perfluoropolyethers were mixed at a mixing ratio shown in Table 1 with Vertrel-
It was used as an XF (manufactured by DuPont) solution, formed into a film by an immersion method, and then baked at 100 ° C. to a thickness of 1.4 n.
m, a uniform lubricating layer was formed.

A CSS test was performed using the obtained disk in a high-temperature and high-humidity environment by the following method.
It was shown to.

<CSS Test> 32 ° C., 80% R.C. H. After the head is placed in the CSS zone of the magnetic recording medium under the environment described above, the rotation speed is increased from 0 rpm to 7200 rpm to 0 rpm.
The step of setting rpm was repeated 10,000 times at a cycle of 11 seconds, and the frictional force between the disk and the head was measured each time to obtain an average value of the friction coefficient. After the CSS was completed, the sample was left standing for 24 hours in a stopped state, and the frictional force after the standing was measured to obtain a friction coefficient. The head was coated with a carbon coating by a CVD method and used at a pressing pressure of 2.5 g.

Comparative Example 3 In Example 1, a perfluoropolyether represented by the general formula (IV) was used instead of PFPE (II).
Film formation was performed in the same manner except that the mixing ratio with PFPE (I) was as shown in Table 1, and a CSS test was similarly performed. The results are shown in Table 1.

[0056]

[Table 1]

As is clear from Table 1, in Examples 1 to 5, there was no significant difference between the average friction coefficient at the time of CSS and the friction coefficient after standing, and the stiction even after long-term standing at high temperature and high humidity. Is not increasing. On the other hand, in Comparative Examples 1 to 3, the coefficient of friction after standing was 1 or more, which was higher than the average at the time of CSS, and it can be seen that stiction increased by leaving standing. In such a case, if left for a longer period of time, the stiction increases with time, a larger adsorption phenomenon occurs, operation failure may occur, and the head may be destroyed, which is a serious problem in practical use.

[0058]

As described above in detail, according to the present invention, there is no problem of a decrease in lubricity even by a long-term high-speed rotation under a high temperature and a high humidity. A magnetic recording medium that does not cause stiction when left for a long time thereafter is provided. Therefore,
According to the magnetic recording apparatus of the present invention using such a magnetic recording medium, higher density recording can be performed by lowering the flying height of the head.

──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. ⁷ Identification symbol FI Theme coat ゛ (Reference) C10N 40:18

Claims (8)

[Claims] 1. A magnetic recording medium comprising a nonmagnetic substrate having a recording layer, a protective layer and a lubricating layer provided in this order, wherein the lubricating layer is represented by the following general formula (I) and has a number average molecular weight of 50:
Perfluoropolyether having a number average molecular weight of from 500 to 100 represented by the following general formula (II)
A perfluoropolyether which is 00. Embedded image Embedded image 2. The magnetic recording medium according to claim 1, wherein A in the general formula (II) is a phenyl group having a hydrophilic group. 3. A of the general formula (II) is represented by the following structural formula (III)
The magnetic recording medium according to claim 1, wherein the magnetic recording medium is represented by: Embedded image 4. The magnetic recording medium according to claim 1, wherein m is 1 or 2 in the general formulas (I) and / or (II). 5. The mixing ratio (I) :( II) of the perfluoropolyether represented by the general formula (I) to the perfluoropolyether represented by the general formula (II) is 1: 2 by weight.
5. The method according to claim 1, wherein the ratio is 0 to 20: 1.
The magnetic recording medium according to any one of the above items. 6. The magnetic recording medium according to claim 1, wherein the lubricating layer has a thickness of 0.1 to 10 nm. 7. The magnetic recording medium according to claim 1, wherein the protective layer is made of amorphous carbon. 8. The magnetic recording medium according to claim 1, wherein: a disk-shaped magnetic recording medium; rotating means for rotating the magnetic recording medium; A head for reproduction, wherein the rotation speed of the magnetic recording medium during information recording / reproduction is 10,000 rpm
A magnetic recording device characterized by the above.