JP2000309159A - Binder composition for ink jet recording - Google Patents

Abstract

PROBLEM TO BE SOLVED: To improve the ink absorbency is a printing under a high picture quality mode, improve the water-resistance and the coloring property of a printed article, and prevent the strength of a receiving layer from decreasing, by forming a binder for the forming of an ink receiving layer, of a cationic polymer, an inorganic filler, and a sulfosuccinic acid ester based surface active agent. SOLUTION: This binder composition which is used for the ink receiving layer of an ink recording paper is formed of a cationic polymer, an inorganic filler, and a sulfosuccinic acid ester based surface active agent. The cationic polymer which is used in this case means a polymer having a cationic functional group, and for the inorganic filler, a synthetic silica, alumina, calcium carbonate or the like can be counted, and preferably, synthetic silica, and further, an amorphous synthetic silica is used from viewpoints of an ink absorbency and a coloring property or the like. Also, there are various kinds as the sulfosuccinic acid ester based surface active agent, but preferably, dioctyl sodium suflosucciate, dihyexyl sodium sulfosucciate, or dicyclohexyl acid sodium sulfosucciate is used.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a binder composition for ink-jet recording, and more particularly, to a ink-receiving layer having high strength, absorptivity of ink-jet ink, water resistance after printing, coloring, and bleeding. The present invention relates to a binder composition excellent in the above.

[0002]

2. Description of the Related Art Ink-jet recording systems have been rapidly spreading in recent years because they can be easily made full-color, have low noise, and have excellent print quality. Water-based inks are mainly used for inkjet recording from the viewpoint of safety and recording suitability. This water-based ink is turned into fine droplets from the nozzle,
Printing is performed by flying toward the recording sheet. Therefore, the recording sheet is required to absorb the ink promptly. That is, in a recording sheet having a low ink absorbency, the ink remains on the surface of the recording sheet even after the recording is completed, leading to contamination of the apparatus and the next printed matter.

On the other hand, in order to improve the ink absorbency, the problem has been solved by combining an ink receiving layer with a filler such as silica and a hydrophilic resin. However, there has been a problem that the water resistance of the printed matter is extremely reduced. To solve these problems, Japanese Patent Application Laid-Open No. 8-244336,
JP-A-10-195276, JP-A-10-264
No. 511 discloses a technique for improving the water resistance, printability and the like of an ink jet recording sheet based on a cationic latex.

[0004] These techniques have considerably solved ink absorption and water resistance. However, in recent years, in order to make the image quality in ink-jet printing more similar to a photograph, for example, low-concentration ink is used and the amount of the ink is increased. On the other hand, in addition to the conventional technology,
Although an increase in the amount of the inorganic filler can improve the ink absorbency, it leads to a decrease in the strength of the ink receiving layer itself, and also has a problem that the water resistance of the printed matter also decreases. Therefore, there is a demand for an ink-receiving layer that absorbs ink more, maintains the water resistance of the printed matter, and develops coloration close to photographic quality.

[0005]

SUMMARY OF THE INVENTION An object of the present invention is to provide an ink jet printing in a high image quality mode in which the amount of ink is increased as compared with the prior art, which has good ink absorption, water resistance of the printed matter, color development, and the like. An object of the present invention is to provide a binder composition for ink jet recording that can highly improve bleeding property and does not decrease the strength of an ink receiving layer.

[0006]

That is, the present invention is directed to an ink jet recording sheet having an ink receiving layer directly or indirectly on at least one surface of a support, wherein the ink receiving layer is formed of a cationic polymer, An inorganic filler, and a binder composition for ink jet recording, comprising a sulfosuccinate-based surfactant, wherein the cationic polymer is a cationic latex, and the inorganic filler is amorphous synthetic silica. It is.

Hereinafter, the present invention will be described in detail. The cationic polymer of the present invention refers to a polymer having a cationic functional group, and may be in the form of a water-soluble or water-dispersible latex. Latex is preferred in terms of water resistance. The cationic latex can be obtained, for example, by emulsion polymerization using a cationic radically polymerizable monomer as a main component, or can be obtained not by emulsion polymerization but also by water dispersion after addition of water after solution polymerization. Furthermore, after taking the form of a latex, a tertiary amine, a quaternary ammonium compound or the like may be added to make it cationic. Preferably, it is a cationic latex obtained by an emulsion polymerization method.

There is no particular limitation on the method of emulsion polymerization, and conventionally known methods can be applied. For example, the radical polymerizable monomer is polymerized in an aqueous medium in the presence of a radical polymerizable monomer, a radical polymerization initiator, a surfactant, a chain transfer agent as needed, and other additives. In the polymerization, a method in which all radically polymerizable monomers are uniformly polymerized in the entire polymerization process, or a method in which the polymerization is sequentially or continuously changed in the polymerization process, can be used. In order to obtain a cationic latex in the present invention, for example, the radical polymerizable monomer may contain a cationic monomer, the radical polymerization initiator may be cationic, and the surfactant may be cationic. Good, or a combination of these may be used.

The cationic radically polymerizable monomer may be any radically polymerizable monomer having a cationic functional group. Examples of the cationic functional group include a tertiary amino group and a quaternary ammonium group. Examples of the radically polymerizable monomer having a tertiary amino group or a quaternary ammonium group include various radically polymerizable monomers having a tertiary amino group or a base thereof, and a quaternary ammonium base or a quaternary ammonium group. Various radically polymerizable monomers capable of forming a base can be used.

For example, di C _1-4 alkylamino-C _2-3
Alkyl (meth) acrylamide or a salt thereof [dimethylaminoethyl (meth) acrylamide, diethylaminoethyl (meth) acrylamide, dimethylaminopropyl (meth) acrylamide, diethylaminopropyl (meth) acrylamide or a salt thereof, etc.], di C _1-
4 alkylamino-C _2-3 alkyl (meth) acrylate or a salt thereof [dimethylaminoethyl (meth) acrylate, diethylaminoethyl (meth) acrylate, dimethylaminopropyl (meth) acrylate, diethylaminopropyl (meth) acrylate or a salt thereof Etc.], di C _1-4 alkylamino-C _2-3 alkyl group-substituted aromatic vinyl or a salt thereof [4- (2-dimethylaminoethyl) styrene, 4- (2-dimethylaminopropyl)
Styrene and the like and salts thereof], a nitrogen-containing heterocyclic monomer or a salt thereof [vinyl pyridine, vinyl imidazole, vinyl pyrrolidone or a salt thereof] and the like. Salts include hydrohalides (hydrochlorides, hydrobromides, etc.), alkyl halides (methyl chloride, ethyl chloride, propyl chloride, butyl chloride, benzyl chloride,
Epichlorohydrin, methyl bromide, ethyl bromide, propyl bromide, butyl bromide, etc.), sulfate, alkyl sulfate (methyl sulfate, ethyl sulfate, etc.), alkyl sulfonate, aryl sulfonate, carboxylate (Formate, acetate, etc.).

Preferably, di C _1-4 alkylamino-C
_2-3 alkyl (meth) acrylamide or a salt thereof, or di C _1-4 alkylamino-C _2-3 alkyl (meth) acrylate or a salt thereof. In addition to the cationic radically polymerizable monomer, a radically polymerizable monomer may be used in combination, if necessary. For example, an aromatic unsaturated compound, α, β
-Unsaturated monocarboxylic acid alkyl esters, unsaturated carboxylic acids, and the like. Examples of the aromatic unsaturated compound include styrene, α-methylstyrene, vinyltoluene and the like.

The alkyl ester of an α, β-unsaturated monocarboxylic acid includes, for example, an alkyl ester of acrylic acid or methacrylic acid. As an alkyl ester of acrylic acid or methacrylic acid, for example,
Methyl acrylate, ethyl acrylate, propyl acrylate, isopropyl acrylate, butyl acrylate, isobutyl acrylate, hexyl acrylate, cyclohexyl acrylate, 2-ethylhexyl acrylate, lauryl acrylate, methyl methacrylate, ethyl methacrylate, propyl methacrylate, isopropyl acrylate, butyl methacrylate, isobutyl methacrylate, Hexyl methacrylate, cyclohexyl methacrylate, 2-ethylhexyl methacrylate, lauryl methacrylate and the like can be mentioned. Examples of the unsaturated carboxylic acid include acrylic acid, methacrylic acid, maleic acid, fumaric acid, itaconic acid, and monoalkyl itaconate.

[0013] Radical polymerizable monomers other than those described above may be combined as necessary. For example, a hydroxyl group-containing monomer such as 2-hydroxyethyl acrylate, 2
-Hydroxyethyl methacrylate, hydroxypropyl acrylate, hydroxypropyl methacrylate,
Polyethylene glycol acrylate; amide group-containing monomers such as acrylamide, methacrylamide,
N, N-methylenebisacrylamide, diacetoneacrylamide, maleic amide, maleimide; methylol group-containing monomer, for example, N-methylolacrylamide, N-methylolmethacrylamide, dimethylolacrylamide, dimethylolmethacrylamide; alkoxymethyl group-containing monomer For example, N-methoxymethyl acrylamide, N-methoxymethyl methacrylamide, N-butoxymethyl acrylamide, N-butoxymethyl methacrylamide; epoxy group-containing monomers such as glycidyl acrylate, glycidyl methacrylate, allyl glycidyl ether, methyl glycidyl acrylate, Methyl glycidyl methacrylate;
Polyfunctional monomers such as divinylbenzene, polyoxyethylene diacrylate, polyoxyethylene dimethacrylate, polyoxypropylene diacrylate,
Polyoxypropylene dimethacrylate, butanediol diacrylate, butanediol dimethacrylate,
Trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, pentaerythritol tetraacrylate, pentaerythritol tetramethacrylate; mono- or diesters of α, β-ethylenically unsaturated dicarboxylic acids, for example, mono- or dibutyl maleate, mono- or dioctyl fumarate Vinyl esters, for example, vinyl acetate, vinyl propionate; unsaturated nitriles, for example, acrylonitrile, methacrylonitrile; olefins, for example, butadiene, isoprene; chlorine-containing vinyl monomers, for example, vinyl chloride, vinylidene chloride, chloroprene and the like. be able to.

In the present invention, the amount of the cationic radical polymerizable monomer is 0.5 to 50 parts by weight based on 100 parts by weight of the total radical polymerizable monomer. When the amount is 0.5 parts by weight or more, there is no problem in color development, and when it is 50 parts by weight or less, there is no problem in water resistance. Preferably, it is 1 to 40 parts by weight based on 100 parts by weight of the total radical polymerizable monomer. The following can be used as the cationic polymerization initiator. For example, 2,2'-azobis (2-amidinopropane) dihydrochloride, 2,2'-
Azobis (N, N'-dimethyleneisobutylamidine)
Dihydrochloride 2,2′-azobis (2-methylbutanamidooxime) dihydrochloride tetrahydrate and the like.

In addition to these, persulfates, peroxides, water-soluble azobis compounds, redox systems of peroxide-reducing agents and the like are used as required. Examples of the persulfate include ammonium persulfate, potassium persulfate, and sodium persulfate, and examples of the peroxide include hydrogen peroxide,
t-butyl hydroperoxide, t-butyl peroxymaleic acid, succinic peroxide; and water-soluble azobis compounds such as 2,2′-azobis (N-hydroxyethylisobutylamide) and 4,4 ′.
-Azobis (4-cyanopentanoic acid) and the like.

The redox system of the peroxide-reducing agent includes, for example, sodium sulfoxylate formaldehyde, sodium bisulfite, sodium thiosulfate, sodium hydroxymethanesulfinate, L-ascorbic acid and salts thereof in the above peroxide. , Cuprous salts, ferrous salts and the like.

Examples of the oil-soluble polymerization initiator include peroxides and oil-soluble azobis compounds. Examples of the peroxide include dibutyl peroxide, benzoyl peroxide, lauroyl peroxide, cumene hydroperoxide. And the like. Examples of the oil-soluble azobis compound include, for example, 2,2 ′
-Azobisisobutyronitrile, 2,2'-azobis-
2-methylbutyronitrile, 2,2'-azobis-2,
4-dimethylvaleronitrile and the like.

Examples of the cationic surfactant include the following. For example, a quaternary ammonium type, an aliphatic amine type, and a heterocyclic amine type are exemplified. Examples of the quaternary ammonium type include a long-chain primary amine salt, a dialkyldimethylammonium salt, a long-chain tertiary amine salt, Examples thereof include alkyltrimethylammonium salts and alkylpyridinium salts, examples of the aliphatic amine type include polyoxyethylene alkylamines, and examples of the heterocyclic amine type include alkylimidazoline.
In addition to these, a nonionic, anionic, or amphoteric surfactant may be used as necessary.

Examples of the nonionic surfactant include ether type, ester type and alkanolamide type, and examples of the ether type include polyoxyethylene alkyl ether, polyoxyethylene alkyl phenyl ether and polyoxyethylene alkyl thioether. Examples of the ester type include polyoxyethylene monofatty acid ester, polyoxyethylene difatty acid ester, polyoxyethylene propylene glycol fatty acid ester, polyoxyethylene sorbitan monofatty acid ester, glycerin monofatty acid ester, and sucrose fatty acid ester. Examples of the alkanolamide type include fatty acid diethanolamide and polyoxyethylene alkylamide.

Examples of the anionic surfactant include a carboxylic acid type, a sulfate type, a sulfonic acid type and a phosphate type.

Examples of the amphoteric surfactant include N-alkylamino acid type and imidazoline type. In addition, a reactive surfactant may be used together with the non-reactive surfactant described above. The reactive surfactant has a functional group of a radical polymerizable double bond in one molecule and has a polyoxyethylene, polyoxypropylene, polyoxyethylene polyoxypropylene composite type alkyl ether or alcohol. Further, it has a radical polymerizable double bond in one molecule and a sulfonic acid group,
Those having one or more functional groups selected from a sulfonic acid ester group, a sulfonic acid salt group, and a sulfonic acid ester salt (the salt herein refers to a sodium salt, a potassium salt, and an ammonium salt) may be used.

The Tg of the cationic latex is -30 to 6
0 ° C. No problem in water resistance at -30 ° C or higher,
There is no problem in the strength of the ink receiving layer at a temperature of not more than ℃. Preferably it is −20 ° C. to 40 ° C. The particle size of the cationic latex is from 10 nm to 500 nm. If it is 10 nm or more, there is no problem in latex production, and if it is 500 nm or less, there is no problem in the stability of the compound. Preferably 50 nm to 300 nm
It is. In the present invention, the cationic latex may have a different layer structure. The different layer structure includes, for example, a core-shell structure. In the case of core-shell, for example, when there is a difference in Tg between the core part and the shell part, when there is a difference in gel amount, when there is a difference in molecular weight, or when there is a difference in the amount of cationic functional group Is mentioned.

The inorganic filler used in the present invention is synthetic silica, alumina, calcium carbonate, magnesium carbonate, zinc carbonate, magnesium oxide, titanium oxide, zinc oxide, aluminum oxide, barium sulfate, satin white, lithopone, kaolin, aluminum silicate. , Magnesium silicate, aluminum hydroxide, clay, calcined clay, diatomaceous earth, synthetic zeolite, smectite, layered inorganic polymer and the like. Synthetic silica is preferred from the viewpoints of ink absorption and color development, and amorphous synthetic silica is more preferred. The inorganic filler is 10 to 10 parts by weight of the cationic polymer.
500 parts by weight. When the amount of the inorganic filler is 10 parts by weight or more, there is no problem in color development, and when the amount is 500 parts by weight or less, there is no problem in water resistance. Preferably, it is 50 to 400 parts by weight based on 100 parts by weight of the cationic polymer.

The sulfosuccinate-based surfactant used in the present invention includes, for example, the following compounds. Sodium bistridecyl sulfosuccinate, sodium dioctyl sulfosuccinate, sodium dihexyl sulfosuccinate, sodium dicyclohexyl sulfosuccinate, sodium diamyl sulfosuccinate, sodium diisobutyl sulfosuccinate, disodium sulfosuccinate ethoxylated alcohol half ester,
Disodium sulfosuccinate ethoxylated nonylphenol half ester, disodium isodecylsulfosuccinate and the like can be mentioned. One or more sodium sulfosuccinate-based surfactants may be used. Preferred are sodium dioctyl sulfosuccinate, sodium dihexyl sulfosuccinate and sodium dicyclohexyl sulfosuccinate.

The amount of the sodium sulfosuccinate-based surfactant is 0.1 to 100 parts by weight of the cationic polymer.
It is 1 to 10 parts by weight. When the content is 0.1 part by weight or more, the color development of the printed matter becomes good, and when the content is 10 parts by weight or less, there is no problem in water resistance. Preferably it is 0.5 to 8 parts by weight. The timing of adding the sodium sulfosuccinate-based surfactant is not particularly limited, and may be, for example, a cationic polymer, may be added when mixing an inorganic filler, or may be previously added to the cationic polymer. The inorganic filler may be mixed with water and then added.

The cationic latex of the present invention may contain, if necessary, a surfactant, a dispersant, a preservative, an antifoaming agent, a thickener,
A solvent or the like may be added. In the present invention, the following materials may be blended as required. For example, a water-soluble resin,
And water-soluble quaternary ammonium salt oligomers.

Examples of the water-soluble resin include polyvinyl alcohol, cationized polyvinyl alcohol, ethylene-modified polyvinyl alcohol, silanol-modified polyvinyl alcohol, cellulose resins (methylcellulose, ethylcellulose, hydroxycellulose, carboxycellulose, etc.), chitin, chitosan, starch, Cationic starch, polyethylene glycol, polypropylene glycol, polyvinyl ether, polyacrylamide,
Examples include polyvinylpyrrolidone, polyethyleneimine, epoxidized polyamide, polyvinylpyridine, gelatin, caseins, cyclodextrins, and aqueous nitrified cotton.

The water-soluble quaternary ammonium salt oligomer includes, for example, polyethyleneimine salt, dimethylamine epihalohydrin condensate, polyvinylamine salt, polyallylamine salt, polydimethylaminoethyl methacrylate quaternary salt, polydiallyldimethylammonium salt, diallylamina Examples include salts of acrylamide copolymers and quaternary ammonium salts of polystyrene. The support used in the present invention is paper, synthetic paper, plastic paper,
Examples include a film, a metal plate, a metal foil, and a plastic film on which aluminum or the like is deposited.

The ink receiving layer of the present invention may be applied directly on a support, or may have a multi-layer structure as required. For example, an anchor layer may be provided below the ink receiving layer, and a gloss layer may be provided above the ink receiving layer. The method for applying the ink receiving layer of the present invention is not limited. For example, roll coater, air knife coater, blade coater, rod blade coater, curtain coater,
General coaters such as a bar coater, a die coater, and a gravure coater are exemplified.

The ink receiving layer according to the present invention may have a thickness of 1 to 50 on a support.
g / m^TwoIt may be applied. 1g / m ^TwoThis is the question of color development
Untitled, 50g / m^TwoThere is no problem in water resistance below. Good
Preferably 3 to 30 g / m^TwoIt is. Ink receiving of the present invention
Layer is made of cationic polymer, inorganic filler, sulfosuccinic acid
After applying the composition comprising a surfactant to the support, 80-1
It can be obtained by drying at 60 ° C. for 5 to 300 seconds.

[0031]

DESCRIPTION OF THE PREFERRED EMBODIMENTS Embodiments of the present invention will be described below, but they do not limit the scope of the present invention. Unless otherwise specified, it is based on weight. The evaluation of various physical properties in the present invention is as follows. (1) Ink color development Ink jet color printer (BJC-420J;
Solid printing of cyan, magenta, and yellow was performed on the inkjet recording sheet by Canon Inc.).
Printing was performed using a special photo ink, and the mode was set to a super photo mode. The density of solid printing was measured by a Gretag densitometer (D142-3; manufactured by Gretag).

(2) Bleeding Bleeding between the boundaries of solid printing of cyan, magenta, and yellow was visually observed. The evaluation criteria are as follows. Δ: No bleeding Δ: No bleeding of 0.5 mm or more at the boundary portion ×: Bleeding of 0.5 mm or more at the boundary portion. △ or more was considered as a pass.

(3) Ink Absorption Immediately after the solid printing of (1), the printed surface was rubbed with a finger and the state was observed. The evaluation criteria are as follows. 〇: No ink adhered to finger. Δ: Slight adhesion of ink to finger X: Adhesion of ink to finger is recognized. △ or more was considered as a pass.

(4) Water Resistance The solid printed matter was immersed in running water for 5 minutes, and the printed state was visually observed. The evaluation criteria are as follows. 〇: No ink leakage. Δ: Slight outflow of ink ×: Outflow of ink is observed in all colors. △ or more was considered as a pass.

(5) Surface Strength The surface of the ink jet recording sheet before solid printing was rubbed with a finger, and the state was observed. The evaluation criteria are as follows. 〇: No pigment transfer to finger. Δ: Pigment (inorganic filler) slightly transferred to finger ×: Pigment transferred to finger △ or more was considered as a pass.

[0036]

EXAMPLES (Production Examples 1 to 4) Production examples of cationic latex will be described. Radical polymerizable monomer 1000 shown in Table 1
In the part, stearyltrimethylammonium chloride 25%
10 parts of an aqueous solution adjusted to 25%, 10 parts of an aqueous solution adjusted to 25% of Emulgen 920 [manufactured by Kao Corporation, polyoxyethylene nonylphenyl ether], 3 parts of 2,2′-azobis (2-amidinopropane) dihydrochloride , Distilled water 5
86 parts were added and stirred with a homomixer to prepare a pre-emulsion.

Separately, add 780 distilled water to a flask equipped with a stirrer.
, 10 parts of a 25% aqueous solution of stearyltrimethylammonium chloride and 20 parts of a 25% aqueous solution of emulgen 920, and the mixture was heated to 80 ° C., and 3 parts of 2,2′-azobis (2-amidinopropane) dihydrochloride was added to water. The solution dissolved in 50 parts is added. To this, the pre-emulsion is continuously dropped over 4 hours. Thereafter, stirring was continued at the same temperature for 2 hours.
Thereafter, the temperature was cooled to 30 ° C. or lower, and then filtration was performed using an 80-mesh wire net. After filtration, water was added to adjust the solid content to 40%. Table 1 shows the particle size of the obtained latex.

(Examples 1 to 8) The materials shown in Table 2 were blended as follows (the numerical values in Table 2 represent solid contents). While stirring 1000 parts of water, a predetermined amount of amorphous synthetic silica (Fine Seal X37: manufactured by Tokuyama Corporation) and a sulfosuccinate-based surfactant were added, and the mixture was stirred for 15 minutes. Next, a predetermined amount of latex was added, and stirring was continued for another 15 minutes. Thereafter, water was added with stirring so that the solid content of the blended product became 20%, to obtain a blended product.

Next, the blended product was applied to a high-quality paper having a basis weight of 70 g with a bar coater. After the application, the coated paper was immediately left for 90 seconds in a hot air dryer controlled at 130 ° C., and dried to obtain a coated paper. The coating amount was adjusted with a bar coater so as to be 10 g / m ² . The dried coated paper was passed through a calender having a linear pressure of 50 kg to obtain an ink jet recording sheet. Table 2 also shows the evaluation results of the obtained inkjet recording sheets of the present invention.

Comparative Examples 1 to 5 Compounds shown in Table 3 were prepared in the same manner as in the examples. Further, a recording sheet was prepared in the same manner as in the example, and the ink jet recording sheet was evaluated in the same manner as in the example. Table 3 shows the evaluation results.

[0041]

[Table 1]

[0042]

[Table 2]

[0043]

[Table 3]

[0044]

According to the present invention, in ink jet printing in a high image quality mode in which the amount of ink is increased as compared with the prior art, the ink absorption is good, and the water resistance, color development, and bleeding of the printed matter are enhanced. And a binder composition for ink jet recording that does not decrease the strength of the ink receiving layer.

Continued on the front page F term (reference) 2C056 EA13 FC06 2H086 BA15 BA31 BA33 BA34 4L055 AG18 AG36 AG71 AG73 AG94 AH02 AH29 AH37 AH50 AJ04 FA15 FA19 GA09

Claims (3)

[Claims] 1. An ink jet recording sheet having an ink receiving layer directly or indirectly on at least one surface of a support for forming an ink receiving layer, comprising a cationic polymer, an inorganic filler, and a sulfosuccinate ester A binder composition for inkjet recording, comprising a surfactant. 2. The ink jet recording binder composition according to claim 1, wherein the cationic polymer is a cationic latex. 3. The binder composition for ink jet recording according to claim 1, wherein the inorganic filler is an amorphous synthetic silica.