JP2000263668A - Sandwiched panel made of frp and its manufacture - Google Patents
Sandwiched panel made of frp and its manufactureInfo
- Publication number
- JP2000263668A JP2000263668A JP11070296A JP7029699A JP2000263668A JP 2000263668 A JP2000263668 A JP 2000263668A JP 11070296 A JP11070296 A JP 11070296A JP 7029699 A JP7029699 A JP 7029699A JP 2000263668 A JP2000263668 A JP 2000263668A
- Authority
- JP
- Japan
- Prior art keywords
- frp
- sandwich panel
- hollow box
- resin
- plates
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、ＦＲＰ製サンドイ
ッチパネルおよびその製造方法に関し、とくに軽量で低
コストのＦＲＰ製サンドイッチパネルおよびその製造方
法に関する。The present invention relates to a sandwich panel made of FRP and a method of manufacturing the same, and more particularly to a lightweight and low-cost sandwich panel made of FRP and a method of manufacturing the same.
【０００２】[0002]
【従来の技術】従来、種々の構造体として用いるサンド
イッチパネルには、たとえば発泡体や断熱材をコアに用
いて、それを金属の板や木製の板で挟む構造を採ってい
る。しかしながら、金属の板を使用する場合には剛性や
強度は高いが、重量が重くまた組立に時間が掛かる欠点
があった。一方、木製の板を使用する場合には、軽量で
はあるものの剛性や強度が低いことが構造体として使う
場合に難点であり、また木製であるため、湿気により杤
ちることがあり寿命も極めて短い。2. Description of the Related Art Conventionally, sandwich panels used as various structures have a structure in which, for example, a foam or a heat insulating material is used for a core, and the core is sandwiched between metal plates or wooden plates. However, when a metal plate is used, the rigidity and strength are high, but the weight is heavy and the assembly takes time. On the other hand, when a wooden board is used, it is lightweight but has low rigidity and strength when used as a structure, and it is difficult to use as a structure. .
【０００３】これらの欠点を解決するために、金属に比
べ比強度、比弾性率が高いＦＲＰの板、特に炭素繊維を
使用したＣＦＲＰの板が提案されている。[0003] In order to solve these drawbacks, there have been proposed FRP plates having higher specific strength and specific elastic modulus than metals, particularly CFRP plates using carbon fibers.
【０００４】[0004]
【発明が解決しようとする課題】ＦＲＰのサンドイッチ
パネルについては、軽量かつ高強度、高剛性であること
から種々の分野、特に土木・建材用途で使用されている
が、サンドイッチパネルの成形のために、通常サンドイ
ッチパネルの中に発泡体をコア材として使用している。
通常コア材はウレタンフォーム、ポリスチレンフォー
ム、フェノールフォームなどの有機の発泡体が広く用い
られているが、これらのフォーム材はいずれもポリマー
に発泡剤を混入したものを原料に用いて製造する必要が
あるため、製造コストが高く付いており、これがサンド
イッチパネルの製造コストを引き上げていた。[0005] FRP sandwich panels are used in various fields, particularly in civil engineering and construction materials, because of their light weight, high strength and high rigidity. Foams are commonly used as core materials in sandwich panels.
Generally, organic foams such as urethane foam, polystyrene foam, and phenol foam are widely used as the core material, but all of these foam materials need to be manufactured using a mixture of a polymer and a foaming agent as a raw material. As a result, manufacturing costs are high, which has increased the manufacturing costs of sandwich panels.
【０００５】また特に、近年低コストでかつ高強度のＦ
ＲＰを製造できる成形法として注目されている真空ＲＴ
Ｍ法（Ｒｅｓｉｎ Ｔｒａｎｓｆｅｒ Ｍｏｌｄｉｎ
ｇ）に使用するためには、コア材は真空の圧力に耐える
ことが必要であり、そのための高い圧縮強度を得るため
に、コア材の密度は高くならざるを得ず、通常の発泡体
に比べさらにコストが高い上に重量も重いものを使用し
ていた。従って結果的にそれを使用したサンドイッチパ
ネルは、成形法としては低コストの方法を用いても、コ
ア材の価格が高いために製造コストが高くなっていた。In particular, in recent years, low-cost and high-strength F
Vacuum RT attracting attention as a molding method that can produce RP
M method (Resin Transfer Moldin)
In order to use g), the core material must be able to withstand the pressure of vacuum, and in order to obtain high compressive strength, the density of the core material must be high. In addition, the cost was higher and the weight was higher. Therefore, as a result, even if a low cost method is used as a molding method, the manufacturing cost of the sandwich panel using the same is high due to the high price of the core material.
【０００６】本発明の課題は、十分に高い機械的物性を
備えた軽量のＦＲＰ製サンドイッチパネルを安価に製造
することにあり、とくに屋根材等の建材用途に好適なＦ
ＲＰ製サンドイッチパネルおよびその製造方法を提供す
ることにある。An object of the present invention is to manufacture a lightweight FRP sandwich panel having sufficiently high mechanical properties at a low cost, and particularly to a FRP sandwich panel suitable for building materials such as roofing materials.
An object of the present invention is to provide an RP sandwich panel and a method of manufacturing the same.
【０００７】[0007]
【課題を解決するための手段】上記課題を解決するため
に、本発明のＦＲＰ製サンドイッチパネルは、少なくと
も一方にＦＲＰを含む一対の板が間隙をもって配置さ
れ、該間隙に両板を接合するリブ構造体が介装されてい
るＦＲＰ製サンドイッチパネルにおいて、中空の箱状物
を該間隙に包含してなることを特徴とするものからな
る。In order to solve the above-mentioned problems, a sandwich panel made of FRP according to the present invention comprises a pair of plates including FRP disposed at least on one side thereof with a gap, and a rib for joining the two plates to the gap. An FRP sandwich panel in which a structure is interposed, wherein a hollow box-like material is included in the gap.
【０００８】このリブ構造体の材料には、ＦＲＰ、金
属、木材等を使用でき、リブ構造体は一対の板の成形と
同時に配置し組み込むことが好ましい。As the material of the rib structure, FRP, metal, wood or the like can be used, and it is preferable that the rib structure is arranged and incorporated at the same time as the molding of the pair of plates.
【０００９】前記一対の板間の間隙の寸法としては、板
延在方向において、実質的に一定であってもよく、変化
していてもよい。The size of the gap between the pair of plates may be substantially constant in the direction in which the plates extend, or may vary.
【００１０】また、板自身の形状としては、単なる平板
状のものでもよいが、たとえば、少なくとも一方の板
が、山部と谷部が交互に配置された折板形状に形成され
ているものとすることもできる。この山部または／およ
び谷部は、ある方向に直線状に延びるものの他、ピラミ
ッド形等に立体的に形成されたものであってもよい。The plate itself may have a simple flat plate shape. For example, at least one of the plates has a folded plate shape in which peaks and valleys are alternately arranged. You can also. The peaks and / or valleys may be linearly extended in a certain direction, or may be three-dimensionally formed in a pyramid shape or the like.
【００１１】前記リブ構造体は、各種断面形状を採用で
きるが、さらに、トラスまたはラーメン構造体に構成す
ることもできる。The rib structure can have various cross-sectional shapes, but can also be configured as a truss or ramen structure.
【００１２】中空の箱状物としては、熱可塑性樹脂で作
られたもの、熱硬化製樹脂で作られたもののいずれも使
用できる。これら樹脂で作られた箱状物に強化繊維を巻
き、サンドイッチパネル成形後には実質的にＦＲＰ製の
箱状物が形成されるようにしてもよい。箱状物の表面に
溝を形成しておけば、成形時に樹脂を拡散させることが
できる。また、箱状物の形状については、直方体形状の
他、断面形状が台形のものも使用できる。[0012] As the hollow box-shaped material, any of those made of a thermoplastic resin and those made of a thermosetting resin can be used. Reinforcing fibers may be wound around a box made of these resins so that a box made of substantially FRP is formed after the sandwich panel is formed. If grooves are formed on the surface of the box-shaped material, the resin can be diffused during molding. As for the shape of the box-like material, a rectangular shape or a trapezoidal cross-sectional shape can be used.
【００１３】また、本発明に係るＦＲＰ製サンドイッチ
パネルにおいては、耐火性をを向上するために、少なく
とも一方の板のマトリックス樹脂がフェノール樹脂から
なることが好ましい。さらに、少なくとも片面に、耐火
材、たとえば耐火性の材料や耐火塗料からなる層を設け
ておくこともできる。In the sandwich panel made of FRP according to the present invention, it is preferable that the matrix resin of at least one plate is made of a phenol resin in order to improve fire resistance. Further, a layer made of a refractory material, for example, a refractory material or a refractory paint may be provided on at least one side.
【００１４】さらに、本発明に係るＦＲＰ製サンドイッ
チパネルは、屋根材等の建材として好適に使用できるも
のである。その際、ＦＲＰ製屋根材全体、あるいは屋根
を構成するためのＦＲＰ製屋根材一単位全体について、
立体的な形状に形成することが可能である。たとえば、
少なくとも一方の板が、多面体状の立体形状部を有して
いる構造や、少なくとも一方の板が、三次元曲面部をも
つ立体形状部を有している構造とすることができる。ま
たこれら立体形状部の両方をもつ構造とすることもでき
る。Further, the sandwich panel made of FRP according to the present invention can be suitably used as a building material such as a roof material. At that time, for the entire FRP roofing material or the entire FRP roofing material unit to constitute the roof,
It can be formed in a three-dimensional shape. For example,
A structure in which at least one plate has a polyhedral three-dimensional shape portion or a structure in which at least one plate has a three-dimensional shape portion having a three-dimensional curved surface portion can be employed. Further, a structure having both of these three-dimensionally shaped portions may be adopted.
【００１５】本発明に係るＦＲＰ製サンドイッチパネル
の製造方法は、成形型上に強化繊維を配置し、その上の
所定の位置に強化繊維を巻いた中空の箱状物を配置し、
さらに強化繊維を配置した後、全体を真空用フィルム基
材で覆った後フィルム基材で覆われた内部を真空にし、
樹脂を注入して強化繊維に含浸させることを特徴とする
方法からなる。[0015] In the method for producing a sandwich panel made of FRP according to the present invention, a reinforcing fiber is arranged on a mold, and a hollow box-like material having the reinforcing fiber wound is arranged at a predetermined position on the reinforcing fiber.
After further arranging the reinforcing fibers, the inside covered with the film substrate is evacuated after covering the whole with the film substrate for vacuum,
The method is characterized by injecting a resin and impregnating the reinforcing fibers.
【００１６】上記のような本発明に係るＦＲＰ製サンド
イッチパネルにおいては、両板間の間隙に中空の箱状物
が内包されるので、この箱状物もコア材および／または
リブとして機能してサンドイッチパネル全体の機械的物
性を十分に高く確保しつつ、中空構造のため全体の軽量
性も維持、あるいは他のリブ構造に比べ向上できる。そ
して、この中空の箱状物はサンドイッチパネル全体の成
形前には単なる樹脂成形物でよいから、安価に製造でき
る。In the sandwich panel made of FRP according to the present invention as described above, a hollow box-like material is included in the gap between the two plates, and this box-like material also functions as a core material and / or a rib. While maintaining the mechanical properties of the entire sandwich panel at a sufficiently high level, the hollow structure can maintain the overall lightness or can be improved compared to other rib structures. The hollow box-shaped article may be a simple resin molded article before the entire sandwich panel is formed, and thus can be manufactured at low cost.
【００１７】[0017]
【発明の実施の形態】以下に、本発明の望ましい実施の
形態を、図面を参照しながら説明する。まず、本発明の
基本技術思想について、本発明者らは、低コストかつ高
い強度剛性を持つＦＲＰ製サンドイッチパネルを得るた
めの最適なサンドイッチパネルの構造を鋭意検討した結
果、サンドイッチパネルの板間の間隙に中空の箱状物
を、コア材あるいはその一部の代わりに使用することに
よって、前述の課題を解決できることを見いだした。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Preferred embodiments of the present invention will be described below with reference to the drawings. First, with regard to the basic technical concept of the present invention, the present inventors have conducted intensive studies on the optimum sandwich panel structure for obtaining a low-cost and high-strength rigidity FRP sandwich panel, and as a result, the sandwich panel It has been found that the above-mentioned problem can be solved by using a hollow box-like material in the gap instead of the core material or a part thereof.
【００１８】中空状の箱状物は成形の際にコア材の代わ
りに、ＦＲＰ成形法として最も一般的なハンドレイアッ
プ法でも用いることができる。さらに真空成形法におい
ても中空状の箱状物の内圧が通常の空気圧と同じでよい
ので、全体を真空フィルム基材で覆って成形をする際に
も、外気圧と圧力がつり合うことから、箱状物がつぶれ
ることなく成形可能である。The hollow box-shaped material can be used by the most common hand lay-up method as the FRP molding method instead of the core material at the time of molding. Furthermore, in the vacuum forming method, the internal pressure of the hollow box-shaped material may be the same as the normal air pressure, so even when the whole is covered with a vacuum film substrate and formed, the external pressure and the pressure are balanced, so the box It can be molded without crushing the object.
【００１９】中空状の箱状物の素材は何であってもよい
が、特に熱可塑性の樹脂を用いて、射出成形あるいはブ
ロー成形によって製造されるものがコストの面から非常
に有利である。さらに射出成形、あるいはブロー成形で
は所望の形状の中空箱状物が簡単に成形できる。従って
サンドイッチパネルの形状がどんなものであっても、中
空の箱状物の形状を変えることによって作ることができ
る。例えば、サンドイッチパネルの間隙の寸法が変化し
ているものでも、また一方の板が山部と谷部が交互に配
置された折板形状であっても、容易に作ることが可能で
ある。The material of the hollow box-shaped material may be any material. In particular, a material manufactured by injection molding or blow molding using a thermoplastic resin is very advantageous in terms of cost. Further, a hollow box having a desired shape can be easily formed by injection molding or blow molding. Thus, whatever the shape of the sandwich panel, it can be made by changing the shape of the hollow box. For example, even if the size of the gap of the sandwich panel changes, or if one of the plates has a folded plate shape in which peaks and valleys are alternately arranged, it can be easily manufactured.
【００２０】中空の箱状物の大きさはどんなものであっ
てもよいが、体積があまり小さいと、発泡体のコアに比
べ軽量化効果が出にくく、したがって１，０００ｃｍ3
以上のものが好適に用いられる。またあまり体積が大き
いと構造上問題があるため、１００，０００ｃｍ3 以下
が好ましい。Although the size of the hollow box-shaped object may be any size, if the volume is too small, the effect of reducing the weight is less likely to be obtained as compared with the foam core, and therefore, 1,000 cm 3
The above are preferably used. If the volume is too large, there is a structural problem. Therefore, the volume is preferably 100,000 cm 3 or less.
【００２１】発泡体のコアの代わりに用いる場合、その
全部あるいは一部を中空の箱状物にすることによって、
低コスト化が可能である。サンドイッチパネルの物性上
の要求特性によっては、コア材として中空の箱状物と共
に木材、コンクリートなどを使用することも可能であ
る。When used in place of the foam core, all or a part of the core is formed into a hollow box,
Cost reduction is possible. Depending on the required properties of the sandwich panel in terms of physical properties, it is possible to use wood, concrete, etc. together with the hollow box-like material as the core material.
【００２２】本発明のサンドイッチパネルを形成する一
対の板は、軽量化のために少なくとも一方がＦＲＰを含
む板である。この板の厚みとしては、０．６〜７ｍｍが
好ましい。０．６ｍｍ未満では所望の強度・剛性を得る
のが難しいほか、衝撃によって板を貫通してしまうよう
な傷が生じる可能性が高い。一方７ｍｍを越えると、強
度・剛性は十分であるが、重量の面で非常に重くなって
しまう欠点がある。At least one of the pair of plates forming the sandwich panel of the present invention is a plate containing FRP for weight reduction. The thickness of this plate is preferably 0.6 to 7 mm. If the thickness is less than 0.6 mm, it is difficult to obtain desired strength and rigidity, and there is a high possibility that a flaw that penetrates the plate due to an impact is generated. On the other hand, if it exceeds 7 mm, the strength and rigidity are sufficient, but there is a disadvantage that the weight becomes very heavy.
【００２３】サンドイッチパネルに要求される各種特性
によって、板としてはＦＲＰと金属の一体構造の板も用
いることができる。また、例えば、サンドイッチパネル
を形成する板の内、下面はＦＲＰ、上面は耐火性の要求
から金属、コンクリート、モルタルなどの不燃材で形成
することも、可能である。Depending on various characteristics required for the sandwich panel, a plate having an integral structure of FRP and metal can be used as the plate. Further, for example, of the plates forming the sandwich panel, the lower surface may be formed of FRP, and the upper surface may be formed of a non-combustible material such as metal, concrete, mortar or the like from the viewpoint of fire resistance.
【００２４】ＦＲＰの強化繊維としてはガラス繊維、ア
ラミド繊維、炭素繊維などが通常用いられる。軽量・高
強度のＦＲＰを得るためには、炭素繊維が最も好ましい
が、コストとのバランスを取るため、ガラス繊維／炭素
繊維のハイブリッドのものも好ましい。また用いられる
繊維の形態としては、クロス、マット、ストランドなど
を好適に用いることができる。さらに用いる炭素繊維の
種類は、炭素繊維の高い強度・剛性を考えると、どんな
ものでもよいが、より低コストを考えると、いわゆるラ
ージ・トウの炭素繊維を用いるのが最も好ましい。Glass fibers, aramid fibers, carbon fibers and the like are usually used as the reinforcing fibers of FRP. Carbon fiber is most preferred for obtaining a lightweight and high-strength FRP, but a glass fiber / carbon fiber hybrid is also preferred for balancing cost. As the form of the fiber used, cloth, mat, strand, and the like can be suitably used. Further, any kind of carbon fiber may be used in consideration of the high strength and rigidity of the carbon fiber. However, in view of lower cost, it is most preferable to use a so-called large tow carbon fiber.
【００２５】たとえば、炭素繊維糸１本のフィラメント
数が通常の１０，０００本未満のものではなく、１０，
０００〜３００，０００本の範囲、より好ましくは５
０，０００〜１５０，０００本の範囲にあるトウ状の炭
素繊維フィラメント糸を使用する方が、樹脂の含浸性、
強化繊維基材としての取扱い性、さらには強化繊維基材
の経済性において、より優れるため、好ましい。またＦ
ＲＰ構造体の表面に炭素繊維の織物を配置すると、表面
の意匠性が高められ、より好ましい。また、必要に応じ
て、あるいは要求される機械特性等に応じて、強化繊維
の層を複数層に積層して強化繊維基材を形成し、その強
化繊維基材に樹脂を含浸する。積層する強化繊維層に
は、一方向に引き揃えた繊維層や織物層を適宜積層で
き、その繊維配向方向も、要求される強度の方向に応じ
て適宜選択できる。For example, the number of filaments per carbon fiber yarn is not less than the usual number of 10,000,
000 to 300,000, more preferably 5
The use of tow-like carbon fiber filament yarns in the range of 0000 to 150,000 yarns has better resin impregnation,
It is preferable because it is more excellent in handleability as a reinforcing fiber base material and further in economic efficiency of the reinforcing fiber base material. Also F
Placing a carbon fiber woven fabric on the surface of the RP structure enhances the design of the surface, which is more preferable. In addition, a reinforcing fiber base is formed by laminating a plurality of layers of reinforcing fibers as necessary or according to required mechanical properties and the like, and the reinforcing fiber base is impregnated with a resin. On the reinforcing fiber layer to be laminated, a fiber layer or a fabric layer aligned in one direction can be appropriately laminated, and the fiber orientation direction can be appropriately selected according to the direction of required strength.
【００２６】また、ＦＲＰの樹脂としては、ビニルエス
テル樹脂、不飽和ポリエステル樹脂、フェノール樹脂な
どが好適に用いられるが、特に建築材料・土木材料用途
では、燃焼性の規格があるため、フェノール樹脂が最も
好適に用いられる。As the FRP resin, a vinyl ester resin, an unsaturated polyester resin, a phenol resin and the like are preferably used. Particularly, for building materials and civil engineering materials, phenol resin is used because of its flammability standard. Most preferably used.
【００２７】サンドイッチパネルの構造としては、一対
の板がある間隙をもって配置されその間隙に上下の板を
接合するリブ構造体があり、中空の箱状物がその間隙内
に存在すればどんな構造でもよい。また少なくとも一方
の板が、山部と谷部が交互に配置された折板形状をして
いるサンドイッチパネルも用途によっては好適に用いら
れる。As the structure of the sandwich panel, there is a rib structure in which a pair of plates are arranged with a gap therebetween and the upper and lower plates are joined to the gap. Any structure can be used as long as a hollow box-like object exists in the gap. Good. Further, a sandwich panel in which at least one plate has a folded plate shape in which peaks and valleys are alternately arranged is suitably used depending on the application.
【００２８】一対の板の形状としては用途に応じて、平
板形状、波板形状などを使い分けることができる。また
一対の板の間隔も、実質的に一定であるものの他、間隔
が変化していても何ら問題はない。As the shape of the pair of plates, a flat plate shape, a corrugated plate shape, or the like can be used depending on the application. In addition to the fact that the interval between the pair of plates is substantially constant, there is no problem even if the interval changes.
【００２９】リブの形状も一対の板からいずれも垂直に
延びて一対の板を繋いでいる構造を取れる他、トラス構
造、ラーメン構造のリブ構造でもよい。The shape of the rib may be a structure in which each of the ribs extends vertically from the pair of plates and connects the pair of plates, or a rib structure of a truss structure or a rigid frame structure may be used.
【００３０】本サンドイッチパネルを建築材料用途など
に用いる場合には、耐火性の要求から少なくとも片面に
耐火材が設けられていてもよい。耐火材としては、ロッ
クウール成形板、樹脂発泡体、ロックウールのフェルト
材、セラミックファイバーのフェルト材、耐火性塗料、
発泡性塗料、耐火性シーラントなど、あるいはそれらの
組み合わせたものが好適に用いられる。When the present sandwich panel is used for building materials and the like, a fire-resistant material may be provided on at least one side from the viewpoint of fire resistance. Refractory materials include rock wool molded plate, resin foam, rock wool felt material, ceramic fiber felt material, fire resistant paint,
A foaming paint, a fire-resistant sealant, or the like, or a combination thereof is preferably used.
【００３１】本発明のサンドイッチパネルの製造方法を
以下に順を追って説明する。 （１）成形型上に強化繊維を配置する。この時強化繊維
を配置する方法としては、繊維をそのまま型上に置く方
法もあるが、製造の効率化からあらかじめクロスとした
繊維を配置した方が好ましい。The method for manufacturing a sandwich panel according to the present invention will be described below in order. (1) Reinforcing fibers are arranged on a mold. At this time, as a method of arranging the reinforcing fibers, there is a method of arranging the fibers as they are on a mold, but it is more preferable to arrange the fibers which have been made into a cloth in advance from the viewpoint of production efficiency.
【００３２】（２）強化繊維を巻いた中空の箱状物を強
化繊維状に配置する。中空の箱状物はサンドイッチパネ
ルの所望の形状に合わせて、ブロー成形あるいは射出成
形などで成形されたものを用いることができる。また中
空の箱状物の間には樹脂注入後リブとなるように強化繊
維を挿入してもよい。強化繊維を挿入せずに、箱状物に
巻いた強化繊維をリブとしてもよい。サンドイッチパネ
ルの物性に応じてコア材については中空の箱状物のみで
なく、有機の発泡体、木材、コンクリートなどを中空の
箱状物と組み合わせて使用してもよい。(2) A hollow box-shaped material wound with reinforcing fibers is arranged in the form of reinforcing fibers. As the hollow box-shaped material, a material formed by blow molding, injection molding, or the like according to a desired shape of the sandwich panel can be used. Reinforcing fibers may be inserted between the hollow box-shaped objects so as to become ribs after resin injection. Instead of inserting the reinforcing fiber, a reinforcing fiber wound around a box may be used as the rib. Depending on the physical properties of the sandwich panel, the core material may be not only a hollow box-shaped material but also an organic foam, wood, concrete or the like in combination with the hollow box-shaped material.
【００３３】（３）さらにサンドイッチパネルの上面に
なる強化繊維を配置する。(3) Further, reinforcing fibers to be the upper surface of the sandwich panel are arranged.
【００３４】（４）成形体全体を真空用フィルム基材で
覆う。(4) The entire molded body is covered with a vacuum film substrate.
【００３５】（５）覆われた内部を真空とする。(5) The covered interior is evacuated.
【００３６】（６）内部に樹脂を注入して強化繊維に含
浸させる。この時含浸の補助手段として、中空の箱状物
あるいはそれと合わせて使用するコア材の少なくとも一
面に、樹脂の通り道となる溝を切ったものを用いてもよ
い。成形体が大型になると特にこのような樹脂含浸の補
助手段が有効である。(6) A resin is injected into the inside to impregnate the reinforcing fibers. At this time, as an auxiliary means for impregnation, a hollow box-like material or a material obtained by cutting a groove serving as a resin passage on at least one surface of a core material used in combination therewith may be used. In particular, when the size of the molded article is large, such an auxiliary means for resin impregnation is effective.
【００３７】（７）樹脂を硬化させた後、脱型する。硬
化には必要に応じて熱を与えてもよい。また脱型後にア
フターキュアとしてさらに熱を加えてもよい。(7) After the resin is cured, it is released from the mold. Heat may be applied to the curing as needed. Further, after demolding, heat may be further applied as after-curing.
【００３８】以下、本発明のより具体的な実施態様を図
を用いて説明する。図１は本発明の一実施態様を示した
ものである。サンドイッチパネル１は、上下の板２およ
び、リブ３によって形成されたサンドイッチパネルの中
に中空の箱状物４が包含されている。リブ３と中空箱状
物４の側壁は一体成形されてもよい。Hereinafter, more specific embodiments of the present invention will be described with reference to the drawings. FIG. 1 shows an embodiment of the present invention. The sandwich panel 1 includes a hollow box-shaped object 4 in a sandwich panel formed by upper and lower plates 2 and ribs 3. The rib 3 and the side wall of the hollow box-shaped material 4 may be integrally formed.
【００３９】図２は本発明の別の実施態様を示したもの
である。折板形状に賦形されたサンドイッチパネル１１
の上下の板１２、およびリブ１３によって形成されたサ
ンドイッチパネル１１の中に、中空の箱状物１４が包含
されている。リブ１３と中空箱状物１４の側壁は一体成
形されてもよい。FIG. 2 shows another embodiment of the present invention. Sandwich panel 11 shaped like a folded plate
A hollow box 14 is contained in the sandwich panel 11 formed by the upper and lower plates 12 and the ribs 13. The rib 13 and the side wall of the hollow box 14 may be integrally formed.
【００４０】図３は本発明のさらに別の実施態様を示し
たものである。サンドイッチパネル２１の上下の板２２
とリブ２３、中空の箱状物２４とおよびウレタン発泡体
のコア２５のサンドイッチパネル２１の片面に耐火材２
６の層が形成されている。FIG. 3 shows still another embodiment of the present invention. Upper and lower plates 22 of sandwich panel 21
And the ribs 23, the hollow box-like material 24 and the urethane foam core 25 on one side of the sandwich panel 21
Six layers are formed.
【００４１】図４は本発明の中空の箱状物の一形態を示
したものである。図４に示す中空箱状物３１の表面（図
示例では上下面）には、溝３２が形成されており、成形
の際の樹脂の流路として機能できるようになっている。FIG. 4 shows an embodiment of the hollow box-shaped object of the present invention. A groove 32 is formed on the surface (upper and lower surfaces in the illustrated example) of the hollow box 31 shown in FIG. 4, and can function as a resin flow path during molding.
【００４２】図５は、サンドイッチパネル４１の一対の
板４２ａ、４２ｂのうちの一方の板４２ａが折板構造を
有し、両板の間隙が板延在方向に変化している例を示し
ている。４３はリブ、４４は中空箱状物を示している。
リブ４３と中空箱状物４４の側壁は一体成形されてもよ
い。FIG. 5 shows an example in which one of the pair of plates 42a and 42b of the sandwich panel 41 has a folded plate structure, and the gap between both plates changes in the plate extending direction. I have. Reference numeral 43 denotes a rib, and reference numeral 44 denotes a hollow box.
The rib 43 and the side wall of the hollow box-shaped member 44 may be integrally formed.
【００４３】図６に示すサンドイッチパネル５１では、
一対の板５２ａ、５２ｂ間に、リブ構造体としてトラス
構造体５３が設けられている。そして、内部の適当な位
置に、中空の箱状物５４とコア５５が設けられた例を示
している。In the sandwich panel 51 shown in FIG.
A truss structure 53 is provided between the pair of plates 52a and 52b as a rib structure. In addition, an example is shown in which a hollow box-shaped object 54 and a core 55 are provided at appropriate positions inside.
【００４４】さらに図７は、サンドイッチパネル６１が
全体として種々の形状を採り得ることを示しており、図
示例ではピラミッド状に形成された部分６２が連接され
た形状になっている。FIG. 7 shows that the sandwich panel 61 can take various shapes as a whole. In the illustrated example, the sandwich panel 61 has a shape in which pyramid-shaped portions 62 are connected.
【００４５】とくに図８に示すような半円形状に賦形さ
れたサンドイッチパネル７１とすることにより、屋根材
として使用する上で、より好適なものとなる。図７にお
いて、７２は一対の板、７３はリブ、７４は中空箱状物
を示している。In particular, the sandwich panel 71 formed into a semicircular shape as shown in FIG. 8 is more suitable for use as a roofing material. 7, reference numeral 72 denotes a pair of plates, 73 denotes a rib, and 74 denotes a hollow box.
【００４６】このように、本発明に係るＦＲＰサンドイ
ッチパネルは種々の形態を採り得る。とくに屋根材等の
建材に好適な種々の形態とすることができ、かつ、前述
の如く軽量でありながら十分な機械的物性を備えること
ができ、しかも安価に製造できる。As described above, the FRP sandwich panel according to the present invention can take various forms. In particular, it can be made into various forms suitable for building materials such as roofing materials, and as described above, it can be provided with sufficient mechanical properties while being lightweight, and can be manufactured at low cost.
【００４７】[0047]
【発明の効果】以上説明したように本発明のＦＲＰ製サ
ンドイッチパネルおよびその製造方法によれば、低コス
トでかつ十分な物性を備えたサンドイッチパネルが提供
できる。As described above, according to the sandwich panel made of FRP and the method of manufacturing the same according to the present invention, a sandwich panel which is low in cost and has sufficient physical properties can be provided.
【図１】本発明の一実施態様に係るＦＲＰ製サンドイッ
チパネルの部分断面図である。FIG. 1 is a partial cross-sectional view of an FRP sandwich panel according to an embodiment of the present invention.
【図２】本発明の別の実施態様に係るＦＲＰ製サンドイ
ッチパネルの部分断面図である。FIG. 2 is a partial cross-sectional view of an FRP sandwich panel according to another embodiment of the present invention.
【図３】本発明のさらに別の実施態様に係るＦＲＰ製サ
ンドイッチパネルの部分断面図である。FIG. 3 is a partial cross-sectional view of an FRP sandwich panel according to still another embodiment of the present invention.
【図４】中空箱状物の一例を示す斜視図である。FIG. 4 is a perspective view showing an example of a hollow box-shaped object.
【図５】本発明のさらに別の実施態様に係るＦＲＰ製サ
ンドイッチパネルの部分断面図である。FIG. 5 is a partial cross-sectional view of an FRP sandwich panel according to still another embodiment of the present invention.
【図６】本発明のさらに別の実施態様に係るＦＲＰ製サ
ンドイッチパネルの部分断面図である。FIG. 6 is a partial sectional view of an FRP sandwich panel according to still another embodiment of the present invention.
【図７】本発明のさらに別の実施態様に係るＦＲＰ製サ
ンドイッチパネルの部分斜視図である。FIG. 7 is a partial perspective view of an FRP sandwich panel according to still another embodiment of the present invention.
【図８】本発明のさらに別の実施態様に係るＦＲＰ製サ
ンドイッチパネルの斜視断面図である。FIG. 8 is a perspective sectional view of an FRP sandwich panel according to still another embodiment of the present invention.
１、１１、２１、４１、５１、６１、７１ ＦＲＰ製サ
ンドイッチパネル ２、１２、２２、４２ａ、４２ｂ、５２ａ、５２ｂ、７
２ 板 ３、１３、２３、４３、７３ リブ ４、１４、２４、４４、５４、７４ 中空箱状物 ２５、５５ コア ２６ 耐火材 ５３ トラス構造体 ６２ ピラミッド部分1, 11, 21, 41, 51, 61, 71 FRP sandwich panel 2, 12, 22, 42a, 42b, 52a, 52b, 7
2 plate 3, 13, 23, 43, 73 rib 4, 14, 24, 44, 54, 74 hollow box 25, 55 core 26 refractory 53 truss structure 62 pyramid
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｅ０４Ｃ 2/20 Ｅ０４Ｃ 2/30 Ｌ 2/30 Ｂ２９Ｃ 67/14 Ｌ // Ｂ２９Ｋ 61:04 Ｂ２９Ｌ 31:10 Ｆターム(参考） 2E001 DE01 FA16 GA23 GA42 GA48 HD11 HD12 JA29 KA01 2E162 CD05 FA20 GA05 GA07 GB00 4F100 AD11A AK01A AK33A AR00B BA01 BA02 BA10A BA10B DC05A DC07A DG01A DH02A EC182 EH312 EJ082 EJ242 EJ822 EJ951 GB07 JB16A JJ07B JK01 JL02 JL03 YY00A 4F205 AB18 AD05 AD16 AD17 AD18 AG28 AH43 AH47 AR14 HA06 HA09 HA14 HA22 HA33 HA35 HB01 HB11 HC17 HF23 HK16 HK31 HM02 HT26 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) E04C 2/20 E04C 2/30 L 2/30 B29C 67/14 L // B29K 61:04 B29L 31:10 F-term (reference) 2E001 DE01 FA16 GA23 GA42 GA48 HD11 HD12 JA29 KA01 2E162 CD05 FA20 GA05 GA07 GB00 4F100 AD11A AK01A AK33A AR00B BA01 BA02 BA10A BA10B DC05A DC07A DG01A DH02A EC182 EH3B12 EJ082 EJ242 EJ082 EJ082 EJ242 EJ242 AD16 AD17 AD18 AG28 AH43 AH47 AR14 HA06 HA09 HA14 HA22 HA33 HA35 HB01 HB11 HC17 HF23 HK16 HK31 HM02 HT26
Claims (17)
が間隙をもって配置され、該間隙に両板を接合するリブ
構造体が介装されているＦＲＰ製サンドイッチパネルに
おいて、中空の箱状物を該間隙に包含してなることを特
徴とするＦＲＰ製サンドイッチパネル。1. An FRP sandwich panel in which a pair of plates containing FRP is disposed on at least one side with a gap, and a rib structure for joining the two plates is interposed in the gap. An FRP sandwich panel characterized by being included in a gap.
実質的に一定である、請求項１のＦＲＰ製サンドイッチ
パネル。2. The FRP sandwich panel according to claim 1, wherein the size of the gap is substantially constant in a plate extending direction.
変化している、請求項１のＦＲＰ製サンドイッチパネ
ル。3. The FRP sandwich panel according to claim 1, wherein the dimension of the gap changes in the plate extending direction.
互に配置された折板形状に形成されている、請求項１〜
３のいずれかに記載のＦＲＰ製サンドイッチパネル。4. The at least one plate is formed in a folded plate shape in which peaks and valleys are alternately arranged.
3. The sandwich panel made of FRP according to any one of 3.
いることを特徴とする、請求項１〜４のいずれかに記載
のＦＲＰ製サンドイッチパネル。5. The sandwich panel made of FRP according to claim 1, wherein the hollow box-shaped material is made of a thermoplastic resin.
いることを特徴とする、請求項１〜４のいずれかに記載
のＦＲＰ製サンドイッチパネル。6. The FRP sandwich panel according to claim 1, wherein the hollow box-shaped material is made of a thermosetting resin.
以上であることを特徴とする請求項１〜４のいずれかに
記載のＦＲＰ製サンドイッチパネル。7. The volume of the hollow box-shaped object is 1000 cm 3
The sandwich panel made of FRP according to any one of claims 1 to 4, characterized in that:
がフェノール樹脂であることを特徴とする、請求項１〜
７のいずれかに記載のＦＲＰ製サンドイッチパネル。8. The method according to claim 1, wherein the matrix resin of at least one of the plates is a phenol resin.
7. The sandwich panel made of FRP according to any one of 7.
として炭素繊維を含むことを特徴とする、請求項１〜８
のいずれかに記載のＦＲＰ製サンドイッチパネル。9. The carbon fiber as a reinforcing fiber of the FRP of at least one of the plates.
The sandwich panel made of FRP according to any one of the above.
０００〜３００，０００本の範囲にあるトウ状の炭素繊
維フィラメント糸を有することを特徴とする、請求項９
のＦＲＰ製サンドイッチパネル。10. The reinforcing fiber having a filament number of 10,
10. It has tow-like carbon fiber filament yarns in the range of 000 to 300,000 yarns.
FRP sandwich panel.
ン構造体からなる請求項１〜１０のいずれかに記載のＦ
ＲＰ製サンドイッチパネル。11. The F according to claim 1, wherein the rib structure comprises a truss or a ramen structure.
RP sandwich panel.
いることを特徴とする、請求項１〜１１のいずれかに記
載のＦＲＰ製サンドイッチパネル。12. The FRP sandwich panel according to claim 1, wherein a refractory material is provided on at least one side.
１〜１２のいずれかに記載のＦＲＰ製サンドイッチパネ
ル。13. The sandwich panel made of FRP according to claim 1, wherein the hollow box-like object is a rectangular parallelepiped.
る、請求項１〜１２のいずれかに記載のＦＲＰ製サンド
イッチパネル。14. The sandwich panel made of FRP according to claim 1, wherein the cross section of the hollow box-shaped object is trapezoidal.
溝を有することを特徴とする、請求項１〜１４のいずれ
かに記載のＦＲＰ製サンドイッチパネル。15. The FRP sandwich panel according to claim 1, wherein a groove is formed on any one surface of the hollow box-shaped material.
ＲＰ製サンドイッチパネルを用いてなるＦＲＰ製屋根
材。16. The F according to claim 1, wherein
FRP roofing material using RP sandwich panels.
の所定の位置に強化繊維を巻いた中空の箱状物を配置
し、さらに強化繊維を配置した後、全体を真空用フィル
ム基材で覆った後フィルム基材で覆われた内部を真空に
し、樹脂を注入して強化繊維に含浸させることを特徴と
する、ＦＲＰ製サンドイッチパネルの製造方法。17. A reinforcing fiber is placed on a molding die, a hollow box-like material in which the reinforcing fiber is wound is placed at a predetermined position on the reinforcing fiber, and the reinforcing fiber is further placed. A method of manufacturing a sandwich panel made of FRP, comprising: evacuating the inside covered with a film substrate after covering with a material, and injecting a resin to impregnate the reinforcing fibers.