JP2000239685A - Grease composition for constant velocity joint - Google Patents
Grease composition for constant velocity jointInfo
- Publication number
- JP2000239685A JP2000239685A JP4544999A JP4544999A JP2000239685A JP 2000239685 A JP2000239685 A JP 2000239685A JP 4544999 A JP4544999 A JP 4544999A JP 4544999 A JP4544999 A JP 4544999A JP 2000239685 A JP2000239685 A JP 2000239685A
- Authority
- JP
- Japan
- Prior art keywords
- constant velocity
- grease composition
- velocity joint
- lithium
- grease
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、自動車の等速ジョ
イント（Ｃｏｎｓｔａｎｔ ＶｅｌｏｃｉｔｙＪｏｉｎ
ｔｓ：以下ＣＶＪと略記する）の潤滑個所に適用するた
めの等速ジョイント用グリース組成物に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a constant velocity joint for an automobile.
(ts: hereinafter abbreviated as CVJ).
【０００２】[0002]
【従来の技術】自動車のＣＶＪは、ＦＦ化の波に乗って
進歩、発展を続けてきた。最近では、自動車の高速化、
高出力化、軽量コンパクト化に伴い、ＣＶＪも小型化、
高トルク化、高速仕様化されてきており、ＣＶＪのグリ
ース潤滑におけるニーズは一段と厳しさを増してきてい
る。このような状況にあって、フレーキングを発生する
ことなく、ＣＶＪの耐久性を延ばすことが課題となって
きている。2. Description of the Related Art Automobile CVJs have continued to advance and develop along with the trend toward FF technology. These days, speeding up cars,
With high output and light weight and compact size, CVJ is also downsized.
The demands for grease lubrication of CVJs have become even more severe as high torque and high speed specifications have been adopted. Under such circumstances, it has become an issue to extend the durability of the CVJ without causing flaking.
【０００３】プランジング型ジョイント（Ｐｌｕｎｇｉ
ｎｇ Ｊｏｉｎｔｓ）においては、振動を抑制するのに
効果のある有機モリブデン化合物を含有したウレア系グ
リースが多く使用されるようになってきている。しか
し、一般にホイール側に用いる固定型ジョイント（Ｆｉ
ｘｅｄ Ｊｏｉｎｔｓ）ではコスト的に有利なリチウム
石鹸系極圧グリースが主に使われている。固定型ジョイ
ントは、高角度かつ高面圧下で使用され、内外輪みぞと
玉およびケージと玉との複雑なころがりすべり作用を受
ける。このため硫化油脂、硫化オレフィン、ポリサルフ
ァイド、硫黄−リン系などの極圧剤を添加した従来のリ
チウム石鹸系グリースでは、極圧性が不足し、異常摩耗
やフレーキングが発生し、耐久性が不充分であった。A plunging joint (Plungi)
ng Joints), urea-based greases containing an organic molybdenum compound that is effective in suppressing vibration have been increasingly used. However, fixed joints (Fi
xed Joints) mainly uses lithium soap type extreme pressure grease which is advantageous in cost. The fixed joint is used under a high angle and a high surface pressure, and is subjected to a complicated rolling and sliding action between the inner and outer ring grooves and the balls and the cage and the balls. For this reason, conventional lithium soap-based greases to which extreme pressure agents such as sulfurized oils, sulfurized olefins, polysulfides, and sulfur-phosphorus are added have insufficient extreme pressure, cause abnormal wear and flaking, and have insufficient durability. Met.
【０００４】[0004]
【発明が解決しようとする課題】本発明の目的は、ＣＶ
Ｊのフレーキングを防止する極圧性に優れた新規な等速
ジョイント用グリース組成物を提示する点にある。An object of the present invention is to provide a CV
An object of the present invention is to provide a novel grease composition for constant velocity joints which is excellent in extreme pressure property and prevents flaking of J.
【０００５】[0005]
【課題を解決するための手段】本発明は、リチウム石鹸
系増ちょう剤および／またはリチウム複合石鹸系増ちょ
う剤を用いた等速ジョイント用グリース組成物におい
て、チオ硫酸ソーダを０．０５〜３０重量％含有するこ
とを特徴とする等速ジョイント用グリース組成物に関す
る。SUMMARY OF THE INVENTION The present invention provides a grease composition for a constant velocity joint using a lithium soap-based thickener and / or a lithium composite soap-based thickener. The invention relates to a grease composition for constant velocity joints, characterized in that the grease composition contains 0.1% by weight.
【０００６】本発明の等速ジョイント用グリース組成物
は、四球式ＥＰ試験（ＡＳＴＭ Ｄ２５９６）による融
着荷重が３９２２Ｎ（４００ｋｇｆ）以上、できれば４
９０３Ｎ（５００ｋｇｆ）以上であることが好ましい。The grease composition for a constant velocity joint of the present invention has a fusion load of 3922 N (400 kgf) or more, preferably 4 kg, according to a four-ball EP test (ASTM D2596).
It is preferably at least 903 N (500 kgf).
【０００７】本発明に用いることのできる基油として
は、特別の制限はないが通常、鉱油およびエステル油、
エーテル油、炭化水素油などの合成油またはこれらの混
合油を用いることができる。The base oil which can be used in the present invention is not particularly limited, but is usually mineral oil and ester oil,
Synthetic oils such as ether oils and hydrocarbon oils or mixed oils thereof can be used.
【０００８】本発明に用いるチオ硫酸ソーダは、無水チ
オ硫酸ソーダ（Ｎａ２Ｓ２Ｏ３）、チオ硫酸ソーダ５水
和物（Ｎａ２Ｓ２Ｏ３・５Ｈ２Ｏ）またはこれらの混合
物を用いることができる。また、これらの成分を含む市
販の添加剤たとえばチオ硫酸ソーダを含む市販の添加剤
であるＤｅｓｉｌｕｂｅ８８（Ｄｅｓｉｌｕｂｅ Ｔｅ
ｃｈｎｏｌｏｇｙ Ｉｎｃ．ＵＳＡ、商品名）も使用で
きる。As the sodium thiosulfate used in the present invention, anhydrous sodium thiosulfate (Na 2 S 2 O 3 ), sodium thiosulfate pentahydrate (Na 2 S 2 O 3 .5H 2 O) or a mixture thereof is used. be able to. Also, a commercially available additive containing these components, for example, a commercially available additive containing sodium thiosulfate, Desilbe 88 (Desilbe Te)
Chronology Inc. USA, trade name).
【０００９】本発明のチオ硫酸ソーダを配合したリチウ
ム石鹸系増ちょう剤および／またはリチウム複合石鹸系
増ちょう剤を用いた等速ジョイント用グリース組成物の
「融着荷重Ｎ（ｋｇｆ）が高く、ＣＶＪのフレーキング
を防止する効果」については、チオ硫酸ソーダの硫黄が
高温において金属中の鉄と反応し、化学結合により生成
した層が金属接触を防ぎ、高面圧下において摩耗を抑制
するものと考えられる。The grease composition for a constant velocity joint using the lithium soap-based thickener and / or the lithium composite soap-based thickener containing sodium thiosulfate of the present invention has a high fusion load N (kgf). The effect of preventing the flaking of CVJ is that the sulfur of sodium thiosulfate reacts with iron in the metal at high temperature, the layer formed by chemical bonding prevents metal contact, and suppresses abrasion under high surface pressure. Conceivable.
【００１０】前記チオ硫酸ソーダの添加量は、リチウム
石鹸系増ちょう剤および／またはリチウム複合石鹸系増
ちょう剤を用いた等速ジョイント用グリース組成物全量
に対して、０．０５〜３０重量％、好ましくは０．２〜
２０重量％である。０．０５重量％未満の場合は、融着
荷重が低く、フレーキング防止効果が不充分であり、ま
た３０重量％を越えても効果の一層の増大はない。The amount of the sodium thiosulfate added is 0.05 to 30% by weight based on the total amount of the grease composition for a constant velocity joint using a lithium soap-based thickener and / or a lithium composite soap-based thickener. , Preferably 0.2 to
20% by weight. When the amount is less than 0.05% by weight, the fusion load is low, and the effect of preventing flaking is insufficient. When the amount exceeds 30% by weight, the effect is not further increased.
【００１１】また、本発明の組成物には、フエノール系
やアミン系の酸化防止剤、有機モリブデン化合物、二硫
化モリブデン、グラファイト、硫化油脂、硫化オレフィ
ン、ポリサルファイド、チアジアゾール、フォスフェー
ト、フォスファイト、チオフォスフェート、ジチオリン
酸亜鉛などの極圧／耐摩耗剤、ポリブテン、ポリメタク
リレート、ポリイソブチレンなどの増粘剤など公知の各
種添加剤を配合することができる。[0011] The composition of the present invention includes a phenol-based or amine-based antioxidant, an organic molybdenum compound, molybdenum disulfide, graphite, sulfurized oil and fat, sulfurized olefin, polysulfide, thiadiazole, phosphate, phosphite, and thiophosphate. And various known additives such as an extreme pressure / antiwear agent such as zinc oxide and zinc dithiophosphate, and a thickener such as polybutene, polymethacrylate, and polyisobutylene.
【００１２】[0012]
【実施例】本発明を実施例および比較例を挙げて説明す
るが、本発明はこれによりなんら限定されるものではな
い。EXAMPLES The present invention will be described with reference to examples and comparative examples, but the present invention is not limited thereto.
【００１３】表１および表２に示す組成配合で基グリー
スへ各種添加剤を加え、三本ロールで処理し、実施例お
よび比較例の等速ジョイント用グリース組成物を得た。
表中のリチウム石鹸系基グリースおよびリチウム複合石
鹸系基グリースはつぎのとおりのものである。また、表
中の組成に関する数字の単位は重量％である。Various additives were added to the base grease according to the composition shown in Tables 1 and 2, and treated with a three-roll mill to obtain grease compositions for constant velocity joints of Examples and Comparative Examples.
The lithium soap-based grease and lithium composite soap-based grease in the table are as follows. Further, the unit of the numerical value relating to the composition in the table is% by weight.
【００１４】１．リチウム石鹸系基グリース １００℃の粘度が約１１ｍｍ２／ｓの鉱油５４００ｇ中
で１２−ヒドロキシステアリン酸リチウム６００ｇを溶
解し、均一に分散処理することにより、ちょう度（２５
℃、６０Ｗ）２７１、適点１９８℃の性状を有する等速
ジョイント用グリース組成物を得た。リチウム石鹸の含
有量は１０重量％である。1. Lithium soap base grease Dissolve 600 g of lithium 12-hydroxystearate in 5400 g of mineral oil having a viscosity at 100 ° C. of about 11 mm 2 / s, and uniformly disperse to obtain a consistency (25%).
C., 60 W) 271 and a grease composition for constant velocity joints having properties of 198.degree. The content of lithium soap is 10% by weight.
【００１５】２．リチウム複合石鹸系基グリース １００℃の粘度が約１５ｍｍ２／ｓの鉱油４１６５ｇ中
で１２−ヒドロキシステアリン酸リチウム３５０ｇを水
酸化リチウム５０．５ｇと反応させた後、アゼライン酸
１２０．６５ｇを水酸化リチウム５９．０ｇと反応さ
せ、均一に分散処理することにより、ちょう度（２５
℃、６０Ｗ）２９５、適点２５８℃の性状を有する等速
ジョイント用グリース組成物を得た。リチウム石鹸の含
有量は１０．４重量％である。2. Lithium composite soap-based grease After reacting 350 g of lithium 12-hydroxystearate with 50.5 g of lithium hydroxide in 4165 g of mineral oil having a viscosity of about 15 mm2 / s at 100 ° C., 120.65 g of azelaic acid is converted to lithium hydroxide 59 2.0 g, and uniformly dispersed to obtain a consistency (25
C., 60 W) 295 and a grease composition for a constant velocity joint having properties of 258 ° C. at an appropriate point. The content of lithium soap is 10.4% by weight.
【００１６】得られた等速ジョイント用グリース組成物
についてＡＳＴＭ Ｄ２５９６に規定する四球式ＥＰ試
験（ＡＳＴＭ Ｄ２５９６）による融着荷重Ｎ（ｋｇ
ｆ）を求めた。これらの結果は、表１〜２に示す。な
お、表中の１）〜９）は下記のとおりである。The obtained grease composition for constant velocity joints has a welding load N (kg) according to a four-ball EP test (ASTM D2596) specified in ASTM D2596.
f) was determined. These results are shown in Tables 1-2. In addition, 1) to 9) in the table are as follows.
【００１７】１）Ｄｅｓｉｌｕｂｅ８８（Ｄｅｓｉｌｕ
ｂｅ ＴｅｃｈｎｏｌｏｇｙＩｎｃ．製、商品名）は、
チオ硫酸ソーダを含んだ無機のＳ−Ｐ系添加剤である。 ２）Ｐｂ−ＤＴＣ（レッドジチオカーバメート）は、Ｖ
ａｎｌｕｂｅ７１（Ｖａｎｄｅｒｂｉｌｔ社製、商品
名）である。 ３）Ｚｎ−ＤＴＰ（ジンクジチオフォスフェート）は、
Ｌｕｂｒｉｚｏｌ１３７０（Ｌｕｂｒｉｚｏｌ社製、商
品名）である。 ４）ポリサルファイドは、ＴＰＳ３２（フランスｅｌｆ
ＡＴＯＣＨＥＭ社製、商品名）である。 ５）Ｍｏ−ＤＴＰ（モリブデンジチオフォスフェート）
は、ＭｏｌｙｖａｎＬ（Ｖａｎｄｅｒｂｉｌｔ社製、商
品名）である。 ６）硫化オレフィンは、Ａｎｇｌａｍｏｌ３３（Ｌｕｂ
ｒｉｚｏｌ社製、商品名）である。 ７）無灰ジチオカーバメートは、Ｖａｎｌｕｂｅ７７２
３（Ｖａｎｄｅｒｂｉｌｔ社製、商品名）である。 ８）Ｚｎ−ＤＴＣ（ジンクジチオカーバメート）は、Ｖ
ａｎｌｕｂｅ ＡＺ（Ｖａｎｄｅｒｂｉｌｔ社製、商品
名）である。 ９）硫化油脂は、Ｌｕｂｒｉｚｏｌ５００６（Ｌｕｂｒ
ｉｚｏｌ社製、商品名）である。1) Desilube 88 (Desilu
be Technology Inc .. Product name)
It is an inorganic SP additive containing sodium thiosulfate. 2) Pb-DTC (red dithiocarbamate)
anlube71 (manufactured by Vanderbilt, trade name). 3) Zn-DTP (zinc dithiophosphate)
Lubrizol 1370 (trade name, manufactured by Lubrizol). 4) Polysulfide is TPS32 (France elf)
ATOCHEM (trade name). 5) Mo-DTP (molybdenum dithiophosphate)
Is MolyvanL (trade name, manufactured by Vanderbilt). 6) Sulfurized olefins are available from Anglamol 33 (Lub)
Rizol, trade name). 7) Ashless dithiocarbamate is Vanlube 772
3 (manufactured by Vanderbilt, trade name). 8) Zn-DTC (zinc dithiocarbamate)
anlube AZ (trade name, manufactured by Vanderbilt). 9) Sulfurized fats and oils, Lubrizol 5006 (Lubr
izol, trade name).
【００１８】[0018]
【表１】 [Table 1]
【００１９】[0019]
【表２】 [Table 2]
【００２０】[0020]
【効果】本発明の等速ジョイント用グリース組成物は、
従来の等速ジョイント用グリース組成物よりも融着荷重
が高く、有効なフレーキング防止性を与え、その結果、
等速ジョイントの耐久性が向上する。The grease composition for a constant velocity joint of the present invention
Higher fusing load than conventional grease compositions for constant velocity joints, giving effective anti-flaking properties, as a result
The durability of the constant velocity joint is improved.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 益森 隆一 東京都港区台場二丁目３番２号 昭和シェ ル石油株式会社内 Ｆターム(参考） 4H104 AA18C BB15B BB19B DA02A EA01A EB02 FA01 LA03 PA01 QA18 ────────────────────────────────────────────────── ─── Continued on the front page (72) Inventor Ryuichi Masmori 2-3-2 Daiba, Minato-ku, Tokyo Showa Shell Sekiyu KK F-term (reference) 4H104 AA18C BB15B BB19B DA02A EA01A EB02 FA01 LA03 PA01 QA18
Claims (2)
はリチウム複合石鹸系増ちょう剤を用いた等速ジョイン
ト用グリース組成物において、チオ硫酸ソーダを０．０
５〜３０重量％含有することを特徴とする等速ジョイン
ト用グリース組成物。1. A grease composition for a constant velocity joint using a lithium soap-based thickener and / or a lithium composite soap-based thickener, wherein sodium thiosulfate is contained in an amount of 0.03%.
A grease composition for a constant velocity joint, comprising 5 to 30% by weight.
６）による融着荷重が３９２２Ｎ（４００ｋｇｆ）以上
である請求項１記載の等速ジョイント用グリース組成
物。2. A four-ball EP test (ASTM D259)
The grease composition for a constant velocity joint according to claim 1, wherein the fusion load according to 6) is 3922 N (400 kgf) or more.