JP2000239621A - Double-coated self-adhesive tape and perforated docorative sheet - Google Patents
Double-coated self-adhesive tape and perforated docorative sheetInfo
- Publication number
- JP2000239621A JP2000239621A JP11044084A JP4408499A JP2000239621A JP 2000239621 A JP2000239621 A JP 2000239621A JP 11044084 A JP11044084 A JP 11044084A JP 4408499 A JP4408499 A JP 4408499A JP 2000239621 A JP2000239621 A JP 2000239621A
- Authority
- JP
- Japan
- Prior art keywords
- sensitive adhesive
- pressure
- double
- adhesive layer
- adhesive tape
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、支持体の両面に粘
着剤層を有する両面粘着テープに関する。また、本発明
は、該両面粘着テープによって形成された粘着剤層を裏
面に有する、有孔化粧シートに関する。特に本発明は、
支持体の少なくとも一面の粘着剤層が、表面に凹凸が形
成されており、かつ紫外線照射によって硬化して、その
露出面が非粘着性（「タックフリー」ともいう）となる
粘着剤からなる両面粘着テープに関する。さらに、本発
明は、該両面粘着テープを配設することによって形成さ
れた粘着剤層を裏面に有する有孔化粧シートに関する。TECHNICAL FIELD The present invention relates to a double-sided pressure-sensitive adhesive tape having a pressure-sensitive adhesive layer on both sides of a support. The present invention also relates to a perforated decorative sheet having a pressure-sensitive adhesive layer formed by the double-sided pressure-sensitive adhesive tape on the back surface. In particular, the present invention
At least one side of the pressure-sensitive adhesive layer of the support has irregularities on its surface, and is cured by irradiation with ultraviolet rays, and the exposed surface thereof is made of a pressure-sensitive adhesive (also referred to as “tack-free”). Related to adhesive tape. Further, the present invention relates to a perforated decorative sheet having a pressure-sensitive adhesive layer formed on the back surface by disposing the double-sided pressure-sensitive adhesive tape.
【０００２】[0002]
【従来の技術】たとえば、テレビやラジオのキャビネッ
トに接着固定されているスピーカーネットのように、多
数の開孔を有する多孔シート部材をキャビネットへ接着
固定する場合、両面接着テープを使用するのが普通であ
る。2. Description of the Related Art For example, when a perforated sheet member having a large number of openings is adhered and fixed to a cabinet, such as a speaker net adhered and fixed to a television or radio cabinet, it is common to use a double-sided adhesive tape. It is.
【０００３】このような多孔シート部材の場合、通常、
両面粘着テープで電気製品のキャビネット等に貼着した
場合、多孔シート部材中の多数の開孔内に両面粘着テー
プの粘着剤層が露出して外部から見える状態となってい
るため、両面粘着テープ面が塵埃付着等の原因となると
いう問題を有している。また、多孔シート側から光が当
たると、開孔内に露出している平滑な両面接着テープ面
が光を反射して、通常は艶消し面とされていることが多
い多孔シート外面と調和しなくなり、多孔シート部分の
外観を損ねる結果となるという問題がある。In the case of such a porous sheet member, usually,
When affixed to an electric appliance cabinet or the like with a double-sided adhesive tape, the adhesive layer of the double-sided adhesive tape is exposed and visible from the outside in many openings in the porous sheet member. There is a problem that the surface causes dust adhesion and the like. In addition, when light is irradiated from the perforated sheet side, the smooth double-sided adhesive tape surface exposed in the opening reflects light, and is in harmony with the outer surface of the perforated sheet which is usually matted. And the appearance of the porous sheet portion is impaired.
【０００４】上記の問題を解決するために、黒の紗を粘
着剤層と多孔シート部材との間に配置したり、紗を多孔
シート面を覆って張りつけたりして、開孔内に粘着剤面
が露出することを防ぐ手段がとられることが行われてお
り、他に、黒の艶消し塗料のスプレーを開孔部内の接着
剤面に噴射して艶消しと同時に粘着剤層面をタックフリ
ー状態に変えることなどが行われているが、いずれも工
程数が多くなるし、また材料費が嵩むという問題があ
る。In order to solve the above-mentioned problems, a black gauze is disposed between the adhesive layer and the porous sheet member, or a gauze is attached to the porous sheet so as to cover the porous sheet surface. In addition, measures are taken to prevent the surface from being exposed.In addition, a spray of black matting paint is sprayed on the adhesive surface in the opening and the adhesive layer surface is tack-free at the same time as matting Although the state is changed, there is a problem that the number of steps increases and the material cost increases.
【０００５】他には、多孔シートに貼着する側の粘着剤
層を加熱膨張剤を添加したホットメルトで形成した両面
粘着テープも提案されている（特開平４−１９８２９０
号公報）。この両面粘着テープによれば、化粧シートの
開孔内に露出している粘着剤層の粘着性はホットメルト
が冷却された時点で消滅するし（タックフリー状態にな
る）、該露出面が光を反射する点も、膨張剤の膨張によ
って形成される表面凹凸によって解決されるという利点
がある。しかし、多孔シートが熱可塑性樹脂シートの場
合は、ホットメルトを溶融させる際の熱に耐えることが
できないため、使用できない場合が多いし、仮に適用で
きるような融着温度条件を採用したとしても、ホットメ
ルト融着時の加熱による化粧シートの変形や寸法変化を
皆無とすることはできないため好ましくない。[0005] In addition, a double-sided pressure-sensitive adhesive tape in which a pressure-sensitive adhesive layer to be adhered to a porous sheet is formed of a hot melt to which a heat-expanding agent is added has been proposed (Japanese Patent Laid-Open No. 4-198290).
No.). According to this double-sided pressure-sensitive adhesive tape, the tackiness of the pressure-sensitive adhesive layer exposed in the opening of the decorative sheet disappears when the hot melt is cooled (changes to a tack-free state), and the exposed surface is exposed to light. There is an advantage that the point of reflecting is also solved by the surface unevenness formed by the expansion of the expanding agent. However, if the porous sheet is a thermoplastic resin sheet, it cannot withstand the heat of melting the hot melt, so it cannot be used in many cases, and even if a fusing temperature condition that can be applied is adopted, It is not preferable because deformation and dimensional change of the decorative sheet due to heating during hot melt fusion cannot be eliminated.
【０００６】[0006]
【発明が解決しようとする課題】本発明は、通常の両面
粘着テープの製造装置で製造することができる支持体付
両面粘着テープであり、少なくとも一面の粘着剤層が黒
色で、紫外線照射によってその粘着剤層面が非粘着性
（タックフリー）に変化する粘着剤層で形成されている
両面粘着テープと、該両面粘着テープを裏面に配設して
なる有孔シート部材を提供することを目的とするもので
ある。SUMMARY OF THE INVENTION The present invention relates to a double-sided pressure-sensitive adhesive tape with a support, which can be produced by a usual double-sided pressure-sensitive adhesive tape production apparatus, wherein at least one surface of the pressure-sensitive adhesive layer is black and is irradiated with ultraviolet rays. An object of the present invention is to provide a double-sided pressure-sensitive adhesive tape formed of a pressure-sensitive adhesive layer whose pressure-sensitive adhesive layer surface changes to non-tacky (tack-free), and a perforated sheet member provided with the double-sided pressure-sensitive adhesive tape on the back surface. Is what you do.
【０００７】[0007]
【課題を解決するための手段】以上の課題を解決するた
めの本発明は、次の各発明を包含する。The present invention for solving the above problems includes the following inventions.
【０００８】(1) 支持体の一面に設けられている粘着剤
層が、紫外線照射によって実質的に非粘着性に変化する
粘着剤層からなることを特徴とする、両面粘着テープ。(1) A double-sided pressure-sensitive adhesive tape, characterized in that the pressure-sensitive adhesive layer provided on one surface of the support comprises a pressure-sensitive adhesive layer which changes to substantially non-tacky by irradiation with ultraviolet rays.
【０００９】(2) 前記紫外線照射によって実質的に非粘
着性となる粘着剤層に凹凸面を有する剥離ライナーを配
設したことを特徴とする、(1) 項記載の両面粘着テー
プ。 (3) 前記凹凸面を有する剥離ライナーを配設した粘着剤
層の反対側粘着剤層にも剥離ライナーを有することを特
徴とする、(2) 項記載の両面接着テープ。(2) The double-sided pressure-sensitive adhesive tape according to (1), wherein a release liner having an uneven surface is provided on the pressure-sensitive adhesive layer which becomes substantially non-tacky by the irradiation of the ultraviolet rays. (3) The double-sided adhesive tape according to the item (2), wherein the pressure-sensitive adhesive layer on the opposite side of the pressure-sensitive adhesive layer provided with the release liner having the uneven surface has a release liner.
【００１０】(4) 有孔シートと、支持体の一面の粘着剤
層が、表面に凹凸が形成されておりかつ紫外線照射によ
って実質的に非粘着性となる粘着剤層である両面粘着テ
ープとからなり、該両面粘着テープの該紫外線照射によ
って非粘着性となる粘着剤層面と有孔シートの裏面とを
対面貼着し、ついで該有孔シート側から紫外線照射して
形成されていることを特徴とする、裏面に粘着剤層が設
けられた有孔シート。(4) A perforated sheet and a double-sided pressure-sensitive adhesive tape in which the pressure-sensitive adhesive layer on one surface of the support is a pressure-sensitive adhesive layer having irregularities formed on the surface and becoming substantially non-tacky by ultraviolet irradiation. Consisting of a double-sided pressure-sensitive adhesive tape, the pressure-sensitive adhesive layer surface of the double-sided pressure-sensitive adhesive tape, which becomes non-adhesive due to the ultraviolet irradiation, and the back surface of the perforated sheet face-to-face bonded, and then formed by irradiating ultraviolet light from the perforated sheet side. A perforated sheet having a pressure-sensitive adhesive layer on the back surface.
【００１１】(5) 前記有孔シートは、紫外線非透過性の
熱可塑性合成樹脂製で、パンチング加工された多孔化粧
シートであることを特徴とする、(4) 項記載の裏面に粘
着剤層が設けられた有孔シート。 (6) 前記有孔シートは、スピーカーネットであることを
特徴とする、(4) 項又は(5) 項に記載の裏面に粘着剤層
が設けられた有孔シート。 (7) 紫外線非透過性の有孔シートの裏面に、紫外線照射
によって非粘着性となる粘着剤層を一面に有する両面粘
着テープを、該紫外線照射によって非粘着性となる粘着
剤層側を対面貼着して一体化し、ついで、該有孔シート
側から紫外線照射して該有孔シートの開孔内に露出して
いる粘着剤面を硬化させることによって非粘着性面（タ
ックフフリー面）とすることを特徴とする、裏面に粘着
剤層を有する有孔シートの製造方法。(5) The perforated sheet is made of a thermoplastic synthetic resin that is impermeable to ultraviolet light and is a perforated porous decorative sheet. The backing sheet according to (4), wherein Perforated sheet provided with. (6) The perforated sheet according to the above (4) or (5), wherein the pressure-sensitive adhesive layer is provided on the back surface, wherein the perforated sheet is a speaker net. (7) A double-sided pressure-sensitive adhesive tape having a pressure-sensitive adhesive layer that becomes non-adhesive by irradiation with ultraviolet light on the back surface of a perforated sheet that is not permeable to ultraviolet light, facing the pressure-sensitive adhesive layer that becomes non-adhesive by irradiation with ultraviolet light. Non-adhesive surface (tack-free surface) by applying UV light from the perforated sheet side to cure the pressure-sensitive adhesive surface exposed in the opening of the perforated sheet. A method for producing a perforated sheet having a pressure-sensitive adhesive layer on the back surface thereof.
【００１２】[0012]
【発明の実施の形態】本発明の両面粘着テープは、支持
体の少なくとも一面に紫外線照射によって硬化して非粘
着性、すなわち、タックフリー状態に変化する性質を有
する粘着剤層を有している。上記両面粘着テープに使用
される、紫外線照射によって硬化してタックフリー状態
に変化する粘着剤としては、上記の特性を有する粘着剤
として既に知られている種類の粘着剤を使用することが
できる。BEST MODE FOR CARRYING OUT THE INVENTION The double-sided pressure-sensitive adhesive tape of the present invention has a pressure-sensitive adhesive layer on at least one surface of a support, which is cured by irradiation with ultraviolet rays and has a non-tacky property, that is, a property of changing to a tack-free state. . As the pressure-sensitive adhesive used for the double-sided pressure-sensitive adhesive tape, which changes to a tack-free state by being irradiated with ultraviolet rays, a pressure-sensitive adhesive already known as a pressure-sensitive adhesive having the above-mentioned properties can be used.
【００１３】たとえば、特公平１−５６１１２号公報に
記載されている、ウエハダイシング用粘着シートに用い
られている、ポリエステル型又はポリエーテル型のポリ
オール化合物と、多価イソシアナート化合物とを反応さ
せて得られる末端イソシアナートウレタンプレポリマー
にヒドロキシル基を有する（メタ）アクリレートを反応
させて得られる、分子量が３０００〜１００００のウレ
タンアクリレート系オリゴマー、特公平７−１２０６４
０号公報に記載されている半導体用放射線硬化性粘着テ
ープに使用されている、アクリル系粘着剤と、炭素−炭
素二重結合を有するシアヌレート化合物及び／又はイソ
シアヌレート化合物の組合せからなる粘着剤、特公平６
−３５５６９号公報に記載されている感圧接着性シート
に使用されている粘着剤等が使用できる。For example, a polyester-type or polyether-type polyol compound used for an adhesive sheet for wafer dicing described in Japanese Patent Publication No. 1-56112 is reacted with a polyvalent isocyanate compound. Urethane acrylate oligomer having a molecular weight of 3,000 to 10,000, obtained by reacting a (meth) acrylate having a hydroxyl group with the obtained terminal isocyanate urethane prepolymer, Japanese Patent Publication No. 7-120064
No. 0, used for a radiation-curable pressure-sensitive adhesive tape for a semiconductor, an acrylic pressure-sensitive adhesive, a pressure-sensitive adhesive comprising a combination of a cyanurate compound and / or an isocyanurate compound having a carbon-carbon double bond, Tokuhei 6
The pressure-sensitive adhesive used for the pressure-sensitive adhesive sheet described in JP-A-35569 can be used.
【００１４】また、特開昭６０−１９６９５６号公報、
特開昭６０−２２３１３９号公報に記載されているよう
な、光照射によって三次元網状化する、分子内に光重合
性炭素−炭素二重結合を２個以上有する低分子量化合物
からなる粘着剤も使用することができる。また、特公平
６−１６５２４号公報、に記載されているような光重合
性粘着剤組成物を含む接着剤組成物も使用可能である。
これらの接着剤は、支持体上に３０〜１５０μｍ、好ま
しくは５０〜８０μｍの厚さで設けられる。Further, Japanese Patent Application Laid-Open No. Sho 60-196965,
As described in JP-A-60-223139, pressure-sensitive adhesives which are three-dimensionally reticulated by light irradiation and are composed of low molecular weight compounds having two or more photopolymerizable carbon-carbon double bonds in the molecule are also available. Can be used. Further, an adhesive composition containing a photopolymerizable pressure-sensitive adhesive composition as described in JP-B-6-16524 can also be used.
These adhesives are provided on the support with a thickness of 30 to 150 μm, preferably 50 to 80 μm.
【００１５】本発明の両面接着テープの紫外線硬化型粘
着剤以外の粘着剤としては、通常の両面接着テープに使
用されている粘着剤を使用することができる。たとえ
ば、アクリル系、ゴム系等を挙げることができる。これ
らの接着剤は、支持体上に３０〜１５０μｍ、好ましく
は５０〜８０μｍの厚さで設けられる。As the pressure-sensitive adhesive other than the UV-curable pressure-sensitive adhesive of the double-sided adhesive tape of the present invention, the pressure-sensitive adhesive used in ordinary double-sided adhesive tapes can be used. For example, acrylic type, rubber type and the like can be mentioned. These adhesives are provided on the support with a thickness of 30 to 150 μm, preferably 50 to 80 μm.
【００１６】本発明の両面接着テープの支持体として
は、レーヨン不織布、ポリエステルフィルム、和紙、そ
の他一般的な両面テープ用支持体が使用できる。支持体
は、通常、１０〜５０μｍの厚さのものが使用される。As the support for the double-sided adhesive tape of the present invention, rayon nonwoven fabric, polyester film, Japanese paper, and other general support for double-sided tape can be used. The support usually has a thickness of 10 to 50 μm.
【００１７】本発明の両面接着テープの剥離ライナーと
しては、上質紙やグラシン紙、合成樹脂フィルム等の表
面に、たとえばシリコーン樹脂等による離型剤処理を施
したものが使用される。剥離ライナーは、前記紫外線照
射によって粘着性が失われる粘着剤層と接する面に凹凸
があるものが好ましく、エンボス加工された上質紙やグ
ラシン紙、合成樹脂フィルム等の表面に離型剤処理を施
したものが好ましい。As the release liner of the double-sided adhesive tape of the present invention, a release liner treated with, for example, a silicone resin or the like on the surface of high quality paper, glassine paper, synthetic resin film or the like is used. The release liner preferably has irregularities on the surface in contact with the pressure-sensitive adhesive layer whose adhesiveness is lost by the ultraviolet irradiation, and the surface of embossed high-quality paper, glassine paper, synthetic resin film, or the like is subjected to a release agent treatment. Are preferred.
【００１８】本発明における、支持体の少なくとも一面
に紫外線照射によって硬化し、表面がタックフリー状態
に変化する粘着剤層を有する両面接着テープは、支持体
を有する両面接着テープの通常の製造装置を用いて、支
持体の両面に粘着剤層を形成することによって製造する
ことができる。In the present invention, the double-sided adhesive tape having a pressure-sensitive adhesive layer which is cured by irradiation of ultraviolet rays on at least one surface of the support and changes its surface into a tack-free state, is a conventional double-sided adhesive tape manufacturing apparatus having a support. It can be manufactured by forming a pressure-sensitive adhesive layer on both sides of a support.
【００１９】[0019]
【実施例】以下、実施例により本発明を具体的に説明す
るが、本発明は以下の実施例に限定されるものではな
い。EXAMPLES The present invention will be specifically described below with reference to examples, but the present invention is not limited to the following examples.
【００２０】実施例１： 両面粘着テープの製造：紫外線によってタックフリーと
なる下記組成の粘着剤層（Ａ）をエンボス加工した剥離
ライナー（１）面に乾燥後厚さ６０μｍになるように塗
布し、１００℃で３分間乾燥した後、４０μｍのレーヨ
ン不織布からなる支持体（Ｃ）を貼り合わせた。つぎ
に、別の剥離ライナー（２）に、下記組成のアクリル系
粘着剤（Ｂ）を乾燥後厚さ６０μｍになるように塗布
し、１００℃で３分間乾燥した後、上記支持体（Ｃ）の
片側（粘着剤Ａの反対面）に貼り合わせ、粘着剤（Ｂ）
面を内側にして巻き取って、図１に示す積層構造を有す
る両面粘着テープを製造した。このテープを２０ｍｍ幅
にスリットし、小巻サンプルとした。Example 1: Production of a double-sided pressure-sensitive adhesive tape: A pressure-sensitive adhesive layer (A) having the following composition, which is tack-free by ultraviolet rays, is applied to an embossed release liner (1) surface after drying to a thickness of 60 μm. After drying at 100 ° C. for 3 minutes, a support (C) made of a 40 μm rayon non-woven fabric was bonded. Next, an acrylic pressure-sensitive adhesive (B) having the following composition was applied to another release liner (2) so as to have a thickness of 60 μm after drying, and dried at 100 ° C. for 3 minutes. On one side (opposite side of adhesive A), adhesive (B)
Winding was performed with the surface facing inward to produce a double-sided pressure-sensitive adhesive tape having a laminated structure shown in FIG. This tape was slit into a width of 20 mm to obtain a small volume sample.
【００２１】粘着剤Ａ：アクリル酸２エチルヘキシル７
０部、アクリル酸ブチル２５部、アクリル酸５部からな
る配合組成物をトルエン・酢酸エチル溶媒中で重合さ
せ、数平均分子量３８００００のアクリル系共重合物の
４０％溶液を得た。この共重合物溶液１００部に、トリ
メチロールプロパントリイソシアネート（日本ポリウレ
タン社製、商品名：コロネートＬ）２部、多官能オリゴ
エステルアクリレート（東亜合成化学工業社製、商品
名：アロニックスＭ−８０３０）１５部、カーボンブラ
ック粉体０．５部及びα−ヒドロキシシクロヘキシルフ
ェニルケトン１部を添加して混合し、紫外線によってタ
ックフリーとなる粘着剤Ａを調製した。Adhesive A: 2-ethylhexyl acrylate 7
A mixture composition comprising 0 parts, 25 parts of butyl acrylate, and 5 parts of acrylic acid was polymerized in a toluene / ethyl acetate solvent to obtain a 40% solution of an acrylic copolymer having a number average molecular weight of 380000. To 100 parts of the copolymer solution, 2 parts of trimethylolpropane triisocyanate (trade name: Coronate L, manufactured by Nippon Polyurethane Co., Ltd.) and a polyfunctional oligoester acrylate (trade name: Aronix M-8030, manufactured by Toa Gosei Chemical Industry Co., Ltd.) 15 parts, 0.5 part of carbon black powder and 1 part of α-hydroxycyclohexyl phenyl ketone were added and mixed to prepare an adhesive A which became tack-free by ultraviolet rays.
【００２２】粘着剤Ｂ：アクリル酸２エチルヘキシル５
０部、アクリル酸ブチル４５部、アクリル酸４．８部、
アクリル酸２ヒドロキシエチル０．２部からなる配合組
成物をトルエン・酢酸エチル溶媒中で重合させ、数平均
分子量４５００００のアクリル系共重合物の４０％溶液
を得た。この共重合物溶液１００部に、テルペンフェノ
ール樹脂（ヤスハラケミカル社製、商品名：ＹＳポリス
ター２１１０）４部及びトリメチロールプロパントリイ
ソシアネート（日本ポリウレタン社製、商品名：コロネ
ートＬ）２．５部を添加して混合し、粘着剤Ｂを調製し
た。Adhesive B: 2-ethylhexyl acrylate 5
0 parts, butyl acrylate 45 parts, acrylic acid 4.8 parts,
A blended composition comprising 0.2 parts of 2-hydroxyethyl acrylate was polymerized in a toluene / ethyl acetate solvent to obtain a 40% solution of an acrylic copolymer having a number average molecular weight of 450,000. To 100 parts of this copolymer solution, 4 parts of a terpene phenol resin (trade name: YS Polystar 2110, manufactured by Yasuhara Chemical Co., Ltd.) and 2.5 parts of trimethylolpropane triisocyanate (trade name: Coronate L, manufactured by Nippon Polyurethane Co., Ltd.) are added. And mixed to prepare an adhesive B.
【００２３】剥離ライナー（１）：サンドマット処理し
たポリエステルフィルム（７５μｍ）のマット処理面に
シリコン離型剤処理した。 剥離ライナー（２）：グラシン紙セパレーター（平滑
面）Release Liner (1): A matting surface of a polyester film (75 μm) subjected to a sand mat treatment was treated with a silicone release agent. Release liner (2): Glassine paper separator (smooth surface)
【００２４】実施例２： 裏面に粘着剤層を有するパンチング加工シートの製造：
ポリスチレン系樹脂を主成分とする樹脂にカーボンブラ
ックを配合した樹脂製の厚さ０．５ｍｍのシートに孔径
０．１〜１．０ｍｍのパンチング孔を多数施したパンチ
ング加工シートを用意し、その裏面に、実施例１で製造
した小巻テープから両面粘着テープの粘着剤（Ａ）側剥
離ライナー（１）を取り除きながら巻出して、露出する
凹凸面を有する粘着剤層（Ａ）を貼着した。ついで、該
パンチング加工シートの表面側から、紫外線照射装置
（フュージョン社製）の高圧水銀ランプにより３００ｍ
Ｊ／ｃｍ2 の紫外線を照射し、パンチング孔内に露出す
る粘着剤（Ａ）層を硬化させた。製造されたパンチング
加工シートは、表面が黒色であり、パンチング孔内の粘
着剤層（Ａ）面は、タックフリー面で、かつ艶消し面で
あり、黒色の粘着剤（Ｂ）層によって黒色を呈し、黒色
の加工シート面と調和した外観のパンチング孔を形成し
ていた。Example 2: Production of a punched sheet having an adhesive layer on the back side:
Prepare a punched sheet in which a large number of punched holes with a hole diameter of 0.1 to 1.0 mm are formed on a resin sheet of 0.5 mm thickness made of a resin composed mainly of polystyrene resin mixed with carbon black, The tape was unwound while removing the adhesive (A) -side release liner (1) of the double-sided pressure-sensitive adhesive tape from the small-sized tape manufactured in Example 1, and the pressure-sensitive adhesive layer (A) having an exposed uneven surface was stuck. . Then, 300 m from the surface side of the punched sheet by a high pressure mercury lamp of an ultraviolet irradiation device (manufactured by Fusion).
The adhesive (A) layer exposed in the punched holes was cured by irradiating ultraviolet rays of J / cm 2 . The surface of the produced punched sheet is black, the surface of the pressure-sensitive adhesive layer (A) in the punched hole is a tack-free surface and a matte surface, and the black color is formed by the black pressure-sensitive adhesive (B) layer. The punched holes had an appearance that was in harmony with the black processed sheet surface.
【００２５】比較例１：実施例１において、粘着剤組成
物（Ａ）を用いる代わりに、支持体両面に粘着剤組成物
（Ｂ）を塗布し、また、剥離ライナーとして、エンボス
加工を行わない剥離ライナーを使用すること以外は実施
例１と同様にして両面粘着テープを製造した。ついで、
この両面粘着テープを一面の剥離ライナーを剥離した面
と、実施例１で製造した両面粘着テープの粘着剤（Ａ）
側剥離ライナーを剥離した面とに、実施例２で使用した
紫外線照射装置から紫外線を照射し、両テープの紫外線
照射面について、光沢度、粘着力及びタックを測定し
た。また、両テープの裏面ライナーを除いた粘着剤面に
ついても、紫外線照射を行わずに同様の測定を行った。Comparative Example 1: Instead of using the pressure-sensitive adhesive composition (A) in Example 1, the pressure-sensitive adhesive composition (B) is applied to both surfaces of the support, and no embossing is performed as a release liner. A double-sided pressure-sensitive adhesive tape was produced in the same manner as in Example 1 except that a release liner was used. Then
One side of the double-sided pressure-sensitive adhesive tape from which one release liner was peeled off, and the pressure-sensitive adhesive (A) of the double-sided pressure-sensitive adhesive tape manufactured in Example 1
The surface from which the side release liner was peeled off was irradiated with ultraviolet light from the ultraviolet light irradiation device used in Example 2, and the ultraviolet light irradiated surfaces of both tapes were measured for glossiness, adhesion and tack. In addition, the same measurement was performed on the pressure-sensitive adhesive surface excluding the back liner of both tapes without performing ultraviolet irradiation.
【００２６】比較例２：実施例１において、粘着剤組成
物（Ａ）の代わりに、カーボンブラック粉体０．５部を
加えた粘着剤組成物（Ｂ）を使用した以外は実施例１と
同様にして両面粘着テープを製造した。ついで、この両
面粘着テープの粘着剤組成物（Ｂ）側のエンボス加工剥
離ライナーを剥離した面に、実施例２で使用した紫外線
照射装置から紫外線を照射し、光沢度、粘着力及びタッ
クを測定した。また、該テープの裏面ライナーを除いた
粘着剤面についても、紫外線照射を行わずに同様の測定
を行った。Comparative Example 2 Example 1 was repeated except that the pressure-sensitive adhesive composition (B) to which 0.5 part of carbon black powder was added was used instead of the pressure-sensitive adhesive composition (A). Similarly, a double-sided pressure-sensitive adhesive tape was produced. Then, the surface from which the embossed release liner on the side of the pressure-sensitive adhesive composition (B) of the double-sided pressure-sensitive adhesive tape was released was irradiated with ultraviolet rays from the ultraviolet irradiation device used in Example 2 to measure glossiness, adhesive strength and tack. did. In addition, the same measurement was performed on the pressure-sensitive adhesive surface except for the back liner of the tape, without performing ultraviolet irradiation.
【００２７】なお、タック測定は、ポリケンプローブタ
ックテスター「ＭＯＤＥＬ−ＴＭＩ−Ｎｏ．４８０−
２」で、接触時間１．０ｓｅｃ．、スピード１．０ｃｍ
／ｓｅｃ．で行った。また、光沢度の測定は、ＪＩＳ
Ｚ−８７４１によって行った。また、粘着力の測定は、
ＪＩＳ Ｚ−０２３７によって測定した。結果を表１に
示す。The tack measurement was carried out using a Polyken probe tack tester "MODEL-TMI-No. 480-".
2 "and a contact time of 1.0 sec. , Speed 1.0cm
/ Sec. I went in. The measurement of glossiness is based on JIS
Performed with Z-8741. The measurement of adhesive strength
It was measured according to JIS Z-0237. Table 1 shows the results.
【００２８】[0028]
【表１】 [Table 1]
【００２９】[0029]
【発明の効果】表１から明らかなように、本発明の両面
粘着テープを用いたパンチング加工シートは、そのパン
チング孔内の粘着剤（Ａ）の露出面が艶消し面となって
いて光を反射しない面となっており、また、完全に粘着
性を失っていて塵埃等を吸着することがないことから、
黒色のパンチング加工シート面の外観が損なわれること
がない。これに対して、比較例１の両面テープの場合
は、粘着剤面が透明な光沢面であって光を反射し、黒色
のパンチングシートの外観を損なっているものであり、
また、表面が粘着性を呈することに起因して、塵埃等を
吸着し外観を損ねるものであった。また、比較例２の両
面テープの場合も、粘着剤面は黒の艶消しであるが、粘
着性があるため、塵埃の吸着などにより外観を損ねるも
のであった。As is clear from Table 1, in the punched sheet using the double-sided pressure-sensitive adhesive tape of the present invention, the exposed surface of the pressure-sensitive adhesive (A) in the punched hole is a matte surface, and light is not reflected. Because it is a non-reflective surface, and because it has completely lost adhesiveness and does not adsorb dust etc.,
The appearance of the black punched sheet surface is not impaired. On the other hand, in the case of the double-sided tape of Comparative Example 1, the pressure-sensitive adhesive surface is a transparent glossy surface and reflects light, impairing the appearance of the black punching sheet.
Further, due to the surface exhibiting tackiness, dust and the like are adsorbed to impair the appearance. In the case of the double-sided tape of Comparative Example 2, the surface of the pressure-sensitive adhesive was black matte, but had an adhesive property, and the appearance was impaired due to the adsorption of dust and the like.
【図１】本発明の両面粘着テープの積層構造を示す図。FIG. 1 is a view showing a laminated structure of a double-sided pressure-sensitive adhesive tape of the present invention.
１：エンボスライナー、２：平滑面ライナー、Ａ：紫外
線硬化型粘着剤層、Ｂ：通常粘着剤層、Ｃ：支持体1: embossed liner, 2: smooth surface liner, A: UV-curable pressure-sensitive adhesive layer, B: normal pressure-sensitive adhesive layer, C: support
───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 4J004 AA05 AA10 AB01 CA02 CA06 CB01 CB02 CC02 DA04 DB00 DB02 EA05 FA01 4J040 FA011 FA291 JA09 JB08 JB09 LA01 PA42 ──────────────────────────────────────────────────続 き Continued on the front page F term (reference) 4J004 AA05 AA10 AB01 CA02 CA06 CB01 CB02 CC02 DA04 DB00 DB02 EA05 FA01 4J040 FA011 FA291 JA09 JB08 JB09 LA01 PA42
Claims (6)
によって実質的に非粘着性となる粘着剤層からなること
を特徴とする、両面粘着テープ。1. A double-sided pressure-sensitive adhesive tape, wherein the pressure-sensitive adhesive layer on one side of the support comprises a pressure-sensitive adhesive layer which becomes substantially non-tacky upon irradiation with ultraviolet rays.
性となる粘着剤層に凹凸面を有する剥離ライナーを配設
したことを特徴とする、請求項１記載の両面粘着テー
プ。2. The double-sided pressure-sensitive adhesive tape according to claim 1, wherein a release liner having an uneven surface is provided on the pressure-sensitive adhesive layer which becomes substantially non-tacky by the ultraviolet irradiation.
した粘着剤層の反対側粘着剤層にも剥離ライナーを有す
ることを特徴とする、請求項２記載の両面接着テープ。3. The double-sided adhesive tape according to claim 2, wherein the pressure-sensitive adhesive layer on the opposite side of the pressure-sensitive adhesive layer on which the release liner having the uneven surface is provided also has a release liner.
凸が形成されておりかつ紫外線照射によって実質的に非
粘着性となる粘着剤層を有する両面粘着テープとからな
り、該両面テープの該紫外線照射によって実質的に非粘
着性となる粘着剤層面と該有孔シートの裏面とを対面貼
着し、該有孔シート側から紫外線照射してなる、裏面に
粘着剤層が設けられた有孔シート。4. A double-sided pressure-sensitive adhesive tape comprising a perforated sheet and a pressure-sensitive adhesive layer having a surface irregularity formed on one surface of a support and having a substantially non-adhesive layer when irradiated with ultraviolet light. The adhesive layer surface which becomes substantially non-adhesive by the ultraviolet irradiation and the back surface of the perforated sheet are adhered face-to-face, and ultraviolet light is irradiated from the perforated sheet side. Perforated sheet.
の有孔化粧シートであることを特徴とする、請求項４記
載の裏面に粘着剤層が設けられた有孔シート。5. The perforated sheet according to claim 4, wherein the perforated sheet is a perforated decorative sheet made of a thermoplastic synthetic resin.
材であることを特徴とする、請求項４又は５に記載の裏
面に粘着剤層が設けられた有孔化粧シート。6. The perforated decorative sheet according to claim 4, wherein the perforated sheet is a speaker net member.