JP2000239117A - Cosmetic - Google Patents

Cosmetic

Info

Publication number
JP2000239117A
JP2000239117A JP11037728A JP3772899A JP2000239117A JP 2000239117 A JP2000239117 A JP 2000239117A JP 11037728 A JP11037728 A JP 11037728A JP 3772899 A JP3772899 A JP 3772899A JP 2000239117 A JP2000239117 A JP 2000239117A
Authority
JP
Japan
Prior art keywords
powder
fluorine
treated
oil
cosmetic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP11037728A
Other languages
Japanese (ja)
Inventor
Keiji Hosomi
恵児 細見
Masahiko Hishikawa
昌彦 菱川
Hiroaki Konishi
宏明 小西
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nonogawa Shoji Ltd
Original Assignee
Nonogawa Shoji Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nonogawa Shoji Ltd filed Critical Nonogawa Shoji Ltd
Priority to JP11037728A priority Critical patent/JP2000239117A/en
Publication of JP2000239117A publication Critical patent/JP2000239117A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To obtain a cosmetic having excellent water and oil resistance, adhesivity and smoothness, effective for preventing the makeup-comes-off caused by sweat and sebum and having excellent makeup durability by compounding a fluorine-based oil to a powder surface-treated with a specific fluorine- containing silicone. SOLUTION: The objective cosmetic is produced by compounding (A) a powder surface-treated with a fluorine-containing silicone expressed by the formula [R1 is a 1-20C alkyl or an aryl; R2 is R5-Rf (R5 is a 2-6C bivalent alkylene; Rf is a 1-12C perfluoroalkyl); R3 is R5-SiX3 (X is a 1-4C alkoxy or a halogen); R4 is either one of R1 to R3; (1) is 0-500; (m) is 1-500; (n) is 1-500] with (B) a fluorine-based oil (preferably a fluorine-modified silicone oil or a perfluoropolyether). The amount of the fluorine-containing silicone in the surface- treatment is preferably 1-50 wt.% based on the weight of the base powder. The amount of the component B compounded to the cosmetic is preferably 0.1-70 wt.%.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【0001】[0001]

【産業上の利用分野】本発明は、耐水耐油性、付着性、
平滑性に優れ、汗、皮脂による化粧崩れを防止でき、化
粧持ちに優れた化粧料に関する。さらに詳しくは、粉体
の表面を特定の含フッ素シリコーンで処理して得られる
粉体、およびフッ素系油剤を配合することにより、肌上
に生じた汗、皮脂による化粧崩れの防止効果に優れ、且
つ使用感、特にフィット感、平滑性に優れた化粧料に関
する。
BACKGROUND OF THE INVENTION The present invention relates to water resistance, oil resistance,
The present invention relates to a cosmetic that has excellent smoothness, can prevent makeup collapse due to sweat and sebum, and has excellent makeup durability. More specifically, by mixing the powder obtained by treating the surface of the powder with a specific fluorine-containing silicone, and a fluorine-based oil, sweat produced on the skin, the effect of preventing makeup collapse due to sebum is excellent, In addition, the present invention relates to a cosmetic having excellent feeling in use, particularly, fit and smoothness.

【0002】[0002]

【従来の技術】化粧料用粉体を配合する化粧料形態とし
て、ファンデーション、ほほ紅、アイブロウ、アイシャ
ドウ、ボディパウダー、日焼け止め化粧料などがある。
近年、これらの化粧料について、化粧持続効果、日焼け
止め持続効果に対する要求が非常に高まっている。それ
に伴って、これらの化粧料に配合される化粧料用粉体に
対しても、耐水性、耐油性の向上が求められていた。
2. Description of the Related Art Cosmetic forms in which powders for cosmetics are blended include foundation, blusher, eyebrow, eyeshadow, body powder, sunscreen cosmetics and the like.
In recent years, there has been a great demand for these cosmetics for a long-lasting cosmetic effect and a long-lasting sunscreen effect. Accordingly, improvement of water resistance and oil resistance has been required for cosmetic powders to be incorporated in these cosmetics.

【0003】粉体に耐水性を付与する方法として、従来
よりシリコーンで粉体を処理する方法が知られている。
具体的には、メチルハイドロジェンポリシロキサンを粉
体と混合し、加熱焼き付けすることにより粉体を処理す
る(特公昭45−2915)方法、メチルハイドロジェ
ンポリシロキサンあるいはジメチルポリシロキサンを有
機溶媒に溶解した後、架橋用触媒としてオクチル酸亜鉛
などを添加して焼き付けることにより粉体を処理する
(特公昭45−18999)方法、粉体に金属水酸化物
を混合、被覆処理した後、メチルハイドロジェンポリシ
ロキサンを用いてメカノケミカル反応により粉体を処理
する(特公昭56−43264)方法が知られている。
しかしながら、これらの処理粉体は、耐水性、耐油性と
も十分ではなく、肌上に生じた汗および皮脂により容易
に化粧崩れを起こすという問題があった。
[0003] As a method for imparting water resistance to a powder, a method of treating the powder with silicone has conventionally been known.
Specifically, a method in which methyl hydrogen polysiloxane is mixed with a powder and the powder is treated by heating and baking (Japanese Patent Publication No. 45-2915), a method in which methyl hydrogen polysiloxane or dimethyl polysiloxane is dissolved in an organic solvent After that, the powder is treated by adding zinc octylate or the like as a crosslinking catalyst and baking the mixture (Japanese Patent Publication No. 45-18999). The powder is mixed with a metal hydroxide, coated and treated with methyl hydrogen. A method of treating a powder by a mechanochemical reaction using polysiloxane (JP-B-56-43264) is known.
However, these treated powders are not sufficient in water resistance and oil resistance, and have a problem that makeup is easily disintegrated due to sweat and sebum generated on the skin.

【0004】そのため、粉体の耐水性、耐油性を向上さ
せ、汗、皮脂などによる化粧崩れを防止することを目的
として、近年、粉体をフッ素化合物で処理する方法が提
案されている。具体的には、テフロン(登録商標)で粉
体を処理する(特公昭61−55481)方法、フッ素
化アクリレートで粉体を処理する(特公昭61−488
03)方法、パーフルオロアルキルリン酸エステルジエ
タノールアミン塩で粉体を処理する(特公平5−869
84)方法、パーフルオロアルキルシランで粉体を処理
する(特開平2−218603、特開平4−19381
6)方法が提案されている。
[0004] Therefore, in order to improve the water resistance and oil resistance of the powder, and to prevent makeup collapse due to sweat, sebum and the like, a method of treating the powder with a fluorine compound has recently been proposed. Specifically, a method of treating powder with Teflon (registered trademark) (JP-B-61-55481) and a method of treating powder with fluorinated acrylate (JP-B-61-488)
03) Method, treating powder with perfluoroalkyl phosphate diethanolamine salt (JP-B 5-869)
84) Method, treating powder with perfluoroalkylsilane (JP-A-2-218603, JP-A-4-19381)
6) A method has been proposed.

【0005】これらの粉体はいずれも、粉体表面を極め
て表面自由エネルギーの低いフッ素化合物によって被覆
されているため、撥水撥油性を有し、汗や皮脂に対して
もなじまない。しかしながら、化粧料中に含まれる油剤
に対してもなじまず油剤への分散性が悪いため、粉体の
凝集、色ムラが生じ易く、化粧料への配合が極めて困難
であった。また、これらの粉体は、使用感の面で、処理
する前と比べて平滑性が悪くなるという欠点があった。
Since all of these powders are coated with a fluorine compound having an extremely low surface free energy on the surface of the powder, they have water and oil repellency and are not compatible with sweat and sebum. However, the dispersibility of the oil agent contained in the cosmetic is poor, and the agglomeration and color unevenness of the powder are liable to occur, and it is extremely difficult to incorporate the oil into the cosmetic. In addition, these powders have a drawback that, in terms of usability, the smoothness is deteriorated as compared to before the treatment.

【0006】また、化粧料に撥水性を付与することを目
的としてシリコーン油が配合されている。シリコーン油
は撥水性に優れ、なめらかな使用感を有しているため、
化粧料成分として汎用されている。しかしながら、シリ
コーン油は耐水性、耐油性とも十分ではなく、シリコー
ン油を配合した化粧料も、肌上に生じた汗、皮脂により
容易に化粧崩れを起こすという問題があった。
[0006] In addition, silicone oil is blended for the purpose of imparting water repellency to cosmetics. Because silicone oil has excellent water repellency and has a smooth feeling of use,
It is widely used as a cosmetic ingredient. However, silicone oil is not sufficient in water resistance and oil resistance, and there is a problem that cosmetics containing silicone oil easily lose their makeup due to sweat and sebum generated on the skin.

【0007】そのため、化粧料に耐水性、耐油性を付与
することを目的として、液状のパーフルオロポリエーテ
ルを配合した化粧料(特開昭61−234928、特開
昭63−247214)、フッ素変性シリコーン油を配
合した化粧料(特開平5−247214、特開平6−1
84312、特開平6−234858)が提案されてい
る。しかしながら、これらのフッ素系油剤は撥水撥油性
を有するものの、流動性が高く、また肌への付着力が乏
しいため、大量の汗や皮脂に対して化粧崩れを十分に防
止することができないという問題があった。
For the purpose of imparting water resistance and oil resistance to cosmetics, cosmetics containing liquid perfluoropolyether (JP-A-61-234928 and JP-A-63-247214), fluorine-modified Cosmetics containing silicone oil (JP-A-5-247214, JP-A-6-12-1)
84312, JP-A-6-234858). However, although these fluorinated oils have water and oil repellency, they have high fluidity and poor adhesion to the skin, so they cannot sufficiently prevent makeup collapse against a large amount of sweat and sebum. There was a problem.

【0008】[0008]

【発明が解決しようとする課題】従って、本発明は、耐
水耐油性、付着性、平滑性に優れ、汗、皮脂による化粧
崩れを防止でき、化粧持ちに優れた化粧料を提供するこ
とを目的とする。
SUMMARY OF THE INVENTION Accordingly, an object of the present invention is to provide a cosmetic which is excellent in water resistance, oil resistance, adhesion and smoothness, can prevent makeup collapse due to sweat and sebum, and is excellent in long-lasting makeup. And

【0009】[0009]

【課題を解決するための手段】本発明者らはこのような
事情に鑑み、鋭意研究を重ねた結果、粉体の表面を特定
の含フッ素シリコーンで処理することにより、耐水耐油
性、付着性、平滑性に優れ、且つフッ素系油剤への分散
性が良好な粉体が得られること、およびこの処理粉体と
フッ素系油剤を配合することにより、耐水耐油性、付着
性、平滑性に優れ、肌上に生じた汗、皮脂による化粧崩
れの防止効果に優れた化粧料が得られることを見出し本
発明を完成した。
Means for Solving the Problems In view of such circumstances, the present inventors have conducted intensive studies, and as a result, by treating the surface of the powder with a specific fluorine-containing silicone, water resistance, oil resistance, Powder that has excellent smoothness and good dispersibility in fluorinated oils can be obtained. By blending this treated powder with fluorinated oils, it has excellent water and oil resistance, adhesion, and smoothness. The present inventors have found that a cosmetic excellent in the effect of preventing makeup collapse due to sweat and sebum generated on the skin can be obtained, and completed the present invention.

【0010】すなわち、本発明は、(a)粉体の表面を
一般式(1)[式中、R1は同種または異種の炭素数1
〜20のアルキル基またはアリール基、R2は−R5−
Rf(式中、R5は炭素数2〜6の二価のアルキレン基
を示し、Rfは炭素数1〜12のパーフルオロアルキル
基を示す。)、R3は−R5−SiX(式中、Xは炭
素数1〜4のアルコキシル基またはハロゲンを示
す。)、R4はR1またはR2またはR3のいずれかで
あり、l、m、nは整数であって、l=0〜500、m
=1〜500、n=1〜500である。]で表される含
フッ素シリコーンで処理して得られる粉体、および
(b)フッ素系油剤を配合することにより、肌上に生じ
た汗、皮脂による化粧崩れの防止効果に優れ、且つ使用
感、特にフィット感、平滑性に優れた化粧料を提供する
ものである。
That is, according to the present invention, (a) the surface of the powder is represented by the general formula (1) wherein R1 is the same or different
To 20 alkyl groups or aryl groups, R2 is -R5-
Rf (wherein, R5 represents a divalent alkylene group having 2 to 6 carbon atoms, Rf represents a perfluoroalkyl group having 1 to 12 carbon atoms.), R3 is -R5-SiX 3 (wherein, X Represents an alkoxyl group having 1 to 4 carbon atoms or halogen.), R4 is any of R1 or R2 or R3, l, m, and n are integers, and l = 0 to 500, m
= 1 to 500 and n = 1 to 500. ] And a powder obtained by treating with the fluorine-containing silicone represented by formula (1), and (b) a fluorine-based oil, are excellent in the effect of preventing makeup collapse due to sweat and sebum generated on the skin, and provide a feeling of use. In particular, the present invention provides a cosmetic having excellent fit and smoothness.

【0011】[0011]

【化2】 Embedded image

【0012】以下、本発明を詳細に説明する。Hereinafter, the present invention will be described in detail.

【0013】本発明に用いられる粉体には、通常化粧料
として用いられるものであれば全て適用できる。例えば
タルク、マイカ、カオリン、セリサイト、ベントナイ
ト、スメクタイト、雲母チタン、オキシ塩化ビスマス、
ケイ酸、無水ケイ酸、アルミナ、酸化チタン、微粒子酸
化チタン、酸化亜鉛、酸化ジルコニウム、酸化マグネシ
ウム、硫酸バリウム、硫酸マグネシウム、炭酸カルシウ
ム、炭酸マグネシウム、ケイ酸アルミニウム、ケイ酸マ
グネシウム、ケイ酸カルシウム、ケイ酸バリウム、ヒド
ロキシアパタイト、窒化ホウ素、金属石鹸、ベンガラ、
黄酸化鉄、黒酸化鉄、酸化クロム、水酸化クロム、カー
ボンブラック、群青、紺青などの無機粉体、ナイロン、
ポリメチルメタクリレート、ポリエチレン、ポリスチレ
ン、セルロース、アセチル化セルロース、ポリウレタ
ン、ジビニルベンゼン・スチレン共重合体、シリコーン
樹脂、エポキシ樹脂、メラミン樹脂、ポリカーボネート
樹脂、ビニル樹脂、シルクパウダーなどの高分子、赤色
104号、赤色106号、赤色201号、赤色202
号、赤色204号、赤色205号、赤色206号、赤色
226号、赤色227号、赤色228号、黄色4号、黄
色5号、黄色202号、黄色203号、黄色205号、
黄色401号、青色1号、緑色3号などの有機系色素が
挙げられる。また、2種以上の粉体およびこれらの複合
体を用いても構わない。同様に粉体の形状、粒径に関し
ても、特に限定されない。
As the powder used in the present invention, any powder which is usually used as a cosmetic can be applied. For example, talc, mica, kaolin, sericite, bentonite, smectite, mica titanium, bismuth oxychloride,
Silicic acid, silicic anhydride, alumina, titanium oxide, fine particle titanium oxide, zinc oxide, zirconium oxide, magnesium oxide, barium sulfate, magnesium sulfate, calcium carbonate, magnesium carbonate, aluminum silicate, magnesium silicate, calcium silicate, silica Barium acid, hydroxyapatite, boron nitride, metal soap, red iron,
Inorganic powders such as yellow iron oxide, black iron oxide, chromium oxide, chromium hydroxide, carbon black, ultramarine, navy blue, nylon,
Polymethyl methacrylate, polyethylene, polystyrene, cellulose, acetylated cellulose, polyurethane, divinylbenzene / styrene copolymer, silicone resin, epoxy resin, melamine resin, polycarbonate resin, vinyl resin, polymer such as silk powder, Red No. 104, Red No. 106, Red No. 201, Red 202
No., Red No. 204, Red No. 205, Red No. 206, Red No. 226, Red No. 227, Red No. 228, Yellow No. 4, Yellow No. 5, Yellow No. 202, Yellow No. 203, Yellow No. 205,
Organic dyes such as Yellow No. 401, Blue No. 1 and Green No. 3 are exemplified. Further, two or more kinds of powders and composites thereof may be used. Similarly, the shape and particle size of the powder are not particularly limited.

【0014】これらの粉体は、公知の方法により事前に
表面処理されていてもいなくても構わない。表面処理の
方法としては例えば、油剤処理、金属石鹸処理、無機化
合物処理、アミノ酸処理、シリコーン処理、フッ素化合
物処理、ペンダント処理、シランカップリング剤処理、
チタンカップリング剤処理、N−アシル化リジン処理、
ポリアクリル酸処理、プラズマ処理、メカノケミカル処
理などが挙げられる。
These powders may or may not have been previously surface-treated by a known method. Examples of the surface treatment method include oil treatment, metal soap treatment, inorganic compound treatment, amino acid treatment, silicone treatment, fluorine compound treatment, pendant treatment, silane coupling agent treatment,
Titanium coupling agent treatment, N-acylated lysine treatment,
Examples include polyacrylic acid treatment, plasma treatment, and mechanochemical treatment.

【0015】本発明で用いられる含フッ素シリコーンは
一般式(1)[式中、R1は同種または異種の炭素数1
〜20のアルキル基またはアリール基、R2は−R5−
Rf(式中、R5は炭素数2〜6の二価のアルキレン基
を示し、Rfは炭素数1〜12のパーフルオロアルキル
基を示す。)、R3は−R5−SiX(式中、Xは炭
素数1〜4のアルコキシル基またはハロゲンを示
す。)、R4はR1またはR2またはR3のいずれかで
あり、l、m、nは整数であって、l=0〜500、m
=1〜500、n=1〜500である。]で表される構
造を有する。その中でも特に、l=0、m=1〜50、
n=1〜50でmとnの比が9:1〜2:3の構造のも
のが好ましい。さらに好ましくは、mとnの比が3:1
〜1:1である。なお、一般式(1)で表される含フッ
素シリコーンの構造単位の配列は、交互でもブロックで
もランダムでもよい。具体的には、R1としては、CH
、C、C、CH(CH、C
、CHCH(CH)CH、C(C
、C13、Cなどが、R5として
は、C、C、C、CHCH(CH
)CH、CHCHCH(CH)、C12
などが、Rfとしては、CF、C、C
13、C17、C1225などが、Xとし
ては、OCH、OC、OC、OCH(C
、OC、OCHCH(CH)C
、OC(CH、Cl、Brなどが挙げられ
る。
The fluorine-containing silicone used in the present invention has a general formula (1) wherein R1 is the same or different and has 1 carbon atom.
To 20 alkyl groups or aryl groups, R2 is -R5-
Rf (wherein, R5 represents a divalent alkylene group having 2 to 6 carbon atoms, Rf represents a perfluoroalkyl group having 1 to 12 carbon atoms.), R3 is -R5-SiX 3 (wherein, X Represents an alkoxyl group having 1 to 4 carbon atoms or halogen.), R4 is any of R1 or R2 or R3, l, m, and n are integers, and l = 0 to 500, m
= 1 to 500 and n = 1 to 500. ] Is represented. Among them, l = 0, m = 1 to 50,
Those having a structure in which n = 1 to 50 and the ratio of m to n is 9: 1 to 2: 3 are preferable. More preferably, the ratio of m to n is 3: 1.
11: 1. The arrangement of the structural units of the fluorine-containing silicone represented by the general formula (1) may be alternate, block, or random. Specifically, R1 is CH
3, C 2 H 5, C 3 H 7, CH (CH 3) 2, C
4 H 9 , CH 2 CH (CH 3 ) CH 3 , C (C
H 3 ) 3 , C 6 H 13 , C 6 H 5, etc., and R 5 is C 2 H 4 , C 3 H 6 , C 4 H 8 , CH 2 CH (CH
3) CH 2, CH 2 CH 2 CH (CH 3), C 6 H 12
And Rf as CF 3 , C 2 F 5 , C 4 F 9 ,
X represents OCH 3 , OC 2 H 5 , OC 3 H 7 , or OCH (C 6 F 13 , C 8 F 17 , C 12 F 25, etc.
H 3 ) 2 , OC 4 H 9 , OCH 2 CH (CH 3 ) C
H 3 , OC (CH 3 ) 3 , Cl, Br and the like can be mentioned.

【0016】[0016]

【化3】 Embedded image

【0017】含フッ素シリコーンは、上記化合物のうち
それぞれ1種または2種以上を混合して用いることがで
きる。
The fluorine-containing silicone may be used alone or in combination of two or more of the above compounds.

【0018】本発明で用いる表面処理において、含フッ
素シリコーンの添加量は、粉体および含フッ素シリコー
ンの種類によって異なるが、基材粉体の重量に対して1
〜50重量%が好ましい。さらに好ましくは、3〜20
重量%である。1重量%未満では本発明の効果である耐
水性、耐油性が十分ではなく、50重量%を越えて処理
しても、効果の増強は望めない。
In the surface treatment used in the present invention, the amount of the fluorinated silicone varies depending on the type of the powder and the fluorinated silicone.
~ 50% by weight is preferred. More preferably, 3 to 20
% By weight. If the amount is less than 1% by weight, the effects of the present invention such as water resistance and oil resistance are not sufficient, and even if the amount exceeds 50% by weight, the effect cannot be expected to be enhanced.

【0019】本発明で用いられる表面処理の手法として
は、湿式法、乾式法などが挙げられる。本発明でいう湿
式法とは、粉体を適当な溶剤に分散させ、含フッ素シリ
コーンおよび必要に応じて酸またはアルカリを添加し、
撹拌混合後溶剤を除去し、乾燥、場合によっては粉砕し
て得られる手法を指す。溶剤の例としては、ヘキサン、
ヘプタン、トルエン、キシレン、ベンゼン、環状シリコ
ーン、塩化メチレン、クロロホルム、アセトン、ブタノ
ール、プロパノール、イソプロパノール、エタノール、
メタノール、水などが挙げられる。また、酸としては、
塩酸、硝酸、硫酸、酢酸などが、アルカリとしては、ア
ンモニア、ピリジン、アミンなどが挙げられる。また、
乾式法とは、ヘンシェルミキサー、ジェットミル、ボー
ルミル、スーパーミキサーなどの撹拌混合装置で粉体を
混合しながら、含フッ素シリコーンをそのまま、または
適当な溶剤に希釈して添加し、撹拌混合後乾燥、場合に
よっては粉砕して得られる手法を指す。含フッ素シリコ
ーンを希釈する溶剤としては、湿式法による処理で挙げ
た溶剤を用いることができる。その他、スプレードライ
法、流動造粒法などが挙げられるが、いかなる方法であ
れ、含フッ素シリコーンが基材粉体表面に被覆されてい
れば構わない。
The surface treatment used in the present invention includes a wet method and a dry method. The wet method referred to in the present invention is to disperse the powder in an appropriate solvent, add a fluorine-containing silicone and, if necessary, an acid or alkali,
It refers to a technique obtained by removing the solvent after stirring and mixing, drying, and optionally pulverizing. Examples of solvents include hexane,
Heptane, toluene, xylene, benzene, cyclic silicone, methylene chloride, chloroform, acetone, butanol, propanol, isopropanol, ethanol,
Methanol, water and the like can be mentioned. Also, as the acid,
Hydrochloric acid, nitric acid, sulfuric acid, acetic acid and the like, and alkalis include ammonia, pyridine, amine and the like. Also,
With the dry method, while mixing powder with a stirring and mixing device such as a Henschel mixer, a jet mill, a ball mill, and a super mixer, the fluorinated silicone is added as it is or diluted with an appropriate solvent, and the mixture is dried after stirring and mixing. In some cases, it refers to a technique obtained by grinding. As the solvent for diluting the fluorine-containing silicone, the solvents mentioned in the treatment by the wet method can be used. Other examples include a spray drying method and a fluid granulation method, and any method may be used as long as the surface of the base powder is coated with the fluorine-containing silicone.

【0020】(a)成分の処理粉体は、1種または2種
以上を組み合わせて用いることができる。化粧料への配
合量としては、0.1〜99重量%が好ましい。さらに
好ましくは、1〜95重量%である。0.1重量%未満
では本発明の効果である化粧持続効果が十分ではなく、
99重量%を越えて配合しても効果の増強は望めない。
The treated powder of the component (a) can be used alone or in combination of two or more. The compounding amount in the cosmetic is preferably 0.1 to 99% by weight. More preferably, it is 1 to 95% by weight. If it is less than 0.1% by weight, the effect of the present invention, that is, the long-lasting effect of makeup, is not sufficient.
Even if the content exceeds 99% by weight, the effect cannot be expected to be enhanced.

【0021】また、本発明で用いられる(b)成分のフ
ッ素系油剤は、常温で液体のものが好ましい。具体的に
は、パーフルオロデカリン、パーフルオロアダマンタ
ン、パーフルオロブチルテトラハイドロフラン、パーフ
ルオロオクタン、パーフルオロノナン、パーフルオロペ
ンタン、パーフルオロデカン、パーフルオロドデカン、
フルオロアルコール、フッ化ピッチ、パーフルオロポリ
エーテル、一般式(2)[式中、R6は同種または異種
の炭素数1〜20のアルキル基またはアリール基、R7
は−R9−Rf(式中、R9は炭素数2〜6の二価のア
ルキレン基を示し、Rfは炭素数1〜12のパーフルオ
ロアルキル基を示す。)、R8はR6またはR7のいず
れかであり、p、qは整数であって、p=0〜500、
q=1〜500である。]で表されるフッ素変性シリコ
ーン油などが挙げられる。なお、一般式(2)で表され
るフッ素変性シリコーン油の構造単位の配列は、交互で
もブロックでもランダムでもよい。その中でも、フッ素
変性シリコーン油およびパーフルオロポリエーテルが、
(a)成分の分散性の点から特に好ましい。このような
フッ素変性シリコーン油としては、X−22−819、
X−22−820、X−22−821、X−22−82
2、FL100(以上、信越化学工業製)、FQF50
1(東芝シリコーン製)、FS1265(東レ・ダウコ
ーニング・シリコーン製)などの市販品を使用すること
ができる。また、パーフルオロポリエーテルとしては、
フォンブリンHC−01、HC−02、HCー03、H
C−04、HC−25、HC−R(以上、モンテフルオ
ス製)などの市販品を使用することができる。
The fluorine-based oil component (b) used in the present invention is preferably liquid at room temperature. Specifically, perfluorodecalin, perfluoroadamantane, perfluorobutyltetrahydrofuran, perfluorooctane, perfluorononane, perfluoropentane, perfluorodecane, perfluorododecane,
Fluoroalcohol, fluorinated pitch, perfluoropolyether, general formula (2) wherein R6 is the same or different and is an alkyl or aryl group having 1 to 20 carbon atoms, R7
Is -R9-Rf (wherein, R9 represents a divalent alkylene group having 2 to 6 carbon atoms, Rf represents a perfluoroalkyl group having 1 to 12 carbon atoms), and R8 represents any of R6 or R7. And p and q are integers, p = 0 to 500,
q = 1 to 500. A fluorine-modified silicone oil represented by the formula: In addition, the arrangement of the structural units of the fluorine-modified silicone oil represented by the general formula (2) may be alternate, block or random. Among them, fluorine-modified silicone oil and perfluoropolyether,
It is particularly preferable from the viewpoint of dispersibility of the component (a). Examples of such a fluorine-modified silicone oil include X-22-819,
X-22-820, X-22-821, X-22-82
2, FL100 (Shin-Etsu Chemical Co., Ltd.), FQF50
Commercial products such as No. 1 (made by Toshiba Silicone) and FS1265 (made by Dow Corning Toray Silicone) can be used. Also, as perfluoropolyether,
Fomblin HC-01, HC-02, HC-03, H
Commercially available products such as C-04, HC-25, and HC-R (all manufactured by Montefluos) can be used.

【0022】[0022]

【化4】 Embedded image

【0023】(b)成分のフッ素系油剤は、1種または
2種以上を組み合わせて用いることができる。化粧料へ
の配合量としては、0.1〜70重量%が好ましい。さ
らに好ましくは、1〜30重量%である。0.1重量%
未満では(a)成分の処理粉体の分散性が十分ではな
く、70重量%を越えて配合しても(a)成分の処理粉
体の分散性は向上せず、逆に化粧持続効果が低下する。
The fluorine oil of component (b) can be used alone or in combination of two or more. The compounding amount in the cosmetic is preferably 0.1 to 70% by weight. More preferably, it is 1 to 30% by weight. 0.1% by weight
If it is less than 10, the dispersibility of the treated powder of the component (a) is not sufficient, and even if it is more than 70% by weight, the dispersibility of the treated powder of the component (a) is not improved, and conversely, the effect of keeping the makeup is long. descend.

【0024】本発明の化粧料のその他の成分としては、
目的とする化粧料の形態に応じて、通常の化粧料に配合
される成分から選択して用いることができる。これらの
成分としては、例えば油分としては、スクワラン、流動
パラフィン、ワセリン、軽質イソパラフィン、重質流動
イソパラフィンなどの各種炭化水素、マイクロクリスタ
リンワックス、オゾケライト、セレシン、ミツロウ、カ
ルナウバロウ、キャンデリラロウなどのロウ類、ラウリ
ン酸、ミリスチン酸、パルミチン酸、オレイン酸、ステ
アリン酸、イソステアリン酸などの高級脂肪酸、ラウリ
ルアルコール、セチルアルコール、ヘキサデシルアルコ
ール、オレイルアルコール、ステアリルアルコール、ベ
ヘニルアルコールなどの高級アルコール、イソオクタン
酸セチル、ミリスチン酸イソプロピル、パルミチン酸イ
ソプロピル、ミリスチン酸オクチルドデシル、パルミチ
ン酸セチル、トリ(カプリル・カプリン酸)グリセリ
ル、オレイン酸オクチルドデシル、トリオクタン酸グリ
セリル、イソノナン酸イソデシル、コハク酸ジオクチ
ル、乳酸オクチルドデシル、リンゴ酸ジイソステアリ
ル、ジイソステアリン酸ジグリセリル、トリイソステア
リン酸ジグリセリル、ジオクタン酸ネオペンチルグリコ
ール、ミリスチン酸イソステアリル、ステアリン酸コレ
ステリル、トリオクタン酸トリメチロールプロパン、テ
トラオクタン酸ペンタエリスリットなどのエステル類、
オリーブ油、ホホバ油、水添ホホバ油、アボガド油、ヒ
マシ油、マカデミアナッツ油、ミンク油、ラノリンなど
の油脂類、ジメチルポリシロキサン、メチルフェニルポ
リシロキサン、オクタメチルシクロテトラシロキサン、
デカメチルシクロペンタシロキサン、ポリエーテル変性
シリコーン、アミノ変性シリコーン、アルキル変性シリ
コーン、フルオロシリコーン、アクリルシリコーン、シ
リコーン樹脂、シリコーンゴム、トリメチルシロキシケ
イ酸などのシリコーン類などが挙げられる。
Other components of the cosmetic of the present invention include:
Depending on the form of the desired cosmetic, it can be used by selecting from components that are blended with ordinary cosmetics. As these components, for example, oils include various hydrocarbons such as squalane, liquid paraffin, petrolatum, light isoparaffin, and heavy liquid isoparaffin, microcrystalline wax, ozokerite, ceresin, beeswax, carnauba wax, waxes such as candelilla wax, etc. , Higher fatty acids such as lauric acid, myristic acid, palmitic acid, oleic acid, stearic acid, isostearic acid, higher alcohols such as lauryl alcohol, cetyl alcohol, hexadecyl alcohol, oleyl alcohol, stearyl alcohol, behenyl alcohol, cetyl isooctanoate, myristine Isopropyl acetate, isopropyl palmitate, octyl dodecyl myristate, cetyl palmitate, glyceryl tri (caprylate / caprate), oley Octyldodecyl acid, glyceryl trioctanoate, isodecyl isononanoate, dioctyl succinate, octyldodecyl lactate, diisostearyl malate, diglyceryl diisostearate, diglyceryl triisostearate, neopentyl glycol dioctanoate, isostearyl myristate, stearic acid Esters such as cholesteryl, trimethylolpropane trioctanoate, and pentaerythrit tetraoctanoate;
Olive oil, jojoba oil, hydrogenated jojoba oil, avocado oil, castor oil, macadamia nut oil, mink oil, oils such as lanolin, dimethylpolysiloxane, methylphenylpolysiloxane, octamethylcyclotetrasiloxane,
Examples include decamethylcyclopentasiloxane, polyether-modified silicone, amino-modified silicone, alkyl-modified silicone, fluorosilicone, acrylic silicone, silicone resin, silicone rubber, and silicones such as trimethylsiloxysilicic acid.

【0025】その他の成分としては、各種ポリマー、無
機粉体、有機粉体、界面活性剤、多価アルコール、エタ
ノール、増粘剤、防腐剤、酸化防止剤、pH調整剤、キ
レート剤、香料、紫外線吸収剤、殺菌剤、保湿剤、制汗
剤、水などが挙げられ、本発明の目的を損なわない範囲
内で配合可能である。
Other components include various polymers, inorganic powders, organic powders, surfactants, polyhydric alcohols, ethanol, thickeners, preservatives, antioxidants, pH adjusters, chelating agents, fragrances, Examples thereof include an ultraviolet absorber, a bactericide, a humectant, an antiperspirant, and water.

【0026】本発明の化粧料の例としては、例えばパウ
ダーファンデーション、油性ファンデーション、乳化型
ファンデーション、ほほ紅、白粉、プレストパウダー、
アイブロウ、アイシャドウ、アイライナー、マスカラ、
口紅、ネイルカラー、化粧下地、ボディパウダー、クリ
ーム、乳液、ローション、日焼け止め化粧料などが挙げ
られる。
Examples of the cosmetics of the present invention include, for example, powder foundation, oily foundation, emulsion type foundation, blush, white powder, pressed powder,
Eyebrow, eyeshadow, eyeliner, mascara,
Examples include lipstick, nail color, makeup base, body powder, cream, milky lotion, lotion, sunscreen cosmetics and the like.

【0027】本発明の化粧料は、通常の方法に従って製
造することができる。
The cosmetic of the present invention can be produced according to a usual method.

【0028】[0028]

【実施例】次に本発明の一層の理解のために、実施例を
あげて更に詳細に説明するが、本発明はこれらに限定さ
れるものではない。
EXAMPLES The present invention will be described in more detail with reference to examples for a better understanding of the present invention, but the present invention is not limited to these examples.

【0029】実施例1 セリサイト100gをトルエン200gに分散させた
後、式(3)に示す構造を有する含フッ素シリコーンを
加え、80℃で2時間撹拌した。その後、トルエンを減
圧留去し、乾燥、粉砕して表面処理セリサイトを得た。
同様にして、タルク、マイカを表面処理した。なお、含
フッ素シリコーンの添加量を0.5g、1g、3g、2
0g、50g、100gに振ってそれぞれ処理した。
Example 1 After 100 g of sericite was dispersed in 200 g of toluene, a fluorine-containing silicone having a structure represented by the formula (3) was added, and the mixture was stirred at 80 ° C. for 2 hours. Thereafter, toluene was distilled off under reduced pressure, dried and pulverized to obtain surface-treated sericite.
Similarly, talc and mica were surface-treated. In addition, 0.5 g, 1 g, 3 g, 2 g,
Each was shaken to 0 g, 50 g, and 100 g to be processed.

【0030】[0030]

【化5】 Embedded image

【0031】実施例2 セリサイト100gをキシレン200gに分散させた
後、式(4)に示す構造を有する含フッ素シリコーンを
加え、100℃で2時間撹拌した。その後、キシレンを
減圧留去し、乾燥、粉砕して表面処理セリサイトを得
た。同様にして、タルク、マイカを表面処理した。な
お、含フッ素シリコーンの添加量を0.5g、1g、3
g、20g、50g、100gに振ってそれぞれ処理し
た。
Example 2 After 100 g of sericite was dispersed in 200 g of xylene, a fluorinated silicone having a structure represented by the formula (4) was added, and the mixture was stirred at 100 ° C. for 2 hours. Thereafter, xylene was distilled off under reduced pressure, dried and pulverized to obtain surface-treated sericite. Similarly, talc and mica were surface-treated. In addition, 0.5 g, 1 g, 3 g
g, 20 g, 50 g, and 100 g, respectively.

【0032】[0032]

【化6】 Embedded image

【0033】次に、上記のようにして得られた実施例
1、2の処理粉体について撥水撥油性、平滑性を評価し
た。その結果を表1〜3に示す。なお、横軸に含フッ素
シリコーンの添加量(g)を示す。
Next, the treated powders of Examples 1 and 2 obtained as described above were evaluated for water / oil repellency and smoothness. The results are shown in Tables 1 to 3. The abscissa indicates the amount (g) of the fluorine-containing silicone added.

【0034】(評価方法) <撥水性>10mlの試験管に精製水5mlをとり、実
施例の粉体0.1gを添加して100回振とうした。3
0分静置した後の状態を目視で判定した。 ○:大部分が水の表面に浮遊した △:水の表面に一部浮遊するものの、大部分が水中に分
散した。 ×:完全に水中に分散、沈殿した。 <撥油性>10mlの試験管にスクワラン5mlをと
り、実施例の粉体0.1gを添加して100回振とうし
た。30分静置した後の状態を目視で判定した。 ○:大部分がスクワランの表面に浮遊した △:スクワランの表面に一部浮遊するものの、大部分が
スクワラン中に分散した。 ×:完全にスクワラン中に分散、沈殿した。 <平滑性>10人の専門パネラーにより官能評価を行
い、次の基準で示した。 〇:8人以上が良いと感じた △:4〜7人が良いと感じた ×:4人未満が良いと感じた
(Evaluation method) <Water repellency> 5 ml of purified water was placed in a 10 ml test tube, 0.1 g of the powder of the example was added, and the mixture was shaken 100 times. 3
The state after standing for 0 minutes was visually determined. :: Mostly floating on the surface of water △: Partly floating on the surface of water, but most of it was dispersed in water. ×: Completely dispersed and precipitated in water. <Oil repellency> 5 ml of squalane was placed in a 10 ml test tube, 0.1 g of the powder of the example was added, and the mixture was shaken 100 times. The state after standing for 30 minutes was visually determined. :: Most of them floated on the surface of squalane △: Although they partially floated on the surface of squalane, most of them were dispersed in squalane. ×: Completely dispersed and precipitated in squalane. <Smoothness> Sensory evaluation was carried out by 10 expert panelists, and the results were shown according to the following criteria. 〇: 8 or more felt good △: 4 to 7 felt good ×: Less than 4 felt good

【0035】[0035]

【表1】 [Table 1]

【0036】[0036]

【表2】 [Table 2]

【0037】[0037]

【表3】 [Table 3]

【0038】表1〜3から、含フッ素シリコーンの添加
量としては、粉体の重量に対して1〜50重量%が好ま
しく、さらに好ましくは、3〜20重量%であることが
明らかとなった。
From Tables 1 to 3, it was revealed that the amount of the fluorine-containing silicone added is preferably 1 to 50% by weight, more preferably 3 to 20% by weight, based on the weight of the powder. .

【0039】実施例3 セリサイト100gをトルエン200gに分散させた
後、式(3)に示す構造を有する含フッ素シリコーン5
gを加え、80℃で2時間撹拌した。その後、トルエン
を減圧留去し、乾燥、粉砕して表面処理セリサイトを得
た。同様にして、タルク、マイカ、ベンガラ、黄酸化
鉄、黒酸化鉄、酸化チタンを表面処理した。
Example 3 After dispersing 100 g of sericite in 200 g of toluene, a fluorine-containing silicone 5 having a structure represented by the formula (3) was prepared.
g was added and stirred at 80 ° C. for 2 hours. Thereafter, toluene was distilled off under reduced pressure, dried and pulverized to obtain surface-treated sericite. Similarly, talc, mica, red iron oxide, yellow iron oxide, black iron oxide, and titanium oxide were surface-treated.

【0040】[0040]

【化7】 Embedded image

【0041】実施例4 セリサイト100gをキシレン200gに分散させた
後、式(4)に示す構造を有する含フッ素シリコーン6
gを加え、100℃で2時間撹拌した。その後、キシレ
ンを減圧留去し、乾燥、粉砕して表面処理セリサイトを
得た。同様にして、タルク、マイカ、ベンガラ、黄酸化
鉄、黒酸化鉄、酸化チタンを表面処理した。
Example 4 After dispersing 100 g of sericite in 200 g of xylene, a fluorine-containing silicone 6 having a structure represented by the formula (4) was prepared.
g was added and stirred at 100 ° C. for 2 hours. Thereafter, xylene was distilled off under reduced pressure, dried and pulverized to obtain surface-treated sericite. Similarly, talc, mica, red iron oxide, yellow iron oxide, black iron oxide, and titanium oxide were surface-treated.

【0042】[0042]

【化8】 Embedded image

【0043】実施例5 メチルハイドロジェンポリシロキサン3%処理セリサイ
ト100gをトルエン200gに分散させた後、式
(5)に示す構造を有する含フッ素シリコーン5gを加
え、85℃で2時間撹拌した。その後、トルエンを減圧
留去し、乾燥、粉砕して表面処理セリサイトを得た。同
様にして、タルク、マイカ、ベンガラ、黄酸化鉄、黒酸
化鉄、酸化チタンを表面処理した。
Example 5 After 100 g of sericite treated with 3% methylhydrogenpolysiloxane was dispersed in 200 g of toluene, 5 g of a fluorine-containing silicone having a structure represented by the formula (5) was added, and the mixture was stirred at 85 ° C. for 2 hours. Thereafter, toluene was distilled off under reduced pressure, dried and pulverized to obtain surface-treated sericite. Similarly, talc, mica, red iron oxide, yellow iron oxide, black iron oxide, and titanium oxide were surface-treated.

【0044】[0044]

【化9】 Embedded image

【0045】比較例1 大東化成工業製のパーフルオロアルキルリン酸エステル
塩5%処理セリサイト、タルク、マイカ、ベンガラ、黄
酸化鉄、黒酸化鉄、酸化チタンをもって比較例1とし
た。
Comparative Example 1 Comparative Example 1 was prepared using sericite, talc, mica, red iron oxide, yellow iron oxide, black iron oxide, and titanium oxide treated with 5% perfluoroalkyl phosphate ester salt manufactured by Daito Kasei Kogyo.

【0046】比較例2 セリサイト100gをトルエン200gに分散させた
後、ジメチルポリシロキサン(1000cs)6gを加
え、実施例3と同様の手法で処理した。同様にして、タ
ルク、マイカ、ベンガラ、黄酸化鉄、黒酸化鉄、酸化チ
タンを表面処理し、比較例2とした。
Comparative Example 2 After dispersing 100 g of sericite in 200 g of toluene, 6 g of dimethylpolysiloxane (1000 cs) was added and treated in the same manner as in Example 3. Similarly, talc, mica, red iron oxide, yellow iron oxide, black iron oxide, and titanium oxide were subjected to a surface treatment to obtain Comparative Example 2.

【0047】比較例3 東色ピグメント製のメチルハイドロジェンポリシロキサ
ン3%処理セリサイト、タルク、マイカ、ベンガラ、黄
酸化鉄、黒酸化鉄、酸化チタンをもって比較例3とし
た。
COMPARATIVE EXAMPLE 3 Comparative Example 3 was prepared using sericite, talc, mica, red iron oxide, yellow iron oxide, black iron oxide, and titanium oxide treated with 3% methylhydrogenpolysiloxane manufactured by Toshiki Pigment.

【0048】次に、本発明の処理粉体およびフッ素系油
剤を配合した化粧料の実施例について説明する。なお、
成分の配合割合は重量%である。
Next, examples of cosmetics containing the treated powder of the present invention and a fluorinated oil will be described. In addition,
The mixing ratio of the components is% by weight.

【0049】実施例6(パウダーファンデーション) 実施例3の処理粉体を使用し、表4に示す組成のパウダ
ーファンデーションを製造した。製法は次の通りであ
る。
Example 6 (Powder Foundation) Using the treated powder of Example 3, a powder foundation having the composition shown in Table 4 was produced. The production method is as follows.

【0050】(製法)実施例3の処理粉体を混合、粉砕
してヘンシェルミキサーに移し、残りの成分を加熱混合
し均一にしたものを顔料に混合した後、再び粉砕してふ
るいに通した。これを金皿に圧縮成型してパウダーファ
ンデーションを得た。
(Preparation method) The treated powder of Example 3 was mixed, pulverized and transferred to a Henschel mixer. The remaining components were mixed by heating and homogenized, mixed with a pigment, and then pulverized again and passed through a sieve. . This was compression-molded on a metal plate to obtain a powder foundation.

【0051】実施例7(パウダーファンデーション) 実施例4の処理粉体を使用し、実施例6と同様の方法で
表4に示す組成のパウダーファンデーションを製造し
た。
Example 7 (Powder Foundation) A powder foundation having the composition shown in Table 4 was produced in the same manner as in Example 6, except that the treated powder of Example 4 was used.

【0052】実施例8(パウダーファンデーション) 実施例5の処理粉体を使用し、実施例6と同様の方法で
表4に示す組成のパウダーファンデーションを製造し
た。
Example 8 (Powder Foundation) A powder foundation having the composition shown in Table 4 was produced in the same manner as in Example 6, except that the treated powder of Example 5 was used.

【0053】比較例4(パウダーファンデーション) 実施例3の処理粉体を使用し、実施例6と同様の方法で
表4に示す組成のパウダーファンデーションを製造し
た。
Comparative Example 4 (Powder Foundation) Using the treated powder of Example 3, a powder foundation having the composition shown in Table 4 was produced in the same manner as in Example 6.

【0054】比較例5(パウダーファンデーション) 比較例1の処理粉体を使用し、実施例6と同様の方法で
表4に示す組成のパウダーファンデーションを製造し
た。
Comparative Example 5 (Powder Foundation) Using the treated powder of Comparative Example 1, a powder foundation having the composition shown in Table 4 was produced in the same manner as in Example 6.

【0055】比較例6(パウダーファンデーション) 比較例2の処理粉体を使用し、実施例6と同様の方法で
表4に示す組成のパウダーファンデーションを製造し
た。
Comparative Example 6 (Powder Foundation) Using the treated powder of Comparative Example 2, a powder foundation having the composition shown in Table 4 was produced in the same manner as in Example 6.

【0056】比較例7(パウダーファンデーション) 比較例3の処理粉体を使用し、実施例6と同様の方法で
表4に示す組成のパウダーファンデーションを製造し
た。
Comparative Example 7 (Powder Foundation) Using the treated powder of Comparative Example 3, a powder foundation having the composition shown in Table 4 was produced in the same manner as in Example 6.

【0057】次に、上記のようにして得られた実施例6
〜8および比較例4〜7のパウダーファンデーションに
ついて汗および皮脂に対する化粧持ち、使用感について
評価した。その結果を表5に示す。
Next, Example 6 obtained as described above was used.
The powder foundations of Comparative Examples 4 to 7 and Comparative Examples 4 to 7 were evaluated for their durability and perceived use against sweat and sebum. Table 5 shows the results.

【0058】(評価方法) <化粧持ちおよび使用感>10人の専門パネラーにより
官能評価を行い、次の基準で示した。 〇:8人以上が良いと感じた △:4〜7人が良いと感じた ×:4人未満が良いと感じた
(Evaluation method) <Cosmetic durability and feeling of use> Sensory evaluation was carried out by 10 expert panelists, and the results were shown according to the following criteria. 〇: 8 or more felt good △: 4 to 7 felt good ×: Less than 4 felt good

【0059】[0059]

【表4】 [Table 4]

【0060】[0060]

【表5】 [Table 5]

【0061】表5から明らかなように、本発明のパウダ
ーファンデーション(実施例6〜8)は、本発明の処理
粉体およびフッ素系油剤を配合することにより、比較例
5〜7と比べて、使用感に優れ、化粧持ちが極めて良好
なものであった。また、比較例4から、本発明の処理粉
体とフッ素系油剤を組み合わせて配合することの必然性
が明らかとなった。
As is evident from Table 5, the powder foundations of the present invention (Examples 6 to 8) were mixed with the treated powder of the present invention and a fluorine-based oil agent to give a powder foundation in comparison with Comparative Examples 5 to 7. The feeling of use was excellent and the makeup lasted very well. Further, from Comparative Example 4, the necessity of combining and treating the treated powder of the present invention and a fluorinated oil was clarified.

【0062】実施例9 ほほ紅 実施例3の処理粉体を使用し、実施例6と同様にして目
的のほほ紅を得た。 組成(%) 1 表面処理タルク 60.6 2 表面処理マイカ 20.0 3 表面処理酸化チタン 5.0 4 表面処理ベンガラ 2.0 5 スクワラン 6.0 6 フッ素変性シリコーン油 3.0 (信越化学工業製 FL100) 7 トリオクタン酸グリセリル 3.0 8 防腐剤 0.2 9 香料 0.2
Example 9 Blush The desired blush was obtained in the same manner as in Example 6 except that the treated powder of Example 3 was used. Composition (%) 1 Surface treated talc 60.6 2 Surface treated mica 20.0 3 Surface treated titanium oxide 5.0 4 Surface treated bengara 2.0 5 Squalane 6.0 6 Fluorine-modified silicone oil 3.0 (Shin-Etsu Chemical Co., Ltd.) FL100) 7 Glyceryl trioctanoate 3.0 8 Preservative 0.2 9 Fragrance 0.2

【0063】実施例10 パウダーアイシャドウ 実施例3の処理粉体を使用し、実施例6と同様にして目
的のパウダーアイシャドウを得た。 組成(%) 1 表面処理セリサイト 28.0 2 表面処理マイカ 54.6 3 表面処理ベンガラ 1.0 4 表面処理黄酸化鉄 2.0 5 トリオクタン酸グリセリル 5.0 6 メチルフェニルポリシロキサン 7.0 7 フッ素変性シリコーン油 2.0 (信越化学工業製 FL100) 8 防腐剤 0.2 9 香料 0.2
Example 10 Powder Eye Shadow The desired powder eye shadow was obtained in the same manner as in Example 6 except that the treated powder of Example 3 was used. Composition (%) 1 Surface treated sericite 28.0 2 Surface treated mica 54.6 3 Surface treated bengala 1.0 4 Surface treated yellow iron oxide 2.0 5 Glyceryl trioctanoate 5.0 6 Methylphenyl polysiloxane 7.0 7 Fluorine-modified silicone oil 2.0 (FL100 manufactured by Shin-Etsu Chemical Co., Ltd.) 8 Preservative 0.2 9 Fragrance 0.2

【0064】実施例11 プレストパウダー 実施例3の処理粉体を使用し、実施例6と同様にして目
的のプレストパウダーを得た。 組成(%) 1 表面処理セリサイト 30.0 2 表面処理タルク 57.89 3 表面処理ベンガラ 0.2 4 表面処理黄酸化鉄 0.5 5 表面処理黒酸化鉄 0.01 6 表面処理酸化チタン 3.0 7 トリオクタン酸グリセリル 3.0 8 ジメチルポリシロキサン 3.0 9 フッ素変性シリコーン油 2.0 (信越化学工業製 FL100) 10 防腐剤 0.2 11 香料 0.2
Example 11 Pressed Powder Using the treated powder of Example 3, the same procedure as in Example 6 was carried out to obtain a desired pressed powder. Composition (%) 1 Surface treated sericite 30.0 2 Surface treated talc 57.89 3 Surface treated red iron oxide 0.2 4 Surface treated yellow iron oxide 0.5 5 Surface treated black iron oxide 0.01 6 Surface treated titanium oxide 3 0.07 Glyceryl trioctanoate 3.08 Dimethylpolysiloxane 3.09 Fluorine-modified silicone oil 2.0 (FL100 manufactured by Shin-Etsu Chemical Co., Ltd.) 10 Preservative 0.2 11 Fragrance 0.2

【0065】実施例12 乳化型ファンデーション 実施例3の処理粉体を使用し、目的の乳化型ファンデー
ションを得た。 組成(%) 1 表面処理処理セリサイト 5.0 2 表面処理酸化チタン 7.0 3 表面処理ベンガラ 0.4 4 表面処理黄酸化鉄 1.4 5 表面処理黒酸化鉄 0.2 6 ペンタステアリン酸デカグリセリル 3.0 7 POEメチルグルコシド 1.0 8 スクワラン 10.0 9 デカメチルシクロペンタシロキサン 10.0 10 フッ素変性シリコーン油 12.0 (信越化学工業製 FL100) 11 塩化ジメチルジステアリルアンモニウム 処理ベントナイト 2.0 12 1,3−ブチレングリコール 3.0 13 グリセリン 2.0 14 精製水 42.6 15 防腐剤 0.2 16 香料 0.2 (製法)成分6〜10の混合溶液に成分1〜5および1
1を添加、分散させる。これに成分12〜15の水相を
撹拌しながら添加して乳化し、次いで成分16を添加し
て乳化型ファンデーションを得た。
Example 12 Emulsion-type foundation The target emulsification-type foundation was obtained using the treated powder of Example 3. Composition (%) 1 Surface-treated sericite 5.0 2 Surface-treated titanium oxide 7.0 3 Surface-treated red iron oxide 0.4 4 Surface-treated yellow iron oxide 1.4 5 Surface-treated black iron oxide 0.26 Pentastearic acid Decaglyceryl 3.0 7 POE methyl glucoside 1.08 Squalane 10.0 9 Decamethylcyclopentasiloxane 10.0 10 Fluorine-modified silicone oil 12.0 (FL100 manufactured by Shin-Etsu Chemical Co., Ltd.) 11 Bentonite treated with dimethyl distearyl ammonium chloride 2 0.012 1,3-butylene glycol 3.0 13 Glycerin 2.0 14 Purified water 42.6 15 Preservative 0.2 16 Perfume 0.2 (Production method) Components 1 to 5 and 1
1 is added and dispersed. The aqueous phase of the components 12 to 15 was added thereto while stirring to emulsify, and then the component 16 was added to obtain an emulsified foundation.

【0066】実施例13 油性ファンデーション 実施例3の処理粉体を使用し、目的の油性ファンデーシ
ョンを得た。 組成(%) 1 表面処理処理セリサイト 19.8 2 表面処理処理マイカ 10.0 3 表面処理処理タルク 3.0 4 表面処理酸化チタン 10.0 5 表面処理ベンガラ 0.4 6 表面処理黄酸化鉄 1.4 7 表面処理黒酸化鉄 0.2 8 メチルフェニルポリシロキサン 12.0 9 スクワラン 10.0 10 トリオクタン酸グリセリル 8.0 11 マルチワックス 4.5 12 フッ素変性シリコーン油 20.0 (信越化学工業製 FL100) 13 ソルビタンイソステアレート 0.5 14 香料 0.2 (製法)成分8〜13を加熱混合し、これに成分1〜7
を添加、分散させる。次いで成分14を添加して金皿に
充填し、油性ファンデーションを得た。
Example 13 Oily foundation The target oily foundation was obtained using the treated powder of Example 3. Composition (%) 1 Surface-treated sericite 19.8 2 Surface-treated mica 10.0 3 Surface-treated talc 3.0 4 Surface-treated titanium oxide 10.0 5 Surface-treated Bengala 0.46 Surface-treated iron oxide yellow 1.4 7 Surface-treated black iron oxide 0.28 Methylphenylpolysiloxane 12.09 Squalane 10.0 10 Glyceryl trioctanoate 8.0 11 Multiwax 4.5 12 Fluorine-modified silicone oil 20.0 (Shin-Etsu Chemical Co., Ltd.) FL100) 13 Sorbitan isostearate 0.5 14 Fragrance 0.2 (Production method) Components 8 to 13 are heated and mixed, and components 1 to 7 are added thereto.
Is added and dispersed. Next, component 14 was added and the mixture was filled in a gold plate to obtain an oily foundation.

【0067】実施例9〜13で得られた化粧料はいずれ
も使用感に優れ、化粧持ちが極めて良好なものであっ
た。
The cosmetics obtained in Examples 9 to 13 were all excellent in use feeling and extremely good in cosmetic durability.

【0068】[0068]

【発明の効果】本発明の化粧料は、汗、皮脂による化粧
崩れの防止効果に優れ、且つ使用感、特にフィット感、
平滑性に優れたものである。
EFFECT OF THE INVENTION The cosmetic of the present invention is excellent in the effect of preventing makeup collapse due to sweat and sebum, and has a feeling of use, especially a feeling of fit.
Excellent in smoothness.

───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 FI テーマコート゛(参考) A61K 7/032 A61K 7/032 7/035 7/035 Fターム(参考) 4C083 AB232 AB242 AB432 AB442 AC022 AC122 AC392 AC692 AD041 AD042 AD151 AD161 AD162 AD172 AD202 CC11 CC12 CC14 DD17 DD22 DD33 EE06 EE07 FF01 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) A61K 7/032 A61K 7/032 7/035 7/035 F term (Reference) 4C083 AB232 AB242 AB432 AB442 AC022 AC122 AC122 AC392 AC692 AD041 AD042 AD151 AD161 AD162 AD172 AD202 CC11 CC12 CC14 DD17 DD22 DD33 EE06 EE07 FF01

Claims (5)

【特許請求の範囲】[Claims] 【請求項1】 (a)粉体の表面を一般式(1)[式
中、R1は同種または異種の炭素数1〜20のアルキル
基またはアリール基、R2は−R5−Rf(式中、R5
は炭素数2〜6の二価のアルキレン基を示し、Rfは炭
素数1〜12のパーフルオロアルキル基を示す。)、R
3は−R5−SiX(式中、Xは炭素数1〜4のアル
コキシル基またはハロゲンを示す。)、R4はR1また
はR2またはR3のいずれかであり、l、m、nは整数
であって、l=0〜500、m=1〜500、n=1〜
500である。]で表される含フッ素シリコーンで処理
して得られる粉体、および(b)フッ素系油剤を配合す
ることを特徴とする化粧料。 【化1】
(1) The surface of a powder is represented by the following general formula (1): wherein R1 is the same or different alkyl or aryl group having 1 to 20 carbon atoms, R2 is -R5-Rf (wherein R5
Represents a divalent alkylene group having 2 to 6 carbon atoms, and Rf represents a perfluoroalkyl group having 1 to 12 carbon atoms. ), R
3 -R5-SiX 3 (wherein, X represents an alkoxyl group or a halogen having 1 to 4 carbon atoms.), R4 is either R1 or R2 or R3, l, m, n is a integer Where l = 0 to 500, m = 1 to 500, n = 1 to
500. ] A cosmetic obtained by blending a powder obtained by treating with a fluorine-containing silicone represented by formula (1) and (b) a fluorine-based oil. Embedded image
【請求項2】 一般式(1)の構造中、l=0、m=1
〜50、n=1〜50で、mとnの比が9:1〜2:3
であることを特徴とする請求項1記載の化粧料。
2. In the structure of the general formula (1), 1 = 0, m = 1
-50, n = 1-50, and the ratio of m to n is 9: 1 to 2: 3
The cosmetic according to claim 1, wherein
【請求項3】 一般式(1)の構造中、l=0、m=1
〜50、n=1〜50で、mとnの比が3:1〜1:1
であることを特徴とする請求項1記載の化粧料。
3. In the structure of the general formula (1), 1 = 0, m = 1
-50, n = 1-50, and the ratio of m to n is 3: 1 to 1: 1
The cosmetic according to claim 1, wherein
【請求項4】 フッ素系油剤がフッ素変性シリコーン油
であることを特徴とする請求項1、請求項2または請求
項3記載の化粧料。
4. The cosmetic according to claim 1, wherein the fluorinated oil is a fluorine-modified silicone oil.
【請求項5】 フッ素系油剤がパーフルオロポリエーテ
ルであることを特徴とする請求項1、請求項2または請
求項3記載の化粧料。
5. The cosmetic according to claim 1, wherein the fluorinated oil is perfluoropolyether.
JP11037728A 1999-02-16 1999-02-16 Cosmetic Pending JP2000239117A (en)