JP2000140756A - Coating structure for aluminum wheel - Google Patents
Coating structure for aluminum wheelInfo
- Publication number
- JP2000140756A JP2000140756A JP10319471A JP31947198A JP2000140756A JP 2000140756 A JP2000140756 A JP 2000140756A JP 10319471 A JP10319471 A JP 10319471A JP 31947198 A JP31947198 A JP 31947198A JP 2000140756 A JP2000140756 A JP 2000140756A
- Authority
- JP
- Japan
- Prior art keywords
- coat
- color
- solvent
- powder
- plating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、アルミホールの塗
膜構造に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a coating structure of an aluminum hole.
【０００２】[0002]
【従来の技術】アルミホイールには、意匠性、耐蝕性を
向上させるために、塗装またはめっきが施される。塗装
は、通常、シルバー塗装であるが、高級感を出すために
めっき調コートのニーズもある。メッキは、通常、クロ
ムめっきである。2. Description of the Related Art Painting or plating is applied to aluminum wheels in order to improve design and corrosion resistance. The coating is usually silver coating, but there is also a need for a plating-like coat to give a sense of quality. The plating is usually chrome plating.
【０００３】[0003]
【発明が解決しようとする課題】しかし、従来のアルミ
ホイールの塗装およびめっきにはつぎの問題がある。 １）シルバー塗装では、顔料が不定形で、かつランダム
な配列をしているため、光輝感が出ない。 ２）めっき調コートでは、平滑で薄膜なアルミフレーク
顔料（厚み＝１μｍ以下）を使用するため、光輝感を出
しやすいが、 平行配列しないと光輝感が出にくい。すなわち、アル
ミ鋳肌（飾り窓部はアルミ鋳肌への塗装となる）のよう
に凹凸がある場合は光輝感が発揮できない、 隠蔽性に劣るため、下地の色が全体の外観に影響を及
ぼす、などの特性がある。したがって、めっき調コート
のみの色調では意匠性に乏しい。 ３）クロムの湿式めっきは、作業環境がよくない。ま
た、製造工程が複雑なためコストが極めて高い。 本発明の目的は、めっきの使用を排除でき、めっき調で
しかも深みのある色調を出すことができるアルミホール
の塗膜構造を提供することにある。However, the conventional aluminum wheel coating and plating have the following problems. 1) In silver coating, since the pigments are irregular and have a random arrangement, no glitter is produced. 2) In the plating-like coating, a smooth and thin aluminum flake pigment (thickness: 1 μm or less) is used, so it is easy to give a brilliant feeling. In other words, if there is unevenness such as aluminum casting surface (the decorative window part is painted on aluminum casting surface), the glitter cannot be exhibited. There are such characteristics. Therefore, the color tone of only the plating coat is poor in design. 3) The working environment of chrome wet plating is not good. Further, the cost is extremely high due to the complicated manufacturing process. An object of the present invention is to provide a coating structure of an aluminum hole which can eliminate the use of plating and can produce a plating tone and a deep color tone.
【０００４】[0004]
【課題を解決するための手段】上記の目的を達成する本
発明はつぎの通りである。 （１） アルミホイールの表面に、カラーコートおよび
該カラーコートの上のめっき調コートを含む複数コート
の塗膜を形成したアルミホイールの塗膜構造。 （２） アルミホイールの前処理した表面に、下層側か
ら上層側に順に、粉体プライマー、溶剤あるいは水性カ
ラーベースコート、溶剤あるいは水性めっき調コート、
溶剤あるいは粉体トップコートを形成したアルミホイー
ルの塗膜構造。 （３） アルミホイールの前処理した表面に、下層側か
ら上層側に順に、粉体カラー＆プライマーあるいは溶剤
カラー＆プライマー、溶剤あるいは水性あるいは粉体め
っき調コート、溶剤あるいは粉体トップコートを形成し
たアルミホイールの塗膜構造。 （４） アルミホイールの前処理した表面に、下層側か
ら上層側に順に、粉体あるいは溶剤カラー、粉体あるい
は溶剤あるいは水性めっき調コート、溶剤あるいは粉体
トップコートを形成したアルミホイールの塗膜構造。 （５） アルミホイールの前処理した表面に、下層側か
ら上層側に順に、粉体カラー＆プライマーあるいは溶剤
カラー＆プライマー、粉体あるいは溶剤あるいは水性め
っき調コートを形成したアルミホイールの塗膜構造。The present invention to achieve the above object is as follows. (1) A coating structure of an aluminum wheel in which a plurality of coating films including a color coat and a plating-like coat on the color coat are formed on the surface of the aluminum wheel. (2) In order from the lower layer side to the upper layer side, a powder primer, a solvent or an aqueous color base coat, a solvent or an aqueous plating coat,
Film structure of aluminum wheel with solvent or powder top coat. (3) Powder color & primer or solvent color & primer, solvent or aqueous or powder plating coat, solvent or powder top coat were formed on the pretreated surface of the aluminum wheel in order from the lower layer to the upper layer. Aluminum wheel coating structure. (4) Aluminum wheel coating with powder or solvent color, powder or solvent or aqueous plating tone coat, solvent or powder top coat on the pre-treated surface of the aluminum wheel in order from the lower layer to the upper layer Construction. (5) The coating structure of an aluminum wheel in which a powder color & primer or a solvent color & primer, a powder or a solvent or an aqueous plating coat is formed in order from the lower layer to the upper layer on the pretreated surface of the aluminum wheel.
【０００５】上記（１）、（２）、（３）、（４）、
（５）のアルミホイールの塗膜構造では、複数コート層
中に、カラーコートおよび該カラーコートの上のめっき
調コートが含まれるので、めっき調コートのアルミフレ
ーク顔料の反射だけでなくカラーコートの反射が加わる
ことで、外観意匠ニーズに合った色調を創出することが
でき、意匠性が向上する。また、アルミホイールの膜は
塗膜であり、めっき層でないので、めっきの使用を排除
でき、作業環境はよい。The above (1), (2), (3), (4),
In the coating structure of the aluminum wheel of (5), the color coat and the plating-like coat on the color coat are included in the plurality of coat layers, so that not only the reflection of the aluminum flake pigment of the plating-like coat but also the color coat By adding reflection, it is possible to create a color tone that meets the external design needs, and the design properties are improved. Further, since the film of the aluminum wheel is a coating film and not a plating layer, the use of plating can be eliminated and the working environment is good.
【０００６】[0006]
【発明の実施の形態】本発明実施例のアルミホイールの
塗膜構造を、図面を参照して、説明する。図１、図２は
本発明の第１実施例を示し、図３、図４は本発明の第２
実施例を示し、図５、図６は本発明の第３実施例を示
し、図７〜図９は本発明の第４実施例を示している。本
発明の全実施例にわたって共通または類似する部分に
は、本発明の全実施例にわたって同じ符合を付してあ
る。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The coating film structure of an aluminum wheel according to an embodiment of the present invention will be described with reference to the drawings. 1 and 2 show a first embodiment of the present invention, and FIGS. 3 and 4 show a second embodiment of the present invention.
FIGS. 5 and 6 show a third embodiment of the present invention, and FIGS. 7 to 9 show a fourth embodiment of the present invention. Parts that are common or similar throughout all embodiments of the present invention are given the same reference numerals throughout all embodiments of the present invention.
【０００７】まず、本発明の全実施例にわたって共通ま
たは類似する部分を、たとえば図１、図２を参照して、
説明する。本発明の全実施例のアルミホイールの塗膜構
造は、アルミホイール１の表面に、カラーコート３およ
びカラーコート３の上のめっき調コート４を含む複数コ
ートの塗膜を形成した塗膜構造からなる。First, common or similar parts in all embodiments of the present invention will be described with reference to FIGS. 1 and 2, for example.
explain. The coating structure of the aluminum wheel according to all the embodiments of the present invention is different from the coating structure in which a plurality of coating films including the color coat 3 and the plating coat 4 on the color coat 3 are formed on the surface of the aluminum wheel 1. Become.
【０００８】カラーコート３は、溶剤コートであっても
よいし、水性コートであってもよいし、あるいは粉体コ
ートであってもよい。また、カラーコート３は、カラー
コートのみであってもよいし、あるいはカラー＆プライ
マーコートであってもよい。カラーコート３の色調は、
めっき調コート４と協働して、外観意匠ニーズに合った
色調を創出できる色とする。カラーコート３の色は、外
観意匠ニーズがクロムめっき調である場合、黒または灰
色をベースにした色であることが望ましく、そうするこ
とによって、めっき調コート４をアルミフレーク顔料を
含むコートとして、めっき調コート４と協働してクロム
めっき調を出すことができ、黒または灰色をベースのカ
ラーコート３の色を反映して、クロムめっき調の深みを
増すことができる。[0008] The color coat 3 may be a solvent coat, an aqueous coat, or a powder coat. The color coat 3 may be a color coat alone or a color & primer coat. The color of color coat 3 is
In cooperation with the plating tone coat 4, a color that can create a color tone that meets the external design needs is provided. The color of the color coat 3 is desirably a color based on black or gray when the appearance design needs are chrome plating tone, so that the plating tone coat 4 is a coat containing aluminum flake pigment, The chrome plating tone can be produced in cooperation with the plating tone coat 4, and the depth of the chrome plating tone can be increased by reflecting the color of the color coat 3 based on black or gray.
【０００９】めっき調コート４は、めっき調の光沢を出
すことができるコートであればよいが、たとえば平滑薄
膜（厚み＝１μｍ以下）のアルミフレーク顔料を含むコ
ートはクロムめっき調の光輝性を出すことができるの
で、使用に適する。この場合、図２に示すように、めっ
き調コート４のフレーク４ａがある部分では光６ａはフ
レーク４ａに反射するが、フレーク４ａがない部分では
光６ｂはカラーコート３で反射するので、めっき調にカ
ラーコート３の色を反映することができる。そして、フ
レーク４ａがアルミフレークである場合めっき調はクロ
ムめっき調となり、ベースのカラーコート３の色が黒ベ
ースまたは灰色ベースである場合、クロムめっき調の深
みを増すことができる。The plating coat 4 may be any coat that can give a plating-like luster. For example, a coat containing an aluminum flake pigment having a smooth thin film (thickness of 1 μm or less) gives a chrome-plated glitter. So it can be suitable for use. In this case, as shown in FIG. 2, the light 6a is reflected by the flakes 4a in the portion where the flakes 4a of the plating tone coat 4 exist, but the light 6b is reflected by the color coat 3 in the portion where the flakes 4a do not exist. Can reflect the color of the color coat 3. When the flakes 4a are aluminum flakes, the plating tone is a chrome plating tone, and when the color of the base color coat 3 is a black base or a gray base, the depth of the chrome plating tone can be increased.
【００１０】アルミホイール１のうち外から見える部分
の、複数のコートが塗装される表面は、図１に示すよう
に、切削面１ａと鋳肌面１ｂを含む。アルミホイール１
の前面は切削面１ａであり、飾り窓（ベンチレーショ
ン）の表面は鋳肌面１ｂである。As shown in FIG. 1, the surface of the aluminum wheel 1 on which a plurality of coats are painted includes a cut surface 1a and a casting surface 1b. Aluminum wheel 1
Is a cutting surface 1a, and a surface of a decorative window (ventilation) is a casting surface 1b.
【００１１】アルミホイール１の複数のコートが塗装さ
れる表面は、塗装に先立ち前処理が施される。この前処
理は、従来は 脱脂＋化成（クロメート）であり、従来と同じ前処理
を適用してもよいが、望ましくは、酸洗をいれてつぎの
〜の何れかによる。 脱脂＋酸洗＋化成（クロメート） 脱脂（酸洗効果を付与）＋化成（クロメート） 脱脂＋酸洗＋化成（ノンクロメート） 脱脂＋酸洗＋化成（ノンクロメート）＋後処理 脱脂（酸洗効果を付与）＋化成（ノンクロメート） 脱脂（酸洗効果を付与）＋化成（ノンクロメート）＋
後処理 このように、酸洗を入れることで、従来に比し、優れた
耐蝕性能を発揮させることができる。The surface of the aluminum wheel 1 to be coated with a plurality of coats is subjected to a pre-treatment before painting. This pretreatment is conventionally degreasing + chemical conversion (chromate), and the same pretreatment as in the prior art may be applied. Degreasing + Pickling + Chemical formation (Chromate) Degreasing (providing pickling effect) + Chemical formation (Chromate) Degreasing + Pickling + Chemical formation (Non-chromate) Degreasing + Pickling + Chemical formation (Non-chromate) + Post-treatment Degreasing (Pickling effect) + Chemical formation (non-chromate) Degreasing (providing pickling effect) + Chemical formation (non-chromate) +
Post-treatment In this way, by adding pickling, it is possible to exhibit excellent corrosion resistance performance as compared with the conventional case.
【００１２】つぎに、上記の本発明の全実施例にわたっ
て共通または類似する部分の作用を説明する。第１に、
めっき調コート４を設けたことにより、シルバー塗装で
は得られない光輝外観が得られる。第２に、複数コート
がカラーコート３およびカラーコート３の上のめっき調
コート４を含むので、めっき調アルミフレーク顔料の反
射だけでなく、カラーコート３の反射を加えることで、
外観意匠ニーズに合った色調を創出することができる。
とくに、カラーコート３の色を黒ベースにした場合、従
来のめっきより、深みのある光沢感が得られる。第３
に、前処理に酸洗を入れることで、従来に比し、優れた
耐蝕性能を発揮させることができる。第４に、めっきを
使用しないので、従来のクロムを使った湿式めっきが環
境劣悪であったのに対し、環境がよくなる。また、塗装
であるので、製造工程が湿式めっきに比べて、製造工程
が単純になり、コストを低減できる。Next, the operation of the common or similar parts in all the embodiments of the present invention will be described. First,
By providing the plating tone coat 4, a brilliant appearance which cannot be obtained by silver painting is obtained. Second, since the plurality of coats include the color coat 3 and the plating coat 4 on the color coat 3, the reflection of the color coat 3 as well as the reflection of the plating aluminum flake pigment is added.
A color tone that meets the appearance design needs can be created.
In particular, when the color of the color coat 3 is based on black, a deeper gloss can be obtained as compared with the conventional plating. Third
In addition, by adding pickling to the pretreatment, it is possible to exhibit excellent corrosion resistance performance as compared with the related art. Fourth, since no plating is used, the environment is better than conventional wet plating using chromium, which is poor in environment. Further, since the coating is performed, the manufacturing process is simpler and the cost can be reduced as compared with the wet plating.
【００１３】つぎに、本発明の各実施例に特有な部分を
説明する。本発明の第１実施例では、図１、図２に示す
ように、アルミホイールの塗膜構造が、アルミホイール
１の前処理した表面に、下層側から上層側に順に、粉体
プライマー２、溶剤あるいは水性カラーベースコート
３、溶剤あるいは水性めっき調コート４、溶剤あるいは
粉体トップコート５を形成したものからなる。粉体プラ
イマー２は、アクリル、ポリエステル、エポキシ等から
なる。溶剤あるいは粉体トップコート５はアクリル等か
らなり、クリヤー層である。本発明の第１実施例の作用
はつぎの通りである。粉体プライマー２で、鋳肌面１ｂ
の凹部を平滑化できるので、めっき調アルミフレーク顔
料が平行配列し、鏡面反射が得られ、高意匠化をはかる
ことができる。また、溶剤あるいは粉体トップコート５
を形成したので、耐候性に優れる。Next, parts unique to each embodiment of the present invention will be described. In the first embodiment of the present invention, as shown in FIGS. 1 and 2, the coating structure of the aluminum wheel is formed on the pretreated surface of the aluminum wheel 1 in order from the lower layer to the upper layer, A solvent or aqueous color base coat 3, a solvent or aqueous plating coat 4, and a solvent or powder top coat 5 are formed. The powder primer 2 is made of acrylic, polyester, epoxy or the like. The solvent or powder top coat 5 is made of acrylic or the like and is a clear layer. The operation of the first embodiment of the present invention is as follows. With powder primer 2, casting surface 1b
Can be smoothed, so that the plating-like aluminum flake pigments are arranged in parallel, mirror reflection is obtained, and high design can be achieved. Solvent or powder top coat 5
Formed, it is excellent in weather resistance.
【００１４】本発明の第２実施例では、図３、図４に示
すように、アルミホイールの塗膜構造が、アルミホイー
ル１の前処理した表面に、下層側から上層側に順に、粉
体カラー＆プライマーあるいは溶剤カラー＆プライマー
３（カラーコート３として働く）、溶剤あるいは水性あ
るいは粉体めっき調コート４、溶剤あるいは粉体トップ
コート５を形成したものからなる。粉体カラー＆プライ
マーあるいは溶剤カラー＆プライマー３は、アクリル、
ポリエステル、エポキシ等からなる。溶剤あるいは粉体
トップコート５はアクリル等からなり、クリヤー層であ
る。本発明の第２実施例の作用はつぎの通りである。粉
体カラー＆プライマーあるいは溶剤カラー＆プライマー
３で、鋳肌面１ｂの凹部を平滑化できるので、めっき調
アルミフレーク顔料が平行配列し、鏡面反射が得られ、
高意匠化をはかることができる。また、溶剤あるいは粉
体トップコート５を形成したので、耐候性に優れる。In the second embodiment of the present invention, as shown in FIGS. 3 and 4, the coating structure of the aluminum wheel is applied to the pretreated surface of the aluminum wheel 1 in order from the lower layer to the upper layer. Color & primer or solvent Color & primer 3 (working as color coat 3), solvent or aqueous or powder plating coat 4, and solvent or powder top coat 5 are formed. Powder color & primer or solvent color & primer 3 is acrylic,
It is made of polyester, epoxy or the like. The solvent or powder top coat 5 is made of acrylic or the like and is a clear layer. The operation of the second embodiment of the present invention is as follows. The concave portion of the casting surface 1b can be smoothed with the powder color & primer or the solvent color & primer 3, so that the plating-like aluminum flake pigments are arranged in parallel, and specular reflection is obtained.
High design can be achieved. Further, since the solvent or powder top coat 5 is formed, the weather resistance is excellent.
【００１５】本発明の第３実施例では、図５、図６に示
すように、アルミホイールの塗膜構造が、アルミホイー
ル１の前処理した表面に、下層側から上層側に順に、粉
体あるいは溶剤カラー３（カラーコート３として働
く）、粉体あるいは溶剤あるいは水性めっき調コート
４、溶剤あるいは粉体トップコート５を形成したものか
らなる。粉体あるいは溶剤カラー３は、アクリル、ポリ
エステル、エポキシ等からなる。溶剤あるいは粉体トッ
プコート５はアクリル等からなり、クリヤー層である。
本発明の第３実施例の作用はつぎの通りである。粉体あ
るいは溶剤カラー３で、鋳肌面１ｂの凹部を平滑化でき
るので、めっき調アルミフレーク顔料が平行配列し、鏡
面反射が得られ、高意匠化をはかることができる。ま
た、溶剤あるいは粉体トップコート５を形成したので、
耐候性に優れる。In the third embodiment of the present invention, as shown in FIGS. 5 and 6, the coating structure of the aluminum wheel is applied to the pretreated surface of the aluminum wheel 1 in the order from the lower layer to the upper layer. Alternatively, it is formed by forming a solvent color 3 (working as a color coat 3), a powder or solvent or aqueous plating tone coat 4, and a solvent or powder top coat 5. The powder or solvent color 3 is made of acrylic, polyester, epoxy or the like. The solvent or powder top coat 5 is made of acrylic or the like and is a clear layer.
The operation of the third embodiment of the present invention is as follows. Since the concave portions of the casting surface 1b can be smoothed with the powder or the solvent color 3, the plating-like aluminum flake pigments are arranged in parallel, mirror reflection can be obtained, and high design can be achieved. Also, since the solvent or powder top coat 5 was formed,
Excellent weather resistance.
【００１６】本発明の第４実施例では、図７〜図９に示
すように、アルミホイールの塗膜構造が、アルミホイー
ル１の前処理した表面に、下層側から上層側に順に、粉
体カラー＆プライマーあるいは溶剤カラー＆プライマー
３（カラーコート３として働く）、粉体あるいは溶剤あ
るいは水性めっき調コート４を形成したものからなる。
粉体カラー＆プライマーあるいは溶剤カラー＆プライマ
ー３は、アクリル、ポリエステル、エポキシ等からな
る。粉体あるいは溶剤あるいは水性めっき調コート４
は、図９に示すように、望ましくは２層分離粉体めっき
調コートからなり、下層４ｂがめっき調コートで上層４
ｃがトップクリアーである。粉体あるいは溶剤あるいは
水性めっき調コート４は、アルミフレーク顔料を含み、
樹脂はたとえばアクリルである。本発明の第４実施例の
作用はつぎの通りである。粉体カラー＆プライマーある
いは溶剤カラー＆プライマー３で、鋳肌面１ｂの凹部を
平滑化できるので、めっき調アルミフレーク顔料が平行
配列し、鏡面反射が得られ、高意匠化をはかることがで
きる。粉体あるいは溶剤あるいは水性めっき調コート４
が２層分離粉体めっき調コートからなる場合は、上層が
トップコートとして働き、耐候性に優れる。In the fourth embodiment of the present invention, as shown in FIGS. 7 to 9, the coating structure of the aluminum wheel is applied to the pretreated surface of the aluminum wheel 1 in order from the lower layer to the upper layer. Color & primer or solvent Color & primer 3 (working as color coat 3), powder or solvent or aqueous plating coat 4 formed.
The powder color & primer or the solvent color & primer 3 is made of acrylic, polyester, epoxy or the like. Powder or solvent or aqueous plating coat 4
As shown in FIG. 9, the lower layer 4b is desirably composed of a two-layered powder plating coat,
c is top clear. The powder or solvent or water-based plating tone coat 4 contains aluminum flake pigment,
The resin is, for example, acrylic. The operation of the fourth embodiment of the present invention is as follows. The concave portion of the casting surface 1b can be smoothed by the powder color & primer or the solvent color & primer 3, so that the plating-like aluminum flake pigments are arranged in parallel, mirror reflection is obtained, and high design can be achieved. Powder or solvent or aqueous plating coat 4
Is composed of a two-layer separated powder plating tone coat, the upper layer acts as a top coat and is excellent in weather resistance.
【００１７】[0017]
【発明の効果】請求項１、２、３、４、５のアルミホイ
ールの塗膜構造によれば、複数コート層中に、カラーコ
ートおよび該カラーコートの上のめっき調コートが含ま
れるので、めっき調コートのアルミフレークの反射だけ
でなくカラーコートの反射が加わることで、外観意匠ニ
ーズに合った色調を創出することができ、意匠性が向上
する。また、アルミホイールの膜は塗膜であり、めっき
層でないので、めっきの使用を排除でき、環境上望まし
く、またコスト低減をはかることができる。請求項２の
アルミホイールの塗膜構造によれば、アルミホイール表
面に粉体プライマーを設け、粉体プライマーの上に溶剤
あるいは水性カラーベースコート、溶剤あるいは水性め
っき調コートを設けるので、粉体プライマーが鋳肌の凹
部を埋めて平滑化し、溶剤あるいは水性めっき調コート
中のアルミフレークが平行配列し、鏡面反射が得られ、
高意匠化をはかることができる。また、溶剤あるいは粉
体トップコートを有するので、耐候性に優れる。請求項
３のアルミホイールの塗膜構造によれば、アルミホイー
ル表面に粉体カラー＆プライマーあるいは溶剤カラー＆
プライマー、溶剤あるいは水性あるいは粉体めっき調コ
ートを設けるので、粉体カラー＆プライマーあるいは溶
剤カラー＆プライマーが鋳肌の凹部を埋めて平滑化し、
溶剤あるいは水性あるいは粉体めっき調コート中のアル
ミフレークが平行配列し、鏡面反射が得られ、高意匠化
をはかることができる。また、溶剤あるいは粉体トップ
コートを有するので、耐候性に優れる。請求項４のアル
ミホイールの塗膜構造によれば、アルミホイール表面に
粉体あるいは溶剤カラー、粉体あるいは溶剤あるいは水
性めっき調コートを設けるので、粉体あるいは溶剤カラ
ーが鋳肌の凹部を埋めて平滑化し、粉体あるいは溶剤あ
るいは水性めっき調コート中のアルミフレークが平行配
列し、鏡面反射が得られ、高意匠化をはかることができ
る。また、溶剤あるいは粉体トップコートを有するの
で、耐候性に優れる。請求項５のアルミホイールの塗膜
構造によれば、アルミホイール表面に粉体カラー＆プラ
イマーあるいは溶剤カラー＆プライマー、粉体あるいは
溶剤あるいは水性めっき調コートを設けるので、粉体カ
ラー＆プライマーあるいは溶剤カラー＆プライマーが鋳
肌の凹部を埋めて平滑化し、粉体あるいは溶剤あるいは
水性めっき調コート中のアルミフレークが平行配列し、
鏡面反射が得られ、高意匠化をはかることができる。According to the coating structure of the aluminum wheel of the first, second, third, fourth and fifth aspects, the color coat and the plating-like coat on the color coat are included in the plurality of coat layers. The reflection of the color coat as well as the reflection of the aluminum flake of the plating-like coat can create a color tone that meets the external design needs, and the design property is improved. Further, since the film of the aluminum wheel is a coating film and not a plating layer, the use of plating can be eliminated, which is environmentally desirable and can reduce costs. According to the coating film structure of the aluminum wheel of claim 2, the powder primer is provided on the aluminum wheel surface, and the solvent or aqueous color base coat, the solvent or aqueous plating tone coat is provided on the powder primer. Filling the concave part of the casting surface and smoothing it, the aluminum flakes in the solvent or aqueous plating tone coat are arranged in parallel, mirror reflection is obtained,
High design can be achieved. Also, since it has a solvent or powder top coat, it has excellent weather resistance. According to the coating structure of the aluminum wheel according to the third aspect, a powder color & primer or a solvent color &
Primer, solvent or water-based or powder plating-like coat is provided, so powder color & primer or solvent color & primer fills the recesses of the casting surface and smoothes,
Aluminum flakes in a solvent, water-based, or powder-plating-like coat are arranged in parallel, mirror reflection is obtained, and high design can be achieved. Also, since it has a solvent or powder top coat, it has excellent weather resistance. According to the coating structure of the aluminum wheel according to the fourth aspect, since the powder or solvent color, the powder or solvent or aqueous plating coat is provided on the aluminum wheel surface, the powder or solvent color fills the concave portion of the casting surface. The aluminum flakes in the powder or solvent or water-based plating tone coat are arranged in parallel, and the mirror reflection is obtained, so that the design can be improved. Also, since it has a solvent or powder top coat, it has excellent weather resistance. According to the coating film structure of the aluminum wheel according to the fifth aspect, the powder color & primer or the solvent color & primer, the powder / solvent or aqueous plating tone coat is provided on the aluminum wheel surface, so that the powder color & primer or the solvent color is provided. & Primer fills the recesses of the casting surface and smoothes it, and the aluminum flakes in the powder, solvent or aqueous plating tone coat are arranged in parallel,
Specular reflection can be obtained, and high design can be achieved.
【図１】本発明の第１実施例のアルミホイールの塗膜構
造の、トップコート形成前の状態の、一部断面図であ
る。FIG. 1 is a partial cross-sectional view of a coating structure of an aluminum wheel according to a first embodiment of the present invention in a state before a top coat is formed.
【図２】本発明の第１実施例のアルミホイールの塗膜構
造の一部断面図である。FIG. 2 is a partial sectional view of a coating structure of the aluminum wheel according to the first embodiment of the present invention.
【図３】本発明の第２実施例のアルミホイールの塗膜構
造の、トップコート形成前の状態の、一部断面図であ
る。FIG. 3 is a partial cross-sectional view of a coating structure of an aluminum wheel according to a second embodiment of the present invention in a state before a top coat is formed.
【図４】本発明の第２実施例のアルミホイールの塗膜構
造の一部断面図である。FIG. 4 is a partial sectional view of a coating structure of an aluminum wheel according to a second embodiment of the present invention.
【図５】本発明の第３実施例のアルミホイールの塗膜構
造の、トップコート形成前の状態の、一部断面図であ
る。FIG. 5 is a partial cross-sectional view of a coating structure of an aluminum wheel according to a third embodiment of the present invention, in a state before a top coat is formed.
【図６】本発明の第３実施例のアルミホイールの塗膜構
造の一部断面図である。FIG. 6 is a partial sectional view of a coating structure of an aluminum wheel according to a third embodiment of the present invention.
【図７】本発明の第４実施例のアルミホイールの塗膜構
造の、トップコート形成前の状態の、一部断面図であ
る。FIG. 7 is a partial sectional view of a coating structure of an aluminum wheel according to a fourth embodiment of the present invention, in a state before a top coat is formed.
【図８】本発明の第４実施例のアルミホイールの塗膜構
造の一部断面図である。FIG. 8 is a partial sectional view of a coating structure of an aluminum wheel according to a fourth embodiment of the present invention.
【図９】本発明の第４実施例のアルミホイールの塗膜構
造の粉体めっき調コートが２層分離粉体コートからなる
場合の粉体めっき調コートの一部断面図である。FIG. 9 is a partial cross-sectional view of a powder coating tone coat having a coating film structure of an aluminum wheel according to a fourth embodiment of the present invention in the case where the powder plating tone coat comprises a two-layer separated powder coat.
１ アルミホイール １ａ 切削面 １ｂ 鋳肌面 ２ 粉体プライマー ３ カラーコート ４ めっき調コート ５ トップコート DESCRIPTION OF SYMBOLS 1 Aluminum wheel 1a Cutting surface 1b Casting surface 2 Powder primer 3 Color coat 4 Plating coat 5 Top coat
───────────────────────────────────────────────────── フロントページの続き (72)発明者 清水 徹 東京都千代田区四番町５番地９ トピー工 業株式会社内 (72)発明者 斉藤 卓章 東京都千代田区四番町５番地９ トピー工 業株式会社内 (72)発明者 佐藤 隆行 東京都千代田区四番町５番地９ トピー工 業株式会社内 (72)発明者 小栗 立也 東京都千代田区四番町５番地９ トピー工 業株式会社内 Ｆターム(参考） 4D075 CB13 DA04 DB07 ──────────────────────────────────────────────────続 き Continuing on the front page (72) Inventor Toru Shimizu 5-9, Yonbancho, Chiyoda-ku, Tokyo Topy Engineering Co., Ltd. (72) Inventor Takusho Saito 5-9, Yonbancho, Chiyoda-ku Tokyo (72) Inventor Takayuki Sato 5-9, Yonbancho, Chiyoda-ku, Tokyo Topy Industries, Ltd. (72) Tatsuya Oguri 5-9, Yonbancho, Chiyoda-ku, Tokyo Topy Industries, Ltd. F term (reference) 4D075 CB13 DA04 DB07
Claims (5)
および該カラーコートの上のめっき調コートを含む複数
コートの塗膜を形成したアルミホイールの塗膜構造。1. A coating film structure of an aluminum wheel in which a plurality of coating films including a color coat and a plating coat on the color coat are formed on the surface of the aluminum wheel.
層側から上層側に順に、粉体プライマー、溶剤あるいは
水性カラーベースコート、溶剤あるいは水性めっき調コ
ート、溶剤あるいは粉体トップコートを形成したアルミ
ホイールの塗膜構造。2. An aluminum wheel in which a powder primer, a solvent or aqueous color base coat, a solvent or aqueous plating tone coat, a solvent or aqueous plating tone coat, and a solvent or powder top coat are formed on the pretreated surface of the aluminum wheel in order from the lower layer to the upper layer. Coating structure.
層側から上層側に順に、粉体カラー＆プライマーあるい
は溶剤カラー＆プライマー、溶剤あるいは水性あるいは
粉体めっき調コート、溶剤あるいは粉体トップコートを
形成したアルミホイールの塗膜構造。3. A pre-treated surface of an aluminum wheel is provided with a powder color & primer, a solvent color & primer, a solvent or aqueous or powder plating coat, a solvent or powder top coat in order from the lower layer to the upper layer. Film structure of the formed aluminum wheel.
層側から上層側に順に、粉体あるいは溶剤カラー、粉体
あるいは溶剤あるいは水性めっき調コート、溶剤あるい
は粉体トップコートを形成したアルミホイールの塗膜構
造。4. An aluminum wheel having a powder or solvent color, a powder or solvent or aqueous plating tone coat, a solvent or powder top coat formed in order from the lower layer to the upper layer on the pretreated surface of the aluminum wheel. Coating structure.
層側から上層側に順に、粉体カラー＆プライマーあるい
は溶剤カラー＆プライマー、粉体あるいは溶剤あるいは
水性めっき調コートを形成したアルミホイールの塗膜構
造。5. A coating film of an aluminum wheel on which a powder color & primer or a solvent color & primer, a powder or a solvent or an aqueous plating coat is formed in order from the lower layer to the upper layer on the pretreated surface of the aluminum wheel. Construction.