JP2000129927A - Repairing method of coated surface - Google Patents
Repairing method of coated surfaceInfo
- Publication number
- JP2000129927A JP2000129927A JP10324539A JP32453998A JP2000129927A JP 2000129927 A JP2000129927 A JP 2000129927A JP 10324539 A JP10324539 A JP 10324539A JP 32453998 A JP32453998 A JP 32453998A JP 2000129927 A JP2000129927 A JP 2000129927A
- Authority
- JP
- Japan
- Prior art keywords
- painted
- painted surface
- polishing
- repairing
- wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、建物の外壁や屋根
等における塗装面の補修方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for repairing a painted surface on an outer wall or a roof of a building.
【０００２】[0002]
【従来の技術】従来より、建物の外壁や屋根等の塗装に
際しては、一般に有機系塗料が使用されている。この有
機系塗料の使用された外壁等は近年問題となっている紫
外線や酸性雨等に弱く、これらの被害により塗装面は５
〜７年程度、早いものでは４年程度で劣化、腐食する状
況にある。このような場合、現在では再度塗装を施すこ
とにより外壁等の補修を行っている。2. Description of the Related Art Conventionally, organic paints have been generally used for painting exterior walls and roofs of buildings. The outer walls and the like where this organic paint is used are vulnerable to ultraviolet rays and acid rain, which have become problems in recent years.
Deterioration and corrosion occur in about 7 years or as early as about 4 years. In such a case, the outer walls and the like are currently repaired by painting again.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、外壁等
の塗装面の再塗装を行う場合には以下のような問題があ
る。 （１）補修工事に長期間（一般の家一軒当たり７日〜１
０日）を要す。 （２）塗料等を大量に使用するため作業コストが非常に
かかり、結果として依頼人の必要コストも大きくなる。 （３）補修工事の際に発生する塗料の飛散、悪臭、及び
騒音（塗料吹きつけの際に使用するコンプレッサー等の
音）により近隣住宅へ迷惑がかかる。 （４）産業廃棄物（塗装缶等）が発生し、処分が困難で
ある。 本発明はかかる事情に鑑みてなされたもので、周囲環境
への影響を抑制すると共に補修工事の期間及びコストを
低減し、かつ、補修後の塗装面を長期にわたって維持可
能な塗装面の補修方法を提供することを目的とする。However, when repainting a painted surface such as an outer wall, there are the following problems. (1) Long term repair work (7 days to 1 house per house)
0 days). (2) Since a large amount of paint or the like is used, the operation cost is extremely high, and as a result, the required cost of the client increases. (3) Dispersion of paint, odor, and noise (sound of compressor used when spraying paint) generated during repair work may cause trouble to nearby houses. (4) Industrial waste (painted cans, etc.) is generated, making disposal difficult. The present invention has been made in view of the above circumstances, a method for repairing a painted surface capable of suppressing the influence on the surrounding environment, reducing the period and cost of the repair work, and maintaining the painted surface after the repair for a long period of time. The purpose is to provide.
【０００４】[0004]
【課題を解決するための手段】前記目的に沿う本発明に
係る塗装面の補修方法は、建物の塗装壁を洗浄し、該塗
装壁の表面の汚れを除去する第１工程と、前記表面の汚
れを除去した塗装壁をバフを装着したポリッシャーで研
磨し、新しい塗装面を露出させる第２工程と、前記新し
い塗装面に該新しい塗装面を保護するコーティング剤を
塗布する第３工程とを有している。本発明に係る塗装面
の補修方法においては、塗装壁を研磨することにより、
塗装壁の劣化及び／又は腐食した部分（表面層）を除去
し、新しい塗装面を露出させる。そして、この新しい塗
装面にコーティング処理を施す。これにより、塗装面は
非常に美しいものとなり、再度塗装を行うことなく塗装
面の補修を行うことが可能となる。According to the present invention, there is provided a method for repairing a painted surface according to the present invention, comprising the steps of: cleaning a painted wall of a building and removing dirt on the surface of the painted wall; A second step of polishing the dirt-removed painted wall with a polisher equipped with a buff to expose a new painted surface, and a third step of applying a coating agent for protecting the new painted surface to the new painted surface; are doing. In the method for repairing a painted surface according to the present invention, by polishing the painted wall,
The degraded and / or corroded portions (surface layer) of the painted wall are removed to expose a new painted surface. Then, a coating process is applied to the new painted surface. As a result, the painted surface becomes very beautiful, and it becomes possible to repair the painted surface without performing painting again.
【０００５】ここで、前記第２工程では、前記塗装壁の
表面から３〜１５μｍの表面層を除去することが望まし
い。これにより確実に新しい塗装面を露出することがで
きる。この範囲とするのは、３μｍ未満であると塗装面
の劣化及び／又は腐食部分を充分に除去することができ
ないという問題があり、１５μｍを超えると下地が表面
に露出する可能性があるという問題があるからである。
また、前記第２工程は、前記塗装壁の一部の塗装層を除
去する粗研磨工程と、該粗研磨工程後の塗装面を滑らか
に整える仕上げ研磨工程とを有することが望ましい。劣
化部分を除去する工程と塗装面を滑らかに整える工程と
が分割され、効率よく滑らかな新しい塗装面を得ること
ができる。Here, in the second step, it is desirable to remove a surface layer of 3 to 15 μm from the surface of the painted wall. This ensures that the new painted surface is exposed. If the thickness is less than 3 μm, there is a problem that the deterioration of the painted surface and / or the corroded portion cannot be sufficiently removed, and if it exceeds 15 μm, the base may be exposed on the surface. Because there is.
Preferably, the second step includes a rough polishing step of removing a part of the coating layer of the coating wall, and a finish polishing step of smoothing a coated surface after the rough polishing step. The step of removing the deteriorated portion and the step of smoothing the painted surface are divided, so that a new smooth painted surface can be obtained efficiently.
【０００６】前記粗研磨工程における研磨にはスポンジ
バフを装着した回転式ポリッシャーを使用し、前記仕上
げ研磨工程における研磨にはタオル地のバフを装着した
振動式ポリッシャーを使用することが望ましい。粗研磨
にスポンジバフを装着した回転式ポリッシャーを使用す
ることで劣化及び／又は腐食部分の除去が容易となり、
また、仕上げ研磨にタオル地のバフを装着した振動式ポ
リッシャーを使用することで塗装面を滑らかに整えるこ
とが容易となると共に塗装面につやを出すことが可能と
なる。前記第２工程は、さらに、毛の長いバフを装着し
た振動式ポリッシャーを使用して目地部を滑らかに整え
る補足研磨工程を有することが望ましい。これにより、
目地部が存在する場合にも目地部表面を確実に滑らかに
整えることができる。Preferably, a rotary polisher equipped with a sponge buff is used for polishing in the rough polishing step, and a vibration polisher equipped with a buff of toweling is used for polishing in the finish polishing step. The use of a rotary polisher equipped with a sponge buff for rough polishing facilitates removal of deteriorated and / or corroded parts,
In addition, by using a vibratory polisher equipped with a buff of toweling for finish polishing, it becomes easy to smoothly prepare the painted surface, and it is possible to gloss the painted surface. It is preferable that the second step further includes a supplementary polishing step of using an oscillating polisher equipped with a long buff to smooth the joints. This allows
Even when the joint is present, the joint surface can be reliably and smoothly arranged.
【０００７】[0007]
【発明の実施の形態】続いて、添付した図面を参照しつ
つ、本発明を具体化した実施の形態つき説明し、本発明
の理解に供する。ここに、図１は本発明の一実施の形態
に係る塗装面の補修方法の工程説明図である。DESCRIPTION OF THE PREFERRED EMBODIMENTS Next, with reference to the attached drawings, embodiments of the present invention will be described to provide an understanding of the present invention. Here, FIG. 1 is a process explanatory view of a method for repairing a painted surface according to one embodiment of the present invention.
【０００８】図１に示すように、本発明の一実施の形態
に係る塗装面の補修方法は、まず始めに建物の塗装壁
（１５０ｍ2 程度）の洗浄を行う（ステップ１）。ま
ず、塗装面の鳥の巣、蜂の巣の跡（土部分）等を皮スキ
等を用いて塗装面を傷つけないように削り取る。次い
で、ホースで水を流しながら塗装面に付着している大気
中の不純物やゴミ、虫の死骸等の表面の汚れを毛ブラシ
を使って洗い流す。なお、塗装壁とは例えば、一般に構
造材料として使用される石材、セメント、モルタル、コ
ンクリート、アスファルト、セラミックス、木材、金属
等からなる壁に塗料を塗布したもの、及びこれらの材料
からなる塗装タイルを壁面に備えたものをいい、外壁の
みならず屋根面も含む。As shown in FIG. 1, in a method for repairing a painted surface according to an embodiment of the present invention, first, a painted wall (about 150 m 2 ) of a building is washed (step 1). First, the bird's nest and beehive's mark (soil portion) on the painted surface are scraped off using a leather bar or the like so as not to damage the painted surface. Next, while pouring water with a hose, dirt on the surface such as impurities in the atmosphere, dust, and dead insects attached to the painted surface is washed away using a bristle brush. In addition, the painted wall is, for example, a stone that is generally used as a structural material, cement, mortar, concrete, asphalt, ceramics, wood, a paint applied to a wall made of metal, etc., and painted tiles made of these materials It refers to the one provided on the wall surface, and includes not only the outer wall but also the roof surface.
【０００９】次に、粗研磨を行う（ステップ２）。回転
式ポリッシャー（シングルアクションポリッシャー）に
例えば合成樹脂（ウレタン等）又はゴム等からなる円板
状のスポンジバフを装着し、そのスポンジバフに研磨剤
を軽く一周程度塗布する。ここで研磨剤には、例えばア
ルミナ等の微粉末（０．５〜２μｍ程度、場合によって
はそれより大きいもの）を含む研磨剤を使用することが
できる。スポンジバフを壁面に押し当ててから、回転式
ポリッシャーのスイッチを入れる。回転式ポリッシャー
の回転数は、通常１５００〜２０００ｒｐｍ程度とする
のが好ましい。回転式ポリッシャーを回転させながら、
右側へ（又は左側へ）押し上げながら研磨剤を薄く延ば
すつもりで研磨を行う。磨きムラがでる恐れがあるので
同じ部分を１秒以上磨かないようにする。この１回の研
磨面積は５ｍ2 とし、例えば１５０ｍ2 の研磨を行う場
合には、３０回程度に分けて行うことが好ましい。な
お、劣化又は腐食がひどい部分は、回転式ポリッシャー
の回転数を１２００〜１５００ｒｐｍ程度として２回に
分けて磨くようにし、磨きムラができるだけでないよう
にする。Next, rough polishing is performed (step 2). A disk-shaped sponge buff made of, for example, synthetic resin (urethane or the like) or rubber is mounted on a rotary polisher (single action polisher), and the abrasive is lightly applied to the sponge buff for about one round. Here, as the abrasive, for example, an abrasive containing a fine powder of alumina or the like (about 0.5 to 2 μm, in some cases larger than that) can be used. Press the sponge buff against the wall and switch on the rotary polisher. The rotational speed of the rotary polisher is preferably set to about 1500 to 2000 rpm. While rotating the rotary polisher,
Polishing is intended to spread the abrasive thinly while pushing up to the right (or to the left). Do not polish the same part for more than 1 second, because polishing unevenness may occur. The polishing area at one time is 5 m 2. For example, in the case of polishing 150 m 2 , it is preferable to perform the polishing in about 30 times. In addition, the portion where deterioration or corrosion is severe is polished in two times by setting the rotation speed of the rotary polisher to about 1200 to 1500 rpm so that polishing unevenness is minimized.
【００１０】こうして塗装面を磨くことにより、劣化及
び／又は腐食部分（一部の塗装層）が除去され、劣化さ
れていない塗装面を露出させることができる。なお、こ
の工程で使用するバフには、スポンジバフの他にフェル
ト製バフ等も使用することができる。[0010] By polishing the painted surface in this way, the deteriorated and / or corroded portion (part of the painted layer) is removed, and the undegraded painted surface can be exposed. In addition, as a buff used in this step, a felt buff or the like can be used in addition to the sponge buff.
【００１１】次に、仕上げ研磨を行う（ステップ３）。
この仕上げ研磨により塗装面のバフ目や磨き傷等を取り
除くと共に、場合によっては粗研磨で研磨できない塗装
面の凹部を研磨する。まず、例えば木綿からなる円板状
のタオル地のバフを振動式ポリッシャー（ダブルアクシ
ョンポリッシャー）に装着する。タオル地のバフに研磨
剤を軽く１周する程度塗布する。ここで使用する研磨剤
は、粗研磨で使用したものと同等のものを使用すること
ができ、これを水で希釈して使用するとよい。タオル地
のバフを壁面に押し当ててから、振動式ポリッシャーの
スイッチを入れる。振動式ポリッシャーを上から下方向
に押し当てて研磨を行う。この１回の研磨面積は５ｍ2
とすることが好ましい。この仕上げ研磨により、粗研磨
後の露出した塗装面を滑らかに整え、つやを出すことが
できる。なお、これらの粗研磨及び仕上げ研磨により塗
装面の表面から３〜１５μｍより好ましくは５〜１０μ
ｍの表面層を取り除くようにする。また、場合（塗装層
が厚い場合等）によっては、３０μｍ程度の表面層を取
り除くことも可能である。Next, finish polishing is performed (step 3).
This finish polishing removes buffs and polishing scratches on the painted surface, and in some cases, polishes recesses on the painted surface which cannot be polished by rough polishing. First, a disk-shaped towel buff made of, for example, cotton is attached to a vibration-type polisher (double-action polisher). Apply the abrasive lightly to the buff of the toweling to make one round. The abrasive used here can be the same as that used in the rough polishing, and it is preferable to dilute this with water before use. Press the towel buff against the wall and switch on the vibratory polisher. Polishing is performed by pressing a vibration type polisher downward from above. This one polishing area is 5m 2
It is preferable that By this finish polishing, the exposed painted surface after the rough polishing can be smoothed and polished. In addition, by these rough polishing and finish polishing, the surface of the painted surface is 3 to 15 μm, more preferably 5 to 10 μm.
Remove the surface layer of m. In some cases (such as when the coating layer is thick), a surface layer of about 30 μm can be removed.
【００１２】次に、補足研磨を行う（ステップ４）。こ
れは塗装面がタイル調である場合の目地部を研磨し、そ
の目地部を滑らかに整えるためである。まず、例えば羊
毛等からなる円板状の毛の長いバフを振動式ポリッシャ
ーに装着する。そして、研磨剤を毛の長いバフに軽く１
周する程度塗布する。このとき使用する研磨剤も前記粗
研磨及び仕上げ研磨で使用したものを使用することがで
き、仕上げ研磨のときよりもさらに水で希釈して使用す
るとよい。また、より軟らかい研磨剤を使用すると更に
よい。次に、毛の長いバフを目地部分に押し当ててか
ら、振動式ポリッシャーのスイッチを入れる。バフを目
地部に入れ込むつもりで振動式ポリッシャーを上から下
方向に押し当てて研磨を行う。なお、ここで使用するバ
フは、毛の長さが１０〜４０ｍｍ程度、より好ましくは
２０〜３０ｍｍ程度のものがよい。Next, supplementary polishing is performed (step 4). This is to grind the joints when the painted surface is tile-like, and to smooth the joints. First, a disk-shaped long buff made of, for example, wool or the like is attached to the vibration type polisher. Then, apply the abrasive lightly to a buff with a long hair.
Apply to the extent that it goes around. The polishing agent used at this time may be the same as that used in the rough polishing and the final polishing, and it is preferable to further dilute the polishing agent with water as compared with the final polishing. It is even better to use a softer abrasive. Next, press the long buff on the joint, and then turn on the vibration polisher. Polishing is performed by pressing the vibrating polisher downward from above with the intention of inserting the buff into the joint. The buff used here has a hair length of about 10 to 40 mm, more preferably about 20 to 30 mm.
【００１３】次に、洗浄して研磨剤の除去を行う（ステ
ップ５）。研磨剤の入っていない洗剤をブラシにつけ、
塗装面をこする。汚れがひどいときは濃いめの洗剤、汚
れが少ないときは薄めの洗剤とする。場所によりスプレ
ーを使って直接吹きつけるとよい。洗剤で洗浄した後
は、水で洗い流す。水で洗い流す際は、壁面に洗剤のし
みが残らないように地面まで確実に洗い流す。そして、
壁面の乾燥を行う（ステップ６）。Next, the abrasive is removed by washing (step 5). Apply a non-abrasive detergent to the brush,
Rub the painted surface. If the stain is severe, use a thicker detergent. If the stain is less, use a thinner detergent. It is good to spray directly with a spray depending on the location. After washing with detergent, rinse with water. When flushing with water, be sure to wash down to the ground so that no detergent stains remain on the wall. And
The wall surface is dried (step 6).
【００１４】乾燥後、コーキング目地（目地部）に破損
部分がある場合には、コーキング材の補修を行う（ステ
ップ７）。まず、コーキング目地の破損部分の両側の壁
面にマスキングテープをはり、コーキング材が新しい塗
装面に飛散しないようにする。次に、破損部分にコーキ
ングガンを用いてコーキング材を充填する。余ったコー
キング材はへらで延ばす。そして、マスキングテープを
はがす。ここで、コーキング材には例えばエチレン・酢
酸ビニル共重合体エマルジョンと、ポリオレフィン、ポ
リスチレン、ポリ塩化ビニル、ポリウレタン等の各種合
成樹脂発泡体の粒子とからなる組成物を使用することが
できる。次に、コーキング目地に沿って両側にそれぞれ
１〜２ｍｍの間隔をあけて新たなマスキングテープをは
り、新しい塗装面に塗料が飛散するのを防止する。壁色
に合わせて塗料を調合し、コーキング材を充填した部分
に塗料を塗布する。そして、乾燥を行う。After drying, if the caulking joint (joint part) has a damaged portion, the caulking material is repaired (step 7). First, apply masking tape to the walls on both sides of the damaged part of the caulking joint to prevent the caulking material from scattering on the new painted surface. Next, the damaged portion is filled with a caulking material using a caulking gun. Extra caulk is spread with a spatula. Then, remove the masking tape. Here, as the caulking material, a composition comprising, for example, an ethylene / vinyl acetate copolymer emulsion and particles of various synthetic resin foams such as polyolefin, polystyrene, polyvinyl chloride, and polyurethane can be used. Next, a new masking tape is applied on both sides along the caulking joint at an interval of 1 to 2 mm to prevent the paint from scattering on the new painted surface. A paint is prepared according to the wall color, and the paint is applied to a portion filled with the caulking material. Then, drying is performed.
【００１５】コーキング材の補修の後に、新しい塗装面
を保護するためコーティング剤の塗布を行う（ステップ
８）。このコーティング剤は、市販されている透明なフ
ッ素配合のコーティング剤等を使用することができる。
まず、コーティング剤を容器へ移す。ハンドローラを容
器に入れ、コーティング剤を充分に浸した後、垂れない
程度にコーティング剤を除去する。ハンドローラを壁面
にあて、上から下へ垂れが残らないように延ばす。ハン
ドローラを当てた後、すぐに刷毛で延ばしていく。な
お、刷毛は毛が抜けないように抜いておく。コーティン
グ剤を塗布後、乾燥させる（ステップ９）。ここまでの
工程は、天候の影響及び塗装面の劣化及び／又は腐食の
程度によって多少遅延する場合もあるが、普通４日程度
で終了する。なお、本ステップにおいては例えば、ＥＣ
１８シリーズ（有限会社クリーンエクセル製浸透性強化
剤）を塗布した後に、ＥＣ３０シリーズ（同社製被膜形
成強化剤）を塗布することもでき、表面を長期間にわた
って保護できるものであれば他の１種又は２種以上のコ
ーティング剤を使用することも可能である。また、例え
ばメチルトリメトキシシラン又はフェニルトリメトキシ
シラン等の一般式Ｒ1Ｓｉ（ＯＲ2 )3（式中、Ｒ1 は炭
素数１〜１０の有機基、Ｒ2 は炭素数１〜５のアルキル
基及び／又は炭素数１〜４のアシル基を表す）で示され
るオルガノアルコキシシラン、シリコーン樹脂エマルジ
ョン、親水性有機溶剤、水、及び硬化触媒を主成分とす
る組成物からなるコーティング剤を使用することもでき
る。After repairing the caulking material, a coating agent is applied to protect the new painted surface (step 8). As this coating agent, a commercially available coating agent containing fluorine and the like can be used.
First, the coating agent is transferred to a container. After putting the hand roller in the container and immersing the coating agent sufficiently, the coating agent is removed to the extent that it does not drip. Place the hand roller on the wall and extend it from top to bottom without dripping. Immediately after applying the hand roller, it is spread with a brush. The brush should be pulled out so that the hair does not come off. After applying the coating agent, it is dried (step 9). The above steps may be slightly delayed depending on the influence of the weather and the degree of deterioration and / or corrosion of the painted surface, but are usually completed in about four days. In this step, for example, EC
After applying the 18 series (a penetration enhancer manufactured by Clean Excel Co., Ltd.), the EC30 series (a film formation enhancer manufactured by the company) can also be applied. Alternatively, two or more coating agents can be used. Further, for example, a general formula R 1 Si (OR 2 ) 3 such as methyltrimethoxysilane or phenyltrimethoxysilane (wherein, R 1 is an organic group having 1 to 10 carbon atoms, and R 2 is an alkyl group having 1 to 5 carbon atoms) Group and / or an acyl group having 1 to 4 carbon atoms), a coating agent comprising a composition mainly composed of an organoalkoxysilane, a silicone resin emulsion, a hydrophilic organic solvent, water, and a curing catalyst. You can also.
【００１６】最後に、補修工事の品質検査を行う（ステ
ップ１０）。目視でコーティング未施工部分、汚れた部
分の有無を検査する。コーティング未施工部分がある場
合はコーティング剤の塗布を行い、汚れが残っている部
分がある場合には、その部分のコーティング剤を剥がし
仕上げ研磨以降の工程を繰り返し行う。この補足工事は
１日程度で終了する。Finally, a quality inspection of the repair work is performed (step 10). Visually inspect for uncoated and dirty areas. If there is an uncoated portion, the coating agent is applied. If there is a remaining portion, the coating agent is removed from that portion, and the steps after finish polishing are repeated. This supplementary work is completed in about one day.
【００１７】このように本実施の形態に係る塗装面の補
修方法においては、もとの塗装色を蘇生することにより
再塗装を施すことなく塗装面を補修することができる。
また、補修工事に要する期間は、検査での補足工事が必
要ない場合には４日程度で終了し、補足工事が必要な場
合でも５日程度で終了することができる。As described above, in the method for repairing a painted surface according to the present embodiment, the painted surface can be repaired without repainting by reviving the original paint color.
In addition, the period required for repair work can be completed in about four days when supplementary work for inspection is not required, and can be completed in about five days even when supplementary work is required.
【００１８】以上、本発明を一実施の形態を参照して説
明してきたが、本発明は何ら上記した実施の形態に記載
の構成に限定されるものでなく、特許請求の範囲に記載
されている事項の範囲内で考えられるその他の実施の形
態や変形例も含むものである。例えば本実施の形態にお
いては、補足研磨及び目地の補修を行ったが、これらの
処理は必要な場合のみ行えばよい。また、もともと（補
修前）の塗装面に塗料が剥がれている部分がある場合に
は、その部分のみに適宜塗装を施すようにするとよい。
更に、塗装の厚みにもよるが本発明は、同一塗装面に対
して２度、３度と繰り返して実施することが可能であ
る。As described above, the present invention has been described with reference to an embodiment. However, the present invention is not limited to the configuration described in the above embodiment, and is described in the claims. The present invention also includes other embodiments and modifications that can be considered within the scope of the matters. For example, in the present embodiment, supplementary polishing and joint repair are performed, but these processes may be performed only when necessary. Further, if there is a portion where the paint has been peeled off from the originally painted surface (before the repair), it is preferable to appropriately paint only that portion.
Further, depending on the thickness of the coating, the present invention can be repeatedly performed twice or three times on the same coated surface.
【００１９】[0019]
【発明の効果】請求項１〜５記載の塗装面の補修方法に
おいては、塗装壁の表面の汚れを除去する第１工程と、
新しい塗装面を露出させる第２工程と、新しい塗装面に
該新しい塗装面を保護するコーティング剤を塗布する第
３工程とを有しているので、塗装を施すことなく劣化及
び／又は腐食した塗装面を非常に美しい塗装面に補修す
ることができ、その補修後の塗装面を長期にわたって維
持することが可能となる。また、以下の効果がある。 （１）補修工事期間の短縮が可能となる。 （２）作業コスト及び依頼人の必要コストの低減が可能
となる。 （３）塗料の飛散がない。 （４）悪臭を発生しない。 （５）塗装面を磨く際に使用されるポリッシャーの音は
塗料を吹き付ける際に使用されるコンプレッサー等に比
較して音が小さく、騒音を抑制することができる。 （６）塗料缶等を使用しないため産業廃棄物を必要最小
限まで減らすことができる。According to the method for repairing a painted surface according to the first to fifth aspects, a first step of removing stains on the surface of the painted wall;
A second step of exposing a new painted surface and a third step of applying a coating agent for protecting the new painted surface to the new painted surface, so that the deteriorated and / or corroded coating is not applied. The surface can be repaired to a very beautiful painted surface, and the repaired painted surface can be maintained for a long time. The following effects are also obtained. (1) The repair work period can be shortened. (2) It is possible to reduce the operation cost and the required cost of the client. (3) There is no paint scattering. (4) No odor is generated. (5) The sound of a polisher used when polishing a painted surface is smaller than that of a compressor or the like used when spraying paint, and noise can be suppressed. (6) Since no paint cans are used, industrial waste can be reduced to a minimum.
【００２０】請求項２記載の塗装面の補修方法において
は、第２工程では、塗装壁の表面から３〜１５μｍの表
面層を除去するので、確実に新たな塗装面を露出するこ
とができる。請求項３記載の塗装面の補修方法において
は、第２工程では、塗装壁の一部の塗装層を除去する粗
研磨工程と粗研磨工程後の塗装面を滑らかに整える仕上
げ研磨工程とを有しているので、主として劣化及び／又
は腐食部分を除去する工程と主として塗装面を滑らかに
する工程が分割され、効率よく滑らかな新しい塗装面を
得ることができる。すなわち、補修期間の短縮が可能と
なる。In the method for repairing a painted surface according to the second aspect, in the second step, a surface layer of 3 to 15 μm is removed from the surface of the painted wall, so that a new painted surface can be reliably exposed. In the method for repairing a painted surface according to claim 3, the second step includes a rough polishing step of removing a part of the painted layer of the painted wall and a finish polishing step of smoothing the painted surface after the rough polishing step. Therefore, the step of mainly removing the deteriorated and / or corroded portion and the step of mainly smoothing the painted surface are divided, so that a new smooth painted surface can be obtained efficiently. That is, the repair period can be shortened.
【００２１】請求項４記載の塗装面の補修方法において
は、粗研磨にスポンジバフを装着した回転式ポリッシャ
ーを使用するので劣化及び／又は腐食部分の除去が容易
となる。また、仕上げ研磨にタオル地のバフを装着した
振動式ポリッシャーを使用するので塗装面を滑らかに整
え、つやを出すことができると共に場合によっては粗研
磨により研磨できない凹部を滑らかに整えることが可能
となる。請求項５記載の塗装面の補修方法においては、
第２工程は、さらに、毛の長いバフを装着した振動式ポ
リッシャーを使用して目地部を滑らかに整える補足研磨
工程を有しているので、目地部が存在する場合にもその
目地部の表面を研磨することが可能となって、目地部の
ある塗装面に対応できるようになる。In the method for repairing a painted surface according to the fourth aspect, since a rotary polisher equipped with a sponge buff is used for rough polishing, deterioration and / or corroded portions can be easily removed. In addition, the use of a vibratory polisher fitted with a buff of toweling for finish polishing makes it possible to make the painted surface smooth and glossy, and in some cases it is possible to make smooth the concave parts that cannot be polished by rough polishing. . In the method for repairing a painted surface according to claim 5,
The second step further includes a supplementary polishing step for smoothing the joints using a vibrating polisher equipped with a long buff, so that the joints have a surface even when the joints are present. Can be polished, and it is possible to cope with a painted surface having joints.
【図１】本発明の一実施の形態に係る塗装面の補修方法
の工程説明図である。FIG. 1 is a process explanatory view of a method for repairing a painted surface according to one embodiment of the present invention.
Claims (5)
の汚れを除去する第１工程と、 前記表面の汚れを除去した塗装壁をバフを装着したポリ
ッシャーで研磨し、新しい塗装面を露出させる第２工程
と、 前記新しい塗装面に該新しい塗装面を保護するコーティ
ング剤を塗布する第３工程とを有することを特徴とする
塗装面の補修方法。1. A first step of cleaning a painted wall of a building and removing dirt on the surface of the painted wall, and polishing the painted wall from which the dirt on the surface has been removed by a polisher equipped with a buff to obtain a new painted surface. And a third step of applying a coating agent for protecting the new painted surface to the new painted surface.
て、前記第２工程では、前記塗装壁の表面から３〜１５
μｍの表面層を除去することを特徴とする塗装面の補修
方法。2. The method for repairing a painted surface according to claim 1, wherein in the second step, the surface of the painted wall is 3 to 15 minutes away from the surface of the painted wall.
A method for repairing a painted surface, characterized by removing a surface layer of μm.
において、前記第２工程は、前記塗装壁の一部の塗装層
を除去する粗研磨工程と、該粗研磨工程後の塗装面を滑
らかに整える仕上げ研磨工程とを有することを特徴とす
る塗装面の補修方法。3. The method for repairing a painted surface according to claim 1 or 2, wherein the second step includes a rough polishing step of removing a part of a painted layer of the painted wall, and a painted surface after the rough polishing step. A method of repairing a painted surface, comprising: a finishing polishing step for smoothing the surface.
て、前記粗研磨工程における研磨にはスポンジバフを装
着した回転式ポリッシャーを使用し、前記仕上げ研磨工
程における研磨にはタオル地のバフを装着した振動式ポ
リッシャーを使用することを特徴とする塗装面の補修方
法。4. The method for repairing a painted surface according to claim 3, wherein a rotary polisher equipped with a sponge buff is used for polishing in said rough polishing step, and a buff of toweling is mounted for polishing in said finish polishing step. A method for repairing painted surfaces, characterized by using a vibrating polisher.
において、前記第２工程は、さらに、毛の長いバフを装
着した振動式ポリッシャーを使用して目地部を滑らかに
整える補足研磨工程を有することを特徴とする塗装面の
補修方法。5. The method for repairing a painted surface according to claim 3, wherein the second step further comprises a supplementary polishing step of using an oscillating polisher equipped with a buff having a long hair to smooth the joints. A method for repairing a painted surface, comprising: