JP2000119972A - Fiber for artificial hair applied with new processing agent and ornament for head - Google Patents
Fiber for artificial hair applied with new processing agent and ornament for headInfo
- Publication number
- JP2000119972A JP2000119972A JP10289675A JP28967598A JP2000119972A JP 2000119972 A JP2000119972 A JP 2000119972A JP 10289675 A JP10289675 A JP 10289675A JP 28967598 A JP28967598 A JP 28967598A JP 2000119972 A JP2000119972 A JP 2000119972A
- Authority
- JP
- Japan
- Prior art keywords
- compound
- fiber
- agent
- ethylene oxide
- wig
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION
【０００１】[0001]
【発明の属する技術分野】本発明は新規な処理剤を付着
してなる人工毛髪用繊維、並びに頭飾製品に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a fiber for artificial hair to which a novel treating agent is attached and a head decoration product.
【０００２】[0002]
【従来の技術】一般に人工毛髪繊維を頭飾製品に加工す
る場合には、要求品質として、繊維の分繊性や櫛通り性
および帯電防止性といった加工特性に加え、自然な触
感、外観、、保湿性、およびフリッツ防止性（フリッツ
とは、頭飾製品をブラッシングしたり、着用した頭飾製
品と衣服との摩擦等によって生じるもつれや縮れのこと
をいう）といった美容特性を満足するものが望まれてい
る。これらの要求品質を満足させるために様々な人工毛
髪繊維用処理剤が使用されている。たとえば分繊性、櫛
通り性やフリッツ防止性の改善には、ジメチルシリコー
ンに代表されるシリコーンオイルを主成分とした処理
剤、ケラチンやコラーゲン等蛋白質の誘導体、４級アン
モニウム塩、高級アルコール硫酸エステル塩、ポリエチ
レングリコールの脂肪酸エステル塩類、ポリエチレング
リコールエーテル類等の平滑性を有する界面活性剤等が
用いられており、また帯電防止性や触感の改善には長鎖
アルキルアルコール類、長鎖アルキルを含む４級アンモ
ニウム塩類、グリコール類やオキシラン誘導体を始めと
する多価アルコール類、ケラチンやコラーゲン等蛋白質
の誘導体、あるいは帯電防止性や保湿性を有する界面活
性剤等が用いられている。しかしながら、これらの従来
の処理剤は、それぞれ、開繊性や帯電防止性といった単
独の特性の改良には効果があるものの、頭飾製品に要求
される数多くの特性をバランス良く満足するものではな
かった。たとえば頭飾製品の櫛通りを向上させる特長の
ある処理剤を用いると保湿性が失われたり、逆に保湿性
を向上させる特長のある処理剤を用いると頭飾製品の触
感がべたついて櫛通りが重くなったりするなどである。
また、処理剤は取り扱いの面から、水溶性あるいは水分
散型のものが多く用いられているが、頭飾製品は人間の
頭髪装飾に用いるものは勿論のこと、人形等その他の用
途に用いた場合でも、使用時には汚れ等が発生し、シャ
ンプー等による洗浄が付加欠である。従来の処理剤で
は、要求品質を満たすための必要量を人工毛髪繊維ある
いは頭飾品製品に付着させても、シャンプー等により洗
浄を行うことで、処理剤が容易に脱落し、要求品質を満
足できなくなるという問題が有った。一方特公平６−４
７７８７にシリコーン系繊維処理剤について記載され、
シリコーン系処理剤を有機溶剤及び又は乳化剤を用いて
エマルジョンにして付与した繊維は柔軟性が良くなり、
耐洗濯性が向上すると記載されている。しかし人工毛髪
繊維に使用する記載がなく、このシリコーン系繊維処理
剤を人工毛髪繊維に用いた時、頭飾製品の要求品質は得
られなかった。さらに、処理剤に耐シャンプー性を向上
させるためジメチルシリコーンに代表されるシリコーン
オイルを主成分とした処理剤と前述のシリコーン系処理
剤以外の処理剤を混合した場合には、混合後の処理剤の
安定性が低下したり、その処理剤を付与して加工された
頭飾製品の光沢が変化（処理剤により光沢が強くなった
り、弱くなる。）するといった問題点等があり、要求品
質を満足するバランスの取れる処理剤は見出されていな
い実状があった。2. Description of the Related Art In general, when artificial hair fibers are processed into head decoration products, in addition to processing characteristics such as fiber separation properties, combability and antistatic properties, natural texture, appearance, and moisture retention are required. What has been desired is one that satisfies cosmetic properties such as properties and fritz prevention properties (frits refers to entanglement or frizziness caused by brushing of a head decoration product or friction between a worn head decoration product and clothes, etc.). . Various treatment agents for artificial hair fibers have been used to satisfy these required qualities. For example, in order to improve fiber separation, combability, and fritz prevention, a treatment agent containing silicone oil as a main component represented by dimethyl silicone, a derivative of a protein such as keratin or collagen, a quaternary ammonium salt, or a higher alcohol sulfate ester Surfactants having smoothness such as salts, fatty acid ester salts of polyethylene glycol, polyethylene glycol ethers and the like are used, and long-chain alkyl alcohols and long-chain alkyl are included for improving antistatic properties and tactile sensation. Polyhydric alcohols such as quaternary ammonium salts, glycols and oxirane derivatives, protein derivatives such as keratin and collagen, and surfactants having antistatic properties and moisturizing properties are used. However, although these conventional treatment agents are effective in improving individual properties such as spreadability and antistatic property, respectively, they do not satisfy a number of properties required for head decoration products in a well-balanced manner. . For example, if a treatment agent that has the property of improving the combability of a head decoration product is used, the moisturizing property is lost, and if a processing agent that has a feature of improving the moisture retention property is used, the feel of the head decoration product is sticky and the combing is heavy. And so on.
In addition, water-soluble or water-dispersed treatment agents are often used from the viewpoint of handling, but head decoration products are used not only for human hair decoration, but also for dolls and other uses. However, when used, dirt and the like are generated, and washing with a shampoo or the like is not necessary. With conventional treatment agents, even if the necessary amount to satisfy the required quality is attached to artificial hair fibers or head ornament products, the treatment agent can easily fall off by washing with shampoo etc., and the required quality can be satisfied. There was a problem of disappearing. On the other hand, 6-6-4
7787 describes a silicone fiber treatment agent,
Fibers obtained by emulsifying a silicone-based treatment agent with an organic solvent and / or an emulsifier have improved flexibility,
It states that washing resistance is improved. However, there is no description for use in artificial hair fibers. When this silicone fiber treating agent is used in artificial hair fibers, the required quality of a head decoration product cannot be obtained. Furthermore, when a treating agent containing a silicone oil as a main component represented by dimethyl silicone and a treating agent other than the above-mentioned silicone treating agent are mixed in order to improve the shampooing resistance, the treating agent after mixing is used. The required quality is satisfied, for example, there is a problem such as a decrease in stability, or a change in the gloss of the head decoration product processed by applying the treating agent (the gloss increases or becomes weaker by the treating agent). There was a situation in which a balanced treatment agent was not found.
【０００３】[0003]
【発明が解決しようとする課題】本発明の目的は、水溶
性で取り扱い易い油剤の性質は維持しながら要求品質を
満足し、且つ従来の問題点であった耐シャンプー性を改
善した処理剤を付与した人工毛髪用繊維並びに頭飾製品
を提供するものである。SUMMARY OF THE INVENTION An object of the present invention is to provide a treating agent which satisfies the required quality while maintaining the properties of a water-soluble and easy-to-handle oil agent and which has improved the conventional problems of shampooing resistance. The present invention provides an artificial hair fiber and a head decoration product provided.
【０００４】[0004]
【課題を解決するための手段】上記課題を達成すべく鋭
意検討した結果、エチレンオキシドとプロピレンオキシ
ドを主成分とする化合物とアミノ変性シリコーンを主成
分とする油剤を用いてなる処理剤を使用する事により上
記課題を解決出来る事を見出した。すなわち本発明は、
エチレンオキシドとプロピレンオキシドを主成分とする
化合物（Ａ）と、アミノ変性シリコーンを主成分とする
油剤（Ｂ）を含有する処理剤を付着してなる人工毛髪用
繊維であり、化合物（Ａ）がエチレンオキシドとプロピ
レンオキシドのブロック共重合体、エチレンオキシドと
プロピレンオキシドのランダム共重合体およびエチレン
オキシドとプロピレンオキシドのアルキルエーテルから
なる群より選択される少なくとも１種の化合物であるの
が好ましい。また処理剤中の化合物（A）の固形成分と
油剤（B）のシリコーン純分の重量比が３０／７０〜９
５／５％であるのが好ましく、またアミノ変性シリコー
ンが下記一般式（Ｉ）で表されるシリコーン系化合物で
あるのがより好ましい。Means for Solving the Problems As a result of intensive studies to achieve the above object, the use of a treating agent comprising a compound containing ethylene oxide and propylene oxide as main components and an oil containing amino-modified silicone as a main component has been proposed. Have found that the above problem can be solved. That is, the present invention
An artificial hair fiber obtained by adhering a compound (A) containing ethylene oxide and propylene oxide as main components and a treating agent containing an oil agent (B) containing amino-modified silicone as a main component, wherein the compound (A) is ethylene oxide. It is preferably at least one compound selected from the group consisting of a block copolymer of ethylene oxide and propylene oxide, a random copolymer of ethylene oxide and propylene oxide, and an alkyl ether of ethylene oxide and propylene oxide. Further, the weight ratio of the solid component of the compound (A) to the pure silicone of the oil agent (B) in the treating agent is 30 / 70-9.
It is preferably 5/5%, and the amino-modified silicone is more preferably a silicone-based compound represented by the following general formula (I).
【化３】 （但し式中、R1、R2、R3、R5、R6及びR7は炭素数１〜６
のアルキルであり、R4は−R8―NH−CH2―CH2―NH2であ
り、R8は炭素数３〜６のアルキレンである。アミン当量
は５００以上４０００未満であり、平均分子量は５００
０〜１０００００の範囲である。またｍは１００〜２７
００の整数、ｎは１〜２００の整数である。） 本発明の頭飾製品は、上記した人工毛髪用繊維を加工し
て頭飾製品としたものと、頭飾製品に加工する段階にお
いて、はじめて上記処理剤を付着させたもの、および、
上記した人工毛髪用繊維を加工する段階においても、前
記処理剤を付着してなる頭飾製品を含むものであり、上
記処理剤における化合物（Ａ）の固形成分と、油剤
（Ｂ）のシリコーン純分が合計で人工毛髪繊維に対し
０.０２〜５重量％となるように付着してなる頭飾製品
が好ましい。Embedded image (Wherein, R 1 , R 2 , R 3 , R 5 , R 6 and R 7 have 1 to 6 carbon atoms)
R 4 is —R 8 —NH—CH 2 —CH 2 —NH 2 , and R 8 is alkylene having 3 to 6 carbon atoms. The amine equivalent is 500 or more and less than 4000, and the average molecular weight is 500
The range is from 0 to 100,000. M is 100 to 27
An integer of 00 and n is an integer of 1 to 200. The head decoration product of the present invention is obtained by processing the above-described artificial hair fiber to form a head decoration product, and in the stage of processing into the head decoration product, the first treatment agent is attached thereto, and
At the stage of processing the above-mentioned artificial hair fiber, it also includes a head decoration product to which the above-mentioned treating agent is adhered, and comprises a solid component of the compound (A) and a silicone pure component of the oil agent (B) in the above-mentioned treating agent. Is preferably a head decoration product adhered to the artificial hair fiber in a total amount of 0.02 to 5% by weight.
【０００５】[0005]
【発明の実施の形態】本発明でいう毛髪用繊維とは、ウ
ィッグ、ツーペ、ヘアアクセサリーや人形用頭髪等とい
った頭飾製品への加工を目的として製造された頭飾製品
への加工前の繊維であり、例えば人毛やヤクの毛等から
なる動物系の天然繊維、コラーゲン等タンパク質を可溶
化してなる再生繊維、あるいはポリ塩化ビニル、ポリプ
ロピレン、ポリエステル、ポリアミド、ポリクラール、
ポリアクリロニトリル及びモダクリル等からなる合成繊
維等が挙げられる。BEST MODE FOR CARRYING OUT THE INVENTION The fiber for hair referred to in the present invention is a fiber which has been manufactured for the purpose of processing into a head decoration product such as a wig, a tub, a hair accessory, a hair for a doll, etc., and has not been processed into a head decoration product. For example, animal-based natural fibers such as human hair and yak hair, regenerated fibers obtained by solubilizing proteins such as collagen, or polyvinyl chloride, polypropylene, polyester, polyamide, polyclar,
Synthetic fibers made of polyacrylonitrile, modacrylic, and the like are included.
【０００６】本発明でいうウィッグとは婦人用、紳士用
を問わず頭部に面で取り付ける主におしゃれを楽しむた
めの装飾品であり、その装着面積によって部分ウィッ
グ、ハーフウィッグ、七分ウィッグ、フルウィッグ等に
分けられる。[0006] The wig referred to in the present invention is a decorative article mainly attached to the head of a woman or a gentleman for enjoying the fashion, mainly for a woman, and depending on the mounting area, a partial wig, a half wig, a seven-minute wig, It is divided into full wigs and the like.
【０００７】本発明でいうツーペとは婦人用、紳士用を
問わず主に薄毛の人や何らかの事情により一部乃至全体
の頭髪が脱毛した人が薄毛や脱毛部分を隠すために装着
する疑似頭髪製品をいう。[0007] The term "tupe" used in the present invention refers to a pseudo hair that is worn by a person with thin hair or a person who has partially or completely depilated hair for some reason, regardless of whether it is for women or men, to hide the thin or depilated portion. Refers to a product.
【０００８】本発明でいうヘアアクセサリーとは地毛や
頭皮に取り付ける主におしゃれを楽しむことを目的とし
たウィッグを除く装飾品の総称であり、例えばヘアピン
やヘアクリップ等を介して地毛に取り付けて地毛を長く
見せるためのエクステンションや、頭皮に沿って縄状に
編んだ地毛に縫いつけたり頭皮や地毛に接着剤等で主に
帯状に取り付けるウィービング（単に繊維を束ねたもの
や当業者では一般にウェフトとよばれる繊維を腰ミノ状
に加工した繊維束、更にはそれらにカール形状を付与し
た装飾品）等が挙げられる。[0008] The hair accessory as referred to in the present invention is a generic name of ornaments attached to the ground hair or scalp, mainly for the purpose of enjoying fashion, excluding wigs. For example, the hair accessory is attached to the ground hair via a hairpin or a hair clip. Extensions to make the ground hair look longer, sewn to the ground hair knitted in a rope shape along the scalp, or weaving that is mainly attached to the scalp or the hair with an adhesive etc. Fiber bundles obtained by processing fibers generally called wafts into a waist-mino shape, and decorative articles having a curl shape added thereto.
【０００９】本発明でいう人形用頭髪とは一般にいう人
形やぬいぐるみ、マネキン等の頭部に取り付けるための
頭飾製品をいう。The hair for a doll in the present invention means a head decoration product for attaching to a head of a doll, a stuffed animal, a mannequin or the like.
【００１０】また本発明の処理剤で用いられるエチレン
オキシドとプロピレンオキシドを主成分とする化合物
（Ａ）とは、エチレンオキシドとプロピレンオキシドの
共重合体を意味しており、中でもエチレンオキシドとプ
ロピレンオキシドのブロック共重合体、エチレンオキシ
ドとプロピレンオキシドのランダム共重合体、およびエ
チレンオキシドとプロピレンオキシドのアルキルエーテ
ルが好ましい。尚、本発明で言うエチレンオキシドとプ
ロピレンオキシドの共重合体とは、ポリオキシエチレン
とポリオキシプロピレンの共重合体と同じ物を意味して
いる。The compound (A) having ethylene oxide and propylene oxide as main components used in the treating agent of the present invention means a copolymer of ethylene oxide and propylene oxide, and particularly, a block copolymer of ethylene oxide and propylene oxide. Polymers, random copolymers of ethylene oxide and propylene oxide, and alkyl ethers of ethylene oxide and propylene oxide are preferred. In the present invention, the copolymer of ethylene oxide and propylene oxide means the same as the copolymer of polyoxyethylene and polyoxypropylene.
【００１１】エチレンオキシドとプロピレンオキシドの
共重合体とは一般に酸化プロピレンを重合してポリプロ
ピレングリコールを製造し、さらに酸化エチレンを付加
重合することによって製造されるブロックポリマー型非
イオン活性剤であり、乳化剤や分散剤として知られてお
り一般にフレーク状で市販されている。又エチレンオキ
シドとプロピレンオキシドのランダム共重合体は酸化エ
チレンと酸化プロピレンを共重合させて得られ、エチレ
ンオキシドとプロピレンオキシドのアルキルエーテルは
高級アルコールに酸化プロピレンを付加重合し、さらに
酸化エチレンを付加重合させたものである。これらは、
本処理剤中のアミノ変性シリコーンの乳化、分散を助
け、また親水性の性質が頭飾製品の繊維部分に保湿性を
付与することで、加工後の頭飾製品の触感からガサツキ
感を排除し同時に帯電防止性を付与することができる。
しかしながら前記化合物（Ａ）を単一成分とした人工毛
髪繊維用処理剤では他の親水性のある界面活性剤と同様
に保湿性、触感、帯電防止性は向上できてもそれ以外の
頭飾製品に要求される特性に対して不十分であるだけで
なく、せっかく付与した保湿性、触感、帯電防止性も洗
浄耐久性がなく、例えば頭飾製品をシャンプーする等に
より水に濡らしたときに処理剤が洗い流されてしまうと
いう問題が発生しやすい。A copolymer of ethylene oxide and propylene oxide is a block polymer type nonionic activator generally produced by polymerizing propylene oxide to produce polypropylene glycol and then subjecting ethylene oxide to addition polymerization. It is known as a dispersant and is generally commercially available in flake form. In addition, a random copolymer of ethylene oxide and propylene oxide is obtained by copolymerizing ethylene oxide and propylene oxide, and the alkyl ether of ethylene oxide and propylene oxide is obtained by addition polymerization of propylene oxide to a higher alcohol and further addition polymerization of ethylene oxide. Things. They are,
Helps emulsify and disperse the amino-modified silicone in this treatment agent.Hydrophilic property imparts moisture retention to the fiber part of the head decoration product, eliminating the rough feeling from the touch of the processed head decoration product and charging at the same time. Prevention can be imparted.
However, the treatment agent for artificial hair fibers containing the compound (A) as a single component can improve the moisturizing property, the tactile sensation and the antistatic property as well as other hydrophilic surfactants, but can be applied to other head ornament products. Not only is it inadequate for the required properties, but also the moisturizing, touch, and antistatic properties imparted with no preservative cleaning durability, for example, when the treatment agent is wet with water by shampooing the head decoration product, etc. The problem of being washed away is likely to occur.
【００１２】一方、本発明でいうアミノ変性シリコーン
を主成分とする油剤（Ｂ）のアミノ変性シリコーンと
は、炭化水素の塩化物に高温下で触媒を作用させて得た
オルガノクロルシランを加水分解、縮合重合する過程の
中でメチル基の一部をアミノアルキル基に置き換えたも
のである。このアミノ変性シリコーンは、シリコーンオ
イルの中では比較的容易に乳化することができ、安定な
可溶化物を得ることができる点で他のシリコーンオイル
より優れており、またシリコーンオイル特有の潤滑性、
撥水性、防水性、平滑性等を付与することができること
から、開繊性（繊維同士の分離性やそれに伴う櫛通り
等）や帯電防止性といった加工特性を向上させることに
加え、自然な触感、外観、良好な櫛通り、保湿性、およ
びフリッツ防止性（フリッツとは、頭飾製品をブラッシ
ングしたり、着用した頭飾製品と衣服との摩擦等によっ
て生じるもつれや縮れのことをいう）といった頭飾製品
の美容特性を満足することができる上、頭飾製品にアミ
ノ変性シリコーン特有の著しい柔軟性を付与することが
できる。この柔軟性は人工毛髪用繊維の水酸基、カルボ
キシル基等とシリコーンオイル中のアミノ基との反応に
よって、シリコーンが強く繊維に配向、皮膜形成するこ
とに起因すると考えられる。またその反応により頭飾製
品に付与した自然な触感、外観、良好な櫛通り、保湿性
やフリッツ防止性といった美容特性には洗浄耐久性があ
り、頭飾製品が例えばシャンプー等で水に濡れたりした
ときでも付与した特性を保持することができるのであ
る。このアミノ変性シリコーンの特性を表す要素の一つ
にアミン当量がある。このアミン当量が低くなるとその
アミノ変性シリコーンと繊維との反応性が高くなる傾向
にあるが、反面シリコーンオイルに由来する潤滑性や平
滑性といった特徴が出にくい傾向にあるばかりでなく、
極端な場合にはアミノアルキル基の影響で処理剤を使用
中に手あれを起こす等というような安全衛生上の問題が
発生する可能性がある。逆にアミン当量が高くなるとシ
リコーンオイルの潤滑性、平滑性が強くなる傾向にあ
り、開繊性の向上や頭飾製品の櫛通り性の向上は期待で
きる反面、極端な場合には、潤滑性、平滑性が強調され
過ぎてかえって加工性を悪化させたり、加工後の頭飾製
品の触感がドライで硬い仕上がりになる等の問題が発生
することがある。また官能基の割合が低いことで頭飾製
品をなす繊維の種類によっては処理剤と繊維との反応性
が乏しくなり、処理剤の効果の洗浄耐久性にも問題が発
生することがある。以上のような理由からアミン当量は
５００以上４０００未満の範囲であることが望ましく、
アミン当量がこの範囲であるアミノ変性シリコーンは特
に人工毛髪繊維との反応性に富み、それでいながら安全
衛生上の問題のない、頭飾製品の加工及び頭飾製品の特
性に優れた効果を発揮する処理剤の原料の一部となりう
るのである。またアミノ変性シリコーンの平均分子量も
アミン当量と同様にそのアミノ変性シリコーンの特性を
表す要素の一つである。この平均分子量が小さいと分散
性や溶解性は向上するがシリコーンオイルに由来する潤
滑性や平滑性といった特徴は出にくくなる傾向にあり、
極端な場合には開繊性や帯電防止性といった加工性や頭
飾製品の櫛通りの向上が期待できない事がある。逆に平
均分子量が高いと、シリコーンオイルに由来する潤滑性
や平滑性といった特徴は出やすくなるが、反面そのアミ
ノ変性シリコーンオイルの粘度が高過ぎて取り扱いにく
く、水に対する乳化、分散性が悪くなる傾向にある。以
上のような理由からアミノ変性シリコーンの平均分子量
は５０００乃至１０００００の範囲であることが望まし
い。このアミノ変性シリコーンは水や乳化剤などが配合
されて水系エマルジョンや水溶液の状態で市販されてい
るのでそれらを用いるのが便利である。次に本発明でい
う処理剤の製法について説明する。該処理剤はエチレン
オキシドとプロピレンオキシドを主成分とする化合物
（A）とアミノ変性シリコーンを主成分とする油剤（B）
を含有する人工毛髪繊維用処理剤であり、（Ａ）（Ｂ）
両者の混合方法について本発明では何ら限定するもので
はないが、それぞれを混合し易いように水等で溶解、希
釈したのち混合することが好ましい。例えば、一般にエ
チレンオキシドプロピレンオキシドブロック共重合体は
フレーク状の固形物でありこれを４０℃程度の温湯で溶
解し、前記ブロック共重合体の水溶液を得る。この時の
水溶液の濃度は水溶液が扱いやすい粘度であれば特に限
定はされない。また溶解の際に水溶液の安定性を低下さ
せない限り他の薬剤、例えば界面活性剤、溶剤、充填
剤、油脂類、糊剤、ｐＨ調整剤等を添加することも可能
である。一方、油剤（Ｂ）は前述したように水溶液状の
ものが市販されており、それをそのまま使用してもよい
が、水溶液の安定性を低下させない限り、水や他の薬
剤、例えば界面活性剤、溶剤、充填剤、油脂類、糊剤、
ｐＨ調整剤等を添加して使用してもよい。このようにし
て化合物（Ａ）の水溶液と油剤（Ｂ）の水溶液を混合す
るには、公知の方法を用いることができるが、混合後の
処理剤の液安定性や利便性を考慮した場合、人工毛髪用
繊維を製造する時は、短時間で消費してしまうため問題
ないが、人工毛髪用繊維を加工時使用する時は、直前に
両水溶液を混合することが好ましい。On the other hand, the amino-modified silicone of the oil agent (B) containing the amino-modified silicone as a main component in the present invention refers to an organochlorosilane obtained by reacting a hydrocarbon chloride with a catalyst at a high temperature. In this process, a part of the methyl group is replaced with an aminoalkyl group in the course of the condensation polymerization. This amino-modified silicone is relatively easy to emulsify in silicone oil and is superior to other silicone oils in that it can obtain a stable solubilized product.
Because it can impart water repellency, waterproofness, smoothness, etc., in addition to improving processing properties such as openability (separability between fibers and accompanying combing) and antistatic properties, a natural tactile sensation , Appearance, good combability, moisturizing properties, and anti-fritz properties (Frits refers to tangling or frizzing caused by brushing of the headdress product or friction between the worn headdress product and clothes, etc.) In addition to satisfying the cosmetic properties, the head decoration product can be given remarkable flexibility unique to amino-modified silicone. It is considered that this flexibility is due to the strong orientation and film formation of silicone on the fibers due to the reaction between the hydroxyl groups, carboxyl groups, etc. of the artificial hair fibers and the amino groups in the silicone oil. In addition, the natural feel given to the headdress product by the reaction, appearance, good combability, cosmetic properties such as moisturizing and anti-fritz properties have washing durability, and when the headdress product gets wet with water, for example, shampoo etc. However, it is possible to retain the imparted characteristics. One of the factors that characterize this amino-modified silicone is the amine equivalent. When the amine equivalent is low, the reactivity between the amino-modified silicone and the fiber tends to be high, but not only characteristics such as lubricity and smoothness derived from silicone oil tend to be hard to appear,
In extreme cases, there is a possibility that safety and hygiene problems such as the occurrence of handwork during use of the treating agent due to the influence of the aminoalkyl group may occur. Conversely, when the amine equivalent is increased, the lubricating properties and smoothness of the silicone oil tend to become stronger, and while it is expected that the spreadability and the combability of the head decoration product can be improved, in extreme cases, the lubricity, Problems such as excessive deterioration of workability due to excessive emphasis on smoothness, and a feeling of dry and hard finish of the processed head decoration product may occur. In addition, since the ratio of the functional group is low, the reactivity between the treating agent and the fiber becomes poor depending on the type of the fiber constituting the head decoration product, and a problem may occur in the cleaning durability of the effect of the treating agent. For the above reasons, the amine equivalent is preferably in the range of 500 or more and less than 4000,
Amino-modified silicones with an amine equivalent in this range are particularly rich in reactivity with artificial hair fibers, yet have no problem in terms of safety and hygiene, and are effective in processing head ornament products and exhibiting excellent properties of head ornament products. It can be a part of the raw material of the agent. The average molecular weight of the amino-modified silicone is also one of the factors that express the characteristics of the amino-modified silicone, like the amine equivalent. If this average molecular weight is small, dispersibility and solubility are improved, but characteristics such as lubricity and smoothness derived from silicone oil tend to be difficult to appear,
In an extreme case, it may not be possible to expect improvement in workability such as spreadability and antistatic property and in combability of a head decoration product. Conversely, if the average molecular weight is high, characteristics such as lubricity and smoothness derived from the silicone oil are likely to appear, but on the other hand, the viscosity of the amino-modified silicone oil is too high to handle, and the emulsification and dispersibility in water deteriorate. There is a tendency. For the above reasons, the average molecular weight of the amino-modified silicone is preferably in the range of 5,000 to 100,000. Since this amino-modified silicone is commercially available in the form of an aqueous emulsion or an aqueous solution containing water and an emulsifier, it is convenient to use them. Next, a method for producing the treating agent according to the present invention will be described. The treating agent is a compound (A) containing ethylene oxide and propylene oxide as main components and an oil agent (B) containing amino-modified silicone as a main component.
And (A) and (B).
The method of mixing the two is not particularly limited in the present invention, but it is preferable that each is dissolved and diluted with water or the like and then mixed so that each can be easily mixed. For example, an ethylene oxide propylene oxide block copolymer is generally a flake-like solid, which is dissolved in hot water at about 40 ° C. to obtain an aqueous solution of the block copolymer. The concentration of the aqueous solution at this time is not particularly limited as long as the aqueous solution has a viscosity that is easy to handle. It is also possible to add other agents such as surfactants, solvents, fillers, oils and fats, sizing agents, pH adjusters and the like as long as the stability of the aqueous solution is not reduced during dissolution. On the other hand, the oil agent (B) is commercially available in the form of an aqueous solution as described above, and may be used as it is. However, as long as the stability of the aqueous solution is not reduced, water and other chemicals such as surfactants are used. , Solvents, fillers, fats and oils, sizing agents,
A pH adjuster or the like may be added for use. In order to mix the aqueous solution of the compound (A) and the aqueous solution of the oil agent (B) in this manner, a known method can be used. However, in consideration of the liquid stability and convenience of the mixed processing agent, There is no problem in producing the artificial hair fiber because it is consumed in a short time, but when the artificial hair fiber is used in processing, it is preferable to mix both aqueous solutions immediately before.
【００１３】更には両水溶液を混合する際にイオン交換
水を加える等して、処理剤重量に対する化合物（Ａ）の
固形成分と油剤（Ｂ）のシリコーン純分の合計重量の割
合つまり有効成分濃度が０．０１〜１０重量％になるよ
うに濃度調整しておくのがより好ましい。Further, when mixing the two aqueous solutions, the ratio of the total weight of the solid component of the compound (A) and the pure silicone of the oil agent (B) to the weight of the treating agent, that is, the concentration of the active ingredient, is added. Is more preferably adjusted so as to be 0.01 to 10% by weight.
【００１４】すなわち、後で詳細に述べるが、両水溶液
を別々に用意しておき、随時混合比率を変更できる状態
にしておくことで加工する頭飾製品の様々な要求特性に
対応することができる。また本発明でいう処理剤は通常
の保管状態で有れば経時安定性に問題があるわけではな
いが、やはり化合物（Ａ）と油剤（Ｂ）の両者を混合す
ることは、それぞれが単体で存在することに比べると安
定性が低下する可能性があるため、処理剤使用時の頭飾
製品の繊維部分への付着量に支障を来さない範囲で処理
剤の濃度を低く設定しておくことが望ましい。That is, as will be described in detail later, by preparing both aqueous solutions separately and keeping the mixing ratio at any time, it is possible to cope with various required characteristics of the head decoration product to be processed. Further, the treating agent according to the present invention does not necessarily have a problem in stability over time if it is in a normal storage state. However, mixing both of the compound (A) and the oil agent (B) can be considered as a single treatment. Since the stability may be lower than the presence of the treatment agent, the concentration of the treatment agent should be set low as long as the amount of adhesion to the fiber part of the head decoration product when using the treatment agent is not affected. Is desirable.
【００１５】次に化合物（Ａ）と油剤（Ｂ）とを混合す
る比率であるが、本発明では化合物（Ａ）と油剤（Ｂ）
の混合処理剤を付与した人工毛髪用繊維を熱セットした
時、アミノ変性シリコーンが熱により反応することによ
って、繊維表面に混合成分が強固な配向した皮膜を形成
するため、化合物（Ａ）の持つ処理剤の湿潤性や帯電防
止性に対する効果と、油剤（Ｂ）の持つ開繊性、櫛通り
性、柔軟性、フリッツ性に対する効果や洗浄耐久性が得
られると推定している。The mixing ratio of the compound (A) and the oil agent (B) is as follows. In the present invention, the compound (A) and the oil agent (B) are mixed.
When the artificial hair fiber to which the mixing treatment agent is applied is heat-set, the amino-modified silicone reacts by heat to form a strongly oriented film of the mixed component on the fiber surface. It is estimated that the effect on the wettability and antistatic property of the treatment agent, the effect on the fiber-opening property, combability, flexibility, and fritz properties of the oil agent (B) and the washing durability are obtained.
【００１６】それらの効果の洗浄耐久性とのバランスを
考慮した場合、処理剤中の化合物（Ａ）の固形成分と油
剤（B）のシリコーン純分の重量比が３０／７０〜９５
／５となるように混合するのが好ましく、更に好ましく
は４０／６０〜９０／１０となるように混合するのが良
い。In consideration of the balance between these effects and the washing durability, the weight ratio of the solid component of the compound (A) to the pure silicone of the oil agent (B) in the treating agent is 30/70 to 95.
/ 5 is preferably mixed, and more preferably 40/60 to 90/10.
【００１７】これらの処理剤に含有する化合物（Ａ）と
油剤（Ｂ）の混合比率を任意に変更することによって人
工毛髪繊維用処理剤として所望の特性にコントロールす
ることができるのが本発明の優れた点であり、この点を
有効に活用するためにも先に述べた様に、化合物（Ａ）
の水溶液と油剤（Ｂ）の水溶液は頭飾製品の加工に使用
する直前に混合することが望ましい。つまりあらかじめ
濃度調節した化合物（Ａ）の水溶液と油剤（Ｂ）の水溶
液を別々に準備しておき、付与したい特性に応じて水溶
液の比率を設定して随時混合するのが望ましい。According to the present invention, it is possible to control the desired properties as an artificial hair fiber treating agent by arbitrarily changing the mixing ratio of the compound (A) and the oil agent (B) contained in these treating agents. This is an excellent point. In order to make effective use of this point, as described above, the compound (A)
It is desirable that the aqueous solution of (A) and the aqueous solution of the oil agent (B) be mixed immediately before use in processing of a head decoration product. That is, it is desirable to separately prepare an aqueous solution of the compound (A) and an aqueous solution of the oil agent (B) whose concentration has been adjusted in advance, and to set the ratio of the aqueous solutions according to the properties to be imparted and mix them as needed.
【００１８】人工毛髪繊維用処理剤として所望の特性に
コントロールするための混合比率の設定は、化合物
（Ａ）と油剤（Ｂ）のそれぞれの特性から推測される
が、例えば、頭飾製品に、より湿潤感を付与することの
できる処理剤を製造するには、化合物（Ａ）の固形成分
と油剤（Ｂ）のシリコーン純分の合計に対して、化合物
（Ａ）の固形成分の比率がより高くなるように混合して
やればよいし、より櫛通りや開繊性、柔軟性、フリッツ
防止性等を付与することのできる処理剤を製造するに
は、化合物（Ａ）の固形成分と油剤（Ｂ）のシリコーン
純分の合計に対して油剤（Ｂ）のシリコーン純分の比率
が高くなるように混合してやればよい。またこの様に化
合物（Ａ）と油剤（Ｂ）を混合した後に、処理剤の安定
性を低下させない限り、他の薬剤、例えば界面活性剤、
溶剤、充填剤、油脂類、糊剤、ｐＨ調整剤等を添加して
も良い。The setting of the mixing ratio for controlling the desired properties as a treating agent for artificial hair fibers can be inferred from the respective properties of the compound (A) and the oil agent (B). In order to produce a treating agent capable of imparting a wet feeling, the ratio of the solid component of the compound (A) to the sum of the solid component of the compound (A) and the pure silicone of the oil agent (B) is higher. In order to produce a treating agent capable of imparting more combability, openability, flexibility, anti-fritz properties, etc., the solid component of the compound (A) and the oil agent (B) It is sufficient to mix the oil agent (B) so that the ratio of the silicone pure component to the total silicone pure component becomes high. Further, after mixing the compound (A) and the oil agent (B) in this way, as long as the stability of the treating agent is not reduced, other agents such as a surfactant,
Solvents, fillers, fats and oils, sizing agents, pH adjusters and the like may be added.
【００１９】次に本発明でいう処理剤の一般的な使用方
法を説明するが、本発明はこれら使用方法に何ら限定さ
れるものではない。Next, general methods of using the treating agent according to the present invention will be described, but the present invention is not limited to these methods.
【００２０】本発明でいう処理剤は、有効成分すなわち
処理剤中に含有する化合物（Ａ）の固形成分と油剤
（Ｂ）のシリコーン純分の合計重量が、処理される繊維
の重量に対して０．０２〜５重量％の範囲、好ましくは
０．１〜２．５重量％の範囲で付着するのが好ましい。
この付着量が０．０２％を下回った場合には処理剤の効
果を期待できず、開繊性や帯電防止性といった加工性の
向上や、頭飾製品の自然な触感、自然な外観、良好な櫛
通り、保湿性、フリッツ防止性といった良好な美容特性
やその洗浄耐久性に対する効果が得られない可能性があ
る。逆に付着量が５％を越えた場合には加工時に人工毛
髪用繊維がべたついて加工性を悪化させたり、加工後の
頭飾製品の触感や外観がべたつき感により不自然に仕上
がる可能性がある。また処理剤を繊維に付着する方法に
は特に限定はなく公知の方法を用いることができる。例
えば濃度調整した処理剤の水溶液中に人工毛髪用繊維を
金属ローラーを介して浸漬し、ニップローラーで所定の
付着量になるように脱液を行い、均熱乾燥機等で乾燥し
てから頭飾製品に加工する方法や、人工毛髪用繊維を頭
飾製品の途中段階である半製品まで加工し、その半製品
を処理剤の水溶液中に浸漬し、遠心脱水機等で所定の付
着率になるように脱液を行いその状態でカールセットを
行うといった方法や、カールセットを行う工程で濃度調
整した処理剤の水溶液を霧吹きによって半製品に付着せ
しめる方法などが挙げられる。また頭飾製品に付与した
処理剤の洗浄耐久性を更に向上させるために、処理後の
人工毛髪用繊維または頭飾製品をそれらが熱的ダメージ
を受けない温度の範囲内で加熱処理することも有効な方
法である。また本発明でいう処理剤は単独で使用するこ
とはもちろん、水や他の薬剤、例えば界面活性剤、油脂
類、溶剤、充填剤、糊剤、ｐＨ調整剤等と併用すること
も可能である。このように本発明の処理剤を付着してな
る人工毛髪用繊維により、開繊性や帯電防止性といった
加工特性が改善されることに加え、自然な触感、外観、
良好な櫛通り、保湿性、およびフリッツ防止性といった
美容特性に優れた頭飾製品を得ることができるのであ
る。また本発明でいう処理剤を用いて加工される頭飾製
品に限定はなく、例えばウィッグ、ツーペ、ヘアアクセ
サリーや人形用頭髪が挙げられるが、いずれの頭飾製品
の加工に対しても有効に作用し、また頭飾製品に良好で
洗浄耐久性のある美容特性を付与することができる。例
えば、ウィッグは他の頭飾製品に比べて様々な外観や触
感が要求される。The treating agent referred to in the present invention is such that the total weight of the active ingredient, ie, the solid component of the compound (A) and the pure silicone of the oil agent (B) contained in the treating agent is based on the weight of the fiber to be treated. It is preferred that it adhere in the range of 0.02 to 5% by weight, preferably in the range of 0.1 to 2.5% by weight.
If the amount is less than 0.02%, the effect of the treating agent cannot be expected, and the processability such as spreadability and antistatic property is improved, and the natural feel, natural appearance, There is a possibility that good cosmetic properties such as combing, moisturizing properties, and anti-fritz properties and effects on the washing durability may not be obtained. Conversely, if the amount exceeds 5%, the artificial hair fibers may become sticky at the time of processing, thereby deteriorating the workability, or the head decoration product after processing may have an unnatural finish due to the sticky feeling. . The method for attaching the treating agent to the fibers is not particularly limited, and a known method can be used. For example, an artificial hair fiber is immersed in an aqueous solution of a treatment agent whose concentration has been adjusted through a metal roller, and is then drained to a predetermined amount with a nip roller. A method of processing into a product, or processing artificial hair fiber into a semi-finished product, which is an intermediate stage of a head decoration product, immersing the semi-finished product in an aqueous solution of a treating agent, and using a centrifugal dehydrator or the like to obtain a predetermined adhesion rate And a method of performing curl setting in that state, or a method of attaching an aqueous solution of the treatment agent whose concentration has been adjusted in the curl setting step to the semi-finished product by spraying. In order to further improve the washing durability of the treatment agent applied to the head decoration product, it is also effective to heat-treat the treated artificial hair fibers or the head decoration product within a temperature range in which they are not thermally damaged. Is the way. In addition, the treating agent according to the present invention can be used alone, or can be used in combination with water and other chemicals such as surfactants, fats and oils, solvents, fillers, sizing agents, pH adjusters, and the like. . As described above, the artificial hair fiber having the treatment agent of the present invention attached thereto improves processing characteristics such as spreadability and antistatic property, and also has a natural feel and appearance.
It is possible to obtain a head decoration product excellent in cosmetic properties such as good combability, moisturizing property, and anti-fritz property. Further, there is no limitation on the head decoration products processed using the treatment agent according to the present invention, and examples thereof include wigs, coupe, hair accessories and hair for dolls, but they effectively act on the processing of any head decoration products. In addition, it is possible to impart good and wash-resistant cosmetic properties to the head decoration product. For example, wigs are required to have various appearances and touches compared to other headdress products.
【００２１】一般にウィッグといっても例えば触感や外
観がドライなものやウェットなものというように様々な
質感のものがあるが、処理剤中の化合物（Ａ）と油剤
（Ｂ）の混合比率や付着量を変更することでウィッグの
質感を容易に調節することができ、要求に応じた様々な
質感のウィッグを得ることができる。更にウィッグは他
の頭飾製品に比べて毛足が長いスタイルを要求されるこ
とが多いが、そのような場合においても処理剤中のアミ
ノ変性シリコーンが有効に働き、良好な櫛通りのウィッ
グを得ることができる。またツーペは他の頭飾製品に比
べてより自然な触感や外観が求められ、更に装着頻度が
高くその上頭皮から出る油分や汗が付着し易いために洗
浄する頻度が高くなりがちであるが、処理剤を用いるこ
とにより自然な触感と外観に洗浄耐久性のあるツーペを
得ることができる。またウィッグと同様に様々な質感が
求められるヘアアクセサリーの加工においてもウィッグ
と同様の理由から処理剤は有効に作用し、要求に応じた
様々な質感のヘアアクセサリーを得ることができる。ま
た人形用頭髪はその製品の性質上、必要以上に櫛を通さ
れたりシャンプー洗浄等水に漬けられる等乱暴に取り扱
われやすいが、処理剤を用いることによって櫛通り性を
含めた美容特性の洗浄耐久性が向上し、その商品性は大
幅に向上する。In general, wigs have various textures, such as those having a dry or wet feel and a wet appearance. However, the mixing ratio of the compound (A) and the oil agent (B) in the treating agent can be reduced. By changing the amount of adhesion, the texture of the wig can be easily adjusted, and wigs having various textures according to demand can be obtained. Furthermore, wigs are often required to have a style with longer hairs compared to other headdress products, but even in such a case, the amino-modified silicone in the treatment agent works effectively to obtain a good comb-like wig be able to. In addition, TUPE requires a more natural feel and appearance than other headdress products, and is more frequently worn, and tends to adhere to oil and sweat coming out of its upper scalp, so it tends to be washed more frequently, By using the treating agent, it is possible to obtain a two-piece having a natural feel and a cleaning durability with a natural appearance. Also, in the processing of hair accessories that require various textures like wigs, the treatment agent works effectively for the same reason as wigs, and hair accessories with various textures according to demand can be obtained. Also, due to the nature of the product, hair for dolls is easy to handle violently, such as being unnecessarily combed or immersed in water such as shampoo washing. Durability is improved, and its commercial value is greatly improved.
【００２２】[0022]
【実施例】以下に実施例を挙げて本発明を説明するが、
本発明はこれによって何ら限定されるものではない。ま
た本実施例及び比較例で用いた％表示は全て重量％を示
す。各実施例、比較例で用いた人工毛髪繊維用処理剤の
組成を下記の表１にまとめて示した。EXAMPLES The present invention will be described below with reference to examples.
The present invention is not limited by this. The percentages used in the examples and comparative examples all indicate% by weight. The compositions of the treating agents for artificial hair fibers used in each of the examples and comparative examples are shown in Table 1 below.
【００２３】[0023]
【表１】 また表、実施例、比較例中で用いた語句の意味は次の通
りである。ＰＯＥＯ水溶液とはフレーク状で市販されて
いるエチレンオキシドプロピレンオキシドブロック共重
合体（アデカプルロニックＬ−６２：旭電化製）を４０
℃の温湯により固形分濃度が２０％になるように溶解、
調製したものである。アミノ変性シリコーン水溶液とは
次の化学式（II）に示すアミノ変性シリコーンからなる
水溶液をイオン交換水にてシリコーン純分濃度２０％に
なるよう調製したものである。[Table 1] The meanings of the terms used in the tables, examples and comparative examples are as follows. The POEO aqueous solution refers to a commercially available flake-form ethylene oxide propylene oxide block copolymer (Adecapluronic L-62: manufactured by Asahi Denka).
Dissolve so that the solid content concentration becomes 20% with hot water at ℃.
It was prepared. The amino-modified silicone aqueous solution is prepared by preparing an aqueous solution of an amino-modified silicone represented by the following chemical formula (II) with ion-exchanged water so as to have a silicone concentration of 20%.
【００２４】[0024]
【化４】 （但し上式中、Ｒは−Ｃ3Ｈ6−ＮＨ−Ｃ2Ｈ4−ＮＨ2で
あり、アミン当量は２５００である。また平均分子量は
１５０００であり、またｍ及びｎはアミン当量と平均分
子量から割り出される数値である。） ４級アンモニウム塩水溶液とは次の化学式（III）に示
す４級アンモニウム塩からなる固形分１８％の水溶液で
ある。Embedded image (However in Ueshiki, R is -C 3 H 6 -NH-C 2 H 4 -NH 2, amine equivalent is 2500. The average molecular weight of 15000, and m and n are average amine equivalent weight The quaternary ammonium salt aqueous solution is an aqueous solution of a quaternary ammonium salt represented by the following chemical formula (III) and having a solid content of 18%.
【００２５】[0025]
【化５】 ラウリルアルコール硫酸エステル水溶液とは市販の水溶
液をイオン交換水にて２０％になるよう調整したもので
ある。ジメチルシリコーン分散液とは次の化学式（IV）
に示すジメチルシリコーンからなる市販の分散液をイオ
ン交換水にてシリコーン純分濃度２０％になるよう調製
したものである。Embedded image The aqueous solution of lauryl alcohol sulfate is obtained by adjusting a commercially available aqueous solution to 20% with ion-exchanged water. Dimethyl silicone dispersion is represented by the following chemical formula (IV)
A commercially available dispersion of dimethylsilicone shown in (1) was prepared with ion-exchanged water to a silicone concentration of 20%.
【００２６】[0026]
【化６】 （但し上式中、ｍは約２００であり、数平均分子量は概
ね１５０００である。） また各実施例、比較例における加工性や美容特性等の評
価は、頭飾製品加工の有識者５名が各評価項目について
各々５点満点（１点単位）の評価を行い（各評価項目２
５点満点）、その合計点が９点以下を×、１０〜１４点
を△、１５〜１９点を○、２０点以上を◎とし表２にま
とめて示した。また洗浄耐久性とは頭飾製品を市販のリ
ンス等入ってない通常のシャンプー（サラ：鐘紡製）を
加えて５％にした４０℃の温湯ですすぎ洗いし自然乾燥
する工程を３サイクル行ったときに、洗浄前の特性をい
かに維持しているかの評価であり、また処理剤付着量と
は頭飾製品に処理剤の有効成分が付着している量を表
し、処理剤を付着していない頭飾製品の重量に対しての
加工後及び洗浄後の頭飾製品重量の増加分の百分率であ
る。なお各評価項目に１つでも×のある水準は総合判定
にて不合格とした。Embedded image (However, in the above formula, m is about 200, and the number average molecular weight is about 15000.) In each of the examples and comparative examples, the evaluation of processability and beauty characteristics was performed by five experts in head decoration product processing. Each of the evaluation items was evaluated on a scale of 1 to 5 (each evaluation item 2).
Table 5 shows the total score of 9 points or less as x, 10 to 14 points as Δ, 15 to 19 points as 、, and 20 or more as ◎. Washing durability refers to a process in which a headwear product is rinsed with warm water of 40 ° C. to 5% by adding a normal shampoo (manufactured by Kanebo) that does not contain a commercially available rinse, and then naturally dried, and subjected to three cycles. In addition, it is an evaluation of how to maintain the properties before cleaning, and the treatment agent adhesion amount indicates the amount of the active ingredient of the treatment agent adhering to the head decoration product, and the head decoration product without the treatment agent attached Is the percentage increase in headdress product weight after processing and after washing with respect to the weight of the product. In addition, the level with at least one x in each evaluation item was judged as unacceptable in the comprehensive judgment.
【００２７】[0027]
【表２】 （実施例１）ＰＯＥＯ水溶液を２．５部、アミノ変性シ
リコーン水溶液を２．５部、イオン交換水９５部の重量
比で撹拌混合し、全重量に対するエチレンオキシドプロ
ピレンオキシドブロック共重合体の固形成分とアミノ変
性シリコーンのシリコーン純分の合計重量の割合、つま
り有効成分濃度が１．０％となる処理剤（１）を得た。
次にアクリロニトリル４８．５部、塩化ビニル５１．０
部、スチレンスルホン酸ソーダ０．５部からなるアクリ
ロニトリル系共重合体から得られた樹脂をアセトンによ
って溶解して固形分濃度が２９％の紡糸原液を得た。そ
の紡糸原液を紡糸用口金からアセトン水溶液中に押し出
し、水洗、オイリング、乾燥、延伸、熱処理を行うとい
う公知の湿式紡糸法により単繊維繊度５０デニールの頭
飾用、モダクリル合成繊維を得た。この頭飾用モダクリ
ル合成繊維を婦人用ウィッグに加工する際にカールセッ
ト工程において、前記の処理剤（１）を使用した。[Table 2] (Example 1) 2.5 parts of an aqueous POEO solution, 2.5 parts of an amino-modified silicone aqueous solution and 95 parts of ion-exchanged water were stirred and mixed at a weight ratio of solid components of an ethylene oxide propylene oxide block copolymer to the total weight. A treating agent (1) having a ratio of the total weight of the silicone pure content of the amino-modified silicone, that is, the active ingredient concentration of 1.0% was obtained.
Next, 48.5 parts of acrylonitrile, 51.0 parts of vinyl chloride
A resin obtained from an acrylonitrile copolymer composed of 0.5 parts by weight of sodium styrene sulfonate was dissolved with acetone to obtain a spinning dope having a solid content of 29%. The spinning stock solution was extruded from a spinneret into an aqueous acetone solution, and a modacrylic synthetic fiber for head decoration having a single fiber fineness of 50 denier was obtained by a known wet spinning method in which washing, oiling, drying, stretching, and heat treatment were performed. The above-mentioned treating agent (1) was used in the curl setting step when the modacrylic synthetic fiber for head decoration was processed into a wig for women.
【００２８】カールセット工程以外は、婦人用ウィッグ
の一般的な公知の製法を用いた。本実施例では、ウェフ
トを不織布と共にアルミパイプに巻き付ける際、頭飾製
品加工用に処理剤（１）を霧吹きを用いて繊維重量に対
して約３０％になる量をウェフトに吹き付け、不織布と
共にアルミパイプに巻き付けて不織布の先端を固定した
状態で、１００℃にコントロールされた熱風乾燥機に６
０分間入れカールセット処理を行った。このカールセッ
ト工程において不織布と共にアルミパイプに巻き付ける
際のウェフトの整条性は良好であり、カールセット処理
後アルミパイプからウェフトを取り外す際もウェフトの
開繊性は良好で絡まる等することなくカールセット工程
の作業性や仕上がりは非常に良好であった。またウィッ
グ加工の最終工程であるスタイリング工程においても頭
飾製品の櫛通り、ブラッシングはスムーズであった。か
くして加工された婦人用ウィッグは処理剤（１）で処理
していない婦人用ウィッグと比較して０．２４％の重量
増があり、この重量増は婦人用ウィッグに付着した処理
剤（１）の有効成分と考えられる。処理剤（１）で処理
を行った婦人用ウィッグは櫛通りが優れていた上、ブラ
ッシング等による静電気やフリッツの発生が少なく、人
毛さながらの外観、適度な湿潤性や柔軟性のある触感を
有していた。またこの婦人用ウィッグを市販シャンプー
を添加した４０℃の温湯ですすぎ洗いし自然乾燥すると
いう工程を３サイクル実施した後の婦人用ウィッグ重量
は処理剤（１）で処理していない婦人用ウィッグと比較
して０．２１％の重量増となっていた。この重量増分は
洗浄後に頭飾製品に残留している処理剤（１）の有効成
分と考えられる。またその洗浄後の婦人用ウィッグの品
質は加工直後の櫛通り性、フリッツ防止性、帯電防止
性、触感、外観を保持していた。Except for the curl setting step, a general known manufacturing method of a women's wig was used. In this embodiment, when the weft is wound around an aluminum pipe together with the nonwoven fabric, the treatment agent (1) is sprayed onto the weft using a spray to spray the treatment agent (1) in an amount of about 30% with respect to the fiber weight. Wrapped in a hot air dryer controlled at 100 ° C.
Curl set treatment was performed for 0 minutes. In the curl setting process, the weft is well-aligned when it is wound around an aluminum pipe together with the nonwoven fabric, and when the weft is removed from the aluminum pipe after the curl setting process, the opening of the weft is good and the curl set without tangling The workability and finish of the process were very good. Also, in the styling step, which is the final step of the wig processing, the brushing of the head decoration product was smooth and the brushing was smooth. The thus-processed women's wig has a weight increase of 0.24% compared to the women's wig not treated with the treatment agent (1), and this weight increase is due to the treatment agent (1) attached to the women's wig. Is considered an active ingredient. The women's wig treated with the treatment agent (1) has excellent combability, is free from static electricity and frits due to brushing, etc., has the appearance of human hair, moderate wettability and flexible touch. Had. After three cycles of rinsing this woman's wig with hot water at 40 ° C to which commercial shampoo was added and drying it naturally, the weight of the woman's wig was equal to that of the woman's wig not treated with the treatment agent (1). The weight increased by 0.21% in comparison. This weight increase is considered to be an active ingredient of the treating agent (1) remaining in the headdress product after washing. In addition, the quality of the women's wig after washing retained the combability, fritz prevention, antistatic properties, touch, and appearance immediately after processing.
【００２９】（実施例２）実施例１同様の方法で処理剤
（１）を得た。またそれとは別にＰＯＥＯ水溶液を６．
０部、アミノ変性シリコーン水溶液を１．５部、イオン
交換水を９２．５部の重量比で撹拌混合し、処理剤全重
量に対するエチレンオキシドプロピレンオキシドブロッ
ク共重合体の固形成分とアミノ変性シリコーンのシリコ
ーン純分の合計重量の割合、つまり有効成分濃度が１．
５％となる処理剤（２）を得た。本実施例においても頭
飾繊維には実施例１で用いた単繊維繊度５０デニールの
モダクリル合成繊維を用い、これをヘアアクセサリーの
一種であるウィービングでウェットルックと呼ばれる湿
潤感の豊富なアイテムに加工する際に、カールセット工
程において、処理剤（１）を、またスタイリング工程に
おいては処理剤（２）を使用した。カールセット工程及
びスタイリング工程において本発明の処理剤を用いる以
外はウェットルックのウィービングの一般的な公知の製
法を用いた。本実施例では、ウェフトを不織布と共にア
ルミパイプに巻き付ける際、処理剤（１）を霧吹きを用
いて繊維重量に対して約３０％になる量をウェフトに吹
き付け、不織布と共にアルミパイプに巻き付けて不織布
の先端を固定した状態で、１００℃にコントロールされ
た熱風乾燥機に６０分間入れカールセットを行った。こ
のカールの付与されたウェフトを処理剤（２）を満たし
た処理槽に５分間浸した後取り出しブラシでスタイリン
グを行い、室温で２４時間の吊し乾燥を行った。かくし
て加工されたウィービングは処理剤で処理していないウ
ィービングと比較して０．９７％の重量増があり、この
重量増はウィービングに付着した処理剤（１）及び
（２）の有効成分と考えられる。このウィービングへの
加工中のカールセット工程におけるウェフトの整条性は
良好であり、カールセット後アルミパイプからのウェフ
ト取り外しもウェフトが絡まる等することなく非常に作
業性良好であった。またウィービング加工の最終工程で
あるスタイリング工程においても櫛通り、ブラッシング
はスムーズであった。かくして加工されたウィービング
は櫛通りが優れていた上、ブラッシング等による静電気
やフリッツの発生が少なく、人毛を整髪用スタイリング
ムースで処理したような湿潤性のある外観と触感、つま
りウェットルックを有していた。またこのウィービング
を市販のシャンプーを添加した４０℃の温湯ですすぎ洗
いし自然乾燥するという工程を３サイクル実施したとこ
ろ、そのウィービングの重量は処理剤で処理していない
ウィービング重量に対して０．８６%の重量増があり、
この重量増分は洗浄後に頭飾製品に残留している処理剤
（１）及び（２）の有効成分と考えられる。洗浄後のウ
ィービングの品質は加工直後の湿潤感はやや失われてい
たが、ウィービングとして必要な外観、櫛通り性、フリ
ッツ防止性、帯電防止性等の美容特性は良好な状態を保
持していた。Example 2 A treating agent (1) was obtained in the same manner as in Example 1. Separately, a POEO aqueous solution is used.
0 parts, 1.5 parts of an amino-modified silicone aqueous solution and 92.5 parts of ion-exchanged water are stirred and mixed, and the solid component of the ethylene oxide propylene oxide block copolymer and the silicone of the amino-modified silicone with respect to the total weight of the treating agent. The ratio of the total weight of the pure components, that is, the active ingredient concentration is 1.
5% of the treating agent (2) was obtained. Also in this embodiment, the head decoration fiber is a modacrylic synthetic fiber having a single fiber fineness of 50 denier used in Example 1 and processed into a wet-rich item called a wet look by weaving, which is a kind of hair accessory. At this time, the treating agent (1) was used in the curl setting step, and the treating agent (2) was used in the styling step. Except for using the treating agent of the present invention in the curl setting step and the styling step, a general known method of weaving of wet look was used. In this embodiment, when the weft is wound around the aluminum pipe together with the nonwoven fabric, the treating agent (1) is sprayed onto the weft in an amount of about 30% with respect to the fiber weight using a mist sprayer. While the tip was fixed, it was placed in a hot air dryer controlled at 100 ° C. for 60 minutes to perform curl setting. This curled waft was immersed in a treatment tank filled with the treatment agent (2) for 5 minutes, taken out, styled with a brush, and suspended and dried at room temperature for 24 hours. The weaving thus processed has a weight increase of 0.97% as compared to the weaving not treated with the treating agent, and this weight increase is considered to be an active ingredient of the treating agents (1) and (2) attached to the weaving. Can be The alignment property of the weft in the curl setting step during processing into the weaving was good, and the workability was very good without removing the weft from the aluminum pipe after curl setting without the weft getting tangled. In the styling step, which is the final step of the weaving process, the brushing was smooth as well as the comb. The weaving processed in this way has excellent combability, is free from static electricity and frits due to brushing, etc., and has a wet appearance and touch, that is, a wet look as if human hair was treated with a styling mousse for hairdressing. Was. When the weaving was rinsed with 40 ° C. hot water to which a commercially available shampoo was added and air-dried three times, the weight of the weaving was 0.86% of the weight of the weaving not treated with the treating agent. % Increase in weight,
This weight increase is considered to be an active ingredient of the treating agents (1) and (2) remaining in the headdress product after washing. The quality of the weaving after washing was slightly lost in the wet feeling immediately after processing, but the cosmetic properties required for weaving, such as appearance, combability, anti-fritz properties, and antistatic properties, were in good condition. .
【００３０】（実施例３）ＰＯＥＯ水溶液を１．５部、
アミノ変性シリコーン水溶液を１．５部、イオン交換水
を９７部の重量比で撹拌混合し、全重量に対するエチレ
ンオキシドプロピレンオキシドブロック共重合体の固形
成分とアミノ変性シリコーンのシリコーン純分の合計重
量の割合、つまり有効成分濃度が０．６％となる処理剤
（３）を得た。次に実施例１と同様の方法で単繊維繊度
４２デニールの頭飾用モダクリル合成繊維を得、それを
処理剤（３）を用いて紳士用ツーペに加工した。紳士用
ツーぺの加工方法は公知の手植え植毛法を用いた。この
加工においてカールセット工程における繊維束の整条性
は良好であり、カールセット後にアルミパイプから繊維
束を取り外す際も繊維束が絡まる等することなく非常に
作業性良好であった。また繊維束を植毛する際の繊維の
滑り感や植毛部の締まり具合も良好であり、ツーぺの加
工の最終工程であるスタイリング工程においても櫛通
り、ブラッシングはスムーズであった。かくして加工さ
れた紳士用ツーぺは処理剤で処理していない紳士用ツー
ぺと比較して０．１６％の重量増があり、この重量増は
紳士用ツーぺに付着した処理剤（３）の有効成分と考え
られる。処理剤（３）で処理を行った紳士用ツーぺは櫛
通りが優れていた上、ブラッシング等による静電気やフ
リッツの発生が少なく、人毛さながらの外観、適度な湿
潤性のある触感を有していた。この紳士用ツーぺを市販
のシャンプーを添加した４０℃の温湯ですすぎ洗いし自
然乾燥するという工程を３サイクル実施したところ、こ
の紳士用ツーぺの重量は処理剤で処理をしていない紳士
用ツーぺの重量に対して０．１２％の重量増があり、こ
の重量増分は洗浄後に頭飾製品に残留している処理剤
（３）の有効成分と考えられる。その洗浄後の紳士用ツ
ーぺの品質は加工直後に比べると触感はやや硬くなった
が、櫛通り性は良好で、頭飾製品としては十分に使用に
耐えうるだけの品質は維持していた。Example 3 1.5 parts of an aqueous POEO solution
Stir and mix 1.5 parts of the amino-modified silicone aqueous solution and 97 parts of ion-exchanged water at the weight ratio, and the ratio of the total weight of the solid component of the ethylene oxide propylene oxide block copolymer and the silicone pure of the amino-modified silicone to the total weight. That is, a treating agent (3) having an active ingredient concentration of 0.6% was obtained. Next, a modacrylic synthetic fiber for head decoration having a monofilament fineness of 42 denier was obtained in the same manner as in Example 1, and was processed into a gentleman's tupe using the treating agent (3). As a processing method of the men's tool, a known hand-planting method was used. In this processing, the fiber bundles had good arranging properties in the curl setting step, and even when the fiber bundles were removed from the aluminum pipe after curl setting, the workability was very good without the fiber bundles becoming entangled. In addition, the feeling of slippage of the fibers and the tightness of the flocked portions at the time of implantation of the fiber bundle were good, and the brushing was smooth even in the styling step, which is the final step of the two-step processing. The gentleman's tool thus processed has a 0.16% weight increase compared to the gentleman's tool not treated with the treating agent, and this weight increase is due to the treating agent attached to the gentleman's tool (3). Is considered an active ingredient. The gentleman's tool treated with the treatment agent (3) has excellent combability, less occurrence of static electricity and fritz due to brushing, etc., and has the appearance of human hair and a moderate wettability. I was The cycle of rinsing this gentleman's tool with hot water at 40 ° C with commercial shampoo and drying naturally was carried out for 3 cycles. The weight of this gentleman tool was untreated for the gentleman who had not been treated with a treating agent. There is a 0.12% weight increase relative to the weight of the two-piece, which is considered to be the active ingredient of the treating agent (3) remaining in the headdress product after washing. After washing, the quality of the men's tool was slightly harder than immediately after processing, but the combability was good, and it was maintained at a quality enough to withstand use as a head decoration product.
【００３１】（実施例４）ＰＯＥＯ水溶液を３．５部、
アミノ変性シリコーン水溶液を１．５部、イオン交換水
を９５部の重量比で撹拌混合し、全重量に対するエチレ
ンオキシドプロピレンオキシドブロック共重合体の固形
成分とアミノ変性シリコーンのシリコーン純分の合計重
量の割合、つまり有効成分濃度が１．０％となる処理剤
（４）を得た。最初に実施例１と同様の方法の湿式紡糸
法により単繊維繊度２０デニールのモダクリル合成繊維
を得、次にそれを処理剤（４）の中に金属ローラーを介
して浸漬し、更にゴム製のニップローラーを用いて繊維
重量に対して４０％の処理剤（４）を付着させた後、１
２０℃にコントロールされた熱風乾燥機において乾燥を
行った。こうして得られた人形用頭髪は処理剤で処理し
ていない人形用頭髪の重量に対して０．３６％の重量増
があり、この重量増は人形用頭髪に付着した処理剤
（４）の有効成分と考えられる。この処理剤（４）で処
理した人形用頭髪はドーリーミシンによる植毛工程にお
いて開繊性、植毛性等良好な加工性を示し、その繊維は
櫛通り性、触感、外観、帯電防止性、フリッツ防止性に
も優れていた。またこの人形用頭髪を４０℃の温湯です
すぎ洗いし自然乾燥するという工程を３サイクル実施し
た後の人形用頭髪の重量は処理剤で処理していない人形
用頭髪と比較して０．２７％の重量増となっていた。こ
の重量増分は洗浄後に人形用頭髪に残留している処理剤
（４）の有効成分と考えられる。またその洗浄後の人形
用頭髪の品質は加工直後の良好な櫛通り性、フリッツ防
止性、帯電防止性、自然な外観、触感を保持していた。Example 4 3.5 parts of POEO aqueous solution
1.5 parts of an amino-modified silicone aqueous solution and 95 parts of ion-exchanged water were stirred and mixed, and the ratio of the total weight of the solid component of the ethylene oxide propylene oxide block copolymer and the pure silicone of the amino-modified silicone to the total weight. That is, a treating agent (4) having an active ingredient concentration of 1.0% was obtained. First, a modacrylic synthetic fiber having a single fiber fineness of 20 denier was obtained by a wet spinning method in the same manner as in Example 1, and then immersed in a treating agent (4) through a metal roller. After using a nip roller to attach 40% of the treating agent (4) to the fiber weight,
Drying was performed in a hot air dryer controlled at 20 ° C. The doll hair thus obtained has a weight increase of 0.36% with respect to the weight of the doll hair not treated with the treatment agent, and this weight increase is due to the effective use of the treatment agent (4) attached to the doll hair. It is considered an ingredient. The hair for dolls treated with this treating agent (4) shows good workability such as spreadability and flocking properties in the flocking process with a dolly sewing machine, and the fibers have combability, tactile sensation, appearance, antistatic properties, and fritz prevention. It was also excellent. The weight of the doll hair after rinsing the doll hair with hot water of 40 ° C. and naturally drying it for three cycles is 0.27% of that of the doll hair not treated with the treating agent. Had increased in weight. This weight increase is considered to be an active ingredient of the treating agent (4) remaining on the doll's hair after washing. In addition, the quality of the doll's hair after washing had good combability, fritz prevention, antistatic properties, natural appearance and tactile sensation immediately after processing.
【００３２】（比較例１）５部のＰＯＥＯ水溶液を重量
比９５部のイオン交換水で希釈し、全重量に対するエチ
レンオキシドプロピレンオキシドブロック共重合体の固
形成分の割合、つまり有効成分濃度が１．０％となる処
理剤（５）を得た。次に実施例１同様の方法で単繊維繊
度５０デニールの頭飾用モダクリル合成繊維を得、この
頭飾用モダクリル合成繊維を婦人用ウィッグに加工する
際にカールセット工程において、処理剤（５）を使用し
た。カールセット工程以外は、婦人用ウィッグの一般的
な公知の製法を用いた。本比較例では、ウェフトに加工
した繊維を不織布と共にアルミパイプに巻き付ける際、
処理剤（５）を霧吹きを用いて繊維重量に対して約３０
％になる量をウェフトに吹き付け、不織布と共にアルミ
パイプに巻き付けて不織布の先端を固定した状態で、１
００℃にコントロールされた熱風乾燥機に６０分間入れ
カールセットを行った。このカールセット工程において
ウェフトの整条性は良好であったが、カールセット後ア
ルミパイプからのウェフト取り外しの際に希にウェフト
の毛先が絡まるという問題が発生し、またウィッグ加工
の最終工程であるスタイリング工程においては櫛通りに
やや問題があった。かくして加工された婦人用ウィッグ
は、処理剤で処理していない婦人用ウィッグと比較して
０．２５％の重量増があり、この重量増は婦人用ウィッ
グに付着した処理剤（５）の有効成分と考えられる。こ
の婦人用ウィッグはややベタツキ感のある触感で櫛通り
も重く、またこの婦人用ウィッグを市販のシャンプーを
添加した４０℃の温湯ですすぎ洗いし自然乾燥するとい
う工程を３サイクル実施したところ、その婦人用ウィッ
グの重量は処理剤で処理していない婦人用ウィッグの重
量と比較して０．０７％の重量増があった。この重量増
分は洗浄後に頭飾製品に残留している処理剤（５）の有
効成分と考えられる。また洗浄後の婦人用ウィッグの品
質は櫛通りが悪く、ブラッシング等により静電気やフリ
ッツが発生するという問題を有していただけでなく、触
感は硬くガサついており、頭飾製品としては商品価値は
低いものなった。(Comparative Example 1) 5 parts of a POEO aqueous solution was diluted with 95 parts by weight of ion-exchanged water, and the ratio of the solid component of the ethylene oxide propylene oxide block copolymer to the total weight, that is, the active ingredient concentration was 1.0%. % Of the treating agent (5). Next, in the same manner as in Example 1, a modacrylic synthetic fiber for head decoration having a single fiber fineness of 50 denier was obtained, and the processing agent (5) was used in the curl setting step when the synthetic fiber for decorative head was processed into a wig for women. did. Except for the curl setting step, a general known manufacturing method of a women's wig was used. In this comparative example, when winding the fiber processed into the weft around the aluminum pipe together with the nonwoven fabric,
The treating agent (5) is sprayed with a spray to about 30 wt.
%, Sprayed onto the weft, wrapped around an aluminum pipe with the non-woven fabric, and fixed the tip of the non-woven fabric.
The sheet was placed in a hot-air dryer controlled at 00 ° C. for 60 minutes to perform curl setting. In this curl setting process, the alignment property of the weft was good, but when the weft was removed from the aluminum pipe after curl setting, the problem that the tip of the weft rarely became entangled occurred, and in the final process of wig processing In one styling step, there was a slight problem with combing. The thus-processed women's wig has a weight increase of 0.25% compared to the women's wig not treated with the treatment agent, and this weight increase is due to the effectiveness of the treatment agent (5) attached to the women's wig. It is considered an ingredient. The women's wig was slightly sticky and had a heavy feel through the comb, and the women's wig was rinsed with 40 ° C hot water to which a commercially available shampoo was added, followed by natural drying. The weight of the women's wig increased by 0.07% compared to the weight of the women's wig not treated with the treatment agent. This weight increase is considered to be an active ingredient of the treating agent (5) remaining in the headdress product after washing. In addition, the quality of women's wigs after cleaning is poor in combability, not only has the problem of generating static electricity and frits due to brushing, etc., but also has a hard touch and a rough feel, which is low commercial value as a head decoration product became.
【００３３】（比較例２）５部のアミノ変性シリコーン
水溶液を重量比９５部イオン交換水で希釈し、全重量に
対するアミノ変性シリコーンのシリコーン純分の割合、
つまり有効成分濃度が１．０％となる処理剤（６）を得
た。次に実施例１同様の方法で単繊維繊度５０デニール
の頭飾用モダクリル合成繊維を得、この頭飾用モダクリ
ル合成繊維を婦人用ウィッグに加工する際にカールセッ
ト工程において、処理剤（６）を使用した。カールセッ
ト工程以外は、婦人用ウィッグの一般的な公知の製法を
用いた。本比較例ではウェフトを不織布と共にアルミパ
イプに巻き付ける際、処理剤（６）を霧吹きを用いて繊
維重量に対して約３０％になる量をウェフトに吹き付
け、不織布と共にアルミパイプに巻き付けて不織布の先
端を固定した状態で１００℃にコントロールされた熱風
乾燥機に６０分間入れカールセットを行った。このカー
ルセット工程においてウェフトの整条性は良好でカール
セット後アルミパイプからのウェフト取り外しもウェフ
トが絡まる等することなく作業性は良好であったが、カ
ールセット後のウェフトをキャップに縫いつけるポステ
ィングの工程においてウェフトの滑りすぎる触感が作業
性や仕上がりを阻害するという問題が発生した。またウ
ィッグ加工の最終工程であるスタイリング工程において
も櫛通り、ブラシの通りは良好であったが、ブローを行
う際に頭飾製品が滑りすぎてブラシに絡みにくく、作業
性は良好とは言えなかった。かくして加工された婦人用
ウィッグは処理剤で処理していない婦人用ウィッグと比
較して０．２７％の重量増があり、この重量増は婦人用
ウィッグに付着した処理剤（６）の有効成分と考えられ
る。この処理剤（６）で処理を行った婦人用ウィッグは
櫛通りには優れていたが、触感はドライタッチで滑りす
ぎて頭飾製品としては不自然であり、外観も頭飾製品と
しては強すぎる光沢を有していた。またこの婦人用ウィ
ッグを市販のシャンプーを添加した４０℃の温湯ですす
ぎ洗いし自然乾燥するという工程を３サイクル実施した
ところ、この婦人用ウィッグの重量は処理剤で処理して
いない婦人用ウィッグと比較して０．２４％の重量増が
あり、この重量増分は洗浄後に頭飾製品に残留している
処理剤（６）の有効成分と考えられる。また洗浄後の婦
人用ウィッグの品質は、良好な櫛通りには変化はないも
のの触感は更にドライで硬くなり、光沢も更に強くなっ
た。(Comparative Example 2) 5 parts of an amino-modified silicone aqueous solution was diluted with 95 parts by weight of ion-exchanged water, and the ratio of the amino-modified silicone to the total weight of the silicone was calculated as follows:
That is, a treating agent (6) having an active ingredient concentration of 1.0% was obtained. Next, a modacrylic synthetic fiber for head decoration having a monofilament fineness of 50 denier was obtained in the same manner as in Example 1, and the processing agent (6) was used in the curl setting step when the synthetic fiber for modulating head decoration was processed into a wig for women. did. Except for the curl setting step, a general known manufacturing method of a women's wig was used. In this comparative example, when the weft is wound around an aluminum pipe together with the nonwoven fabric, the treating agent (6) is sprayed onto the weft using a spray to an amount of about 30% with respect to the fiber weight, and wound around the aluminum pipe together with the nonwoven fabric to form a tip of the nonwoven fabric. In a state where was fixed, the mixture was placed in a hot air drier controlled at 100 ° C. for 60 minutes to perform curl setting. In this curl setting process, the workability of the weft was good without removing the weft from the aluminum pipe after the curl setting, and the workability was good without entanglement of the weft. In the process, there was a problem that the touch feeling of the weft being too slippered hindered workability and finish. In the styling step, which is the final step of the wig processing, the brush and the brush were good in the styling step, but the head decoration product slipped too much when blowing, and it was difficult to get tangled with the brush, and the workability was not good. . The thus-processed women's wig has a weight increase of 0.27% as compared to the women's wig not treated with the treatment agent, and this weight increase is due to the active ingredient of the treatment agent (6) attached to the women's wig. it is conceivable that. The women's wig treated with this treating agent (6) was excellent for combing, but the touch was too slippery due to dry touch and was unnatural as a headdress product, and the appearance was too strong for a headdress product. Had. In addition, when this woman's wig was rinsed with 40 ° C. hot water to which a commercially available shampoo was added and air-dried three cycles, the weight of the woman's wig was equal to that of a woman's wig that had not been treated with a treating agent. There is a weight increase of 0.24% in comparison, which is considered to be the active ingredient of the treatment agent (6) remaining in the headdress product after washing. In addition, the quality of the women's wig after washing did not change for good combing, but the touch was further dried and hardened, and the gloss became stronger.
【００３４】（比較例３）５．６部の４級アンモニウム
塩水溶液を重量比９４．４部のイオン交換水で希釈調整
し、全重量に対する４級アンモニウム塩の固形成分重量
の割合、つまり有効成分濃度が１．０％となる処理剤
（７）を得た。次に実施例１同様の方法で単繊維繊度５
０デニールの頭飾用モダクリル合成繊維を得、この頭飾
用モダクリル合成繊維を婦人用ウィッグに加工する際に
カールセット工程において処理剤（７）を使用した。カ
ールセット工程以外は、婦人用ウィッグの一般的な公知
の製法を用いた。本比較例ではウェフトを不織布と共に
アルミパイプに巻き付ける際、処理剤（７）を霧吹きを
用いて繊維重量に対して約３０％になる量をウェフトに
吹き付け、不織布と共にアルミパイプに巻き付けて不織
布の先端を固定した状態で１００℃にコントロールされ
た熱風乾燥機に６０分間入れカールセットを行った。こ
のカールセット工程においてウェフトの整条性は良好で
あったものの、カールセット後アルミパイプからのウェ
フト取り外しの際に希にウェフトの先端が絡まるという
問題が発生した。またウィッグ加工の最終工程であるス
タイリング工程においても、静電気やフリッツの発生は
少なかったが、櫛通り性に若干の問題が見られた。かく
して加工された婦人用ウィッグは処理剤で処理していな
い婦人用ウィッグと比較して０．２４％の重量増があ
り、この重量増は婦人用ウィッグに付着した処理剤
（７）の有効成分と考えられる。この処理剤（７）で処
理を行った婦人用ウィッグは触感、帯電防止性には優れ
ていたが、櫛通りは良好とは言えず、またこの婦人用ウ
ィッグを市販のシャンプーを添加した４０℃の温湯です
すぎ洗いし自然乾燥するという工程を３サイクル実施し
たところ、その婦人用ウィッグの重量は処理剤で処理し
ていない婦人用ウィッグの重量と比較して０．０３％の
重量増があった。この重量増分は洗浄後に頭飾製品に残
留している処理剤（７）の有効成分と考えられる。この
洗浄後の婦人用ウィッグの品質は、洗浄前と比較して櫛
通りは更に悪化し、静電気やフリッツの発生も多く、婦
人用ウィッグとして使用に耐えうる品質を有していなか
った。Comparative Example 3 5.6 parts of an aqueous quaternary ammonium salt solution was diluted with 94.4 parts by weight of ion-exchanged water to adjust the ratio of the solid component weight of the quaternary ammonium salt to the total weight, ie, the effective amount. A treating agent (7) having a component concentration of 1.0% was obtained. Next, a single fiber fineness of 5 was obtained in the same manner as in Example 1.
A 0 denier modacrylic synthetic fiber for head decoration was obtained, and the processing agent (7) was used in the curl setting step when processing this synthetic fiber for modal acrylic head into a wig for women. Except for the curl setting step, a general known manufacturing method of a women's wig was used. In this comparative example, when the weft is wound around an aluminum pipe together with the nonwoven fabric, the treatment agent (7) is sprayed onto the weft using a spray to an amount of about 30% of the fiber weight, and wound around the aluminum pipe together with the nonwoven fabric to form a tip of the nonwoven fabric. In a state where was fixed, the mixture was placed in a hot air drier controlled at 100 ° C. for 60 minutes to perform curl setting. In this curl setting step, the alignment property of the weft was good, but there was a problem that the tip of the weft rarely became entangled when the weft was removed from the aluminum pipe after curl setting. Also, in the styling step, which is the final step of the wig processing, the generation of static electricity and frits was small, but there were some problems in combability. The thus-processed women's wig has a weight increase of 0.24% as compared to the women's wig not treated with the treatment agent, and this weight increase is due to the active ingredient of the treatment agent (7) attached to the women's wig. it is conceivable that. The women's wig treated with this treating agent (7) was excellent in tactile sensation and antistatic properties, but not good in combability, and the women's wig was added to a commercial shampoo at 40 ° C. After three cycles of rinsing with hot water and drying naturally, the weight of the women's wig increased by 0.03% compared to the weight of the women's wig not treated with the treating agent. Was. This weight increase is considered to be an active ingredient of the treating agent (7) remaining in the headdress product after washing. The quality of the women's wig after the washing was worse in combing than before the washing, and there were many occurrences of static electricity and frits, and did not have a quality that could be used as a women's wig.
【００３５】（比較例４）実施例１で調製した人工毛髪
繊維用処理剤（１）のＰＯＥＯ水溶液の代わりにラウリ
ルアルコール硫酸エステル水溶液を用いた。つまりラウ
リルアルコール硫酸エステル水溶液を２．５部、アミノ
変性シリコーン水溶液を２．５部、イオン交換水９５部
の重量比で撹拌混合し、全重量に対するラウリルアルコ
ール硫酸エステルの固形成分とアミノ変性シリコーンの
シリコーン純分の合計重量の割合、つまり有効成分濃度
が１．０％となる処理剤（８）を得た。次に実施例１同
様の方法で単繊維繊度５０デニールの頭飾用モダクリル
合成繊維を得、この頭飾用モダクリル合成繊維を婦人用
ウィッグに加工する際にカールセット工程において、処
理剤（８）を使用した。この加工においてカールセット
工程におけるウェフトの整条性は良好であり、カールセ
ット後アルミパイプからのウェフト取り外しもウェフト
が絡まる等することなく非常に作業性良好であった。ま
たウィッグ加工の最終工程であるスタイリング工程にお
いても櫛通り、ブラッシングはスムーズであった。かく
して加工された婦人用ウィッグは処理剤で処理していな
い婦人用ウィッグと比較して０．２７％の重量増があ
り、この重量増は婦人用ウィッグに付着した処理剤
（８）の有効成分と考えられる。この処理剤（８）で処
理を行った婦人用ウィッグは触感、櫛通り性、フリッツ
防止性や帯電防止性は良好であった。この婦人用ウィッ
グを市販のシャンプーを添加した４０℃の温湯ですすぎ
洗いし自然乾燥するという工程を３サイクル実施したと
ころ、その婦人用ウィッグの重量は処理剤で処理してい
ない婦人用ウィッグの重量と比較して０．１２％の重量
増があった。この重量増分は洗浄後に頭飾製品に残留し
ている処理剤（８）の有効成分と考えられる。この洗浄
後の婦人用ウィッグの品質は、櫛通り性は良好な状態を
維持していたが、櫛通しやブラッシング時に静電気やフ
リッツが発生し、また触感は湿潤感が失われ、婦人用ウ
ィッグとして良好な品質とは言えない状態になった。Comparative Example 4 An aqueous solution of lauryl alcohol sulfate was used in place of the aqueous POEO solution for the artificial hair fiber treating agent (1) prepared in Example 1. That is, 2.5 parts of the aqueous solution of lauryl alcohol sulfate, 2.5 parts of the aqueous solution of amino-modified silicone, and 95 parts of ion-exchanged water were stirred and mixed at a weight ratio of the solid component of lauryl alcohol sulfate and amino-modified silicone with respect to the total weight. A treating agent (8) having a ratio of the total weight of the silicone pure, that is, the active ingredient concentration of 1.0% was obtained. Next, in the same manner as in Example 1, a modacrylic synthetic fiber for head decoration having a monofilament fineness of 50 denier was obtained, and the processing agent (8) was used in the curl setting step when processing this synthetic synthetic fiber for head decoration into a female wig. did. In this processing, the alignment property of the weft in the curl setting step was good, and the removal of the weft from the aluminum pipe after the curl setting was very good without tangling the weft. Also in the styling step, which is the final step of the wig processing, the brushing was smooth and smooth. The thus-processed women's wig has a weight increase of 0.27% compared to the women's wig not treated with the treatment agent, and this weight increase is due to the active ingredient of the treatment agent (8) attached to the women's wig. it is conceivable that. The women's wig treated with this treating agent (8) had good tactile sensation, combability, anti-fritz properties and antistatic properties. When this woman's wig was rinsed with hot water of 40 ° C to which a commercially available shampoo was added and air-dried three times, the weight of the woman's wig was the weight of the woman's wig not treated with the treatment agent There was a 0.12% weight increase compared to. This weight increase is considered to be an active ingredient of the treating agent (8) remaining in the headdress product after washing. As for the quality of the women's wig after this washing, the combability was maintained in a good state, but static electricity and fritz occurred during combing and brushing, and the tactile feeling lost the wet feeling, as a women's wig It was not good quality.
【００３６】（比較例５）実施例１で調製した処理剤
（１）のアミノ変性シリコーン水溶液の代わりにジメチ
ルシリコーン分散液を用いた。つまりＰＯＥＯ水溶液を
２．５部、ジメチルシリコーン分散液を２．５部、イオ
ン交換水９５部の重量比で撹拌混合し、全重量に対する
エチレンオキシドプロピレンオキシドブロック共重合体
の固形成分とジメチルシリコーンのシリコーン純分の合
計重量の割合、つまり有効成分濃度が１．０％となる処
理剤（９）を得た。次に実施例１同様の方法で単繊維繊
度５０デニールの頭飾用モダクリル合成繊維を得、この
頭飾用モダクリル合成繊維を婦人用ウィッグに加工する
際にカールセット工程において、処理剤（９）を使用し
た。この加工においてカールセット工程におけるウェフ
トの整条性は良好であり、カールセット後アルミパイプ
からのウェフト取り外しもウェフトが絡まる等すること
なく非常に作業性良好であった。またウィッグ加工の最
終工程であるスタイリング工程においても櫛通り、ブラ
ッシングはスムーズであった。Comparative Example 5 A dimethyl silicone dispersion was used in place of the amino-modified silicone aqueous solution of the treating agent (1) prepared in Example 1. That is, 2.5 parts of an aqueous POEO solution, 2.5 parts of a dimethyl silicone dispersion and 95 parts of ion-exchanged water were stirred and mixed at a weight ratio of the solid components of the ethylene oxide propylene oxide block copolymer and the silicone of the dimethyl silicone to the total weight. A treating agent (9) having a ratio of the total weight of the pure components, that is, an active ingredient concentration of 1.0% was obtained. Next, in the same manner as in Example 1, a modacrylic synthetic fiber for head decoration having a monofilament fineness of 50 denier was obtained, and the processing agent (9) was used in the curl setting step when processing the synthetic fiber for modal head decoration into a wig for women. did. In this processing, the alignment property of the weft in the curl setting step was good, and the removal of the weft from the aluminum pipe after the curl setting was very good without tangling the weft. Also in the styling step, which is the final step of the wig processing, the brushing was smooth and smooth.
【００３７】かくして加工された婦人用ウィッグは処理
剤で処理していない婦人用ウィッグと比較して０．２６
％の重量増があり、この重量増は婦人用ウィッグに付着
した処理剤（９）の有効成分と考えられる。この処理剤
（９）で処理を行った婦人用ウィッグは櫛通り性や帯電
防止性、フリッツ防止性は良好であったが、湿潤感がな
く硬い触感となった。またこの婦人用ウィッグを市販の
シャンプーを添加した４０℃の温湯ですすぎ洗いし自然
乾燥するという工程を３サイクル実施したところ、その
婦人用ウィッグの重量は処理剤で処理していない婦人用
ウィッグの重量と比較して０．１１％の重量増があっ
た。この重量増分は洗浄後に頭飾製品に残留している処
理剤（９）の有効成分と考えられる。この洗浄後の婦人
用ウィッグの品質は、櫛通り性は良好な状態を維持して
いたが、櫛通しやブラッシング時に静電気やフリッツが
発生し、また触感は更に硬さを増し、婦人用ウィッグと
して良好な品質とは言えない状態になった。The thus-processed women's wig is 0.26 compared to a women's wig not treated with the treating agent.
% Of the treatment agent (9) attached to the women's wig. The women's wig treated with this treating agent (9) had good combability, antistatic property, and antifritz property, but had a hard feel without wet feeling. In addition, when this woman's wig was rinsed with hot water of 40 ° C. to which a commercially available shampoo was added and air-dried three cycles, the weight of the woman's wig was that of a woman's wig that had not been treated with a treating agent. There was a weight gain of 0.11% compared to the weight. This weight increase is considered to be an active ingredient of the treating agent (9) remaining in the headdress product after washing. As for the quality of the women's wig after washing, the combability was maintained in a good state, but static electricity and frits were generated during combing and brushing, and the tactile sensation further increased, and as a women's wig, It was not good quality.
【００３８】[0038]
【発明の効果】本発明の処理剤を用いることにより、エ
チレンオキシドとプロピレンオキシドを主成分とする化
合物（Ａ）とアミノ変性シリコーンを主成分とする油剤
（Ｂ）の両者の優れた特性を持ちあわせるだけでなく、
本来洗浄に対する耐久性のなかった化合物（Ａ）にも洗
浄耐久性が備わり、使用面、品質面、耐久面といった従
来の処理剤が有していた問題点を改善され、水溶性で取
り扱いやすく、該処理剤を付着してなる人工毛髪用繊維
の開繊性や帯電防止性といった加工性や頭飾製品の触感
の柔軟性、外観、櫛通り、フリッツ防止性、帯電防止性
や保湿性といった美容特性を付与することができる。ま
た本発明の処理剤により処理された頭飾製品は触感、外
観、櫛通り、フリッツ防止性、帯電防止性や保湿性とい
った美容特性に優れており、その美容特性は洗浄等に対
する耐久性がある。By using the treating agent of the present invention, both the compound (A) containing ethylene oxide and propylene oxide as the main components and the oil agent (B) containing amino-modified silicone as the main component have excellent properties. not only,
The compound (A), which was originally not durable to washing, is provided with washing durability, improving the problems of conventional processing agents such as use, quality, and durability, and is water-soluble and easy to handle. Processability such as opening properties and antistatic properties of artificial hair fibers to which the treatment agent is attached, and flexibility of appearance and touch of head decoration products, appearance, combability, fritz prevention properties, cosmetic properties such as antistatic properties and moisture retention properties. Can be provided. Further, the head decoration product treated with the treating agent of the present invention is excellent in cosmetic properties such as tactile sensation, appearance, combability, anti-fritz property, antistatic property and moisturizing property, and the cosmetic property has durability against washing and the like.
───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 4C081 AB20 BB01 BB03 BB09 BC02 CA091 CA182 CA272 CC01 CC02 DA04 DA15 DB01 DC14 EA02 EA03 EA06 4L033 AB01 BA28 BA96 CA18 CA48 CA60 ──────────────────────────────────────────────────続 き Continued on the front page F term (reference) 4C081 AB20 BB01 BB03 BB09 BC02 CA091 CA182 CA272 CC01 CC02 DA04 DA15 DB01 DC14 EA02 EA03 EA06 4L033 AB01 BA28 BA96 CA18 CA48 CA60
Claims (14)
主成分とする化合物（Ａ）と、アミノ変性シリコーンを
主成分とする油剤（Ｂ）を含有する処理剤を付着してな
る人工毛髪用繊維。An artificial hair fiber obtained by adhering a treating agent containing a compound (A) containing ethylene oxide and propylene oxide as main components and an oil agent (B) containing amino-modified silicone as a main component.
レンオキシドのブロック共重合体、エチレンオキシドと
プロピレンオキシドのランダム共重合体およびエチレン
オキシドとプロピレンオキシドのアルキルエーテルから
なる群より選択される少なくとも１種の化合物である請
求項１記載の人工毛髪用繊維。2. The compound (A) is at least one compound selected from the group consisting of a block copolymer of ethylene oxide and propylene oxide, a random copolymer of ethylene oxide and propylene oxide, and an alkyl ether of ethylene oxide and propylene oxide. The artificial hair fiber according to claim 1.
コーン純分の重量比が３０／７０〜９５／５である請求
項１記載の人工毛髪用繊維。3. The fiber for artificial hair according to claim 1, wherein the weight ratio of the solid component of the compound (A) to the pure silicone of the oil agent (B) is 30/70 to 95/5.
（B）が下記一般式（Ｉ）で表される物質である請求項
１記載の人工毛髪用繊維。 【化１】 （但し式中、R1、R2、R3、R5、R6及びR7は炭素数１〜６
のアルキルである。R4は−R8―NH−CH2―CH2―NH2であ
り、R8は炭素数３〜６のアルキレンである。アミン当量
は５００以上４０００未満であり、平均分子量は５００
０〜１０００００の範囲である。またｍは１００〜２７
００整数、ｎは１〜２００の整数である。）4. The artificial hair fiber according to claim 1, wherein the oil agent (B) containing amino-modified silicone as a main component is a substance represented by the following general formula (I). Embedded image (Wherein, R 1 , R 2 , R 3 , R 5 , R 6 and R 7 have 1 to 6 carbon atoms)
Is an alkyl. R 4 is -R 8 -NH-CH 2 -CH 2 -NH 2, R 8 is alkylene of 3 to 6 carbon atoms. The amine equivalent is 500 or more and less than 4000, and the average molecular weight is 500
The range is from 0 to 100,000. M is 100 to 27
00 integer, n is an integer of 1 to 200. )
用繊維を加工してなる頭飾製品。5. A head decoration product obtained by processing the fiber for artificial hair according to claim 1.
頭飾製品。6. The headdress product according to claim 5, wherein the headdress product is a wig.
飾製品。7. The headdress product according to claim 5, wherein the headdress product is a two-piece.
５記載の頭飾製品。8. The headdress product according to claim 5, wherein the headdress product is a hair accessory.
の頭飾製品。9. The headdress product according to claim 5, wherein the headdress product is doll hair.
を主成分とする化合物（Ａ）と、アミノ変性シリコーン
を主成分とする油剤（Ｂ）を含有する処理剤を付着して
なる頭飾製品。10. A head decoration product obtained by adhering a treating agent containing a compound (A) containing ethylene oxide and propylene oxide as main components and an oil agent (B) containing amino-modified silicone as a main component.
ピレンオキシドのブロック共重合体、エチレンオキシド
とプロピレンオキシドのランダム共重合体およびエチレ
ンオキシドとプロピレンオキシドのアルキルエーテルか
らなる群より選択される少なくとも１種の化合物である
請求項１０記載の頭飾製品。11. The compound (A) is at least one compound selected from the group consisting of a block copolymer of ethylene oxide and propylene oxide, a random copolymer of ethylene oxide and propylene oxide, and an alkyl ether of ethylene oxide and propylene oxide. A headdress product according to claim 10.
リコーン純分の重量比が３０／７０〜９５／５である請
求項１０記載の頭飾製品。12. The head decoration product according to claim 10, wherein the weight ratio of the solid component of the compound (A) to the pure silicone of the oil agent (B) is 30/70 to 95/5.
剤（B）が下記一般式（Ｉ）で表される物質である請求
項１０記載の頭飾製品。 【化２】 （但し式中、R1、R2、R3、R5、R6及びR7は炭素数１〜６
のアルキルであり、R4は−R8―NH−CH2―CH2―NH2であ
り、R8は炭素数３〜６のアルキレンである。アミン当量
は５００以上４０００未満であり、平均分子量は５００
０〜１０００００の範囲である。またｍは１００〜２７
００の整数、ｎは１〜２００の整数である。）13. The head decoration product according to claim 10, wherein the oil agent (B) containing amino-modified silicone as a main component is a substance represented by the following general formula (I). Embedded image (Wherein, R 1 , R 2 , R 3 , R 5 , R 6 and R 7 have 1 to 6 carbon atoms)
R 4 is —R 8 —NH—CH 2 —CH 2 —NH 2 , and R 8 is alkylene having 3 to 6 carbon atoms. The amine equivalent is 500 or more and less than 4000, and the average molecular weight is 500
The range is from 0 to 100,000. M is 100 to 27
An integer of 00 and n is an integer of 1 to 200. )
シリコーン純分が合計で頭飾製品に対し０.０２〜５重
量％となるように付着してなる頭飾製品。14. A head decoration product wherein the solid component of the compound (A) and the silicone component of the oil agent (B) adhere to the head decoration product in a total amount of 0.02 to 5% by weight.