JP2000097241A - Holder for rolling bearing - Google Patents
Holder for rolling bearingInfo
- Publication number
- JP2000097241A JP2000097241A JP10267964A JP26796498A JP2000097241A JP 2000097241 A JP2000097241 A JP 2000097241A JP 10267964 A JP10267964 A JP 10267964A JP 26796498 A JP26796498 A JP 26796498A JP 2000097241 A JP2000097241 A JP 2000097241A
- Authority
- JP
- Japan
- Prior art keywords
- lubricating oil
- cage
- supply
- bearing
- rolling bearing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は転がり軸受用の保持
器に関し、例えば工作機械用軸受など、比較的高い回転
数で使用されて高精度が要求される軸受に用いるのに適
した保持器に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cage for a rolling bearing, and more particularly, to a cage suitable for use in a bearing used at a relatively high rotational speed and requiring high precision, such as a bearing for a machine tool. .
【０００２】[0002]
【従来の技術】転がり軸受においては、一般に、内輪と
外輪の間に、周方向に複数のポケットを備えた保持器を
配置し、その各ポケット内に転動体を収容することによ
り、各転動体相互の周方向への位置が規制される。この
ような保持器としては、金属製もしくは合成樹脂成形品
が用いられる。2. Description of the Related Art In a rolling bearing, generally, a cage having a plurality of pockets in a circumferential direction is arranged between an inner ring and an outer ring, and each rolling element is accommodated in each pocket. The positions in the circumferential direction are restricted. As such a cage, a metal or synthetic resin molded product is used.
【０００３】また、転がり軸受の潤滑には、一般的には
潤滑油を用いる方法とグリースを用いる方法があるが、
工作機械の主軸等、中・高速域で使用されて高精度が要
求される軸受には、通常、潤滑油が用いられる。[0003] Rolling bearings are generally lubricated by a method using lubricating oil or a method using grease.
Lubricating oil is usually used for bearings that are used in the middle and high speed regions and require high accuracy, such as the main shaft of machine tools.
【０００４】[0004]
【発明が解決しようとする課題】ところで、潤滑油を用
いた転がり軸受において、回転中に何らかの原因で潤滑
油の供給が止まった場合、潤滑不良を起こして焼き付き
に至る。特に金属製保持器を使用している軸受では、給
油の停止から焼き付きに至るまでの時間、つまり無給油
状態での焼き付き寿命が短い傾向にあり、潤滑油の供給
停止後に直ちに潤滑不良を生起し、焼き付きに至ってし
まう。In a rolling bearing using lubricating oil, if the supply of lubricating oil is stopped for some reason during rotation, poor lubrication occurs and seizure occurs. Especially in bearings using metal cages, the time from the stop of lubrication to seizure, that is, the seizure life without lubrication, tends to be short. , Resulting in burn-in.
【０００５】本発明の目的は、何らかの原因で潤滑油の
供給が止まった状態における軸受の焼き付き寿命を向上
させることのできる転がり軸受用保持器を提供すること
にある。An object of the present invention is to provide a rolling bearing retainer that can improve the seizure life of a bearing when lubricating oil supply is stopped for some reason.
【０００６】[0006]
【課題を解決するための手段】上記の目的を達成するた
め、本発明の転がり軸受用保持器は、転がり軸受の軌道
輪に沿って配置され、複数の転動体を軸受の周方向に一
定の間隔を開けて保持する保持器において、合成樹脂の
成形体からなり、かつ、充填材として無機多孔質の粒状
体が混入されていることによって特徴づけられる（請求
項１）。In order to achieve the above object, a rolling bearing cage according to the present invention is arranged along a race of a rolling bearing, and a plurality of rolling elements are fixed in a circumferential direction of the bearing. The retainer which is held at an interval is characterized by being formed of a synthetic resin molded article and being mixed with inorganic porous particles as a filler.
【０００７】ここで、本発明においては、無機多孔質の
粒状体の材質として、二酸化珪素を好適に使用すること
ができる（請求項２）。Here, in the present invention, silicon dioxide can be suitably used as the material of the inorganic porous granular material (claim 2).
【０００８】本発明においては、保持器のベース樹脂、
つまり主成分である合成樹脂の種類は任意であり、熱可
塑性、熱硬化性のいずれの樹脂をも用いることができ
る。また、その合成樹脂には、ガラス繊維、カーボン繊
維、有機繊維、あるいは布チップ等を強化材として含有
させてもよいし、含有させなくてもよい。[0008] In the present invention, the base resin of the cage,
That is, the type of the synthetic resin as the main component is arbitrary, and any of a thermoplastic resin and a thermosetting resin can be used. Further, the synthetic resin may or may not contain glass fiber, carbon fiber, organic fiber, cloth chip, or the like as a reinforcing material.
【０００９】また、本発明における無機多孔質粒状体の
粒径は、保持器としての強度やその他の機能を損なわな
い範囲で任意とすることができるが、一般には数μｍな
いしは数十μｍ程度とされる。The particle size of the inorganic porous granular material in the present invention can be arbitrarily set within a range that does not impair the strength and other functions as a retainer, but is generally about several μm to several tens μm. Is done.
【００１０】更に、本発明における保持器中での無機多
孔質粒状体の組成比は任意であるが、保持器としての強
度および油の吸収量等の観点から、好ましくは１０〜５
０重量％程度とされる。Furthermore, the composition ratio of the inorganic porous granular material in the cage in the present invention is arbitrary, but from the viewpoint of the strength as the cage and the amount of oil absorption, etc., it is preferably 10 to 5%.
It is about 0% by weight.
【００１１】本発明は、無機多孔質の粒状体の油の吸収
機能を利用して、合成樹脂製の保持器に充填材として混
入することによって、給油が停止したときの軸受の焼き
付き寿命を向上させようとするものである。The present invention improves the seizure life of a bearing when lubrication is stopped by mixing it as a filler into a synthetic resin cage by utilizing the oil absorbing function of the inorganic porous granular material. It is to try to make it.
【００１２】すわなち、二酸化珪素、いわゆるシリカ等
の無機多孔質は、油の存在下においては毛細管現象によ
り油を吸収するとともに、周囲に油がなくなれば、吸収
されている油は外部に滲み出す。このような無機多孔質
を粒状体の形で合成樹脂製の保持器内に充填材として混
入させておくと、その保持器を組み込んだ転がり軸受を
潤滑油を用いた潤滑方法のもとに使用すれば、潤滑油が
正常に供給されている状態では保持器内にその潤滑油が
吸収され、何らかの原因で潤滑油の供給が停止した場合
には、保持器内の潤滑油が滲み出して転動体と軌道輪と
の間に供給される。従って、軸受に対する潤滑油の供給
停止後、ある期間内においては所定量の潤滑油の供給状
態が実質的に継続されることになり、無給油状態におけ
る焼き付き寿命が向上する。That is, inorganic porous materials such as silicon dioxide, so-called silica, absorb oil by capillary action in the presence of oil, and when there is no oil around the oil, the absorbed oil bleeds to the outside. put out. If such an inorganic porous material is mixed as a filler in a synthetic resin cage in the form of granules, the rolling bearing incorporating the cage can be used under a lubricating method using lubricating oil. If the lubricating oil is supplied normally, the lubricating oil will be absorbed into the cage, and if the lubricating oil supply is stopped for any reason, the lubricating oil in the cage will ooze out and rotate. It is supplied between the moving body and the race. Therefore, after the supply of the lubricating oil to the bearing is stopped, the supply state of the predetermined amount of the lubricating oil is substantially continued within a certain period, and the seizure life in the non-lubricating state is improved.
【００１３】また、請求項２に係る発明のように、二酸
化珪素からなる無機多孔質の粒状体は、加熱や酸化、ア
ルカリ処理等に対してもその形態が変化せず、しかもベ
ース樹脂に対する悪影響を及ぼすことがないとともに、
製造に際しての比表面積や細孔分布の調整法が確立され
ているなど、所望の性能を有する多孔質粒状体を入手し
やすいという利点がある。Further, as in the invention according to the second aspect, the inorganic porous granular material made of silicon dioxide does not change its form even when heated, oxidized, or treated with alkali, and has an adverse effect on the base resin. Has no effect,
There is an advantage that a porous granular material having desired performance can be easily obtained, for example, a method for adjusting a specific surface area and a pore distribution at the time of production has been established.
【００１４】[0014]
【発明の実施の形態】以下、本発明の好適な実施の形態
を図面を参照しつつ説明する。図１は本発明の実施の形
態の構成を示す断面図である。この実施の形態はアンギ
ュラ玉軸受に本発明を適用した例であり、内輪１と外輪
２の間に、合成樹脂の成形体からなる保持器３により保
持された複数のボール（転動体）４が組み込まれてい
る。保持器３は、その形状・構造自体は従来の合成樹脂
製保持器と同等であって、全体として円環状ないしは短
円筒状をなし、その周方向に各ボール４を収容するため
の複数のポケット３１が互いに一定の間隔のもとに形成
されている。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Preferred embodiments of the present invention will be described below with reference to the drawings. FIG. 1 is a sectional view showing the configuration of the embodiment of the present invention. This embodiment is an example in which the present invention is applied to an angular ball bearing. A plurality of balls (rolling elements) 4 held by a retainer 3 made of a synthetic resin molded body are provided between an inner ring 1 and an outer ring 2. It has been incorporated. The retainer 3 has the same shape and structure as the conventional synthetic resin retainer, has a ring shape or short cylindrical shape as a whole, and has a plurality of pockets for accommodating the balls 4 in the circumferential direction. 31 are formed at a constant interval from each other.
【００１５】さて、この保持器３は、例えばノボラック
樹脂をベース樹脂として、強化材としてガラス繊維が用
いられているとともに、充填材として二酸化珪素からな
る無機多孔質の粒状体が混入されている。この例におい
ては、無機多孔質粒状体として、鈴木油脂工業株式会社
製の商品名ゴッドボールＥ−２Ｃ（平均粒径０．９〜約
１４μｍ、真密度２．１ｇ／ｃｍ3 、かさ密度約０．２
ｇ／ｃｍ3 、表面細孔直径５０〜１５０Å、比表面積３
５０〜５００ｍ2 ／ｇ、細孔容積１．３０〜１．４０ｍ
ｌ／ｇ）を用いた。また、この保持器３の材料組成は、
重量％でベース樹脂２８％、強化ガラス繊維４２％、上
記の無機多孔質粒状体３０％である。このような組成比
の保持器３は、実験によれば、潤滑油内に浸漬した状態
を所定期間にわたって継続した後には、１２重量％以上
の潤滑油が保持器３内に吸収されることが確かめられて
いる。The cage 3 is made of, for example, a novolak resin as a base resin, glass fibers as a reinforcing material, and an inorganic porous granular material made of silicon dioxide as a filler. In this example, as an inorganic porous granular material, Suzuki Yushi Kogyo Co., Ltd. trade name Godball E-2C (average particle size 0.9 to about 14 μm, true density 2.1 g / cm 3 , bulk density about 0 .2
g / cm 3 , surface pore diameter 50-150 °, specific surface area 3
50-500 m 2 / g, pore volume 1.30-1.40 m
1 / g) was used. The material composition of the cage 3 is as follows:
It is 28% by weight of the base resin, 42% of the reinforced glass fiber, and 30% of the above-mentioned inorganic porous granular material by weight%. According to the experiment, the cage 3 having such a composition ratio is capable of absorbing 12% by weight or more of the lubricating oil into the cage 3 after continuing the state of being immersed in the lubricating oil for a predetermined period. Has been verified.
【００１６】以上の実施の形態は、例えば工作機械にお
ける各種スピンドル用の軸受等として、潤滑油を用いた
潤滑方法のもとに使用される。このような使用ほうほう
ににおいて、軸受に対して正常に潤滑油が供給されてい
る状態では、保持器３中の無機多孔質粒状体が潤滑油を
吸収して含油状態となり、何らかの原因によって軸受に
対する潤滑油の供給が停止した状態では、無機多孔質粒
状体に含まれている潤滑油が外部に滲み出して、内輪１
と外輪２の軌道面と各ボール４の間に供給される。The above embodiment is used as a bearing for various spindles in a machine tool, for example, under a lubricating method using lubricating oil. In such a manner of use, when lubricating oil is normally supplied to the bearing, the inorganic porous granules in the retainer 3 absorb the lubricating oil and become oil-impregnated. When the supply of the lubricating oil to the inner ring 1 is stopped, the lubricating oil contained in the inorganic porous granular material oozes out and the inner ring 1
And between the raceway surface of the outer ring 2 and each ball 4.
【００１７】従って、潤滑油の供給停止後にも、ある期
間内においては完全な無潤滑状態にはならず、実質的に
ある程度の潤滑油の供給状態が継続する。そのため、何
らかの原因で潤滑油の供給が停止した後、焼き付きに至
るまでの時間が従来に比して長くなる。これにより、例
えば、工作機械に潤滑油の供給が停止したことを何らか
の方法により検知する手段を設けて、その検知信号が発
生したときに直ちに工作機械を停止させずに、工作機械
の動作サイクル中において都合のよい状態となるまで、
軸受を焼き付かせることなく機械の動作を継続させる、
といった使用方法の採用も可能となる。Therefore, even after the supply of the lubricating oil is stopped, the lubricating oil is not completely lubricated for a certain period of time, and the lubricating oil is supplied to some extent. For this reason, after the supply of the lubricating oil is stopped for some reason, the time until the seizure is longer than in the related art. Accordingly, for example, a means for detecting the stop of the supply of the lubricating oil to the machine tool by some method is provided, and the machine tool is not stopped immediately when the detection signal is generated, and the machine tool is operated during the operation cycle. Until it is in a convenient state at
Continue the operation of the machine without burning the bearing,
It is also possible to adopt such a usage method.
【００１８】なお、本発明は以上の実施の形態に限られ
ることなく、ベース樹脂の種類や、同樹脂中における無
機多孔質および強化材の組成比、あるいは強化材の有無
は、用途に応じて任意とすることができ、また、無機多
孔質粒状体の材質、更にはその構造についても、混入に
よって保持器としての強度等の基本性能を損なうことな
く、所要量の潤滑油の吸収・放出能力があれば任意とす
ることができ、特に構造については多孔質を壁体として
内部に空洞を備えた中空タイプのものなどを好適に使用
することができる。The present invention is not limited to the above embodiment, and the type of the base resin, the composition ratio of the inorganic porous material and the reinforcing material in the resin, or the presence or absence of the reinforcing material depends on the application. The material of the inorganic porous granular material, and also its structure, can absorb and release the required amount of lubricating oil without impairing the basic performance such as the strength as a cage by mixing. Any structure can be used as long as there is a hollow structure. In particular, a hollow structure having a cavity inside with a porous wall can be suitably used.
【００１９】更に、本発明の保持器が適用される軸受の
種類は、上記のようなアンギュラ玉軸受に限られること
なく、他の種々の軸受に対して等しく適用し得ることは
言うまでもない。Further, it goes without saying that the type of bearing to which the cage of the present invention is applied is not limited to the above-mentioned angular ball bearing, but can be equally applied to various other bearings.
【００２０】[0020]
【発明の効果】以上のように、本発明によれば、合成樹
脂製の保持器内に充填材として無機多孔質の粒状体を含
ませることにより、保持器に潤滑油の吸収機能を持たせ
ているので、潤滑油の正常な供給状態においてはその潤
滑油を保持器内に吸収するとともに、潤滑油の供給が停
止したときには保持器内に吸収している潤滑油が放出さ
れて軸受内に供給されるから、何らかの原因で潤滑油の
供給が停止したとき、ある期間内においては所定量の潤
滑油の供給状態が継続することになり、無給油状態での
焼き付き寿命が向上する。As described above, according to the present invention, the cage has a function of absorbing lubricating oil by including inorganic porous granular material as a filler in the cage made of synthetic resin. Therefore, in the normal lubricating oil supply state, the lubricating oil is absorbed into the cage, and when the lubricating oil supply is stopped, the lubricating oil absorbed in the cage is released and enters the bearing. When the supply of the lubricating oil is stopped for some reason, the supply state of the predetermined amount of the lubricating oil is continued within a certain period, and the seizure life in an unlubricated state is improved.
【図１】本発明の構成を示す断面図である。FIG. 1 is a sectional view showing a configuration of the present invention.
１ 内輪 ２ 外輪 ３ 保持器 ３１ ポケット ４ ボール（転動体） Reference Signs List 1 inner ring 2 outer ring 3 cage 31 pocket 4 ball (rolling element)
Claims (2)
複数の転動体を軸受の周方向に一定の間隔を開けて保持
する保持器において、合成樹脂の成形体からなり、か
つ、充填材として無機多孔質の粒状体が混入されている
ことを特徴とする転がり軸受用保持器。Claims: 1. A rolling bearing is arranged along a race of a rolling bearing,
In a cage for holding a plurality of rolling elements at predetermined intervals in the circumferential direction of the bearing, the cage is made of a synthetic resin molded article, and is characterized by being mixed with inorganic porous granular material as a filler. Rolling bearing retainer.
珪素であることを特徴とする請求項１に記載の転がり軸
受用保持器。2. The cage for a rolling bearing according to claim 1, wherein the material of said inorganic porous granular material is silicon dioxide.